KR20140108803A - Sheetless hydrogel film and Preparing method ofthere - Google Patents

Sheetless hydrogel film and Preparing method ofthere Download PDF

Info

Publication number
KR20140108803A
KR20140108803A KR1020130022199A KR20130022199A KR20140108803A KR 20140108803 A KR20140108803 A KR 20140108803A KR 1020130022199 A KR1020130022199 A KR 1020130022199A KR 20130022199 A KR20130022199 A KR 20130022199A KR 20140108803 A KR20140108803 A KR 20140108803A
Authority
KR
South Korea
Prior art keywords
hydrogel
film
weight
swelling agent
adipate
Prior art date
Application number
KR1020130022199A
Other languages
Korean (ko)
Other versions
KR102078334B1 (en
Inventor
최영권
나승연
김성수
호환기
홍동현
Original Assignee
아이큐어 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 아이큐어 주식회사 filed Critical 아이큐어 주식회사
Priority to KR1020130022199A priority Critical patent/KR102078334B1/en
Publication of KR20140108803A publication Critical patent/KR20140108803A/en
Application granted granted Critical
Publication of KR102078334B1 publication Critical patent/KR102078334B1/en

Abstract

The present invention relates to a sheetless hydrogel film and a manufacturing method thereof and, more specifically, to a sheetless hydrogel film excellent in mechanical properties such as tensile strength, tensile stress, etc. and adhesive properties even without a bottom layer such as a non-woven fabric, mesh, and a net, and to a manufacturing method thereof.

Description

시트리스 하이드로겔 필름 및 그 이의 제조 방법{Sheetless hydrogel film and Preparing method ofthere}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a sheetless hydrogel film and a preparation method thereof,

본 발명은 부직포, 메쉬, 망과 같은 기재층이 없으면서도 기계적 물성 및 부착성이 우수한 시트리스 하이드로겔 필름 및 그 제조방법에 관한 것이다.The present invention relates to a sheetless hydrogel film excellent in mechanical properties and adhesion without a substrate layer such as a nonwoven fabric, a mesh, and a mesh, and a method for producing the same.

하이드로겔이란, 삼차원 친수성 고분자 망상구조를 가진 물질로서 많은 양의 물이 고분자 물질의 격자 내에 채워져 팽윤된, 수분을 흡수할 수 있는 능력이 있는 상태의 필름을를 말한다. 이러한 하이드로겔 필름은 외부 이력에 의한 유동성이 거의 없는 구조적으로 안정한 삼차원 네트워크 구조를 형성하여 수분을 흡수할 수 있는 능력이 있어 천연 조직과 같은 유연성을 가지고 있다.A hydrogel refers to a film having a three-dimensional hydrophilic polymer network structure in which a large amount of water is filled in a lattice of a polymer material and swelled, and capable of absorbing moisture. Such a hydrogel film has the flexibility as a natural tissue because it has the ability to absorb moisture by forming a structurally stable three dimensional network structure with little fluidity due to external history.

이러한 하이드로겔 또는 하이드로겔로 제조한 필름의 탄성, 밀착성 및 부드러운 촉감을 이용하여 하이드로겔 패취나 화장품 팩 등에 대한 연구 개발이 활발히 이루어져왔다. 그러나 하이드로겔 자체만을 이용하여 필름을 제조할 경우 기계적 강도가 약하여 형태를 유지하기 어렵거나 찢어지는 경우가 종종 발생하여 부직포, 메쉬, 망에 부가하여 사용하는 것이 일반적이였다. 그런데, 이 경우 부직포, 메쉬, 망과 같은 기재층을 팩제층에 도포나 전사하는 공정이 필요함으로써 공정이 복잡하고, 화장수나 기능성 추출물을 첨가하면 뻣뻣하게 되어 부착성이 좋지 않고, 부직포에서 하이드로겔이 떨어져 나가는 경우가 등의 많은 문제점이 있었다.
Research and development on hydrogel patches, cosmetic packs, and the like have been actively conducted by utilizing elasticity, adhesion, and soft touch of films made of such hydrogels or hydrogels. However, when a film is produced using only the hydrogel itself, it is generally difficult to maintain its shape due to its low mechanical strength, and sometimes it is torn, so that it is generally used in addition to nonwoven fabric, mesh and net. However, in this case, a step of coating or transferring a substrate layer such as a nonwoven fabric, a mesh, and a mesh is required, so that the process is complicated. When the cosmetic lotion or the functional extract is added, the stiffness becomes poor and the adhesion is poor. There are many problems such as a problem of falling off.

따라서, 본 발명은 기존 하이드로겔 필름의 문제점을 해결하고자 부직포 등의 기재층(또는 기재필름, 또는 기재시트)을 사용하지 않는 하이드로겔 자체만으로 이루어진 하이드로겔 필름을 제공하고자 한다.Accordingly, it is an object of the present invention to provide a hydrogel film comprising only a hydrogel itself which does not use a substrate layer (or a substrate film or a substrate sheet) such as a nonwoven fabric in order to solve the problems of existing hydrogel films.

상기 과제를 해결하기 위한 본 발명은 시트리스 하이드로겔 필름 수용성 고분자 및 천연 고분자 중에서 선택된 1종 이상을 함유한 고분자 수지, 알긴산나트륨, 가소제 및 보습제를 포함하는 하이드로겔; 및 가교팽윤제;를 포함하는 것을 특징으로 한다.The present invention for solving the above problems is a hydrogel comprising a polymer resin containing at least one selected from the group consisting of a water-soluble polymer and a natural polymer, a sodium alginate, a plasticizer and a humectant; And a cross-linking swelling agent.

본 발명의 바람직한 일실시예로서, 본 발명에 있어서, 상기 가교팽윤제는 Ca2+, Mg2 +, Cu2 +, Fe2 +, Al3 + 및 Fe3 + 중에서 선택된 1종 이상을 함유한 화합물을 포함하는 것을 특징으로 할 수 있다.In a preferred embodiment of the invention, according to the present invention, the cross-linked swelling agent containing Ca 2+, Mg 2 +, Cu 2 +, Fe 2 +, Al 3 + Fe 3 + and at least one selected from Or a compound thereof.

본 발명의 바람직한 다른 일실시예로서, 상기 가교팽윤제는 가교팽윤제 전체 중량 중 상기 화합물 0.01 ~ 10 중량% 및 증류수를 90 ~ 99.99 중량% 포함하고 있는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the crosslinking and swelling agent may include 0.01 to 10% by weight of the compound and 90 to 99.99% by weight of distilled water in the total weight of the crosslinking and swelling agent.

본 발명의 바람직한 다른 일실시예로서, 본 발명의 시트리스 하이드로겔 필름은 상기 하이드로겔 100 중량부에 대하여, 상기 가교팽윤제를 10 ~ 40 중량부로 포함하는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the citrus hydrogel film of the present invention comprises 10 to 40 parts by weight of the crosslinking swelling agent per 100 parts by weight of the hydrogel.

본 발명의 바람직한 또 다른 일실시예로서, 본 발명에 있어서, 상기 수용성 고분자는 수용성 고분자 및 천연 고분자로는 폴리리신, 카르복시메틸 키틴, 피브린, 덱스트란, 폴리비닐알콜, 폴리비닐아세테이트/폴리비닐알콜, 폴리(N-비닐 피롤리돈), 알지네이트-g-(폴리에틸렌옥사이드-폴리프로필렌옥사이드-폴리에틸렌옥사이드), 알지네이트-아크릴레이트, 폴리에틸렌옥사이드 및 폴리에틸렌옥사이드-폴리프로필렌옥사이드 공중합체 중에서 선택된 1종 이상을 포함하는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the water-soluble polymer is a water-soluble polymer and natural polymers include polylysine, carboxymethylchitin, fibrin, dextran, polyvinyl alcohol, polyvinylacetate / polyvinyl alcohol (Polyethylene oxide-polypropylene oxide-polyethylene oxide), alginate-acrylate, polyethylene oxide, and polyethylene oxide-polypropylene oxide copolymer .

본 발명의 바람직한 또 다른 일실시예로서, 본 발명에 있어서, 상기 천연 고분자는 펙틴, 잔탄검, 젤라틴, 로커스트콩 검, 한천, 글루코만난, 카라기난, 젤라틴, 젤란검, 키토산, 콜라겐, 히알루론산, 아카시아검, 아라비아검 및 셀룰로오스 중에서 선택된 1종 이상을 포함하는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the natural polymer is selected from the group consisting of pectin, xanthan gum, gelatin, locust bean gum, agar, glucomannan, carrageenan, gelatin, gellan gum, chitosan, collagen, hyaluronic acid, Gum, gum arabic, and cellulose.

본 발명의 바람직한 또 다른 일실시예로서, 본 발명에 있어서, 상기 가소제로써는 헥실데실벤조에이트, 피피지-3벤질에테르미리스테이트, 폴리에틸렌글리콜, 피이지-8/에스엠디아이코폴리머, 트리카프릴릴/카프릴트리멜리테이트, 트리올레일포스페이트, 트리옥틸리멜리테이트, 트리에틸헥실트리멜리테이트, 트리에틸헥실시트레이트, 트리아세틴, 트리세틸포스페이트, 트리부틸시트레이트, 트리메틸하이드록시펜틸이소부티레이트, 트리메틸펜탄디일디벤조에이트, 캠퍼, 아세틸트리에틸시트레이트, 아세틸트리부틸시트레이트, 슈크로오스아세테이트이소부티레이트, 부틸옥틸벤조에이트, 디펜타에리스리틸헥사 C5-9 애시드에스터, 디카프릴아디페이트, 디이소프로필아디페이트, 디이소프로필세바케이트, 디이소스테아릴아디페이트, 디이소부틸아디페이트, 디이소데실아디페이트, 디에틸헥실아디페이트, 디에틸헥실세바케이트, 디에틸헥실석시네이트, 디에틸프탈레이트, 디에틸옥살레이트, 디에틸세바케이트, 디에틸렌글라이콜디이소노나노에이트, 디부틸아디페이트, 디메치콘피이지-8폴리아크릴레이트, 및 데실옥사졸리디논 중에서 선택된 1종 이상을 포함하는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the plasticizers include hexyldecyl benzoate, piperidine-3 benzyl ether myristate, polyethylene glycol, phage-8 / MDI icopolymer, tricaprylyl / Trioctyl trimellitate, triethyl hexyl tristate, triacetin, tricetyl phosphate, tributyl citrate, trimethylhydroxypentyl isobutyrate, trimethylolpropyl isobutyrate, trimethylolpropyl isobutyrate, Trimethylpentane dibenzoate, camphor, acetyltriethyl citrate, acetyl tributyl citrate, sucrose acetate isobutyrate, butyl octyl benzoate, dipentaerythritol hexa C5-9 acid ester, dicapryl adipate, di Isopropyl adipate, diisopropyl sebacate, diisostearyl adipate, diisobutyl adipate Diethoxyl adipate, diethylhexyl sebacate, diethyl hexyl succinate, diethyl phthalate, diethyl oxalate, diethyl sebacate, diethylene glycol diisononano Dibutyl adipate, dimethicone phosphite-8 polyacrylate, and decyl oxazolidinone.

