KR20120028696A - Waterproof and berathable fabric having deodrant and antistatic, and a method of fabricating the same - Google Patents
Waterproof and berathable fabric having deodrant and antistatic, and a method of fabricating the same Download PDFInfo
- Publication number
- KR20120028696A KR20120028696A KR1020100090700A KR20100090700A KR20120028696A KR 20120028696 A KR20120028696 A KR 20120028696A KR 1020100090700 A KR1020100090700 A KR 1020100090700A KR 20100090700 A KR20100090700 A KR 20100090700A KR 20120028696 A KR20120028696 A KR 20120028696A
- Authority
- KR
- South Korea
- Prior art keywords
- deodorant
- fabric
- moisture
- antistatic
- hydrophilic non
- Prior art date
Abstract
Description
본 발명은 소취성 및 제전성을 가지는 투습방수 직물 및 그의 제조방법에 관한 것으로 직물에 친수무공형 폴리우레탄계 수지로 코팅하여 투습도 및 내수도가 우수하면서 소취성 및 제전성을 가지는 투습방수 직물 및 그의 제조방법에 관한 것이다.
The present invention relates to a moisture-permeable waterproof fabric having a deodorant and antistatic properties, and a method for manufacturing the same, which is coated with a hydrophilic non-porous polyurethane-based resin on the fabric and has excellent moisture permeability and water resistance, and has a deodorant and antistatic property, and It relates to a manufacturing method.
일반적으로 투습방수 직물은 100㎛의 빗방울이 섬유 밖에서 섬유 안으로 통과 못하게 하고 몸의 체내에서 방출되는 0.004㎛의 수분을 섬유 안에서 섬유 밖으로 나갈 수 있도록 피막층을 직물위에 형성시켜 투습성과 방수성 등이 우수한 스포츠웨어, 군복, 텐트 등에 사용되는 직물을 의미한다.In general, moisture-permeable fabric is a sportswear that has excellent moisture permeability and waterproofness by forming a coating layer on the fabric so that raindrops of 100 μm do not pass into the fiber from the outside of the fiber and 0.004 μm of moisture released from the body can flow out of the fiber in the fiber. Means fabrics used in military uniforms, tents, etc.
투습방수 기능을 갖도록 하는 방법은 라미네이팅(Laminating) 방식에 의한 PTFE 미세다공 성막법과 다이렉트 코팅방식에 의한 폴리우레탄 미다공 성막법, 그리고 초고밀도 직물에 의한 방법 등으로 크게 나눌 수 있다. 폴리우레탄을 이용한 다이렉트 코팅방식에 의한 종래의 투습방수직물은 DMF(디메칠포름아미드) 및 MEK(메틸에틸케톤) 등과 같이 환경에 유해한 솔벤트를 사용함으로써 환경오염을 초래하는 원인이 되어 최근에는 수분산형 폴리우레탄 코팅액을 이용하고 다단 건조하여 건식다공형 투습방수포를 제작법과 친수무공형의 폴리우레탄을 이용한 건식코팅법이 연구되고 있다.Methods to have a moisture-permeable waterproof function can be broadly divided into a PTFE microporous film forming method by the laminating method, a polyurethane microporous film forming method by the direct coating method, and an ultra high density fabric method. The conventional moisture-permeable waterproof fabric by direct coating method using polyurethane is the cause of environmental pollution by using environmentally harmful solvents such as DMF (dimethylformamide) and MEK (methyl ethyl ketone). The method of manufacturing a dry porous permeable waterproof fabric by using a polyurethane coating solution and drying in multiple stages and a dry coating method using a hydrophilic non-porous polyurethane have been studied.
친수무공형 폴리우레탄을 이용한 투습방수직물의 종래기술로 대한민국 등록특허 제0795386호의 '친수무공형 투습방수포'에서는 폴리에틸렌글리콜(Polyethylene Glycol) 또는 폴리프로필렌글리콜(Polyprophylene Glycol)의 소프트세그먼트(soft segment)의 폴리올(Polyol)을 갖는 친수무공형 폴리우레탄 수지를 사용하여 건식코팅법에 의한 투습성이 우수한 방수포를 기재하였고, 대한민국 공개특허 제2008-0042309호는 '투습방수용 코팅조성물, 이를 이용한 건식무공형투습 방수원단 및 이의 제조방법'에는 친수무공형 폴리우레탄을 원단-코팅층의 2단계 제조공정으로 코팅하여 생산성 향상, 환경오염 감소 및 우수한 코팅 품질을 확보할 수 있는 코팅법을 제안한다. As a conventional technology of a moisture-permeable waterproof fabric using a hydrophilic non-porous polyurethane, in the 'hydrophilic non-porous moisture-proof cloth' of Korean Patent No. 0795386, a soft segment of polyethylene glycol or polyproplyylene glycol is used. Using a hydrophilic non-porous polyurethane resin having a polyol has described a waterproof cloth having excellent moisture permeability by the dry coating method, Korean Patent Laid-Open No. 2008-0042309 discloses a coating composition for moisture-permeable waterproof, dry non-porous moisture-permeable waterproof using the same. Fabric and its manufacturing method is proposed a coating method that can be coated with a hydrophilic non-porous polyurethane in a two-step manufacturing process of the fabric-coating layer to improve productivity, reduce environmental pollution and ensure excellent coating quality.
