KR20120107283A - Nitriding surface treated nuclear fuel powder and dispersion nuclear fuel having the same - Google Patents
Nitriding surface treated nuclear fuel powder and dispersion nuclear fuel having the same Download PDFInfo
- Publication number
- KR20120107283A KR20120107283A KR1020110024879A KR20110024879A KR20120107283A KR 20120107283 A KR20120107283 A KR 20120107283A KR 1020110024879 A KR1020110024879 A KR 1020110024879A KR 20110024879 A KR20110024879 A KR 20110024879A KR 20120107283 A KR20120107283 A KR 20120107283A
- Authority
- KR
- South Korea
- Prior art keywords
- fuel
- nuclear fuel
- alloy powder
- powder
- alloy
- Prior art date
Abstract
Description
본 발명은 표면이 질화처리된 핵연료용 합금 분말 및 이를 포함하는 고밀도 분산 핵연료에 관한 것이다.
The present invention relates to an alloy powder for the surface-nitrided nuclear fuel and a high density dispersed nuclear fuel comprising the same.
우라늄 등의 핵분열 원소를 포함하는 핵연료 금속 분말이 기지 물질에 분산된 형태인 분산 핵연료는 연구로 및 중소형 발전로의 핵연료로 널리 이용되고 있다. 일반적으로 분산 핵연료는 핵연료 합금 분말과 기지 물질 분말을 혼합하고, 혼합 분말을 고압으로 압출성형한 후 판재 형태로 압연하여 제조한다. 이때, 핵연료 합금 분말은 합금 주괴를 기계적인 방법으로 파쇄하여 제조하거나, 고온의 합금 용탕을 고속으로 회전하는 원반에 공급하여 미세한 용적으로 분무시킨 후 이를 급속 응고시켜 분말로 제조하는 원심분무기술을 이용하여 제조하고, 미국 등록특허 US005978432A 및 대한민국 등록특허 10-0279880호에 원심 분무법으로 우라늄 합금 분말을 제조하는 방법이 개시되어 있으며, 제조된 핵연료 합금 분말은 기지 물질에 분산 혼합되어 핵연료로 제조된다.
Dispersed fuels in which nuclear fuel metal powder containing nuclear fission elements such as uranium are dispersed in a known material have been widely used as research fuels and small and medium power plants. In general, the dispersed fuel is prepared by mixing the fuel alloy powder and the powder of the known material, by extrusion molding the mixed powder at a high pressure and then rolling in a plate form. At this time, the nuclear fuel alloy powder is produced by crushing the alloy ingot by mechanical method, or by supplying a hot alloy molten metal to the rotating disk at high speed, spraying it into fine volume, and then rapidly solidifying it to make powder by using centrifugal spraying technology. And a method for producing uranium alloy powder by centrifugal spray method are disclosed in US Patent No. US005978432A and Korean Patent No. 10-0279880, and the prepared nuclear fuel alloy powder is dispersed and mixed in a known material to prepare a nuclear fuel.
분산 핵연료에 있어서, 핵연료 합금 분말은 기지 물질과 밀착되어 존재한다. 핵분열에 의해 핵연료 연소가 시작되면 핵연료의 온도가 올라가고, 또한 핵분열에 의해 발생하는 고 에너지 입자들에 의해 핵연료 합금 분말과 기지 물질 사이에 상호 확산이 일어나며, 이에 따라 핵연료 합금 분말과 기지물질 사이에 반응상이 형성된다. 핵연료 합금 분말과 기지 물질에 사이에 형성되는 반응상은 핵연료 합금과 기지물질에 비하여 밀도가 낮고 열전도도가 낮은 특성을 나타낸다. 이에 따라 낮은 밀도의 반응층이 형성되면 핵연료 부피가 팽창하고, 낮은 열전도도의 반응층에 의해 핵연료 내부에서 발생된 열이 효과적으로 방출되지 않아 핵연료 입자 주변의 온도를 상승시킨다. 핵연료 입자 주변온도가 상승하면 상호 확산이 더욱 촉진되어 반응층의 두께가 증가하고, 핵연료 온도가 증가하는 연쇄반응에 의해 핵연료 팽윤이 급격하게 일어나 핵연료 파손까지 이르게 된다.
In dispersed fuels, the fuel alloy powder is in close contact with the known material. When fuel combustion begins by fission, the temperature of the fuel rises, and the high energy particles generated by the nuclear fission cause mutual diffusion between the fuel alloy powder and the matrix material, thereby reacting between the fuel alloy powder and the matrix material. An image is formed. The reaction phase formed between the fuel alloy powder and the matrix material exhibits lower density and lower thermal conductivity than the fuel alloy and matrix material. Accordingly, when a low density reaction layer is formed, the fuel volume is expanded, and heat generated inside the fuel is not effectively released by the low thermal conductivity reaction layer, thereby increasing the temperature around the fuel particles. As the temperature of the fuel particles increases, the interdiffusion is further promoted to increase the thickness of the reaction layer, and the fuel swelling is suddenly caused by a chain reaction in which the temperature of the fuel increases.
따라서 분산 핵연료에 있어서, 핵연료 합금과 기지 물질 사이의 반응상 형성을 억제하여 반응층의 형성에 의한 핵연료 파손 위험성을 최소화하여야 한다. 핵연료 합금과 기지 물질과의 반응층 성장을 억제하는 방법은 제3의 원소를 사용하는 방법, 반응층의 형성을 억제할 수 있는 보호막을 형성시키는 방법이 있다.Therefore, in the dispersion fuel, it is necessary to suppress the formation of the reaction phase between the fuel alloy and the known material to minimize the risk of nuclear fuel breakage due to the formation of the reaction layer. As a method of suppressing the reaction layer growth between the nuclear fuel alloy and the known material, there are a method using a third element and a method of forming a protective film capable of suppressing the formation of the reaction layer.
