KR20150072901A - Cover window - Google Patents

Cover window Download PDF

Info

Publication number
KR20150072901A
KR20150072901A KR1020130160570A KR20130160570A KR20150072901A KR 20150072901 A KR20150072901 A KR 20150072901A KR 1020130160570 A KR1020130160570 A KR 1020130160570A KR 20130160570 A KR20130160570 A KR 20130160570A KR 20150072901 A KR20150072901 A KR 20150072901A
Authority
KR
South Korea
Prior art keywords
layer
elastic layer
plastic substrate
cover window
elastic
Prior art date
Application number
KR1020130160570A
Other languages
Korean (ko)
Other versions
KR102252194B1 (en
Inventor
안명진
권나영
박선아
Original Assignee
엘지이노텍 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엘지이노텍 주식회사 filed Critical 엘지이노텍 주식회사
Priority to KR1020130160570A priority Critical patent/KR102252194B1/en
Publication of KR20150072901A publication Critical patent/KR20150072901A/en
Application granted granted Critical
Publication of KR102252194B1 publication Critical patent/KR102252194B1/en

Abstract

The present invention relates to a cover window. The cover window comprises: a plastic substrate; an elastic layer arranged on the plastic substrate and having the hardness of shore A 70 to 90; and a hard coating layer arranged on the elastic layer.

Description

커버 윈도우{COVER WINDOW}Cover window {COVER WINDOW}

본 발명은 커버 윈도우에 관한 것으로서, 더욱 상세하게는 이동 단말기의 디스플레이 표면을 보호하기 위한 커버 윈도우에 관한 것이다. The present invention relates to a cover window, and more particularly to a cover window for protecting a display surface of a mobile terminal.

스마트폰, 태블릿 PC(tablet PC) 등 이동 단말기의 디스플레이 표면을 보호하기 위한 커버 윈도우로 강화 유리가 사용될 수 있다. 그러나, 강화 유리는 외부 충격에 의해 쉽게 깨질 수 있으며, 플렉서블 디스플레이에는 적용이 어려운 단점이 있다. Tempered glass can be used as a cover window to protect the display surface of a mobile terminal, such as a smart phone or a tablet PC. However, the tempered glass can be easily broken by an external impact, and it is difficult to apply to a flexible display.

최근에는 강화 유리의 문제점으로 인해 강화 유리가 아닌 플라스틱 재질로 커버 윈도우를 구현하는 시도들이 이어지고 있다. In recent years, due to the problems of tempered glass, attempts have been made to implement a cover window with a plastic material instead of a tempered glass.

한편, 플라스틱 재질로 커버 윈도우를 구현하는 경우, 표면 경도를 증가시키기 위해 경도 9H 정도의 하드 코팅층(hard coating layer)이 결합될 수 있다. 그러나, 수 um의 두께로 형성되는 하드 코팅층으로는 물리적 충격을 완전히 흡수할 수 없어 디스플레이의 메인 기판에 찍힘이 발생할수 있으며, 이는 디스플레이 불량으로 이어질 수 있다.On the other hand, when a cover window is formed of a plastic material, a hard coating layer having a hardness of about 9H can be bonded to increase the surface hardness. However, a hard coating layer formed to a thickness of several um can not completely absorb a physical impact, and may be struck on the main substrate of the display, which may lead to display failure.

본 발명이 이루고자 하는 기술적 과제는 물리적 충격을 흡수하여 디스플레이로 전달되는 것을 방지하는 커버 윈도우를 제공하는데 있다. SUMMARY OF THE INVENTION The present invention provides a cover window for absorbing a physical impact and preventing transmission to a display.

본 발명의 일 실시 예에 따른 커버 윈도우는 플라스틱 기재층, 상기 플라스틱 기재층 상에 배치되며, 쇼어(Shore) A 70 내지 90의 경도를 가지는 탄성층, 그리고 상기 탄성층 상에 배치되는 하드 코팅층을 포함할 수 있다. A cover window according to an embodiment of the present invention includes a plastic substrate layer, an elastic layer disposed on the plastic substrate layer and having a hardness of Shore A 70-90, and a hard coating layer disposed on the elastic layer .

상기 탄성층은 75um 내지 300um의 두께를 가질 수 있다. The elastic layer may have a thickness of from 75 [mu] m to 300 [mu] m.

