KR20090117522A - Light guiding plate, inc for manufacturing light guiding plate, and manufacturing method of light guiding plate using inkjet printing - Google Patents

Light guiding plate, inc for manufacturing light guiding plate, and manufacturing method of light guiding plate using inkjet printing Download PDF

Info

Publication number
KR20090117522A
KR20090117522A KR1020080043612A KR20080043612A KR20090117522A KR 20090117522 A KR20090117522 A KR 20090117522A KR 1020080043612 A KR1020080043612 A KR 1020080043612A KR 20080043612 A KR20080043612 A KR 20080043612A KR 20090117522 A KR20090117522 A KR 20090117522A
Authority
KR
South Korea
Prior art keywords
guide plate
light
light guide
binder
scattering
Prior art date
Application number
KR1020080043612A
Other languages
Korean (ko)
Other versions
KR100972845B1 (en
Inventor
김종인
정진만
Original Assignee
주식회사 삼한일렉트로닉스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 삼한일렉트로닉스 filed Critical 주식회사 삼한일렉트로닉스
Priority to KR1020080043612A priority Critical patent/KR100972845B1/en
Publication of KR20090117522A publication Critical patent/KR20090117522A/en
Application granted granted Critical
Publication of KR100972845B1 publication Critical patent/KR100972845B1/en

Abstract

PURPOSE: A light guide plate, an ink for manufacturing the light guide plate, and a manufacturing method of the light guide plate using inkjet printing are provided to improve an optical property by controlling orientation of liquid crystal molecules of a liquid crystal layer. CONSTITUTION: A light scattering reflector(20) is formed in a rear surface of a substrate(10). A binder(21) and a scattering particle(22) are mixed in the light scattering reflector. A diameter of the scattering particle is less than 5um. The scattering particle is TiO2 or silica-based nano particle. The binder includes at least one of acryl, urethane, and epoxy resin. Distribution density of the light scattering reflector is enhanced from both sides of the substrate to the center. The binder and the scattering particle are transparently formed.

Description

도광판, 도광판 제조용 잉크 및 잉크젯 프린팅을 이용한 도광판의 제조 방법 {LIGHT GUIDING PLATE, INC FOR MANUFACTURING LIGHT GUIDING PLATE, AND MANUFACTURING METHOD OF LIGHT GUIDING PLATE USING INKJET PRINTING}LIGHT GUIDING PLATE, INC FOR MANUFACTURING LIGHT GUIDING PLATE, AND MANUFACTURING METHOD OF LIGHT GUIDING PLATE USING INKJET PRINTING}

본 발명은 도광판, 도광판 제조용 잉크 및 잉크젯 프린팅을 이용한 도광판의 제조 방법에 관한 것이다.The present invention relates to a light guide plate, an ink for manufacturing a light guide plate, and a manufacturing method of a light guide plate using ink jet printing.

액정 표시 장치는 현재 가장 널리 사용되고 있는 평판 표시 장치로서, 기판에 전기장 생성 전극이 형성된 두 장의 표시판과 그 사이에 들어 있는 액정층을 포함하며, 빛을 공급하기 위한 백라이트 유닛을 구비한다. 액정 표시 장치는 전기장 생성 전극에 전압을 인가하여 액정층의 액정 분자들의 배향을 제어함으로써 백라이트 유닛이 공급하는 빛의 투과량을 조절함으로써 화상을 표시한다. The liquid crystal display is the most widely used flat panel display, and includes two display panels having an electric field generating electrode formed on a substrate and a liquid crystal layer interposed therebetween, and includes a backlight unit for supplying light. The liquid crystal display displays an image by adjusting a transmission amount of light supplied by the backlight unit by applying a voltage to the field generating electrode to control the alignment of liquid crystal molecules of the liquid crystal layer.