제3의 원소를 이용하여 반응층 성장을 억제하는 방법 중 하나로, U-Mo 핵연료 합금이 Al 기지에 분산된 핵연료의 Al 기지에 Si을 첨가하여 반응층 성장 속도를 낮추는 방법이 있다. 이때, 약 5 중량%의 Si을 Al 기지에 첨가하고, 첨가된 Si은 연소 중 핵연료 합금 분말과 기지 물질 사이에 축적되어 Al과 U이 반응하는 것을 방해하는 역할을 한다. 그러나 첨가된 Si이 기지의 열전도도를 낮추어 핵연료 온도를 상승시킬 수 있으며, Si의 재처리가 어려워 사용 후 핵연료 처분이 어려운 문제가 있다.As a method of suppressing the reaction layer growth by using a third element, there is a method of lowering the reaction layer growth rate by adding Si to the Al base of the nuclear fuel in which the U-Mo fuel alloy is dispersed in the Al base. At this time, about 5% by weight of Si is added to the Al base, and the added Si accumulates between the fuel alloy powder and the base material during combustion, and serves to prevent Al and U from reacting. However, the added Si can increase the nuclear fuel temperature by lowering the thermal conductivity of the matrix, and it is difficult to dispose of the spent fuel since the reprocessing of Si is difficult.
반응층 성장을 억제하는 보호막을 형성시키는 방법에는 산화물 층을 이용하는 방법이 있으며, 프랑스 CEA에서는 U-Mo 합금 분말 표면에 산화물 층을 형성시켜 반응을 억제하는 방법을 개발한 바 있다. 그러나 강도가 약한 산화물 층이 핵연료 제조 공정 중 손실되어 반응억제 효과를 나타내지 못하는 문제가 있다. A method of forming a protective film that suppresses the growth of a reaction layer includes a method of using an oxide layer. In France CEA, a method of suppressing a reaction by forming an oxide layer on the surface of a U-Mo alloy powder has been developed. However, there is a problem in that the oxide layer having a weak strength is lost during the fuel manufacturing process and thus does not exhibit a reaction suppression effect.
대한민국 등록특허 제10-0959152호에는 금속 합금 핵연료 봉과 피복관 사이의 반응층 형성을 억제하기 위해 피복관 내측 면에 산화물 또는 질화물을 코팅하는 방법이 개시되어 있으나, 핵연료 합금과 조성이 다른 산화물 또는 질화물을 코팅하므로 단위 부피당 우라늄 장입량을 낮추고, 재처리 부담을 증가시키는 문제가 있다. U-Mo 합금 분말 표면에 Si을 코팅시키는 방법도 연구되고 있으나, 고체-고체 반응을 이용하므로 공정이 복잡하고, 제조 시간이 긴 문제점이 있으며, Si 재처리 문제를 해결하지 못한다.
Korean Patent No. 10-0959152 discloses a method of coating an oxide or nitride on an inner surface of a cladding tube to suppress the formation of a reaction layer between a metal alloy fuel rod and a cladding tube, but coating an oxide or nitride having a composition different from that of the fuel alloy. Therefore, there is a problem of lowering the amount of uranium per unit volume and increasing the reprocessing burden. Although a method of coating Si on the surface of the U-Mo alloy powder is also being studied, the process is complicated because the solid-solid reaction is used, and the manufacturing time is long, and the Si reprocessing problem is not solved.
이에 본 발명자들은 반응상 형성을 억제하여 핵연료 파손 위험성을 최소화할 수 있는 방법을 연구하던 중 핵연료용 합금 분말 표면을 질화처리하여 반응상 형성을 억제할 수 있는 핵연료용 합금 분말을 개발하고, 본 발명을 완성하였다.
Accordingly, the present inventors developed a fuel alloy alloy powder capable of suppressing the reaction phase formation by nitriding the surface of the alloy powder for nuclear fuel while studying a method of minimizing the risk of nuclear fuel damage by suppressing the reaction phase formation. Was completed.
본 발명의 목적은 표면이 질화처리된 핵연료용 합금 분말 및 이를 포함하는 고밀도 분산 핵연료를 제공하는 데 있다.
It is an object of the present invention to provide an alloy powder for nuclear fuel whose surface is nitrided and a high density dispersed nuclear fuel comprising the same.
상기 목적을 달성하기 위하여, 본 발명은 핵연료용 합금 분말과 질소가 반응하여 형성된 질화표면층을 포함하는 핵연료용 합금 분말을 제공한다.
In order to achieve the above object, the present invention provides an alloy powder for nuclear fuel comprising a nitride surface layer formed by reacting the alloy powder for nuclear fuel and nitrogen.
본 발명에 따른 표면이 질화처리된 핵연료용 합금 분말 및 이를 포함하는 고밀도 분산 핵연료는 핵연료 연소 중 핵연료 합금 분말과 기지 물질 사이에 반응층 형성이 효과적으로 억제되어 핵연료의 온도와 팽윤을 효과적으로 낮출 수 있고, 고 연소도에서의 핵연료 건전성 및 안전성이 향상되며, 운전 출력 및 운전 온도를 높일 수 있는 효과가 있다.
