KR20160037721A - Two-sided adhesive tape for touch screen panel fixing - Google Patents
Two-sided adhesive tape for touch screen panel fixing Download PDFInfo
- Publication number
- KR20160037721A KR20160037721A KR1020150017513A KR20150017513A KR20160037721A KR 20160037721 A KR20160037721 A KR 20160037721A KR 1020150017513 A KR1020150017513 A KR 1020150017513A KR 20150017513 A KR20150017513 A KR 20150017513A KR 20160037721 A KR20160037721 A KR 20160037721A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- methacrylate
- touch screen
- adhesive layer
- Prior art date
Abstract
Description
본 발명은 터치스크린 패널 고정용 양면 점착 테이프에 관한 것으로, 더욱 상세하게는 점착성이 우수할 뿐만 아니라, 우수한 내열성, 방수성 및 내충격성 등을 나타내어, 터치스크린의 패널을 고정하는데 유용한 효과를 나타내는 터치스크린 패널 고정용 양면 점착 테이프에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a double-sided pressure-sensitive adhesive tape for fixing a touch screen panel, and more particularly, to a double-sided pressure-sensitive adhesive tape for fixing a touch screen panel which is excellent in adhesiveness and exhibits excellent heat resistance, water resistance, To a double-sided pressure-sensitive adhesive tape for fixing a panel.
최근 휴대전화나 태블릿PC 등과 같이 터치패널을 사용하는 제품의 사용이 크게 증가하고 있는데, 이러한 전자기기들의 터치스크린은 저항막 방식의 필름 형태에서 정전식 방법의 강화유리 형태로 변화하고 있고, 이러한 강화유리에 각종 전도성 필름 및 점착필름이 부착되는 형태로 이루어진다.In recent years, the use of touch panel products such as mobile phones and tablet PCs has been greatly increased. Touch screens of such electronic devices are changing from resistive film type to reinforced glass type electrostatic type. And various conductive films and adhesive films are attached to the glass.
또한, 터치패널의 하부에는 시인성의 향상을 위한 OCA(Optically Clear Adhesive)뿐만 아니라 ITO film 등이 사용되는데, 터치스크린 분야에서 양면 점착 테이프는 서로 다른 재질의 부품의 표면을 부착하기 위해 사용되는데, 일반적인 양면테이프는 PET와 같은 강직성이 있는 필름의 양면에 점착제를 도포하여 이루어진다.In addition, in addition to OCA (Optically Clear Adhesive) for improving visibility, an ITO film or the like is used as a lower part of the touch panel. In the touch screen field, a double-sided adhesive tape is used for attaching the surface of a component made of different materials. Double-sided tape is made by applying a pressure-sensitive adhesive on both sides of a rigid film such as PET.
그러나, PET와 같은 강직성의 필름을 사용한 전자기기는 외부로부터 충격이 전달되면 터치스크린과 기기 본체 혹은 LCD 패널부가 서로 분리되는 문제점이 발생할 수 있으며, 터치스크린이 가벼운 필름재질에서 무거운 강화유리 재질로 변화하면서 내충격성의 향상이 요구되고 있으며, 피착제의 종류와 상관없이 안정적인 점착 성능을 유지할 수 있는 특성이 요구되고 있다.However, in the case of an electronic device using a rigid film such as PET, when a shock is transmitted from the outside, there may arise a problem that the touch screen and the body of the device or the LCD panel are separated from each other, and the touch screen is changed from a light film material to a heavy reinforcing glass material It is required to improve the impact resistance and to maintain a stable adhesive performance irrespective of the kind of the adhesive agent.
뿐만 아니라, 휴대전화나 테블릿 PC 등과 같은 전자기기는 환경을 선택하지 않고 사용되는 기기로, 해안가나 욕실 등과 같이 수분에 노출될 수 있는 장소에서의 사용이 늘어나고 있기 때문에, 터치스크린 패널에 사용되는 양면 점착 테이프는 2mm 이하의 얇은 폭을 가지면서도, 우수한 내열성, 방수성 및 내충격성 등의 물성을 나타내어야 한다.In addition, since electronic devices such as mobile phones and tablet PCs are used without selecting the environment, they are used in places where they can be exposed to water, such as the shore or bathroom, The double-sided pressure-sensitive adhesive tape should exhibit properties such as excellent heat resistance, water resistance and impact resistance while having a width of 2 mm or less.
상기의 문제점을 해소하기 위해 비교적 내충격성이 우수한 PE-foam과 같은 발포체를 기재로 사용하고 양면에 점착제층을 도포한 양면 점착 테이프가 사용되고 있으나, 발포체를 기재로 사용한 양면 점착 테이프는 수분의 침투를 제어하는 독립 기포의 기포벽을 폭 방향에 대해서 충분히 확보할 수 없어 방수성능이 저하되며, 발포 형상의 크기에는 한계가 있어 그 크기를 미세하게 제어하는 것이 곤란하고 저밀도의 구조와 낮은 탄성률을 가지고 있기 때문에 내구성의 신뢰도를 보장하지 못하는 문제점이 있었다.In order to solve the above problems, a double-sided adhesive tape having a relatively high impact resistance such as PE-foam and a double-sided adhesive tape having a pressure-sensitive adhesive layer coated on both sides thereof is used. However, The bubble walls of the independent bubbles to be controlled can not be sufficiently secured in the width direction, and the waterproof performance is lowered. There is a limit to the size of the foamed shape, and it is difficult to finely control the size thereof. Therefore, the reliability of durability can not be guaranteed.