상기 탄성층의 연신률(elongation)은 40% 내지 80%를 만족할 수 있다. The elongation of the elastic layer may be in the range of 40% to 80%.

상기 탄성층은 실리콘(silicone) 또는 우레탄(urethane) 계열의 고탄성 수지로 형성될 수 있다. The elastic layer may be formed of a high elasticity resin such as silicone or urethane.

상기 플라스틱 기재층은 폴리카보네이트(PolyCarbonate, PC), 폴리메틸메타크릴레이트(PolyMethylMethacrylate PMMA), 폴리스티렌(PolyStyrene PS) 또는 이들의 공중합체(copolymer), 폴리에틸렌테레프탈레이트(PolyEthyleneTerephthalate,PET), 폴리에틸렌나프탈레이트(PolyEthyleneNaphthalate,PEN), 폴리에테르설폰(Polyethersulfone, PES), 알릴(allyl) 수지 중 적어도 하나 또는 이들의 선택적 조합으로부터 형성될 수 있다. The plastic substrate layer may be formed of at least one selected from the group consisting of polycarbonate (PC), polymethyl methacrylate PMMA, polystyrene PS or copolymers thereof, polyethylene terephthalate (PET), polyethylene naphthalate (PEN), polyethersulfone (PES), and allyl resin, or an optional combination thereof.

상기 플라스틱 기재층은 1mm 내지 3mm의 두께를 만족할 수 있다. The plastic substrate layer may have a thickness of 1 mm to 3 mm.

상기 하드 코팅층은 아크릴레이트(acrylate)계, 폴리실라잔(polysilazane)계, 아크릴(acrylic)계, 폴리우레탄(polyurethane)계, 에폭시(epoxy)계 화합물 중 적어도 하나 또는 이들의 선택적 조합으로부터 형성될 수 있다. The hard coating layer may be formed from at least one of acrylate, polysilazane, acrylic, polyurethane, epoxy, or an optional combination thereof. have.

상기 하드 코팅층은 10um 내지 250um의 두께를 만족할 수 있다. The hard coating layer may have a thickness of 10 to 250 탆.

본 발명의 실시 예에 따르면, 하드 코팅층을 형성하여 커버 윈도우의 표면 경도를 증가시킬 수 있다. 또한, 하드 코팅층과 플라스틱 기재층 사이에 개재된 탄성층을 통해 외부로부터 가해지는 물리적 충격을 흡수시켜 디스플레이로 전달되는 물리적 충격을 최소화함으로써, 찍힘 등 디스플레이의 변형과 이로 인한 불량 발생을 최소화할 수 있다.According to an embodiment of the present invention, a hard coating layer may be formed to increase the surface hardness of the cover window. In addition, by absorbing physical impact externally applied through the elastic layer interposed between the hard coating layer and the plastic substrate layer, the physical impact transmitted to the display is minimized, thereby minimizing the deformation of the display and the occurrence of defects .

도 1은 본 발명의 일 실시 예에 따른 커버 윈도우를 도시한 것이다.
도 2는 본 발명의 일 실시 예에 따른 커버 윈도우에서 탄성층의 성능을 실험하기 위해 사용되는 모양 추를 도시한 것이다. 1 shows a cover window according to an embodiment of the present invention.
2 illustrates a shape weight used to test the performance of an elastic layer in a cover window according to an embodiment of the present invention.

본 발명은 다양한 변경을 가할 수 있고 여러 가지 실시 예를 가질 수 있는 바, 특정 실시 예들을 도면에 예시하고 설명하고자 한다. 그러나, 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. The present invention is capable of various modifications and various embodiments, and specific embodiments are illustrated and described in the drawings. It should be understood, however, that the invention is not intended to be limited to the particular embodiments, but includes all modifications, equivalents, and alternatives falling within the spirit and scope of the invention.

제2, 제1 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되지는 않는다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. 예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제2 구성요소는 제1 구성요소로 명명될 수 있고, 유사하게 제1 구성요소도 제2 구성요소로 명명될 수 있다. 및/또는 이라는 용어는 복수의 관련된 기재된 항목들의 조합 또는 복수의 관련된 기재된 항목들 중의 어느 항목을 포함한다. The terms including ordinal, such as second, first, etc., may be used to describe various elements, but the elements are not limited to these terms. The terms are used only for the purpose of distinguishing one component from another. For example, without departing from the scope of the present invention, the second component may be referred to as a first component, and similarly, the first component may also be referred to as a second component. And / or < / RTI > includes any combination of a plurality of related listed items or any of a plurality of related listed items.

