KR20130078607A - Adhesive composition for polarizing plate - Google Patents
Adhesive composition for polarizing plate Download PDFInfo
- Publication number
- KR20130078607A KR20130078607A KR1020110147632A KR20110147632A KR20130078607A KR 20130078607 A KR20130078607 A KR 20130078607A KR 1020110147632 A KR1020110147632 A KR 1020110147632A KR 20110147632 A KR20110147632 A KR 20110147632A KR 20130078607 A KR20130078607 A KR 20130078607A
- Authority
- KR
- South Korea
- Prior art keywords
- crosslinking agent
- polarizer
- adhesive composition
- metal oxide
- polarizing plate
- Prior art date
Abstract
Description
본 발명은 편광판 접착제 조성물 및 이를 이용한 편광판에 관한 것이다. 보다 구체적으로 본 발명은 특정 가교제를 특정 비율로 도입하여 접착성이 우수할 뿐만 아니라, 양호한 외관으로 면내의 균일한 접착성을 가지며, 제품 합지부터 건조구간까지의 환경에서 소자의 크랙 발생을 줄일 수 있는 편광판 접착제 조성물 및 이를 이용한 편광필름에 관한 것이다.
The present invention relates to a polarizer adhesive composition and a polarizer using the same. More specifically, the present invention relates to a resin composition which is excellent in adhesiveness by introducing a specific crosslinking agent at a specific ratio, has a uniform appearance in a surface with good appearance, and can reduce the occurrence of cracks in an environment from the product laminator to the drying section And a polarizing film using the same.
편광판은 편광자와 1쌍의 보호필름을 접착제를 개재하여 합지한 다층판이다. The polarizing plate is a multilayer plate composed of a polarizer and a pair of protective films laminated via an adhesive.
편광자는 일반적으로 폴리비닐 알코올계 필름을 2색성 물질로 염색한 뒤 가교제를 이용하여 가교하고 1축 연신하여 얻어진다. 이러한 편광자는 연신 처리가 행해지기 때문에 수축하기 쉽고 폴리비닐 알코올이 친수성 폴리머이기 때문에 가습 조건에서 상당히 변형되기 쉽다. 이 때문에 필름의 기계적 강도를 높이기 위해 편광판의 양면 혹은 편면에 투명 보호 필름인 트리 아세틸 셀룰로오스 필름(Tri-acetylcellulose film)을 적층시켜 편광판을 제조한다. Polarizers are generally obtained by dyeing a polyvinyl alcohol-based film with a dichroic material and then crosslinking and uniaxially stretching using a crosslinking agent. Such a polarizer is susceptible to shrinkage because stretching treatment is performed, and polyvinyl alcohol is a hydrophilic polymer, so that it is likely to be significantly deformed under humidification conditions. For this reason, in order to increase the mechanical strength of the film, a polarizing plate is produced by laminating a triacetylcellulose film, which is a transparent protective film, on both sides or one side of the polarizing plate.
이 때 편광자와 투명 보호 필름과의 접착제 이용하는 편광판용 접착제로는 수용성 접착제가 사용되는데 주로 폴리비닐 알코올 수용액에 가교제를 혼합한 폴리비닐 알코올계 접착제가 사용되고 있다. 이러한 수용성 접착제는 투명 보호 필름과의 결합력이 충분하지 않을 경우 가습 조건 하에서 편광자와 투명 보호 필름과의 계면에서 벗겨짐이 발생하는 경우가 있다. At this time, a water-soluble adhesive is used as an adhesive for a polarizer using an adhesive between a polarizer and a transparent protective film, and a polyvinyl alcohol adhesive mainly comprising a polyvinyl alcohol aqueous solution and a crosslinking agent is used. Such a water-soluble adhesive may peel off at the interface between the polarizer and the transparent protective film under humidified conditions when the bonding strength with the transparent protective film is insufficient.
한편, 편광판을 제작하는데 있어서, 편광자와 투명 보호 필름을 상기 폴리비닐 알코올계 접착제를 이용하여 바르는 경우 외관 불량이 발생할 수 있는데 이러한 외관 불량에는 대표적으로 연신 방향으로의 줄이 발생하는 소자결(레코드성 수지)과 MD방향으로 소자가 파단되는 소자 크랙의 두 가지를 들 수 있다. 이러한 불량은 편광자와 투명 보호 필름이 롤에 의해 합지될 때 접착제의 두께 불안정이나 접착성의 불균일 및 이로 인한 외관의 불안정에 의해 발생하게 된다. On the other hand, when the polarizer and the transparent protective film are applied using the polyvinyl alcohol-based adhesive in the production of the polarizing plate, defective appearance may occur. Such defective appearance may be exemplified by the formation of a strip in the elongation direction Resin) and an element crack in which an element is broken in the MD direction. Such defects are caused by instability of the thickness of the adhesive when the polarizer and the transparent protective film are laminated by the roll, unevenness of the adhesiveness and instability of the appearance due to the unevenness of the adhesive.
