KR20090107469A - Loess composit and loess brick - Google Patents

Abstract

PURPOSE: A loess composition and loess bricks are provided to prevent the loess bricks from being collapsed when they absorb moisture. CONSTITUTION: A loess composition is composed of 60-90vol% loess, 10-40vol% wooden pieces or rice bran, and cement and water. The cement is composed of 70-95wt% loess and 5-30wt% cement. The wooden pieces are slices of timber. The rice bran indicates general rice bran. The loess exhibits effect of emitting far infrared rays as well as antibiotic, dehumidification, and deodorization function. The loess bricks are made of loess composition.

Description

황토조성물과 황토벽돌 {LOESS COMPOSIT AND LOESS BRICK}Loess composition and loess bricks {LOESS COMPOSIT AND LOESS BRICK}

본 고안에 따른 황토조성물과 황토벽돌은 황토 60∼90 체적％와: 목재 세편 또는 왕겨 10∼40 체적％에 시멘트(황토 70∼95 무게％에 시멘트 5∼30 무게％)와 물의 혼합으로 이루어진 조성물로, 이와 같이 제작되어 지는 황토 조성물은 점도를 희석시켜주어 황토벽돌을 형상화하는데 어려움이 없고, 아울러 황토의 단점인 양생 후 균열이 전혀 발생하지 않으며, 이와 같이 제작된 황토벽돌은 순수한 황토와 목재 세편 또는 왕겨 및 소량의 시멘트의 혼합으로만 형성되어 순수한 황토 고유의 효과와 효능을 최대한 발휘할 수 있을 뿐 아니라, 황토와 혼합되어 지는 목재 세편 또는 왕겨는 시간이 흐름에도 변함이 없이 자연 그대로 유지하고 있어서 건축의 내 외장용 벽돌로 사용할 시에, 황토의 특성인 다량의 원적외선을 방출하고, 목재 세편 또는 왕겨의 작용으로 인하여 열전도성 및 축열성이 우수하며 탈취, 탈습, 항균 작용 등을 하여 각종 유해 독성을 정화 및 차단하여주며 유해 전자파를 차단하여주고, 아울러 목재 세편 또는 왕겨를 혼합하여 방음 및 방충의 효과가 있으며, 또한 단열효과가 아주 뛰어나 에너지 절감 및 건강증진에 크게 기여할 수 있어, 각종 유해 건축자재의 대체 건축자재로 활용함으로서 유해 건축자재의 생산과 폐기 시에 유발하는 공해를 줄여주고, 아울러 본 고안으로 개발된 황토벽돌은 생산과 폐기시 에 공해를 전혀 발생하지 않는다. 또한 일반적인 시멘트 벽돌이나 콘크리트 등 다른 건축자재 보다 크기기준으로 무게를 최대 20％까지 줄일 수 있는 특징을 가지고 있어 건축에서 차지하고 있는 건축물의 하중을 줄여주는 효과가 있을 뿐 아니라, 강도가 매우 높은 다 기능성 황토벽돌에 관한 것으로서, 최근 대두 되고 있는 유해 독성이 많은 시멘트벽돌이나 기타 건축자재의 대체 건축 내 외장재로 제공하여 우리 환경을 각종 건축자재의 공해로부터 벗어나서 보다 쾌적한 환경을 만들어주어 우리 생활 및 건강증진에 이바지하는데 그 목적이 있다.The ocher composition and the ocher brick according to the present invention consist of a mixture of 60 to 90% by volume of ocher and 10 to 40% by volume of wood shreds or rice husks (70 to 95% by weight of clay and 5 to 30% by weight of cement) and water. As such, the ocher composition produced in this way has no difficulty in shaping the ocher brick by diluting the viscosity, and also does not cause cracking after curing, which is a disadvantage of the ocher, and the ocher brick thus manufactured is pure ocher and wood chips. Or, it is formed only by mixing chaff and a small amount of cement to maximize the inherent effect and efficacy of pure ocher, as well as wood pieces or chaff mixed with ocher remain unchanged over time. When used as an interior brick of the house, it emits a large amount of far-infrared rays characteristic of ocher, and the action of wood chips or chaff Due to its excellent thermal conductivity and heat storage, it deodorizes, dehumidifies, and antibacterial to purify and block various harmful toxicities, blocks harmful electromagnetic waves, and also mixes wood chips or rice husks with soundproofing and insect repellent effect. In addition, it has excellent thermal insulation effect, which can greatly contribute to energy saving and health promotion, and can be used as an alternative building material for various harmful building materials to reduce pollution caused during the production and disposal of hazardous building materials, and also developed by the present invention. The old ocher brick produces no pollution during production and disposal. In addition, it can reduce weight by up to 20% on the basis of size than other building materials such as cement brick or concrete, which not only reduces the load of the building occupied in construction, but also has high strength and multifunctional loess. As a brick, it provides the exterior materials in the construction of alternative bricks and other building materials, which are emerging as toxic and harmful, and contributes to the improvement of our lives and health by making our environment free from the pollution of various building materials. Its purpose is to.