본 발명의 바람직한 또 다른 일실시예로서, 본 발명에 있어서, 상기 보습제는 글리세린, 솔비톨 및 1,3-부틸렌글리콜 중에서 선택된 1종 이상을 포함하는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the humectant may be at least one selected from the group consisting of glycerin, sorbitol, and 1,3-butylene glycol.

본 발명의 바람직한 또 다른 일실시예로서, 본 발명에 있어서, 상기 하이드로겔은 고분자 수지 20 ~ 80 중량%, 알긴산나트륨 5 ~ 20 중량%, 가소제 2 ~ 35 중량%, 보습제 5 ~ 40 중량%를 포함하는 것을 할 수 있다.In another preferred embodiment of the present invention, the hydrogel comprises 20 to 80% by weight of a polymer resin, 5 to 20% by weight of sodium alginate, 2 to 35% by weight of a plasticizer, and 5 to 40% Can do.

또한, 본 발명의 바람직한 일실시예로서, 상기 하이드로겔은 평균두께 20㎛ ~ 100㎛인 것을 특징으로 할 수 있다.Also, as a preferred embodiment of the present invention, the hydrogel may have an average thickness of 20 탆 to 100 탆.

또한, 본 발명의 바람직한 일실시예로서, 본 발명의 시트리스 하이드로겔 필름은 활성물질 및 수분의 저장고가 형성될 수 있도록 피부와 맞닿는 면에 양음각의 홈부와 돌기부가 형성되되, 상기 홈부의 경계에는 건조필름의 표면보다 돌출된 돌출경계라인이 형성되어 있는 것을 특징으로 할 수 있다. 또한, 본 발명의 시트리스 하이드로겔 필름은 필름의 양면 모두에 상기 홈부와 돌기부가 형성되어 있는 것을 특징으로 할 수 있다.In a preferred embodiment of the present invention, the sheet-like hydrogel film of the present invention has grooves and protrusions of positive intaglio angles on the surface contacting the skin to form a reservoir of active material and moisture, A protruding boundary line protruding from the surface of the dry film is formed. The sheet-free hydrogel film of the present invention can be characterized in that the groove and the protrusion are formed on both sides of the film.

또한, 본 발명의 바람직한 일실시예로서, 본 발명의 시트리스 하이드로겔 필름은 평균두께 25 ㎛~ 250 ㎛인 것을 특징으로 할 수 있다. Further, as a preferred embodiment of the present invention, the citrus hydrogel film of the present invention may be characterized by having an average thickness of 25 탆 to 250 탆.

본 발명의 다른 태양은 앞서 설명한 시트리스 하이드로겔 필름의 제조방법에 관한 것으로서, 하이드로겔용 수지를 제조하는 단계; 이형필름 표면에 상기 하이드로겔용 수지를 도포한 후, 건조시켜서 하이드로겔을 형성시키는 단계; 및 상기 이형필름 표면에 형성된 하이드로겔에 가교팽윤제를 침투시켜서 하이드로겔을 가교 및 팽윤시키는 단계;를 포함하는 것을 공정을 거쳐서 제조하는 것을 특징으로 할 수 있다.Another aspect of the present invention relates to a method for producing the above-mentioned citrus hydrogel film, comprising the steps of: preparing a resin for hydrogel; Applying the resin for hydrogel to the surface of the release film, and then drying the resin to form a hydrogel; And crosslinking and swelling the hydrogel by infiltrating the hydrogel formed on the surface of the release film with a cross-linking swelling agent.

본 발명의 바람직한 일실시예로서, 상기 하이드로겔용 수지는 수용성 고분자 및 천연 고분자 중에서 선택된 1종 이상을 함유한 고분자 수지, 알긴산나트륨, 가소제, 보습제 및 증류수를 포함할 수 있다. 그리고, 그 함유량은 상기 고분자 수지 1 ~ 40 중량%, 상기 알긴산나트륨 0.05 ~ 20중량%, 상기 가소제 0.1 ~ 20 중량%, 상기 보습제 0.1 ~ 20 중량% 및 상기 증류수 20 ~ 98 중량%를 포함하는 것을 특징으로 할 수 있다. In one preferred embodiment of the present invention, the resin for hydrogel may include a polymer resin containing at least one selected from a water-soluble polymer and a natural polymer, sodium alginate, a plasticizer, a humectant, and distilled water. And the content thereof is 1 to 40% by weight of the polymer resin, 0.05 to 20% by weight of the sodium alginate, 0.1 to 20% by weight of the plasticizer, 0.1 to 20% by weight of the moisturizer and 20 to 98% .

본 발명의 바람직한 일실시예로서, 하이드로겔을 형성시키는 단계의 상기 건조는 50℃ ~ 90℃ 하에서, 2분 ~ 20 분간 수행하는 것을 특징으로 할 수 있다.In one preferred embodiment of the present invention, the drying in the step of forming the hydrogel is performed at 50 ° C to 90 ° C for 2 minutes to 20 minutes.

본 발명의 바람직한 다른 일실시예로서, 상기 가교 및 팽윤시키는 단계는 가교팽윤제에 상기 이형필름 표면에 형성된 하이드로겔을 함침시키는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the cross-linking and swelling step may include impregnating a cross-linking swelling agent with a hydrogel formed on the surface of the release film.

본 발명의 바람직한 또 다른 일실시예로서, 상기 가교 및 팽윤시키는 단계는 상기 이형필름 표면에 형성된 하이드로겔의 표면에 가교팽윤제를 분무시키는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the cross-linking and swelling step may be performed by spraying a cross-linking swelling agent on the surface of the hydrogel formed on the surface of the release film.

본 발명의 또 다른 태양은 앞서 설명한 다양한 형태의 시트리스 하이드로겔 필름을 다양한 제품에 응용시킬 수 있으며, 상기 제품은 화장품용 마스크팩, 의료용 패취 등을 포함할 수 있다.Another aspect of the present invention is that the various types of the sheetless hydrogel films described above can be applied to various products, and the products may include mask packs for cosmetics, medical patches and the like.

본 발명의 시트리스 하이드로겔 필름은 그 자체가 인장강도 및 인장응력 등의 기계적 강도가 우수한 바, 필름의 형태 유지, 기계적 강도를 유지시키기 위한 부직포, 메쉬, 망과 같은 기재층이 불필요할 뿐만 아니라, 기재층이 없기 때문에 유연성이 좋고, 피부와의 밀착성, 부착성 및 사용감 등이 우수하며, 기재층 형성을 위한 제조공정이 없기 때문에 기존 하이드로겔 필름을 제조하는 공정에 비해 공정이 단순화되어 제품의 경제성이 우수하다.
The sheet-free hydrogel film of the present invention is excellent in mechanical strength such as tensile strength and tensile stress, and it is not only unnecessary for a base layer such as a nonwoven fabric, a mesh, and a mesh to maintain the shape and mechanical strength of the film , Since it has no base layer, it has good flexibility, has excellent adhesion with skin, adherence and feeling of use, and since there is no manufacturing process for forming a base layer, the process is simplified compared to a process for producing an existing hydrogel film, It is economical.

도 1은 본 발명의 일실시예로서, 시트리스 하이드로겔 마스크팩의 정면도이다.
도 2는 도 1에 도시된 Ⅱ-Ⅱ선에 의한 단면도이다.
도 3 내지 도 7은 도 1 및 도 2에 나타낸 일실시예와 다른 형태로 홈부를 형성시킨 하이드로겔 필름에 대한 개략도이다.
도 8은 본 발명의 시트리스 하이드로겔 필름을 화장용 마스크팩 형태로 응용한 예를 나타낸 것이다.1 is a front view of a sheetless hydrogel mask pack according to one embodiment of the present invention.
2 is a sectional view taken along the line II-II shown in Fig.
FIGS. 3 to 7 are schematic views of a hydrogel film in which a groove is formed in a manner different from the embodiment shown in FIGS. 1 and 2. FIG.
Fig. 8 shows an application example of the citrus hydrogel film of the present invention in the form of a cosmetic mask pack.

본 발명에서 사용하는 용어인 "증류수"는 탈이온수, 정수된 물 등의 순수한 물을 포함하는 의미이다As used herein, the term "distilled water" is meant to include pure water, such as deionized water, purified water, and the like

본 발명에서 사용하는 용어인 "활성물질" 및/또는 "유효성분"의 의미는 본 발명의 시트리스 하이드로겔 필름의 용도에 따라 사용되는 화장성분, 미용성분, 약제성분 등을 포함하는 의미이다.The meaning of the term "active substance" and / or "active ingredient" used in the present invention is meant to include cosmetic ingredients, cosmetic ingredients, pharmaceutical ingredients and the like used depending on the use of the citrus hydrogel film of the present invention.

이하, 본 발명을 더욱 구제적으로 설명을 한다.Hereinafter, the present invention will be described further.

본 발명의 하이드로겔 필름은 그 자체로 우수한 기계적 물성을 갖는 바, 기재층(또는 기재시트, 기재필름)이 불필요하며, 본 발명의 하이드로겔 필름은 하이드로겔; 및 가교팽윤제;를 포함할 수 있다.Since the hydrogel film of the present invention itself has excellent mechanical properties, the base layer (or substrate sheet, base film) is not required, and the hydrogel film of the present invention is a hydrogel; And a cross-linking swelling agent.