또한, 대한민국 등록특허 제0823630호 투습 및 발수성이 우수한 직물 및 그의 제조과정에서는 광경화형 불소계 발수발유제를 패딩처리한 후 스크린 메쉬를 이용하여 선택적 자외선 조사에 의한 투습발수직물을 제조하는 방법을 제안하였다.In addition, the Republic of Korea Patent No. 0831630 has excellent water vapor permeability and water-repellent fabric and a process of manufacturing the water-repellent water-repellent fabric by selective ultraviolet irradiation using a screen mesh after padding the photo-curing fluorine-based water and oil repellent was proposed. .
상기의 친수무공형 폴리우레탄을 이용한 건식코팅법은 환경오염 문제에서는 자유롭지만 세탁 내구성이 약한 단점을 지니고, 소취성에 취약하고, 제전공정이 어려운 문제가 있었다.The dry coating method using the hydrophilic non-porous polyurethane has the disadvantages of free from environmental pollution problems, but weak washing durability, vulnerable to deodorization, and difficult to antistatic process.
또한 대부분의 폴리우레탄 수지를 사용하는 투습방수 직물은 열경화를 위해 유기용매를 사용하지만, 유기용매는 열경화과정에서 원단의 염료가 유기용매에 의해 빠져나가 불량율을 높이는 문제가 있으며, 환경오염을 유발시키는 문제가 있었다.
In addition, most moisture-permeable waterproof fabrics using polyurethane resins use organic solvents for thermal curing. However, organic solvents have a problem in that dyes of fabrics are released by organic solvents during thermal curing to increase the defective rate. There was a problem that caused it.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로써, 본 발명은 폴리우레탄 수지를 사용하면서 소취성 및 제전성을 가지는 투습방수 직물을 제공하는 것을 목적으로 한다.The present invention is to solve the above problems, it is an object of the present invention to provide a moisture-permeable waterproof fabric having a deodorant and antistatic properties while using a polyurethane resin.
또한, 본 발명은 광경화로 폴리우레탄 수지를 직물에 부착시켜 유기용매를 사용하지 않는 친환경적인 소취성 및 제전성을 가지는 투습방수 직물의 제조방법을 제공하는 것을 목적으로 한다.In addition, an object of the present invention is to provide a method for producing a moisture-permeable waterproof fabric having an environmentally friendly deodorant and antistatic properties without using an organic solvent by attaching a polyurethane resin to the fabric by photocuring.
또한, 직물상에 친수무공형 폴리우레탄 수지를 도포하여 투습도 및 내수도가 우수한 소취성 및 제전성을 가지는 투습방수 직물 및 그 제조방법을 제공하는 것을 목적으로 한다.
Another object of the present invention is to provide a moisture-permeable waterproof fabric having a deodorizing property and an antistatic property excellent in moisture permeability and water resistance by applying a hydrophilic non-porous polyurethane resin on the fabric.
본 발명은 투습방수 직물에 있어서, 제전성을 가지는 제전성 직물에 광개시제와 소취제를 포함하는 친수무공형 폴리우레탄계 수지가 코팅되고 광경화하여 제조되는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물을 제공한다. The present invention is a moisture-permeable waterproof fabric, characterized in that the water-repellent moisture-repellent waterproof and antistatic property characterized in that the anti-static non-porous polyurethane-based resin comprising a photoinitiator and a deodorant coated on the antistatic fabric having an antistatic property is prepared by photocuring Provide the fabric.
또한, 상기 제전성 직물은 도전사를 포함하거나, 또는 제전제를 포함하는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물을 제공한다.In addition, the antistatic fabric provides a moisture-permeable waterproof fabric having a deodorant and antistatic properties comprising a conductive yarn or an antistatic agent.
또한, 상기 광개시제는 1-하이드록시사이클로헥실페닐케톤(시바 사, Igacure 184)과 디페닐 2,4,6-트리메틸벤조일 포스핀옥사이드(Darocur TPO)를 4:1 내지 3:2로 혼합되어 형성되는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물을 제공한다.In addition, the photoinitiator is formed by mixing 1-hydroxycyclohexylphenyl ketone (Siga Co., Igacure 184) and diphenyl 2,4,6-trimethylbenzoyl phosphine oxide (Darocur TPO) in 4: 1 to 3: 2. It provides a moisture-permeable waterproof fabric having a deodorant and antistatic properties.
또한, 상기 친수무공형 폴리우레탄계 수지는 친수무공형 폴리우레탄 아크릴레이트 수지인 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물을 제공한다.In addition, the hydrophilic non-porous polyurethane-based resin provides a breathable waterproof fabric having a deodorant and antistatic properties, characterized in that the hydrophilic non-porous polyurethane acrylate resin.
