KR20100053293A - Ceramic flowerpot radiating far-infrared rays and manufacturing method thereof - Google Patents

Ceramic flowerpot radiating far-infrared rays and manufacturing method thereof Download PDF

Info

Publication number
KR20100053293A
KR20100053293A KR1020080112340A KR20080112340A KR20100053293A KR 20100053293 A KR20100053293 A KR 20100053293A KR 1020080112340 A KR1020080112340 A KR 1020080112340A KR 20080112340 A KR20080112340 A KR 20080112340A KR 20100053293 A KR20100053293 A KR 20100053293A
Authority
KR
South Korea
Prior art keywords
weight
parts
sorting
far
clay
Prior art date
Application number
KR1020080112340A
Other languages
Korean (ko)
Other versions
KR101076467B1 (en
Inventor
양갑수
최용수
조송미
Original Assignee
전남과학대학 산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 전남과학대학 산학협력단 filed Critical 전남과학대학 산학협력단
Priority to KR1020080112340A priority Critical patent/KR101076467B1/en
Publication of KR20100053293A publication Critical patent/KR20100053293A/en
Application granted granted Critical
Publication of KR101076467B1 publication Critical patent/KR101076467B1/en

Abstract

PURPOSE: A far-infrared ray radiating ceramic flowerpot and a method for manufacturing the same are provided to use for human body or plants and to purify indoor air. CONSTITUTION: A far-infrared ray radiating ceramic flowerpot is formed by mixing 13-25 weight parts of pegmatite, 15-25 weight parts of bentonite based on 100.0 weight parts clay to make a base composition; a step of mixing the base composition with water; a step of molding and plasticizing. The base composition further contains 3-9 weight parts of volcanic rock and 3-9 weight parts of charcoal powder.

Description

원적외선 방사 세라믹 화분 및 그 제조방법{Ceramic flowerpot radiating far-infrared rays and manufacturing method thereof}Far-infrared radiation flower pot and its manufacturing method {Ceramic flowerpot radiating far-infrared rays and manufacturing method

본 발명은 세라믹 화분 및 그 제조방법에 관한 것으로서, 더욱 상세하게는 원적외선이 방사되어 인체에 유용한 원적외선 방사 세라믹 화분 및 그 제조방법에 관한 것이다.The present invention relates to a ceramic flowerpot and a method for manufacturing the same, and more particularly, to a far-infrared radiation ceramic flowerpot useful for the human body by radiating far infrared rays and a method for manufacturing the same.

생활 수준이 향상되면서 아파트 거실이나 베란다 혹은 빌딩 로비 등의 실내에 실내 조경을 위해 화분이나 화단을 꾸미는 일이 많아지고 있다. As the standard of living improves, there are more and more plants and flower beds for indoor landscaping in the apartment living room, veranda or building lobby.

실내조경에 이용되는 화분에는 관상용 초본이나 꽃, 키 작은 관목, 분재 등이 식재된다. 이와같이 주거공간이나 사무공간 안으로 도입된 식물을 바라보고 있으면 심리적으로 안정되는 기분을 느낄 수 있다. 또한, 화분에 채워진 토양은 주위 습도가 높은 경우 습기를 빨아들이면서 습도가 낮은 경우에는 습기를 분출하는 가습기의 역할을 하고, 토양에 식재된 식물은 광합성 등의 작용을 통해 실내공기를 정화하는 공기청정기의 역할을 함으로 우리의 생활환경을 쾌적하게 만들면서 우리에게 여러 가지 유익을 주는 장점이 있다.Potted plants used for indoor landscaping include ornamental herbs, flowers, short shrubs, and bonsai. Looking at the plants introduced into the residential or office spaces in this way can feel psychologically stable. In addition, the soil filled in the pot acts as a humidifier that absorbs moisture when the ambient humidity is high and emits moisture when the humidity is low, and the plants planted in the soil purify indoor air through photosynthesis and the like. By acting as a purifier, it has many advantages for us while making our living environment comfortable.

일반적으로 화분의 소재로는 주로 합성수지나 세라믹이 이용된다. 이 중 합 성수지로 이루어진 화분은 가격이 저렴하고 가볍다는 장점이 있는 반면 친환경적이지 못하고 유해물질이 배출될 수 있다는 문제점이 있다. Generally, synthetic resin or ceramic is used as the material of flower pots. Among these, the flower pots made of synthetic resins have the advantage of being inexpensive and light, while not being environmentally friendly and may have harmful substances.

세라믹 소재의 화분은 점토를 반죽하여 성형 소결되는 소결체이며, 외표면이 유약으로 처리된다. 이러한 세라믹 화분은 친환경적인 소재를 이용하기 때문에 식물과 잘 조화된다는 장점이 있다.Pots made of ceramic material are sintered bodies that are molded and sintered by kneading clay, and the outer surface is treated with glaze. These ceramic pots have the advantage of being well harmonized with plants because they use environmentally friendly materials.

하지만 기존의 세라믹 화분은 단순히 점토만을 이용함으로써 그 기능이 극히 제한적이다는 문제점이 있다.However, the conventional ceramic flowerpot has a problem that its function is extremely limited by using only clay.

본 발명은 상술한 문제점을 개선하고자 창출된 것으로서, 점토 외에 원적외선을 다량 방사하는 세라믹을 함께 이용함으로써 가벼우면서도 실내의 공기를 정화시키고 인체 또는 식재된 식물에 유용한 세라믹 화분 및 그 제조방법을 제공하는 데 그 목적이 있다.The present invention has been made to improve the above-described problems, by using a ceramic that emits a large amount of far-infrared radiation in addition to clay, to provide a ceramic pot and a method of manufacturing a ceramic pot that is light and useful for human body or planted plants, The purpose is.

