KR20090087151A - A fabric for raincoat, a raincoat using that and method of production thereof - Google Patents

A fabric for raincoat, a raincoat using that and method of production thereof Download PDF

Info

Publication number
KR20090087151A
KR20090087151A KR1020080012418A KR20080012418A KR20090087151A KR 20090087151 A KR20090087151 A KR 20090087151A KR 1020080012418 A KR1020080012418 A KR 1020080012418A KR 20080012418 A KR20080012418 A KR 20080012418A KR 20090087151 A KR20090087151 A KR 20090087151A
Authority
KR
South Korea
Prior art keywords
fabric
paper
polyvinyl chloride
film
pattern
Prior art date
Application number
KR1020080012418A
Other languages
Korean (ko)
Inventor
김준상
Original Assignee
김준상
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김준상 filed Critical 김준상
Priority to KR1020080012418A priority Critical patent/KR20090087151A/en
Publication of KR20090087151A publication Critical patent/KR20090087151A/en

Abstract

Cloth for a raincoat, the raincoat using the same, and a manufacturing method thereof are provided to express various patterns on the cloth by bonding transparent polyvinyl chloride film and textile. Cloth for a raincoat is comprised by bonding textile sheet(10) and a transparent polyvinyl chloride film(20). A pattern is printed on one side of the textile. The polyvinyl chloride film is transparent. The polyvinyl chloride film is adhered to the pattern surface of the textile. The pattern surface of the textile is coated with polyurethanes.

Description

우의용 원단 및 이를 이용한 우의 그리고 이의 제작방법 { A fabric for raincoat, A raincoat using that and Method of production thereof }A fabric for raincoat, A raincoat using that and Method of production

본 발명은 우의용 원단 및 이를 이용한 우의 그리고 이의 제작방법에 관한 것으로, 더욱 상세하게는 투명 PVC 필름을 사용하여 직물지에 인쇄된 다양한 무늬가 외부로 드러나도록 하고, PCV 필름과 직물지 사이에 PU 코팅층을 두어 PVC 필름과 직물지 사이의 마찰이 발생하지 않도록 하는 우의용 원단 및 이를 이용한 우의 그리고 이의 제작방법에 관한 것이다.The present invention relates to a fabric for the woof and a method for producing the woof using the same, and more particularly, using a transparent PVC film to be exposed to the various patterns printed on the fabric paper, the PU coating layer between the PCV film and the fabric paper The present invention relates to a fabric for woofer, a woowoo using the same, and a manufacturing method thereof, so that friction between the PVC film and the fabric paper does not occur.

도 1은 종래의 우의용 원단을 도시한 분해 사시도이고, 도 2는 종래의 우의용 원단을 도시한 측 단면도이다.1 is an exploded perspective view showing a conventional right fabric for the right, Figure 2 is a side cross-sectional view showing a conventional right fabric for.

이들 도면에 도시된 바와 같이, 종래의 우의용 원단은 부직포 또는 면과 같은 직물지(1)에 폴리염화비닐(이하 'PVC'라 함) 필름(3)을 접착하여 제작하였다.As shown in these figures, conventional fabrics for woes were made by adhering a polyvinyl chloride (hereinafter referred to as 'PVC') film 3 to a nonwoven fabric or fabric paper 1 such as cotton.

이때, 상기 PVC 필름(3)에 무늬를 인쇄하면, 제작 원가가 높아지고 특히 사용중 인쇄무늬가 벗겨지기 때문에 상기 PVC 필름(3)은 자체적으로 단 색을 갖은 PVC 필름(3)이 사용되었다.In this case, when the pattern is printed on the PVC film 3, the production cost is high, and in particular, since the printed pattern is peeled off during use, the PVC film 3 has a single color PVC film 3 itself.

그러나 상기한 바와 같은 종래기술에서는 다음과 같은 문제점이 있다.However, the prior art as described above has the following problems.

