KR20110109245A - Non pvc eraser composition - Google Patents
Non pvc eraser composition Download PDFInfo
- Publication number
- KR20110109245A KR20110109245A KR1020100028889A KR20100028889A KR20110109245A KR 20110109245 A KR20110109245 A KR 20110109245A KR 1020100028889 A KR1020100028889 A KR 1020100028889A KR 20100028889 A KR20100028889 A KR 20100028889A KR 20110109245 A KR20110109245 A KR 20110109245A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- styrene
- eraser
- eraser composition
- butadiene
- Prior art date
Abstract
본 발명은 논-피브이씨 지우개 조성물에 관한 것으로, 보다 상세하게는 스타이렌-부타디엔-스타이렌, 니트릴 부타디엔 러버 및 폴리스타이렌 공중합체로 이루어지는 열가소성 엘라스토머, 왁스, 미네랄 오일, 탄산칼슘(CaCO3), 산화마그네슘(MgO) 및 이산화티탄(TiO2)을 포함하는 논-피브이씨 지우개 조성물에 관한 것이다.
본 발명에 따른 지우개는 기존 지우개에 사용되던 PVC(폴리염화비닐)을 전혀 사용하지 않아 독성이 없고 인체에 무해하여 어린이도 안심하고 사용할 수 있으며, 환경호르몬을 방출하지 않아 환경친화적인 동시에 글자소거 성능이 우수하여 지우개 본연의 기능을 충분히 발휘할 수 있다.The present invention relates to a non-fibse eraser composition, and more particularly, thermoplastic elastomer, wax, mineral oil, calcium carbonate (CaCO 3 ), consisting of styrene-butadiene-styrene, nitrile butadiene rubber and polystyrene copolymer, A non-fibse eraser composition comprising magnesium oxide (MgO) and titanium dioxide (TiO 2 ).
Eraser according to the present invention does not use any PVC (polyvinyl chloride) used in the conventional eraser is not toxic and harmless to the human body can be used with confidence, it does not emit environmental hormones environmentally friendly at the same time erase performance It is excellent in this and can fully exhibit the eraser original function.
Description
본 발명은 논-피브이씨 지우개 조성물에 관한 것으로, 보다 상세하게는 스타이렌-부타디엔-스타이렌, 니트릴 부타디엔 러버 및 폴리스타이렌 공중합체로 이루어지는 열가소성 엘라스토머, 왁스, 미네랄 오일, 탄산칼슘(CaCO3), 산화마그네슘(MgO) 및 이산화티탄(TiO2)을 포함하는 논-피브이씨 지우개 조성물에 관한 것이다.The present invention relates to a non-fibse eraser composition, and more particularly, thermoplastic elastomer, wax, mineral oil, calcium carbonate (CaCO 3 ), consisting of styrene-butadiene-styrene, nitrile butadiene rubber and polystyrene copolymer, A non-fibse eraser composition comprising magnesium oxide (MgO) and titanium dioxide (TiO 2 ).
일반적으로 지우개는 PVC라는 폴리염화비닐을 소재로 하여 만들어진다. Generally, the eraser is made of polyvinyl chloride called PVC.
상기 폴리염화비닐은 환경유해물질 중의 하나로 알려져 있지만, 생활에서 접하는 거의 모든 플라스틱 제품에 기본적으로 사용되는 물질로, 극히 미미한 정도의 환경유해물질과 환경호르몬이 검출되므로 건강에 그다지 영향을 주지 않는 수준이다.Although polyvinyl chloride is known as one of environmentally harmful substances, it is basically used in almost all plastic products encountered in the life, and it is a level that does not affect health very much because only a very small amount of environmentally harmful substances and environmental hormones are detected. .
염화비닐계 수지는 염화비닐의 단독 중합체 및 염화비닐을 50% 이상 함유한 혼성 중합체로서, 현탁중합과 유화중합으로 제조되는 5대 범용 열가소성 플라스틱 수지 중의 하나이다. 이러한 염화비닐계 수지는 컴파운드 압출성형, 사출성형, 캘린더링, 졸 성형 등의 여러 가지 가공법에 의해 성형되어 파이프, 건축용 내·외장재, 전선, 전기기계 제품, 장난감, 필름, 시트, 인조가죽, 테이프, 식품 포장재, 의료용품에 이르기까지 다양한 제품의 소재로 광범위하게 사용되고 있다. The vinyl chloride resin is a hybrid polymer containing at least 50% of a vinyl chloride homopolymer and vinyl chloride, and is one of five general-purpose thermoplastic resins produced by suspension polymerization and emulsion polymerization. The vinyl chloride resin is molded by various processing methods such as compound extrusion molding, injection molding, calendering, sol molding, and the like. It is widely used as a material for a variety of products, from food packaging to medical supplies.
