KR20080076071A - Tile having humidity sensing and humidity control function - Google Patents

Tile having humidity sensing and humidity control function Download PDF

Info

Publication number
KR20080076071A
KR20080076071A KR1020070015513A KR20070015513A KR20080076071A KR 20080076071 A KR20080076071 A KR 20080076071A KR 1020070015513 A KR1020070015513 A KR 1020070015513A KR 20070015513 A KR20070015513 A KR 20070015513A KR 20080076071 A KR20080076071 A KR 20080076071A
Authority
KR
South Korea
Prior art keywords
humidity
tile
layer
moisture
humidity control
Prior art date
Application number
KR1020070015513A
Other languages
Korean (ko)
Other versions
KR101413358B1 (en
Inventor
예성훈
노병현
민일홍
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to KR1020070015513A priority Critical patent/KR101413358B1/en
Publication of KR20080076071A publication Critical patent/KR20080076071A/en
Application granted granted Critical
Publication of KR101413358B1 publication Critical patent/KR101413358B1/en

Abstract

A tile having humidity-sensing and humidity-controlling functions is provided to sense humidity by changing color according to the surrounding humidity, and to control humidity by absorbing or releasing moisture according to the amount of humidity. A tile(10) having humidity-sensing and humidity-controlling functions is obtained by forming a humidity recognition layer(12) on the surface of a porous plate-like base material layer(11). The humidity recognition layer comprises a humidity recognition material which changes color by absorbing moistures from the air and consists of a cobalt compound, an iron compound, an organic dye, or a compound combined with an alkali metal or alkaline earth metal. A resin layer is interposed between the humidity recognition layer and a base material layer. Further, the cobalt compound is cobalt chloride and a balance layer additionally is laminated inside the base material layer.

Description

감습 및 조습기능을 갖는 타일{Tile having humidity sensing and humidity control function}Tile having humidity sensing and humidity control function

도 1은 본 발명의 하나의 구체예에 따른 감습 및 조습기능을 갖는 감습타일을 개략적으로 도시한 사시도이다.1 is a perspective view schematically showing a damping tile having a damping and humidity control function according to an embodiment of the present invention.

도 2는 본 발명의 다른 하나의 구체예에 따른 감습 및 조습기능을 갖는 감습타일을 개략적으로 도시한 측단면도이다.Figure 2 is a side cross-sectional view schematically showing a damping tile having a damping and humidity control according to another embodiment of the present invention.

도 3은 본 발명의 또 다른 하나의 구체예에 따른 감습 및 조습기능을 갖는 감습타일을 개략적으로 도시한 측단면도이다.Figure 3 is a side cross-sectional view schematically showing a damping tile having a damping and humidity control function according to another embodiment of the present invention.

도 4는 본 발명의 또 다른 하나의 구체예에 따른 감습 및 조습기능을 갖는 감습타일을 개략적으로 도시한 측단면도이다.Figure 4 is a side cross-sectional view schematically showing a damping tile having a damping and humidity control function according to another embodiment of the present invention.

도 5는 본 발명의 또 다른 하나의 구체예에 따른 감습 및 조습기능을 갖는 감습타일을 개략적으로 도시한 측단면도이다.Figure 5 is a side cross-sectional view schematically showing a damping tile having a damping and humidity control function according to another embodiment of the present invention.

도 6은 본 발명의 또 다른 하나의 구체예에 따른 감습 및 조습기능을 갖는 감습타일을 개략적으로 도시한 측단면도이다.Figure 6 is a side cross-sectional view schematically showing a damping tile having a damping and humidity control according to another embodiment of the present invention.

도 7은 본 발명에 따른 감습타일을 포함하는 감습패널을 개략적으로 도시한 분해사시도이다.7 is an exploded perspective view schematically showing a moisture absorbing panel including a moisture absorbing tile according to the present invention.

도 8은 본 발명에 따른 감습타일(실시예 1)과 이 감습타일에 사용된 습도인 지물질과 동일한 습도인지물질을 동일한 농도로 사용하여 제조한 감습지(비교예)의 시간의 경과에 따른 흡습도를 비교하여 도시한 그래프이다.FIG. 8 is a view illustrating a humidity paper (Example 1) according to the present invention and a humidity paper (Comparative Example) prepared by using the same humidity-sensitive material as the humidity-sensitive material used in the humidity-sensitive tile at the same concentration. It is a graph comparing the hygroscopicity.

도 9 및 도 10은 본 발명에 따른 감습타일에 무늬인쇄부를 더 형성시켜 무늬인쇄부에 의해 직접적으로 감습타일의 변색을 육안으로 쉽게 확인하도록 한 것으로서, 상대습도 25%의 상태(도 9)와 상대습도 50%의 상태(도 10)를 비교하여 나타낸 사진들이다.9 and 10 are to form a pattern printing part in the tactile tile according to the present invention to easily check the discoloration of the tactile tile directly by the pattern printing, the state of relative humidity 25% (Fig. 9) and The photographs are shown by comparing the state of relative humidity 50% (Fig. 10).

* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

10 : 감습타일 11 : 기재층10: the damp tile 11: base layer

12 : 감습물질내포층 13 : 무늬인쇄부12: layer containing the moisture-sensitive material 13: pattern printing

21 : 수지층 31 : 밸런스층21: resin layer 31: balance layer

41 : 표면보호층 50 : 감습패널41: surface protective layer 50: moisture sensitive panel

51 : 패널기판 52 : 타일고정홈51: panel substrate 52: tile fixing groove

본 발명은 감습 및 조습기능을 갖는 타일에 관한 것으로 특히, 주변의 습도에 따라 색상이 변하여 습도를 감지할 수 있도록 함과 동시에 자체적으로 습도의 고저에 따라 수분을 흡수하거나 방출하여 습도를 조절할 수 있고, 탈취 및 흡착기능을 나타낼 수 있는 감습 및 조습기능을 갖는 타일에 관한 것이다.The present invention relates to a tile having a humidity and humidity control function. In particular, the color is changed according to the surrounding humidity so that the humidity can be sensed, and at the same time, the moisture can be adjusted or absorbed or released according to the height of the humidity itself. The present invention relates to a tile having a humidity and humidity control function that can exhibit deodorization and adsorption functions.