즉, 단 색을 갖은 PVC 필름이 사용되기 때문에 우의에 다양한 무늬를 표현할 수 없는 문제점이 있었다.In other words, since a PVC film having a single color is used, there is a problem in that various patterns cannot be expressed on the right.

따라서 본 발명은 상기와 같은 종래의 문제점을 해결하기 위하여 안출된 것으로, 본 발명의 목적은 투명 폴리염화비닐 필름과 직물지를 접착하여 직물지에 인쇄된 다양한 무늬가 외부에 보이도록 하는 우의용 원단 및 이를 이용한 우의 그리고 이의 제작방법을 제공하는 것이다.Therefore, the present invention has been made to solve the conventional problems as described above, the object of the present invention is to bond the transparent polyvinyl chloride film and the fabric paper, the fabric for the rain to make a variety of patterns printed on the fabric paper and the same It is to provide the use of the woe and its production method.

본 발명의 다른 목적은 상기 폴리염화비닐 필름과 직물지 사이에 폴리우레탄(PU) 코팅층을 두어 직물지와 폴리염화비닐 필름 사이에 마찰에 의해 발생하는 스크레치(초크마크)를 방지하는 우의용 원단 및 이를 이용한 우의 그리고 이의 제작방법을 제공하는 것이다.Another object of the present invention is to place a polyurethane (PU) coating layer between the polyvinyl chloride film and the fabric paper to prevent scratches (choke marks) caused by friction between the fabric paper and the polyvinyl chloride film and using the same To provide a way of making them.

상기한 바와 같은 목적을 달성하기 위한 본 발명의 특징에 따르면, 본 발명은 직물지와 폴리염화비닐 필름이 접착되어 구성되는 우의용 원단에 있어서, 상기 직물지 일면에는 패턴이 인쇄되고; 상기 폴리염화비닐 필름은 투명함을 특징으로 하는 우의용 원단을 포함한다.According to a feature of the present invention for achieving the object as described above, the present invention is a textile fabric and a polyvinyl chloride film is adhered to the fabric for woe, the fabric paper is printed on one surface; The polyvinyl chloride film includes a fabric for the womb characterized in that it is transparent.

이때, 폴리염화비닐 필름은, 상기 직물지의 패턴 인쇄면에 접착된다.At this time, the polyvinyl chloride film is adhered to the pattern printing surface of the fabric paper.

그리고 상기 직물지의 패턴 인쇄면은 폴리우레탄(PU)이 코팅된다.And the pattern printing surface of the fabric paper is coated with polyurethane (PU).

한편, 본 발명은 일면에 패턴이 인쇄된 직물지와, 상기 직물지의 패턴 인쇄면에 접착되는 투명 폴리염화비닐 필름을 포함하고; 상기 직물지의 패턴 인쇄면은 폴리우레탄(PU)이 코팅되는 우의용 원단을 이용하여 제작되는 우의를 포함한다.On the other hand, the present invention comprises a fabric paper with a pattern printed on one side, and a transparent polyvinyl chloride film adhered to the pattern printing surface of the fabric paper; The pattern printing surface of the fabric paper includes a raincoat fabricated using a raincoat fabric coated with polyurethane (PU).

이때, 상기 우의의 이음부는, 상기 우의용 원단을 중첩하여 고주파 접착 방식에 의해 접착된다.At this time, the joint portion of the right is bonded by a high frequency bonding method by overlapping the fabric for the right.

또한, 본 발명은 (A) 직물지에 패턴을 인쇄하는 단계와; (B) 상기 직물지의 패턴 인쇄 면을 폴리우레탄(PU)으로 코팅하는 단계; 그리고 (C) 상기 폴리우레탄 코팅면에 폴리염화비닐 필름을 접착하는 단계를 포함하여 수행되고: 상기 폴리염화비닐 필름은 투명 필름인 우의용 원단의 제작방법을 포함한다.In addition, the present invention comprises the steps of (A) printing a pattern on the woven paper; (B) coating the pattern printing side of the fabric paper with polyurethane (PU); And (C) adhering a polyvinyl chloride film to the polyurethane-coated surface: wherein the polyvinyl chloride film includes a method of manufacturing a fabric for woof which is a transparent film.

