KR20150122827A - Photosensitive waterprroof agent and waterproof coating method of printed circuit board using the same - Google Patents
Photosensitive waterprroof agent and waterproof coating method of printed circuit board using the same Download PDFInfo
- Publication number
- KR20150122827A KR20150122827A KR1020140048506A KR20140048506A KR20150122827A KR 20150122827 A KR20150122827 A KR 20150122827A KR 1020140048506 A KR1020140048506 A KR 1020140048506A KR 20140048506 A KR20140048506 A KR 20140048506A KR 20150122827 A KR20150122827 A KR 20150122827A
- Authority
- KR
- South Korea
- Prior art keywords
- light
- water
- coating
- agent
- waterproof coating
- Prior art date
Abstract
Description
본 발명은 광감성 방수 코팅제 및 이를 이용한 인쇄회로기판의 방수 코팅 방법에 관한 것으로, 보다 상세하게는 양산 과정 시 전자 부품이 실장된 인쇄회로기판의 표면에 광감성 방수 코팅제를 코팅한 후, 방수 코팅이 균일하게 이루어진 상태를 육안으로 식별하는 것이 가능한 육안 검사가 가능한 광감성 방수 코팅제 및 이를 이용한 인쇄회로기판의 방수 코팅 방법에 관한 것이다.The present invention relates to a light-sensitive water-repellent coating agent and a method of coating a water-repellent coating on a printed circuit board using the same, and more particularly, And a waterproof coating method for a printed circuit board using the same. 2. Description of the Related Art
최근, 모바일(mobile) 및 웨어러블(wearable) 디바이스들에 방수 코팅을 실시하고자 하는 연구가 활발히 진행되고 있다.In recent years, studies have been actively conducted to apply waterproof coatings to mobile and wearable devices.
이러한 방수 코팅은 제품의 외부에 더불어 내부, 즉 전자 부품에 대해서도 이루어져야 한다. 이를 위해, 전자 부품이 실장된 인쇄회로기판에 대해서도 방수 코팅을 실시하게 되는데, 전자 부품이 실장된 인쇄회로기판의 경우 필름과 같이 완전한 평면이 아니므로 방수 코팅이 균일하면서 빈틈 없이 이루어지기 어려울 뿐만 아니라, 방수 코팅이 균일하게 이루어진 것을 확인하는 것조차 어려운 실정이다.Such a waterproof coating should be made for the interior of the product, as well as for the electronic components. For this purpose, a waterproof coating is also applied to a printed circuit board on which electronic components are mounted. In the case of a printed circuit board on which electronic components are mounted, the waterproof coating is not uniformly and seamlessly formed , It is difficult to confirm that the waterproof coating is evenly formed.
따라서, 종래에 따른 방수 코팅제를 이용하여 전자 부품이 실장된 인쇄회로기판의 표면에 방수 코팅을 실시하더라도, 방수 코팅이 균일하면서 빈틈 없이 확인하는 것 자체가 불가능한 관계로 양산 적용에 어려움이 따르고 있다.Accordingly, even if the waterproof coating is applied to the surface of the printed circuit board on which the electronic component is mounted using the conventional waterproof coating agent, it is impossible to check the waterproof coating uniformly and tightly.
관련 선행 문헌으로는 대한민국 등록실용신안공보 제20-0409852호 (2006.03.03. 공고)가 있으며, 상기 문헌에는 방수 기능이 있는 휴대형 데이터 저장 장치가 기재되어 있다.
A related prior art document is the Korean Utility Model Registration No. 20-0409852 (published on Mar. 3, 2006), which describes a portable data storage device having a waterproof function.
본 발명의 목적은 방수 코팅 용액인 변성 불소실산 나노 고분자 화합물의 말단기를 활성시키고 UV-Vis 영역 내의 특정 파장 조사시 가시광선을 발산시키는 광감응제를 첨가함으로써, 방수 코팅이 균일하게 이루어진 상태를 육안으로 식별할 수 있는 광감성 방수 코팅제 및 이를 이용한 인쇄회로기판의 방수 코팅 방법을 제공하는 것이다.
It is an object of the present invention to provide a water-repellent coating solution which activates a terminal group of a modified nanofiber polymeric nanofiber compound and adds a light-sensitive agent which emits visible light when irradiating a specific wavelength in a UV-Vis region, And to provide a waterproof coating method for a printed circuit board using the same.
상기 목적을 달성하기 위한 본 발명의 실시 예에 따른 육안 검사가 가능한 광감성 방수 코팅제는 방수 코팅 용액 100 부피비에 대하여, 광감응제 10 부피비 이하로 첨가된 것을 특징으로 한다.
In order to accomplish the above object, the present invention provides a water-repellent, water-repellent coating material capable of being visually inspected according to an embodiment of the present invention.
상기 목적을 달성하기 위한 본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제를 이용한 인쇄회로기판의 방수 코팅 방법은 (a) 방수 코팅 용액 100 부피비에 대하여, 광감응제 10 부피비 이하로 혼합한 광감성 방수 코팅제를 전자 부품이 실장된 인쇄회로기판의 표면에 코팅하여 광감성 방수 코팅 물질층을 형성하는 단계; (b) 상기 광감성 방수 코팅 물질층을 경화하여 광감성 방수 코팅층을 형성하는 단계; 및 (c) 상기 광감성 방수 코팅층에 200 ~ 700nm의 UV-Vis 영역 내의 특정 파장을 조사하여, 상기 광감성 방수 코팅층의 코팅 상태를 육안으로 검사하는 단계를 포함하는 것을 특징으로 한다.
