KR20080040605A - Flexible flat cable - Google Patents

Abstract

A flexible flat cable is provided to facilitate division or branching into a plurality flexible flat cables with a predetermined number of straight angle conductors by including cutting grooves on both surfaces of an insulating coating along a longitudinal direction. A flexible flat cable(10) is formed by insulating coating of a plurality of straight angle conductors(11) arranged in parallel with an insulating coating material(12) at once. The insulating coating material is composed of a flame-retardance resin composition including a resin component 100 parts by weight and a metal hydroxide 40~250 parts by weight. The resin component includes a thermoplastic polyurethane elastomer with a JIS hardness of below A97 measured according to JIS K 7311 and an ethylene acetic vinyl copolymer with an acetic vinyl unit 50~90 wt% at a ratio of 40:60 to 90:10.

Description

플렉시블 플랫 케이블{FLEXIBLE FLAT CABLE}Flexible Flat Cable {FLEXIBLE FLAT CABLE}

본 발명은 병렬로 배치한 복수 개의 평각 도체를 절연 피복 재료에 의해 일괄적으로 절연 피복 성형하여 이루어지는 플렉시블 플랫 케이블에 관한 것으로서, 더욱 상세하게는, 할로젠계 난연제를 함유하지 않는 절연 피복 재료를 사용한, 고도의 난연성을 발휘하고, 기계 물성, 내열성, 내열 노화성, 내가열 변형성, 저온 특성(저온에서의 가요성), 전기 절연성이 뛰어난 플렉시블 플랫 케이블에 관한 것이다.The present invention relates to a flexible flat cable formed by collectively insulating coating molding a plurality of flat conductors arranged in parallel with an insulating coating material, and more particularly, using an insulating coating material containing no halogen-based flame retardant. The present invention relates to a flexible flat cable that exhibits high flame retardancy, and has excellent mechanical properties, heat resistance, heat aging resistance, heat deformation resistance, low temperature characteristics (flexibility at low temperatures), and electrical insulation.

절연 전선이나 실드 전선, 절연 케이블 등의 각종 절연 피복 전선은 도체가 절연 피복 재료에 의해 절연 피복되어 있다. 절연 피복 전선에는 절연성 이외에, 일반적으로 난연성이 요구되고 있다. 따라서, 전자 기기의 기내 배선에 사용하는 절연 피복 전선의 절연 피복 재료로서 예컨대 연질 폴리염화 바이닐 수지, 난연제를 배합한 폴리올레핀 수지 조성물 등이 사용되고 있다.The conductor is insulated and coat | covered with the insulation coating material in various insulation coating wires, such as an insulated wire, a shielded wire, and an insulated cable. In addition to insulation, flame-retardant insulation wires are generally required. Therefore, for example, a soft polyvinyl chloride resin, a polyolefin resin composition incorporating a flame retardant, or the like is used as an insulation coating material of an insulated wire used for in-flight wiring of an electronic device.

연질 폴리염화 바이닐 수지는 결합 염소 원자를 함유하며, 게다가 다량의 가소제를 함유하고 있다. 폴리올레핀 수지 조성물에 배합되는 난연제는 분자 내에 브롬 원자나 염소 원자를 포함하는 할로젠계 난연제가 사용되고 있다. 할로젠계 난연제 중에서도 분자 내에 브롬 원자를 포함하는 브롬계 난연제는 난연화 효과가 높아, 일반적으로 산화 안티몬과의 병용에 의한 상승 효과를 이용하여 난연화를 행하고 있다. 브롬계 난연제는 인 화합물과의 병용에 따른 난연화 효과도 높다.Soft polyvinyl chloride resins contain bound chlorine atoms and, in addition, contain large amounts of plasticizers. As the flame retardant to be blended into the polyolefin resin composition, a halogen flame retardant containing a bromine atom or a chlorine atom in its molecule is used. Among the halogen flame retardants, bromine flame retardants containing a bromine atom in a molecule have a high flame retardant effect, and are generally flame retarded by utilizing a synergistic effect by use in combination with antimony oxide. Brominated flame retardants also have a high flame retardant effect in combination with phosphorus compounds.

그러나, 연질 폴리염화 바이닐 수지나 할로젠계 난연제를 함유하는 폴리올레핀 수지 조성물 등의 절연 피복 재료에 의해 절연 피복된 전선을 소각 처리하면 폴리염화 바이닐 수지 또는 할로젠계 난연제로부터 부식성 가스나 다이옥신류가 발생할 우려가 있다. 또한 가소제나 인 화합물을 포함하는 전선을 폐기장에 퇴적하고 있는 동안 그들이 용출되어 환경을 오염시킬 우려가 있다.However, incineration of an electric wire coated with an insulating coating material, such as a polyvinyl chloride resin or a polyolefin resin composition containing a halogen flame retardant, may cause corrosive gas or dioxins from the polyvinyl chloride resin or halogen flame retardant. There is concern. In addition, there is a fear that they will elute and pollute the environment while wires containing plasticizers or phosphorus compounds are being deposited on the dump site.

최근 환경 부하의 저감에 대한 요구가 높아지는 것에 부응하기 위하여 폴리염화 바이닐 수지나 할로젠계 난연제를 함유하지 않는 할로젠 프리 전선이 개발되어 있다.In order to meet the increasing demand for reducing environmental load, halogen-free wires containing no polyvinyl chloride resin or halogen-based flame retardant have been developed.

다른 한편, 전자 기기의 기내 배선에 사용하는 절연 전선이나 절연 케이블 등의 전선에는 일반적으로 UL(Underwriters Laboratories inc.) 규격에 적합한 제반 특성을 가질 것이 요구되고 있다. UL 규격에는 제품이 만족해야 할 난연성, 가열 변형성, 저온 특성, 피복 재료의 초기와 열노화 후의 인장 특성 등의 제반 특성에 대하여 상세하게 규정되어 있다. 이들 제반 특성 중에서도 난연성에 대해서는 VW-1 시험이라 칭해지는 수직 연소 시험에 합격할 필요가 있으며, UL 규격 중에서도 이 수직 연소 시험이 가장 까다로운 요구 항목 중 하나로 되어 있다. On the other hand, wires such as insulated wires and insulated cables used for in-flight wiring of electronic devices are generally required to have various characteristics that comply with UL (Underwriters Laboratories Inc.) standard. The UL standard specifies in detail the various properties such as flame retardancy, heat deformation, low temperature properties, and tensile properties after initial and thermal aging of the coating material. Among these characteristics, it is necessary to pass the vertical combustion test called the VW-1 test for flame retardancy, and this vertical combustion test is one of the most demanding requirements among UL standards.