본 발명의 목적은 점착성이 우수할 뿐만 아니라, 우수한 내열성, 방수성 및 내충격성 등을 나타내어, 터치스크린의 패널을 고정하는데 유용한 효과를 나타내는 터치스크린 패널 고정용 양면 점착 테이프를 제공하는 것이다.An object of the present invention is to provide a double-sided pressure-sensitive adhesive tape for fixing a touch screen panel, which exhibits excellent heat resistance, water resistance, impact resistance and the like as well as excellent effect of fixing the panel of the touch screen.
본 발명의 목적은 기재층, 상기 기재층의 일면에 형성되는 제1점착층 및 상기 기재층의 타면에 형성되며 비드가 함유되는 제2점착층으로 이루어지는 것을 특징으로 하는 터치스크린 패널 고정용 양면 점착 테이프를 제공함에 의해 달성된다.The object of the present invention is to provide a double-sided adhesive for fixing a touch screen panel, which comprises a substrate layer, a first adhesive layer formed on one surface of the substrate layer, and a second adhesive layer formed on the other surface of the substrate layer, Tape. ≪ / RTI >
본 발명의 바람직한 특징에 따르면, 상기 기재층은 두께가 1.4 내지 50㎛이며, 양면이 코로나 방전처리된 합성수지로 이루어지는 것으로 한다.According to a preferred feature of the present invention, the base layer is made of a synthetic resin having a thickness of 1.4 to 50 탆 and corona discharge-treated on both sides.
본 발명의 더 바람직한 특징에 따르면, 상기 제1점착층은 아크릴계 수지 100 중량부, 용제 10 내지 50 중량부 및 경화제 0.1 내지 10 중량부로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the first adhesive layer comprises 100 parts by weight of an acrylic resin, 10 to 50 parts by weight of a solvent and 0.1 to 10 parts by weight of a curing agent.
본 발명의 더욱 바람직한 특징에 따르면, 상기 제2점착층은 비드가 함유된 아크릴계 수지 100 중량부, 용제 10 내지 50 중량부 및 경화제 0.1 내지 10 중량부로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the second adhesive layer comprises 100 parts by weight of an acrylic resin containing beads, 10 to 50 parts by weight of a solvent and 0.1 to 10 parts by weight of a curing agent.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 아크릴계 수지는 부틸아크릴레이트, 부틸메타크릴레이트, 헥실아크릴레이트, 헥실메타크릴레이트, n-옥틸아크릴레이트, n-옥틸메타크릴레이트, 이소옥틸아크릴레이트, 이소옥틸메타크릴레이트, 2-에틸헥실아크릴레이트, 2-에틸헥실메타크릴레이트, 이소노닐아크릴레이트 및 이소노닐메타크릴레이트로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것으로 한다.According to a more preferred feature of the present invention, the acrylic resin is at least one selected from the group consisting of butyl acrylate, butyl methacrylate, hexyl acrylate, hexyl methacrylate, n-octyl acrylate, n-octyl methacrylate, isooctyl acrylate, Acrylate, isooctyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, isononyl acrylate and isononyl methacrylate.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 아크릴계 수지는 메타아크릴산, 2-메타아크릴옥시 아세트산, 3-메타아크릴옥시 프로필산, 4-메타아크릴옥시 부틸산, 푸마르산, 말레산 및 말레산 무수물로 이루어진 그룹에서 선택된 하나와, 2-하이드록시에틸 메타아크릴레이트, 2-하이드록시프로필 메타아크릴레이트, 4-하이드록시부틸 메타아크릴레이트, 6-하이드록시헥실 메타아크릴레이트, 8-하이드록시옥틸 메타아크릴레이트 및 2-하이드록시에틸렌 글리콜 메타아크릴레이트로 이루어진 그룹에서 선택된 하나를 공중합하여 제조되는 것으로 한다.According to a further preferred feature of the present invention, the acrylic resin is selected from the group consisting of methacrylic acid, 2-methacryloxy oxyacetic acid, 3-methacryloxypropic acid, 4-methacryloxybutyric acid, fumaric acid, maleic acid and maleic anhydride Hydroxyethyl methacrylate, 4-hydroxybutyl methacrylate, 6-hydroxyhexyl methacrylate, 8-hydroxyoctyl methacrylate, 2-hydroxyethyl methacrylate, And 2-hydroxyethylene glycol methacrylate.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 비드는 입자크기가 5 내지 200㎛이며, 열팽창성 수지, 글라스 마크로벌룬(glass macroballoon), 글라스 버블 및 실리카로 이루어진 그룹에서 선택된 하나로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the beads have a particle size of 5 to 200 탆 and are made of one selected from the group consisting of thermally expandable resin, glass macroballoon, glass bubble and silica.
본 발명에 따른 터치스크린 패널 고정용 양면 점착 테이프는 점착성이 우수할 뿐만 아니라, 우수한 내열성, 방수성 및 내충격성 등을 나타내어, 터치스크린의 패널을 고정하는데 유용한 효과를 나타낸다.INDUSTRIAL APPLICABILITY The double-sided adhesive tape for fixing a touch screen panel according to the present invention exhibits excellent heat resistance, water resistance and impact resistance as well as excellent tackiness, and is useful for fixing a panel of a touch screen.