In order to accomplish the above object, there is provided a waterproof coating method of a printed circuit board using a photosensitive waterproof coating agent capable of visual inspection according to an embodiment of the present invention, comprising the steps of: (a) Forming a light-sensitive waterproof coating material layer by coating a light-sensitive waterproof coating agent on a surface of a printed circuit board on which electronic components are mounted; (b) curing the photosensitive waterproof coating material layer to form a light-sensitive waterproof coating layer; And (c) irradiating the light-sensitive waterproof coating layer with a specific wavelength within a UV-Vis region of 200 to 700 nm to visually inspect the coating state of the light-sensitive waterproof coating layer.
본 발명에 따른 육안 검사가 가능한 광감성 방수 코팅제 및 이를 이용한 검사 방법은 양산 과정시 전자 부품이 실장된 인쇄회로기판의 표면에 광감성 방수 코팅제를 코팅한 후, 200 ~ 700nm의 UV-Vis 영역 내의 특정 파장을 조사하게 되면 광감성 방수 코팅제에 함유된 광감응제가 화학발광에 의해 가시광선의 빛을 발산하게 됨으로써, 방수 코팅이 균일하게 이루어진 상태를 육안으로 식별하는 것이 가능해질 수 있다.In the light-sensitive water-repellent coating agent capable of visual inspection according to the present invention and the inspection method using the same, the light-sensitive water-repellent coating agent is coated on the surface of the printed circuit board on which electronic components are mounted during the mass production process, When a specific wavelength is irradiated, the light-sensitive material contained in the light-sensitive water-repellent coating agent emits light of visible light by chemiluminescence, thereby making it possible to visually discriminate a state in which the water-repellent coating is uniform.
따라서, 본 발명에 따른 육안 검사가 가능한 광감성 방수 코팅제 및 이를 이용한 인쇄회로기판의 방수 코팅 방법은 방수 코팅 양산 과정에서 코팅의 유무와 코팅 상태를 육안으로 판별하는 것이 가능해짐으로써, 생산 수율을 향상시킬 수 있다.
Accordingly, the light-sensitive water-repellent coating agent that can be visually inspected according to the present invention and the water-repellent coating method of a printed circuit board using the same provide the ability to visually discriminate presence or absence of coating and the coating state during the process of mass- .
도 1은 본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제를 이용한 인쇄회로기판의 방수 코팅 방법을 나타낸 공정 순서도이다.1 is a flowchart showing a waterproof coating method of a printed circuit board using a light-sensitive waterproof coating agent capable of visual inspection according to an embodiment of the present invention.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예를 참조하면 명확해질 것이다. 그러나, 본 발명은 이하에서 개시된 실시예에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예는 본 발명의 개시가 완전하도록 하고, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이다. 또한, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. 명세서 전체에 걸쳐 동일 참조 부호는 동일 구성요소를 지칭한다.BRIEF DESCRIPTION OF THE DRAWINGS The advantages and features of the present invention, and how to accomplish them, will become apparent by reference to the embodiments described in detail below with reference to the accompanying drawings. It should be understood, however, that the present invention is not limited to the disclosed embodiments, but may be embodied in many different forms and should not be construed as limited to the exemplary embodiments set forth herein, It is provided to inform the person completely of the scope of the invention. Further, the present invention is only defined by the scope of the claims. Like reference numerals refer to like elements throughout the specification.
이하 첨부된 도면을 참조하여 본 발명의 바람직한 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제 및 이를 이용한 인쇄회로기판의 방수 코팅 방법에 관하여 상세히 설명하면 다음과 같다.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Reference will now be made in detail to the preferred embodiments of the present invention, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the like elements throughout.
광감성Light sensitivity 방수 코팅제 Waterproof coating agent
본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제는 방수 코팅 용액 100 부피비에 대하여, 광감응제 10 부피비 이하로 첨가되는 것이 바람직하며, 구체적으로는 0.1 ~ 10 부피비, 보다 구체적으로는 3 ~ 6 부피비로 첨가되는 것이 바람직하다.The light-sensitive water-repellent coating agent which can be visually inspected according to the embodiment of the present invention is preferably added in an amount of 10 volume% or less, preferably 0.1 to 10 volume%, more preferably 3 volume% To 6 parts by volume.
이때, 광감응제의 첨가량이, 방수 코팅 용액 100 부피비에 대하여, 0.1 부피비 미만일 경우에는 그 첨가량이 미미한 관계로 UV-Vis 영역 내의 특정 파장 조사시 발광 효율이 미미할 수 있으므로 바람직하지 못하다. 반대로, 광감응제의 첨가량이, 방수 코팅 용액 100 부피비에 대하여, 10 부피비를 초과할 경우에는 접착력을 저하시킬 뿐만 아니라, 다량 첨가로 제조 원가를 상승시킬 우려가 크므로, 경제적이지 못하다.
If the addition amount of the photo-sensitizer is less than 0.1 volume ratio with respect to 100 volume ratio of the water-proof coating solution, the light-emitting efficiency may be insignificant when the specific wavelength is irradiated in the UV-Vis region because the added amount thereof is insignificant. On the other hand, when the amount of the photosensitizer added is more than 10 parts by volume with respect to 100 parts by volume of the waterproof coating solution, not only the adhesive strength is lowered but also the production cost is increased by adding a large amount of the photosensitive agent.
상기 방수 코팅 용액은 변성 불소실란 나노 고분자 화합물 : 0.5 ~ 7 중량%, 경화제 : 0.1 ~ 2.5 중량 % 및 유기 용매 : 90.5 ~ 99.4 중량%로 조성되는 것이 바람직하다.
The waterproof coating solution is preferably composed of 0.5 to 7 wt% of a modified fluorine silane nano-polymer compound, 0.1 to 2.5 wt% of a curing agent, and 90.5 to 99.4 wt% of an organic solvent.
변성 불소실산 나노 고분자 화합물은 하기 화학식 1의 분자 구조를 갖는다.
The denatured fluorine-containing nano-polymer compound has a molecular structure represented by the following formula (1).
