KR20130002154A - Manufacturing of hybrid composites encapsulating the magnetic particles - Google Patents
Manufacturing of hybrid composites encapsulating the magnetic particles Download PDFInfo
- Publication number
- KR20130002154A KR20130002154A KR1020110063214A KR20110063214A KR20130002154A KR 20130002154 A KR20130002154 A KR 20130002154A KR 1020110063214 A KR1020110063214 A KR 1020110063214A KR 20110063214 A KR20110063214 A KR 20110063214A KR 20130002154 A KR20130002154 A KR 20130002154A
- Authority
- KR
- South Korea
- Prior art keywords
- iron oxide
- polymer
- particles
- acrylate
- solvent
- Prior art date
Abstract
Description
본 발명은 라디칼 중합을 통하여 생성된 고분자 입자를 빈용매에 분산 및 용해시킨 후 산화철 나노입자를 도입하여 이를 함께 냉각하는 과정을 통해 자성입자가 내부에 캡슐화된 안정한 하이브리드 구상입자를 제조하는 방법에 관한 것이다.
The present invention relates to a method for producing stable hybrid spherical particles in which magnetic particles are encapsulated inside by dispersing and dissolving the polymer particles produced through radical polymerization in a poor solvent and introducing iron oxide nanoparticles and cooling them together. will be.
산화철 나노입자는 강자성체로서 현재 데이터 저장, 전자파 차폐, 자기공명 영상 조영제, 약물 전달 시스템 등의 다양한 응용분야에서 널리 쓰이고 있다. Iron oxide nanoparticles are ferromagnetic materials and are widely used in various applications such as data storage, electromagnetic shielding, magnetic resonance imaging contrast agents, and drug delivery systems.
고분자와 산화철을 이용하여 하이브리드 입자를 제조하는 방법은 다양하게 연구되어 왔지만, 산화철 전처리 과정을 거쳐 이러한 입자를 고분자 중합과정에 도입하는 것이 대부분이었다. 그러나 상기 방법의 경우 산화철의 전처리 과정이 복잡하거나, 다양한 크기의 하이브리드 입자를 수득하는 것이 어렵다는 단점이 있다. 또한 하이브리드 입자 합성 실패 시 중합과정을 처음부터 다시 진행해야 함으로써 추가적인 비용을 부담해야 한다.Various methods for producing hybrid particles using polymers and iron oxide have been studied, but most of these particles have been introduced into the polymer polymerization process through iron oxide pretreatment. However, the above method has a disadvantage in that the pretreatment of iron oxide is complicated or difficult to obtain hybrid particles of various sizes. In addition, if the hybrid particle synthesis fails, the polymerization process must be restarted from the beginning, and additional costs are required.
지금까지 구형의 산화철/고분자 하이브리드 입자를 제조하는 방법은 다양하게 연구되어 왔다. 대한민국 공개특허 제2006-0114170호에서는 산화철/고분자 나노 복합체를 다공성 고분자와 산화철 나노 입자의 흡착에 의해 제조하는 방법을 제시하고 있다. 그러나 상기 방법에 의한 제조는 마이크로 단위의 다공성 고분자에 한정하여 복합체를 제조할 수 있으며, 포어(pore) 사이즈에도 제한을 받는다. 또한 물리적 흡착에 의한 방법으로 내충격성이 약하다는 단점이 있다.Until now, various methods for producing spherical iron oxide / polymer hybrid particles have been studied. Korean Patent Laid-Open Publication No. 2006-0114170 proposes a method for preparing the iron oxide / polymer nanocomposite by adsorption of porous polymer and iron oxide nanoparticles. However, the preparation by the above method may be limited to the microporous polymer, and the composite may be prepared, and the pore size is also limited. In addition, there is a disadvantage that the impact resistance by the method by physical adsorption is weak.
대한민국 공개특허 제2010-0124878호에서는 가교된 고분자의 팽윤부여를 통해 하이브리드 입자를 제조하는 방법을 제시한다. 가교 고분자의 팽윤 부여를 위한 유기용제의 사용이 필요하고, 팽윤된 고분자의 외부에 산화철을 함유하는 하이브리드 입자를 제조하는 방법으로 한정된다.Republic of Korea Patent Publication No. 2010-0124878 proposes a method for producing a hybrid particle by swelling the crosslinked polymer. The use of an organic solvent for swelling the crosslinked polymer is necessary, and is limited to a method for producing hybrid particles containing iron oxide on the outside of the swollen polymer.
T. Alan Hatton 외 연구원들은 Langmuir 2009, 25(14)에서 용매증발법을 통해 고분자/산화철 하이브리드 입자의 제조법을 제시하고 있다. 이 방법 또한 계면활성제의 사용과 유화공정이 필요하고 유기용매의 증발로 인한 문제점이 발생할 수 있다. 또한 외부에 존재하는 산화철에 의한 응집현상이 발생하여 분상성이 떨어지는 단점이 있다.T. Alan Hatton et al. (2007) present a method for preparing polymer / iron oxide hybrid particles by solvent evaporation in Langmuir 2009, 25 (14). This method also requires the use of surfactants and emulsification and may cause problems due to evaporation of the organic solvent. In addition, there is a disadvantage in that the coagulation phenomenon due to the iron oxide existing in the outside is poor in powder separation.
대한민국 공개특허 제2006-0084702호, 대한민국 공개특허 제2004-0097566호, 대한민국 공개특허 제2011-0035134호에서도 산화철 나노입자와 고분자의 복합체 제조방법을 제시한다. 상기 방법들에 의한 제조로는 나노사이즈 이상의 복합체 제조가 어렵고 이용 가능한 고분자가 제한적이라는 단점이 있다.Republic of Korea Patent Application Publication No. 2006-0084702, Republic of Korea Patent Publication No. 2004-0097566, Republic of Korea Patent Publication No. 2011-0035134 also provides a method for producing a composite of iron oxide nanoparticles and polymer. The production by the above methods has a disadvantage in that it is difficult to manufacture a composite of nano size or more and the available polymer is limited.
그리고 Journal of Industrial and Engineering Chemistry 2010,16(6)에서는 미니에멀전 중합을 이용하여 산화철 나노입자가 내부에 분산된 고분자 복합체의 제조방법에 관한 것으로, 중합 과정에 산화철 나노입자를 도입하여 나노크기의 복합체를 제조할 수 있다. 그러나 산화철의 합성과 유기산 코팅의 과정이 필요하고 계면활정제 없이는 안정한 구형 입자를 합성할 수 없으며, 이 또한 입자 크기제어가 제한적이다.And Journal of Industrial and Engineering Chemistry 2010, 16 (6) relates to a method for producing a polymer composite in which iron oxide nanoparticles are dispersed therein using miniemulsion polymerization. Can be prepared. However, the synthesis of iron oxide and organic acid coating process are required, and stable spherical particles cannot be synthesized without interfacial stabilizer, which also has limited particle size control.