본 출원에서 사용한 용어는 단지 특정한 실시 예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terminology used in this application is used only to describe a specific embodiment and is not intended to limit the invention. The singular expressions include plural expressions unless the context clearly dictates otherwise. In the present application, the terms "comprises" or "having" and the like are used to specify that there is a feature, a number, a step, an operation, an element, a component or a combination thereof described in the specification, But do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, or combinations thereof.

다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms such as those defined in commonly used dictionaries are to be interpreted as having a meaning consistent with the contextual meaning of the related art and are to be interpreted as either ideal or overly formal in the sense of the present application Do not.

이하, 첨부된 도면을 참조하여 실시 예를 상세히 설명하되, 도면 부호에 관계없이 동일하거나 대응하는 구성 요소는 동일한 참조 번호를 부여하고 이에 대한 중복되는 설명은 생략하기로 한다.Hereinafter, embodiments will be described in detail with reference to the accompanying drawings, wherein like or corresponding elements are denoted by the same reference numerals, and redundant description thereof will be omitted.

도 1은 본 발명의 일 실시 예에 따른 커버 윈도우를 도시한 단면도이다. 1 is a cross-sectional view illustrating a cover window according to an embodiment of the present invention.

도 1을 참조하면, 커버 윈도우는 플라스틱 기재층(100), 플라스틱 기재층(100) 상에 형성되는 턴성층(200), 탄성층(200) 상에 형성되는 하드 코팅(hard coating)층(300) 등을 포함할 수 있다. 1, the cover window includes a plastic substrate layer 100, a turn-up layer 200 formed on the plastic substrate layer 100, a hard coating layer 300 formed on the elastic layer 200, ), And the like.

플라스틱 기재층(100)은 표시장치의 디스플레이(미도시) 상에 적층 형성됨으로써, 디스플레이에 결합될 수 있다. The plastic substrate layer 100 may be laminated on a display (not shown) of the display device so that it can be bonded to the display.

플라스틱 기재층(100)은 1mm 내지 3mm의 두께를 만족하며, 투명 수지를 를 이용하여 형성될 수 있다. The plastic substrate layer 100 satisfies a thickness of 1 mm to 3 mm and can be formed using a transparent resin.

예를 들어, 플라스틱 기재층(100)은 폴리카보네이트(PolyCarbonate, PC), 폴리메틸메타크릴레이트(PolyMethylMethacrylate PMMA), 폴리스티렌(PolyStyrene PS) 또는 이들의 공중합체(copolymer), 폴리에틸렌테레프탈레이트(PolyEthyleneTerephthalate,PET), 폴리에틸렌나프탈레이트(PolyEthyleneNaphthalate,PEN), 폴리에테르설폰(Polyethersulfone, PES), 알릴(allyl) 수지 중 적어도 하나 또는 이들의 선택적 조합으로부터 형성될 수 있다. For example, the plastic substrate layer 100 may be formed of a material selected from the group consisting of polycarbonate (PC), polymethyl methacrylate PMMA, polystyrene PS or copolymers thereof, polyethylene terephthalate (PET) ), Polyethylene naphthalate (PEN), polyethersulfone (PES), allyl resin, or an optional combination thereof.

탄성층(200)은 플라스틱 기재층(100)의 일면에 적층 형성되며, 탄성을 이용하여 하드 코팅층(300)을 통해 전달되는 물리적 충격이 디스플레이에 전달되는 것을 방지하는 기능을 수행한다. The elastic layer 200 is formed on one surface of the plastic substrate layer 100 and functions to prevent physical shock transmitted through the hard coating layer 300 from being transmitted to the display using elasticity.

한편, 물리적 충격을 완충시키기 위하여 탄성층(200)의 탄성을 높일 경우 물리적 충격에 의한 변형은 방지할 수 있으나, 높은 연신률(elongation)로 인해 공정 중 불량 발생률이 높아지거나, 터치 오작동의 발생 가능성이 증가하며, 탄성층(200) 상에 형성되는 하드 코팅층(300)의 크랙(crack)을 유발할 수도 있다. On the other hand, if the elasticity of the elastic layer 200 is increased in order to buffer physical impacts, deformation due to physical impact can be prevented. However, due to high elongation, And may cause a crack in the hard coating layer 300 formed on the elastic layer 200.