이러한 액정 표시 장치의 백라이트 유닛에는 냉음극관(CCFL) 또는 발광 다이오드(LED)가 발하는 빛을 면광으로 변환하기 위한 도광판이 포함된다. 도광판은 측면에서 공급되는 빛을 배면에 형성되어 있는 광산란반사체가 반사하여 정면을 통해 균일하게 배출되도록 한 것이다. The backlight unit of the liquid crystal display includes a light guide plate for converting light emitted from a cold cathode tube (CCFL) or a light emitting diode (LED) into surface light. The light guide plate reflects the light supplied from the side so that the light scattering reflector formed on the rear side reflects the light evenly through the front surface.

이러한 도광판은 광산란반사체 형상이 만들어져 있는 금형에 용융된 액체 상 태의 도광판 재료를 주입하여 제조하는 사출 성형 방법을 사용하거나, 광산란반사체가 없는 도광판을 형성하고 광산란반사체를 스크린 프린팅(screen printing)하는 방법을 통하여 제조한다. Such a light guide plate may be manufactured by injecting molten liquid light guide plate material into a mold in which a light scattering reflector shape is made, or forming a light guide plate without a light scattering reflector and screen printing a light scattering reflector. Manufacture through.

그런데 액정 표시 장치의 경박단소화의 요구가 거세지면서 도광판도 점점 더 얇은 것이 요구되고 있다. 그러나 사출 성형 방법이나 스크린 프린팅 방법에 의하여는 광산란반사체(이후 광산란반사체)를 가지는 도광판을 1mm 이하의 두께로 만들기가 어렵다. 1mm 이하의 사출 성형의 경우 광산란반사체가 너무 작게 되어 원하는 모양으로 균일하게 형성되지 않거나 과도한 응력으로 인해 휨 변형이 발생하여 양산 수율 저하로 인해 생산에 어려움 있고 스크린 프린팅 방법의 경우에는 패턴 사이즈가 200um 이하로 작아지기 때문에 스크린 막힘이나 광산란 반사체 크기의 과도한 편차로 도광판의 광균일성이 나빠서 양산에 적용하기 어려운 문제가 있다. However, as the demand for light and small sized liquid crystal display devices is increasing, thinner light guide plates are required. However, it is difficult to make a light guide plate having a light scattering reflector (hereinafter light scattering reflector) to a thickness of 1 mm or less by an injection molding method or a screen printing method. In case of injection molding of 1mm or less, the light scattering reflector is too small to be uniformly formed in a desired shape, or bending deformation occurs due to excessive stress, which is difficult to produce due to the decrease in mass production yield, and in the case of screen printing method, the pattern size is 200um or less Because of the small size of the light guide plate due to screen clogging or excessive variation in light scattering reflector is bad, there is a problem that is difficult to apply to mass production.

본 발명은 얇고 광 특성이 우수한 도광판 및 그 제조 방법을 제공하고, 이러한 도광판의 제조에 사용되는 잉크를 제공하기 위한 것이다. The present invention is to provide a light guide plate that is thin and excellent in optical properties, and a method of manufacturing the same, and to provide an ink used for manufacturing such a light guide plate.

본 발명의 한 실시예에 따른 도광판은 투명한 기판, 상기 기판의 배면에 형성되어 있으며, 바인더와 산란 입자가 혼합되어 있는 복수의 30Pl 이하의 체적을 가지는 광산란반사체를 포함하고, 상기 산란 입자는 직경이 5㎛ 이하이다.The light guide plate according to the embodiment of the present invention is formed on a transparent substrate, the back surface of the substrate, and includes a light scattering reflector having a plurality of volumes of 30Pl or less, the binder and the scattering particles are mixed, the scattering particles having a diameter It is 5 micrometers or less.

바인더와 상기 산란 입자는 투명하고, 상기 산란 입자의 굴절률은 상기 바인 더의 굴절률에 비하여 0.01 ~ 1.6 만큼 더 클 수 있고, 산란 입자는 TiO2 또는 실리카계 나노 입자일 수 있고, 상기 바인더는 아크릴, 우레탄 및 에폭시 레진 중의 적어도 하나를 포함할 수 있다. 산란 입자는 상기 광산란반사체에 0.1 ~ 20wt% 포함될 수 있고, 상기 기판은 PMMA, PC, PET 등을 포함할 수 있다.The binder and the scattering particles are transparent, the refractive index of the scattering particles may be larger than 0.01 to 1.6 by the refractive index of the binder, the scattering particles may be TiO 2 or silica-based nanoparticles, the binder is acrylic, It may comprise at least one of urethane and epoxy resin. Scattering particles may be included in the light scattering reflector 0.1 ~ 20wt%, the substrate may include PMMA, PC, PET and the like.