위에서 살핀 바와 같은 본 발명에 의한 우의용 원단 및 이를 이용한 우의 그리고 이의 제작방법에서는 다음과 같은 효과를 기대할 수 있다.In the above-described fabric for the woe according to the present invention as described above, and the woe and its manufacturing method using the same, the following effects can be expected.

즉, 투명 폴리염화비닐 필름과 직물지를 접착하여 직물지에 인쇄된 무늬가 외부에 보이도록 하므로, 다양한 무늬가 인쇄된 우의용 원단을 제작할 수 있는 장점이 있다.That is, the transparent polyvinyl chloride film and the fabric paper is bonded so that the printed pattern on the fabric paper is visible to the outside, there is an advantage that can produce a fabric for the womb printed various patterns.

그리고 본 발명은 폴리염화비닐 필름과 직물지 사이에 폴리우레탄(PU) 코팅층이 형성되어 직물지와 폴리염화비닐 필름 사이에 마찰에 의해 스크레치(초크마크)가 발생하지 않는 장점이 있다.In addition, the present invention has an advantage that a polyurethane (PU) coating layer is formed between the polyvinyl chloride film and the woven paper so that scratches (choke marks) do not occur due to friction between the woven paper and the polyvinyl chloride film.

또한, 본 발명은 폴리우레탄 코팅층을 갖는 우비용 원단을 이용하므로, 우비 제작에 있어 이음부의 고주파 접착시 접착력이 우수한 이음부가 형성되는 장점이 있다.In addition, since the present invention uses a non-woven fabric having a polyurethane coating layer, there is an advantage that the joint portion is excellent in the adhesive strength during high-frequency bonding of the joint in the raincoat fabrication.

이하에서는 상기한 바와 같은 본 발명에 의한 우의용 원단의 구체적인 실시 예를 첨부된 도면을 참고하여 상세하게 설명한다.Hereinafter will be described in detail with reference to the accompanying drawings a specific embodiment of the woof fabric according to the present invention as described above.

도 3은 본 발명에 의한 우의용 원단의 구체적인 실시예를 도시한 분해 사시도 이고, 도 4는 본 발명에 의한 우의용 원단의 구체적인 실시예를 도시한 측단면도이다.Figure 3 is an exploded perspective view showing a specific embodiment of the right fabric for the present invention, Figure 4 is a side cross-sectional view showing a specific embodiment of the right fabric for the present invention.

이들 도면에 도시된 바와 같이, 본 발명에 의한 우의용 원단(30)은 직물지(10)와 폴리염화비닐(이하 'PVC'라 한다) 필름(20)이 결합되어 형성된다.As shown in these figures, the woojae fabric 30 according to the present invention is formed by combining the fabric paper 10 and the polyvinyl chloride (hereinafter referred to as 'PVC') film 20.

상기 직물지(10)는 면사 등의 원사로 직조된 면 등의 직물을 말하는 것으로 면 이외에 폴리에스텔 등의 천일 수도 있다. 다만, 본 명세서에서는 설명의 편의상 면인 경우를 예로 들어 설명한다.The woven fabric 10 refers to a woven fabric such as cotton woven from yarn such as cotton yarn, and may be a cloth such as polyester in addition to cotton. In the present specification, for convenience of description, the case will be described as an example.

상기 직물지(10)는 도 4에 확대하여 도시된 바와 같이, 원사가 격자형태로 원사가 짜여져 형성된다.As the textile paper 10 is enlarged in FIG. 4, the yarn is woven in a lattice form.

그리고 상기 직물지(10) 일면(도 4를 기준으로 상면을 말한다)에는 무늬가 인쇄되어 인쇄 층(12)을 형성한다.Then, a pattern is printed on one surface of the fabric paper 10 (refer to the upper surface of FIG. 4) to form a printing layer 12.

