KR20150111654A

KR20150111654A - Composition for improving tooth-whitening effect and kit comprising the same

Info

Publication number: KR20150111654A
Application number: KR1020140035266A
Authority: KR
Inventors: 김종훈; 안재현; 김지혜; 이인호
Original assignee: 주식회사 엘지생활건강
Priority date: 2014-03-26
Filing date: 2014-03-26
Publication date: 2015-10-06

Abstract

The present invention as a composition for whitening teeth comprising peroxides or a (pretreatment) composition for improving tooth-whitening effects of a patch, is applied on the surface of teeth before using the patch or the composition for whitening teeth, wherein the (pretreatment) composition comprises a metal salt catalyst for discharging trivalent metal ions in a state of an aqueous solution and, particularly, significantly desirable iron chloride (III). In addition, the present invention provides a kit for whitening teeth comprising the composition. The present invention provides excellent tooth-whitening effects.

Description

치아 미백 효과 증진을 위한 조성물 및 이를 포함하는 키트{Composition for improving tooth-whitening effect and kit comprising the same}TECHNICAL FIELD The present invention relates to a composition for enhancing tooth whitening effect and a kit comprising the same,

본 발명은 치아 미백 효과 증진을 위한 조성물 및 이를 포함하는 키트에 관한 것으로, 더욱 상세하게는 치아 미백 성분으로 사용되는 과산화물의 분해를 촉진시켜 치아 미백 효과를 증대시킬 수 있는 조성물 및 이를 포함하는 키트에 관한 것이다.The present invention relates to a composition for enhancing a tooth whitening effect and a kit comprising the same, and more particularly, to a composition capable of enhancing a tooth whitening effect by promoting decomposition of peroxides used as a tooth whitening ingredient, .

최근 들어 미에 대한 대중의 관심이 증가하면서 치아 미백에 대한 대중의 관심이 증가하고 있다. 치아 미백을 위한 선택으로 치약, 마우스린스 (mouthrinse), 츄잉 껌, 실내 미백, 및 가장 일반적인 상점 또는 치과의사로부터 구입되는 트레이(tray)를 사용하는 치아 미백 용액을 포함한다. 치아 미백 용액은 통상적으로 과산화수소와 같은, 치아를 표백하는 활성 성분을 함유한다.In recent years, public interest in teeth whitening has increased as public interest in the beauty has increased. Choices for tooth whitening include toothpaste, mouthrinse, chewing gum, indoor whitening, and tooth whitening solutions using trays purchased from the most common shops or dentists. The tooth whitening solution typically contains an active ingredient that bleaches teeth, such as hydrogen peroxide.

이러한 과산화수소는 불안정한 물질로, 시간이 경과하면 활성이 계속 낮아지게 된다. 따라서 통상적인 치아 미백 제품은 유통과정에서 과산화수소의 활성이 떨어지는 것을 방지하기 위하여 과산화수소 안정화제를 이용해 활성을 유지하기도 한다. This hydrogen peroxide is an unstable substance, and its activity is continuously lowered over time. Thus, a typical tooth whitening product may maintain its activity by using a hydrogen peroxide stabilizer to prevent the activity of hydrogen peroxide from deteriorating during the distribution process.

실제 치아 미백제 사용 시 이러한 안정화제에 의해 과산화수소가 활성을 제대로 나타내지 못하는 문제가 발생할 수 있어, 사용 전에 촉매를 이용하여 과산화수소의 신속한 활성을 유도하고 있다. When using actual tooth whitening agents, the hydrogen peroxide may not exhibit its activity properly due to these stabilizers. Therefore, the hydrogen peroxide is rapidly activated by using the catalyst before use.

이러한 촉매로는 과산화물과 반응하여 퍼하이드록시라디칼을 발생시켜 치아 미백 효과를 증진시키는 성분을 이용하기도 하며, 과산화물의 분해를 촉진시키는 금속 촉매를 이용하기도 한다.Such a catalyst may be a component that reacts with a peroxide to generate a perhydroxy radical to enhance the tooth whitening effect, or a metal catalyst that promotes the decomposition of peroxide.

본 발명은 과산화수소와 같은 치아 미백 성분을 활성화시킬 수 있는 조성물을 제공하고자 한다.The present invention seeks to provide a composition capable of activating a tooth whitening component such as hydrogen peroxide.