황토는 본 고안의 실시 예에 따른 황토벽돌의 주요한 구성 성분으로서, 야산이나 밭에서 흔히 채취가 가능 하지만 지역에 따라서 황토의 성분에 약간의 차이가 있는데, 보통 황토는 입경이 0.002∼0.005mm 정도의 입자들로 이루어져 물속에서 분산되어 콜로이드화되며, 물이 증발되면 단단하게 굳는 특성이 있어, 황토만으로 건축자재로 활용하는데 많은 어려움이 있는데, 그것은 황토가 가지고 있는 장점이자 단점인 높은 점성 때문인데, 종래에는 높은 점성을 희석시키기 위하여 볏집,시멘트, 석회, 모래 등의 다양한 물질을 혼합하여 황토의 점성을 희석시켜 벽돌을 생산하거나, 높은 압력으로 압축하여 벽돌을 생산하여 왔는데, 그것은 황토의 순수성을 상실하지 않고 황토가 가지고 있는 효과와 효능을 극대화하기 위한 방법으로 많은 사람이 연구개발하여 제품으로 생산하여 사용하고 있는데, 문제는 물을 혼합하지 않고 높은 압력으로 압축한 벽돌은 시간의 경과로 갈라짐과 부스러짐의 현상을 초래하고, 아울러 더 큰 문제는 물을 흡수할 시에 무너져 내리는 결과를 가져왔으 며, 또한 시멘트나, 석회, 모래 등을 혼합하여 생산하고 있는 경우에는, 황토의 단점을 보완하여 높은 강도와 물에 강한 결과는 얻을 수 있었지만, 황토가 가지고 있는 고유의 효과 효능이 상실된 것이다.Ocher is a major constituent of ocher bricks according to an embodiment of the present invention. Although it can be commonly collected in wild mountains or fields, there are some differences in the ocher constituents depending on the region. Usually, ocher has a particle size of 0.002 to 0.005 mm. It is composed of particles, dispersed in water and colloidal, and when water evaporates, it hardens hardly, so it is difficult to use it as a building material only with ocher, which is due to its high viscosity, which is an advantage and disadvantage of ocher. In order to dilute high viscosity, various materials such as crest, cement, lime, sand, etc. are mixed to dilute the viscosity of ocher to produce brick, or to produce brick by compressing at high pressure. Many people research and develop as a way to maximize the effect and efficacy of loess. The problem is that bricks compressed at high pressure without mixing water cause the cracking and chipping over time, and the bigger problem is that they collapse when absorbing water. In the case of producing a mixture of cement, lime, sand, etc., it is possible to compensate for the disadvantages of the yellow soil and obtain high strength and water resistance. It is lost.

상술한 바와 같이 황토의 장점이자 단점인 높은 점성으로 인하여 황토벽돌의 형상화에 어려움이 있어 고안한 방법들인데, 본 고안에서는 실시 예에 따라서 목재 세편 또는 왕겨를 혼합하는데 그것은 황토가 가지고 있는 높은 점성을 희석시켜 주어 벽돌의 형상화의 문제점을 완전히 해소하여주고, 아울러 황토의 단점인 수분의 증발로 인하여 생기는 갈라짐의 현상을 막아주는 중요한 역할을 목재 세편 또는 왕겨가 하며, 소량의 시멘트 혼합은 황토의 단점인 물에 약함을 보완하여주고 성형과정에서 아주 높은 강도를 유지하게 하여준다.As described above, due to the high viscosity, which is an advantage and a disadvantage of loess, it is difficult to shape the loess bricks. In the present invention, the wood pieces or chaff are mixed according to the embodiment. By diluting, it completely solves the problem of the shaping of the brick, and also prevents cracking caused by evaporation of moisture, which is a disadvantage of ocher, and wood chips or chaff, and mixing a small amount of cement is a disadvantage of ocher. It compensates for the weakness of water and maintains very high strength during the molding process.