기존의 하이브리드 입자를 제조하는 방법으로는 입자 크기의 제어가 제한적이고, 원하는 크기와 함량을 갖는 입자를 한번에 수득하지 못하면 다시 다른 공정을 거쳐 제조하는 추가적 공정시간 및 비용부담이 소요되어 하이브리드 입자의 생산 단가가 상승하게 된다. 또한 제조 공정 중에 사용된 용매의 재사용이 까다롭다는 점과 안정한 입자 합성을 위해 분산 안정제 및 계면활성제와 같은 별도의 첨가물이 필요하다는 문제점이 있다.
Existing hybrid particle manufacturing method has limited control of particle size, and if a particle having a desired size and content cannot be obtained at one time, additional process time and cost for producing the hybrid particle are required to produce the hybrid particle. The unit price will rise. In addition, there is a problem that the reuse of the solvent used during the manufacturing process is difficult and separate additives such as dispersion stabilizers and surfactants are required for stable particle synthesis.
이에 본 발명자들은 상기 기존 제조방법들이 가지는 문제점을 해결하고 새로운 방법으로 하이브리드 입자를 제조하기 위해 연구, 노력한 결과 10,000 ~ 150,000 g/mol 범위의 중량평균분자량과 1.0 ~ 2.0 범위의 분자량 분포(PDI)를 갖는 고분자 입자를 상온에서 불용상태로 빈용매에 분산시킨 후 가열하여 완전히 용해시킨 다음, 유기 용매에 분산된 산화철 나노입자와 상기 고분자 용액을 함께 분산시킨 뒤 다시 냉각시키는 경우 중합과정 없이 냉각속도의 조절만으로도 다양한 크기의 구상 하이브리드 입자를 제조할 수 있음을 밝혀냄으로써 본 발명을 완성하게 되었다.Therefore, the present inventors have solved the problems of the existing manufacturing methods and researched and tried to produce a hybrid particle in a new method, the weight average molecular weight in the range of 10,000 ~ 150,000 g / mol and molecular weight distribution (PDI) in the range of 1.0 ~ 2.0 After dispersing the polymer particles in an insoluble state at room temperature in a poor solvent and completely dissolved by heating, when the iron oxide nanoparticles dispersed in an organic solvent and the polymer solution are dispersed together and then cooled again, the cooling rate is controlled without polymerization. The present invention has been completed by discovering that spherical hybrid particles of various sizes can be produced by themselves.
따라서 본 발명은 산화철 나노입자가 고분자 내부에 캡슐화된 안정된 하이브리드 구상입자를 제조하는 방법을 제공하는 것을 그 목적으로 한다.
Accordingly, an object of the present invention is to provide a method for producing stable hybrid spherical particles in which iron oxide nanoparticles are encapsulated inside a polymer.
상기 과제를 해결하기 위해, 본 발명은 (a) 중량평균분자량이 10,000 ~ 150,000 g/mol이고, 분자량분포(PDI)가 1.0 ~ 2.0 범위인 고분자 입자를 빈용매에 분산시킨 후 이를 가열하여 용해시킨 고분자 용액을 제조하는 단계; (b) 산화철 나노입자를 올레익산과 옥탄을 포함하는 용매에 분산시키는 단계; (c) 상기 고분자 용액과 산화철 나노입자가 분산된 용액을 혼합하는 단계; (d) 상기 혼합 용액을 냉각시켜 산화철/고분자 하이브리드 구상입자를 제조하는 단계; 및 (e) 상기 하이브리드 구상입자를 세척 및 건조하여 분말화시키는 단계를 포함하는 것을 특징으로 하는 안정된 하이브리드 구상입자의 제조방법을 제공한다.
In order to solve the above problems, the present invention (a) a polymer having a weight average molecular weight of 10,000 ~ 150,000 g / mol, molecular weight distribution (PDI) of 1.0 to 2.0 dispersed in a poor solvent and then dissolved by heating it Preparing a polymer solution; (b) dispersing the iron oxide nanoparticles in a solvent comprising oleic acid and octane; (c) mixing the polymer solution with a solution in which the iron oxide nanoparticles are dispersed; (d) cooling the mixed solution to produce iron oxide / polymer hybrid spherical particles; And (e) washing and drying the hybrid spherical particles to powder the hybrid spherical particles.
본 발명에서 제시하는 하이브리드 입자의 제조방법은 기존의 중합 공정 방법보다 방법이 단순하고, 산화철을 원하는 고분자 입자의 내부에 손쉽게 도입할 수 있어 효과적이다. 또한 하이브리드 입자의 제조 공정에서 냉각속도를 조절하면 석출되는 고분자 입자의 크기를 조절할 수 있는데 이러한 방법을 통해 다양한 크기를 갖는 구상 하이브리드입자의 제조가 가능하다는 장점이 있다. 또한 재용해 및 재석출 과정만을 반복하여 원하는 사이즈의 하이브리드 입자를 쉽게 수득할 수 있어 수지의 재활용이 용이하다는 장점이 있다. 뿐만 아니라, 제조 과정 중에 사용된 빈용매는 계속적으로 재사용이 가능하며, 고분자와 산화철로 이루어진 하이브리드 입자를 각각의 원료 물질별로 손쉽게 분리하여 재활용할 수 있다. 따라서 본 발명에 따른 제조방법을 산업적으로 적용할 때 공정 시간 및 비용 절감 효과를 기대할 수 있을 뿐만 아니라, 원하는 크기의 산화철/고분자 하이브리드 입자를 수득하는 것이 자유로우며, 전도성이나 자성과 같은 산화철의 특성과 고분자의 우수한 가공성과 분산성 및 탄성을 동시에 갖기 때문에 산업적으로 다양한 분야에 적용할 수 있다.
The method for producing a hybrid particle according to the present invention is simpler than a conventional polymerization method and is effective because iron oxide can be easily introduced into a desired polymer particle. In addition, by controlling the cooling rate in the manufacturing process of the hybrid particles, it is possible to control the size of the precipitated polymer particles, there is an advantage that it is possible to produce spherical hybrid particles having various sizes through this method. In addition, it is possible to easily obtain a hybrid particle of a desired size by repeating the re-dissolution and re-precipitation process, there is an advantage that the resin is easy to recycle. In addition, the poor solvent used during the manufacturing process can be continuously reused, and hybrid particles made of polymer and iron oxide can be easily separated and recycled for each raw material. Therefore, when industrially applying the manufacturing method according to the present invention can not only expect the process time and cost reduction effect, it is free to obtain the iron oxide / polymer hybrid particles of the desired size, and the characteristics of the iron oxide such as conductivity or magnetic Since the polymer has excellent processability, dispersibility and elasticity, it can be applied to various industrial fields.