본 발명은 또한 치아 미백용 조성물 또는 패치와 함께 사용하면서, 치아 미백 성분의 효과를 더욱 향상시킬 수 있는 조성물을 제공하고자 한다.The present invention also provides a composition that can be used with a tooth whitening composition or patch to further enhance the effect of the whitening component.

본 발명은 또한 가장 우수한 촉매 효과를 나타내, 치아 미백 성분의 미백 효과를 더욱 활성화시킬 수 있는 미백 효과 증진을 위한 조성물을 제공하고자 한다.The present invention also provides a composition for promoting a whitening effect that can exhibit the most excellent catalytic effect and can further activate the whitening effect of a tooth whitening component.

상기 과제를 해결하기 위하여, 본 발명은 과산화물을 함유하는 치아 미백용 조성물 또는 패치의 치아 미백 효과 증진을 위한 전처리 조성물로서, 상기 전처리 조성물은 수용액 상태에서 3가의 금속이온을 방출하는 금속염 촉매를 포함하며, 상기 치아 미백용 조성물 또는 패치의 사용 전 치아 표면에 적용되는 것을 특징으로 하는 조성물을 제공한다. The present invention provides a pretreatment composition for enhancing tooth whitening effect of a tooth whitening composition or a patch containing a peroxide, wherein the pretreatment composition comprises a metal salt catalyst which releases trivalent metal ions in an aqueous solution state , The composition being applied to a tooth surface before use of the tooth whitening composition or patch.

치아 미백 성분으로 주로 사용되고 있는 과산화물은 미백 효과의 증대를 위해서 유통상태에서는 안정화되고, 사용 시점에 즉시 활성을 나타낼 필요가 있다. Peroxides, which are mainly used as tooth whitening ingredients, must be stabilized in a circulating state and exhibit immediate activity at the time of use in order to increase the whitening effect.

따라서 과산화수소 등과 같은 치아 미백 성분의 즉각적인 활성을 위해, 촉매를 치아 미백의 전처리를 위한 액상 또는 겔 제형의 형태로 치아에 먼저 바르고 이후 미백용 패치를 그 위에 사용하는 방법이 제안되어왔다. Thus, for immediate activation of tooth whitening components such as hydrogen peroxide, methods have been proposed in which a catalyst is first applied to teeth in the form of a liquid or gel formulation for pretreatment of teeth whitening, and then a whitening patch is applied thereon.

본 발명은 치아 미백 성분의 활성화를 증진시키기 위하여 활성제 역할을 하는 금속염 촉매를 포함한다. The present invention includes a metal salt catalyst that acts as an activator to enhance the activation of the tooth whitening component.

상기 금속염 촉매는 치아 미백 성분의 활성을 촉진시키는 작용을 할 수 있으며, 제품 유통 시 미백 성분의 안정화를 위해 사용될 수 있는 안정화제에 의해 치아에 미백 활성이 저해되는 것을 방지하고 우수한 미백 효과를 유도하기 위하여 사용될 수 있다. The metal salt catalyst can act to accelerate the activity of the tooth whitening component and can prevent the whitening activity of the teeth from being inhibited by the stabilizing agent that can be used for stabilizing the whitening component during the product circulation, Can be used.

본 발명의 발명자들은 치아 미백 조성물 또는 패치와 관련된 다양한 실험을 진행하던 중에 3가 금속이온을 이용하여 전처리할 경우에 치아 미백 조성물 또는 치아 미백 패치의 치아 미백 효과가 탁월히 높아진다는 예기치 못한 효과를 확인하였으며, 특히 그 중에서 염화철(FeCl₃)이 다른 금속이온들 대비 현저히 우수한 효과를 나타냄을 확인하였다.The inventors of the present invention have found that unexpected effects that tooth whitening effect of teeth whitening composition or tooth whitening patch is remarkably increased when pretreatment using trivalent metal ion during various experiments related to tooth whitening composition or patch Especially, it was confirmed that iron chloride (FeCl ₃ ) showed remarkably superior effect to other metal ions.

상기 염화철은 특히 우수한 치아 미백 효과를 나타내었으며, 뿐만 아니라, 흡습성이 우수하여 겔 제형의 제조에 유리하게 작용할 수 있다.The iron chloride exhibits particularly excellent tooth whitening effect and is also excellent in hygroscopicity and can be advantageously used in the production of gel formulations.