또한, 상기 소취제는 피톤치드, 목초액, 호박조성물, 키토산, 아크릴레이트계 화합물, 아민기계 화합물, 히드라진계 화합물, 제올라이트, 은, 인이온, 규산염, 산화티탄, 백금 중 어느 하나 또는 2이상 혼합한 혼합물인 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물을 제공한다.In addition, the deodorant is phytoncide, wood vinegar, amber composition, chitosan, acrylate-based compound, amine-mechanical compound, hydrazine-based compound, zeolite, silver, phosphorus ion, silicate, titanium oxide, platinum or any mixture of two or more It provides a moisture-permeable waterproof fabric having a deodorant and antistatic properties.
또한, 상기 친수무공형 폴리우레탄 아크릴레이트 수지는 70~120㎛의 두께로 코팅되는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물을 제공한다.In addition, the hydrophilic non-porous polyurethane acrylate resin provides a moisture-permeable waterproof fabric having a deodorant and antistatic properties, characterized in that the coating to a thickness of 70 ~ 120㎛.
또한, 상기 투습방수 직물은 내수압이 3,000~7000㎜H2O인 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물을 제공한다.In addition, the moisture-permeable waterproof fabric provides a moisture-repellent waterproof fabric having a deodorant and antistatic properties, characterized in that the water pressure is 3,000 ~ 7000 mmH 2 O.
또한, 상기 투습방수 직물은 투습도가 5,000~10,000g/㎡/24hr인 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물을 제공한다.In addition, the moisture-permeable waterproof fabric provides a moisture-repellent waterproof fabric having a deodorant and antistatic properties, characterized in that the moisture permeability of 5,000 ~ 10,000g / ㎡ / 24hr.
또한, 본 발명은 투습방수 직물의 제조방법에 있어서, 친수무공형 폴리우레탄 아크릴레이트 수지 100 중량부에 광개시제 1 내지 5 중량부, 소취제 1내지 10 중량부로 혼합하는 혼합단계; 상기 광개시제와 소취제가 혼합된 친수무공형 폴리우레탄 아크릴레이트 수지를 제전성 직물에 70~120㎛ 두께로 코팅하는 코팅단계; 및 상기 직물에 자외선을 조사하여 친수무공형 폴리우레탄 아크릴레이트 수지를 경화하는 자외선 경화단계를 포함하는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물 제조방법을 제공한다.In addition, the present invention is a method for producing a moisture-permeable waterproof fabric, the mixing step of mixing 1 to 5 parts by weight of photoinitiator, 1 to 10 parts by weight of deodorant to 100 parts by weight of hydrophilic non-porous polyurethane acrylate resin; A coating step of coating the hydrophilic non-porous polyurethane acrylate resin mixed with the photoinitiator and the deodorant to a thickness of 70 to 120 μm on an antistatic fabric; And an ultraviolet curing step of curing the hydrophilic non-porous polyurethane acrylate resin by irradiating the fabric with ultraviolet rays.
또한, 상기 코팅단계는 나이프 오버 롤(knife over roll) 코팅법으로 1~10회 코팅하는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물 제조방법을 제공한다.In addition, the coating step provides a breathable waterproof fabric manufacturing method having a deodorant and antistatic properties, characterized in that the coating 1 to 10 times by knife over roll (knife over roll) coating method.
또한, 상기 자외선 경화는 0.6 내지 4.0J/㎠의 조사에너지로 경화하는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물 제조방법을 제공한다.
In addition, the UV curing provides a method for producing a moisture-permeable waterproof fabric having a deodorant and antistatic properties, characterized in that curing with irradiation energy of 0.6 to 4.0J / ㎠.
이하 본 발명에 첨부된 도면을 참조하여 본 발명의 바람직한 일실시예를 상세히 설명하기로 한다. 우선, 도면들 중, 동일한 구성요소 또는 부품들은 가능한 한 동일한 참조부호를 나타내고 있음에 유의하여야 한다. 본 발명을 설명함에 있어, 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하지 않게 하기 위하여 생략한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. First, it should be noted that, in the drawings, the same components or parts have the same reference numerals as much as possible. In describing the present invention, detailed descriptions of related well-known functions or configurations are omitted in order not to obscure the subject matter of the present invention.
본 명세서에서 사용되는 정도의 용어 "약", "실질적으로" 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.
As used herein, the terms "about", "substantially", and the like, are used at, or in close proximity to, numerical values when manufacturing and material tolerances inherent in the meanings indicated are intended to aid the understanding of the invention. Accurate or absolute figures are used to assist in the prevention of unfair use by unscrupulous infringers.
도 1은 본 발명에 따른 소취성 및 제전성을 가지는 투습방수 직물을 나타낸 단면도이고, 도 2는 본 발명에 따른 소취성 및 제전성을 가지는 투습방수 직물의 제조방법을 나타낸 공정도이다.1 is a cross-sectional view showing a moisture-permeable waterproof fabric having a deodorant and antistatic properties according to the present invention, Figure 2 is a process chart showing a method of manufacturing a moisture-repellent waterproof fabric having a deodorant and antistatic properties according to the present invention.