The alloy powder for the surface-nitrided fuel according to the present invention and the high-density dispersed fuel comprising the same can effectively reduce the reaction layer formation between the fuel alloy powder and the matrix material during fuel combustion, thereby effectively lowering the temperature and swelling of the fuel, Nuclear fuel integrity and safety at high combustion is improved, and there is an effect of increasing the operating power and operating temperature.
도 1은 본 발명에 따른 핵연료용 합금 분말의 단면을 나타낸 사진이고;
도 2는 본 발명에 따른 분산 핵연료에 있어서, 연료심의 단면을 나타낸 모식도이고;
도 3은 표면이 질화처리되지 않는 핵연료용 합금 분말을 사용하여 제조된 연료심의 단면을 나타낸 모식도이고;
도 4는 본 발명에 따른 분산 핵연료에 있어서, 연료심의 단면을 관찰한 주사전자현미경 사진이고;
도 5는 비교예 1의 분산 핵연료에 있어서, 연료심의 단면을 관찰한 주사전자현미경 사진이고;
도 6은 비교예 2의 분산 핵연료에 있어서, 연료심의 단면을 관찰한 주사전자현미경 사진이다.1 is a photograph showing a cross section of the alloy powder for nuclear fuel according to the present invention;
2 is a schematic diagram showing a cross section of a fuel core in a dispersed fuel according to the present invention;
3 is a schematic view showing a cross section of a fuel core manufactured using an alloy powder for nuclear fuel whose surface is not nitrided;
4 is a scanning electron microscope photograph of a cross section of a fuel core in the dispersion fuel according to the present invention;
5 is a scanning electron microscope photograph of a cross section of a fuel core in the dispersion fuel of Comparative Example 1;
FIG. 6 is a scanning electron microscope photograph of a cross section of a fuel core in the dispersion fuel of Comparative Example 2. FIG.
본 발명은 핵연료용 합금 분말과 질소가 반응하여 형성된 질화표면층을 포함하는 핵연료용 합금 분말을 제공한다.
The present invention provides an alloy powder for nuclear fuel comprising a nitride surface layer formed by reacting an alloy powder for nuclear fuel with nitrogen.
이하, 본 발명을 상세히 설명한다.
Hereinafter, the present invention will be described in detail.
핵연료 합금 분말은 금속 기지에 분산되어 분산 핵연료로 제조될 수 있고, 연구용 원자로 혹은 동력로 등의 핵연료로 이용될 수 있으며, 중소형 발전로용 핵연료로도 이용될 수 있다. 그러나, 금속 기지 내에 핵연료 합금 분말이 분산된 핵연료의 경우 기지 물질과 핵연료 분말 물질 간에 상호 확산이 일어날 수 있고, 반응상 생성의 자유에너지가 음의 값을 가질 경우 확산에 의한 반응상 생성이 용이하여 온도가 올라갈수록 반응상 생성이 더욱 활발해 진다. 특히, 우라늄-몰리브덴(U-Mo) 핵연료 합금 분말이 알루미늄(Al) 기지에 분산된 U-Mo/Al 분산 핵연료는 UAl3 등의 우라늄과 알루미늄 사이의 반응상이 쉽게 생성되고, 형성된 반응상은 우라늄에 비하여 밀도 및 열전도도가 낮다. 밀도가 낮은 반응상이 핵연료 합금 분말과 기지 물질 경계 면에 형성되면 핵연료의 부피가 증가되고, 열전도도가 낮은 반응상이 생성되면 핵연료 합금 분말에서 발생한 열이 외부로 방출되는 속도가 늦어져 핵연료의 온도가 상승하게 된다. 핵연료의 온도 상승은 반응상 형성 속도를 높이고, 핵분열에 의해 생성된 핵분열 기체 팽창을 유발하므로 핵연료의 부피 팽창을 가속화 시켜 핵연료의 파손을 유발하게 된다. 즉, 연소 중 분산 핵연료의 파손이 일어나지 않고 핵연료 건전성을 유지시키기 위해서는 핵연료 합금 분말과 기지 물질의 상호 확산을 억제하여 경계 면에서 생성되는 반응상의 성장을 최소화하는 것이 중요하다.The fuel alloy powder may be dispersed in a metal base to be produced as a dispersed fuel, used as a nuclear fuel for research reactors or power reactors, or as a fuel for small and medium power plants. However, in the case of nuclear fuel in which a fuel alloy powder is dispersed in a metal base, cross diffusion between the base material and the fuel powder material may occur, and when the free energy of reaction phase generation has a negative value, the reaction phase is easily generated by diffusion. As temperature rises, reaction phase formation becomes more active. In particular, U-Mo / Al dispersed fuel in which uranium-molybdenum (U-Mo) fuel alloy powder is dispersed at an aluminum (Al) base easily generates a reaction phase between uranium such as UAl 3 and aluminum, and the formed reaction phase is formed in uranium. Compared with the lower density and thermal conductivity. When the low density reaction phase is formed at the interface between the fuel alloy powder and the matrix, the volume of the fuel is increased. When the reaction phase with low thermal conductivity is generated, the heat generated from the fuel alloy powder is released to the outside, and thus the temperature of the fuel is increased. Will rise. Increasing the temperature of the fuel increases the reaction phase formation rate and causes the fission gas expansion generated by the fission, thereby accelerating the volume expansion of the fuel to cause breakage of the fuel. That is, it is important to minimize the growth of the reaction phase generated at the interface by suppressing the interdiffusion of the fuel alloy powder and the matrix material in order to maintain the fuel integrity without breaking the dispersed fuel during combustion.