상기 염화철을 함유하는 조성물은 치아 미백용 조성물 또는 패치의 사용 전 치아 표면에 적용될 수 있다. The composition containing the iron chloride may be applied to the tooth surface prior to use of the tooth whitening composition or patch.

상기 염화철은 상기 조성물의 전체 중량 대비 0.01 내지 5 중량% 포함될 수 있으며, 바람직하게는 0.1 내지 3 중량%, 더욱 바람직하게는 0.3 내지 1 중량% 포함될 수 있다. The iron chloride may be contained in an amount of 0.01 to 5% by weight, preferably 0.1 to 3% by weight, more preferably 0.3 to 1% by weight based on the total weight of the composition.

상기 염화철의 함량이 0.01 중량% 미만일 경우 과산화물 분해 촉진 효과가 미비할 수 있으며, 함량이 5 중량%를 초과하는 경우 치아 및 구강 내 자극감을 주는 문제가 발생할 수 있다. If the content of iron chloride is less than 0.01% by weight, the effect of accelerating peroxide decomposition may be insufficient. If the content of iron chloride is more than 5% by weight, irritation may occur in the teeth and oral cavity.

상기 전처리 조성물은 치아 미백 조성물 또는 치아 미백 패치를 치아에 적용할 때 이들이 흘러내리는 것을 방지하도록 치면 부착 성질을 가질 수 있으며, 치아와의 부착성을 높이기 위해 바람직하게는 겔 제형일 수 있다.The pretreatment composition may have a tooth adhesion property to prevent the teeth whitening composition or the tooth whitening patch from flowing down when the tooth whitening composition or the teeth whitening patch is applied to the teeth, and may be preferably in a gel form in order to improve the adhesion with the teeth.

본 명세서에 있어 상기 겔 제형은 점성이 있는 액상 제형을 포함하며, 액상 제형에 비해 유동성을 상실한 상태를 포함하는 넓은 의미로 사용된다. As used herein, the gel formulation includes a viscous liquid formulation and is used in a broad sense including a state of loss of fluidity compared to a liquid formulation.

겔 제형을 갖기 위해서 상기 전처리 조성물은 수용성 폴리머 및 용매를 더 포함할 수 있으며, 그 외에도 연마제, 유화제 등과 같은 성분들을 추가로 포함할 수 있다. In order to have a gel formulation, the pretreatment composition may further include a water-soluble polymer and a solvent, and may further include components such as an abrasive, an emulsifier, and the like.

치아 점착성을 갖는 역할을 하기 위해 사용 가능한 고분자는 폴리 알킬 비닐 에테르-말레인산 공중합체(PVM/MA copolymer, Gantrez AN 119, AN 139, S-97), 폴리 비닐 알코올, 폴리 아크릴 산, Poloxamer (poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) triblock copolymer), 폴리 에틸렌 옥사이드(Polyox), 폴리 비닐 피롤리돈-비닐 아세테이트 공중합체(PVP/VA copolymer; Luviskol VA, Plasdone S PVP/VA), 폴리 비닐 피롤리돈(PVP, K15 ~ K-120), Polyquaterium-11(Gafquat 755N), Polyquaterium-39(Merquat plus 3330), 카르복시 폴리 메틸렌(Carbopol), 하이드록시 프로필 메틸 셀룰로오즈, 하이드록시 에틸 셀룰로오즈, 하이드록시 프로필 셀룰로오즈, 젤라틴(Gelatin), 알긴 산(Sodium Alginate) 또는 이들의 혼합물 중에서 선택할 수 있다. 이들의 용매로는 주로 물, 에탄올 단독 또는 이들의 혼합물, 그리고 다른 유기 용매들 예를 들면 에틸 아세테이트, 메틸렌 클로라이드, 이소프로필 알코올, 아세토 나이트릴 단독이나 이들의 혼합물을 비율을 조절하여 사용할 수도 있다.Polymers that can be used for tooth adhesion include polyalkyl vinyl ether-maleic acid copolymer (PVM / MA copolymer, Gantrez AN 119, AN 139, S-97), polyvinyl alcohol, polyacrylic acid, polyoxamer (ethylene oxide) -poly (ethylene oxide) -poly (ethylene oxide) triblock copolymer, polyethylene oxide, polyvinylpyrrolidone-vinyl acetate copolymer (PVP / VA copolymer; Luviskol VA, Plasdone S PVP / VA ), Polyvinylpyrrolidone (PVP, K15 to K-120), Polyquaterium-11 (Gafquat 755N), Polyquaterium-39 (Merquat plus 3330), carboxypolymethylene (Carbopol), hydroxypropylmethylcellulose, Cellulose, hydroxypropylcellulose, gelatin, sodium alginate, or a mixture thereof. These solvents may be mainly water, ethanol alone or a mixture thereof, and other organic solvents such as ethyl acetate, methylene chloride, isopropyl alcohol, acetonitrile alone or a mixture thereof.