본 발명에 따른 소취성 및 제전성을 가지는 투습방수 직물은 도 1에 도시된 바와 같이 직물 100에 친수무공형 폴리우레탄계 수지가 코팅된 코팅층 200으로 구성된 투습방수 직물이다.The moisture-permeable waterproof fabric having deodorant and antistatic properties according to the present invention is a moisture-permeable waterproof fabric composed of a
상기 직물 100은 제전성을 가지는 제전성 직물을 사용하여 본 발명의 소취성 및 제전성을 가지는 투습방수 직물에 제전성을 부여한다.The
상기 제전성 직물은 직물에 도전사를 포함하여 직물에 제전성을 부여할 수 있으며, 제전제를 고분자 중합단계에서 첨가하거나 비활성 제전제를 섬유 방사전에 고분자 수지에 첨가하여 섬유자체에 제전성을 부여하여 직물로 제조함으로서 제전성 직물을 제조할 수 있으며, 직물에 제전제를 코팅, 라미테이팅하는 대전방지가공으로 제전성 직물을 제조할 수 있을 것이다.The antistatic fabric may include a conductive yarn in the fabric to impart antistatic properties to the fabric, and impart antistatic properties to the fiber itself by adding an antistatic agent in the polymer polymerization step or adding an inert antistatic agent to the polymer resin before fiber spinning. By manufacturing the fabric to produce an antistatic fabric, it will be possible to produce an antistatic fabric by the antistatic processing coating, laminating the antistatic agent on the fabric.
상기 친수무공형 폴리우레탄계 수지는 광개시제와 소취제를 포함하여 자외선경화를 가능하게 하며, 소취제를 포함하여 직물에 소취성을 부여한다.The hydrophilic non-porous polyurethane-based resin includes a photoinitiator and a deodorant to enable ultraviolet curing and impart deodorant to the fabric, including a deodorant.
상기 광개시제는 1-하이드록시사이클로헥실페닐케톤(시바 사, Igacure 184)과 디페닐 2,4,6-트리메틸벤조일 포스핀옥사이드(Darocur TPO)가 4:1 내지 3:2로 혼합되어 제조되는 것이 바람직할 것이다.The photoinitiator is prepared by mixing 1-hydroxycyclohexylphenyl ketone (Igacure 184, Ciba, Inc.) and diphenyl 2,4,6-trimethylbenzoyl phosphine oxide (Darocur TPO) in 4: 1 to 3: 2. Would be desirable.
상기 1-하이드록시사이클로헥실페닐케톤과 디페닐 2,4,6-트리메틸벤조일 포스핀옥사이드가 혼합된 광개시제는 표면에서의 충분한 경화를 이룰 수 있게 해 줄 뿐만 아니라 디페닐 2,4,6-트리메틸벤조일 포스핀옥사이드를 사용함으로 인하여 내부까지 깊숙이 경화가 가능함으로써 두꺼운 코팅층까지도 충분히 경화가 가능한 장점이 있다.The photoinitiator mixed with the 1-hydroxycyclohexylphenyl ketone and diphenyl 2,4,6-trimethylbenzoyl phosphine oxide not only allows sufficient curing at the surface but also diphenyl 2,4,6-trimethyl By using benzoyl phosphine oxide it is possible to cure deep to the inside there is an advantage that can be sufficiently cured even a thick coating layer.
상기 소취제는 천연 소취제와 인공적으로 제조되는 소취제로 구분될 수 있다.The deodorant may be classified into a natural deodorant and an artificially manufactured deodorant.
상기 천연 소취제로는 피톤치드, 목초액, 호박조성물, 키토산 등을 사용하여 제조되는 소취제가 있으며, 인공적인 소취제로 유기계 화합물로는 아크릴레이트계 화합물, 아민기계 화합물, 히드라진계 화합물 등을 사용하여 제조되는 소취제와, 무기계 화합물로 제올라이트, 은, 인이온, 규산염, 산화티탄, 백금 등 포함하는 소취제가 있으면 본 발명에서는 상기에서 언급된 모든 소취제를 사용할 수 있다.The natural deodorant may be a deodorant manufactured using phytoncide, wood vinegar, pumpkin composition, chitosan, etc., and an organic deodorant is an artificial deodorant. An odorant manufactured using an acrylate compound, an amine mechanical compound, a hydrazine compound, or the like And, if there is a deodorant containing zeolite, silver, phosphorus ion, silicate, titanium oxide, platinum and the like as the inorganic compound in the present invention, all the above-mentioned deodorant can be used.
상기 친수무공형 폴리우레탄계 수지는 친수무공형 폴리우레탄 아크릴레이트 수지를 사용하는 것이 바람직할 것이다.As the hydrophilic non-porous polyurethane-based resin, it is preferable to use a hydrophilic non-porous polyurethane acrylate resin.
상기 광개시제와 소취제를 포함하는 친수무공형 폴리우레탄계 수지는 제전성 직물에 70~120㎛의 두께로 코팅되는 것이 바람직하다. Hydrophilic non-porous polyurethane-based resin comprising the photoinitiator and deodorant is preferably coated with a thickness of 70 ~ 120㎛ on the antistatic fabric.