도 1은 실시예 1에서 제조한 하이브리드 입자의 주사전자현미경(SEM) 사진이다.
도 2는 실시예 1에서 제조한 하이브리드 입자의 투과전자현미경(TEM) 사진이다.
도 3은 실시예 1에서 제조한 하이브리드 입자의 열중량분석(TGA) 그래프이다.1 is a scanning electron microscope (SEM) photograph of the hybrid particles prepared in Example 1. FIG.
2 is a transmission electron microscope (TEM) photograph of the hybrid particles prepared in Example 1. FIG.
3 is a thermogravimetric analysis (TGA) graph of the hybrid particles prepared in Example 1. FIG.
본 발명은 일정 범위의 분자량을 갖는 고분자 입자를 상온에서 불용성인 빈용매에 분산시키고 일정 범위의 온도로 가열하여 완전히 용해시킨 후 산화철 입자를 함께 용매에 분산하여 냉각함으로써 구상의 고분자 입자 내부에 산화철이 존재하는 안정된 하이브리드 입자를 제조하는 방법에 관한 것이다. The present invention is to disperse the polymer particles having a range of molecular weight in a poor solvent insoluble at room temperature, and to completely dissolve by heating to a range of temperature, iron oxide particles are dispersed together in a solvent to cool the iron oxide inside the spherical polymer particles It relates to a process for producing stable hybrid particles present.
구체적으로는 본 발명은 (a) 중량평균분자량이 10,000 ~ 150,000 g/mol이고, 분자량분포(PDI)가 1.0 ~ 2.0 범위인 고분자 입자를 빈용매에 분산시킨 후 이를 가열하여 용해시킨 고분자 용액을 제조하는 단계; (b) 산화철 나노입자를 올레익산과 옥탄을 포함하는 용매에 분산시키는 단계; (c) 상기 가열된 고분자 용액과 산화철 나노입자가 분산된 용액을 혼합하는 단계; (d) 상기 혼합 용액을 냉각시켜 산화철/고분자 하이브리드 구상입자를 제조하는 단계; 및 (e) 상기 하이브리드 구상입자를 세척 및 건조하여 분말화시키는 단계를 포함하여 이루어지는 것을 특징으로 한다.Specifically, the present invention provides a polymer solution in which (a) a weight average molecular weight is 10,000 to 150,000 g / mol and a polymer particle having a molecular weight distribution (PDI) of 1.0 to 2.0 is dispersed in a poor solvent and then heated and dissolved therein. Doing; (b) dispersing the iron oxide nanoparticles in a solvent comprising oleic acid and octane; (c) mixing the heated polymer solution and a solution in which the iron oxide nanoparticles are dispersed; (d) cooling the mixed solution to produce iron oxide / polymer hybrid spherical particles; And (e) washing and drying the hybrid spherical particles to form a powder.
이하에서, 본 발명에 따른 구상의 하이브리드 입자의 제조방법을 보다 상세하게 설명하면 다음과 같다.Hereinafter, the method for producing spherical hybrid particles according to the present invention in more detail as follows.
상기 (a)단계는 특정한 분자량을 갖는 고분자 입자를 빈용매에 분산시킨 후 이를 가열하여 용해시키는 단계로, 이를 통해 고분자 용액이 제조된다. 이용되는 고분자 입자는 10,000 ~ 150,000 g/mol의 중량평균분자량을 가지며, 분자량 분포가 1.0 ~ 2.0 범위인 것을 이용한다. 이때 고분자는 입자(particle) 형태를 갖는 것을 사용하는 것이 바람직하며, 이는 빈용매에 용해시키는 과정에서 입자 형태인 고분자의 비표면적이 비 입자 형태인 고분자 보다 넓어 용해시키는 시간이 짧아지는 효과가 있기 때문이다. 또한 상기 중량평균분자량이 10,000 g/mol 미만일 경우 최초 입자 생성 시에는 안정된 입자를 얻을 수 있지만 입자표면이 부드러워져(softness의 증가) 장기 보존 시 입자간의 응집이 발생할 수 있으며, 냉각 과정에서도 고분자가 완전히 석출되지 않고, 고분자 체인 형태로 빈용매에 용해되어 존재할 수 있어 산화철/고분자 하이브리드 입자 제조 시 생산 수득율이 떨어지는 문제점이 발생할 수 있다. 중량평균분자량이 150,000 g/mol을 초과하는 경우에는 온도를 가열하여도 빈용매에 완전히 용해되지 않거나, 빈용매에 용해시키는 공정 시간이 길어지고 용해시키는데 필요한 온도가 비교적 높아지기 때문에 생산 단가가 올라가는 문제점이 발생할 수 있으므로, 상기 범위를 유지하는 것이 바람직하다. Step (a) is a step of dispersing the polymer particles having a specific molecular weight in a poor solvent and then dissolving it by heating, thereby producing a polymer solution. The polymer particles to be used have a weight average molecular weight of 10,000 to 150,000 g / mol, and the molecular weight distribution is used in the range 1.0 to 2.0. In this case, it is preferable to use a polymer having a particle form, since the specific surface area of the polymer in the form of particles is wider than that in the non-particle form in the process of dissolving in a poor solvent, so that the dissolution time is shortened. to be. In addition, when the weight average molecular weight is less than 10,000 g / mol, stable particles may be obtained at the time of initial particle formation, but the surface of the particles may be softened (increase in softness), thereby causing aggregation between particles during long-term storage. It does not precipitate, may be present in the form of a polymer chain dissolved in the poor solvent, there may be a problem that the production yield decreases when manufacturing iron oxide / polymer hybrid particles. If the weight-average molecular weight exceeds 150,000 g / mol, the problem of increasing the production cost is that it does not completely dissolve in the poor solvent even when the temperature is heated, or the process time for dissolving in the poor solvent increases and the temperature required for dissolving becomes relatively high. It may be desirable to maintain this range.
