KR20140090291A - Method of manufacturing hard-coated polarizing plate - Google Patents
Method of manufacturing hard-coated polarizing plate Download PDFInfo
- Publication number
- KR20140090291A KR20140090291A KR1020120149161A KR20120149161A KR20140090291A KR 20140090291 A KR20140090291 A KR 20140090291A KR 1020120149161 A KR1020120149161 A KR 1020120149161A KR 20120149161 A KR20120149161 A KR 20120149161A KR 20140090291 A KR20140090291 A KR 20140090291A
- Authority
- KR
- South Korea
- Prior art keywords
- coating layer
- film
- hard
- cellulose
- resin film
- Prior art date
Abstract
Description
본 발명은 하드코팅된 편광판의 제조방법에 관한 것이다.
The present invention relates to a method for producing a hard coated polarizing plate.
액정표시장치(Liquid crystal display device, LCD)에는 편광자과 같은 고가의 광학필름이 적층되어 있는데 편광자는 액정셀과의 조립, 접합공정, 또는 운반, 유통 과정에서 손상되거나 오염될 수 있다.BACKGROUND ART An expensive optical film such as a polarizer is laminated on a liquid crystal display device (LCD). Polarizers may be damaged or contaminated during assembly, bonding process, transportation or distribution with a liquid crystal cell.
편광자의 미세한 손상과 결함은 액정표시장치의 불량을 야기시키므로, 이를 방지하기 위하여 편광자의 표면에 편광자 보호필름을 적층하여 사용된다. 또한 편광자 보호필름의 경도를 향상시키기 위해 보호필름의 일면 에 하드코팅층을 형성하여 사용한다.The minute damage and defects of the polarizer cause defects of the liquid crystal display device, and therefore, a polarizer protective film is laminated on the surface of the polarizer in order to prevent it. Further, a hard coat layer is formed on one side of the protective film to improve the hardness of the polarizer protective film.
하드코팅층이 형성된 편광판을 제조하기 위한 방법으로 한국등록특허 제1,036,735호는 편광자 보호필름의 일면에 하드코팅층 형성용 조성물을 도포하여 도포층을 형성시킨 후, 도포층을 광경화하는 방법이 개시되어 있다. 이는 하드코팅층을 형성시키기 위하여 당업계에서 통상적으로 이용하고 있는 방법으로 이렇게 제조된 편광자 보호필름은 검화처리 후 편광자에 접합하여 사용한다.Korean Patent No. 1,036,735 discloses a method for producing a polarizing plate on which a hard coating layer is formed by coating a composition for forming a hard coating layer on one surface of a polarizer protective film to form a coating layer and then curing the coating layer . This is a method commonly used in the art for forming a hard coating layer. The polarizer protective film thus prepared is bonded to a polarizer after saponification treatment.
한편, 상기 통상의 제조방법을 이용할 경우 하드코팅 필름의 끝부분이 말아오르는 컬(curl) 현상이 일어난다. 특히 경도 향상을 위하여 하드코팅층의 두께를 두껍게 형성할 경우 컬 현상은 심화된다. 이는 경화단계에서 경화 수축 및 열습 수축이 증가하기 때문인데, 컬이 발생하면 보호필름과 편광자와 접합이 어려워지고 심한 경우 크랙이 발생하는 문제점이 있다.On the other hand, when the above-mentioned conventional manufacturing method is used, a curl phenomenon occurs in which the end portion of the hard coating film is curled. In particular, when the hard coating layer is formed thick to improve the hardness, the curling phenomenon is intensified. This is because the hardening shrinkage and the heat and moisture shrinkage increase in the curing step. When curling occurs, it is difficult to bond with the protective film and the polarizer, and cracks are generated in severe cases.
또한 편광자와의 접착력을 향상시키기 위하여 보호필름 표면에 검화처리를 하는 과정에서 하드코팅층 표면까지 검화되는 문제점이 있다. 이러한 하드코팅층의 손상은 하드코팅층의 접촉각을 떨어뜨리고, 내찰상성을 떨어뜨려 편광판의 품질을 저하시키는 요인이 된다.
Further, there is a problem that the surface of the hard coat layer is saponified in the process of saponifying the surface of the protective film in order to improve the adhesion with the polarizer. Such damage to the hard coating layer lowers the contact angle of the hard coating layer and deteriorates the scratch resistance, thereby deteriorating the quality of the polarizing plate.
본 발명의 목적은 하드코팅층이 검화 처리 용액에 의해 손상되지 않아 하드코팅층의 내찰상성 및 경도가 우수하고, 편광자와 편광자 보호필름과의 접착력이 향상된 하드코팅된 편광판의 제조방법을 제공하는 것이다.
An object of the present invention is to provide a method for producing a hard-coated polarizing plate in which the hard coat layer is not damaged by the saponification treatment solution, the hard coat layer is excellent in scratch resistance and hardness, and the adhesion between the polarizer and the polarizer protective film is improved.