본 발명에 있어서, 상기 가교팽윤제는 하이드로겔을 가교 및 팽창시키는 역할을 하는데, 이러한 가교팽윤제로서 다가양이온을 함유한 화합물을 사용할 수 있으며, 바람직하게는 Ca2 +, Mg2 +, Cu2 +, Fe2 +, Al3 + 및 Fe3 + 중에서 선택된 1종 이상을 함유한 화합물을 포함하는 것을, 더욱 바람직하게는 Ca2 + 및 Mg2 + 중에서 선택된 1종 이상을 포함하는 화합물을 사용할 수 있다. 이를 좀 더 구체적으로 설명하면, Ca(OH)2, CaCl2, C6H10CaO6, Mg(OH)2,MgCl2, Mg(NO3)2, MgS, MgSO4 및 MgCO3 등의 화합물을 사용할 수 있다.In the present invention, the crosslinking swelling agent serves to crosslink and expand the hydrogel. As such a crosslinking swelling agent, a compound containing a polyvalent cation can be used, preferably Ca 2 + , Mg 2 + , Cu 2 + , Fe 2 + , Al 3 + and Fe 3 + , more preferably compounds containing at least one selected from Ca 2 + and Mg 2 + can be used have. More specifically, compounds such as Ca (OH) 2 , CaCl 2 , C 6 H 10 CaO 6 , Mg (OH) 2 , MgCl 2 , Mg (NO 3 ) 2 , MgS, MgSO 4 and MgCO 3 Can be used.

본 발명에 있어서, 상기 가교팽윤제는 가교팽윤제 전체 중량 중 상기 화합물 0.01 중량% ~ 10 중량%를, 바람직하게는 0.1 중량%~ 8 중량%를, 더욱 바람직하게는 1 중량% ~ 5 중량%를 포함할 수 있으며, 가교팽윤제의 다른 나머지 조성은 상기 화합물 외에 증류수를 포함할 수 있다. 그리고, 가교팽윤제에 있어서, 상기 화합물의 함량이 0.01 중량% 미만이면 하이드로겔과의 충분한 가교 및 팽윤 효과를 볼 수 없고, 10 중량%를 초과하면 하이드로겔이 너무 팽윤되어서 필름의 두께가 두꺼워지게 되고, 단단하여 유연성이 없는 문제가 있을 수 있으므로 상기 범위 내로 상기 화합물을 포함하는 것이 좋다.In the present invention, the crosslinking and swelling agent preferably contains 0.01 wt% to 10 wt%, preferably 0.1 wt% to 8 wt%, more preferably 1 wt% to 5 wt% of the compound in the total weight of the crosslinking swelling agent, And other components of the crosslinking swelling agent may include distilled water in addition to the compound. If the content of the compound is less than 0.01% by weight, sufficient crosslinking and swelling effects with the hydrogel can not be obtained. When the content of the compound exceeds 10% by weight, the hydrogel is excessively swollen to increase the thickness of the film And there may be a problem that it is hard and not flexible. Therefore, it is preferable to include the above compound within the above range.

또한, 본 발명의 시트리스 하이드로겔 필름에 있어서, 가교팽윤제의 사용량은 상기 하이드로겔 100 중량부에 대하여, 상기 가교팽윤제를 10 중량부 ~ 40 중량부로 사용하는 것이 좋다. 여기서, 가교팽윤제의 사용량이 10 중량부 미만이면 그 사용량이 너무 적어서 충분한 가교 및 팽윤 효과를 볼 수 없고, 40 중량부를 초과하여 사용하더라도 더 이상의 가교 및 팽윤 효과 증가가 없는 바, 비경제적이다.In addition, in the citrus hydrogel film of the present invention, the amount of the crosslinking swelling agent is preferably 10 parts by weight to 40 parts by weight of the crosslinking swelling agent per 100 parts by weight of the hydrogel. If the amount of the cross-linking swelling agent is less than 10 parts by weight, the amount of the cross-linking swelling agent used is too small to exhibit sufficient crosslinking and swelling effects, and even when used in excess of 40 parts by weight, there is no further increase in crosslinking and swelling effects.

본 발명에 있어서, 상기 하이드로겔은 수용성 고분자 및 천연 고분자 중에서 선택된 1종 이상을 함유한 고분자 수지, 알긴산나트륨, 가소제 및 보습제를 포함할 수 있으며, 상기 하이드로겔은 고분자 수지 20 중량% ~ 80 중량%, 알긴산나트륨 5 중량% ~ 20 중량%, 가소제 2 중량% ~ 35 중량% 및 보습제 5 중량% ~ 40 중량%를 포함할 수 있다.In the present invention, the hydrogel may include a polymer resin containing at least one selected from a water-soluble polymer and a natural polymer, sodium alginate, a plasticizer, and a humectant. The hydrogel may include 20 to 80 wt% 5 to 20% by weight of sodium alginate, 2 to 35% by weight of a plasticizer and 5 to 40% by weight of a moisturizer.

상기 수용성 고분자는 수용성 고분자 및 천연 고분자로는 폴리리신(polylysine), 카르복시메틸 키틴, 피브린(fibrin), 덱스트란(dextran), 폴리비닐알콜(PVA) 폴리비닐아세테이트/폴리비닐알콜(PVAc/PVA), 폴리(N-비닐 피롤리돈)(PVP), 알지네이트-g-(폴리에틸렌옥사이드-폴리프로필렌옥사이드-폴리에틸렌옥사이드)(alginate-g-(PEO-PPO-PEO)), 알지네이트-아크릴레이트(alginate-acrylate), 폴리에틸렌옥사이드(PEO), 및 폴리에틸렌옥사이드-폴리프로필렌옥사이드 공중합체(PEO-PPO, Pluronic series), 중에서 선택된 1종 이상을, 바람직하게는 PVA, PVAc/PVA, PVP, PEO 및 PEO-PPO 중에서 선택된 1종 이상을 포함할 수 있다.Examples of the water-soluble polymer include polylysine, carboxymethylchitin, fibrin, dextran, polyvinyl alcohol (PVA) polyvinyl acetate / polyvinyl alcohol (PVAc / PVA) , Poly (N-vinylpyrrolidone) (PVP), alginate-g- (polyethylene oxide-polypropylene oxide-polyethylene oxide), alginate-g- (PEO-PPO-PEO), alginate- PVA, PVP, PEO, and PEO-PPO (PEO-PPO), preferably at least one selected from the group consisting of polyethylene oxide (PEO), acrylate, polyethylene oxide (PEO), and polyethylene oxide- And the like.

그리고, 상기 천연 고분자는 펙틴(Pectin), 잔탄검(Xanthan gum), 젤라틴, 로커스트콩 검(LBG; Locust Bean Gum), 한천(Agar), 글루코만난(Glucomannan), 카라기난(Carrageenan), 젤란검(gellangum), 키토산, 콜라겐, 히알루론산, 아카시아검, 아라비아검 및 셀룰로오스 중에서 선택된 1종 이상을, 바람직하게는 젤라틴, 팩틱, 잔탄검, 글루코만난, 구아검, 키토산, 골라겐 및 셀룰로오스 중에서 선택된 1종 이상을 포함하는 것을 특징으로 할 수 있다.The natural polymers may be selected from the group consisting of pectin, Xanthan gum, gelatin, locust bean gum, agar, glucomannan, carrageenan, gellangum, ), Chitosan, collagen, hyaluronic acid, acacia gum, gum arabic and cellulose, preferably at least one selected from gelatin, phacic, xanthan gum, glucomannan, guar gum, chitosan, And the like.

상기 고분자 수지는 하이드로겔 전체 중량 중 20 중량% ~ 80 중량%를, 바람직하게는 20 중량% ~ 75 중량%를 포함할 수 있는데, 20 중량% 미만인 경우 제조된 하이드로겔 필름의 기계적 물성이 떨어질 수 있고, 80 중량%를 초과하면 점도가 너무 높아서 도포 작업에 어려움이 있을 수 있으므로 상기 범위 내에서 사용하는 것이 좋다.The polymer resin may contain 20% by weight to 80% by weight, preferably 20% by weight to 75% by weight in the total weight of the hydrogel. If the amount is less than 20% by weight, the mechanical properties of the hydrogel film may be deteriorated If it exceeds 80% by weight, the viscosity may be too high, which may cause difficulty in the coating operation.

본 발명에 있어서, 하이드로겔 성분 중 하나인 상기 알긴산나트륨은 친수성 천연 고분자로 다가 양이온에 의해 가교역할, 즉 매트릭스(matrix)를 형성시키는 역할을 하며, 하이드로겔 전체 중량 중 5 중량% ~ 20 중량%를, 바람직하게는 6 ~ 18 중량%를 포함할 수 있는데, 5 중량% 미만인 경우 가교성이 떨어져서 매트릭스 형성이 어려운 문제가 발생할 수 있고, 20 중량%를 초과하면 점도가 너무 높아 사용이 용이하지 않는 문제가 있을 수 있으므로 상기 범위 내에서 사용하는 것이 좋다.In the present invention, the sodium alginate, which is one of the hydrogel components, is a hydrophilic natural polymer and serves to form a matrix by cross-linking with polyvalent cations. The sodium alginate is used in an amount of 5 wt% to 20 wt% If the amount is less than 5% by weight, crosslinking may be difficult and matrix formation may be difficult. If it is more than 20% by weight, viscosity may be too high to be easily used It is recommended to use within the above range because there may be a problem.

하이드로겔 성분 중 하나인 상기 가소제로써는 본 발명에 있어서, 건조된 필름에 유연성을 부가하는 역할을 하며, 하이드로겔 전체 중량 중 2 중량% ~ 35 중량%를, 바람직하게는 5 중량% ~ 35 중량%를 포함할 수 있는데, 2 중량% 미만인 경우 건조된 필름이 유연성이 떨어져서 갈라지거나 부서지는 문제가 발생할 수 있고, 35 중량%를 초과하면 건조가 잘 안되거나, 건조되더라도 건조된 필름이 끈적거리는 문제가 있을 수 있으므로 상기 범위 내에서 사용하는 것이 좋다.The plasticizer, which is one of the components of the hydrogel, serves to add flexibility to the dried film in the present invention and is used in an amount of 2 wt% to 35 wt%, preferably 5 wt% to 35 wt% If it is less than 2% by weight, the dried film may become less flexible and may cause cracking or breakage. If it exceeds 35% by weight, drying may be difficult or the dried film may become sticky It is recommended to use it within the above range.