할로젠 프리 전선의 절연 피복 재료로는 예컨대 폴리올레핀 수지에 수산화마그네슘이나 수산화알루미늄 등의 금속 수산화물("금속 수화물"이라고도 함)을 배합 한 난연성 수지 조성물이 사용되고 있다. 그러나, 금속 수산화물의 난연화 효과는 할로젠계 난연제에 비하여 낮기 때문에 UL 규격의 수직 연소 시험에 합격하려면 폴리올레핀 수지 내에 다량의 금속 수산화물을 배합할 필요가 있다. 그 결과, 폴리올레핀 수지 조성물의 인장 특성(인장 강도 및 인장 파단 연신도)이나 내가열 변형성 등이 현저하게 저하하여 절연 피복 재료로 부적당한 것이 된다. As an insulation coating material of a halogen-free electric wire, the flame-retardant resin composition which mix | blended the metal hydroxide (also called "metal hydrate"), such as magnesium hydroxide and aluminum hydroxide, with polyolefin resin is used, for example. However, since the flame retardant effect of the metal hydroxide is lower than that of the halogen-based flame retardant, it is necessary to blend a large amount of metal hydroxide in the polyolefin resin to pass the UL standard vertical combustion test. As a result, the tensile properties (tensile strength and tensile elongation at break), heat resistance, and the like of the polyolefin resin composition are remarkably lowered, which makes them unsuitable as an insulating coating material.

폴리올레핀 수지에 금속 수산화물을 배합한 폴리올레핀 수지 조성물로 이루어지는 절연 피복에 가속 전자선 등의 전리 방사선을 조사하여 가교함으로써 인장 특성이나 내가열 변형성을 개량할 수 있다. 그러나, 상기와 같은 할로젠 프리의 난연성 수지 조성물은 폴리염화 바이닐 수지에 비하면 고가인 것 이외에, 전리 방사선의 조사에 고가의 조사 장치를 필요로 하기 때문에 제조 비용이 더욱 증가한다는 결점이 있었다. 따라서, 가교 처리를 하지 않고도 UL 규격의 수직 연소 시험을 만족시키는 할로젠 프리 전선의 개발이 요망되고 있다. Tensile properties and heat resistance deformation can be improved by irradiating and crosslinking an insulating coating made of a polyolefin resin composition in which a polyolefin resin is blended with a metal hydroxide by irradiating ionizing radiation such as an accelerated electron beam. However, the halogen-free flame-retardant resin composition as described above has a drawback in that the production cost is further increased because it requires an expensive irradiation apparatus for irradiation with ionizing radiation, in addition to being expensive compared to polyvinyl chloride resin. Therefore, development of a halogen-free electric wire which satisfies the vertical combustion test of UL standard without crosslinking process is desired.

종래 할로젠 프리의 난연성 수지 조성물로서 에틸렌 공중합체와 폴리에스터 엘라스토머를 포함하는 수지 성분에 다량의 금속 수화물을 배합한 전송선 피복용 수지 조성물(특허 문헌 1)이 제안된 바 있다. 에틸렌 공중합체로는 아세트산 바이닐 함유량이 25 내지 85질량%인 에틸렌-아세트산 바이닐 공중합체가 사용되고 있다. 그러나 특허 문헌 1에 개시되어 있는 폴리에스터 엘라스토머를 함유하는 난연성 수지 조성물은 난연성이나 절연 저항이 반드시 충분하지 않으며, 특히 UL 규격의 수직 연소 시험에서의 합격률이 높지 않다.As a halogen-free flame retardant resin composition, a resin composition for transmission line coating (Patent Document 1) in which a large amount of metal hydrate is blended with a resin component containing an ethylene copolymer and a polyester elastomer has been proposed. As an ethylene copolymer, the ethylene-vinyl acetate copolymer whose vinyl acetate content is 25-85 mass% is used. However, the flame retardant resin composition containing the polyester elastomer disclosed in Patent Document 1 does not necessarily have sufficient flame retardancy or insulation resistance, and in particular, the pass rate in the vertical combustion test of the UL standard is not high.

에틸렌 공중합체와 폴리에스터형 및/또는 폴리에터형 세그먼트를 갖는 열가 소성 수지를 포함하는 수지 성분에 유기 퍼옥사이드 및 실레인 커플링제로 처리한 금속 수화물을 용융 혼련하여 이루어지는 난연성 수지 조성물(특허 문헌 2)이 제안된 바 있다. 특허 문헌 2에는 폴리에스터형 및/또는 폴리에터형 세그먼트를 갖는 열가소성 수지로서 예컨대 열가소성 폴리에스터 엘라스토머, 열가소성 폴리우레탄 엘라스토머 및 열가소성 폴리아마이드 엘라스토머를 들고 있다.Flame retardant resin composition obtained by melt kneading a metal hydrate treated with an organic peroxide and a silane coupling agent to a resin component comprising an ethylene copolymer and a thermoplastic resin having a polyester type and / or a polyether type segment (Patent Document 2) ) Has been proposed. Patent Document 2 holds thermoplastic polyester elastomers, thermoplastic polyurethane elastomers and thermoplastic polyamide elastomers as thermoplastic resins having polyester-type and / or polyether-type segments, for example.

그러나, 특허 문헌 2의 실시예에서 사용되고 있는 열가소성 폴리우레탄 엘라스토머(디아이씨 바이엘 폴리머 가부시키가이샤 제품, 상품명 "T-8180N")와 아세트산 바이닐 함유량이 41중량%인 에틸렌-아세트산 바이닐 공중합체(미쓰이 듀퐁 가부시키가이샤 제품, 상품명 "에바플렉스 EV40LX")를 함유하는 수지 성분에 금속 수화물을 용융 혼련한 수지 조성물을 사용한 것에서는 난연성, 기계 물성, 내열성, 내열 노화성, 내가열 변형성 등이 고도로 균형을 이룬 절연 피복을 형성하기가 어려우며, 특히 UL 규격의 수직 연소 시험에 합격하는 고도의 난연성을 보이는 절연 피복 전선을 얻기는 매우 어렵다. However, the thermoplastic polyurethane elastomer (trade name "T-8180N" manufactured by Daishi Bayer Polymer Co., Ltd., trade name "T-8180N") used in the examples of Patent Document 2 and ethylene-vinyl acetate copolymer (Mitsui DuPont Co., Ltd.) having 41% by weight of vinyl acetate In the case of using a resin composition obtained by melt-kneading a metal hydrate in a resin component containing a Shikiisha company product name "Evaplex EV40LX"), highly balanced insulation including flame retardancy, mechanical properties, heat resistance, heat aging resistance, and heat deformation resistance It is difficult to form sheaths, and it is very difficult to obtain an insulated sheathed wire that exhibits a high degree of flame retardancy, in particular passing the UL standard vertical combustion test.

