KR20160020680A - Retadation film and preparing method for retadation film - Google Patents
Retadation film and preparing method for retadation film Download PDFInfo
- Publication number
- KR20160020680A KR20160020680A KR1020140105646A KR20140105646A KR20160020680A KR 20160020680 A KR20160020680 A KR 20160020680A KR 1020140105646 A KR1020140105646 A KR 1020140105646A KR 20140105646 A KR20140105646 A KR 20140105646A KR 20160020680 A KR20160020680 A KR 20160020680A
- Authority
- KR
- South Korea
- Prior art keywords
- film
- retardation
- retardation film
- coating layer
- group
- Prior art date
Abstract
Description
본 발명은 위상차 필름 및 그 제조 방법에 관한 것으로, 보다 구체적으로는 IPS 모드 액정표시장치에 위상차 필름으로 적용이 가능한 위상차 필름 및 그 제조 방법에 관한 것이다.
The present invention relates to a retardation film and a manufacturing method thereof, and more specifically, to a retardation film that can be applied to an IPS mode liquid crystal display device as a retardation film and a method of manufacturing the retardation film.
액정 디스플레이는 음극선관 디스플레이에 비해 소비 전력이 낮고, 부피가 작고, 가벼워 휴대가 용이하기 때문에 광학 디스플레이 소자로서 보급이 확산되고 있다. 일반적으로 액정 디스플레이는 액정 셀의 양측에 편광판을 설치한 기본 구성을 가지며, 구동회로의 전계 인가 여부에 따라 액정 셀의 배향이 변하게 되고, 그에 따라 편광판을 통해 나온 투과광의 특성이 달라지게 됨으로써 빛의 가시화가 이루어진다. 이 때 입사광의 입사 각도에 따라 빛의 경로와 복굴절성이 변화하게 되는데, 이는 액정이 두 개의 상이한 굴절률을 가지는 이방성 물질이기 때문이다.
The liquid crystal display is spreading as an optical display device because it has lower power consumption, smaller volume, lighter weight and easier to carry than a cathode ray tube display. In general, a liquid crystal display has a basic structure in which a polarizing plate is provided on both sides of a liquid crystal cell, and the orientation of the liquid crystal cell is changed according to whether an electric field of the driving circuit is applied or not and the characteristics of light transmitted through the polarizing plate are changed, Visualization is done. At this time, the path of light and the birefringence change depending on the incident angle of the incident light because the liquid crystal is an anisotropic material having two different refractive indices.
이와 같은 특성으로 인해, 액정 디스플레이는 시야각(viewing angle)에 따라 상이 얼마나 뚜렷하게 보이는지를 가늠하는 척도인 콘트라스트 비(contrast ratio)가 달라지고 계조 반전(gray scale inversion) 현상이 발생하여 시인성이 떨어진다는 단점을 지닌다. 상기와 같은 단점을 극복하기 위하여 액정 디스플레이 장치에는 액정 셀에서 발생하는 광학 위상차를 발현시켜 주는 광학 위상차 필름(compensation film)이 사용되고 있다.
Due to such characteristics, the liquid crystal display has a disadvantage that the contrast ratio, which is a measure of how clearly the image looks depending on the viewing angle, is changed and a gray scale inversion phenomenon occurs, . In order to overcome such disadvantages, an optical compensation film for developing an optical retardation generated in a liquid crystal cell is used for a liquid crystal display device.
한편, 액정 디스플레이에 있어서 선명한 화질 및 넓은 광시야각을 확보하기 위해 다양한 액정 모드가 개발되고 있으며, 대표적으로는 Double Domain TN(Twisted Nematic), ASM(axially sy㎜etric aligned microcell), OCB(optically compensated blend), VA(vertical alig㎚ent), MVA(multidomain VA), SE(surrounding electrode), PVA(patterned VA), IPS(in-plane switching), FFS(fringe-field switching) 모드 등을 들 수 있다. 이들 각각의 모드는 고유한 액정 배열을 하고 있으며, 고유한 광학 이방성을 갖고 있다.
Various liquid crystal modes have been developed to secure a clear image quality and a wide viewing angle in a liquid crystal display. Typical examples thereof include a double domain TN (twisted nematic), an axially symmetric aligned microcell (ASM), an optically compensated blend ), VA (vertical alignmnt), MVA (multidomain VA), SE (surrounding electrode), PVA (patterned VA), IPS (in-plane switching) and FFS (fringe-field switching) modes. Each of these modes has a unique liquid crystal arrangement and has inherent optical anisotropy.
따라서, 이들 액정 모드의 광학 이방성으로 인한 위상차를 발현하기 위해서는 각각의 모드에 대응하는 광학 이방성의 위상차 필름이 요구된다. 특히 IPS 모드의 경우에는 양의 유전률 이방성을 가지는 액정이 수평 배향되어 있기 때문에 비구동 상태에서 경사각에서의 광학 이방성이 타 모드 대비 크지 않아 등방성 보호필름 사용만으로도 우수한 광시야각을 확보할 수 있다는 장점이 있다. 하지만 이 경우 고경사각에서 편광자의 흡수축에 대한 보상은 전혀 이루어지지 않아 여전히 시야각에 따른 콘트라스트 저하, 색상 변조 등이 일어날 수 있으며, 따라서 완벽한 광시야각 확보를 위해서는 IPS 모드 액정디스플레이 또한 적절한 위상차 필름을 사용해야 한다.
Therefore, in order to manifest the phase difference due to the optical anisotropy of these liquid crystal modes, an optically anisotropic phase difference film corresponding to each mode is required. Especially, in the case of the IPS mode, since the liquid crystal having a positive dielectric anisotropy is horizontally aligned, the optical anisotropy at the oblique angle in the non-driven state is not greater than that of the other modes, so that an excellent viewing angle can be obtained by using the isotropic protective film alone . In this case, however, compensation for the absorption axis of the polarizer at the high inclination angle is not performed at all, so that the contrast may be deteriorated due to the viewing angle and color modulation may occur. Therefore, in order to secure a perfect viewing angle, the IPS mode liquid crystal display should also use an appropriate retardation film do.
IPS 모드용 보상을 위해서는 nx>nz>ny 조건을 만족하는 위상차 보상층이 필요하다. 여기서 nx, ny, nz는 필름 각 방향으로의 굴절률을 나타내며, x, y, z방향은 필름 면에서 굴절률이 가장 큰 방향, 면에서 굴절률이 가장 작은 방향, 두께 방향을 각각 나타낸다. 그런데, nx>nz>ny 조건을 만족하는 위상차 보상층은 일반적으로 일축/이축 연신 필름 단독으로는 구현하기 어렵다고 알려져 있다. 따라서, 상기 굴절율 조건을 만족하는 위상차 보상층을 형성하기 위해, 종래에 수축 필름을 사용하여 연신시 과도한 폭 수축을 유도하는 방법, 연신된 필름에 강한 전기장을 가하는 방법 등 3차원적으로 굴절률을 제어하는 여러 방안들이 제안되었으나, 현재까지 여러 가지 기술적/설비적 문제들로 인해 광폭의 필름을 연속적으로 생산하는 데는 한계가 있다.
In order to compensate for the IPS mode, a retardation compensation layer satisfying the condition of n x > n z > n y is required. Here, n x , n y , and n z are refractive indices in the directions of the film, and x, y, and z indicate the direction with the greatest refractive index on the film surface, the direction with the smallest refractive index on the surface, and the thickness direction, respectively. However, it is generally known that the retardation compensation layer satisfying the condition of n x > n z > n y is difficult to realize by a uniaxial / biaxially stretched film alone. Therefore, in order to form the retardation compensation layer satisfying the refractive index condition, conventionally, a method of inducing excessive width shrinkage during stretching using a shrink film, a method of applying a strong electric field to the stretched film, However, to date, there have been limitations in continuously producing wide-width films due to various technical / equipment problems.
따라서, IPS 모드용 위상차 필름은 두 층 이상의 다층 필름으로 구성하는 구조가 현실적으로 제시되고 있다. 예를 들면, 이러한 다층 복합 필름을 구성하는 방법으로 접착제 또는 점착제를 사용하여 적층(lamination)하는 방법, 별도의 연신 과정을 통해 연신 필름을 제조한 후 액정을 코팅하는 방법 등이 제안된바 있다. 그러나, 접착제 또는 점착제를 사용하여 적층(lamination)하는 방법의 경우 각층의 필름을 각각 제조해야 하고, 그 후 접착, 건조 등 여러 공정을 거쳐야 하기 때문에 제조단가가 높으며, 제조되는 위상차 필름의 두께가 두꺼운바, 이를 포함하는 디스플레이 장치의 박형 경량화 추세에 부응하지 못하는 단점이 있으며, 나아가 접착제 또는 점착제 사용에 따른 얼룩, 쿠닉, 이물 혼입 등의 불량 발생률이 높은 단점이 있다. 또한, 액정을 코팅하는 방법의 경우 필름 연신 후 배향막을 코팅한 후 액정 코팅의 공정이 필요하기 때문에 공정이 복잡하고 공정 단가가 높아지는 단점이 있다.
Therefore, the structure in which the retardation film for IPS mode is constituted by a multilayer film of two or more layers is presented realistically. For example, a method of forming such a multilayer composite film by lamination using an adhesive or a pressure-sensitive adhesive, a method of coating a liquid crystal after preparing a stretched film through another stretching process, and the like have been proposed. However, in the case of the lamination method using an adhesive or a pressure-sensitive adhesive, it is necessary to manufacture each film of each layer, and then various steps such as adhesion and drying have to be performed, so that the production cost is high, There is a disadvantage in that it can not meet the trend of thinner and lighter display devices including bar and the like, and further, there is a high incidence of defects such as smearing, kicking, foreign matter incorporation and the like due to use of adhesive or pressure- Further, in the case of a method of coating a liquid crystal, after the film is stretched, a liquid crystal coating process is required after coating the alignment film, which complicates the process and increases the process cost.
한편, 최근에는 기재 필름을 제조하고, 그 위에 직접 위상차 발현 물질을 코팅하여 다층 복합 필름을 구성하는 방법이 제안된바 있다. 이때, 기재 필름으로는 아크릴계 필름, 스티렌계 필름 등이 사용될 수 있으며, 위상차 발현 물질로는 배향성이 높아 박막으로도 높은 위상차를 구현할 수 있는 폴리이미드 수지 등이 사용될 수 있는데, 폴리이미드 수지 등은 일반적으로 투명성이 떨어져 광학 용도로 사용하기에 부적합하다는 단점이 있으며, 또한 접착제와의 접착력이 매우 나빠, 편광판이나 액정 패널 등에 부착되기 어렵다는 문제점이 있다.
On the other hand, recently, a method has been proposed in which a base film is prepared and a phase difference developing material is directly coated thereon to constitute a multilayer composite film. The base film may be an acrylic film or a styrenic film. The phase difference developing material may be a polyimide resin having a high orientation property and capable of realizing a high retardation even in a thin film. Which is disadvantageous in that it is not suitable for use in optical applications because of its low transparency and also has a problem that it is difficult to adhere to a polarizing plate or a liquid crystal panel due to a poor adhesive force with an adhesive.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로, IPS 모드 액정표시장치에 적용시 시야각 개선 효과가 매우 우수하고, 박형으로 제조가 가능하며, 편광판용 접착제와의 우수한 접착력을 가지고, 간소한 공정으로 제조가 가능한 위상차 필름 및 그 제조방법을 제공하고자 한다.
SUMMARY OF THE INVENTION The present invention has been made to solve the above problems and it is an object of the present invention to provide an IPS mode liquid crystal display device which is excellent in the viewing angle improving effect and can be manufactured in a thin shape and has excellent adhesion with a polarizer adhesive, And a method for producing the same.
한편, 본 발명의 과제는 상술한 내용에 한정하지 않는다. 본 발명의 과제는 본 명세서의 내용 전반으로부터 이해될 수 있을 것이며, 본 발명이 속하는 기술분야에서 통상의 지식을 가지는 자라면 본 발명의 부가적인 과제를 이해하는데 아무런 어려움이 없을 것이다.
On the other hand, the object of the present invention is not limited to the above description. It will be understood by those of ordinary skill in the art that there is no difficulty in understanding the additional problems of the present invention.
일 측면에서, 본 발명은 부의 위상차 물질을 포함하는 기재 필름; 및 상기 기재 필름의 적어도 일면에 형성되며, 하기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체를 포함하는 코팅층을 포함하는 위상차 필름을 제공한다.In one aspect, the present invention provides a film comprising a substrate film comprising a negative retardation material; And a coating layer formed on at least one surface of the base film and including a polyimide copolymer containing a repeating unit represented by the following formula (1).
[화학식 1][Chemical Formula 1]
상기 [화학식 1]에서, X1은 에스테르기 또는 에테르기를 포함하는 지환족 또는 방향족 산 이무수물로부터 유도된 4가 유기기이며; X2는 X1과 상이한 산 이무수물로부터 유도된 4가 유기기이고; Q1 및 Q2는 각각 독립적으로 디아민으로부터 유도된 2가 유기기이며; 상기 a, b, c 및 d는 각 반복단위의 몰비를 나타내는 것으로, a+b+c+d =1이고, 0.1 ≤ a+b ≤ 1 이고, 0 ≤ c+d ≤ 0.9 임.
Wherein X 1 is a divalent organic group derived from an alicyclic or aromatic acid dianhydride containing an ester group or an ether group; X 2 is a divalent organic group derived from an acid dianhydride different from X 1 ; Q 1 and Q 2 are each independently a divalent organic group derived from a diamine; Wherein a, b, c and d represent the molar ratio of the respective repeating units, a + b + c + d = 1, 0.1? A + b? 1 and 0? C + d? 0.9.
한편, 상기 위상차 필름은 상기 코팅층을 편광판용 접착제를 매개로 폴리비닐알코올계 편광자에 부착한 후 측정한 접착력이 1N/2cm 이상인 것이 바람직하다.
On the other hand, it is preferable that the retardation film has an adhesion of at least 1 N / 2 cm measured after attaching the coating layer to a polyvinyl alcohol polarizer via an adhesive for a polarizer.
또한, 상기 위상차 필름은 하기 식 (1) 및 (2)를 만족하는 것이 바람직하다.It is also preferable that the retardation film satisfies the following formulas (1) and (2).
식 (1): 50nm ≤ Rin , total ≤ 300nm(1): 50 nm? R in , total ? 300 nm
식 (2): 10nm ≤ Rth , total ≤ 300nm(2): 10 nm? R th , total ? 300 nm
상기 식 (1) 및 (2)에서, Rin , total은 파장 550nm에서 측정한 위상차 필름 전체의 면 방향 위상차값이고; Rth , total은 파장 550nm에서 측정한 위상차 필름 전체의 두께 방향 위상차값임.
In the above formulas (1) and (2), R in , total is the retardation value of the entire retardation film measured at a wavelength of 550 nm; R th , total is the retardation value in the thickness direction of the entire retardation film measured at a wavelength of 550 nm.
또한, 상기 위상차 필름은 하기 식 (3)으로 표시되는 Nz 값이 1 이하인 것이 바람직하다.The retardation film preferably has an Nz value represented by the following formula (3) of 1 or less.
식 (3): Nz = Rth , total/Rin , total Equation (3): Nz = R th , total / R in, total
상기 식 (3)에서, Rin , total은 위상차 필름 전체의 면 방향 위상차값이고; Rth , total은 위상차 필름 전체의 두께 방향 위상차값이며; 이때, 상기 Rin , total 및 Rth , total은 모두 파장 550nm에서 측정한 위상차값임.
In the above formula (3), R in , total is the retardation value in the plane direction of the entire retardation film; R th , total is the retardation value in the thickness direction of the entire retardation film; At this time, R in , total and R th , total are retardation values measured at a wavelength of 550 nm.
또한, 상기 기재 필름은 하기 식 (4) 및 (5)을 만족하는 것이 바람직하다.It is preferable that the base film satisfies the following formulas (4) and (5).
식 (4): 0nm ≤ Rin ,a ≤ 250nm(4): 0 nm? R in , a ? 250 nm
식 (5): 10nm ≤ Rth ,a ≤ 300nm(5): 10 nm? R th , a ? 300 nm
상기 식 (4) 및 (5)에서, Rin ,a은 파장 550nm에서 측정한 기재 필름의 면 방향 위상차값이고; Rth ,a은 파장 550nm에서 측정한 기재 필름의 두께 방향 위상차값임.
In the formulas (4) and (5), R in , a is the retardation value in the plane direction of the base film measured at a wavelength of 550 nm; Rth , a is the retardation value in the thickness direction of the base film measured at a wavelength of 550 nm.
또한, 상기 코팅층은 하기 식 (6) 및 (7)을 만족하는 것이 바람직하다.It is preferable that the coating layer satisfies the following formulas (6) and (7).
식 (6): 50nm ≤ Rin ,b ≤ 300nm(6): 50 nm? R in , b ? 300 nm
식 (7): -290nm ≤ Rth ,b ≤ 0nm(7): -290 nm? R th , b ? 0 nm
상기 식 (6) 및 (7)에서, Rin ,b은 파장 550nm에서 측정한 코팅층의 면 방향 위상차값이고; Rth ,b은 파장 550nm에서 측정한 코팅층의 두께 방향 위상차값임.
In the formulas (6) and (7), R in , b is the retardation value in the plane direction of the coating layer measured at a wavelength of 550 nm; Rth , b is the thickness direction retardation value of the coating layer measured at a wavelength of 550 nm.
한편, 상기 기재 필름은 길이 방향(MD) 및 폭 방향(TD)으로 이축 연신된 것이고, 상기 코팅층은 폭 방향(TD)으로 일축 연신된 것이 바람직하다.
On the other hand, it is preferable that the base film is biaxially stretched in the longitudinal direction (MD) and the width direction (TD), and the coating layer is uniaxially stretched in the width direction (TD).
한편, 상기 X1은 하기 [화학식 2] 또는 [화학식 3]로 표시되는 산 이무수물로부터 유도된 4가 유기기인 것이 바람직하다.It is preferable that X 1 is a tetravalent organic group derived from an acid dianhydride represented by the following formula (2) or (3).
[화학식 2] (2)
상기 [화학식 2]에서, A1은 탄소수 1~10의 지방족 고리 또는 방향족 고리이며; B1은 단일 결합, 치환 또는 비치환된 지방족 사슬, 치환 또는 비치환된 지방족 고리, 치환 또는 비치환된 방향족 고리, 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 고리, 또는 이들의 조합임.
In the above formula (2), A 1 is an aliphatic ring or aromatic ring having 1 to 10 carbon atoms; B 1 is a single bond, a substituted or unsubstituted aliphatic chain, a substituted or unsubstituted aliphatic ring, a substituted or unsubstituted aromatic ring, two or more aromatic rings connected through a direct or crosslinked structure, or a combination thereof.
[화학식 3](3)
상기 [화학식 3]에서, A2는 탄소수 1~10의 지방족 고리 또는 방향족 고리이며; B2는 단일 결합, 치환 또는 비치환된 지방족 사슬, 치환 또는 비치환된 지방족 고리, 치환 또는 비치환된 방향족 고리; 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 고리; 또는 이들의 조합임.
In Formula 3, A 2 is an aliphatic ring or aromatic ring having 1 to 10 carbon atoms; B 2 is a single bond, a substituted or unsubstituted aliphatic chain, a substituted or unsubstituted aliphatic ring, a substituted or unsubstituted aromatic ring; Two or more aromatic rings linked directly or via a bridging structure; Or a combination thereof.
한편, 상기 X1은 하기 [화학식 4]에 표시된 화합물들로 이루어진 군으로부터 선택된 산 이무수물로부터 유도된 4가 유기기인 것이 보다 바람직하다.It is more preferable that X 1 is a tetravalent organic group derived from an acid dianhydride selected from the group consisting of the compounds represented by Formula 4 below.
[화학식 4][Chemical Formula 4]
상기 [화학식 4]에서, B1 및 B2는 각각 독립적으로 단일 결합; 치환 또는 비치환된 지방족 사슬; 치환 또는 비치환된 지방족 고리; 치환 또는 비치환된 방향족 고리; 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 고리; 또는 이들의 조합임.
In Formula 4, B 1 and B 2 each independently represent a single bond; A substituted or unsubstituted aliphatic chain; A substituted or unsubstituted aliphatic ring; A substituted or unsubstituted aromatic ring; Two or more aromatic rings linked directly or via a bridging structure; Or a combination thereof.
한편, 상기 Q1 또는 Q2는 하기 [화학식 5]에 표시되는 화합물들로 이루어진 군으로부터 선택된 디아민으로부터 유도된 2가 유기기인 것이 바람직하다.Meanwhile, it is preferable that Q 1 or Q 2 is a divalent organic group derived from a diamine selected from the group consisting of compounds represented by the following formula (5).