이처럼 상기에 소개한 수용성 접착제의 내수성 및 접착제 두께 불안정에 따른 문제들에 대한 해결이 필요하다.
Thus, it is necessary to solve the problems caused by the water resistance of the water-soluble adhesive and the instability of the adhesive thickness.
본 발명의 하나의 목적은 소자크랙과 소자결을 함께 개선한 편광판 접착제 조성물을 제공하기 위한 것이다. It is an object of the present invention to provide a polarizer adhesive composition in which device cracks and device texture are improved together.
본 발명의 다른 목적은 내수성 및 접착제 두께 불안정에 따른 문제를 해소할 수 있는 편광판 접착제 조성물을 제공하기 위한 것이다. Another object of the present invention is to provide a polarizer adhesive composition capable of solving the problems caused by water resistance and adhesive thickness instability.
본 발명의 또 다른 목적은 접착성이 우수할 뿐만 아니라, 양호한 외관으로 면내의 균일한 접착성을 가지며, 제품 합지부터 건조구간까지의 환경에서 소자의 크랙 발생을 줄일 수 있는 편광판 접착제 조성물을 제공하기 위한 것이다. Another object of the present invention is to provide a polarizer adhesive composition which not only exhibits excellent adhesiveness but also has a uniform appearance in a surface with good appearance and can reduce the occurrence of cracks of the device in an environment from the product lid to the dry section .
본 발명의 또 다른 목적은 편광자와 보호필름간에 밀착력이 우수한 편광판 접착제 조성물을 제공하기 위한 것이다. It is still another object of the present invention to provide a polarizer adhesive composition excellent in adhesion between a polarizer and a protective film.
본 발명의 또 다른 목적은 상기 편광판 접착제 조성물을 이용한 편광판을 제공하기 위한 것이다.
It is still another object of the present invention to provide a polarizing plate using the polarizer adhesive composition.
본 발명의 하나의 관점은 편광판 접착제 조성물에 관한 것이다. 한 구체예에서 상기 편광판 접착제 조성물은 폴리비닐알코올계 수지; 제1가교제와 제2가교제를 포함하는 가교제; 및 금속산화물을 포함하고, 상기 제1가교제는 글리옥살이며, 상기 제2 가교제는 무기 가교제이고, 상기 제1가교제와 상기 제2 가교제의 중량비는 1: 2~4 : 1인 것을 특징으로 한다. One aspect of the present invention relates to a polarizer adhesive composition. In one embodiment, the polarizer adhesive composition comprises a polyvinyl alcohol-based resin; A crosslinking agent comprising a first crosslinking agent and a second crosslinking agent; And a metal oxide, wherein the first crosslinking agent is glyoxal, the second crosslinking agent is an inorganic crosslinking agent, and the weight ratio of the first crosslinking agent to the second crosslinking agent is 1: 2 to 4: 1.
다른 구체예에서 상기 편광판 접착제 조성물은 폴리비닐알코올계 수지, 가교제 및 금속 산화물을 포함하고, 85 ℃에서 측정한 모듈러스가 500MPa 이상인 것을 특징으로 한다. In another embodiment, the polarizer adhesive composition comprises a polyvinyl alcohol-based resin, a crosslinking agent, and a metal oxide, and has a modulus measured at 85 캜 of 500 MPa or more.
상기 무기 가교제는 붕산, 붕사를 포함하는 붕소 화합물; 클로로히드록시옥소지르코늄, 질산지르코닐을 포함하는 지르코늄 화합물; 테트라 알콕시치터네이트,수용성 티타늄 화합물을 포함하는 티타늄 화합물; 황산알루미늄, 염화알루미늄, 질산알루미늄을 포함하는 알루미늄 화합물; 아인산에스테르, 비스페놀A 변성 폴리인산을 포함하는 인산 화합물; 알콕시기 또는 글리시딜기를 포함하는 반응성 작용기를 갖는 실리콘화합물로 이루어진 군으로부터 1종 이상 포함할 수 있다. Wherein the inorganic cross-linking agent is selected from the group consisting of a boron compound including boric acid and borax; Zirconium compounds including chlorohydroxyoxo zirconium, zirconyl nitrate; A titanium compound including a tetraalkoxy diterate, a water-soluble titanium compound; Aluminum compounds including aluminum sulfate, aluminum chloride and aluminum nitrate; Phosphoric acid ester, bisphenol A-modified polyphosphoric acid; An alkoxy group or a silicon compound having a reactive functional group containing a glycidyl group.
상기 금속산화물은 산화 지르코늄, 산화 규소, 산화알루미늄, 산화아연 및 산화티타늄으로 이루어진 군으로부터 1종 이상 포함할 수 있다. The metal oxide may include at least one selected from the group consisting of zirconium oxide, silicon oxide, aluminum oxide, zinc oxide, and titanium oxide.
상기 금속산화물은 평균입경이 10 내지 100 nm 일 수 있다. The metal oxide may have an average particle diameter of 10 to 100 nm.