본 발명의 목적을 달성하기 위하여, (a) 셀룰로오스계 수지 필름의 일면에, 이형필름을 접합하는 단계; (b) 상기 이형필름이 접합된 셀룰로오스계 수지 필름을 검화하는 단계; (c) 상기 셀룰로오스계 수지 필름으로부터 이형필름을 박리하는 단계; (d) 상기 검화된 셀룰로오스계 수지 필름 표면에 편광자를 접합하는 단계; (e) 상기 셀룰로오스계 수지 필름의 이형필름 박리면에 하드코팅층 형성용 조성물을 도포하여 도포층을 형성하는 단계; 및 (f) 상기 도포층을 경화시켜 하드코팅층을 형성하는 단계를 포함하는 것을 특징으로 하는 하드코팅된 편광판의 제조방법을 제공한다.In order to achieve the object of the present invention, there is provided a method for producing a cellulose resin film, comprising the steps of: (a) bonding a release film to one surface of a cellulose resin film; (b) saponifying the cellulosic resin film to which the release film is bonded; (c) peeling the release film from the cellulose-based resin film; (d) bonding a polarizer to the surface of the saponified cellulose based resin film; (e) applying a composition for forming a hard coating layer on the releasing film peeling surface of the cellulose resin film to form a coating layer; And (f) curing the coating layer to form a hard coating layer.
상기 (c)단계와 (d)단계의 순서를 바꾸어, (d)단계 후에 (c)단계를 실시할 수 있다.The steps (c) and (d) may be reversed, and the step (c) may be performed after the step (d).
상기 하드코팅층 형성용 조성물은 광경화성 투광성 수지 및 개시제를 포함할 수 있고, 용제, 항산화제, UV 흡수제, 광안정제, 레벨링제, 계면활성제, 방오제로 이루어진 군으로부터 선택되는 적어도 1종을 추가로 포함할 수 있다.The composition for forming a hard coat layer may further include at least one selected from the group consisting of a solvent, an antioxidant, a UV absorber, a light stabilizer, a leveling agent, a surfactant and an antifouling agent, can do.
상기 하드코팅층 형성용 조성물은 체적 수축율이 5~40%인 것일 수 있다. The composition for forming a hard coat layer may have a volume shrinkage of 5 to 40%.
상기 도포층의 두께는 10~30㎛인 것일 수 있다.The thickness of the coating layer may be 10 to 30 占 퐉.
상기 하드코팅된 편광판의 표면경도는 4H 이상인 것일 수 있다.
The surface hardness of the hard-coated polarizing plate may be 4H or more.
본 발명에 따른 방현성 하드코팅 필름의 제조방법은 보호필름 상에 하드코팅층 형성시 보호필름에 컬이 발생하지 않아 편광자와의 접합이 용이하고 접합력이 뛰어나며, 편광자와 접합을 위해 편광자 보호필름 표면을 검화처리할 때 하드코팅층 표면에 손상이 없어 내찰상성 및 표면 경도가 우수한 하드코팅된 편광판을 제공한다는 장점이 있다.
The method for producing a hard-coating film of the present invention is characterized in that a curtain is not formed on a protective film on a protective film to form a hard coat layer, so that it is easy to bond with a polarizer and has excellent bonding strength. There is no damage to the surface of the hard coating layer at the time of saponification treatment, thereby providing a hard coated polarizer excellent in scratch resistance and surface hardness.
본 발명의 하드코팅된 편광판의 제조방법은 (a) 셀룰로오스계 수지 필름의 일면에, 이형필름을 접합하는 단계; (b) 상기 이형필름이 접합된 셀룰로오스계 수지 필름을 검화하는 단계; (c) 상기 셀룰로오스계 수지 필름으로부터 이형필름을 박리하는 단계; (d) 상기 검화된 셀룰로오스계 수지 필름 표면에 편광자를 접합하는 단계; (e) 상기 셀룰로오스계 수지 필름의 이형필름 박리면에 하드코팅층 형성용 조성물을 도포하여 도포층을 형성하는 단계; 및 (f) 상기 도포층을 경화시켜 하드코팅층을 형성하는 단계를 포함한다.
A method of producing a hard coated polarizer of the present invention comprises the steps of: (a) bonding a release film to one side of a cellulose resin film; (b) saponifying the cellulosic resin film to which the release film is bonded; (c) peeling the release film from the cellulose-based resin film; (d) bonding a polarizer to the surface of the saponified cellulose based resin film; (e) applying a composition for forming a hard coating layer on the releasing film peeling surface of the cellulose resin film to form a coating layer; And (f) curing the coating layer to form a hard coat layer.
이하, 본 발명을 더욱 상세하게 설명하나, 이는 본 발명의 설명을 위한 것이며, 본 발명의 범위를 제한하는 것이 아니다.
Hereinafter, the present invention will be described in more detail, but it is for the purpose of illustrating the present invention and is not intended to limit the scope of the present invention.
우선 (a) 셀룰로오스계 수지 필름의 일면에, 이형필름을 접합한다.
First, a releasing film is bonded to one surface of the cellulose-based resin film (a).
셀룰로오스계 수지는 셀룰로오스와 지방산 에스테르로 이루어진 것으로서, 구체적인 예로는 셀룰로오스트리아세테이트 수지, 셀룰로오스디아세테이트 수지, 셀룰로오스트리프로피오네이트 수지, 셀룰로오스디프로피오네이트 수지 등을 들 수 있으며, 이들 중에서도 투명성, 접합성이 뛰어난 셀룰로오스트리아세테이트(트리아세틸 셀룰로오스) 수지가 바람직하다. Examples of the cellulose-based resin include cellulose and fatty acid esters. Specific examples thereof include cellulose triacetate resin, cellulose diacetate resin, cellulose tripropionate resin and cellulose dipropionate resin. Among them, transparency and bonding property Excellent cellulose triacetate (triacetylcellulose) resin is preferable.
셀룰로오스계 수지 필름의 두께는 30~100㎛일 수 있고, 보다 바람직하게는 40~80㎛일 수 있다.
The thickness of the cellulose-based resin film may be 30 to 100 탆, and more preferably 40 to 80 탆.