겨울철에는 에너지 효율 증가를 위하여 건물 내부의 밀폐성이 높아져 공기가 건조해질 수 있으며, 그에 따라 피부도 건조해져서 신체 일부에 각질이 생겨나고, 가려운 곳이 발생하여 아토피성 피부질환이 악화된다. 이를 방지하기 위해 빨래를 방안에 널어 놓거나 가습기를 가동시키는 것이 일반적이었다.In winter, the airtightness of the building may be increased due to the increased airtightness of the building, and thus, the skin may be dried, resulting in dead skin cells, and itchy areas, resulting in atopic dermatitis. To prevent this, it was common to put laundry in a room or run a humidifier.

최근에는 조습기능을 갖는 벽지, 타일 또는 판넬들의 시공에 의해 피부질환을 완화시키고자 하는 시도가 있었다. 이러한 조습기능을 갖는 제품을 시공할 경우, 흡습에 따른 벽면의 결로를 방지할 수 있지만, 높은 흡습에 의해 곰팡이나 세균류의 번식이 촉진되어 기침, 감기, 비염 또는 천식과 같은 호흡기질환을 일으키는 문제점이 있었다.Recently, there have been attempts to alleviate skin diseases by the construction of wallpaper, tiles or panels with humidity control. When the product with the humidity control function is installed, condensation of the wall surface can be prevented due to moisture absorption, but the problem of causing respiratory diseases such as cough, cold, rhinitis or asthma is promoted by the high moisture absorption which promotes the growth of mold or bacteria. there was.

또한 습도가 비교적 높은 여름철에도 제품의 과도한 흡습에 따른 문제점을 내포하고 있다.In addition, there is a problem due to excessive moisture absorption of the product even in the summer when the humidity is relatively high.

상기한 바와 같은 종래의 각종 흡습기능을 갖는 기능성 타일 또는 판넬의 경우, 흡착, 탈취, 흡습이라는 기능적인 면 만을 강조하는 경향이 있었을 뿐, 제품이 사용자들에게 적절한 습도인지의 여부를 인지시킬 수 있는 기능은 없었다. 또한, 최근 널리 활용되고 있는 가습기와 흡착, 탈취, 흡습 중 어느 하나를 포함하는 기능성 제품을 동시에 사용할 경우, 제품 내부의 결로와 미세척 등의 원인으로 녹농균(Pseudomonas aeruginosa), 폐렴간구균(Klebsiella pneumoniae), 황색포도상구균(Staphylococcus aureus), 알러지(allergy)와 천식(asthma) 등을 유발시키는 클래도스포리움균(cladosporium), 알터나리아균(Alternaria) 등의 병원성 미생물이 발생되는 문제점이 있었다.In the case of the functional tiles or panels having various moisture absorption functions as described above, there is a tendency to emphasize only functional aspects such as adsorption, deodorization, and moisture absorption, and it is possible to recognize whether the product is appropriate humidity to users. There was no function. In addition, when simultaneously using a widely used humidifier and a functional product containing any one of adsorption, deodorization, and hygroscopicity, Pseudomonas aeruginosa and Klebsiella pneumoniae caused by condensation and fine chuck inside the product. ), Staphylococcus aureus (Staphylococcus aureus), allergic (allergy) and asthma (asthma) causing pathogenic microorganisms (cladosporium), Alternaria (Alternaria), such as causing the problem.

한편 본 출원인의 등록실용신안 제20-0370971호는 습도인지형 벽지에 관한 것으로서, 습도를 인지하는 기능을 가지고 있는 물질로 코팅 또는 침적처리한 실리카 겔, 알루미노-실리케이트 비드, 제올라이트 등의 흡방습제를 20㎛ 이하의 입자크기로 스캐터링(Scattering)하여 제품의 표면 최상부에 부착함으로써 습도 인지 및 인테리어 효과를 극대화하도록 하는 내용이 기술되어 있다. 그러나 이러한 습도인지형 벽지는 벽지 자체의 구조적인 제한으로 인하여 조습기능이 충분치 못하고, 또한 함습율도 낮아 공기 중의 습도에 대해 충분히 습도인지를 할 수 있을 정도로 변색되지 못한다는 단점이 있다.Meanwhile, the applicant's registered utility model No. 20-0370971 relates to a humidity-aware wallpaper, and a moisture absorbent such as silica gel, alumino-silicate beads, and zeolite coated or deposited with a material having a function of detecting humidity. Scattering to a particle size of 20㎛ or less is attached to the top of the product has been described to maximize the humidity recognition and interior effect. However, due to the structural limitation of the wallpaper itself, the humidity-aware wallpaper has a disadvantage in that the humidity control function is not sufficient, and the moisture content is low, so that it is not discolored enough to recognize the humidity in the air.

본 발명은 위와 같은 종래 기술의 문제점을 해결하기 위하여 창안한 것으로 주변의 습도에 따라 색상이 변하여 습도를 감지할 수 있도록 함과 동시에 자체적으로 습도의 고저에 따라 수분을 흡수하거나 방출하여 습도를 조절할 수 있는 감습 및 조습기능을 갖는 타일을 제공함을 목적으로 한다.The present invention was devised to solve the problems of the prior art as described above, so that the color changes according to the surrounding humidity so that the humidity can be sensed, and at the same time, the moisture can be adjusted or absorbed according to the height of the humidity itself. An object of the present invention is to provide a tile having a dehumidifying and humidifying function.

상기한 바와 같이 본 발명의 목적을 달성하기 위한 감습 및 조습기능을 갖는 타일은, 다공질 판상의 기재층의 표면에 습도인지층을 형성시켜서 이루어지되, 상기 습도인지층이 코발트화합물, 철화합물, 유기염료 또는 알칼리금속이나 알칼리토금속과 결합된 화합물 등 공기 중의 수분을 흡수하여 변색하는 습도인지물질을 포 함하여 이루어진다.As described above, a tile having a humidity and humidity control function for achieving the object of the present invention is formed by forming a humidity recognition layer on the surface of the base plate layer of the porous plate, the humidity recognition layer is cobalt compound, iron compound, organic It contains humidity-sensitive materials that absorb color in the air, such as dyes or compounds combined with alkali or alkaline earth metals.