상기 가교제 총 함량과 상기 금속 화합물의 중량비는 1: 1.8~1: 3일 수 있다. The total content of the crosslinking agent and the weight ratio of the metal compound may be 1: 1.8 to 1: 3.
상기 편광판 접착제 조성물은 고형분 기준으로 폴리비닐알코올계 수지 100 중량부에 대하여, 가교제 10~40 중량부 및 금속산화물 20~150 중량부로 포함할 수 있다. The polarizer adhesive composition may include 10 to 40 parts by weight of a crosslinking agent and 20 to 150 parts by weight of a metal oxide based on 100 parts by weight of a polyvinyl alcohol-based resin on a solid basis.
본 발명의 다른 관점은 상기 편광판 접착제 조성물을 이용한 편광판에 관한 것이다. 상기 편광판은 편광자; 및 상기 편광판 접착제 조성물을 매개로 하여 상기 편광자의 일면 또는 양면에 접착된 보호 필름을 포함한다.
Another aspect of the present invention relates to a polarizing plate using the polarizing plate adhesive composition. Wherein the polarizer comprises a polarizer; And a protective film adhered to one surface or both surfaces of the polarizer through the polarizer adhesive composition.
본 발명은 소자크랙과 소자결을 함께 개선하고, 내수성 및 접착제 두께 불안정에 따른 문제를 해소할 수 있으며, 접착성이 우수할 뿐만 아니라, 양호한 외관으로 면내의 균일한 접착성을 가지며, 제품 합지부터 건조구간까지의 환경에서 소자의 크랙 발생을 줄일 수 있고 편광자와 보호필름간에 밀착력이 우수한 편광판 접착제 조성물 및 이를 이용한 편광판을 제공하는 발명의 효과를 갖는다.
It is an object of the present invention to improve the device crack and element texture together, to solve the problem caused by the water resistance and unstable thickness of the adhesive, to have excellent adhesiveness, to have uniform adhesiveness in the surface with good appearance, The present invention has the effect of providing a polarizer adhesive composition and a polarizer using the same that can reduce the occurrence of cracks in an environment up to the drying zone and has an excellent adhesion between the polarizer and the protective film.
도 1은 본 발명의 하나의 구체예에 따른 편광판의 단면도이다. 1 is a cross-sectional view of a polarizing plate according to one embodiment of the present invention.
본 발명의 편광판 접착제 조성물은 폴리비닐알코올계 수지, 가교제 및 금속 산화물을 포함한다. 이하, 본 발명의 각 성분에 대해 하기에 상세히 설명한다.
The polarizer adhesive composition of the present invention comprises a polyvinyl alcohol-based resin, a crosslinking agent and a metal oxide. Hereinafter, each component of the present invention will be described in detail below.
(A) 폴리비닐알코올계 수지(A) a polyvinyl alcohol-based resin
상기 폴리비닐알코올계 수지는 아세트아세틸기를 함유하는 변성 폴리비닐알코올계 수지를 사용할 수 있다. As the polyvinyl alcohol-based resin, a modified polyvinyl alcohol-based resin containing an acetacetyl group can be used.
구체예에서 상기 폴리비닐알코올계 수지는 평균중합도가 100~5000, 바람직하게는 1000~3000 일 수 있다. 상기 범위에서 우수한 접착성을 갖는다. In an embodiment, the polyvinyl alcohol resin may have an average degree of polymerization of 100 to 5,000, preferably 1,000 to 3,000. And has excellent adhesiveness in the above range.
또한 상기 폴리비닐알코올계 수지는 검화도가 85몰%~99.9몰%, 바람직하게는 90몰%~95 몰% 일 수 있다. 상기 범위 내에서, 접착제의 결정화도 향상에 의한 응집 에너지 향상 및 계면결합의 활성을 기대할 수 있다. The degree of saponification of the polyvinyl alcohol-based resin may be 85 mol% to 99.9 mol%, preferably 90 mol% to 95 mol%. Within the above range, it is expected that the cohesion energy can be improved by the improvement of the degree of crystallization of the adhesive and the activity of interfacial bonding.
상기 폴리비닐알코올계 수지는 아세트아세틸기를 5~50몰%로 포함하는 변성 폴리비닐알코올계 수지가 바람직하다. 상기 범위 내에서 수용성 가교제와의 반응이 원활할 수 있으며, 접착제 내수성이 우수하다.
The polyvinyl alcohol-based resin is preferably a modified polyvinyl alcohol-based resin containing 5 to 50 mol% of an acetacetyl group. The reaction with the water-soluble crosslinking agent can be performed smoothly within the above range, and the water resistance of the adhesive is excellent.
(B) 가교제(B) crosslinking agent
본 발명의 가교제는 제1가교제와 제2가교제의 2종 이상을 사용한다. The crosslinking agent of the present invention uses two or more kinds of the first crosslinking agent and the second crosslinking agent.
상기 제1 가교제로는 글리옥살이 사용되며, 상기 제2 가교제는 무기 가교제가 사용될 수 있다. As the first crosslinking agent, glyoxal may be used, and as the second crosslinking agent, an inorganic crosslinking agent may be used.
