KR20140046755A - Method of preparing alkyl acrylate-vinyl aromatic compound-vinylcyan compound copolymer and thermoplastic resin composition comprising the same having excellent impact strength - Google Patents
Method of preparing alkyl acrylate-vinyl aromatic compound-vinylcyan compound copolymer and thermoplastic resin composition comprising the same having excellent impact strength Download PDFInfo
- Publication number
- KR20140046755A KR20140046755A KR1020120112800A KR20120112800A KR20140046755A KR 20140046755 A KR20140046755 A KR 20140046755A KR 1020120112800 A KR1020120112800 A KR 1020120112800A KR 20120112800 A KR20120112800 A KR 20120112800A KR 20140046755 A KR20140046755 A KR 20140046755A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- compound
- parts
- vinyl
- alkyl acrylate
- Prior art date
Abstract
Description
본 발명은 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법 및 이를 포함하는 열가소성 수지 조성물에 관한 것으로서, 더욱 상세하게는 공중합체의 코어 부분에 폴리에틸렌계 가교제를 사용하여 아크릴레이트-스티렌-아크릴로니트릴 공중합체를 제조하고, 이를 열가소성 수지 조성물에 적용함으로써, 수지의 충격강도를 보다 향상시키는 효과를 나타내는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법 및 이를 포함하는 열가소성 수지 조성물에 관한 것이다.The present invention relates to a method for preparing an alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer and a thermoplastic resin composition comprising the same, and more particularly, to an acrylate-styrene using a polyethylene-based crosslinking agent in a core portion of the copolymer. A method for producing an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer and a thermoplastic comprising the same, by producing an acrylonitrile copolymer and applying the same to a thermoplastic resin composition, thereby further improving the impact strength of the resin. It relates to a resin composition.
일반적으로 부타디엔 고무질 중합체에 스티렌과 아크릴로니트릴 단량체를 그라프트 공중합시켜 제조하는 아크릴로니트릴-부타디엔-스티렌(acrylonitrile-butadiene-styrene, ABS) 수지는 내충격성, 가공성, 미려한 외관, 우수한 기계적 강도, 및 높은 열변형 온도 등의 특성을 갖추고 있어 자동차 부품, 전기전자제품, 건축자재 등 다양한 용도로 사용되고 있다.Generally, acrylonitrile-butadiene-styrene (ABS) resins prepared by graft copolymerizing styrene and acrylonitrile monomers to a butadiene rubber polymer have excellent impact resistance, processability, beautiful appearance, High heat distortion temperature, etc., and is used for various purposes such as automobile parts, electrical and electronic products, and building materials.
그러나 ABS 수지는 충격보강제로 사용된 부타디엔 고무에 에틸렌계 불포화 중합체가 존재하기 때문에 산소의 존재 하에서 자외선, 광, 열에 의하여 쉽게 산호가 일어나 수지의 외형 및 색깔 변화가 일어나며 기계적 물성이 저하되는 취약점을 가지고 있어 실외용 재료로 적합하지 못하다는 문제점이 있다.However, because ABS resin has ethylenically unsaturated polymer in butadiene rubber used as impact modifier, corals are easily generated by ultraviolet rays, light and heat in the presence of oxygen, so the resin's appearance and color change and mechanical properties are deteriorated. There is a problem that it is not suitable for outdoor materials.
따라서 물성이 우수하며 내후성과 내노화성이 우수한 열가소성 수지를 얻기 위해서 충격보강제로 부타디엔 고무 대신에 에틸렌계 불포화 중합체가 존재하지 않는 아크릴 고무를 사용한 아크릴로니트릴-스티렌-아크릴레이트(acrylonitrile-styrene-acrylate, ASA) 삼원 공중합체 수지가 사용되고 있다. 이러한 ASA 수지는 옥외에 사용되는 전기전자부품, 건축자재, 자동차, 선박, 레저용품, 원예용 등 다방면에 사용되고 있다.Therefore, in order to obtain a thermoplastic resin excellent in physical properties and excellent in weather resistance and aging resistance, an acrylonitrile-styrene-acrylate (hereinafter referred to as " acrylonitrile- styrene- acrylate "), which uses an acrylic rubber in which an ethylenically unsaturated polymer is not present instead of butadiene rubber as an impact modifier, ASA) terpolymer resin is used. Such ASA resins are used in various fields such as electric and electronic parts used for outdoor use, building materials, automobiles, ships, leisure goods, and gardening.
그러나 ABS 충격강도에 비해 다소 떨어지는 경향이 있어 충격강도 향상에 대한 많은 시도가 있었다. 고무의 입경을 기존보다 크게 만들어 충격강도를 올리는 시도가 있다. 하지만 고무의 입경이 커지면 라텍스 안정성이 떨어지고, 인장강도와 같은 다른 물성이 떨어지는 단점이 있다.However, there have been many attempts to improve the impact strength since it tends to be somewhat lower than the ABS impact strength. Attempts have been made to increase the impact strength by making the particle size of the rubber larger than before. However, when the rubber particle size increases, latex stability is lowered, and other physical properties such as tensile strength are inferior.
그러므로 고무의 입경을 조절하지 않고도 충격강도를 향상시킬 수 있는 아크릴레이트-스티렌-아크릴로니트릴 수지가 요구되고 있는 실정이다.Therefore, there is a need for an acrylate-styrene-acrylonitrile resin that can improve impact strength without adjusting the particle size of rubber.
이에 본 발명에서는 상기와 같은 종래 기술의 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 충격강도가 우수한 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법 및 상기 제조방법에 의하여 제조된 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체를 포함하는 열가소성 수지 조성물을 제공하는 데에 있다.Therefore, in the present invention to solve the problems of the prior art as described above, an object of the present invention is to prepare an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer excellent in impact strength and prepared by the method It is to provide a thermoplastic resin composition comprising an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer.
본 발명의 상기 목적은 하기 설명되는 본 발명에 의하여 모두 달성 될 수 있다.The above object of the present invention can be achieved by the present invention described below.
상기 목적을 달성하기 위하여, 본 발명은 비닐시안 화합물-비닐방향족 화합물 공중합체 40 내지 80중량%; 및 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체 20 내지 60중량%;를 포함하며, 상기 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체는 (A) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상을 포함하여 이루어진 시드; (B) 상기 시드를 감싸고 알킬 아크릴레이트 단량체 및 폴리에틸렌계 가교제를 포함하여 이루어진 고무 코어; 및 (C) 상기 고무 코어를 감싸고 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상을 포함하여 이루어진 그라프트 쉘;을 포함하여 이루어지는 것을 특징으로 하는 열가소성 수지 조성물을 제공한다.In order to achieve the above object, the present invention is a vinyl cyan compound-vinylaromatic compound copolymer 40 to 80% by weight; And 20 to 60 wt% of an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer, wherein the alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer comprises (A) a vinyl aromatic compound, a vinyl cyan compound and A seed comprising at least one member selected from the group consisting of alkyl acrylates; (B) a rubber core surrounding the seed and comprising an alkyl acrylate monomer and a polyethylene-based crosslinker; And (C) a graft shell surrounding the rubber core and including at least one selected from the group consisting of an aromatic vinyl compound and a vinyl cyan compound.