상기 가열은 빈용매의 끓는점 이하로 진행하며, 고분자 입자를 완전히 용해시킬 수 있는 온도가 바람직하다. 고분자 입자의 경우 분자량별로 녹는 온도가 다르기 때문에 온도가 특별히 제한되지는 않지만 바람직하게는 40 ℃ ~ 100 ℃, 더욱 바람직하게는 40 ℃ ~ 70 ℃ 범위로 가열하는 것이 알코올계 빈용매의 끓는점 이하에서 고분자 입자를 완전히 용해시킬 수 있어 좋다. 상기 온도 범위가 40 ℃ 미만인 경우 고분자 입자가 완전히 용해되지 않는다는 문제가 있으며, 상기 온도 범위가 100 ℃를 초과하는 경우 용매의 증발로 인해 용해도가 떨어져 목표하는 입도를 얻을 수 없게 되며, 용매가 완전히 증발하는 경우 수지 형태의 고분자를 얻게 되고, 본 발명의 장점인 용매의 재활용을 할 수 없다는 문제점이 있기 때문에 상기 범위를 유지하는 것이 바람직하다. 상기 빈용매로는 알코올계 빈용매 또는 알코올계 빈용매와 1종 이상의 이종 용매, 즉 양용매 또는 비용매와의 혼합물을 사용할 수 있다. 상기와 같은 빈용매를 사용함으로써 상온에서는 고분자 입자를 용해시키지 못하지만 상기 온도 범위에서 고분자를 완전히 용해시킬 수 있다.The heating proceeds below the boiling point of the poor solvent, and a temperature at which the polymer particles can be completely dissolved is preferable. In the case of the polymer particles, the melting temperature varies depending on the molecular weight, but the temperature is not particularly limited. Preferably, the polymer particles are heated at a temperature in the range of 40 ° C. to 100 ° C., more preferably in the range of 40 ° C. to 70 ° C., below the boiling point of the alcohol-based poor solvent. The particles can be dissolved completely. If the temperature range is less than 40 ℃ there is a problem that the polymer particles are not completely dissolved, if the temperature range exceeds 100 ℃ solubility due to the evaporation of the solvent is not possible to obtain the target particle size, the solvent is completely evaporated If it is to obtain a polymer in the form of a resin, it is preferable to maintain the above range because there is a problem that can not recycle the solvent which is an advantage of the present invention. The poor solvent may be a mixture of an alcohol-based poor solvent or an alcohol-based poor solvent and at least one hetero solvent, that is, a good solvent or a non-solvent. By using the poor solvent as described above, the polymer particles cannot be dissolved at room temperature, but the polymer can be completely dissolved in the above temperature range.
상기 (b)단계는 산화철 나노입자 분말을 올레익산과 옥탄에 분산시키는 단계이다. 산화철 분말을 가열된 고분자 용액에 직접 도입하였을 경우 산화철 입자 간의 응집 현상이 발생하므로 이를 방지하기 위한 과정이 필요하다. 이를 위해 본 발명에서는 산화철 분말을 소량의 올레익산에 분산시킨 뒤 과량의 옥탄을 첨가함으로써 고분자 용액 내에서 산화철이 응집되는 문제점을 해결할 수 있다. 이때 사용되는 산화철은 크기가 수나노에서 수십나노까지 이용이 가능하며, 보다 바람직하게는 5 nm ~ 70 nm 범위인 것이 좋다. 나노입자가 응집되어 마이크론 크기가 되면 다음 단계인 하이브리드 입자 형성에서 고분자 입자와 산화철 입자가 분리되는 현상이 발생하므로 초음파분산기를 이용하여 산화철 입자를 균일하게 분산시켜야한다.Step (b) is a step of dispersing the iron oxide nanoparticle powder in oleic acid and octane. When iron oxide powder is directly introduced into a heated polymer solution, aggregation of iron oxide particles occurs, and thus a process for preventing the iron oxide powder is necessary. To this end, the present invention can solve the problem of iron oxide agglomeration in the polymer solution by dispersing the iron oxide powder in a small amount of oleic acid and then adding an excess of octane. At this time, the iron oxide used may be available in size from several nanometers to several tens of nanometers, and more preferably in the range of 5 nm to 70 nm. When the nanoparticles are agglomerated to a micron size, a phenomenon in which the polymer particles and the iron oxide particles are separated in a hybrid particle formation, which is the next step, needs to uniformly disperse the iron oxide particles using an ultrasonic disperser.
상기 (c)단계는 상기 (a)단계를 통해 제조된 고분자 용액과 (b)단계를 통해 제조된 산화철 나노입자가 분산된 용액을 혼합하는 단계이다. The step (c) is a step of mixing the polymer solution prepared in step (a) and the solution in which the iron oxide nanoparticles prepared in step (b) are dispersed.
가열된 상태의 상기 고분자 용액에 올레익산과 옥탄에 분산된 산화철 입자를 첨가하여 교반한다. 이때 함량은 고분자 입자 100 중량부를 기준으로 산화철 나노입자 0.1 ~ 30 중량부를 사용하는 것이 바람직하다. 또한 상기 교반의 교반 속도는 20 ~ 500 rpm에서 수행 할 수 있다.Iron oxide particles dispersed in oleic acid and octane are added to the polymer solution in a heated state and stirred. At this time, the content is preferably used 0.1 to 30 parts by weight of iron oxide nanoparticles based on 100 parts by weight of the polymer particles. In addition, the stirring speed of the stirring can be performed at 20 ~ 500 rpm.
상기 (d)단계는 상기 (c)단계에서 제조된 혼합 용액을 냉각시켜 구상의 하이브리드 입자를 제조하는 단계이다. 본 발명은 냉각속도의 조절만으로도 원하는 사이즈를 갖는 구상의 하이브리드 입자를 제조할 수 있는 것을 특징으로 한다. 본 발명에서 상기 냉각속도의 조절에 따라 다양한 크기의 구상 하이브리드 입자를 제조할 수 있어 냉각속도는 특별히 제한되지 않는다.Step (d) is a step of preparing spherical hybrid particles by cooling the mixed solution prepared in step (c). The present invention is characterized in that spherical hybrid particles having a desired size can be produced only by controlling the cooling rate. According to the present invention, the spherical hybrid particles of various sizes can be prepared according to the control of the cooling rate, and the cooling rate is not particularly limited.
냉각속도가 빨라질수록 보다 작은 크기의 구상 하이브리드 입자가 제조되며, 냉각속도가 느려질수록 보다 큰 크기의 입자가 제조된다.The faster the cooling rate, the smaller spherical hybrid particles are produced. The slower the cooling rate, the larger particles are produced.
또한 목표하는 입도를 가지는 구상입자를 얻지 못하는 경우, 또는 산화철의 함량이 목표량에 맞지 않는 경우 다시 가열과 냉각을 반복하여 냉각속도에 따라 다른 크기, 분포 및 산화철의 함량을 갖는 하이브리드 입자를 제조할 수 있다.In addition, when spherical particles having a desired particle size are not obtained, or when the iron oxide content does not meet the target amount, heating and cooling may be repeated to produce hybrid particles having different sizes, distributions, and iron oxide contents depending on the cooling rate. have.
