KR20090023030A - The manufacturring method of the eco-friendly living vessel - Google Patents
The manufacturring method of the eco-friendly living vessel Download PDFInfo
- Publication number
- KR20090023030A KR20090023030A KR1020080033010A KR20080033010A KR20090023030A KR 20090023030 A KR20090023030 A KR 20090023030A KR 1020080033010 A KR1020080033010 A KR 1020080033010A KR 20080033010 A KR20080033010 A KR 20080033010A KR 20090023030 A KR20090023030 A KR 20090023030A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- mixture
- plate
- mold
- powder
- Prior art date
Abstract
Description
본 발명은 왕겨와 고분자 천연수지를 이용한 생활용기의 견고성을 향상시키고 생산성과 산업성을 향상시키는 친환경생활용기 제조방법에 관한 것으로, 상세하게는 천연섬유질인 왕겨와, 천연 고분자인 전분과, 열경화성 물질인 멜라민수지 및 요소수지와, 실리콘고무 콤파운드 분말과, 천연수지인 셀루로즈와, 탄산나토륨과, 안료를 사용하여 합성수지로 구성되는 용기와 같은 물리적 특성을 갖는 친환경 생활용기 제조방법에 관한 것이다.The present invention relates to a method for manufacturing an environmentally friendly living container that improves the firmness of the living container using chaff and natural polymer resin, and improves productivity and industriality. Specifically, the chaff, which is a natural fiber, starch which is a natural polymer, and a thermosetting material The present invention relates to a method for producing an environmentally friendly living container having physical properties such as a container composed of synthetic resin using phosphorus melamine resin and urea resin, silicone rubber compound powder, natural resin cellulose, sodium carbonate and pigment.
일회용에서 다회용의 생활용기의 사용은 실생활에서 환경적, 사회적, 경제적으로 많은 영향이 있었다.The use of multi-use household containers in single-use had many environmental, social and economic impacts in real life.
정부에서 일회용일 경우 합성수지를 사용할 수 없도록 규제하고 있으나 다 회용 용기는 규제하고 있지 않기 때문에 다 회용 용기라 하더라도 그 용기의 가격이 매우 저렴할 경우 사용 회수에 관계없이 폐기하는 경우가 있으므로 정부의 규제를 피하기 위해 수단에 불과하여 현실적으로는 일회용과 다회용의 구분은 환경적으로, 사회적으로 다르게 구분되지 않습니다. 따라서 일회용 용기와 다회용 용기의 일부는 폐기시 환경에 영향이 되는 환경적 문제와 그 쓰레기를 폐기해야하는 사회적이고 경제적인 문제가 있었다.The government does not regulate the use of synthetic resins for single use, but the multi-use containers are not regulated, so even if they are very cheap, they may be disposed of regardless of the number of times they are used. In reality, the distinction between disposable and multi-use is not environmentally and socially different. Therefore, some of the disposable containers and multi-use containers have environmental problems that affect the environment at the time of disposal and social and economic problems that require disposal of the waste.
일반적으로 정부에서 규제하고 있는 일회용 또는 다회용 용기는 자판기에서 사용하는 종이컵, 폴리에칠렌으로 구성된 합성수지컵, 발포수지로 구성된 라면 컵, 발포수지로 구성된 사각트레이, 발포수지로 구성된 접시 등으로 구분할 수 있다.Disposable or multi-use containers regulated by the government are generally classified into paper cups used in vending machines, synthetic resin cups made of polyethylene, ramen cups made of foamed resin, rectangular trays made of foamed resin, and plates made of foamed resin.
상기 폴리에칠렌으로 구성된 컵을 제외하면 일회용이라 할 수 있고, 폴리에칠렌 컵의 경우도 정부규제를 우회하기 수단이지만 일반적으로 일 회만 사용하기 때문에 일회용용기가 가지는 문제점과 동일한 문제점이 있었다.Except for the cup made of polyethylene, it may be referred to as disposable, and in the case of polyethylene cup, it is a means of bypassing government regulations, but generally there is a problem similar to the problem of having a disposable container because it is used only once.
정부규제를 피하기 위해 전분으로 구성된 컵 등이 있으나 전분은 수용성 물질이기 때문에 방습이 필요한 용기로는 사용할 수 없으므로 사용에 제한이 있는 문제 점이 있으며, 전분용기에 방습을 목적으로 폴리에칠렌수지를 피복 하는 경우가 있으나 폴리에칠렌은 생분해가 어렵기 때문에 정부의 규제에 해당한다 할 수 있었고, 종이 등에 폴리에칠렌으로 피복 하여 컵, 접시, 트레이 등을 생산하고 있으나 이 또한, 정부규정에 해당할 뿐 아니라 강도가 현저하게 떨어지기 때문에 용기의 기능을 온전히 발휘할 수 없는 문제점이 있었다.In order to avoid government regulation, there are cups made of starch, but starch is a water-soluble substance, so it cannot be used as a container that requires moisture proof. However, since it is difficult to biodegrade, it could be said to be a government regulation. It is coated with polyethylene on paper to produce cups, plates, trays, etc. This also corresponds to government regulations, and its strength is significantly lowered. Therefore, there was a problem that can not fully exhibit the function of the container.
전분과 생분해성 합성수지를 혼용하여 용기를 구성하는 경우가 있으나, 생분해성 합성수지를 저렴하게 생산할 수 있는 기술이 아직 미치지 못하여 용기의 원가 상승 때문에 일회용으로는 그 실시와 유통에 한계가 있었다.In some cases, a container may be formed by mixing starch and biodegradable synthetic resin. However, since the technology for producing biodegradable synthetic resin at a low price is still insufficient, the implementation and distribution of the container was limited due to the increase in the cost of the container.