또한, 본 발명은 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조에 사용된 총 단량체 100중량부에 대하여, (a) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상 4 내지 30중량부를 포함하는 단량체 혼합물을 중합함으로써 시드를 제조하는 단계; (b) 상기 시드의 존재하에 알킬 아크릴레이트 단량체 20 내지 80중량부 및 폴리에틸렌계 가교제 0.01 내지 3중량부를 중합함으로써 고무 코어를 제조하는 단계; 및 (c) 상기 고무 코어의 존재하에 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상 10 내지 70중량부를 포함하는 단량체 혼합물 및 가교제 0.01 내지 5중량부를 중합함으로써 가교된 그라프트 쉘을 제조하는 단계;를 포함하여 이루어지는 것을 특징으로 하는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법을 제공한다.In addition, the present invention is selected from the group consisting of (a) a vinyl aromatic compound, a vinyl cyan compound and an alkyl acrylate, based on 100 parts by weight of the total monomers used in the preparation of the alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer. Preparing a seed by polymerizing a monomer mixture including at least one 4 to 30 parts by weight; (b) preparing a rubber core by polymerizing 20 to 80 parts by weight of an alkyl acrylate monomer and 0.01 to 3 parts by weight of a polyethylene-based crosslinking agent in the presence of the seed; And (c) polymerizing a monomer mixture comprising 10 to 70 parts by weight of at least one selected from the group consisting of aromatic vinyl compounds and vinyl cyan compounds and 0.01 to 5 parts by weight of a crosslinking agent in the presence of the rubber core to produce a crosslinked graft shell. It provides a method for producing an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer comprising a step.
본 발명에 따라 제조된 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체를 포함하여 이루어진 열가소성 수지 조성물은 충격강도가 매우 우수한 효과를 가진다.The thermoplastic resin composition comprising the alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer prepared according to the present invention has an excellent impact strength.
상기와 같은 목적을 달성하기 위한 본 발명의 열가소성 수지 조성물은 비닐시안 화합물-비닐방향족 화합물 공중합체 40 내지 80중량%; 및 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체 20 내지 60중량%;를 포함하며, 상기 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체는 (A) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상을 포함하여 이루어진 시드; (B) 상기 시드를 감싸고 알킬 아크릴레이트 단량체 및 폴리에틸렌계 가교제를 포함하여 이루어진 고무 코어; 및 (C) 상기 고무 코어를 감싸고 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상을 포함하여 이루어진 그라프트 쉘;을 포함하여 이루어지는 것을 특징으로 한다.The thermoplastic resin composition of the present invention for achieving the above object is 40 to 80% by weight of a vinyl cyan compound-vinylaromatic compound copolymer; And 20 to 60 wt% of an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer, wherein the alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer comprises (A) a vinyl aromatic compound, a vinyl cyan compound and A seed comprising at least one member selected from the group consisting of alkyl acrylates; (B) a rubber core surrounding the seed and comprising an alkyl acrylate monomer and a polyethylene-based crosslinker; And (C) a graft shell surrounding the rubber core and comprising at least one selected from the group consisting of an aromatic vinyl compound and a vinyl cyan compound.
또한, 본 발명의 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물의 제조방법은 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조에 사용된 총 단량체 100중량부에 대하여, (a) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상 4 내지 30중량부를 포함하는 단량체 혼합물을 중합함으로써 시드를 제조하는 단계; (b) 상기 시드의 존재하에 알킬 아크릴레이트 단량체 20 내지 80중량부를 포함하는 단량체 혼합물 및 폴리에틸렌계 가교제 0.01 내지 3중량부를 중합함으로써 고무 코어를 제조하는 단계; 및 (c) 상기 고무 코어의 존재하에 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상 10 내지 70중량부를 포함하는 단량체 혼합물 및 가교제 0.01 내지 5중량부를 중합함으로써 가교된 그라프트 쉘을 제조하는 단계;를 포함하여 이루어지는 것을 특징으로 한다.In addition, the method for producing the alkylacrylate-vinylaromatic compound-vinylcyan compound of the present invention is based on 100 parts by weight of the total monomers used in the preparation of the alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer, (a) vinyl Preparing a seed by polymerizing a monomer mixture comprising 4 to 30 parts by weight of at least one selected from the group consisting of an aromatic compound, a vinyl cyan compound and an alkyl acrylate; (b) preparing a rubber core by polymerizing a monomer mixture comprising 20 to 80 parts by weight of an alkyl acrylate monomer and 0.01 to 3 parts by weight of a polyethylene-based crosslinking agent in the presence of the seed; And (c) polymerizing a monomer mixture comprising 10 to 70 parts by weight of at least one selected from the group consisting of aromatic vinyl compounds and vinyl cyan compounds and 0.01 to 5 parts by weight of a crosslinking agent in the presence of the rubber core to produce a crosslinked graft shell. Characterized in that it comprises a;
이하, 본 발명을 더욱 상세하게 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail.
본 발명의 열가소성 수지 조성물은 비닐시안 화합물-비닐방향족 화합물 공중합체 40 내지 80중량%; 및 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체 20 내지 60중량%;를 포함하며, 상기 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체는 (A) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상을 포함하여 이루어진 시드; (B) 상기 시드를 감싸고 알킬 아크릴레이트 단량체 및 폴리에틸렌계 가교제를 포함하여 이루어진 고무 코어; 및 (C) 상기 고무 코어를 감싸고 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상을 포함하여 이루어진 그라프트 쉘;을 포함하여 이루어지는 것을 특징으로 한다.The thermoplastic resin composition of the present invention is 40 to 80% by weight of a vinyl cyan compound-vinylaromatic compound copolymer; And 20 to 60 wt% of an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer, wherein the alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer comprises (A) a vinyl aromatic compound, a vinyl cyan compound and A seed comprising at least one member selected from the group consisting of alkyl acrylates; (B) a rubber core surrounding the seed and comprising an alkyl acrylate monomer and a polyethylene-based crosslinker; And (C) a graft shell surrounding the rubber core and comprising at least one selected from the group consisting of an aromatic vinyl compound and a vinyl cyan compound.
상기 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조에 사용된 총 단량체 100중량부에 대하여, (A) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상 4 내지 30중량부를 포함하여 이루어진 시드; (B) 상기 시드를 감싸고 알킬 아크릴레이트 단량체 20 내지 80중량부 및 폴리에틸렌글리콜 디아크릴레이트, 폴리에틸렌글리콜 디메타크릴레이트, 폴리프로필렌글리콜 디아크릴레이트 및 폴리프로필렌글리콜 디메타크릴레이트로 이루어진 군으로부터 선택된 가교제 0.01 내지 3중량부를 포함하여 이루어진 고무 코어; 및 (C) 상기 고무 코어를 감싸고 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상 10 내지 70중량부 및 가교제 0.01 내지 3중량부를 포함하여 이루어진 가교된 그라프트 쉘;을 포함하여 이루어질 수 있다.The alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer is based on 100 parts by weight of the total monomers used in the preparation of the alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer, (A) vinyl aromatic compound, vinyl cyan A seed comprising 4 to 30 parts by weight of at least one selected from the group consisting of a compound and an alkyl acrylate; (B) an alkyl acrylate monomer surrounding the seed A rubber core comprising 20 to 80 parts by weight and 0.01 to 3 parts by weight of a crosslinking agent selected from the group consisting of polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, polypropylene glycol diacrylate and polypropylene glycol dimethacrylate; And (C) a crosslinked graft shell surrounding the rubber core and comprising at least one 10 to 70 parts by weight and at least 3 parts by weight of a crosslinking agent selected from the group consisting of an aromatic vinyl compound and a vinyl cyan compound. have.