상기 코팅층의 두께가 70㎛미만일 경우에는 투습 및 방수기능이 저하될 수 있으며, 코팅층의 두께가 120㎛를 초과할 경우에는 기능상의 상승효과가 미미하고 직물의 초감을 저해할 수 있다. If the thickness of the coating layer is less than 70㎛ moisture permeability and waterproof function may be lowered, if the thickness of the coating layer exceeds 120㎛ the functional synergistic effect is insignificant and may inhibit the texture of the fabric.
상기와 같이 제전성 직물에 광개시제와 소취제를 포함하는 친수무공형 폴리우레탄계 수지가 코팅된 본 발명은 내수압이 3,000~7000㎜H2O로 방수성이 뛰어나며,투습도는 5,000~10,000g/㎡/24hr로 우수한 방습효과를 가진다.
The present invention is coated with a hydrophilic non-porous polyurethane-based resin containing a photoinitiator and a deodorant on the antistatic fabric as described above has excellent water resistance of 3,000 ~ 7000 mmH 2 O, water permeability is 5,000 ~ 10,000 g / ㎡ / 24hr Excellent moisture proof effect
상기에서 설명된 본 발명의 소취성 및 제전성을 가지는 투습방수 직물은 도 2에 도시된 바와 같이 혼합단계, 코팅단계, 자외선 경화단계로 투습방수 직물을 제조된다.As described above, the moisture-permeable waterproof fabric having the deodorant and antistatic properties of the present invention is prepared by the mixing step, the coating step, and the UV curing step.
상기 혼합단계는 친수무공형 폴리우레탄 아크릴레이트 수지 100 중량부에 광개시제 1 내지 5 중량부, 소취제 1 내지 10 중량부로 혼합하는 단계이다.The mixing step is a step of mixing 1 to 5 parts by weight of photoinitiator, 1 to 10 parts by weight of deodorant to 100 parts by weight of hydrophilic non-porous polyurethane acrylate resin.
상기 광개시제가 친수무공형 폴리우레탄 아크릴레이트 수지에 너무 적게 포함되면 경화속도가 늦어질 수 있으며, 부분적으로 경화되지않을 수 있다. 또한 광개시제가 너무 많이 포함되면 폴리우레탄 아크릴레이트 수지의 코팅층의 물성이 저하될 수 있으므로 적정한 양으로 조절되어야할 것이다.If the photoinitiator is included in the hydrophilic non-porous polyurethane acrylate resin too little, the curing speed may be slow and may not be partially cured. In addition, when too much photoinitiator is included, the physical properties of the coating layer of the polyurethane acrylate resin may be lowered, so it should be adjusted to an appropriate amount.
상기 소취제는 너무 적은 양이 포함되면 소취성이 미흡할 수 있으며, 너무 많은 양이 포함되면 경화속도를 저하시키고 기능상의 상승효과가 미미하며 직물 촉감을 저하시킬 수 있다. 따라서 상기 소취제는 사용되는 소취제의 종류에 따라 적정한 양으로 조절하여야 할 것이다.If the amount of the deodorant is included in too small amount may be insufficient deodorant, if included too much amount may lower the curing speed, the functional synergistic effect is insignificant and may lower the fabric feel. Therefore, the deodorant will have to be adjusted in an appropriate amount depending on the type of deodorant used.
상기 코팅단계는 상기 광개시제와 소취제가 혼합된 친수무공형 폴리우레탄 아크릴레이트 수지를 제전성 직물에 70~120㎛ 두께로 코팅하는 코팅단계이다.The coating step is a coating step of coating a hydrophilic non-porous polyurethane acrylate resin mixed with the photoinitiator and the deodorant to a thickness of 70 ~ 120㎛ antistatic fabric.
상기 코팅단계는 현재까지 개발된 모든 코팅방법으로 코팅될 수 있으나 나이프 오버 롤(knife over roll) 코팅법으로 1~10회 코팅하는 것을 가장 바람직할 것이다.The coating step may be coated with any coating method developed to date, but it will be most preferable to coat 1 to 10 times with a knife over roll coating method.
상기 자외선 조사단계는 상기 친수무공형 폴리우레탄 아크릴레이트 수지가 코팅된 직물에 자외선을 조사하여 친수무공형 폴리우레탄 아크릴레이트 수지를 경화하여 친수무공형 폴리우레탄 아크릴레이트 수지가 직물에 견고하게 부착되도록 하는 단계이다.The ultraviolet irradiation step is to cure the hydrophilic non-porous polyurethane acrylate resin by irradiating the ultraviolet ray to the fabric coated with the hydrophilic non-porous polyurethane acrylate resin so that the hydrophilic non-porous polyurethane acrylate resin is firmly attached to the fabric Step.
상기 자외선 경화는 조사에너지가 낮을 경우 친수무공형 폴리우레탄 아크릴레이트 수지의 경화율이 떨어질 수 있으며, 조사에너지가 너무 높을 경우 직물과 친수무공형 폴리우레탄 아크릴레이트 수지와의 결합력이 저하될 수 있으므로 적정한 조사에너지로 조사하여야 한다.The UV curing may lower the curing rate of the hydrophilic non-porous polyurethane acrylate resin when the irradiation energy is low, and if the irradiation energy is too high, the bonding force between the fabric and the hydrophilic non-porous polyurethane acrylate resin may be reduced. It should be investigated with irradiation energy.