상기 코발트화합물로는 염화코발트, 상기 철화합물로는 공지의 습도인지가 가능한 화합물이 사용될 수 있다.Cobalt chloride may be used as the cobalt compound, and a compound capable of knowing a known humidity may be used as the iron compound.

상기 유기염료로는 뉴트랄 레드, 페놀 레드, 브로모티몰 블루, 페놀프탈레인, 크레졸 레드, 티몰 블루, 브로모크레졸 그린, 브로모크레졸 퍼플, 브로모크레졸 블루 또는 메틸 레드 또는 이들 중 2이상의 혼합물로 이루어지는 그룹으로부터 선택된 것이 사용될 수 있다. The organic dye includes neutral red, phenol red, bromothymol blue, phenolphthalein, cresol red, thymol blue, bromocresol green, bromocresol purple, bromocresol blue or methyl red or a mixture of two or more thereof. Any one selected from the group can be used.

상기 알칼리금속이나 알칼리토금속과 결합된 화합물도 통상적인 습도인지가 가능한 화합물이 사용될 수 있다.Compounds capable of bonding with the alkali metals or alkaline earth metals may also be used.

상기 다공질 판상의 기재층은 규조토, 백토, 황토, 점토, 알로펜, 패분, 이산화규소 를 포함하는 규산계 물질, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라이트, 세피올라이트, 제올라이트, 포졸란 또는 마이크로시멘트 등과 같은 분상 성형재료를 판상으로 성형하여 이루어진다.The porous plate-like base layer may be a diatomaceous earth, clay, loess, clay, allophene, powder, silicate-based material including silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, vermiculite, sepiolite, zeolite It is made by molding a powdery molding material such as pozzolanic or microcement into a plate.

상기 습도인지층과 기재층 사이에 수지층이 더 적층될 수 있다. 상기 수지층은 에폭시수지, 아크릴수지, 폴리에틸렌, 폴리우레탄, 페놀수지, 멜라민수지 또는 폴리염화비닐 중에서 선택되는 1종 이상의 수지로 이루어진다. 상기 기재층의 이면에는 밸런스층이 더 적층될 수 있다. 상기 습도인지층의 표면에는 투습성을 갖는 표면보호층이 더 적층될 수 있다. 상기 습도인지층의 표면에 무늬인쇄부가 더 형성될 수 있다.A resin layer may be further laminated between the humidity recognition layer and the base layer. The resin layer is composed of at least one resin selected from epoxy resin, acrylic resin, polyethylene, polyurethane, phenol resin, melamine resin or polyvinyl chloride. A balance layer may be further stacked on the back surface of the base layer. The surface protective layer having moisture permeability may be further laminated on the surface of the humidity recognition layer. The pattern printing unit may be further formed on the surface of the humidity recognition layer.

또한 본 발명에 따른 감습패널은 감습 및 조습기능을 갖는 다수의 감습타일 들을 다수의 타일고정 홈이 형성된 패널기판에 고정되어 이루어진다.In addition, the humidity panel according to the present invention is made of a plurality of tiles having a humidity control and humidity control is fixed to a panel substrate having a plurality of tile fixing grooves.

이하, 본 발명의 구체적인 실시예를 첨부한 도면을 참조하여 상세히 설명한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1 내지 도 3에 도시한 바와 같이, 상기한 바와 같이 본 발명의 목적을 달성하기 위한 감습 및 조습기능을 갖는 타일은, 다공질의, 판상의 기재층(11)의 표면에 습도인지층(12)을 형성시켜서 이루어지되, 상기 습도인지층(12)이 코발트화합물, 철화합물 또는 알칼리금속이나 알칼리토금속과 결합된 화합물 등 공기 중의 수분을 흡수하여 변색하는 습도인지물질을 포함하여 이루어짐을 특징으로 한다.As shown in Fig. 1 to Fig. 3, as described above, the tile having the humidity and humidity control function for achieving the object of the present invention is a humidity-sensitive layer 12 on the surface of the porous base plate layer 11. The humidity recognition layer 12 is characterized in that it comprises a humidity recognition material that absorbs moisture in the air, such as cobalt compound, iron compound or a compound combined with alkali metal or alkaline earth metal. .

상기 다공질의, 판상의 기재층(11)은 내부에 많은 기공을 포함하여 이 기공 내로 습기가 응결되어 수분을 함유 내지는 내포하는 함습기능을 갖는 것으로서, 특히 벽체 등에의 고정을 용이하게 하기 위하여 얇은 판상으로 성형된 것이다. 이러한 형상을 통상 "타일"이라고 하며, 본 발명에서는 달리 특별히 언급하지 않는 한, 유약 등의 처리를 하지 않아 표면에 기공들이 노출된 상태의 것을 그대로 사용한다. 종래의 장식용 타일의 경우, 장식성을 높이기 위하여 유약으로 표면을 처리한 후, 소성하여 상기 유약이 유리질로 변화되면서 표면이 매끄럽고 광택이 나도록 함에 비해, 본 발명에서는 함습기능 및 습도인지기능을 위하여 유약처리를 하지 않는 것이 바람직하다. 그러나, 달리 본 발명에 따른 타일의 경우도 상기 흡도인지층이 형성되지 않은 부분에는 유약의 처리에 의하여 매끄럽고, 광택이 있는 표면을 형성할 수도 있음은 당업자에게는 당연히 이해될 수 있는 것이다.The porous, plate-like base material layer 11 includes a lot of pores therein and has a moisture-condensing function containing moisture or condensation by moisture condensation into the pores, and in particular, a thin plate-like layer for facilitating fixing to a wall or the like. Molded into. Such a shape is generally referred to as a "tile", and in the present invention, unless otherwise specified, a state in which pores are exposed on the surface without being treated with glaze or the like is used as it is. In the case of conventional decorative tiles, the surface of the glaze is treated with a glaze to enhance the decor, and then fired so that the surface is smooth and glossy as the glaze is changed into glassy, in the present invention, the glaze treatment for the moisture function and the humidity recognition function. It is preferable not to. However, it will be understood by those skilled in the art that, in the case of the tile according to the present invention, a smooth, glossy surface may be formed on the part where the absorbent recognition layer is not formed by the treatment of glaze.