플랫 케이블에서도 상기와 동일한 사정이 있어 개선이 요구되고 있다. 플랫 케이블 중에서도 병렬로 배치한 복수 개의 평각 도체를 절연 피복 재료에 의해 일괄적으로 절연 피복 성형하여 이루어지는 플랫 케이블은 플렉시블 플랫 케이블(FFC)이라 불리는 띠형의 케이블이며, 전자 기기 등의 가동 부분이나 좁은 장소에서의 사용에 적합하다.Flat cables have the same circumstances as above, and improvement is required. Among flat cables, a flat cable formed by collectively insulating coating a plurality of flat conductors arranged in parallel with an insulating coating material is a strip-shaped cable called a flexible flat cable (FFC). Suitable for use in

플렉시블 플랫 케이블의 절연 피복 재료로는 예컨대 폴리염화 바이닐 수지가 사용되고 있다(특허 문헌 3). 염화 바이닐 수지는 결합 염소 원자를 포함하는데다 가 연질화를 위하여 다량의 연화제를 함유시킬 필요가 있다. 실제로 특허 문헌 3에는 염화 바이닐 수지의 연질화를 위하여 다량의 가소제를 함유시킨 것이 기재되어 있다. 이러한 연질 폴리염화 바이닐 수지는 소각하면 부식성 가스나 다이옥신류가 발생할 위험이 있는 것 이외에 폐기 후에 가소제가 용출될 우려가 있다. As an insulating coating material of a flexible flat cable, polyvinyl chloride resin is used, for example (patent document 3). The vinyl chloride resin contains a bound chlorine atom and needs to contain a large amount of softener for softening. In fact, Patent Document 3 describes that a large amount of plasticizer is contained for soft nitriding of vinyl chloride resin. Such soft polyvinyl chloride resins may incur corrosive gases or dioxins when incinerated, and there is a concern that the plasticizer may elute after disposal.

[특허 문헌 1] 일본 특허 공개 2004-10840호 공보[Patent Document 1] Japanese Unexamined Patent Publication No. 2004-10840

[특허 문헌 2] 일본 특허 공개 2004-51903호 공보[Patent Document 2] Japanese Unexamined Patent Publication No. 2004-51903

[특허 문헌 3] 일본 특허 공개 평 1-276514호 공보 [Patent Document 3] Japanese Unexamined Patent Application Publication No. 1-276514

본 발명의 과제는 병렬로 배치한 복수 개의 평각 도체를 절연 피복 재료에 의해 일괄적으로 절연 피복 성형하여 이루어지는 플렉시블 플랫 케이블로서, 결합 할로젠 원자나 할로젠계 난연제를 포함하지 않는 절연 피복 재료를 이용하여 UL 규격을 만족시키는 고도의 난연성을 보이며, 가요성, 기계 물성, 내열성, 내열 노화성, 내가열 변형성, 저온 특성, 전기 절연성 등이 뛰어난 플렉시블 플랫 케이블을 제공하는 것에 있다. SUMMARY OF THE INVENTION An object of the present invention is to provide a flexible flat cable in which a plurality of flat conductors arranged in parallel are insulated and molded by an insulating coating material, using an insulating coating material containing no bonded halogen atoms or a halogen flame retardant. The present invention provides a flexible flat cable that exhibits a high flame retardancy that satisfies UL standards, and is excellent in flexibility, mechanical properties, heat resistance, heat aging resistance, heat deformation resistance, low temperature characteristics, and electrical insulation.

본 발명의 다른 과제는 상기 제반 특성을 구비함과 아울러, 원하는 평각 도체 수를 포함하는 복수 개의 플렉시블 플랫 케이블로 용이하게 분할 또는 분기할 수 있는 플렉시블 플랫 케이블을 제공하는 것에 있다. Another object of the present invention is to provide a flexible flat cable that can be easily divided or branched into a plurality of flexible flat cables having the above characteristics and having a desired number of flat conductors.

본 발명의 또 다른 과제는, 상기 제반 특성을 구비함과 아울러, 원한다면 깔끔하게 접거나 묶기가 용이한 플렉시블 플랫 케이블을 제공하는 것에 있다. Another object of the present invention is to provide a flexible flat cable having the above characteristics and easy to fold or bundle neatly if desired.

본 발명자들은 상기 과제를 해결하기 위하여 예의 연구한 결과, 경도가 특정 범위 내에 있는 열가소성 폴리우레탄 엘라스토머와 아세트산 바이닐 단위의 함유량이 특정 범위 내에 있는 에틸렌-아세트산 바이닐 공중합체를 특정 비율로 함유하는 수지 성분에 대하여 특정량의 금속 수산화물을 함유시킴으로써, 전리 방사선에 의한 가교 처리를 하지 않고도 UL 규격의 수직 연소 시험 VW-1에 합격하는 고도의 난연성을 보이며, 가요성(유연성), 기계 물성(인장 강도 및 인장 파단 연신도), 내열성, 내열 노화성, 내가열 변형성, 저온 특성, 전기 절연성 등이 뛰어난 절연 피복 을 형성할 수 있는 난연성 수지 조성물이 얻어짐을 발견하였다. MEANS TO SOLVE THE PROBLEM As a result of earnestly researching in order to solve the said subject, it turned out that the resin component containing the thermoplastic polyurethane elastomer whose hardness is in a specific range, and the ethylene-vinyl acetate copolymer in which content of a vinyl acetate unit exists in a specific range in a specific ratio is carried out. By containing a specific amount of metal hydroxide with respect to the high flame retardancy to pass the UL standard vertical combustion test VW-1 without crosslinking treatment by ionizing radiation, flexibility (flexibility), mechanical properties (tensile strength and tension) It was found that a flame-retardant resin composition capable of forming an insulating coating excellent in elongation at break), heat resistance, heat aging resistance, heat deformation resistance, low temperature characteristics, electrical insulation, and the like was obtained.

특히, 본 발명의 난연성 수지 조성물을 플렉시블 플랫 케이블의 절연 피복 재료로 사용하면 UL 규격의 수직 연소 시험 VW-1에 합격하는 고도의 난연성을 보이며, 가요성, 기계 물성, 내열성, 내열 노화성, 내가열 변형성, 저온 특성, 전기 절연성 등이 뛰어난 절연 피복을 갖는 플렉시블 플랫 케이블을 얻을 수 있다. In particular, when the flame retardant resin composition of the present invention is used as an insulating coating material of a flexible flat cable, it exhibits a high flame retardancy that passes the UL standard vertical combustion test VW-1, and has flexibility, mechanical properties, heat resistance, heat aging resistance, and A flexible flat cable having an insulating coating excellent in heat deformation property, low temperature property, electrical insulation, and the like can be obtained.