상기 폴리에틸렌계 가교제는 폴리알킬렌글리콜 디아크릴레이트 또는 폴리알킬렌글리콜 디메타크릴레이트로 이루어진 군으로부터 1종 이상 선택될 수 있으며, 구체적으로 폴리에틸렌글리콜 디메타크릴레이트, 폴리프로필렌글리콜 디아크릴레이트 및 폴리프로필렌글리콜 디메타크릴레이트로 이루어진 군으로부터 1종 이상 선택될 수 있다. 일례로 폴리에틸렌글리콜 디아크릴레이트를 사용하나, 이에 한정되는 것은 아니다.The polyethylene-based crosslinking agent may be at least one selected from the group consisting of polyalkylene glycol diacrylate or polyalkylene glycol dimethacrylate, and specifically, polyethylene glycol dimethacrylate, polypropylene glycol diacrylate, and poly It may be selected from the group consisting of propylene glycol dimethacrylate. For example, polyethylene glycol diacrylate is used, but not limited thereto.
상기 방향족 비닐 화합물은 스티렌, α-메틸스티렌, p-메틸스티렌 및 비닐톨루엔으로 이루어진 군으로부터 1종 이상 선택될 수 있으며, 일례로 스티렌을 사용하나, 이에 한정되는 것은 아니다.The aromatic vinyl compound may be at least one selected from the group consisting of styrene, α-methylstyrene, p-methylstyrene, and vinyltoluene. For example, styrene is used, but is not limited thereto.
상기 비닐시안 화합물은 아크릴로니트릴, 메타크릴로니트릴 및 에타크릴로니트릴로 이루어진 군으로부터 1종 이상 선택될 수 있으며, 일례로는 아크릴로니트릴을 사용하나, 이에 한정되는 것은 아니다.The vinyl cyan compound may be selected from one or more selected from the group consisting of acrylonitrile, methacrylonitrile and ethacrylonitrile, and examples thereof include acrylonitrile, but are not limited thereto.
상기 알킬아크릴레이트는 탄소수가 2 내지 8인 알킬기를 포함할 수 있으며, 일례로는 알킬 부분의 탄소수가 1 내지 4인 메틸아크릴레이트, 에틸아크릴레이트 또는 부틸아크릴레이트를 사용하나, 이에 한정되는 것은 아니다.The alkyl acrylate may include an alkyl group having 2 to 8 carbon atoms. For example, methyl acrylate, ethyl acrylate or butyl acrylate having 1 to 4 carbon atoms in the alkyl portion may be used, but is not limited thereto. .
상기 비닐시안 화합물-비닐방향족 화합물 공중합체의 일례로는 아크릴로니트릴-스티렌(acrylonitrile-styrene, AS) 공중합체일 수 있다.An example of the vinyl cyan compound-vinylaromatic compound copolymer may be an acrylonitrile-styrene (AS) copolymer.
상기 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 일례로는 아크릴레이트-스티렌-아크릴로니트릴(acrylate-styrene-acrylonitrile, ASA)일 수 있다.An example of the alkyl acrylate-vinyl aromatic compound-vinyl cyan compound copolymer may be acrylate-styrene-acrylonitrile (ASA).
본 발명의 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법의 구체적인 일 실시예는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조에 사용된 총 단량체 100중량부에 대하여, (a) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상 4 내지 30중량부를 포함하는 단량체, 전해질 0.001 내지 1중량부, 가교제 0.01 내지 1중량부, 그라프팅제 0.01 내지 3중량부, 개시제 0.01 내지 3중량부 및 유화제 0.01 내지 5중량부를 포함하는 단량체 혼합물을 중합함으로써 시드를 제조하는 단계; (b) 상기 시드의 존재하에 알킬 아크릴레이트 단량체 20 내지 80중량부 및 폴리에틸렌글리콜 디아크릴레이트, 폴리에틸렌글리콜 디메타크릴레이트, 폴리프로필렌글리콜 디아크릴레이트 및 폴리프로필렌글리콜 디메타크릴레이트로 이루어진 군으로부터 선택된 가교제 0.01 내지 3중량부, 개시제 0.01 내지 3중량부 및 유화제 0.01 내지 5중량부를 포함하는 단량체 혼합물을 중합함으로써 고무 코어를 제조하는 단계; 및 (c) 상기 고무 코어의 존재하에 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상 10 내지 70중량부, 가교제 0.01 내지 3중량부, 개시제 0.01 내지 3중량부 및 유화제 0.01 내지 5중량부를 포함하는 단량체 혼합물을 중합함으로써 가교된 그라프트 쉘을 제조하는 단계;를 포함하여 이루어지는 것을 특징으로 한다.One specific embodiment of the method for preparing the alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer of the present invention is based on 100 parts by weight of the total monomers used to prepare the alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer. (a) a monomer comprising 4 to 30 parts by weight of at least one selected from the group consisting of a vinyl aromatic compound, a vinyl cyan compound and an alkyl acrylate, 0.001 to 1 parts by weight of an electrolyte, 0.01 to 1 parts by weight of a crosslinking agent, and 0.01 to 1 part by weight of a grafting agent. Preparing a seed by polymerizing a monomer mixture comprising 3 parts by weight, 0.01 to 3 parts by weight of an initiator and 0.01 to 5 parts by weight of an emulsifier; (b) 20 to 80 parts by weight of alkyl acrylate monomer in the presence of said seed and selected from the group consisting of polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, polypropylene glycol diacrylate and polypropylene glycol dimethacrylate Preparing a rubber core by polymerizing a monomer mixture comprising 0.01 to 3 parts by weight of a crosslinking agent, 0.01 to 3 parts by weight of an initiator and 0.01 to 5 parts by weight of an emulsifier; And (c) at least one selected from the group consisting of an aromatic vinyl compound and a vinyl cyan compound in the presence of the rubber core, 10 to 70 parts by weight, 0.01 to 3 parts by weight of a crosslinking agent, 0.01 to 3 parts by weight of an initiator, and 0.01 to 5 parts by weight of an emulsifier. Producing a cross-linked graft shell by polymerizing a monomer mixture including parts.
상기 (a) 및 (c) 단계에서 사용되는 방향족 비닐 화합물은 스티렌, α-메틸스티렌, p-메틸스티렌 및 비닐톨루엔으로 이루어진 군으로부터 1종 이상 선택될 수 있으며, 바람직하게는 스티렌을 사용하나, 이에 한정되는 것은 아니다.The aromatic vinyl compound used in the steps (a) and (c) may be selected from the group consisting of styrene, -methylstyrene, p-methylstyrene and vinyltoluene. Styrene is preferably used, But is not limited thereto.
상기 (a) 및 (c) 단계에서 사용되는 비닐시안 화합물은 아크릴로니트릴, 메타크릴로니트릴 및 에타크릴로니트릴로 이루어진 군으로부터 1종 이상 선택될 수 있으며, 바람직하게는 아크릴로니트릴을 사용하나, 이에 한정되는 것은 아니다.The vinyl cyan compound used in the steps (a) and (c) may be selected from the group consisting of acrylonitrile, methacrylonitrile, and ethacrylonitrile, preferably acrylonitrile , But is not limited thereto.