상기 무늬의 인쇄는 직물지(10)의 인쇄에 통용되는 다양한 방법에 의한 것일 수 있으므로, 본 명세서에서 그 방법을 상세히 설명하지는 않도록 한다.Since the printing of the pattern may be by various methods commonly used for printing of the woven paper 10, the method will not be described in detail herein.

또한, 상기 무늬는 일정한 패턴일 수도 있고, 꽃무늬 등의 미적 감각을 살릴 수 있는 특정 무늬일 수도 있다.In addition, the pattern may be a predetermined pattern, or may be a specific pattern that can make use of aesthetics such as floral patterns.

그리고, 상기 무늬가 인쇄된 직물지(10)는 폴리우레탄(이하 'PU'라 한다)을 이용하여 코팅되어, PU 코팅층(14)을 형성한다.And, the patterned fabric paper 10 is coated using a polyurethane (hereinafter referred to as "PU"), to form a PU coating layer (14).

상기 PU 코팅방법은, 종래 직물지(10)의 PU 코팅에 사용되는 다양한 코팅방 법이 사용될 수 있다.As the PU coating method, various coating methods used for PU coating of the conventional textile paper 10 may be used.

예를 들면, 대한민국 공개특허 공개번호 제10-2005-0014337에 개시된 바와 같이, 습식 PU 수지에 통상의 첨가제를 혼합하여 PU 코팅용액을 배합하는 단계, 불소 계열의 발수제를 이용하여 발수 처리하는 단계, 천을 몰드에 끼우고 습식 PU 코팅용액에 침지시켜 함침시키는 단계, 함침된 천을 응고조에서 응고와 엠보싱 무늬를 동시에 수행하는 단계, 함침된 천을 온수에서 수세하여 잔류 용제를 추출하는 단계 및 수세한 장갑을 건조로에서 건조시키는 단계를 거쳐 제조하는 방법이 있다.For example, as disclosed in Korean Patent Laid-Open Publication No. 10-2005-0014337, mixing the PU coating solution by mixing a conventional additive with a wet PU resin, a step of water repellent treatment using a fluorine-based water repellent, Impregnating the cloth by placing it in a mold and immersing it in a wet PU coating solution, simultaneously performing solidification and embossing patterns in the coagulation bath, washing the impregnated cloth in hot water, extracting residual solvent, and washing the gloves There is a method of manufacturing through the step of drying in a drying furnace.

또한, 대한민국 특허공보 공고번호 특1998-0000497에 개시된 바와 같이, 분산염료로 염색한 기포를 사용하여 PU코팅시 특별한 조건을 만족시키는 금속산화물 혹은 불화물을 초회 코팅시 사용하여 분산염료의 이염(移染)을 방지케 하는 투습, 방수 PU코팅 가공법이 있다.In addition, as disclosed in Korean Patent Publication No. 1998-0000497, using a bubble dyed with a disperse dye to disperse the dye of the disperse dye by using a metal oxide or fluoride for the first coating when satisfying the special conditions when PU coating Moisture-proof, waterproof PU coating.

그리고 대한민국 공개특허 10-2004-0033852호에 개시된 바와 같이, PU를 롤러를 이용하여 기재 필름상에 도포하여 우레탄 막을 형성하고, 이 우레탄 막 형성단계에서 수득된 PU막 상에 접착제를 도포하여 우레탄필름을 형성한 후, 상기 PU필름의 접착제 층이 원단의 일 측 표면과 접촉하도록 하여 우레탄 막이 가죽원단의 표면상으로 이행되도록 하는 PU가 코팅된 원단의 제조방법 등이 있다.And, as disclosed in Korean Patent Laid-Open Publication No. 10-2004-0033852, PU is coated on a base film using a roller to form a urethane film, and an urethane film is applied by applying an adhesive on the PU film obtained in the urethane film forming step. After the formation, there is a method of manufacturing a PU-coated fabric, such that the adhesive layer of the PU film is in contact with the surface of one side of the fabric so that the urethane film is transferred onto the surface of the leather fabric.

