KR20160007149A - manufacture method of pipe clad alumicum pipe for heat exchanger - Google Patents
manufacture method of pipe clad alumicum pipe for heat exchanger Download PDFInfo
- Publication number
- KR20160007149A KR20160007149A KR1020140087396A KR20140087396A KR20160007149A KR 20160007149 A KR20160007149 A KR 20160007149A KR 1020140087396 A KR1020140087396 A KR 1020140087396A KR 20140087396 A KR20140087396 A KR 20140087396A KR 20160007149 A KR20160007149 A KR 20160007149A
- Authority
- KR
- South Korea
- Prior art keywords
- pipe
- clad aluminum
- heat exchanger
- outer diameter
- groove
- Prior art date
Abstract
Description
본 발명은 열교환기용 클래드 알루미늄 파이프의 제조방법에 관한 것으로, 보다 상세하게는 구리 파이프에 비해 생산단가를 절감할 수 있고, 내부의 그루브를 형성하고 최대 용접성을 확보하기 위해 용접 규격을 변화시키더라도 정밀한 두께 및 직경의 최종제품을 생산할 수 있는 열교환기용 클래드 알루미늄 파이프의 제조방법에 관한 것이다.
The present invention relates to a method of manufacturing a clad aluminum pipe for a heat exchanger, and more particularly, to a method of manufacturing a clad aluminum pipe for a heat exchanger, which can reduce production cost compared with a copper pipe, To a process for producing a clad aluminum pipe for a heat exchanger capable of producing a final product of thickness and diameter.
자동차, 선박, 발전소, 가정 등 광범위한 산업 분야에 걸쳐 열교환기가 사용되고 있다.Heat exchangers have been used in a wide range of industries, including automobiles, ships, power plants, and homes.
도 1에 도시된 바와 같이, 종래의 열교환기(10)는 열 교환 성능을 향상시키기 위한 핀(11)과 작동 유체의 유로를 형성하는 파이프 튜브(12)로 구성된다.As shown in FIG. 1, the
또한, 열교환기는 경량화와 높은 열 전도도가 요구되므로, 상기 핀(11)에 삽입되는 열교환기용 파이프는 일반적으로 구리를 소재로 한 파이프가 제작되어 사용되고 있다.Since the heat exchanger is required to have a light weight and a high thermal conductivity, the pipe for the heat exchanger to be inserted into the
하지만, 구리 파이프의 경우에는 상기 핀(11)에 삽입되었을 때, 용접이 불가하여 서로 이격되므로, 열 교환 성능이 저하되고, 구리 소재 가격의 급등으로 제품의 제조비용이 높은 실정이다.However, in the case of a copper pipe, when it is inserted into the
따라서, 구리 소재를 알루미늄 소재로 대체할 수 있는 기술개발이 진행되고 있다. Therefore, technology for replacing copper material with aluminum material is being developed.
특허 출원번호 KR 1999-0033407호에는 Al-Mg-Si-Cu계의 알루미늄 합금으로 이루어져 알루미늄 합금의 압출성을 향상시킬 수 있도록 하는 압출성이 우수한 강도 알루미늄 합금이 개시되어 있다.Patent Application No. KR 1999-0033407 discloses a strength aluminum alloy excellent in extrudability, which is made of an Al-Mg-Si-Cu-based aluminum alloy to improve the extrudability of the aluminum alloy.
하지만, 단일 소재로 제조된 알루미늄 파이프는 상기 핀(11)과 파이프를 결합하는 엄셈블리 공정에서 브레이징(blazing) 공법이 불가능하여, 기존의 구리파이프 보다 열 교환성능이 떨어지게 된다.However, in the aluminum pipe manufactured from a single material, the blazing method is not possible in the Sambling process in which the
이와 같은 문제를 해결하기 위해, 클래드 알루미늄을 이용하여, 브레이징 공법이 가능한 기술들이 개발되어 있다. In order to solve such a problem, techniques capable of performing a brazing method using clad aluminum have been developed.
특허 출원번호 KR 2009-0096118호에는 알루미늄 합금의 모재와 상기 모재 위에 브레이징이 가능한 클래드재가 위치된 파이프 제조용 시트를 튜브밀에 투입하여 파이프를 제조하는 기술이 개시되어 있다.Patent Application No. KR 2009-0096118 discloses a technique for manufacturing a pipe by injecting a pipe manufacturing sheet in which a base material of an aluminum alloy and a cladding material capable of brazing is placed on the base material into a tube mill.