상기 가소제는 헥실데실벤조에이트(Hexyldecyl Benzoate), 피피지-3벤질에테르미리스테이트(PPG-3 Benzyl Ether Myristate), 폴리에틸렌글리콜(Polyethyleneglycol, PEG), 피이지-8/에스엠디아이코폴리머(PEG-8/SMDI Copolymer), 트리카프릴릴/카프릴트리멜리테이트(Tricaprylyl/Capryl Trimellitate), 트리올레일포스페이트(Trioeyl Phosphate), 트리옥틸리멜리테이트(Trioctyl Trimellitate), 트리에틸헥실트리멜리테이트(Triethylhexyl Trimellitate), 트리에틸헥실시트레이트(Tricthylhexyl Citrate), 트리아세틴(Triacetin), 트리세틸포스페이트(Tricetyl Phosphate), 트리부틸시트레이트(Tributyl Citrate), 트리메틸하이드록시펜틸이소부티레이트(Trimethyl Hydroxypentyl Isobutyrate), 트리메틸펜탄디일디벤조에이트(Trimethylpentanediyl Dibenzoate), 캠퍼(Camphor), 아세틸트리에틸시트레이트(Acetyl Triethyl Citrate), 아세틸트리부틸시트레이트(Acetyl Tributyl Citrate), 슈크로오스아세테이트이소부티레이트(Sucrose Acetate Isobutyrate), 부틸옥틸벤조에이트(Butyloctyl Benzoate), 디펜타에리스리틸헥사 C5-9애씨애시드에스터(Dipentaerythrityl Hexa C5-9 Acid Esters), 디카프릴아디페이트(Dicapryl Adipate), 디이소프로필아디페이트(Diisopropyl Adipate), 디이소프로필세바케이트(Diisopropyl Sebacate), 디이소스테아릴아디페이트(Diisostearyl Adipate), 디이소부틸아디페이트(Diisobutyl Adipate), 디이소데실아디페이트(Diisodecyl Adipate), 디에틸헥실아디페이트(Diethylhexyl Adipate), 디에틸헥실세바케이트(Diethylhexyl Sebacate), 디에틸헥실석시네이트(Diethylhexyl Succinate), 디에틸프탈레이트(Diethyl Phthalate), 디에틸옥살레이트(Diethyl Oxalate), 디에틸세바케이트(Diethyl Sebacate), 디에틸렌글라이콜디이소노나노에이트(Diethylene Glycol Diisononanoate), 디부틸아디페이트(Dibutyl Adipate), 디메치콘피이지-8폴리아크릴레이트(Dimethicone PEG-8 Polyacrylate), 및 데실옥사졸리디논(Decyloxazolidinone) 중에서 선택된 1종 이상을 포함하는 것을 특징으로 할 수 있다.The plasticizer is selected from the group consisting of Hexyldecyl Benzoate, PPG-3 Benzyl Ether Myristate, Polyethyleneglycol (PEG), Pigment-8 / SMDI Copolymer), Tricaprylyl / Capryl Trimellitate, Trioeyl Phosphate, Trioctyl Trimellitate, Triethylhexyl Trimellitate, Tricetyl Hexyl Citrate, Triacetin, Tricetyl Phosphate, Tributyl Citrate, Trimethyl Hydroxypentyl Isobutyrate, trimethylpentane diisobutyrate, Trimethylpentanediyl Dibenzoate, Camphor, Acetyl Triethyl Citrate, Acetyl Tributyl Citrate (Acetyl Tr ibutyl Citrate, Sucrose Acetate Isobutyrate, Butyloctyl Benzoate, Dipentaerythrityl Hexa C5-9 Acid Esters, Dicapril Adipate, (Dicapryl Adipate), diisopropyl adipate, diisopropyl sebacate, diisostearyl adipate, diisobutyl adipate, diisopropyl adipate, diisopropyl adipate, But are not limited to, diisobutyl adipate, diisodecyl adipate, diethylhexyl adipate, diethylhexyl sebacate, diethylhexyl succinate, diethyl phthalate, diethyl oxalate, For example, diethyl oxalate, diethyl sebacate, diethylene glycol diisononanoate, dibutyl adipate, , Dimethicone PEG-8 Polyacrylate, and Decyloxazolidinone. The term " polyglycidyl "

또한, 하이드로겔 성분 중 하나인 상기 보습제로써는 본 발명의 하이드로겔 필름의 수분, 활성물질 등의 유효성분을 유지하는 역할을 하며, 하이드로겔 전체 중량 중 5 중량% ~ 40 중량%를, 바람직하게는 5 중량% ~ 35 중량%를 포함할 수 있는데, 5 중량% 미만인 경우 그 효과가 미비하여 보습효과가 떨어지는 문제가 발생할 수 있고, 40 중량%를 초과하면 너무 끈쩍거릴 수 있으므로 상기 범위 내에서 사용하는 것이 좋다. 그리고, 상기 보습제로는 글리세린, 솔비톨, 프로필렌글리콜, 폴리프로필렌글리콜, 및 1,3-부틸렌글리콜 중에서 선택된 1종 이상을, 바람직하게는 글리세린, 솔비톨 및 1,3-부틸렌글리콜 중에서 선택된 1종 이상을 사용할 수 있다.The moisturizing agent, which is one of the components of the hydrogel, serves to retain the active ingredient such as moisture and active substance of the hydrogel film of the present invention, and is used in an amount of 5 wt% to 40 wt% of the total weight of the hydrogel, If the amount is less than 5% by weight, the effect may be insufficient and the moisturizing effect may be deteriorated. If the amount is more than 40% by weight, it may be too hard to be used. It is good. The moisturizing agent may be at least one selected from glycerin, sorbitol, propylene glycol, polypropylene glycol, and 1,3-butylene glycol, preferably at least one selected from glycerin, sorbitol and 1,3-butylene glycol Or more can be used.

상기 조성을 통해 제조된 하이드로겔은 평균두께 20㎛ ~ 100㎛인 것을, 바람직하게는 25㎛ ~ 80 ㎛인 것이 좋은데, 하이드로겔의 평균두께가 20㎛ 미만이면 하이드로겔 필름의 두께가 너무 얇아서 기계적 강도가 약해지는 문제가 있을 수 있고, 100 ㎛를 초과하면 팽윤된 하이드로겔 필름의 두께가 너무 두꺼워지는 문제가 있을 수 있다.When the average thickness of the hydrogel is less than 20 μm, the thickness of the hydrogel film is too thin, so that the mechanical strength There may be a problem that the thickness of the swollen hydrogel film becomes too thick if it exceeds 100 mu m.

상기 하이드로겔은 가교팽윤제에 의해 가교 및 팽윤되어 본 발명의 시트리스 하이드로겔 필름으로 제조되며, 팽윤된 시트리스 하이드로겔 필름의 평균두께는 25㎛ ~ 250㎛를, 바람직하게는 30㎛ ~ 200㎛를, 더욱 바람직하게는 50㎛ ~ 150㎛인 것이 좋다.The hydrogel is crosslinked and swollen by the crosslinking swelling agent to produce the sheetless hydrogel film of the present invention. The average thickness of the swelled sheetless hydrogel film is 25 to 250 탆, preferably 30 to 200 탆 Mu m, and more preferably 50 mu m to 150 mu m.

본 발명의 시트리스 하이드로겔 필름은 홈부와 돌기부가 없는 무형으로 제조할 수 있으며 또는 홈부와 돌기부가 형성된 음각 및/또는 양각 형태로 제조할 수 있다. 일례로서, 도 1의 정면도 및 도 2의 단면도에 도시된 바와 같이 활성물질 등의 유효성분 및 수분의 저장고가 형성될 수 있도록 피부와 맞닿는 면에 양음각의 홈부(10a, 10b)와 홈부 사이에 돌기부가 형성되되, 상기 홈부의 경계에는 필름의 표면보다 돌출된 돌출경계라인(10c)이 형성되어 있는 것을 특징으로 할 수 있다. 또한, 본 발명의 시트리스 하이드로겔 필름은 필름의 일면에만 또는 양면 모두에 상기 홈부와 돌기부가 형성되어 있는 것을 특징으로 할 수 있다. The sheet-like hydrogel film of the present invention can be produced as an intaglio without grooves and protrusions, or can be produced in the form of intaglio and / or relief formed with grooves and protrusions. For example, as shown in the front view of FIG. 1 and the sectional view of FIG. 2, grooves 10a and 10b of positive intaglio angles are formed on the surface contacting with the skin so that a reservoir of active ingredients such as active substances, And protruding boundary lines 10c protruding from the surface of the film are formed at the boundaries of the groove portions. The sheetless hydrogel film of the present invention may be characterized in that the grooves and protrusions are formed on only one side or both sides of the film.

도 2를 참고하면, 본 발명에 의한 마스크팩(10)의 양면을 볼 수 있다. 상하부에 모두 홈부(10a, 10b)들이 형성되어 있는 것을 볼 수 있다. 따라서 활성물질 등의 유효성분과 수분이 상하부면 어느 쪽이든지 공급되어 사용자가 어느 면이든지 사용할 수 있다. 그리고, 참조번호 20으로 표현된 것은 활성물질 등의 유효성분이 묻은 것을 상정하여 그린 것이다. 일반적인 표면에 비하여 홈부(10a,10b)가 형성됨으로써 활성물질 등의 유효성분 및 수분과 접하는 표면적이 크기 때문에 표면장력이 그만큼 증가하여 더욱 많은 양을 저장할 수 있을 뿐만 아니라 흘러내리지 않게 된다. 또한 본 발명의 하이드로겔 필름의 홈부(10a, 10b)의 경계에는 하이드로겔 필름(10) 표면보다 돌출된 돌출경계라인(10c)이 형성되어 있으며, 이것에 의해 더욱 표면장력이 증가하게 되어 흘러내림 방지 효과를 향상시킬 수 있다. Referring to FIG. 2, both sides of the mask pack 10 according to the present invention can be seen. It can be seen that the groove portions 10a and 10b are formed on the upper and lower portions. Therefore, the active ingredient such as the active substance and moisture can be supplied to either the upper or lower surface, so that the user can use any surface. The reference numeral 20 is drawn on the assumption that an active ingredient such as an active substance is added. Since the grooves 10a and 10b are formed in comparison with a general surface, the surface tension in contact with the active ingredient such as the active material and the moisture is large, so that the surface tension increases to such an extent that a larger amount can be stored and the flow can not be reduced. In addition, a protruding boundary line 10c protruding from the surface of the hydrogel film 10 is formed at the boundary of the groove portions 10a and 10b of the hydrogel film of the present invention, It is possible to improve the prevention effect.