[화학식 1][Chemical Formula 1]
AO-(-CF2-CF(CF3)-O-)x-(-CF2-CF2-O)y-(-CF2-O-)z-B AO - (- CF 2 -CF ( CF 3) -O-) x - (- CF 2 -CF 2 -O) y - (- CF 2 -O-) zB
(여기서, A, B는 CF2CH2O-(-C2H4-O)n-C3H6Si-(-OR)3이며, 1≤x≤8, 1≤y≤6, 1≤z≤6이고, R은 탄소수 1 ~ 10의 직쇄 또는 분지쇄 알킬기이며, n은 1 ~ 8의 정수임.)(Where A and B are CF 2 CH 2 O - (- C 2 H 4 --O) n C 3 H 6 Si - (- OR) 3 and 1≤x≤8, 1≤y≤6, 1≤z R is a linear or branched alkyl group having 1 to 10 carbon atoms, and n is an integer of 1 to 8).
PFPE(과불소에테르기) 고분자는 일반적인 유기 용제와는 상용성이 전혀 없다. 따라서 불소용제만을 이용하여 매우 묽은 희석상태에서 히드로실레이션(hydrosilylation) 계면 반응을 실시하여야 한다.PFPE (perfluorinated ether group) polymers are incompatible with common organic solvents. Therefore, a hydrosilylation interfacial reaction should be performed in a very diluted state using only a fluorine solvent.
본 발명에서는 PFPE를 기본 구조로 하되, 접착력 향상을 위하여 PFPE 구조와 실란 구조 사이에 폴리알킬렌 옥사이드 기능기를 포함하는 퍼플루오로폴리에테르 변성 실란계 불소 고분자 화합물을 합성 및 정제한 후, UV-Vis 영역 내의 특정 파장에 의해 화학발광이 가능한 광감응제를 결합시켰다.In the present invention, a perfluoropolyether-modified silane-based fluorine polymer compound having a polyalkylene oxide functional group between a PFPE structure and a silane structure was synthesized and purified to have a basic structure of PFPE, And a photo-sensitizer capable of chemiluminescence by specific wavelengths in the region were combined.
특히, 본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제는 전자 부품이 실장된 인쇄회로기판의 표면에 코팅되며, 200 ~ 700nm의 UV-Vis 영역 내의 특정 파장을 조사시 화학발광에 의해 가시광선의 빛을 발산하게 된다. 이 결과, 본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제는 방수코팅 양산 과정에서 코팅의 유무와 코팅 상태를 육안으로 판별하는 것에 의해 생산 수율을 향상시킬 수 있다.In particular, the light-sensitive water-repellent coating agent capable of visual inspection according to the embodiment of the present invention is coated on the surface of a printed circuit board on which electronic components are mounted, and is chemically luminescent when irradiating a specific wavelength within a UV- And emits visible light. As a result, the light-sensitive water-repellent coating agent which can be visually inspected according to the embodiment of the present invention can improve production yield by visually discriminating presence or absence of the coating and the coating state during the water-resistance coating mass production process.
이때, 화학식 1의 변성 불소실란 나노 고분자 화합물은 양말단이 히드록시 기능기로 특성화된 PFPE를 이용하여 양말단을 트리알콕시실란으로 변성하여 고농축 PFPE계 변성 실란계 고분자 화합물을 제조하고, 상용성이 우수한 용제 및 경화제를 선정하여 지문방지 특성 등 우수한 방수성 및 방오성을 확보할 수 있음과 더불어, 광감응제를 결합시켜 방수코팅의 유무와 코팅 상태를 육안으로 검사하는 것이 가능하다.
At this time, the modified fluorine silane nano-macromolecular compound of the formula (1) is modified with trialkoxysilane at both ends using PFPE characterized by hydroxy functional groups at both ends to produce highly concentrated PFPE-based modified silane-based polymer compounds, It is possible to visually inspect whether or not the waterproof coating is present and the coating state by bonding the light-sensitive agent, in addition to securing excellent waterproofness and antifouling property such as a fingerprint prevention characteristic by selecting a solvent and a curing agent.
유기 용매는 퍼플루오로카본계(perfluorocarbon), 퍼플루오로알칸계(perfluoroalkan), 퍼플루오로폴리에테르계(perfluoroplyether), 히드로플루오로카본계(hydrofluorocarbon) 등을 포함하는 불소계 용매 중 선택된 1종 이상이 이용될 수 있다.The organic solvent may be at least one selected from the group consisting of perfluorocarbons, perfluoroalkanes, perfluoroplyethers, and fluorinated solvents including hydrofluorocarbons Can be used.
경화제는 R-(NCO)3의 화합물이 이용될 수 있다. 여기서, R은 탄소수 1 ~ 10의 알킬기이다. 이들 중, 바람직한 경화제는 폴리카복실산 무수물, 예를들면, 나드산 무수물(NA), 메틸나드산 무수물, 1,4-사이클로헥산-비스(메틸아민), 1,3-비스(3-아미노프로필)테트라메틸디실록산, 헥사메틸렌디아민, 트리에틸렌테트라아민, N-아미노에틸 피페라진, 1,3-디아미노벤젠, 1,4-디아미노벤젠, 4,4'-디아미노디페닐메탄 및 폴리아미노설폰, 또한 폴리올, 예를들면 에틸렌 글리콜, 폴리(프로필렌 글리콜), 및 폴리(비닐알콜)를 제시할 수 있다.
The curing agent may be a compound of R- (NCO) 3 . Here, R is an alkyl group having 1 to 10 carbon atoms. Among these, preferred curing agents are polycarboxylic acid anhydrides such as nadic anhydride (NA), methylnadic anhydride, 1,4-cyclohexane-bis (methylamine), 1,3- Tetramethyldisiloxane, hexamethylenediamine, triethylenetetramine, N-aminoethylpiperazine, 1,3-diaminobenzene, 1,4-diaminobenzene, 4,4'-diaminodiphenylmethane and polyamino Sulfone, polyols such as ethylene glycol, poly (propylene glycol), and poly (vinyl alcohol).