이건 출원인이 실시하고 있는 특허 제660068(천연플라스틱제조방법, 이하 인용특허라 합니다.)호의 기술인 왕겨와 전분과 멜라민수지와 물의 혼합비를 적용하 고 각종 생활용기를 얻도록 구성되어 있으나, 인용특허에서 주성분은 왕겨이므로 전분의 함유량은 적을 뿐 아니라, 전분은 내수성이 약하므로 내수성을 강하게 하기 위해 고분자 구조인 멜라민수지를 사용하였다.It is configured to apply various mixing ratios of chaff, starch, melamine resin and water, which is the technology of Patent No. 660068 (natural plastic manufacturing method, hereinafter referred to as patent), which is applied by the applicant, Since the main component is rice husk, not only starch content is low, but starch is weak in water resistance, and thus, melamine resin, which is a polymer structure, is used to increase water resistance.
인용특허에서 사용하는 멜라민수지는 열경화성 수지로서 수용성이기 때문에 멜라민수지가 물에 수용되면 고분자 구조에서 저 분자 구조로 변형되어 분자의 결합성과 점액질 성이 저하되고 왕겨와 전분과 멜라민수지의 혼합물에 의해 용기가 성형 되더라도, 특히 용기의 두께가 엷은 용기의 경우, 전체적 또는 부분적으로 휨, 크랙, 저강도 등이 현저하게 발생하므로 인용특허의 실시에서 생산성과 산업성을 얻을 수 없었다. Since the melamine resin used in the cited patent is water-soluble as a thermosetting resin, when the melamine resin is contained in water, it is transformed from the polymer structure into the low molecular structure, thereby decreasing the binding and mucus properties of the molecule, and the container by the mixture of chaff, starch and melamine resin. Even in the case of molding, especially in the case of a thin container, since warpage, cracks, low strength, etc., remarkably occur in whole or in part, productivity and industrial performance could not be obtained in the practice of the cited patent.
용기의 성형시간과 건조시간을 단축하기 위한 인용특허의 왕겨와 전분과 멜라민수지와 물의 혼합비에서 물의 혼합비가 적은 상태로 성형할 때, 고압(5~10㎏/㎠)이 필요하므로 한 개의 프레스에 여러 개의 성형기를 장착할 수 없는 문제점이 있고 한 개의 프레스에 여러 개의 성형기를 장착할 경우 그 크기와 규모에 의한 비용과 설치 장소에 한계가 있었다.In order to reduce the molding time and drying time of the container, the high pressure (5 ~ 10㎏ / ㎠) is required when molding in a state where the water mixing ratio is small at the mixing ratio of the chaff, starch, melamine resin and water. There is a problem that can not be equipped with a plurality of molding machines and when mounting a plurality of molding machines in one press there was a limit in the cost and installation site by the size and size.
본 발명은 농산물 폐기물을 재활용하여 생활용기를 제조하며 제조되는 용기의 불량률을 저하시키며 생산성을 향상시키는데 목적이 있다.The present invention aims to reduce the defect rate of the container produced by recycling agricultural wastes and to improve the productivity.
본 발명은 전분 40중량%와 멜라민수지 또는 요소수지 30중량%와, 실리콘고무 콤파운드(silicone rubber compounds)분말 15중량%와, 셀루로스(cellulose)10중량%, 탄산나토륨 3중량%와 안료 2중량%를 혼합하는 제1혼합물 35중량%와 왕겨분말 65중량%를 혼합하는 제2혼합물 65~85중량%와 물 15~35중량%를 혼합한 제3혼합물의 조성에 의해 휨, 크랙, 신장률, 강도 등을 개선하는데 그 목적이 있다.The present invention is 40% by weight starch, 30% by weight melamine resin or urea resin, 15% by weight of silicone rubber compound (silicone rubber compounds), 10% by weight cellulose (cellulose), 3% by weight of sodium carbonate and pigment 2 The warpage, crack and elongation rate are determined by the composition of the third mixture in which the first mixture 35% by weight and the second mixture 65% by weight of the chaff powder 65% by weight and the water mixture 15-35% by weight are mixed. The purpose is to improve strength, strength and so on.
본 발명은 특허 제3혼합물을 정량으로 성형기에 이송하는 장치와, 성형기에 이송된 제3혼합물을 성형하는 장치와, 성형 된 성형물을 분리하는 장치와, 분리된 용기를 건조하는 장치로 구성하여 산업성을 구현한 친환경 생활용기의 제조방법을 제공하는데 목적이 있다.The present invention is composed of a device for transferring the third mixture to the molding machine in a quantitative manner, an apparatus for molding the third mixture transferred to the molding machine, a device for separating the molded molding, and a device for drying the separated container The purpose of the present invention is to provide a manufacturing method of eco-friendly living containers.
전분 40중량%와, 멜라민수지 또는 요소수지 30중량%와, 실리콘고무 콤파운드(silicone rubber compounds)분말 15중량%와, 셀루로스(cellulose)10중량%, 탄산나토륨 3중량%와 안료 2중량%를 혼합하는 제1혼합물 35중량%와 왕겨분말 65중량%를 혼합하는 제2혼합물 65~85중량%와 물 15~35중량%를 혼합한 제3혼합물을 조성한다.40% by weight of starch, 30% by weight of melamine or urea resin, 15% by weight of silicone rubber compounds, 10% by weight of cellulose, 3% by weight of sodium carbonate and 2% by weight of pigment To prepare a third mixture of 35% by weight of the first mixture and 65% to 85% by weight of the second mixture to mix 65% by weight of chaff powder and 15% to 35% by weight of water.
상기 혼합물은 130~355℃의 온도와 2~10㎏/㎠의 압력으로 성형한다.The mixture is molded at a temperature of 130 ~ 355 ℃ and a pressure of 2 ~ 10kg / ㎠.
상기 혼합물의 멜라민수지와 요소수지는 용도를 상이하게 적용한다.Melamine resins and urea resins of the mixture have different applications.
멜라민수지와 요소수지는 열경화성이고 수용성이지만 멜라민수지의 경화 온도는 300~355℃이고 요소수지의 경화 온도는 130~155℃이므로 성형방법을 달리하기 때문이다.Melamine resin and urea resin is thermosetting and water soluble, but the curing temperature of melamine resin is 300 ~ 355 ℃ and the curing temperature of urea resin is 130 ~ 155 ℃, so the molding method is different.