도 1은 본 발명에 따른 터치스크린 패널 고정용 양면 점착 테이프를 나타낸 분해사시도이다.1 is an exploded perspective view showing a double-sided adhesive tape for fixing a touch screen panel according to the present invention.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.Hereinafter, preferred embodiments of the present invention and physical properties of the respective components will be described in detail with reference to the accompanying drawings. However, the present invention is not limited thereto, And this does not mean that the technical idea and scope of the present invention are limited.
본 발명에 따른 터치스크린 패널 고정용 양면 점착 테이프는 기재층(10), 상기 기재층(10)의 일면에 형성되는 제1점착층(20) 및 상기 기재층(10)의 타면에 형성되며 비드가 함유되는 제2점착층(30)으로 이루어진다.A double-sided adhesive tape for fixing a touch screen panel according to the present invention comprises a
상기 기재층(10)은 본 발명에 따른 터치스크린 패널 고정용 양면 점착 테이프의 기재가 되는 층으로, 1.4 내지 50㎛ 두께의 합성수지 필름으로 이루어지는데, 1.4내지 12㎛의 두께를 나타내는 것이 더욱 바람직하다.The
또한, 상기 기재층(10)을 구성하는 합성 수지 필름은, 양면에 도포되는 제1점착층(10)과 제2점착층(20)의 밀착성을 향상시킬 목적으로 필요에 따라 양면에 산화법이나 요철화법 등에 의해 표면 처리를 실시할 수 있는데, 상기 산화법은 코로나 방전처리, 크로산 처리, 플라즈마 방전 처리 및 자외선 조사 처리 등이 있고 요철화법은 샌드 블라스트법 및 용제처리 법 등이 있는데, 그 중 단가와 효율성 측면을 고려하여 코로나 방전 처리법이 가장 바람직하다.The synthetic resin film constituting the
또한, 본 발명의 양면 점착테이프에 적용되는 기재층(10)은 폴리에틸렌테레프탈레이트로 이루어지는 것이 바람직하며, 기재층(10)의 색은 차광기능을 나타내는 검은색으로 착색되어 있는 것이 더욱 바람직하다.The
상기 제1점착층(20)은 상기 기재층(10)의 일면에 30 내지 100㎛의 두께로 형성되며, 실리콘계, 아크릴계, 고무계 및 우레탄계 점착수지 등으로 이루어진 그룹에서 선택된 하나 이상의 수지에 용제 및 경화제를 혼합하여 이루어지는데, 수지 100 중량부에 용제 10 내지 50 중량부 및 경화제 0.1 내지 10 중량부를 혼합하여 이루어지며, 상기 수지로는 황변저항성이 있고 광학적 특성이 우수한 아크릴계를 사용하는 것이 바람직하다.The first
고분자는 낮은 분자량의 물질의 함유량이 많을수록 점착력이 높아지고 반대로 높은 분자량의 물질의 함유량이 많을수록 응집력이 높아지기 때문에 상기 아크릴계 수지의 분산도 PDI(polydispersity index)는 6 내지 10 바람직하게는 5 내지 12로 설계하는 것이 바람직하며, 상기 아크릴계 수지의 조성은 특별히 한정되지 않지만 아크릴산 에스테르계 모노머를 포함할 수 있다.As the content of the low molecular weight material increases, the cohesive force increases, and as the content of the high molecular weight material increases, the cohesive force increases. Therefore, the dispersity of the acrylic resin is designed to be 6 to 10, preferably 5 to 12, And the composition of the acrylic resin is not particularly limited, but may include an acrylate-based monomer.
상기 아크릴산 에스테르계 모노머는 부틸아크릴레이트, 부틸메타크릴레이트, 헥실아크릴레이트, 헥실메타크릴레이트, n-옥틸아크릴레이트, n-옥틸메타크릴레이트, 이소옥틸아크릴레이트, 이소옥틸메타크릴레이트, 2-에틸헥실아크릴레이트, 2-에틸헥실메타크릴레이트, 이소노닐아크릴레이트, 이소노닐메타크릴레이트로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는데, 본 발명에 사용되는 아크릴 모노머는 내충격성과 점착력을 고려하여 유리전이온도가 -80℃ 내지 -50℃ 범위에 있는 아크릴산 에스테르계 모노머를 사용하는 것이 가장 바람직하다.The acrylic ester monomer may be selected from the group consisting of butyl acrylate, butyl methacrylate, hexyl acrylate, hexyl methacrylate, n-octyl acrylate, n-octyl methacrylate, isooctyl acrylate, isooctyl methacrylate, 2- Ethylhexyl acrylate, 2-ethylhexyl methacrylate, isononyl acrylate, isononyl methacrylate. The acrylic monomer used in the present invention has a glass transition temperature in consideration of impact resistance and adhesion, It is most preferable to use an acrylic ester monomer having a temperature in the range of -80 占 폚 to -50 占 폚.