물론, 상기 PU 코팅은 이에 개시되지 않은 당업자 사이에서 통용되는 다양한 코팅방법에 의해 이루어질 수 있다.Of course, the PU coating may be made by various coating methods commonly used among those skilled in the art.

한편, 상기 PU 코팅된 직물지(10)의 코팅층(14) 상면에는 상기 PVC 필름(20)이 접착된다. 상기 PVC 필름(20)의 접착 방법 역시 종래의 직물지에 PVC 필름을 접 착하는 방법과 동일하므로, 그 방법을 본 명세서에서 상세히 설명하지는 않도록 한다.On the other hand, the PVC film 20 is bonded to the upper surface of the coating layer 14 of the PU coated textile paper 10. Since the adhesion method of the PVC film 20 is also the same as the method of bonding a PVC film to a conventional textile paper, the method will not be described in detail herein.

이때, 상기 PVC 필름은 투명한 PVC 필름(20)이다. 또한, 상기 코팅층(14)은 투명층으므로 상기 인쇄 층(12)에 인쇄된 무늬가 투명한 상기 PU 코팅층(14)과 PVC 필름(20)을 통해 외부로 드러나게 되고, 직물지(10)의 무늬가 된다.At this time, the PVC film is a transparent PVC film (20). In addition, since the coating layer 14 is a transparent layer, the pattern printed on the printing layer 12 is exposed to the outside through the transparent PU coating layer 14 and the PVC film 20, and becomes a pattern of the textile paper 10.

여기서, 상기 PU코팅층(14)은 상기 우비용 원단(30)이 구겨지는 경우, 상기 직물지(10)와 PVC 필름(20) 사이에 발생하는 마찰을 방지하는 역할을 한다.Here, the PU coating layer 14 serves to prevent friction generated between the fabric paper 10 and the PVC film 20 when the woofer fabric 30 is wrinkled.

즉, 상기 PU 코팅 없이 인쇄된 직물지(10) 위에 PVC 필름(20)이 직접 접착된 원단(30)을 구길 경우, 상기 직물지(10)가 PVC 필름(20) 저면을 마찰시켜 뿌연 선형 스크래치(이하 '초크마크'라 한다)를 발생시킨다.That is, when the PVC film 20 is directly bonded to the fabric 30 printed on the fabric paper 10 printed without the PU coating, the fabric paper 10 rubs the bottom surface of the PVC film 20 to form a cloudy linear scratch (hereinafter, Is called a chalk mark).

종래 우의용 원단의 경우, 상기 PVC가 투명하지 않은 단색을 띄므로, 외부로 드러나지 않아 문제되지 않았지만, 본 발명에서와 같이, 상기 PVC 필름(20)이 투명한 경우 외부로 드러나 미관을 저해한다.In the case of the conventional fabric for the right, since the PVC is not a transparent color, it is not a problem because it is not exposed to the outside, as in the present invention, when the PVC film 20 is transparent, it is exposed to the outside to hinder aesthetics.

따라서, 상기 PVC 필름(20)이 투명 필름(20)인 경우, 상기 PU 코팅층(14)은 상기 초크 마크의 발생을 방지하는 역할을 한다.Therefore, when the PVC film 20 is a transparent film 20, the PU coating layer 14 serves to prevent the generation of the chalk mark.

이하에서는 본 발명에 따른 우의의 구체적인 실시예를 첨부된 도면을 참조하여 상세하게 설명하기로 한다.Hereinafter, with reference to the accompanying drawings, a specific embodiment of the rain according to the present invention will be described in detail.

도 5는 본 발명에 의한 우의의 구체적인 실시예에를 도시한 예시도이고, 도 6은 본 발명에 의한 우의의 이음부를 확대 도시한 측 단면도이다.5 is an exemplary view showing a specific embodiment of the right according to the present invention, Figure 6 is an enlarged side cross-sectional view showing the joint portion of the right according to the present invention.