또한, 특허 출원번호 US 2009-653894호에는 클래드 알루미늄을 이용하여, 열교환기용 파이프를 제조하는 기술이 개시되어 있다.In addition, Patent Application No. US 2009-653894 discloses a technique for manufacturing a pipe for a heat exchanger by using clad aluminum.
종래의 기술들은 클래드 알루미늄 파이프를 제조하여, 브레이징 공법으로 열교환기의 방열핀에 용접할 수 있으므로 열 교환성능은 개선되었으나, 보다 향상된 열 교환성능을 지닐 수 있는 클래드 알루미늄 파이프 제조 기술의 개발이 필요하다. Conventional techniques can improve the heat exchange performance by manufacturing the clad aluminum pipe and welding it to the heat radiating fins of the heat exchanger by the brazing method, but it is necessary to develop a clad aluminum pipe manufacturing technology capable of having improved heat exchange performance.
또한, 최종 용접성을 확보하면서도 원하는 두께 및 직경의 최종제품을 제조할 수 있는 클래드 알루미늄 파이프의 제조 기술의 개발이 필요하다.
Further, it is necessary to develop a manufacturing technology of a clad aluminum pipe which can produce a final product having a desired thickness and diameter while securing the final weldability.
본 발명은 이러한 필요성에 의해 안출된 것으로 본 발명의 목적은 구리 소재를 클래드 알루미늄으로 대체하여 생산비용을 절감할 수 있고, 열 교환기의 방열핀과 브레이징 공법으로 결합될 수 있으므로, 상기 방열핀으로 열전달효율을 향상시킬 수 있는 열교환기용 클래드 알루미늄 파이프의 제조방법을 제공하는 것이다.SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned needs, and it is an object of the present invention to reduce the production cost by replacing the copper material with the clad aluminum and to be combined with the heat dissipating fin of the heat exchanger by the brazing method. And a method for manufacturing a clad aluminum pipe for a heat exchanger.
또한, 본 발명의 목적은 클래드 알루미늄 파이프의 내측에 길이방향으로 나란한 복수개의 직선형 그루브(groove)가 형성되어, 냉매의 유체거동 효과가 상승되고 열전달효율을 보다 향상시킬 수 있는 열교환기용 클래드 알루미늄 파이프의 제조방법을 제공하는 것이다.It is another object of the present invention to provide a clad aluminum pipe for a heat exchanger in which a plurality of linear grooves are formed parallel to each other in the longitudinal direction on the inner side of a clad aluminum pipe to improve a fluid behavior effect of the refrigerant and further improve heat transfer efficiency And a method for manufacturing the same.
또한, 본 발명의 목적은 고주파 용접단계에서 파이프의 외경 및 두께를 일정 수준으로 조절하여, 최대 용접성을 확보하면서도 원하는 두께 및 직경의 최종 제품을 생산할 수 있는 열교환기용 클래드 알루미늄 파이프의 제조방법을 제공하는 것이다.It is another object of the present invention to provide a method for manufacturing a clad aluminum pipe for a heat exchanger which can produce a final product having a desired thickness and diameter while maintaining maximum weldability by adjusting the outer diameter and thickness of the pipe to a certain level in a high- will be.
본 발명의 목적들은 이상에서 언급한 목적들로 제한되지 않으며, 언급되지 않은 또 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
The objects of the present invention are not limited to the above-mentioned objects, and other objects not mentioned can be clearly understood by those skilled in the art from the following description.
