KR20090124485A - Aqueous gel ink composition for marker pen and method of preparing the same - Google Patents
Aqueous gel ink composition for marker pen and method of preparing the same Download PDFInfo
- Publication number
- KR20090124485A KR20090124485A KR1020080050732A KR20080050732A KR20090124485A KR 20090124485 A KR20090124485 A KR 20090124485A KR 1020080050732 A KR1020080050732 A KR 1020080050732A KR 20080050732 A KR20080050732 A KR 20080050732A KR 20090124485 A KR20090124485 A KR 20090124485A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- ink composition
- water
- marker pen
- aqueous
- Prior art date
Abstract
Description
본 발명은 마커펜용 수성 겔 잉크 조성물 및 그 제조방법에 관한 것으로서, 보다 상세하게는 접착강도가 우수하여 요철칠판에 사용된 후 별도의 클리너 없이 제거할 수 있는 요철칠판에 사용가능한 마커펜용 수성 겔 잉크 조성물 및 그 제조방법에 관한 것이다.The present invention relates to an aqueous gel ink composition for a marker pen and a method of manufacturing the same, and more particularly, to an aqueous gel ink for a marker pen that can be removed without a separate cleaner after being used on an uneven blackboard due to excellent adhesive strength. A composition and a method for producing the same.
학교의 교실, 세미나실, 회의실 및 사무실 등에 사용되고 있는 흑판은 통상 흑색 또는 녹색의 표면을 가지고 있으며, 근래에는 시력보호 차원에서 녹색의 흑판을 사용하고 있고, 상기 흑판 표면에는 분필을 사용하여 문자 등을 기재하여 왔다.Blackboards, which are used in classrooms, seminar rooms, conference rooms, and offices of schools, usually have a black or green surface, and in recent years, green blackboards are used to protect eyesight. It has been described.
일반적으로, 상기 분필용의 기존 칠판 표면은 미세한 요철이 형성되어 거친 표면을 가지고 있기 때문에, 분필을 거친 칠판 표면에 사용하면 분필과 칠판표면이 마찰되면서 분필가루가 분필의 이동궤적을 따라 칠판에 잔존하게 된다. 이와 같이 분필궤적을 따라 칠판표면에 남아 있는 분필가루에 의하여 원하는 사항을 칠판에 판서하게 된다. In general, since the existing blackboard surface for the chalk has a rough surface formed with fine irregularities, when used on the rough surface of the chalk, the chalk and the surface of the blackboard is rubbed and the chalk powder remains on the blackboard along the trajectory of the chalk. Done. In this way, the desired matter is written on the blackboard by the chalk powder remaining on the surface of the blackboard along the chalk trace.
그러나 상기 요철 있는 칠판에 분필을 이용하여 문자 등을 기재하거나 문자를 지우는 과정에서 다량의 분필가루가 발생함으로써 실내가 오염되고, 특히 상기 발생된 분필가루가 호흡과정에서 인체 내로 침투하여 교사, 학생 등에 각종 폐질환의 원인으로 작용하는 문제점이 발생하였다. However, indoors are contaminated by the generation of a large amount of chalk powder in the process of writing or erasing letters using chalk on the uneven blackboard, and in particular, the generated chalk powder penetrates into the human body in the process of breathing, and so on. There was a problem that acts as a cause of various lung diseases.
이러한 문제점으로 인해 화이트 보드 등에 사용되는 유색 마커 펜이 개발되어 사용되고 있다. 이러한 마커펜은 내부에 잉크 용액을 내재하여 그 잉크 용액을 마커펜 내부의 마커펜 촉에 설치되는 스폰지 등의 흡수재에 흡수시키고 펜촉을 통해 외부로 유출시킴으로써 필기구의 기능을 갖도록 하고 있다.Due to these problems, colored marker pens used for white boards have been developed and used. Such a marker pen has an ink solution therein to absorb the ink solution into an absorbent such as a sponge installed on the marker pen tip inside the marker pen, and to discharge the ink solution to the outside through the pen tip to have a function of a writing instrument.
상술한 마커펜은 기존의 칠판이 아닌 표면이 매끄러운 화이트보드에 사용되는 것이 일반적인데, 상기 화이트보드는 백색 바탕색을 갖고 있으며, 그 표면에 필기하는 마커펜은 소거성이 좋은 다양한 색을 사용하여 필기하고 있다. 그러나 바탕색이 백색인 경우 빛의 반사로 눈이 쉽게 피로해져 시각장애로 인한 학습효과가 떨어진다는 문제점이 발생하였다. 또한, 마커펜은 기본적으로 액체성분과 색상을 나타내는 안료 성분을 포함하고 있는데, 분필과 달리 안료의 침전 등으로 인하여 균일한 색상을 나타내지 못하는 문제점이 나타난다. 아울러, 유성 마커펜의 경우 좋지 않은 알코올 냄새가 발생되고, 필기 후 칠판의 표면에 잔존재하는 기름기로 인하여 백묵 및 마커펜 혼용 시 필기가 어려운 문제점이 발생하였다.The above-described marker pen is generally used for a smooth whiteboard instead of a conventional blackboard. The whiteboard has a white background color, and the marker pen for writing on the surface is written using various colors with good eraseability. Doing. However, when the background color is white, the eye is easily tired by the reflection of light, which causes a problem that the learning effect due to the visual impairment is reduced. In addition, the marker pen basically contains a liquid component and a pigment component representing a color, unlike chalk, there is a problem in that it does not exhibit a uniform color due to the precipitation of the pigment. In addition, in the case of the oily marker pen, a bad alcohol odor is generated, and the writing is difficult due to the mixing of chalk and the marker pen due to the oil remaining on the surface of the blackboard after the writing.
이에, 상기 문제점을 해결하기 위하여 다양한 기술들이 개발되어 왔다.Accordingly, various techniques have been developed to solve the above problems.
이러한 일예로서, 일본국 특허공보 제 2524689호(1995년4월25일 공개)에는 9 내지 12 중량%의 산화티탄과 0.9 내지 1.2 중량%의 탄산칼륨, 1.8 내지 2.2 중량%의 비닐수지, 30 내지 40 중량%의 이소프로필알코올, 8 내지 11 중량%의 이소옥틸스테아레이트, 2.8 내지 3.2 중량%의 폴리옥실에칠렌타우릴에텔, 0.8 내지 1.2 중량%의 폴리옥시에틸렌올레인세틸에텔, 30 내지 40 중량%의 에칠알코올 및 7 내지 8.5 중량%의 디옥틸아디페이트 등으로 구성되는 것을 특징으로 하는 흑판용 잉크 조성물이 개시되어 있다.As one example, Japanese Patent Publication No. 2524689 (published on April 25, 1995) includes 9 to 12 wt% titanium oxide, 0.9 to 1.2 wt% potassium carbonate, 1.8 to 2.2 wt% vinyl resin, and 30 to 40% by weight of isopropyl alcohol, 8 to 11% by weight of isooctylstearate, 2.8 to 3.2% by weight of polyoxysyylenetauryl ether, 0.8 to 1.2% by weight of polyoxyethylene oleincetyl ether, 30 to 40% by weight Disclosed is an ink composition for a blackboard, characterized in that the composition consists of% ethyl alcohol, 7 to 8.5 wt% dioctyl adipate, and the like.