상기의 목적을 달성하기 위한 본 발명의 원적외선 방사 세라믹 화분은 점토 100중량부에 대하여 페그마타이트 13 내지 25중량부와, 벤토나이트 15 내지 25중량부를 포함하는 소지조성물을 물과 혼합한 후 성형 및 소성하여 형성된 것을 특징으로 한다.Far-infrared radiation ceramic flowerpot of the present invention for achieving the above object is formed by mixing and forming a plastic composition containing 13 to 25 parts by weight pegmatite and 15 to 25 parts by weight bentonite with water based on 100 parts by weight of clay It is characterized by.

상기 소지조성물은 상기 점토 100중량부를 기준으로 화산석 3 내지 9중량부또는 숯 가루 3 내지 9중량부를 더 포함하는 것을 특징으로 한다.The holding composition is characterized in that it further comprises 3 to 9 parts by weight of volcanic stone or 3 to 9 parts by weight of charcoal powder based on 100 parts by weight of clay.

그리고 상기의 목적을 달성하기 위한 본 발명의 원적외선 방사 세라믹 화분의 제조방법은 점토, 페그마타이트, 벤토나이트, 화산석을 포함하는 원료를 분쇄하는 분쇄단계와; 상기 분쇄단계에서 분쇄된 점토 100중량부에 대하여 페그마타이트 13 내지 25중량부와, 벤토나이트 15 내지 25중량부와, 화산석 3 내지 9중량부를 혼합하여 소지조성물을 준비하는 소지조성단계와; 상기 소지조성물을 물과 혼합하여 반죽하는 혼련단계와; 상기 혼련단계에서 반죽된 반죽물을 일정 모양을 가지는 성형물로 성형하는 성형단계와; 상기 성형물을 건조 후 소성시키는 소성단계;를 포함 하는 것을 특징으로 한다.And a method for producing a far-infrared radiation ceramic pot of the present invention for achieving the above object is a pulverizing step of grinding a raw material including clay, pegmatite, bentonite, volcanic stone; 13 to 25 parts by weight of pegmatite, 15 to 25 parts by weight of bentonite, and 3 to 9 parts by weight of volcanic stone based on 100 parts by weight of the clay pulverized in the grinding step to prepare a body composition; A kneading step of kneading the base material composition with water; A molding step of molding the dough kneaded in the kneading step into a molding having a predetermined shape; It characterized in that it comprises a; firing step of firing the molding after drying.

상기 분쇄단계는 상기 원료를 1차로 분쇄한 후 선별기에서 선별된 원료를 2차로 분쇄하여 미분화시키며, 상기 선별기는 프레임과, 상기 프레임의 내부에 회전가능하도록 설치되며 상호 이격되어 나란하게 배치되는 한쌍의 선별롤러와, 상기 선별롤러와 이격되어 나란하게 설치되며 상기 선별롤러 사이를 통과하지 못한 원료를 상기 선별롤러의 가장자리로 이송시키는 스크루바와, 상기 선별롤러의 가장자리의 하방에 위치하여 상기 스크루바에 의해 이송된 원료가 배출되는 슈트와, 상기 선별롤러를 회전시키기 위한 제 1구동부와, 상기 스크루바를 회전시키기 위한 제 2구동부를 구비하고, 상기 제 1구동부는 상기 프레임의 외측에 설치되며 상기 한 쌍의 선별롤러의 축에 각각 결합되어 상호 치합하는 한쌍의 종동 기어와, 상기 프레임의 외측면에 설치된 제 1전동모터와, 상기 제 1전동모터의 구동축과 축결합되며 상기 한 쌍의 종동기어 중 어느 하나의 종동기어와 치합하는 구동기어를 구비하며,상기 제 2구동부는 상기 프레임의 외측면에 설치된 제 2전동모터와, 상기 스크루바의 축에 결합되는 종동풀리와, 상기 제 2전동모터의 구동축에 축결합되며 상기 종동풀리와 벨트로 연결되는 구동풀리를 구비하는 것을 특징으로 한다.The pulverizing step is to pulverize the raw material first and then finely pulverize the raw material selected in the sorting machine, the sorting machine is a frame and a pair of rotatably spaced and arranged side by side are installed rotatably inside the frame. A sorting roller and a screw bar which are installed side by side separated from the sorting roller and which do not pass between the sorting rollers are transferred to the edges of the sorting rollers, and are positioned below the edges of the sorting rollers and are conveyed by the screw bars. A chute for discharging the raw material, a first driving unit for rotating the sorting roller, and a second driving unit for rotating the screwbar, wherein the first driving unit is installed outside the frame and the pair of sorting A pair of driven gears coupled to the shafts of the rollers and engaged with each other, and installed on an outer surface of the frame And a drive gear axially coupled to the drive shaft of the first drive motor and engaged with any of the driven gears of the pair of driven gears, wherein the second drive part is provided on an outer surface of the frame. And a second pull motor installed, a driven pulley coupled to the shaft of the screw bar, and a drive pulley axially coupled to the drive shaft of the second electric motor and connected to the driven pulley and the belt.

상술한 바와 같이 본 발명의 원적외선 방사 세라믹 화분 및 그 제조방법에 의하면 기존의 단순한 기능적 작용과 관상용 효과에 더하여, 실내 주거공간의 공기나 습도를 조절할 수 있고, 화분으로부터 다량의 원적외선이 연속적으로 방사됨으로써, 실내의 항균, 탈취, 정화 기능은 물론, 인체의 혈액순환 개선, 세포조직의 활성, 노화방지, 신진대사 촉진 등 원적외선 고유의 각종 유익한 기능을 통해 쾌적한 실내 주거환경을 만들 수 있는 효과가 있다.As described above, according to the far-infrared radiation ceramic pot of the present invention and its manufacturing method, in addition to the existing simple functional action and ornamental effect, it is possible to control the air or humidity of the indoor living space, and by continuously radiating a large amount of far-infrared rays from the pot In addition, antibacterial, deodorant, cleansing function of the room, as well as improving the blood circulation of the human body, activation of cellular tissues, anti-aging, promoting metabolism has the effect of creating a comfortable indoor living environment through various beneficial functions unique to far infrared rays.