PVC 수지는 내수성, 내약품성, 난연성 등이 우수하다는 특징이 있어 다양한 용도로 사용되고 있으나, 수지가 불완전 연소를 하게되면 공해물질인 다이옥신이 발생되어 환경오염을 유발시키는 문제점이 있기 때문에 최근에는 사용을 규제하고 있는 추세이다. PVC resin is used for various purposes because of its excellent water resistance, chemical resistance, and flame retardancy.However, since the resin is incompletely burned, it is polluted, causing dioxin, which causes environmental pollution. The trend is.
이러한 염화비닐계 수지에는 가소제, 2차 가소제, 안정제, 안료, 충전제, 발포제, 활제, 점도조절제 등 여러 가지 첨가제를 적절하게 첨가하여 다양한 가공 물성을 부여할 수 있다.The vinyl chloride resin may be imparted with various additives by appropriately adding various additives such as plasticizers, secondary plasticizers, stabilizers, pigments, fillers, blowing agents, lubricants, and viscosity modifiers.
가소제는 고분자 수지간의 마찰계수를 줄여 가공성을 향상시키는 역할을 하는 첨가제로서, 지금까지 사용되고 있는 가소제의 유형은 종류가 매우 다양하고 용도도 각각 다르다. 염화비닐계 수지에 사용되는 가소제로는 주로 프탈레이트계 가소제, 특히 DEHP(Di-2-EthylHexyl Phthalate), DBP(Di-Butyl Phthalate), DIDP(Di-IsoDecyl Phthalate), BBP(Butyl Benzyl Phthalate), DINP(Di-IsoNonyl Phthalate), DNOP(Di-n-Octyl Phthalate) 등이 가장 널리 사용되고 있다. 특히 디에틸헥실프탈레이트는 가소화 효율, 내한성 등의 제물성의 밸런스가 좋아서 폭넓게 사용되고 있다.Plasticizers are additives that play a role of improving the processability by reducing the friction coefficient between polymer resins. The types of plasticizers used up to now are very diverse in their types and their uses are different. Plasticizers used in vinyl chloride resins are mainly phthalate plasticizers, especially DEHP (Di-2-EthylHexyl Phthalate), DBP (Di-Butyl Phthalate), DIDP (Di-IsoDecyl Phthalate), BBP (Butyl Benzyl Phthalate), DINP (Di-IsoNonyl Phthalate) and DNOP (Di-n-Octyl Phthalate) are the most widely used. In particular, diethylhexyl phthalate is widely used because it has a good balance of physical properties such as plasticization efficiency and cold resistance.
그러나 프탈레이트계 가소제들은 동물이나 사람의 몸 속에 들어가서 호르몬의 작용을 방해하거나 혼란시키는 내분비계 교란물질(endocrine disrupter), 즉 환경호르몬으로 의심받고 있으며, 이 중 디에틸헥실프탈레이트(DEHP) 및 디부틸프탈레이트(DBP)는 특히 위험물질로서 규제의 대상이 되고 있어 대체물질이 요구되고 있다. 또한 DEHP는 분자량이 작고 내열성이 약해 열에 의해 쉽게 변형될 수 있다는 점도 대체물질의 요구를 불러일으키는 요인이 되고 있다.However, phthalate-based plasticizers are suspected as endocrine disruptors, or environmental hormones, that enter or hinder the action of hormones in the body of animals or humans, including diethylhexyl phthalate (DEHP) and dibutyl phthalate. (DBP) is particularly dangerous and subject to regulation, requiring alternatives. In addition, DEHP has a low molecular weight and poor heat resistance, which can be easily transformed by heat, causing a demand for alternative materials.
종래로부터 사용되고 있는 지우개로는 염화비닐계 지우개, 엘라스토머계 지우개 및 천연고무계 지우개가 알려져 있다. 이 중에서, 천연고무계 지우개는 내구성에 문제가 있어 거의 사용되지 않고 있으며, 엘라스토머계 지우개도 지우는 능력의 한계로 인하여 많이 사용되지 않고 있다. 염화비닐계 지우개는 글자를 지우는 능력의 특성 면에 있어서 매우 우수하기 때문에 주로 사용되고 있으나, 사용되는 프탈산계 가소제, 특히 DEHP와 DBP에 의한 환경적 악영향과 가소제 이행성의 문제로 인하여 대체 지우개의 개발이 시급한 실정이다.As the erasers used in the related art, vinyl chloride erasers, elastomeric erasers and natural rubber erasers are known. Of these, natural rubber erasers are rarely used due to problems in durability, and elastomeric erasers are not used much due to limitations in their ability to erase. Vinyl chloride erasers are mainly used because of their excellent character-writing ability, but the development of replacement erasers is urgent due to the environmentally adverse effects of plasticizers used, especially DEHP and DBP, and the performance of plasticizers. It is true.