광산란반사체는 상기 기판의 상기 제1 측면으로부터 상기 제2 측면으로 갈수록 분포 밀도가 높아질수 있고, 상기 광산란반사체는 상기 기판의 양쪽 측면으로부터 가운데로 갈수록 분포 밀도가 높아질 수 있다.The light scattering reflector may have a high distribution density from the first side to the second side of the substrate, and the light scattering reflector may have a high distribution density toward both sides of the substrate.

본 발명의 한 실시예에 따른 도광판 제조용 잉크는 투명하고, 굴절률이 1.4 ~ 1.6 인 바인더, 상기 바인더에 혼합되어 있고 굴절률이 1.41 ~ 3.0 인 산란 입자를 포함하고, 상기 산란 입자는 직경이 5㎛ 이하이다.The ink for manufacturing a light guide plate according to an embodiment of the present invention is transparent, and includes a binder having a refractive index of 1.4 to 1.6, scattering particles mixed in the binder and having a refractive index of 1.41 to 3.0, wherein the scattering particles have a diameter of 5 μm or less. to be.

산란 입자는 TiO2 또는 실리카계 나노 입자일 수 있고, 상기 바인더는 아크릴, 우레탄 및 에폭시 레진 중의 적어도 하나를 포함할 수 있으며, 상기 산란 입자는 상기 광산란반사체에 0.1 ~ 20wt% 포함될 수 있다.Scattering particles may be TiO 2 or silica-based nanoparticles, the binder may include at least one of acrylic, urethane and epoxy resin, the scattering particles may be included in the light scattering reflector 0.1 ~ 20wt%.

본 발명의 한 실시예에 따른 도광판의 제조 방법은 투명한 기판을 준비하는 단계, 상기 투명한 기판의 일면에 바인더와 산란 입자가 혼합되어 있는 잉크를 잉크젯 프린팅하여 광산란반사체를 형성하는 단계를 포함한다.A method of manufacturing a light guide plate according to an embodiment of the present invention includes preparing a transparent substrate, and forming a light scattering reflector by inkjet printing an ink in which a binder and scattering particles are mixed on one surface of the transparent substrate.

상기 투명한 기판을 준비하는 단계는 압출 성형 또는 사출 성형 방법을 사용하여 진행할 수 있고, 상기 바인더와 상기 산란 입자는 투명하고, 상기 산란 입자의 굴절률은 상기 바인더의 굴절률에 비하여 0.01 ~ 1.6 만큼 더 클 수 있고, 상기 산란 입자는 상기 광산란반사체에 0.1 ~ 20wt% 포함될 수 있으며, 산란 입자는 TiO2 또는 실리카계 나노 입자일 수 있고, 상기 바인더는 아크릴, 우레탄 및 에폭시 레진 중의 적어도 하나를 포함할 수 있다.The preparing of the transparent substrate may be performed using an extrusion or injection molding method, wherein the binder and the scattering particles are transparent, and the refractive index of the scattering particles may be larger by 0.01 to 1.6 than the refractive index of the binder. The scattering particles may be included in the light scattering reflector 0.1 ~ 20wt%, the scattering particles may be TiO 2 or silica-based nanoparticles, the binder may include at least one of acrylic, urethane and epoxy resin.

본 발명의 실시예에 따르면, 얇고 광 특성이 우수한 도광판을 제조할 수 있고, 도광판의 제조 비용을 절감할 수 있다.According to the embodiment of the present invention, a light guide plate that is thin and excellent in optical characteristics may be manufactured, and manufacturing cost of the light guide plate may be reduced.

이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 첨부한 도면을 참고로 하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art may easily implement the present invention. As those skilled in the art would realize, the described embodiments may be modified in various different ways, all without departing from the spirit or scope of the present invention.