또한, 화분에 식재된 식물들은 원적외선이 생체에 흡수되어 물분자의 활성화 등의 작용을 통해 생체의 기능을 촉진하여 배양 및 생육에 도움을 줄 수 있다.In addition, plants planted in pots can be aided in cultivation and growth by promoting the function of the living body through the action of the far infrared rays are absorbed by the living body, such as activation of water molecules.

이하, 첨부된 도면을 참조하면서 본 발명의 바람직한 실시 예에 따른 원적외선 방사 세라믹 화분에 대해서 구체적으로 설명한다.Hereinafter, a far-infrared radiation ceramic pot according to a preferred embodiment of the present invention with reference to the accompanying drawings will be described in detail.

도 1은 본 발명의 일 실시 예에 따른 세라믹 화분의 제조방법을 나타내는 블록도이고, 도 2는 도 1의 세라믹 화분의 제조방법에 사용되는 분별기의 내부를 나타내는 평면도이다.1 is a block diagram illustrating a method of manufacturing a ceramic pot according to an embodiment of the present invention, Figure 2 is a plan view showing the inside of the separator used in the method of manufacturing a ceramic pot of Figure 1;

도 1 및 도 2를 참조하면, 본 발명의 세라믹 화분은 점토, 페그마타이트, 벤토라이트를 포함하는 원료을 혼합하여 만들어진 소지조성물을 물과 반죽한 후 성형 및 소성하여 형성된다. 1 and 2, the ceramic flowerpot of the present invention is formed by kneading a base material composition made by mixing a raw material including clay, pegmatite, bentorite with water and then molding and firing.

점토(粘土, clay)는 암석 부스러기 또는 광물 알갱이로 이루어진 것으로서, 암석이 풍화, 분해되면서 주로 규소, 알루미늄과 물이 결합하여 점토 광물이 이루어진다. 일반적으로 점토로 백자토, 청자토, 분청토, 옹기토 등 다양한 종류를 이용할 수 있는 데, 본 발명에서는 백토와 청자토를 적당히 혼합하여 이용한다. 일 예로 백토와 청자토를 중량비로 약 10:1로 혼합하여 이용한다. Clay is composed of rock debris or mineral grains. As the rocks are weathered and decomposed, they are mainly composed of silicon, aluminum and water to form clay minerals. In general, various types of clay, such as white clay, blue clay, powdered blue clay, or clay, may be used. In the present invention, a mixture of white clay and blue clay is appropriately used. For example, a mixture of white clay and blue clay is used in a weight ratio of about 10: 1.

페그마타이트(pegmatite)는 석영, 장석, 운모 따위의 거친 입자의 결정으로 이루어진 화성암으로서, 마그마가 화강암으로 엉겨 굳은 다음, 남은 일부가 화강암 보다 낮은 온도에서 엉겨 굳어서 이루어진 것으로 거정 화강암으로 불리우기도 한다.Pegmatite is a igneous rock composed of coarse grains of quartz, feldspar, mica, etc. Maggite is entangled with granite, and the remainder is entangled at a lower temperature than granite.

페그마타이트(Pegamtite)는 마그마의 분화광상(分化鑛床) 생성물로서, 유색방사능 광물질이며 약리작용을 할 수 있는 광석으로 널리 알려져 있다. 또한 상기 페그마타이트는 단일 20종의 성분을 함유한 광물질로서 단독 방사체의 소재로도 충분히 사용될 수 있으며, 특히 원적외선 응용으로 작용하는 방사파장의 빛이 인체 깊숙이 침투하여 산화되기 쉬운 혈액을 알칼로이드화시키는 일반광물질 성분인 칼슘, 칼륨, 마그네슘 및 철등과 특수광물질 성분인 나트륨, 세륨, 셀레늄, 란타늄, 게르마늄 및 홀뮴 등의 알칼리성 이온을 띄는 성분들이 존재하기 때문에 이들 성분이 원적외선과의 작용으로 체내의 세포활성, 혈액순환촉진, 신진대사강화, 조직재생의 능력증가로 피로와 노화현상을 억제하는 효능을 나타내는 광물로 알려졌다.Pegmtite is a product of the differentiation of magma, and is widely known as a colored radioactive mineral and a pharmacological ore. In addition, the pegmatite is a mineral containing a single 20 kinds of components, and can be used as a material of a single radiator. In particular, the pegmatite is a general mineral component that alkaloids blood that is easily oxidized by penetrating deep into the human body. Since alkaline ions such as phosphorus calcium, potassium, magnesium and iron and special minerals such as sodium, cerium, selenium, lanthanum, germanium and holmium are present, these components interact with the far-infrared rays to activate the body's cellular activity and blood circulation. It is known to be a mineral that has been shown to be effective in suppressing fatigue and aging due to its ability to promote, enhance metabolism and increase tissue regeneration.

이러한 페그마타이트는 다량의 원적외선을 방사하기 때문에 혈액순환 및 신진대사 촉진 등 인체에 유익한 효과를 가진다. 원적외선은 인체에 방사되면 피부 속 4~5cm까지 심층으로 스며들고 세포를 60초에 2000번 이상 미세하게 흔들어 주는 진동을 통하여 세포조직을 활발하게 한다. 이러한 세포작용으로 열에너지를 분출하면서 얻어지는 효과로 노폐물 및 독성물질이 배출되며, 혈전을 분해하여 혈액순환을 촉진하면서 혈액정화작용을 한다.Since pegmatite emits a large amount of far infrared rays, it has a beneficial effect on the human body, such as promoting blood circulation and metabolism. Far infrared rays penetrate deep into the skin to 4 ~ 5cm when radiated to the human body, and activate the tissue through vibrations that vibrate the cells more than 2000 times in 60 seconds. Wastewater and toxic substances are discharged by the effect obtained by releasing thermal energy through such cellular action, and blood purification is performed by decomposing thrombi and promoting blood circulation.