상기 무기 가교제의 예로는 붕산, 붕사를 포함하는 붕소 화합물; 클로로히드록시옥소지르코늄, 질산지르코닐을 포함하는 지르코늄 화합물; 테트라 알콕시치터네이트,수용성 티타늄 화합물을 포함하는 티타늄 화합물; 황산알루미늄, 염화알루미늄, 질산알루미늄을 포함하는 알루미늄 화합물; 아인산에스테르, 비스페놀A 변성 폴리인산을 포함하는 인산 화합물; 알콕시기 또는 글리시딜기를 포함하는 반응성 작용기를 갖는 실리콘화합물 등을 들 수 있다. 이들은 단독 또는 2종 이상 혼합하여 사용될 수 있다. Examples of the inorganic crosslinking agent include boron compounds including boric acid and borax; Zirconium compounds including chlorohydroxyoxo zirconium, zirconyl nitrate; A titanium compound including a tetraalkoxy diterate, a water-soluble titanium compound; Aluminum compounds including aluminum sulfate, aluminum chloride and aluminum nitrate; Phosphoric acid ester, bisphenol A-modified polyphosphoric acid; A silicon compound having a reactive functional group containing an alkoxy group or a glycidyl group, and the like. These may be used alone or in combination of two or more.
본 발명에서는 상기 제1가교제와 상기 제2 가교제의 중량비는 1: 2~4 : 1인 것을 특징으로 한다. 상기 범위에서 우수한 모듈러스와 접착력 및 내수성을 가질 수 있다. In the present invention, the weight ratio of the first crosslinking agent to the second crosslinking agent is 1: 2 to 4: 1. In the above range, it can have excellent modulus, adhesion and water resistance.
본 발명에서 상기 가교제는 (A) 폴리비닐알코올계 수지 100 중량부에 대하여 10~40 중량부로 사용될 수 있다. 상기 범위에서 내구성과 가공성이 우수하다. 바람직하게는 15~35 중량부이다.
In the present invention, the crosslinking agent may be used in an amount of 10 to 40 parts by weight based on 100 parts by weight of the polyvinyl alcohol resin (A). In the above range, durability and workability are excellent. And preferably 15 to 35 parts by weight.
(C)금속산화물(C) a metal oxide
상기 금속산화물은 물에 분산시켜 분산액으로 사용할 수 있다. 상기 금속 산화물은 접착제 가교를 제한하고 접착제 분자쇄 간 슬립 발생을 용이하게 한다. The metal oxide may be dispersed in water and used as a dispersion. The metal oxide restricts the crosslinking of the adhesive and facilitates the occurrence of slip between the adhesive molecular chains.
구체예에서 상기 금속산화물은 물에 금속산화물 입자를 배합한 후 교반 분산시켜 사용할 수 있다. 상기 물과 금속 산화물입자의 배합비는 중량비로 5 : 1 ~ 20 : 1 일 수 있다. 예를 들면, 볼밀, 페인트쉐이커, 비드밀, 호모게나이저, 소니케이터, 고속교반기 등을 이용하여 교반 분산시킬 수 있다. 이때 입자의 재응집을 방지하기 위해 계면활성제가 더 포함될 수 있다. 상기 계면활성제로는 BYK-191, D-2015(이상 BYK), Dis-752W, Dis-755W(이상 Tego), EFKA-4585, EFKA-5440(이상 EFKA), OROTAN731A(이상 Rohm&Haas) 등이 사용될 수 있다. 상기 계면활성제는 금속산화물 입자 100 중량부를 기준으로 5~100 중량부 정도를 사용할 수 있다. 상기 범위에서 입자간 적절한 반발력으로 안정하게 분산되는 장점이 있다. In an embodiment, the metal oxide may be used after mixing the metal oxide particles with water, followed by stirring and dispersing. The mixing ratio of the water and the metal oxide particles may be 5: 1 to 20: 1 by weight. For example, it can be stirred and dispersed using a ball mill, a paint shaker, a bead mill, a homogenizer, a sonicator, and a high-speed stirrer. At this time, a surfactant may be further added to prevent re-aggregation of the particles. DISK 755W (more than Tego), EFKA-4585, EFKA-5440 (more than EFKA) and OROTAN 731A (Rohm & Haas) can be used as the surfactant. have. The surfactant may be used in an amount of about 5 to 100 parts by weight based on 100 parts by weight of the metal oxide particles. There is an advantage that the particles are stably dispersed with appropriate repulsion between particles in the above range.
구체예에서, 상기 금속산화물의 금속산화물은 평균입자직경(D50)이 10~100 nm, 바람직하게는 12~50 nm 일 수 있다. 상기 범위에서 크랙결함을 최소화할 수 있다. In an embodiment, the metal oxide of the metal oxide may have an average particle diameter (D50) of 10 to 100 nm, preferably 12 to 50 nm. In this range, crack defects can be minimized.