이형필름은 당 업계에서 통상적으로 사용되는 필름이라면 그 종류가 특별히 제한되지 않는다. The type of the release film is not particularly limited as long as it is a film ordinarily used in the art.
구체적인 예로는, 폴리에틸렌, 폴리프로필렌, 폴리-1-부텐, 폴리-4-메틸-1-펜텐, 에틸렌-프로필렌 공중합체, 에틸렌-1-부텐 공중합체, 에틸렌-아세트산비닐 공중합체, 에틸렌-에틸아크릴레이트 공중합체, 에틸렌-비닐알코올 공중합체 등의 폴리올레핀계 필름; 폴리에틸렌테레프탈레이트, 폴리에틸렌나프탈레이트, 폴리부틸렌테레프탈레이트 등의 폴리에스테르계 필름; 폴리아크릴레이트계 필름; 폴리스티렌계 필름; 나일론6, 부분 방향족 폴리아미드 등의 폴리아미드계 필름; 폴리염화비닐 필름; 폴리염화비닐리덴 필름; 또는 폴리카보네이트 필름 등을 사용할 수 있다. 또한, 이들은 실리콘계, 불소계, 실리카 분말 등과 같은 이형제로 적절히 이형처리하여 사용할 수 있다.
Specific examples thereof include polyethylene, polypropylene, poly-1-butene, poly-4-methyl-1-pentene, ethylene-propylene copolymer, ethylene-1-butene copolymer, ethylene- A polyolefin-based film such as an ethylene-vinyl alcohol copolymer; Polyester films such as polyethylene terephthalate, polyethylene naphthalate and polybutylene terephthalate; Polyacrylate-based films; A polystyrene type film; Polyamide-based films such as nylon 6 and partially aromatic polyamide; Polyvinyl chloride films; Polyvinylidene chloride films; Or a polycarbonate film may be used. They may be suitably subjected to mold-releasing treatment using a mold-releasing agent such as a silicone type, fluorine type, silica powder or the like.
다음 (b) 이형필름이 접합된 셀룰로오스계 수지 필름을 검화한다.Next, the cellulose-based resin film to which the release film (b) is bonded is subjected to saponification.
검화는 셀룰로오스계 수지 필름과 편광자와의 접착성을 높이기 위한 것으로, 본 발명은 상기와 같이 셀룰로오스계 수지 필름의 일면에 이형필름이 접합된 상태에서 검화가 진행되기 때문에 셀룰로오스계 수지 필름의 다른 일면만 검화시킬 수 있다. 또한 검화시 셀룰로오스계 필름에 하드코팅층이 형성되어 있지 않아 종래의 방법과는 달리 하드코팅층이 검화 처리 용액에 의해 손상될 우려가 없다.
The saponification is intended to enhance the adhesion between the cellulose-based resin film and the polarizer. In the present invention, since the saponification proceeds in a state where the release film is bonded to one surface of the cellulose-based resin film as described above, only the other surface of the cellulose- . Further, since the hard coat layer is not formed on the cellulose-based film during the saponification, unlike the conventional method, there is no fear that the hard coat layer is damaged by the saponification treatment solution.
다음, (c) 상기 셀룰로오스계 수지 필름으로부터 이형필름을 박리한다.Next, (c) the releasing film is peeled from the cellulose resin film.
이형필름은 검화단계에서 셀룰로오스계 수지 필름의 일면을 보호하기 위하여 사용된 것이므로 검화 단계 후 이형필름을 박리하여 제거한다. 이형필름을 부착하는 목적을 고려할 때 (c)단계와 (d)단계의 순서를 바꾸어, (d)단계 후에 (c)단계를 실시하여도 무방하다.
Since the release film is used for protecting one side of the cellulose resin film during the saponification step, the release film is peeled off after the saponification step. Considering the object of attaching the release film, steps (c) and (d) may be changed, and step (d) may be performed after step (c).
다음, (d) 상기 검화된 셀룰로오스계 수지 필름 표면에 편광자를 접합한다. Next, (d) a polarizer is bonded to the surface of the saponified cellulose based resin film.
종래 셀룰로오스계 수지 필름 표면에 하드코팅층을 형성시킨 후 편광자를 접합한 경우 하드코팅층 형성용 조성물의 경화시 경화수축으로 인하여 필름에 컬이 발생하는 문제가 있어 접합에 용이하지 않았다. 그러나 본 발명의 경우 하드코팅층 형성 이전에 편광자와 셀룰로오스계 수지 필름을 접착하기 때문에 접착에 어려움이 없다.
When a hard coat layer is formed on the surface of a conventional cellulose resin film and then a polarizer is bonded, curling of the film occurs due to curing shrinkage of the composition for forming a hard coat layer, which is not easy for bonding. However, in the case of the present invention, since the polarizer and the cellulose resin film are bonded before the hard coating layer is formed, there is no difficulty in adhesion.
다음, (e) 상기 셀룰로오스계 수지 필름의 이형필름 박리면에 하드코팅층 형성용 조성물을 도포하여 도포층을 형성한다. Next, (e) a composition for forming a hard coating layer is applied to the releasing film peeling surface of the cellulose resin film to form a coating layer.
상기 하드코팅층 형성용 조성물은 광경화성 투광성 수지 및 개시제를 포함할 수 있고, 용제, 항산화제, UV 흡수제, 광안정제, 레벨링제, 계면활성제, 방오제로 이루어진 군으로부터 선택되는 적어도 1종을 추가로 포함할 수 있다.The composition for forming a hard coat layer may further include at least one selected from the group consisting of a solvent, an antioxidant, a UV absorber, a light stabilizer, a leveling agent, a surfactant and an antifouling agent, can do.
