KR20110017180A - Resin compositions containing silver particles of nano size and antibacterial film using the same - Google Patents

Resin compositions containing silver particles of nano size and antibacterial film using the same Download PDF

Info

Publication number
KR20110017180A
KR20110017180A KR1020090074737A KR20090074737A KR20110017180A KR 20110017180 A KR20110017180 A KR 20110017180A KR 1020090074737 A KR1020090074737 A KR 1020090074737A KR 20090074737 A KR20090074737 A KR 20090074737A KR 20110017180 A KR20110017180 A KR 20110017180A
Authority
KR
South Korea
Prior art keywords
resin
film
resin composition
curable resin
weight
Prior art date
Application number
KR1020090074737A
Other languages
Korean (ko)
Other versions
KR101160190B1 (en
Inventor
이찬봉
Original Assignee
이찬봉
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이찬봉 filed Critical 이찬봉
Priority to KR1020090074737A priority Critical patent/KR101160190B1/en
Publication of KR20110017180A publication Critical patent/KR20110017180A/en
Application granted granted Critical
Publication of KR101160190B1 publication Critical patent/KR101160190B1/en

Abstract

PURPOSE: A resin composition is provided to reinforce antibacterial activity and sterilizing power on the surface of materials, to prevent the proliferation of bacteria through contact, and to prevent the generation of bad odor caused by excellent deodorization effects. CONSTITUTION: A resin composition comprises 0.01-10 weight% of nanosilver particle colloid solution and 90-99.99 weight% of curable resin. The nanosilver particle colloid solution includes nanosilver particles as a disperse material with organic solvent system, water system, or a mixture of organic solvent system with water system as a dispersing medium. The curable resin is a thermosetting resin ultraviolet curable resin, heat and UV simultaneous curable resin, moisture curable resin, and their mixture.

Description

나노 크기의 은 입자를 함유한 수지 조성물 및 이를 이용한 항균 필름{RESIN COMPOSITIONS CONTAINING SILVER PARTICLES OF NANO SIZE AND ANTIBACTERIAL FILM USING THE SAME} RESIN COMPOSITIONS CONTAINING SILVER PARTICLES OF NANO SIZE AND ANTIBACTERIAL FILM USING THE SAME}

본 발명은 나노 크기의 은 입자를 함유한 수지 조성물 및 이를 이용한 항균 필름에 관한 것으로, 보다 상세하게는 나노 크기의 은 입자를 함유하여 항균성, 살균성을 부여하는 동시에 내구성을 향상시키는 수지 조성물 및 이를 이용한 항균 필름에 관한 것이다.The present invention relates to a resin composition containing nano-sized silver particles and an antimicrobial film using the same, and more particularly to a resin composition containing nano-sized silver particles to provide antimicrobial and bactericidal properties and to improve durability. It relates to an antimicrobial film.

최근 들어 나노기술의 발달로 나노 크기를 갖는 무기입자 또는 금속입자들을 제조하는 것이 용이해졌다. 무기물 또는 금속의 나노 입자들은 그들의 극대화된 표면적 및 양자효과로 인해 벌크(bulk) 상태에서 나타내는 물리, 화학적 성질들을 적은 양으로도 뛰어나게 구현할 뿐만 아니라, 벌크 상태에서와는 다른 성질들을 나타내기도 하는 것으로 보고되고 있다.Recent advances in nanotechnology have made it easier to produce nanoparticles of inorganic or metal particles. Due to their maximized surface area and quantum effects, nanoparticles of inorganic or metals have been reported to not only achieve excellent physical and chemical properties in bulk but also exhibit properties different from those in bulk. .

이와 같이, 나노 입자들은 극소량 사용하여도 벌크 상태로 사용되는 재료와 거의 동등하거나 더욱 우수한 효과를 나타내며, 나노 입자들은 극소량 사용되기 때문에 인체 및 환경에 대한 독성도 거의 존재하지 않으므로, 환경친화적이고 인체에도 유익한 재료로 인정되어, 새로운 재료로 각광받으며 수많은 연구가 진행되고 있다.As such, the nanoparticles exhibit almost the same or better effect as the material used in the bulk state even when the microparticles are used. Since the nanoparticles are used in the small amount, there is little toxicity to the human body and the environment. It is recognized as a beneficial material, has been spotlighted as a new material, and a lot of research is being conducted.

상기 나노 입자들을 합성섬유, 플라스틱 성형품, 필름, 도료, 잉크 등의 고분자수지 제품에 혼입시켜 복합재료로 사용할 경우에는, 고분자수지와 무기 또는 금속 나노 입자와의 낮은 상용성, 응집, 불균일 분포 등으로 인한 복합재료의 물성의 열화 및/또는 불투명화 등의 문제점을 야기하여, 나노 입자화에 따른 의도하는 효과를 수득하는 것이 어려운 것으로 알려져 있다. 이러한 불상용성, 응집, 불균일 분포와 같은 문제점을 해결하기 위하여, 예를 들면 분산제와 같은 상용화제의 사용이나, 나노 입자 존재하의 중합반응 등의 방법들이 제안되었지만, 아직 만족스러운 해결 방법은 개발되지 않았다.When the nanoparticles are mixed with polymer resin products such as synthetic fibers, plastic molded articles, films, paints, and inks to be used as a composite material, the polymer particles and inorganic or metal nanoparticles may have low compatibility, agglomeration, and heterogeneous distribution. It is known that it is difficult to obtain the intended effect of nanoparticles by causing problems such as deterioration and / or opacity of physical properties of the composite material. In order to solve such problems such as incompatibility, aggregation, and non-uniform distribution, methods such as the use of a compatibilizer such as a dispersant or a polymerization reaction in the presence of nanoparticles have been proposed, but a satisfactory solution has not been developed yet. .

한편, 은(銀, silver)은 전도성을 갖는 금속으로서 항균, 살균, 항곰팡이, 탈취, 원적외선 방출, 대전 방지 등의 복합적인 성능을 가지는 것으로 고대로부터 알려져 왔다. 그러나 은은 값비싼 귀금속이기 때문에, 은의 전도성, 항균성, 탈취성 등을 경제적으로 이용하기 위해 미립자화, 실리카와 제올라이트 등의 다공성물질에 담지, 코팅 또는 도금을 통해 이용하여 왔다.On the other hand, silver has been known since ancient times as a conductive metal having a complex performance of antibacterial, antiseptic, anti-fungal, deodorizing, far-infrared emission, antistatic. However, since silver is an expensive precious metal, in order to economically use silver's conductivity, antimicrobial activity, and deodorizing property, it has been used by supporting, coating or plating on porous materials such as silica and zeolite.