상기 기재층(11)의 표면에 상기 습도인지층(12)의 형성은 습도인지물질이 상 기 기재층(11)의 표면 상에 분포하도록 하는 것에 의해 형성될 수 있다. 예를 들어, 상기 습도인지층(12)은 습도인지물질이 용해된 용액을 상기 기재층(11)의 표면에 적하시키거나 분사하는 등의 방법으로 기재층(11)의 기공들 사이로 함침되도록 하는 것에 의하여 도 1에 나타낸 바와 같이 기재층(11)의 표면 쪽에 습도인지물질이 내포된 습도인지층(12)을 형성시킬 수 있다. 그러나 본 발명은 이에 제한되는 것은 아니며, 통상의 도료용 바인더에 상기 습도인지물질을 혼합하고, 통상의 도료용 용제를 가하여 점도를 조절하고, 상기 기재층(11)의 표면에 도포함으로써 도 2에 나타낸 바와 같이 습도인지층(12)을 형성할 수도 있다. 달리, 도 3에 나타낸 바와 같이, 기재층(11)의 표면 일부에 음각을 수행하여 홈을 형성하고, 이 홈 내에 펠렛(pellet)으로 성형한 습도인지층(12)을 내삽하여 고정시키는 것도 가능하며, 본 발명은 이들에 제한되는 것은 아니며, 기재층(11) 상에 습도인지층(12)을 형성시키는 것은 어느 방법이나 가능함은 당업자에게는 당연히 이해될 수 있는 것이다. 상기한 바와 같이 펠렛으로 성형한 습도인지층(12)은 상기 기재층(11)에 형성된 홈에 착탈가능하게 고정될 수 있다. 예를 들어, 인쇄에 의한 경우, 상기 기재층(11) 상에 습도인지물질을 포함하는 조성물을 인쇄, 특히 공지의 그라비아인쇄, 플렉소인쇄, 오프셋인쇄 또는 스크린인쇄 등에 의해 인쇄하여 습도인지층(12)을 형성시킬 수도 있다.The humidity sensing layer 12 may be formed on the surface of the base layer 11 by forming a humidity sensing material on the surface of the base layer 11. For example, the humidity recognition layer 12 may be impregnated between the pores of the base layer 11 by dropping or spraying a solution in which the humidity sensing material is dissolved onto the surface of the base layer 11. As a result, as shown in FIG. 1, the humidity recognition layer 12 containing the humidity-sensitive material may be formed on the surface side of the substrate layer 11. However, the present invention is not limited thereto, and the humidity-sensitive substance is mixed with a conventional paint binder, a viscosity is adjusted by adding a conventional paint solvent, and the coating is applied to the surface of the base layer 11 in FIG. 2. As shown, the humidity sensitive layer 12 may be formed. Alternatively, as shown in FIG. 3, it is also possible to indent a portion of the surface of the base layer 11 to form a groove, and to insert and fix the humidity recognition layer 12 molded into pellets in the groove. The present invention is not limited thereto, and any method or method of forming the humidity-sensitive layer 12 on the base layer 11 may be naturally understood by those skilled in the art. As described above, the humidity recognition layer 12 formed into pellets may be detachably fixed to the groove formed in the base layer 11. For example, in the case of printing, the composition containing the humidity-sensitive material on the base layer 11 is printed, in particular, by printing by a gravure printing, flexo printing, offset printing or screen printing, etc. 12) may be formed.