멜라민수지의 경화 시 내수성이 강하고, 요소수지의 내수성은 멜라민수지와 비교하여 상대적으로 약하므로 요소수지의 용도 적용이 제한되기 때문이다.This is because the water resistance of the melamine resin is strong, and the water resistance of the urea resin is relatively weak compared to the melamine resin, thereby limiting the application of the urea resin.
본 발명에서 사용하는 고분자 멜라민수지와 요소수지는 분자량을 더 크게 하기 위해 섬유소(셀루로스)가 소정의 비율로 첨가된 콤파운드의 분말을 사용하며 시중에는 섬유소의 혼합 비율에 따라 형성된 여러 종류의 상품이 출시되어 있으므로 본 발명에서는 종류에 관계없이 사용할 수 있다.The polymer melamine resin and urea resin used in the present invention use a compound powder in which cellulose (cellulose) is added in a predetermined ratio in order to increase the molecular weight, and various kinds of products formed according to the mixing ratio of cellulose are commercially available. Since it is marketed, it can be used regardless of a kind in this invention.
실리콘 고무의 특성은 그 자체로 내열성이 뛰어나 고온(250~315℃)에서 물리적, 화학적으로 안정되어 있다.Silicone rubber has excellent heat resistance in itself and is physically and chemically stable at high temperatures (250 to 315 ° C).
실리콘 고무는 그 자체로 내한성이 뛰어나 -20~-115℃의 온도에서 물리적, 화학적으로 안정되어 있다.Silicone rubber has excellent cold resistance in itself and is physically and chemically stable at a temperature of -20 to -115 ° C.
실리콘 고무는 불활성 물질이기 때문에 음식용기, 의료용기에 사용할 수 있다.Since silicone rubber is an inert substance, it can be used in food containers and medical containers.
상기와 같이 콤파운드로 구성한 기성품의 멜라민수지 또는 요소수지가 물에 수용하게 되면 물의 혼합 비율에 따라 고분자 상태에서 저 분자량으로 변화되므로 제1혼합물에 셀루로스를 첨가하여 멜라민수지와 요소수지가 물에 희석된 상태에서 고분자 상태를 최대한으로 유지하기 위한 것이다.When the ready-made melamine resin or urea resin composed of the compound is accommodated in the water as described above, the melamine resin and the urea resin are diluted in the water by adding cellulose to the first mixture because the polymer is changed to low molecular weight according to the water mixing ratio. In order to maintain the state of the polymer to the maximum.
제1혼합물에 혼합되는 실리콘 고무 콤파운드는 실리콘 고무에 석영, 탄산칼슘, 생석회 등을 혼합하여 실리콘 고무의 내열성(315℃), 내한성(-47℃), 신장률(150~300%), 유연성 등을 가진 실리콘 고무에 인장 강도(90㎏/㎠) 등 물리적, 화학적 성능을 향상시키기 위한 것이다.The silicone rubber compound mixed in the first mixture is mixed with silicone rubber, quartz, calcium carbonate, quicklime, etc. to improve the heat resistance (315 ° C), cold resistance (-47 ° C), elongation (150-300%) and flexibility of the silicone rubber. It is for improving physical and chemical performance such as tensile strength (90㎏ / ㎠) in the silicone rubber.
상기 실리콘 고무 콤파운드에 혼합되는 물질은 석영, 탄산칼슘, 생석회 등이 있고 이들 전부를 동시에 혼합하여 사용할 수 있으며, 일부만 사용할 수 있다.The material to be mixed in the silicone rubber compound is quartz, calcium carbonate, quicklime, etc., all of them can be mixed and used at the same time, only a part can be used.
실리콘 고무만을 사용할 수 있다.Only silicone rubber can be used.
본 발명에서 실리콘 고무와 실리콘 고무 콤파운드를 사용하는 것은 멜라민수지 또는 요소수지의 분자량을 고분자량으로 구성하여 멜라민 또는 요소수지가 물에 수용되어 경화되고 건조될 때 수축율을 저하시키기 위한 것이다.The use of the silicone rubber and silicone rubber compound in the present invention is to reduce the shrinkage rate when the melamine or urea resin is composed of high molecular weight of the melamine resin or urea resin is accommodated in water and cured and dried.
본 발명에서 실리콘 고무 또는 실리콘 고무 콤파운드를 사용하는 것은 용기가 일회용일 경우 용기의 인장강도를 높이기 위한 것이고, 성형시 고온(315℃)에서 실리콘 고무의 물성을 유지하기 때문이다.The use of the silicone rubber or silicone rubber compound in the present invention is to increase the tensile strength of the container when the container is disposable, because it maintains the physical properties of the silicone rubber at high temperature (315 ℃) during molding.
본 발명의 제1혼합물 탄산나트륨은 제3혼합물의 메틸기(-CH3)의 안정으로 용기의 표면 거칠기를 방지하기 위한 것이다.The first mixture sodium carbonate of the present invention is for preventing the surface roughness of the container by stabilizing the methyl group (-CH3) of the third mixture.
본 발명의 제1혼합물 안료는 용기의 색상을 다양하게 구성하기 위한 것으로 천연염료를 사용한다.The first mixture pigment of the present invention uses various natural dyes to construct various colors of the container.
상기 제3혼합물의 혼합비는 성형기의 압력에 따라 상이하게 적용할 수 있다.The mixing ratio of the third mixture may be applied differently according to the pressure of the molding machine.
즉, 성형기의 압력이 낮으면 성형이 용이하도록 물의 혼합비를 높이고, 성형기의 압력이 높으면 물의 혼합비를 낮출 수 있으며, 1대의 성형기에 여러 대의 성 형몰드가 장착될 경우에도 물의 혼합비를 높여 낮은 압력에서도 성형이 가능하도록 구성한다.In other words, if the pressure of the molding machine is low, the mixing ratio of water can be increased to facilitate molding, and if the pressure of the molding machine is high, the mixing ratio of water can be reduced, and even if several molding molds are installed in one molding machine, the mixing ratio of water can be increased even at low pressure. It is configured to enable molding.
본 발명은 상기 제3혼합물의 성형 생산 시 대량생산을 목적으로 한다.The present invention aims at mass production in the molding production of the third mixture.