본 발명에 이용되는 페그마타이트는 SiO2 65중량%이상 함유된 것을 이용한다. 이외에 미량 성분으로서 Ge 0.014중량%, He 0.00053중량%, Se 0.02중량%, Ce0.02중량%, Na2O 3.59중량%, CaO 2.98중량%, MgO 1.91중량%, K2O 3.52중량%를 함유한다.Pegmatite used in the present invention is used containing 65% by weight or more of SiO 2 . In addition, it contains 0.014% by weight of Ge, 0.00053% by weight of He, 0.02% by weight of Se, 0.02% by weight of Ce, 2.59% by weight of Na 2 O, 2.98% by weight of CaO, 1.91% by weight of MgO, and 3.52% by weight of K 2 O. do.

페그마타이트는 점토 100중량부에 대하여 13 내지 25중량부를 혼합한다. 페그마타이트가 25중량부를 초과하면 화분의 물성을 저하시키고, 13중량부 미만이면 그 효과가 저하된다.Pegmatite is mixed with 13 to 25 parts by weight based on 100 parts by weight of clay. When pegmatite exceeds 25 parts by weight, the physical properties of the pollen are lowered, and when it is less than 13 parts by weight, the effect is lowered.

벤토나이트(bentonite)는 몬모릴로나이트 계통의 점토광물로서 수분을 가하면 점력이 발현되고 건조, 소성시 굳게 소결되는 특성이 있다. 화산회(火山灰)의 유리성분이 분해해서 생성된 매우 점력이 강한 소재이다. 특히 우수한 양이온 교환성을 갖고 있으며 일반적으로 석영, 제올라이트, 장석 등의 성분을 포함하고 있다. Bentonite is a montmorillonite-based clay mineral, and when moisture is added, viscous force is expressed, and it is hardly sintered during drying and firing. It is a very viscous material produced by the decomposition of the glass component of volcanic ash. In particular, it has excellent cation exchange properties and generally contains components such as quartz, zeolite and feldspar.

본 발명에서 벤토나이트는 성형시 배합된 원료들의 점력을 증가시켜 성형체의 형태를 유지시키며 CaO, MgO, Na2O, K2O 등의 알칼리(토류) 성분을 함유하고 있어 소성시 소결을 촉진시켜 압축강도 및 휨강도를 증가시키는 역할을 한다.Bentonite in the present invention increases the viscosity of the raw materials blended during molding to maintain the shape of the molded body and contains alkali (earth) components, such as CaO, MgO, Na 2 O, K 2 O to promote sintering during firing It serves to increase strength and flexural strength.

본 발명에서 이용되는 벤토나이트의 성분은 SiO2 62.4중량%, Al2O3 15.7중량%, Fe2O3 4.58중량%, CaO 3.14중량%, MgO 3.11중량%, K2O 0.88중량%, Na2O 2.76중량%이다.Bentonite component used in the present invention is 62.4% by weight of SiO 2 , 15.7% by weight of Al 2 O 3 , 4.58% by weight of Fe 2 O 3 , CaO 3.14% by weight, MgO 3.11% by weight, K 2 O 0.88% by weight, Na 2 0, 2.76 weight%.

상기 벤토나이트는 점토 100중량부에 대하여 15 내지 25중량부를 혼합한다. 벤토나이트의 함량이 15중량부 미만일 경우에는 점토 고유의 특성인 점력을 발휘하기 어렵고, 25중량부를 초과 할 경우에는 점력은 증가하지만 성형시 제품의 경도가 낮아지고 수분증가로 인한 휨현상이 발생될 수 있다. The bentonite is mixed with 15 to 25 parts by weight based on 100 parts by weight of clay. If the content of bentonite is less than 15 parts by weight, it is difficult to exhibit the clay's inherent properties, and if it exceeds 25 parts by weight, the viscosity increases, but the hardness of the product during molding may decrease and warpage may occur due to an increase in moisture. .

본 발명에서 소지조성물의 다른 예로 점토 100중량부를 기준으로 숯 가루 3 내지 9중량부가 더 포함될 수 있다. 숯은 알려진 바와 같이 항균, 탈취효과가 우수하여 본 발명에서 실내 공기 정화 효과를 더욱 증대시킬 수 있다. 본 발명에서 숯은 대나무 숯이나 삼나무 숯을 이용할 수 있다.Another example of the body composition in the present invention may further include 3 to 9 parts by weight of charcoal powder based on 100 parts by weight of clay. Charcoal is known as excellent antibacterial, deodorizing effect can further increase the indoor air purification effect in the present invention. In the present invention, charcoal may use bamboo charcoal or cedar charcoal.

또한, 본 발명에서 소지조성물의 또 다른 예로 점토 100중량부를 기준으로 화산석 3 내지 9중량부가 더 포함될 수 있다.Further, in the present invention, another example of the base material composition may further include 3 to 9 parts by weight of volcanic stone based on 100 parts by weight of clay.