상기와 같은 종래기술의 문제점을 해결하고자, 본 발명은 기존 지우개에 사용되던 PVC(폴리염화비닐)을 전혀 사용하지 않아 독성이 없고 인체에 무해하여 어린이도 안심하고 사용할 수 있으며, 환경호르몬을 방출하지 않아 환경친화적인 논-피브이씨 지우개 조성물을 제공하는 것을 목적으로 한다.In order to solve the problems of the prior art as described above, the present invention does not use any PVC (polyvinyl chloride) used in the conventional eraser is not toxic and harmless to the human body can be used safely in children, do not emit environmental hormones Therefore, an object of the present invention is to provide an environmentally friendly non-fibse eraser composition.
또한 본 발명은 무독성이며, 글자소거 성능이 우수하여 지우개 본연의 기능을 충분히 발휘할 수 있는 논-피브이씨 지우개 조성물을 제공하는 것을 목적으로 한다.In addition, an object of the present invention is to provide a non-fibrous eraser composition which is non-toxic and has excellent letter erasing performance and can sufficiently exhibit the original function of the eraser.
상기 목적을 달성하기 위하여, 본 발명은 스타이렌-부타디엔-스타이렌, 니트릴 부타디엔 러버 및 폴리스타이렌 공중합체로 이루어지는 열가소성 엘라스토머, 왁스, 미네랄 오일, 탄산칼슘(CaCO3), 산화마그네슘(MgO) 및 이산화티탄(TiO2)을 포함하는 것을 특징으로 하는 논-피브이씨 지우개 조성물을 제공한다.In order to achieve the above object, the present invention is a thermoplastic elastomer, wax, mineral oil, calcium carbonate (CaCO 3 ), magnesium oxide (MgO) and titanium dioxide composed of styrene-butadiene-styrene, nitrile butadiene rubber and polystyrene copolymer It provides a (non-fib) C eraser composition characterized in that (TiO 2 ).
바람직하게, 상기 지우개 조성물은 스타이렌-부타디엔-스타이렌 6~15중량%, 니트릴 부타디엔 러버 5~15중량% 및 폴리스타이렌 공중합체 1~6중량%로 이루어지는 열가소성 엘라스토머 10~40중량%, 왁스 1~5중량%, 미네랄 오일 5~20중량% 및 탄산칼슘(CaCO3) 50~70중량%, 산화마그네슘(MgO) 0.1~5phr 및 이산화티탄(TiO2) 0.5~5phr를 포함한다.Preferably, the eraser composition is 10 to 40% by weight of thermoplastic elastomer consisting of 6 to 15% by weight of styrene-butadiene-styrene, 5 to 15% by weight of nitrile butadiene rubber and 1 to 6% by weight of polystyrene copolymer, and 1 to wax. 5 wt%, mineral oil 5-20 wt%, calcium carbonate (CaCO 3 ) 50-70 wt%, magnesium oxide (MgO) 0.1-5 phr and titanium dioxide (TiO 2 ) 0.5-5 phr.
본 발명에 따른 지우개는 기존 지우개에 사용되던 PVC(폴리염화비닐)을 전혀 사용하지 않아 독성이 없고 인체에 무해하여 어린이도 안심하고 사용할 수 있으며, 환경호르몬을 방출하지 않아 환경친화적인 동시에 글자소거 성능이 우수하여 지우개 본연의 기능을 충분히 발휘할 수 있다.Eraser according to the present invention does not use any PVC (polyvinyl chloride) used in the conventional eraser is not toxic and harmless to the human body can be used with confidence, it does not emit environmental hormones environmentally friendly at the same time erase performance It is excellent in this and can fully exhibit the eraser original function.
이하 본 발명을 상세히 설명한다. Hereinafter, the present invention will be described in detail.
본 발명의 지우개 조성물은 기존 지우개에 사용되던 PVC를 사용하지 않음으로써 프탈레이트계 가소제, 포름알데하이드, 납 등의 인체 유해물질이 검출되지 않아 무독성으로 어린이도 안심하고 사용할 수 있으며, 환경호르몬을 방출하지 않아 환경친화적인 특징이 있다. 뿐만 아니라, 본 발명의 논-피브이씨 지우개 조성물은 기존 PVC 지우개와 비교하여도 글자소거 성능이 우수하여 지우개 본연의 기능을 충분히 발휘할 수 있다.Since the eraser composition of the present invention does not use the PVC used in the conventional eraser, no harmful substances such as phthalate-based plasticizers, formaldehyde, and lead are detected, and thus non-toxic children can be used safely, and do not emit environmental hormones. It is environmentally friendly. In addition, the non-fib C eraser composition of the present invention is excellent in the erase performance, even compared to the conventional PVC eraser can fully exhibit the original function of the eraser.