도면에서 여러 층 및 영역을 명확하게 표현하기 위하여 두께를 확대하여 나타내었다. 명세서 전체를 통하여 유사한 부분에 대해서는 동일한 도면 부호를 붙였다. 층, 막, 영역, 판 등의 부분이 다른 부분 "위에" 있다고 할 때, 이는 다른 부분 "바로 위에" 있는 경우뿐 아니라 그 중간에 또 다른 부분이 있는 경우도 포함한다. 반대로 어떤 부분이 다른 부분 "바로 위에" 있다고 할 때에는 중간에 다른 부분이 없는 것을 뜻한다.In the drawings, the thickness of layers, films, panels, regions, etc., are exaggerated for clarity. Like parts are designated by like reference numerals throughout the specification. When a part of a layer, film, region, plate, etc. is said to be "on" another part, this includes not only the other part being "right over" but also another part in the middle. On the contrary, when a part is "just above" another part, there is no other part in the middle.

그러면 본 발명의 한 실시예에 따른 도광판에 대하여 도 1 및 도 2를 참고하여 설명한다.Next, a light guide plate according to an exemplary embodiment of the present invention will be described with reference to FIGS. 1 and 2.

도 1은 본 발명의 한 실시예에 따른 도광판의 단면도이고, 도 2는 도 1의 A 부분을 확대한 도면이다.1 is a cross-sectional view of a light guide plate according to an exemplary embodiment of the present invention, and FIG. 2 is an enlarged view of a portion A of FIG. 1.

도 1 및 도 2를 참고하면, 도광판(100) 측면에 발광 다이오드 등의 광원(30)이 배치되어 있다.1 and 2, a light source 30 such as a light emitting diode is disposed on the side of the light guide plate 100.

도광판(100)은 투명한 기판(10)과 투명한 기판(10)의 배면에 형성되어 있는 광산란반사체(20)를 포함한다. 투명한 기판(10)은 PMMA, PC, PET 등의 굴절률이 1.4 ~ 1.6 사이인 물질로 이루어져 있고, 광산란반사체(20)는 바인더(21)와 바인더(21)에 혼합되어 있는 산란 입자(22)를 포함한다. 도광판(100)은 바인더(21)와 산란 입자(22)의 굴절률 차이로 인해 빛이 산란하고, 이를 통해 도광판(100) 측면의 광원(30)로부터 오는 빛의 경로를 바꿔 도광판(100) 정면으로 출사하도록 만든다.The light guide plate 100 includes a transparent substrate 10 and a light scattering reflector 20 formed on the rear surface of the transparent substrate 10. The transparent substrate 10 is made of a material having a refractive index of 1.4 to 1.6, such as PMMA, PC, PET, etc., the light scattering reflector 20 is the scattering particles 22 mixed in the binder 21 and the binder 21 Include. The light guide plate 100 scatters light due to a difference in refractive index between the binder 21 and the scattering particles 22, thereby changing the path of the light coming from the light source 30 on the side of the light guide plate 100 to the front of the light guide plate 100. Make it exit

바인더(21)는 아크릴, 우레탄 또는 에폭시 레진 등의 투명하고 굴절률이 1.4 ~ 1.6 사이인 물질로 이루어져 있고, 산란 입자(22)는 TiO2 또는 실리카계 나노 입자 등의 투명하고 굴절률이 1.41 ~ 3.0 사이인 입자이다. 바인더(21)의 굴절률은 기판(10)의 굴절률과 동일할 수 있다.The binder 21 is made of a transparent and refractive index of 1.4 to 1.6, such as acrylic, urethane or epoxy resin, the scattering particles 22 are transparent and refractive index of 1.41 to 3.0, such as TiO 2 or silica-based nanoparticles Phosphorus particles. The refractive index of the binder 21 may be the same as the refractive index of the substrate 10.