본 발명에서 구성에서 제3혼합물을 정량으로 성형기에 이송하는 과정과, 성형기에 이송된 제3혼합물을 성형하는 과정과, 성형 된 성형물을 분리하는 과정과, 분리된 용기를 건조하는 과정은 장치로 구성되어 있다.In the present invention, the process of quantitatively transferring the third mixture to the molding machine, the process of molding the third mixture transferred to the molding machine, the process of separating the molded molding, and the process of drying the separated container is an apparatus Consists of.
본 발명의 제3혼합물의 이송하는 과정은 여러 개의 성형기에 균일한 량을 동시에 공급할 수 있는 장치를 제공한다.The process of conveying the third mixture of the present invention provides an apparatus capable of simultaneously supplying a uniform amount to several molding machines.
제3혼합물의 이송방법은 제3혼합물의 물의 혼합비에 따라 이송방법이 상이하게 적용된다.The transfer method of the third mixture is applied differently depending on the mixing ratio of the water of the third mixture.
본 발명의 분리하는 과정은 여러 개의 성형기에서 동시에 분리할 수 있는 장치를 제공한다.The separating process of the present invention provides a device that can be separated at the same time in several molding machines.
본 발명의 건조과정에서 성형물의 분자결합으로 성형물을 견고하게 하기 위해 스팀건조 과정을 가진다.In the drying process of the present invention has a steam drying process in order to solidify the molding by molecular bonding of the molding.
본 발명은 왕겨 등의 농산물 폐기물을 재활용하는 효과가 있다.The present invention has the effect of recycling agricultural waste, such as chaff.
본 발명은 생활용기의 폐기 시 자연 분해에 의해 환경을 보호할 수 있는 효과가 있다.The present invention has the effect of protecting the environment by natural decomposition during disposal of household containers.
본 발명은 환경을 오염시키는 일회용 용기를 대체할 수 있는 효과가 있다.The present invention has the effect of replacing the disposable container to pollute the environment.
본 발명은 농산물 폐기물의 판매로 농가의 수익을 증가시킬 수 있는 효과가 있다.The present invention has the effect of increasing the profit of the farm by the sale of agricultural waste.
본 발명은 지하자원의 고갈에 이를 대체할 수 있는 효과가 있다.The present invention has an effect that can replace this in the depletion of underground resources.
본 발명의 사용시 환경 호르몬에 의한 건강을 보호할 수 있는 효과가 있다.The use of the present invention has the effect of protecting the health by environmental hormones.
본 발명은 전분 40중량%와 멜라민수지 또는 요소수지분말 30중량%와, 실리콘고무 콤파운드(silicone rubber compounds)분말 15중량%와, 셀루로스(cellulose)분말 10중량%, 탄산나토륨 3중량%와 안료 2중량%를 혼합하는 제1혼합물 35중량%와 왕겨 분말 65중량%를 혼합하는 제2혼합물 65~85중량%와 물 15~35중량%를 혼합한 제3혼합물의 조성물로 구성된다.The present invention is 40% by weight starch, 30% by weight of melamine resin or urea resin powder, 15% by weight of silicone rubber compound (silicone rubber compounds) powder, 10% by weight of cellulose (cellulose) powder, 3% by weight of sodium carbonate and It consists of the composition of the 3rd mixture which mixed 35 weight% of the 1st mixture which mixes 2 weight% of pigments, 65-85 weight% of the 2nd mixture which mixes 65 weight% of chaff powder, and 15-35 weight% of water.
본 발명은 상기 제3혼합물을 130~355℃의 온도와 2~10㎏/㎠의 압력으로 성형 되도록 구성된다.The present invention is configured to form the third mixture at a temperature of 130 to 355 ° C. and a pressure of 2 to 10 kg / cm 2.
본 발명은 상기 제3혼합물을 용기로 성형하기 위해 이송장치와, 성형 장치와, 성형물의 분리장치와, 분리된 성형물의 건조장치가 제공된다.The present invention provides a conveying apparatus, a molding apparatus, a separating apparatus of a molding, and a drying apparatus of a separate molding for molding the third mixture into a container.
도 1은 본 발명의 공정 과정을 도시한 것이다.1 illustrates the process of the present invention.
도 2는 성형과정의 각 장치의 전체를 도시한 것이다.2 shows the entirety of each device in the forming process.
도 3은 제3혼합물의 저장장치를 도시한 것이다.3 shows a storage device of a third mixture.
도 4는 이송장치의 공급판과 차단판의 작동 상태를 도시한 것이다.Figure 4 shows the operating state of the supply plate and the blocking plate of the transfer device.
도 5는 제3혼합물이 분말인 상태의 공급기 작업 상태를 도시한 것이다.Fig. 5 shows the feeder working state with the third mixture being powder.
도 6은 제3혼합물이 겔 상태의 공급기 작업 상태를 도시한 것이다.Figure 6 shows the feeder working state in which the third mixture is in a gel state.
도 7은 분리장치의 흡착 작업을 도시한 것이다.7 shows the adsorption operation of the separator.
도 8은 공급판의 작동 상태를 평면으로 도시한 것이다.8 is a plan view showing the operating state of the supply plate.
도 9는 흡착판의 구조를 상세하게 도시한 것이다.9 shows the structure of the adsorption plate in detail.
본 발명은 전분 40중량%와 멜라민수지 또는 요소수지분말 30중량%와, 실리콘고무 콤파운드(silicone rubber compounds)분말 15중량%와, 셀루로스(cellulose)분말 10중량%, 탄산나토륨 3중량%와 안료 2중량%로 혼합되는 제1혼합물이 혼합기(도시 되지않음)에서 충분히 혼합된다.The present invention is 40% by weight starch, 30% by weight of melamine resin or urea resin powder, 15% by weight of silicone rubber compound (silicone rubber compounds) powder, 10% by weight of cellulose (cellulose) powder, 3% by weight of sodium carbonate and The first mixture mixed with 2% by weight of the pigment is sufficiently mixed in a mixer (not shown).