한편, 질화 우라늄에서 우라늄의 자기 확산 속도는 방향성을 지닌 전자간의 공유 결합 특성에 의해 우라늄 금속에서의 우라늄 자기 확산 속도보다 매우 낮다. 자기 확산 속도가 낮을수록 상호 확산 속도도 낮으므로, 우라늄 합금 표면에 질화물 층을 형성시키면 질화물 층이 우라늄과 알루미늄의 상호 확산을 방지하는 방어막 역할을 하여 반응상의 생성을 억제할 수 있다. 이에 본 발명은 핵연료용 합금 분말과 질소가 반응하여 도 1의 사진과 같이 표면이 질화처리된 질화표면층을 구비하는 핵연료용 합금 분말을 제공한다. 본 발명에 따른 핵연료용 합금 분말은 질화표면층에 의하여 기지물질과의 반응층 형성을 억제할 수 있다. 또한, 반응층 형성을 억제함으로써 핵연료의 연소 중 반응상 생성에 의한 핵연료 부피 팽창이나 온도 상승을 억제할 수 있고 핵연료의 안전성을 향상시킬 수 있으며, 운전 출력 및 운전 온도를 높일 수 있는 장점이 있다. On the other hand, the uranium self-diffusion rate in uranium nitride is much lower than the uranium self-diffusion rate in uranium metal due to the covalent bonding property between the directional electrons. The lower the self-diffusion rate, the lower the interdiffusion rate. Therefore, when the nitride layer is formed on the surface of the uranium alloy, the nitride layer serves as a protective film to prevent the interdiffusion of uranium and aluminum, thereby suppressing the formation of the reaction phase. Accordingly, the present invention provides an alloy powder for nuclear fuel having a nitride surface layer whose surface is nitrided by reacting nitrogen with the alloy powder for nuclear fuel. The alloy powder for nuclear fuel according to the present invention can suppress the formation of the reaction layer with the matrix by the nitride surface layer. In addition, by suppressing the formation of the reaction layer, it is possible to suppress the fuel volume expansion or the temperature rise due to the formation of the reaction phase during combustion of the fuel, to improve the safety of the fuel, and to increase the operating output and the operating temperature.
본 발명에 따른 핵연료용 합금 분말은 핵연료용 합금 분말은 우라늄, 토륨, 플루토늄, 아메리슘, 넵티늄 및 퀴륨으로 이루어지는 군으로부터 선택되는 1종 이상의 합금원소를 포함하고, The alloy powder for nuclear fuel according to the present invention, the alloy powder for nuclear fuel includes one or more alloying elements selected from the group consisting of uranium, thorium, plutonium, americium, neptinium, and curium,
상기 핵연료용 합금 분말은 추가적으로 열적?기계적 안정화를 위해 몰리브덴, 지르코늄, 티타늄, 실리콘, 철, 크롬, 바나듐, 니오븀, 루테늄, 팔라듐, 텅스텐 및 탄탈륨으로 이루어진 군으로부터 선택되는 1종 이상의 합금원소를 더 포함한다. The fuel alloy powder further includes one or more alloying elements selected from the group consisting of molybdenum, zirconium, titanium, silicon, iron, chromium, vanadium, niobium, ruthenium, palladium, tungsten and tantalum for thermal and mechanical stabilization. do.
본 발명에 따른 핵연료용 합금 분말에 있어서, 상기 질화표면층은 핵연료용 합금 분말과 질소를 반응시켜 생성되고 핵연료용 합금 분말과 질소만을 포함하는 층으로 상기 핵연료용 합금 분말과 질소 외의 어떠한 원소도 포함하지 않으며, 핵연료 합금 분말에 포함된 원소 중 1종 이상을 포함한다. 즉, 질화표면층 또한 핵연료 합금 분말을 구성하는 물질로 이루어지고, 이에 따라 핵연료 합금 분말의 밀도가 낮아지지 않는다.In the fuel alloy powder according to the present invention, the nitride surface layer is formed by reacting the fuel alloy powder with nitrogen and contains only the alloy powder for fuel and nitrogen and does not contain any elements other than the alloy powder for fuel and nitrogen. And at least one of the elements contained in the fuel alloy powder. In other words, the nitride surface layer is also made of a material constituting the fuel alloy powder, so that the density of the fuel alloy powder is not lowered.
상기 질화표면층의 두께는 0.1 내지 300 μm인 것이 바람직하다. 만약 질화표면층의 두께가 0.1 μm 미만인 경우에는 질화표면층의 얇은 두께로 인하여 기지물질과의 반응층 형성 억제 효과가 나타나지 않는 문제가 있고, 질화표면층의 두께가 300 μm를 초과하는 경우에는 질화층의 건전성이 저하될 수 있다.
The thickness of the nitride surface layer is preferably 0.1 to 300 μm. If the thickness of the nitride surface layer is less than 0.1 μm, there is a problem in that the reaction layer formation inhibition effect with the known material does not appear due to the thin thickness of the nitride surface layer, and if the thickness of the nitride surface layer exceeds 300 μm, the integrity of the nitride layer This can be degraded.
또한, 본 발명은 핵연료용 합금 분말을 제조한 후 제조된 핵연료용 합금 분말을 질소분위기에서 열처리하는 것을 특징으로 하는 표면이 질화처리된 핵연료용 합금 분말의 제조방법을 제공한다.