그리고 대한민국 특허공개공보 제 1995-0032524호(1995년12월22일 공개)에는 산화티탄 9 내지 12 중량%와 탄산칼슘 1 내지 1.5 중량%를 혼합 분쇄한 후 여기에 비닐레진 1.5 내지 1.8 중량%, 이소프로필알코올(IPA) 50 내지 60 중량%를 혼합하여 95 내지 110℃에서 약 20 내지 30분간 중탕으로 가열하여 점액상태의 원액을 일차생성한 후, 이소옥시스테아레이트(IOS) 8 내지 11 중량%, 폴리옥시에틸렌 라우릴에텔 2.8 내지 3.2 중량%, 폴리옥시에틸렌 올레인세틸에텔 0.8 내지 1.2 중량% 및 아세톤 10 내지 12 중량%를 첨가 혼합한 다음 디옥틸아디페이트(DOA) 7 내지 8.5 중량%를 첨가 혼합하여서 되는 것을 특징으로 하는 마커펜용 백색잉크의 제조방법이 개시되어 있다.And the Republic of Korea Patent Publication No. 1995-0032524 (published Dec. 22, 1995) is mixed and pulverized 9 to 12% by weight of titanium oxide and 1 to 1.5% by weight of calcium carbonate, 1.5 to 1.8% by weight of vinyl resin, 50 to 60% by weight of isopropyl alcohol (IPA) was mixed and heated in a hot bath at 95 to 110 ° C. for about 20 to 30 minutes to form a mucus stock solution, followed by 8 to 11% by weight of isooxystearate (IOS). 2.8 to 3.2% by weight of polyoxyethylene lauryl ether, 0.8 to 1.2% by weight of polyoxyethylene oleincetyl ether and 10 to 12% by weight of acetone were added and mixed, followed by 7 to 8.5% by weight of dioctyl adipate (DOA). Disclosed is a method for producing a white ink for a marker pen, which is added and mixed.
그러나 상기 발명들은 칠판에 마커펜으로 판서를 할 수 있으나, 요철이 있는 칠판의 미세한 틈새에 잉크조성물이 끼여 고착화된 경우 소거가 용이하지 못한 문제점이 있다. 구체적으로, 판서 후 단시간 내에 잉크를 소거할 경우에는 잉크가 용이하게 소거될 수 있으나, 소정 시간이 경과된 후에는 잉크에 포함된 유연제인 준휘발성 성분의 폴리옥시에틸렌올레인세틸에텔, 이소옥틸스테아레이트 등이 휘발 및 건조되어 잉크가 용이하게 소거되지 않는다는 문제점이 있다. 이러한 문제점을 해결하기 위해서는 별도의 클리너(cleaner)를 사용할 수 있으나, 별도의 비용이 소요될 뿐만 아니라 판서내용을 제거하는 것이 매우 번거로워지게 된다.However, the above inventions can be written with a marker pen on the board, but there is a problem that the erase is not easy when the ink composition is stuck in a minute gap of the board having the unevenness. Specifically, when the ink is erased within a short time after writing, the ink can be easily erased, but after a predetermined time has elapsed, polyoxyethylene oleincetyl ether, isooctyl stearate of a semivolatile component which is a softener included in the ink There is a problem that the ink is not easily erased because the rate or the like is volatilized and dried. In order to solve this problem, a separate cleaner may be used, but it is not only expensive, but it is very cumbersome to remove the writing contents.
따라서, 마커펜을 기존의 칠판에 사용하는 경우 발생되는 상술한 문제점을 근본적으로 해결하기 위해서는 기존의 요철이 형성된 분필용 칠판을 잉크를 사용하는 마커펜에 적합한 전용의 화이트보드 등으로 교체하여 사용하는 것이 바람직하다. 그러나 기존의 요철이 형성된 칠판을 화이트보드로 교체하는 데에는 막대한 비용이 소요될 뿐만 아니라, 기존에 생산된 분필을 사용할 수 없게 되는 문제점이 있다. 또한, 일단 기존 칠판을 화이트보드로 교체한 후에는 여전히 분필의 사용을 선호하는 사람도 분필을 사용할 수 없게 되는 문제점이 있다. Therefore, in order to fundamentally solve the above-mentioned problems caused when using a marker pen on an existing blackboard, the existing blackboard for chalk having formed irregularities is replaced with a dedicated white board suitable for a marker pen using ink. It is preferable. However, replacing the existing irregularities formed blackboard with a white board takes a huge cost, there is a problem that can not use the existing chalk. In addition, once the existing blackboard is replaced with a whiteboard, there is a problem that people who still prefer to use chalk cannot use chalk.
따라서, 본 발명의 제 1 목적은 인체에 무해하며, 비흡수성을 갖는 어떠한 재질에서도 자국이나 얼룩이 잔존하지 않고, 별도의 클리너 사용이 불필요하며, 필기면으로부터 소거시 필기면에 잔존하는 이물질을 제거할 수 있는 마커펜용 수성 겔 잉크 조성물을 제공하는 것이다.Therefore, the first object of the present invention is harmless to the human body, no marks or stains remain in any material having non-absorbency, no need to use a separate cleaner, and to remove foreign substances remaining on the writing surface when erased from the writing surface. It is to provide an aqueous gel ink composition for a marker pen.
본 발명의 제 2 목적은 인체에 무해하며, 비흡수성을 갖는 어떠한 재질에서도 자국이나 얼룩이 잔존하지 않고, 별도의 클리너 사용이 불필요하며, 필기면으로 부터 소거시 필기면에 잔존하는 이물질을 제거할 수 있는 마커펜용 수성 겔 잉크 조성물의 제조방법을 제공하는 것이다.The second object of the present invention is harmless to the human body, no marks or stains remain in any material having non-absorbency, no need to use a separate cleaner, and can remove foreign substances remaining on the writing surface when erased from the writing surface. It is to provide a method for producing an aqueous gel ink composition for a marker pen.