또한, 본 발명에서 사용할 수 있는 아크릴계 수지는 메타아크릴산, 2-메타아크릴옥시 아세트산, 3-메타아크릴옥시 프로필산, 4-메타아크릴옥시 부틸산, 푸마르산, 말레산 및 말레산 무수물로 이루어진 그룹에서 선택된 하나와, 2-하이드록시에틸 메타아크릴레이트, 2-하이드록시프로필 메타아크릴레이트, 4-하이드록시부틸 메타아크릴레이트, 6-하이드록시헥실 메타아크릴레이트, 8-하이드록시옥틸 메타아크릴레이트 및 2-하이드록시에틸렌 글리콜 메타아크릴레이트로 이루어진 그룹에서 선택된 하나를 공중합하여 이루어질 수도 있다.The acrylic resin that can be used in the present invention is selected from the group consisting of methacrylic acid, 2-methacryloxy oxyacetic acid, 3-methacryloxypropic acid, 4-methacryloxybutyric acid, fumaric acid, maleic acid and maleic anhydride Hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, 4-hydroxybutyl methacrylate, 6-hydroxyhexyl methacrylate, 8-hydroxyoctyl methacrylate and 2- Hydroxyethyleneglycol methacrylate, and hydroxyethyleneglycol methacrylate.
또한, 상기 용제는 10 내지 50 중량부가 함유되며, 상기의 아크릴계 수지를 합성하는데 사용될 수 있는 성분이면 특별히 한정되지 않고 어떠한 것이든 사용가능하나, 에틸아세테이트, 사이클로헥산, n-헥산, 아세톤, 디메틸카보네이트, 메탄올, 에탄올 및 이소프로필알콜 등으로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직한데, 상기 용제의 함량이 10 중량부 미만이면 점착수지의 점도가 높아져 코팅작업시의 문제가 발생할 수 있고, 상기 용제의 양이 50 중량부를 초과하게 되면 고형분의 함량이 줄어들어 제1점착층의 물성이 저하될 우려가 있다.In addition, the solvent is contained in an amount of 10 to 50 parts by weight, and is not particularly limited as long as it is a component that can be used for synthesizing the acrylic resin. Any solvent can be used, and ethyl acetate, cyclohexane, n-hexane, acetone, dimethyl carbonate , Methanol, ethanol, isopropyl alcohol, etc. If the content of the solvent is less than 10 parts by weight, the viscosity of the pressure-sensitive adhesive resin may be increased to cause a problem during coating, Is more than 50 parts by weight, the content of the solid content may be reduced and the physical properties of the first adhesive layer may be deteriorated.
또한, 상기 경화제는 0.1 내지 10 중량부가 함유되며, 상기 아크릴계 수지를 가교시키는 역할을 하는데, 이소시아네이트 화합물, 에폭시 수지, 멜라민 수지, 요소 수지, 다이알데하이드류 및 금속 킬레이트 화합물로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직하다.The above-mentioned curing agent is contained in an amount of 0.1 to 10 parts by weight, and serves to crosslink the acrylic resin. The curing agent is one or more selected from the group consisting of an isocyanate compound, an epoxy resin, a melamine resin, a urea resin, a dialdehyde and a metal chelate compound .
이때, 상기 경화제의 함량이 0.1 중량부 미만이면, 고온 및 고습 조건 하에서 제1점착제층의 응집 파괴 현상이 발생하여 내구 신뢰성이 저하될 우려가 있고, 상기 경화제의 함량이 10 중량부를 초과하게 되면 상용성 저하로 인해 유동성이 감소할 우려가 있다.If the content of the curing agent is less than 0.1 parts by weight, the first pressure-sensitive adhesive layer may undergo coagulation failure under high temperature and high humidity conditions, resulting in deterioration in durability reliability. When the content of the curing agent exceeds 10 parts by weight, There is a fear that the fluidity may decrease due to the deterioration of the property.
상기의 성분으로 이루어지는 제1점착층(20)은 바코트법, 리버스 롤 코트법, 나이프 코트법, 롤 나이프 코트법, 그라비아 코트법 및 닥터 블레이드 코트법 등과 같이 종래에 테이프의 제조시에 사용되는 방법을 이용하여 이형성을 가지는 기재 상에 도포한 후에 경화시켜 점착층을 형성하고, 형성된 점착층을 상기 기재층(10)과 합지하는 과정을 통해 상기 기재층(10)의 일면에 제1점착층(20)을 형성한다.The first
이때, 상기 이형성을 가지는 기재는 폴리에틸렌테레프탈레이트, 폴리에틸렌, 폴리프로필렌, 폴리부텐, 폴리부타다이엔, 폴리메틸펜텐, 폴리염화비닐, 염화비닐 공중합체, 폴리우레탄, 폴리스타이렌, 폴리카보네이트, 불소수지, 저밀도 폴리에틸렌, 트리아세틸셀루로스 등의 수지 필름이나 상질지, 코트지, 글라신지, 라미네이트지 등으로 이루어진 그릅에서 선택된 하나로 이루어지는데, 상기의 성분들 중 하나로 이루어지는 이형성을 갖는 기재는 탄력성이 뛰어나고 가격측면에서 저렴한 폴리에틸렌테레프탈레이트 필름이 바람직하며, 이때, 상기 이형성을 갖는 기재의 두께는 5 내지 200㎛로 이루어지는 것이 바람직하며, 50 내지 100㎛로 이루어지는 것이 더욱 바람직하다.In this case, the substrate having the releasing property may be selected from the group consisting of polyethylene terephthalate, polyethylene, polypropylene, polybutene, polybutadiene, polymethylpentene, polyvinyl chloride, vinyl chloride copolymer, polyurethane, polystyrene, polycarbonate, Polyethylene, or triacetylcellulose, or a group consisting of a high-quality paper, a coated paper, a glossy paper, a laminate paper, etc. The substrate having a releasing property composed of one of the above- An inexpensive polyethylene terephthalate film is preferable, and the thickness of the substrate having the releasing property is preferably 5 to 200 탆, more preferably 50 to 100 탆.