나노 크기로 미립자화 된 은나노 입자들은 벌크상의 은에 비해 더욱 탁월한 성질들을 나타낼 것으로 기대되어, 은나노 입자를 분말 또는 액상으로 제조하는 나노기술에 대해 여러 연구가 있었다. 한편, 이렇게 제조된 은나노 입자를 사용한 연구에서, 은나노 입자들은 어떠한 종류의 세균들에 대해서는 수초 이내에 99% 이상의 살균력을 보여주는 등, 벌크상의 은에 비해 현저히 향상된 항균, 살균, 항곰팡이 등의 효과를 보여주는 것으로 보고되었다.Silver nanoparticles that have been micronized to nano size are expected to exhibit more excellent properties than bulk silver, and there have been many studies on nanotechnology for preparing silver nanoparticles in powder or liquid form. On the other hand, in the study using the silver nanoparticles prepared in this way, silver nanoparticles show the effect of antibacterial, bactericidal, anti-mildew, etc. over the silver in the bulk, showing more than 99% bactericidal power in a few seconds for any kind of bacteria. Has been reported.

이러한 나노 입자화 된 은을 중합체와 같은 고분자수지에 첨가하여 섬유(대한민국 공개특허공보 제2003-0055197호, 제2003-0091574호), 필름(대한민국 공개특허공보 제2003-0036491호) 등과 같은 항균성 물품을 제조하는 것이 제안되어 있다. 그러나 콜로이드 상태의 은나노 입자들은 건조 시에 서로 응집하여 마이크로미터 단위의 입자로 성장하게 되며, 고분자수지 내에서 나노미터 크기로 재 분산이 어려운 문제점이 있다. 또한, 분말상태의 은나노 입자들은 중합체와 같은 고분자수지와의 상용성이 적어 혼합이 어려운 문제점이 있다. Antimicrobial articles such as fibers (Korea Patent Publication Nos. 2003-0055197, 2003-0091574), films (Korea Patent Publication No. 2003-0036491), and the like, are added to a polymer resin such as a polymer. It has been proposed to produce. However, the colloidal silver nanoparticles are agglomerated with each other when dried to grow into micrometer-based particles, which is difficult to redistribute to nanometer size in the polymer resin. In addition, the powdered silver nanoparticles are difficult to mix due to their low compatibility with polymer resins such as polymers.

이러한 입자의 응집 등은 필연적으로 나노 입자화에 따른 우수한 효과를 반감시키며, 은나노 입자-고분자수지 복합재료의 물성, 즉 고분자수지의 성능을 저하시키고, 특히 섬유 또는 필름 형태로 제조를 불가능하게 한다.Such agglomeration of particles inevitably halves the excellent effect due to nanoparticles, and deteriorates the physical properties of the silver nanoparticle-polymer resin composite material, that is, the performance of the polymer resin, and makes it impossible to prepare the fiber or film in particular.

이밖에도, 은나노 입자와 모노머를 포함하는 용액의 중합반응에 의해 은나노 입자를 고분자수지 내에 혼입시키는 방법이 제안되었다(대한민국 공개특허공보 제2003-0049007호, 제2003-0031090호). 이러한 방법으로는 은나노 입자가 비교적 균일하게 분산되어 있는 복합재료를 얻을 수 있지만, 용액중합에만 적용할 수 있고, 은나노 입자를 균일하게 분산시키기 위해 사용되는 분산제 등의 첨가제가 중합반응에 영향을 끼칠 수 있다는 문제점이 있다.In addition, a method of incorporating silver nanoparticles into a polymer resin by a polymerization reaction of a solution containing silver nanoparticles and a monomer has been proposed (Korea Patent Publication Nos. 2003-0049007 and 2003-0031090). In this way, a composite material in which silver nanoparticles are relatively uniformly dispersed can be obtained, but it can be applied only to solution polymerization, and additives such as a dispersant used to uniformly disperse silver nanoparticles can affect the polymerization reaction. There is a problem.

구체적으로. 첨가제로 분산제를 사용하면 은나노 입자의 응집은 상당히 억제 되지만, 은나노 입자 콜로이드 용액의 중성 물성이 산성화되어 항균성이 저하하거나 복합재료의 물성이 저하된다는 문제점이 발생한다.Specifically. When the dispersant is used as an additive, aggregation of the silver nanoparticles is significantly suppressed, but the neutral physical properties of the silver nanoparticle colloidal solution are acidified, resulting in a decrease in the antimicrobial properties or the physical properties of the composite material.

따라서, 고분자수지의 물성 및 성능을 저하시키지 않고도 은의 항균효과를 극대화시킬 수 있는 새로운 복합재료의 개발이 요구되고 있다.Therefore, the development of a new composite material that can maximize the antimicrobial effect of silver without deteriorating the physical properties and performance of the polymer resin.

따라서, 본 발명의 제 1 목적은 경화성수지에 나노 크기의 은 입자가 함유된 콜로이드 용액을 혼합시킴으로써, 도포 후 항균성, 살균성, 항곰팡이성, 탈취성, 내구성을 부여할 수 있는 수지 조성물을 제공하는데 있다.Accordingly, a first object of the present invention is to provide a resin composition capable of imparting antimicrobial, bactericidal, antifungal, deodorant and durability after application by mixing a colloidal solution containing nano-sized silver particles with a curable resin. have.

또한, 본 발명의 제 2 목적은 터치패널, 쇼핑카트의 손잡이 등에 사용되는 고분자 필름에 도포하거나, 액상 또는 팰릿(pallet) 형태의 고상의 고분자 원료물질과 균일하게 혼합하여 필름형태로 제조함으로써 항균성, 살균성, 항곰팡이성, 탈취성, 내구성을 부여할 수 있는 항균 필름을 제공하는데 있다.In addition, the second object of the present invention is applied to the polymer film used in the touch panel, the handle of the shopping cart, or the like, or uniformly mixed with a solid polymer material in the form of a liquid or a pallet (pallet) to produce a film form antibacterial, It is to provide an antimicrobial film that can provide bactericidal, anti-mildew, deodorant, durability.

상술한 본 발명의 제 1 목적을 달성하기 위하여, 본 발명의 일 실시예에서는 은나노 입자 콜로이드 용액 0.01 내지 10 중량%, 및 경화성수지 90 내지 99.99 중량%를 포함하는 나노 크기의 은 입자를 함유한 수지 조성물을 제공한다. In order to achieve the first object of the present invention described above, in one embodiment of the present invention, the resin containing nano-sized silver particles containing 0.01 to 10% by weight silver nanoparticle colloidal solution, and 90 to 99.99% by weight curable resin To provide a composition.

또한, 본 발명의 제 2 목적을 달성하기 위하여, 본 발명의 일 실시예 에서는 상기 수지 조성물이 0.1 내지 100 ㎛의 두께로 도포된 고분자 필름을 포함하는 항균 필름을 제공한다.In addition, in order to achieve the second object of the present invention, an embodiment of the present invention provides an antimicrobial film comprising a polymer film coated with a thickness of 0.1 to 100 ㎛.