상기 제1혼합물의 실리콘 고무 콤파운드(silicone rubber compounds)분말은 용기의 종류(원통형 용기)에 따라 실리콘고무(silicone rubber)분말로 대체되어도 무방하다. The silicone rubber compound powder of the first mixture may be replaced with silicone rubber powder according to the type of container (cylindrical container).
혼합된 제1혼합물 35중량%와 100~200메쉬로 형성되는 65중량%의 왕겨가 혼합기(도시되지않음)에서 충분히 혼합되어 제2혼합물로 구성된다.35% by weight of the mixed first mixture and 65% by weight of chaff formed from 100 to 200 mesh are sufficiently mixed in a mixer (not shown) to constitute the second mixture.
상기 제2혼합물 65~85중량%와 물 15~35중량%를 혼합기로 충분히 혼합하여 제3혼합물을 구성한다.65 to 85% by weight of the second mixture and 15 to 35% by weight of water are sufficiently mixed with a mixer to form a third mixture.
예; 제1혼합물에 왕겨를 같이 혼합할 경우 물의 혼합비가 낮아져서 단시간에 균일한 혼합을 얻지 못하는 문제점이 있다. Yes; When chaff is mixed with the first mixture, there is a problem in that the mixing ratio of water is lowered to obtain uniform mixing in a short time.
상기와 같이 구성된 제3혼합물은 이송장치를 통하여 성형장치의 금형으로 이송되도록 형성되어 있다.The third mixture configured as described above is formed to be transferred to the mold of the molding apparatus through a conveying apparatus.
상기 프레스기(11)에는 상. 하 플레이트(12a,12b)가 형성되고 상부 플레이트(12a)는 메인실린더(13)에 의해 상. 하로 이동할 수 있도록 형성되고 하부 플레이트(12b)는 고정되어 있다.The
상기 상. 하 플레이트(12a,12b)에는 다수개의 금형(14a,14b)을 장착할 수 있도록 형성되어 있다.Above phase. The
상부플레이트(12a)에는 철부금형(14a)이 장착되고 하부플레이트(12b)에는 요부금형(14b)이 장착되도록 형성되어 있다.An
상기 철부금형(14a)과 요부금형(14b)에는 전기가 제공되어 고온(130~355℃)으로 히팅되도록 형성되어 있다.The
요부금형(14b)에는 공급기(19)의 작동에 의해 제3혼합물이 수용되도록 형성되어 있다.The recessed
상기 제3혼합물을 이송하는 공급기(19)는 상. 하로 신축 작동할 수 있는 실린더(26a)와 전. 후로 이동할 수 있는 실린더(26b)가 장착되어 있다.The
실린더(26a)의 하부에는 공급기(19)가 좌·우로 회전할 수 있도록 동력(15)이 형성되어 있다.The
실린더(26b) 끝 부분에 공급판(31a)이 장착 고정되어 있다.The
상기 공급판(31a)에는 다수개의 홀(32a)이 천공되어 있고 공급판(31a)의 밑바닥에는 홀(32a)의 하단부를 차단할 수 있도록 전. 후로 이동하는 차단판(33a)이 형성되어 있다.A plurality of holes (32a) are perforated in the supply plate (31a) and the bottom of the supply plate (31a) to block the lower end of the hole (32a). The blocking
상기 차단판(33a)에는 공급판(31a)의 홀(32a)과 동일한 간격으로 구멍(34a)이 천공되어 차단판(33a)의 동작에 의해 차단판(33a)의 구멍(34a)과 공급판(31a)의 홀(32a)이 일치되기도 하고 공급판(31a)의 홀(32a)을 차단하기도 할 수 있도록 형성 되어 있다.
즉 차단판(33a)이 완전히 공급판(31a)에 삽입된 상태에서 차단판(33a)의 작동에 의해 공급판(31a)의 홀(32a)을 차단판(33a)의 구멍(34a)이 밀폐하거나 개방할 수 있도록 형성되어 차단판(33a)에 의해 공급판(31a)의 홀(32a)이 밀폐되면 제3혼합물을 수용할 수 있고 홀(32a)이 개방되면 홀(32a)에 수용된 제3혼합물이 낙하하도록 형성되어 있다.That is, the
제3혼합물이 낙하한 후 공급판(31a)의 실린더(35a)가 작동되어 차단판(33a)이 삽입되면 공급판(31a)의 홀(32a)이 차단판(33a)에 의해 하부에서 폐쇄되도록 형성 되어 있다.After the third mixture falls, the
상기 공급기(19)는 동력(15)에 의해 좌. 우로 회전하고 전. 후로 작동하면서 제3혼합물을 공급받고 요부금형(14b)에 이송하도록 형성되어 있다.The
상기 공급기(19)는 실린더(26a,26b)의 전. 후 작동으로 공급판(31a)이 신장하여 저장실(28)에 진입할 수 있도록 형성되어 있다.The
저장실(28) 내부에는 공급판(31a) 홀(32a)의 배열과 동일하게 홀(32b)이 배열된 공급판(31b)이 형성되어 있고 상기 공급판(31b)의 윗부분에 제3혼합물이 저장되어 있다.In the
공급판(31b)의 밑바닥에는 공급판(31b)에 형성된 홀(32b)과 동일하게 구멍(34b)이 배열된 차단판(33b)이 전. 후로 작동하도록 형성되어 있다.At the bottom of the
상기 차단판(33b)은 차단판(33b)에 연계된 실린더(35b)에 의해 전, 후로 작동하도록 형성되어 있다.The blocking
차단판(33b)의 작동으로 저장실(28)의 공급판(31b)의 홀(32b)이 폐쇄되고 개 방 되도록 형성되어 있다.The
상기와 같은 구성은 공급기(19)의 작동에 의해 공급판(31a)이 저장실(28)에 진입하면 저장실(28)의 공급판(31b)의 차단판(33b)이 개방되어 저장실(28)의 제3혼합물이 공급판(31b)의 홀(32b)을 통하여 아래로 이동하여 공급판(31a)의 홀(32a)에 수용되고 차단판(33b)이 다시 작동하게 되면 차단판(33b)이 공급판(31b)의 홀(32b)을 폐쇄하는 구성이다.As described above, when the
상기와 같이 저장실(28)의 공급판 홀(32b)이 폐쇄되면 공급기(19)가 작동하여 후퇴하고 회전하여 요부금형(14b)위에 이동하도록 형성되어 있다.As described above, when the
상기와 같이 공급판(31a)이 요부금형(14b) 위에 위치하게 되면 공급판(31a)의 차단판(33a)이 작동하여 공급판(31a)의 홀(32a)과 차단판(33a)의 구멍(34a)이 일치되어 제3혼합물은 하강하여 요부금형(14b)에 수용되도록 형성되어 있다.When the