본 발명의 논-피브이씨 지우개 조성물은 스타이렌-부타디엔-스타이렌, 니트릴 부타디엔 러버 및 폴리스타이렌 공중합체로 이루어지는 열가소성 엘라스토머, 왁스, 미네랄 오일, 탄산칼슘(CaCO3), 산화마그네슘(MgO) 및 이산화티탄(TiO2)을 포함한다.The non-fibse eraser composition of the present invention is a thermoplastic elastomer consisting of styrene-butadiene-styrene, nitrile butadiene rubber and polystyrene copolymer, wax, mineral oil, calcium carbonate (CaCO 3 ), magnesium oxide (MgO) and dioxide Titanium (TiO 2 ).
상기 열가소성 엘라스토머는 상온에서 가황고무와 같은 고무 탄성을 가지고, 고온으로 가열하면 용융 가소화되어 통상의 플라스틱 성형기로 성형 가공이 가능한 고분자 재료이다.The thermoplastic elastomer is a polymer material having a rubber elasticity such as vulcanized rubber at room temperature, melt plasticized when heated to high temperature, and can be molded into a conventional plastic molding machine.
본 발명에 사용되는 상기 열가소성 엘라스토머는 스타이렌-부타디엔-스타이렌(SBS, stylene-butadiene-stylene)과 니트릴 부타디엔 러버(NBR, nitrile butadiene rubber) 및 폴리스타이렌(PS, polystylene) 공중합체를 혼합하여 사용할 수 있다.The thermoplastic elastomer used in the present invention may be used by mixing a styrene-butadiene-styrene (SBS, stylene-butadiene-stylene) and a nitrile butadiene rubber (NBR, nitrile butadiene rubber) and polystyrene (PS, polystylene) copolymer have.
상기 스타이렌-부타디엔-스타이렌은 지우개에 탄성을 부여하는 작용을 한다. 상기 스타이렌-부타디엔-스타이렌은 지우개 조성물에 6~15중량%로 포함되는 것이 바람직하다. 그 함량이 6중량% 미만일 경우에는 탄성을 부여하는 스타이렌 블록의 생성이 불가능하여 최종 생성된 지우개가 부서지기 쉽고, 상온에서의 냉흐럼 현상으로 형상을 유지할 수 없다. 또한, 15중량%를 초과할 경우에는 지우개의 탄성과 강도가 증가하여 dust가 분리되지 않을 수 있다.The styrene-butadiene-styrene acts to give elasticity to the eraser. The styrene-butadiene-styrene is preferably included in the eraser composition in 6 to 15% by weight. If the content is less than 6% by weight, it is impossible to generate the styrene block to impart elasticity, so that the final eraser is brittle, and the shape cannot be maintained due to cold flow phenomenon at room temperature. In addition, when it exceeds 15% by weight, the elasticity and strength of the eraser may increase, and dust may not be separated.
상기 니트릴 부타디엔 러버는 지우개에 점성을 부여하는 작용을 한다. 상기 니트릴 부타디엔 러버는 지우개 조성물에 5~15중량%로 포함되는 것이 바람직하다. 그 함량이 5중량% 미만일 경우에는 지우개의 점성이 없어져 지우개의 dust가 뭉쳐지지 않으며, 15중량%를 초과할 경우에는 지우개의 점성에 비례하여 신율이 증가함으로써 지우개 사용 시 dust가 지우개 몸체에 붙어 늘어날 뿐 분리되지 않을 수 있다.The nitrile butadiene rubber acts to impart viscosity to the eraser. The nitrile butadiene rubber is preferably included in the eraser composition 5 to 15% by weight. If the content is less than 5% by weight, the viscosity of the eraser is lost and the dust of the eraser does not aggregate.If the content exceeds 15% by weight, the elongation is increased in proportion to the viscosity of the eraser. It may not be separated as well.
상기 폴리스타이렌은 지우개 조성물에 1~6중량%로 포함되는 것이 바람직하다. 그 함량이 1중량% 미만일 경우에는 지우개의 지움성(글자소거 성능)이 약해질 수 있으며, 6중량%를 초과할 경우에는 지우개 경도의 허용범위를 초과하여 사용할 수 없게 된다.The polystyrene is preferably contained in 1 to 6% by weight in the eraser composition. If the content is less than 1% by weight, the eraser (erasing performance) of the eraser may be weakened. If the content exceeds 6% by weight, the eraser may not be used beyond the allowable range of hardness.