본 고안에서의 황토벽돌은 황토, 목재 세편 또는 왕겨 및 시멘트와 물이 적정의 비율로 혼합되어 지는바, 이때 목재 세편 또는 왕겨의 혼합되어 지는 양과 입자에 따라서 제품으로 생산되는 황토벽돌은 중량이 상대적으로 낮아지기도 하고, 아울러 강도 또한 높게 나타나는 장점이 있다, 위에서 언급한 종래의 방법으로 생산하여 생기는 모든 문제점을 완전히 해소하는 결과를 얻게 된다.In the present invention, the ocher brick, wood chips or chaff, and cement and water are mixed at an appropriate ratio. At this time, the ocher brick produced as a product according to the amount and particles of wood chips or chaff are mixed in relative weight. In addition, it has the advantage of lowering, and also high strength, it is possible to completely solve all the problems caused by the conventional method mentioned above.

황토는 한반도를 비롯한 중국의 화북지방 황하연안 등 주로 동북아에 집중적으로 분포되어 있지만 일부 북미 등 세계 각지에 분포되어 있다, 황토는 주로 석영을 함유하면서 그 밖에 휘석 각섬석 등을 함유하는 황갈색 석회질로서, 실리카 60 ∼65％, 철분 5∼6％, 알루미나 10∼13％, 마그네슘과 나트륨 각 2％ 내외, 칼리 1.5％, 석회 8％ 내외의 화학적 조성을 가지며, 분해력, 자장력, 흡수력 등이 뛰어나며 인체에 유익한 약성을 갖는 것으로 알려져 왔다. 이에, 예로부터 가옥의 건축자재로서 중요하게 쓰여졌으며, 식기나 기구로 만들어져 생활의 도구로도 활용되었다. 그 뿐 아니라 황토는 해독과 질병 치료에도 탁월한 약효를 가지고 있어 동양의학에서는 중요한 약제로 쓰여 졌다. 그중 대표적인 동양 의서들인 본초강목(本草綱目), 동의보감(東醫寶鑑) 및 향약집성방(鄕藥集成方) 등에는 황토가 본디 색을 지닌 흙으로 약성이 가장 뛰어나 널리 중요하게 쓰이는 것으로서 맛은 달고 독이 없으며 부인병(婦人病)과 소아병(小兒病)에 탁월한 효능이 있다고 기록되어 있으며, 또한 본초강목(本草綱目)의 중수부편에는 황토에 물을 부어 우러나오는 물을 지장(地漿) 또는 토장(土漿)이라 하며, 이는 각종 독을 해독하고 마음을 안정시키는 효능이 있다고 기록되어 있다.Ocher is mainly distributed in Northeast Asia, including the Korean Peninsula and the Yellow River coast of China, but is distributed in some parts of the world such as North America. Ocher is a yellowish brown lime that contains quartz and other hornblende. It has a chemical composition of 60-65%, iron 5-6%, alumina 10-13%, magnesium and sodium 2%, Kali 1.5%, lime 8% and so on. It has been known to have weakness. Therefore, it has been used importantly as a building material of houses since ancient times, and was made of tableware and utensils and used as a tool for living. In addition, ocher has excellent efficacy in treating detoxification and disease, so it has been used as an important medicine in oriental medicine. Among them, the main oriental texts, such as Boncho River, Tongbobogam and Hyangyakseongbang, are the most commonly used clays with the most medicinal properties. It has no poison and is said to have excellent effects on gynecological diseases and pediatric diseases. ), Which is said to have the ability to detoxify the various poisons and stabilize the mind.

최근 들어서는 황토에 대한 과학적 규명에 많은 연구가 이루어져 황토가 다량의 원적외선을 방출하고 유해 전자파를 차단하며, 황토 1g에는 수억 마리의 미생물과 다양한 효소들이 들어있어 이들이 순환작용을 하여 여러 면에서 인체에 매우 유익한 영향을 준다는 것이 과학적으로 입증되고 있다. 이에 황토가 건축자재, 생활용품, 가구, 미용 등에 다양하게 활용되고 있어 그 활용범위는 급속히 늘어나는 추세에 있다.In recent years, many studies have been conducted on scientific research on ocher, and the ocher emits a large amount of far-infrared rays and blocks harmful electromagnetic waves. It has been scientifically proven to have a beneficial effect. As a result, loess is being used in a variety of construction materials, household goods, furniture, and beauty, and its range of use is rapidly increasing.