상기 제2점착층(30)은 상기 기재층(10)의 타면에 30 내지 100㎛의 두께로 형성되며 비드가 함유되어 이루어지는데, 비드가 함유된 아크릴계 수지 100 중량부, 용제 10 내지 50 중량부 및 경화제 0.1 내지 50 중량부로 이루어지는 것이 바람직하다.The second
상기 비드는 아크릴계 수지 100 중량부 대비 0.5 내지 1 중량부가 함유되는데, 입자크기가 5 내지 200㎛이고, 열팽창성 수지, 글라스 마크로벌룬, 글라스 버블 및 실리카로 이루어진 그룹에서 선택된 하나로 이루어지며, 본 발명에 따른 터치스크린 패널 고정용 양면 점착 테이프의 내열성 및 내충격성을 향상시키는 역할을 한다.The beads are contained in an amount of 0.5 to 1 part by weight based on 100 parts by weight of the acrylic resin. The beads have a particle size of 5 to 200 μm and consist of one selected from the group consisting of thermally expandable resin, glass macrobalon, glass bubble and silica, Sensitive adhesive tape for fixing a touch screen panel according to the present invention.
상기 비드의 함량이 0.5 중량부 미만이면 상기의 효과가 미미하며, 상기 비드의 함량이 1 중량부를 초과하게 되면, 상기 제2점착층(30)의 점착강도가 저하될 수 있다.If the content of the beads is less than 0.5 parts by weight, the above effect is insignificant. If the content of the beads exceeds 1 part by weight, the adhesive strength of the second
이때, 상기 아크릴계 수지, 용제 및 경화제의 성분 및 역할은 상기 제1점착층(20)을 설명하는 부분에 기재된 내용과 동일하므로 이에 대한 설명은 생략하기로 한다.At this time, components and roles of the acrylic resin, the solvent and the curing agent are the same as those described in the description of the first
이하에서는, 본 발명에 따른 터치스크린 패널 고정용 양면 점착 테이프의 제조방법 및 그 제조방법을 통해 제조된 터치스크린 패널 고정용 양면 점착 테이프의 물성을 실시예를 들어 설명하기로 한다.Hereinafter, the properties of a double-sided pressure-sensitive adhesive tape for fixing a touch screen panel and a double-sided pressure-sensitive adhesive tape for fixing a touch screen panel according to the present invention will be described.
<실시예 1>≪ Example 1 >
에틸 아크릴레이트 모노머 10 중량부, 부틸 아크릴레이트 모노머 10 중량부, 2-에틸헥실 아크릴레이트 모노머 60 중량부, 비닐 아크릴레이트 모노머 10 중량부, 2-하이드록시에틸 메타아크릴레이트 2 중량부, 하이드록시 프로필아크릴레이트 3 중량부, 아크릴 산 5 중량부, 중합 개시제로 AIBN(Azobis isobutyronitrile) 0.5 중량부를 4구 1리터 유리 반응기에 투입하여 중합하고, 상기 중합물의 고형분 함량이 40%가 되도록 유기용제인 에틸아세테이트를 혼합하여 희석하고 이소시아네이트 경화제 1 중량부를 혼합하여 코팅액 혼합물을 제조한 후에, 제조된 코팅액 혼합물을 50㎛ 두께의 폴리에틸렌테레프탈레이트 필름의 이형면에 70㎛의 두께로 코팅하고 건조하여 제1점착층을 제조하고, 제조된 제1점착층을 양면에 코로나가 처리되며, 폴리에틸렌테레프탈레이트 필름으로 이루어진 25㎛ 두께인 기재층의 일면과 합지시키고, 상기 코팅액 혼합물에 글라스버블(3M Microspheres, K20)을 0.5 중량부를 혼합하고 균일하게 분산하도록 충분히 교반하여 글라스버블이 함유된 코팅액 혼합물을 제조하고, 제조된 글라스버블 함유 코팅액을 상기 제1점착층을 제조하는 방법과 동일한 방법으로 상기 기재층의 타면에 80㎛의 두께로 제2점착층을 형성하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.10 parts by weight of ethyl acrylate monomer, 10 parts by weight of butyl acrylate monomer, 60 parts by weight of 2-ethylhexyl acrylate monomer, 10 parts by weight of vinyl acrylate monomer, 2 parts by weight of 2-hydroxyethyl methacrylate, 3 parts by weight of acrylate, 5 parts by weight of acrylic acid, and 0.5 part by weight of AIBN (Azobis isobutyronitrile) as a polymerization initiator were put into a four-necked one liter glass reactor and polymerized. To this, the organic solvent, ethyl acetate And 1 part by weight of an isocyanate curing agent were mixed to prepare a coating solution mixture. The prepared coating solution mixture was coated on the release surface of a 50 탆 thick polyethylene terephthalate film to a thickness of 70 탆 and dried to form a first adhesive layer The prepared first adhesive layer was corona-treated on both sides, and a polyethylene terephthalate film , And 0.5 parts by weight of a glass bubble (3M Microspheres, K20) was sufficiently mixed with the coating liquid mixture to prepare a coating liquid mixture containing glass bubbles, A second adhesive layer was formed on the other surface of the substrate layer to a thickness of 80 탆 in the same manner as in the above-mentioned method of producing the first adhesive layer to prepare a double-faced adhesive tape for fixing a touch screen panel.