상기 투광성 수지는 광경화형 (메타)아크릴레이트 올리고머, 모노머를 포함할 수 있고, 각각 단독으로 또는 둘 이상을 조합하여 사용할 수 있다.The light transmitting resin may include a photocurable (meth) acrylate oligomer and a monomer, and each may be used alone or in combination of two or more thereof.
광경화형 (메타)아크릴레이트 올리고머는, 예를 들어 에폭시 (메타)아크릴레이트, 우레탄 (메타)아크릴레이트 등을 사용할 수 있으며, 그 중에서도 우레탄 (메타)아크릴레이트를 사용하는 것이 보다 바람직하다. As the photocurable (meth) acrylate oligomer, for example, epoxy (meth) acrylate, urethane (meth) acrylate and the like can be used, and among them, urethane (meth) acrylate is more preferably used.
우레탄 (메타)아크릴레이트는 분자내에 히드록시기를 갖는 다관능 (메타)아크릴레이트와 이소시아네이트기를 갖는 화합물을 촉매 존재 하에서 제조할 수 있다. The urethane (meth) acrylate can be produced in the presence of a catalyst having a polyfunctional (meth) acrylate having a hydroxyl group in the molecule and an isocyanate group.
분자내 히드록시기를 갖는 (메타)아크릴레이트로는 2-히드록시에틸(메타)아크릴레이트, 2-히드록시이소프로필(메타)아크릴레이트, 4-히드록시부틸(메타)아크릴레이트, 카프로락톤 개환 히드록시아크릴레이트, 펜타에리스리톨트리/테트라(메타)아크릴레이트 혼합물 및 디펜타에리스리톨펜타/헥사(메타)아크릴레이트 혼합물로 이루어진 군으로부터 선택되는 1종 이상을 사용할 수 있다. Examples of the (meth) acrylate having a hydroxyl group in the molecule include 2-hydroxyethyl (meth) acrylate, 2-hydroxyisopropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, caprolactone ring- A mixture of pentaerythritol tetra (meth) acrylate, and a mixture of dipentaerythritol penta / hexa (meth) acrylate can be used.
분자내에 이소시아네이트기를 갖는 화합물로는 1,4-디이소시아나토부탄, 1,6-디이소시아나토헥산, 1,8-디이소시아나토옥탄, 1,12-디이소시아나토도데칸, 1,5-디이소시아나토-2-메틸펜탄, 트리메틸-1,6-디이소시아나토헥산, 1,3-비스(이소시아나토메틸)시클로헥산, 트랜스-1,4-시클로헥센디이소시아네이트, 4,4'-메틸렌비스(시클로헥실이소시아네이트), 이소포론디이소시아네이트, 톨루엔-2,4-디이소시아네이트, 톨루엔-2,6-디이소시아네이트, 자일렌-1,4-디이소시아네이트, 테트라메틸자일렌-1,3-디이소시아네이트, 1-클로로메틸-2,4-디이소시아네이트, 4,4'-메틸렌비스(2,6-디메틸페닐이소시아네이트), 4,4'-옥시비스(페닐이소시아네이트), 헥사메틸렌디이소시아네이트로부터 유도되는 3관능 이소시아네이트, 및 트리메탄프로판올어덕트톨루엔디이소시아네이트로 이루어진 군으로부터 선택되는 1종 이상을 사용할 수 있다.Examples of the compound having an isocyanate group in the molecule include 1,4-diisocyanatobutane, 1,6-diisocyanatohexane, 1,8-diisocyanatooctane, 1,12-diisocyanatododecane, (Isocyanatomethyl) cyclohexane, trans-1,4-cyclohexene diisocyanate, 4,4'-methylene (isocyanatoethyl) isocyanate, Bis (cyclohexyl isocyanate), isophorone diisocyanate, toluene-2,4-diisocyanate, toluene-2,6-diisocyanate, xylene-1,4-diisocyanate, tetramethyl xylene- (Isocyanate) derived from isocyanate, 1-chloromethyl-2,4-diisocyanate, 4,4'-methylenebis (2,6-dimethylphenylisocyanate), 4,4'- Trifunctional isocyanate, and trimethylene propanol adduct. Toluene diisocyanate Eojin it can be used at least one member selected from the group.
모노머는 통상적으로 사용하는 것을 사용할 수 있고, 광경화형 관능기로 예를 들어 (메타)아크릴로일기, 비닐기, 스티릴기, 알릴기 등의 불포화기를 갖는 것을 사용할 수 있으며, 그 중에서도 (메타)아크릴로일기를 사용하는 것이 보다 바람직하다. As the monomer, conventionally used ones can be used. As the photo-curable functional group, for example, those having an unsaturated group such as (meth) acryloyl group, vinyl group, styryl group and allyl group can be used. Among them, It is more preferable to use a diary.