이에, 순수한 황토는 강한 점성으로 인하여 건축자재로 활용하는데 많은 어려움이 있는데 그중에 물과 혼합되면 높은 점도로 인하여 황토벽돌의 형상화가 용 이하지 않으며, 또한 양생 후에는 표면에 균열이 생기는 등의 단점으로 인하여, 제품화에 많은 어려움이 있었다. 이에, 종래에는 황토의 단점을 보완하기 위하여 황토에 볏집, 시멘트, 석회, 모래 또는 돌가루 등과 같은 제3의 물질을 혼합하여 벽돌을 생산하거나, 물을 혼합하지 않고 높은 압력으로 압축하여 생산하여왔다. 그러나 종래 황토제품들의 경우에는 황토의 혼합 비율이 너무 낮거나, 다른 혼합물들이 황토 고유의 성분과 효과와 효능을 희석시키는 결과를 가져와 황토가 가진 순수한 효과와 효능을 효과적으로 살리지 못하고 있으며, 물을 혼합하지 않고 높은 압력으로 압축하여 생산되는 벽돌은 강도가 높은 것처럼 보이지만 , 시간의 흐름으로 갈라짐과 부스러지는 현상이 나타나며 물을 흡수할 시에 쉽게 무너지는 단점이 있다.Therefore, pure ocher has many difficulties in using it as a building material due to its strong viscosity. Among them, when it is mixed with water, it is not easy to shape the ocher brick due to its high viscosity. Due to this, there were many difficulties in commercialization. Thus, in order to make up for the shortcomings of the yellow soil, the clay has been mixed with a third material such as crest, cement, lime, sand or stone powder to produce bricks or compressed to high pressure without mixing water. . However, in the case of conventional ocher products, the mixing ratio of the loess is too low, or other mixtures result in diluting the inherent ingredients and effects and efficacy of the loess. The brick produced by compressing it without pressure seems to have high strength, but has a disadvantage in that it breaks and crumbles with the passage of time and easily collapses when water is absorbed.

이에, 본 고안은 상술한 바와 같은 종래 황토벽돌 제품의 문제점을 해소할 수 있는 것으로서, 보다 자세 하게는 황토 60∼90 체적％와: 목재 세편 또는 왕겨 10∼40 체적％에 용도에 따라 적정량의 시멘트(황토 70∼95 무게％에 시멘트 5∼30 무게％)와 물의 혼합으로 이루어진 조성물로, 이와 같이 조성되어진 황토 조성물은 황토의 장점이자 단점인 점도를 희석시켜주어 황토벽돌을 형상화하는데 어려움이 없고, 아울러 황토의 단점인 양생 후 균열이 전혀 발생하지 않으며, 이와 같이 제작된 황토벽돌은 순수한 황토와 목재 세편 또는 왕겨 및 소량의 시멘트의 혼합으로만 형성되어 순수한 황토 고유의 효과와 효능을 최대한 발휘할 수 있을 뿐 아니라, 황토와 혼합되어 지는 목재 세편 또는 왕겨는 시간이 흐름에도 변함이 없이 자연 그대로 유지하고 있어서 건축물의 내 외장용 벽돌로 사용할 시에, 황토의 특성인 다량의 원적외선을 방출하고, 혼합되어진 목재 세편 또는 왕겨의 작용으로 인하여 열전도성 및 축열성이 우수하며 탈취, 탈습, 항균 작용 등을 하여 각종 유해 독성을 정화 및 차단하여주며 유해 전자파를 차단하여주고, 아울러 목재 세편 또는 왕겨를 혼합으로 방음 및 방충의 효과 등이 있으며, 또한 단열효과가 아주 뛰어나 에너지 절감 및 건강 증진에 크게 기여할 수 있으며, 각종 유해 건축자재의 대체 건축자재로 활용함으로서 유해 건축자재의 생산과 폐기 시에 발생하는 공해를 줄여주고, 아울러 본 고안으로 개발된 황토벽돌은 일반적인 시멘트 벽돌이나 시멘트 콘크리트 등 다른 건축자재 보다 크기 기준으로 무게를 최대 20％까지 줄일 수 있는 것의 특징을 가지고 있어 건축에서 차지하고 있는 건축물의 하중을 줄여주는 효과가 있을 뿐 아니라, 강도가 매우 높은 다 기능성 황토벽돌로서. 최근 대두 되고 있는 유해 독성이 많은 시멘트벽돌이나 기타 건축자재의 대체 건축용 내 외장재로 제공하여 우리 환경을 보다 쾌적 하게 바꿔주어 각종 건축자재의 공해로부터 벗어나서 쾌적한 환경을 만들어 우리 생활 및 건강증진에 이바지하는데 그 목적이 있다. 또한 본 고안의 황토조성물 및 황토벽돌은 생산과 폐기시에 공해를 발생하지 않을 뿐 아니라, 100％ 재활용이 가능하다.Accordingly, the present invention can solve the problems of the conventional ocher brick products as described above, and more specifically, 60 to 90% by volume of ocher and 10 to 40% by volume of wood shreds or rice hulls, depending on the application of an appropriate amount of cement. (70 to 95% by weight of cement and 5 to 30% by weight of cement) and water, the composition of the ocher composition thus prepared dilutes the viscosity, which is an advantage and disadvantage of ocher, and thus has no difficulty in shaping ocher bricks. In addition, cracks do not occur at all after curing, which is a disadvantage of ocher, and thus the ocher bricks are formed only by mixing pure ocher and wood chips or chaff and a small amount of cement, and thus can exhibit the unique effects and efficacy of pure ocher. In addition, wood chips or chaff mixed with ocher remain unchanged over time. When used as a building's interior brick, it emits a large amount of far-infrared rays, which is characteristic of ocher, and is excellent in thermal conductivity and heat storage due to the action of mixed wood chips or chaff. It cleanses and blocks toxic and blocks harmful electromagnetic waves. It also has the effect of soundproofing and insect repellent by mixing wood chips or chaff. Also, it has excellent thermal insulation effect and can greatly contribute to energy saving and health promotion. By using it as a substitute for building materials, it reduces pollution caused during the production and disposal of hazardous building materials, and the ocher brick developed by this design weighs on the basis of size than other building materials such as cement brick or cement concrete. Features up to 20% reduction in occupancy in construction Not only have the effect that reduces the load of the building, which, with very high strength versatility as ocher brick. As a substitute for cement bricks and other building materials, which have recently emerged as hazardous materials, they can be used as exterior materials for building construction to change our environment more comfortably, creating a pleasant environment away from the pollution of various building materials, and contributing to the improvement of our lives and health. There is a purpose. In addition, the ocher composition and the ocher brick of the present invention do not generate pollution during production and disposal, and are 100% recyclable.