[화학식 5][Chemical Formula 5]
상기 [화학식 5]에서, 상기 R1 내지 R7은 각각 독립적으로, 치환 또는 비치환된 지방족 사슬, 치환 또는 비치환된 지방족 고리, 치환 또는 비치환된 방향족 고리, 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 고리, 또는 이들의 조합이며; R8 내지 R11은 각각 독립적으로, 탄소수 1 내지 10 알킬기, 탄소수 1 내지 10의 할로알킬기 또는 히드록시기이며; q는 1~ 8인 정수임.
In Formula 5, R 1 to R 7 each independently represents a substituted or unsubstituted aliphatic chain, a substituted or unsubstituted aliphatic ring, a substituted or unsubstituted aromatic ring, a straight or branched An aromatic ring, or a combination thereof; R 8 to R 11 are each independently a C 1-10 alkyl group, a C 1-10 haloalkyl group or a hydroxy group; q is an integer of 1 to 8;
한편, 상기 부의 위상차 물질은 아크릴계 수지, 스티렌계 수지, 아크릴계 수지와 스티렌계 수지를 포함하는 블렌딩 수지, 폴리비닐카바졸 및 폴리비닐나프탈렌으로 이루어진 군으로부터 선택된 1 이상인 것이 바람직하다.
The negative retardation material is preferably at least one selected from the group consisting of an acrylic resin, a styrene resin, a blending resin including an acrylic resin and a styrene resin, polyvinyl carbazole, and polyvinyl naphthalene.
한편, 상기 위상차 필름의 전체 두께는 80㎛ 이하인 것이 바람직하다.
On the other hand, the total thickness of the retardation film is preferably 80 탆 or less.
한편, 본 발명은 상기 위상차 필름을 포함하는 편광판 및 액정표시장치를 제공한다.
Meanwhile, the present invention provides a polarizing plate and a liquid crystal display including the retardation film.
다른 측면에서, 본 발명은 부의 위상차 물질을 포함하는 기재 필름을 제조하는 단계; 및 상기 기재 필름의 적어도 일면에 하기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체를 포함하는 코팅층을 형성하는 단계를 포함하는 위상차 필름의 제조 방법을 제공한다.In another aspect, the present invention provides a method of manufacturing a light emitting device, comprising: preparing a substrate film comprising a negative retardation material; And forming a coating layer comprising a polyimide copolymer containing at least one repeating unit represented by the following formula (1) on at least one side of the base film.
[화학식 1][Chemical Formula 1]
상기 [화학식 1]에서, X1은 에스테르기 또는 에테르기를 포함하는 지환족 또는 방향족 산 이무수물로부터 유도된 4가 유기기이며; X2는 X1과 상이한 산 이무수물로부터 유도된 4가 유기기이고; Q1 및 Q2는 각각 독립적으로 디아민으로부터 유도된 2가 유기기이며; 상기 a, b, c 및 d는 각 반복단위의 몰비를 나타내는 것으로, a+b+c+d =1이고, 0.1 ≤ a+b ≤ 1 이고, 0 ≤ c+d ≤ 0.9 임.
Wherein X 1 is a divalent organic group derived from an alicyclic or aromatic acid dianhydride containing an ester group or an ether group; X 2 is a divalent organic group derived from an acid dianhydride different from X 1 ; Q 1 and Q 2 are each independently a divalent organic group derived from a diamine; Wherein a, b, c and d represent the molar ratio of the respective repeating units, a + b + c + d = 1, 0.1? A + b? 1 and 0? C + d? 0.9.
보다 구체적으로, 본 발명의 위상차 필름의 제조 방법은, 부의 위상차 필름을 포함하는 미연신 기재 필름을 준비하는 단계; 상기 미연신 기재 필름을 연신하는 단계; 상기 연신 처리된 기재 필름의 적어도 일면에 상기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체를 포함하는 미연신 코팅층을 형성하는 단계; 및 상기 미연신 코팅층이 형성된 기재 필름을 연신하는 단계를 포함하는 것이 바람직하다.
More specifically, the method for producing a retardation film of the present invention comprises: preparing an unstretched base film comprising a negative retardation film; Stretching the unstretched base film; Forming an unstretched coating layer comprising a polyimide copolymer containing at least one repeating unit represented by the formula (1) on at least one surface of the stretched substrate film; And stretching the base film on which the non-stretched coating layer is formed.
이때, 상기 미연신 기재 필름을 연신하는 단계는 길이 방향(MD)으로의 일축 연신이고, 상기 미연신 코팅층이 형성된 기재 필름을 연신하는 단계는 폭 방향(TD)으로의 일축 연신인 것이 보다 바람직하다.
At this time, the step of stretching the unstretched base film is uniaxial stretching in the longitudinal direction (MD), and the step of stretching the base film in which the unoriented coating layer is formed is more preferably uniaxially stretched in the transverse direction (TD) .
덧붙여, 상기한 과제의 해결수단은, 본 발명의 특징을 모두 열거한 것은 아니다. 본 발명의 다양한 특징과 그에 따른 장점과 효과는 아래의 구체적인 실시형태를 참조하여 보다 상세하게 이해될 수 있을 것이다.
In addition, the solution of the above-mentioned problems does not list all the features of the present invention. The various features of the present invention and the advantages and effects thereof will be more fully understood by reference to the following specific embodiments.
본 발명에 따른 위상차 필름은 IPS 모드용 위상차 필름으로 이용하기에 적합한 위상차 특성을 가지며, 박형으로 제조가 가능하다. 특히, 본 발명에 따른 위상차 필름은 상기 코팅층이 편광판용 접착제와 매우 우수한 접착력을 가지는바, 편광자 등에 쉽게 부착될 수 있으며, 그 결과 위상차 필름을 포함하는 편광판 등을 쉽게 제조할 수 있다.
The retardation film according to the present invention has a retardation property suitable for use as an IPS mode retardation film and can be manufactured in a thin shape. In particular, the retardation film according to the present invention can be easily attached to a polarizer or the like because the coating layer has a very good adhesion strength with an adhesive for a polarizing plate, and as a result, a polarizing plate or the like including the retardation film can be easily manufactured.
또한, 본 발명에 따른 위상차 필름은 별도의 배향 공정 등이 불필요하기 때문에, 종래의 액정 물질을 코팅하는 방법에 비하여 제조 방법이 간단하며, 나아가 접착제를 이용하여 적층하는 공정 등이 요구되지 않기 때문에, 접착제층의 존재에 의한 광학 특성의 저하 또는 위상차 판 축의 어긋남 등이 발생하지 않는다.
Further, since the phase difference film according to the present invention does not require a separate alignment process or the like, the manufacturing method is simpler than the conventional method of coating a liquid crystal material, and further, there is no need for a step of laminating using an adhesive, There is no decrease in optical characteristics or deviation of the retardation plate axis due to the presence of the adhesive layer.
도 1은 본 발명의 위상차 필름의 일례를 보여주기 위한 도면이다.1 is a view showing an example of a retardation film of the present invention.
먼저 본 명세서에 사용되는 용어를 정의한다.
First, terms used in this specification are defined.
(1) Rin은 면 방향 위상차값을 의미하는 것으로, 면 방향 위상차값 Rin=(nx-ny)×d에 의해 구해진다. 이때, nx는 면 방향 굴절율이 최대가 되는 방향(즉, 지상축 방향)의 굴절율이며, ny는 면 방향에 있어서 지상축에 수직인 방향인 방향(즉, 진상축 방향)의 굴절율이고, d는 위상차값을 측정하고자 하는 필름 또는 코팅층의 두께를 나타낸다. 한편, Rin ,a는 기재 필름의 면 방향 위상차값을 나타내며, Rin ,b는 코팅층의 면 방향 위상차값을 나타내고, Rin , total는 기재 필름과 코팅층을 포함하는 위상차 필름 전체의 면 방향 위상차값을 나타낸다. 한편, 상기 Rin은 당해 기술분야에 있어서 잘 알려진 공지의 방법으로 측정이 가능하며, 예를 들면, Axomatrics社의 Axoscan 장비를 이용하여 측정할 수 있다.
(1) R in means a retardation value in the plane direction, which is obtained from the retardation value R in = (n x -n y ) x d. Here, n x is the refractive index in the direction in which the refractive index in the plane direction is the maximum (that is, in the slow axis direction), and n y is the refractive index in the direction perpendicular to the slow axis in the plane direction and d represents the thickness of the film or coating layer on which the retardation value is to be measured. Meanwhile, R in, a denotes a plane direction retardation value of the substrate film, R in, b denotes a plane direction retardation value of the coating layer, R in, total phase difference surface of the entire retardation film comprising a substrate film and the coating direction Value. On the other hand, in the R it can be measured by a known method known in the art and, for example, can be measured using the equipment of Axoscan Axomatrics社.
(2) Rth은 두께 방향 위상차값을 의미하는 것으로, 두께 방향 위상차값 Rth=(nz-ny)×d에 의해 구해진다. 이때, ny는 면 방향에 있어서 지상축에 수직인 방향인 방향(즉, 진상축 방향)의 굴절율이고, nz는 두께 방향의 굴절율이며, d는 위상차값을 측정하고자 하는 필름 또는 코팅층의 두께를 나타낸다. 한편, Rth ,a는 기재 필름의 두께 방향 위상차값을 나타내며, Rth ,b는 코팅층의 두께 방향 위상차값을 나타내고, Rth , total는 기재 필름과 코팅층을 포함하는 위상차 필름 전체의 두께 방향 위상차값을 나타낸다. 한편, 상기 Rth은 당해 기술분야에 있어서 잘 알려진 공지의 방법으로 측정이 가능하며, 예를 들면, Axomatrics社의 Axoscan 장비를 이용하여 측정할 수 있다.
(2) Rth means a retardation value in the thickness direction, and is obtained by the retardation value in the thickness direction R th = (n z -n y ) x d. Here, n y is the refractive index in the direction perpendicular to the slow axis in the plane direction (i.e., the fast axis direction), n z is the refractive index in the thickness direction, d is the thickness of the film or coating layer . R th , a represents the retardation value in the thickness direction of the base film, R th , b represents the retardation value in the thickness direction of the coating layer, R th , total represents the retardation in the thickness direction of the whole retardation film including the base film and the coating layer Value. On the other hand, the R th can be determined by well-known methods known in the art and, for example, can be measured using the equipment of Axoscan Axomatrics社.
(3) Nz는 면 방향 위상차값에 대한 두께 방향 위상차 값의 비를 의미하는 것으로, Nz = Rth , total/Rin , total에 의해 구해진다.
(3) Nz is to mean the ratio of the retardation value in the thickness direction to the retardation value in the plane direction is obtained by Nz = R th, total / R in, total.
(4) 정의 위상차란, 연신 시에 연신 방향을 따라 최대 굴절율이 발현되는 것을 의미하며, 부의 위상차란, 연신 시에 연신 방향에 대해 수직인 방향을 따라 최대 굴절율이 발현되는 것을 의미한다.
(4) The positive phase difference means that the maximum refractive index is expressed along the stretching direction at the time of stretching, and the negative phase difference means that the maximum refractive index is expressed along the direction perpendicular to the stretching direction at the time of stretching.
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시 형태들을 설명한다. 그러나, 본 발명의 실시형태는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 이하 설명하는 실시 형태로 한정되는 것은 아니다. 또한, 본 발명의 실시형태는 당해 기술분야에서 평균적인 지식을 가진 자에게 본 발명을 더욱 완전하게 설명하기 위해서 제공되는 것이다. 도면에서 요소들의 형상 및 크기 등은 보다 명확한 설명을 위하여 과장될 수 있다.
Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings. However, the embodiments of the present invention can be modified into various other forms, and the scope of the present invention is not limited to the embodiments described below. Further, the embodiments of the present invention are provided to more fully explain the present invention to those skilled in the art. The shape and size of elements in the drawings may be exaggerated for clarity.
1. One. 위상차Phase difference 필름 film
먼저, 본 발명의 위상차 필름에 대하여 설명한다.
First, the retardation film of the present invention will be described.
본 발명의 위상차 필름은 하기 도 1에 예시적으로 도시한 바와 같이, 부의 위상차 물질을 포함하는 기재 필름(1); 및 상기 기재 필름의 적어도 일면에 형성되며, 하기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체를 포함하는 코팅층(2)을 포함한다.The retardation film of the present invention, as exemplarily shown in Fig. 1 below, comprises a base film 1 comprising a negative retardation material; And a coating layer (2) comprising a polyimide copolymer formed on at least one side of the base film and containing a repeating unit represented by the following formula (1).
[화학식 1][Chemical Formula 1]
상기 [화학식 1]에서, X1은 에스테르기 또는 에테르기를 포함하는 지환족 또는 방향족 산 이무수물로부터 유도된 4가 유기기이며; X2는 X1과 상이한 산 이무수물로부터 유도된 4가 유기기이고; Q1 및 Q2는 각각 독립적으로 디아민으로부터 유도된 2가 유기기이며; 상기 a, b, c 및 d는 각 반복단위의 몰비를 나타내는 것으로, a+b+c+d =1이고, 0.1 ≤ a+b ≤ 1 이고, 0 ≤ c+d ≤ 0.9 임.
Wherein X 1 is a divalent organic group derived from an alicyclic or aromatic acid dianhydride containing an ester group or an ether group; X 2 is a divalent organic group derived from an acid dianhydride different from X 1 ; Q 1 and Q 2 are each independently a divalent organic group derived from a diamine; Wherein a, b, c and d represent the molar ratio of the respective repeating units, a + b + c + d = 1, 0.1? A + b? 1 and 0? C + d? 0.9.
한편, 본 발명의 위상차 필름은 상기 코팅층을 편광판용 접착제를 매개로 폴리비닐알코올계 편광자에 부착한 후 측정한 접착력이 1N/2cm 이상인 것이 바람직하며, 보다 바람직하게는 1 N/2cm 내지 4 N/2cm 정도일 수 있다. 이때, 상기 접착력은 편광판용 접착제를 이용하여 편광소자의 일면에 상기 미연신 코팅층이 접착되도록 위상차 필름을 부착하여 편광판을 제조한 후, 폭 2cm, 길이 8cm의 편광판 샘플을 texture analyser(XT-Plus, Stable Micro System)의 아랫면에 고정하고, 5cm 거리에서 90도 필(feel) 박리력을 가하여 위상차 필름을 박리시키면서 측정할 수 있다.
On the other hand, the retardation film of the present invention preferably has an adhesive force of 1 N / 2 cm or more, more preferably 1 N / 2 cm to 4 N / cm, after the coating layer is attached to the polyvinyl alcohol polarizer through an adhesive for polarizing plate, It may be about 2 cm. At this time, the polarizing plate was prepared by attaching a retardation film so that the non-stretched coating layer was adhered to one surface of the polarizing element by using an adhesive for polarizing plate, and then polarizer samples having a width of 2 cm and a length of 8 cm were applied to a texture analyzer (XT- Stable Micro System), and a 90 degree feel force is applied at a distance of 5 cm to peel off the retardation film.
한편, 상기 편광판용 접착제는 특별히 제한되지 않으며, 예컨대 통상의 (메타)아크릴레이트계 접착제, 엔/티올계 접착제, 불포화 폴리에스테르계 잡착제 등의 라디칼계 접착제나, 에폭시계 접착제, 옥세탄계 접착제, 에폭시/옥세탄계 접착제, 비닐에테르계 접착제 등의 양이온계 접착제 등일 수 있다.
On the other hand, the adhesive for a polarizing plate is not particularly limited, and examples thereof include radical-based adhesives such as ordinary (meth) acrylate adhesives, EN / THY adhesives and unsaturated polyester adhesives, epoxy adhesives, Epoxy-based adhesives such as epoxy / oxetane adhesives, and vinyl ether-based adhesives.
보다 바람직하게는, 상기 편광판용 접착제는 호모폴리머의 유리전이온도가 120℃ 이상인 제1에폭시 화합물 100 중량부; 호모폴리머의 유리전이온도가 60℃ 이하인 제2에폭시 화합물 30 내지 100 중량부; 및 양이온성 광 중합 개시제 0.5 내지 20 중량부를 포함하는 것일 수 있다.
More preferably, the adhesive for a polarizing plate comprises 100 parts by weight of a first epoxy compound having a glass transition temperature of 120 DEG C or higher of the homopolymer; 30 to 100 parts by weight of a second epoxy compound having a glass transition temperature of 60 占 폚 or less of the homopolymer; And 0.5 to 20 parts by weight of a cationic photopolymerization initiator.
이때, 상기 제1에폭시 화합물은, 예를 들면, 3,4-에폭시시클로헥실메틸-3,4'-에폭시시클로헥산카복실레이트, 비닐사이클로헥센디옥사이드 디시클로펜타디엔디옥사이드, 비스에폭시사이클로펜틸에테르, 비스페놀 A 계 에폭시 화합물, 비스페놀 F 계 에폭시 화합물 등일 수 있다.
The first epoxy compound may be, for example, 3,4-epoxycyclohexylmethyl-3,4'-epoxycyclohexanecarboxylate, vinylcyclohexene dioxide dicyclopentadienedioxide, bis epoxycyclopentyl ether, bisphenol A-based epoxy compounds, and bisphenol F-based epoxy compounds.
또한, 상기 제2에폭시 화합물은 글리시딜 에테르기를 하나 이상 포함하는 것일 수 있으며, 예를 들면, 1,4-시클로헥산디메탄올 디글리시딜 에테르, 1,4-부탄디올디글시딜에테르, 1,6-헥산디올디글리시딜에테르, 네오펜틸디글시딜에테르, 레조시놀디글리시딜에테르, 디에틸렌글라이콜디글리시딜에테르, 에틸렌글라이콜디글리시딜에테르, 트리메틸올프로판트리글리시딜에테르, n-부틸 글리시딜 에테르, 2-에틸헥실 글리시딜 에테르, 페닐 글리시딜 에테르, 및 o-크레실(Cresyl) 글리시딜 에테르로 이루어진 그룹으로부터 선택된 1종 이상일 수 있다.
Also, the second epoxy compound may be one containing at least one glycidyl ether group, for example, 1,4-cyclohexanedimethanol diglycidyl ether, 1,4-butanediol diglycidyl ether, 1 , 6-hexanediol diglycidyl ether, neopentyldiglycidyl ether, resorcinol diglycidyl ether, diethylene glycol di glycidyl ether, ethylene glycol diglycidyl ether, trimethylol propane triglycidyl Ethylhexyl glycidyl ether, phenyl glycidyl ether, and o-cresyl glycidyl ether may be used in combination with one or more of glycidyl ether, diethyl ether, n-butyl glycidyl ether, 2-ethylhexyl glycidyl ether,
또한, 상기 양이온성 광 중합 개시제는 활성 에너지 선의 조사에 의해 양이온(cation) 종이나 루이스산을 만들어내는 화합물로서, 예를 들면 방향족 디아조늄염, 방향족 요오드 알루미늄염이나 방향족 설포늄염과 같은 오늄염, 철-아렌 착제 등일 수 있다.
The cationic photopolymerization initiator is a compound which produces a cationic species or Lewis acid by irradiation with an active energy ray. Examples of the cationic photopolymerization initiator include an onium salt such as an aromatic diazonium salt, an aromatic iodo aluminum salt or an aromatic sulfonium salt, Iron-arene complex, and the like.
한편, 상기 편광판용 접착제는, 필요에 따라, 분자 내에 적어도 1개의 옥세타닐기를 갖는 옥세탄 화합물 100 내지 400 중량부를 더 포함할 수 있으며, 이때 상기 옥세탄 화합물로는, 이로써 제한되는 것은 아니나, 3-에틸-3-〔(3-에틸옥세탄-3-일)메톡시메틸〕옥세탄, 1,4-비스〔(3-에틸옥세탄-3-일)메톡시메틸〕벤젠, 1,4-비스〔(3-에틸옥세탄-3-일)메톡시〕벤젠, 1,3-비스〔(3-에틸옥세탄-3-일)메톡시〕벤젠, 1,2-비스〔(3-에틸옥세탄-3-일)메톡시〕벤젠, 4,4'-비스〔(3-에틸옥세탄-3-일)메톡시〕비페닐, 2,2'-비스〔(3-에틸옥세탄-3-일)메톡시〕비페닐, 3,3',5,5'-테트라메틸-4,4'-비스〔(3-에틸옥세탄-3-일)메톡시〕비페닐, 2,7-비스〔(3-에틸옥세탄-3-일)메톡시〕나프탈렌, 비스〔4-{(3-에틸옥세탄-3-일)메톡시}페닐〕메탄, 비스〔2-{(3-에틸옥세탄-3-일)메톡시}페닐〕메탄, 2,2-비스〔4-{(3-에틸옥세탄-3-일)메톡시}페닐〕프로판, 노볼락형페놀-포름알데히드 수지의 3-클로로메틸-3-에틸옥세탄에 의한 에테르화 변성물, 3(4),8(9)-비스〔(3-에틸옥세탄-3-일)메톡시메틸〕-트리시클로[5.2.1.0 2,6]데칸, 2,3-비스〔(3-에틸옥세탄-3-일)메톡시메틸〕노르보르난, 1,1,1-트리스〔(3-에틸옥세탄-3-일)메톡시메틸〕프로판, 1-부톡시-2,2-비스〔(3-에틸옥세탄-3-일)메톡시메틸〕부탄, 1,2-비스〔{2-(3-에틸옥세탄-3-일)메톡시}에틸티오〕에탄, 비스〔{4-(3-에틸옥세탄-3-일)메틸티오}페닐〕술피드, 1,6-비스〔(3-에틸옥세탄-3-일)메톡시〕-2,2,3,3,4,4,5,5-옥타플루오로헥산 등이 사용될 수 있다.