상기 연마제는 침강 실리카, 실리카겔, 지르코늄 실리케이트, 인산일수소칼슘, 무수인산일수소칼슘, 함수 알루미나, 경질 탄산칼슘, 중질 탄산칼슘, 칼슘피로인산염, 불용성 메타인산염, 알루미늄실리케이트, 또는 이들의 혼합물 중에서 선택된 어느 하나를 사용할 수 있다. The abrasive is selected from the group consisting of precipitated silica, silica gel, zirconium silicate, calcium monohydrogenphosphate, anhydrous calcium hydrogen phosphate, hydrated alumina, light calcium carbonate, heavy calcium carbonate, calcium pyrophosphate, insoluble metaphosphate, aluminum silicate, Either one can be used.

본 발명의 다른 실시예에 따르면, 본 발명은 치아 미백을 위한 키트에 있어서, (a) 수용액 상태에서 3가의 금속이온을 방출하는 금속염 촉매를 포함하는 조성물; 및 (b) 상기 조성물과 접촉하며, 과산화물을 포함하는 치아 미백용 조성물 또는 패치를 포함하는 치아 미백을 위한 키트를 제공한다.According to another embodiment of the present invention, there is provided a kit for tooth whitening comprising: (a) a composition comprising a metal salt catalyst releasing trivalent metal ions in an aqueous solution state; And (b) a tooth whitening composition or patch in contact with the composition and comprising a peroxide.

본 발명의 또 다른 실시예에 따르면, 상기 키트는 상기 겔 제형의 치면 부착용 조성물을 치아 표면에 바르기 위한 수단을 더 포함할 수 있으며, 바람직하게는 브러쉬, 스펀지 등의 형태를 가질 수 있다. According to another embodiment of the present invention, the kit may further comprise means for applying the gel-type tooth-surface attaching composition to the tooth surface, and may preferably have the form of a brush, a sponge, or the like.

상기 치아 미백용 패치는 치아 표면에 부착이 가능한 패치의 형태로 제작될 수 있으며, 본 발명에 따른 치아 부착용 패치는, 예를 들어, 미국특허 제6,682,721호, 제6,689,344호, 제6,780,401호, 제6,946,142호 등에 개시된 방법으로 제조될 수 있으나, 본 발명은 이러한 패치의 구성 성분과 제조 방법에 한정되는 것은 아니다.The tooth whitening patch can be manufactured in the form of a patch that can be attached to the surface of a tooth, and the patch for dental attachment according to the present invention can be used, for example, in US Patents 6,682,721, 6,689,344, 6,780,401, 6,946,142 And the like, but the present invention is not limited to the constituent components and the production method of such a patch.

상기 과산화물은 과산화 수소(hydrogen peroxide), 과산화 요소(carbamide peroxide), 과산화 칼슘(calcium peroxide), 과탄산 나트륨(sodium percarbonate), 과붕산 나트륨(sodium perborate), 및 과산화피로인산나트륨(tetrasodium pyrophosphate peroxidate)으로 이루어진 군에서 선택된 1종 이상일 수 있으며, 더욱 바람직하게는 과산화수소 또는 과산화 요소를 포함할 수 있다.The peroxide is selected from the group consisting of hydrogen peroxide, carbamide peroxide, calcium peroxide, sodium percarbonate, sodium perborate, and tetrasodium pyrophosphate peroxidate. , And more preferably hydrogen peroxide or peroxide element.

상기 치아 미백 성분은 상기 패치의 총 중량 대비 0.01중량% 내지 50중량%를, 바람직하게는 0.1 중량% 내지 30 중량%포함할 수 있으며, 가장 바람직하게 0.5중량% 내지 20중량%포함될 수 있다. The tooth whitening component may include 0.01 wt% to 50 wt%, preferably 0.1 wt% to 30 wt%, and most preferably 0.5 wt% to 20 wt% of the total weight of the patch.