이러한 평각 도체를 이용한 플렉시블 플랫 케이블은 원한다면 깔끔하게 접거나 묶기가 용이하며, 특히 전자 기기 내부에서의 다방 분기 배선재로 사용할 수 있다. 본 발명의 플렉시블 플랫 케이블은 인접하는 평각 도체의 중간 위치에서 길이 방향을 따라 절연 피복의 양 표면에 절개홈을 마련한 구조로 함으로써 원하는 평각 도체 수를 포함하는 복수 개의 플렉시블 플랫 케이블로 용이하게 분할 또는 분기시킬 수 있다. 절개홈이 있으면 플렉시블 플랫 케이블을 접거나 묶기가 훨씬 용이하다. 본 발명은 이들 깨달음에 기초하여 완성되기에 이른 것이다. Flexible flat cables using such flat conductors are easy to fold or bundle neatly, if desired, and can be used as multi-branch branch wiring materials, especially inside electronic devices. The flexible flat cable of the present invention has a structure in which cutouts are provided on both surfaces of the insulating coating along the longitudinal direction at an intermediate position of adjacent flat conductors, thereby easily dividing or branching into a plurality of flexible flat cables containing a desired number of flat conductors. You can. With a cutout, it is much easier to fold or bundle the flexible flat cable. The present invention has been completed based on these realizations.

본 발명에 따르면, 병렬로 배치한 복수 개의 평각 도체를 절연 피복 재료에 의해 일괄적으로 절연 피복 성형하여 이루어지는 플렉시블 플랫 케이블에 있어서, 이 절연 피복 재료가, JIS K 7311에 따라 측정한 JIS 경도가 A97 이하인 열가소성 폴리우레탄 엘라스토머(A)와 아세트산 바이닐 단위의 함유량이 50 내지 90중량%인 에틸렌-아세트산 바이닐 공중합체(B)를 중량비(A:B)로 40:60 내지 90:10의 비율로 함유하는 수지 성분 100중량부에 대하여 금속 수산화물(C)을 40 내지 250중량부의 비율로 함유시킨 난연성 수지 조성물인 것을 특징으로 하는 플렉시블 플랫 케이블 이 제공된다. According to the present invention, in a flexible flat cable obtained by collectively insulating coating molding a plurality of flat conductors arranged in parallel with an insulating coating material, the JIS hardness measured according to JIS K 7311 is A97. The following thermoplastic polyurethane elastomer (A) and an ethylene-vinyl acetate copolymer (B) having a content of 50 to 90% by weight of vinyl acetate units are contained in a ratio of 40:60 to 90:10 by weight ratio (A: B). A flexible flat cable is provided, which is a flame-retardant resin composition containing a metal hydroxide (C) in a ratio of 40 to 250 parts by weight relative to 100 parts by weight of the resin component.

본 발명에 따르면, 전리 방사선에 의한 가교 처리를 하지 않고도 UL 규격의 수직 연소 시험 VW-1에 합격하는 고도의 난연성을 보이며, 가요성, 기계 물성, 내열성, 내열 노화성, 내가열 변형성, 저온 특성, 전기 절연성 등이 뛰어난 절연 피복(이하, "절연 피복층" 또는 단순히 "피복층"이라고 할 수 있음)을 형성한 플렉시블 플랫 케이블을 제공할 수 있다. According to the present invention, it exhibits a high flame retardancy that passes the UL standard vertical combustion test VW-1 without crosslinking treatment by ionizing radiation, and has flexibility, mechanical properties, heat resistance, heat aging resistance, heat deformation resistance, and low temperature characteristics. It is possible to provide a flexible flat cable having an insulating coating (hereinafter referred to as an "insulating coating layer" or simply a "coating layer") having excellent electrical insulation and the like.

본 발명의 플렉시블 플랫 케이블은 인접하는 평각 도체의 중간 위치에서 길이 방향을 따라 절연 피복의 양 표면에 절개홈을 마련한 구조로 함으로써 원하는 평각 도체 수를 포함하는 복수 개의 플렉시블 플랫 케이블로 용이하게 분할 또는 분기할 수 있다. The flexible flat cable of the present invention has a structure in which cutouts are provided on both surfaces of the insulating coating along the longitudinal direction at an intermediate position of adjacent flat conductors, thereby easily dividing or branching into a plurality of flexible flat cables containing a desired number of flat conductors. can do.

플렉시블 플랫 케이블은 그 띠형 형상 때문에 전자 기기 내에서의 공기의 순환을 저해할 수가 있으며, 접거나 묶는 것이 바람직한 경우가 있다. 본 발명에 따르면, 플렉시블 플랫 케이블을 깔끔하게 접거나 묶을 뿐만 아니라, 절개홈 구조를 마련함으로써 다방 분기 배선재로도 사용할 수 있다. Because of its strip shape, the flexible flat cable can hinder the circulation of air in electronic equipment, and it may be desirable to fold or bundle it. According to the present invention, the flexible flat cable is not only neatly folded or bundled, but also can be used as a multi-branch branch wiring material by providing a cutout structure.

1. 플렉시블 플랫 케이블의 개요 1. Outline of Flexible Flat Cable

본 발명의 플렉시블 플랫 케이블은 예컨대 도 1에 도시한 단면 구조를 가지고 있다. 구체적으로, 본 발명의 플렉시블 플랫 케이블(10)은 복수 개의 평각 도체(평판형의 도체)(11，11，11…)를 병렬로 배치하고, 각 평각 도체의 주위 및 각 평각 도체 사이를 절연 피복 재료에 의해 일괄적으로 절연 피복 성형하여 절연 피복(12)을 마련한 띠형의 케이블이다. 이 플렉시블 플랫 케이블의 바람직한 구조에 대해서는 나중에 상세하게 설명하기로 한다.The flexible flat cable of the present invention has, for example, a cross-sectional structure shown in FIG. Specifically, the flexible flat cable 10 of the present invention arranges a plurality of flat conductors (flat conductors) 11, 11, 11, ... in parallel, and insulates the sheath of each flat conductor and between each flat conductor. It is a strip | belt-shaped cable which provided the insulation coating 12 by carrying out insulation coating molding by the material collectively. The preferable structure of this flexible flat cable is demonstrated in detail later.

2. 절연 피복 재료 2. Insulation sheath material

본 발명의 가장 큰 특징은 절연 피복(12)을 형성하는 절연 피복 재료에 있다. 본 발명에서 사용하는 절연 피복 재료는 JIS K 7311에 따라 측정한 JIS 경도가 A97 이하인 열가소성 폴리우레탄 엘라스토머(A)와 아세트산 바이닐 단위의 함유량이 50 내지 90중량%인 에틸렌-아세트산 바이닐 공중합체(B)를 중량비(A:B)로 40:60 내지 90:10의 비율로 함유하는 수지 성분 100중량부에 대하여 금속 수산화물(C)을 40 내지 250중량부의 비율로 함유시킨 난연성 수지 조성물이다. The greatest feature of the present invention lies in the insulating coating material forming the insulating coating 12. The insulation coating material used by this invention is an ethylene-vinyl acetate copolymer (B) whose content of the thermoplastic polyurethane elastomer (A) whose JIS hardness is A97 or less and the vinyl acetate unit of 50-90 weight% is measured according to JISK7311. It is a flame-retardant resin composition which contained the metal hydroxide (C) in the ratio of 40-250 weight part with respect to 100 weight part of resin components containing in a ratio of 40: 60-90: 10 by weight ratio (A: B).