상기 금속산화물은 산화 지르코늄, 산화규소, 산화알루미늄, 산화아연 및 산화티타늄 등이 사용될 수 있다. 이들은 단독 또는 2종 이상 혼합하여 사용될 수 있다. The metal oxide may be zirconium oxide, silicon oxide, aluminum oxide, zinc oxide, titanium oxide, or the like. These may be used alone or in combination of two or more.
본 발명에서 상기 금속산화물은 (A) 폴리비닐알코올계 수지 100 중량부에 대하여 20~150 중량부로 사용될 수 있다. 상기 범위에서 밀착력과 접착성이 우수하고 크랙결함을 최소화할 수 있다. In the present invention, the metal oxide may be used in an amount of 20 to 150 parts by weight based on 100 parts by weight of the polyvinyl alcohol resin (A). In this range, the adhesive force and adhesive property are excellent and crack defects can be minimized.
구체예에서는 상기 가교제 총 함량과 상기 금속 화합물의 중량비는 1: 1.8~1: 3일 수 있다. 이 경우 보다 우수한 내수 접착력과 보관 안정성을 확보할 수 있다.
In an embodiment, the total content of the crosslinking agent and the weight ratio of the metal compound may be 1: 1.8 to 1: 3. In this case, it is possible to secure better water-resistance and storage stability.
상기 편광판 접착제 조성물은 폴리비닐알코올 수용액에 가교제를 투입하고, 여기에 금속산화물을 교반하면서 투입하여 제조될 수 있다. The polarizer adhesive composition may be prepared by charging a cross-linking agent into a polyvinyl alcohol aqueous solution and adding the metal oxide thereto while stirring.
본 발명의 다른 관점은 상기 편광판 접착제 조성물을 포함하는 편광판에 관한 것이다. Another aspect of the present invention relates to a polarizing plate comprising the polarizing plate adhesive composition.
상기 편광판 접착제 조성물은 보호필름 - 접착제 - 편광자 - 접착제 - 보호필름의 순서로 합지하여 제조 조건에 따라 건조 오븐에서 건조 하여 제작한다The polarizer adhesive composition is prepared by laminating in the order of a protective film-adhesive-polarizer-adhesive-protective film and drying in a drying oven according to the production conditions
도 1은 본 발명의 하나의 구체예에 따른 편광판의 단면도이다. 도시된 바와같이 본 발명의 편광판은 제1보호필름(11), 제1 접착층(12), 편광자 (13), 제2 접착층(14) 및 제2 보호필름(15)이 순차적으로 적층된 구조를 갖는다. 1 is a cross-sectional view of a polarizing plate according to one embodiment of the present invention. As shown in the figure, the polarizer of the present invention has a structure in which a first
구체예에서, 상기 편광판 접착제 조성물은 85 ℃에서 측정한 모듈러스가 500MPa 이상, 예를 들면 600~10,000 MPa 일 수 있다. 이처럼 본 발명의 편광판 접착제 조성물은 특정 가교제를 특정 비율로 적용함으로서, 우수한 모듈러스를 확보할 수 있는 것이다. In an embodiment, the polarizer adhesive composition may have a modulus of at least 500 MPa, for example 600 to 10,000 MPa, measured at 85 캜. As described above, the polarizer adhesive composition of the present invention can secure a good modulus by applying a specific crosslinking agent at a specific ratio.
구체예에서 상기 제1 및 제2 접착층의 두께는 50 내지 300 nm 일 수 있다. 본 발명의 접착제 조성물을 이용해 형성한 접착층은 금속 산화물이 균일하게 분산된 구조를 갖는다. In embodiments, the thickness of the first and second adhesive layers may be between 50 and 300 nm. The adhesive layer formed using the adhesive composition of the present invention has a structure in which the metal oxide is uniformly dispersed.
이하, 실시예를 통하여 본 발명을 보다 구체적으로 설명하고자 하나, 이러한 실시예들은 단지 설명의 목적을 위한 것으로 본 발명을 제한하는 것으로 해석되어서는 안 된다.
Hereinafter, the present invention will be described in more detail with reference to examples, but these examples are for illustrative purposes only and should not be construed as limiting the present invention.
실시예Example
실시예 및 비교예에서 사용된 각 성분의 사양은 다음과 같다;The specifications of each component used in Examples and Comparative Examples are as follows;
(A) PVA : 일본합성화학 공업(주), 상품명 [고세파이마 Z-200], 평균 중합도 : 1200, 검화도 : 98.5몰 mol%, 아세트아세틸(acetylaceto)화 : 5몰%(A) PVA: Nippon Synthetic Chemical Industry Co., Ltd. [Koshefima Z-200], average degree of polymerization: 1200, degree of saponification: 98.5 mol%, acetylaceto:
(B)가교제(B) cross-linking system
(B1)제1가교제 : 글리옥살(10%, water solution, 일본합성화학 공업(주))(B1) First crosslinking agent: glyoxal (10%, water solution, manufactured by Nippon Synthetic Chemical Industry Co., Ltd.)