상기 (e)단계는 제조된 하이브리드 입자를 세척 및 건조 과정을 통해 분말화 하는 단계로, 세척 용매로 한 차례 이상 세척한 후 질소 분위기 하에서 2 시간 동안 30 ~ 40 ℃의 온도로 완전히 건조시켜, 최종으로 구상화된 분말 상태의 하이브리드 입자를 수득하는 과정이다. 이 과정에서 건조 온도가 40 ℃를 초과하는 경우 하이브리드 입자가 서로 엉겨붙어 안정된 분말화 입자를 얻기 어렵다는 문제점이 있다.The step (e) is a step of pulverizing the prepared hybrid particles through a washing and drying process, after washing with a washing solvent one or more times and completely dried at a temperature of 30 ~ 40 ℃ for 2 hours under a nitrogen atmosphere, the final It is a process of obtaining a hybrid particle in the form of a powder spheroidized by. In this process, when the drying temperature exceeds 40 ℃, there is a problem that the hybrid particles are entangled with each other to obtain a stable powdered particles.
본 발명에 따른 산화철 나노입자가 구상의 고분자 입자 내부에 캡슐화된 하이브리드 입자의 제조방법은 용매에 완전히 용해된 고분자와 산화철을 함께 분산시킨 후 냉각시키는 과정에서 안정제 또는 계면활성제와 같은 별도의 첨가제를 사용하지 않고도 안정한 하이브리드 입자를 석출할 수 있는 것을 특징으로 한다. 또한 상기 용해와 냉각을 반복해도 이러한 특징이 계속해서 반복적으로 나타남으로써 간편하고 용이하게 산화철/고분자 하이브리드 입자를 제조할 수 있는 것을 특징으로 한다.In the method for producing a hybrid particle in which the iron oxide nanoparticles are encapsulated inside a spherical polymer particle, a separate additive such as a stabilizer or a surfactant is used in the process of dispersing the polymer and iron oxide completely dissolved in a solvent and cooling the same. It is characterized by being able to precipitate stable hybrid particles without having to. In addition, even if the above dissolution and cooling are repeated, these characteristics are repeatedly shown, characterized in that the iron oxide / polymer hybrid particles can be easily and easily produced.
이하, 본 발명에서 사용되는 구성성분을 구체적으로 설명한다.
Hereinafter, the components used in the present invention will be described in detail.
(1) 고분자 입자(1) polymer particles
본 발명에 이용될 수 있는 고분자 입자는 라디칼 중합성 단량체를 이용해 제조된 고분자 입자로써 바람직하게는 상온에서는 알코올계 빈용매 또는 알코올계 빈용매와 이종 용매간의 혼합 용매에서 불용성이지만 가열 시 완전하게 용해되는 고분자 물성을 가지고 있는 것을 사용하는 것이 좋다.The polymer particles that can be used in the present invention are polymer particles prepared by using a radical polymerizable monomer. Preferably, the polymer particles are insoluble in an alcohol-based poor solvent or a mixed solvent between an alcohol-based poor solvent and a heterogeneous solvent, but are completely dissolved upon heating. It is better to use the one with high polymer properties.
이에 본 발명에서 사용가능한 고분자를 제조할 수 있는 라디칼 중합성 단량체로는, 메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, 부틸(메타)아크릴레이트, 옥틸(메타)아크릴레이트, 스테아릴(메타)아크릴레이트, 벤질(메타)아크릴레이트, 글리시딜(메타)아크릴레이트, 플루오르에틸아크릴레이트, 트리플루오르에틸메타크릴레이트, 펜타플루오르프로필메타크릴레이트, 플로로에틸메타크릴레이트, 헥사플루오르부틸(메타)아크릴레이트, 헥사플루오르이소프로필메타크릴레이트, 퍼플루오르알킬아크릴레이트, 옥타플루오르페닐메타크릴레이트 등의 (메타)아크릴레이트계 단량체 중에서 선택된 1종 또는 2종 이상이 혼합된 단량체를 이용하여 중합된 고분자의 사용이 가능하다.
Accordingly, as the radical polymerizable monomer capable of producing a polymer usable in the present invention, methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, octyl (meth) acrylate, stearyl ( Meth) acrylate, benzyl (meth) acrylate, glycidyl (meth) acrylate, fluoroethyl acrylate, trifluoroethyl methacrylate, pentafluoropropyl methacrylate, fluoroethyl methacrylate, hexafluorobutyl Using a monomer selected from one or two or more selected from (meth) acrylate monomers such as (meth) acrylate, hexafluoroisopropyl methacrylate, perfluoroalkyl acrylate and octafluorophenyl methacrylate The use of polymerized polymers is possible.
(2) 빈용매(2) poor solvent
본 발명의 (a)단계에 있어서, 빈용매라 함은 알코올계 빈용매 또는 알코올계 빈용매와 1종 이상의 이종 용매와의 혼합물을 뜻하는데, 메틸아크릴레이트 또는 아크릴레이트계 수지를 40 ℃ 미만의 저온에서는 5 중량％ 이상 용해시킬 수 없지만, 40 ℃ 이상 또한 메틸아크릴레이트 또는 아크릴레이트계 수지의 융점 이하(예를 들면, 폴리메틸메타아크릴레이트 단독으로 사용되는 경우 110 ℃ 정도)의 고온 영역에서 5 중량％ 이상 용해시킬 수 있는 용매를 의미한다. 본 발명에 있어서, 빈용매에 대해 40 ℃ 미만의 저온에서도 메틸아크릴레이트 또는 아크릴레이트계 수지를 5 중량％ 이상 용해시킬 수 있는 용매를 양용매, 메틸아크릴레이트 또는 아크릴레이트계 수지의 융점 또는 액체의 비점까지 폴리불화비닐리덴계 수지를 용해나 팽윤도 시키지 않은 용매를 비용매라고 정의한다.In the step (a) of the present invention, the poor solvent means an alcohol-based poor solvent or a mixture of an alcohol-based poor solvent and one or more heterogeneous solvents, the methyl acrylate or acrylate resin is less than 40 ℃ It is not possible to dissolve at least 5% by weight at low temperatures, but at temperatures above 40 ° C and below the melting point of methyl acrylate or acrylate-based resins (for example, about 110 ° C when polymethylmethacrylate is used alone), 5 It means the solvent which can melt | dissolve by weight or more. In the present invention, a solvent capable of dissolving 5% by weight or more of the methyl acrylate or the acrylate-based resin even at a low temperature of less than 40 ° C with respect to the poor solvent is obtained by melting the melting point of the good solvent, the methyl acrylate or the acrylate-based resin or the liquid. The solvent which does not melt | dissolve or swell polyvinylidene fluoride system resin until boiling point is defined as a nonsolvent.