열가소성 엘라스토머(TPE)는, 분자 내에 탄성을 갖는 고무 성분(소프트 세그먼트)와 소성 변형을 방지하는 분자 구속 성분(하드 세그먼트)의 두 성분을 갖는 폴리머이다. Thermoplastic elastomer (TPE) is a polymer having two components, a rubber component (soft segment) having elasticity in a molecule and a molecular restraining component (hard segment) which prevents plastic deformation.

본 발명에서 사용하는 열가소성 폴리우레탄 엘라스토머(TPU)는 고분자량 다이올(장쇄 다이올), 다이아이소시아네이트 및 저분자량 다이올(단쇄 다이올)의 3 성분의 분자간 반응에 의해 생성하는 것으로서, 분자 내에 우레탄기(-NH-COO-)를 갖는 폴리머이다. 장쇄 다이올과 단쇄 다이올은 다이아이소시아네이트와 부가 반응하여 선형 폴리우레탄을 생성한다. 이들 중에서 장쇄 다이올은 엘라스토머의 유연한 부분(소프트 세그먼트)을 형성하고, 다이아이소시아네이트와 단쇄 다이올은 딱딱한 부분(하드 세그먼트)을 형성한다. 열가소성 폴리우레탄 엘라스토머의 기본 특성은 주로 장쇄 다이올의 종류로 결정되는데, 경도는 하드 세그먼트의 비율로 조정된다. Thermoplastic polyurethane elastomer (TPU) used in the present invention is produced by the intermolecular reaction of three components of high molecular weight diol (long chain diol), diisocyanate and low molecular weight diol (short chain diol), It is a polymer having a group (-NH-COO-). Long-chain diols and short-chain diols react with addition of diisocyanates to produce linear polyurethanes. Among them, the long chain diol forms the flexible portion (soft segment) of the elastomer, and the diisocyanate and the short chain diol form the hard portion (hard segment). The basic properties of thermoplastic polyurethane elastomers are mainly determined by the type of long chain diol, with the hardness being adjusted by the proportion of hard segments.

장쇄 다이올로는 예컨대, 폴리프로필렌글리콜(PPG), 폴리테트라메틸렌글리콜(PTMG), 폴리(뷰틸렌아디페이트)다이올(PBA), 폴리-ε-카프로락톤다이올(PCL), 폴리(헥사메틸렌카보네이트)다이올(PHC), 폴리(에틸렌/1,4-아디페이트)다이올, 폴리(1,6-헥실렌/네오펜틸렌아디페이트)다이올 등을 들 수 있다. 열가소성 폴리우레탄 엘라스토머의 종류는 장쇄 다이올의 종류에 따라 예컨대 카프로락톤형, 아디페이트형, PTMG형, 폴리카보네이트(PC)형 등으로 나뉜다. Examples of long chain diols include polypropylene glycol (PPG), polytetramethylene glycol (PTMG), poly (butylene adipate) diol (PBA), poly-ε-caprolactonediol (PCL), poly (hexa) Methylene carbonate) diol (PHC), a poly (ethylene / 1, 4- adipate ) diol, a poly (1, 6- hexylene / neopentylene adipate) diol, etc. are mentioned. The type of thermoplastic polyurethane elastomer is divided into, for example, caprolactone type, adipate type, PTMG type, polycarbonate (PC) type, and the like according to the type of long chain diol.

다이아이소시아네이트로는 예컨대, 4,4'-다이페닐메탄다이아이소시아네이트, 헥사메틸렌다이아이소시아네이트, 아이소포론다이아이소시아네이트, 4,4'-다이사이클로헥실메탄다이아이소시아네이트 등을 들 수 있다. 단쇄 다이올로는 1,4-뷰탄다이올, 1,6-헥세인다이올, 1,4-비스(2-하이드록시에톡시)벤젠 등을 들 수 있다. As diisocyanate, 4,4'- diphenylmethane diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, 4,4'- dicyclohexyl methane diisocyanate, etc. are mentioned, for example. Examples of the short-chain diols include 1,4-butanediol, 1,6-hexanediol, 1,4-bis (2-hydroxyethoxy) benzene, and the like.

본 발명에서 사용하는 열가소성 폴리우레탄 엘라스토머는 JIS K 7311(폴리우레탄계 열가소성 엘라스토머의 시험 방법)에 따라 타입 A 듀로미터를 이용하여 측정한 경도(단위=JIS; "JIS A경도"라고도 함)가 A97 이하이다. 열가소성 폴리우레탄 엘라스토머의 JIS 경도가 A98 이상이면 난연성 수지 조성물로 이루어지는 절연 피복의 인장 파단 연신도가 현저하게 낮아져 절연 피복의 가요성이 손상된다. 본 발명에서 사용하는 열가소성 폴리우레탄 엘라스토머의 JIS 경도는 바람직하게는 A50 내지 A96, 보다 바람직하게는 A60 내지 A95, 특히 바람직하게는 A70 내지 A93이다. 열가소성 폴리우레탄 엘라스토머의 JIS 경도가 상기 범위 내에 있음으로써 난연성 수지 조성물로 이루어지는 절연 피복의 기계 물성, 내열성, 내열 노화성, 내가열 변형성, 저온 특성 등 제반 특성을 고도로 균형을 이루게 할 수 있으므로 바람직하다. The thermoplastic polyurethane elastomer used in the present invention has a hardness measured using a type A durometer according to JIS K 7311 (testing method of polyurethane-based thermoplastic elastomer) (unit = JIS; also referred to as “JIS A hardness”) of A97 or less. to be. When the JIS hardness of the thermoplastic polyurethane elastomer is A98 or more, the tensile fracture elongation of the insulating coating made of the flame retardant resin composition is significantly lowered, thereby impairing the flexibility of the insulating coating. The JIS hardness of the thermoplastic polyurethane elastomer used in the present invention is preferably A50 to A96, more preferably A60 to A95, particularly preferably A70 to A93. Since JIS hardness of a thermoplastic polyurethane elastomer exists in the said range, since mechanical properties, heat resistance, heat aging resistance, heat deformation resistance, and low temperature characteristics of the insulation coating which consists of a flame-retardant resin composition can be highly balanced, it is preferable.

본 발명에서 사용하는 열가소성 폴리우레탄 엘라스토머의 분자량의 지표인 멜트 플로 레이트(이하, "MFR"로 약칭; JIS K 7210에 따라 온도 210℃, 하중 5000g에서 측정)는 압출 가공성이나 기계 물성 등의 관점에서, 바람직하게는 0.1 내지 100g/10분, 보다 바람직하게는 0.5 내지 50g/10분이다. Melt flow rate (hereinafter, abbreviated as "MFR"; measured at a temperature of 210 ° C and a load of 5000 g according to JIS K 7210), which is an index of the molecular weight of the thermoplastic polyurethane elastomer used in the present invention, is in view of extrusion processability and mechanical properties. It is preferably 0.1 to 100 g / 10 minutes, more preferably 0.5 to 50 g / 10 minutes.