If necessary, the adhesive for a polarizing plate may further include 100 to 400 parts by weight of an oxetane compound having at least one oxetanyl group in the molecule. The oxetane compound may include, but is not limited to, (3-ethyloxetan-3-yl) methoxymethyl] benzene, 1,4-bis [ Bis (3-ethyloxetan-3-yl) methoxy] benzene, 1,2-bis [(3 Methoxy] benzene, 4,4'-bis [(3-ethyloxetan-3-yl) methoxy] biphenyl, 2,2'-bis [ 3-yl) methoxy] biphenyl, 3,3 ', 5,5'-tetramethyl-4,4'-bis [ Methoxy] naphthalene, bis [4- {(3-ethyloxetan-3-yl) methoxy} phenyl] methane, bis [2- { 3-ethyloxetan-3-yl) methoxy} phenyl] methane, 2,2-bis [ Methoxy} phenyl] propane, an etherified product of 3-chloromethyl-3-ethyloxetane of a novolac phenol-formaldehyde resin, 3 (4-ethyloxetane- ), 8 (9) -bis [(3-ethyloxetan-3-yl) methoxymethyl] -tricyclo [5.2.1.0 2,6] decane, 2,3- Methoxymethyl] norbornane, 1,1,1-tris [(3-ethyloxetan-3-yl) methoxymethyl] propane, 1-butoxy-2,2- Ethyloxetane-3-yl) methoxymethyl] butane, 1,2-bis [{2- Ethyloxetane-3-yl) methylthio} phenyl] sulfide, 1,6-bis [ 5,5-octafluorohexane and the like can be used.
또한, 상기 위상차 필름은 하기 식 (1) 및 (2)를 만족하는 것이 바람직하며, 보다 바람직하게는 Rin , total이 50 내지 200nm, 60 내지 150nm, 또는 80nm 내지 130nm 정도이고, Rth , total가 10 내지 200nm, 20 내지 150nm, 또는 40 내지 100nm 정도일 수 있다. 본 발명자들의 연구에 따르면, 본 발명의 위상차 필름이 이와 같은 범위를 만족하는 경우, IPS 모드 액정표시장치에 위상차 필름으로 이용시 시야각 개선 효과가 우수한 것으로 나타났다.The retardation film preferably satisfies the following formulas (1) and (2), more preferably R in , total is 50 to 200 nm, 60 to 150 nm, or 80 nm to 130 nm, R th , total May be about 10 to 200 nm, 20 to 150 nm, or about 40 to 100 nm. According to research conducted by the present inventors, when the retardation film of the present invention satisfies such a range, it has been shown that the IPS mode liquid crystal display device has an excellent viewing angle improving effect when used as a retardation film.
식 (1): 50nm ≤ Rin , total ≤ 300nm(1): 50 nm? R in , total ? 300 nm
식 (2): 10nm ≤ Rth , total ≤ 300nm(2): 10 nm? R th , total ? 300 nm
상기 식 (1) 및 (2)에서, Rin , total은 파장 550nm에서 측정한 위상차 필름 전체의 면 방향 위상차값이고, Rth , total은 파장 550nm에서 측정한 위상차 필름 전체의 두께 방향 위상차값이다.
In the above formulas (1) and (2), R in , total is the retardation value of the entire retardation film measured at a wavelength of 550 nm, and R th , total is retardation value in the thickness direction of the entire retardation film measured at a wavelength of 550 nm .
또한, 상기 위상차 필름은 하기 식 (3)으로 표시되는 Nz 값이 1 이하인 것이 바람직하고, 보다 바람직하게는 0.3 내지 0.9 또는 0.4 내지 0.8정도 일 수 있다. 이 경우 다양한 모드의 액정표시장치, 특히 IPS 모드의 액정표시장치의 위상차 필름으로서 사용하기에 매우 적합하다.The retardation film preferably has an Nz value of 1 or less, more preferably 0.3 to 0.9 or 0.4 to 0.8, expressed by the following formula (3). In this case, it is very suitable for use as a retardation film of a liquid crystal display device of various modes, in particular, an IPS mode liquid crystal display device.
식 (3): Nz = Rth , total/Rin , total Equation (3): Nz = R th , total / R in, total
상기 식 (3)에서, Rin , total은 위상차 필름 전체의 면 방향 위상차값이고, Rth,total은 위상차 필름 전체의 두께 방향 위상차값이며, 이때, 상기 Rin , total 및 Rth,total은 모두 파장 550nm에서 측정한 위상차 값이다.
R in , total is the retardation value of the entire retardation film, R th, total is the thickness retardation value of the entire retardation film, and R in , total and R th, Are all retardation values measured at a wavelength of 550 nm.
또한, 상기 위상차 필름은 기재 필름이 하기 식 (4) 및 (5)를 만족하는 것이 바람직하며, 보다 바람직하게는 Rin ,a가 0nm 내지 100nm, 0nm 내지 70nm, 또는 0nm 내지 40nm 정도이고, Rth ,a가 10nm 내지 250nm, 50nm 내지 200nm, 또는 80nm 내지 160nm 정도일 수 있다. 이 경우 하기 코팅층의 위상차와 함께 위상차 필름 전체의 면 방향 위상차값 및 두께 방향 위상차값을 IPS 모드용 위상차 필름으로 적용하기 위한 적절한 수치로 조절할 수 있다.It is preferable that the retardation film satisfies the following formulas (4) and (5), more preferably R in , a is 0 nm to 100 nm, 0 nm to 70 nm, or 0 nm to 40 nm, and R th , a may be about 10 nm to 250 nm, 50 nm to 200 nm, or 80 nm to 160 nm. In this case, the retardation value in the plane direction and the thickness direction retardation value of the entire retardation film together with the retardation of the following coating layer can be adjusted to appropriate values for application as an IPS mode retardation film.
식 (4): 0nm ≤ Rin ,a ≤ 250nm(4): 0 nm? R in , a ? 250 nm
식 (5): 10nm ≤ Rth ,a ≤ 300nm(5): 10 nm? R th , a ? 300 nm
상기 식 (4) 및 (5)에서, Rin ,a은 파장 550nm에서 측정한 기재 필름의 면 방향 위상차값이고, Rth ,a은 파장 550nm에서 측정한 기재 필름의 두께 방향 위상차값이다.
In the formulas (4) and (5), R in , a is the retardation value in the plane direction of the base film measured at a wavelength of 550 nm, and R th , a is the retardation value in the thickness direction of the base film measured at a wavelength of 550 nm.
또한, 상기 위상차 필름은 코팅층이 하기 식 (6) 및 (7)을 만족하는 것이 바람직하며, 보다 바람직하게는 Rin ,b가 50nm 내지 200nm, 80nm 내지 180nm, 또는 90nm 내지 160nm 정도이고, Rth ,b가 -200nm 내지 0nm, -100nm 내지 0nm, 또는 -80nm 내지 0nm 정도일 수 있다. 이 경우 상기 기재 필름과 함께 위상차 필름 전체의 면 방향 위상차값 및 두께 방향 위상차값을 IPS 모드용 위상차 필름으로 적용하기 위한 적절한 수치로 조절할 수 있다.In addition, the above described retardation film coating is the following formula (6) and (7) it is desirable to satisfy and, more preferably, R in, b is 50nm to 200nm, 80nm to 180nm, or 90nm to 160nm approximately, R th , b may be about -200 nm to 0 nm, -100 nm to 0 nm, or about -80 nm to 0 nm. In this case, the retardation value in the plane direction and the thickness direction retardation value of the entire retardation film may be adjusted to appropriate values for application as the IPS mode retardation film together with the base film.
식 (6): 50nm ≤ Rin ,b ≤ 300nm(6): 50 nm? R in , b ? 300 nm
식 (7): -290nm ≤ Rth ,b ≤ 0nm(7): -290 nm? R th , b ? 0 nm
상기 식 (6) 및 (7)에서, Rin ,b은 파장 550nm에서 측정한 코팅층의 면 방향 위상차값이고, Rth ,b은 파장 550nm에서 측정한 코팅층의 두께 방향 위상차값이다.
In the formulas (6) and (7), R in , b is the retardation value in the plane direction of the coating layer measured at a wavelength of 550 nm, and R th , b is the retardation value in the thickness direction of the coating layer measured at a wavelength of 550 nm.
한편, 본 발명의 위상차 필름은 상기 기재 필름이 길이 방향(MD) 및 폭 방향(TD)으로 이축 연신 처리된 것이고, 코팅층이 폭 방향(TD)으로 일축 연신 처리된 것이 바람직하다. 이 경우 상기 식 (1) 내지 (7) 중 하나 이상을 바람직하게 만족하는 IPS 모드에 적합한 위상차의 구현이 용이하기 때문이다.
On the other hand, in the retardation film of the present invention, it is preferable that the base film is biaxially stretched in the longitudinal direction (MD) and the width direction (TD), and the coating layer is uniaxially stretched in the width direction (TD). This is because it is easy to realize the phase difference suitable for the IPS mode satisfying at least one of the above-mentioned formulas (1) to (7).
한편, 본 발명의 위상차 필름은 전체 두께가 80㎛이하인 것이 바람직하며, 예를 들면, 5㎛ 내지 75㎛ 또는 10㎛ 내지 70㎛ 정도일 수 있다. 본 발명의 위상차 필름은 다층 구조임에도 불구하고 이와 같이 박형일 수 있다.
On the other hand, the retardation film of the present invention preferably has a total thickness of 80 탆 or less, for example, about 5 탆 to 75 탆 or 10 탆 to 70 탆. The retardation film of the present invention may be as thin as such a multilayer structure.
한편, 상기와 같은 코팅층의 접착력을 가지며, 식 (1) 내지 (7) 중 하나 이상을 바람직하게 만족하는 본 발명의 위상차 필름은 상기 기재 필름 및 코팅층을 형성하는 원료 물질 및 연신 조건 등을 적절하게 제어함으로써 제조될 수 있다.
On the other hand, the retardation film of the present invention having the above-mentioned coating layer adhesion and satisfying at least one of the formulas (1) to (7) preferably satisfies the following conditions: the raw material for forming the base film and the coating layer, . ≪ / RTI >
가. 기재 필름end. Base film
먼저, 상기 기재 필름의 원료 물질은 부의 위상차 물질이면 특별한 제한 없이 사용이 가능하다. 예를 들면, 이에 한정되는 것은 아니나, 상기 부의 위상차 물질은 아크릴계 수지, 스티렌계 수지, 아크릴계 수지와 스티렌계 수지를 포함하는 블렌딩 수지, 폴리비닐카바졸, 폴리비닐나프탈렌 등을 들 수 있다.
First, the raw material of the base film can be used without any particular limitation as long as it is a negative retardation substance. Examples of the negative retardation material include acrylic resin, styrene resin, blending resin including acrylic resin and styrene resin, polyvinyl carbazole, polyvinyl naphthalene, and the like.
이때, 상기 아크릴계 수지는 (메트)아크릴계 단량체를 주성분으로 포함하는 것으로, (메트)아크릴계 단량체로 이루어진 호모폴리머 수지뿐 아니라 (메트)아크릴계 단량체 이외에 다른 단량체가 공중합된 공중합체 수지를 포함하는 개념이다.
The acrylic resin includes a (meth) acrylic monomer as a main component, and includes not only a homopolymer resin composed of a (meth) acrylic monomer but also a copolymer resin in which a monomer other than a (meth) acrylic monomer is copolymerized.
한편, 상기 (메트)아크릴계 단량체는 아크릴레이트 및 메타크릴레이트 뿐만 아니라 아크릴레이트 및 메타크릴레이트의 유도체를 포함하는 개념으로, 예컨대 메틸 메타크릴레이트, 에틸 메타크릴레이트, 프로필 메타크릴레이트, n-부틸 메타크릴레이트, t-부틸 메타크릴레이트, 시클로헥실 메타크릴레이트, 페닐 메타크릴레이트, 벤질 메타크릴레이트, 메톡시에틸 메타크릴레이트, 에톡시에틸 메타크릴레이트, 부톡시메틸 메타크릴레이트, 메틸 아크릴레이트, 에틸 아크릴레이트, 프로필 아크릴레이트, n-부틸 아크릴레이트, t-부틸 아크릴레이트, 시클로헥실 아크릴레이트, 페닐 아크릴레이트, 벤질 아크릴레이트, 메톡시에틸 아크릴레이트, 에톡시에틸 아크릴레이트, 부톡시 메틸 아크릴레이트 또는 이들의 올리고머 등 일 수 있으며, 그 중에서도 메틸 메타크릴레이트, 메틸 아크릴레이트 등의 알킬 (메트)아크릴레이트인 것이 보다 바람직하나, 반드시 이에 한정되는 것은 아니다. 이들은 단독으로 또는 혼합하여 사용될 수 있다.
On the other hand, the (meth) acrylic monomers include not only acrylates and methacrylates but also derivatives of acrylates and methacrylates, such as methyl methacrylate, ethyl methacrylate, propyl methacrylate, n -butyl Methacrylate, t -butyl methacrylate, cyclohexyl methacrylate, phenyl methacrylate, benzyl methacrylate, methoxyethyl methacrylate, ethoxyethyl methacrylate, butoxy methyl methacrylate, Acrylates such as ethyl acrylate, propyl acrylate, n -butyl acrylate, t -butyl acrylate, cyclohexyl acrylate, phenyl acrylate, benzyl acrylate, methoxyethyl acrylate, ethoxyethyl acrylate, Acrylate, oligomers thereof, etc. Among them, Methacrylate, one or more preferably alkyl (meth) acrylates such as methyl acrylate, is not limited thereto. These may be used alone or in combination.
한편, 부의 위상차 특성을 보다 향상시키기 위하여, 상기 아크릴계 수지는 상기 (메트)아크릴계 단량체이외의 단량체로 스티렌계 단량체를 포함하는 것이 바람직하다. 이에 한정되는 것은 아니나, 스티렌계 단량체 중에서도 스티렌 또는 α-메틸스티렌이 포함되는 것이 더욱 바람직하다. 이들은 단독으로 또는 혼합하여 사용될 수 있다.
On the other hand, in order to further improve the negative retardation property, the acrylic resin preferably contains a styrene monomer as a monomer other than the (meth) acrylic monomer. Although not limited thereto, it is more preferable that styrene or? -Methylstyrene is included among the styrene-based monomers. These may be used alone or in combination.
한편, 내열성을 향상시키기 위하여, 상기 아크릴계 수지는 상기 (메트)아크릴계 단량체 이외의 다른 단량체로 말레산 무수물계 단량체, 말레이미드계 단량체 등을 포함할 수 있다. 그 중에서도 말레산 무수물계 단량체 또는 말레이미드계 단량체를 포함하는 것이 보다 바람직하다. 이때, 상기 말레산 무수물계 단량체로는 말레산 무수물, 메틸 말레산 무수물, 에틸 말레산 무수물, 프로필 말레산 무수물, 이소프로필 말레산 무수물, 시클로헥실 말레산 무수물, 페닐 말레산 무수물 등을 그 예로 들 수 있으며; 상기 말레이미드계 단량체로는 말레이미드, N-메틸 말레이미드, N-에틸 말레이미드, N-프로필 말레이미드, N-이소프로필 말레이미드, N-시클로헥실 말레이미드, N-페닐 말레이미드 등을 그 예로 들 수 있으나, 반드시 이에 한정되는 것은 아니다. 이들은 단독으로 또는 혼합하여 사용될 수 있다.
On the other hand, in order to improve heat resistance, the acrylic resin may include a maleic anhydride monomer, a maleimide monomer, and the like, other than the (meth) acrylic monomer. Among them, it is more preferable to include a maleic anhydride-based monomer or a maleimide-based monomer. Examples of the maleic anhydride monomer include maleic anhydride, methyl maleic anhydride, ethyl maleic anhydride, propyl maleic anhydride, isopropyl maleic anhydride, cyclohexyl maleic anhydride and phenyl maleic anhydride. ; Examples of the maleimide-based monomer include maleimide, N-methylmaleimide, N-ethylmaleimide, N-propylmaleimide, N-isopropylmaleimide, N-cyclohexylmaleimide, But are not limited thereto. These may be used alone or in combination.
한편, 상기 아크릴계 수지에는 상기한 스티렌계 단량체, 말레산 무수물계 단량체, 말레이미드계 단량체 등이 2종 이상 혼합되어 (메트)아크릴계 단량체와 함께 사용될 수도 있다. 예컨대, 상기 아크릴계 (메트)아크릴계 단량체; 및 스티렌계 단량체, 말레산 무수물계 단량체 및 말레이미드계 단량체로 이루어진 군으로부터 선택된 1 이상의 단량체가 포함될 수 있다.
On the other hand, the acrylic resin may be used in combination with (meth) acrylic monomers by mixing two or more kinds of styrenic monomers, maleic anhydride monomers, maleimide monomers, and the like. For example, the acrylic (meth) acrylic monomer; And one or more monomers selected from the group consisting of styrene-based monomers, maleic anhydride-based monomers and maleimide-based monomers.
보다 구체적으로, 상기 아크릴계 수지는, 이에 한정되는 것은 아니나, 시클로헥실 말레산 무수물-메틸 메타크릴레이트 공중합체, N-시클로헥실 말레이미드-메틸 메타크릴레이트 공중합체, 스티렌-시클로헥실 말레산 무수물-메틸 메타크릴레이트 공중합체, 스티렌-N-시클로헥실 말레이미드-메틸 메타크릴레이트 공중합체, α-메틸스티렌-N-시클로헥실 말레이미드-메틸 메타크릴레이트 공중합체, α-메틸스티렌-N-페닐 말레이미드-메틸 메타크릴레이트 공중합체, α-메틸스티렌-N-페닐 말레이미드-메틸 메타크릴레이트-메타크릴레이트 공중합체, α-메틸스티렌-N-시클로헥실 말레이미드-메틸 메타크릴레이트-시클로헥실 메타크릴레이트 공중합체 등일 수 있다.
More specifically, the acrylic resin includes, but is not limited to, cyclohexyl maleic anhydride-methyl methacrylate copolymer, N-cyclohexyl maleimide-methyl methacrylate copolymer, styrene-cyclohexyl maleic anhydride- Methyl methacrylate copolymer, styrene-N-cyclohexylmaleimide-methyl methacrylate copolymer,? -Methylstyrene-N-cyclohexylmaleimide-methyl methacrylate copolymer,? -Methylstyrene-N-phenyl Maleimide-methyl methacrylate copolymer,? -Methylstyrene-N-phenylmaleimide-methylmethacrylate-methacrylate copolymer,? -Methylstyrene-N-cyclohexylmaleimide-methylmethacrylate-cyclo Hexyl methacrylate copolymer, and the like.
또한, 상기 스티렌계 수지는 스티렌계 단량체를 주 성분으로 포함하는 것이면 특별한 제한 없이 사용이 가능하다. 이때 상기 스티렌계 단량체의 예로는, 이에 한정되는 것은 아니나, 스티렌, α-메틸스티렌, 3-메틸스티렌, 4-메틸스티렌, 2,4-디메틸스티렌, 2,5-디메틸스티렌, 2-메틸-4-클로로스티렌, 2,4,6-트리메틸스티렌, cis-β-메틸스티렌, trans-β-메틸스티렌, 4-메틸-α-메틸스티렌, 4-플루오르-α-메틸스티렌, 4-클로로-α-메틸스티렌, 4-브로모-α-메틸스티렌, 4-t-부틸스티렌, 2-플루오르스티렌, 3-플루오르스티렌, 4-플루오로스티렌, 2,4-디플루오로스티렌, 2,3,4,5,6-펜타플루오로스티렌, 2-클로로스티렌, 3-클로로스티렌, 4-클로로스티렌, 2,4-디클로로스티렌, 2,6-디클로로스티렌, 옥타클로로스티렌, 2-브로모스티렌, 3-브로모스티렌, 4-브로모스티렌, 2,4-디브로모스티렌, α-브로모스티렌, β-브로모스티렌, 2-하이드록시스티렌, 4-하이드록시스티렌 등을 들 수 있으며, 그 중에서도 스티렌 및 α-메틸스티렌인 것이 보다 바람직하다. 이들은 단독으로 또는 혼합하여 사용될 수 있다.