(B2)제2가교제 : Zircosol-ZN(25%, Water Solution, 제일희원소화학공업)(B2) Second crosslinking agent: Zircosol-ZN (25%, Water Solution, produced by Cheil Industries, Ltd.)
(C)금속산화물 :Aluminium Oxide(Al2O3 Nano Particle, China, 평균 입자직경 : 12㎚ )
(C) Metal oxide: Aluminum Oxide (Al 2 O 3 Nano Particle, China, average particle diameter: 12 nm)
실시예Example 1 One
반응기에 상온수 950ml을 넣고 교반을 하면서 PVA (A) 50g을 서서히 투입하였다. 반응기 온도를 90℃까지 상승시킨 후 2시간 용해 후 서서히 냉각시켜 변성폴리비닐알콜 5% 수용액을 제조하였다. 950 ml of warm water was added to the reactor, and 50 g of PVA (A) was slowly added while stirring. The temperature of the reactor was raised to 90 ° C, and after dissolving for 2 hours, the solution was gradually cooled to prepare a 5% aqueous solution of modified polyvinyl alcohol.
이와 별도로 상온수 900ml와 Aluminium Oxide(Al2O3 Nano Particle, China) (C1) 100g을 배합하여 볼밀을 이용하여 충분히 교반 분산 시켜 금속산화물 분산액을 제조하였다. Separately, 900 ml of room temperature water and Aluminum Oxide (Al 2 O 3 Nano Particle, China) (C1) were mixed and thoroughly stirred and dispersed using a ball mill to prepare a metal oxide dispersion.
상기에서 제조된 변성폴리비닐알콜 수용액에 가교제로 글리옥살(B1)과 Zircosol-ZN(B2)을 잘 교반하며 투입하여 혼합용액을 제조하고, 상기 혼합용액에 상기에서 제조된 금속 화합물 필러를 교반하면서 투입하여 편광판 접착제 조성물을 제조하였다.
The mixed solution was prepared by adding glyoxal (B1) and Zircosol-ZN (B2) as a crosslinking agent to the aqueous solution of the modified polyvinyl alcohol prepared above with stirring, and the metal compound filler prepared above was stirred in the mixed solution To prepare a polarizer adhesive composition.
실시예Example 2~9 2 to 9
금속산화물의 종류 및 배합량을 하기 표 1과 같이 변경하여 투입한 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다.
Except that the kind and the compounding amount of the metal oxide were changed as shown in the following Table 1 and the addition was carried out.
비교예Comparative example 1 One
글리옥살을 적용하지 않은 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다.
The procedure of Example 1 was repeated except that glyoxal was not applied.
비교예Comparative example 2 2
무기 가교제를 적용하지 않은 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다.
The procedure of Example 1 was repeated except that the inorganic crosslinking agent was not used.
비교예Comparative example 3 3
글리옥살과 무기가교제의 비율을 변경한 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다.
The procedure of Example 1 was repeated except that the ratio of glyoxal to inorganic crosslinking agent was changed.
상기 실시예 및 비교예에서 제조된 편광판 접착제 조성물을 편광판과 보호필름 사이에 개재시켜 보호필름 - 접착제 - 편광자 - 접착제 - 보호필름의 순서로 합지하였다. 합지된 필름을 건조 오븐에서 건조하여 편광판을 제조하였다. 상기 사용된 편광자 및 보호필름은 하기의 것을 사용하였다. The polarizer adhesive compositions prepared in the above Examples and Comparative Examples were interposed between the polarizing plate and the protective film and laminated in the order of the protective film-adhesive-polarizer-adhesive-protective film. The laminated film was dried in a drying oven to prepare a polarizing plate. The following polarizer and protective film were used.
(1) 편광자 : 기재필름으로 80 ㎛ 두께의 폴리비닐알코올 필름(검화도:99.5, 중합도:2000)을 사용하였으며, 상기 기재필름을 0.3% 요오드 수용액에 침지시켜 염착한 후, 연신배율이 5.0이 되도록 연신하였다. 이어서 연신된 기재필름을 3% 농도의 붕산 용액과 2% 요오드화 칼륨 수용액에 침지시켜 색상 보정을 한 후, 40 ℃에서 3분간 건조하여 제조하였다.(1) Polarizer: A polyvinyl alcohol film (degree of saponification: 99.5, degree of polymerization: 2000) having a thickness of 80 탆 was used as a base film. The base film was immersed in an aqueous 0.3% iodine solution and salt- . Subsequently, the stretched substrate film was immersed in a 3% boric acid solution and a 2% potassium iodide aqueous solution to perform color correction, followed by drying at 40 ° C for 3 minutes.