이상에서 상세히 설명한 바와 같이 본 고안에 따른 황토 조성물 및 황토벽돌은 황토와 목재 세편 또는 왕겨 그리고 소량의 시멘트와 물의 혼합으로만 조성되어 황토와 목재 세편 또는 왕겨가 갖는 특유의 효과와 효능을 최대한 발휘할 수 있고, 아울러 높은 압력으로 압축한 타벽돌의 문제점인 갈라짐이나 부스러짐과 물을 흡수 하였을 때 생기는 무너짐도 없는 기능성 황토 조성물 및 황토벽돌인 것이며, 황토벽돌의 형상화 시에 따르는 어려움도 완전히 해소되어 손쉽고 간단한 방법으로 생산이 가능하며, 건조 방법 역시 열을 가하지 않고 태양열에 자연 건조 방식으로 건조하기 때문에, 살아숨쉬는 자연 황토 고유의 효과와 효능은 물론이고 혼합되어지는 목재 세편 또는 왕겨의 특성과 효능도 자연 그대로여서 살아숨쉬는 기능성 황토벽돌인 것이다.As described in detail above, the ocher composition and the ocher brick according to the present invention may be composed of only ocher and wood shreds or chaff and a small amount of cement and water mixed to exhibit the unique effects and efficacy of the ocher and wood shreds or chaff. In addition, it is a functional ocher composition and ocher brick which have no problems of cracking, crushing and absorbing water, which are problems of other bricks compressed at high pressure, and the difficulty of shaping ocher bricks is completely solved. It can be produced by the method, and the drying method does not apply heat, but also dries it by solar drying. Therefore, the characteristics and efficacy of living wood loess or chaff are mixed as well as the inherent effects and effects of natural ocher. It is a functional ocher brick that lives and breathes.