In addition, the styrenic resin can be used without particular limitation as long as it contains a styrene-based monomer as a main component. Examples of the styrenic monomer include but are not limited to styrene,? -Methylstyrene, 3-methylstyrene, 4-methylstyrene, 2,4-dimethylstyrene, 2,5-dimethylstyrene, ? -Methylstyrene, 4-fluoro-? -Methylstyrene, 4-chlorostyrene, 2,4,6-trimethylstyrene, cis-? -Methylstyrene, trans-? methylstyrene, 4-t-butylstyrene, 2-fluorostyrene, 3-fluorostyrene, 4-fluorostyrene, 2,4-difluorostyrene, 2,3 , 4,5,6-pentafluorostyrene, 2-chlorostyrene, 3-chlorostyrene, 4-chlorostyrene, 2,4-dichlorostyrene, 2,6-dichlorostyrene, octachlorostyrene, , 3-bromostyrene, 4-bromostyrene, 2,4-dibromostyrene,? -Bromostyrene,? -Bromostyrene, 2-hydroxystyrene and 4-hydroxystyrene. Among them, And more preferably in the α- methyl styrene. These may be used alone or in combination.
한편, 상기 스티렌계 수지에는 상기한 스티렌계 단량체 외에 말레산 무수물계 단량체, 말레이미드계 단량체, 아크릴로니트릴계 단량체 등이 2종 이상 혼합되어 스티렌계 단량체와 함께 사용될 수도 있다. 예컨대, 상기 스티렌계 수지에는 스티렌계 단량체; 및 말레산 무수물계 단량체, 말레이미드계 단량체 및 아크릴로니트릴계 단량체로 이루어진 군으로부터 선택된 1 이상의 단량체가 포함될 수 있다.
On the other hand, in addition to the above styrene type monomer, the styrene type resin may be used in combination with a styrene type monomer by mixing two or more kinds of maleic anhydride type monomer, maleimide type monomer, acrylonitrile type monomer and the like. For example, the styrene-based resin includes styrene-based monomers; And at least one monomer selected from the group consisting of maleic anhydride-based monomer, maleimide-based monomer and acrylonitrile-based monomer.
이때, 상기 말레산 무수물계 단량체로는 말레산 무수물, 메틸 말레산 무수물, 에틸 말레산 무수물, 프로필 말레산 무수물, 이소프로필 말레산 무수물, 시클로헥실 말레산 무수물, 페닐 말레산 무수물 등을 그 예로 들 수 있고; 상기 말레이미드계 단량체로는 말레이미드, N-메틸 말레이미드, N-에틸 말레이미드, N-프로필 말레이미드, N-이소프로필 말레이미드, N-시클로헥실 말레이미드, N-페닐 말레이미드 등을 그 예로 들 수 있으며; 상기 아크릴로니트릴계 단량체로는 아크릴로니트릴, 메타크릴로니트릴, 에타크릴로니트릴, 페닐아크릴로니트릴 등을 그 예로 들 수 있으나, 반드시 이에 한정되는 것은 아니다.
Examples of the maleic anhydride monomer include maleic anhydride, methyl maleic anhydride, ethyl maleic anhydride, propyl maleic anhydride, isopropyl maleic anhydride, cyclohexyl maleic anhydride and phenyl maleic anhydride. Can be; Examples of the maleimide-based monomer include maleimide, N-methylmaleimide, N-ethylmaleimide, N-propylmaleimide, N-isopropylmaleimide, N-cyclohexylmaleimide, For example; Examples of the acrylonitrile-based monomer include acrylonitrile, methacrylonitrile, ethacrylonitrile, and phenyl acrylonitrile. However, the present invention is not limited thereto.
보다 구체적으로, 상기 스티렌계 수지는, 이에 한정되는 것은 아니나, 스티렌-말레산 무수물 공중합체, 스티렌-아크릴로니트릴 공중합체, α-메틸스티렌-아크릴로니트릴 공중합체, N-페닐 말레이미드-α-메틸스티렌-아크릴로니트릴 공중합체, N-페닐 말레이미드-스티렌-아크릴로니트릴 공중합체, N-페닐 말레이미드-α-메틸스티렌-아크릴로니트릴 등일 수 있다.
More specifically, the styrenic resin includes, but is not limited to, styrene-maleic anhydride copolymer, styrene-acrylonitrile copolymer,? -Methylstyrene-acrylonitrile copolymer, N-phenylmaleimide-? -Methylstyrene-acrylonitrile copolymer, N-phenylmaleimide-styrene-acrylonitrile copolymer, N-phenylmaleimide-a-methylstyrene-acrylonitrile and the like.
또한, 상기 스티렌계 수지와 아크릴계 수지를 포함하는 블렌딩 수지에 있어서, 상기 스티렌계 수지는 블렌딩 수지 100 중량부에 대하여 1 내지 99 중량부 정도인 것이 바람직하며, 예를 들면, 5 내지 95 중량부 또는 10 내지 90 중량부 정도일 수 있다. 스티렌계 수지의 함량이 너무 적은 경우에는 위상차 발현성의 저하로 원하는 위상차 값을 내는 위상차 필름을 제작하기 곤란한 문제가 있으며, 따라서, 원하는 위상차 값을 내기 위해서는 필름의 두께가 두꺼워질 수 있는 문제가 발생할 수 있다.
In the blending resin comprising the styrene resin and the acrylic resin, the styrene resin is preferably about 1 to about 99 parts by weight, more preferably about 5 to about 95 parts by weight per 100 parts by weight of the blending resin, 10 to 90 parts by weight. When the content of the styrene-based resin is too small, there is a problem that it is difficult to produce a retardation film which gives a desired retardation value due to lowering of the retardation development. Therefore, there is a problem that the thickness of the film may become thick have.
또한, 상기 폴리비닐카보졸은, 폴리(9-비닐카바졸)과 같이 분자 내에 카바졸 골격을 가지는 것으로, 당해 기술분야에서 일반적으로 사용되는 폴리비닐카바졸이면 특별한 제한 없이 사용이 가능하다.
In addition, the polyvinylcarbazole has a carbazole skeleton in the molecule such as poly (9-vinylcarbazole), and polyvinylcarbazole generally used in the art can be used without any particular limitation.
또한, 상기 폴리비닐나프탈렌은, 폴리(2-비닐나프탈렌)과 같이 분자 내에 나프탈렌 골격을 가지는 것으로, 당해 기술분야에서 일반적으로 사용되는 폴리비닐나프탈렌이면 특별한 제한 없이 사용이 가능하다.
The polyvinylnaphthalene has a naphthalene skeleton in the molecule such as poly (2-vinylnaphthalene), and polyvinylnaphthalene generally used in the art can be used without particular limitation.
한편, 본 발명에 있어서, 상기 부의 위상차 물질은 그 중에서도 특히 스티렌계 수지인 것이 바람직하다. 스티렌계 수지의 경우 얇은 두께에서도 충분한 부의 위상차 특성의 구현이 가능하기 때문에, 최종적으로 제조되는 위상차 필름을 더욱 얇게 제조할 수 있다는 장점이 있다.
On the other hand, in the present invention, the negative retardation material is preferably a styrene-based resin. In the case of a styrenic resin, since it is possible to realize a sufficient negative retardation even in a thin thickness, the retardation film finally produced can be further thinned.
한편, 본 발명의 상기 기재 필름은 두께가 70㎛이하인 것이 바람직하며, 예를 들면, 5㎛ 내지 60㎛ 정도일 수 있다. 두께가 상기 범위보다 두꺼운 경우에는 이를 포함하는 위상차 필름의 박형 경량화에 어려움이 있을 뿐만 아니라, 원하는 범위보다 위상차가 크게 발현될 수 있다는 문제점이 있다.
On the other hand, the base film of the present invention preferably has a thickness of 70 탆 or less, for example, about 5 탆 to 60 탆. When the thickness is larger than the above range, it is difficult to reduce the thickness and weight of the retardation film including the retardation film, and the phase difference can be expressed more than a desired range.
나. 코팅층I. Coating layer
다음으로, 본 발명에 있어서 상기 코팅층의 원료 물질은 하기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체이다. 본 발명자들의 연구에 의하면, 하기와 같은 폴리이미드 공중합체를 이용하여 코팅층을 형성하는 경우, 박막으로 코팅층을 형성하는 경우에도 원하는 높은 위상차를 구현할 수 있으며, 나아가 투명성이 우수하고, 접착제와의 우수한 접착력 구현이 가능하다는 장점이 있다.
Next, in the present invention, the starting material of the coating layer is a polyimide copolymer containing a repeating unit represented by the following formula (1). According to the studies of the present inventors, it has been found that when a coating layer is formed using a polyimide copolymer as described below, a desired high retardation can be realized even when a coating layer is formed of a thin film, and furthermore, excellent transparency, It has the advantage that it can be implemented.
[화학식 1][Chemical Formula 1]
상기 [화학식 1]에서, X1은 에스테르기 또는 에테르기를 포함하는 지환족 또는 방향족 산 이무수물로부터 유도된 4가 유기기이며; X2는 X1과 상이한 산 이무수물로부터 유도된 4가 유기기이고; Q1 및 Q2는 각각 독립적으로 디아민으로부터 유도된 2가 유기기이다.
Wherein X 1 is a divalent organic group derived from an alicyclic or aromatic acid dianhydride containing an ester group or an ether group; X 2 is a divalent organic group derived from an acid dianhydride different from X 1 ; Q 1 and Q 2 are each independently a divalent organic group derived from a diamine.
한편, 상기 a, b, c, d는 각 반복단위의 몰비를 나타내는 것으로, a+b+c+d =1이고, 0.1 ≤ a+b ≤ 1 이고, 0 ≤ c+d ≤ 0.9 이다. 상기 a+b 및 c+d는 상기 수치 범위를 만족하는 범위에서 적절한 값을 가질 수 있으며, 예를 들면, 0.6 ≤ a+b ≤ 0.9 이고, 0.1 ≤ c+d ≤ 0.4이거나, 또는, 0.1 ≤ a+b ≤ 0.5 이고, 0.5 ≤ c+d ≤ 0.9일 수 있다.
A, b, c and d represent the molar ratios of the respective repeating units, wherein a + b + c + d = 1, 0.1? A + b? 1, and 0? C + d? 0.9. A + b and c + d may have appropriate values in a range that satisfies the numerical range. For example, 0.6? A + b? 0.9, 0.1? C + d? 0.4, or 0.1? a + b? 0.5, and 0.5? c + d? 0.9.
보다 구체적으로는, 상기 a는 0.1 ~ 1, b는 0 ~ 0.5, c는 0 ~ 1, d는 0 ~ 1일 수 있으며, 바람직하게는 a는 0.1 ~ 0.9, b는 0.1 ~ 0.5, c는 0.1 ~ 0.8, d는 0.1 ~ 0.3일 수 있으며, 더 바람직하게는, a는 0.1 ~ 0.5, b는 0.1 ~ 0.3, c는 0.5 ~ 0.8, d는 0.1 ~ 0.2 일 수 있다.
More specifically, a may be 0.1 to 1, b may be 0 to 0.5, c may be 0 to 1, d may be 0 to 1, preferably a is 0.1 to 0.9, b is 0.1 to 0.5, c is 0.1 to 0.8, and d may be 0.1 to 0.3. More preferably, a may be 0.1 to 0.5, b may be 0.1 to 0.3, c may be 0.5 to 0.8, and d may be 0.1 to 0.2.
한편, 본 명세서에 있어서, 지방족 사슬은 직쇄 또는 분지쇄 형태의 지방족 화합물을 의미하는 것으로, 이로써 한정되는 것은 아니나, 예를 들면, 탄소수 1 내지 20의 포화 또는 불포화 탄화수소, 탄소수 1 내지 20의 알콕시, 탄소수 1 내지 20의 알킬 에스테르, 탄소수 1 내지 20의 알킬 에테르, 탄소수 1 내지 20의 티오알킬 등일 수 있다. 이때, 상기 지방족 사슬은 주쇄 및/또는 측쇄에 적어도 하나 이상의 치환기를 포함할 수 있으며, 이때, 상기 치환기는, 이로써 한정되는 것은 아니나, 예를 들면, 할로겐, 산소, 황, 질소, 히드록시기, 카르복시기, 알킬기, 할로알킬기, 니트로기, 시아노기, 에스테르기, 에테르기, 아미드기, 이미드기, 알콕시기 또는 이들의 조합일 수 있다.
In the present specification, the aliphatic chain means an aliphatic compound in the form of a straight chain or branched chain, and includes, but is not limited to, saturated or unsaturated hydrocarbons having 1 to 20 carbon atoms, alkoxy having 1 to 20 carbon atoms, Alkyl esters having 1 to 20 carbon atoms, alkyl ethers having 1 to 20 carbon atoms, thioalkyl having 1 to 20 carbon atoms, and the like. The aliphatic chain may include at least one substituent on the main chain and / or side chain, and the substituent may include, for example, a halogen, an oxygen, a sulfur, a nitrogen, a hydroxyl group, An alkyl group, a haloalkyl group, a nitro group, a cyano group, an ester group, an ether group, an amide group, an imide group, an alkoxy group or a combination thereof.
또한, 본 명세서에서, 지방족 고리는, 고리 형태의 지방족 화합물을 의미하는 것으로, 단환식 또는 2 이상의 고리가 축합되어 형성되는 다환식 화합물일 수 있으며, 예를 들면, 사이클로알킬과 같은 탄소수 3 내지 20의 포화 또는 불포화 탄화수소 고리일 수 있다. 상기 지방족 고리는 적어도 하나 이상의 치환기를 포함할 수 있으며, 이때, 상기 치환기는, 이로써 한정되는 것은 아니나, 예를 들면, 할로겐, 산소, 황, 질소, 히드록시기, 카르복시기, 알킬기, 할로알킬기, 니트로기, 시아노기, 에스테르기, 에테르기, 아미드기, 이미드기, 알콕시기 또는 이들의 조합일 수 있다.
In the present specification, an aliphatic ring means an aliphatic compound in the form of a ring, and may be a monocyclic or a polycyclic compound formed by condensation of two or more rings, and includes, for example, Of saturated or unsaturated hydrocarbon rings. The substituent may include, but is not limited to, halogen, oxygen, sulfur, nitrogen, a hydroxyl group, a carboxy group, an alkyl group, a haloalkyl group, a nitro group, A cyano group, an ester group, an ether group, an amide group, an imide group, an alkoxy group, or a combination thereof.
또한, 본 명세서에 있어서, 방향족 고리는, 고리 형태의 방향족 화합물을 의미하는 것으로, 단환식 또는 2 이상의 고리가 축합되어 형성되는 다환식 화합물일 수 있으며, 예를 들면, 페닐, 나프탈렌 등과 같은 탄소수 6 내지 20의 아릴일 수 있다. 상기 방향족 고리는 적어도 하나 이상의 치환기를 포함할 수 있으며, 이때, 상기 치환기는, 이로써 한정되는 것은 아니나, 예를 들면, 할로겐, 산소, 황, 질소, 히드록시기, 카르복시기, 알킬기, 할로알킬기, 니트로기, 시아노기, 에스테르기, 에테르기, 아미드기, 이미드기, 알콕시기 또는 이들의 조합일 수 있다.
In the present specification, the aromatic ring means an aromatic compound in the form of a ring, which may be a monocyclic or a polycyclic compound formed by condensation of two or more rings, and includes, for example, ≪ / RTI > The aromatic ring may contain at least one or more substituents such as, but not limited to, halogen, oxygen, sulfur, nitrogen, hydroxyl, carboxyl, alkyl, haloalkyl, nitro, A cyano group, an ester group, an ether group, an amide group, an imide group, an alkoxy group, or a combination thereof.
한편, 본 발명에 있어서 2 이상의 고리가 직접 연결된다는 것은, 비페닐(biphenyl) 비사이클로헥실 등과 같이, 고리와 고리 사이가 결합(bond)에 의해 연결되어 있는 경우를 의미하며, 가교 구조로 연결된다는 것은, 알킬렌, -O-, -SO2- -S-, -SO-, -C(=O)-, -C(=O)O-, -C(=O)NH-, -O[CH2CH2O]p-(이때, p는 1~20의 정수) 등과 같은 구조에 의해 연결되어 있는 경우를 의미한다.
In the present invention, when two or more rings are directly connected, it means that a ring is connected to a ring by a bond, such as biphenyl, bicyclohexyl and the like, It is, alkylene, -O-, -SO 2 - -S-, -SO-, -C (= O) -, -C (= O) O-, -C (= O) NH-, -O [ CH 2 CH 2 O] p - wherein p is an integer of 1 to 20, and the like.
한편, 본 발명에서 사용되는 상기 폴리이미드 공중합체는 에스테르기 또는 에테르기를 포함하는 지방족 또는 방향족 산 이무수물로부터 유도된 4가 유기기 X1을 포함하며, 상기와 같이 에스테르기 또는 에테르기를 포함하는 산 이무수물로부터 유도된 4가 유기기를 포함하는 폴리이미드 공중합체는 유기 용매, 특히 비점이 낮은 유기 용매에 대한 용해도가 높으며, 종래와 같이 전구체를 이미드화하기 위해 고온 처리를 수행할 필요가 없다는 장점이 있다. 또한 이와 같은 폴리이미드 공중합체를 사용하는 경우, 낮은 이미드화율로 인한 코팅층의 기계적 물성 및 광학 특성의 저하를 방지할 수 있다.
On the other hand, the polyimide copolymer used in the present invention includes a tetravalent organic group X 1 derived from an aliphatic or aromatic acid dianhydride containing an ester group or an ether group, and an acid having an ester group or an ether group The polyimide copolymer containing a tetravalent organic group derived from dianhydride has a high solubility in an organic solvent, particularly an organic solvent having a low boiling point, and has an advantage that a high temperature treatment is not required to imidize a precursor as in the prior art have. In addition, when such a polyimide copolymer is used, it is possible to prevent deterioration of the mechanical properties and optical properties of the coating layer due to a low imidization ratio.
바람직하게는, 상기 X1은, 하기 [화학식 2] 또는 [화학식 3]로 표시되는 산 이무수물로부터 유도된 4가 유기기일 수 있다. Preferably, X 1 is a tetravalent organic group derived from an acid dianhydride represented by the following formula (2) or (3).
[화학식 2](2)
상기 [화학식 2]에서, A1은 탄소수 1~10의 지방족 고리 또는 방향족 고리이며, B1은 단일 결합, 치환 또는 비치환된 지방족 사슬기, 치환 또는 비치환된 지방족 고리기, 치환 또는 비치환된 방향족 고리기; 직접 또는 가교 구조를 통해 연결된 2 이상의 지방족 또는 방향족 고리기; 또는 이들의 조합이다.
Wherein A 1 is an aliphatic ring or aromatic ring having 1 to 10 carbon atoms, B 1 is a single bond, a substituted or unsubstituted aliphatic chain group, a substituted or unsubstituted aliphatic cyclic group, An aromatic ring group; Two or more aliphatic or aromatic ring groups connected either directly or via a bridging structure; Or a combination thereof.
[화학식 3](3)
상기 [화학식 3]에서, A2는 탄소수 1~10의 지방족 고리 또는 방향족 고리이며, B2는 단일 결합, 치환 또는 비치환된 지방족 사슬기, 치환 또는 비치환된 지방족 고리기, 치환 또는 비치환된 방향족 고리기; 직접 또는 가교 구조를 통해 연결된 2 이상의 지방족 또는 방향족 고리기; 또는 이들의 조합이다.
Wherein A 2 is an aliphatic ring or aromatic ring having 1 to 10 carbon atoms, B 2 is a single bond, a substituted or unsubstituted aliphatic chain group, a substituted or unsubstituted aliphatic ring group, a substituted or unsubstituted ring An aromatic ring group; Two or more aliphatic or aromatic ring groups connected either directly or via a bridging structure; Or a combination thereof.
보다 구체적으로는, 상기 X1은 하기 [화학식 4]에 표시된 화합물들로 이루어진 군으로부터 선택된 산 이무수물로부터 유도된 4가 유기기일 수 있으나, 이에 한정되는 것은 아니다. More specifically, X 1 may be, but is not limited to, a tetravalent organic group derived from an acid dianhydride selected from the group consisting of compounds represented by Formula 4 below.
[화학식 4][Chemical Formula 4]
상기 [화학식 4]에서, B1 및 B2는 각각 독립적으로 단일 결합; 치환 또는 비치환된 지방족 사슬기; 치환 또는 비치환된 지방족 고리기; 치환 또는 비치환된 방향족 고리기; 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 또는 지방족 고리기; 또는 이들의 조합이다. 바람직하게는, 상기 B1 및 B2는 각각 독립적으로, 탄소수 1 ~ 10의 알킬렌기; 탄소수 6 ~ 20의 단환식 또는 다환식 사이클로알킬렌기; 탄소수 6 ~ 20의 단환식 또는 다환식 아릴렌기; 알킬렌 구조에 의해 연결된 2 이상의 사이클로알킬기; 또는 알킬렌 구조에 의해 연결된 2 이상의 아릴기일 수 있으며, 보다 바람직하게는, 페닐렌기, 나프탈렌기, 플루오렌기, 사이클로헥실렌기, 비페닐기, 비사이클로헥실기, 트리사이클로데칸일기 또는 알킬렌 구조에 의해 연결된 비스사이클로헥실기일 수 있다.