이에 도시된 바와 같이, 본 발명에 의한 우의(40)는 일반적인 우의(40)의 형 태와 동일한 형태로 형성된다.As shown in the figure, the raincoat 40 according to the present invention is formed in the same shape as that of the general raincoat 40.

다만, 상기 우의(40)의 원단은 전술한 본 발명에 의한 우의용 원단(30)이 사용된다.However, the fabric of the right 40 is used for the fabric 30 of the right according to the present invention described above.

즉, 본 발명에 의한 우의(40)는 일면에 패턴이 인쇄된 직물지(10)와, 상기 직물지(10)의 패턴 인쇄면에 접착되는 투명 폴리염화비닐 필름(20)을 포함하고, 상기 직물지(10)의 패턴 인쇄면은 폴리우레탄(PU)이 코팅되는 우의용 원단(30)이 이용되어 제작된다.That is, the rain 40 according to the present invention includes a fabric paper 10 having a pattern printed on one surface, and a transparent polyvinyl chloride film 20 bonded to the pattern printing surface of the fabric paper 10, wherein the fabric paper ( The pattern printing surface of 10) is manufactured by using the fabric 30 for womb coated with polyurethane (PU).

또한, 본 발명에 의한 우의(40)는 그 이음부(50)가 원단(30)을 중첩하여 고주파 접착 방식에 의해 접착된다.In addition, the right side 40 according to the present invention is bonded by the high frequency bonding method that the joint 50 overlaps the fabric 30.

즉, 상기 이음부(50)는 두 겹 이상의 원단(30)이 겹쳐진 상태에서, 고온 고압을 이용하여 원단(30)을 접착시킨다. 이는 각 원단(30)에 포함된 PVC 필름(20) 및 PU 코팅층(14)이 고온/고압에 의해 융해되어 상기 직물지(10)를 통과하여 엉겨 붙음에 의해 접착된다.That is, the joint part 50 adheres the fabric 30 by using high temperature and high pressure in a state where two or more fabrics 30 are overlapped. This is because the PVC film 20 and the PU coating layer 14 included in each fabric 30 is melted by the high temperature / high pressure is bonded by tangling through the fabric paper 10.

도 6에 도시된 바와 같이, 3겹의 원단(30)이 겹쳐져 접착되는 경우를 예로 들어 설명하기로 한다.As shown in FIG. 6, a case where three layers of fabrics 30 are overlapped and bonded will be described as an example.

상기 PVC 필름(20)과 PU 코팅층(14)은 녹는 점이 다르다. 즉, 상기 PVC 필름(20)이 상기 PU 코팅층(14) 보다 녹는점이 높다.The PVC film 20 and the PU coating layer 14 is different in melting point. That is, the melting point of the PVC film 20 is higher than that of the PU coating layer 14.

따라서, 상기 PVC 필름(20)이 녹는 온도로 중첩된 원단(30)의 상하를 압착하면, 상층(52) 및 하층(54)의 PVC 필름(20) 및 PU 코팅층(14)이 용융되고, 중간층(56)의 원단(30)은 비교적 용융온도가 낮은 PU 코팅층(14)이 용융되어, 이들 상 하층(52,54) 원단(30)의 PVC 필름(20)/ PU 코팅층(14)과 중간층(54) 원단(30)의 PU 코팅층(14)의 용융체가 엉겨붙어 이음부(50)를 형성한다.Therefore, when the upper and lower portions of the fabric 30 overlapped at the melting temperature of the PVC film 20 are pressed, the PVC film 20 and the PU coating layer 14 of the upper layer 52 and the lower layer 54 are melted, and the intermediate layer is melted. The fabric 30 of 56 is a PU coating layer 14 having a relatively low melting temperature is melted, so that the PVC film 20 / PU coating layer 14 of the upper and lower layers 52 and 54 of the fabric 30 and the intermediate layer ( 54. The melt of the PU coating layer 14 of the fabric 30 is entangled to form the joint 50.