<실시예 2>≪ Example 2 >
상기 실시예 1과 동일하게 진행하되, 부틸 아크릴레이트 모노머 30 중량부, 2-에틸헥실 아크릴레이트 모노머 40 중량부를 혼합하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.The procedure of Example 1 was followed except that 30 parts by weight of butyl acrylate monomer and 40 parts by weight of 2-ethylhexyl acrylate monomer were mixed to prepare a double-sided adhesive tape for fixing a touch screen panel.
<실시예 3>≪ Example 3 >
상기 실시예 1과 동일하게 진행하되, 부틸 아크릴레이트 모노머 40 중량부, 2-에틸헥실 아크릴레이트 모노머 30 중량부를 혼합하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.The procedure of Example 1 was repeated except that 40 parts by weight of butyl acrylate monomer and 30 parts by weight of 2-ethylhexyl acrylate monomer were mixed to prepare a double-sided adhesive tape for fixing a touch screen panel.
<실시예 4><Example 4>
상기 실시예 1과 동일하게 진행하되, 부틸 아크릴레이트 모노머 40 중량부, 2-에틸헥실 아크릴레이트 모노머 20 중량부를 혼합하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.The procedure of Example 1 was repeated except that 40 parts by weight of butyl acrylate monomer and 20 parts by weight of 2-ethylhexyl acrylate monomer were mixed to prepare a double-sided adhesive tape for fixing a touch screen panel.
<실시예 5>≪ Example 5 >
상기 실시예 1과 동일하게 진행하되, 2-하이드록시에틸 메타아크릴레이트 7 중량부를 혼합하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.The procedure of Example 1 was repeated except that 7 parts by weight of 2-hydroxyethylmethacrylate was mixed to prepare a double-sided pressure-sensitive adhesive tape for fixing a touch screen panel.
<실시예 6>≪ Example 6 >
상기 실시예 1과 동일하게 진행하되, 하이드록시 프로필아크릴레이트 8 중량부를 혼합하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.The procedure of Example 1 was followed except that 8 parts by weight of hydroxypropyl acrylate was mixed to prepare a double-sided adhesive tape for fixing a touch screen panel.
<비교예 1>≪ Comparative Example 1 &
상기 실시예 1과 동일하게 진행하되, 글라스버블(3M Microspheres, K20)을 1 중량부를 혼합하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.The procedure of Example 1 was followed except that 1 part by weight of glass bubbles (3M Microspheres, K20) was mixed to prepare a double-sided adhesive tape for fixing a touch screen panel.
<비교예 2>≪ Comparative Example 2 &
상기 실시예 1과 동일하게 진행하되, 글라스버블(3M Microspheres, K20)을 2 중량부를 혼합하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.The procedure of Example 1 was followed except that 2 parts by weight of glass bubbles (3M Microspheres, K20) were mixed to prepare a double-sided adhesive tape for fixing a touch screen panel.
<비교예 3>≪ Comparative Example 3 &
상기 실시예 1과 동일하게 진행하되, 글라스버블을 혼합하지 않고 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.A double-sided pressure-sensitive adhesive tape for fixing a touch screen panel was prepared in the same manner as in Example 1 except that glass bubbles were not mixed.
<비교예 4>≪ Comparative Example 4 &
상기 실시예 1과 동일하게 진행하되, 100㎛ 두께의 PE Foam을 기재층으로 하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.A double-faced pressure-sensitive adhesive tape for fixing a touch screen panel was prepared using a PE foam having a thickness of 100 탆 as a base layer.
<비교예 5>≪ Comparative Example 5 &
상기 실시예 1과 동일하게 진행하되, 200㎛ 두께의 PE Foam을 기재층으로 하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.A double-faced pressure-sensitive adhesive tape for fixing a touch screen panel was prepared using the PE foams having a thickness of 200 μm as a base layer.
<비교예 6>≪ Comparative Example 6 >
상기 실시예 1과 동일하게 진행하되, 하이드록시기 모노머 대신 메타아크릴산 2 중량부 및 말레산 무수물 3 중량부를 사용하여 터치스크린 패널 고정용 양면 점착 테이프를 제조하였다.The procedure of Example 1 was repeated except that 2 parts by weight of methacrylic acid and 3 parts by weight of maleic anhydride were used instead of the hydroxyl group monomer to prepare a double-sided adhesive tape for fixing a touch screen panel.
상기 실시예 1 내지 6 및 비교예 1 내지 6을 통해 제조된 터치스크린 패널 고정용 양면 점착 테이프의 박리강도를 측정하여 아래 표 1에 나타내었다.The peel strengths of the double-sided adhesive tape for fixing the touch screen panel manufactured through Examples 1 to 6 and Comparative Examples 1 to 6 were measured and shown in Table 1 below.
{단, 박리강도는 양면 점착 테이프의 일면에 25㎛의 PET를 합지하여 폭 25mm 길이 200mm인 측정시편을 제작하고, SUS(steel use stainless), PC(poly carbonate) 및 Glass에 각각 5개의 시편을 2kg의 핸드롤러(hand roller)로 왕복 2회 압착하여 부착하고, 상온에서 30분 동안 방치한 후 인장시험기를 이용하여 박리강도를 측정하였는데, 이때, 인장속도 300mm/min 으로 180o 의 조건에서 측정하였다.}(However, the peel strength was obtained by forming a test specimen having a width of 25 mm and a length of 200 mm by laminating 25 μm of PET on one side of a double-sided adhesive tape, and 5 specimens for stainless steel, PC (polycarbonate) The peel strength was measured by using a tensile tester after standing at room temperature for 30 minutes. The peel strength was measured at 180 ° C at a tensile speed of 300 mm / min. .