In Formula 4, B 1 and B 2 each independently represent a single bond; A substituted or unsubstituted aliphatic chain group; A substituted or unsubstituted aliphatic cyclic group; A substituted or unsubstituted aromatic ring group; Two or more aromatic or aliphatic ring groups linked directly or through a bridging structure; Or a combination thereof. Preferably, B 1 and B 2 each independently represent an alkylene group having 1 to 10 carbon atoms; A monocyclic or polycyclic cycloalkylene group having 6 to 20 carbon atoms; A monocyclic or polycyclic arylene group having 6 to 20 carbon atoms; Two or more cycloalkyl groups linked by an alkylene structure; Or two or more aryl groups connected by an alkylene structure, and more preferably a phenylene group, a naphthalene group, a fluorene group, a cyclohexylene group, a biphenyl group, a bicyclohexyl group, a tricyclodecanyl group or an alkylene structure Lt; RTI ID = 0.0 > cyclohexyl < / RTI >
본 발명에서 상기 X1을 유도하기 위해 사용될 수 있는 산 이무수물의 구체적인 예는 다음과 같다. 다만 하기 화합물들은 본 발명에서 사용가능한 화합물들의 예시일 뿐, 본 발명이 이에 한정되는 것은 아니다.Specific examples of the acid dianhydride which can be used in the present invention to derive the X < 1 > However, the following compounds are only examples of the compounds usable in the present invention, but the present invention is not limited thereto.
(1) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 1,4-페닐렌다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,4-phenylenediyl ester),(1) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1, 5-isobenzofurancarboxylic acid, dioxo-, 1,4-phenylenediyl ester),
(2) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 1,3-페닐렌다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,3-phenylenediyl ester),(2) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,3-phenylene dicarboxylic acid, dioxo-, 1,3-phenylenediyl ester),
(3) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 1,4-사이클로헥산다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,4-cyclohexanediyl ester),(3) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,4-cyclohexanedicarboxylic acid, 1,3-dihydro- dioxo-, 1,4-cyclohexanediyl ester),
(4) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 1,3-사이클로헥산다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,3-cyclohexanediyl ester),(4) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,3-cyclohexanedicarboxylic acid, dioxo-, 1,3-cyclohexanediyl ester),
(5) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, [1,1'-비사이클로헥실]-4,4'-다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, [1,1'-bicyclohexyl]-4,4'-diyl ester),(5) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, [1,1'-bicyclohexyl] -4,4'- 1,3-dihydro-1,3-dioxo-, [1,1'-bicyclohexyl] -4,4'-diyl ester),
(6) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 트리사이클로[3.3.1.1]데칸-1,3-다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, tricycle[3.3.1.1]decane-1,3-diyl ester)(6) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, tricyclo [3.3.1.1] decane- 1,3-diyl ester dihydro-1,3-dioxo-, tricycle [3.3.1.1] decane-1,3-diyl ester)
(7) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 메틸렌디-4,1-사이클로헥실다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, methylenedi-4,1-cyclohexyldiyl ester),(7) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, methylenedi-4,1-cyclohexyl dicyl ester , 3-dioxo-, methylenedio-4,1-cyclohexyldiyl ester),
(8) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, (1-메틸에틸리덴)다이-4,1-사이클로헥실다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, (1-methylethylidend)di-4,1-cyclohexyldiyl ester),(8) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, (1-methylethylidene) 1,3-dihydro-1,3-dioxo-, (1-methylethylidene) di-4,1-cyclohexyldiyl ester)
(9) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 2,7-나프탈렌다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 2,7-naphthalenediyl ester),(9) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo -, 2,7-naphthalenediyl ester),
(10) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 2,6-나프탈렌다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 2,6-naphthalenediyl ester),(10) isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 2,6-naphthalenedicarboxylic acid, 1,3-dihydro-1,3-dioxo -, 2,6-naphthalenediyl ester),
(11) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 1,5-나프탈렌다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,5-naphthalenediyl ester),(11) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,5-naphthalenedicarboxylic acid, 1,3-dihydro- -, 1,5-naphthalenediyl ester),
(12) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 1,4-나프탈렌다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,4-naphthalenediyl ester),(12) isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 1,4-naphthalenedicarboxylic acid, 1,3-dihydro-1,3-dioxo -, 1,4-naphthalenediyl ester),
(13) 5-이소벤조퓨란 카르복시산, 1,3-디하이드로-1,3-디옥소-, 9H-플루오렌-2,7-다이일 에스테르(5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 9H-fluorene-2,7-diyl ester),(13) 5-isobenzofurancarboxylic acid, 1,3-dihydro-1,3-dioxo-, 9H-fluorene-2,7- , 3-dioxo-, 9H-fluorene-2,7-diyl ester),
(14) 에틸렌 글리콜 비스(4-트리멜리릭 언하이드라이드) 에스테르,(14) ethylene glycol bis (4-trimellitic anhydride) ester,
(15) 1, 2, 4-벤젠트리카르복시산, 사이클 1,2-언하이드라이드, 디에스테르-, 4,4'-이소프로필리덴디페논,(15) A liquid crystal composition comprising 1, 2, 4-benzenetricarboxylic acid, cyclic 1,2-anhydride, diester-, 4,4'-
(16) 4,4'-옥시디프탈릭다이언하이드라이드, (16) 4,4'-oxydiphthalic dianhydride,
(17) 2,2-비스[4-(2,3-디카르복시페녹시)페닐]프로판 다이언하이드라이드,(17) Synthesis of 2,2-bis [4- (2,3-dicarboxyphenoxy) phenyl] propanedialdehyde,
(18) 2,2-비스[4-(3,4-디카르복시페녹시)페닐]프로판 다이언하이드라이드,(18) 2,2-bis [4- (3,4-dicarboxyphenoxy) phenyl] propane dianhydride,
(19) 4,4'-(3,4-디카르복시페녹시)디페닐술파이드 다이언하이드라이드,(19) Synthesis of 4,4 '- (3,4-dicarboxyphenoxy) diphenyl sulfide dianhydride,
(20) 1,1,1,3,3,3-헥사플루오로-2,2-비스[4-(2,3-디카르복시페녹시)페닐]프로판 다이언하이드라이드,(20) Synthesis of 1,1,1,3,3,3-hexafluoro-2,2-bis [4- (2,3-dicarboxyphenoxy) phenyl] propanedial hydride,
(21) 1,1,1,3,3,3-헥사플루오로-2,2-비스[4-(3,4-디카르복시페녹시)페닐]프로판 다이언하이드라이드.
(21) 1,1,1,3,3,3-Hexafluoro-2,2-bis [4- (3,4-dicarboxyphenoxy) phenyl] propanedial hydride.
한편, 본 발명에서 사용되는 폴리이미드 공중합체는, 폴리이미드 공중합체의 열적 성질, 위상차값, 기계적 물성 및/또는 광학 특성을 제어하기 위해, 상기 X1이 유도되는 산 이무수물(편의상 제1산 이무수물이라 함)과 상이한 종류의 산 이무수물(편의상, 제2산 이무수물이라 함)로부터 유도되는 4가 유기기 X2를 더 포함할 수 있다.
On the other hand, the polyimide copolymer used in the present invention, polyimide in order to control the thermal properties, a phase difference value, the mechanical properties and / or optical properties of the copolymer, the acid dianhydride that the X 1 is induced (for convenience the first acid dianhydride 4 which is derived from the term water quot;) different kind of dianhydride (for convenience, the second dianhydride) may further include an organic group X 2.
예를 들면, 상기 X2는 치환 또는 비치환된 지방족 사슬기; 치환 또는 비치환된 지방족 고리기; 치환 또는 비치환된 방향족 고리기; 2 이상의 방향족 또는 지방족 고리가 직접 또는 가교 구조로 연결된 구조; 또는 이들의 조합을 포함하는 산 이무수물로부터 유도되는 4가 유기기일 수 있다.
For example, X 2 is a substituted or unsubstituted aliphatic chain group; A substituted or unsubstituted aliphatic cyclic group; A substituted or unsubstituted aromatic ring group; A structure wherein two or more aromatic or aliphatic rings are linked directly or in a bridged structure; Or a tetravalent organic group derived from an acid dianhydride containing a combination thereof.
상기 X2를 유도하기 위해 사용되는 제2산 이무수물은, 제1산 이무수물과 다르기만 하면 되고, 그 종류가 특별히 한정되지 않는다. 즉, 상기 제2산 이무수물로는, 지방족 산 이무수물, 지환족 산 이무수물, 방향족 산 이무수물들과 같이 당해 기술 분야에 알려져 있는 다양한 종류의 산 이무수물들이 제한없이 사용될 수 있으며, 이로써 제한되는 것은 아니나, 예를 들면, 4,4'-옥시디프탈릭다이언하이드라이드, 1,2,3,4-사이클로부탄테트라카르복실릭 다이언하이드라이드, 1,2,3,4-사이클로펜탄테트라카르복실릭 다이언하이드라이드, 1,2,4,5-사이클로헥산테트라카르복실릭 다이언하이드라이드, 비사이클로펜탄테트라카르복실릭 다이언하이드라이드, 사이클로프로판테트라카르복실릭 다이언하이드라이드, 3,3',4,4'-벤조페논테트라카르복실릭 다이언하이드라이드, 3,4,9,10-페릴렌테트라카르복실릭 다이언하이드라이드, 4,4'-술포닐디프탈릭 다이언하이드라이드, 3,3',4,4'-비페닐테트라카르복실릭 다이언하이드라이드, 1,2,5,6-나프탈렌테트라카르복실릭 다이언하이드라이드, 1,4,5,8-나프탈렌테트라카르복실릭 다이언하이드라이드, 2,3,5,6-피리딘테트라카르복실릭 언하이드라이드, m-터페닐-3,3',4,4'-테트라카르복실릭 다이언하이드라이드, p-터페닐-3,3',4,4'-테트라카르복실릭 다이언하이드라이드 및 이들의 혼합물로 이루어진 군으로부터 선택되는 것일 수 있다.
The second acid dianhydride used to derive X 2 may be different from the first acid dianhydride, and the kind thereof is not particularly limited. That is, as the second acid dianhydride, various kinds of acid dianhydrides known in the art, such as an aliphatic acid dianhydride, an alicyclic dianhydride, an aromatic acid dianhydride, can be used without limitation, But not limited to, for example, 4,4'-oxydiphthalic dianhydride, 1,2,3,4-cyclobutane tetracarboxylic dianhydride, 1,2,3,4-cyclopentanetetracarboxyl Cyclohexanetetracarboxylic dianhydride, cyclopropane tetracarboxylic dianhydride, 3,3 ', 4 < RTI ID = 0.0 > , 4'-benzophenone tetracarboxylic dianhydride, 3,4,9,10-perylene tetracarboxylic dianhydride, 4,4'-sulfonyldiphthalic dianhydride, 3,3 '4,4'-biphenyltetracarboxylate Naphthalene tetracarboxylic dianhydride, 1,2,5,6-naphthalene tetracarboxylic dianhydride, 1,4,5,8-naphthalene tetracarboxylic dianhydride, 2,3,5,6-pyridine tetracarboxylic dianhydride, M-terphenyl-3,3 ', 4,4'-tetracarboxylic dianhydride, p-terphenyl-3,3', 4,4'-tetracarboxylic dianhydride Rides, and mixtures thereof.
다음으로, 상기 폴리이미드 공중합체에 있어서, 상기 Q1 및 Q2는 각각 독립적으로 디아민으로부터 유도되는 2가 유기기이며, 바람직하게는, 예를 들면, 탄소수 1~10의 지방족 사슬; 1~5개의 방향족 고리; 1~5개의 지방족 고리; 에테르기; 에스테르기; 또는 이들의 조합을 포함하는 디아민으로부터 유도된 2가 유기기일 수 있다. 이때, 상기 Q1 및 Q2는 서로 동일하거나 상이할 수 있다.
Next, in the above polyimide copolymer, Q 1 and Q 2 are each independently a divalent organic group derived from a diamine, preferably an aliphatic chain having 1 to 10 carbon atoms; 1 to 5 aromatic rings; 1 to 5 aliphatic rings; Ether group; An ester group; Or a combination thereof. ≪ / RTI > Here, Q 1 and Q 2 may be the same or different from each other.
한편, 본 발명에서 사용가능한 디아민 화합물은 특별히 제한되지 않으며, 당해 기술 분야에서 일반적으로 사용되는 방향족 디아민, 지환족 디아민 또는 지방족 디아민들이 제한없이 사용될 수 있다.
The diamine compounds usable in the present invention are not particularly limited, and aromatic diamines, alicyclic diamines or aliphatic diamines generally used in the art can be used without limitation.
예를 들면, 상기 Q1 및 Q2는 각각 독립적으로 하기 [화학식 5]에 표시되는 화합물들로 이루어진 군으로부터 선택된 디아민으로부터 유도된 2가 유기기일 수 있다.For example, Q 1 and Q 2 may each independently be a divalent organic group derived from a diamine selected from the group consisting of compounds represented by the following formula (5).
[화학식 5][Chemical Formula 5]
이때, 상기 [화학식 5]에서, 상기 R1 내지 R7은 각각 독립적으로, 치환 또는 비치환된 지방족 사슬기; 치환 또는 비치환된 지방족 고리기; 치환 또는 비치환된 방향족 고리기; 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 또는 지방족 고리기; 또는 이들의 조합이며, R8 내지 R11은 각각 독립적으로, 탄소수 1 내지 10 알킬기, 탄소수 1 내지 10의 할로알킬기 또는 히드록시기이고, q는 1~8인 정수이다.
In the formula (5), each of R 1 to R 7 independently represents a substituted or unsubstituted aliphatic chain group; A substituted or unsubstituted aliphatic cyclic group; A substituted or unsubstituted aromatic ring group; Two or more aromatic or aliphatic ring groups linked directly or through a bridging structure; And R 8 to R 11 are each independently a C 1-10 alkyl group, a haloalkyl group having 1 to 10 carbon atoms or a hydroxy group, and q is an integer of 1 to 8.
경제성 및 필름의 물성 등을 감안할 때, 상기 Q1 및 Q2 중 적어도 하나는, 상기 [화학식 5] 중 5(e), 5(f) 및 5(h)로 표시되는 화합물들로 이루어진 군으로부터 선택된 1종 이상(이하, 편의상 제1디아민이라 함)인 것이 바람직하다. 보다 바람직하게는, 상기 Q1은 제1디아민 화합물로부터 유도된 2가 유기기일 수 있으며, 보다 더 바람직하게는 상기 Q1 및 Q2 모두 제1디아민 화합물로부터 유도된 2가 유기기일 수 있다.
Given such properties of the economy and the film, at least one of the Q 1 and Q 2 are, the from the [Formula 5] of 5 (e), 5 (f ) and 5 (h) the group consisting of the compounds represented by (Hereinafter, referred to as a first diamine for convenience). More preferably, Q 1 may be a divalent organic group derived from a first diamine compound, more preferably Q 1 And Q 2 may all be a divalent organic group derived from the first diamine compound.
보다 구체적으로는, 상기 제1디아민 화합물은, 2,2-비스(3-아미노-4-히드록시페닐)헥사플루오로프로판, 4,4'-디아미노디페닐에테르, 4,4'-디아미노디페닐술파이드, 4,4'-디아미노페닐술폰, 4,4'-디아미노벤조페논, 4,4'-비스(4-아미노페닐술포닐)디페닐에테르, 3,3'-디아미노 디페닐에테르, 3,3'-디아미노 디페닐술파이드, 3,3'-디아미노디페닐술폰, 2,2'-비스(트리플루오로메틸)-4,4'-디아미노비페닐, 4,4'-메틸렌비스(사이클로헥실아민), 3,3'-디아미노벤조페논, 4,4'-메틸렌비스(2-메틸사이클로헥실아민), 비스(3-아미노페닐)술페이드, 및 이들의 혼합물로 이루어진 군으로부터 선택될 수 있으나, 이에 한정되는 것은 아니다.
More specifically, the first diamine compound may be at least one selected from the group consisting of 2,2-bis (3-amino-4-hydroxyphenyl) hexafluoropropane, 4,4'-diaminodiphenyl ether, 4,4'-diaminobenzophenone, 4,4'-bis (4-aminophenylsulfonyl) diphenyl ether, 3,3'-dia Aminodiphenyl ether, 3,3'-diaminodiphenyl sulfide, 3,3'-diaminodiphenyl sulfone, 2,2'-bis (trifluoromethyl) -4,4'-diaminobiphenyl , 4,4'-methylenebis (cyclohexylamine), 3,3'-diaminobenzophenone, 4,4'-methylenebis (2-methylcyclohexylamine) And mixtures thereof, but are not limited thereto.
보다 구체적으로는, 상기 Q1 및 Q2 중 적어도 하나는, 하기 [화학식 6]로 표시되는 작용기들로 이루어진 군으로부터 선택된 1종 이상일 수 있으며, 보다 바람직하게는, 상기 Q1은 하기 [화학식 6]로 표시되는 작용기들로 이루어진 군으로부터 선택된 1종 이상일 수 있고, 보다 더 바람직하게는 상기 Q1 및 Q2는 하기 [화학식 6]로 표시되는 작용기들로 이루어진 군으로부터 선택된 1종 이상일 수 있다.More specifically, at least one of Q 1 and Q 2 may be at least one selected from the group consisting of the functional groups represented by the following formula (6), more preferably the above Q 1 is represented by the following formula ], And still more preferably Q 1 and Q 2 may be at least one kind selected from the group consisting of functional groups represented by the following formula (6).
[화학식 6][Chemical Formula 6]
상기 [화학식 6]에서, R12는 -0-, -CR13R14-(이때, R13 및 R14는 각각 독립적으로 수소원자, 탄소수 1 내지 10의 알킬기 및 탄소수 1 내지 10의 할로알킬기(예를 들면, 트리플루오로메틸기)로 이루어진 군으로부터 선택되는 것임), -C(=O)-, -C(=O)O-, -C(=O)NH-, -S-, -S0-, -SO2-, -O[CH2CH2O]P-(이때, p는 1~20인 정수), 탄소수 6 내지 19의 단환식 또는 다환식 시클로알킬렌기(예를 들면, 사이클로헥실렌기), 탄소수 6 내지 19의 단환식 또는 다환식 아릴렌기(예를 들면, 페닐렌기, 나프탈렌기 등) 및 이들의 조합으로 이루어진 군에서 선택되는 것이다.
The [Formula 6] in, R 12 is -0-, -CR 13 R 14 - (wherein, R 13 and R 14 each independently represent a hydrogen atom, a haloalkyl group having 1 to 10 carbon atoms and an alkyl group having 1 to 10 carbon atoms in the ( (= O) -, -C (= O) O-, -C (= O) NH-, -S-, -S0 -, -SO 2 -, -O [CH 2 CH 2 O] P - (wherein p is an integer of 1 to 20), a monocyclic or polycyclic cycloalkylene group having 6 to 19 carbon atoms (for example, cyclohexyl A silylene group), a monocyclic or polycyclic arylene group having 6 to 19 carbon atoms (e.g., a phenylene group, a naphthalene group, etc.), and combinations thereof.
또한, 상기 Q1 및 Q2 중 적어도 하나는 에스테르기, 에테르기 또는 이들의 조합을 함유하는 방향족 또는 지환족 디아민 화합물(편의상, 제2디아민이라 함)로부터 유도된 2가 유기기일 수 있다. 예를 들면, 상기 제2디아민은 하기 [화학식 5] 중 5(a) ~ 5(d) 및 5(g)로 표시되는 화합물들로 이루어진 군으로부터 선택된 1종 이상일 수 있다.
The above Q 1 and Q 2 medium At least one of which may be a divalent organic group derived from an aromatic or alicyclic diamine compound (conveniently referred to as a second diamine) containing an ester group, an ether group or a combination thereof. For example, the second diamine may be at least one compound selected from the group consisting of compounds represented by 5 (a) to 5 (d) and 5 (g) in the following formula 5.