상술된 본 발명의 목적을 달성하기 위해, 먼저 본 발명은 열교환기의 방열핀에 브레이징 용접시키기 위한 열교환기용 클래드 알루미늄 파이프의 제조방법에 있어서, 클래드 알루미늄 판재를 이송시키며, 알루미늄 코어면에 그루브를 형성하는 그루브 형성단계; 그루브가 형성된 클래드 알루미늄 판재를 복수개의 이송 롤러를 통해 파이프 형상으로 말아지게 하는 파이프 조관단계; 상기 조관단계를 통해 말아진 클래드 알루미늄 파이프의 마주하는 끝단부를 고주파 용접시키는 고주파 용접단계; 상기 고주파 용접단계를 통해 얻어진 파이프의 직경을 축소시키는 사이징 단계; 및 사이징된 파이프를 설정된 길이로 절단하여 최종제품을 생산하는 절단단계를 포함하고, 상기 고주파 용접단계를 통해 얻어진 파이프의 외경은 상기 최종제품의 외경보다 0.8 내지 1.2mm 큰 것을 특징으로 하는 열교환기용 클래드 알루미늄 파이프의 제조방법을 제공한다.In order to accomplish the object of the present invention, the present invention provides a method of manufacturing a clad aluminum pipe for a heat exchanger for brazing a heat radiating fin of a heat exchanger, the method comprising: transporting a clad aluminum plate, A groove forming step; A pipe gauging step of causing a clad aluminum plate material on which a groove is formed to roll in a pipe shape through a plurality of feed rollers; A high frequency welding step of high-frequency welding the opposite end portions of the rolled clad aluminum pipe through the tube making step; A sizing step of reducing the diameter of the pipe obtained through the high frequency welding step; And a cutting step of cutting the sized pipe to a predetermined length to produce a final product, wherein an outer diameter of the pipe obtained through the high frequency welding step is 0.8 to 1.2 mm larger than the outer diameter of the final product. A method of manufacturing an aluminum pipe is provided.
바람직한 실시예에 있어서, 상기 고주파 용접단계를 통해 얻어진 파이프의 외경이 상기 최종 제품의 외경보다 0.8mm 내지 0.9mm 크게 형성될 경우에는 상기 클래드 알루미늄 판재의 두께와 상기 그루브의 높이를 0.04mm 감소시켜 용접을 수행하고, 상기 고주파 용접단계를 통해 얻어진 파이프의 외경이 상기 최종 제품의 외경보다 1.0mm 내지 1.2mm 크게 형성될 경우에는 상기 클래드 알루미늄 판재의 두께와 상기 그루브의 높이를 0.05mm 감소시켜 용접을 수행한다.In a preferred embodiment, when the outer diameter of the pipe obtained through the high frequency welding step is 0.8 mm to 0.9 mm larger than the outer diameter of the final product, the thickness of the clad aluminum plate and the height of the groove are reduced by 0.04 mm, And when the outer diameter of the pipe obtained through the high frequency welding step is larger than the outer diameter of the final product by 1.0 mm to 1.2 mm, the thickness of the clad aluminum plate and the height of the groove are decreased by 0.05 mm to perform welding do.
바람직한 실시예에 있어서, 상기 이송 롤러들은 세로 회전축을 중심으로 회전하는 세로축 회전 롤러이며, 이웃하는 상기 이송 롤러들은 지면에 대해 설치된 높이가 서로 다르다.In a preferred embodiment, the conveying rollers are longitudinally rotating rollers rotating about a longitudinal axis of rotation, and the adjacent conveying rollers are different in height from the ground.
또한, 본 발명은 클래드 알루미늄 파이프의 제조방법에 의해 제조된 클래드 알루미늄 파이프를 제공한다.Further, the present invention provides a clad aluminum pipe produced by a method for producing a clad aluminum pipe.
또한, 본 발명은 클래드 알루미늄 파이프가 구비된 열교환기를 제공한다.The present invention also provides a heat exchanger equipped with a clad aluminum pipe.
또한, 본 발명은 열교환기가 구비된 공조기를 제공한다.
The present invention also provides an air conditioner equipped with a heat exchanger.
본 발명은 다음과 같은 우수한 효과를 갖는다.The present invention has the following excellent effects.
먼저 본 발명의 열교환기용 클래드 알루미늄 파이프의 제조방법에 의하면, 구리 소재를 클래드 알루미늄으로 대체하여 생산비용을 절감할 수 있고, 열 교환기의 방열핀과 브레이징 공법으로 결합될 수 있으므로, 상기 방열핀으로 열전달효율을 향상시킬 수 있다.According to the method for manufacturing a clad aluminum pipe for a heat exchanger of the present invention, the production cost can be reduced by replacing the copper material with the clad aluminum, and the heat transfer efficiency can be reduced by the heat dissipation fin Can be improved.