상기 자외선 경화는 0.6 내지 4.0J/㎠의 조사에너지로 경화하는 것이 가장 바람직할 것이다.The ultraviolet curing will most preferably be cured with an irradiation energy of 0.6 to 4.0J / ㎠.
상기 제전성 직물에 친수무공형 폴리우레탄 아크릴레이트 수지를 코팅하고 다른 가공을 할 경우 친수무공형 폴리우레탄 아크릴레이트 수지가 박리되고 내구성이 떨어지므로 본 발명의 친수무공형 폴리우레탄 아크릴레이트 수지를 코팅하기 전에 발수처리와 시레가공을 먼저 실시하는 것이 바람직하다. 상기 발수처리는 테프론 발수제로 처리할 수 있고 130 내지 150℃, 50 내지 70kg/㎠의 압력으로 시레(Cire)가공을 할 수 있다.
When the hydrophilic non-porous polyurethane acrylate resin is coated on the antistatic fabric and subjected to other processing, the hydrophilic non-porous polyurethane acrylate resin is peeled off and the durability is reduced, thereby coating the hydrophilic non-porous polyurethane acrylate resin of the present invention. It is desirable to perform water repellent treatment and shire processing first. The water repellent treatment may be treated with a Teflon water repellent and may be subjected to Cire processing at a pressure of 130 to 150 ° C. and 50 to 70 kg / cm 2.
본 발명에 의한 투습방수 직물은 제전성 직물에 소취제를 포함하는 친수무공형 폴리우레탄계 수지를 사용하여 제조되는 것으로 제전성과 소취성을 가지는 효과가 있다.Water-permeable waterproof fabric according to the present invention is produced by using a hydrophilic non-porous polyurethane-based resin containing a deodorant in the antistatic fabric has the effect of having antistatic properties and deodorant.
또한, 본 발명은 친수무공형 폴리우레탄계 수지를 직물표면에 코팅한 후, 자외선 조사에 의해 직물에 부착시켜 제조되는 것으로 유기용매를 사용하지 않는 소취성 및 제전성을 가지는 투습방수 직물의 제조방법으로 친환경적인 공법이다.In addition, the present invention is prepared by coating a hydrophilic non-porous polyurethane-based resin on the fabric surface, and then attached to the fabric by ultraviolet irradiation as a method of manufacturing a moisture-permeable waterproof fabric having a deodorant and antistatic properties without using an organic solvent It is an environmentally friendly method.
또한, 본 발명의 광경화공정은 열경화공정으로 실시되는 종래의 제조방법에 비해 에너지 소비를 50~60% 감소시킬 수 있는 효과가 있다.
In addition, the photocuring process of the present invention has the effect of reducing the energy consumption by 50 to 60% compared to the conventional manufacturing method performed by the thermosetting process.
도 1은 본 발명에 따른 소취성 및 제전성을 가지는 투습방수 직물을 나타낸 단면도.
도 2는 본 발명에 따른 소취성 및 제전성을 가지는 투습방수 직물의 제조방법을 나타낸 공정도.1 is a cross-sectional view showing a moisture-permeable waterproof fabric having deodorant and antistatic properties in accordance with the present invention.
Figure 2 is a process chart showing a method of manufacturing a moisture-permeable waterproof fabric having deodorant and antistatic properties in accordance with the present invention.
이하, 본 발명의 실시예 및 비교예에 대하여 상세히 설명한다. 그러나, 본 발명은 하기 실시 예로 의해 권리범위가 한정되는 것은 아니다.
Hereinafter, the Example and comparative example of this invention are demonstrated in detail. However, the present invention is not limited by the following examples.
실시예Example 1 One
직물은 경사, 위사 밀도 150본과 110본이며 경위사 원사는 50 데니어 144 필라멘트의 도전사를 포함하는 제전성 폴리에스테르원단에 발수제로 발수처리 후 130 내지 150도와 50 내지 70kg/㎠의 압력으로 시레 가공하였다.The fabric is warp, weft density 150 and 110, and the weft yarn is processed to a pressure of 130 to 150 degrees and 50 to 70kg / cm2 after water repellent treatment with an antistatic polyester fabric containing 50 denier and 144 filament conductive yarns. It was.
친수무공형 폴리우레탄 아크릴레이트 수지 100 중량부에 1-하이드록시사이클로헥실페닐케톤(시바 사, Igacure 184)과 디페닐 2,4,6-트리메틸벤조일 포스핀옥사이드 (Darocur TPO)를 4:1로 혼합된 광개시제 3 중량부를 첨가하였다.1-hydroxycyclohexylphenyl ketone (Igacure 184, Ciba) and diphenyl 2,4,6-trimethylbenzoyl phosphine oxide (Darocur TPO) are added to 100 parts by weight of a hydrophilic non-porous polyurethane acrylate resin. 3 parts by weight of the mixed photoinitiators were added.