상술한 본 발명의 제 1 목적을 달성하기 위하여, 본 발명의 일실시예에 의하면 물 35 내지 50 중량%, 멜라민수지 및 요소수지로 구성된 수용성 합성수지 7 내지 13 중량%, 색상안료 20 내지 30 중량%, 수성분산제 4 내지 6 중량%, 유화제 1 내지 3 중량%, 이형제 4 내지 6 중량%, 및 안정제 8 내지 12 중량%를 포함하는 마커펜용 수성 겔 잉크 조성물을 제공한다.In order to achieve the first object of the present invention described above, according to one embodiment of the present invention 35 to 50% by weight of water, 7 to 13% by weight of water-soluble synthetic resin consisting of melamine resin and urea resin, 20 to 30% by weight of color pigments It provides an aqueous gel ink composition for marker pens, comprising 4 to 6% by weight of an aqueous acidic acid, 1 to 3% by weight of an emulsifier, 4 to 6% by weight of a release agent, and 8 to 12% by weight of a stabilizer.
상술한 본 발명의 제 2 목적을 달성하기 위하여, 본 발명의 일실시예에 의한 제조방법은 (ⅰ) 물 35 내지 50 중량%에 멜라민수지 및 요소수지로 구성된 수용성 합성수지 7 내지 13 중량%를 첨가하고, 1 내지 3시간 동안 교반하여 겔 조성물을 형성하는 단계, (ⅱ) 단계 (ⅰ)을 통해 생성된 겔 조성물에 색상안료 20 내지 30 중량%를 첨가하고 분쇄하는 단계, 및 (ⅲ) 단계 (ⅱ)를 통해 생성된 혼합물에 수성분산제 4 내지 6 중량%, 유화제 4 내지 6 중량%, 이형제 4 내지 6 중량% 및 안정제 8 내지 12 중량%를 첨가하고, 1 내지 2시간 동안 교반하는 단계를 포함하는 마커펜용 수성 겔 잉크 조성물의 제조방법을 제공한다.In order to achieve the above-described second object of the present invention, the manufacturing method according to one embodiment of the present invention (i) to 7 to 13% by weight of water-soluble synthetic resin consisting of melamine resin and urea resin to 35 to 50% by weight of water And stirring for 1 to 3 hours to form a gel composition, (ii) adding 20 to 30% by weight of the color pigment to the gel composition produced through step (iii) and pulverizing, and (iii) Ii) adding 4 to 6% by weight of the aqueous acidic acid, 4 to 6% by weight of emulsifier, 4 to 6% by weight of release agent and 8 to 12% by weight of stabilizer, and stirring for 1 to 2 hours. It provides a method for producing an aqueous gel ink composition for a marker pen.
본 발명에 의하면, 별도의 클리너 사용 없이 일반 지우개로도 잔상이나 찌꺼 기 없이 용이하게 제거할 있는 잉크조성물을 제공할 수 있다. 또한, 흑판, 유리, 표면이 고운 우드목이나 플라스틱판 등의 비흡수성 물체의 필기판에 필기가 가능하고, 필기한 후 오랜 시간이 경과되어도 마치 껌이 매끈한 표면에서 분리되는 것처럼 소거성이 뛰어나다. According to the present invention, it is possible to provide an ink composition which can be easily removed without an afterimage or residue even with a general eraser without using a separate cleaner. In addition, writing is possible on writing boards of non-absorbing objects such as black board, glass, and fine wood or plastic boards, and even after a long time after writing, it is excellent in erasability as the gum is separated from the smooth surface.
아울러, 상분리 및 침전이 발생하지 아니하므로 장기보관이 가능하며, 필기면으로부터 소거시 필기면에 잔존하는 이물질을 제거할 수 있다. 나아가, 알코올 대신 물을 사용하여 인체에 무해하고 자극적인 냄새가 발생되지 않는다.In addition, long-term storage is possible because phase separation and sedimentation do not occur, it is possible to remove foreign matter remaining on the writing surface when erasing from the writing surface. Furthermore, the use of water instead of alcohol does not produce harmless and irritating odors to the human body.
이하, 본 발명의 바람직한 실시예들에 의한 마커펜용 수성 겔 잉크 조성물(이하, "잉크 조성물"이라 한다.) 및 그 제조방법을 상세하게 설명한다.Hereinafter, an aqueous gel ink composition (hereinafter, referred to as an "ink composition") for a marker pen according to preferred embodiments of the present invention and a manufacturing method thereof will be described in detail.
본 발명의 일 실시예는 잉크 조성물에 관한 것으로서 그 내부의 함유 성분을 대별하면, 잉크 조성물의 점도 및 건조성을 조절하는 물과, 상기 물과 결합하여 상기 잉크 조성물의 접착강도를 증가시키는 수용성 합성수지와, 색상을 나타내는 색상안료와, 상기 잉크 조성물의 색상안료가 뭉치지 않고 분산되도록 하는 수성분산제와, 상기 잉크 조성물을 유연하게 하는 유화제와, 상기 잉크 조성물이 필기면으로부터 용이하게 분리되도록 하는 이형제, 및 잉크 조성물의 변색을 방지하는 안정제가 사용된다.One embodiment of the present invention relates to an ink composition, when the components contained therein are roughly divided into water for controlling the viscosity and dryness of the ink composition, and a water-soluble synthetic resin which combines with the water to increase the adhesive strength of the ink composition; A color pigment representing a color, an aqueous acidic agent for dispersing the color pigments of the ink composition without aggregation, an emulsifier for softening the ink composition, a release agent for easily separating the ink composition from a writing surface, and an ink Stabilizers are used to prevent discoloration of the composition.
이러한 각각의 성분들은 색상안료처럼 단일의 기능을 수행하는 것도 있지만, 서로 화학적인 작용을 통하여 공동으로 기능을 수행할 수도 있는데, 이는 화학 물질의 특성상 당연한 것이다. 따라서, 본 발명은 특정 기능 성분에만 의존 한다기보다는 여러 조성의 조합과 그 조합량에 특이성이 있다고 할 수 있다. Each of these components may perform a single function like a color pigment, but may also function jointly through a chemical action with each other, which is natural due to the nature of the chemicals. Therefore, the present invention may be said to be specific in the combination of the various compositions and the amount thereof, rather than only depending on the specific functional ingredient.
본 발명의 일 실시예에 의한 잉크 조성물은 물을 포함한다.The ink composition according to one embodiment of the present invention contains water.