특히, 광감응제는 변성 불소실산 나노 고분자 화합물의 말단기에 결합하여 UV-Vis 영역 내의 특정 파장을 흡수시 가시광선, 보다 구체적으로는 550 ~ 800nm의 흡수파장 영역에서 빛을 발산시키는 역할을 한다.Particularly, the photo-sensitizer has a role of emitting light in visible light, more specifically in the absorption wavelength region of 550 to 800 nm when absorbing a specific wavelength in the UV-Vis region by binding to the terminal group of the modified non-aqueous polymer nano- do.
이러한 광감응제로는 블루(blue) 영역의 중심 파장대에서 광흡수피크를 갖는 광감응제 A, 그린(green) 영역의 중심 파장대에서 광흡수피크를 갖는 광감응제 B, 레드(red) 영역의 중심 파장대에서 광흡수피크를 갖는 광감응제 C 중 선택된 1종 이상이 이용될 수 있다.Examples of such photosensitizer include a photosensitizer A having a light absorption peak at a central wavelength region of a blue region, a photo-sensitizer B having a light absorption peak at a central wavelength region of a green region, And a photosensitizer C having a light absorption peak at a wavelength band may be used.
이때, 광감응제 A는 하이포크레린 B(Hypocrellin B), 아크리딘오렌지(Acridine orange) 및 쿠마린(Coumarin) 중 선택된 1종 이상을 포함하고, 광감응제 B는 로즈 벵갈(Rose Bengal), 로다민 B(Rhodamine B), 메로시아닌 540(Merocyanine 540) 중 선택된 1종 이상을 포함하며, 광감응제 C는 메틸렌 블루(Methylene blue), 페오포르바이드 A(Pheophorbide A), 크립토시아닌(Cryotocyanine) 중 선택된 1종 이상을 포함할 수 있다.The photosensitizer A comprises at least one selected from the group consisting of Hypocrellin B, Acridine orange and Coumarin, and the photosensitizer B is at least one selected from the group consisting of Rose Bengal, Rhodamine B, Merocyanine 540, and the photosensitizer C includes at least one selected from the group consisting of methylene blue, Pheophorbide A, cryptoside Cryotocyanine). ≪ / RTI >
또한, 광감응제는 포리피린계 화합물 및 그 치환체, 프탈로시아닌계 화합물 및 그 치환체 및 염료 중 선택된 1종 이상을 포함할 수 있다.Further, the photosensitizer may include at least one selected from the group consisting of a polyimide compound, a substituent thereof, a phthalocyanine compound, a substituent thereof, and a dye.
또한, 광감응제는 5,10,15-트리페닐-20-(4-카르복시페닐)-포르피린백금(5,10,15-triphenyl-20-(4-carboxyphenyl)-porphyrin platinum, PtCP), 5,15-비스페닐-10,20-비스(4-메톡시카르보닐페닐)-포르피린백금(5-15-bisphenyl-10,20-bis(4-methoxycarbonylphenyl)-porphyrin platinum, tPtCP), 테트라페닐포르피린(tetraphenyl porphyrin, H2TPP), 헤마토포르피린(hemato porphyrin, HP), 프로토포르피린(proto porphyrin, PP), 인도시아닌그린(indocyanin green, ICG) 및 메조-테트라키스(p-설포나토페닐)포르피린(meso-tetrakis (p-sulfonatopheny)porphyrin, TSPP) 중 선택된 1종 이상을 포함할 수도 있다.
Also, the photosensitizer is 5,10,15-triphenyl-20- (4-carboxyphenyl) -porphyrin platinum (PtCP), 5 Bisphenyl-10,20-bis (4-methoxycarbonylphenyl) -porphyrin platinum, tPtCP), 15-bisphenyl-10,20-bis (4-methoxycarbonylphenyl) (HTPP), hemato porphyrin (HP), proto porphyrin (PP), indocyanin green (ICG) and meso-tetrakis (p-sulphonatophenyl) porphyrin meso-tetrakis (p-sulfonatopheny) porphyrin, TSPP).
이하, 첨부된 도면을 참조하여 본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제를 이용한 인쇄회로기판의 방수 코팅 방법에 대하여 설명하도록 한다.
Hereinafter, a waterproof coating method of a printed circuit board using a light-sensitive waterproof coating agent capable of visual inspection according to an embodiment of the present invention will be described with reference to the accompanying drawings.
도 1은 본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제를 이용한 인쇄회로기판의 방수 코팅 방법을 나타낸 공정 순서도이다.1 is a flowchart showing a waterproof coating method of a printed circuit board using a light-sensitive waterproof coating agent capable of visual inspection according to an embodiment of the present invention.
도 1을 참조하면, 도시된 본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제를 이용한 인쇄회로기판의 방수 코팅 방법은 코팅 단계(S110), 경화 단계(S120) 및 육안 검사 단계(S130)를 포함한다.
Referring to FIG. 1, a waterproof coating method of a printed circuit board using a light-sensitive waterproof coating agent capable of visual inspection according to an embodiment of the present invention includes a coating step S110, a curing step S120, and a visual inspection step S130 ).
코팅coating
코팅 단계(S110)에서는 방수 코팅 용액 100 부피비에 대하여, 광감응제 10 이하의 부피비로 혼합한 광감성 방수 코팅제를 전자 부품이 실장된 인쇄회로기판의 표면에 코팅하여 광감성 방수 코팅 물질층을 형성한다.In the coating step (S110), a light-sensitive water-repellent coating agent mixed at a volume ratio of 10 or less of the photosensitive agent to 100 parts by volume of the water-repellent coating solution is coated on the surface of the printed circuit board on which the electronic parts are mounted to form a photosensitive water- do.