상기 (a) 및 (b) 단계의 알킬아크릴레이트는 탄소수가 2 내지 8인 알킬기를 포함하는 것을 특징으로 하며, 바람직하게는 알킬 부분의 탄소수가 1 내지 4인 메틸아크릴레이트, 에틸아크릴레이트 또는 부틸아크릴레이트를 사용하나, 이에 한정되는 것은 아니다.The alkyl acrylate of step (a) and (b) is characterized in that it comprises an alkyl group having 2 to 8 carbon atoms, preferably methyl acrylate, ethyl acrylate or butyl having 1 to 4 carbon atoms of the alkyl portion An acrylate is used, but is not limited thereto.
본원 발명에서는 (b) 단계에서 수평균분자량 250 이상의 폴리에틸렌계 가교제가 사용될 수 있으며, 예를 들면 수평균분자량 250 내지 1,000의 가교제가 사용될 수 있다. 구체적으로 폴리에틸렌글리콜 디아크릴레이트(polyethyleneglycol diacrylate, PEGDA), 폴리에틸렌글리콜 디메타크릴레이트(polyethyleneglycol dimethacrylate, PEGDMA), 폴리프로필렌글리콜 디아크릴레이트(polypropyleneglycol diacrylate, PPGDA) 및 폴리프로필렌글리콜 디메타크릴레이트(polypropyleneglycol dimethacrylate, PPGDMA)로 이루어진 군으로부터 선택된 폴리에틸렌계열의 가교제를 사용하여 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체를 포함하는 열가소성 수지 조성물의 충격강도를 보다 개선하는 것이 특징이다.In the present invention, a polyethylene-based crosslinking agent having a number average molecular weight of 250 or more may be used in step (b), for example, a crosslinking agent having a number average molecular weight of 250 to 1,000 may be used. Specifically, polyethyleneglycol diacrylate (PEGDA), polyethyleneglycol dimethacrylate (PEGDMA), polypropyleneglycol diacrylate (PPGDA) and polypropyleneglycol dimethacrylate (polypropyleneglycol dimethacrylate). , PPGDMA) using a polyethylene-based crosslinking agent selected from the group consisting of further improving the impact strength of the thermoplastic resin composition comprising an alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer.
또한, 폴리에틸렌계 가교제에 그라프팅제를 추가로 투입할 수 있다. 상기 그라프팅제는 알릴 메타크릴레이트(AMA), 트리알릴 이소시아누레이트(TAIC), 트리알릴 아민(TAA) 또는 디알릴 아민(DAA) 등을 사용할 수 있다.In addition, a grafting agent may be further added to the polyethylene-based crosslinking agent. The grafting agent may be allyl methacrylate (AMA), triallyl isocyanurate (TAIC), triallylamine (TAA) or diallyl amine (DAA).
또한, 상기 (c)의 단계에서 사용되는 가교제는 디비닐벤젠, 에틸렌글리콜 디메타크릴레이트, 디에틸렌글리콜 디메타크릴레이트, 트리에틸렌글리콜 디메타크릴레이트, 1,3-부타디올 디메타크릴레이트, 에틸렌글리콜디아크릴레이트, 헥산디올에톡시레이트디아크릴레이트, 헥산디올에톡시레이트디아크릴레이트, 헥산디올프로폭시레이트 디아크릴레이트, 네오펜틸글리콜 디메타크릴레이트, 네오펜틸글리콜 에톡시레이트디아크릴레이트, 네오펜틸글리콜 프로폭시레이트디아크릴레이트, 트리메틸올프로판 트리메타크릴레이트, 트리메틸올메탄 트리아크릴레이트, 트리메틸프로판에톡시레이트 트리아크릴레이트, 트리메틸프로판프로폭시레이트 트리아크릴레이트, 펜타에리트리톨에톡시레이트 트리아크릴레이트, 펜타에리트로톨프로폭시레이트 트리아크릴레이트 및 비닐트리메톡시실란으로 이루어진 군으로부터 1종 이상 선택될 수 있으며, 바람직하게는 디비닐벤젠을 사용하나, 이에 한정되는 것은 아니다.The crosslinking agent used in the step (c) may be at least one selected from the group consisting of divinylbenzene, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, 1,3-butadiol dimethacrylate , Ethylene glycol diacrylate, hexanediol ethoxylate diacrylate, hexanediol ethoxylate diacrylate, hexanediol propoxylate diacrylate, neopentyl glycol dimethacrylate, neopentyl glycol ethoxylate diacrylate Acrylate, trimethylolpropane triacrylate, trimethylolpropane triacrylate, trimethylolpropane triacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, trimethylolmethane triacrylate, trimethylpropaneethoxylate triacrylate, trimethylpropane propoxylate triacrylate, pentaerythritol ethoxy Triacrylate, pentaerythritol propoxylate tri Methacrylate and vinyl triethoxysilane may be one or more selected from the group consisting of silane, preferably a single use of divinylbenzene, and the like.
상기 (a), (b) 및 (c) 단계에 사용되는 유화제로서는 특별히 한정되진 않지만, 예를 들어, 음이온성 계면활성제, 비이온성 계면활성제, 양이온성 계면활성제, 양성 계면활성제 등을 사용할 수 있다.The emulsifier used in the above steps (a), (b) and (c) is not particularly limited, but an anionic surfactant, a nonionic surfactant, a cationic surfactant, a positive surfactant and the like can be used .
이중에서 알케닐 석시네이트 금속염, 알킬벤젠 술폰산염, 지방족 술폰산염, 고급 알코올의 황산 에스테르염, α-올레핀 술폰산염, 및 알킬 에테르 황산 에스테르염으로 이루어진 군으로부터 선택된 음이온성 계면활성제가 특히 바람직하게 사용될 수 있다.Of these, anionic surfactants selected from the group consisting of alkenyl succinate metal salts, alkyl benzene sulfonic acid salts, aliphatic sulfonic acid salts, sulfuric acid ester salts of higher alcohol,? -Olefin sulfonic acid salts and alkyl ether sulfuric acid ester salts are particularly preferably used .
상기 전해질로는 KCl, NaCl, KHCO3, NaHCO3, K2CO3, Na2CO3, KHSO3, NaHSO4, Na2S2O7, K4P2O7, K3PO4, Na3PO4 또는 Na2HPO4 등을 단독 또는 2종 이상 혼합하여 사용할 수 있다.In the electrolyte is KCl, NaCl, KHCO 3, NaHCO 3, K 2 CO 3, Na 2 CO 3, KHSO 3, NaHSO 4, Na 2 S 2 O 7, K 4 P 2 O 7, K 3 PO 4, Na 3 PO 4 or Na 2 HPO 4, etc. alone, or two or more kinds may be mixed.