상기 알코올계 빈용매로는 메탄올, 에탄올, 아이소프로필알콜, 에틸렌글라이콜, 부틸렌글라이콜, m-크레졸, 글리세롤, 누졸 등을 사용할 수 있으며, 이중 메탄올, 에탄올 등이 바람직하다. 상기 이종 용매로 사용가능한 양용매의 경우에는 아세톤, 벤젠, 톨루엔, 테트라하이드로퓨란, 시클로헥사논, 다이옥신, 2-에톡시에탄올, 에틸아세테이트, 메틸렌클로라이드 등을 사용할 수 있다. 또한 비용매의 경우에 물, 과산화수소, 카스터오일(castor oil), 시클로헥산(cyclohexane), 다이에틸에테르(diethyl ether), 포름아마이드(formamide), 가솔린, 헥산 등을 사용할 수 있다.
As the alcohol-based poor solvent, methanol, ethanol, isopropyl alcohol, ethylene glycol, butylene glycol, m-cresol, glycerol, nusol and the like can be used, of which methanol and ethanol are preferable. In the case of a good solvent usable as the heterogeneous solvent, acetone, benzene, toluene, tetrahydrofuran, cyclohexanone, dioxin, 2-ethoxyethanol, ethyl acetate, methylene chloride and the like can be used. In the case of non-solvent, water, hydrogen peroxide, castor oil, cyclohexane, diethyl ether, formamide, gasoline, hexane and the like may be used.
(3) 산화철(3) iron oxide
본 발명의 (c)단계에 있어서, 고분자 용액에 첨가되어 (d)단계에서 고분자 내부에 캡슐화되는 산화철 입자로써, 마그네타이트(magnetite), 마그헤마이트(maghemite), 페라이트(ferrite) 중에서 선택된 1종 또는 2종 이상이 혼합된 수나노 ~ 수십나노 크기의 나노입자를 사용할 수 있다.
In the step (c) of the present invention, the iron oxide particles are added to the polymer solution and encapsulated inside the polymer in the step (d), one selected from magnetite, maghemite, ferrite or Two or more kinds of nanoparticles of several tens of nanometers in size can be used.
(4) 산화철 분산용매(4) Iron oxide dispersion solvent
본 발명의 (c)단계에 있어서, 산화철 나노입자를 분산시키는 용매로서 유기산인 올레익산(oleic acid)과 옥탄(n-octane)의 혼합물을 사용할 수 있다.
In step (c) of the present invention, a mixture of an organic acid, oleic acid and octane, may be used as a solvent for dispersing the iron oxide nanoparticles.
(5) 응집 억제제(5) aggregation inhibitors
본 발명의 (d)단계에 있어서, 고분자 입자의 석출 과정에서 사용되는 공지의 응집 억제제가 통상적인 용도와 방법으로 부가 사용될 수 있다. 미소 액적의 분산성을 높여 응집을 방지하기 위한 응집 억제제로서 양이온성 첨가제, 음이온성 첨가제, 양쪽이온성 첨가제, 비이온성 첨가제, 고분자 첨가제 등을 추가하여 사용할 수 있다. 상기 양이온성 첨가제로는 4급 암모늄염, 지방족 아민, 알콕시폴리아민, 지방족아민폴리글리콜에테르, 지방족 아민과 지방족 알콜에서 유도되는 디아민 또는 폴리아민 등을 사용할 수 있다. 음이온성 첨가제로는 지방산염, 알킬폴리인산에스테르염, 알킬황산에스테르염, 알킬아릴술폰산염, 아릴황산에스테르염, 아실메틸타우린산염, 알킬인산에스테르염, 아릴인산에스테르염, 아릴술폰산포르말린축합물, 또는 폴리옥시에틸렌알킬황산에스테르염 등을 사용할 수 있다. 양쪽이온성 첨가제는 상기 기술한 양이온성 분산제의 양이온 구조와 음이온성 분산제의 음이온 구조가 한분자 내에 포함되어 있는 화합물이다. 또한 비이온성 첨가제로는 폴리옥시에틸렌지방산에스테르, 폴리옥시에틸렌알킬에테르, 폴리옥시에틸렌알킬아릴에테르, 폴리옥시에틸렌알킬아민, 폴리옥시알킬아릴아민, 폴리옥시에틸렌지방산에스테르, 글리세린지방산에스테르, 솔비탄지방산에스테르, 폴리옥시에틸렌솔비탄지방산에스테르 등을 사용할 수 있다. 고분자 첨가제로는 알킬히드록시셀룰로즈, 셀룰로즈 유도체, 폴리비닐알콜, 폴리비닐피롤리돈, 폴리아크릴레이트 및 그의 유도체, 폴리비닐알콜, 초산 비닐 공중합체, 폴리에틸렌글리콜, 폴리프로필렌글리콜, 폴리에틸렌옥사이드, 폴리카보네이트, 폴리비닐메틸에테르, 폴리아크릴아마이드, 폴리이미드, 폴리아릴아민염 폴리에틸렌옥사이-폴리프로필렌옥사이드 공중합체, 폴리아크릴산염, 축합아릴렌슬폰산염, 폴리비닐황산염, 또는 스틸렌-아크릴산염 공중합체 등이 필요에 따라 부가될 수 있다.
In step (d) of the present invention, a known aggregation inhibitor used in the precipitation of the polymer particles may be added and used in a conventional use and method. Cationic additives, anionic additives, zwitterionic additives, nonionic additives, polymer additives, etc. may be added and used as an aggregation inhibitor for preventing aggregation by raising the dispersibility of a microdroplet. As the cationic additive, quaternary ammonium salts, aliphatic amines, alkoxypolyamines, aliphatic amine polyglycol ethers, diamines or polyamines derived from aliphatic amines and aliphatic alcohols can be used. Anionic additives include fatty acid salts, alkyl polyphosphate ester salts, alkyl sulfate ester salts, alkyl aryl sulfonates, aryl sulfate ester salts, acylmethyltaurate salts, alkyl phosphate ester salts, aryl phosphate ester salts, aryl sulfonic acid formalin condensates, Or polyoxyethylene alkyl sulfate ester salt etc. can be used. Zwitterionic additives are compounds in which the cationic structure of the cationic dispersant described above and the anionic structure of the anionic dispersant are contained in one molecule. As nonionic additives, polyoxyethylene fatty acid ester, polyoxyethylene alkyl ether, polyoxyethylene alkyl aryl ether, polyoxyethylene alkylamine, polyoxyalkylarylamine, polyoxyethylene fatty acid ester, glycerin fatty acid ester, sorbitan fatty acid Ester, polyoxyethylene sorbitan fatty acid ester, etc. can be used. Polymeric additives include alkyl hydroxycellulose, cellulose derivatives, polyvinyl alcohol, polyvinylpyrrolidone, polyacrylates and derivatives thereof, polyvinyl alcohol, vinyl acetate copolymers, polyethylene glycol, polypropylene glycol, polyethylene oxide, polycarbonate , Polyvinyl methyl ether, polyacrylamide, polyimide, polyarylamine salt polyethylene oxy-polypropylene oxide copolymer, polyacrylate, condensed arylene sulfonate, polyvinyl sulfate, or styrene-acrylate copolymer Can be added according to.