본 고안으로 황토 조성물 및 그 조성물로 제작된 황토벽돌은 그 강도가 높고, 중량을 타제품보다 최대 20％까지 줄여 만들 수 있는 장점이 있어 건축물에서 차지하는 하중의 부담을 그만큼 덜어주어 건축물의 구조 역학에도 커다란 영향을 미치는 다기능의 황토 조성물 및 황토벽돌이며, 기존의 타벽돌과 비교하여 높은 황토 함유량과 살아숨쉬는 자연 황토와 목재 세편 또는 왕겨의 효과로 인하여 다량의 원적외선의 방출은 물론이고 시멘트나 기타 건축자재에서 나오는 독성 및 유해 전자파까지를 차단하여주어 인체에 매우 유익한 장점이 있다. 또한 혼합되어 지는 목재 세편 또는 왕겨의 특성으로 열전도성, 열축열성이 뛰어나 에너지 절약은 물론이고, 방음, 방충의 효과가 우수하며, 아울러 탈취, 탈습, 항균의 효과도 아주 뛰어나는 등의 다양한 기능으로 인하여 우리 건축물의 환경 개선에도 기여하여 건강한 생활환경을 만들어주게 될 것이다.The ocher composition and the ocher brick made of this composition have high strength and can reduce weight by up to 20% compared to other products, thus relieving the load on the building and thus greatly improving the structural dynamics of the building. It is a multifunctional ocher composition and ocher brick that affects, in addition to the release of large amount of far-infrared rays, as well as in the cement or other building materials, due to the effect of high ocher content and living natural ocher and wood chips or chaff compared to other bricks. It is very beneficial to the human body by blocking out toxic and harmful electromagnetic waves. In addition, the characteristics of wood chips or rice husks are mixed, so it has excellent thermal conductivity and heat storage ability, which saves energy, and provides excellent soundproofing and insect repellent effects, as well as excellent deodorization, dehumidification, and antibacterial effects. Therefore, it will contribute to the improvement of the environment of our building and create a healthy living environment.

장점:Advantages:

1. 크기대비 중량이 최대 20％까지 줄여 생산이 가능하여, 건축물의 하중을 줄여주는 효과가 있어 건축구조 역학에도 커다란 영향을 미쳐 건축구조 설계에 변 화가 기대된다.1. It is possible to produce by reducing the weight by up to 20% compared to the size, and it has the effect of reducing the load of the building, and it is expected to change the design of the building structure by having a great influence on the structure structure dynamics.

2. 순수한 황토 함유비율이 매우 높고, 순수한 황토의 성질과 성분을 그대로 유지하고 있어 황토가 가지고 있는 효과와 효능이 매우 높아 다량의 원적외선은 물론이고, 기타 건축자재의 독성과 유해 전자파까지를 차단하는 등 다양한 기능의 황토벽돌로서 인체에 이로운 황토의 효과로 인하여 건강증진에 크게 기여할 수 있다.2. The content of pure ocher is very high, and it retains the properties and ingredients of pure ocher as it is, so the effect and efficacy of ocher is very high. It blocks the toxic and harmful electromagnetic wave of not only a large amount of far infrared rays but also other building materials. It can contribute greatly to health promotion due to the effect of loess that is beneficial to human body as ocher bricks of various functions.

3. 목재 세편 또는 왕겨를 혼합함으로서 열전도성 및 축열성이 매우 우수하여 에너지 절감효과가 매우 높다.3. The mixture of wood chips or rice husks is very good in thermal conductivity and heat storage.

4. 목재 세편 또는 왕겨를 혼합함으로서 탈취와 탈습의 작용이 매우 뛰어나 실내환경을 보다 쾌적 하게 만들어 준다.4. The combination of wood chips or rice husk makes deodorizing and dehumidifying very good, making the indoor environment more comfortable.

5. 목재 세편 또는 왕겨를 혼합함으로서 왕겨가 가지고 있는 특성으로 인하여 방음과 방충의 효과를 동시에 얻을 수 있다.5. By mixing wood chips or rice husks, the characteristics of rice husks can be obtained at the same time.

6. 원자재의 자급자족이 가능하고 수급에도 전혀 영향을 받지 않아 생산비가 아주 저렴하다.6. Self-sufficiency of raw materials is possible and production cost is very low because it is not affected by supply and demand.

7. 혼합되어진 조성물이 천연재이기 때문에 생산과 폐기 시에도 공해를 유발하지 않을 뿐 아니라, 100％ 재활용이 가능하고, 폐기 시에는 자연으로 환원됨은 물론이고 식물이 성장하는데 오히려 이로움을 더해주는 친환경 황토 조성물 및 황토벽돌인 것이다.7. Since the mixed composition is a natural material, it does not cause pollution during production and disposal, and is 100% recyclable, and when it is disposed, it is reduced to nature and eco-friendly ocher composition that adds benefits to plant growth. And ocher bricks.