<표 1><Table 1>
위에 표 1에 나타낸 것처럼, 비교예 1 내지 2의 경우는 과량의 글라스버블이 함유되어 점착층과 기재층의 밀착성이 저해되어 박리강도가 낮게 나타났으며, PE Foam 기재를 사용한 비교예 4 내지 5 보다는 PET 기재를 사용한 실시예의 점착력이 더 우수하게 나타났고, 아크릴 모노머 조성에 따른 점착력은 큰 차이를 보이지 않았다.As shown in Table 1 above, in Comparative Examples 1 and 2, an excess amount of glass bubbles was contained and the adhesion between the adhesive layer and the base layer was impaired and the peeling strength was low. In Comparative Examples 4 to 5 The adhesive force of the PET substrate was better than that of the PET substrate, and the adhesive force of the acrylic monomer composition did not show any significant difference.
또한, 상기 실시예 1 내지 6 및 상기 비교예 1 내지 6을 통해 제조된 터치스크린 패널 고정용 양면 점착 테이프의 방수성, 내구 신뢰성 및 내충격성을 측정하여 아래 표 2에 나타내었다.The waterproofness, durability and impact resistance of the double-sided adhesive tape for fixing the touch screen panel manufactured through Examples 1 to 6 and Comparative Examples 1 to 6 were measured and shown in Table 2 below.
{단, 방수성은 제조된 양면 점착 테이프를 액자틀 모양으로 가로 40mm×세로 60mm×폭 1mm로 타발하여 가로 50mm×세로 70mm×폭 5mm의 아크릴판 일면에 부착하고, 타면에는 아크릴 판을 덮어 아크릴 판 사이에 양면 점착테이프가 위치하도록 시편을 제작하고, 이후, 깊이가 1m인 수조에 30분간 침지한 후에 외관을 관찰하여 시험편 내부의 침수여부를 판단하였다.(The waterproof property was evaluated by sticking the produced double-sided adhesive tape to a side of an acrylic plate of 50 mm in width x 70 mm in width x 5 mm in width with a width of 40 mm x 60 mm x width of 1 mm in the form of a frame and covering the acrylic plate on the other side, , And then immersed in a water tank having a depth of 1 m for 30 minutes. Then, the appearance of the specimen was observed to determine whether the specimen was immersed in water.
또한, 내구 신뢰성(cleavage)은 ASTM D3433에 따라 PC판(가로 50mm×세로 100mm×두께 5mm)과 L형 SUS판(가로 30mm×세로 30mm×두께 1mm)을 준비하고, 양면 점착 테이프를 가로 25mm×세로 25mm로 타발하여 만든 시편을 PC판과 L형 SUS판 사이에 부착하고, 85℃의 오븐에 넣고 250g 추를 걸고 시편이 떨어지는 시간을 확인하여 측정하였다.The endurance reliability was evaluated by preparing a PC plate (50 mm x 100 mm x 5 mm thick) and an L-type SUS plate (30 mm x 30 mm x 1 mm thick) in accordance with ASTM D3433, A specimen made by punching with a length of 25 mm was attached between a PC plate and an L-shaped SUS plate, placed in an oven at 85 ° C, and a 250 g weight was placed thereon.
또한, 내충격성은 Glass 시편(가로 25mm×세로 25mm×높이 5mm), PC판(가로 50mm×세로 25mm×높이 2mm×홀 10Ø)을 준비하였다. 이후, 양면 점착테이프를 3mm 크기로 잘라 Glass 시편 양끝면에 붙이고, 남는 테이프를 시편사이즈에 맞춰 자른 후에 PC판의 중앙에 맞춰 Glass를 부착하고, 3kg의 하중으로 1분 압착 후 24시간 동안 Aging 하고, 150g 추를 50mm부터 400mm까지 순차적으로 높이가 증가된 상태에서 낙하시켜 시편이 박리되는 높이를 측정하여 나타내었다.}A glass plate (25 mm wide × 25 mm high × 5 mm high) and a PC plate (width 50 mm × length 25 mm × height 2 mm ×
<표 2><Table 2>
위에 표 2를 보면 과량의 글라스버블이 함유된 비교예 1 내지 2를 통해 제조된 양면 점착 테이프는 침수되는 현상이 발생했으며 Foam 기재를 사용한 비교예 4 내지 5는 내구 신뢰성과 내충격성은 우수하나 침수되는 현상이 발생하여 방수성능이 낮은 것을 알 수 있다.As shown in Table 2 above, the double-faced pressure-sensitive adhesive tapes prepared in Comparative Examples 1 and 2 containing excessive amounts of glass bubbles were inundated, and Comparative Examples 4 to 5 using the foam substrate showed excellent endurance reliability and impact resistance, And the waterproof performance is low.
반면, 본원발명의 실시예 1 내지 6을 통해 제조된 양면 점착 테이프는 방수성, 내구 신뢰성 및 내충격성에서 우수한 물성을 나타내는 것을 알 수 있다.On the other hand, the double-sided pressure-sensitive adhesive tapes produced through Examples 1 to 6 of the present invention show excellent physical properties in terms of water resistance, endurance reliability and impact resistance.