본 발명에서 사용하는 에틸렌-아세트산 바이닐 공중합체는 아세트산 바이닐 단위의 함유량(단순히 아세트산 바이닐 함유량이라고 할 수 있음)이 50 내지 90중량%인 에틸렌과 아세트산 바이닐과의 공중합체이다. 에틸렌-아세트산 바이닐 공중합체의 아세트산 바이닐 단위의 함유량이 지나치게 낮으면 난연성, 기계 물성, 내열성, 내열 노화성, 내가열 변형성 등이 뛰어난 수지 조성물을 얻기가 어렵고, 특히 수직 연소 시험 VW-1에 합격하는 고도의 난연성을 보이는 절연 피복을 형성할 수 없다. 아세트산 바이닐 단위의 함유량은 바람직하게는 55 내지 85중량%, 보다 바람직하게는 60 내지 83중량%이다. 본 발명에서 사용하는 에틸렌-아세트산 바이닐 공중합체는 아세트산 바이닐 단위의 함유량이 상기 범위에 있음으로써 난연성이나 인장 특성 등의 제반 특성이 뛰어난 난연성 수지 조성물로 이루어지는 절연 피복을 형성할 수 있다. The ethylene-vinyl acetate copolymer used in the present invention is a copolymer of ethylene and vinyl acetate having a content of vinyl acetate unit (simply called vinyl acetate content) of 50 to 90% by weight. When the content of the vinyl acetate unit of the ethylene-vinyl acetate copolymer is too low, it is difficult to obtain a resin composition excellent in flame retardancy, mechanical properties, heat resistance, heat aging resistance, heat deformation resistance, and the like, and particularly passes the vertical combustion test VW-1. It is not possible to form an insulating coating that exhibits high flame retardancy. The content of the vinyl acetate unit is preferably 55 to 85% by weight, more preferably 60 to 83% by weight. The ethylene-vinyl acetate copolymer used by this invention can form the insulation coating which consists of a flame-retardant resin composition excellent in various characteristics, such as flame retardance and tensile characteristics, because content of a vinyl acetate unit exists in the said range.

본 발명에서 사용하는 에틸렌-아세트산 바이닐 공중합체의 분자량의 지표인 MFR(JIS K 7210에 따라 온도 190℃, 시험 하중 2160g에서 측정)은 압출 가공성이나 기계 물성 등의 관점에서 바람직하게는 0.1 내지 100g/10분, 보다 바람직하게는 0.5 내지 50g/10분이다. MFR (measured at 190 DEG C according to JIS K 7210, test load 2160 g according to JIS K 7210), which is an index of molecular weight of the ethylene-vinyl acetate copolymer used in the present invention, is preferably 0.1 to 100 g / from the viewpoint of extrusion processability and mechanical properties. 10 minutes, More preferably, it is 0.5-50 g / 10 minutes.

본 발명에서는 열가소성 폴리우레탄 엘라스토머(A 성분) 및 에틸렌-아세트산 바이닐 공중합체(B 성분)를 양자의 중량비(A:B)로 40:60 내지 90:10의 범위 내에서 함유하는 수지 성분을 사용한다. 수지 성분 내의 열가소성 폴리우레탄 엘라스토머의 중량 비율이 지나치게 낮으면 난연성이 저하하여 UL 규격의 수직 연소 시험 VW-1에 합격할 수 없다. 수지 성분 내의 열가소성 폴리우레탄 엘라스토머의 중량 비율이 지나치게 높아도 난연성이 저하하여 UL 규격의 수직 연소 시험 VW-1에 합격할 수 없다. 에틸렌-아세트산 바이닐 공중합체의 중량비가 지나치게 낮으면 난연성이 저하하고, 지나치게 높으면 난연성이 저하하거나 또는 인장 파단 연신도가 저하하기 쉬워진다. 열가소성 폴리우레탄 엘라스토머(A 성분)와 에틸렌-아세트산 바이닐 공중합체(B 성분)와의 중량비(A:B)는 바람직하게는 45:55 내지 85:15, 보다 바람직하게는 50:50 내지 80:20이다.In the present invention, a resin component containing a thermoplastic polyurethane elastomer (component A) and an ethylene-vinyl acetate copolymer (component B) in a weight ratio (A: B) of both in the range of 40:60 to 90:10 is used. . If the weight ratio of the thermoplastic polyurethane elastomer in the resin component is too low, the flame retardancy is lowered and the UL standard cannot pass the vertical combustion test VW-1. Even if the weight ratio of the thermoplastic polyurethane elastomer in a resin component is too high, a flame retardance will fall and it cannot pass the UL standard vertical combustion test VW-1. If the weight ratio of the ethylene-vinyl acetate copolymer is too low, the flame retardancy is lowered. If the weight ratio is too high, the flame retardancy is reduced or the tensile elongation at break tends to be lowered. The weight ratio (A: B) of the thermoplastic polyurethane elastomer (component A) and the ethylene-vinyl acetate copolymer (component B) is preferably 45:55 to 85:15, more preferably 50:50 to 80:20. .

금속 수산화물로는 예컨대, 수산화마그네슘 및 수산화알루미늄을 들 수 있다. 이들 중에서도 수산화마그네슘은 난연성이 뛰어난 점에서 바람직하다. 수산화마그네슘은 합성품뿐만 아니라 브루사이트(brucite) 광을 원료로 하는 천연 산물인 수산화마그네슘(천연 수산화마그네슘)을 사용하여도 난연성, 인장 물성, 가열 변형성, 저온 특성 등의 UL 규격의 스펙을 만족하는 절연 피복을 형성할 수 있기 때문에 제조 비용의 저감에 유리하다.Examples of the metal hydroxides include magnesium hydroxide and aluminum hydroxide. Among these, magnesium hydroxide is preferable at the point which is excellent in flame retardancy. Magnesium hydroxide is an insulating material that meets the specifications of UL standards such as flame retardancy, tensile properties, heat deformation, and low temperature properties even when using magnesium hydroxide (natural magnesium hydroxide), a natural product based on brucite light as well as synthetic products. Since the coating can be formed, it is advantageous to reduce the manufacturing cost.

수산화마그네슘 등의 금속 수산화물은 수지 성분에 대한 분산성의 관점에서, 평균 입자 직경(레이저 회절/산란법에 의한 메디안 지름)이 바람직하게는 0.3 내지 7μm, 보다 바람직하게는 0.5 내지 5μm이고, BET 비표면적이 바람직하게는 2 내지 20m²/g, 보다 바람직하게는 3 내지 15m²/g의 범위 내에 있는 것을 선택하는 것이 바람직하다. Metal hydroxides, such as magnesium hydroxide, have an average particle diameter (median diameter by laser diffraction / scattering method) from the viewpoint of dispersibility to the resin component, preferably 0.3 to 7 μm, more preferably 0.5 to 5 μm, and BET specific surface area. It is preferable to select what is preferably in the range of 2-20 m <^2> / g, More preferably, it is 3-15 m <^2> / g.