이와 같이 여러 장점을 가지고 있으며, 또한 생산과 폐기시에 공해를 유발하며, 우리 인체에 유해한 다량의 시멘트 사용을 줄일 수 있을 뿐 아니라, 시멘트 사용에 필요한 모래의 만성 수급 불균형을 미연에 방지하여 주는 대체 효과도 가져오 는 등의 장점을 고루 갖추고 있는 다기능의 황토 조성물 및 황토벽돌인 것이다.This has many advantages, it also causes pollution during production and disposal, and it can reduce the use of large amount of cement that is harmful to human body, and also prevent the chronic supply and demand imbalance of sand required for cement use. It is a multi-functional ocher composition and ocher brick which are equipped with advantages such as effects.

본 고안에 따른 황토벽돌은 황토 60∼90 체적％와, 목재 세편 또는 왕겨 10∼40 체적％와 시멘트(황토 70∼95 무게％에 시멘트 5∼30 무게％)와 물의 혼합으로 이루어진 것을 특징으로 한다. 상술한 바와 같은 구성에 있어서, 상기 황토, 목재 세편 또는 왕겨 및 시멘트의 혼합비율은 벽돌의 크기 및 사용용도에 따라서 구성비를 다르게 하게 되는데, 그것은 제품의 중량 및 강도의 차이 때문이다.The ocher brick according to the present invention is characterized by consisting of a mixture of 60 to 90 volume% of ocher, 10 to 40 volume% of wood shreds or rice husk, cement (70 to 95 weight% of ocher and 5 to 30 weight% of cement) and water. . In the configuration as described above, the mixing ratio of the ocher, wood chips or chaff and cement will vary the composition ratio depending on the size and use of the brick, because of the difference in the weight and strength of the product.

이하, 본 고안에 따른 황토 조성물 및 황토벽돌의 바람직한 실시 예를 보다 자세히 설명하면, 황토는 본 고안의 실시 예에 따른 황토 조성물 및 황토벽돌의 가장 중요한 구성 성분으로서, 야산이나 밭에서 흔히 채취가 가능하지만 지역에 따라서 황토의 성분에 약간의 차이가 있는데, 보통 황토는 입경이 0.002∼0.005mm 정도의 입자들로 이루어져 있으며, 황토는 주로 석영을 함유하면서 그 밖에 휘석 각섬석 등을 함유하는 황갈색 석회질로서, 실리카 60∼65％, 철분 5∼6％, 알루미나 10∼13％, 마그네슘과 나트륨 각 2％ 내외, 칼리 1.5％, 석회 8％ 내외의 화학적 조성을 가지며, 물속에서 분산되어 콜로이드화되며, 물이 증발되면 단단하게 굳는 특성이 있어, 황토만으로 건축자재로 활용하는데 많은 어려움이 있는데 그것은 황토가 가지고 있는 장점이자 단점인 높은 점성 때문이다. 종래에는 황토의 높은 점성을 희석시키기 위하여 볏집, 시멘트, 석회, 모래 등의 다양한 물질을 혼합하여 황토의 점성을 희석시켜 벽돌을 생산하거나, 높은 압력으로 압축하여 생산하는 단계들로 벽돌을 생산하여 왔는데, 물을 혼합하지 않고 높은 압력으로 압축한 벽돌은 시간의 경과로 갈라짐과 부스러짐의 현상을 초래하고, 아울러 더 큰 문제는 물을 흡수할 시에 무너져 내리는 결과를 가져오고 있다.Hereinafter, when the loess composition and the loess brick according to the present invention are described in more detail, the loess is the most important component of the loess composition and the loess brick according to the embodiment of the present invention. However, there is a slight difference in the composition of loess depending on the region. Usually, loess is composed of particles having a particle diameter of 0.002 to 0.005 mm, and loess is a yellowish brown lime that mainly contains quartz and fluorite hornblende. It has a chemical composition of 60 to 65% of silica, 5 to 6% of iron, 10 to 13% of alumina, about 2% of magnesium and sodium, about 1.5% of Kali, and about 8% of lime, and is dispersed and colloided in water to evaporate water. There is a lot of difficulty in using it as a building material with only loess because it is hardly hardened. It is due to the high viscosity. Conventionally, in order to dilute the high viscosity of loess, various materials such as crest, cement, lime, sand, etc. are mixed to produce bricks by diluting the viscosity of loess, or by compressing at high pressure to produce bricks. In other words, bricks compressed at high pressure without mixing of water result in cracking and chipping over time, and the bigger problem is that they collapse when absorbing water.