(메타)아크릴로일기를 갖는 모노머는 네오펜틸글리콜아크릴레이트, 1,6-헥산디올(메타)아크릴레이트, 프로필렌글리콜디(메타)아크릴레이트, 트리에틸렌글리콜디(메타)아크릴레이트, 디프로필렌글리콜디(메타)아크릴레이트, 폴리에틸렌글리콜디(메타)아크릴레이트, 폴리프로필렌글리콜디(메타)아크릴레이트, 트리메틸올프로판트리(메타)아크릴레이트, 트리메틸올에탄트리(메타)아크릴레이트, 1,2,4-시클로헥산테트라(메타)아크릴레이트, 펜타글리세롤트리(메타)아크릴레이트, 펜타에리스리톨테트라(메타)아크릴레이트, 펜타에리스리톨트리(메타)아크릴레이트, 디펜타에리스리톨트리(메타)아크릴레이트, 디펜타에리스리톨펜타(메타)아크릴레이트, 디펜타에리스리톨테트라(메타)아크릴레이트, 디펜타에리스리톨헥사(메타)아크릴레이트, 트리펜타에리스리톨트리(메타)아크릴레이트, 트리펜타에리스리톨헥사트리(메타)아크릴레이트, 비스(2-하이드록시에틸)이소시아누레이트디(메타)아크릴레이트, 하이드록시에틸(메타)아크릴레이트, 하이드록시프로필(메타)아크릴레이트, 하이드록시부틸(메타)아크릴레이트, 이소옥틸(메타)아크릴레이트, 이소-덱실(메타)아크릴레이트, 스테아릴(메타)아크릴레이트, 테트라하이드로퍼푸릴(메타)아크릴레이트, 페녹시에틸(메타)아크릴레이트,이소보네올(메타)아크릴레이트로 이루어진 군으로부터 선택된 1종 이상을 사용할 수 있다.The monomer having a (meth) acryloyl group may be at least one monomer selected from the group consisting of neopentyl glycol acrylate, 1,6-hexanediol (meth) acrylate, propylene glycol di (meth) acrylate, triethylene glycol di Acrylate, trimethylolpropane tri (meth) acrylate, trimethylol ethane tri (meth) acrylate, 1, 2, 3 or 4 di (meth) acrylate, polyethylene glycol di (meth) acrylate, polypropylene glycol di (Meth) acrylate, dipentaerythritol tri (meth) acrylate, dipentaerythritol tri (meth) acrylate, dipentaerythritol tetra (meth) acrylate, pentaerythritol tri (Meth) acrylate, dipentaerythritol tetra (meth) acrylate, dipentaerythritol hexa (metha) acrylate, tripentaerythritol tetra (Meth) acrylate, hydroxypropyl (meth) acrylate, hydroxypropyl (meth) acrylate, isopentyl (meth) acrylate, (Meth) acrylate, stearyl (meth) acrylate, tetrahydroperfuryl (meth) acrylate, isobutyl (meth) acrylate, At least one selected from the group consisting of phenoxyethyl (meth) acrylate and isobonol (meth) acrylate can be used.
상기 개시제는 당해 기술분야에서 사용되는 것을 제한 없이 사용할 수 있고, 구체적으로는 2-메틸-1-[4-(메틸티오)페닐]2-모폴린프로판온-1, 디페닐케톤 벤질디메틸케탈, 2-히드록시-2-메틸-1-페닐-1-온, 4-히드록시시클로페닐케톤, 디메톡시-2-페닐아테토페논, 안트라퀴논, 플루오렌, 트리페닐아민, 카바졸, 3-메틸아세토페논, 4-크놀로아세토페논, 4,4-디메톡시아세토페논, 4,4-디아미노벤조페논, 1-히드록시시클로헥실페닐케톤 및 벤조페논으로 이루어진 군으로부터 선택된 적어도 하나를 사용할 수 있다 The initiator may be any of those used in the art without limitation. Specific examples thereof include 2-methyl-1- [4- (methylthio) phenyl] 2-morpholinepropanone-1, diphenylketone benzyldimethylketal, 2-methyl-1-phenyl-1-on, 4-hydroxycyclophenyl ketone, dimethoxy-2-phenyl aetetophenone, anthraquinone, fluorene, triphenylamine, carbazole, 3- At least one selected from the group consisting of methyl acetophenone, 4-quinolone acetophenone, 4,4-dimethoxyacetophenone, 4,4-diaminobenzophenone, 1-hydroxycyclohexyl phenyl ketone and benzophenone can be used have
개시제는 하드코팅층 형성용 조성물 전체 100중량부에 대하여 0.1 내지 10중량부인 것이 바람직하다. 개시제의 함량이 0.1중량부 미만인 경우 경화 속도가 늦어질 수 있고, 10중량부를 초과 할 경우 방현성 하드코팅층의 과경화로 인하여 크랙이 발생할 수 있다. The initiator is preferably 0.1 to 10 parts by weight per 100 parts by weight of the total composition for forming a hard coat layer. If the content of the initiator is less than 0.1 part by weight, the curing rate may be lowered. If the content of the initiator exceeds 10 parts by weight, cracking may occur due to overcuring of the antireflective hard coat layer.
용제는 본 기술분야에서 코팅층 형성용 조성물의 용제로 알려진 것이라면 제한되지 않고 사용할 수 있고, 구체적으로 알코올계(메탄올, 에탄올, 이소프로판올, 부탄올, 메틸셀루소브, 에틸솔루소브 등), 케톤계(메틸에틸케톤, 메틸부틸케톤, 메틸이소부틸케톤, 디에틸케톤, 디프로필케톤, 시클로헥사논 등), 헥산계(헥산, 헵탄, 옥탄 등), 벤젠계(벤젠, 톨루엔, 자일렌 등)로 이루어진 군으로부터 선택된 적어도 하나를 사용할 수 있다.The solvent is not limited as long as it is known in the art as a solvent for the coating layer forming composition. Specific examples of the solvent include alcohols such as methanol, ethanol, isopropanol, butanol, methylcellulose, ethylsorbox, (Hexane, heptane, octane, etc.), benzene series (benzene, toluene, xylene, etc.) such as methylene chloride, methyl ethyl ketone, methyl butyl ketone, methyl isobutyl ketone, diethyl ketone, dipropyl ketone, cyclohexanone, Lt; / RTI > may be used.