본 발명은 하기의 실시예에 의하여 보다 구체화될 것이나, 하기의 실시예는 본 발명의 구체적인 예시에 불과하고 본 발명의 보호범위를 한정하거나 제한하고자 하는 것이 아니다.
The present invention will be further illustrated by the following examples, but the following examples are only specific examples of the present invention and are not intended to limit or limit the protection scope of the present invention.
실시예Example 1 One
(a) 고분자 입자의 용해(a) Dissolution of Polymer Particles
교반기가 부착된 300 ml 3 구 분리형 반응기에서 용매인 메탄올 150 g에 중량평균 분자량이 37,000 g/mol이고, 입자 크기가 2.3 ㎛인 폴리메틸메타크릴레이트 입자 10 g(PDI = 1.80)을 불용성 상태로 분산시킨 후 이를 60 ℃에서 200 rpm으로 교반하면서 10 분간 가열하여 완전히 용해시켜 고분자 용액을 제조하였다.In a 300 ml three-neck separate reactor with a stirrer, 10 g of polymethyl methacrylate particles (PDI = 1.80) having a weight average molecular weight of 37,000 g / mol and a particle size of 2.3 μm were dissolved in 150 g of methanol as a solvent. After dispersing, the mixture was heated for 10 minutes while stirring at 200 rpm at 60 ° C. to completely dissolve the polymer solution.
(b) 산화철 나노입자의 분산(b) Dispersion of Iron Oxide Nanoparticles
고분자 입자에 캡슐화시킬 마그헤마이트 나노입자 2.0 g을 올레익산 3 g에 초음파분산기로 분산시킨 후 10 g의 옥탄과 혼합하여 초음파분산기로 10 분 동안 분산시켰다.2.0 g of maghemite nanoparticles to be encapsulated in the polymer particles was dispersed in 3 g of oleic acid with an ultrasonic disperser, mixed with 10 g of octane, and dispersed with an ultrasonic disperser for 10 minutes.
(c) 산화철이 분산된 고분자 혼합 용액 제조(c) Preparation of polymer mixed solution in which iron oxide is dispersed
상기 제조된 고분자 용액에 산화철 나노 입자가 분산된 용액 15 g을 가열된 고분자 용액이 들어있는 반응기에 투입하여 완전 분산시키기 위하여 3 시간 동안 60 ℃에서 300 rpm으로 가열하며 교반하였다.15 g of a solution in which the iron oxide nanoparticles were dispersed in the prepared polymer solution was added to a reactor containing a heated polymer solution and stirred at 300 ° C. and heated at 300 rpm for 3 hours for complete dispersion.
(d) 냉각속도 조절을 통한 안정된 (d) stable through cooling rate control 하이브리드hybrid 구상 입자의 제조 Preparation of Spherical Particles
상기 제조된 첨가제가 분산된 고분자 용액을 300 ml 3 구 분리형 반응기에서 200 rpm으로 교반하면서 분당 2 ℃의 냉각속도로 60 ℃에서 25 ℃까지 냉각하여, 4.2 마이크로미터의 평균 입도를 갖는 하이브리드 입자를 제조하였다.The polymer solution prepared with the additives dispersed therein was cooled from 60 ° C. to 25 ° C. at a cooling rate of 2 ° C. per minute while stirring at 200 rpm in a 300 ml three-neck separate reactor, thereby preparing hybrid particles having an average particle size of 4.2 micrometers. It was.
(e) 세척 및 건조(e) washing and drying
상기 제조된 입자를 원심분리를 통한 세척을 실시하여 용액과 입자에 침투하지 못한 산화철을 분리한 후 하이브리드 입자를 수거하고, 이를 질소 분위기에서 30 ~ 40 ℃의 온도로 2 시간 건조하여 분말 상태의 자성 하이브리드 입자를 얻었다.
The prepared particles were washed by centrifugation to separate iron oxides that did not penetrate the solution and the particles, and then the hybrid particles were collected and dried at a temperature of 30 to 40 ° C. in a nitrogen atmosphere for 2 hours to form magnetic powder. Hybrid particles were obtained.
실시예Example 2 2
(a) 단계에서 분자량이 83,000 g/mol인 폴리메틸메타크릴레이트 입자(PDI = 1.67)를 사용한 것을 제외하고는 상기 실시예 1과 동일하게 진행하였다.
In the step (a), the procedure was the same as in Example 1, except that polymethyl methacrylate particles having a molecular weight of 83,000 g / mol (PDI = 1.67) were used.
실시예Example 3 3
(a) 단계에서 139,000 g/mol인 폴리메틸메타크릴레이트 입자(PDI = 1.43)를 사용한 것을 제외하고는 상기 실시예 1과 동일하게 진행하였다.
The same procedure as in Example 1 was carried out except that in step (a), 139,000 g / mol of polymethylmethacrylate particles (PDI = 1.43) was used.
실시예Example 4 4
냉각속도를 분당 2 ℃에서 분당 1 ℃로 조절한 것 외에는 상기 실시예 1과 동일하게 진행하였다.
Cooling rate per minute The procedure was the same as in Example 1 except that the temperature was adjusted to 2 ° C. at 1 ° C. per minute.
실시예Example 5 5
냉각속도를 분당 2 ℃에서 분당 7 ℃로 조절한 것 외에는 상기 실시예 1과 동일하게 진행하였다.
It proceeded in the same manner as in Example 1 except that the cooling rate was adjusted from 2 ° C. per minute to 7 ° C. per minute.
실시예Example 6 6
(a) 단계에서 이용한 고분자 입자를 폴리메틸메타크릴레이트 대신 평균분자량분포가 17,300이고 입자 크기가 1.1 ㎛인 폴리부틸메타크릴레이트(PDI = 1.77)를 사용한 것 이외에는 상기 실시예 1과 동일하게 진행하였다.
The polymer particles used in step (a) were processed in the same manner as in Example 1 except that polybutyl methacrylate (PDI = 1.77) having an average molecular weight distribution of 17,300 and a particle size of 1.1 μm was used instead of polymethyl methacrylate. .
실시예Example 7 7
용매를 메탄올 대신에 메탄올과 과산화수소의 혼합물을 사용한 것 외에는 상기 실시예 1과 동일하게 진행하였다.
The solvent was the same as in Example 1 except that a mixture of methanol and hydrogen peroxide was used instead of methanol.