금속 수산화물은 표면 처리를 실시하지 않은 그레이드를 사용할 수 있는데, 분산성의 관점에서 스테아르산이나 올레산 등의 지방산, 인산 에스터, 실레인계 커플링제, 타이타늄계 커플링제, 알루미늄계 커플링제 등의 표면 처리제로 표면 처리한 그레이드를 사용하는 것이 바람직하다. The metal hydroxide may be a grade which has not been surface-treated, but in view of dispersibility, it may be a surface treatment agent such as fatty acid such as stearic acid or oleic acid, phosphate ester, silane coupling agent, titanium coupling agent, aluminum coupling agent or the like. Preference is given to using treated grades.

금속 수산화물의 배합 비율은 수지 성분 100중량부에 대하여 40 내지 250중량부, 바람직하게는 50 내지 240중량부, 보다 바람직하게는 80 내지 200중량부이다. 금속 수산화물의 배합 비율이 지나치게 낮으면 난연성이 불충분해지고, 지나치게 높으면 난연성 수지 조성물의 용융 토크가 높아지기 때문에 압출 성형성의 점에서 바람직하지 않으며, 인장 파단 연신도도 저하한다. The compounding ratio of a metal hydroxide is 40-250 weight part with respect to 100 weight part of resin components, Preferably it is 50-240 weight part, More preferably, it is 80-200 weight part. If the blending ratio of the metal hydroxide is too low, the flame retardancy becomes insufficient, and if it is too high, the melt torque of the flame retardant resin composition becomes high, which is not preferable in terms of extrusion moldability, and the tensile breaking elongation also decreases.

본 발명에서 사용하는 난연성 수지 조성물에는 원한다면 3산화 안티몬, 주석산 아연, 하이드록시주석산 아연, 붕산 아연, 탄산 아연, 염기성 탄산 마그네슘 등의 무기계 난연제 또는 난연조제; 멜라민시아누레이트 등의 질소계 난연제; 축합형 인산 에스터와 같은 인계 난연제; 등을 첨가하는 것이 가능하다. Flame retardant resin compositions used in the present invention include inorganic flame retardants or flame retardants such as antimony trioxide, zinc stannate, zinc hydroxytartrate, zinc borate, zinc carbonate, basic magnesium carbonate, if desired; Nitrogen-based flame retardants such as melamine cyanurate; Phosphorus flame retardants such as condensed phosphate esters; Etc. can be added.

본 발명에서 사용하는 난연성 수지 조성물에는 원한다면 활제, 산화 방지제, 가공 안정제, 가수 분해 억제제, 중금속 비활성화제, 착색제, 충전제, 보강재, 발 포제 등의 이미 알려진 배합 약품을 필요에 따라 첨가할 수 있다. To the flame retardant resin composition used in the present invention, if desired, known formulations such as lubricants, antioxidants, processing stabilizers, hydrolysis inhibitors, heavy metal deactivators, colorants, fillers, reinforcing agents, foaming agents and the like may be added as necessary.

본 발명에서 사용하는 난연성 수지 조성물은 수지 성분, 금속 수산화물 및 필요에 따라 첨가되는 다른 성분을 오븐 롤, 밴버리 믹서, 가압 니더, 단축 또는 다축 혼합기 등의 이미 알려진 용융 혼합기를 사용하여 혼합함으로써 조제할 수 있다. 이 난연성 수지 조성물은 펠렛 형태로 형성할 수 있다. The flame retardant resin composition used in the present invention can be prepared by mixing a resin component, a metal hydroxide and other components added as necessary using a known melt mixer such as an oven roll, a Banbury mixer, a pressurized kneader, a single screw or a multiaxial mixer. have. This flame retardant resin composition can be formed in pellet form.

본 발명에서 사용하는 난연성 수지 조성물은 플렉시블 플랫 케이블의 절연 피복에 사용되는데, 그때 가교 처리를 하지 않아도 인장 특성이나 난연성 등의 제반 특성이 뛰어난 절연 피복을 형성할 수 있다 The flame retardant resin composition used in the present invention is used for insulating coating of a flexible flat cable, and at this time, an insulating coating excellent in various characteristics such as tensile properties and flame retardancy can be formed without crosslinking treatment.

다른 한편, 이 난연성 수지 조성물을 이용하여 형성한 절연 피복을 가교하는 것이 바람직한 경우에는 가교 처리를 실시할 수도 있다. 구체적으로는, 이 난연성 수지 조성물을 이용하여 플렉시블 플랫 케이블의 절연 피복을 형성하고, 가속 전자선이나 γ선 등의 전리 방사선을 조사하면 이 절연 피복을 가교시킬 수 있다. 이 난연성 수지 조성물에 유기 과산화물을 함유시키면 가열에 의해 절연 피복을 가교할 수 있다. 가교 처리함에 있어서 난연성 수지 조성물 내에 미리 다작용 모노머를 첨가할 수도 있다. 가교 처리를 실시함으로써 인장 특성이나 내열성 등의 특성을 향상시킬 수 있다.On the other hand, when it is preferable to bridge | crosslink the insulating coating formed using this flame-retardant resin composition, you can also carry out a crosslinking process. Specifically, the insulation coating of a flexible flat cable is formed using this flame-retardant resin composition, and irradiation with ionizing radiation, such as an acceleration electron beam and a gamma ray, can crosslink this insulation coating. When an organic peroxide is contained in this flame-retardant resin composition, insulation coating can be bridge | crosslinked by heating. In crosslinking process, you may add a polyfunctional monomer in a flame-retardant resin composition previously. By carrying out the crosslinking treatment, properties such as tensile properties and heat resistance can be improved.