본 발명에 의한 수지 조성물은 각종 터치패널, 쇼핑카트 등 다수의 사람이 접촉하는 물체에 사용되는 고분자 필름의 표면에 도포되거나, 고분자 필름의 제조단계에서 혼합하여 항균성 등이 우수한 기능성 고분자 필름을 제조할 수 있다. 또한, 상기 항균성 등이 우수한 기능성 고분자 필름을 버선형태로 제작하여 신은 후, 스키장에서 대여하는 스키 부츠 등을 착화할 수도 있다. The resin composition according to the present invention may be applied to the surface of a polymer film used for various touch panels, shopping carts, or other objects in contact with each other, or may be mixed in the manufacturing step of the polymer film to produce a functional polymer film having excellent antibacterial properties. Can be. In addition, after producing and wearing a functional polymer film having excellent antimicrobial activity in a tabular form, it may be ignited ski boots and the like rented at a ski resort.

이와 같이, 불특정 다수가 사용하는 물체에 적용하면, 해당 물체에 항균력, 살균력, 탈취력을 부여함으로써, 손이나 발 등의 접촉을 통해 세균이 번식되는 것을 방지한다. 특히, 공중이 이용하는 공공물의 표면 등을 지속적으로 청결하게 유지할 수 있으므로, 별도의 공중위생 활동 없이도 세균의 번식을 억제할 수 있다.In this way, when applied to an object used by an unspecified number of people, by providing antimicrobial, sterilizing, and deodorizing power to the object, bacteria are prevented from propagating through contact with hands or feet. In particular, since the surface of the public used by the public can be kept clean constantly, it is possible to suppress the growth of bacteria without a separate public health activity.

또한, 물로 세척한 이후에도 부착된 물체의 표면에 99% 이상의 항균력을 제공한다. 아울러, 수지 조성물이 도포된 항균 필름은 각종 터치패널, PDP, LCD 등의 표면에 구비됨에 따라 상기 표면의 내구성을 강화시켜 손 등에 의해 지속적으로 접촉되어도 흠집이 발생되는 것이 억지된다. 이와 같이, 액정의 흠집 발생이 억지됨에 따라 액정의 교체주기가 길어져 전자제품의 관리비용이 감소되는 효과가 있다.In addition, even after washing with water provides more than 99% antimicrobial activity on the surface of the attached object. In addition, the antimicrobial film to which the resin composition is applied is provided on the surface of various touch panels, PDPs, LCDs, etc., thereby enhancing the durability of the surface, and thus preventing scratches from occurring even when continuously contacted by a hand or the like. As such, as the occurrence of scratches on the liquid crystal is inhibited, the replacement cycle of the liquid crystal is prolonged, thereby reducing the management cost of the electronic product.

이하, 본 발명의 바람직한 실시예들에 의한 나노 크기의 은 입자를 함유한 수지 조성물(이하, "수지 조성물"이라 한다) 및 이를 이용한 항균 필름을 상세하게 설명한다.Hereinafter, a resin composition containing nano-sized silver particles according to preferred embodiments of the present invention (hereinafter referred to as a "resin composition") and an antimicrobial film using the same will be described in detail.

본 발명의 일 실시예에 의한 수지 조성물은 은나노 입자 콜로이드 용액 및 경화성수지를 포함하고, 첨가제를 추가적으로 포함할 수 있다. 이러한, 수지 조성물은 터치폰을 비롯하여 은행과 증권사의 ATM기기, 관공서에서 사용되는 민원발급기 등에 사용되는 TFT-LCD 등의 터치패널, 쇼핑카트의 손잡이 등의 표면부에 적용하거나, 스키 부츠용 버선 등의 제작에 사용되어 각종 세균 등으로부터 안전하게 표면부를 유지하도록 하는 역할을 수행한다.The resin composition according to an embodiment of the present invention includes a silver nanoparticle colloidal solution and a curable resin, and may further include an additive. Such a resin composition is applied to a touch panel, a touch panel such as a TFT-LCD used in an ATM machine of a bank and securities company, a civil service dispenser used in a public office, a handle of a shopping cart, or a tab for ski boots. It is used in the production of serves to keep the surface portion safe from various bacteria and the like.

이러한 각각의 성분들은 서로 화학적인 작용을 통하여 공동으로 기능을 수행할 수도 있는데, 이는 화학 물질의 특성상 당연한 것이다. 따라서, 본 발명은 특정 기능 성분에만 의존 한다기보다는 여러 조성의 조합과 그 조합량에 특이성이 있다고 할 수 있다. Each of these components may also function jointly through a chemical action with each other, which is natural due to the nature of the chemicals. Therefore, the present invention may be said to be specific in the combination of the various compositions and the amount thereof, rather than only depending on the specific functional ingredient.

본 발명의 일 실시예에 의한 수지 조성물은 은나노 입자 콜로이드 용액을 포함한다.The resin composition according to an embodiment of the present invention includes a silver nanoparticle colloidal solution.

상기 은나노 입자 콜로이드 용액은 수지 조성물이 사용되어 항균력, 살균력 을 부여하는 것으로서, 항곰팡이성, 탈취성이 우수하다. The silver nanoparticle colloidal solution is used to impart antimicrobial and bactericidal power by using a resin composition, and has excellent antifungal and deodorizing properties.

상기 은나노 입자 콜로이드 용액은 은나노 입자가 콜로이드 상태로 존재하는 것이라면 어떠한 은나노 입자 콜로이드 용액을 사용하여도 무방하지만, 바람직하게는 당업계에서 통상적으로 사용되는 은나노 입자 콜로이드 용액을 사용하는 것이 좋으며, 보다 바람직하게는 분산질로서 1 내지 20㎚ 크기의 은나노 입자와 분산매로서 수계, 유기용제계, 또는 수계와 유기용제계의 혼합물을 사용할 수 있다. The silver nanoparticle colloidal solution may be any silver nanoparticle colloidal solution as long as the silver nanoparticles are present in a colloidal state, but preferably, a silver nanoparticle colloidal solution commonly used in the art is preferably used. As the dispersoid, silver nanoparticles having a size of 1 to 20 nm and an aqueous solvent, an organic solvent, or a mixture of an aqueous solvent and an organic solvent may be used.