실시예Example 8 8
고분자 입자 내에 캡슐화시킨 마그헤마이트를 마그네타이트로 사용한 것을 제외하고는 상기 실시예 1과 동일하게 진행하였다.It proceeded in the same manner as in Example 1, except that maghemite encapsulated in the polymer particles was used as the magnetite.
실시예Example 9 9
상기 (c) 단계에서 옥탄에 분산시킨 마그헤마이트를 고분자 용액에 혼합할 때 6.5 g을 사용한 것을 제외하고는 상기 실시예 1과 동일하게 진행하였다.
The same procedure as in Example 1 was performed except that 6.5 g was used to mix the maghemite dispersed in octane in the step (c) in the polymer solution.
비교예Comparative example 1 One
중량평균분자량이 167,000(g/mol)인 폴리메틸메타크릴레이트를 사용한 것을 제외하고는 상기 실시예 1과 동일하게 진행하였다.
The procedure was the same as in Example 1, except that polymethyl methacrylate having a weight average molecular weight of 167,000 (g / mol) was used.
비교예Comparative example 2 2
용매를 메탄올 대신에 물을 사용한 것 외에는 상기 실시예 1과 동일하게 진행하였다.The solvent was the same as in Example 1 except that water was used instead of methanol.
비교예Comparative example 3 3
산화철 나노 입자를 올레익산과 옥탄에 분산시키는 대신 올레익산에 단독으로 분산시킨 것을 제외하고는 상기 실시예 1과 동일하게 진행하였다. The same procedure as in Example 1 was conducted except that the iron oxide nanoparticles were dispersed in oleic acid alone instead of being dispersed in oleic acid and octane.
고분자use
Polymer
평균분자량
(g/mol)weight
Average molecular weight
(g / mol)
산화철양 (g)use
Iron oxide amount (g)
용매use
menstruum
속도
(℃/분)Cooling
speed
(℃ / min)
크기
(㎛)final
size
(Μm)
(wt.%)Iron oxide content in the particles
(wt.%)
H2O2 Methanol /
H 2 O 2
상기 결과를 통해, 자유라디칼 중합을 통하여 제조된 일정 범위의 분자량을 갖는 고분자를 상온에서 불용성인 알코올계 용매에 완전히 분산시키고 가열하여 용해시킨 후, 올레익산과 옥탄에 분산된 산화철 나노입자와 함께 냉각하면 산화철 나노입자가 고분자 입자 내부에 분산된 하이브리드 입자 제조가 가능함을 확인 할 수 있었다. 이러한 입자의 확인은 도 1에 SEM(주사전자현미경) 사진과 도 2의 TEM(투과전자현미경) 사진을 통해 확인할 수 있고, 입자 내부의 산화철 함량은 도 3의 TGA(열중량분석) 그래프를 통해 확인할 수 있다. 또한 사용한 산화철 나노입자의 양과 냉각 속도의 조절을 통해 다양한 산화철 함량과 입자크기를 갖는 하이브리드 입자를 제조할 수 있음을 확인하였다.Through the above results, the polymer having a range of molecular weights prepared through free radical polymerization was completely dispersed in an insoluble alcohol solvent at room temperature, dissolved by heating, and cooled together with iron oxide nanoparticles dispersed in oleic acid and octane. When it was confirmed that the iron oxide nanoparticles can be produced hybrid particles dispersed inside the polymer particles. The identification of such particles can be confirmed through a scanning electron microscope (SEM) photograph and a transmission electron microscope (TEM) photograph of FIG. 2, and the iron oxide content inside the particles is determined through a thermogravimetric analysis (TGA) graph of FIG. You can check it. In addition, it was confirmed that hybrid particles having various iron oxide contents and particle sizes can be prepared by controlling the amount of iron oxide nanoparticles used and the cooling rate.
Claims (8)
(b) 산화철 나노입자를 올레익산과 옥탄을 포함하는 용매에 분산시키는 단계;
(c) 상기 고분자 용액과 산화철 나노입자가 분산된 용액을 혼합하는 단계;
(d) 상기 혼합 용액을 냉각시켜 산화철/고분자 하이브리드 구상입자를 제조하는 단계; 및
(e) 상기 하이브리드 구상입자를 세척 및 건조하여 분말화시키는 단계
를 포함하는 것을 특징으로 하는 안정된 하이브리드 구상입자의 제조방법.
(a) dispersing the polymer particles having a weight average molecular weight of 10,000 to 150,000 g / mol and having a molecular weight distribution (PDI) of 1.0 to 2.0 in a poor solvent and then heating them to prepare a dissolved polymer solution;
(b) dispersing the iron oxide nanoparticles in a solvent comprising oleic acid and octane;
(c) mixing the polymer solution with a solution in which the iron oxide nanoparticles are dispersed;
(d) cooling the mixed solution to produce iron oxide / polymer hybrid spherical particles; And
(e) washing and drying the hybrid spherical particles to powder
Method for producing a stable hybrid spherical particles comprising a.
According to claim 1, wherein the radical polymerizable monomer for preparing the polymer particles used in step (a) is methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, octyl (meth) acrylate , Stearyl (meth) acrylate, benzyl (meth) acrylate, glycidyl (meth) acrylate, fluoroethyl acrylate, trifluoroethyl methacrylate, pentafluoropropyl methacrylate, fluoroethyl methacrylate And hexafluorobutyl (meth) acrylate, hexafluoroisopropyl methacrylate, perfluoroalkyl acrylate, and octafluorophenyl methacrylate.
The method according to claim 1, wherein the dispersion of the polymer particles of step (a) is made in the insoluble state.
The method of claim 1, wherein the heating of the step (a) is a method for producing a hybrid spherical particles, characterized in that made in the temperature range of 40 ℃ ~ 100 ℃.
The poor solvent of step (a) is an alcohol-based poor solvent, or a mixture of an alcohol-based poor solvent and at least one good solvent or a non-solvent, and the alcohol-based poor solvent is methanol, ethanol, iso At least one selected from propyl alcohol, ethylene glycol, butylene glycol, m-cresol, glycerol and nusol, and the good solvent is acetone, benzene, toluene, tetrahydrofuran, cyclohexanone, dioxin, 2-ethoxy Hybrid spherical particles, characterized in that at least one selected from ethanol, ethyl acetate and methylene chloride, wherein the non-solvent is at least one selected from water, hydrogen peroxide, castor oil, cyclohexane, diethyl ether, formamide, gasoline and hexane Manufacturing method.
The method of claim 1, wherein the iron oxide nanoparticles used in the step (b) is a method for producing hybrid spherical particles, characterized in that one or two or more selected from magnetite, maghemite and ferrite.
The method for producing hybrid spherical particles according to claim 1, wherein the iron oxide nanoparticles are used in an amount of 0.1 to 30 parts by weight based on 100 parts by weight of the polymer particles.