요부금형(14b)에 제3혼합물이 수용되면 상부플레이트(12a)가 하강하여 철부금형(14a)과 요부금형(14b)이 결합하여 제3혼합물을 성형하도록 형성되어 있다.When the third mixture is accommodated in the recessed
제3혼합물이 성형 되고 상부플레이트(12a)가 상승한 후에는 흡착기(22)가 작동하여 흡착판(36)이 요부금형(14b) 위에 위치하도록 형성되어 있다.After the third mixture is molded and the
상기 흡착기(22)는 공급기(19)와 같이 실린더(27a,27b)에 의해 상. 하, 전. 후로 신축할 수 있도록 형성되고 그 하부의 동력(15)으로 회전할 수 있도록 형성되어 있다.The
상기 흡착판(36)은 요부금형(14b)의 숫자와 동일하게 형성되어 요부금형(14b)의 성형물을 흡착할 수 있도록 형성되어 있다.The
각 흡착판(36)에는 성형물을 흡착할 수 있도록 에어라인(29)이 형성되어 있다.Each
성형물을 흡착한 흡착판(36)은 흡착기(22)의 실린더(27a,27b)의 작동과 동력(15)의 작동으로 성형물을 요부금형(14b)에서 분리하여 이동하는 이송 컨베이어(23)로 이송시키도록 형성되어 있고 컨베이어(23)로 이송되는 성형물은 건조장치(도시되지 않음)로 이송된다.The
제3혼합물의 물 혼합비가 커서 혼합물이 겔 상태가 될 경우 공급기(19)의 공급판(31a)의 저부에는 홀(32a)의 숫자와 같은 노즐(24)이 형성되고 공급판(31a)의 상부에는 상기 노즐과 연계하여 제3혼합물을 이송하는 호스(37)가 겔 상태의 제3혼합물 저장소(도시되지 않음)에 연계하여 각 요부금형(14b)에 노즐(24)에서 제3혼합물이 제공되도록 형성되어 있다. When the water mixture ratio of the third mixture is so large that the mixture is in a gel state, a
실시 예Example
종래의 기술 특허 제660068(천연플라스틱제조방법, 인용특허라 합니다.)호는 왕겨와 전분과 멜라민수지와 물의 혼합비를 적용하고 각종 생활용기를 얻도록 구성되어 있고 상기 멜라민수지가 용기의 내수성을 위한 표면 피막, 용기의 견고성, 용기의 표면 윤택, 용기의 표면 박리 등의 효과를 얻을 수 있으나, Conventional technical patent 660068 (natural plastic manufacturing method, referred to as a cited patent) is configured to apply the mixing ratio of chaff, starch, melamine resin and water and to obtain various living containers, the melamine resin for water resistance of the container Although the surface coating, the firmness of the container, the surface shine of the container, the surface peeling of the container can be obtained,
인용특허의 주성분은 왕겨이므로 전분의 함유량은 적을 뿐 아니라, 전분은 내수성이 약하므로 내수성을 강하게 하기 위해 고분자 구조인 멜라민수지를 사용하였다.Since the main component of the cited patent is chaff, not only starch content is low, but starch is weak in water resistance, and thus, melamine resin, which is a polymer structure, is used to increase water resistance.
인용특허에서 사용하는 멜라민수지는 열경화성 수지로서 수용성이기 때문에 멜라민수지가 물에 수용되면 고분자 구조에서 저 분자 구조로 변형되어 분자의 결합성과 점액질 성이 저하되고 왕겨와 전분과 멜라민수지의 혼합물에 의해 용기가 성형 되더라도, 특히 용기의 두께가 엷은 용기의 경우, 전체적 또는 부분적으로 휨, 크랙, 저강도 등이 현저하게 발생하므로 인용특허의 실시에서 생산성과 산업성을 얻을 수 없었다. Since the melamine resin used in the cited patent is water-soluble as a thermosetting resin, when the melamine resin is contained in water, it is transformed from the polymer structure into the low molecular structure, thereby decreasing the binding and mucus properties of the molecule, and the container by the mixture of chaff, starch and melamine resin. Even in the case of molding, especially in the case of a thin container, since warpage, cracks, low strength, etc., remarkably occur in whole or in part, productivity and industrial performance could not be obtained in the practice of the cited patent.
용기의 성형시간과 건조시간을 단축하기 위한 인용특허의 혼합방법은 처음부터 물과 같이 혼합하게 되어 온전한 혼합을 얻기 어렵고 성형방법은 왕겨와 전분과 멜라민수지와 물의 혼합비에서 물의 혼합비가 적은 상태로 성형하기 때문에 고압(10㎏/㎠)이 필요하므로 한 개의 프레스에 여러 개의 성형기를 장착하는데 크기, 장소, 비용 등의 한계가 있었다.The mixing method of the cited patent for shortening the forming time and drying time of the container is mixed with water from the beginning, so that it is difficult to obtain a perfect mixing, and the molding method is formed with a low mixing ratio of water at the mixing ratio of chaff, starch, melamine resin and water. Therefore, high pressure (10 kg / ㎠) is required, so there was a limit in size, location, cost, etc. for mounting several molding machines in one press.
본 발명을 구성하는 각 소재는 인체에 무해한 소재를 사용하는 것을 특징으로 한다.Each material constituting the present invention is characterized by using a material harmless to the human body.