용제는 방현성 하드코팅층 형성용 조성물 전체 100중량부에 대하여 10 내지 95중량부 포함될 수 있다. 상기 용제가 상기 기준으로 10중량부 미만이면 점도가 높아 작업성이 떨어질 수 있고, 95중량부를 초과할 경우에는 건조 과정에서 시간이 많이 소요되어 경제성이 떨어질 수 있다.The solvent may be contained in an amount of 10 to 95 parts by weight based on 100 parts by weight of the total amount of the composition for forming the antiglare hard coat layer. If the amount of the solvent is less than 10 parts by weight, the viscosity may be high and the workability may be deteriorated. If the amount of the solvent is more than 95 parts by weight, the drying process may take a long time and the cost may be reduced.
상기 하드코팅층 형성용 조성물의 도포 방법은 특별히 제한되지 않으며, 다이코터, 에어 나이프, 리버스 롤, 블레이드, 캐스팅 및 그라비아 등을 이용할 수 있다.The coating method of the composition for forming a hard coat layer is not particularly limited, and a die coater, an air knife, a reverse roll, a blade, a casting and a gravure can be used.
도포 후 필요에 따라 건조 단계를 수행할 수 있는데, 건조 방법으로는 자연 건조, 에어 건조, 가열 건조 등의 방법을 이용할 수 있으며, 일반적으로 가열 건조가 바람직하게 이용된다. 예를 들면, 20 내지 80?에서 1 내지 10분 동안 가열 건조될 수 있다. After the application, the drying step may be carried out if necessary. Examples of the drying method include natural drying, air drying, heat drying and the like. In general, heat drying is preferably used. For example, from 20 to 80 占 폚 for 1 to 10 minutes.
도포층의 두께는 통상 500㎛ 이하일 수 있으며, 바람직하게는 1~300㎛, 보다 바람직하게는 10~30㎛일 수 있다. 도포층의 두께가 10㎛ 미만일 경우 경도가 충분히 높지 않을 수 있고, 30㎛ 초과인 경우 하드코팅층 형성용 조성물의 도포층이 경화되면서 컬이 발생할 수 있다. 이러한 컬 발생은 편광자와 이미 접착한 후에 발생하기 때문에 편광자와의 접착에 문제가 되지는 않으나 편광판 품질을 떨어뜨리는 요인이 될 수 있다.
The thickness of the coating layer may be usually 500 μm or less, preferably 1 to 300 μm, and more preferably 10 to 30 μm. When the thickness of the coating layer is less than 10 mu m, the hardness may not be sufficiently high. When the thickness is more than 30 mu m, curl may occur while the coating layer of the composition for forming a hard coating layer is cured. This curling occurs after bonding with the polarizer, so that it does not cause a problem in adhesion with the polarizer, but it may cause a deterioration in the quality of the polarizer.
본 발명의 하드코팅된 편광판의 구조는 특별히 제한되지 않으며, 편광자의 한 면에는 상기 하드코팅된 보호필름이 적층되고, 다른 한 면에는 필요한 광학특성을 만족시킬 수 있는 여러 종류의 광학층이 적층될 수 있다.The structure of the hard-coated polarizing plate of the present invention is not particularly limited, and the hard-coated protective film may be laminated on one side of the polarizer, and various kinds of optical layers may be laminated on the other side .
예를 들어, 편광자의 한 면에는 상기 보호필름이 적층되고, 편광자의 다른 한 면 또는 통상의 보호필름 상에 하드코팅층 이외에 반사방지층, 점착방지층, 확산방지층, 눈부심방지층 등의 표면처리층이 적층될 수 있다. 또한, 편광자의 적어도 한 면 또는 보호필름 상에 시야각을 보상하는 배향액정층 또는 또 다른 기능성 막이 적층될 수 있다. 또한 상황에 따라 편광자의 양 면에 모두 적층될 수 있다.
For example, the protective film is laminated on one side of a polarizer, and a surface treatment layer such as an antireflection layer, an anti-adhesion layer, a diffusion prevention layer, and an anti-glare layer is laminated on the other surface of the polarizer or on a normal protective film in addition to the hard coating layer . Further, an alignment liquid crystal layer or another functional film for compensating the viewing angle on at least one surface of the polarizer or on the protective film may be laminated. It can also be laminated on both sides of the polarizer depending on the situation.
이하, 본 발명을 하기의 실시예 및 비교예에 의하여 보다 구체적으로 설명될 것이며, 하기의 실시예는 본 발명의 구체적인 일부 예시에 불과하고, 본 발명의 보호범위를 한정하거나 제한하고자 하는 것은 아니다.
Hereinafter, the present invention will be described in more detail with reference to the following examples and comparative examples, but the following examples are only specific examples of the present invention and are not intended to limit or limit the scope of protection of the present invention.
실시예Example 1 One
(a) 두께가 80㎛인 트리아세틸 셀룰로오스(TAC) 필름의 일면에 실리콘 이형필름(린텍,상품명 PET3811)을 접합시키고, (b) 이형필름이 적층된 트리아세틸 셀룰로오스(TAC) 필름을 5N농도의 KOH수용액에 30초간 침지하여 이형필름이 접합되지 않은 면을 검화 실시 후 80도 오븐에서 2분간 건조하여 수분을 제거하였다. (c) 이형필름을 트리아세틸 셀룰로오스(TAC) 필름으로부터 박리한 후 (d) 검화된 트리아세틸셀룰로오스 필름의 다른 일면에 변성 폴리비닐알코올계 접착제를 사용하여 PVA 편광자를 접합하였다. (a) A triacetyl cellulose (TAC) film laminated with a release film was laminated on one side of a triacetyl cellulose (TAC) film having a thickness of 80 탆 and a silicone release film (LINTEC, KOH aqueous solution for 30 seconds to conduct the saponification of the unbonded surface of the release film, followed by drying in an oven at 80 DEG C for 2 minutes to remove moisture. (c) The release film was peeled off from the triacetyl cellulose (TAC) film, and (d) the PVA polarizer was bonded to the other surface of the saponified triacetyl cellulose film using a modified polyvinyl alcohol adhesive.