The present invention also provides a method for producing a surface-nitrided alloy powder for nuclear fuel, characterized in that after the preparation of the alloy powder for nuclear fuel, the prepared alloy powder for fuel is heat treated in a nitrogen atmosphere.
본 발명에 따른 표면이 질화처리된 핵연료용 합금 분말의 제조방법에 있어서, 상기 핵연료용 합금 분말은 원심분무법 또는 분쇄에 의하여 제조될 수 있다.In the method for producing a surface-nitrided nuclear fuel alloy powder according to the present invention, the nuclear fuel powder may be prepared by centrifugal spraying or grinding.
상기 원심분무법은 핵연료용 합금을 고온으로 용융한 후 고속으로 회전하는 원판에 용탕을 붓고, 생성된 입자를 냉각하여 분말화함으로써 수행될 수 있으며, 상기 분쇄는 핵연료용 합금 잉곳을 분쇄하여 수행될 수 있다. The centrifugal spraying method may be performed by melting the alloy for nuclear fuel at a high temperature, pouring molten metal into a rotating disk at high speed, and cooling the resulting particles to cool the powder, and pulverizing the alloy ingot for nuclear fuel. have.
본 발명에 따른 표면이 질화처리된 핵연료용 합금 분말의 제조방법에 있어서, 제조된 핵연료용 합금 분말은 질소분위기에서 열처리된다. 상기 열처리는 질소분위기에서 수행되어 핵연료용 합금 분말의 표면을 질화처리할 수 있고, 상기 질소분위기는 순수한 질소 분위기 또는 헬륨(He), 네온(Ne), 알곤(Ar), 크립톤(Kr), 제논(Xe) 및 수소 기체로 이루어진 군으로부터 선택되는 1종 이상인 기체를 더 포함할 수 있으며, 반응속도 및 질화표면층 두께 조절을 위하여 질소의 비율을 적절히 조절하여 열처리를 수행할 수 있다. In the method for producing a surface-nitrided nuclear fuel alloy powder according to the present invention, the prepared nuclear fuel powder is heat-treated in a nitrogen atmosphere. The heat treatment may be performed in a nitrogen atmosphere to nitride the surface of the alloy powder for nuclear fuel, and the nitrogen atmosphere may be a pure nitrogen atmosphere or helium (He), neon (Ne), argon (Ar), krypton (Kr), xenon (Xe) and may further include at least one gas selected from the group consisting of hydrogen gas, heat treatment may be performed by appropriately adjusting the ratio of nitrogen for the reaction rate and the nitride surface layer thickness control.
상기 열처리는 300 내지 1500 ℃의 온도에서 수행될 수 있고, 더욱 바람직하게는 800 내지 1200℃의 온도에서 수행될 수 있으며, 질화표면층의 두께를 고려하여 상기 범위 내에서 적절하게 조절할 수 있다. 만약 상기 열처리가 300 ℃ 미만의 온도에서 수행되는 경우, 핵연료용 합금 분말의 표면이 질화처리 되지 않는 문제가 있고, 상기 열처리가 1500 ℃를 초과하는 온도에서 수행되는 경우, 핵연료 합금 조성에 따라 핵연료 분말의 용융이 일어날 수 있다.
The heat treatment may be carried out at a temperature of 300 to 1500 ℃, more preferably may be carried out at a temperature of 800 to 1200 ℃, can be appropriately adjusted within the above range in consideration of the thickness of the nitride surface layer. If the heat treatment is carried out at a temperature of less than 300 ℃, there is a problem that the surface of the alloy powder for nuclear fuel is not nitrided, if the heat treatment is performed at a temperature exceeding 1500 ℃, the fuel powder according to the fuel alloy composition Melting may occur.
한편, 상기 핵연료용 합금 분말로 염화암모늄 분말을 첨가한 후 진공분위기, 불활성기체 분위기 또는 질소분위기에서 열처리하여 표면이 질화처리된 핵연료용 합금 분말을 제조할 수 있다. 상기 염화암모늄 분말은 활성화제 역할을 수행하며, 염화암모늄 분말을 첨가한 핵연료용 합금 분말을 진공분위기, 불활성기체 분위기 또는 질소분위기에서 열처리하여 본 발명에 따른 핵연료용 합금 분말을 제조할 수 있다.
Meanwhile, after adding ammonium chloride powder to the alloy powder for nuclear fuel, the alloy powder for nitriding the surface may be manufactured by heat treatment in a vacuum atmosphere, an inert gas atmosphere, or a nitrogen atmosphere. The ammonium chloride powder serves as an activator, and the alloy powder for nuclear fuel added with ammonium chloride powder may be heat-treated in a vacuum atmosphere, an inert gas atmosphere, or a nitrogen atmosphere to prepare the alloy powder for nuclear fuel according to the present invention.
본 발명은 알루미늄 금속기지 물질에 핵연료 합금 분말 표면이 질화처리된 상기 핵연료 합금 분말이 분산된 연료심; 및The present invention is a fuel core in which the fuel alloy powder in which the surface of the fuel alloy powder is nitrided in an aluminum metal base material is dispersed; And
상기 연료심을 환형 또는 판형으로 둘러싸고 있는 피복재를 포함하는 분산 핵연료를 제공한다.
It provides a distributed fuel comprising a coating material surrounding the fuel core in an annular or plate shape.