본 발명은 성형물의 전체적인 견고성, 휨, 크랙, 표면 거칠기 등의 문제점을 개선하기 위한 것이며, 특히 멜라민수지와 요소수지의 분자량을 크게 하여 건조시 체적 변화를 최소화하기 위한 것이다.The present invention is to improve the problems of the overall rigidity of the molding, warpage, cracks, surface roughness, etc., in particular to increase the molecular weight of the melamine resin and urea resin to minimize the volume change during drying.
상기 제1혼합물의 실리콘 고무 콤파운드(silicone rubber compounds)분말은 용기의 종류(원통형 용기)에 따라 실리콘고무(silicone rubber)분말로 대체되어도 무방하다. The silicone rubber compound powder of the first mixture may be replaced with silicone rubber powder according to the type of container (cylindrical container).
본 발명에 의한 제3혼합물을 시료로 하여 성분 검사 내용은 표-1의 기재와 같다.Using the third mixture according to the present invention as a sample, the contents of the component inspection are as described in Table-1.
시료 명 : 왕겨식품용기Sample Name: Rice husk food container
표-1TABLE-1
상기 표-1은 본 발명에서 제조한 왕겨를 이용한 용기를 한국화학시험연구원에서 성분 검사를 한 시험성적서이다.Table 1 is a test report of the components tested by the Korea Testing Institute for the container using the chaff prepared in the present invention.
상기 시험성적서에서 알 수 있듯이 중금속의 성분이 나타나지 않거나 허가 기준치를 넘지 않는 수치로 나타난 것을 알 수 있다.As can be seen from the above test report, it can be seen that the components of the heavy metals do not appear or appear in numerical values that do not exceed the acceptance criteria.
따라서 본 발명에 의한 용기는 실생활에 음식 용기로 사용하는데 인체에 무해한 것을 알 수 있다. Therefore, it can be seen that the container according to the present invention is harmless to the human body when used as a food container in real life.
실시 예-1Example-1
본 발명의 실시 예는 건조된 왕겨 분말로 실시한다.An embodiment of the present invention is carried out with dried chaff powder.
본 발명의 실시 예는 멜라민수지로 실시한다.An embodiment of the present invention is carried out with melamine resin.
본 발명의 실시 예는 실리콘 고무 콤파운드로 실시한다.An embodiment of the present invention is carried out with a silicone rubber compound.
본 발명은 전분 40중량%와 멜라민수지분말 30중량%와, 실리콘고무 콤파운드(silicone rubber compounds)분말 15중량%와, 셀루로스(cellulose)분말 10중량%, 탄산나토륨 3중량%와 안료 2중량%를 혼합하여 제1혼합물을 구성한다.The present invention is 40% by weight starch, 30% by weight of melamine resin powder, 15% by weight of silicone rubber compound (silicone rubber compounds) powder, 10% by weight of cellulose powder, 3% by weight of sodium carbonate and 2% by weight of pigment % Is mixed to form a first mixture.
상기 제1혼합물 35중량%와 왕겨분말 65중량%를 혼합하여 제2혼합물을 구성한다.35 wt% of the first mixture and 65 wt% of chaff powder are mixed to form a second mixture.
상기 제2혼합물 65~85중량%와 물 15~35중량%를 혼합하여 제3혼합물을 구성한다.65 to 85% by weight of the second mixture and 15 to 35% by weight of water are mixed to form a third mixture.
상기 제3혼합물은 공급기(19)에 의해 300~355℃의 요부금형(14b)으로 이송하게 된다.The third mixture is transferred to the recessed
제3혼합물이 요부금형(14b)에 수용된 후에 프레스(11)의 작동으로 철부금형(14a)이 요부금형(14b)과 5~10㎏/㎠의 힘으로 약 20~40초 동안 압착하여 제3혼합물을 성형한다.After the third mixture is accommodated in the recessed
실시 예-2Example-2
본 발명의 실시 예는 건조된 왕겨로 실시한다.An embodiment of the present invention is carried out with dried chaff.
본 발명의 실시 예는 요소수지로 실시한다.Embodiment of the present invention is carried out with urea resin.
본 발명의 실시 예는 실리콘 고무 콤파운드로 실시한다.An embodiment of the present invention is carried out with a silicone rubber compound.
본 발명은 전분 40중량%와 요소수지분말 30중량%와, 실리콘고무 콤파운드(silicone rubber compounds)분말 15중량%와, 셀루로스(cellulose)분말 10중량%, 탄산나토륨 3중량%와 안료 2중량%를 혼합하여 제1혼합물을 구성한다.The present invention is 40% by weight starch, 30% by weight of urea resin powder, 15% by weight of silicone rubber compound (silicone rubber compounds) powder, 10% by weight of cellulose powder, 3% by weight of sodium carbonate and 2% by weight of pigment % Is mixed to form a first mixture.
상기 제1혼합물 35중량%와 왕겨분말 65중량%를 혼합하여 제2혼합물을 구성한다.35 wt% of the first mixture and 65 wt% of chaff powder are mixed to form a second mixture.
상기 제2혼합물 65~85중량%와 물 15~35중량%를 혼합하여 제3혼합물을 구성한다.65 to 85% by weight of the second mixture and 15 to 35% by weight of water are mixed to form a third mixture.
상기 제3혼합물은 공급기(19)에 의해 130~150℃의 요부금형(14b)으로 이송하게 된다.The third mixture is transferred to the
제3혼합물이 요부금형(14b)에 수용된 후에 플레스(11)의 작동으로 철부금형(14a)이 요부금형(14b)과 5~10㎏/㎠의 힘으로 약 20~40초 동안 압착하여 제3혼합물을 성형한다.After the third mixture is accommodated in the recessed
실시 예-3Example-3
본 발명의 실시 예는 건조된 왕겨 분말로 실시한다.An embodiment of the present invention is carried out with dried chaff powder.
본 발명의 실시 예는 멜라민수지로 실시한다.An embodiment of the present invention is carried out with melamine resin.
본 발명의 실시 예는 실리콘 고무로 실시한다.An embodiment of the present invention is carried out with silicone rubber.