도 3 ~ 도 7 각각은 도 1 및 도 2에 나타낸 일실시예와 다른 형태로 홈부를 형성시킨 하이드로겔 필름을 나타낸 것으로서, 도 3및 도 4 각각은 홈부를 사각형 및 육각형으로 형성시킨 형태이며, 도 5 내지 도 7 각각은 홈부 대신 원형, 사각형 및 육각형으로 돌출불 형성시킨 것이며, 상황에 따라 효과적인 형태로 홈부 및 돌출부를 형성시켜서 본 발명의 하이드로겔 필름을 제조할 수 있다. 그리고, 도 8에 화장용 마스크팩 형태로 본 발명의 시트리스 하이드로겔 필름을 응용한 예를 나타낸 것으로서, 상부마스크팩(100)과 하부마스크팩(200)으로 나뉘어져 있다. 이러한 구성을 가짐으로써 시트리스 하이드로겔 필름 한 장으로 이루어진 경우보다 좀 더 얼굴의 굴곡에 맞게 적용할 수 있게 된다. 얼굴은 평면이 아니라 3차원의 굴곡을 갖는 3차원 구조이기 때문에 두 개로 제작함으로써 더욱 얼굴의 굴곡에 대응할 수 있다. 물론 이러한 모든 면에는 상술한 음각 및/또는 양각이 형성된 형태로 적용시킬 수 있다.
3 to 7 each show a hydrogel film in which a groove is formed in a manner different from the embodiment shown in Figs. 1 and 2. Each of Figs. 3 and 4 is a shape in which a groove is formed in a rectangular shape and a hexagon, Each of FIGS. 5 to 7 may be formed in a shape of a circle, a square, or a hexagon instead of a groove, and the groove and protrusion may be formed in an effective form according to the circumstances to produce the hydrogel film of the present invention. FIG. 8 shows an application example of the sheetless hydrogel film of the present invention in the form of a cosmetic mask pack, which is divided into an upper mask pack 100 and a lower mask pack 200. By adopting such a configuration, it is possible to apply the film more flexibly to the face than in the case of a single sheet of hydrogel film. Since the face is not a plane but a three-dimensional structure with three-dimensional bending, it can cope with the bending of the face more by making it with two pieces. Of course, all of these aspects can be applied to the embossed and / or embossed forms described above.

이하에서는 앞서 설명한 시트리스 하이드로겔 필름을 제조하는 방법에 대하여 설명을 한다.Hereinafter, a method for producing the above-described citrus hydrogel film will be described.

본 발명의 하이드로겔 필름은 하이드로겔에 가교팽윤제를 침투시켜서 제조할 수 있는데, 이를 구체적으로 설명을 하면, 하이드로겔용 수지를 제조하는 단계; 이형필름 표면에 상기 하이드로겔용 수지를 도포한 후, 건조시켜서 하이드로겔을 형성시키는 단계; 및 상기 이형필름 표면에 형성된 하이드로겔에 가교팽윤제를 침투시켜서 하이드로겔을 가교 및 팽윤시키는 단계;를 포함하는 것을 공정을 거쳐서 제조할 수 있다. The hydrogel film of the present invention can be prepared by impregnating a hydrogel with a cross-linking swelling agent. Specifically, the hydrogel film can be produced by: preparing a resin for hydrogel; Applying the resin for hydrogel to the surface of the release film, and then drying the resin to form a hydrogel; And crosslinking and swelling the hydrogel by infiltrating the hydrogel formed on the surface of the release film with a crosslinking swelling agent.

상기 하이드로겔용 수지는 수용성 고분자 및 천연 고분자 중에서 선택된 1종 이상을 함유한 고분자 수지, 알긴산나트륨, 가소제, 보습제 및 증류수를 포함할 수 있다. 그리고, 그 함유량은 상기 고분자 수지 1 중량% ~ 40 중량%, 상기 알긴산나트륨 0.05 중량% ~ 20중량%, 상기 가소제 0.1 중량% ~ 20 중량%, 상기 보습제 0.1 중량% ~ 20 중량% 및 상기 증류수 20 중량% ~ 98 중량%를 포함하는 것을 특징으로 할 수 있다. The resin for hydrogel may include a polymer resin containing at least one selected from a water-soluble polymer and a natural polymer, sodium alginate, a plasticizer, a humectant, and distilled water. The content of the polymeric resin is 1 wt% to 40 wt%, the sodium alginate 0.05 wt% to 20 wt%, the plasticizer 0.1 wt% to 20 wt%, the humectant 0.1 wt% to 20 wt%, and the distilled water 20 By weight to 98% by weight.

그리고, 하이드로겔을 형성시키는 단계의 상기 건조는 50℃ ~ 90℃ 하에서, 2분 ~ 20 분간, 바람직하게는 50℃ ~ 80℃ 하에서, 5분 ~ 10 분간 수행할 수 있으며, 건조를 수행하면 이형필름 표면에 도포된 하이드로겔용 수지에 함유된 증류수가 증발하면서 하이드로겔용 수지가 겔화되어 하이드로겔이 형성하게 된다.The drying in the step of forming the hydrogel may be carried out at 50 to 90 ° C for 2 to 20 minutes, preferably at 50 to 80 ° C for 5 to 10 minutes, The distilled water contained in the resin for hydrogel applied to the surface of the film is evaporated, and the hydrogel resin is gelled to form a hydrogel.

또한, 가교 및 팽윤시키는 단계는 가교팽윤제에 상기 이형필름 표면에 형성된 하이드로겔을 함침시키거나 또는 이형필름 표면에 형성된 하이드로겔의 표면에 가교팽윤제를 분무(또는 도포)시켜서 하이드로겔에 가교팽윤제를 침투시켜서 가교 및 팽윤을 수행할 수 있다.The crosslinking and swelling step may be performed by impregnating a crosslinking swelling agent with a hydrogel formed on the surface of the release film or by spraying (or applying) a crosslinking swelling agent on the surface of the hydrogel formed on the surface of the releasing film, Crosslinking and swelling can be carried out by penetrating the agent.

그리고, 가교팽윤제에 의하여 하이드로겔이 팽윤되면 팽윤에 의해 하이드로겔이 이형필름으로부터 저절로 분리가 이루어진다. 따라서, 제조된 시트리스 하이드로겔 필름을 이형필름으로부터 분리시키는 별도의 공정을 불필요하다.When the hydrogel is swollen by the crosslinking swelling agent, the hydrogel is spontaneously separated from the release film by swelling. Therefore, a separate step of separating the produced sheetless hydrogel film from the release film is unnecessary.

앞서 설명한 다양한 형태의 시트리스 하이드로겔 필름은 그 자체로 우수한 기계적 강도를 갖는 바, 기재필름(또는 기재층)을 반드시 요하지 않기 때문에 높은 박리성, 피부와의 밀착성, 부착성 등이 우수하다. 이러한 본 발명의 시트리스 하이드로겔 필름은 화장품용 마스크팩, 의료용 패취 등의 다양한 제품으로 광범위하게 응용할 수 있다.
The above-described various types of the sheet-like hydrogel films have excellent mechanical strengths themselves and do not necessarily require a substrate film (or substrate layer), so they have high peelability, adhesion to the skin, and adhesion. Such a sheetless hydrogel film of the present invention can be widely applied to various products such as mask packs for cosmetics, medical patches and the like.

이하에서는 실시예를 통하여 본 발명을 더욱 상세히 설명하기로 하나, 본 발명은 하기의 실시예에 의해 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited by the following Examples.

[[ 실시예Example ]]

준비예Preparation Example :  : 가교팽윤제의Of crosslinking swelling agent 제조 Produce

2-하이드록시프로패노익산(2-Hydroxypropanoic acid calcium salt, C6H10CaO6) 30 g을 증류수 1 L에 투입, 교반하여 C6H10CaO6을 3 중량%로 함유한 가교팽윤제를 제조하였다.
30 g of 2-hydroxypropanoic acid calcium salt (C 6 H 10 CaO 6 ) was added to 1 L of distilled water and stirred to prepare a crosslinking swelling agent containing 3 wt% of C 6 H 10 CaO 6 .

실시예Example 1 One

25℃에서, 폴리비닐알코올(PVA) 수지(O사의 PVA 제품, 중량평균분자량= 85,000), 알긴산 나트륨, 잔탄검(J사의 JMU), 팩틴, 글리세린(M사의 글리세린), 폴리에틸렌글리콜(PEG, G사의 PEG1500) 및 증류수를 하기 표 1에 나타낸 바와 같은 중량%로 교반 및 혼합하여 하이드로겔용 수지를 제조하였다.(PVA product of O company, weight average molecular weight = 85,000), sodium alginate, xanthan gum (JMU of J company), pectin, glycerin (glycerin of M company), polyethylene glycol (PEG, G Ltd.) and distilled water were mixed and stirred at the weight percentages shown in Table 1 below to prepare a resin for hydrogel.

다음으로 도 1에 나타낸 바와 같은 형태와 반대로 표면에 원형의 양각이 형성되어 있는 폴리에틸렌테레프탈레이트 필름(PET 필름, 이형필름)의 표면에 상기 하이드로겔용 수지를 자동 도포기를 사용하여 도포시켰다.Next, the above-mentioned resin for hydrogel was applied to the surface of a polyethylene terephthalate film (PET film, release film) having a round embossed surface formed on the surface as shown in Fig. 1, using an automatic applicator.

다음으로 하이드로겔용 수지가 도포된 PET 필름을 건조기에 투입한 후, 70℃에서 10 분간 건조를 수행하여 하이드로겔용 수지를 겔화시켜서 PET 필름 상단면에 하이드로겔(PET 필름-하이드로겔)을 형성시켰다. 겔화 또는 건조된 하이드로겔의 두께는 62 ㎛였다. Next, a PET film coated with a resin for a hydrogel was put in a dryer, followed by drying at 70 ° C for 10 minutes to gel the resin for hydrogel to form a hydrogel (PET film-hydrogel) on the top surface of the PET film. The thickness of the gelated or dried hydrogel was 62 탆.