상기 물은 마커펜용 수성 겔 잉크 조성물의 용매로서, 상기 잉크 조성물의 점도 및 건조성을 조절하며, 잉크 조성물의 전사 성능을 조절한다. 또한, 물은 에칠알코올 등 알코올류 용매에 비하여 환경 친화적이고, 무색, 무미, 무취하며, 온도 변화에 따른 화재 발생의 위험이 작다. 이와 같이, 알코올 등을 용매로 사용하지 않고, 인체에 무해한 물을 용매로 사용함으로써, 인체에 무해하고 환경친화적인 성질의 수성 겔 잉크 조성물을 제조할 수 있다. 이러한 물은 어떠한 물질도 포함하지 않는 연수, 증류수, 탈이온수 또는 여과된 수돗물을 이용할 수 있으며, 바람직하게는 증류수를 사용하는 것이 좋다. The water is a solvent of the aqueous gel ink composition for a marker pen, and controls the viscosity and dryness of the ink composition, and controls the transfer performance of the ink composition. In addition, water is environmentally friendly, colorless, tasteless, and odorless compared to alcohol solvents such as ethyl alcohol, and the risk of fire due to temperature change is small. As such, by using water, which is harmless to the human body, as the solvent, without using alcohol or the like as the solvent, an aqueous gel ink composition which is harmless to the human body and which is environmentally friendly can be produced. Such water may use soft water, distilled water, deionized water, or filtered tap water that does not contain any substance. Preferably, distilled water is used.
이때, 상기 물은 35 내지 50 중량%가 포함되는 것이 바람직하다. 여기서, 잉크 조성물에 물의 함량이 35 중량% 미만으로 사용되면 잉크의 점도가 적정 점도 이상으로 상승하여 펜촉을 통한 필기판에 필기가 어려워지고, 50 중량% 초과로 사용되면 잉크 조성물의 점도가 감소되어 잉크 조성물이 과량 유출되거나 색상안료 및 수용성 합성수지의 분리 속도가 적정수준의 물이 포함된 잉크 조성물보다 빨라져 장기보관하기 어려워진다. 또한, 물이 과량 사용될 경우에는 필기 후에 사용된 잉크의 건조 속도가 적정수준의 물이 포함된 잉크 조성물보다 느려진다. At this time, the water is preferably contained 35 to 50% by weight. Here, when the content of water in the ink composition is less than 35% by weight, the viscosity of the ink rises above the proper viscosity, making writing on the writing board through the nib difficult, and when used in excess of 50% by weight, the viscosity of the ink composition is reduced. Excess spillage of the ink composition or separation rate of the color pigment and the water-soluble synthetic resin is faster than the ink composition containing the appropriate level of water, making it difficult to store long-term. In addition, when excess water is used, the drying speed of the ink used after writing becomes slower than the ink composition containing an appropriate level of water.
본 발명의 일실시예에 의한 잉크 조성물은 수용성 합성수지를 포함한다. Ink composition according to an embodiment of the present invention comprises a water-soluble synthetic resin.
상기 수용성 합성수지는 물과 혼합됨으로써 겔 형태로 변환되어 색상안료의 분산을 촉진하고 색상안료의 침전을 방지하며 필기판에 접착력을 부여하는 것으로서, 멜라민수지(melamine resin)와 요소수지(urea resin)의 혼합물로 구성된다.The water-soluble synthetic resin is converted into a gel form by mixing with water to promote the dispersion of color pigments, prevent the precipitation of color pigments and impart adhesion to the writing plate, the melamine resin (urea resin) and urea resin (urea resin) It consists of a mixture.
여기서, 멜라민수지는 멜라민와 포름알데히드의 축합 반응으로 만든 열경화성 수지를 의미하며, 요소수지는 요소와 포르말린의 축합 반응으로 만든 합성수지를 의미한다.Here, melamine resin means a thermosetting resin made by the condensation reaction of melamine and formaldehyde, urea resin means a synthetic resin made by the condensation reaction of urea and formalin.
보다 구체적으로, 상기 수용성 합성수지는 멜라민수지 60 내지 80 중량%와 요소수지 20 내지 40 중량%가 혼합되어 형성되는 것을 사용하는 것이 좋으며, 바람직하게는 멜라민수지 70 중량%와 요소수지 30 중량%가 혼합되어 형성되는 것을 사용하는 것이 좋다.More specifically, the water-soluble synthetic resin is preferably used is formed by mixing 60 to 80% by weight of melamine resin and 20 to 40% by weight of urea resin, preferably 70% by weight of melamine resin and 30% by weight of urea resin It is good to use what is formed.
또한, 수용성 합성수지의 사용량은 특별히 제한되지 않고, 잉크 조성물의 구성 성분에 따라 사용량이 조절될 수 있지만, 7 내지 13 중량%가 포함되는 것이 바람직하다. 여기서, 상기 수용성 합성수지의 함량이 7 중량% 미만인 경우에는 점도가 묽어져 글자의 피막이 형성되지 않아 소거 시 잔상이 존재할 수 있다. 또한, 수용성 합성수지의 함량이 13 중량%를 초과하는 경우에는 점도가 증가되어 잉크 조성물 내에서 색상안료의 유동성이 저하되어 펜촉을 통한 잉크의 유출이 균일하지 아니하므로 필기면에서 필기가 불충분하게 된다.In addition, the amount of the water-soluble synthetic resin is not particularly limited, and the amount of the water-soluble synthetic resin may be adjusted according to the constituents of the ink composition, but preferably 7 to 13% by weight. In this case, when the content of the water-soluble synthetic resin is less than 7% by weight, the viscosity is thinned, so that the film of the letter is not formed, so an afterimage may exist when erasing. In addition, when the content of the water-soluble synthetic resin exceeds 13% by weight, the viscosity is increased, the fluidity of the color pigment in the ink composition is lowered, so that the outflow of the ink through the nib is not uniform, writing on the writing surface is insufficient.
본 발명의 일실시예에 의한 잉크 조성물은 색상안료를 포함한다. Ink composition according to an embodiment of the present invention comprises a color pigment.
상기 색상안료는 잉크 조성물에 색상을 부여하기 위해 첨가되는 것으로서, 인체와 환경에 무해한 색상안료라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 이산화티타늄, 화이트 카본, 탄산칼슘, 침강성 탄산마그네슘, 유기 안료류 또는 이들의 혼합물이 사용되는 것이 좋고, 보다 바람직하게는 이산화티타늄을 사용하는 것이 좋다. The color pigment is added to impart a color to the ink composition, but any color pigment that is harmless to humans and the environment may be used, but preferably titanium dioxide, white carbon, calcium carbonate, precipitated magnesium carbonate, or organic pigment. Or mixtures thereof are preferably used, and more preferably titanium dioxide.
이때, 상기 색상안료는 20 내지 30 중량%가 포함되는 것이 바람직하다. 여기서, 상기 색상안료의 함량이 20 중량% 미만인 경우에는 잉크 조성물의 색상이 선명하지 못하고, 필기된 잉크 조성물이 용이하게 소거되지 않으며, 색상안료의 함량이 30 중량%를 초과하는 경우에는 색상은 선명하나 잉크 조성물의 점도가 증가되어 잉크 조성물이 펜촉을 통해 균일하게 유출되지 아니한다. At this time, the color pigment is preferably contained 20 to 30% by weight. Here, when the content of the color pigment is less than 20% by weight, the color of the ink composition is not clear, the written ink composition is not easily erased, and when the content of the color pigment is more than 30% by weight, the color is clear. However, the viscosity of the ink composition is increased so that the ink composition does not flow out evenly through the nib.