구체적으로 상기 분산매로는 물, 알코올, 케톤류(아세톤, 메틸에틸케톤, 메틸이소부틸케톤, 시클로헥사논 등), 에테르류(메틸셀루솔브, 에틸셀루솔브, 부틸셀루솔브 등), 에스테르류(에틸아세테이트, 부틸아세테이트 등), 디메틸포름아마이드(dimethylformamide : 이하, "DMF"라 한다.), n-메틸피로리딘, 프로필렌 글리콜모노메틸 에테르 아세테이트, 디베이직 에스테르, 디메틸카보네이트, 또는 톨루엔 등을 사용할 수 있으며, 이들을 2 이상 혼합하여 사용할 수도 있다. Specifically, examples of the dispersion medium include water, alcohols, ketones (acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, etc.), ethers (methyl celusolve, ethyl celusolve, butyl celusolve, etc.), esters (ethyl Acetate, butyl acetate, etc.), dimethylformamide (hereinafter referred to as "DMF"), n-methylpyrrolidine, propylene glycol monomethyl ether acetate, dibasic ester, dimethyl carbonate, or toluene. These can also be used in mixture of 2 or more.

여기서, 상기 은나노 입자 콜로이드 용액은 25℃에서 5 내지 10 ㎫·s 범위의 점도를 나타내며, 25℃에서 0.97 내지 0.99 범위의 액상비중을 가지는 물성의 은나노 입자 콜로이드를 사용하는 것이 바람직하다. Here, the silver nanoparticle colloidal solution exhibits a viscosity in the range of 5 to 10 MPa · s at 25 ° C., and it is preferable to use a silver nano particle colloid of physical properties having a liquid specific gravity in the range of 0.97 to 0.99 at 25 ° C.

필요에 따라, 은나노 입자 콜로이드 용액은 분산제, 반응첨가제를 더 포함할 수도 있다. 여기서, 상기 분산제로는 왁스를 사용할 수 있으며, 상기 반응첨가제로는 퓨란계, 타이타니아계, 지르코니아계 등을 사용할 수 있다. If necessary, the silver nanoparticle colloidal solution may further include a dispersant and a reaction additive. Here, a wax may be used as the dispersant, and as the reaction additive, a furan-based, titania-based, zirconia-based, etc. may be used.

본 발명에 따른 수지 조성물에 포함되는 은나노 입자 콜로이드 용액은 전체 100 중량%를 기준으로 0.01 내지 10 중량%가 포함된다. 이때, 수지 조성물에 포함 되는 은나노 입자 콜로이드 용액의 함량이 0.01 중량% 미만이면 수지 조성물에 포함된 은나노 입자의 함량이 낮아서 필름에 도포하거나, 필름 제조시 필름제조용 고분자 원료물질, 예를 들면 고분자 용융액(액상의 고분자) 또는 팰릿 형태의 고상의 고분자 필름 제조용 원료물질과 혼합하여 사용할 경우 상기 필름의 표면에 증식하는 세균을 살균하는데 어려움이 발생될 수 있으며, 은나노 입자 콜로이드 용액의 함량이 10 중량%를 초과하면 사용량 증가에 따른 효과의 향상은 미비하지만 생산비가 증가된다.The silver nanoparticle colloidal solution included in the resin composition according to the present invention contains 0.01 to 10% by weight based on the total 100% by weight. In this case, when the content of the silver nanoparticle colloidal solution included in the resin composition is less than 0.01% by weight, the content of the silver nanoparticles included in the resin composition is low and applied to the film, or a polymer raw material for manufacturing a film, for example, a polymer melt ( When used in combination with a raw material for preparing a solid polymer film in the form of a liquid or pallet), it may be difficult to sterilize the bacteria that grow on the surface of the film, and the content of the silver nanoparticle colloid solution exceeds 10% by weight. In this case, the effect of increased usage is insignificant, but production costs increase.

일 실시 양태로서, 상기 은나노 입자 콜로이드 용액은 100 중량%를 기준으로 은나노 입자 1 내지 7 중량%와 물, 알코올, 케톤류(아세톤, 메틸에틸케톤, 메틸이소부틸케톤, 시클로헥사논 등), 에테르류(메틸셀루솔브, 에틸셀루솔브, 부틸셀루솔브 등), 에스테르류(에틸아세테이트, 부틸아세테이트 등), DMF, n-메틸피로리딘, 프로필렌 글리콜모노메틸 에테르 아세테이트, 디베이직 에스테르, 디메틸카보네이트, 톨루엔, 또는 이들을 2 이상 혼합한 분산매를 93 내지 99 중량%를 포함할 수 있다.  In one embodiment, the silver nanoparticle colloidal solution is based on 100% by weight of the silver nanoparticles 1 to 7% by weight, water, alcohol, ketones (acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, etc.), ethers (Methyl cellosolve, ethyl cellosolve, butyl cellosolve, etc.), esters (ethyl acetate, butyl acetate, etc.), DMF, n-methylpyrrolidine, propylene glycol monomethyl ether acetate, dibasic ester, dimethyl carbonate, toluene, Or 93 to 99% by weight of a dispersion medium obtained by mixing two or more thereof.

본 발명의 일 실시예에 의한 수지 조성물은 경화성수지를 포함한다.The resin composition according to an embodiment of the present invention includes a curable resin.

상기 경화성수지는 건조된 수지 조성물의 경도를 향상시키기 위해 첨가된 것으로서, 바람직하게는 2H 내지 5H(표준번호 KS M ISO 15184:2002 방법에 의함)의 경도를 갖는 열경화성수지, UV경화성수지, 열 및 UV 동시 경화성수지, 습기경화성 수지 또는 이들을 2 이상 혼합한 수지를 사용할 수도 있다.The curable resin is added to improve the hardness of the dried resin composition, preferably a thermosetting resin, a UV curable resin, a heat and a hardness of 2H to 5H (by the standard number KS M ISO 15184: 2002 method) UV simultaneous curable resins, moisture-curable resins, or resins of two or more thereof may be used.

상기 열경화성수지로는 에폭시수지, 우레탄수지, 아크릴수지, 불소수지 등을 사용하는 것이 바람직하지만, 이들에 한정되지 않는다.The thermosetting resin is preferably epoxy resin, urethane resin, acrylic resin, fluorine resin or the like, but is not limited thereto.

상기 UV경화성수지로는 어떠한 UV경화성수지를 사용하여도 무방하지만, 바람직하게는 폴리우레탄아크릴레이트 25 내지 35 중량부, 반응성 모노머 희석제 10 내지 27 중량부, 접착촉진제 1 내지 3 중량부, 메틸에틸케톤(methyl ethyl ketone : 이하 "MEK"라 한다.) 15 내지 20 중량부, 톨루엔 20 내지 25 중량부로 이루어진 혼합물을 사용하는 것이 좋다. 이때, 상기 UV경화성수지에는 기타용제 5 내지 27 중량부가 더 포함될 수 있다. 여기서, 상기 반응성 모노머 희석제로는 단관능 아크릴레이트모노머, 삼관능 아크릴레이트모노머 또는 이들의 혼합물을 사용하는 것이 바람직하다.The UV curable resin may be any UV curable resin, but preferably 25 to 35 parts by weight of polyurethane acrylate, 10 to 27 parts by weight of reactive monomer diluent, 1 to 3 parts by weight of adhesion promoter, and methyl ethyl ketone (Methyl ethyl ketone: hereinafter referred to as "MEK".) A mixture consisting of 15 to 20 parts by weight and 20 to 25 parts by weight of toluene is preferably used. At this time, the UV curable resin may further include 5 to 27 parts by weight of other solvents. Here, as the reactive monomer diluent, it is preferable to use a monofunctional acrylate monomer, a trifunctional acrylate monomer or a mixture thereof.