상기 다공질의, 판상의 기재층(11)은 규조토, 백토, 황토, 점토, 알로펜, 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라이트, 세피올라이트, 제올라이트, 포졸란 또는 마이크로시멘트 등과 같은 분상 성형재료를 판상으로 성형하여 이루어진다. 상기한 분상 성형재료들은 각 재료들의 특성에 따라 통상의 방법을 이용하여 판상으로 성형할 수 있다. 예를 들어, 규조토, 백토, 황토, 점토 또는 알로펜 등은 물을 가하여 반죽하고, 이를 판상으로 성형한 후, 가열, 소성시켜 타일로 성형할 수 있음은 당업자에게는 당연히 이해될 수 있는 것이다. 상기에서 알로펜은 화산재의 천연광물점토를 구성하는 주성분으로서, 다공질의 미세한 입자들로 구성되어 있으며, 일본에서는 "에코카라트"라는 상품명으로 판매되고 있다. 에코카라트는 무엇보다 새집증후군의 원인인 포름알데히드의 저감 기능이 뛰어나다는 장점을 가지고 있는 것으로 알려져 있다. 시공 후, 24시간이 지나면 급속도로 농도가 떨어지고, 이후에도 저감효과가 지속되는 것으로 일본 최초로 일본건축센터로부터 실내공기 중의 휘발성유기화합물 오염을 저감시키는 건축재로 인증을 받았을 정도다. 또 에코카라트는 다공질 미세한 입자들로 뛰어난 습도조절기능을 지니고 있는 화산재를 주재료로 만들어져 규조토의 4 내지 5배, 조습벽지의 15배에 이르는 흡, 방습 능력을 지닌 것으로 알려져 있다. 에코카라트는 실내의 습도가 높을 경우 습기를 흡수해 습도를 낮추고, 습도가 낮을 때는 반대로 습기를 방출한다. 때문에 생활공간의 최적 습도(50% 내지 60%)를 유지, 잡균의 번식억제를 통한 알레르기, 아토피 질환 등을 예방할 수 있다. 한편 일본 연구기관의 실험 결과 에코카라트는 악취의 주성분인 암모니아, 트리메칠아민 등의 알카리성 냄새와 석화수소, 메틸머캡탄 등의 산성 냄새 성분에도 효과를 갖고 있다. 냄새의 제거와 경감 효과가 규조토벽 및 다른 제품들보다도 뛰어난 것으로 입증됐다. 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나 이트, 버미큘라이트, 세피올라이트, 제올라이트 또는 포졸란 등은 유기바인더 또는 무기바인더와 혼합하여 성형한 후, 소성하여 타일로 성형할 수 있음은 당업자에게는 용이하게 이해될 수 있는 것이다. 또한 상기 마이크로시멘트는 자체의 수화작용으로 인하여 물과의 혼합에 의해 단단한 콘크리트를 구성하며, 역시 수화작용에 의해 타일형상으로 성형할 수 있다. 마이크로시멘트는 무기질계 지반주입재와 각종 보수용재 또는 보강용재에 적합하도록 개발된 미립자 시멘트로서, 일반적인 미립자 시멘트의 특성인 조강성, 고강도, 고내구성은 물론 균일한 입경 크기가 요구되는 지반주입재와 보수보강재에 탁월한 성능을 발휘한다. 마이크로시멘트의 특성으로는 조기강도가 우수하고(미분말이므로 활성화가 빠르게 진행하여 조기강도가 우수), 고강도의 발현이 가능하고(치밀한 매트릭스를 조직하므로 강도 발현율이 우수), 침투성이 우수하고(입경이 고르고 최대입경 크기가 작아 높은 침투율을 발현), 탁월한 내구성을 나타낸다(염과 산 등의 유해물에 대한 내화학성이 우수). The porous, plate-like base layer 11 is made of diatomaceous earth, clay, ocher, clay, allophene, patch, silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, vermiculite, sepiolite, zeolite, It is made by molding a powdery molding material such as pozzolanic or microcement into a plate shape. The powder-forming molding materials described above may be shaped into plates using conventional methods according to the properties of the materials. For example, diatomaceous earth, clay, ocher, clay, or allophen, etc. can be kneaded by adding water, molded into a plate, and then heated and fired to form a tile. In the above, allophene is a main component constituting the natural mineral clay of volcanic ash, and is composed of porous fine particles, and is sold under the trade name "Ecokarat" in Japan. Eco-carat is known to have the advantage of reducing formaldehyde, the cause of sick house syndrome. After 24 hours of construction, the concentration drops rapidly, and the reduction effect continues afterwards. It was the first Japanese construction center to be certified as a building material to reduce volatile organic compound contamination in indoor air. In addition, eco-carat is made of volcanic ash, which has excellent humidity control function with porous fine particles, and is known to have 4-5 times the diatomaceous earth's ability to absorb and moisture as much as 15 times the humidity wall. Ecocarat absorbs moisture when the humidity is high in the room, lowers the humidity, and releases moisture when the humidity is low. Therefore, maintaining the optimal humidity (50% to 60%) of the living space, it is possible to prevent allergies, atopic diseases, etc. through the suppression of propagation of various bacteria. Echo Karat, on the other hand, has an effect on alkaline odors such as ammonia and trimethylamine, and acidic odors such as petrified hydrogen and methylmercaptan. Odor removal and abatement has been proven to be superior to diatomaceous earth walls and other products. Shell powder, silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, vermiculite, sepiolite, zeolite or pozzolan are mixed with an organic binder or an inorganic binder, and then fired to form a tile. It can be easily understood by those skilled in the art. In addition, the microcement constitutes a hard concrete by mixing with water due to its hydration, and can also be formed into a tile shape by hydration. Microcement is a microparticle cement developed to be suitable for inorganic ground injection materials and various repair or reinforcement materials. Ground cement and repair reinforcement materials that require uniform grain size as well as roughness, high strength and high durability, which are characteristics of general particulate cement Excellent performance. The characteristics of the microcement are excellent early strength (because of fine powder, the activation progresses quickly and excellent early strength), high strength can be expressed (high strength expression rate due to the formation of dense matrix), and excellent penetration (particle size Even and small maximum particle size, high penetration rate), excellent durability (excellent chemical resistance against harmful substances such as salt and acid).

상기 습도인지층(12)을 형성하는 습도인지물질은 공지된 것으로서, 특히 코발트화합물, 철화합물 또는 알칼리금속이나 알칼리토금속과 결합된 화합물 등 공기 중의 수분을 흡수하여 변색하는 물질 중에서 선택된 것이 사용될 수 있다. Humidity-sensitive material forming the humidity-sensitive layer 12 is known, in particular, selected from materials that absorb and discolor moisture in the air, such as cobalt compounds, iron compounds or compounds combined with alkali metals or alkaline earth metals may be used. .

예를 들면, 상기 코발트화합물로는 염화코발트, 상기 유기염료로는 뉴트랄 레드, 페놀 레드, 브로모티몰 블루, 페놀프탈레인, 크레졸 레드, 티몰 블루, 브로모크레졸 그린, 브로모크레졸 퍼플, 브로모크레졸 블루 또는 메틸 레드 또는 이들 중 2이상의 혼합물로 이루어지는 그룹으로부터 선택된 것이 사용될 수 있다. For example, the cobalt compound is cobalt chloride, the organic dye is neutral red, phenol red, bromothymol blue, phenolphthalein, cresol red, thymol blue, bromocresol green, bromocresol purple, bromocresol Blue or methyl red or a mixture selected from the group consisting of two or more thereof can be used.

도 4에 도시한 바와 같이, 상기 습도인지층(12)과 기재층(11) 사이에 수지 층(21)이 더 적층될 수 있다. 이 수지층은 에폭시수지, 아크릴수지, 폴리에틸렌, 폴리우레탄, 페놀수지, 멜라민수지 또는 폴리염화비닐수지 중에서 선택되는 1종 이상의 수지로 형성할 수 있다. As shown in FIG. 4, a resin layer 21 may be further stacked between the humidity recognition layer 12 and the base layer 11. The resin layer may be formed of at least one resin selected from epoxy resin, acrylic resin, polyethylene, polyurethane, phenol resin, melamine resin or polyvinyl chloride resin.

도 5에 도시한 바와 같이, 상기 기재층(11)의 이면에는 밸런스층(31)이 더 적층될 수 있다. 상기 밸런스층(31)은 공지의 합판, 무기질 보드류, 합성수지로 이루어진 판상 제품이나 하드보드지 등으로 이루어지며, 예를 들어 타카작업 등 시공작업을 용이하게 하는 기능을 한다. 이러한 밸런스층(31)의 적층 및 이를 이용한 타카작업 등은 당업자에게는 용이하게 이해될 수 있는 것이다. 타카작업이라 함은 수동, 전동, 유압 또는 공압 등을 이용하여 스테이플러와 유사한 철심을 고정시키고자 하는 대상체에 박아 넣어 고정시키는 것을 의미한다.As shown in FIG. 5, a balance layer 31 may be further stacked on the back surface of the base layer 11. The balance layer 31 is made of a plate-like product or hard board made of known plywood, inorganic boards, synthetic resin, and the like, for example, functions to facilitate construction work such as taka work. The stacking of the balance layer 31 and the taka work using the same may be easily understood by those skilled in the art. Taka work means driving by fixing to the object to be fixed to the staple-like iron core using manual, electric, hydraulic or pneumatic.