화산석은 마그마의 냉각 ·고결이 빨리 진행되어 형성된 것으로서, 화산분출물 중 비교적 다공질이 많은 현무암의 암괴이다. 화산석의 대부분은 광물입자가 매우 작은 결정질(結晶質) 또는 유리질이며, 화산암석에 포유되어 있는 큰 결정을 반정(斑晶)이라 하고 이와 같은 조직을 반상조직(斑狀組織)이라 한다. 화산석은 그것을 만드는 마그마의 성질 ·화학성분 ·광물조성 등이 다양하므로 다종 다양하게 산출된다. 이 때 각 군의 화산암류 중 가장 많은 양을 차지하는 것은 현무암으로 화산석 전체의 90% 이상을 차지한다. Volcanic stones are formed by the rapid cooling and solidification of magma, and are a relatively porous basaltic mass among volcanic eruptions. Most of the volcanic rocks are very small crystalline or glassy mineral particles, and the large crystals in the volcanic rocks are called semi-crystals. Volcanic stones are produced in a variety of ways because they vary in the nature, chemical composition, and mineral composition of the magma. At this time, the largest amount of volcanic rocks in each group is basalt, accounting for more than 90% of all volcanic rocks.

본 발명에서 화산석은 SiO2, Al2O3, Fe2O3, CaO, MgO, K2O, Na2O 및 MnO2 의 성분을 포함하는 현무암인 것이 바람직하다. 화산석은 내화도가 매우 낮고, Na2O, K2O 성분 등이 융제역할을 하여 소결을 촉진시켜 소결강도 및 압축강도를 크게 향상시키고 흡수율을 저하시킬 뿐 아니라, 성분중의 철(Fe)과 망간(MnO2) 등이 발색을 하여 흑색의 반점을 형성시키는 역할을 한다.In the present invention, the volcanic stone is preferably basalt including components of SiO 2 , Al 2 O 3 , Fe 2 O 3 , CaO, MgO, K 2 O, Na 2 O, and MnO 2 . Volcanic stone has very low fire resistance, and Na 2 O, K 2 O components act as a flux to promote sintering, which greatly improves the sintering strength and compressive strength and lowers the absorption rate, as well as iron (Fe) and manganese in the components. (MnO 2 ) and the like develop color and play a role of forming black spots.

화산석의 함량이 3중량부 미만일 경우에는 화산석 첨가에 상기 효과가 미약 하고, 9중량부를 초과할 경우에는 소결이 너무 이루어져 화분의 표면이 과용융되거나 색상이 너무 검을 수 있기 때문에 점토 100 중량부에 대하여 3 내지 9중량부가 바람직하다.When the content of volcanic stone is less than 3 parts by weight, the above effect is weak for volcanic stone addition. When the content of the volcanic stone exceeds 9 parts by weight, the surface of the flower pot may be over-melted or the color may be too dark. 3-9 weight part is preferable.

한편, 상술한 원료들에 원적외선을 방사하는 게르마늄, 모나자이트, 히게리온, 맥반석, 황토 등을 더 추가할 수 있다. 또한, 음이온을 방사하는 토르말린, 귀양석, 황토, 맥섬석, 게르마늄 등을 더 첨가하여 이용할 수 있다. 원적외선 방사 세라믹과 음이온 방사 세라믹은 단독 또는 혼합하여 사용할 수 있다.Meanwhile, germanium, monazite, higerion, elvan, loess, etc., emitting far infrared rays may be further added to the above-described raw materials. In addition, tourmaline that emits negative ions, ear lapis lazuli, loess, macsumite, germanium and the like may be further added and used. Far-infrared radiation ceramics and anion radiation ceramics may be used alone or in combination.

상기와 같이 이루어진 소지조성물은 물과 혼합하여 반죽한 다음 일정한 모양으로 성형한 뒤 건조, 소성시켜 만들어진다. 이렇게 제조된 본 발명의 세라믹 화분은 기존의 단순한 기능적 작용과 관상용 효과에 더하여, 실내 주거공간의 공기나 습도를 조절할 수 있고, 화분으로부터 다량의 원적외선이 연속적으로 방사됨으로써, 실내의 항균, 탈취, 정화 기능은 물론, 인체의 혈액순환 개선, 세포조직의 활성, 노화방지, 신진대사 촉진 등 원적외선 고유의 각종 유익한 기능을 통해 쾌적한 실내 주거환경을 만들 수 있는 효과가 있다.The base composition made as described above is made by mixing with water, kneading and then molding to a certain shape and then drying and baking. The ceramic flower pot of the present invention manufactured as described above can control the air or humidity of the indoor living space in addition to the existing simple functional action and ornamental effect, and by emitting a large amount of far-infrared rays continuously from the flower pot, antibacterial, deodorizing, purifying the room Not only functions, but also improve the blood circulation of the human body, the activation of cellular tissues, anti-aging, promoting metabolism, etc. There is an effect that can create a comfortable indoor living environment through various beneficial functions inherent in far infrared.

또한, 화분에 식재된 식물들은 원적외선이 생체에 흡수되어 물분자의 활성화 등의 작용을 통해 생체의 기능을 촉진하여 배양 및 생육에 도움을 줄 수 있다.In addition, plants planted in pots can be aided in cultivation and growth by promoting the function of the living body through the action of the far infrared rays are absorbed by the living body, such as activation of water molecules.

이하, 본 발명의 일 실시 예에 따른 원적외선 방사 세라믹 화분의 제조방법에 대해서 상세하게 설명한다.Hereinafter, a method of manufacturing a far-infrared radiation ceramic pot according to an embodiment of the present invention will be described in detail.

준비된 원료를 미분화시키기 위해 분쇄단계를 수행한다. 분쇄단계는 괴상의 점토, 페그마타이트, 벤토나이트를 1차로 분쇄한 후 선별기(20)에서 선별공정을 거 친 다음, 선별된 원료를 2차로 분쇄하여 미분화시킨다.A grinding step is performed to micronize the prepared raw materials. In the crushing step, the clay, pegmatite and bentonite are pulverized first and then subjected to the sorting process in the sorting machine 20, and then the selected raw materials are crushed secondly to be micronized.