위에서 설명한 황토의 장점이자 단점인 높은 점성으로 인하여 벽돌의 형상화에 어려움이 있는데, 본 고안에서는 실시 예에 따라 목재 세편 또는 왕겨를 혼합하는데, 목재 세편 또는 왕겨의 혼합은 황토가 가지고 있는 높은 점성을 희석시켜주어 벽돌의 형상화의 문제점을 완전히 해소하여주고, 아울러 황토의 단점인 수분의 증발로 인하여 생기는 갈라짐의 현상을 막아주는 중요한 역할을 목재 세편 또는 왕겨가 하고, 또한 시멘트의 혼합은 황토의 단점인 물에 약함을 보완하여주고 성형과정에서 아주 높은 강도를 유지하게 하여주며, 아울러 물에 담가 놓아도 풀어지지 않아, 시멘트 벽돌 강도 실험 방법인 KS L 4201:2003 실시한 실험 결과 흡수율(％) 17 ∼ 12, 압축강도(N/㎟) 4.46 ∼ 11.36가 나왔다.It is difficult to shape the brick due to the high viscosity, which is an advantage and disadvantage of the ocher described above. In the present invention, the wood chips or chaff are mixed according to the embodiment, and the wood chips or chaff are mixed to dilute the high viscosity of the ocher. It completely solves the problem of the shaping of the brick and prevents cracking caused by evaporation of moisture, which is a disadvantage of ocher, and wood chips or chaff plays an important role. It compensates the weakness and maintains very high strength during the molding process, and it does not release even when immersed in water. As a result of the experiment of cement brick strength test, KS L 4201: 2003, absorption rate (%) 17-12, compression The strengths (N / mm 2) were 4.46 to 11.36.

시험기관 : 전북지방 중소기업청Test organization: Jeonbuk Regional Small and Medium Business Administration

시험기간 : 2007년 10월 31일 ∼ 2007년 11월 16일Test period: October 31, 2007-November 16, 2007

본 고안에서 황토 조성물 및 황토벽돌은 황토, 목재 세편 또는 왕겨 및 시멘트와 물이 적정의 비율로 혼합되여지는바, 이때 혼합되어지는 목재 세편 또는 왕겨의 양과 입자에 따라서 제품으로 생산되는 황토벽돌의 중량이 상대적으로 낮아질 수도 있으며, 시멘트의 혼합량에 따라서 강도 또한 높게 나타나는 장점이 있다, 앞에서 언급한 종래의 방법으로 생산하여 생기는 모든 문제점을 완전히 해소하는 결과를 얻게 된다.-In the present invention, the ocher composition and the ocher brick are mixed with ocher, wood chips or chaff, cement and water at an appropriate ratio, and the weight of the ocher brick produced as a product according to the amount and particles of wood chips or chaff to be mixed. This may be relatively low, and the strength is also high depending on the amount of cement mixed, resulting in completely eliminating all the problems caused by the conventional method mentioned above.

본 발명의 황토벽돌 제조과정은 먼저 오염되지 않은 황토 흙을 채취하고, 채 취한 황토 흙을 자연광에 건조시켜 선별하고, 잘 건조된 목재와 왕겨를 제품의 용도에 맞게 분쇄하여, 믹서기에 황토, 목재 세편 또는 왕겨, 시멘트, 물을 각 제품의 용도에 맞게 균일하게 혼합하여, 성형기에서 제품의 용도에 맞게 형상화시켜 열을 가하지 않고 태양열에 일정 기간 동안 자연 건조시키면, 본 발명의 다 기능성 황토벽돌이 완성된다.The ocher brick manufacturing process of the present invention first collects uncontaminated ocher soil, selects the collected ocher soil by drying it in natural light, and grinds well-dried wood and rice hulls according to the purpose of the product, and in the blender ocher, wood When three pieces or chaff, cement and water are uniformly mixed according to the use of each product, and shaped in accordance with the use of the product in the molding machine and dried naturally for a certain period of time without applying heat, the multifunctional ocher brick of the present invention is completed. do.

Claims (2)

황토 60∼90 체적％와 목재 세편 또는 왕겨 10∼40 체적％와 적정량의 시멘트(황토 70∼95 무게％와 시멘트 5∼30 무게％)와 물의 혼합으로 이루어진 것을 특징으로 만들어진 다 기능성의 황토 조성물 및 황토벽돌Multifunctional ocher composition, characterized in that it consists of a mixture of 60 to 90% by volume of ocher, 10 to 40% by volume of wood chips or chaff, and an appropriate amount of cement (70 to 95% by weight of clay and 5 to 30% by weight of cement) and water; Ocher bricks 제1항에 있어서 목재 세편은 모든 목재 세편을 말하며, 왕겨는 일반적인 왕겨를 말한다.According to claim 1, three pieces of wood refers to all pieces of wood, chaff refers to the general chaff.