또한 소취제는 키토산과 무기계 화합물를 포함하는 소취제를 혼합하여 친수무공형 폴리우레탄 아크릴레이트 수지 100 중량부에 4 중량부를 첨가하였다.In addition, the deodorant was mixed with a deodorant containing chitosan and an inorganic compound was added 4 parts by weight to 100 parts by weight of a hydrophilic non-porous polyurethane acrylate resin.
상기 광개시제, 소취제를 포함하는 친수무공형 폴리우레탄 아크릴레이트 수지를 상온에서 30분 동안 교반기를 이용하여 500~800rpm으로 충분히 교반(stirring)하였다.The hydrophilic non-porous polyurethane acrylate resin including the photoinitiator and the deodorant was sufficiently stirred at 500 to 800 rpm using a stirrer at room temperature for 30 minutes.
상기 광개시제, 소취제를 포함하는 친수무공형 폴리우레탄 아크릴레이트 수지를 폴리에스테르 직물 상에 나이프 오버 롤(knife over roll) 코팅법으로 3회 코팅하여 직물상에 90㎛의 코팅막을 형성하고, Fe 램프가 장착된 경화기에 1.2J/㎠ 의 자외선 조사에너지로 조사하여 소취성 및 제전성을 가지는 투습방수 직물을 제조하였다.
The hydrophilic non-porous polyurethane acrylate resin including the photoinitiator and the deodorant was coated three times by a knife over roll coating method on a polyester fabric to form a 90 μm coating film on the fabric, and the Fe lamp was The mounted curing machine was irradiated with ultraviolet irradiation energy of 1.2J / cm 2 to prepare a moisture-permeable waterproof fabric having deodorant and antistatic properties.
실시예Example 2 2
상기 실시예 1과 동일하게 실시하였으나 100㎛의 코팅막을 형성하였으며, Fe 램프가 장착된 경화기로 2.4J/㎠ 의 자외선 조사에너지로 조사하여 소취성 및 제전성을 가지는 투습방수 직물을 제조하였다.
A coating film having a thickness of 100 μm was formed in the same manner as in Example 1, and a moisture-permeable waterproof fabric having a deodorant and antistatic property was prepared by irradiating with ultraviolet irradiation energy of 2.4 J / cm 2 with a curing lamp equipped with a Fe lamp.
비교예Comparative example
경사, 위사 밀도는 150본과 110본으로 경위사 원사는 50 데니어 144 필라멘트의 폴리에스테르원단에 발수제로 발수처리 후 130 내지 150도와 50 내지 70kg/㎠의 압력으로 시레 가공하여 폴리에스테르 직물을 제조하였다.
The warp and weft densities were 150 and 110, and the weft yarn was made of polyester fabric of 50 denier 144 filaments and water-repellent treated with a water repellent agent to prepare a polyester fabric by pressure treatment at 130 to 150 degrees and 50 to 70 kg / cm 2. .
상기의 실시예들과 비교예들로 제조된 직물을 AATCC Test Method 135-1995로 41℃에서 세탁 후 텀블건조 방법으로 건조한 후 ASTM E96(CaCl2)법에 의해 34℃, 습도 90%에서 24시간 동안 투습도를 평가하였고, 내수도는 ISO 0811에 의해 상승속도 600㎜/min로 측정하여 그 결과를 표 1에 나타내었다.
The fabrics prepared according to the above examples and comparative examples were washed at 41 ° C. with AATCC Test Method 135-1995 and dried by tumble drying, followed by ASTM E96 (CaCl 2) method at 34 ° C., humidity of 90% for 24 hours. The moisture permeability was evaluated, and the water resistance was measured at an ascending rate of 600 mm / min according to ISO 0811 and the results are shown in Table 1.
division
(J/㎠)UV irradiation
(J / ㎠)
(㎛)Coating thickness
(Μm)
(g/㎡/24hr)Moisture permeability
(g / ㎡ / 24hr)
(㎜H2O)Water supply
(MmH2O)
(kV)High voltage
(kV)
7,300
3,800
8,600
5,900
2,500
1,900
상기 표 1의 결과에서 나타나듯이 본 발명에 따른 소취성 및 제전성을 가지는 투습방수 직물인 실시예 1, 2의 직물은 비교예 직물보다 투습도 및 내수도가 모두 3배이상 높은 것을 알 수 있으며, 대전압에서도 비교예에 비해 현저하게 낮은것을 알 수 있다.
As shown in the results of Table 1, it can be seen that the fabrics of Examples 1 and 2, which are moisture-permeable waterproof fabrics having deodorant and antistatic properties according to the present invention, are three times higher in both moisture permeability and water resistance than the comparative fabrics. It can be seen that even at a high voltage, it is significantly lower than the comparative example.
<도면의 주요 부호에 대한 설명>
100: 직물 200: 친수무공형 폴리우레탄계 코팅층 <Description of Major Symbols in Drawing>
100: fabric 200: hydrophilic non-porous polyurethane-based coating layer
Claims (11)
제전성을 가지는 제전성 직물에 광개시제와 소취제를 포함하는 친수무공형 폴리우레탄계 수지가 코팅되고 광경화하여 제조되는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물.Waterproof breathable fabric,
A moisture-repellent waterproof fabric having a deodorant and antistatic property, characterized in that the antistatic fabric having an antistatic property is produced by coating a hydrophilic non-porous polyurethane-based resin including a photoinitiator and a deodorant and photocuring.