이때, 혼합은 200 ~ 800rpm의 교반 속도로 1 ~ 10분 동안 실시하는 것이 바람직하다. 교반 속도가 200rpm 미만이거나, 교반 시간이 1분 미만일 경우에는 균일한 혼합이 이루어지지 못할 우려가 크다. 반대로, 교반 속도가 800rpm을 초과하거나, 교반 시간이 10분을 초과할 경우에는 더 이상의 효과 상승 없이 제조 비용만을 상승시키는 요인으로 작용할 수 있으므로, 경제적이지 못하다.
In this case, mixing is preferably carried out at a stirring speed of 200 to 800 rpm for 1 to 10 minutes. When the stirring speed is less than 200 rpm or the stirring time is less than 1 minute, there is a possibility that uniform mixing is not achieved. On the other hand, when the stirring speed exceeds 800 rpm or the stirring time exceeds 10 minutes, it may be a factor for raising the manufacturing cost without further increase in the effect, which is not economical.
경화Hardening
경화 단계(S120)에서는 광감성 방수 코팅 물질층을 경화하여 광감성 방수 코팅층을 형성한다. 이때, 경화는 70 ~ 150℃로 실시하는 것이 적절하다. 이러한 경화 과정에 의해, 광감성 방수 코팅 물질층에 함유된 유기 용매가 제거될 수 있다. 또한, 경화 단계(S120)를 거치면서 방수코팅물질이 인쇄회로기판의 표면과 단단한 결합을 하며 코팅이 이루어진다.
In the curing step S120, the light-sensitive waterproof coating material layer is cured to form a light-sensitive waterproof coating layer. In this case, the curing is preferably carried out at 70 to 150 ° C. By this curing process, the organic solvent contained in the light-sensitive waterproof coating material layer can be removed. In addition, through the curing step (S120), the waterproof coating material is tightly bonded to the surface of the printed circuit board and coating is performed.
육안 검사Visual inspection
육안 검사 단계(S130)에서는 광감성 방수 코팅층에 200 ~ 700nm의 UV-Vis 영역 내의 특정 파장을 조사하여, 광감성 방수 코팅층의 코팅 상태를 육안으로 검사한다.In the visual inspection step (S130), a specific wavelength in a UV-Vis region of 200 to 700 nm is irradiated on the light-sensitive water-repellent coating layer, and the coating state of the light-emissive water-repellent coating layer is visually inspected.
이와 같이, 전자 부품이 실장된 인쇄회로기판의 표면을 덮는 광감성 방수 코팅층에 대하여 200 ~ 700nm의 UV-Vis 영역 내의 특정 파장을 조사하게 되면, 화학발광에 의해 가시광선의 빛을 발산하게 되며, 이 결과 방수 코팅 양산 과정에서 코팅의 유무와 코팅 상태를 육안으로 판별하는 것이 가능해질 수 있다.
When a specific wavelength in a UV-Vis region of 200 to 700 nm is irradiated on the light-sensitive water-repellent coating layer covering the surface of the printed circuit board on which the electronic component is mounted, visible light is emitted by chemiluminescence, As a result, it is possible to visually discriminate presence or absence of the coating and the coating state during the process of mass production of the waterproof coating.
전술한 본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제 및 이를 이용한 인쇄회로기판의 방수 코팅 방법은 양산 과정시 전자 부품이 실장된 인쇄회로기판의 표면에 광감성 방수 코팅제를 코팅한 후, 200 ~ 700nm의 UV-Vis 영역 내의 특정 파장을 조사하게 되면 광감성 방수 코팅제에 함유된 광감응제가 화학발광에 의해 가시광선의 빛을 발산하게 됨으로써, 방수 코팅이 균일하게 이루어진 상태를 육안으로 식별하는 것이 가능해질 수 있다.A light-sensitive water-repellent coating agent capable of visual inspection according to an embodiment of the present invention and a water-repellent coating method of a printed circuit board using the same can be manufactured by coating a light-sensitive water-repellent coating agent on the surface of a printed circuit board , When the specific wavelength in the UV-Vis region of 200 to 700 nm is irradiated, the photosensitive agent contained in the light-sensitive water-proof coating agent emits light of visible light by chemiluminescence, thereby visually recognizing the state in which the water- It can be possible.
따라서, 본 발명의 실시예에 따른 육안 검사가 가능한 광감성 방수 코팅제 및 이를 이용한 인쇄회로기판의 방수 코팅 방법은 방수 코팅 양산 과정에서 코팅의 유무와 코팅 상태를 육안으로 판별하는 것이 가능해짐으로써, 생산 수율을 향상시킬 수 있다.
Accordingly, the light-sensitive water-repellent coating agent capable of visual inspection according to the embodiment of the present invention and the water-repellent coating method of the printed circuit board using the same can visually discriminate the presence or the coating state of the water- The yield can be improved.
실시예Example
이하, 본 발명의 바람직한 실시예를 통해 본 발명의 구성 및 작용을 더욱 상세히 설명하기로 한다. 다만, 이는 본 발명의 바람직한 예시로 제시된 것이며 어떠한 의미로도 이에 의해 본 발명이 제한되는 것으로 해석될 수는 없다.Hereinafter, the configuration and operation of the present invention will be described in more detail with reference to preferred embodiments of the present invention. It is to be understood, however, that the same is by way of illustration and example only and is not to be construed in a limiting sense.
여기에 기재되지 않은 내용은 이 기술 분야에서 숙련된 자이면 충분히 기술적으로 유추할 수 있는 것이므로 그 설명을 생략하기로 한다.
The contents not described here are sufficiently technically inferior to those skilled in the art, and a description thereof will be omitted.