본 발명에 따른 분산 핵연료는 표면이 질화처리된 핵연료용 합금 분말을 금속기지 물질에 분산시켜 제조된 연료심 및 상기 연료심을 환형 또는 판형으로 둘러싸는 피복재를 포함하여, 핵연료 합금 분말과 기지 물질 사이에 반응층 형성이 효과적으로 억제되고, 핵연료의 온도와 팽윤을 효과적으로 낮출 수 있으며, 고 연소도에서의 핵연료 건전성 및 안전성이 향상되어 운전 출력 및 운전 온도를 높일 수 있다.The dispersed fuel according to the present invention includes a fuel core prepared by dispersing a surface-nitrided alloy powder for nuclear fuel in a metal-based material, and a coating material surrounding the fuel core in an annular or plate shape, between the fuel alloy powder and the matrix material. Formation of the reaction layer can be effectively suppressed, the temperature and swelling of the fuel can be effectively lowered, and the fuel integrity and safety at high combustion degree can be improved to increase operating output and operating temperature.
상기 연료심은 본 발명에 따른 표면이 질화처리된 핵연료용 합금 분말을 알루미늄(Al) 기지에 분산시켜 제조될 수 있으나, 금속기지가 이에 제한되는 것은 아니다. 본 발명에 따른 표면이 질화처리된 핵연료용 합금 분말을 금속기지 물질에 분산시켜 제조된 연료심의 단면을 도 2의 모식도를 통해 나타내었고, 표면이 질화처리되지 않은 핵연료용 합금 분말을 금속기지 물질에 분산시켜 제조된 연료심의 단면을 도 3의 모식도를 통해 나타내었다.The fuel core may be prepared by dispersing the alloy powder for nuclear fuel treated with the surface according to the present invention on an aluminum (Al) base, but the metal base is not limited thereto. A cross section of a fuel core prepared by dispersing the surface-nitrided nuclear fuel powder according to the present invention in a metal-based material is shown through the schematic diagram of FIG. 2. The cross section of the fuel core prepared by dispersing is shown through the schematic diagram of FIG. 3.
상기 피복관은 연료심을 환형 또는 판형으로 둘러싸고 있으며, 알루미늄 합금으로 이루어진 긴 튜브 또는 판형 형태로 제조될 수 있으나, 이에 제한되는 것은 아니다.
The cladding tube surrounds the fuel core in an annular or plate shape, and may be manufactured in an elongated tube or plate shape made of aluminum alloy, but is not limited thereto.
본 발명에 따른 분산 핵연료는 표면이 질화처리된 핵연료 합금 분말을 사용하여 연료심을 제조함으로써, 핵연료 분말과 금속기지 사이의 반응상 생성이 현저하게 억제할 수 있고, 이에 따라 핵연료의 온도와 팽윤을 효과적으로 낮출 수 있다. 또한, 고 연소도에서의 핵연료 건전성 및 안전성이 향상되어 높은 운전 출력 및 운전 온도에서 연소될 수 있다.
In the dispersed fuel according to the present invention, by producing a fuel core using a surface-nitrided fuel alloy powder, the reaction phase between the fuel powder and the metal base can be remarkably suppressed, thereby effectively reducing the temperature and swelling of the fuel. Can be lowered. In addition, fuel integrity and safety at high combustion levels can be improved to allow combustion at high operating power and operating temperatures.
본 발명은 알루미늄 분말과 표면이 질화처리된 제1항의 핵연료 합금 분말을 혼합한 후 성형 또는 압출하여 연료심을 제조하는 단계(단계 1); 및The present invention comprises the steps of preparing a fuel core by mixing the aluminum powder and the fuel alloy powder of claim 1, the surface is nitrided, followed by molding or extrusion; And
상기 단계 1에서 제조된 연료심 외주면을 피복재로 둘러싼 후 동심 압축 또는 압연하여 분산 핵연료를 제조하는 단계(단계 2)를 포함하는 것을 특징으로 하는 분산 핵연료의 제조방법을 제공한다.
Comprising a fuel core outer circumferential surface prepared in step 1 and covering the concentric material, and concentric compression or rolling provides a method for producing dispersed fuel comprising the step (step 2) of producing a dispersed fuel.
본 발명에 따른 분산 핵연료의 제조방법에 있어서, 단계 1은 알루미늄 분말과 표면이 질화처리된 제1항의 핵연료 합금 분말을 혼합한 후 성형 또는 압출하여 연료심을 제조하는 단계이다. 상기 단계 1에서 제조되는 연료심은 본 발명의 표면이 질화처리된 핵연료 합금 분말을 기지 물질인 알루미늄 분말에 분산시켜 제조됨으로써, 핵연료 합금 분말과 알루미늄 사이의 반응층 형성이 억제되어 핵연료의 온도와 팽윤을 낮출 수 있다.
In the method for producing dispersed fuel according to the present invention, step 1 is a step of preparing a fuel core by mixing or extruding aluminum powder and the nuclear fuel alloy powder of claim 1, wherein the surface is nitrided. The fuel core prepared in step 1 is prepared by dispersing the surface of the present invention, the nitrided nuclear fuel alloy powder in a known material aluminum powder, thereby suppressing the formation of a reaction layer between the nuclear fuel alloy powder and aluminum, thereby reducing the temperature and swelling of the nuclear fuel. Can be lowered.
본 발명에 따른 분산 핵연료의 제조방법에 있어서, 단계 2는 상기 단계 1에서 제조된 연료심 외주면을 피복재로 둘러싼 후 동심 압출 또는 압연하여 분산 핵연료를 제조하는 단계이다. 이때, 동심 압출 또는 압연을 통해 분산 핵연료를 선재 또는 판재와 같은 원하는 형태로 성형가공할 수 있다.