상기 (a), (b) 및 (c) 단계에서 사용되는 개시제로서는 특별히 한정되진 않지만, 라디칼 개시제가 바람직하게는 사용될 수 있다. 라디칼 개시제로서는 과황산나트륨, 과황산칼륨, 과황산암모늄, 과인산칼륨, 과산화수소 등의 무기과산화물; t-부틸 퍼옥사이드, 큐멘 하이드로퍼옥사이드, p-멘탄하이드로 퍼옥사이드, 디-t-부틸 퍼옥사이드, t-부틸쿠밀 퍼옥사이드, 아세틸 퍼옥사이드, 이소부틸 퍼옥사이드, 옥타노일 퍼옥사이드, 디벤조일 퍼옥사이드, 3,5,5-트리메틸헥산올 퍼옥사이드, t-부틸 퍼옥시 이소부틸레이트 등의 유기 과산화물; 아조비스 이소부티로니트릴, 아조비스-2,4-디메틸발레로니트릴, 아조비스시클로헥산카르보니트릴, 및 아조비스 이소 낙산(부틸산)메틸로 이루어진 그룹으로부터 선택된 1종 이상의 것이며, 이러한 라디칼 개시제 중에서 무기 과산화물이 보다 바람직하고, 이중에서도 과황산염이 특별히 바람직하게 사용될 수 있다.The initiator used in the above steps (a), (b) and (c) is not particularly limited, but a radical initiator can be preferably used. Examples of the radical initiator include inorganic peroxides such as sodium persulfate, potassium persulfate, ammonium persulfate, potassium persulfate, and hydrogen peroxide; t-butyl peroxide, cumene hydroperoxide, p-menthol hydroperoxide, di-t-butyl peroxide, t-butyl cumyl peroxide, acetyl peroxide, isobutyl peroxide, octanoyl peroxide, dibenzoyl peroxide Organic peroxides such as oxides, 3,5,5-trimethylhexanol peroxide, t-butyl peroxyisobutyrate; At least one member selected from the group consisting of azobisisobutyronitrile, azobis-2,4-dimethylvaleronitrile, azobiscyclohexanecarbonitrile, and azobisisobutyric acid (butyl acid) methyl, Inorganic peroxides are more preferable, and persulfates are particularly preferably used.
상기 중합개시제와 함께 과산화물의 개시반응을 촉진시키기 위해 활성화제를 사용할 수 있으며, 상기 활성화제로는 소디움포름알데히드, 설폭실레이트, 소디움에틸렌디아민, 테트라아세테이트, 황산 제1철, 덱스트로오스, 피롤린산나트륨 또는 아황산나트륨 등을 단독 또는 2종 이상 혼합하여 사용하는 것이 바람직하다.An activator may be used to promote the initiation reaction of the peroxide with the polymerization initiator. Examples of the activator include sodium formaldehyde, sulfoxylate, sodium ethylenediamine, tetraacetate, ferrous sulfate, dextrose, Sodium or sodium sulfite, etc. are preferably used alone or in combination of two or more.
상기 (a) 단계에서의 그라프팅제는 알릴 메타크릴레이트(AMA), 트리알릴 이소시아누레이트(TAIC), 트리알릴 아민(TAA) 또는 디알릴 아민(DAA) 등을 사용할 수 있다.The grafting agent in the step (a) may be allyl methacrylate (AMA), triallyl isocyanurate (TAIC), triallylamine (TAA) or diallylamine (DAA).
상기 유화 중합시 중합 온도는 특별히 한정되진 않지만, 보통 50~85℃, 바람직하게는 60~80℃이다.Although the polymerization temperature at the time of the said emulsion polymerization is not specifically limited, Usually, 50-85 degreeC, Preferably it is 60-80 degreeC.
본 발명의 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체는 평균입경이 0.1~0.3㎛인 시드를 포함하는 것이 바람직하며, 평균입경이 0.1㎛ 미만에서는 충격강도가 떨어지며, 0.3㎛ 초과인 경우에는 라텍스 안정성이 떨어지는 문제점이 있다. 또한, 본 발명의 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체는 평균입경이 0.15~0.5㎛인 고무 코어를 포함하는 것이 바람직하다.The alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer of the present invention preferably includes a seed having an average particle diameter of 0.1 to 0.3 µm, and an impact strength is lowered at an average particle diameter of less than 0.1 µm, and more than 0.3 µm. There is a problem that the latex stability is poor. Moreover, it is preferable that the alkylacrylate-vinylaromatic compound-vinyl cyan compound copolymer of this invention contains the rubber core whose average particle diameter is 0.15-0.5 micrometer.
상기 열가소성 수지 조성물은 용도에 따라 통상적으로 사용되는 염료, 안료, 활제, 산화방지제, 자외선안정제, 열안정제, 보강제, 충전제, 난연제, 발포제, 가소제 또는 무광택제 등의 첨가제를 더 포함할 수 있다.The thermoplastic resin composition may further include additives such as dyes, pigments, lubricants, antioxidants, ultraviolet stabilizers, heat stabilizers, reinforcing agents, fillers, flame retardants, foaming agents, plasticizers, or matting agents, which are commonly used according to uses.
본 발명에 의한 상기 열가소성 수지 조성물을 포함하여 외장재를 제조할 수 있으며, 구체적으로는 자동차 외장재 또는 핸드폰 외장재로서 유용하게 제조될 수 있다.
Including the thermoplastic resin composition according to the present invention can be prepared an exterior material, specifically, it can be usefully manufactured as a vehicle exterior material or a mobile phone exterior material.
이하 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범주 및 기술사상 범위 내에서 다양한 변경 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변경 및 수정이 첨부된 특허청구범위에 속하는 것도 당연한 것이다.It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope and spirit of the invention as disclosed in the accompanying claims. Changes and modifications may fall within the scope of the appended claims.
[실시예][Example]
실시예Example 1 One
하드한Hard 고분자 시드 제조단계 Step of polymer seed preparation
질소치환된 중합 반응기에 증류수 40중량부를 넣고 75℃까지 승온시킨 후, 칼륨 퍼설페이트 0.025중량부를 일괄투입하여 반응을 개시한 후, 스티렌 5중량부, Na2CO3 0.05중량부, 에틸렌 글리콜 디메타크릴레이트 0.025중량부, 알릴 메타크릴레이트 0.025중량부 및 라우릴 황산나트륨 0.05중량부를 혼합한 혼합물을 75℃에서 연속투입하여 평균입경이 0.1㎛인 하드한 고분자 시드를 제조하였다.40 parts by weight of distilled water was added to the polymerization reactor purged with nitrogen and the temperature was raised to 75 캜. Then, 0.025 part by weight of potassium persulfate was added thereto in a total amount of 5 parts by weight. Styrene 5 parts by weight, Na 2 CO 3 0.05 parts by weight, 0.025 part by weight of acrylate, 0.025 part by weight of allyl methacrylate and 0.05 part by weight of sodium laurylsulfate were continuously added at 75 DEG C to prepare a hard polymer seed having an average particle diameter of 0.1 mu m.
고무 중합체 코어 제조단계Rubber polymer core preparation step
상기 제조한 하드한 고분자 시드 라텍스의 존재 하에, 증류수 60중량부, 부틸아크릴레이트 55중량부, 폴리에틸렌글리콜 디아크릴레이트(분자량 258) 0.3중량부, 알릴 메타크릴레이트 0.3중량부, 큐멘 하이드로 퍼옥사이드 0.5중량부 및 라우릴황산나트륨 0.5중량부를 혼합한 혼합물을 75℃에서 연속투입하여 평균입경이 0.3㎛인 고무중합체 코어를 제조하였다.In the presence of the prepared hard polymer seed latex, 60 parts by weight of distilled water, 55 parts by weight of butyl acrylate, 0.3 parts by weight of polyethylene glycol diacrylate (molecular weight 258), 0.3 part by weight of allyl methacrylate, cumene hydroperoxide 0.5 A mixture of parts by weight and 0.5 parts by weight of sodium lauryl sulfate was continuously added at 75 ° C. to prepare a rubber polymer core having an average particle diameter of 0.3 μm.