도 6에 도시한 바와 같이, 상기 습도인지층(12)의 표면에는 투습성을 갖는 표면보호층(41)이 더 적층될 수 있다. 상기 표면보호층(41)은 그 하방에 위치하는 습도인지층(12)을 구성하는 물질이 직접 인체에 닿거나 또는 손을 통한 접촉으로 눈, 코 또는 입에 들어가는 것을 방지하고, 습도인지층(12)이 마모되거나 오염되는 것을 방지하면서 습기는 통과시켜 습도인지층(12)에 포함된 습도인지물질이 습기에 대응하여 변색되도록 하는 기능을 한다. 상기 표면보호층(41)은 공지의 통기성 필름을 피복하는 것에 의해 형성시킬 수 있다. 투습성의 표면보호층(41)은 0.01 내지 0.15㎛의 범위 이내의 두께의 필름을 열융착시키는 방법으로 고정시킬 수 있다.As shown in FIG. 6, a surface protective layer 41 having moisture permeability may be further stacked on the surface of the humidity recognition layer 12. The surface protective layer 41 prevents substances constituting the humidity recognition layer 12 positioned below the human body from entering the eyes, nose, or mouth by direct contact with the human body or through contact with the hands, and the humidity recognition layer ( While preventing moisture from being worn or contaminated 12, the moisture passes therethrough so that the humidity-sensitive material contained in the humidity-sensitive layer 12 discolors in response to moisture. The surface protection layer 41 can be formed by coating a known breathable film. The moisture-permeable surface protection layer 41 can be fixed by the method of heat-sealing the film of the thickness within the range of 0.01-0.15 micrometer.

도 1 및 도 9에 나타난 바와 같이, 상기 습도인지층(12)의 표면에는 무늬인쇄부(13)가 더 형성될 수 있다. 상기 무늬인쇄부(13)는 불투명한 도료 등의 도포 에 의해 형성되며, 상기 습도인지층(12)의 변색의 정도를 육안으로 직접적으로 무늬인쇄부(13)의 무늬를 구성하는 색상과 비교할 수 있도록 하여 변색의 정도를 더욱 쉽게 인지할 수 있도록 기능한다.1 and 9, a pattern printing part 13 may be further formed on the surface of the humidity recognition layer 12. The pattern printing unit 13 is formed by applying an opaque paint or the like, and the degree of discoloration of the humidity recognition layer 12 can be directly compared with the color constituting the pattern of the pattern printing unit 13 with the naked eye. This function makes it easier to recognize the degree of discoloration.

또한 도 7에 도시한 바와 같이, 본 발명에 따른 감습패널은 감습 및 조습기능을 갖는 다수의 감습타일(10)들을 다수의 타일고정홈(52)이 형성된 패널기판(51)에 고정시켜서 이루어짐을 특징으로 한다. 이는 여러 장의 작은 감습타일들을 하나의 패널로 구성하여 취급, 보관 및 설치의 작업을 용이하게 할 수 있도록 하는 기능을 한다. 즉, 현장에서 작은 여러 장의 감습타일들을 일일이 고정시키는 대신 미리 패널기판(51)에 형성된 타일고정홈(52)에 여러 장의 감습타일(10)들을 고정시킨 하나의 큰 감습패널(50)을 현장에서 고정시키는 작업을 할 수 있도록 함으로써 한 번에 많은 양의 감습타일들이 고정된 것과 같은 작업효과를 얻을 수 있도록 할 수 있다.In addition, as shown in FIG. 7, the moisture absorbing panel according to the present invention is formed by fixing a plurality of moisture-absorbing tiles 10 having a moisture absorbing and controlling function to a panel substrate 51 on which a plurality of tile fixing grooves 52 are formed. It features. This function makes it easy to handle, store and install several small humidity tiles in one panel. That is, instead of fixing several small pieces of humidity tiles in the field, one large humidity panel 50 in which several sheets of humidity tiles 10 are fixed in the tile fixing groove 52 formed in the panel substrate 51 in the field is installed. By allowing you to do the fixing work, you can get the same effect as fixing a lot of moisture tiles at one time.

이하에서 본 발명의 바람직한 실시예 및 비교예들이 기술되어질 것이다.Hereinafter, preferred embodiments and comparative examples of the present invention will be described.

이하의 실시예들은 본 발명을 예증하기 위한 것으로서 본 발명의 범위를 국한시키는 것으로 이해되어져서는 안될 것이다.The following examples are intended to illustrate the invention and should not be understood as limiting the scope of the invention.

실시예 1Example 1

BET 식(Brunauer, Emmett, Teller Equation)에 따라 측정된 기공 크기(pore size)가 40 내지 200㎛인 규조토 분말을 100㎜(길이)*100㎜(넓이)*7㎜(두께)의 규격으로 가압, 성형한 후, 1차로 120℃에서 건조시키고, 2차로 900℃까지 승온시키면서 소성시켜 타일을 구성하는 기재층을 형성하고, 이 기재층의 표면에 50중량%의 농도의 염화코발트 수용액 0.5㎖를 주입, 함침시킨 후, 건조시켜 본 발명에 따른 감습타일을 제조하였다.Pressurized diatomaceous earth powder with a pore size of 40 to 200 µm, measured according to the BET equation (Brunauer, Emmett, Teller Equation) to a standard of 100 mm (length) * 100 mm (width) * 7 mm (thickness) After molding, the substrate was first dried at 120 ° C. and calcined while heating up to 900 ° C. in a second manner to form a substrate layer constituting the tile, and 0.5 ml of an aqueous solution of cobalt chloride at a concentration of 50% by weight was placed on the surface of the substrate layer. After injection, impregnation and drying, a moisture-sensitive tile according to the present invention was prepared.