In the method for producing dispersed fuel according to the present invention, step 2 is a step of preparing dispersed nuclear fuel by surrounding the fuel core outer circumferential surface prepared in step 1 with a coating material and then concentrically extruding or rolling. At this time, the dispersed nuclear fuel may be formed into a desired shape such as wire or plate by concentric extrusion or rolling.
이하, 본 발명을 실시예를 통해 보다 구체적으로 설명한다. 그러나, 하기 실시예는 본 발명을 설명하기 위한 것일 뿐, 하기 실시예에 의하여 본 발명의 권리범위가 한정되는 것은 아니다.
Hereinafter, the present invention will be described more specifically by way of examples. However, the following examples are intended to illustrate the present invention, but the scope of the present invention is not limited by the following examples.
<실시예 1> 표면이 질화처리된 핵연료 합금 분말의 제조Example 1 Preparation of Nuclear Fuel Alloy Powders Surface-Treated
단계 1 : 원심 분무 장치를 이용하여 구형의 우라늄(U)93중량% - 몰리브덴(Mo) 7중량%인 합금 분말을 1kg을 제조하였다.
Step 1: Using a centrifugal spray apparatus, 1 kg of an alloy powder of 93% by weight of spherical uranium (U) to 7% by weight of molybdenum (Mo) was prepared.
단계 2 : 상기 단계 1의 핵연료 합금 분말 중 20 g을 알루미나 용기에 장입하고 반응 온도인 970 ℃까지 300 ℃/h의 속도로 가열하였다. 상기 가열은 아르곤(Ar) 기체 분위기에서 수행하였고, 아르곤(Ar) 기체와 핵연료 합금 분말이 고르게 접촉할 수 있도록 알루미나 용기 하단으로 장착된 주입구를 통해 아르곤(Ar) 기체를 주입하였으며, 아르곤 기체는 핵연료 합금 분말을 통과하여 배기구를 통해 배출하였다. 핵연료 합금 분말의 온도가 반응 온도인 970 ℃에 도달하면 970 ℃의 온도에서 30분 동안 질화 열처리를 수행하였고, 상기 질화 열처리는 질소(N2) 기체가 아르곤(Ar) 기체에 1/20의 부피비로 혼합된 혼합기체 분위기에서 수행하여 표면이 질화처리된 핵연료 합금 분말을 제조하였다. 이때, 제조된 핵연료 합금 분말의 질화표면층의 두께는 20 μm였다.
Step 2: 20 g of the fuel alloy powder of Step 1 was charged to an alumina vessel and heated to a reaction temperature of 970 ° C. at a rate of 300 ° C./h. The heating was performed in an argon (Ar) gas atmosphere, and argon (Ar) gas was injected through an inlet mounted at the bottom of the alumina container so that the argon (Ar) gas and the fuel alloy powder could be uniformly contacted, and the argon gas was a nuclear fuel. Passed through the alloy powder and discharged through the exhaust port. When the temperature of the nuclear fuel alloy powder reached the reaction temperature of 970 ° C., the nitriding heat treatment was performed for 30 minutes at the temperature of 970 ° C., wherein the nitriding heat treatment had a volume ratio of 1/20 to argon (Ar) gas in nitrogen (N 2 ) gas. It was carried out in a mixed gas atmosphere mixed with to prepare a surface-nitrided nuclear fuel alloy powder. At this time, the thickness of the nitride surface layer of the prepared nuclear fuel alloy powder was 20 μm.
<실시예 2> 분산 핵연료의 제조 1Example 2 Preparation of Dispersed Fuel 1
단계 1 : 상기 실시 예 1의 단계 2 에서 제조된 핵연료 합금 분말 20 g을 알루미늄 분말 7 g과 혼합한 후 이를 성형하여 연료심을 제조하였다.
Step 1: The fuel core was manufactured by mixing 20 g of the nuclear fuel alloy powder prepared in Step 2 of Example 1 with 7 g of aluminum powder and then molding it.
단계 2 : 상기 단계 1에서 제조된 연료심을 스테인리스 강으로 이루어진 피복관으로 둘러싼 후 압연하여 긴 튜브형태의 분산 핵연료를 제조하였다.
Step 2: The fuel core prepared in Step 1 was surrounded by a cladding tube made of stainless steel, and then rolled to prepare dispersed nuclear fuel in the form of a long tube.
<비교예 1> 분산 핵연료의 제조 2Comparative Example 1 Production of Dispersed Fuel 2
상기 실시예 1의 단계 1에서 제조된 핵연료 합금 분말 20g을 질화처리 하지 않고 알루미늄 분말과 혼합하여 연료심을 제조한 것을 제외하고는 상기 실시예 2와 동일하게 수행하여 분산 핵연료를 제조하였다.
20 g of the nuclear fuel alloy powder prepared in Step 1 of Example 1 was prepared in the same manner as in Example 2 except that the fuel core was prepared by mixing with aluminum powder without nitriding to prepare a dispersed fuel.
<비교예 2> 분산 핵연료의 제조 3Comparative Example 2 Production of Dispersed Fuels 3
상기 실시예 1의 단계 1에서 제조된 핵연료 합금 분말 20g, 알루미늄 분말 6.65g, 실리콘(Si) 분말 0.35g을 함께 혼합하여 연료 심을 제조한 것을 제외하고는 상기 실시예 2와 동일하게 수행하여 분산 핵연료를 제조하였다.