준비된 큰 덩어리 형태의 원료를 통상적인 롤 분쇄기에서 1차적으로 중분쇄 또는 조분쇄시킨다. 이는 원료를 1차적으로 분쇄하여 2차 분쇄시 미분화를 용이하게 하기 위함이다. 1차로 분쇄된 원료는 컨베어 벨트를 통해 선별기(20)로 투입되며, 선별기(20)에서 입자가 큰 원료와 잘게 분쇄된 원료를 효과적으로 선별한다. The prepared large chunks of raw material are primarily pulverized or coarsely pulverized in a conventional roll mill. This is to facilitate the micronization during the second milling by grinding the raw material first. The primary pulverized raw material is introduced into the sorter 20 through a conveyor belt, and the sorter 20 effectively sorts large raw materials and finely pulverized raw materials.

도 2에 도시된 바와 같이 선별기(20)는 크게 프레임(21)과, 프레임(21)의 내부에 회전가능하도록 설치되며 상호 일정 거리 이격되어 나란하게 배치되는 한쌍의 선별롤러(23)와, 한쌍의 선별롤러(23)가 상호 이격되어 형성된 이격공간의 상방에 선별롤러와 나란하게 설치되며 선별롤러(23) 사이를 통과하지 못한 부피가 큰 원료를 선별롤러(23)의 가장자리로 이송시키는 스크루바(31)와, 선별롤러(23)의 가장자리의 하방에 위치하여 스크루바(31)에 의해 이송된 부피가 큰 원료들이 외부로 배출되는 슈트(35)와, 선별롤러(23)를 회전시키기 위한 제 1구동부와, 스크루바(31)를 회전시키기 위한 제 2구동부로 구비된다. 제 1구동부는 제 1프레임(21)의 외측에 설치되며 선별롤러(23)의 축에 결합되어 상호 치합하는 한쌍의 종동 기어(25)와, 프레임(21)의 외측면에 설치된 제 1전동모터(27)와, 제 1전동모터(27)의 구동축과 축결합되며 한쌍의 종동기어(25) 중 어느 하나의 종동기어와 치합하는 구동기어(29)로 이루어진다. 그리고 제 2구동부는 프레임(21)의 외측면에 설치된 제 2전동모터(37)와, 스크루바(31)의 축에 결합되는 종동풀리(32)와, 제 2전동모터(37)의 구동축에 축결합된 구동풀리(34)와, 구동풀리(34)와 종동풀리(32)를 연결하는 벨트(33)로 이루어진다. As shown in FIG. 2, the sorter 20 is largely provided with a frame 21 and a pair of sorting rollers 23 installed to be rotatable inside the frame 21 and arranged side by side at a predetermined distance from each other. The sorting rollers 23 are installed in parallel with the sorting rollers above the separation space formed by spaced apart from each other, the screw bar for transferring the bulky raw material that did not pass between the sorting rollers 23 to the edge of the sorting rollers 23. (31) and the chute (35) located below the edge of the sorting roller (23) to which the bulky raw materials conveyed by the screwbar (31) are discharged to the outside, and for rotating the sorting roller (23). It is provided with a 1st drive part and a 2nd drive part for rotating the screw bar 31. As shown in FIG. The first driving unit is installed on the outer side of the first frame 21 and coupled to the shaft of the sorting roller 23 and engaged with each other, and a first electric motor installed on the outer surface of the frame 21. (27) and a drive gear 29 axially coupled to the drive shaft of the first electric motor 27 and engaged with any of the driven gears of the pair of driven gears 25. The second driving unit includes a second electric motor 37 provided on an outer surface of the frame 21, a driven pulley 32 coupled to the shaft of the screwbar 31, and a drive shaft of the second electric motor 37. It consists of a drive pulley 34 coupled to the shaft, and a belt 33 connecting the drive pulley 34 and the driven pulley 32.

상기 선별기(20)에 의해 부피가 큰 원료들은 슈트(35)를 통해 외부로 배출되어 신속하게 분리되고, 양 선별롤러(23)의 상호 이격거리보다 크기가 더 작은 원료들은 선별롤러(23) 사이를 통과함으로써 원료들이 선별된다. 그리고 도시되지 않았지만 선별된 원료들을 선별롤러(23)의 하방에 설치된 컨베어벨트(40)에 의해 2차 분쇄기로 이송될 수 있다. The bulky raw materials are discharged to the outside through the chute 35 to be separated quickly by the sorter 20, and raw materials having a size smaller than the mutual separation distance of the two sorting rollers 23 are separated between the sorting rollers 23. Raw materials are sorted by passing through. Although not shown, the selected raw materials may be transferred to the secondary grinder by the conveyor belt 40 installed below the sorting roller 23.

이러한 선별기(20)에 의해 1차로 분쇄된 원료 중에서 비교적 부피가 작은 원료만이 균일하게 선별된다. 따라서 2차 분쇄시 분쇄작업이 빠르고 효과적으로 이루어질 수 있으며, 2차 분쇄기의 효율을 높일 수 있다. Only raw materials having a relatively small volume among the raw materials ground by the sorting unit 20 are uniformly selected. Therefore, the grinding operation can be made quickly and effectively during the secondary grinding, it is possible to increase the efficiency of the secondary grinder.

2차 분쇄기로는 통상적인 볼밀 분쇄기를 이용한다. 선별된 원료는 볼밀에서 100 내지 200메쉬 입도 크기로 미분화시킨다. 미분화된 점토, 페그마타이트, 벤토나이트는 상기한 비율로 혼합한다. 상기의 원료들의 혼합은 선별기에서 선별된 직후 수행될 수 있음은 물론이다. As a secondary mill, a conventional ball mill grinder is used. Selected raw materials are micronized to a size of 100 to 200 mesh particle size in a ball mill. Undifferentiated clay, pegmatite and bentonite are mixed in the above ratio. Of course, the mixing of the raw materials can be performed immediately after the screening in the sorting machine.