비교예Comparative example

기재층으로서 상기한 바와 같은 소성 타일이 아닌 벽지용 종이를 사용하는 것을 제외하고는 상기 실시예 1과 동일하게 수행하여 감습지를 제조하였다.A damp paper was prepared in the same manner as in Example 1, except that the paper for wallpaper was used instead of the calcined tile as the substrate layer.

실험예 1Experimental Example 1

습도인지실험Humidity Cognitive Experiment

상대습도에 따른 변색에 의해 습도를 인지할 수 있는 지의 여부에 대한 실험을 다음과 같이 수행하였다. 대형 항온항습조 내에 상기 실시예 1의 감습타일과 비교예의 감습지를 함께 투입하고, 상대습도를 변화시키면서 습도변화에 따른 색상의 변화를 육안으로 관찰하였으며, 그 결과를 하기 표 1에 나타내었다.The experiment was performed as to whether the humidity can be recognized by the discoloration according to the relative humidity. In the large-scale constant temperature and humidity bath, the damping tile of Example 1 and the damping paper of the comparative example were put together, and the change of the color according to the humidity change was observed visually while changing the relative humidity, and the results are shown in Table 1 below.

상대습도 변화Relative humidity change 비교예Comparative example 실시예 1Example 1 32%32% 푸른색Blue 푸른색Blue 55%55% 푸른색Blue 보라색purple 80%80% 붉은색Red 붉은색Red 55%55% 푸른색Blue 붉은색Red 32%32% 푸른색Blue 보라색purple 80%80% 붉은색Red 붉은색Red 32%32% 푸른색Blue 보라색purple

상기 표 1에 나타난 바와 같이, 본 발명에 따른 감습타일은 기재층을 종이로 사용하는 것을 제외하고는 동일한 감습인지물질을 동일한 농도로 사용하는 비교예와 비교하여 볼 때, 동일한 습도변화에 대해 비교예가 4회의 변색됨에 비해 실시예 1은 5회의 변색이 나타나고, 색상도 비교예가 푸른색과 붉은색의 2색으로 변색되는 것에 비해 실시예 1은 푸른색과 붉은색에 더해 뚜렷하게 보라색으로 변색되는 것을 확인할 수 있었다.As shown in Table 1, the moisture-sensitive tile according to the present invention is compared to the same humidity change when compared with the comparative example using the same moisture-sensitive cognitive material in the same concentration except for using the substrate layer as a paper Example 1 shows five discolorations compared to the case of four discolorations, and Example 1 shows a distinctive discoloration of purple in addition to blue and red colors, while the comparative example discolors into two colors of blue and red. I could confirm it.

실험예 1Experimental Example 1

조습기능실험Humidity Function Test

대형 항온항습조 내에 상기 실시예 1의 감습타일과 비교예의 감습지를 함께 투입하고, 시간의 경과에 따른 흡습량을 측정하였으며, 그 결과를 도 8에 나타내었다.In the large-scale constant temperature and humidity bath, the damping tile of Example 1 and the damping paper of the comparative example were put together, and the amount of moisture absorption was measured over time, and the results are shown in FIG. 8.

도 8에 나타난 바와 같이, 본 발명에 따른 감습타일(실시예 1)은 감습지(비교예)에 비하여 흡습도에서 현격한 차이가 나며, 특히 본 발명에 따른 감습타일은 외부의 습도변화에 따라 수분을 흡수 및 방출하는 양이 비교예에 비하여 현저하게 커서 조습기능이 우수함을 확인할 수 있었다. 도 8에서 흡습도의 단위는 ㎎/㎠이다.As shown in FIG. 8, the humidity tile according to the present invention (Example 1) has a drastic difference in hygroscopicity compared to the wet paper (comparative example), and in particular, the humidity tile according to the present invention is changed according to an external humidity change. The amount of absorbing and releasing moisture was significantly greater than that of the comparative example, and it was confirmed that the humidity control function was excellent. In Figure 8, the unit of hygroscopicity is mg / cm 2.

실시예 2Example 2

상기 실시예 1의 감습타일의 표면에 통상의 불투명한 도료를 이용하여 클로버 잎의 형상의 무늬인쇄부를 더 형성시켜 본 발명에 따른 감습타일의 무늬인쇄부의 색상과 무늬인쇄부 이외의 습도인지층의 부분의 습도에 따른 변색을 육안으로 더욱 쉽게 대조하여 관찰할 수 있도록 한 감습타일을 제조하였다.The pattern printing part of the shape of the clover leaf is further formed on the surface of the moisture-sensitive tile of Example 1 by using a conventional opaque paint, and the color of the pattern-printing part of the moisture-sensitive tile according to the present invention and the humidity recognition layer other than the pattern printing part. Humidity tiles were prepared to easily observe the discoloration according to the humidity of the part with the naked eye.

상기 실시예 2의 감습타일을 상대습도 25%의 상태 및 상대습도 50%의 상태의 분위기에서 사진촬영을 하였으며, 그 결과를 도 9 및 도 10에 나타내었다.The wet tiles of Example 2 were photographed in an atmosphere of 25% relative humidity and 50% relative humidity, and the results are shown in FIGS. 9 and 10.

상대습도 25%의 상태에서는 도 9에 나타난 바와 같이 감습타일의 무늬인쇄부가 뚜렷하게 육안으로 볼 수 있으나, 상대습도 50%의 상태에서는 도 10에 나타난 바와 같이 감습타일의 무늬인쇄부가 육안으로 볼 수 없을 정도로 유사한 색으로 변색됨을 확인할 수 있었다. 따라서 무늬의 육안식별 가능여부에 따라 상대습도의 변화를 쉽게 인지할 수 있음을 확인할 수 있었다.In the state of 25% relative humidity, the pattern printing part of the moisture-sensing tile can be clearly seen with the naked eye as shown in FIG. 9, but in the state of relative humidity 50%, the pattern printing part of the moisture-sensing tile cannot be seen by the naked eye. It was confirmed that the color fading to a similar degree. Therefore, it was confirmed that the change of relative humidity could be easily recognized depending on whether the pattern could be visually identified.