또한, 상기 UV경화성수지로는 폴리우레탄아크릴레이트 25 내지 35 중량부, 반응성 모노머 희석제 15 내지 40 중량부, 접착촉진제 1 내지 3 중량부, 광개시제 8 내지 14 중량부, 레벨링제 0.5 내지 1.5 중량부, MEK 15 내지 20 중량부, 톨루엔 20 내지 25 중량부 및 부틸아세테이트 1 내지 10 중량부로 이루어진 혼합물을 사용할 수도 있다. 여기서, 상기 반응성 모노머 희석제로는 단관능 아크릴레이트 모노머, 이관능 아크릴레이트 모노머, 삼관능 아크릴레이트 모노머, 다관능 아크릴레이트 모노머, 또는 이들의 혼합물을 사용할 수 있다. In addition, the UV curable resin 25 to 35 parts by weight of polyurethane acrylate, 15 to 40 parts by weight of reactive monomer diluent, 1 to 3 parts by weight of adhesion promoter, 8 to 14 parts by weight of photoinitiator, 0.5 to 1.5 parts by weight of leveling agent, It is also possible to use a mixture consisting of 15 to 20 parts by weight of MEK, 20 to 25 parts by weight of toluene and 1 to 10 parts by weight of butyl acetate. Here, as the reactive monomer diluent, a monofunctional acrylate monomer, a bifunctional acrylate monomer, a trifunctional acrylate monomer, a polyfunctional acrylate monomer, or a mixture thereof may be used.

상기 열 및 UV 동시 경화성수지로는 에폭시 아크릴레이트 10 내지 65 중량부, 반응성 모노머 15 내지 60 중량부, 광개시제 2 내지 10 중량부, 레벨링제 0.5 내지 5 중량부 및 경화제 20 내지 50 중량부로 이루어진 혼합물을 사용할 수 있다.The heat and UV co-curable resin is a mixture consisting of 10 to 65 parts by weight of epoxy acrylate, 15 to 60 parts by weight of reactive monomer, 2 to 10 parts by weight of photoinitiator, 0.5 to 5 parts by weight of leveling agent and 20 to 50 parts by weight of curing agent. Can be used.

상기 반응성 모노머로는 단관능 모노머, 2관능 모노머, 3관능 모노머, 다관능 모노머, 또는 이들의 혼합물을 사용할 수 있다.As said reactive monomer, a monofunctional monomer, a bifunctional monomer, a trifunctional monomer, a polyfunctional monomer, or a mixture thereof can be used.

구체적으로, 상기 단관능 모노머로는 2-에틸 헥실 아크릴레이트, 옥틸데실 아크릴레이트, 이소데실아크릴레이트, 트리데실메타아크릴레이트, 라우릴아크릴레이트, 스테아릴아크릴레이트, 베헤닐아크릴레이트, 2-페녹시에틸아크릴레이트, 노닐페놀에톡시레이티드모노아크릴레이트, 베타카르복시에틸아크릴레이트, 이소보닐아크릴레이트, 테트라하이드로퍼푸릴아크릴레이트, 테트라하이드로퍼푸릴메타아크릴레이트, 4-부틸사이클로헥실아크릴레이트, 디사이클로펜테닐아크릴레이트, 디사이클로펜테닐옥시에틸아크릴레이트, 에톡시레이티드모노아크릴레이트 등을 사용할 수 있다.Specifically, the monofunctional monomer is 2-ethyl hexyl acrylate, octyldecyl acrylate, isodecyl acrylate, tridecyl methacrylate, lauryl acrylate, stearyl acrylate, behenyl acrylate, 2-phenoxy Cethylethylacrylate, nonylphenolethoxylated monoacrylate, betacarboxyethylacrylate, isobonylacrylate, tetrahydrofurfuryl acrylate, tetrahydrofurfuryl methacrylate, 4-butylcyclohexyl acrylate, di Cyclopentenyl acrylate, dicyclopentenyl oxyethyl acrylate, ethoxylated monoacrylate and the like can be used.

상기 2관능 모노머로는 1,6-헥산디올디아크릴레이트, 트리페닐글리콜디아크릴레이트, 부탄디올디아크릴레이트, 1,3-부틸렌글리콜디메타크릴레이트, 1,6-헥산디올디메타크릴레이트, 네오펜틸글리콜디아크릴레이트, 에틸렌글리콜디아크릴레이트, 디에틸렌글리콜디메타크릴레이트, 테트라에틸렌글리콜디메타아크릴레이트, 트리에틸렌글리콜디메타아크릴레이트, 폴리에틸렌글리콜디아크릴레이트, 폴리에틸렌글리콜디메타아크릴레이트, 디프로필렌글리콜디아크릴레이트, 에톡시레이티드네오펜틸글리콜디아크릴레이트 등을 사용할 수 있다.As said bifunctional monomer, 1, 6- hexanediol diacrylate, a triphenyl glycol diacrylate, butanediol diacrylate, 1, 3- butylene glycol dimethacrylate, 1, 6- hexanediol dimethacrylate Neopentyl glycol diacrylate, ethylene glycol diacrylate, diethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, triethylene glycol dimethacrylate, polyethylene glycol diacrylate, polyethylene glycol dimethacrylate , Dipropylene glycol diacrylate, ethoxylated neopentyl glycol diacrylate, and the like can be used.

상기 3관능 모노머로는 트리메틸올프로판트리아크릴레이트, 트리메틸을프로판트리메타아크릴레이트, 펜타에리쓰리톨트리아크릴레이트, 에톡시레이티드트리메틸올프로판트리아크릴레이트, 프로필레이티드 트리메틸올프로판트리아크릴레이트, 글리세릴프로필레이티드트리아크릴레이트, 트리스(2-하이드록시에틸)이소시아누레이트 트리아크릴레이트 등을 사용할 수 있다.Examples of the trifunctional monomers include trimethylolpropane triacrylate, trimethyl propane trimethacrylate, pentaerythritol triacrylate, ethoxylated trimethylolpropane triacrylate, propylated trimethylolpropane triacrylate, Glyceryl propylated triacrylate, tris (2-hydroxyethyl) isocyanurate triacrylate, etc. can be used.

상기 다관능 모노머로는 펜타에리쓰리톨테트라아크릴레이트, 알콕시레이티드테트라아크릴레이트 등을 사용할 수 있다.As said polyfunctional monomer, pentaerythritol tetraacrylate, an alkoxylated tetraacrylate, etc. can be used.