또한, 본 발명의 열교환기용 클래드 알루미늄 파이프의 제조방법에 의하면, 클래드 알루미늄 파이프의 내측에 길이방향으로 나란한 복수개의 직선형 그루브(groove)가 형성되어, 냉매의 유체거동 효과가 상승되고 열전달효율을 보다 향상시킬 수 있다.According to the method of manufacturing a clad aluminum pipe for a heat exchanger of the present invention, a plurality of linear grooves arranged in the longitudinal direction are formed on the inner side of the clad aluminum pipe to improve the fluid behavior effect of the refrigerant and further improve the heat transfer efficiency .
또한, 본 발명의 열교환기용 클래드 알루미늄 파이프의 제조방법에 의하면, 고주파 용접단계에서 파이프의 외경 및 두께를 일정 수준으로 조절하여, 최대 용접성을 확보하면서도 원하는 두께 및 직경의 최종 제품을 생산할 수 있다.
In addition, according to the method for manufacturing a clad aluminum pipe for a heat exchanger of the present invention, the outer diameter and thickness of the pipe can be adjusted to a certain level in the high frequency welding step to produce a final product having a desired thickness and diameter while ensuring maximum weldability.
도 1은 종래의 열교환기를 보여주는 도면이다.
도 2는 본 발명의 일실시예에 따른 열교환기용 클래드 알루미늄 파이프의 제조방법을 보여주는 공정순서도이다.
도 3은 본 발명의 일실시예에 따른 열교환기용 클래드 알루미늄 파이프의 제조방법을 통해 제조된 열교환기용 클래드 알루미늄 파이프를 보여주는 사시도이다.1 is a view showing a conventional heat exchanger.
2 is a process flow diagram illustrating a method of manufacturing a clad aluminum pipe for a heat exchanger according to an embodiment of the present invention.
3 is a perspective view illustrating a clad aluminum pipe for a heat exchanger manufactured through a method of manufacturing a clad aluminum pipe for a heat exchanger according to an embodiment of the present invention.
본 발명에서 사용되는 용어는 가능한 현재 널리 사용되는 일반적인 용어를 선택하였으나, 특정한 경우는 출원인이 임의로 선정한 용어도 있는데 이 경우에는 단순한 용어의 명칭이 아닌 발명의 상세한 설명 부분에 기재되거나 사용된 의미를 고려하여 그 의미가 파악되어야 할 것이다.Although the terms used in the present invention have been selected as general terms that are widely used at present, there are some terms selected arbitrarily by the applicant in a specific case. In this case, the meaning described or used in the detailed description part of the invention The meaning must be grasped.
이하, 첨부한 도면에 도시된 바람직한 실시예들을 참조하여 본 발명의 기술적 구성을 상세하게 설명한다.Hereinafter, the technical structure of the present invention will be described in detail with reference to preferred embodiments shown in the accompanying drawings.
그러나, 본 발명은 여기서 설명되는 실시예에 한정되지 않고 다른 형태로 구체화 될 수도 있다. 명세서 전체에 걸쳐 동일한 참조번호는 동일한 구성요소를 나타낸다.
However, the present invention is not limited to the embodiments described herein but may be embodied in other forms. Like reference numerals designate like elements throughout the specification.
본 발명의 일실시예에 따른 열교환기용 클래드 알루미늄 파이프 제조방법은 열교환기의 방열핀에 브레이징 용접시키기 위한 열교환기용 클래드 알루미늄 파이프를 제조하기 위한 방법으로, 도 2에 공정도가 도시되어 있다.The method for manufacturing a clad aluminum pipe for a heat exchanger according to an embodiment of the present invention is a method for manufacturing a clad aluminum pipe for a heat exchanger for brazing welding to a heat radiating fin of a heat exchanger.
본 발명의 일실시예에 따른 열교환기용 클래드 알루미늄 파이프 제조방법은 그루브 형성단계, 파이프 조관 단계, 고주파 용접단계, 사이징 단계, 절단단계로 수행된다.The method for manufacturing a clad aluminum pipe for a heat exchanger according to an embodiment of the present invention is performed by a groove forming step, a pipe forming step, a high frequency welding step, a sizing step, and a cutting step.