1. 광감성 방수 코팅층 제조 1. Fabrication of light-sensitive waterproof coating layer
실시예 1Example 1
방수 코팅 용액 100 vol%에 대하여, 광감응제로 테트라페닐포르피린(tetraphenyl porphyrin, H2TPP) 3 vol%로 혼합한 광감성 방수 코팅제를 전자 부품이 실장된 인쇄회로기판의 표면에 분무 코팅 방식으로 5㎛의 두께로 코팅하여 광감성 방수 코팅 물질층을 형성하였다. 다음으로, 광감성 방수 코팅 물질층을 90℃에서 120℃ 사이의 인라인 오븐기에서 1분 내외로 처리되며 이때 용액이 경화하여 광감성 방수 코팅층을 형성하였다.The light-sensitive waterproof coating agent prepared by mixing 100 vol% of the waterproof coating solution with 3 vol% of tetraphenyl porphyrin (H2TPP) as a photosensitizer was applied to the surface of the printed circuit board on which electronic components were mounted by spray coating, To form a light-sensitive waterproof coating material layer. Next, the light-sensitive water-repellent coating material layer was treated in an in-line oven at 90 ° C to 120 ° C for about 1 minute, at which time the solution cured to form a light-sensitive water-repellent coating layer.
이때, 방수 코팅 용액으로는 변성 불소실란 나노 고분자 화합물(CF2CH2O-(-CH2-CH2-O)2-CH2-CH2-CH2Si-(-OCH3)3) 2 wt%, 경화제(헥사메틸렌디아민) 4 wt% 및 유기 용매(에톡시-노나플루오로부탄) 94 wt%로 조성된 것을 이용하였다.
In this case, the water the coating solution is a fluorine-modified silane nano polymer compound (CF 2 CH 2 O - ( - CH 2 -CH 2 -O) 2 -CH 2 -CH 2 -CH 2 Si - (- OCH 3) 3) 2 , 4 wt% of a hardening agent (hexamethylenediamine), and 94 wt% of an organic solvent (ethoxy-nonafluorobutane).
실시예 2Example 2
방수 코팅 용액 100 vol%에 대하여, 광감응제로 테트라페닐포르피린(tetraphenyl porphyrin, H2TPP) 6 vol%로 혼합한 광감성 방수 코팅제를 이용한 것을 제외하고는 실시예 1과 동일한 방법으로 광감성 방수 코팅층을 제조하였다.
A photosensitive waterproof coating layer was prepared in the same manner as in Example 1, except that a photosensitive waterproof coating agent prepared by mixing 6 vol% of tetraphenyl porphyrin (H2TPP) as a photosensitizer to 100 vol% of a waterproof coating solution was used. Respectively.
실시예 3Example 3
방수 코팅 용액 100 vol%에 대하여, 광감응제로 테트라페닐포르피린(tetraphenyl porphyrin, H2TPP) 2 vol%로 혼합한 광감성 방수 코팅제를 이용한 것을 제외하고는 실시예 1과 동일한 방법으로 광감성 방수 코팅층을 제조하였다.
A light-sensitive waterproof coating layer was prepared in the same manner as in Example 1, except that a photosensitive water-repellent coating material prepared by mixing 2 vol% of tetraphenyl porphyrin (H2TPP) as a photosensitizer with respect to 100 vol% of a water- Respectively.
실시예 4Example 4
광감응제로 인도시아닌그린(indocyanin green, ICG)을 이용한 것을 제외하고는 실시예 1과 동일한 방법으로 광감성 방수 코팅층을 제조하였다.
A light-sensitive waterproof coating layer was prepared in the same manner as in Example 1, except that indocyanin green (ICG) was used as a photosensitizer.
실시예 5Example 5
광감성 방수 코팅 물질층을 15㎛의 두께로 코팅한 것을 제외하고는 실시예 1과 동일한 방법으로 광감성 방수 코팅층을 제조하였다.
A light-sensitive waterproof coating layer was prepared in the same manner as in Example 1, except that the light-sensitive waterproof coating material layer was coated to a thickness of 15 탆.
비교예 1Comparative Example 1
방수 코팅 용액 100 vol%에 대하여, 광감응제로 테트라페닐포르피린(tetraphenyl porphyrin, H2TPP) 0.05 vol%로 혼합한 광감성 방수 코팅제를 이용한 것을 제외하고는 실시예 1과 동일한 방법으로 광감성 방수 코팅층을 제조하였다.
A light-sensitive waterproof coating layer was prepared in the same manner as in Example 1, except that a photosensitive waterproof coating agent prepared by mixing 0.05 vol% of tetraphenyl porphyrin (H2TPP) as a photosensitizer with respect to 100 vol% of a waterproof coating solution was used. Respectively.
2. UV-Vis 영역 내의 특정 파장 조사2. Specific wavelength irradiation in the UV-Vis region
실시예 1 ~ 5 및 비교예 1에 따라 제조된 광감성 방수 코팅층에 UV-Vis 영역 내의 특정 파장을 조사한 후, 광감성 방수 코팅층으로부터 발산되는 가시광선 영역의 특정 파장과 광량을 측정하였다. 이때, 광감성 방수 코팅층을 여기시키기 위하여 UV-Vis 램프(LAMP)를 이용하여 200 ~ 1100nm의 파장범위의 빛을 조사하였으며, 발광(excitation)된 스펙트럼 및 광량은 PL분광계(F-7000, Hitachi)를 이용하여 측정하였다.
The specific wavelengths and the amounts of light in the visible light region emitted from the light-sensitive waterproof coating layer were measured after irradiating specific wavelengths in the UV-Vis region to the light-sensitive waterproof coating layer prepared according to Examples 1 to 5 and Comparative Example 1. The excitation spectrum and the amount of light were measured with a PL spectrometer (F-7000, Hitachi) using a UV-Vis lamp (LAMP) to excite the light- .