상기 광개시제는 자외선에 의해 활성을 띠는 벤조페논계, 벤조인, 벤조인에테르계, 벤질케탈계, 아세토페논계, 안트라퀴논계, 티옥산톤계를 사용할 수 있으며, 상기 레벨링제는 실리콘 디아크릴레이트계나 실리콘 폴리 아크릴레이트계의 화합물을 사용할 수 있으며, 상기 경화제는 산무수물과 아민계 촉매를 사용할 수 있다. The photoinitiator may be benzophenone-based, benzoin, benzoin ether-based, benzyl ketal-based, acetophenone-based, anthraquinone-based, thioxanthone-based active by the ultraviolet ray, the leveling agent is silicone diacrylate The compound of the type | system | group or silicone polyacrylate type can be used, The said hardening | curing agent can use an acid anhydride and an amine catalyst.

한편, 상기 습기경화성 수지로는 습기 경화성 폴리우레탄 수지 등을 예시할 수 있다. On the other hand, as the moisture-curable resin may be a moisture-curable polyurethane resin and the like.

본 발명에 따른 수지 조성물에 포함되는 경화성수지는 전체 100 중량%를 기준으로 90 내지 99.99 중량%가 포함된다. 이때, 수지 조성물에 포함되는 경화성수지의 함량이 90 중량% 미만이면 충분한 내구성을 나타낼 수 없다. 또한, 수지 조성물에 포함되는 경화성수지의 함량이 99.99 중량%를 초과하면 전체 조성에서 은나노 입자 콜로이드 용액의 첨가량이 감소하여 항균성이 저하될 수 있다. Curable resin included in the resin composition according to the present invention contains 90 to 99.99% by weight based on 100% by weight. At this time, if the content of the curable resin contained in the resin composition is less than 90% by weight can not exhibit sufficient durability. In addition, when the content of the curable resin contained in the resin composition exceeds 99.99% by weight, the amount of the silver nanoparticle colloidal solution in the total composition may decrease, which may lower the antimicrobial activity.

본 발명의 일 실시예에 의한 수지 조성물은 첨가제를 더 포함할 수 있다.The resin composition according to an embodiment of the present invention may further include an additive.

상기 첨가제로는 필름에 부착증진을 위하여 실란 커플링 첨가제를 사용할 수 있다. 이때, 실란 커플링 첨가제로는 비닐관능기의 트리메톡시 실란, 클로로 프로 필 트리메톡시 실란, 글리시딜 에테르 관능기의 트리메톡시 실란, 메타아크릴레이트 관능기의 트리메톡시 실란, 1급아민 관능기 및 2관능 아민 관능기의 트리메톡시 실란, 머캅토 프로필 트리메톡시 실란, 양이온 스터럴 트리메톡시 실란, 크로스링커 트리메톡시 실란 등을 사용할 수 있다.As the additive, a silane coupling additive may be used to promote adhesion to the film. In this case, as the silane coupling additive, trimethoxy silane of vinyl functional group, chloro profile trimethoxy silane, trimethoxy silane of glycidyl ether functional group, trimethoxy silane of methacrylate functional group, primary amine functional group and Trimethoxy silane, mercapto propyl trimethoxy silane, cationic sterral trimethoxy silane, crosslinker trimethoxy silane, etc. of a bifunctional amine functional group can be used.

이와 같이, 본 발명에 따른 수지 조성물은 항균성 및 내구성을 부여할 수 있으므로, 터치폰, ATM기기, 민원발급기 등에 사용되는 터치패널, 및 자동판매기의 버튼이나 쇼핑카트의 손잡이, 부츠 착용시 신을 수 있는 버선의 표면 또는 그 재료로 사용될 수 있다.Thus, since the resin composition according to the present invention can impart antimicrobial properties and durability, the touch panel used in touch phones, ATM devices, civil service dispensers, etc., and the buttons of the vending machines, the handles of shopping carts, and the boots can be worn. It may be used as the surface of the tab or the material thereof.

본 발명은 상기 수지 조성물이 고분자 필름에 적용된 항균 필름을 제공한다. The present invention provides an antimicrobial film to which the resin composition is applied to a polymer film.

먼저, 상기 수지 조성물은 액상 또는 고상의 고분자 필름 제조용 고분자 원료물질과 균일하게 혼합하여 항균 필름을 제작하는 방식으로 사용될 수 있다. 이때, 상기 수지 조성물은 약 1 내지 40 중량%, 상기 고분자 원료물질은 약 60 내지 99 중량%를 사용하는 것이 바람직하다. 상기 수지 조성물을 1 중량% 미만 사용하면 함유된 은나노 콜로이드의 함량이 함께 적어지기 때문에 충분한 항균성이 나타나지 않으며, 반대로 40 중량%를 초과하여 사용하면 고가인 은나노 콜로이드의 사용량 증가에 따라 제품의 경제성이 저하될 뿐만 아니라, 필름형태로 제조된 완성품을 각종 기기나 제품 등에 적용할 때 요구되는 필름으로서의 물성이 저하되는 문제점이 발생된다. First, the resin composition may be used by uniformly mixing with a polymer raw material for preparing a liquid or solid polymer film to prepare an antimicrobial film. At this time, the resin composition is about 1 to 40% by weight, the polymer raw material is preferably used about 60 to 99% by weight. If the resin composition is used in less than 1% by weight, the content of the silver nano-colloids contained is less together, so there is no sufficient antimicrobial activity. In addition, there is a problem that the physical properties as a film required when applying the finished product manufactured in the form of a film to various equipment or products, etc. occurs.

상기 고분자 필름 제조용 고분자 원료물질은 폴리프로필렌, 폴리에틸렌, 폴리에틸렌테레프탈레이트, 폴리우레탄, 폴리스티렌, 폴리염화비닐, 에틸렌비닐아세테이트, ABS, 폴리카보네이트, 또는 나일론 필름을 제조하기 위한 액상 또는 고상의 고분자 원료물질이거나, 이런 원료물질들을 2 이상 혼합한 고분자의 원료물질일 수 있다. The polymer raw material for producing the polymer film is a liquid or solid polymer raw material for producing polypropylene, polyethylene, polyethylene terephthalate, polyurethane, polystyrene, polyvinyl chloride, ethylene vinyl acetate, ABS, polycarbonate, or nylon film For example, the raw material of the polymer may be a mixture of two or more such raw materials.

이와 같이 상기 수지 조성물과 상기 고분자 원료물질을 혼합하여 제작한 항균 필름은 표면뿐만 아니라 필름 전체가 항균성 등의 기능성을 가지므로, 설사 표면 필름이 손상되더라도 항균성 등의 기능성을 그대로 유지할 수 있다. As described above, the antimicrobial film prepared by mixing the resin composition and the polymer raw material has functionalities such as the surface as well as the antimicrobial, and thus, even if the surface film is damaged, the antimicrobial and the like can be maintained as it is.