따라서, 본 발명에 따른 양면 접착 테이프는 터치스크린의 패널을 고정하는데 유용한 효과를 나타낸다.Therefore, the double-sided adhesive tape according to the present invention has an advantageous effect for fixing the panel of the touch screen.
10 ; 기재층
20 ; 제1점착층
30 ; 제2점착층10; The substrate layer
20; The first adhesive layer
30; The second adhesive layer
Claims (7)
상기 기재층의 일면에 형성되는 제1점착층; 및
상기 기재층의 타면에 형성되며 비드가 함유되는 제2점착층;으로 이루어지는 것을 특징으로 하는 터치스크린 패널 고정용 양면 점착 테이프.
A base layer;
A first adhesive layer formed on one surface of the substrate layer; And
And a second adhesive layer formed on the other surface of the substrate layer and containing beads.
상기 기재층은 두께가 1.4 내지 50㎛이며, 양면이 코로나 방전처리된 합성수지로 이루어지는 것을 특징으로 하는 터치스크린 패널 고정용 양면 점착 테이프.
The method according to claim 1,
Wherein the base layer is made of synthetic resin having a thickness of 1.4 to 50 탆 and corona discharge treated on both sides thereof.
상기 제1점착층은 아크릴계 수지 100 중량부, 용제 10 내지 50 중량부 및 경화제 0.1 내지 10 중량부로 이루어지는 것을 특징으로 하는 터치스크린 패널 고정용 양면 점착 테이프.
The method according to claim 1,
Wherein the first adhesive layer comprises 100 parts by weight of acrylic resin, 10 to 50 parts by weight of a solvent, and 0.1 to 10 parts by weight of a curing agent.
상기 제2점착층은 비드가 함유된 아크릴계 수지 100 중량부, 용제 10 내지 50 중량부 및 경화제 0.1 내지 50 중량부로 이루어지는 것을 특징으로 하는 터치스크린 패널 고정용 양면 점착 테이프.
The method according to claim 1,
Wherein the second adhesive layer comprises 100 parts by weight of an acrylic resin containing beads, 10 to 50 parts by weight of a solvent, and 0.1 to 50 parts by weight of a curing agent.
상기 아크릴계 수지는 부틸아크릴레이트, 부틸메타크릴레이트, 헥실아크릴레이트, 헥실메타크릴레이트, n-옥틸아크릴레이트, n-옥틸메타크릴레이트, 이소옥틸아크릴레이트, 이소옥틸메타크릴레이트, 2-에틸헥실아크릴레이트, 2-에틸헥실메타크릴레이트, 이소노닐아크릴레이트 및 이소노닐메타크릴레이트로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것을 특징으로 하는 터치스크린 패널 고정용 양면 점착 테이프.
The method according to claim 3 or 4,
The acrylic resin may be at least one selected from the group consisting of butyl acrylate, butyl methacrylate, hexyl acrylate, hexyl methacrylate, n-octyl acrylate, n-octyl methacrylate, isooctyl acrylate, isooctyl methacrylate, Acrylate, 2-ethylhexyl methacrylate, isononyl acrylate, and isononyl methacrylate. 2. The double-sided pressure-sensitive adhesive tape for fixing a touch screen panel according to claim 1,
상기 아크릴계 수지는 메타아크릴산, 2-메타아크릴옥시 아세트산, 3-메타아크릴옥시 프로필산, 4-메타아크릴옥시 부틸산, 푸마르산, 말레산 및 말레산 무수물로 이루어진 그룹에서 선택된 하나와,
2-하이드록시에틸 메타아크릴레이트, 2-하이드록시프로필 메타아크릴레이트, 4-하이드록시부틸 메타아크릴레이트, 6-하이드록시헥실 메타아크릴레이트, 8-하이드록시옥틸 메타아크릴레이트 및 2-하이드록시에틸렌 글리콜 메타아크릴레이트로 이루어진 그룹에서 선택된 하나를 공중합하여 제조되는 것을 특징으로 하는 터치스크린 패널 고정용 양면 점착 테이프.
The method according to claim 3 or 4,
Wherein the acrylic resin is one selected from the group consisting of methacrylic acid, 2-methacryloxy oxyacetic acid, 3-methacryloxypropionic acid, 4-methacryloxybutyric acid, fumaric acid, maleic acid and maleic anhydride,
Hydroxypropylmethacrylate, 2-hydroxyethylmethacrylate, 2-hydroxypropylmethacrylate, 4-hydroxybutylmethacrylate, 6-hydroxyhexylmethacrylate, 8-hydroxyoctylmethacrylate, and 2-hydroxyethylene Wherein the adhesive layer is formed by copolymerizing one selected from the group consisting of acrylic acid, methacrylic acid and glycol methacrylate.
상기 비드는 입자크기가 5 내지 200㎛이며, 열팽창성 수지, 글라스 마크로벌룬, 글라스 버블 및 실리카로 이루어진 그룹에서 선택된 하나로 이루어지는 것을 특징으로 하는 터치스크린 패널 고정용 양면 점착 테이프.The method according to claim 1,
Wherein the beads have a particle size of 5 to 200 占 퐉 and are made of one selected from the group consisting of thermally expandable resin, glass macrobullet, glass bubble, and silica.