상기 치아 미백 성분은 안정화제와 함께 혼합될 수 있다. The tooth whitening component may be mixed with a stabilizing agent.

상기 안정화제로는 피로인산나트륨, 산성 피로인산나트륨, 메타인산나트륨, 폴리인산나트륨, 피로인산나트륨칼륨, 피로인산칼륨, 울트라메타인산염, 산성폴리인산나트륨, 에틸렌디아민테트라아세테이트, 아미노트리메틸렌포스페이트 및 이의 염, 하이드록시에틸렌디포스포네이트 및 이의 염, 에틸렌디아민테트라메틸렌포스포네이트 및 이의 염, 디에틸렌트리아민펜타메틸렌포스포네이트 및 이의 염, 알킬 아릴 설포네이트, 알킬 설포네이트 염, 알킬 카르복실레이트 염, 알킬 디페닐 옥사이드 디설포네이트, 스판20(Span 20, Sorbitan Monolaurate), 스판 40(Span 40, Sorbitan Monopalmitate), 스판 60(Span 60, Sorbitan Mono stearate), 스판 80(Span 80; Sorbitan Monooleate), 스판 85(Span 85, Sorbitan Trioleate), 트윈(Tween, POE sorbitan fatty acid ester) 계 및 이들의 혼합물로 이루어진 군에서 선택된 1 종 이상을 포함할 수 있다.Examples of the stabilizer include sodium pyrophosphate, sodium pyrophosphate, sodium metaphosphate, sodium polyphosphate, potassium sodium pyrophosphate, potassium pyrophosphate, ultrametaphosphate, acidic sodium polyphosphate, ethylenediamine tetraacetate, aminotrimethylene phosphate, Salts thereof, hydroxyethylenepolyphosphonates and salts thereof, ethylenediamine tetramethylenephosphonate and salts thereof, diethylenetriaminepenta methylenephosphonate and salts thereof, alkylarylsulfonates, alkylsulfonate salts, alkylcarboxylates Span 20, Sorbitan Monoalate, Span 40, Sorbitan Monopalmitate, Span 60, Sorbitan Mono stearate, Span 80, Sorbitan Monooleate, , Span 85 (Sorbitan Trioleate), Tween (POE sorbitan fatty acid ester), and mixtures thereof. Or more species.

상기 패치는 치아의 굴곡면을 따라 유연하게 구부러지게 하기 위해, 폴리프로필렌 글리콜(polypropylene glycol), 글리세린(glycerin) 또는 폴리에틸렌 글리콜(polyethylene glycol), 피마자 오일(castor oil), 수소화 피마자 오일(hydrogenated castor oil) 등의 가소제를 첨가할 수 있다.The patch may be made of polypropylene glycol, glycerin or polyethylene glycol, castor oil, hydrogenated castor oil, or the like in order to flexibly bend along the curved surface of the teeth. ) May be added.

본 발명에 따른, 과산화물을 함유하는 치아 미백용 조성물 또는 패치의 치아 미백 효과 증진을 위한 조성물은 치아 미백 성분을 포함한 조성물 또는 패치의 치아 미백 효과를 더욱 향상시킬 수 있다. The composition for enhancing the tooth whitening effect of a tooth whitening composition or patch containing peroxide according to the present invention can further improve the teeth whitening effect of a composition or a patch containing a tooth whitening component.

또한 본 발명의 조성물은 치아 미백용 조성물 또는 패치의 미백 효과가 짧은 시간 내에 발휘될 수 있도록 한다.In addition, the composition of the present invention enables the whitening effect of the composition or patch for teeth whitening to be exhibited within a short time.

도 1은 치아 시편들의 초기 대비 명도 변화량을 측정하여 나타낸 그래프이다. FIG. 1 is a graph showing a change in initial brightness of a tooth specimen measured.

이하, 본 발명을 보다 구체적으로 설명하기 위하여 하기 실시예 등을 들어 설명한다. 그러나, 본 발명에 따른 실시예들은 여러 가지 다른 형태로 변형될 수 있으며 본 발명의 범위가 아래에서 상술하는 실시예들에 한정되는 것으로 해석되어서는 안 된다. 본 발명의 실시예들은 본 발명의 구체적 이해를 돕기 위해 예시적으로 제공되는 것이다.
Hereinafter, the present invention will be described in more detail with reference to the following examples. However, the embodiments according to the present invention can be modified into various other forms, and the scope of the present invention should not be construed as being limited to the embodiments described below. The embodiments of the present invention are provided by way of example to facilitate a specific understanding of the present invention.