3. 광량 측정 평가3. Photometric measurement evaluation
표 1은 실시예 1 ~ 5 및 비교예 1에 대한 광량 측정 결과를 나타낸 것이다.
Table 1 shows the results of the light amount measurement for Examples 1 to 5 and Comparative Example 1.
[표 1][Table 1]
표 1을 참조하면, 실시예 1 ~ 5의 경우에는 0.227 ~ 0.315 lmㆍs로 측정되었다. 반면, 비교예 1의 경우에는 실시예 1에 비하여 절반에 미치지 못하는 0.089 lmㆍs로 측정되었다.
Referring to Table 1, in the case of Examples 1 to 5, it was measured to be 0.227 to 0.315 lm · s. On the other hand, in the case of Comparative Example 1, it was measured to be 0.089 lm · s, which is less than half of that in Example 1. [
위의 실험 결과를 토대로, 실시예 1 ~ 5의 경우에는 자외선 조사 후, 광감성 방수 코팅층으로부터 발산되는 광량이 0.227 ~ 0.315 lmㆍs를 가짐으로써, 양산 과정시에도 코팅 유무 및 코팅 상태를 육안으로 판별하는 것이 가능하다는 것을 확인하였다.
On the basis of the above experimental results, in Examples 1 to 5, since the amount of light emitted from the light-sensitive waterproof coating layer after ultraviolet irradiation was 0.227 to 0.315 lm · s, the presence or the coating state of the coating It was confirmed that it is possible to discriminate between them.
이상에서는 본 발명의 실시예를 중심으로 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 기술자의 수준에서 다양한 변경이나 변형을 가할 수 있다. 이러한 변경과 변형은 본 발명이 제공하는 기술 사상의 범위를 벗어나지 않는 한 본 발명에 속한다고 할 수 있다. 따라서 본 발명의 권리범위는 이하에 기재되는 청구범위에 의해 판단되어야 할 것이다.
Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. These changes and modifications may be made without departing from the scope of the present invention. Accordingly, the scope of the present invention should be determined by the following claims.
S110 : 코팅 단계
S120 : 경화 단계
S130 : 육안 검사 단계S110: coating step
S120: Curing step
S130: visual inspection step
Claims (12)
Wherein the water-insoluble coating solution is added at a volume ratio of not more than 10 parts by volume of the photosensitive agent per 100 parts by volume of the water-proof coating solution.
상기 방수 코팅 용액은
변성 불소실란 나노 고분자 화합물 : 0.5 ~ 7 중량%, 경화제 : 0.1 ~ 2.5 중량 % 및 유기 용매 : 90.5 ~ 99.4 중량%로 조성되는 것을 특징으로 하는 육안 검사가 가능한 광감성 방수 코팅제.
The method according to claim 1,
The waterproof coating solution
The photosensitive waterproof coating composition according to any one of claims 1 to 3, wherein the fluorinated silane nano-polymer compound is 0.5 to 7 wt%, the curing agent is 0.1 to 2.5 wt%, and the organic solvent is 90.5 to 99.4 wt%.
상기 변성 불소실산 나노 고분자 화합물은
하기 화학식 1의 분자 구조를 갖는 것을 특징으로 하는 육안 검사가 가능한 광감성 방수 코팅제.
[화학식 1]
AO-(-CF2-CF(CF3)-O-)x-(-CF2-CF2-O)y-(-CF2-O-)z-B
(여기서, A, B는 CF2CH2O-(-C2H4-O)n-C3H6Si-(-OR)3이며, 1≤x≤8, 1≤y≤6, 1≤z≤6이고, R은 탄소수 1 ~ 10의 직쇄 또는 분지쇄 알킬기이며, n은 1 ~ 8의 정수임.)
3. The method of claim 2,
The modified fluorine-containing nano-polymer compound
A water-repellent, water-repellent coating capable of being visually inspected, having a molecular structure represented by the following formula (1).
[Chemical Formula 1]
AO - (- CF 2 -CF ( CF 3) -O-) x - (- CF 2 -CF 2 -O) y - (- CF 2 -O-) zB
(Where A and B are CF 2 CH 2 O - (- C 2 H 4 --O) n C 3 H 6 Si - (- OR) 3 and 1≤x≤8, 1≤y≤6, 1≤z R is a linear or branched alkyl group having 1 to 10 carbon atoms, and n is an integer of 1 to 8).
상기 광감성 방수 코팅제는
전자 부품이 실장된 인쇄회로기판의 표면에 코팅되며, 200 ~ 700nm의 UV-Vis 영역 내의 특정 파장을 조사하는 것에 의해 가시광선의 빛을 발산하는 것을 특징으로 하는 유안 검사가 가능한 광감성 방수 코팅제.
The method according to claim 1,
The light-sensitive waterproof coating agent
Wherein the coating layer is coated on a surface of a printed circuit board on which electronic components are mounted and emits visible light rays by irradiating a specific wavelength within a UV-Vis region of 200 to 700 nm.
상기 광감응제는
상기 방수 코팅 용액 100 부피비에 대하여, 3 ~ 6 부피비로 첨가된 것을 특징으로 하는 육안 검사가 가능한 광감성 방수 코팅제.
The method according to claim 1,
The light-
Wherein the water-repellent coating solution is added in a volume ratio of 3 to 6 per 100 parts by volume of the water-repellent coating solution.
상기 광감응제는
블루(blue) 영역의 중심 파장대에서 광흡수피크를 갖는 광감응제 A, 그린(green) 영역의 중심 파장대에서 광흡수피크를 갖는 광감응제 B, 레드(red) 영역의 중심 파장대에서 광흡수피크를 갖는 광감응제 C 중 선택된 1종 이상을 포함하는 것을 특징으로 하는 육안 검사가 가능한 광감성 방수 코팅제.