보다 구체적으로는, 상기 제2디아민 화합물은, 2,2-비스[4-(4-아미노페녹시)페닐]프로판, 2,2-비스[4-(4-아미노페녹시)페닐]-1,1,1,3,3,3-헥사플루오로프로판, 1,3-비스(4-아미노페녹시)페닐)벤젠, 4,4'-비스(4-아미노페녹시)비페닐, 비스[4-(4-아미노페녹시)페닐]케톤, 비스[4-(4-아미노페녹시)페닐]술폭사이드, 비스[4-(4-아미노페녹시)페닐]술폰, 비스[4-(4-아미노페녹시)페닐]에테르, 4,4'-비스[4-아미노티오페녹시)디페닐술폰, 1,4-비스[4-(4-아미노페녹시)벤조일]벤젠, 비스[4-(3-아미노페녹시)-페닐]메탄, 2,2-비스[4-(3-아미노페녹시)페닐]프로판, 2,2-비스[4-(3-아미노페녹시)페닐-1,1,1,3,3,3-헥사플루오로프로판, 1,3-비스(3-아미노페녹시)벤젠, 4,4'-비스(3-아미노페녹시)비페닐, 비스[4-(3-아미노페녹시)페닐]케톤, 비스[4-(3-아미노페녹시)페닐]술파이드, 비스[4-(3-아미노페녹시)페닐]술폰, 비스[4-(3-아미노페녹시)페닐]에테르, 4,4'-비스[3-아미노티오페녹시)디페닐술폰, 1,4-비스[4-(3-아미노페녹시)벤조일]벤젠, O,O'-비스(2-아미노프로필)폴리프로필렌글리콜 및 이들의 혼합물로 이루어진 군으로부터 선택된 것일 수 있으나, 이에 한정되는 것은 아니다.
More specifically, the second diamine compound may be selected from the group consisting of 2,2-bis [4- (4-aminophenoxy) phenyl] propane, 2,2- , 1,1,3,3,3-hexafluoropropane, 1,3-bis (4-aminophenoxy) phenyl) benzene, 4,4'-bis (4-aminophenoxy) Bis [4- (4-aminophenoxy) phenyl] sulfone, bis [4- (4-aminophenoxy) benzoyl] benzene, bis [4-aminophenoxy) phenyl] Phenyl] propane, 2,2-bis [4- (3-aminophenoxy) phenyl-1, , 1,1,3,3,3-hexafluoropropane, 1,3-bis (3-aminophenoxy) benzene, 4,4'-bis (3-aminophenoxy) biphenyl, bis [4- (3-aminophenoxy) phenyl] ketone, bis [4- (3-aminophenoxy) phenyl] sulfide, bis [4- Bis [4- (3-aminophenoxy) phenyl] ether, 4,4'-bis [3-aminothiophenoxy) diphenyl sulfone, ) Benzoyl] benzene, O, O'-bis (2-aminopropyl) polypropylene glycol, and mixtures thereof.
보다 구체적으로는, 상기 Q1 및 Q2 중 적어도 하나는 하기 [화학식 7]로 표시되는 작용기들로 이루어진 군으로부터 선택된 1종 이상일 수 있으며, 보다 바람직하게는, 상기 Q2는 하기 [화학식 7]으로 표시되는 작용기들로 이루어진 군으로부터 선택된 1종 이상일 수 있다.
More specifically, Q 1 and Q 2 medium At least one of them may be at least one selected from the group consisting of functional groups represented by the following formula (7), more preferably Q 2 is at least one selected from the group consisting of the functional groups represented by the following formula Or more.
[화학식 7](7)
상기 화학식 7에서, q는 1 내지 8의 정수임.
In Formula (7), q is an integer of 1 to 8.
상기와 같이, Q1 및 Q2 중 적어도 하나가 에스테르, 에테르 또는 이들의 조합을 포함하는 제2디아민 화합물로부터 유도되는 경우, 저비점 용매에 대한 용해도 및 접착제와의 접착력을 더욱 향상시키는 효과를 얻을 수 있다.
As described above, Q 1 and Q 2 Is derived from a second diamine compound containing an ester, an ether or a combination thereof, the solubility in a low-boiling solvent and the adhesive strength with an adhesive can be further improved.
상기와 같은 구조를 갖는 본 발명의 폴리이미드 공중합체는 당해 기술 분야에 잘 알려진 폴리이미드 공중합체의 합성 방법을 통해 제조될 수 있으며, 이로써 한정되는 것은 아니나, 예를 들면, 디아민 화합물을 유기 용매에 용해시킨 후, 결과로 수득된 용액에 산 이무수물을 첨가하여 중합 반응시켜 폴리이미드 전구체를 제조한 후, 상기 폴리이미드 전구체를 용액 용융 중합방법으로 중합시켜 제조하거나, 또는 디아민 및 산 무수물을 유기 용매에 용해시킨 후, 촉매 존재 하에서 중합시켜 전구체인 폴리아믹산을 거치지 않고 폴리이미드 공중합체를 직접 제조할 수도 있다.
The polyimide copolymer of the present invention having the above structure can be produced by a method of synthesizing a polyimide copolymer that is well known in the art and includes, but is not limited to, for example, a method in which a diamine compound is dissolved in an organic solvent Dissolving the polyimide precursor in an organic solvent, dissolving the polyimide precursor in the solution, adding an acid dianhydride to the resultant solution to cause a polymerization reaction to prepare a polyimide precursor, and polymerizing the polyimide precursor with a solution melt polymerization method, And then polymerized in the presence of a catalyst to directly prepare the polyimide copolymer without passing through the precursor polyamic acid.
이때, 상기 디아민 화합물 및/또는 산 이무수물은 각각 1종 또는 2종 이상을 혼합하여 사용할 수 있으며, 2종 이상의 디아민 화합물 및/또는 산 이무수물을 반응물로 사용할 경우에, 각 화합물의 함량비는 최종적으로 제조되는 폴리이미드 공중합체에서 각각의 산 무수물 및 디아민 화합물로부터 유도되는 작용기의 비율을 고려하여 적절하게 조절될 수 있다.
The diamine compound and / or acid dianhydride may be used alone or in combination of two or more. When two or more diamine compounds and / or acid dianhydride are used as a reactant, the content ratio of each compound is Can be suitably adjusted in consideration of the ratio of the functional groups derived from the respective acid anhydrides and diamine compounds in the finally produced polyimide copolymer.
한편, 폴리아미드 전구체를 거쳐 폴리이미드 공중합체를 제조할 경우, 상기 중합 반응은 무수 조건에서 실시될 수 있다. 또한, 상기 폴리이미드 전구체 중합 반응 시의 온도는 25℃ 내지 50℃ 정도, 바람직하게는, 40℃ 내지 45℃ 정도일 수 있으며, 용액 용융 중합 시의 온도는 130℃ 내지 200℃, 바람직하게는 150℃ 내지 180℃ 정도일 수 있다.
On the other hand, when the polyimide copolymer is produced through the polyamide precursor, the polymerization reaction can be carried out under anhydrous conditions. The temperature for the polymerization reaction of the polyimide precursor may be about 25 캜 to 50 캜, preferably about 40 캜 to 45 캜, and the temperature for solution melt polymerization is preferably 130 캜 to 200 캜, To 180 < 0 > C.
한편, 반응물로부터 폴리이미드 공중합체를 직접 제조할 경우, 상기 촉매는 비점이 60℃ ~ 100℃인 촉매인 것이 바람직하며, 예를 들면, N,N-디에틸메틸아민, N,N-디메틸이소프로필아민, N-메틸피롤리딘, 피롤리딘 및 트리에틸아민으로 이루어진 군으로부터 선택되는 1종 이상일 수 있다. 한편, 상기 촉매는 반응물인 디아민 및 산 이무수물의 함량의 합 100중량부에 대하여, 0.5 ~ 30중량부 정도의 함량으로 포함되는 것이 바람직하며, 이때 중합 온도는 120℃ 내지 200℃ 정도인 것이 바람직하다.
On the other hand, when the polyimide copolymer is directly produced from the reaction product, the catalyst is preferably a catalyst having a boiling point of 60 ° C to 100 ° C, for example, N, N-diethylmethylamine, N, Propylamine, N-methylpyrrolidine, pyrrolidine, and triethylamine. Preferably, the catalyst is contained in an amount of about 0.5 to 30 parts by weight based on 100 parts by weight of the sum of the contents of diamines and acid dianhydrides, and the polymerization temperature is preferably about 120 to 200 ° C .
한편, 상기 폴리이미드 공중합체의 제조에 사용되는 유기 용매로는, N,N-디메틸아세트아미드(DMAc), N-메틸피롤리돈(NMP), N,N-디메틸포름아미드(DMF), 1,3-디메틸-2-이미다졸리디논, N,N-디에틸아세트아미드(DEAc), N,N-디메틸메톡시아세트아미드, 디메틸술폭사이드, 피리딘, 디메틸술폰, 헥사메틸포스포아미드, 테트라메틸우레아, N-카프로락탐, 테트라하이드로퓨란, m-디옥산, p-디옥산, 1,2-디메톡시에탄, 비스(2-메톡시에틸)에테르, 1,2-비스(2-메톡시에틸)에탄, 비스[2-(2-메톡시에톡시)]에테르, 폴리(에틸렌글리콜)메타크릴레이트(PMGMA), γ-부티로락톤(GBL), 에크아미드(Equamide M100, Idemitsu Kosan Co., Ltd)와 같은 아미드계 용매, 물 및 이들의 혼합물로 이루어진 군으로부터 선택되는 것을 사용할 수 있다.
Examples of the organic solvent used for preparing the polyimide copolymer include N, N-dimethylacetamide (DMAc), N-methylpyrrolidone (NMP), N, N-dimethylformamide , N, N-diethylacetamide (DEAc), N, N-dimethylmethoxyacetamide, dimethylsulfoxide, pyridine, dimethylsulfone, hexamethylphosphoramide, tetra (2-methoxyethyl) ether, 1,2-bis (2-methoxyethyl) ether, 1,2-dimethoxyethane, 1,2-dimethoxyethane, Ethyl) ethane, bis [2- (2-methoxyethoxy)] ether, poly (ethylene glycol) methacrylate (PMGMA), gamma -butyrolactone (GBL), equamide M100, Idemitsu Kosan Co. , Ltd), water and mixtures thereof can be used.
상기와 같은 방법으로 제조된 본 발명의 폴리이미드 공중합체는, 10,000g/mol 이상의 중량평균분자량을 갖는 것이 바람직할 수 있으며, 보다 바람직하게는 10,000g/mol 내지 100,000g/mol의 중량평균분자량을 갖는 것일 수 있다. 폴리이미드 공중합체의 분자량이 10,000g/mol 미만이면 기계적 물성이 저하될 우려가 있기 때문이다.
The polyimide copolymer of the present invention produced by the above process may have a weight average molecular weight of 10,000 g / mol or more, more preferably 10,000 to 10,000 g / mol, . If the molecular weight of the polyimide copolymer is less than 10,000 g / mol, the mechanical properties may deteriorate.
또한, 상기 본 발명의 폴리이미드 공중합체는, 25℃에서, 상기 비점이 80℃ 내지 200℃인 유기 용매 100g에 대한 용해도가 1% 내지 60%정도, 바람직하게는 5% 내지 40% 정도, 더 바람직하게는 10% 내지 30% 정도일 수 있다. 저비점 유기 용매에 대한 용해도가 상기 수치범위를 만족할 경우, 제막 시에 우수한 가공성 및 코팅성을 확보할 수 있기 때문이다.
The polyimide copolymer of the present invention preferably has a solubility of about 1% to about 60%, preferably about 5% to about 40%, more preferably about 5% to about 40%, at 25 ° C in an organic solvent having a boiling point of 80 ° C to 200 ° C And preferably about 10% to 30%. When the solubility in the low-boiling organic solvent is in the above range, excellent workability and coating properties can be ensured at the time of film formation.
또한, 상기 본 발명의 폴리이미드 공중합체는, 중합시 이미드 전환율이 90% 이상, 바람직하게는 90% 내지 100%인 것이 바람직하다. 이미드 전환율이 상기 수치 범위를 만족할 경우, 저비점의 용매에 대한 가용성이 향상되기 때문에, 폴리이미드 수지 자체를 이용하여 코팅층을 형성할 수 있을 뿐 아니라, 코팅 용매로 비점이 낮은 용매를 사용할 수 있게 된다, 또한, 미전환 전구체로 인해 기계적 강도나 광학 특성이 저하되는 것도 방지할 수 있다.
The polyimide copolymer of the present invention preferably has an imide conversion of 90% or more, and preferably 90% to 100% at the time of polymerization. When the imide conversion ratio satisfies the above-described numerical range, solubility in a solvent having a low boiling point is improved, so that not only a coating layer can be formed using the polyimide resin itself but a solvent having a low boiling point can be used as a coating solvent , And it is also possible to prevent the deterioration of the mechanical strength and optical characteristics due to the unconverted precursor.
한편, 상기 본 발명의 폴리이미드 공중합체는 유리전이온도가 170℃ 내지 280℃ 정도, 바람직하게는 170℃ 내지 270℃, 더 바람직하게는 170℃ 내지 250℃일 수 있다. 폴리이미드 공중합체의 유리전이온도가 상기 수치 범위를 만족할 경우, 내열성이 우수하다는 장점이 있다.
On the other hand, the polyimide copolymer of the present invention may have a glass transition temperature of about 170 ° C to 280 ° C, preferably 170 ° C to 270 ° C, and more preferably 170 ° C to 250 ° C. When the glass transition temperature of the polyimide copolymer satisfies the above-described numerical range, there is an advantage that the heat resistance is excellent.
한편, 본 발명의 상기 코팅층은 두께가 10㎛이하인 것이 바람직하며, 예를 들면, 1㎛ 내지 8㎛ 또는 1㎛ 내지 6㎛ 정도일 수 있다. 본 발명의 경우 코팅층 역시 이와 같이 박형인 것을 특징으로 하며, 두께가 상기 범위보다 두꺼운 경우에는 이를 포함하는 위상차 필름의 박형 경량화에 어려움이 있을 뿐만 아니라, 원하는 범위보다 위상차가 크게 발현될 수 있다는 문제점이 있다.
On the other hand, the coating layer of the present invention preferably has a thickness of 10 탆 or less, for example, 1 탆 to 8 탆 or 1 탆 to 6 탆. In the case of the present invention, the coating layer is also thin as described above. When the thickness is thicker than the above range, it is difficult to reduce the thickness and weight of the retardation film including the retardation film, .
2. 2. 위상차Phase difference 필름의 제조 방법 Method of manufacturing film
다음으로 본 발명의 상기 위상차 필름의 제조 방법에 대해 설명한다.
Next, a method for producing the retardation film of the present invention will be described.
본 발명의 위상차 필름의 제조 방법은, 부의 위상차 물질을 포함하는 기재 필름을 제조하는 단계; 및 상기 기재 필름의 적어도 일면에 상기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체를 포함하는 코팅층을 형성하는 단계를 포함한다.
A manufacturing method of a retardation film of the present invention comprises the steps of: preparing a base film comprising a negative retardation material; And forming a coating layer comprising a polyimide copolymer containing at least one repeating unit represented by the formula (1) on at least one side of the base film.
보다 구체적으로는, 본 발명의 위상차 필름의 제조 방법은, 부의 위상차 필름을 포함하는 미연신 기재 필름을 준비하는 단계; 상기 미연신 기재 필름을 연신하는 단계; 상기 연신 처리된 기재 필름의 적어도 일면에 상기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체를 포함하는 미연신 코팅층을 형성하는 단계; 및 상기 미연신 코팅층이 형성된 기재 필름을 연신하는 단계를 포함할 수 있다.
More specifically, the method for producing a retardation film of the present invention comprises the steps of: preparing an unstretched base film comprising a negative retardation film; Stretching the unstretched base film; Forming an unstretched coating layer comprising a polyimide copolymer containing at least one repeating unit represented by the formula (1) on at least one surface of the stretched substrate film; And stretching the base film on which the non-stretched coating layer is formed.
이때, 상기 미연신 기재 필름을 연신하는 단계는 길이 방향(MD)으로의 일축 연신이고, 상기 미연신 코팅층이 형성된 기재 필름을 연신하는 단계는 폭 방향(TD)으로의 일축 연신인 것이 보다 바람직하다. 이 경우 기재 필름은 길이 방향(MD) 및 폭 방향(TD)으로 이축 연신 처리가 되고, 코팅층은 폭 방향(TD)으로 일축 연신 처리가 되며, 그 결과 간단한 방법으로 IPS 모드에 적합한 위상차를 구현할 수 있다.
At this time, the step of stretching the unstretched base film is uniaxial stretching in the longitudinal direction (MD), and the step of stretching the base film in which the unoriented coating layer is formed is more preferably uniaxially stretched in the transverse direction (TD) . In this case, the base film is subjected to the biaxial stretching process in the longitudinal direction (MD) and the width direction (TD), and the coating layer is uniaxially stretched in the width direction (TD). As a result, a phase difference suitable for the IPS mode can be realized have.
가. 기재 필름 제조 단계end. Base film production step
미연신 기재 필름은 상술한 부의 위상차 물질을 이용하여 당해 기술 분야에 잘 알려진 필름 성형 방법, 예를 들면, 압출 성형, 용액 캐스팅, 캘린더 성형, 필름 유연법 등을 이용하여 제조함으로써 준비할 수도 있으며, 또는 부의 위상차 물질을 포함하는 시판되는 미연신 기재 필름을 사용하여도 무방하다.
The unstretched base film may be prepared by a film forming method well known in the art, for example, extrusion molding, solution casting, calender molding, film casting, or the like, using the negative retardation material described above, Or a commercially available unoriented substrate film containing a negative retardation material may be used.
한편, 상기 미연신 기재 필름의 길이 방향(MD)으로의 일축 연신은 1.1 내지 4.0 배, 보다 바람직하게는 1.2 내지 3.5 배의 연신 배율로 수행될 수 있다. 연신비가 상기 범위 미만인 경우에는 필름의 인성이 저하되어, 제조된 위상차 필름이 편광판에 적용하기 어려울 수 있으며, 연신비가 상기 범위를 초과하는 경우는 연신 과정에서 필름의 파단이 발생할 수 있어, 안정적인 필름 생산이 어려울 수 있다. 연신 방법은 특별히 한정되지 않으며, 당해 기술분야에서 널리 알려진 연신 방법으로 수행될 수 있다. 예컨대, 상기 길이 방향(MD)으로의 연신은 롤간 연신 방법, 압축 연신 방법 등을 이용할 수 있다.
On the other hand, the uniaxial stretching in the longitudinal direction (MD) of the unstretched base film may be performed at a draw magnification of 1.1 to 4.0 times, more preferably 1.2 to 3.5 times. When the stretching ratio is less than the above range, the toughness of the film is lowered, and the produced retardation film may be difficult to apply to the polarizing plate. If the stretching ratio exceeds the above range, the film may be broken during stretching, This can be difficult. The stretching method is not particularly limited and may be carried out by a stretching method well known in the art. For example, in the stretching in the longitudinal direction (MD), a roll-to-roll stretching method, a compression stretching method, or the like can be used.
또한, 상기 미연신 기재 필름의 길이 방향(MD)으로의 일축 연신은 기재 필름의 유리전이온도를 Tg라 할 때, (Tg-20)℃ 내지 (Tg+30)℃의 온도, 보다 바람직하게는 (Tg)℃ 내지 (Tg+20)℃ 또는 (Tg)℃ 내지 (Tg+15)℃ 정도의 온도에서 수행될 수 있다. 상기 유리전이온도는 시차주사형 열량계(DSC)에 의해 측정될 수 있다. 예컨대, 시차주사형 열량계(DSC)를 이용하는 경우, 약 10mg의 시료를 전용 팬(pan)에 밀봉하고 일정 승온 조건으로 가열할 때 상변이가 일어남에 따른 물질의 흡열 및 발열량을 온도에 따라 그려 유리전이온도를 측정할 수 있다.
The uniaxially stretching in the longitudinal direction (MD) of the unstretched base film is preferably conducted at a temperature of (Tg-20) DEG C to (Tg + 30) DEG C, more preferably (Tg) ° C to (Tg + 20) ° C or (Tg) ° C to (Tg + 15) ° C. The glass transition temperature can be measured by a differential scanning calorimeter (DSC). For example, in the case of using a differential scanning calorimeter (DSC), when a sample of about 10 mg is sealed in a dedicated pan and heated at a constant temperature, the amount of endothermic heat The transition temperature can be measured.
나. 코팅층 형성 단계I. Coating layer formation step
미연신 코팅층을 형성하는 방법은 특별히 한정되지 않으며 당해 기술분야에서 널리 알려진 방법을 이용할 수 있다. 예컨대, 폴리이미드 공중합체와 용매를 포함하는 코팅층 형성 조성물을 마이크로 그라비아 코팅법, 콤마 코팅법, 바 코팅법, 롤러 코팅법, 스핀 코팅법, 프린트법, 딥 코팅법, 유연 성막법, 다이 코팅법, 블레이드 코팅법, 그라비아 인쇄 법 등의 방법을 이용하여 도포하여 건조하는 방법으로 수행될 수 있다.