산란 입자(22)는 직경이 5㎛ 이하의 미세한 입자이다. 후술하는 바와 같이, 본 발명의 실시예에서는 잉크젯 프린팅을 사용하여 기판(10) 위에 광산란반사체(20)를 형성한다. 그런데, 산란 입자(22)의 직경이 5㎛를 초과하는 경우에는 잉크젯 프린터의 노즐이 막힐 수 있다.The scattering particles 22 are fine particles having a diameter of 5 μm or less. As will be described later, in the embodiment of the present invention, the light scattering reflector 20 is formed on the substrate 10 using inkjet printing. By the way, when the diameter of the scattering particles 22 exceeds 5 µm, the nozzle of the inkjet printer may be clogged.

또한 산란 입자(22)는 굴절률이 바인더(21)에 비하여 0.01 ~ 1.6 만큼 더 크고, 광산란반사체(20)의 산란 입자(22) 함유 농도는 0.01 ~ 20wt%이다. 바인더(21)와 산란 입자(22)의 굴절률 차이가 0.01 미만인 경우에는 굴절률 차이가 너무 작아서 빛의 산란이 잘 이루어지지 않을 수 있다. 굴절률 차이가 1.6 보다 큰 경우에는 각 산란 입자(22)에 의한 광 산란률이 너무 크고, 광손실이 많아져, 기판(10) 위의 광산란반사체(20)의 분포 밀도를 조절하기 어려울 수 있다. 도 1에 나타낸 바와 같이, 기판(10)은 두께가 일정하고, 광산란반사체(20)는 광원(30)이 배치되어 있는 측면으로부터 멀어질수록 분포 밀도가 증가한다. 이는 빛을 발하는 광원(30)과 가까울수록 빛이 강하므로 광산란반사체(20)의 밀도를 낮게 형성하여 반사량을 줄이고, 멀수록 광산란반사체(20)의 밀도를 높게 형성하여 반사량을 증가시킴으로써 도광판(100)의 정면으로 출사하는 광을 균일하게 만들기 위함이다. 그런데 광산란반사체(20) 각각의 광 반사량이 너무 많으면, 광원(30)과 인접한 부분에서는 광산란반사체(20)의 밀도는 매우 작게 형성해야 하는데, 광산란반사체(20)가 반사하는 빛이 강해서 액정 표시 장치의 화면에 밝은 점으로 나타날 수 있다. 따라서, 광산란반사체(20) 각각의 광 반사율을 적당한 범위로 조절할 필요가 있는데, 산란 입자(22)와 바인더(21)의 굴절률 차이를 0.01 ~ 1.6로 하고, 산란 입자(22)의 함유 농도를 0.1 ~ 20 wt%로 함으로써 광산란반사체(20) 각각의 광 반사율을 적당한 범위로 조절할 수 있다. 예를 들어, 굴절률이 1.5인 아크릴레진 바인더(21)로 하고 굴절률이 1.55인 SiO2 입자를 산란 입자(22)로 할 수 있다. 광산란 반사체(20)의 체적은 30Pl(피코리터) 이하일 수 있다.In addition, the scattering particles 22 have a refractive index larger than that of the binder 21 by 0.01 to 1.6, and the scattering particles 22 containing concentration of the light scattering reflector 20 is 0.01 to 20 wt%. When the difference between the refractive indices of the binder 21 and the scattering particles 22 is less than 0.01, the difference in the refractive indices may be too small to scatter light. If the difference in refractive index is greater than 1.6, the light scattering rate by each scattering particle 22 may be too large and the light loss may increase, making it difficult to control the distribution density of the light scattering reflector 20 on the substrate 10. As shown in FIG. 1, the substrate 10 has a constant thickness, and the light scattering reflector 20 increases in distribution density as it moves away from the side where the light source 30 is disposed. Since the light is stronger as the light source 30 emits light, the density of the light scattering reflector 20 is lowered to decrease the reflection amount, and the light scattering plate 100 is increased by increasing the density of the light scattering reflector 20 to increase the reflection amount. This is to make the light emitted from the front of the panel uniformly. However, if the amount of light reflection of each of the light scattering reflector 20 is too large, the density of the light scattering reflector 20 should be formed very small in the portion adjacent to the light source 30, but the light reflected by the light scattering reflector 20 is strong and the liquid crystal display device is strong. May appear as bright dots on the screen. Therefore, it is necessary to adjust the light reflectance of each of the light scattering reflectors 20 to an appropriate range, the difference in refractive index between the scattering particles 22 and the binder 21 is 0.01 ~ 1.6, the concentration of the scattering particles 22 is 0.1 By setting it at 20 wt%, the light reflectance of each of the light scattering reflectors 20 can be adjusted to an appropriate range. For example, SiO 2 particles having a refractive index of 1.5 and an acryl resin binder 21 having a refractive index of 1.55 can be used as scattering particles 22. The volume of the light scattering reflector 20 may be equal to or less than 30 Pl (picoliter).