(2) 투명 보호필름: 투명 보호필름으로 80 ㎛ 두께의 트리아세테이트 셀룰로오스(TAC)를 사용하였으며, 0.1 N 농도의 수산화나트륨 수용액에 50 ℃에서 2분 30초간 침지시켜 비누화 공정을 수행하여 제조하였다.(2) Transparent Protective Film: Triacetate cellulose (TAC) having a thickness of 80 탆 was used as a transparent protective film, and the film was immersed in an aqueous sodium hydroxide solution at a concentration of 0.1 N for 2 minutes and 30 seconds at 50 캜 for saponification.
(3) 편광판 제작 : 상기 보호 필름의 편면에, 실시예 1~9 및 비교예 1~3의 접착제 조성물을 건조 후의 접착제층의 두께가 80nm가 되도록 도포하였다. 접착제의 도포 후 23℃의 온도 조건에서 편광자의 양면에 접착제가 부착된 투명 보호 필름을 롤로 접착시킨 후, 55℃에서 6분간 건조시켜 편광판을 제조하였다. (3) Preparation of polarizing plate: The adhesive compositions of Examples 1 to 9 and Comparative Examples 1 to 3 were applied to one side of the protective film so that the thickness of the dried adhesive layer became 80 nm. After application of the adhesive, a transparent protective film having an adhesive attached to both sides of the polarizer was adhered with a roll at a temperature condition of 23 캜, and dried at 55 캜 for 6 minutes to prepare a polarizing plate.
제조된 편광판에 대하여 하기의 방법으로 물성을 평가하였다. 평가 결과는 표 2에 나타내었다.
The properties of the prepared polarizing plate were evaluated by the following methods. The evaluation results are shown in Table 2.
1) 외관평가(Crack 결함) : 제조된 편광판을 1000㎜ x 1000㎜가 되도록 준비한다. 샘플을 형광등아래의 반사모드 및 Back Light 모드에서 MD 방향으로의 편광자 Crack이 발생하였는지를 확인하여 그 개수를 측정하여 결함 여부를 check하였다.1) Appearance evaluation (Crack defect): Prepare the prepared polarizing plate so as to have a size of 1000 mm x 1000 mm. The sample was checked for polarizer cracks in the MD direction in the reflection mode under the fluorescent lamp and in the back light mode, and the number of defects was checked by measuring the number.
- 0 ~ 5개 : O- 0 to 5: O
- 5개 초과 : X- More than 5: X
2) 밀착력: 단부의 보호필름과 편광자의 사이에 커터 칼끝을 삽입하였다. 밀착력이 부족한 경우 편광자와 보호필름 사이가 벌어지게 되며 밀착력이 양호한 경우 편광자나 보호필름이 파단이 되었다. 2) Adhesion force: A cutter tip was inserted between the protective film at the end and the polarizer. In the case of insufficient adhesion, the polarizer and the protective film are opened. If the adhesion is good, the polarizer or protective film is broken.
3) 내수 접착력 : 편광판을 편광자의 흡수 축방향으로 50mm, 흡수축에 직교하는 방향으로 50mm 크기로 자르고 각 샘플을 60℃, 95% RH의 내열-내습 분의기 하에 120시간 방치하였다. 이 때, 소자/보호필름 사이에 박리 정도를 비교하였다.3) Water-resistant adhesive force: The polarizing plate was cut into a size of 50 mm in the direction of the absorption axis of the polarizer and 50 mm in the direction orthogonal to the absorption axis, and each sample was left for 120 hours under the conditions of heat and humidity resistant at 60 캜 and 95% RH. At this time, the degree of peeling between the element / protective film was compared.
- 박리가 발생하지 않는 경우 O- O if peeling does not occur
- 단부가 뜨는 경우는 △- When the end is rising △
- 전부 벗겨진 경우 X - When all stripped X
4)보관 안정성 : Brookfield 점도계(LDVD-II)로 액의 분산제조 후부터 점도가 50% 이상 상승하는 시점(가사시간의 기준)을 측정하였다. 4) Storage stability: The time point at which the viscosity increased by 50% or more (based on the pot life time) was measured after the dispersion of the liquid by a Brookfield viscometer (LDVD-II).
5) 모듈러스(MPa) : 수용액 상태의 접착제를 상온에서 3일동안 방치/건조하여 50㎛ 두께의 필름 시트로 제작 후 폭 5mm, 길이 20mm의 시편으로 제작하여 Rheometer(Seiko Instrument Inc. DMS6100)를 이용하여 30℃부터 100℃까지(승온온도 : 10℃/min) Temp. sweep test를 진행하여 85℃에서의 저장탄성률을 측정하였다.5) Modulus (MPa): Adhesive in aqueous solution was left to stand for 3 days at room temperature and dried to produce a film sheet of 50 μm thickness. The specimen was 5 mm in width and 20 mm in length and was measured using Rheometer (Seiko Instrument Inc. DMS6100) 30 ° C to 100 ° C (temperature elevation temperature: 10 ° C / min). sweep test was conducted to measure the storage elastic modulus at 85 ° C.
6) 투습도(g/m2*24hr) : 수용액 상태의 접착제를 상온에서 3일동안 방치/건조하여 50㎛ 두께의 필름 시트로 제작하여 지름이 60mm인 원형 시편으로 제작하여 KS K0594 중 A-1 방법으로 접착제 필름을 통해 투과해서 수분이 흡습된 양을 측정하였다.