(e) 우레탄아크릴레이트(미원상사, MU9500 제품) 10중량부, 펜타에리스리톨트리아크릴레이트(미원상사, M340 제품) 10중량부, 나노 실리카 졸(촉매화성사, V8802(12nm, 고형분 40%)) 50중량부, 메틸에틸케톤(대정화금사), 20중량부, 프로필렌글리콜모노메틸에테르(대정화금사) 7중량부, 광개시제(시바사, I-184 제품) 2.5중량부, 레벨링제(BYK케미사, BYK3570 제품) 0.5중량부를 포함하는 하드코팅층 형성용 조성물을 PP재질의 필터를 이용하여 여과한 후, 상기 트리아세틸 셀룰로오스(TAC) 필름의 다른 일면에 10㎛ 두께로 도포하고 이를 70℃에서 2분간 건조하였다. 10 parts by weight of urethane acrylate (product of MIWON Corporation, product of MU9500), 10 parts by weight of pentaerythritol triacrylate (product of MIWON Corporation, product of M340), 10 parts by weight of nano silica sol (V8802 (12 nm, solid content 40%)) , 7 parts by weight of propyleneglycol monomethyl ether (purified gold), 2.5 parts by weight of a photoinitiator (product of Shibasa, I-184), a leveling agent (BYKKE (BYK 3570, manufactured by BYK 3570) was coated on the other surface of the triacetylcellulose (TAC) film to a thickness of 10 탆, and the coating was applied at 70 캜 for 2 Lt; / RTI >
그 다음, (f) 이형필름이 접합된 도포층을 적산광량이 500mJ/cm2이 되도록 UV를 조사하여 경화시켜, 하드코팅된 편광판을 형성하였다.Then, (f) the coated layer to which the release film was bonded was cured by irradiating UV light so that the accumulated light quantity became 500 mJ / cm 2 to form a hard coated polarizing plate.
실시예Example 2 2
실시예 1에 있어서, 도포층의 두께가 20㎛인 것을 제외하고는 실시예 1과 동일한 방법으로 하드코팅된 편광판을 제조하였다.
A hard-coated polarizing plate was prepared in the same manner as in Example 1 except that the thickness of the coating layer was 20 占 퐉.
실시예Example 3 3
실시예 1에 있어서, 도포층의 두께가 30㎛인 것을 제외하고는 실시예 1과 동일한 방법으로 하드코팅된 편광판을 제조하였다.
A hard-coated polarizing plate was prepared in the same manner as in Example 1, except that the coating layer had a thickness of 30 탆.
실시예Example 4 4
실시예 1에 있어서, 트리아세틸 셀룰로오스(TAC) 필름의 두께가 40㎛인 것을 제외하고는 실시예 1과 동일한 방법으로 하드코팅된 편광판을 제조하였다.
A hard-coated polarizing plate was prepared in the same manner as in Example 1, except that the thickness of the triacetylcellulose (TAC) film was 40 占 퐉.
실시예Example 5 5
실시예 1에 있어서, (c)단계와 (d)단계의 순서를 바꾸어, (d)단계 후에 (c)단계를 실시하는 것 이외에는 실시예 1과 동일한 방법으로 하드코팅된 편광판을 제조하였다.
A hard-coated polarizing plate was produced in the same manner as in Example 1 except that the procedure of (c) and the process of (d) were changed and the process of (d) was followed by the process of (c).
비교예Comparative Example 1 One
실시예 2에 있어서, (a)단계 및 (c)단계를 실시하지 않는 것(이형필름이 도포층에 접합되지 않은 상태에서 검화 단계 실시) 이외에는 실시예 2와 동일한 방법으로 하드코팅된 편광판을 제조하였다.A hard coated polarizing plate was produced in the same manner as in Example 2 except that steps (a) and (c) were not carried out (a saponification step in a state where the release film was not bonded to the application layer) Respectively.
비교예Comparative Example 2 2
실시예 2에 있어서, (g)단계를 (f)단계 다음으로 실시(하드코팅층 형성 후에 편광자 부착 단계 실시)하는 것 이외에는 실시예 2와 동일한 방법으로 하드코팅된 편광판을 제조하였다.
A hard-coated polarizing plate was prepared in the same manner as in Example 2 except that the step (g) was carried out in the same manner as in Example 2 except that the step (f) was carried out (after the hard coating layer was formed and the polarizer was attached).
실험예Experimental Example
상기 실시예 및 비교예에서 제조한 방현성 하드코팅 필름의 물성을 아래와 같은 방법으로 측정하고, 그 결과를 표 1에 나타내었다. 측정법 및 평가방법은 다음과 같다.
The physical properties of the light-scattering hard coating film prepared in the above Examples and Comparative Examples were measured by the following methods, and the results are shown in Table 1. The measurement method and evaluation method are as follows.
(1) 연필경도 평가(1) Evaluation of pencil hardness
JIS K5600에 의거, Pencil Hardness Tester(연필경도기, 석보과학)를 이용하여 측정하였다. 하중 500g, 45° 각도로 연필을 고정시킨 후 표면을 연필 경도별로 긁어 육안으로 긁히는지 여부를 판단하였다.