상기 이산화티타늄은 착색력 및 은폐력이 색상안료 중에서 가장 크고, 내산성, 내알칼리성, 내광성, 내열성 등이 있고, 그 사용량이 색상안료 중 가장 많으며, 도료, 고무, 인쇄잉크, 제지, 인견, 합성수지, 그림물감, 화장품, 법랑(琺瑯) 등 그 용도가 다양하다. The titanium dioxide has the greatest coloring power and hiding power among color pigments, and has acid resistance, alkali resistance, light resistance, heat resistance, etc., and its usage is the most among color pigments, paints, rubber, printing ink, papermaking, seal, synthetic resin, and coloring. , Cosmetics, enamel (琺 瑯) has a variety of uses.
본 발명의 일실시예에 의한 잉크 조성물은 수성분산제를 포함한다. An ink composition according to an embodiment of the present invention includes an aqueous acidic agent.
상기 수성분산제는 색상안료의 분산을 촉진하여 색상안료의 침전 및 수용성 합성수지와의 분리 현상을 억제하고, 색의 발색과 저장성을 지속시켜주는 것으로서, 이러한 목적으로 사용되는 수성분산제라면 어떠한 수성분산제를 사용하여도 무 방하지만, 바람직하게는 당업계에서 통상적으로 사용되는 수성분산제를 사용하는 것이 좋고, 특정적으로는 독일 BYK-Chemie GmbH사의 Disperbyk-190(상품명)을 사용하는 것이 좋다. The aqueous acidic acid is to promote the dispersion of color pigments to inhibit the precipitation of color pigments and separation from water-soluble synthetic resins, and to maintain the color development and storage properties, if any water-based acidic acid is used for this purpose Although, it is preferable to use a water-based acid powder commonly used in the art, and in particular, it is preferable to use Disperbyk-190 (trade name) of BYK-Chemie GmbH of Germany.
이때, 상기 수성분산제는 4 내지 6 중량%가 포함되는 것이 바람직하다. 여기서, 수성분산제의 함량이 4 중량% 미만인 경우에는 색상안료의 분산 효력이 저하됨에 따라 색상안료가 분리되어 잉크의 저장성과 수명이 단축되고, 마커펜으로부터 색상안료가 균일하게 유출되지 않을 수 있으며, 상기 수성분산제의 함량이 6 중량%를 초과하는 경우에는 색상안료나 수용성 합성수지의 침전이 발생할 수 있다.At this time, it is preferable that the water-based acid agent is included 4 to 6% by weight. In this case, when the content of the water-based powder is less than 4% by weight, as the dispersing effect of the color pigment is reduced, the color pigment is separated and the shelf life of the ink is shortened, and the color pigment may not be uniformly spilled from the marker pen. If the content of the water-based powder is more than 6% by weight precipitation of color pigments or water-soluble synthetic resin may occur.
본 발명의 일실시예에 의한 잉크 조성물은 유화제를 포함한다. The ink composition according to an embodiment of the present invention includes an emulsifier.
상기 유화제는 잉크 조성물을 유연하게 함으로써 도포막을 형성하여 펜촉에서 습윤상태를 유지시키고, 잉크 조성물이 원활히 혼합되어 분산되지 않도록 하는 것으로서, 이러한 목적으로 사용되는 유화제라면 어떠한 유화제라도 상기 유화제에 포함된다 할 것이지만, 바람직하게는 당업계에서 통상적으로 사용되는 유화제를 사용하는 것이 좋고, 특정적으로는 동성화공의 X-100(상품명)을 사용하는 것이 좋다. The emulsifier is to soften the ink composition to form a coating film to maintain a wet state in the nib and to prevent the ink composition from being mixed and dispersed smoothly, any emulsifier used for this purpose will be included in the emulsifier. Preferably, it is preferable to use an emulsifier commonly used in the art, and it is particularly preferable to use X-100 (trade name) of the same chemical.
이때, 유화제는 4 내지 6 중량%가 포함되는 것이 바람직하다. 여기서, 상기 유화제의 함량이 4 중량% 미만인 경우에는 잉크 조성물이 원활히 혼합되지 않아 시간의 지남에 따라 침전물이 발생될 수 있으며, 유화제의 함량이 6 중량%를 초과하는 경우에는 잉크 조성물의 점성 저하로 인해 유색안료가 서로 엉겨 침강되고, 필 기 후 잔류물이 글자에 잔존하여 잉크 조성물이 번지거나 흘러내려 필기면에 얼룩이 발생될 수 있으며, 적정 수준의 유화제가 포함된 잉크 조성물보다 건조속도가 늦어진다.At this time, the emulsifier is preferably contained 4 to 6% by weight. Here, when the content of the emulsifier is less than 4% by weight, the ink composition may not be smoothly mixed, and a precipitate may be generated over time. When the content of the emulsifier exceeds 6% by weight, the viscosity of the ink composition may be reduced. Due to the color pigments are entangled with each other and settled, the residue after writing, the ink composition may be smeared or spilled due to smearing or flowing down the writing surface, the drying speed is slower than the ink composition containing an appropriate level of emulsifier.
본 발명의 일실시예에 의한 잉크 조성물은 이형제를 포함한다. An ink composition according to an embodiment of the present invention includes a release agent.
상기 이형제는 필기면에 형성된 잉크 조성물의 코팅이 필기면으로부터 용이하게 소거될 수 있도록 잉크 조성물 코팅의 소거성을 향상시키는 것으로서, 상기 수용성 합성수지 및 유화제와 함께 소거성에 중요한 역할을 수행하는 물질이다. 상기 이형제로는 지방족 카르복실레이트, 디부칠프탈레이트, 에칠올레이트, 부칠라우레이트, 액상파라핀, 다가변성알코올, 또는 이들의 2 이상의 혼합물을 사용할 수 있고, 특정적으로는 일본 신에츠(ShinEtsu)사의 KS737(상품명) 또는 KMK740(상품명)을 사용하는 것이 좋다. The release agent is to improve the eraseability of the ink composition coating so that the coating of the ink composition formed on the writing surface can be easily erased from the writing surface, and is a material that plays an important role in erasability with the water-soluble synthetic resin and the emulsifier. As the release agent, an aliphatic carboxylate, dibutyl phthalate, ethylate, butylaurate, liquid paraffin, multivariable alcohol, or a mixture of two or more thereof may be used. Specifically, KS737 of ShinEtsu, Japan. (Brand name) or KMK740 (brand name) is recommended.