이상과 같이, 바인더(21)에 산란 입자(22)를 혼입하여 광산란반사체(20)를 형성하면, 광산란반사체(20)의 모양이 다소 일정하지 않더라도 체적이 일정하기 때문에 광산란반사체(20)의 광 반사율은 거의 달라지지 않는다. 따라서 광산란반사체(20)를 형성하기가 용이하다. 또한, 광산란반사체(20)를 잉크젯 프린팅 방법으로 형성할 수 있어서, 도광판(100)을 1mm 이하의 두께로 매우 얇게 만들 수 있다.As described above, when the scattering particles 22 are mixed into the binder 21 to form the light scattering reflector 20, the light of the light scattering reflector 20 is constant because the volume of the light scattering reflector 20 is constant even though the shape of the light scattering reflector 20 is not somewhat constant. The reflectance hardly varies. Therefore, it is easy to form the light scattering reflector 20. In addition, since the light scattering reflector 20 can be formed by an inkjet printing method, the light guide plate 100 can be made very thin with a thickness of 1 mm or less.

도 3은 본 발명의 다른 실시예에 따른 도광판의 단면도이다.3 is a cross-sectional view of a light guide plate according to another embodiment of the present invention.

도 3의 도광판(100)은 두께가 균일하고, 광산란반사체(20)의 분포 밀도가 기판(10)의 양측면으로부터 중앙에 가까워질수록 높아진다. 이는 도광판(100)의 양측면 모두에 광원(31, 32)이 배치되어 있기 때문이다. 기타 광산란반사체(20)나 기판(10)의 특성들은 도 1 및 2이 실시예에서 설명한 바와 같다.The light guide plate 100 of FIG. 3 has a uniform thickness, and increases as the distribution density of the light scattering reflector 20 approaches the center from both sides of the substrate 10. This is because the light sources 31 and 32 are disposed on both side surfaces of the light guide plate 100. The characteristics of the other light scattering reflector 20 or the substrate 10 are as described with reference to FIGS. 1 and 2.

그러면, 이러한 도광판(100)을 제조하는 방법을 설명한다.Next, a method of manufacturing the light guide plate 100 will be described.

도 4는 본 발명의 한 실시예에 따라 도광판을 제조하는 과정 중의 한 단계를 나타내는 공정 단면도이다.4 is a cross-sectional view illustrating a step in a process of manufacturing a light guide plate according to an embodiment of the present invention.

먼저, 투명한 기판(10)을 준비한다. 투명한 기판(10)은 압출 성형 또는 사출 성형 등의 방법으로 제조할 수 있다.First, the transparent substrate 10 is prepared. The transparent substrate 10 can be manufactured by a method such as extrusion molding or injection molding.

다음, 산란 입자와 바인더가 혼합되어 있는 광산란반사체 형성용 잉크 카트리지를 장착한 잉크젯 프린터(200)를 사용하여 기판(10) 위에 광산란반사체를 인쇄한다. 기판(10) 위에 토출된 광산란반사체 액적(2)은 용제를 포함할 수 있고, 이 경우에는 용제가 휘발하고 남은 것이 광산란반사체를 형성한다. 여기서, 광산란반 사체 형성용 잉크가 포함하는 바인더와 산란 입자는 앞서 설명한 바와 같은 특성을 가진다.Next, the light scattering reflector is printed on the substrate 10 using an inkjet printer 200 equipped with an ink cartridge for forming a light scattering reflector in which scattering particles and a binder are mixed. The light scattering reflector droplets 2 discharged onto the substrate 10 may contain a solvent, in which case the solvent volatilizes and the light scattering reflector forms. Here, the binder and scattering particles included in the light scattering reflector forming ink have the same characteristics as described above.