먼저, 상기 그루브 형성단계는 클래드 알루미늄 판재(100)를 풀어 이송시키고, 그루브를 형성하는 단계이다.First, the groove forming step is a step of loosening and transporting the
또한, 그루브(911)의 형성은 복수개의 그루브 형성 돌기(210)가 형성된 그루브 형성 드럼(200)이 이송되는 클래드 알루미늄 판재에 접촉하여 회전함으로써 형성된다.Further, the
다음, 상기 파이프 조관단계는 그루브가 형성된 클래드 알루미늄 판재를 복수개의 이송 롤러(300)를 통해 파이프 형상으로 말아지게 하는 단계이다.Next, the pipe making step is a step of making the clad aluminum plate having grooves rolled into a pipe shape through a plurality of
또한, 상기 이송 롤러(300)들은 세로 회전축을 중심으로 회전하는 세로축 회전 롤러이다.The
이는 클래드 알루미늄의 상하면에 접촉하는 가로축 회전 롤러를 사용하게 될 경우, 상기 알루미늄 코어면에 형성된 그루브(911)가 홰손되기 때문이다.This is because the
즉, 본 발명의 파이프 조관단계에서는 세로축 회전 롤러만을 사용한다.That is, in the pipe making step of the present invention, only the vertical axis rotating roller is used.
또한, 이웃하는 상기 이송 롤러들은 지면에 대해 설치된 높이(h1 및 h2)가 서로 다르게 형성된다. In addition, the adjacent transporting rollers are formed to have different heights h1 and h2 provided with respect to the ground.
이와 같이, 지면에 대해 설치된 높이가 서로 다르게 되면, 세로축 회전 롤러로만 구성되어 말려진 상기 클래드 알루미늄 판재(100)가 다시 펴지려는 모멘트(back spring 현상)를 줄일 수 있으므로, 가로축 회전 롤러를 사용하지 않고도 상기 클래드 알루미늄 판재(100)를 파이프 형성으로 용이하게 조관 할 수 있게 된다.As described above, when the heights provided to the paper surface are different from each other, the back spring phenomenon that the rolled clad
다음, 상기 고주파 용접단계는 상기 조관단계를 통해 말아진 파이프의 마주하는 끝단부를 고주파 용접시키는 단계이다.Next, the high-frequency welding step is a step of high-frequency welding the opposing end portions of the pipe rolled through the pipe making step.
또한, 상기 고주파 용전답계는 유도코일(420)을 통해 전류가 흐르고, 임피더코어(410)에 의해 상기 클래드 알루미늄 파이프의 마주하는 끝단부로 전류가 집중되어, 높은 저항의 접촉면 금속을 녹이면서 파이프로 용접이 된다.The current flows through the
또한, 종래에 사용되고 있는 임피더코어의 직경보다 0.3mm가 더 긴 직경의 임피더코어(410)를 이용하게 되면, 용접성을 향상시킬 수 있다.In addition, if the use of the
다음, 사이징 단계는 고주파 용접단계를 통해 얻어진 파이프를 최종 제품으로 규격화시키는 단계이다. Next, the sizing step is a step of normalizing the pipe obtained through the high-frequency welding step to the final product.
또한, 상기 사이징 단계는 복수개의 세로축 회전 롤러 및 가로축 회전롤러로 구성되는 사이징기(700)를 이용하여, 상기 파이프의 직경을 축소시킨다.In the sizing step, the diameter of the pipe is reduced by using a
또한, 상기 고주파 용접단계를 통해 얻어진 파이프의 외경은 최종제품의 외경보다 0.8 내지 1.2mm 크게 용접되어, 상기 사이징 단계가 수행되는 것이 바람직하다.The outer diameter of the pipe obtained through the high frequency welding step is preferably 0.8 to 1.2 mm larger than the outer diameter of the final product, and the sizing step is preferably performed.
이는 최종 제품의 외경보다 0.8 내지 1.2mm 크게 용접하여, 최적의 용접성을 확보하기 위함이다.This is to ensure optimal weldability by welding 0.8 to 1.2 mm larger than the outer diameter of the final product.
하지만, 상기 사이징 단계에서 상기 파이프의 외경을 축소시키게 되면, 상기 파이프의 두께가 증가하게 되어, 원하는 두께의 최종제품을 생산할 수 없다.However, if the outer diameter of the pipe is reduced in the sizing step, the thickness of the pipe increases, so that a final product having a desired thickness can not be produced.