The method of forming the non-stretched coating layer is not particularly limited and a method well known in the art can be used. For example, a coating layer-forming composition comprising a polyimide copolymer and a solvent may be coated by a microgravure coating method, a comma coating method, a bar coating method, a roller coating method, a spin coating method, a printing method, a dip coating method, , A blade coating method, a gravure printing method, and the like, followed by drying.
이때, 상기 폴리이미드 공중합체에 대한 구체적인 내용은 상기한 바와 동일하며, 사용 가능한 용매로는 메틸렌클로라이드, 클로로포름, 테트라하이드로퓨란(THF), 1,3-디옥살레인, 시클로펜타논, 시클로헥사논, N-메틸 피롤리돈(NMP), 디메틸폼아마이드(DMF), 디메틸아세트아마이드(DMAc), 메틸에틸케톤(MEK), 톨루엔, 에탄올, 메탄올 등의 알코올류, 물 등을 들 수 있다. 이들 용매는 단독으로 이용해도 되고 2종 이상을 병행해도 된다. 건조 조건 등도 특별히 한정되지 않으며, 예를 들면, 열풍이나 IR 히터 등을 이용하여 기재 필름의 위상차가 변하지 않는 범위 내에서 온도 및 시간을 조절하여 건조할 수 있다.
The specific examples of the polyimide copolymer are the same as those described above. Examples of usable solvents include methylene chloride, chloroform, tetrahydrofuran (THF), 1,3-dioxolane, cyclopentanone, cyclohexanone , N-methylpyrrolidone (NMP), dimethylformamide (DMF), dimethylacetamide (DMAc), methyl ethyl ketone (MEK), alcohols such as toluene, ethanol and methanol and water. These solvents may be used alone or in combination of two or more. The drying conditions and the like are not particularly limited. For example, hot air or an IR heater can be used to adjust the temperature and time within the range in which the retardation of the base film does not change.
한편, 상기 미연신 코팅층이 형성된 기재 필름의 폭 방향(TD)으로의 일축 연신은 1.1 내지 4.0 배, 보다 바람직하게는 1.5 내지 3.5 배의 연신 배율로 수행될 수 있다. 연신비가 상기 범위 미만인 경우에는 필름의 인성이 저하되어, 제조된 위상차 필름이 편광판에 적용하기 어려울 수 있으며, 연신비가 상기 범위를 초과하는 경우는 연신 과정에서 필름의 파단이 발생할 수 있어, 안정적인 필름 생산이 어려울 수 있다. 연신 방법은 특별히 한정되지 않으며, 예컨대 텐터 연신기를 이용하는 방법 등 당해 기술분야에서 널리 알려진 연신 방법으로 수행될 수 있다.
On the other hand, the uniaxial stretching in the width direction (TD) of the base film on which the non-stretched coating layer is formed can be performed at a draw magnification of 1.1 to 4.0 times, more preferably 1.5 to 3.5 times. When the stretching ratio is less than the above range, the toughness of the film is lowered, and the produced retardation film may be difficult to apply to the polarizing plate. If the stretching ratio exceeds the above range, the film may be broken during stretching, This can be difficult. The stretching method is not particularly limited and may be carried out by a stretching method well known in the art such as a method using a tenter stretcher.
또한, 상기 미연신 코팅층이 형성된 기재 필름의 폭 방향(TD)으로의 일축 연신은 기재 필름의 유리전이온도를 Tg라 할 때, (Tg-20)℃ 내지 (Tg+30)℃의 온도에서 수행되는 것이 바람직하며, 보다 바람직하게는 (Tg)℃ 내지 (Tg+20)℃ 또는 (Tg)℃ 내지 (Tg+15)℃ 정도의 온도에서 수행될 수 있다. 이때, 폭 방향(TD)으로 일축 연신 하는 단계가 (Tg-20)℃ 미만의 온도에서 수행될 경우, 필름의 저장 탄성율이 저하될 수 있으며, 이에 따라 손실 탄성율이 저장 탄성률보다 커질 수 있다. 또한, (Tg+30)℃ 초과의 온도에서 수행될 경우, 고분자 사슬의 배향이 완화되어 소실될 수 있다. 한편, 상기 유리전이온도는 시차주사형 열량계(DSC)에 의해 측정될 수 있다. 예컨대, 시차주사형 열량계(DSC)를 이용하는 경우, 약 10mg의 시료를 전용 팬(pan)에 밀봉하고 일정 승온 조건으로 가열할 때 상변이가 일어남에 따른 물질의 흡열 및 발열량을 온도에 따라 그려 유리전이온도를 측정할 수 있다.
The uniaxial stretching in the width direction (TD) of the base film on which the non-stretch coating layer is formed is performed at a temperature of (Tg-20) DEG C to (Tg + 30) DEG C, where Tg is the glass transition temperature of the base film And more preferably at a temperature of about (Tg) ° C to (Tg + 20) ° C or (Tg) ° C to (Tg + 15) ° C. In this case, when the uniaxial stretching in the transverse direction (TD) is performed at a temperature lower than (Tg-20) ° C, the storage elastic modulus of the film may be lowered, so that the loss elastic modulus may become larger than the storage elastic modulus. Further, when the polymerization is carried out at a temperature higher than (Tg + 30) DEG C, the orientation of the polymer chain may be alleviated and lost. On the other hand, the glass transition temperature can be measured by a differential scanning calorimeter (DSC). For example, in the case of using a differential scanning calorimeter (DSC), when a sample of about 10 mg is sealed in a dedicated pan and heated at a constant temperature, the amount of endothermic heat The transition temperature can be measured.
한편, 필요에 따라, 상기 기재 필름과 코팅층 사이의 접착력을 향상시키기 위하여, 상기 코팅층을 형성하기 전에 기재 필름의 표면을 코로나로 처리할 수도 있다.
On the other hand, if necessary, the surface of the base film may be treated with corona before the coating layer is formed, in order to improve the adhesion between the base film and the coating layer.
상기와 같은 방법으로 제조되는 본 발명의 위상차 필름은 IPS 모드 액정표시장치에서 적용되는 경우 시야각 개선 효과가 매우 우수한바, IPS 모드 액정표시장치용 위상차 필름으로 매우 적합하게 사용될 수 있다.
The retardation film of the present invention produced by the above-described method has an excellent viewing angle improving effect when applied to an IPS mode liquid crystal display, and can be suitably used as a retardation film for an IPS mode liquid crystal display.
3. 편광판, 액정표시장치3. Polarizer, liquid crystal display
한편, 본 발명은 상기 위상차 필름을 적어도 하나 이상 포함하는 편광판을 제공한다. 이 경우, 본 발명에 따른 상기 위상차 필름은 편광자의 일면 또는 양면에 직접 부착 되거나, 편광자의 양면에 보호 필름이 부착된 편광판의 보호 필름 상에 부착되어, 유용하게 사용될 수 있다.
Meanwhile, the present invention provides a polarizing plate comprising at least one or more of the retardation films. In this case, the retardation film according to the present invention may be directly attached to one side or both sides of the polarizer, or may be attached to a protective film of a polarizing plate having a protective film on both sides of the polarizer.
상기 위상차 필름을 편광자의 일면 또는 양면에 직접 부착시키는 경우, 예를 들어, 그 구조는 상 보호필름/편광자/위상차 필름, 위상차 필름/편광자/하 보호필름, 위상차 필름/상 보호필름/편광자/하 보호필름 또는 상 보호필름/편광자/하 보호필름/위상차 필름 일 수 있다.
When the retardation film is directly attached to one surface or both surfaces of the polarizer, for example, the structure may be a structure of an upper protective film / polarizer / retardation film, retardation film / polarizer / lower protective film, retardation film / Protective film or an upper protective film / polarizer / lower protective film / retardation film.
한편, 본 발명은 상기 위상차 필름을 적어도 하나 이상 포함하는 액정표시장치를 제공한다. 예컨대 본 발명은 상기 위상차 필름을 적어도 하나 이상 포함하는 IPS 모드 액정표시장치를 제공한다.
Meanwhile, the present invention provides a liquid crystal display device including at least one or more of the retardation films. For example, the present invention provides an IPS mode liquid crystal display device including at least one or more retardation films.
이때, 상기 액정표시장치는 액정 셀 및 상기 액정 셀의 양면에 각각 구비된 제 1 편광판 및 제 2 편광판을 포함하는 것일 수 있으며, 상기 위상차 필름은 상기 액정 셀과 상기 제 1 편광판 및/또는 제 2 편광판 사이에 구비될 수 있다. 즉, 제 1 편광판과 액정 셀 사이에 위상차 필름이 구비될 수 있고, 제 2 편광판과 액정 셀 사이에, 또는 제 1 편광판과 액정 셀 사이와 제 2 편광판과 액정 셀 사이 모두에 위상차 필름이 하나 또는 2 이상 구비될 수 있다.
The liquid crystal display may include a liquid crystal cell and a first polarizing plate and a second polarizing plate respectively provided on both surfaces of the liquid crystal cell, and the retardation film may be disposed between the liquid crystal cell and the first polarizing plate and / And may be provided between the polarizing plates. That is, a retardation film may be provided between the first polarizing plate and the liquid crystal cell, and a retardation film may be provided between the second polarizing plate and the liquid crystal cell, or between the first polarizing plate and the liquid crystal cell, 2 or more .
이하에서는 실시예를 통하여 본 발명을 보다 상세히 설명한다. 그러나, 이하의 실시예는 본 발명의 예시를 위한 것이며, 하기 실시예에 의해 본 발명의 범위가 한정되는 것으로 의도되지 않는다.
Hereinafter, the present invention will be described in more detail with reference to Examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the invention by the following examples.
제조예Manufacturing example 1: 폴리이미드 공중합체 A 1: polyimide copolymer A
250ml 둥근 바닥 플라스크에 2,2-비스(3-아미노-4-하이드록시페닐)헥사플루오로프로판(BisAP/AF) 2.9019g과 다이메틸아세트아미드(DMAc, 비점: 약 165℃) 10g을 순차적으로 투입하고, 천천히 교반하여 완전히 용해시킨 후, 상기 플라스크를 0℃로 유지하면서 에틸렌글리콜 비스(4-트리멜리릭 언하이드라이드)(TMEG-100) 20.980g과 다이메틸아세트아미드 20g을 천천히 첨가한 다음, 4,4'-메틸렌비스(2-메틸사이클로헥실아민)(MBMCHA) 13.22g과 O,O'-비스(2-아미노프로필)폴리프로필렌글리콜 3.64g을 다이메틸아세트아미드 30g에 용해시킨 후, 드롭핑 퓨넬(dropping funnel)을 사용하여 0℃에서 1시간동안 적하(dropping)하여 교반한 후 50℃에서 23시간동안 더 교반한 다음, 톨루엔 13.8g을 넣고 딘-스탁 증류장치(dean-starkdistillation)를 통해 물을 제거할 수 있도록 설치한 후, 180℃에서 6시간 환류시켰다. 딘-스탁 증류장치의 물을 제거한 후, 상온 냉각하여 폴리이미드 공중합체 A를 얻었다. 제조된 폴리이미드 공중합체 A는 중량평균분자량이 25,000이었다.
2.9019 g of 2,2-bis (3-amino-4-hydroxyphenyl) hexafluoropropane (BisAP / AF) and 10 g of dimethylacetamide (DMAc, boiling point: about 165 ° C) were sequentially added to a 250 ml round bottom flask After the solution was completely dissolved by slow stirring, 20.980 g of ethylene glycol bis (4-trimellitic anhydride) (TMEG-100) and 20 g of dimethylacetamide were added slowly while maintaining the flask at 0 캜 , 13.22 g of 4,4'-methylenebis (2-methylcyclohexylamine) (MBMCHA) and 3.64 g of O, O'-bis (2-aminopropyl) polypropylene glycol were dissolved in 30 g of dimethylacetamide, After dropping for 1 hour at 0 ° C using a dropping funnel and stirring, the mixture was further stirred at 50 ° C for 23 hours, 13.8g of toluene was added thereto, and the mixture was subjected to dean-stark distillation. To remove water. After refluxing at 180 ° C for 6 hours The. After the water in the Dean-Stark distillation apparatus was removed, the solution was cooled at room temperature to obtain a polyimide copolymer A. The polyimide copolymer A produced had a weight average molecular weight of 25,000.
제조예Manufacturing example 2: 폴리이미드 공중합체 B 2: polyimide copolymer B
250ml 둥근 바닥 플라스크에 3,3',4,4'-바이페닐테트라카르복실릭 다이언하이드라이드(BPDA) 15.9g, 에틸렌글리콜 비스(4-트리멜리릭 언하이드라이드)(TMEG-100) 9.46g과, 다이메틸아세트아미드 30g을 천천히 첨가한 다음, 여기에 비스(3-아미노페놀)술페이드(3,3, DDS) 9.54g과 다이메틸아세트아미드 10g을 천천히 첨가하였다. 그런 다음, 4,4'-메틸렌비스(2-메틸사이클로헥실아민)(MBMCHA) 9.16g을 다이메틸아세트아미드 30g에 용해시킨 후, 드롭핑 퓨넬(dropping funnel)을 사용하여 0℃에서 1시간동안 적하(dropping)하여 교반한 후 50℃에서 23시간동안 더 교반한 다음, 톨루엔 13.8g을 넣고 딘-스탁 증류장치(dean-starkdistillation)를 통해 물을 제거할 수 있도록 설치한 후, 180℃에서 6시간 환류시켰다. 딘-스탁 증류장치의 물을 제거한 후, 상온 냉각하여 폴리이미드 공중합체 B를 얻었다. 제조된 폴리이미드 공중합체 B는 중량평균분자량이 36,000이었다.
In a 250 ml round-bottomed flask, 15.9 g of 3,3 ', 4,4'-biphenyltetracarboxylic dihydride (BPDA), 9.46 g of ethylene glycol bis (4-trimellitic anhydride) And 30 g of dimethylacetamide were slowly added thereto. Then 9.54 g of bis (3-aminophenol) sulfide (3,3, DDS) and 10 g of dimethylacetamide were slowly added thereto. Then, 9.16 g of 4,4'-methylenebis (2-methylcyclohexylamine) (MBMCHA) was dissolved in 30 g of dimethylacetamide, and the mixture was stirred at 0 ° C. for 1 hour using a dropping funnel After dropping and stirring, the mixture was further stirred at 50 ° C. for 23 hours. 13.8 g of toluene was added thereto, and water was removed through a dean-stark distillation apparatus. Lt; / RTI > After the water in the Dean-Stark distillation apparatus was removed, it was cooled at room temperature to obtain a polyimide copolymer B. The produced polyimide copolymer B had a weight average molecular weight of 36,000.
제조예Manufacturing example 3: 폴리이미드 공중합체 C 3: Polyimide Copolymer C
250ml 둥근 바닥 플라스크에 에틸렌글리콜 비스(4-트리멜리릭 언하이드라이드)(TMEG-100) 20g과, 다이메틸아세트아미드 30g을 천천히 첨가한 다음, 4,4'-메틸렌비스(2-메틸사이클로헥실아민)(MBMCHA) 10.0g을 다이메틸아세트아미드 30g에 용해시킨 후, 드롭핑 퓨넬(dropping funnel)을 사용하여 0℃에서 1시간동안 적하(dropping)하여 교반한 후 50℃에서 23시간동안 더 교반한 다음, 톨루엔 13.8g을 넣고 딘-스탁 증류장치(dean-starkdistillation)를 통해 물을 제거할 수 있도록 설치한 후, 180℃에서 6시간 환류시켰다. 딘-스탁 증류장치의 물을 제거한 후, 상온 냉각하여 폴리이미드 공중합체 C를 얻었다. 제조된 폴리이미드 공중합체 C는 중량평균분자량이 34,000이었다.
20 g of ethylene glycol bis (4-trimellitic anhydride) (TMEG-100) and 30 g of dimethylacetamide were slowly added to a 250 ml round-bottom flask and then 4,4'-methylenebis (2-methylcyclohexyl Amine) (MBMCHA) was dissolved in 30 g of dimethylacetamide, and the mixture was dropwise added at 0 ° C for 1 hour using a dropping funnel, stirred and further stirred at 50 ° C for 23 hours Then, 13.8 g of toluene was added thereto, and water was removed through a dean-stark distillation apparatus, and the mixture was refluxed at 180 ° C for 6 hours. After the water in the Dean-Stark distillation apparatus was removed, it was cooled at room temperature to obtain a polyimide copolymer C. The prepared polyimide copolymer C had a weight average molecular weight of 34,000.
실시예Example 1 One
아크릴계 수지(폴리 시클로헥실말레이므드-co-메틸메타크릴레이트, (주)LG화학社 830HR) 및 스티렌계 수지(스티렌-아크릴로니트릴 공중합체, ㈜LG화학社 SAN82TR)를 각각 78:22의 중량비로, 트윈 압출기를 이용하여 250℃, 200rpm 조건으로 컴파운딩하여 수지 조성물를 제조하였다. 상기 수지 조성물을 250℃ 조건 하에서 T- 다이 제막기를 이용하여 폭 800mm, 두께 185㎛의 미연신 필름을 제조하였다. 상기 미연신 필름을 125℃의 온도에서 길이 방향(MD)으로 롤투롤(roll to roll) 방식으로 2배 연신하여 일축 연신 하여, 일축 연신 기재 필름을 제조하였다. 다음으로, 상기 일축 연신(MD방향)된 기재 필름상에 상기 제조예에서 제조한 폴리이미드 공중합체 A가 11wt%로 포함되어 있는 용액(용매 1,3-dioxolane)을 마이크로비아 코터를 이용하여 도포하여, 4㎛ 두께로 코팅하여, 최종 두께 123㎛의 위상차 필름을 제조하였다. 다음으로 상기 위상차 필름을 125℃의 온도에서 폭 방향(TD)으로 텐터 연신 방식으로 2.0배 일축 연신 하여, 두께 61㎛ 위상차 필름을 제조하였다
Acrylic resin (polycyclohexylmaleimide-co-methylmethacrylate, LG Chemical Co., Ltd. 830HR) and styrene resin (styrene-acrylonitrile copolymer, SAN82TR, LIG Chemical Co., Ltd.) were mixed at a weight ratio of 78:22 At a temperature of 250 DEG C and 200 rpm using a twin extruder to prepare a resin composition. An undrawn film having a width of 800 mm and a thickness of 185 占 퐉 was prepared using the T-die film under the conditions of 250 占 폚. The unstretched film was uniaxially stretched by a roll-to-roll method in a longitudinal direction (MD) at a temperature of 125 캜 to obtain a uniaxially stretched base film. Next, a solution (solvent 1,3-dioxolane) containing 11 wt% of the polyimide copolymer A prepared in the above Production Example was coated on the uniaxially stretched (MD direction) base film using a microvia coater And coated to a thickness of 4 mu m to prepare a phase difference film having a final thickness of 123 mu m. Next, the retardation film was uniaxially stretched 2.0 times in a tenter stretching manner at a temperature of 125 DEG C in a width direction (TD) to produce a 61 mu m thick retardation film
실시예Example 2 2
상기 실시예 1에 있어서, 폴리이미드 공중합체 A 대신 폴리이미드 공중합체 B를 사용한 것을 제외하고는 동일한 방법으로 최종 두께 61㎛의 위상차 필름을 제조하였다.
A retardation film having a final thickness of 61 탆 was prepared in the same manner as in Example 1 except that polyimide copolymer B was used instead of polyimide copolymer A.
실시예Example 3 3
상기 실시예 1에 있어서, 폴리이미드 공중합체 A 대신 폴리이미드 공중합체 C를 사용한 것을 제외하고는 동일한 방법으로 최종 두께 61㎛의 위상차 필름을 제조하였다.
A retardation film having a final thickness of 61 탆 was prepared in the same manner as in Example 1 except that polyimide copolymer C was used instead of polyimide copolymer A.
비교예Comparative Example 1 One
상기 실시예 1에 있어서, 상기 일축 연신(MD방향)된 기재 필름상에 폴리카보네이트(㈜LG화학社 DVD1080)가 18wt%로 포함되어 있는 용액(용매 1,3-dioxolane)을 바 코터를 이용하여 도포하여, 12㎛ 두께로 코팅한 것을 제외하고는 동일한 방법으로 최종 두께 65㎛의 위상차 필름을 제조하였다.
In Example 1, a solution (solvent 1,3-dioxolane) in which 18 wt% of polycarbonate (DVD Chemical Industry Co., Ltd., DVD1080) was contained on the substrate film in the uniaxially stretched (MD direction) And a retardation film having a final thickness of 65 탆 was prepared in the same manner as above except that the coating was applied to a thickness of 12 탆.
비교예Comparative Example 2 2
상기 실시예 1에 있어서, 상기 일축 연신(MD방향)된 기재 필름상에 폴리에테르이미드(Sabic社 XH6050)가 10wt%로 포함되어 있는 용액(용매 1,3-dioxolane)을 바 코터를 이용하여 도포하여, 4㎛ 두께로 코팅한 것을 제외하고는 동일한 방법으로 최종 두께 60㎛ 의 위상차 필름을 제조하였다.