6) Water vapor permeability (g / m 2 * 24hr): The adhesive in aqueous solution was left to stand for 3 days at room temperature and dried to prepare a 50 ㎛ thick film sheet. The film was made into a circular specimen with a diameter of 60 mm. The amount of moisture absorbed through the adhesive film was measured.
(g/m2*24hr)Moisture permeability
(g / m 2 * 24 hr)
상기 표 2에 나타난 바와 같이 실시예 1~4에서 제조된 편광판 접착제 조성물은 크랙결함이 없으며 밀착력, 내수접착력, 보관 안정성, 모듈러스 및 투습도가 우수한 것을 알 수 있다. 이에 비해 비교예 1은 내수 접착력이 저하되었으며, 비교예 2는 모듈러스 저하에 따른 제품의 외관 성능이 떨어진 것을 확인할 수 있다. 또한 제1 가교제와 제2 가교제간 비율이 본 발명의 범위를 벗어난 비교예 3의 경우 내수 접착력이 저하되었을 뿐만 아니라 보관 안정성도 떨어짐을 알 수 있다.
As shown in Table 2, the polarizer adhesive compositions prepared in Examples 1 to 4 had no crack defects and excellent adhesion, water resistance, storage stability, modulus and moisture permeability. On the contrary, in Comparative Example 1, the water-resistant adhesive strength was lowered, and in Comparative Example 2, the appearance of the product deteriorated due to the modulus deterioration. In addition, in Comparative Example 3 in which the ratio between the first crosslinking agent and the second crosslinking agent was out of the range of the present invention, not only the water resistance of the water-resistance was lowered but also the storage stability was lowered.
본 발명은 상기 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 제조될 수 있으며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야 한다.
It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the following claims. As will be understood by those skilled in the art. It is therefore to be understood that the embodiments described above are in all respects illustrative and not restrictive.
11 : 제1 보호필름 12 : 제1접착층
13 : 편광자 14 : 제2접착층
15 : 제2 보호필름 11: first protective film 12: first adhesive layer
13: Polarizer 14: Second adhesive layer
15: second protective film
Claims (8)
제1가교제와 제2가교제를 포함하는 가교제; 및
금속산화물;
을 포함하고, 상기 제1가교제는 글리옥살이며, 상기 제2 가교제는 무기 가교제이고, 상기 제1가교제와 상기 제2 가교제의 중량비는 1: 2 ~ 4 : 1인 것을 특징으로 하는 편광판 접착제 조성물.
Polyvinyl alcohol-based resin;
A crosslinking agent comprising a first crosslinking agent and a second crosslinking agent; And
Metal oxides;
Wherein the first crosslinking agent is glyoxal, the second crosslinking agent is an inorganic crosslinking agent, and the weight ratio of the first crosslinking agent to the second crosslinking agent is 1: 2 to 4: 1.
85 ℃에서 측정한 모듈러스가 500MPa 이상인 편광판 접착제 조성물.
A polyvinyl alcohol-based resin, a crosslinking agent, and a metal oxide,
And a modulus measured at 85 캜 of 500 MPa or more.
The method of claim 1, wherein the inorganic cross-linking agent is selected from the group consisting of a boron compound including boric acid and borax; Zirconium compounds including chlorohydroxyoxo zirconium, zirconyl nitrate; A titanium compound including a tetraalkoxy diterate, a water-soluble titanium compound; Aluminum compounds including aluminum sulfate, aluminum chloride and aluminum nitrate; Phosphoric acid ester, bisphenol A-modified polyphosphoric acid; And a silicone compound having a reactive functional group containing an alkoxy group or a glycidyl group.
3. The polarizer adhesive composition according to any one of claims 1 to 2, wherein the metal oxide comprises at least one selected from the group consisting of zirconium oxide, silicon oxide, aluminum oxide, zinc oxide and titanium oxide.
The polarizer adhesive composition according to any one of claims 1 to 2, wherein the metal oxide has an average particle diameter of 10 to 100 nm.
The polarizer adhesive composition according to any one of claims 1 to 2, wherein the total content of the crosslinking agent and the weight ratio of the metal compound is 1: 1.8 to 1: 3.
The polarizer adhesive composition according to any one of claims 1 to 2, wherein the polarizer adhesive composition comprises 10 to 40 parts by weight of a crosslinking agent and 20 to 150 parts by weight of a metal oxide based on 100 parts by weight of a polyvinyl alcohol based resin on a solid basis By weight based on the total weight of the composition.
제1항 내지 제2항중 어느 한 항의 편광판 접착제 조성물을 매개로 하여 상기 편광자의 일면 또는 양면에 접착된 보호 필름을 포함하는 편광판.
A polarizer; And
A polarizer comprising a protective film adhered to one or both sides of the polarizer through the polarizer adhesive composition of any one of claims 1 to 2.