그래서, 상기 고주파 용접단계를 통해 얻어진 파이프의 외경이 상기 최종 제품의 외경보다 0.8mm 내지 0.9mm 크게 형성될 경우에는 상기 클래드 알루미늄 판재의 두께와 상기 그루브의 높이를 0.04mm 감소시켜 용접을 수행한다.Therefore, when the outer diameter of the pipe obtained through the high frequency welding step is 0.8 mm to 0.9 mm larger than the outer diameter of the final product, the thickness of the clad aluminum plate and the height of the groove are reduced by 0.04 mm.
또한, 상기 고주파 용접단계를 통해 얻어진 파이프의 외경이 상기 최종 제품의 외경보다 1.0mm 내지 1.2mm 크게 형성될 경우에는 상기 클래드 알루미늄 판재의 두께와 상기 그루브의 높이를 0.05mm 감소시켜 용접을 수행한다.When the outer diameter of the pipe obtained through the high frequency welding step is larger than the outer diameter of the final product by 1.0 mm to 1.2 mm, welding is performed by reducing the thickness of the clad aluminum plate and the height of the groove by 0.05 mm.
이는 아래의 표1과 같이 용접규격 증가에 따른 사이징 단계 후 두께 증가율에 기반한 것으로 증가하는 두께만큼 클래드 알루미늄의 두께와 그루브의 높이를 감소시켜 원하는 규격의 최종제품을 얻기 위함이다.
This is based on the thickness increase rate after the sizing step according to the increase of the welding standard as shown in Table 1 below. In order to obtain the final product of the desired standard by decreasing the thickness of the clad aluminum and the height of the groove by the increased thickness.
이와 같이, 상기 고주파 용접단계에서 증가된 상기 파이프의 외경 길이를 기준으로, 상기 클래드 알루미늄 판재의 두께와 상기 그루브의 높이를 본 발명에 따라 설정된 기준으로 조절하게 되면, 원하는 규격의 최종제품을 제조할 수 있게 된다.If the thickness of the clad aluminum plate and the height of the groove are adjusted to the reference value set in accordance with the present invention based on the outer diameter of the pipe increased in the high frequency welding step, .
또한, 상기 고주파 용접단계와, 상기 사이징 단계 사이에는, 비파과검사기(500)를 이용하여, 파이프 내부의 결함을 확인할 수 있고, 비드제거기(600)를 이용하여, 용접시 발생한 비드를 제거하는 과정이 수반될 수 있다.Also, between the high-frequency welding step and the sizing step, a defect in the pipe can be confirmed by using the
다음으로, 사이징된 파이프를 설정된 길이로 커팅기(800)를 이용하여 절단하는 절단단계가 수행되어, 클래드 알루미늄 파이프(900)를 제조한다.Next, a cutting step of cutting the sized pipe to a predetermined length by using the
상기 클래드 알루미늄 파이프(900)는 도 3에 도시된 바와 같이, 알루미늄 코어(910) 및 알루미늄 클래드(920)를 포함하고, 상기 그루부 형성단계를 통해, 상기 알루미늄 코어(910)의 내측에는 그루브(211)가 복수개 형성된다.As shown in FIG. 3, the clad
또한, 상기 그루브(211)는 냉매의 유체거동 효과가 상승되고, 열전달효율을 보다 향상시킬 수 있다.In addition, the grooves 211 can increase the fluid behavior of the refrigerant and improve the heat transfer efficiency.
또한, 상기 클래드 알루미늄 파이프가(900)가 방열핀에 결합하여, 하나의 열교환기로 제공될 수 있다.Also, the clad
또한, 상기 열교환기가 구비된 공조기로도 제공될 수 있다.Also, the air conditioner may be provided with the heat exchanger.
이상에서 살펴본 바와 같이 본 발명은 바람직한 실시예를 들어 도시하고 설명하였으나, 상기한 실시예에 한정되지 아니하며 본 발명의 정신을 벗어나지 않는 범위 내에서 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 다양한 변경과 수정이 가능할 것이다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation in the present invention. Various changes and modifications will be possible.