이상과 같이, 본 발명의 실시예에 따르면 잉크젯 프린팅 방법으로 30pL 이하 체적의 광산란반사체를 형성하므로 도광판의 두께를 충분히 얇게 할 수 있고, 도광판의 제조가 용이하게 되어 제조 비용을 절감할 수 있다.As described above, according to the embodiment of the present invention, since the light scattering reflector having a volume of 30 pL or less is formed by the inkjet printing method, the thickness of the light guide plate can be made sufficiently thin, and the manufacturing of the light guide plate can be facilitated, thereby reducing the manufacturing cost.

이상에서 본 발명의 바람직한 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다. Although the preferred embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and improvements of those skilled in the art using the basic concepts of the present invention defined in the following claims are also provided. It belongs to the scope of rights.

도 1은 본 발명의 한 실시예에 따른 도광판의 단면도이고, 1 is a cross-sectional view of a light guide plate according to an embodiment of the present invention,

도 2는 도 1의 A 부분을 확대한 도면이고,FIG. 2 is an enlarged view of a portion A of FIG. 1;

도 3은 본 발명의 다른 실시예에 따른 도광판의 단면도이고,3 is a cross-sectional view of a light guide plate according to another embodiment of the present invention;

도 4는 본 발명의 한 실시예에 따라 도광판을 제조하는 과정 중의 한 단계를 나타내는 공정 단면도이다.4 is a cross-sectional view illustrating a step in a process of manufacturing a light guide plate according to an embodiment of the present invention.

<도면 부호의 설명> <Description of Drawing>

100: 도광판 30, 31, 32: 광원100: light guide plate 30, 31, 32: light source

10: 투명 기판 20: 광산란반사체10: transparent substrate 20: light scattering reflector

21: 바인더 22: 산란 입자21: binder 22: scattering particles

200: 잉크젯 프린터 2: 광산란반사체 액적200: inkjet printer 2: light scattering reflector droplets

Claims (18)