이때, 상기 이형제는 4 내지 6 중량%가 포함되는 것이 바람직하다. 여기서, 이형제의 함량이 4 중량% 미만인 경우에는 잉크 조성물의 이형 효과가 미약하여 필기면으로부터 용이하게 소거되지 않고, 이형제의 함량이 6 중량%를 초과하는 경우에는 소거성은 향상되나 색상의 선명도가 저하된다.At this time, the release agent is preferably included 4 to 6% by weight. Here, when the content of the release agent is less than 4% by weight, the release effect of the ink composition is weak so that it is not easily erased from the writing surface, and when the content of the release agent exceeds 6% by weight, the eraseability is improved, but the vividness of color is lowered. do.
본 발명의 일실시예에 의한 잉크 조성물은 안정제를 포함한다.The ink composition according to an embodiment of the present invention includes a stabilizer.
상기 안정제는 잉크 조성물의 일정한 점도와 보형성을 유지시켜 주고, 변색을 방지하며, 성분간 분리를 방지하는 것으로서, 상기 목적으로 사용되는 안정제라 면, 어떠한 안정제를 사용하여도 무방하지만, 바람직하게는 글리세린(glycerin)을 사용하는 좋다. The stabilizer is to maintain a constant viscosity and shape retention of the ink composition, to prevent discoloration, and to prevent separation between components, and any stabilizer may be used as long as the stabilizer is used for the above purpose. Glycerin (glycerin) is good to use.
이때, 상기 안정제는 8 내지 12 중량%가 포함되는 것이 바람직하다. 여기서, 상기 안정제의 함량이 8 중량% 미만인 경우에는 점도 및 보형성이 저하되어 변색이 발생될 수 있고, 상기 안정제의 함량이 12 중량%를 초과하는 경우에는 잉크 조성물의 소거성이 저하될 수 있다.At this time, the stabilizer is preferably contained 8 to 12% by weight. In this case, when the content of the stabilizer is less than 8% by weight, the viscosity and the shape retaining property may be reduced, and discoloration may occur. When the content of the stabilizer is more than 12% by weight, the eraseability of the ink composition may be reduced. .
본 발명은 전술한 구성을 갖는 잉크 조성물의 제조방법을 제공한다.The present invention provides a method for producing an ink composition having the above-described configuration.
도 1은 본 발명에 따른 잉크 조성물의 제조방법의 제조 공정을 순서도로 표시한 것이다.1 is a flow chart showing the manufacturing process of the manufacturing method of the ink composition according to the present invention.
도 1을 참조하면, 본 발명에 의한 잉크 조성물의 제조방법은 다음과 같다.Referring to Figure 1, the manufacturing method of the ink composition according to the present invention is as follows.
먼저, 물 35 내지 50 중량%에 멜라민수지 및 요소수지로 구성된 수용성 합성수지 7 내지 13 중량%를 첨가하고, 1 내지 3시간 동안 교반하여 겔 조성물을 형성한다.First, 7 to 13% by weight of a water-soluble synthetic resin composed of melamine resin and urea resin is added to 35 to 50% by weight of water, and stirred for 1 to 3 hours to form a gel composition.
그 다음, 상기 겔 조성물에 색상안료 20 내지 30 중량%를 첨가하고 분쇄하며, 수성분산제 4 내지 6 중량%, 유화제 4 내지 6 중량%, 이형제 4 내지 6 중량% 및 안정제 8 내지 12 중량%를 첨가하고, 1 내지 2시간 동안 교반하여 잉크 조성물을 제조한다.Then, 20 to 30% by weight of color pigments are added to the gel composition and ground, and 4 to 6% by weight of an aqueous acidic acid, 4 to 6% by weight of an emulsifier, 4 to 6% by weight of a release agent, and 8 to 12% by weight of a stabilizer are added. And stirred for 1 to 2 hours to prepare an ink composition.
보다 구체적으로, 첫 번째 단계는 물 35 내지 50 중량%에 멜라민수지 및 요소수지로 구성된 수용성 합성수지 7 내지 13 중량%를 첨가하는 단계로서, 상기 물 과 수용성 합성수지를 반응기에서 1 내지 3시간 동안 혼합시켜 겔 조성물을 형성한다. 이때, 반응기의 교반속도는 1,500 내지 2,000rpm으로 수행될 수 있다.More specifically, the first step is to add 7 to 13% by weight of water-soluble synthetic resin consisting of melamine resin and urea resin to 35 to 50% by weight of water, by mixing the water and water-soluble synthetic resin in the reactor for 1 to 3 hours To form a gel composition. At this time, the stirring speed of the reactor may be performed at 1,500 to 2,000rpm.
두 번째 단계는 첫 번째 단계를 통해 생성된 겔 조성물에 색상안료 20 내지 30 중량%를 첨가하는 단계로서, 상기 겔 조성물에 색상안료를 첨가시켜 혼합물을 형성한 후 상기 혼합물을 분쇄기로 분쇄한다. 상기 분쇄기로는 당업계에서 통상적으로 사용되는 것이라면, 어떠한 것을 사용하여도 무방하지만, 바람직하게는 삼본롤밀(3 roll mill), 스텐드밀, 제트밀(jetmill) 등을 사용하는 것이 좋으며, 보다 바람직하게는 삼본롤밀을 사용하는 것이 좋다.The second step is to add 20 to 30% by weight of the color pigment to the gel composition produced through the first step, the color composition is added to the gel composition to form a mixture, and then the mixture is ground with a grinder. As the grinder, any one may be used as long as it is commonly used in the art, but it is preferable to use a three roll mill, a stand mill, a jet mill, and the like, more preferably. It is recommended to use a three-bone roll mill.
상기 삼본롤밀을 사용하여 혼합물을 분쇄하는 경우에, 상기 혼합물은 삼본롤밀을 3회 이상, 바람직하게는 3 내지 5회를 수행하여 분쇄하는 것이 좋다. When the mixture is pulverized using the sambon roll mill, the mixture may be pulverized by performing the sambon roll mill three or more times, preferably three to five times.
상기 스텐드밀 또는 제트밀을 사용하여 혼합물을 분쇄하는 경우에, 상기 혼합물은 1 내지 3시간, 바람직하게는 약 2시간 동안 분쇄시키는 것이 좋다. When the mixture is ground using the stand mill or jet mill, the mixture is preferably ground for 1 to 3 hours, preferably about 2 hours.