이와는 달리, 필름형태로 제작된 고분자 필름 표면에 상기 수지 조성물을 도포하여 상기 항균 필름을 제작할 수도 있다. Alternatively, the antimicrobial film may be prepared by applying the resin composition to the surface of the polymer film made in the form of a film.

상기 고분자 필름은 1 내지 300 ㎛ 두께의 폴리프로필렌, 폴리에틸렌, 폴리에틸렌테레프탈레이트, 폴리우레탄, 폴리스티렌, 폴리염화비닐, 에틸렌비닐아세테이트, ABS, 폴리카보네이트, 또는 나일론 소재의 필름이거나, 이러한 각각의 고분자 필름 제조를 위한 원료물질을 복수 개 혼합하여 제작한 복합소재의 필름이 사용될 수 있지만, 이에 한정되지는 않는다.The polymer film is a film made of polypropylene, polyethylene, polyethylene terephthalate, polyurethane, polystyrene, polyvinyl chloride, ethylene vinyl acetate, ABS, polycarbonate, or nylon having a thickness of 1 to 300 μm, or each of these polymer films The film of the composite material produced by mixing a plurality of raw materials for may be used, but is not limited thereto.

이러한 항균 필름은 고분자 필름의 표면에 0.01 내지 100 ㎛ 두께의 수지 조성물을 도포하는 단계와, 상기 고분자 필름에 300 내지 500 mJ/㎠의 자외선(UV) 광량을 제공하는 동시에 70 내지 80℃로 2분 동안 건조하는 단계를 통하여 제조할 수 있다.The antimicrobial film is coated with a resin composition having a thickness of 0.01 to 100 μm on the surface of the polymer film, and at the same time providing the polymer film with an ultraviolet (UV) light amount of 300 to 500 mJ / cm 2 at 70 to 80 ° C. for 2 minutes. It can be prepared through the step of drying.

특정 양태로서, 본 발명에 따른 항균 필름은 30 내지 70 ㎛ 두께의 제 2 고 분자 필름, 상기 제 2 고분자 필름의 상부에 구비된 제 1 실리콘 압력밀봉접착제(Pressure Sealing Adhesive: PSA) 점착층, 상기 제 1 실리콘 PSA 점착층의 상부에 구비된 1 내지 300 ㎛ 두께의 고분자 필름, 상기 고분자 필름 상부에 구비된 수지 조성물, 상기 수지 조성물 상부에 구비된 제 2 실리콘 PSA 점착층, 및 상기 제 2 실리콘 PSA 점착층의 상부에 구비된 30 내지 70 ㎛ 두께의 제 3 고분자 필름을 포함할 수 있다. 여기서, 제 2 고분자 필름과 제 3 고분자 필름은 상기 고분자 필름과 동일한 소재를 사용하는 것이 바람직하다.In a particular embodiment, the antimicrobial film according to the present invention comprises a second high molecular film having a thickness of 30 to 70 μm, a first silicone pressure-sealing adhesive (PSA) adhesive layer provided on the second polymer film, and A polymer film having a thickness of 1 to 300 μm provided on the first silicon PSA adhesive layer, a resin composition provided on the polymer film, a second silicon PSA adhesive layer provided on the resin composition, and the second silicon PSA It may include a third polymer film of 30 to 70 ㎛ thickness provided on the adhesive layer. Here, it is preferable that the second polymer film and the third polymer film use the same material as the polymer film.

이와 같이, 제 2 고분자 필름 및 제 3 고분자 필름이 구비된 항균 필름은 제품에 사용하는 시점에, 제 1 실리콘 PSA 점착층으로부터 제 2 고분자 필름을 분리시키고, 제 2 실리콘 PSA 점착층으로부터 제 3 고분자 필름을 분리시켜 사용할 수 있다.As described above, the antimicrobial film provided with the second polymer film and the third polymer film separates the second polymer film from the first silicone PSA adhesive layer at the time of use in the product, and the third polymer from the second silicone PSA adhesive layer. The film can be used separately.

즉, 상기 제 2 고분자 필름 및 제 3 고분자 필름은 임의적으로 분리시킬 수 있도록 구비되어 수지 조성물이 도포된 고분자 필름의 사용성을 향상시킨다. That is, the second polymer film and the third polymer film are provided to be separated from each other to improve the usability of the polymer film coated with a resin composition.

이하, 본 발명을 바람직한 일 실시예를 참조하여 다음에서 구체적으로 상세하게 설명한다. 단, 다음의 실시예는 본 발명을 구체적으로 예시하기 위한 것이며, 이것만으로 한정하는 것은 아니다.Hereinafter, the present invention will be described in detail with reference to a preferred embodiment. However, the following Example is for illustrating this invention concretely, It does not limit only to this.

UV경화성수지 제조UV Curable Resin Manufacture

교반기 및 냉각기가 장치되어 있는 반응용기에 폴리우레탄아크릴레이트 250g, 이소보닐아크릴레이트 50g, 트리메틸올프로판트리아크릴레이트 100g, 접착촉진제 30g, MEK 200g, 톨루엔 250g, 부틸아세테이트 50g을 투입하여 상온에서 2시간 동안 400rpm으로 교반하고 방치하여 기포가 제거된 UV경화성수지를 수득하였다. Into the reaction vessel equipped with a stirrer and a cooler, 250 g of polyurethane acrylate, 50 g of isobornyl acrylate, 100 g of trimethylolpropane triacrylate, 30 g of adhesion promoter, 200 g of MEK, 250 g of toluene, and 50 g of butyl acetate were added thereto at room temperature for 2 hours. The mixture was stirred at 400 rpm and left to obtain a UV-curable resin free of bubbles.

은나노 콜로이드 용액 제조Silver Nano Colloidal Solution Preparation

1. 물 592g에 AgNO3 1.863g, 이소프로필알코올 395g 및 75:25 혼합중량비의 (1-비닐 피롤리돈)-아크릴산 공중합체(M.W. 96,000) 11.137g을 완전히 용해시켰다. 1. Dissolve 1.863 g of AgNO 3 , 395 g of isopropyl alcohol and 11.137 g of (1-vinyl pyrrolidone) -acrylic acid copolymer (MW 96,000) in a mixed weight ratio of 592 g of water.

2. 1시간 동안 N2 가스로 불순물을 제거하고 용기를 완전히 밀폐시켰다.2. The impurities were removed with N 2 gas for 1 hour and the vessel was completely sealed.

3. 30KGy 선폭량이 되도록 감마선 처리하여 노란색의 나노 입자 콜로이드 용액을 수득하였다. 3. Gamma-ray treatment to a line width of 30KGy yielded a yellow nanoparticle colloidal solution.