탄성층(200)의 연신률은 탄성층(400)과 반비례 관계로, 탄성층(200)의 경도를 높일수록 연신률이 감소한다. The elongation percentage of the elastic layer 200 is in inverse proportion to the elastic layer 400, and the elongation rate decreases as the hardness of the elastic layer 200 increases.

아래 표 1은 탄성층(200)의 경도와 연신률 간의 관계를 나타낸 것으로서, 탄성층(200)이 실리콘(silicon)으로 형성되는 경우를 예로 들어 나타낸 것이다. Table 1 below shows the relationship between the hardness of the elastic layer 200 and the elongation rate, and shows an example in which the elastic layer 200 is formed of silicon.

표 1. 실리콘 탄성층의 경도와 연성률 간의 관계Table 1. Relationship between Hardness and Ductility of Silicone Elastic Layer

Figure pat00001
Figure pat00001

표 1을 참조하면, 경도가 쇼어(Shore) A 74인 실리콘 A로 탄성층(200)을 형성하는 경우 연신률은 80%이고, 경도가 쇼어(Shore) A 52인 실리콘 B로 탄성층(200)을 형성하는 경우 연신률은 325% 정도이다. 즉, 탄성층(200)의 경도가 증가할수록 탄성층(200)의 연신률은 감소한다. Referring to Table 1, when the elastic layer 200 is formed of silicone A having a hardness of Shore A 74, the elastic layer 200 is formed of silicone B having an elongation of 80% and a hardness of Shore A 52, The elongation is about 325%. That is, as the hardness of the elastic layer 200 increases, the elongation percentage of the elastic layer 200 decreases.

따라서, 탄성층(200)이 하드 코팅층(300)을 통해 전달되는 물리적 충격을 완충시키는 기능을 수행하면서, 불량 발생률과 터치 오작동의 발생 가능성을 감소시키고 하드 코팅층(300)의 크랙을 방지하기 위해서는, 탄성층(200)의 연신률을 적절하게 제어할 필요가 있다. 탄성층(200)의 연신률은 탄성층(200)의 경도를 제어함으로써 조절될 수 있다. Therefore, in order to reduce the possibility of occurrence of defective incidence and malfunction of the touch and to prevent cracking of the hard coat layer 300 while the elastic layer 200 functions to buffer the physical impact transmitted through the hard coat layer 300, It is necessary to control the elongation of the elastic layer 200 appropriately. The elongation percentage of the elastic layer 200 can be adjusted by controlling the hardness of the elastic layer 200.

아래의 수학식 1은 크랙 지수를 나타낸 것이다. The following equation (1) represents the crack index.

Figure pat00002
Figure pat00002

여기서, 크랙 지수는 하드 코팅층(300)의 크랙 발생 지수를 나타내며, 0.7이하일 경우 크랙이 발생하지 않는 것으로 판단한다. 이를 참조하면, 경도가 쇼어(shore) A 74인 실리콘 A로 탄성층(200)을 형성하는 경우 탄성층(200)의 두께가 425um 이하인 경우 하드 코팅층(300)에 크랙이 발생하지 않고, 쇼어(shore) A 52인 실리콘 B로 탄성층(200)을 형성하는 경우 두께와 상관 없이 크랙지수가 0.7을 넘어가 크랙이 발생함을 알 수 있다. Here, the crack index represents the crack occurrence index of the hard coat layer 300, and it is judged that no crack occurs when the index is 0.7 or less. Referring to this, when the elastic layer 200 is formed of silicon A having a hardness of A 74, when the thickness of the elastic layer 200 is 425 μm or less, cracks do not occur in the hard coat layer 300, when the elastic layer 200 is formed of silicon B of 52 A, cracks occur when the crack index exceeds 0.7 regardless of the thickness.

탄성층(200)은 이로 한정되는 것은 아니나, 터치 윈도우를 포함하는 디스플레이에 적용하는 경우, 쇼어(Shore) A 70 내지 쇼어(Shore) A 90의 경도와, 40% 내지 80%의 연신률을 만족할 수 있다. 또한, 탄성층(200)은 75um 내지 300um의 두께를 가지도록 형성될 수 있다. The elastic layer 200 may be applied to a display including a touch window, although it is not limited thereto, it is possible to satisfy the hardness of the Shore A 70 to Shore A 90 and the elongation of 40% to 80% have. Further, the elastic layer 200 may be formed to have a thickness of 75 [mu] m to 300 [mu] m.