Dispersion fuel was carried out in the same manner as in Example 2, except that 20 g of the nuclear fuel alloy powder prepared in Step 1 of Example 1, 6.65 g of aluminum powder, and 0.35 g of silicon (Si) powder were mixed together to prepare a fuel shim. Was prepared.
<실험 예 1> 주사전자현미경 분석Experimental Example 1 Scanning Electron Microscope Analysis
본 발명에 따른 실시예 2 및 비교예 1 내지 2의 단계 1에서 제조된 연료심을 580 ℃의 온도에서 5시간 동안 열처리한 후 핵연료 분말과 기지 물질 경계 면에서의 반응상 생성 양상을 주사전자현미경을 이용하여 관찰하였고, 그 결과를 도 4 내지 도 6에 나타내었다.After the heat treatment of the fuel core prepared in Example 2 and Step 1 of Comparative Examples 1 to 2 for 5 hours at a temperature of 580 ℃, the reaction phase generation pattern at the interface between the fuel powder and the matrix material is a scanning electron microscope It observed using, and the results are shown in FIGS.
도 4 내지 도 6에 나타낸 바와 같이, 실시예 2의 단계 1에서 제조된 연료심은 질화표면층이 열처리 후에도 존재하고 있음을 알 수 있고, 새로운 반응상이 형성되지 않은 것을 알 수 있다. 그러나, 비교예 1의 단계 1에서 제조된 연료심의 경우 열처리 후 약 400 μm 두께의 반응층이 형성된 것을 알 수 있고, 비교예 2의 단계 1에서 제조된 연료심의 경우 열처리 후 약 40 μm 두께의 반응층이 형성된 것을 알 수 있다. 이를 통하여, 본 발명에 따른 표면이 질화처리된 핵연료용 합금 분말을 이용하여 분산 핵연료를 제조함으로써 핵연료 합금 분말과 기지 물질 사이에 반응층 형성이 효과적으로 억제할 수 있음을 알 수 있었고, 반응층 형성이 억제됨에 따라 핵연료의 온도와 팽윤을 효과적으로 낮출 수 있어 본 발명에 따른 분산 핵연료의 건전성 및 안전성을 향상시킬 수 있음을 확인하였다.As shown in Figures 4 to 6, the fuel core prepared in step 1 of Example 2 can be seen that the nitride surface layer is present after the heat treatment, it can be seen that no new reaction phase is formed. However, in the case of the fuel core manufactured in step 1 of Comparative Example 1, it can be seen that a reaction layer having a thickness of about 400 μm was formed after the heat treatment, and the reaction of the fuel core prepared in step 1 of Comparative Example 2 had a thickness of about 40 μm after the heat treatment. It can be seen that a layer is formed. Through this, it was found that by producing dispersed fuel using the alloy powder for the surface-nitrided fuel according to the present invention, the formation of the reaction layer between the fuel alloy powder and the matrix material can be effectively suppressed. As it is suppressed, it was confirmed that the temperature and swelling of the nuclear fuel can be effectively lowered, thereby improving the soundness and safety of the dispersed fuel according to the present invention.
Claims (10)
An alloy powder for nuclear fuel comprising a nitride surface layer formed by reaction of an alloy powder for nuclear fuel with nitrogen.
The alloy for nuclear fuel according to claim 1, wherein the alloy powder for nuclear fuel comprises at least one alloying element selected from the group consisting of uranium, thorium, plutonium, americium, neptinium, and curium. powder.
The method of claim 2, wherein the alloy powder for fuel further comprises at least one alloy element selected from the group consisting of molybdenum, zirconium, titanium, silicon, iron, chromium, vanadium, niobium, ruthenium, palladium, tungsten and tantalum. Alloy powder for nuclear fuel comprising a nitride surface layer, characterized in that.
The alloy powder for nuclear fuel according to claim 1, wherein the nitride surface layer has a thickness of 0.1 to 300 μm.
A method of producing a surface-nitrided alloy powder for nuclear fuel, characterized in that after the preparation of the alloy powder for nuclear fuel, the prepared fuel alloy powder is heat-treated in a nitrogen atmosphere.
6. The method of claim 5, wherein the alloy powder for nuclear fuel is prepared by centrifugal spraying or pulverization.
The method of claim 5, wherein the nitrogen atmosphere is at least one gas selected from the group consisting of helium (He), neon (Ne), argon (Ar), krypton (Kr), xenon (Xe) and hydrogen gas in addition to nitrogen. Method for producing an alloy powder for the surface-nitrided nuclear fuel characterized in that it further comprises.
The method of claim 5, wherein the heat treatment is performed at a temperature of 300 to 1500 ° C. 6.
상기 연료심을 환형 또는 판형으로 둘러싸고 있는 피복재를 포함하는 분산 핵연료.
A fuel core in which the nuclear fuel alloy powder of claim 1, wherein the surface is nitrided on an aluminum base; And
Dispersed fuel comprising a coating material surrounding the fuel core in an annular or plate shape.
상기 단계 1에서 제조된 연료심 외주면을 피복재로 둘러싼 후 동심압출 또는 압연하여 분산 핵연료를 제조하는 단계(단계 2)를 포함하는 것을 특징으로 하는 분산 핵연료의 제조방법.Preparing a fuel core by mixing the aluminum powder and the nuclear fuel alloy powder of claim 1, wherein the surface is nitrided and then molded or extruded (step 1); And
Comprising the fuel core outer peripheral surface prepared in step 1 and covering the concentric material and then concentric extrusion or rolling to produce a dispersed nuclear fuel comprising the step (step 2).