그리고 혼합된 점토, 페그마타이트, 벤토나이트에 화산석 분말이나 숯가루가 더 혼합될 수 있다. 이 경우 화산석 분말은 상술한 방법과 동일한 방법으로 미분화시킨다.And the mixed clay, pegmatite, bentonite may be further mixed with volcanic stone powder or charcoal powder. In this case, the volcanic stone powder is micronized by the same method as described above.

상기와 같이 조성된 소지조성물은 통상적인 혼련기에서 물이 공급되면서 반죽된다. 혼련단계에서는 반죽물의 함수율이 약 55 내지 65%가 되도록 수분조절한다.The base material composition thus prepared is kneaded while water is supplied in a conventional kneader. In the kneading step, the moisture content of the dough is adjusted to about 55 to 65%.

혼련단계에서 반죽된 반죽물은 일정한 모양으로 성형하기 위해 성형단계가 수행된다. 성형은 통상적인 물레성형방식의 수공작업이나 기계작업을 통해 화분의 형상으로 성형한다. The kneaded dough kneaded in the kneading step is performed to form a predetermined shape. Molding is carried out in the shape of a flower pot by manual or mechanical operations of a conventional spinning wheel molding method.

성형된 성형물은 적재대에 쌓고 음지에서 10 내지 14일 정도 건조를 시킨다. 건조 후 성형물은 가마에서 1차로 800 내지 850℃에서 초벌구이하고, 2차로 1200 내지 1220℃에서 재벌구이하여 소성시킨다. 이외에도 초벌 구이 후 통상적인 유약을 바를 수 있다. Molded moldings are stacked on a mounting table and dried in the shade for about 10 to 14 days. After drying, the molded product is first roasted at 800 to 850 ° C. in a kiln and secondly baked at 1200 to 1220 ° C. in a kiln, and then fired. Other glazes can be applied after the initial roasting.

이하, 실시 예를 통하여 본 발명의 제조방법에 대해 설명하고자 한다. 다만, 하기의 실시 예는 본 발명을 구체적으로 설명하기 위한 것으로, 본 발명의 범위를 하기의 실시 예로 한정하는 것은 아니다.Hereinafter, the manufacturing method of the present invention will be described through examples. However, the following examples are only for illustrating the present invention in detail, and the scope of the present invention is not limited to the following examples.

(실시예)(Example)

롤분쇄기에서 1차로 분쇄된 원료를 선별기에서 선별한 후, 백토와 청자토가 중량비로 10:1로 혼합된 점토 100중량부에 대하여 페그마타이트 19중량부와, 벤토나이트 20중량부를 볼밀에서 150메쉬크기로 2차로 분쇄하여 미분화시켜 소지조성물을 준비하였다. 소지조성물은 혼련기에서 물을 첨가하면서 반죽하여 함수량 60%의 반죽물로 만든 다음 화분 형상으로 성형한 후 건조실에서 12일간 건조시켰다. 건조된 성형물은 가마에서 1차로 820℃에서 초벌구이하고, 2차로 1200℃에서 재벌구이하여 세라믹 화분을 제조하였다. 제조된 세라믹 화분의 시편에 대하여 KFIA-FI-1005시험방법에 의해 원적외선 방사율과 방사에너지를 측정하였고, 그 결과를 표1에 나타냈다. 하기 표 1의 값은 37℃에서 FT-IR spectromet를 이용한 black body대비 측정결과이다.After sorting the raw material firstly crushed in a roll crusher, 19 parts by weight of pegmatite and 20 parts by weight of bentonite were used in a 150 millimeter size, based on 100 parts by weight of clay mixed with 10: 1 clay and blue clay in a weight ratio. Secondary milling to finely prepare a body composition. The base composition was kneaded while adding water in a kneader to make a water-containing 60% dough, and then molded into a flowerpot shape and dried in a drying chamber for 12 days. The dried molding was first roasted at 820 ° C. in a kiln and secondly roasted at 1200 ° C. in a kiln to prepare a ceramic pot. The far-infrared emissivity and the radiant energy of the prepared ceramic pots were measured by the KFIA-FI-1005 test method, and the results are shown in Table 1. The values in Table 1 below are the measured results of black body using FT-IR spectromet at 37 ° C.

방사율(5~20㎛)Emissivity (5 ~ 20㎛) 방사에너지(W/㎡·㎛)Radiation energy (W / ㎡ · ㎛) 0.9120.912 3.45×102 3.45 × 10 2

상기 표 1에서 나타난 바와 같이 본 발명의 원적외선 방사 세라믹 화분은 우수한 원적외선 방사 효과를 가짐을 알 수 있다.As shown in Table 1, it can be seen that the far-infrared radiation ceramic pot of the present invention has an excellent far-infrared radiation effect.

이상에서 본 발명은 도면에 도시된 실시 예를 참고로 설명되었으나 이는 예시적인 것에 불과하며, 당해 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 실시 예가 가능하다는 점을 이해할 것이다.Although the present invention has been described with reference to the embodiments illustrated in the drawings, this is merely exemplary, and it will be understood by those skilled in the art that various modifications and equivalent embodiments thereof are possible.

따라서 본 발명의 진정한 보호 범위는 첨부된 청구범위에 의해서만 정해져야 할 것이다.Therefore, the true scope of protection of the present invention should be defined only by the appended claims.