상기와 같은 함량으로 포함되는 스타이렌-부타디엔-스타이렌, 니트릴 부타디엔 러버 및 폴리스타이렌 공중합체로 이루어지는 열가소성 엘라스토머는 지우개 조성물에 10~40중량%로 포함되는 것이 바람직하다. 그 함량이 상기 범위내일 경우에는 제조되는 지우개에 적당한 경도를 부여할 수 있어 더욱 좋다.The thermoplastic elastomer consisting of styrene-butadiene-styrene, nitrile butadiene rubber and polystyrene copolymers contained in the above content is preferably included in the eraser composition in an amount of 10 to 40% by weight. When the content is within the above range, it is possible to impart an appropriate hardness to the eraser produced.
상기 열가소성 엘라스토머는 스타이렌-부타디엔-스타이렌, 니트릴 부타디엔 러버 및 폴리스타이렌 공중합체 이외에 스타이렌-부타디엔 공중합체(SBR), 스타이렌-이소프렌(styrene-isoprene) 공중합체, 스타이렌-에틸렌-부타디엔(styrene-ethylene-buthylene) 공중합체, 스타이렌-에틸렌-프로필렌(styrene-ethylene-propylene) 공중합체 등의 스타이렌계 열가소성 수지나 열가소성 엘라스토머와 함께 혼합하여 사용할 수도 있다.The thermoplastic elastomer may be a styrene-butadiene copolymer (SBR), a styrene-isoprene copolymer, a styrene-ethylene-butadiene (styrene) in addition to styrene-butadiene-styrene, nitrile butadiene rubber and polystyrene copolymer. It can also be used in combination with a styrene-based thermoplastic resin or thermoplastic elastomer such as -ethylene-buthylene copolymer, styrene-ethylene-propylene copolymer.
상기 왁스는 액상인 것이 좋으며, 지우개에 들어가는 다른 조성물이 용융온도를 저하시켜 제품의 가공온도를 낮추며 흐름성을 부여하는 작용을 한다. It is preferable that the wax is liquid, and the other composition entering the eraser lowers the melting temperature, thereby lowering the processing temperature of the product and providing flowability.
상기 왁스는 지우개 조성물에 1~5중량%로 포함되는 것이 바람직하며, 그 함량이 상기 범위내일 경우에는 적절한 가공온도와 흐름성을 부여하고, 지우개의 경도를 적절히 유지시킬 수 있다.It is preferable that the wax is included in the eraser composition in an amount of 1 to 5% by weight. If the content is within the above range, the wax may be provided with an appropriate processing temperature and flowability, and the hardness of the eraser may be properly maintained.
상기 미네랄 오일은 연화제의 작용을 하며, 그 함량은 지우개 조성물에 5~20중량%로 포함되는 것이 바람직하다. 상기 미네랄 오일이 상기 범위내일 경우에는 적정량의 미네랄 오일이 사용되어 지우개 제조 시 블리드 아웃 없이 적당한 연화를 시킬 수 있다.The mineral oil acts as a softener, the content of which is preferably contained in 5 to 20% by weight in the eraser composition. When the mineral oil is within the above range, an appropriate amount of mineral oil may be used to soften properly without bleeding out when the eraser is manufactured.
상기 탄산칼슘(CaCO3), 산화마그네슘(MgO) 및 이산화티탄(TiO2)은 각각 충진제로 사용되며, 상기 탄산칼슘, 산화마그네슘 및 이산화티탄 이외에 실리카, 알루미나, 규조토, 글라스(glass), 탈크, 세리사이트, 석영분말, 몬모릴로나이트, 가리비, 굴조개, 가막조개 등의 조개 껍질 분말, 알껍질 분말, 유기 중공 입자, 무기 중공 입자 등 통상의 충진제들과 혼합하여 사용할 수도 있다.The calcium carbonate (CaCO 3 ), magnesium oxide (MgO) and titanium dioxide (TiO 2 ) is used as a filler, respectively, in addition to the calcium carbonate, magnesium oxide and titanium dioxide, silica, alumina, diatomaceous earth, glass, talc, It can also be used in combination with conventional fillers such as sericite, quartz powder, montmorillonite, scallops, oyster shells, clam shell powder, egg shell powder, organic hollow particles, inorganic hollow particles.