본 발명은 전분 40중량%와 멜라민수지분말 30중량%와, 실리콘고무(silicone rubber)분말 13중량%와, 셀루로스(cellulose)분말 12량%, 탄산나토륨 3중량%와 안료 2중량%를 혼합하여 제1혼합물을 구성한다.The present invention comprises 40% by weight starch, 30% by weight of melamine resin powder, 13% by weight of silicone rubber powder, 12% by weight of cellulose powder, 3% by weight of sodium carbonate and 2% by weight of pigment. Mixing to form a first mixture.
상기 셀루로스의 량이 증가한 것은 제1혼합물의 분자량을 증가하기 위한 것이다. The increase in the amount of cellulose is for increasing the molecular weight of the first mixture.
상기 제1혼합물 35중량%와 왕겨분말 65중량%를 혼합하여 제2혼합물을 구성한다.35 wt% of the first mixture and 65 wt% of chaff powder are mixed to form a second mixture.
상기 제2혼합물 65~85중량%와 물 15~35중량%를 혼합하여 제3혼합물을 구성한다.65 to 85% by weight of the second mixture and 15 to 35% by weight of water are mixed to form a third mixture.
상기 제3혼합물은 공급기(19)에 의해 300~355℃의 요부금형(14b)에 수용된다.The third mixture is accommodated in the recessed
제3혼합물이 요부금형(14b)에 수용된 후에 프레스(11)의 작동으로 철부금형(14a)이 요부금형(14b)과 2~10㎏/㎠의 힘으로 약 20초 동안 압착하여 제3혼합물을 성형한다.After the third mixture is accommodated in the recessed
실시 예-4Example-4
상기 실시 예-1, 2, 3의 제3혼합물은 하부플레이트(12b)의 요부금형(14b)에 이송하기 위해 공급기(19)는 제3혼합물이 저장되어 있는 저장실(28)의 높이로 신장하고 저장실(28) 방향으로 회전한다.In order to transfer the third mixture of Examples 1, 2, and 3 to the recessed
저장실(28) 방향으로 작동된 실린더(26a)를 작동하여 차단판(33a)에 의해 홀(32a)이 밀폐된 공급판(31a)이 저장실(26)로 삽입되도록 한다. The
저장실(28)에 공급판(31a)이 삽입하면 저장실(28)의 차단판(33b)이 작동하여 저장실(28)의 제3혼합물이 공급판(31a)의 홀(32a)에 수용된다.When the
저장실(26)로 삽입된 공급판(31a)의 홀(32a)에 제3혼합물이 수용되면 실린더(26b)가 작동하여 공급판(31a)이 후퇴하고 이동하여 135~350℃의 온도로 가열된 요부금형(14b)에 제3혼합물을 이송하도록 한다.When the third mixture is accommodated in the
요부금형(14b)으로 이송된 제3혼합물은 철부금형(14a)과 요부금형(14b)이 2~10㎏/㎠힘으로 20~40초의 시간 동안 압착하여 성형하게 된다.The third mixture transferred to the recessed
제3혼합물이 성형된 후에는 철부금형(14a)과 요부금형(14b)이 분리되고 흡착기(22)가 요부금형(14b) 높이로 신장하고 작동하여 요부금형(14b)에서 각각의 성형물을 각각의 흡착판(36)이 흡착하여 콘베어(23)로 이송하게 된다.After the third mixture is molded, the
상기와 같이 흡착판(36)이 성형물을 콘베어(23)로 이송한 후에는 다시 공급기(19)가 제3혼합물을 요부금형(14b)에 이송하는 동작을 반복하므로서 공급기(19)와 금형(14a,14b)의 작업을 반복하게 되고 흡착기(22) 역시 요부금형(14b)의 성형물을 분리하여 이송하는 작업을 반복하게 된다.After the
상기 제3혼합물이 겔인 경우 공급판(31a)의 저부에는 겔 상태의 제3혼합물을 공급하기 위해 요부금형(14b)과 동일한 숫자의 노즐(24)이 형성되고 상부에는 노즐(24)과 연계하여 제3혼합물 이송 호스(37)가 형성되어 제3혼합믈을 분사식으로 배출하여 요부금형(14b)에 공급하도록 한다.When the third mixture is a gel, a
도 1은 본 발명의 공정도1 is a process diagram of the present invention
도 2는 본 발명에 의한 제3혼합물을 용기로 성형하기 위한 장치도2 is a device diagram for forming a third mixture according to the present invention into a container
도 3은 제3혼합물의 저장장치도3 is a storage device of the third mixture
도 4는 공급판과 차단판의 작업도4 is a working diagram of the supply plate and the blocking plate
도 5는 제3혼합물이 분말 상태의 공급기 작업도5 is a working diagram of the feeder of the third mixture in the powder state
도 6은 제3혼합물이 겔 상태의 공급기 작업도6 is a working diagram of the feeder in the third mixture gel state
도 7은 흡착기의 작업도7 is a working diagram of the adsorber
도 8은 공급판의 작동시 평면 상태도8 is a plan view in operation of the supply plate
도 9는 흡착판의 상세도9 is a detailed view of the adsorption plate
**도면의 주요부분에 대한 부호의 설명**** Description of the symbols for the main parts of the drawings **
11 : 프레스 12 : 플레이트(a,b)11: press 12: plate (a, b)
13 : 메인실린더 14 : 금형(a,b)13: main cylinder 14: mold (a, b)
15 : 동력 19 : 공급기 15 power 19: feeder
22 : 흡착기 23 : 이송콘베어22: adsorber 23: conveying conveyor
24 : 노즐 26 : 공급기의 실린더(a,b) 27 : 흡착기의 실린더(a,b) 28 : 저장실 24 nozzles 26 cylinders (a, b) of
29 : 에어라인 31 : 공급판(a,b) 32 : 홀(a,b) 33 : 차단판(a,b) 29 Air line 31 Supply plate (a, b) 32 Hole (a, b) 33 Blocking plate (a, b)
34 : 구멍(a,b) 35 : 차단판 실린더(a,b) 36 : 흡착판 37 : 혼합물 이송호스 34 hole (a, b) 35 blocking plate cylinder (a, b) 36
Claims (8)