다음으로 상기 PET 필름-하이드로겔을 파우치에 넣은 후, 준비예에서 제조한 가교팽윤제를 상기 파우치에 충진시킨 후, 가교팽윤제가 PET 필름-하이드로겔 투습되도록 8 분간 놔뒤서, 두께 105 ㎛의 시트리스 하이드로겔 필름을 제조하였으며, 제조된 필름의 하이드로겔 100 중량부에 대하여 가교팽윤제가 33 중량부로 포함하고 있었으며, 이는 상기 투습 전후의 무게변화를 통해서 확인하였다.
Next, the PET film-hydrogel was poured into the pouch, and the crosslinking swelling agent prepared in the preparation example was filled in the pouch. After the crosslinked swelling agent was allowed to permeate the PET film-hydrogel for 8 minutes, And a crosslinked swelling agent was contained in an amount of 33 parts by weight with respect to 100 parts by weight of the hydrogel of the prepared film. This was confirmed by the weight change before and after the moisture permeation.

실시예Example 2 ~  2 ~ 실시예Example 12 및  12 and 비교예Comparative Example 1 ~ 6 1 to 6

상기 실시예와 동일한 방법으로 시트리스 하이드로겔 필름을 제조하되, 하이드로겔 수지의 조성 및 조성비를 하기 표 1및 표 2와 같이 달리하여 시트리스 하이드로겔 필름을 제조하여 실시예 및 비교예를 실시하였으며, 건조된 후의 하이드로겔의 조성은 하기 표 3에 나타내었다.A sheetless hydrogel film was prepared in the same manner as in the above examples except that the composition and the composition ratio of the hydrogel resin were changed as shown in Tables 1 and 2 to prepare a sheetless hydrogel film, The composition of the hydrogel after drying is shown in Table 3 below.

실시예Example 고분자 수지Polymer resin 알긴산
나트륨Alginic acid
salt 보습제
(글리세린)Moisturizer
(glycerin) 가소제
(PEG)Plasticizer
(PEG) 증류수Distilled water 수용성 고분자Water-soluble polymer 천연고분자Natural polymer 1One (1)-1중량%(1) -1 wt% ①-1.4중량%
②-2중량%(1) - 1.4 wt%
②-2 wt% 2.1중량%2.1 wt% 5중량%5 wt% 5중량%5 wt% 83.5중량%83.5 wt% 22 (1)-3중량%(1) -3 wt% ①-3중량%
②-6중량%①-3 wt%
②-6 wt% 2.1중량%2.1 wt% 5중량%5 wt% 5중량%5 wt% 75.9중량%75.9 wt% 33 (1)-5중량%(1) -5 wt% ①-1.4중량%
②-2중량%(1) - 1.4 wt%
②-2 wt% 2.4중량%2.4 wt% 5중량%5 wt% 5중량%5 wt% 79.2중량%79.2 wt% 44 (1)-10중량%(1) -10 wt% ①-2.5중량%
②-5중량%①-2.5 wt%
②-5 wt% 2.1중량%2.1 wt% 5중량%5 wt% 10중량%10 wt% 65.4중량%65.4 wt% 55 (2)-1중량%(2) -1 wt% ①-1중량%
②-2중량%①-1 wt%
②-2 wt% 2중량%2 wt% 5중량%5 wt% 5중량%5 wt% 84중량%84 wt% 66 (2)-1중량%(2) -1 wt% ①-1.3중량%
②-4중량%①-1.3 wt%
②-4 wt% 1.7중량%1.7 wt% 1.3중량%1.3 wt% 3.3중량%3.3 wt% 87.4중량%87.4 wt% 77 (2)-5중량%(2) -5 wt% ①-0.5중량%
③-3중량%①-0.5 wt%
③-3 wt% 2중량%2 wt% 1중량%1 wt% 4중량%4 wt% 84.5중량%84.5 wt% 88 (2)-2.4중량%(2) -2.4 wt% ①-1.4중량%
②-2.7중량%(1) - 1.4 wt%
②-2.7 wt% 2.1중량%2.1 wt% 3중량%3 wt% 2중량%2 wt% 86.4중량%86.4 wt% 99 (2)-2중량%
(3)-5중량%(2) -2 wt%
(3) -5 wt% ②-6중량%
④-10중량%②-6 wt%
④ -10 wt% 2중량%2 wt% 5중량%5 wt% 5중량%5 wt% 65중량%65 wt% 1010 (3)-3중량%(3) -3 wt% ②-2중량%
④-15중량%②-2 wt%
④ -15 wt% 2.7중량%2.7 wt% 2.5중량%2.5 wt% 2.5중량%2.5 wt% 72.3중량%72.3 wt% 1111 (1)-2중량%
(3)-5중량%(1) -2 wt%
(3) -5 wt% ②-6중량%
⑤-2중량%②-6 wt%
⑤-2 wt% 2중량%2 wt% 5중량%5 wt% 5중량%5 wt% 73중량%73 wt% 1212 (1)-5중량%(1) -5 wt% ②-2.1중량%
⑤-3중량%(2) - 2.1 wt%
⑤-3 wt% 2.7중량%2.7 wt% 2중량%2 wt% 1중량%1 wt% 84.2중량%84.2 wt% (1):PVA (폴리비닐알코올), (2):PVP(폴리(N-비닐피롤리돈), (3):PEO(폴리에틸렌옥사이드)
①:잔탄검, ②:펙틴, ③:글로코만난, ④:구아검, ⑤:키토산(1) PVA (polyvinyl alcohol), (2) PVP (polyvinylpyrrolidone), (3) PEO (polyethylene oxide)
①: xanthan gum, ②: pectin, ③: glocomannan, ④: guar gum, ⑤: chitosan

비교예Comparative Example 고분자 수지Polymer resin 알긴산
나트륨Alginic acid
salt 보습제
(글리세린)Moisturizer
(glycerin) 가소제
(PEG)Plasticizer
(PEG) 증류수Distilled water 수용성 고분자Water-soluble polymer 천연고분자Natural polymer 1One (2)-1중량%(2) -1 wt% ①-7중량%①-7 wt% 2중량%2 wt% 10중량%10 wt% -- 80중량%80 wt% 22 (2)-3.1중량%(2) -3.1 wt% -- 3.6중량%3.6 wt% 15중량%15 wt% -- 78.3중량%78.3 wt% 33 (2)-1중량%
(3)-3중량%(2) -1 wt%
(3) -3 wt% ②-1중량%
④-10중량%②-1 wt%
④ -10 wt% 1.6중량%1.6 wt% -- 3중량%3 wt% 80.4중량%80.4 wt% 44 (2)-1중량%
(3)-3중량%(2) -1 wt%
(3) -3 wt% ②-1중량%
④-10중량%②-1 wt%
④ -10 wt% 1.6중량%1.6 wt% 3중량%3 wt% -- 80.4중량%80.4 wt% 55 (1)-3중량%
(3)-1중량%(1) -3 wt%
(3) -1 wt% ①-1중량%
⑤-2중량%①-1 wt%
⑤-2 wt% 2중량%2 wt% -- 3중량%3 wt% 88중량%88 wt% 66 (1)-3중량%
(3)-1중량%(1) -3 wt%
(3) -1 wt% ①-1중량%
⑤-2중량%①-1 wt%
⑤-2 wt% 2중량%2 wt% 3중량%3 wt% -- 88중량%88 wt% (1):PVA (폴리비닐알코올), (2):PVP(폴리(N-비닐피롤리돈), (3):PEO(폴리에틸렌옥사이드)
①:잔탄검, ②:펙틴, ③:글로코만난, ④:구아검, ⑤:키토산(1) PVA (polyvinyl alcohol), (2) PVP (polyvinylpyrrolidone), (3) PEO (polyethylene oxide)
①: xanthan gum, ②: pectin, ③: glocomannan, ④: guar gum, ⑤: chitosan

구분division 고분자 수지Polymer resin 알긴산
나트륨Alginic acid
salt 보습제
(글리세린)Moisturizer
(glycerin) 가소제
(PEG)Plasticizer
(PEG) 수용성 고분자Water-soluble polymer 천연고분자Natural polymer 실시예1Example 1 6.1중량%6.1 wt% 20.620.6 12.7중량%12.7 wt% 30.3중량%30.3 wt% 30.3중량%30.3 wt% 실시예 2Example 2 12.5중량%12.5 wt% 37.3중량%37.3 wt% 8.8중량%8.8 wt% 20.7중량%20.7 wt% 20.7중량%20.7 wt% 실시예 3Example 3 24중량%24 wt% 16.4중량%16.4 wt% 11.6중량%11.6 wt% 24중량%24 wt% 24중량%24 wt% 실시예 4Example 4 28.9중량%28.9 wt% 21.7중량%21.7 wt% 6.1중량%6.1 wt% 14.4중량%14.4 wt% 28.9중량%28.9 wt% 실시예 5Example 5 6.2중량%6.2 wt% 18.7중량%18.7 wt% 12.5중량%12.5 wt% 31.3중량%31.3 wt% 31.3중량%31.3 wt% 실시예 6Example 6 7.9중량%7.9 wt% 42.1중량%42.1 wt% 13.5중량%13.5 wt% 10.3중량%10.3 wt% 26.2중량%26.2 wt% 실시예 7Example 7 32.3중량%32.3 wt% 22.6중량%22.6 wt% 12.8중량%12.8 wt% 6.5중량%6.5 wt% 25.8중량%25.8 wt% 실시예 8Example 8 17.7중량%17.7 wt% 30.2중량%30.2 wt% 15.4중량%15.4 wt% 22중량%22 wt% 14.7중량%14.7 wt% 실시예 9Example 9 20중량%20 wt% 45.7중량%45.7 wt% 5.7중량%5.7 wt% 14.3중량%14.3 wt% 14.3중량%14.3 wt% 실시예 10Example 10 10.8중량%10.8 wt% 61.5중량%61.5 wt% 9.7중량%9.7 wt% 9중량%9 wt% 9중량%9 wt% 실시예 11Example 11 25.9중량%25.9 wt% 29.6중량%29.6 wt% 7.5중량%7.5 wt% 18.5중량%18.5 wt% 18.5중량%18.5 wt% 실시예 12Example 12 31.6중량%31.6 wt% 32.3중량%32.3 wt% 17.1중량%17.1 wt% 12.7중량%12.7 wt% 6.3중량%6.3 wt% 비교예 1Comparative Example 1 5중량%5 wt% 35중량%35 wt% 10중량%10 wt% 50중량%50 wt% -- 비교예 2Comparative Example 2 14.3중량%14.3 wt% -- 16.7중량%16.7 wt% 69중량%69 wt% -- 비교예 3Comparative Example 3 20.4중량%20.4 wt% 56.1중량%56.1 wt% 8.2중량%8.2 wt% -- 15.3중량%15.3 wt% 비교예 4Comparative Example 4 20.4중량%20.4 wt% 56.1중량%56.1 wt% 8.2중량%8.2 wt% 15.3중량%15.3 wt% -- 비교예 5Comparative Example 5 33.3중량%33.3 wt% 25중량%25 wt% 16.7중량%16.7 wt% 25중량%25 wt% -- 비교예 6Comparative Example 6 33.3중량%33.3 wt% 25중량%25 wt% 16.7중량%16.7 wt% -- 25중량%25 wt% (1):PVA (폴리비닐알코올), (2):PVP(폴리(N-비닐피롤리돈), (3):PEO(폴리에틸렌옥사이드)
①:잔탄검, ②:펙틴, ③:글로코만난, ④:구아검, ⑤:키토산(1) PVA (polyvinyl alcohol), (2) PVP (polyvinylpyrrolidone), (3) PEO (polyethylene oxide)
①: xanthan gum, ②: pectin, ③: glocomannan, ④: guar gum, ⑤: chitosan