상기 탄산칼슘(CaCO3), 산화마그네슘(MgO) 및 이산화티탄(TiO2)은 각각 지우개 조성물에 50~70중량%, 0.1~5phr, 0.5~5phr로 포함되는 것이 바람직하다. 그 함량이 상기 범위내일 경우 충분한 고무탄성이 발현되어 지우개 본연의 글자소거 성능을 최대 발휘할 수 있다.The calcium carbonate (CaCO 3 ), magnesium oxide (MgO) and titanium dioxide (TiO 2 ) is preferably included in the eraser composition 50 to 70% by weight, 0.1 to 5phr, 0.5 to 5phr. When the content is within the above range, sufficient rubber elasticity is expressed, and the eraser can achieve the maximum erase performance.
상기와 같은 성분으로 이루어지는 본 발명의 논-피브이씨 지우개 조성물은 상기 성분들 이외에 가공유(process oil), 폴리부티렌(polybutylene), 열소화 파라핀(chlorinated paraffin), 맥화 파라핀 등의 연화제, 착색제, 향료, 안정제, 윤활제, 상기 기재한 스타이렌-부타디엔-스타이렌, 니트릴 부타디엔 러버 및 폴리스타이렌 공중합체 이외의 열가소성 수지나 열가소성 엘라스토머 등을 추가로 더 포함할 수도 있다.The non-fibse eraser composition of the present invention composed of the above components may contain, in addition to the above components, a softener such as process oil, polybutylene, polychlorinated paraffin, macerated paraffin, colorants, A fragrance, a stabilizer, a lubricant, a thermoplastic resin or thermoplastic elastomer other than the above-described styrene-butadiene-styrene, nitrile butadiene rubber, and polystyrene copolymer may be further included.
상기와 같은 지우개 조성물을 사용한 본 발명의 논-피브이씨 지우개는 상기 지우개 조성물을 프레스 성형, 사출 성형, 압출 성형 등에 의해 성형하고, 소정의 치수로 재단하여 제품으로 제조된다.The non-fibrous eraser of the present invention using the above-described eraser composition is molded into a product by press molding, injection molding, extrusion molding, etc., and cutting the eraser composition.
구체적으로, 상기의 지우개 조성물을 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출성형하고, 소정의 치수로 재단하여 본 발명의 논-피브이씨 지우개를 제조할 수 있다.Specifically, the eraser composition is extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C., a die temperature of 50 to 60 ° C., and a head temperature of 60 to 70 ° C., and cut to a predetermined dimension to provide the present invention. Non-fibse eraser can be prepared.
상기와 같이 얻어지는 본 발명의 논-피브이씨 지우개는 염화비닐수지(PVC)를 사용하지 않으면서도 글자소거 성능이 우수하여 지우개 본연의 기능을 충분히 발휘할 수 있다. 또한, 프탈레이트계 가소제, 포름알데하이드, 납 등 인체 유해물질이 검출되지 않아 무독성으로 어린이들도 안심하고 사용할 수 있으며, 환경호르몬을 방출하지 않아 환경친화적이다.The non-fibrous eraser of the present invention obtained as described above is excellent in letter erasing performance without using vinyl chloride resin (PVC), and thus can sufficiently exhibit the original function of the eraser. In addition, no harmful substances such as phthalate-based plasticizers, formaldehyde, lead, etc. are detected, non-toxic children can safely use, it does not emit environmental hormones, it is environmentally friendly.
이하에서는 실시예를 들어 본 발명에 관하여 더욱 상세하게 설명할 것이나. 이들 실시예는 단지 설명의 목적을 위한 것으로 본 발명의 보호 범위를 제한하고자 하는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to examples. These embodiments are for purposes of illustration only and are not intended to limit the scope of protection of the present invention.
실시예 1Example 1
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 10중량%, 니트릴 부타디엔 러버 7중량% 및 폴리스티렌 2중량%와 왁스 3중량%, 미네랄 오일 15중량%, 탄산칼슘(CaCO3) 63중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.10% by weight of styrene-butadiene-styrene, 7% by weight of nitrile butadiene rubber, 2% by weight of polystyrene and 3% by weight of wax, 15% by weight of mineral oil, 63% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
실시예 2Example 2
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 13중량%, 니트릴 부타디엔 러버 6중량% 및 폴리스티렌 3중량%와 왁스 2중량%, 미네랄 오일 15중량%, 탄산칼슘(CaCO3) 61중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.13% by weight of styrene-butadiene-styrene, 6% by weight of nitrile butadiene rubber, 3% by weight of polystyrene and 2% by weight of wax, 15% by weight of mineral oil, 61% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
비교예 1Comparative Example 1
폴리염화비닐(PVC) 수지 26중량%와 천연가소제 30중량%, 탄산칼슘(CaCO3) 44중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 18~30rpm의 성형속도로 압출 성형하여 PVC 지우개를 제조하였다.Cylinder temperature 65 ~ 85 after kneading 26% by weight of polyvinyl chloride (PVC) resin, 30% by weight of natural plasticizer, 44% by weight of calcium carbonate (CaCO 3 ), 2phr of magnesium oxide (MgO) and 2phr of titanium dioxide (TiO 2 ) A PVC eraser was prepared by extrusion molding at a molding speed of 18 to 30 rpm at a temperature of 50 ° C., a die temperature of 50 ° C. to 60 ° C., and a head temperature of 60 ° C. to 70 ° C.