그라프트Graft 쉘 제조단계 Shell manufacturing step
상기 제조한 고무중합체 코어의 존재 하에, 증류수 50중량부, 스티렌 30중량부, 아크릴로니트릴 10중량부, 디비닐벤젠 0.5중량부, 큐멘 하이드로 퍼옥사이드 0.5중량부 및 라우릴황산나트륨 0.65중량부를 혼합한 혼합물을 75℃에서 연속투입하면서 중합반응을 실시하였다. 또한 중합전환율을 높이기 위하여 상기 혼합물의 투입이 완료된 후 75℃에서 1시간 동안 더 반응시키고 60℃까지 냉각시켜 중합반응을 종료하여 그라프트 공중합체 라텍스를 제조하였다. 제조된 그라프트 공중합체 라텍스의 중합전환율은 98%, 고형분은 40%였다.In the presence of the prepared rubber polymer core, 50 parts by weight of distilled water, 30 parts by weight of styrene, 10 parts by weight of acrylonitrile, 0.5 parts by weight of divinylbenzene, 0.5 parts by weight of cumene hydroperoxide and 0.65 parts by weight of sodium lauryl sulfate were mixed. The polymerization was carried out while the mixture was continuously charged at 75 ° C. After the addition of the mixture was completed, the mixture was further reacted at 75 DEG C for 1 hour and cooled to 60 DEG C to complete the polymerization reaction, thereby preparing a graft copolymer latex. The polymerization conversion ratio of the prepared graft copolymer latex was 98% and the solid content was 40%.
그라프트Graft 공중합체 분말 제조 Preparation of Copolymer Powder
상기 제조된 아크릴레이트-스티렌-아크릴로니트릴 그라프트 공중합체 라텍스를 황산 수용액을 사용하여 80℃에서 상압응집을 한 후, 95℃에서 숙성하고, 탈수 및 세척하여, 90℃ 열풍으로 30분 동안 건조시켜 아크릴레이트-스티렌-아크릴로니트릴 그라프트 공중합체 분말을 제조하였다.
The prepared acrylate-styrene-acrylonitrile graft copolymer latex was subjected to atmospheric coagulation using an aqueous sulfuric acid solution at 80 ° C., and then aged at 95 ° C., dehydrated and washed, and dried for 30 minutes with 90 ° C. hot air. To prepare an acrylate-styrene-acrylonitrile graft copolymer powder.
실시예Example 2 2
상기 실시예 1의 고무 중합체 코어의 제조단계에서 PEGDA 대신에 폴리에틸렌글리콜디메타크릴레이트(분자량 330) 0.3중량부를 사용한 것을 제외하고는 상기 실시예 1과 동일하게 실시하여 그라프트 공중합체 분말을 제조하였다.
Except that 0.3 part by weight of polyethylene glycol dimethacrylate (molecular weight: 330) was used instead of PEGDA in the preparation of the rubber polymer core of Example 1, to prepare a graft copolymer powder .
실시예Example 3 3
상기 실시예 1의 고무 중합체 코어의 제조단계에서 PEGDA (분자량 258) 대신에 PEGDA (분자량 575) 0.3중량부를 사용한 것을 제외하고는 상기 실시예 1과 동일하게 실시하여 그라프트 공중합체 분말을 제조하였다.
A graft copolymer powder was prepared in the same manner as in Example 1 except that 0.3 part by weight of PEGDA (molecular weight: 575) was used instead of PEGDA (molecular weight: 258) in the preparation of the rubber polymer core of Example 1.
실시예Example 4 4
상기 실시예 1의 고무 중합체 코어의 제조단계에서 PEGDA (분자량 258) 대신에 PEGDA (분자량 700) 0.3중량부를 사용한 것을 제외하고는 상기 실시예 1과 동일하게 실시하여 그라프트 공중합체 분말을 제조하였다.
A graft copolymer powder was prepared in the same manner as in Example 1 except that 0.3 part by weight of PEGDA (molecular weight: 700) was used instead of PEGDA (molecular weight: 258) in the preparation of the rubber polymer core of Example 1.
실시예Example 5 5
상기 실시예 1의 가교된 그라프트 쉘의 제조단계에서 디비닐벤젠을 사용하지 않은 것을 제외하고는 상기 실시예 1과 동일하게 실시하여 그라프트 공중합체 분말을 제조하였다.
A graft copolymer powder was prepared in the same manner as in Example 1, except that divinylbenzene was not used in the step of preparing the crosslinked graft shell of Example 1.
비교예Comparative Example 1 One
상기 실시예 1의 고무 중합체 코어의 제조단계에서 PEGDA (분자량 258) 대신에 에틸렌글리콜디메타크릴레이트(EGDMA) 0.3중량부를 사용한 것을 제외하고는 상기 실시예 1과 동일하게 실시하여 그라프트 공중합체 분말을 제조하였다.
Graft copolymer powder was prepared in the same manner as in Example 1 except that 0.3 parts by weight of ethylene glycol dimethacrylate (EGDMA) was used instead of PEGDA (molecular weight 258) in the preparation of the rubber polymer core of Example 1. Was prepared.
비교예Comparative Example 2 2
상기 실시예 1의 고무 중합체 코어의 제조단계에서 PEGDA (분자량 258) 대신에 알릴메타크릴레이트(allyl methacrylate, AMA) 0.6중량부를 사용한 것을 제외하고는 상기 실시예 1과 동일하게 실시하여 그라프트 공중합체 분말을 제조하였다.
Except that 0.6 weight parts of allyl methacrylate (AMA) was used in place of PEGDA (molecular weight 258) in the preparation of the rubber polymer core of Example 1, to prepare a graft copolymer Powder.
비교예Comparative Example 3 3
상기 실시예 5의 고무 중합체 코어의 제조단계에서 PEGDA (분자량 258) 대신에 에틸렌글리콜디메타크릴레이트(EGDMA) 0.3중량부를 사용한 것을 제외하고는 상기 실시예 5와 동일하게 실시하여 그라프트 공중합체 분말을 제조하였다.
Graft copolymer powder was prepared in the same manner as in Example 5 except that 0.3 parts by weight of ethylene glycol dimethacrylate (EGDMA) was used instead of PEGDA (molecular weight 258) in the preparation of the rubber polymer core of Example 5. Was prepared.
[시험예][Test Example]
< ASA 수지 제조>< ASA resin manufacturing>
상기 실시예 1 내지 5 및 비교예 1 내지 3에서 제조한 그라프트 공중합체 분말 40중량부, 경질 매트릭스로 스티렌-아크릴로니트릴 공중합체 90HR (LG화학 제조) 60중량부에 활제 2중량부, 산화방지제 2중량부, 자외선안정제 3중량부를 첨가하고 혼합하였다. 이를 220℃의 실린더 온도에서 40파이 압출혼련기를 사용하여 펠렛 형태로 제조하고, 이 펠렛으로 사출하여 물성시편을 제조하여 하기 물성을 측정하여 표 1에 나타내었다.0 parts by weight of the graft copolymer powder 40 prepared in Examples 1 to 5 and Comparative Examples 1 to 3, 2 parts by weight of lubricant, to 60 parts by weight of styrene-acrylonitrile copolymer 90HR (manufactured by LG Chemical) as a hard matrix, 2 parts by weight of antioxidant and 3 parts by weight of UV stabilizer were added and mixed. This was prepared in pellet form using a 40 pie extrusion kneader at a cylinder temperature of 220 ° C., and injected into the pellet to prepare a physical specimen and measured in the following physical properties.