<실시예 1>&Lt; Example 1 >

1. 상기 은나노 콜로이드 용액 2g, UV경화성수지 98g을 1시간 동안 균일하게 혼합하여, 항균성을 부여하는 수지 조성물을 수득하였다.1. The silver nano colloidal solution 2g, UV curable resin 98g was uniformly mixed for 1 hour to obtain a resin composition to impart antimicrobial properties.

2. 100 ㎛ PET 필름의 상부에 상기 수지 조성물을 도포한 후 자외선 광량을 400mJ/㎠로 하여 온도 75℃하에서 2분 동안 건조하여 항균 필름을 제조하였다. 2. After applying the resin composition on top of the 100 ㎛ PET film and the amount of ultraviolet light 400mJ / ㎠ and dried for 2 minutes at a temperature of 75 ℃ to prepare an antimicrobial film.

<실시예 2><Example 2>

실시예 1과 동일한 조건에서 수지 조성물을 제조하되, 실시예 1의 은나노 콜로이드 용액 2g과 UV경화성수지 98g 대신 은나노 콜로이드 용액 6g과 UV경화성수지 94g을 사용하였다.A resin composition was prepared under the same conditions as in Example 1, but 6 g of silver nano colloidal solution and 94 g of UV curable resin were used instead of 2 g of silver nano colloidal solution and 98 g of UV curable resin of Example 1.

<실험예>Experimental Example

* 항균성 효과 시험 및 결과* Antimicrobial effect test and result

대장균(Escherichia coli ATCC 8739), 포도상구균(Staphylococcus aureus ATCC 6538P)을 대상으로 필름밀착법(JIZ Z 2801)을 사용하여 항균 필름의 항균력을 측정하였다.The antimicrobial activity of the antimicrobial film was measured using the film adhesion method (JIZ Z 2801) for Escherichia coli ATCC 8739 and Staphylococcus aureus ATCC 6538P.

이때, 표준피복필름은 Stomacher 400 poly-bag을 사용하였고, 시험균액을 35±1℃, RH 90% 에서 24시간 정치 배양후 균수를 측정하였고, 그 결과는 표 1로 나타내었다.In this case, Stomacher 400 poly-bag was used as the standard coating film, and the test cells were measured at 35 ± 1 ° C. and RH 90% for 24 hours after incubation, and the results are shown in Table 1 below.

[표 1] TABLE 1

Figure 112009049499277-PAT00001
Figure 112009049499277-PAT00001

*항균율(%) = (24시간 후 BLANK균수 - 24 시간 후 시료균수)÷ 24 시간 후 BLANK균수   * Antibacterial rate (%) = (BLANK bacteria after 24 hours-Sample bacteria after 24 hours) ÷ BLANK bacteria after 24 hours

상기 표 1에서 확인할 수 있는 바와 같이, 본 발명의 항균 필름은 포도상구균과 대장균에 대해 99.9% 이상의 항균율을 가지고 있는 것으로 나타났다. As can be seen in Table 1, the antimicrobial film of the present invention was found to have an antibacterial rate of 99.9% or more against staphylococci and E. coli.

이와 같이, 본 발명에 따른 항균 필름은 터치패널, 자동판매기의 버튼이나 쇼핑카트의 손잡이에 사용되면, 불특정 다수의 손 접촉에 의해 전달된 세균을 99.9% 이상 살균하는 효과를 얻을 수 있었다. As such, when the antimicrobial film according to the present invention is used for a touch panel, a button of a vending machine or a handle of a shopping cart, it was possible to obtain an effect of sterilizing at least 99.9% of bacteria transmitted by an unspecified hand contact.

상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술분야의 숙련된 당업자는 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.While the above has been described with reference to a preferred embodiment of the present invention, those skilled in the art will be able to variously modify and change the present invention without departing from the spirit and scope of the invention as set forth in the claims below. It will be appreciated.

Claims (6)

은나노 입자 콜로이드 용액 0.01 내지 10중량%; 및0.01 to 10 wt% silver nanoparticle colloidal solution; And 경화성수지 90 내지 99.99 중량%를 포함하는 나노 크기의 은 입자를 함유한 수지 조성물. A resin composition containing nano-sized silver particles comprising 90 to 99.99% by weight of the curable resin. 제 1 항에 있어서, 상기 은나노 입자 콜로이드 용액이 The method of claim 1, wherein the silver nanoparticle colloidal solution is 분산질로서 은나노 입자; 및 Silver nano particles as a dispersoid; And 분산매로서 유기용제계, 수계, 또는 유기용제계와 수계의 혼합물을 포함하는 것을 특징으로 하는 나노크기의 은 입자를 함유하는 수지 조성물.A resin composition containing nano-sized silver particles, comprising an organic solvent, an aqueous solvent, or a mixture of an organic solvent and an aqueous solvent as a dispersion medium. 제 1 항에 있어서, 상기 경화성수지가 열경화성수지, UV경화성수지, 열 및 UV 동시경화성 수지, 습기경화성 수지 또는 이들의 혼합물인 것을 특징으로 하는 나노 크기의 은 입자를 함유한 수지 조성물. 2. The resin composition according to claim 1, wherein the curable resin is a thermosetting resin, a UV curable resin, a heat and UV cocurable resin, a moisture curable resin, or a mixture thereof. 제 1 항에 따른 수지 조성물이 고분자 필름 제조를 위한 고분자 원료물질과 균일하게 혼합되어 제조된 항균 필름. An antimicrobial film prepared by mixing the resin composition according to claim 1 with a polymer raw material for preparing a polymer film. 제 1 항에 따른 수지 조성물이 고분자 필름 상에 0.01 내지 100 ㎛의 두께로 도포된 항균 필름.The antimicrobial film of Claim 1 in which the resin composition of Claim 1 was apply | coated in the thickness of 0.01-100 micrometers on a polymer film. 제 4 항 또는 제 5 항에 있어서, 상기 고분자 필름은The method of claim 4 or 5, wherein the polymer film 폴리프로필렌, 폴리에틸렌, 폴리에틸렌테레프탈레이트, 폴리우레탄, 폴리스티렌, 폴리염화비닐, 에틸렌비닐아세테이트, ABS, 폴리카보네이트, 나일론 소재의 필름 또는 이들을 2 이상 혼합하여 제조한 필름인 것을 특징으로 하는 항균 필름.An antimicrobial film comprising a film made of polypropylene, polyethylene, polyethylene terephthalate, polyurethane, polystyrene, polyvinyl chloride, ethylene vinyl acetate, ABS, polycarbonate, nylon, or a mixture of two or more thereof.
KR1020090074737A 2009-08-13 2009-08-13 Resin compositions containing silver particles of nano size and antibacterial film using the same KR101160190B1 (en)