비교예 2Comparative Example 2
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 18중량%, 니트릴 부타디엔 러버 6중량% 및 폴리스티렌 3중량%와 왁스 2중량%, 미네랄 오일 15중량%, 탄산칼슘(CaCO3) 56중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.18% by weight of styrene-butadiene-styrene, 6% by weight of nitrile butadiene rubber, 3% by weight of polystyrene and 2% by weight of wax, 15% by weight of mineral oil, 56% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
비교예 3Comparative Example 3
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 10중량%, 니트릴 부타디엔 러버 4중량% 및 폴리스티렌 3중량%와 왁스 3중량%, 미네랄 오일 15중량%, 탄산칼슘(CaCO3) 65중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.10% by weight of styrene-butadiene-styrene, 4% by weight of nitrile butadiene rubber, 3% by weight of polystyrene and 3% by weight of wax, 15% by weight of mineral oil, 65% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
비교예 4Comparative Example 4
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 8중량%, 니트릴 부타디엔 러버 16중량% 및 폴리스티렌 1중량%와 왁스 2중량%, 미네랄 오일 10중량%, 탄산칼슘(CaCO3) 63중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.8% by weight of styrene-butadiene-styrene, 16% by weight of nitrile butadiene rubber, 1% by weight of polystyrene and 2% by weight of wax, 10% by weight of mineral oil, 63% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
비교예 5Comparative Example 5
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 10중량%, 니트릴 부타디엔 러버 7중량% 및 폴리스티렌 0중량%와 왁스 2중량%, 미네랄 오일 18중량%, 탄산칼슘(CaCO3) 63중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.10% by weight of styrene-butadiene-styrene, 7% by weight of nitrile butadiene rubber, 0% by weight of polystyrene and 2% by weight of wax, 18% by weight of mineral oil, 63% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
비교예 6Comparative Example 6
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 10중량%, 니트릴 부타디엔 러버 6중량% 및 폴리스티렌 8중량%와 왁스 2중량%, 미네랄 오일 14중량%, 탄산칼슘(CaCO3) 60중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.10% by weight of styrene-butadiene-styrene, 6% by weight of nitrile butadiene rubber, 8% by weight of polystyrene and 2% by weight of wax, 14% by weight of mineral oil, 60% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
비교예 7Comparative Example 7
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 10중량%, 니트릴 부타디엔 러버 6중량% 및 폴리스티렌 2중량%와 왁스 0중량%, 미네랄 오일 17중량%, 탄산칼슘(CaCO3) 65중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.10% by weight of styrene-butadiene-styrene, 6% by weight of nitrile butadiene rubber, 2% by weight of polystyrene and 0% by weight of wax, 17% by weight of mineral oil, 65% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
비교예 8Comparative Example 8
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 5중량%, 니트릴 부타디엔 러버 5중량% 및 폴리스티렌 1중량%와 왁스 2중량%, 미네랄 오일 22중량%, 탄산칼슘(CaCO3) 65중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.5% by weight of styrene-butadiene-styrene, 5% by weight of nitrile butadiene rubber, 1% by weight of polystyrene and 2% by weight of wax, 22% by weight of mineral oil, 65% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
비교예 9Comparative Example 9
열가소성 엘라스토머로 스타이렌-부타디엔-스타이렌 8중량%, 니트릴 부타디엔 러버 5중량% 및 폴리스티렌 2중량%와 왁스 2중량%, 미네랄 오일 13중량%, 탄산칼슘(CaCO3) 70중량%, 산화마그네슘(MgO) 2phr 및 이산화티탄(TiO2) 2phr를 혼련시킨 후 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출 성형하여 논-피브이씨 지우개를 제조하였다.8% by weight of styrene-butadiene-styrene, 5% by weight of nitrile butadiene rubber, 2% by weight of polystyrene and 2% by weight of wax, 13% by weight of mineral oil, 70% by weight of calcium carbonate (CaCO 3 ), magnesium oxide ( 2phr of MgO) and 2phr of titanium dioxide (TiO 2 ) were kneaded and extruded at a molding speed of 15 to 25 rpm at a cylinder temperature of 65 to 85 ° C, a die temperature of 50 to 60 ° C, and a head temperature of 60 to 70 ° C. FVC eraser was prepared.