100 : 클래드 알루미늄 판재
200 : 그루브 형성 드럼
210 : 그루브 형성 돌기
300 : 이송롤러
400 : 고주파 용접기
410 : 임피더코어
420 : 유도 코일
500 : 비파괴 검사기
600 : 비드제거기
700 : 사이징기
800 : 커팅기
900 : 클래드 알루미늄 파이프
910 : 알루미늄 코어
920 : 알루미늄 클래드
911 : 그루브100: clad aluminum plate 200: groove forming drum
210: groove forming projection 300: conveying roller
400: High frequency welding machine 410: Impede core
420: induction coil 500: nondestructive inspection machine
600: bead remover 700: sizing machine
800: Cutting machine 900: Clad aluminum pipe
910: Aluminum core 920: Aluminum clad
911: Groove
Claims (6)
클래드 알루미늄 판재를 이송시키며, 알루미늄 코어면에 그루브를 형성하는 그루브 형성단계;
그루브가 형성된 클래드 알루미늄 판재를 복수개의 이송 롤러를 통해 파이프 형상으로 말아지게 하는 파이프 조관단계;
상기 조관단계를 통해 말아진 클래드 알루미늄 파이프의 마주하는 끝단부를 고주파 용접시키는 고주파 용접단계;
상기 고주파 용접단계를 통해 얻어진 파이프의 직경을 축소시키는 사이징 단계; 및
사이징된 파이프를 설정된 길이로 절단하여 최종제품을 생산하는 절단단계를 포함하고,
상기 고주파 용접단계를 통해 얻어진 파이프의 외경은 상기 최종제품의 외경보다 0.8 내지 1.2mm 큰 것을 특징으로 하는 열교환기용 클래드 알루미늄 파이프의 제조방법.
A method of manufacturing a clad aluminum pipe for a heat exchanger for brazing welding to a radiating fin of a heat exchanger,
A groove forming step of transferring the clad aluminum plate material and forming a groove on the aluminum core surface;
A pipe gauging step of causing a clad aluminum plate material on which a groove is formed to roll in a pipe shape through a plurality of feed rollers;
A high frequency welding step of high-frequency welding the opposite end portions of the rolled clad aluminum pipe through the tube making step;
A sizing step of reducing the diameter of the pipe obtained through the high frequency welding step; And
And cutting the sized pipe into a predetermined length to produce a final product,
Wherein the outer diameter of the pipe obtained through the high frequency welding step is 0.8 to 1.2 mm larger than the outer diameter of the final product.
상기 고주파 용접단계를 통해 얻어진 파이프의 외경이 상기 최종 제품의 외경보다 0.8mm 내지 0.9mm 크게 형성될 경우에는 상기 클래드 알루미늄 판재의 두께와 상기 그루브의 높이를 0.04mm 감소시켜 용접을 수행하고, 상기 고주파 용접단계를 통해 얻어진 파이프의 외경이 상기 최종 제품의 외경보다 1.0mm 내지 1.2mm 크게 형성될 경우에는 상기 클래드 알루미늄 판재의 두께와 상기 그루브의 높이를 0.05mm 감소시켜 용접을 수행하는 것을 특징으로 하는 열교환기용 클래드 알루미늄 파이프의 제조방법.
The method according to claim 1,
Wherein when the outer diameter of the pipe obtained through the high frequency welding step is 0.8 mm to 0.9 mm larger than the outer diameter of the final product, welding is performed by reducing the thickness of the clad aluminum plate and the height of the groove by 0.04 mm, Wherein when the outer diameter of the pipe obtained through the welding step is larger than the outer diameter of the final product by 1.0 mm to 1.2 mm, welding is performed by reducing the thickness of the clad aluminum plate and the height of the groove by 0.05 mm. (METHOD FOR MANUFACTURING CLAD ALUMINUM PIPE)
상기 이송 롤러들은 세로 회전축을 중심으로 회전하는 세로축 회전 롤러이며, 이웃하는 상기 이송 롤러들은 지면에 대해 설치된 높이가 서로 다른 것을 특징으로 하는 열교환기용 클래드 알루미늄 파이프의 제조방법.
The method according to claim 1,
Wherein the conveying rollers are longitudinally rotating rollers rotating about a longitudinal axis of rotation and adjacent conveying rollers have different heights relative to the ground.
A clad aluminum pipe produced by the method of manufacturing a clad aluminum pipe according to any one of claims 1 to 3.
A heat exchanger comprising the clad aluminum pipe of claim 4.