<실시예 및 비교예>&Lt; Examples and Comparative Examples &

하기 표 1에 나타낸 바와 같은 구성비로 본 발명에 따른 치아 미백용 키트를 제작하였으며, 단위는 중량%로 나타내었다.The tooth whitening kit according to the present invention was prepared in the composition ratios shown in Table 1 below, and the units are expressed in weight%.

본 발명의 겔(gel)제는 다음의 과정에 따라 제조하였다. The gel agent of the present invention was prepared according to the following procedure.

에탄올과 정제수 혼합용액에 연마제인 실리카와 효능물질인 염화철을 용해시킨 후, 포비돈을 첨가하여 20분간 교반하였다. Silica, which is an abrasive, and iron chloride, which is an efficacious substance, were dissolved in a mixed solution of ethanol and purified water, povidone was added, and the mixture was stirred for 20 minutes.

비교예의 경우 첨가되는 성분을 제외하고 실시예와 동일한 방법으로 제조하였다.In the case of the comparative example, it was prepared in the same manner as in Example except for the components to be added.

정제수에 염화철을 용해시킨 후 에탄올과 실리카를 넣어 실리카가 완전히 분산된 것을 확인하고 포비돈을 넣어 20분간 교반하였다. After dissolving the iron chloride in the purified water, ethanol and silica were added to confirm that the silica was completely dispersed, and povidone was added thereto, followed by stirring for 20 minutes.

또한, 치아 미백을 위한 부착용 패치는 하기와 같이 과산화수소를 미백 성분으로 사용하였으며, 미국특허 제6,682,721호의 실시예 2와 같이 제조하였다. The adhesive patch for tooth whitening was prepared as in Example 2 of U.S. Patent No. 6,682,721 using hydrogen peroxide as a whitening ingredient as described below.

비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 비교예 5Comparative Example 5 비교예 6Comparative Example 6 실시예 1Example 1 제1제(겔제) 효능물질First agent (gel) efficacy material -- 글루콘산철0.5%0.5% 젖산철
0.5%Iron lactate
0.5% 염화마그네슘0.5%Magnesium chloride 0.5% 염화 망간0.5%Manganese chloride 0.5% 황산철
0.5%Iron sulfate
0.5% 염화철
0.5%Ferric chloride
0.5% 제1제(겔제)
첨가물질First agent (gelatin)
Additive substance 글리세린 5%Glycerin 5% 글리세린 5%Glycerin 5% 글리세린 5%Glycerin 5% 글리세린 5%Glycerin 5% 글리세린 5%Glycerin 5% 글리세린 5%Glycerin 5% 글리세린 5%Glycerin 5% Silica 10%Silica 10% Silica 10%Silica 10% Silica 10%Silica 10% Silica 10%Silica 10% Silica 10%Silica 10% Silica 10%Silica 10% Silica 10%Silica 10% 포비돈 10%Povidone 10% 포비돈 10%Povidone 10% 포비돈 10%Povidone 10% 포비돈 10%Povidone 10% 포비돈 10%Povidone 10% 포비돈 10%Povidone 10% 포비돈 10%Povidone 10% 에탄올 10%Ethanol 10% 에탄올 10%Ethanol 10% 에탄올 10%Ethanol 10% 에탄올 10%Ethanol 10% 에탄올 10%Ethanol 10% 에탄올 10%Ethanol 10% 에탄올 10%Ethanol 10% 정제수 to 100%Purified water to 100% 정제수 to 100%Purified water to 100% 정제수 to 100%Purified water to 100% 정제수 to 100%Purified water to 100% 정제수 to 100%Purified water to 100% 정제수 to 100%Purified water to 100% 정제수 to 100%Purified water to 100% 제2제(패치) 효능물질Second agent (patch) efficacy material 과산화수소
3.0%Hydrogen peroxide
3.0% 과산화수소
3.0%Hydrogen peroxide
3.0% 과산화수소
3.0%Hydrogen peroxide
3.0% 과산화수소
3.0%Hydrogen peroxide
3.0% 과산화수소
3.0%Hydrogen peroxide
3.0% 과산화수소
3.0%Hydrogen peroxide
3.0% 과산화수소
3.0%Hydrogen peroxide
3.0%

시험예Test Example 1. 명도 변화량 1. Brightness variation

1) 실험 방법1) Experimental method

비교예 1 내지 6 및 실시예 1을 각각 인공 착색된 HAP disk에 부착하고 1시간 경과 후 제거하여 초기 대비 명도 변화량을 측정하여 ?로 나타내었다.
Comparative Examples 1 to 6 and Example 1 were attached to artificially colored HAP discs, respectively, and after 1 hour, they were removed to measure the initial contrast change.