도 1은 본 발명의 일 실시 예에 따른 세라믹 화분의 제조방법을 나타내는 블록도이고,1 is a block diagram showing a method of manufacturing a ceramic pot according to an embodiment of the present invention,

도 2는 도 1의 세라믹 화분의 제조방법에 사용되는 분별기의 내부를 나타내는 평면도이다.FIG. 2 is a plan view showing the inside of a separator used in the method of manufacturing the ceramic pot of FIG. 1.

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

20: 선별기 21: 프레임 20: sorter 21: frame

23: 선별롤러 25: 종동기어23: Sorting roller 25: Follower gear

31: 스크루바 35: 슈트 31: screwbar 35: suit

Claims (4)

점토 100중량부에 대하여 페그마타이트 13 내지 25중량부와, 벤토나이트 15 내지 25중량부를 포함하는 소지조성물을 물과 혼합한 후 성형 및 소성하여 형성된 것을 특징으로 하는 원적외선 방사 세라믹 화분.A far-infrared radiation ceramic flowerpot, characterized in that it is formed by mixing 13-25 parts by weight of pegmatite and 15-25 parts by weight of bentonite with water, followed by molding and baking. 제 1항에 있어서, 상기 소지조성물은 상기 점토 100중량부를 기준으로 화산석 3 내지 9중량부 또는 숯 가루 3 내지 9중량부를 더 포함하는 것을 특징으로 하는 원적외선 방사 세라믹 화분.The far-infrared radiation ceramic flowerpot of claim 1, further comprising 3-9 parts by weight of volcanic stone or 3-9 parts by weight of charcoal powder based on 100 parts by weight of the clay. 점토, 페그마타이트, 벤토나이트, 화산석을 포함하는 원료를 분쇄하는 분쇄단계와;A grinding step of grinding a raw material including clay, pegmatite, bentonite, and volcanic stone; 상기 분쇄단계에서 분쇄된 점토 100중량부에 대하여 페그마타이트 13 내지 25중량부와, 벤토나이트 15 내지 25중량부와, 화산석 3 내지 9중량부를 혼합하여 소지조성물을 준비하는 소지조성단계와;13 to 25 parts by weight of pegmatite, 15 to 25 parts by weight of bentonite, and 3 to 9 parts by weight of volcanic stone based on 100 parts by weight of the clay pulverized in the grinding step to prepare a body composition; 상기 소지조성물을 물과 혼합하여 반죽하는 혼련단계와;A kneading step of kneading the base material composition with water; 상기 혼련단계에서 반죽된 반죽물을 일정 모양을 가지는 성형물로 성형하는 성형단계와;A molding step of molding the dough kneaded in the kneading step into a molding having a predetermined shape; 상기 성형물을 건조 후 소성시키는 소성단계;를 포함하는 것을 특징으로 하는 원적외선 방사 세라믹 화분의 제조방법.The firing step of firing the molded product after drying; Method of producing a far-infrared radiation ceramic flower pot, characterized in that it comprises a. 제 3항에 있어서, 상기 분쇄단계는 상기 원료를 1차로 분쇄한 후 선별기에서 선별된 원료를 2차로 분쇄하여 미분화시키며,The method of claim 3, wherein the pulverizing step is to pulverize the raw material selected in the sorting machine after the second crushing of the raw material to the second and finely, 상기 선별기는 프레임과, 상기 프레임의 내부에 회전가능하도록 설치되며 상호 이격되어 나란하게 배치되는 한쌍의 선별롤러와, 상기 선별롤러와 이격되어 나란하게 설치되며 상기 선별롤러 사이를 통과하지 못한 원료를 상기 선별롤러의 가장자리로 이송시키는 스크루바와, 상기 선별롤러의 가장자리의 하방에 위치하여 상기 스크루바에 의해 이송된 원료가 배출되는 슈트와, 상기 선별롤러를 회전시키기 위한 제 1구동부와, 상기 스크루바를 회전시키기 위한 제 2구동부를 구비하고,The sorting machine is installed so as to be rotatable inside the frame, and a pair of sorting rollers are arranged side by side spaced apart from each other, and the raw material that is installed side by side separated from the sorting rollers and did not pass between the sorting rollers A screw bar for transferring to the edge of the sorting roller, a chute disposed under the edge of the sorting roller to discharge the raw material conveyed by the screw bar, a first driving unit for rotating the sorting roller, and rotating the screw bar It has a second driving unit for 상기 제 1구동부는 상기 프레임의 외측에 설치되며 상기 한 쌍의 선별롤러의 축에 각각 결합되어 상호 치합하는 한쌍의 종동 기어와, 상기 프레임의 외측면에 설치된 제 1전동모터와, 상기 제 1전동모터의 구동축과 축결합되며 상기 한 쌍의 종동기어 중 어느 하나의 종동기어와 치합하는 구동기어를 구비하며,The first driving unit is provided on the outer side of the frame and coupled to the shaft of the pair of the sorting roller, respectively, a pair of driven gear, a first electric motor provided on the outer surface of the frame, and the first electric drive A drive gear axially coupled to the drive shaft of the motor and engaged with any of the driven gears of the pair of driven gears, 상기 제 2구동부는 상기 프레임의 외측면에 설치된 제 2전동모터와, 상기 스크루바의 축에 결합되는 종동풀리와, 상기 제 2전동모터의 구동축에 축결합되며 상기 종동풀리와 벨트로 연결되는 구동풀리를 구비하는 것을 특징으로 하는 원적외선 방사 세라믹 화분의 제조방법.The second driving unit is coupled to the drive shaft of the second electric motor and the driven motor pulley coupled to the shaft of the screw bar, the second electric motor installed on the outer surface of the frame drive driven by the driven pulley and the belt A method for producing a far-infrared radiation ceramic flowerpot, comprising a pulley.
KR1020080112340A 2008-11-12 2008-11-12 Ceramic flowerpot radiating far-infrared rays and manufacturing method thereof KR101076467B1 (en)