세 번째 단계는 두 번째 단계를 통해 분쇄된 혼합물에 수성분산제 4 내지 6 중량%, 유화제 4 내지 6 중량%, 이형제 4 내지 6 중량% 및 안정제 8 내지 12 중량%를 첨가하는 단계로서, 두 번째 단계를 통과한 혼합물에 수성분산제 4 내지 6 중량%, 유화제 4 내지 6 중량%, 이형제 4 내지 6 중량% 및 안정제 8 내지 12 중량%를 첨가하고, 상온에서 1 내지 2시간 동안 교반시켜 잉크 조성물을 형성한다. 이때, 교반기의 교반속도는 1,000 내지 1,500rpm으로 수행될 수 있다.The third step is to add 4 to 6% by weight of the aqueous acidic acid, 4 to 6% by weight of the emulsifier, 4 to 6% by weight of the release agent and 8 to 12% by weight of the stabilizer to the mixture ground through the second step. To the mixture passed through the addition of 4 to 6% by weight of the water acid agent, 4 to 6% by weight of the emulsifier, 4 to 6% by weight of the release agent and 8 to 12% by weight of the stabilizer, and stirred at room temperature for 1 to 2 hours to form an ink composition do. At this time, the stirring speed of the stirrer may be performed at 1,000 to 1,500 rpm.
이하, 본 발명을 바람직한 일 실시예를 참조하여 다음에서 구체적으로 상세 하게 설명한다. 단, 다음의 실시예는 본 발명을 구체적으로 예시하기 위한 것이며, 이것만으로 한정하는 것은 아니다.Hereinafter, the present invention will be described in detail with reference to a preferred embodiment. However, the following Example is for illustrating this invention concretely, It does not limit only to this.
[실시예]EXAMPLE
1. 상온 1기압 하에서, 멜라민수지 0.6㎏ 및 요소수지 0.4㎏을 반응기에 투입하고, 1,700 rpm으로 2시간 교반하여 수용성 합성수지를 제조하였다.1. Under normal temperature 1 atmosphere, 0.6 kg of melamine resin and 0.4 kg of urea resin were added to a reactor, and stirred at 1,700 rpm for 2 hours to prepare a water-soluble synthetic resin.
2. 상온 1기압 하에서, 증류수 4㎏을 반응기에 투입하고, 수용성 합성수지 1㎏을 반응기에 투입한 후 1,700 rpm으로 2시간 교반하여 겔 조성물을 형성하였다.2. Under 1 atmosphere of room temperature, 4 kg of distilled water was added to the reactor, 1 kg of a water-soluble synthetic resin was added to the reactor, and stirred at 1,700 rpm for 2 hours to form a gel composition.
3. 상온 1기압 하에서, 상기 겔 조성물에 이산화티타늄[R-902, 듀폰, 미국] 2.5㎏을 첨가하여 혼합물을 형성한 후 삼본롤밀을 이용하여 상기 혼합물을 3번 분쇄하였다.3. Under normal pressure of 1 atm, 2.5 kg of titanium dioxide [R-902, DuPont, USA] was added to the gel composition to form a mixture, and the mixture was triturated three times using a sambon roll mill.
4. 상온 1기압 하에서, 상기 분쇄된 혼합물에 수성분산제[Disperbyk-190, BYK-Chemie GmbH, 독일] 0.5㎏, 유화제[X-100, 동성화공, 한국] 0.5㎏, 이형제[KMK740, 신에츠, 일본] 0.5㎏, 안정제[글리세린, 동양케미칼, 한국] 1㎏를 첨가하고, 1,300 rpm으로 1시간 교반하여 잉크 조성물을 제조하였다. 4. Under normal pressure of 1 atm, 0.5 kg of an aqueous powder [Disperbyk-190, BYK-Chemie GmbH, Germany], 0.5 kg of an emulsifier [X-100, Dongsung Chemical, Korea], a release agent [KMK740, Shin-Etsu, Japan] ] 0.5 kg and 1 kg of stabilizer [glycerine, Dongyang Chemical, Korea] were added, followed by stirring at 1,300 rpm for 1 hour to prepare an ink composition.
[비교예 1]Comparative Example 1
실시예와 동일한 조건에서 잉크 조성물을 제조하되, 실시예의 수용성 합성수지 1㎏을 첨가하지 않고 잉크 조성물을 얻었다. An ink composition was prepared under the same conditions as in Example, but the ink composition was obtained without adding 1 kg of the water-soluble synthetic resin of Example.
[비교예 2]Comparative Example 2
실시예와 동일한 조건에서 잉크 조성물를 제조하되, 실시예의 이산화티타늄[R-902, 듀폰, 미국] 2.5㎏ 대신 이산화티타늄[R-902, 듀폰, 미국] 5㎏을 첨가하여 잉크 조성물을 얻었다. An ink composition was prepared under the same conditions as in the example, except that 5 kg of titanium dioxide [R-902, DuPont, USA] was added instead of 2.5 kg of titanium dioxide [R-902, DuPont, USA] to obtain an ink composition.
[비교예 3]Comparative Example 3
실시예와 동일한 조건에서 잉크 조성물를 제조하되, 실시예의 증류수 4㎏ 대신 증류수 8㎏을 첨가하여 잉크 조성물을 얻었다. An ink composition was prepared under the same conditions as in Example, but 8 kg of distilled water was added instead of 4 kg of the distilled water of Example to obtain an ink composition.
[실험예]Experimental Example
상기 실시예와 비교예 1, 비교예 2 및 비교예 3을 통하여 제조된 잉크 조성물의 유출성, 분산성, 백색도, 건조성 및 소거성을 평가하기 위하여 기능 평가 실험을 실시하였으며, 그 결과를 다음의 표 1에 나타내었다.Functional evaluation experiments were conducted to evaluate the outflow, dispersibility, whiteness, dryness, and erasability of the ink compositions prepared through the above Examples, Comparative Examples 1, 2 and 3, and the results are as follows. It is shown in Table 1.
< 표 1 > 마커펜용 수성 겔 잉크 조성물의 기능 평가 실험 결과<Table 1> Experimental results of aqueous gel ink compositions for marker pens
1)유출성1) Spillability
펜촉을 장착한 마커펜 잉크 저장탱크에 잉크 조성물 10g을 주입하고 펜촉을 일정한 시간 간격으로 수직으로 가압하여 잉크가 펜촉의 팁까지 도달하는데 걸리는 시간 및 가압 회수로 유출상태를 평가하였으며, 30회를 가압했을 때 펜촉의 팁까지 도달하는데 걸리는 시간을 측정하여 아래의 내용과 같이 평가하였다.10 g of the ink composition was injected into the marker pen ink storage tank equipped with the nib, and the pen nib was pressed vertically at regular time intervals to evaluate the outflow state by the time and the number of times it takes for the ink to reach the tip of the nib. The time taken to reach the tip of the pen tip was measured and evaluated as follows.
○ : 20초 이하 ○: 20 seconds or less
△ : 21초 내지 50초 △: 21 to 50 seconds
X : 50초 초과 X: greater than 50 seconds
2) 분산성2) Dispersibility
잉크 조성물을 시험관에 넣고 일주일간 방치 후 안료, 첨가제와 용매가 분리된 층의 두께를 측정하여 분산성을 아래의 내용과 같이 평가하였다.After the ink composition was placed in a test tube and left for one week, the thickness of the layer in which the pigment, the additive, and the solvent were separated was measured, and the dispersibility was evaluated as follows.