And measured using a Pencil Hardness Tester (Pencil Hardness Tester, Mobo Scientific) according to JIS K5600. The pencil was fixed with a load of 500 g and a 45 ° angle, and then the surface was scratched by pencil hardness to judge whether or not it was scratched with the naked eye.
(2) (2) 내찰상성Abrasion resistance 평가 evaluation
마찰시험기(rubbing tester, KPD-301, 기배이엔티사)에 강철솜을 장착한 후 1kg의 하중으로 10회 왕복시켜 발생하는 스크래치 개수를 평가하였다. A steel wool was mounted on a rubbing tester (KPD-301, KABEI-TECH), and the number of scratches generated by reciprocating 10 times with a load of 1 kg was evaluated.
- 평가방법 -- Assessment Methods -
A: 0~10개 A: 0 to 10
B: 11~20개B: 11 ~ 20
C: 20개 이상
C: 20 or more
(3) 컬 발생 정도 평가(3) Evaluation of Curl Generation
A4 사이즈(29.7 X 21.0cm)의 정방형 형상으로 절단한 시료를 평탄한 글라스 판 위에, 필름의 도포된 면을 위로해서 두고, 4각의 유리판으로부터의 떨어진 거리를 25℃, 50%RH에서 측정하여 평균값을 측정값으로 하였다. A sample cut into a square shape of A4 size (29.7 x 21.0 cm) was placed on a flat glass plate with the coated side of the film facing up, and the distance from the four glass plates was measured at 25 DEG C and 50% As a measurement value.
- 평가방법 -- Assessment Methods -
매우 양호: 0~15mm Very good: 0-15mm
양호: 15~30mmGood: 15 to 30 mm
불량: 30~50mmBad: 30 ~ 50mm
매우 불량: 50mm 이상
Very poor: more than 50mm
(4) 밀착성 평가(4) Evaluation of adhesion
하드코팅된 편광필름의 하드 코팅면에 1mm 간격으로 가로 세로 각각 11개의 줄을 그어 1mmⅹ1mm 크기의 사각형 100개를 만들었다. 본 격자에 니치방 테이프를 붙였다가 45° 방향으로 테이프를 박리하고, 하기의 표에 [(박리되지 않은 사각형의 수)/100]의 형태로 기재하였다. 이 때 박리되지 않은 사각형의 수가 많을수록 밀착성이 우수한 것이다.
On the hard coated surface of the hard coated polarizing film, 11 squares each having a length of 1 mm and a length of 1 mm were formed to make 100 squares having a size of 1 mm to 1 mm. The tape was peeled off in the direction of 45 DEG after attaching a nicotine tape to this grid and described in the form of [(number of unfixed squares) / 100] in the following table. At this time, the greater the number of unfixed squares, the better the adhesion.
상기 표 1을 통해 보는 바와 같이 본 발명에 따른 실시예의 경우, 하드코팅층의 연필경도가 높고, 내찰상성이 우수함을 확인할 수 있었다. 또한 하드코팅층 형성용 조성물의 경화 후 약간의 컬이 발생하기는 하지만 경화로 인해 컬 발생하기 전에 편광자 보호필름과 편광자를 부착하기 때문에 컬 발생으로 인한 편광판과 부착의 어려움이 없었다. As shown in Table 1, it can be confirmed that the hard coating layer of the embodiment according to the present invention has high pencil hardness and excellent scratch resistance. Also, although the curl of the composition for forming the hard coat layer is slightly curled, the polarizer protective film and the polarizer are adhered before curling due to curing, so that there is no difficulty in adhering to the polarizing plate due to curling.
Claims (7)
(b) 상기 이형필름이 접합된 셀룰로오스계 수지 필름을 검화하는 단계;
(c) 상기 셀룰로오스계 수지 필름으로부터 이형필름을 박리하는 단계;
(d) 상기 검화된 셀룰로오스계 수지 필름 표면에 편광자를 접합하는 단계;
(e) 상기 셀룰로오스계 수지 필름의 이형필름 박리면에 하드코팅층 형성용 조성물을 도포하여 도포층을 형성하는 단계; 및
(f) 상기 도포층을 경화시켜 하드코팅층을 형성하는 단계를 포함하는 것을 특징으로 하는 하드코팅된 편광판의 제조방법.
(a) bonding a releasing film to one surface of a cellulose resin film;
(b) saponifying the cellulosic resin film to which the release film is bonded;
(c) peeling the release film from the cellulose-based resin film;
(d) bonding a polarizer to the surface of the saponified cellulose based resin film;
(e) applying a composition for forming a hard coating layer on the releasing film peeling surface of the cellulose resin film to form a coating layer; And
(f) curing the coating layer to form a hard coating layer.
The method of claim 1, wherein step (c) and step (d) are changed, and step (c) is performed after step (d).
The method of manufacturing a hard-coated polarizing plate according to any one of claims 1 to 2, wherein the composition for forming a hard coating layer comprises a photo-curable light transmitting resin and an initiator.
The hard coating according to claim 3, wherein the composition for forming a hard coating layer further comprises at least one selected from the group consisting of a solvent, an antioxidant, a UV absorber, a light stabilizer, a leveling agent, a surfactant, Of the polarizing plate.
[4] The method of claim 3, wherein the composition for forming a hard coating layer has a volume shrinkage of 5 to 40%.
The method according to any one of claims 1 to 2, wherein the thickness of the coating layer is 10 to 30 μm.