실험예Experimental Example :  : 시트리스Seatless 하이드로겔Hydrogel 필름의  Film 인장강도The tensile strength 측정 실험 Measurement experiment

인장강도 측정은 상기 실시예 및 비교예에서 제조한 시트리스 하이드로겔 필름을 길이 30mm × 폭 12mm로 제조한 후, 이들 각각의 필름을 잡아당겨서 끊어지는 지점 측정하여 인장강도를 실험을 수행하였으며, 그 결과를 하기 표 4에 나타내었다. The tensile strength was measured by preparing the sheetless hydrogel films prepared in the above Examples and Comparative Examples at a length of 30 mm and a width of 12 mm and then measuring the tensile strength by pulling each of the films. The results are shown in Table 4 below.

그리고, 제조한 필름의 평균두께를 하기 표 4에 함께 나타내었다.The average thicknesses of the films thus produced are shown in Table 4 below.

구분division 최대하중에서의 인장강도
(Tensile strain at Maxium Load, %)Tensile strength at maximum load
(Tensile strain at Maxium Load,%) 최대하중에서의 인장응력
(Tensile stress at Maximum Load, kgf/cm2)Tensile stress at maximum load
(Tensile stress at Maximum Load, kgf / cm 2 ) 실시예1Example 1 158.85158.85 28.6928.69 실시예 2Example 2 162.36162.36 29.8529.85 실시예 3Example 3 168.22168.22 30.5430.54 실시예 4Example 4 183.03183.03 32.9832.98 실시예 5Example 5 159.36159.36 28.9228.92 실시예 6Example 6 157.98157.98 27.8827.88 실시예 7Example 7 160.37160.37 29.4129.41 실시예 8Example 8 160.05160.05 30.0130.01 실시예 9Example 9 170.21170.21 31.2331.23 실시예 10Example 10 168.72168.72 30.0830.08 실시예 11Example 11 175.36175.36 32.0332.03 실시예 12Example 12 181.54181.54 33.5733.57 비교예 1Comparative Example 1 133.52133.52 21.5021.50 비교예 2Comparative Example 2 138.64138.64 22.8222.82 비교예 3Comparative Example 3 140.28140.28 23.5523.55 비교예 4Comparative Example 4 142.39142.39 23.8323.83 비교예 5Comparative Example 5 141.25141.25 24.2024.20 비교예 6Comparative Example 6 139.41139.41 24.0524.05

상기 표 4의 실험결과를 살펴보면, 실시예 1 ~ 12의 본 발명의 시트리스 하이드로겔 필름은 하이드로겔 필름을 제품으로서 사용하기 위해 요구되는 최대하중에서의 적정 인장강도 및 인장응력 범위인 150% ~ 190% 및 25 kgf/cm2 ~ 35 kgf/cm2 을 만족하였으나, 비교예 1, 비교예 2, 비교예 4 및 비교예 5의 경우, 적정 인장강도 및/또는 인장응력을 만족하지 못하는 것을 확인할 수 있었다. 그리고, 비교예 3 및 비교예 5는 다른 비교예에 비해 인장강도, 인장응력은 좋았으나, 보습력을 유지하지 못해서 제품성이 매우 열악했다.
As shown in Table 4, the inventive pretreated hydrogel films of Examples 1 to 12 exhibited an optimum tensile strength and tensile stress range of 150% to 150% at the maximum load required for using the hydrogel film as a product, 190% and 25 kgf / cm < 2 > ~ 35 kgf / cm 2 However, it was confirmed that Comparative Examples 1, 2, 4 and 5 do not satisfy the appropriate tensile strength and / or tensile stress. In Comparative Examples 3 and 5, the tensile strength and the tensile stress were good compared with the other comparative examples, but the productability was poor due to failure to maintain the moisture resistance.

상기 실시예 및 실험예를 통하여 본 발명의 하이드로겔 필름은 우수한 인장강도, 보습력, 부착력 등의 우수한 물성을 갖는 바, 기재필름(또는 기재층, 기재시트)가 없더라도 그 형태 유지가 가능함을 확인할 수 있었다. 또한, 기재필름이 없는 바, 필름 자체의 유연성이 확보되고, 박리화가 가능하기 때문에 피부에 대한 부착력 등이 우수함을 알 수 있다. 또한, 기재필름 형성을 위한 제조공정이 없기 때문에 기존 하이드로겔 필름을 제조하는 공정에 비해 공정이 단순화되어 기존 보다 경제성이 우수한 하이드로겔 필름의 제조가 가능함을 확인할 수 있었다.
It can be seen from the above Examples and Experimental Examples that the hydrogel film of the present invention has excellent physical properties such as excellent tensile strength, moisturizing power and adhesion force, and it is possible to maintain its shape without the base film (substrate layer, substrate sheet) there was. Further, it can be seen that the base film is not provided, and the flexibility of the film itself is ensured, and peeling is possible, so that adhesion to skin is excellent. In addition, since there is no manufacturing process for forming a base film, it is possible to manufacture a hydrogel film which is more economical than the existing one, because the process is simplified as compared with the process of producing an existing hydrogel film.

10 : 하이드로겔 필름 10a, 10b : 홈부
10c : 돌출경계라인 100 : 상부마스크팩
200 : 하부마스크팩10: hydrogel film 10a, 10b:
10c: protruding boundary line 100: upper mask pack
200: Lower mask pack

Claims (19)