탄성층(200)은 실리콘(silicone) 또는 우레탄(urethane) 계열의 고탄성 수지로부터 형성될 수 있다. The elastic layer 200 may be formed of a highly elastic resin of silicone or urethane type.

탄성층(200)은 코팅(coating)과 열경화(thermal curing) 공정을 통해 플라스틱 기재층(100) 상에 형성될 수 있다. The elastic layer 200 may be formed on the plastic substrate layer 100 through a coating process and a thermal curing process.

하드 코팅층(300)은 탄성층(200)의 일 면에 형성되며, 경도가 높아 커버 윈도우의 표면 경도를 향상시키는 기능을 수행한다. The hard coating layer 300 is formed on one side of the elastic layer 200 and has a high hardness to perform the function of improving the surface hardness of the cover window.

하드 코팅층(300)은 고경도의 유기 화합물 또는 유무기 복합 화합물로부터 형성될 수 있다. The hard coat layer 300 may be formed from a high-hardness organic compound or an organic compound.

예를 들어, 하드 코팅층(300)은 아크릴레이트(acrylate)계, 폴리실라잔(polysilazane)계, 아크릴(acrylic)계, 폴리우레탄(polyurethane)계, 에폭시(epoxy)계 화합물 중 적어도 하나 또는 이들의 선택적 조합으로부터 형성될 수 있다. For example, the hard coating layer 300 may include at least one of acrylate, polysilazane, acrylic, polyurethane, and epoxy, May be formed from an optional combination.

하드 코팅층(300)은 유기 화합물 또는 유무기 복합 화합물의 단일층으로 마련되거나, 투명 수지에 유기 화합물 또는 유무기 복합 화합물을 적층 형성하여 형성될 수 있다. The hard coat layer 300 may be formed as a single layer of an organic compound or an organic compound complex, or may be formed by laminating an organic compound or an organic-inorganic hybrid compound on a transparent resin.

하드 코팅층(300)은 연필 경도 6H 이상으로, 10um 내지 250um의 두께를 만족할 수 있다. The hard coat layer 300 may have a pencil hardness of 6H or more and a thickness of 10um to 250um.

전술한 바와 같이, 본 발명의 일 실시 예에 따른 커버 윈도우는 플라스틱 기재층(100) 상에 연필 경도 6H 이상의 고경도 하드 코팅층(300)을 결합함으로써, 표면 경도를 높일 수 있다. As described above, the cover window according to an embodiment of the present invention can increase the surface hardness by bonding the hard hard coating layer 300 having a pencil hardness of 6H or more on the plastic substrate layer 100. [

또한, 플라스틱 기재층(100)과 하드 코팅층(300) 사이에 고탄성의 탄성층(200)을 개재함으로써, 탄성층(200)의 탄성을 이용하여 하드 코팅층(300)을 통해 전달되는 물리적 충격이 흡수되도록 할 수 있다. 이에 따라, 물리적 충격이 플라스틱 기재층(100)을 지나 디스플레이로 전달되는 것이 완화되어, 찍힘 등 디스플레이의 변형으로 인한 오동작 또는 불량 발생을 감소시킬 수 있다. In addition, by interposing a high-elasticity elastic layer 200 between the plastic substrate layer 100 and the hard coat layer 300, physical shock transmitted through the hard coat layer 300 is absorbed by the elasticity of the elastic layer 200 . Accordingly, it is alleviated that the physical impact is transmitted to the display through the plastic substrate layer 100, thereby reducing malfunctions or defects caused by deformation of the display, such as being struck.

전술한 본 발명의 일 실시 예에 따른 커버 윈도우는 액정디스플레이(Liquid Crystal Display, LCD) 등의 표시장치, 스마트폰, 태블릿(tablet) PC 등의 이동 단말기의 디스플레이에 결합되어 디스플레이 보호용으로 사용될 수 있다.
The cover window according to an embodiment of the present invention may be combined with a display of a mobile terminal such as a display device such as a liquid crystal display (LCD), a smart phone, a tablet PC, .