In Example 1, a solution (solvent 1,3-dioxolane) containing 10 wt% of polyetherimide (Sabic XH6050) on the uniaxially stretched (MD direction) base film was coated with a bar coater A retardation film having a final thickness of 60 탆 was prepared in the same manner as above except that the coating was coated to a thickness of 4 탆.
비교예Comparative Example 3 3
상기 실시예 1에 있어서, 상기 일축 연신(MD방향)된 기재 필름상에 코팅층을 형성하지 않을 것을 제외하고는 동일한 방법으로, 최종 두께 59㎛의 위상차 필름을 제조하였다.
A retardation film having a final thickness of 59 탆 was prepared in the same manner as in Example 1 except that the coating layer was not formed on the base film in the uniaxially stretched (MD direction).
실험예Experimental Example 1: One: 위상차Phase difference 특성 측정 Characterization
Axometrics 社의 Axoscan장비를 이용하여 상기 실시예 및 비교예에서 제조된 위상차 필름의 파장 550nm에서의 면 방향 위상차값(Rin), 두께 방향 위상차값(Rth) 및 Nz(Rth/Rin)을 측정하여 하기 표 1에 나타내었다.
(R in ), thickness direction retardation values (R th ), and Nz (R th / R in ) at a wavelength of 550 nm of the retardation film prepared in the above Examples and Comparative Examples using an Axoscan equipment of Axometrics, And the results are shown in Table 1 below.
실험예Experimental Example 2: 접착력 평가 2: Evaluation of adhesion
호모폴리머의 유리전이온도가 190도인 3,4-에폭시시클로헥실메틸-3,4-에폭시시클로헥산카복실레이트 25중량% (Dicel사의 Celloxide 2021P), 호모폴리머의 유리전이온도가 25도인 1,4-시클로헥산 디메탄올 디글리시딜에테르 25중량%, 3-에틸-3-[(3-에틸옥세탄-3-일)메톡시메틸]옥세탄(도아 고세이 아론 옥세탄 DOX221) 50중량%를 넣어 제조한 수지 조성물 100중량부에 양이온 개시제인 CPI 100P(Sanapro사) 5 중량부를 첨가하여 편광판용 접착제를 제조하였다.
25% by weight of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (Celloxide 2021P from Dicel) having a glass transition temperature of the homopolymer of 190 ° C, 1,4-cyclohexanedimethanol having a glass transition temperature of 25 ° C of the homopolymer, , 25 wt% of cyclohexanedimethanol diglycidyl ether and 50 wt% of 3-ethyl-3 - [(3-ethyloxetan-3-yl) methoxymethyl] oxetane (DOA GOSAYARONOXETAN DOX 221) To 100 parts by weight of the resin composition, 5 parts by weight of a cationic initiator CPI 100P (Sanapro) was added to prepare an adhesive for a polarizing plate.
그런 다음, 폴리비닐알코올계 편광자 양면에 상기 편광판용 접착제를 도포하고, 한면에 아크릴계 필름을, 다른 면에 상기 실시예 및 비교예에 따른 위상차 필름을 코팅층이 접착제에 접착되도록 적층한 다음, 최종 접착층의 두께가 1~2㎛이 되도록 조건을 설정한 후, 라미네이터(5m/min)를 통과시켰다. 그 후, UV 조사장치(metal halide lamp)를 이용하여, 500mJ/cm2의 자외선을 조사하여, 편광판을 제조하였다. 그 후, TA.XT.Plus(Stable Micro System) texture analyser를 이용하여 90도 박리력을 측정하였다. 구체적으로, 상기 편광판을 폭 2cm, 길이 8cm 시편으로 제단한 후, 위상차 필름을 측정기의 아래면에 고정하고 5cm 거리의 90도 필(peel) 박리력을 측정하였다.
Then, the polarizing plate adhesive was applied to both sides of the polyvinyl alcohol polarizer, and an acrylic film was laminated on one side and a retardation film according to the above-mentioned example and comparative example on the other side to laminate the coating layer to the adhesive, Was set to a thickness of 1 to 2 mu m, and then passed through a laminator (5 m / min). Thereafter, using a metal halide lamp, ultraviolet light of 500 mJ / cm 2 was irradiated to produce a polarizing plate. After that, a 90 degree peel force was measured using a TA.XT.Plus (Stable Micro System) texture analyzer. Specifically, the polarizing plate was cut into a sample having a width of 2 cm and a length of 8 cm, the retardation film was fixed to the lower surface of the measuring device, and peel force of 90 degrees peel distance of 5 cm was measured.
(N/2cm)Adhesion
(N / 2 cm)
(㎚)R in / R th
(Nm)
(㎛)thickness
(탆)
(㎚)R in / R th
(Nm)
(㎛)thickness
(탆)
(㎚)R in / R th
(Nm)
(㎛)thickness
(탆)
상기 표 1에서 확인할 수 있는 바와 같이, 실시예 1 내지 3의 복합 위상차 필름은 면 방향 위상차값(Rin)이 50 내지 300nm 범위 내이고, 두께 방향 위상차값(Rth)이 10 내지 300nm 범위 내이며, Nz(Rth/Rin)이 1 이하로, IPS 모드 액정표시장치에 위상차 필름으로 적용하기에 적합하다. 또한, 실시예의 복합 위상차 필름의 경우 코팅층의 접착력이 매우 우수하며, 따라서 편광판이나 액정 패널 등에 쉽게 부착이 가능하다는 것을 알 수 있다.
As can be seen from the above Table 1, the composite phase difference films of Examples 1 to 3 had a retardation value (R in ) in the range of 50 to 300 nm and a thickness retardation value (R th ) in the range of 10 to 300 nm and, below the (R th / R in) Nz 1, it is adapted to apply a phase difference film for IPS-mode liquid crystal display device. In addition, in the case of the composite phase difference film of the examples, the coating layer has an excellent adhesive force, and thus it can be easily attached to a polarizing plate or a liquid crystal panel.
그러나, 비교예 1 내지 2의 경우, 실시예와 기재 필름이 동일하고, 위상차 필름의 제조 방법이 유사한바, IPS 모드에 적합한 위상차 특성을 구현할 수는 있으나, 코팅층 형성을 위한 재료가 상이한바, 코팅층의 접착력이 매우 불량하여 편광판이나 액정 패널 등에 부착하는데 어려움이 있다는 것을 알 수 있다.
However, in the case of Comparative Examples 1 and 2, the phase difference film suitable for the IPS mode can be realized although the substrate and the base film are the same and the manufacturing method of the retardation film is similar. However, since the material for forming the coating layer is different, It is difficult to adhere to a polarizing plate or a liquid crystal panel.
또한, 비교예 3의 경우 코팅층이 형성되지 않은바, IPS 모드에 적합한 위상차 특성을 구현할 수 없으며, 나아가 코팅층의 접착력이 매우 불량하여, 편광판이나 액정 패널 등에 부착하는데 어려움이 있다는 것을 알 수 있다.
In contrast, in Comparative Example 3, since no coating layer was formed, the retardation characteristics suitable for the IPS mode could not be realized, and further, the adhesion of the coating layer was very poor, making it difficult to adhere to a polarizing plate or a liquid crystal panel.
이상에서 본 발명의 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고, 청구범위에 기재된 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 다양한 수정 및 변형이 가능하다는 것은 당 기술분야의 통상의 지식을 가진 자에게는 자명할 것이다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, It will be obvious to those of ordinary skill in the art.
1: 기재 필름
2: 코팅층1: substrate film
2: Coating layer
Claims (17)
상기 기재 필름의 적어도 일면에 형성되며, 하기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체를 포함하는 코팅층;
을 포함하는 위상차 필름.
[화학식 1]
상기 [화학식 1]에서, X1은 에스테르기 또는 에테르기를 포함하는 지환족 또는 방향족 산 이무수물로부터 유도된 4가 유기기이며; X2는 X1과 상이한 산 이무수물로부터 유도된 4가 유기기이고; Q1 및 Q2는 각각 독립적으로 디아민으로부터 유도된 2가 유기기이며; 상기 a, b, c 및 d는 각 반복단위의 몰비를 나타내는 것으로, a+b+c+d =1이고, 0.1 ≤ a+b ≤ 1 이고, 0 ≤ c+d ≤ 0.9 임.
A base film comprising a negative retardation material; And
A coating layer formed on at least one surface of the base film and comprising a polyimide copolymer containing a repeating unit represented by the following formula (1);
/ RTI >
[Chemical Formula 1]
Wherein X 1 is a divalent organic group derived from an alicyclic or aromatic acid dianhydride containing an ester group or an ether group; X 2 is a divalent organic group derived from an acid dianhydride different from X 1 ; Q 1 and Q 2 are each independently a divalent organic group derived from a diamine; Wherein a, b, c and d represent the molar ratio of the respective repeating units, a + b + c + d = 1, 0.1? A + b? 1 and 0? C + d? 0.9.
상기 위상차 필름은 상기 코팅층을 편광판용 접착제를 매개로 폴리비닐알코올계 편광자에 부착한 후 측정한 접착력이 1N/2cm 이상인 위상차 필름.
The method according to claim 1,
Wherein the retardation film has an adhesion of at least 1 N / 2 cm measured after attaching the coating layer to a polyvinyl alcohol polarizer via an adhesive for a polarizer.
상기 위상차 필름은 하기 식 (1) 및 (2)를 만족하는 위상차 필름.
식 (1): 50nm ≤ Rin , total ≤ 300nm
식 (2): 10nm ≤ Rth , total ≤ 300nm
상기 식 (1) 및 (2)에서,
Rin , total은 파장 550nm에서 측정한 위상차 필름 전체의 면 방향 위상차값이고;
Rth , total은 파장 550nm에서 측정한 위상차 필름 전체의 두께 방향 위상차값임.
The method according to claim 1,
Wherein the retardation film satisfies the following expressions (1) and (2).
(1): 50 nm? R in , total ? 300 nm
(2): 10 nm? R th , total ? 300 nm
In the above formulas (1) and (2)
R in , total is a retardation value in the plane direction of the entire retardation film measured at a wavelength of 550 nm;
R th , total is the retardation value in the thickness direction of the entire retardation film measured at a wavelength of 550 nm.
상기 위상차 필름은 하기 식 (3)으로 표시되는 Nz 값이 1 이하인 위상차 필름.
식 (3): Nz = Rth , total/Rin , total
상기 식 (3)에서,
Rin , total은 위상차 필름 전체의 면 방향 위상차값이고;
Rth , total은 위상차 필름 전체의 두께 방향 위상차값이며;
이때, 상기 Rin , total 및 Rth , total은 모두 파장 550nm에서 측정한 위상차값임.
The method according to claim 1,
Wherein the retardation film is a retardation film having an Nz value of 1 or less represented by the following formula (3).
Equation (3): Nz = R th , total / R in, total
In the above formula (3)
R in and total are plane retardation values of the entire retardation film;
R th , total is the retardation value in the thickness direction of the entire retardation film;
At this time, R in , total and R th , total are retardation values measured at a wavelength of 550 nm.
상기 기재 필름은 하기 식 (4) 및 (5)을 만족하는 위상차 필름.
식 (4): 0nm ≤ Rin ,a ≤ 250nm
식 (5): 10nm ≤ Rth ,a ≤ 300nm
상기 식 (4) 및 (5)에서,
Rin ,a은 파장 550nm에서 측정한 기재 필름의 면 방향 위상차값이고;
Rth ,a은 파장 550nm에서 측정한 기재 필름의 두께 방향 위상차값임.
The method according to claim 1,
Wherein the base film satisfies the following formulas (4) and (5).
(4): 0 nm? R in , a ? 250 nm
(5): 10 nm? R th , a ? 300 nm
In the above formulas (4) and (5)
R in , a is the retardation value in the plane direction of the base film measured at a wavelength of 550 nm;
Rth , a is the retardation value in the thickness direction of the base film measured at a wavelength of 550 nm.
상기 코팅층은 하기 식 (6) 및 (7)을 만족하는 위상차 필름.
식 (6): 50nm ≤ Rin ,b ≤ 300nm
식 (7): -290nm ≤ Rth ,b ≤ 0nm
상기 식 (6) 및 (7)에서,
Rin ,b은 파장 550nm에서 측정한 코팅층의 면 방향 위상차값이고;
Rth ,b은 파장 550nm에서 측정한 코팅층의 두께 방향 위상차값임.
The method according to claim 1,
Wherein the coating layer satisfies the following formulas (6) and (7).
(6): 50 nm? R in , b ? 300 nm
(7): -290 nm? R th , b ? 0 nm
In the above formulas (6) and (7)
R in , b is the retardation value in the plane direction of the coating layer measured at a wavelength of 550 nm;
Rth , b is the thickness direction retardation value of the coating layer measured at a wavelength of 550 nm.
상기 기재 필름은 길이 방향(MD) 및 폭 방향(TD)으로 이축 연신된 것이고, 상기 코팅층은 폭 방향(TD)으로 일축 연신된 것인 위상차 필름.
The method according to claim 1,
Wherein the base film is biaxially stretched in the longitudinal direction (MD) and the transverse direction (TD), and the coating layer is uniaxially stretched in the width direction (TD).
상기 X1은 하기 [화학식 2] 또는 [화학식 3]로 표시되는 산 이무수물로부터 유도된 4가 유기기인 위상차 필름.
[화학식 2]
상기 [화학식 2]에서, A1은 탄소수 1~10의 지방족 고리 또는 방향족 고리이며; B1은 단일 결합, 치환 또는 비치환된 지방족 사슬, 치환 또는 비치환된 지방족 고리, 치환 또는 비치환된 방향족 고리, 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 고리, 또는 이들의 조합임.
[화학식 3]
상기 [화학식 3]에서, A2는 탄소수 1~10의 지방족 고리 또는 방향족 고리이며; B2는 단일 결합, 치환 또는 비치환된 지방족 사슬, 치환 또는 비치환된 지방족 고리, 치환 또는 비치환된 방향족 고리; 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 고리; 또는 이들의 조합임.
The method according to claim 1,
Wherein X < 1 > is a tetravalent organic group derived from an acid dianhydride represented by the following formula (2) or (3)
(2)
In the above formula (2), A 1 is an aliphatic ring or aromatic ring having 1 to 10 carbon atoms; B 1 is a single bond, a substituted or unsubstituted aliphatic chain, a substituted or unsubstituted aliphatic ring, a substituted or unsubstituted aromatic ring, two or more aromatic rings connected through a direct or crosslinked structure, or a combination thereof.
(3)
In Formula 3, A 2 is an aliphatic ring or aromatic ring having 1 to 10 carbon atoms; B 2 is a single bond, a substituted or unsubstituted aliphatic chain, a substituted or unsubstituted aliphatic ring, a substituted or unsubstituted aromatic ring; Two or more aromatic rings linked directly or via a bridging structure; Or a combination thereof.
상기 X1은 하기 [화학식 4]에 표시된 화합물들로 이루어진 군으로부터 선택된 산 이무수물로부터 유도된 4가 유기기인 위상차 필름.
[화학식 4]
상기 [화학식 4]에서, B1 및 B2는 각각 독립적으로 단일 결합; 치환 또는 비치환된 지방족 사슬; 치환 또는 비치환된 지방족 고리; 치환 또는 비치환된 방향족 고리; 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 고리; 또는 이들의 조합임.
The method according to claim 1,
Wherein X < 1 > is a tetravalent organic group derived from an acid dianhydride selected from the group consisting of compounds represented by Formula 4 below.
[Chemical Formula 4]
In Formula 4, B 1 and B 2 each independently represent a single bond; A substituted or unsubstituted aliphatic chain; A substituted or unsubstituted aliphatic ring; A substituted or unsubstituted aromatic ring; Two or more aromatic rings linked directly or via a bridging structure; Or a combination thereof.
상기 Q1 또는 Q2는 하기 [화학식 5]에 표시되는 화합물들로 이루어진 군으로부터 선택된 디아민으로부터 유도된 2가 유기기인 위상차 필름.
[화학식 5]
상기 [화학식 5]에서, 상기 R1 내지 R7은 각각 독립적으로, 치환 또는 비치환된 지방족 사슬, 치환 또는 비치환된 지방족 고리, 치환 또는 비치환된 방향족 고리, 직접 또는 가교 구조를 통해 연결된 2 이상의 방향족 고리, 또는 이들의 조합이며; R8 내지 R11은 각각 독립적으로, 탄소수 1 내지 10 알킬기, 탄소수 1 내지 10의 할로알킬기 또는 히드록시기이며; q는 1~ 8인 정수임.
The method according to claim 1,
Wherein Q 1 or Q 2 is a divalent organic group derived from a diamine selected from the group consisting of compounds represented by the following formula (5).
[Chemical Formula 5]
In Formula 5, R 1 to R 7 each independently represents a substituted or unsubstituted aliphatic chain, a substituted or unsubstituted aliphatic ring, a substituted or unsubstituted aromatic ring, a straight or branched An aromatic ring, or a combination thereof; R 8 to R 11 are each independently a C 1-10 alkyl group, a C 1-10 haloalkyl group or a hydroxy group; q is an integer of 1 to 8;
상기 부의 위상차 물질은 아크릴계 수지, 스티렌계 수지, 아크릴계 수지와 스티렌계 수지를 포함하는 블렌딩 수지, 폴리비닐카바졸 및 폴리비닐나프탈렌으로 이루어진 군으로부터 선택된 1 이상인 위상차 필름.
The method according to claim 1,
Wherein the negative retardation material is at least one selected from the group consisting of an acrylic resin, a styrene resin, a blending resin including an acrylic resin and a styrene resin, polyvinylcarbazole, and polyvinylnaphthalene.
상기 위상차 필름의 전체 두께는 80㎛ 이하인 위상차 필름.
The method according to claim 1,
Wherein the total thickness of the retardation film is 80 占 퐉 or less.
A polarizer comprising the retardation film of any one of claims 1 to 12.
A liquid crystal display device comprising the retardation film of any one of claims 1 to 12.
상기 기재 필름의 적어도 일면에 하기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체를 포함하는 코팅층을 형성하는 단계;
를 포함하는 위상차 필름의 제조 방법.
[화학식 1]
상기 [화학식 1]에서, X1은 에스테르기 또는 에테르기를 포함하는 지환족 또는 방향족 산 이무수물로부터 유도된 4가 유기기이며; X2는 X1과 상이한 산 이무수물로부터 유도된 4가 유기기이고; Q1 및 Q2는 각각 독립적으로 디아민으로부터 유도된 2가 유기기이며; 상기 a, b, c 및 d는 각 반복단위의 몰비를 나타내는 것으로, a+b+c+d =1이고, 0.1 ≤ a+b ≤ 1 이고, 0 ≤ c+d ≤ 0.9 임.
Preparing a substrate film comprising a negative retardation material; And
Forming a coating layer comprising a polyimide copolymer containing at least one surface of the base film and a repeating unit represented by the following formula (1);
Wherein the retardation film has a thickness of 100 to 500 nm.
[Chemical Formula 1]
Wherein X 1 is a divalent organic group derived from an alicyclic or aromatic acid dianhydride containing an ester group or an ether group; X 2 is a divalent organic group derived from an acid dianhydride different from X 1 ; Q 1 and Q 2 are each independently a divalent organic group derived from a diamine; Wherein a, b, c and d represent the molar ratio of the respective repeating units, a + b + c + d = 1, 0.1? A + b? 1 and 0? C + d? 0.9.
부의 위상차 필름을 포함하는 미연신 기재 필름을 준비하는 단계;
상기 미연신 기재 필름을 연신하는 단계;
상기 연신 처리된 기재 필름의 적어도 일면에 상기 [화학식 1]로 표시되는 반복단위를 포함하는 폴리이미드 공중합체를 포함하는 미연신 코팅층을 형성하는 단계; 및
상기 미연신 코팅층이 형성된 기재 필름을 연신하는 단계;
를 포함하는 위상차 필름의 제조 방법.
16. The method of claim 15,
Preparing an unstretched base film comprising a negative retardation film;
Stretching the unstretched base film;
Forming an unstretched coating layer comprising a polyimide copolymer containing at least one repeating unit represented by the formula (1) on at least one surface of the stretched substrate film; And
Stretching the base film on which the non-stretched coating layer is formed;
Wherein the retardation film has a thickness of 100 to 500 nm.
상기 미연신 기재 필름을 연신하는 단계는 길이 방향(MD)으로 일축 연신하는 것이고, 상기 미연신 코팅층이 형성된 기재 필름을 연신하는 단계는 폭 방향(TD)으로 일축 연신하는 것인 위상차 필름의 제조 방법.17. The method of claim 16,
Wherein the step of stretching the unstretched base film is uniaxial stretching in the machine direction (MD), and the step of stretching the base film on which the non-stretched coating layer is formed is uniaxially stretched in the transverse direction (TD) .