상기 제전성 직물은 도전사를 포함하거나, 또는 제전제를 포함하는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물.The method of claim 1,
The antistatic fabric is a breathable waterproof fabric having a deodorant and antistatic properties, characterized in that it comprises a conductive yarn or an antistatic agent.
상기 광개시제는 1-하이드록시사이클로헥실페닐케톤(시바 사, Igacure 184)과 디페닐 2,4,6-트리메틸벤조일 포스핀옥사이드(Darocur TPO)를 4:1 내지 3:2로 혼합되어 형성되는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물.The method of claim 1,
The photoinitiator is formed by mixing 1-hydroxycyclohexylphenyl ketone (Igacure 184, Ciba) and diphenyl 2,4,6-trimethylbenzoyl phosphine oxide (Darocur TPO) in 4: 1 to 3: 2. Breathable waterproof fabric having a deodorant and antistatic properties.
상기 친수무공형 폴리우레탄계 수지는 친수무공형 폴리우레탄 아크릴레이트 수지인 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물.The method of claim 1,
The hydrophilic non-porous polyurethane-based resin is breathable waterproof fabric having a deodorant and antistatic properties, characterized in that the hydrophilic non-porous polyurethane acrylate resin.
상기 소취제는 피톤치드, 목초액, 호박조성물, 키토산, 아크릴레이트계 화합물, 아민기계 화합물, 히드라진계 화합물, 제올라이트, 은, 인이온, 규산염, 산화티탄, 백금 중 어느 하나 또는 2이상을 포함하는 소취제인 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물.The method of claim 1,
The deodorant is a odorant containing any one or two or more of phytoncide, wood vinegar, amber composition, chitosan, acrylate compound, amine mechanical compound, hydrazine compound, zeolite, silver, phosphorus ion, silicate, titanium oxide, platinum Breathable waterproof fabric having a deodorant and antistatic properties.
상기 친수무공형 폴리우레탄 아크릴레이트 수지는 70~120㎛의 두께로 코팅되는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물.The method of claim 1,
The hydrophilic non-porous polyurethane acrylate resin is a moisture-permeable waterproof fabric having a deodorant and antistatic properties, characterized in that the coating to a thickness of 70 ~ 120㎛.
상기 투습방수 직물은 내수압이 3,000~7000㎜H2O인 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물.The method of claim 1,
The moisture-permeable waterproof fabric has a water-absorbent and antistatic property, characterized in that the water pressure is 3,000 ~ 7000 mmH 2 O.
상기 투습방수 직물은 투습도가 5,000~10,000g/㎡/24hr인 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물.The method of claim 1,
The moisture-permeable waterproof fabric is breathable waterproof fabric having a deodorant and antistatic properties, characterized in that the moisture permeability of 5,000 ~ 10,000g / ㎡ / 24hr.
친수무공형 폴리우레탄 아크릴레이트 수지 100 중량부에 광개시제 1 내지 5 중량부, 소취제 1 내지 10 중량부로 혼합하는 혼합단계;
상기 광개시제와 소취제가 혼합된 친수무공형 폴리우레탄 아크릴레이트 수지를 제전성 직물에 70~120㎛ 두께로 코팅하는 코팅단계; 및
상기 직물에 자외선을 조사하여 친수무공형 폴리우레탄 아크릴레이트 수지를 경화하는 자외선 경화단계를 포함하는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물 제조방법.In the method of manufacturing a moisture-permeable waterproof fabric,
Mixing step of mixing 1 to 5 parts by weight of photoinitiator, 1 to 10 parts by weight of deodorant to 100 parts by weight of hydrophilic non-porous polyurethane acrylate resin;
A coating step of coating the hydrophilic non-porous polyurethane acrylate resin mixed with the photoinitiator and the deodorant to a thickness of 70 to 120 μm on an antistatic fabric; And
Ultraviolet radiation step of curing the hydrophilic non-porous polyurethane acrylate resin by irradiating the fabric with ultraviolet rays, characterized in that it comprises a deodorant and antistatic moisture-proof fabric manufacturing method.
상기 코팅단계는 나이프 오버 롤(knife over roll) 코팅법으로 1~10회 코팅하는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물 제조방법.The method of claim 9,
The coating step is a breathable waterproof fabric manufacturing method having a deodorant and antistatic properties, characterized in that the coating by knife over roll (knife over roll) 1 to 10 times.
상기 자외선 경화는 0.6 내지 4.0J/㎠의 조사에너지로 경화하는 것을 특징으로 하는 소취성 및 제전성을 가지는 투습방수 직물 제조방법.The method of claim 9,
The ultraviolet curing is a moisture-absorbing and waterproof fabric manufacturing method having a deodorant and antistatic properties, characterized in that curing with irradiation energy of 0.6 to 4.0J / ㎠.