이하, 실험 예를 통하여 본 발명의 실시 예를 좀더 상세하게 설명한다. 실험 예는 본 발명의 실시 예를 좀더 명확하게 설명하기 위하여 제시한 것에 불과하며, 본 발명의 실시 예가 실험 예로 한정되는 것은 아니다.Hereinafter, embodiments of the present invention will be described in more detail with reference to experimental examples. The experimental examples are provided only for the purpose of more clearly illustrating the examples of the present invention, and the examples of the present invention are not limited to the experimental examples.

실험 예Experimental Example

PC로 마련된 플라스틱 기재층(100) 상에 바 코팅(bar coating) 방식으로 50um, 200um, 500um의 두께로 실리콘 재질이 탄성층(200)을 코팅한다. The elastic layer 200 is coated on the plastic substrate layer 100 provided with a PC in a thickness of 50, 200, and 500 um by a bar coating method.

다음으로, 100도의 온도 조건에서 열경화 공정을 통해 탄성층(200)을 고형화한다. 또한, 고형화된 탄성층(200) 상에 10um의 하드 코팅층(300)을 코팅하여 커버 윈도우 시편을 마련한다. Next, the elastic layer 200 is solidified through a thermosetting process at a temperature of 100 degrees. In addition, a cover window specimen is prepared by coating a hard coating layer 300 of 10 um on the solidified elastic layer 200.

다음으로, 커버 윈도우 시편의 상부에서 150g의 모양 추를 낙하시켜 찍힘 여부를 확인한다. 도 2는 실험에 사용된 모양 추를 도시한 것으로서, 모양 추는 원통형상의 몸통과 원추형상의 단부를 포함한다. 또한, 몸통의 직경은 1.1mm 내지 1.4mm이고, 단부의 최소 직경은 0.1mm이다. 또한, 끝단의 경사도는 30도를 만족한다. Next, check whether the 150g weight is dropped from the top of the cover window specimen. Fig. 2 shows a shape weight used in the experiment. The shape weight includes a cylindrical body and a conical end. The diameter of the body is 1.1 mm to 1.4 mm, and the minimum diameter of the end is 0.1 mm. Further, the inclination of the end portion satisfies 30 degrees.

또한, 각 커버 윈도우 시편의 하드 코팅층(300) 상에 커트 나이프(cut knife)로 두 개의 평행선을 형성하고, 커버 윈도우를 25mm의 원주반경을 갖도록 휘게하여 크랙(crack) 유무를 확인한다. Further, two parallel lines are formed on the hard coat layer 300 of each cover window specimen by a cut knife, and the cover window is bent to have a circumferential radius of 25 mm to check for cracks.

아래의 표 2는 실험 결과를 도시한 것이다. Table 2 below shows the experimental results.

표 2. 실험 결과Table 2. Experimental results

Figure pat00003
Figure pat00003

위 표 2에서 실리콘 A는 경도가 쇼어(shore) A 74인 탄성층을 나타내고, 실리콘 B는 경도가 쇼어(shore) A 5인 탄성층이다. In Table 2 above, Silicone A represents an elastic layer with a hardness of Shore A 74 and Silicone B is an elastic layer with a Shore A 5 hardness.

위 실험결과를 참조하면, 실리콘 A로 탄성층(200)을 형성하는 경우, 탄성층(200)의 두께가 50um이면 물리적 충격의 흡수율이 떨어져 찍힘이 발생하고, 탄성층(200)의 두께가 500um이면 탄성층(200)과 하드 코팅층(300)의 연신률 차이로 인한 크랙이 발생한다. When the thickness of the elastic layer 200 is 50 μm, the absorption rate of the physical impact is lowered and the thickness of the elastic layer 200 is 500 μm A crack occurs due to a difference in elongation between the elastic layer 200 and the hard coat layer 300. [

또한, 실리콘 B로 탄성층(200)을 형성하는 경우, 높은 탄성으로 물리적 충격의 흡수율이 높아 찍힘이 발생하지 않으나, 탄성층(200)의 높은 연신률로 인해 하드 코팅층(300)과의 연신률 차가 커져 50um에서도 하드 코팅층(300)에 크랙이 발생한다.
In addition, when the elastic layer 200 is formed of silicone B, the elastic modulus of the elastic layer 200 does not increase due to the high elasticity and the physical impact absorption rate is high. However, the elongation ratio of the elastic layer 200 increases the difference in elongation from the hard coat layer 300 A crack is generated in the hard coat layer 300 even at 50um.