수용성 고분자 및 천연 고분자 중에서 선택된 1종 이상을 함유한 고분자 수지, 알긴산나트륨, 가소제 및 보습제를 포함하는 하이드로겔; 및
가교팽윤제;를 포함하며,
상기 가교팽윤제는 Ca2 +, Mg2 +, Cu2 +, Fe2 +, Al3 + 및 Fe3 + 중에서 선택된 1종 이상을 함유한 화합물을 포함하고 있는 것을 특징으로 하는 시트리스 하이드로겔 필름.A hydrogel including a polymer resin containing at least one selected from a water-soluble polymer and a natural polymer, sodium alginate, a plasticizer and a humectant; And
A cross-linking swelling agent,
The cross-linking the swelling agent is a Ca 2 +, Mg 2 +, Cu 2 +, Fe 2 +, Al 3 + , and the sheet-less, characterized in that includes a compound containing Fe 3 + at least one selected from hydrogel films . 제1항에 있어서, 상기 가교팽윤제는
가교팽윤제 전체 중량 중 상기 화합물 0.01 ~ 10 중량% 및 증류수를 90 ~ 99.99 중량% 포함하고 있는 것을 특징으로 하는 시트리스 하이드로겔 필름.
The composition of claim 1, wherein the crosslinking swelling agent is
Wherein the crosslinked swelling agent contains 0.01 to 10% by weight of the compound and 90 to 99.99% by weight of distilled water in the total weight of the crosslinked swelling agent.
제1항에 있어서, 상기 가교팽윤제는
상기 하이드로겔 100 중량부에 대하여 10 ~ 40 중량부로 포함하는 것을 특징으로 하는 시트리스 하이드로겔 필름.
The composition of claim 1, wherein the crosslinking swelling agent is
And 10 to 40 parts by weight based on 100 parts by weight of the hydrogel.
제1항에 있어서, 상기 수용성 고분자는
수용성 고분자 및 천연 고분자로는 폴리리신(polylysine), 카르복시메틸 키틴, 피브린(fibrin), 덱스트란(dextran), 폴리비닐알콜(PVA), 폴리비닐아세테이트/폴리비닐알콜(PVAc/PVA), 폴리(N-비닐 피롤리돈)(PVP), 알지네이트-g-(폴리에틸렌옥사이드-폴리프로필렌옥사이드-폴리에틸렌옥사이드)(alginate-g-(PEO-PPO-PEO)), 알지네이트-아크릴레이트(alginate-acrylate), 폴리에틸렌옥사이드(PEO) 및 폴리에틸렌옥사이드-폴리프로필렌옥사이드 공중합체(PEO-PPO, Pluronic series) 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 시트리스 하이드로겔 필름.
The method according to claim 1, wherein the water-soluble polymer
Examples of the water-soluble polymer and natural polymer include polylysine, carboxymethyl chitin, fibrin, dextran, polyvinyl alcohol (PVA), polyvinyl acetate / polyvinyl alcohol (PVAc / PVA) Alginate-g- (PEO-PPO-PEO), alginate-acrylate, polyvinylpyrrolidone (PVP), alginate-g- (polyethylene oxide-polypropylene oxide- Polyethylene oxide (PEO), and polyethylene oxide-polypropylene oxide copolymer (PEO-PPO, Pluronic series).
제1항에 있어서, 상기 천연 고분자는
펙틴(Pectin), 잔탄검(Xanthan gum), 젤라틴, 로커스트콩 검(LBG; Locust Bean Gum), 한천(Agar), 글루코만난(Glucomannan), 카라기난(Carrageenan), 젤란검(gellangum), 키토산, 콜라겐, 히알루론산, 아카시아검, 아라비아검 및 셀룰로오스 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 시트리스 하이드로겔 필름.
The method of claim 1, wherein the natural polymer comprises
Pectin, xanthan gum, gelatin, locust bean gum, agar, glucomannan, carrageenan, gellangum, chitosan, collagen, Hyaluronic acid, acacia gum, gum arabic, and cellulose.
제1항에 있어서, 상기 가소제로써는
헥실데실벤조에이트(Hexyldecyl Benzoate), 피피지-3벤질에테르미리스테이트(PPG-3 Benzyl Ether Myristate), 폴리에틸렌글리콜(Polyethyleneglycol), 피이지-8/에스엠디아이코폴리머(PEG-8/SMDI Copolymer), 트리카프릴릴/카프릴트리멜리테이트(Tricaprylyl/Capryl Trimellitate), 트리올레일포스페이트(Trioeyl Phosphate), 트리옥틸리멜리테이트(Trioctyl Trimellitate), 트리에틸헥실트리멜리테이트(Triethylhexyl Trimellitate), 트리에틸헥실시트레이트(Tricthylhexyl Citrate), 트리아세틴(Triacetin), 트리세틸포스페이트(Tricetyl Phosphate), 트리부틸시트레이트(Tributyl Citrate), 트리메틸하이드록시펜틸이소부티레이트(Trimethyl Hydroxypentyl Isobutyrate), 트리메틸펜탄디일디벤조에이트(Trimethylpentanediyl Dibenzoate), 캠퍼(Camphor), 아세틸트리에틸시트레이트(Acetyl Triethyl Citrate), 아세틸트리부틸시트레이트(Acetyl Tributyl Citrate), 슈크로오스아세테이트이소부티레이트(Sucrose Acetate Isobutyrate), 부틸옥틸벤조에이트(Butyloctyl Benzoate), 디펜타에리스리틸헥사 C5-9애씨애시드에스터(Dipentaerythrityl Hexa C5-9 Acid Esters), 디카프릴아디페이트(Dicapryl Adipate), 디이소프로필아디페이트(Diisopropyl Adipate), 디이소프로필세바케이트(Diisopropyl Sebacate), 디이소스테아릴아디페이트(Diisostearyl Adipate), 디이소부틸아디페이트(Diisobutyl Adipate), 디이소데실아디페이트(Diisodecyl Adipate), 디에틸헥실아디페이트(Diethylhexyl Adipate), 디에틸헥실세바케이트(Diethylhexyl Sebacate), 디에틸헥실석시네이트(Diethylhexyl Succinate), 디에틸프탈레이트(Diethyl Phthalate), 디에틸옥살레이트(Diethyl Oxalate), 디에틸세바케이트(Diethyl Sebacate), 디에틸렌글라이콜디이소노나노에이트(Diethylene Glycol Diisononanoate), 디부틸아디페이트(Dibutyl Adipate), 디메치콘피이지-8폴리아크릴레이트(Dimethicone PEG-8 Polyacrylate), 및 데실옥사졸리디논(Decyloxazolidinone) 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 시트리스 하이드로겔 필름.
The plasticizer according to claim 1, wherein the plasticizer
Hexyldecyl Benzoate, PPG-3 Benzyl Ether Myristate, Polyethyleneglycol, PEG-8 / SMDI Copolymer, Triethyleneglycol, Triallyl trimellitate, trioctyl trimellitate, triethylhexyl trimellitate, triethyl hexyl trimellitate, trioctyl trimellitate, trioctyl trimellitate, trioctyl trimellitate, trioctyl trimellitate, trioctyl trimellitate, trioctyl trimellitate, trioctyl trimellitate, But are not limited to, Tricthylhexyl Citrate, Triacetin, Tricetyl Phosphate, Tributyl Citrate, Trimethyl Hydroxypentyl Isobutyrate, Trimethylpentanediyl (Trimethylpentanediyl Dibenzoate, Camphor, Acetyl Triethyl Citrate, Acetyl Tributyl Citrate, But are not limited to, Sucrose Acetate Isobutyrate, Butyloctyl Benzoate, Dipentaerythrityl Hexa C5-9 Acid Esters, Dicapryl Adipate, Diisopropyl adipate, diisopropyl sebacate, diisostearyl adipate, diisobutyl adipate, diisodecyl adipate, diisopropyl adipate, diisopropyl adipate, Examples thereof include diethylhexyl adipate, diethylhexyl sebacate, diethylhexyl succinate, diethyl phthalate, diethyl oxalate, di Diethyl sebacate, diethylene glycol diisononanoate, dibutyl adipate, dimethicone di-8 Wherein the film comprises at least one selected from the group consisting of polyacrylate, dimethicone PEG-8 polyacrylate, and decyloxazolidinone.
제1항 있어서, 상기 보습제는
글리세린(glycerin), 솔비톨(sorbitol) 및 1,3-부틸렌글리콜(1,3-butylene glycol) 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 시트리스 하이드로겔 필름.
The composition according to claim 1, wherein the humectant
Characterized in that it comprises at least one selected from the group consisting of glycerin, sorbitol and 1,3-butylene glycol.
제1항에 있어서, 상기 하이드로겔은
고분자 수지 20 ~ 80 중량%, 알긴산나트륨 5 ~ 20 중량%, 가소제 2 ~ 35 중량%, 보습제 5 ~ 40 중량%를 포함하는 것을 특징으로 하는 시트리스 하이드로겔 필름.
The method of claim 1, wherein the hydrogel
Wherein the thermoplastic resin composition comprises 20 to 80% by weight of a polymer resin, 5 to 20% by weight of sodium alginate, 2 to 35% by weight of a plasticizer, and 5 to 40% by weight of a moisturizer.
제1항에 있어서, 상기 하이드로겔은
평균두께 20㎛ ~ 100㎛인 것을 특징으로 하는 시트리스 하이드로겔 필름.
The method of claim 1, wherein the hydrogel
Wherein the average thickness is 20 占 퐉 to 100 占 퐉.
제1항 내지 제8항 중에서 선택된 어느 한 항에 있어서,
활성성분 및 수분의 저장고가 형성될 수 있도록 피부와 맞닿는 면에 양음각의 홈부와 돌기부가 형성되되,
상기 홈부의 경계에는 건조필름의 표면보다 돌출된 돌출경계라인이 형성되어 있는 것을 특징으로 하는 시트리스 하이드로겔 필름.
9. The method according to any one of claims 1 to 8,
A groove portion and a protrusion portion having positive intaglio angles are formed on a surface contacting with the skin so that a reservoir of an active ingredient and moisture can be formed,
And a protruding boundary line protruding from the surface of the dry film is formed at the boundary of the groove portion.
제10항에 있어서, 상기 시트리스 하이드로겔 필름은
필름의 양면 모두에 상기 홈부와 돌기부가 형성되어 있는 것을 특징으로 하는 시트리스 하이드로겔 필름.
The method according to claim 10, wherein the sheet-like hydrogel film
Wherein the groove portion and the protrusion portion are formed on both sides of the film.
제10항 중 어느 한 항에 있어서, 상기 시트리스 하이드로겔 필름은 평균두께 25 ㎛ ~ 250㎛인 것을 특징으로 하는 시트리스 하이드로겔 필름.
11. The sheetless hydrogel film according to any one of claims 1 to 10, wherein the sheet-like hydrogel film has an average thickness of 25 mu m to 250 mu m.
하이드로겔용 수지를 제조하는 단계;
이형필름 표면에 상기 하이드로겔용 수지를 도포한 후, 건조시켜서 하이드로겔을 형성시키는 단계; 및
상기 이형필름 표면에 형성된 하이드로겔에 가교팽윤제를 침투시켜서 하이드로겔을 가교 및 팽윤시키는 단계;
를 포함하는 것을 특징으로 하는 시트리스 하이드로겔 필름의 제조방법.
Preparing a resin for hydrogel;
Applying the resin for hydrogel to the surface of the release film, and then drying the resin to form a hydrogel; And
Crosslinking and swelling the hydrogel by infiltrating the hydrogel formed on the surface of the release film with a crosslinking swelling agent;
Wherein the hydrolyzable functional group is a hydrolyzable group.
제13항에 있어서, 상기 하이드로겔용 수지는
수용성 고분자 및 천연 고분자 중에서 선택된 1종 이상을 함유한 고분자 수지, 알긴산나트륨, 가소제, 보습제 및 증류수를 포함하며,
상기 고분자 수지 1 ~ 40 중량%, 상기 알긴산나트륨 0.05 ~ 20 중량%, 상기 가소제 0.1 ~ 20 중량%, 상기 보습제 0.1 ~ 20 중량% 및 상기 증류수 20 ~ 98 중량%를 포함하는 것을 특징으로 하는 시트리스 하이드로겔 필름의 제조방법.
The method according to claim 13, wherein the hydrogel resin
A polymer resin containing at least one selected from a water-soluble polymer and a natural polymer, sodium alginate, a plasticizer, a humectant, and distilled water,
Wherein the plasticizer comprises 1 to 40 wt% of the polymer resin, 0.05 to 20 wt% of the sodium alginate, 0.1 to 20 wt% of the plasticizer, 0.1 to 20 wt% of the moisturizer, and 20 to 98 wt% of the distilled water. A method for producing a hydrogel film.
제13항에 있어서, 상기 건조는
50℃ ~ 90℃ 하에서, 2분 ~ 20 분간 수행하는 것을 특징으로 하는 시트리스 하이드로겔 필름의 제조방법.
14. The method of claim 13,
Wherein the step (b) is carried out at 50 ° C to 90 ° C for 2 minutes to 20 minutes.
제13항에 있어서, 상기 가교 및 팽윤시키는 단계는
가교팽윤제에 상기 이형필름 표면에 형성된 하이드로겔을 함침시키는 것을 특징으로 하는 시트리스 하이드로겔 필름의 제조방법.
14. The method of claim 13, wherein said crosslinking and swelling comprises
Wherein the cross-linked swelling agent is impregnated with a hydrogel formed on the surface of the release film.
제13항에 있어서, 상기 가교 및 팽윤시키는 단계는
상기 이형필름 표면에 형성된 하이드로겔의 표면에 가교팽윤제를 분무시키는 것을 특징으로 하는 시트리스 하이드로겔 필름의 제조방법.
14. The method of claim 13, wherein said crosslinking and swelling comprises
Wherein the cross-linked swelling agent is sprayed on the surface of the hydrogel formed on the surface of the release film.
제12항의 시트리스 하이드로겔 필름을 포함하는 화장품용 마스크팩.
A cosmetic mask pack comprising the sheetless hydrogel film of claim 12.
제12항의 시트리스 하이드로겔 필름을 포함하는 의료용 패취.

A medical patch comprising the sheetless hydrogel film of claim 12.

KR1020130022199A 2013-02-28 2013-02-28 Sheetless hydrogel film and Preparing method ofthere KR102078334B1 (en)