투명한 기판,Transparent substrate, 상기 기판의 배면에 형성되어 있으며, 바인더와 산란 입자가 혼합되어 있는 복수의 30Pl 이하의 체적을 가지는 광산란반사체A light scattering reflector formed on the back surface of the substrate and having a plurality of volumes of 30 Pl or less in which a binder and scattering particles are mixed. 를 포함하고, 상기 산란 입자는 직경이 5㎛ 이하인 도광판.Wherein the scattering particles have a diameter of 5 μm or less. 제1항에서,In claim 1, 상기 바인더와 상기 산란 입자는 투명하고, 상기 산란 입자의 굴절률은 상기 바인더의 굴절률에 비하여 0.01 ~ 1.6 만큼 더 큰 도광판.The binder and the scattering particles are transparent, the refractive index of the scattering particles is larger than the refractive index of the binder by a light guide plate 0.01 ~ 1.6. 제2항에서,In claim 2, 상기 산란 입자는 TiO2 또는 실리카계 나노 입자인 도광판.The scattering particles are TiO 2 or silica-based nanoparticles light guide plate. 제3항에서,In claim 3, 상기 바인더는 아크릴, 우레탄 및 에폭시 레진 중의 적어도 하나를 포함하는 도광판.The binder includes at least one of acrylic, urethane and epoxy resin. 제4항에서,In claim 4, 상기 산란 입자는 상기 광산란반사체에 0.1 ~ 20wt% 포함되어 있는 도광판.The scattering particle is a light guide plate 0.1 to 20wt% contained in the light scattering reflector. 제5항에서, In claim 5, 상기 기판은 PMMA, PC, PET 등을 포함하는 도광판.The substrate is a light guide plate including PMMA, PC, PET and the like. 제1항에서, In claim 1, 상기 광산란반사체는 상기 기판의 상기 제1 측면으로부터 상기 제2 측면으로 갈수록 분포 밀도가 높아지는 도광판.The light scattering reflector is a light guide plate having a higher distribution density from the first side to the second side of the substrate. 제1항에서, In claim 1, 상기 광산란반사체는 상기 기판의 양쪽 측면으로부터 가운데로 갈수록 분포 밀도가 높아지는 도광판.The light scattering reflector is a light guide plate with a higher distribution density toward both sides from the sides of the substrate. 투명하고, 굴절률이 1.4 ~ 1.6 인 바인더,Transparent, the binder having a refractive index of 1.4 to 1.6, 상기 바인더에 혼합되어 있고 굴절률이 1.41 ~ 3.0 인 산란 입자Scattering particles mixed in the binder and having a refractive index of 1.41 to 3.0 를 포함하고, 상기 산란 입자는 직경이 5㎛ 이하인 도광판 제조용 잉크.Wherein the scattering particles have a diameter of 5 μm or less. 제9항에서,In claim 9, 상기 산란 입자는 TiO2 또는 실리카계 나노 입자인 도광판 제조용 잉크.The scattering particles are TiO 2 or silica-based nanoparticles for manufacturing a light guide plate. 제10항에서,In claim 10, 상기 바인더는 아크릴, 우레탄 및 에폭시 레진 중의 적어도 하나를 포함하는 도광판 제조용 잉크.The binder is an ink for manufacturing a light guide plate containing at least one of acrylic, urethane and epoxy resin. 제11항에서,In claim 11, 상기 산란 입자는 상기 광산란반사체에 0.1 ~ 20wt% 포함되어 있는 도광판 제조용 잉크.The scattering particles, the light guide plate manufacturing ink contained in the light scattering reflector 0.1 ~ 20wt%. 투명한 기판을 준비하는 단계,Preparing a transparent substrate, 상기 투명한 기판의 일면에 바인더와 산란 입자가 혼합되어 있는 잉크를 잉크젯 프린팅하여 광산란반사체를 형성하는 단계Forming a light scattering reflector by inkjet printing an ink in which a binder and scattering particles are mixed on one surface of the transparent substrate; 를 포함하는 도광판의 제조 방법.Method of manufacturing a light guide plate comprising a. 제13항에서,In claim 13, 상기 투명한 기판을 준비하는 단계는 압출 성형 또는 사출 성형 방법을 사용하여 진행하는 도광판의 제조 방법.Preparing the transparent substrate is a method of manufacturing a light guide plate to proceed using an extrusion molding or injection molding method. 제14항에서,The method of claim 14, 상기 바인더와 상기 산란 입자는 투명하고, 상기 산란 입자의 굴절률은 상기 바인더의 굴절률에 비하여 0.01 ~ 1.6 만큼 더 큰 도광판의 제조 방법.And the binder and the scattering particles are transparent, and the refractive index of the scattering particles is larger by 0.01 to 1.6 than the refractive index of the binder. 제15항에서,The method of claim 15, 상기 산란 입자는 상기 광산란반사체에 0.1 ~ 20wt% 포함되어 있는 도광판의 제조 방법.The scattering particles are a method of manufacturing a light guide plate is contained in the light scattering reflector 0.1 ~ 20wt%. 제16항에서,The method of claim 16, 상기 산란 입자는 TiO2 또는 실리카계 나노 입자인 도광판의 제조 방법.The scattering particles are TiO 2 or silica-based nanoparticles manufacturing method of the light guide plate. 제17항에서,The method of claim 17, 상기 바인더는 아크릴, 우레탄 및 에폭시 레진 중의 적어도 하나를 포함하는 도광판의 제조 방법.The binder is a method of manufacturing a light guide plate comprising at least one of acrylic, urethane and epoxy resin.
KR1020080043612A 2008-05-09 2008-05-09 Light guiding plate, inc for manufacturing light guiding plate, and manufacturing method of light guiding plate using inkjet printing KR100972845B1 (en)