The method according to claim 1,
The light-
A light-sensitive agent A having a light absorption peak at a central wavelength band of a blue region, a light-sensitive agent B having a light absorption peak at a central wavelength band of a green region, a light absorption agent B having a light absorption peak at a central wavelength band of a red region, And at least one selected from the group consisting of a light-curing agent C having a light-curing property and a light-curing agent C having a light-curing property.
상기 광감응제 A는 하이포크레린 B(Hypocrellin B), 아크리딘오렌지(Acridine orange) 및 쿠마린(Coumarin) 중 선택된 1종 이상을 포함하고,
상기 광감응제 B는 로즈 벵갈(Rose Bengal), 로다민 B(Rhodamine B), 메로시아닌 540(Merocyanine 540) 중 선택된 1종 이상을 포함하며,
상기 광감응제 C는 메틸렌 블루(Methylene blue), 페오포르바이드 A(Pheophorbide A), 크립토시아닌(Cryotocyanine) 중 선택된 1종 이상을 포함하는 것을 특징으로 하는 육안 검사가 가능한 광감성 방수 코팅제.
The method according to claim 6,
The photosensitizer A comprises at least one selected from the group consisting of Hypocrellin B, Acridine orange and Coumarin,
The light-sensitive agent B includes at least one selected from Rose Bengal, Rhodamine B, and Merocyanine 540,
Wherein the photosensitive agent C comprises at least one selected from the group consisting of methylene blue, pheophorbide A, and cryotocyanine.
상기 광감응제는
포리피린계 화합물 및 그 치환체, 프탈로시아닌계 화합물 및 그 치환체 및 염료 중 선택된 1종 이상을 포함하는 것을 특징으로 하는 육안 검사가 가능한 광감성 방수 코팅제.
The method according to claim 1,
The light-
A water-repellent, water-repellent coating capable of being visually inspected, characterized by comprising at least one selected from the group consisting of a polypyrin compound and its substituent, a phthalocyanine compound,
상기 광감응제는
5,10,15-트리페닐-20-(4-카르복시페닐)-포르피린백금(5,10,15-triphenyl-20-(4-carboxyphenyl)-porphyrin platinum, PtCP), 5,15-비스페닐-10,20-비스(4-메톡시카르보닐페닐)-포르피린백금(5-15-bisphenyl-10,20-bis(4-methoxycarbonylphenyl)-porphyrin platinum, tPtCP), 테트라페닐포르피린(tetraphenyl porphyrin, H2TPP), 헤마토포르피린(hemato porphyrin, HP), 프로토포르피린(proto porphyrin, PP), 인도시아닌그린(indocyanin green, ICG) 및 메조-테트라키스(p-설포나토페닐)포르피린(meso-tetrakis (p-sulfonatopheny)porphyrin, TSPP) 중 선택된 1종 이상을 포함하는 것을 특징으로 하는 육안 검사가 가능한 광감성 방수 코팅제.
The method according to claim 1,
The light-
5,10,15-triphenyl-20- (4-carboxyphenyl) -porphyrin platinum, PtCP), 5,15-bisphenyl- Bisphenyl-10,20-bis (4-methoxycarbonylphenyl) -porphyrin platinum, tPtCP), tetraphenyl porphyrin (H2TPP) , Hematoporphyrin (HP), proto porphyrin (PP), indocyanin green (ICG), and meso-tetrakis (p- sulfonatopheny) porphyrin (TSPP). The present invention relates to a water-repellent, water-repellent coating capable of visual inspection.
상기 유기 용매는
퍼플루오로카본계(perfluorocarbon), 퍼플루오로알칸계(perfluoroalkan), 퍼플루오로폴리에테르계(perfluoroplyether) 및 히드로플루오로카본계(hydrofluorocarbon)를 포함하는 불소계 용매 중 선택된 1종 이상인 것을 특징으로 하는 육안 검사가 가능한 광감성 방수 코팅제.
The method according to claim 1,
The organic solvent
Based solvent is at least one selected from the group consisting of perfluorocarbons, perfluoroalkanes, perfluoroplyethers and hydrofluorocarbon-containing fluorocarbon solvents. Water-repellent, water-repellent coating for visual inspection.
상기 경화제는
R-(NCO)3의 화합물인 것을 특징으로 하는 육안 검사가 가능한 광감성 방수 코팅제.
(여기서, R은 탄소수 1 ~ 10의 알킬기임.)
The method according to claim 1,
The curing agent
(NCO) < / RTI >< RTI ID = 0.0 > 3. < / RTI >
(Wherein R is an alkyl group having 1 to 10 carbon atoms)
(b) 상기 광감성 방수 코팅 물질층을 경화하여 광감성 방수 코팅층을 형성하는 단계; 및
(c) 상기 광감성 방수 코팅층에 200 ~ 700nm의 UV-Vis 영역 내의 특정 파장을 조사하여, 상기 광감성 방수 코팅층의 코팅 상태를 육안으로 검사하는 단계;를 포함하는 것을 특징으로 하는 광감성 방수 코팅제를 이용한 인쇄회로기판의 방수 코팅 방법.(a) forming a light-sensitive waterproof coating material layer by coating a surface of a printed circuit board on which an electronic component is mounted by coating a light-sensitive water-repellent coating agent obtained by mixing the photosensitive water-repellent coating agent at a volume ratio of 10 parts by volume of the water-
(b) curing the photosensitive waterproof coating material layer to form a light-sensitive waterproof coating layer; And
(c) irradiating the light-sensitive waterproof coating layer with a specific wavelength within a UV-Vis region of 200 to 700 nm to visually inspect the coating state of the light-sensitive waterproof coating layer. A waterproof coating method of a printed circuit board using the method.