전술한 바와 같이, 본 발명의 실시 예에 따르면, 하드 코팅층을 형성하여 커버 윈도우의 표면 경도를 증가시킬 수 있다. 또한, 하드 코팅층과 플라스틱 기재층 사이에 개재된 탄성층을 통해 외부로부터 가해지는 물리적 충격을 흡수시켜 디스플레이로 전달되는 물리적 충격을 최소화함으로써, 찍힘 등 디스플레이의 변형과 이로 인한 불량 발생을 최소화할 수 있다.
As described above, according to the embodiment of the present invention, a hard coating layer can be formed to increase the surface hardness of the cover window. In addition, by absorbing physical impact externally applied through the elastic layer interposed between the hard coating layer and the plastic substrate layer, physical impact transmitted to the display can be minimized, thereby minimizing the deformation of the display and the occurrence of defects .

상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the present invention as defined by the following claims It can be understood that

Claims (8)

플라스틱 기재층,
상기 플라스틱 기재층 상에 배치되며, 쇼어(Shore) A 70 내지 90의 경도를 가지는 탄성층, 그리고
상기 탄성층 상에 배치되는 하드 코팅층을 포함하는 커버 윈도우.
A plastic substrate layer,
An elastic layer disposed on the plastic substrate layer and having a hardness of Shore A 70 to 90,
And a hard coating layer disposed on the elastic layer.
제1항에 있어서,
상기 탄성층은 75um 내지 300um의 두께를 가지는 커버 윈도우.
The method according to claim 1,
Wherein the elastic layer has a thickness of from about 75 [mu] m to about 300 [mu] m.
제1항에 있어서,
상기 탄성층의 연신률(elongation)은 40% 내지 80%를 만족하는 커버 윈도우.
The method according to claim 1,
Wherein the elongation of the elastic layer satisfies 40% to 80%.
제1항에 있어서,
상기 탄성층은 실리콘(silicone) 또는 우레탄(urethane) 계열의 고탄성 수지로 형성되는 커버 윈도우.
The method according to claim 1,
Wherein the elastic layer is formed of a highly elastic resin such as silicone or urethane.
제1항에 있어서,
상기 플라스틱 기재층은 폴리카보네이트(PolyCarbonate, PC), 폴리메틸메타크릴레이트(PolyMethylMethacrylate PMMA), 폴리스티렌(PolyStyrene PS) 또는 이들의 공중합체(copolymer), 폴리에틸렌테레프탈레이트(PolyEthyleneTerephthalate,PET), 폴리에틸렌나프탈레이트(PolyEthyleneNaphthalate,PEN), 폴리에테르설폰(Polyethersulfone, PES), 알릴(allyl) 수지 중 적어도 하나 또는 이들의 선택적 조합으로부터 형성
The method according to claim 1,
The plastic substrate layer may be formed of at least one selected from the group consisting of polycarbonate (PC), polymethyl methacrylate PMMA, polystyrene PS or copolymers thereof, polyethylene terephthalate (PET), polyethylene naphthalate (PEN), polyethersulfone (PES), allyl resin, or an optional combination thereof.
제1항에 있어서,
상기 플라스틱 기재층은 1mm 내지 3mm의 두께를 만족하는 커버 윈도우.
The method according to claim 1,
Wherein the plastic substrate layer satisfies a thickness of 1 mm to 3 mm.
제1항에 있어서,
상기 하드 코팅층은 아크릴레이트(acrylate)계, 폴리실라잔(polysilazane)계, 아크릴(acrylic)계, 폴리우레탄(polyurethane)계, 에폭시(epoxy)계 화합물 중 적어도 하나 또는 이들의 선택적 조합으로부터 형성되는 커버 윈도우.
The method according to claim 1,
The hard coating layer may be formed of at least one selected from the group consisting of acrylate, polysilazane, acrylic, polyurethane, and epoxy, window.
제1항에 있어서,
상기 하드 코팅층은 10um 내지 250um의 두께를 만족하는 커버 윈도우.The method according to claim 1,
Wherein the hard coat layer satisfies a thickness of from 10 [mu] m to 250 [mu] m.
KR1020130160570A 2013-12-20 2013-12-20 Cover window KR102252194B1 (en)