○ : 층분리 두께가 0 내지 2mm 이하인 경우(Circle): When layer separation thickness is 0-2 mm or less
△ : 층분리 두께가 2 내지 5mm 이하인 경우(Triangle | delta): When layer separation thickness is 2-5 mm or less
X : 층분리 두께가 6mm 이상인 경우X: Delamination thickness is 6mm or more
3) 백색도3) whiteness
녹색의 칠판용 도료를 도장하여 제작한 칠판 표면에 엠보싱이 있는 기존의 백묵 칠판에 백묵과 마커펜을 동시에 잡고 나선형의 선을 기재한 다음 3m 후방에서 육안으로 백묵과 비교하여 아래의 내용과 같이 평가하였다.Grab the chalk and marker pen at the same time and write the spiral line on the existing chalk board with embossing on the surface of the board made by painting the green board paint, and then compare it with the naked eye at 3m behind and evaluate as follows. It was.
○ : 백묵과 동일한 색상 ○: the same color as chalk
△ : 백묵보다 조금 연한 색상 △: slightly lighter color than chalk
X : 백묵보다 연한 색상 X: lighter color than chalk
4) 건조성4) dryness
상온, 습도 60 내지 70%에서, 비흡성이면서 표면이 거친 깨끗한 녹색 칠판과 스톱워치를 준비하고, 상기 녹색 칠판을 바닥에서 70ㅀ각도로 세워놓으며, 본 발명에 의해 제조된 잉크 조성물을 펜에 주입하여 직경 30cm 정도의 원을 필기한 후 몇 초만에 필기된 선이 완전 건조되는지 시간을 측정하였다. At room temperature and humidity of 60 to 70%, a non-absorbing and rough surface of a clean green chalkboard and stopwatch is prepared, the green chalkboard is placed at an angle of 70 ㅀ from the bottom, and the ink composition prepared by the present invention is injected into a pen. After taking a circle having a diameter of about 30 cm, the time was measured for how long the written line was completely dried within a few seconds.
○ : 건조 시간이 8초 이하인 경우○: when the drying time is 8 seconds or less
△ : 건조 시간이 9 내지 15초인 경우Δ: when the drying time is 9 to 15 seconds
X : 건조 시간이 16초 이상인 경우X: When the drying time is 16 seconds or more
5) 소거성5) Scavenging
녹색의 칠판용 도료를 도장한 칠판을 수직상태로 놓고 마커펜용 잉크 조성물이 주입된 마커펜으로 나선형의 선을 기재한 다음 초기 소거성은 1일 경과 후, 후기 소거성은 1주일 경과 후에 마커펜용 지우개로 지워지는 상태를 아래의 내용과 같이 육안으로 평가하였다.Place the board painted with the green chalkboard paint in a vertical position, and write a spiral line with a marker pen injected with the ink composition for the marker pen. The erased state was visually evaluated as follows.
○ : 깨끗하게 지워짐○: erased cleanly
△ : 자국이 약하게 남음△: marks remain weak
X : 부분적으로 지워지지 않음X: not partially erased
상기에서 잉크 조성물의 물성을 측정한 결과 실시예의 경우에는 유출성, 분산성, 백색도, 건조성 및 소거성이 모두 우수한 반면에 비교예 1의 경우에는 수용성 합성수지를 제외한 나머지 조성을 실시예의 조성과 동일하게 사용함에도 불구하고, 분산성 및 소거성이 보통 미만인 것으로 나타났다. 또한, 비교예 2의 경우에는 색상안료를 제외한 나머지 조성을 실시예의 조성과 동일하게 사용함에도 불구하고, 잉크 조성물의 점도에 영향을 미치는 색상안료의 사용양이 적정하지 않음에 따라 유출성 및 소거성이 모두 보통인 것으로 평가되었다.As a result of measuring the physical properties of the ink composition as described above, in the case of Example, all of the outflow, dispersibility, whiteness, dryness and scavenging property were excellent, whereas in Comparative Example 1, the rest of the composition except for the water-soluble synthetic resin was the same as the composition of the Example. Despite use, dispersibility and scavenging were found to be less than moderate. In addition, in the case of Comparative Example 2, although the remaining composition except the color pigments is used in the same manner as in the composition of the embodiment, the amount of color pigments affecting the viscosity of the ink composition is not appropriate, so the spillability and the scavenging properties All were rated as normal.
아울러, 비교예 3의 경우에는 증류수의 사용양이 적정하지 않음에 따라 분산성, 백색도, 소거성은 보통이고, 건조성은 보통 미만으로 평가되었다.In addition, in the case of the comparative example 3, dispersibility, whiteness, scavenging property were moderate, and dryness was evaluated as less than moderate as the use amount of distilled water was not appropriate.
따라서, 상기 평가의 결과에 의하면 실시예의 경우에는 모든 물성이 우수한데 반해 비교예 1 내지 3의 경우에는 잉크 조성물의 성분이 적절하게 배합되지 아니하여 실시예에 비해서 품질이 떨어지는 것으로 평가되었다. Therefore, according to the results of the evaluation, in the case of Examples, all the physical properties were excellent, whereas in the case of Comparative Examples 1 to 3, the components of the ink composition were not properly blended, and the quality was evaluated to be inferior to the Examples.
한편, 본 발명에 의한 잉크 조성물은 흑판에 분필과 혼용하여 사용이 가능하다. 이에, 상기 잉크 조성물은 높은 접착강도로 인하여 흑판에 사용되어 소거될 경우 흑판에 잔존하는 분필가루도 제거하는 부가적인 효과를 얻을 수 있다.On the other hand, the ink composition according to the present invention can be used mixed with chalk on the blackboard. Thus, the ink composition may have an additional effect of removing chalk powder remaining on the blackboard when erased by being used in the blackboard due to high adhesive strength.
상기에서 설명한 바와 같이 본 발명은 상기 실시예를 통해 그 물성의 우수성이 입증되었지만 본 발명은 상기의 실시예에 의해서만 반드시 한정되는 것이 아니 고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능하다.As described above, the present invention has proved its superiority through the above embodiments, but the present invention is not necessarily limited only to the above embodiments, and various substitutions may be made without departing from the technical spirit of the present invention. , Modifications and variations are possible.
도 1은 본 발명의 일실시예에 의한 마커펜용 수성 겔 잉크 조성물의 제조 공정을 나타내는 순서도이다. 1 is a flow chart showing the manufacturing process of the aqueous gel ink composition for a marker pen according to an embodiment of the present invention.
Claims (4)