2) 실험 결과2) Experimental results

효능물질이 함유되지 않은 겔제를 사용한 비교예 1에 비해 금속염 촉매가 함유된 겔제를 사용한 경우(비교예 2 내지 6 및 실시예 1), 미백효과가 증가된 것을 알 수 있었으며, 그 중 염화철을 사용한 실시예 1의 효과가 두드러짐을 확인할 수 있었다. 즉, 염화철을 함유한 조성물이 치아 미백 효과가 가장 우수하다는 것을 실험을 통하여 확인하였으며, 이러한 결과는 도 1에 나타내었다. It was found that the whitening effect was increased when the gel agent containing the metal salt catalyst was used (Comparative Examples 2 to 6 and Example 1) as compared with Comparative Example 1 using the gel agent not containing the efficacious substance, It was confirmed that the effect of Example 1 was conspicuous. That is, it has been confirmed through experiments that the composition containing iron chloride has the best tooth whitening effect, and the results are shown in FIG.

Claims

과산화물을 함유하는 치아 미백용 조성물 또는 패치의 치아 미백 효과 증진을 위한 전처리 조성물로서,
상기 전처리 조성물은 수용액 상태에서 3가의 금속이온을 방출하는 금속염 촉매를 포함하며,
상기 치아 미백용 조성물 또는 패치의 사용 전 치아 표면에 적용되는 것을 특징으로 하는 조성물.A pretreatment composition for enhancing tooth whitening effect of a tooth whitening composition or patch containing peroxide,
The pretreatment composition comprises a metal salt catalyst which releases trivalent metal ions in an aqueous solution state,
Wherein the composition is applied to a tooth surface prior to use of the tooth whitening composition or patch.

제1항에 있어서, 상기 금속염 촉매는 염화철(Ⅲ)인 것을 특징으로 하는 조성물. The composition of claim 1, wherein the metal salt catalyst is iron (III) chloride.

치아 미백을 위한 키트에 있어서,
(a) 수용액 상태에서 3가의 금속이온을 방출하는 금속염 촉매를 포함하는 조성물; 및
(b) 상기 조성물과 접촉하며, 과산화물을 포함하는 치아 미백용 조성물 또는 패치를 포함하는 치아 미백을 위한 키트. A kit for whitening teeth,
(a) a composition comprising a metal salt catalyst that releases trivalent metal ions in an aqueous solution state; And
(b) a kit for teeth whitening comprising a composition or patch for teeth whitening in contact with the composition and comprising peroxide.

제3항에 있어서, 상기 키트는 상기 금속염 촉매를 포함하는 조성물을 치아 표면에 바르기 위한 수단을 더 포함하는 것을 특징으로 하는 키트. 4. The kit of claim 3, wherein the kit further comprises means for applying a composition comprising the metal salt catalyst to a tooth surface.

제3항에 있어서, 상기 금속염 촉매는 염화철(Ⅲ)인 것을 특징으로 하는 키트. The kit according to claim 3, wherein the metal salt catalyst is iron (III) chloride.

제3항에 있어서, 상기 과산화물은 과산화 수소(hydrogen peroxide), 과산화 요소(carbamide peroxide), 과산화 칼슘(calcium peroxide), 과탄산 나트륨(sodium percarbonate), 과붕산 나트륨(sodium perborate), 및 과산화피로인산나트륨(tetrasodium pyrophosphate peroxidate)으로 이루어진 군에서 선택된 1종 이상인 것을 특징으로 하는 키트.The method of claim 3, wherein the peroxide is selected from the group consisting of hydrogen peroxide, carbamide peroxide, calcium peroxide, sodium percarbonate, sodium perborate, (Tetrasodium pyrophosphate peroxidate). &Lt; RTI ID = 0.0 > 8. < / RTI >