* 아이조드 충격강도(1/8", 1/4" notched at (23℃), kg·cm/cm) - ASTM D256에 의거하여 측정하였다.* Izod impact strength (1/8 ", 1/4" notched at (23 ° C), kg cm / cm)-was measured according to ASTM D256.
* 인장강도(50mm/min, kg/cm2): ASTM D638에 의거하여 측정하였다.Tensile strength (50 mm / min, kg / cm 2 ): Measured according to ASTM D638.
(ASA)Graft copolymer
(ASA)
(kg/cm2)The tensile strength
(kg / cm 2 )
(1/8"
(kg·cm/cm)Impact strength
(1/8 "
(kg · cm / cm)
(1/4"
(kg·cm/cm)Impact strength
(1/4 "
(kg · cm / cm)
시험예 1 내지 시험예 5에 따라 아크릴로니트릴-스티렌 수지에 코어 부분에 PEGDA 등의 가교제를 사용하여 제조한 아크릴레이트-스티렌-아크릴로니트릴 공중합체를 포함하였을 때, 상기 PEGDA의 가교제를 사용하지 않는 시험예 6 내지 시험예 8에 비하여 수지의 충격강도를 증가시키는 효과를 확인할 수 있고, 인장강도와 같은 물성 또한 저하시키지 않고 유지가 가능하다는 것을 알 수 있다.When the acrylonitrile-styrene resin according to Test Examples 1 to 5 contained an acrylate-styrene-acrylonitrile copolymer prepared by using a crosslinking agent such as PEGDA in the core portion, the crosslinking agent of PEGDA was not used. It can be seen that the effect of increasing the impact strength of the resin compared to Test Examples 6 to 8 that do not, and can be maintained without lowering the physical properties such as tensile strength.
Claims (16)
알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체 20 내지 60중량%;를 포함하며,
상기 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체는
(A) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상을 포함하여 이루어진 시드;
(B) 상기 시드를 감싸고 알킬 아크릴레이트 단량체 및 폴리에틸렌계 가교제를 포함하여 이루어진 고무 코어; 및
(C) 상기 고무 코어를 감싸고 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상을 포함하여 이루어진 그라프트 쉘;을 포함하여 이루어지는 것을 특징으로 하는 열가소성 수지 조성물.40 to 80% by weight of vinyl cyan compound-vinylaromatic compound copolymer; And
20 to 60 wt% of an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer;
The alkyl acrylate-vinyl aromatic compound-vinyl cyan compound copolymer
(A) a seed comprising at least one member selected from the group consisting of a vinyl aromatic compound, a vinyl cyan compound and an alkyl acrylate;
(B) a rubber core surrounding the seed and comprising an alkyl acrylate monomer and a polyethylene-based crosslinker; And
(C) a graft shell surrounding the rubber core and comprising at least one selected from the group consisting of an aromatic vinyl compound and a vinyl cyan compound.
상기 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체는
알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조에 사용된 총 단량체 100중량부에 대하여,
(A) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상 4 내지 30중량부를 포함하여 이루어진 시드;
(B) 상기 시드를 감싸고 알킬 아크릴레이트 단량체 20 내지 80중량부 및 폴리에틸렌글리콜 디아크릴레이트, 폴리에틸렌글리콜 디메타크릴레이트, 폴리프로필렌글리콜 디아크릴레이트 및 폴리프로필렌글리콜 디메타크릴레이트로 이루어진 군으로부터 선택된 가교제 0.01 내지 3중량부를 포함하여 이루어진 고무 코어; 및
(C) 상기 고무 코어를 감싸고 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상 10 내지 70중량부 및 가교제 0.01 내지 3중량부를 포함하여 이루어진 가교된 그라프트 쉘;을 포함하여 이루어지는 것을 특징으로 하는 열가소성 수지 조성물.The method of claim 1,
The alkyl acrylate-vinyl aromatic compound-vinyl cyan compound copolymer
To 100 parts by weight of the total monomers used in the preparation of the alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer,
(A) a seed comprising 4 to 30 parts by weight of at least one selected from the group consisting of a vinyl aromatic compound, a vinyl cyan compound and an alkyl acrylate;
(B) an alkyl acrylate monomer surrounding the seed A rubber core comprising 20 to 80 parts by weight and 0.01 to 3 parts by weight of a crosslinking agent selected from the group consisting of polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, polypropylene glycol diacrylate and polypropylene glycol dimethacrylate; And
(C) a cross-linked graft shell surrounding the rubber core and comprising at least 10 to 70 parts by weight and 0.01 to 3 parts by weight of a crosslinking agent selected from the group consisting of aromatic vinyl compounds and vinyl cyan compounds; Thermoplastic resin composition.
상기 폴리에틸렌계 가교제는 폴리에틸렌글리콜 디아크릴레이트, 폴리에틸렌글리콜 디메타크릴레이트, 폴리프로필렌글리콜 디아크릴레이트 및 폴리프로필렌글리콜 디메타크릴레이트로 이루어진 군으로부터 1종 이상 선택되며 250 내지 1,000의 수평균분자량을 가지는 것을 특징으로 하는 열가소성 수지 조성물.The method of claim 1,
The polyethylene-based crosslinking agent is selected from the group consisting of polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, polypropylene glycol diacrylate and polypropylene glycol dimethacrylate and has a number average molecular weight of 250 to 1,000. Thermoplastic resin composition, characterized in that.
상기 폴리에틸렌계 가교제에 그라프팅제를 더 포함하며, 상기 그라프팅제는 알릴 메타크릴레이트, 트리알릴 이소시아누레이트, 트리알릴 아민 및 디알릴 아민으로 이루어진 군으로부터 1종 이상 선택되는 것을 특징으로 하는 열가소성 수지 조성물.The method of claim 1,
The polyethylene-based crosslinking agent further comprises a grafting agent, wherein the grafting agent is a thermoplastic resin, characterized in that at least one selected from the group consisting of allyl methacrylate, triallyl isocyanurate, triallyl amine and diallyl amine Composition.
상기 방향족 비닐 화합물은 스티렌, α-메틸스티렌, p-메틸스티렌 및 비닐톨루엔으로 이루어진 군으로부터 1종 이상 선택되는 것을 특징으로 하는 열가소성 수지 조성물.The method of claim 1, wherein
The aromatic vinyl compound is a thermoplastic resin composition, characterized in that at least one selected from the group consisting of styrene, α-methylstyrene, p-methylstyrene and vinyl toluene.
상기 비닐시안 화합물은 아크릴로니트릴, 메타크릴로니트릴 및 에타크릴로니트릴로 이루어진 군으로부터 1종 이상 선택되는 것을 특징으로 하는 열가소성 수지 조성물.The method of claim 1,
The vinyl cyan compound is at least one selected from the group consisting of acrylonitrile, methacrylonitrile and ethacrylonitrile.
상기 알킬아크릴레이트는 탄소수가 2 내지 8인 알킬기를 포함하는 것을 특징으로 하는 열가소성 수지 조성물.The method of claim 1,
The alkyl acrylate is a thermoplastic resin composition comprising an alkyl group having 2 to 8 carbon atoms.