이하에서는 본 발명에 따른 우의용 원단의 제작방법의 구체적인 실시예를 첨부된 도면을 참조하여 상세하게 설명하기로 한다.Hereinafter will be described in detail with reference to the accompanying drawings a specific embodiment of the fabrication method of the woof according to the present invention.

도 7은 본 발명에 의한 우의용 원단을 제작하는 방법을 도시한 흐름도이다.Figure 7 is a flow chart illustrating a method of manufacturing a fabric for woe according to the present invention.

이에 도시된 바와 같이, 본 발명에 의한 우의용 원단은 먼저, 직물지(10)에 무늬를 인쇄하는 것으로부터 시작된다(S10).As shown in this, the fabric for the womb according to the present invention first starts from printing a pattern on the textile paper 10 (S10).

이때, 상기 인쇄방법은 전술한 바와 같다.In this case, the printing method is as described above.

다음으로, 무늬가 인쇄된 직물지(10)에 폴리우레탄(PU)을 이용하여 코팅을 한다(S20).Next, the coating is coated using a polyurethane (PU) on the printed fabric paper 10 (S20).

이때에도, 상기 PU코팅 방법은 전술한 바와 같다.In this case, the PU coating method is as described above.

그리고, 상기 PU 코팅된 직물지(10)의 상기 PU 코팅면에 투명 PVC 필름(20)을 접착시켜 우의용 원단(30)을 완성한다(S30).Then, the transparent PVC film 20 is adhered to the PU coated surface of the PU coated textile paper 10 to complete the fabric 30 for the right (S30).

본 발명의 권리는 위에서 설명된 실시예에 한정되지 않고 청구범위에 기재된 바에 의해 정의되며, 본 발명의 분야에서 통상의 지식을 가진 자가 청구범위에 기재된 권리범위 내에서 다양한 변형과 개작을 할 수 있다는 것은 자명하다.The rights of the present invention are not limited to the embodiments described above, but are defined by the claims, and those skilled in the art can make various modifications and adaptations within the scope of the claims. It is self-evident.

본 발명은 투명 PVC 필름을 사용하여 직물지에 인쇄된 다양한 무늬가 외부로 드러나도록 하고, PCV 필름과 직물지 사이에 PU 코팅층을 두어 PVC 필름과 직물지 사이의 마찰이 발생하지 않도록 하는 우의용 원단 및 이를 이용한 우의 그리고 이 의 제작방법에 관한 것이다. 상기한 바와 같은 본 발명에 의하면, 투명 폴리염화비닐 필름과 직물지를 접착하여 직물지에 인쇄된 무늬가 외부에 보이도록 하므로, 다양한 무늬가 인쇄된 우의용 원단을 제작할 수 있는 장점이 있다.The present invention is to use a transparent PVC film to display a variety of patterns printed on the fabric paper to the outside, and a PU coating layer between the PCV film and the fabric paper to prevent the friction between the PVC film and the fabric paper and using the same And how to make it. According to the present invention as described above, because the transparent polyvinyl chloride film and the fabric paper is bonded so that the printed pattern on the fabric paper is visible to the outside, there is an advantage that can produce a fabric for the womb printed various patterns.

도 1은 종래의 우의용 원단을 도시한 분해 사시도.1 is an exploded perspective view showing a conventional fabric for woes.

도 2는 종래의 우의용 원단을 도시한 측 단면도.Figure 2 is a side cross-sectional view showing a conventional cloth for woes.

도 3은 본 발명에 의한 우의용 원단의 구체적인 실시예를 도시한 분해사시도.Figure 3 is an exploded perspective view showing a specific embodiment of the fabric for woe according to the present invention.