전술한 바와 같이, 본 발명은 주변의 습도에 따라 색상이 변하여 습도를 감지할 수 있도록 함과 동시에 자체적으로 습도의 고저에 따라 수분을 흡수하거나 방출하여 습도를 조절할 수 있고, 탈취 및 흡착기능을 나타낼 수 있는 감습 및 조습기능을 갖는 감습타일을 제공하며, 그에 따라 방안의 습도상태가 적절한 지를 지시해주고, 거기에 더해 실내장식의 효과를 더해 주어 내부장식 등을 돕는 기능을 하며, 집안에 별도로 습도계 등을 구비하지 않아도 실내환경의 습도를 인지할 수 있도록 하는 효과를 제공한다.As described above, the present invention allows the color to be changed according to the surrounding humidity, and at the same time, it can adjust the humidity by absorbing or releasing moisture according to the height of the humidity itself, and exhibits deodorization and adsorption functions. It provides humidity tiles with moisture and humidity control functions, and it indicates whether the humidity condition of the room is appropriate accordingly, and adds the effect of interior decoration to help interior decoration, etc. It does not have to provide the effect to recognize the humidity of the indoor environment.

Claims (10)

다공질 판상의 기재층의 표면에 습도인지층을 형성시켜서 이루어지되, 상기 습도인지층이 코발트화합물, 철화합물, 유기염료 또는 알칼리금속이나 알칼리토금속과 결합된 화합물 등 공기 중의 수분을 흡수하여 변색하는 습도인지물질을 포함하여 이루어짐을 특징으로 하는 감습 및 조습기능을 갖는 타일.Humidity is formed by forming a humidity recognition layer on the surface of the substrate layer of the porous plate, the humidity recognition layer absorbs moisture in the air, such as cobalt compound, iron compound, organic dye or a compound combined with alkali metal or alkaline earth metal Tile with humidity and humidity control, characterized in that it comprises a cognitive substance. 제 1 항에 있어서,The method of claim 1, 상기 코발트화합물이 염화코발트임을 특징으로 하는 감습 및 조습기능을 갖는 타일.Tile having a humidity and humidity control, characterized in that the cobalt compound is cobalt chloride. 제 1 항에 있어서,The method of claim 1, 상기 유기염료가 뉴트랄 레드, 페놀 레드, 브로모티몰 블루, 페놀프탈레인, 크레졸 레드, 티몰 블루, 브로모크레졸 그린, 브로모크레졸 퍼플, 브로모크레졸 블루 또는 메틸 레드 또는 이들 중 2이상의 혼합물로 이루어지는 그룹으로부터 선택된 것임을 특징으로 하는 감습 및 조습기능을 갖는 타일.The organic dye group consisting of neutral red, phenol red, bromothymol blue, phenolphthalein, cresol red, thymol blue, bromocresol green, bromocresol purple, bromocresol blue or methyl red or a mixture of two or more thereof Tiles with moisture and humidity control, characterized in that selected from. 제 1 항에 있어서,The method of claim 1, 상기 다공질의, 판상의 기재층이 규조토, 백토, 황토, 점토, 알로펜, 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라 이트, 세피올라이트, 제올라이트, 포졸란 또는 마이크로시멘트 등과 같은 분상 성형재료를 판상으로 성형하여 이루어짐을 특징으로 하는 감습 및 조습기능을 갖는 타일.The porous, plate-like base layer comprises diatomaceous earth, clay, loess, clay, allophene, patch, silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, vermiculite, sepiolite, zeolite, pozzolan Or a tile having a humidity and humidity control, characterized in that formed by forming a powder-like molding material, such as microcement into a plate shape. 제 1 항에 있어서,The method of claim 1, 상기 습도인지층과 기재층 사이에 수지층이 더 적층되어 이루어짐을 특징으로 하는 감습 및 조습기능을 갖는 타일.Tile having a humidity and humidity control, characterized in that the resin layer is further laminated between the humidity recognition layer and the base layer. 제 5 항에 있어서,The method of claim 5, wherein 상기 수지층이 에폭시수지, 아크릴수지, 폴리에틸렌, 폴리우레탄, 페놀수지, 멜라민수지 또는 폴리염화비닐수지 중에서 선택되는 1종 이상의 수지로 이루어짐을 특징으로 하는 감습 및 조습기능을 갖는 타일.Tile having moisture and humidity control, characterized in that the resin layer is made of at least one resin selected from epoxy resin, acrylic resin, polyethylene, polyurethane, phenol resin, melamine resin or polyvinyl chloride resin. 제 1 항에 있어서,The method of claim 1, 상기 기재층의 이면에 밸런스층이 더 적층되어 이루어짐을 특징으로 하는 감습 및 조습기능을 갖는 타일.Tile having a moisture and humidity control, characterized in that the balance layer is further laminated on the back surface of the base layer. 제 1 항에 있어서,The method of claim 1, 상기 습도인지층의 표면에 투습성을 갖는 표면보호층이 더 적층되어 이루어짐을 특징으로 하는 감습 및 조습기능을 갖는 타일.The tile having a humidity and humidity control, characterized in that the surface protective layer having a moisture permeability is further laminated on the surface of the humidity recognition layer. 제 1 항에 있어서,The method of claim 1, 상기 습도인지층의 표면에 무늬인쇄부가 더 형성되어 이루어짐을 특징으로 하는 감습 및 조습기능을 갖는 타일.Tile having a humidity and humidity control, characterized in that the pattern printing is further formed on the surface of the humidity recognition layer. 다수의 타일고정 홈이 형성된 패널기판과 상기 다수의 타일고정 홈에 타일이 고정된 패널에 있어서, 상기 타일이 상기 청구항 제 1 항 내지 제 9 항 중, 어느 한 항에 기재된 감습 및 조습기능을 갖는 타일인 것을 특징으로 하는 패널.A panel substrate in which a plurality of tile fixing grooves are formed and a panel in which tiles are fixed in the plurality of tile fixing grooves, wherein the tiles have a moisture-sensing and humidity control function according to any one of claims 1 to 9. A panel characterized by being a tile.
KR1020070015513A 2007-02-14 2007-02-14 Tile having humidity sensing and humidity control function KR101413358B1 (en)