(a) 비닐 방향족 화합물, 비닐시안 화합물 및 알킬 아크릴레이트로 이루어진 군으로부터 선택된 1종 이상 4 내지 30중량부를 포함하는 단량체 혼합물을 중합함으로써 시드를 제조하는 단계;
(b) 상기 시드의 존재하에 알킬 아크릴레이트 단량체 20 내지 80중량부 및 폴리에틸렌글리콜 디아크릴레이트, 폴리에틸렌글리콜 디메타크릴레이트, 폴리프로필렌글리콜 디아크릴레이트 및 폴리프로필렌글리콜 디메타크릴레이트로 이루어진 군으로부터 선택된 가교제 0.01 내지 3중량부를 포함하는 단량체 혼합물을 중합함으로써 고무 코어를 제조하는 단계; 및
(c) 상기 고무 코어의 존재하에 방향족 비닐 화합물 및 비닐시안 화합물로 이루어진 군으로부터 선택된 1종 이상 10 내지 70중량부를 포함하는 단량체 혼합물 및 가교제 0.01 내지 3중량부를 중합함으로써 가교된 그라프트 쉘을 제조하는 단계;를 포함하여 이루어지는 것을 특징으로 하는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법.To 100 parts by weight of the total monomers used in the preparation of the alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer,
(a) preparing a seed by polymerizing a monomer mixture comprising 4 to 30 parts by weight of at least one selected from the group consisting of a vinyl aromatic compound, a vinyl cyan compound and an alkyl acrylate;
(b) 20 to 80 parts by weight of alkyl acrylate monomer in the presence of said seed and selected from the group consisting of polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, polypropylene glycol diacrylate and polypropylene glycol dimethacrylate Preparing a rubber core by polymerizing a monomer mixture comprising 0.01 to 3 parts by weight of a crosslinking agent; And
(c) preparing a crosslinked graft shell by polymerizing a monomer mixture comprising 10 to 70 parts by weight of at least one selected from the group consisting of aromatic vinyl compounds and vinyl cyan compounds and 0.01 to 3 parts by weight of a crosslinking agent in the presence of the rubber core; Step; method of producing an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer comprising a.
상기 방향족 비닐 화합물은 스티렌, α-메틸스티렌, p-메틸스티렌 및 비닐톨루엔으로 이루어진 군으로부터 1종 이상 선택되는 것을 특징으로 하는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법.The method of claim 8,
The aromatic vinyl compound is a method for producing an alkylacrylate-vinylaromatic compound-vinyl cyan compound copolymer, characterized in that at least one selected from the group consisting of styrene, α-methylstyrene, p-methylstyrene and vinyl toluene.
상기 비닐시안 화합물은 아크릴로니트릴, 메타크릴로니트릴 및 에타크릴로니트릴로 이루어진 군으로부터 1종 이상 선택되는 것을 특징으로 하는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법.The method of claim 8,
The vinyl cyan compound is at least one selected from the group consisting of acrylonitrile, methacrylonitrile and ethacrylonitrile.
상기 알킬아크릴레이트는 탄소수가 2 내지 8인 알킬기를 포함하는 것을 특징으로 하는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법.The method of claim 8,
The alkyl acrylate is a method for producing an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer, characterized in that it comprises an alkyl group having 2 to 8 carbon atoms.
상기 (c)의 가교제는 디비닐벤젠, 에틸렌글리콜 디메타크릴레이트, 디에틸렌글리콜 디메타크릴레이트, 트리에틸렌글리콜 디메타크릴레이트, 1,3-부타디올 디메타크릴레이트, 에틸렌글리콜디아크릴레이트, 헥산디올에톡시레이트디아크릴레이트, 헥산디올에톡시레이트디아크릴레이트, 헥산디올프로폭시레이트 디아크릴레이트, 네오펜틸글리콜 디메타크릴레이트, 네오펜틸글리콜 에톡시레이트디아크릴레이트, 네오펜틸글리콜 프로폭시레이트디아크릴레이트, 트리메틸올프로판 트리메타크릴레이트, 트리메틸올메탄 트리아크릴레이트, 트리메틸프로판에톡시레이트 트리아크릴레이트, 트리메틸프로판프로폭시레이트 트리아크릴레이트, 펜타에리트리톨에톡시레이트 트리아크릴레이트, 펜타에리트로톨프로폭시레이트 트리아크릴레이트 및 비닐트리메톡시실란으로 이루어진 군으로부터 1종 이상 선택되는 것을 특징으로 하는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법.The method of claim 8,
The crosslinking agent of (c) is divinylbenzene, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, 1,3-butadiol dimethacrylate, ethylene glycol diacrylate , Hexanediol ethoxylate diacrylate, hexanediol ethoxylate diacrylate, hexanediol propoxylate diacrylate, neopentyl glycol dimethacrylate, neopentyl glycol ethoxylate diacrylate, neopentyl glycol pro Foxylate Diacrylate, Trimethylolpropane Trimethacrylate, Trimethylolmethane Triacrylate, Trimethyl Propane Ethoxylate Triacrylate, Trimethyl Propane Propoxylate Triacrylate, Pentaerythritol Ethoxylate Triacrylate, Penta Erythrotol Propoxylate Triacrylate and Vinyl Tree Ethoxy one alkyl acrylate, characterized in that more than species selected from the group consisting of silane-vinyl aromatic compound process for producing a vinyl cyan compound copolymer.
상기 (a)의 단량체 혼합물은 아크릴레이트-스티렌-아크릴로니트릴 공중합체의 제조에 사용된 총 단량체 100중량부에 대하여, 전해질 0.001 내지 1중량부, 가교제 0.01 내지 3중량부, 그라프팅제 0.01 내지 3중량부, 개시제 0.01 내지 3중량부 및 유화제 0.01 내지 5중량부를 더욱 포함하는 것을 특징으로 하는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법.The method of claim 8,
The monomer mixture of (a) is 0.001 to 1 parts by weight of the electrolyte, 0.01 to 3 parts by weight of the crosslinking agent, and 0.01 to 3 parts by weight of the grafting agent with respect to 100 parts by weight of the total monomers used to prepare the acrylate-styrene-acrylonitrile copolymer. A method for producing an alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer, further comprising: by weight, 0.01 to 3 parts by weight of initiator and 0.01 to 5 parts by weight of emulsifier.
상기 (b)의 단량체 혼합물은 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조에 사용된 총 단량체 100중량부에 대하여, 개시제 0.01 내지 3중량부 및 유화제 0.01 내지 5중량부를 더욱 포함하는 것을 특징으로 하는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법.The method of claim 8,
The monomer mixture of (b) further comprises 0.01 to 3 parts by weight of an initiator and 0.01 to 5 parts by weight of an emulsifier based on 100 parts by weight of the total monomers used in the preparation of the alkylacrylate-vinylaromatic compound-vinylcyan compound copolymer. Method for producing an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer, characterized in that.
상기 (c)의 단량체 혼합물은 아크릴레이트-스티렌-아크릴로니트릴 공중합체의 제조에 사용된 총 단량체 100중량부에 대하여, 개시제 0.01 내지 3중량부 및 유화제 0.01 내지 5중량부를 더욱 포함하는 것을 특징으로 하는 알킬아크릴레이트-비닐방향족 화합물-비닐시안 화합물 공중합체의 제조방법.The method of claim 8,
The monomer mixture of (c) further comprises 0.01 to 3 parts by weight of an initiator and 0.01 to 5 parts by weight of an emulsifier based on 100 parts by weight of the total monomers used in the preparation of the acrylate-styrene-acrylonitrile copolymer. Method for producing an alkyl acrylate-vinylaromatic compound-vinyl cyan compound copolymer.