도 4는 본 발명에 의한 우의용 원단의 구체적인 실시예를 도시한 측단면도.Figure 4 is a side cross-sectional view showing a specific embodiment of the woof fabric according to the present invention.

도 5는 본 발명에 의한 우의의 구체적인 실시예에를 도시한 예시도.5 is an exemplary view showing a specific embodiment of the rain according to the present invention.

도 6은 본 발명에 의한 우의의 이음부를 확대 도시한 측 단면도.Fig. 6 is an enlarged side cross-sectional view showing a joint portion of a right according to the present invention.

도 7은 본 발명에 의한 우의용 원단을 제작하는 방법을 도시한 흐름도.7 is a flow chart illustrating a method of manufacturing a fabric for woe according to the present invention.

*도면의 주요 부분에 대한 부호의 설명** Description of the symbols for the main parts of the drawings *

10 : 직물지 12 : 인쇄층10: woven paper 12: printed layer

14 : PU 코팅층 20 : PVC 필름14: PU coating layer 20: PVC film

30 : 원단 40 : 우의30: fabric 40: right

50 : 이음부50: seam

Claims (6)

직물지와 폴리염화비닐 필름이 접착되어 구성되는 우의용 원단에 있어서,In the fabric for woowoo consisting of a bonded fabric and polyvinyl chloride film, 상기 직물지 일면에는 패턴이 인쇄되고;A pattern is printed on one side of the fabric paper; 상기 폴리염화비닐 필름은 투명함을 특징으로 하는 우의용 원단.The polyvinyl chloride film is a woof fabric characterized in that the transparent. 제 1 항에 있어서,The method of claim 1, 폴리염화비닐 필름은,Polyvinyl chloride film, 상기 직물지의 패턴 인쇄면에 접착됨을 특징으로 하는 우의용 원단.The fabric for the woof, characterized in that adhered to the pattern printing surface of the fabric paper. 제 1 항 또는 제 2 항에 있어서,The method according to claim 1 or 2, 상기 직물지의 패턴 인쇄면은 폴리우레탄(PU)이 코팅됨을 특징으로 하는 우의용 원단.The pattern printing surface of the fabric paper is a fabric for woes, characterized in that the coating of polyurethane (PU). 일면에 패턴이 인쇄된 직물지와, 상기 직물지의 패턴 인쇄면에 접착되는 투명 폴리염화비닐 필름을 포함하고;A fabric paper printed with a pattern on one surface, and a transparent polyvinyl chloride film adhered to the pattern printing surface of the fabric paper; 상기 직물지의 패턴 인쇄면은 폴리우레탄(PU)이 코팅되는 우의용 원단을 이용하여 제작됨을 특징으로 하는 우의.The pattern printing surface of the fabric paper is characterized in that the polyurethane (PU) is coated using a fabric for woe. 제 4 항에 있어서,The method of claim 4, wherein 상기 우의의 이음부는,The joint of the right side, 상기 우의용 원단을 중첩하여 고주파 접착 방식에 의해 접착됨을 특징으로 하는 우의.Woo by overlapping the fabric for the Woo is characterized by being bonded by a high frequency bonding method. (A) 직물지에 패턴을 인쇄하는 단계와;(A) printing a pattern on fabric paper; (B) 상기 직물지의 패턴 인쇄 면을 폴리우레탄(PU)으로 코팅하는 단계; 그리고(B) coating the pattern printing side of the fabric paper with polyurethane (PU); And (C) 상기 폴리우레탄 코팅면에 폴리염화비닐 필름을 접착하는 단계를 포함하여 수행되고:(C) attaching a polyvinyl chloride film to the polyurethane coated surface and is performed: 상기 폴리염화비닐 필름은 투명 필름임을 특징으로 하는 우의용 원단의 제작방법.The polyvinyl chloride film is a manufacturing method of the fabric for woes, characterized in that the transparent film.
KR1020080012418A 2008-02-12 2008-02-12 A fabric for raincoat, a raincoat using that and method of production thereof KR20090087151A (en)