상기 실시예 1~2 및 비교예 1~9에서 제조한 지우개를 이용하여 외관상태, 색상, 지워짐율, 종이 구겨짐, 경도, 이행성, 찌꺼기 생성정도 및 성형성능을 측정하고, 그 결과를 하기 표 2 및 표 3에 나타내었다.Using the erasers prepared in Examples 1 to 2 and Comparative Examples 1 to 9, the appearance state, color, erase rate, paper wrinkle, hardness, transferability, residue generation degree and molding performance were measured, and the results are shown in the following table. 2 and Table 3.
상기 표 1 및 표 3에 나타낸 바와 같이, 본 발명에 따른 실시예 1 및 실시예 2의 지우개는 비교예 1 내지 9와 비교하여 외관상태, 색상, 지워짐율, 종이 구겨짐 정도, 경도, 이행성, 찌꺼기 생성정도 및 성형성능에 있어 모두 우수한 결과를 나타내었다.As shown in Table 1 and Table 3, the erasers of Examples 1 and 2 according to the present invention are compared with Comparative Examples 1 to 9 in appearance, color, erase rate, paper wrinkle degree, hardness, transferability, Excellent results were obtained in terms of residue generation and molding performance.
비록 본 발명이 상기에 언급된 바람직한 실시예로서 설명되었으나, 발명의 요지와 범위로부터 벗어남이 없이 다양한 수정이나 변형을 하는 것이 가능하다. 또한 첨부된 청구 범위는 본 발명의 요지에 속하는 이러한 수정이나 변형을 포함한다.Although the present invention has been described as the preferred embodiment mentioned above, it is possible to make various modifications or variations without departing from the spirit and scope of the invention. The appended claims also cover such modifications and variations as fall within the spirit of the invention.
Claims (4)
왁스;
미네랄 오일;
탄산칼슘(CaCO3);
산화마그네슘(MgO); 및
이산화티탄(TiO2);
을 포함하는 것을 특징으로 하는 논-피브이씨 지우개 조성물.Thermoplastic elastomers composed of styrene-butadiene-styrene, nitrile butadiene rubber and polystyrene copolymers;
Wax;
Mineral oils;
Calcium carbonate (CaCO 3 );
Magnesium oxide (MgO); And
Titanium dioxide (TiO 2 );
Non-fib C eraser composition comprising a.
스타이렌-부타디엔-스타이렌 6~15중량%, 니트릴 부티다엔 러버 5~15중량% 및 폴리스타이렌 공중합체 1~6중량%로 이루어지는 열가소성 엘라스토머 10~40중량%;
왁스 1~5중량%;
미네랄 오일 5~20중량%;
탄산칼슘(CaCO3) 50~70중량%;
산화마그네슘(MgO) 0.1~5phr; 및
이산화티탄(TiO2) 0.5~5phr;
를 포함하는 것을 특징으로 하는 논-피브이씨 지우개 조성물.The method of claim 1,
10 to 40% by weight of thermoplastic elastomer composed of 6 to 15% by weight of styrene-butadiene-styrene, 5 to 15% by weight of nitrile butadiene rubber and 1 to 6% by weight of polystyrene copolymer;
1 to 5 weight percent wax;
Mineral oil 5-20% by weight;
50 to 70% by weight of calcium carbonate (CaCO 3 );
Magnesium oxide (MgO) 0.1-5 phr; And
Titanium dioxide (TiO 2 ) 0.5-5phr;
Non-fib C eraser composition comprising a.
상기 지우개 조성물은 충진제, 가공유(process oil), 폴리부티렌(polybutylene), 연화제, 착색제, 향료, 안정제, 윤활제 및 스타이렌-부타디엔-스타이렌 및 에틸렌-프로필렌 공중합체 이외의 열가소성 수지나 열가소성 엘라스토머 중 선택된 어느 하나 이상의 첨가제를 더 포함하는 것을 특징으로 하는 논-피브이씨 지우개 조성물.The method of claim 1,
The eraser composition may be used in thermoplastic resins or thermoplastic elastomers other than fillers, process oils, polybutylenes, softeners, colorants, flavoring agents, stabilizers, lubricants, and styrene-butadiene-styrene and ethylene-propylene copolymers. The non-fib C eraser composition further comprises any one or more additives selected.
상기 지우개 조성물은 실린더 온도 65~85℃, 다이스 온도 50~60℃, 헤드 온도 60~70℃의 온도에서 15~25rpm의 성형속도로 압출성형하는 것을 특징으로 하는 논-피브이씨 지우개 조성물.The method of claim 1,
The eraser composition is extruded at a molding speed of 15-25 rpm at a temperature of 65 to 85 ° C., a die temperature of 50 to 60 ° C., and a head temperature of 60 to 70 ° C.