본 발명의 난연성 수지 조성물로 형성된 절연 피복을 갖는 플렉시블 플랫 케이블은 UL 규격에 적합한 것으로서, 특히 수직 연소 시험 VW-1에 합격할 만큼의 고도의 난연성을 가지고 있다. 이 절연 피복은 초기의 인장 강도 및 인장 파단 연신도가 뛰어날 뿐만 아니라, 열노화 후의 인장 특성도 양호하다. 인장 시험기를 이 용하여 인장 속도 50mm/분, 표선간 거리 25mm, 온도 23℃에서 측정하였을 때, 인장 강도가 8.2MPa 이상, 많은 경우 10.0 내지 20.0MPa이고, 인장 파단 연신도가 100% 이상, 많은 경우 105 내지 230%인 인장 특성을 갖는 절연 피복을 얻는 것이 가능하다. 이 절연 피복은 113℃의 기어 오븐 내에 168시간 방치하는 열노화 시험 후의 인장 강도 잔률이 75% 이상, 바람직하게는 80% 이상, 및 인장 파단 연신도 잔률 75% 이상, 바람직하게는 80% 이상을 달성할 수 있다. The flexible flat cable having an insulation coating formed from the flame retardant resin composition of the present invention is suitable for UL standards, and has a particularly high flame retardancy enough to pass the vertical combustion test VW-1. This insulating coating not only has excellent initial tensile strength and tensile elongation at break, but also has good tensile characteristics after thermal aging. Tensile strength measured at 50 mm / min, 25 mm between marks, and 23 ° C. using a tensile tester has a tensile strength of 8.2 MPa or more, in many cases 10.0 to 20.0 MPa, and tensile elongation at break of 100% or more. It is possible to obtain an insulating coating having a tensile property of 105 to 230%. The insulation coating has a tensile strength residual ratio of 75% or more, preferably 80% or more, and tensile elongation at break 75% or more, preferably 80% or more after a heat aging test in a gear oven at 113 ° C. for 168 hours. Can be achieved.

본 발명의 난연성 수지 조성물로 형성된 절연 피복을 갖는 플렉시블 플랫 케이블은 개개로 분할한 시료(한 개의 평각 도체를 포함하는 시료)를 100℃의 기어 오븐에 세팅하고, 60분간 예열한 후, 이 시료 상부로부터 하중 250g의 외경 9.5mm의 원반형 지그로 60분간 눌러 그 변형 잔률을 측정하였을 때 50% 이상, 바람직하게는 55% 이상, 보다 바람직하게는 60% 이상의 가열 변형 잔률을 나타낼 수 있다. In the flexible flat cable having an insulation coating formed of the flame retardant resin composition of the present invention, a sample (a sample containing one flat conductor) divided into pieces is set in a gear oven at 100 ° C, and preheated for 60 minutes, and then the upper part of the sample When the strain residual ratio was measured for 60 minutes with a disc jig having an outer diameter of 9.5 mm and a load of 250 g, the heating strain residual ratio could be 50% or more, preferably 55% or more, and more preferably 60% or more.

본 발명의 난연성 수지 조성물로 형성된 절연 피복을 구비한 플렉시블 플랫 케이블은 저온 특성이 뛰어나며, 개개로 분할한 시료(한 개의 평각 도체를 포함하는 시료)를 -10℃의 저온조에 4시간 방치한 후, 이 시료의 외경의 2배의 지름의 금속 막대에 -10℃에서 U자 굽힘하였을 때 절연 피복에 갈라짐(크랙)이 발생하지 않는다.The flexible flat cable with the insulation coating formed from the flame retardant resin composition of the present invention has excellent low temperature characteristics, and after leaving the sample (the sample including one flat conductor) separately divided in a -10 ° C low temperature bath for 4 hours, When U-shaped bends were carried out at -10 ° C on a metal rod having a diameter twice the outer diameter of this sample, no cracking occurred in the insulating coating.

이들 제반 특성의 측정법의 구체적인 것에 대해서는 실시예에서 설명하는데, 그 대부분은 UL 규격을 따른 것이다. 즉, 본원 발명의 난연성 수지 조성물로 절연 피복한 전선은 UL 규격의 안전 규격을 만족하는 기기내 배선용 전선으로 적합하며, 화재 방지 등의 안전성을 확보하면서 환경 친화적이라는 특성을 가지고 있다. Although the specific example of the measuring method of these various characteristics is demonstrated in an Example, the majority is based on UL standard. That is, the electric wire insulated and coated with the flame-retardant resin composition of this invention is suitable as the wire for in-device wiring which satisfy | fills the safety standard of UL standard, and has the characteristic of being environmentally friendly, ensuring safety, such as fire prevention.

3. 플렉시블 플랫 케이블의 구체적인 내용 3. Details of Flexible Flat Cable

본 발명의 플렉시블 플랫 케이블에서 사용하는 평각 도체의 재질은 평판형의 선형 도체이면 되며, 특별히 한정되지 않으나, 평판형의 주석 도금 구리선이 대표적인 것이다.The material of the flat conductor used in the flexible flat cable of the present invention may be a flat linear conductor, and is not particularly limited, but a flat tin plated copper wire is typical.

본 발명에서 사용하는 평각 도체의 형상은 그 폭(W)이 통상 0.1 내지 1.6mm이고, 그 두께(T)가 통상 0.03 내지 0.15mm이다. 평각 도체의 형상은 그 두께(T)보다 그 폭(W)이 크며(즉, W＞T), 그 두께(T)에 대한 그 폭(W)의 비(W/T)가 통상 6 내지 45이고, 많은 경우 6 내지 16이다. The width | variety (W) of the flat conductor used by this invention is 0.1-1.6 mm normally, and the thickness T is 0.03-0.15 mm normally. The shape of the flat conductor is larger in width (W) than its thickness (T), i.e., the ratio (W / T) of the width (W) to the thickness (T) is usually 6 to 45. And in many cases 6 to 16.

도체 크기의 구체적인 예(W×T; 단위 mm)로는 예컨대, 0.5×0.05(W/T=10), 0.6×0.1(W/T=6), 0.7×0.032(W/T=22), 0.7×0.1(W/T=7), 0.7×0.05(W/T=12), 0.7×0.035(W/T=20), 0.8×0.1(W/T=10), 0.8×0.05(W/T=13), 1.2×0.15(W/T=8), 1.4×0.032(W/T=44) 등을 들 수 있는데, 이들에 한정되지 않는다. Specific examples of conductor sizes (W × T; unit mm) are, for example, 0.5 × 0.05 (W / T = 10), 0.6 × 0.1 (W / T = 6), 0.7 × 0.032 (W / T = 22), 0.7 × 0.1 (W / T = 7), 0.7 × 0.05 (W / T = 12), 0.7 × 0.035 (W / T = 20), 0.8 × 0.1 (W / T = 10), 0.8 × 0.05 (W / T = 13), 1.2 × 0.15 (W / T = 8), 1.4 × 0.032 (W / T = 44), and the like, but are not limited to these.

평각 도체의 단면적은 AWG #20 내지 AWG #35(0.15mm² 내지 0.52mm²)인 것이 바람직하다.The cross-sectional area of the flat conductor is preferably AWG # 20 to AWG # 35 (0.15 mm ² to 0.52 mm ² ).

하나의 플렉시블 플랫 케이블에서 사용하는 복수 개의 평각 도체는 그 폭이나 두께 등을 포함하는 단면 형상이 동일한 것이 바람직하나, 필요에 따라 단면 형상이 서로 다른 복수 개의 평각 도체를 조합하여 사용할 수 있다 도체 피치에 대해서도 등간격인 것이 바람직하나, 필요에 따라 부분적으로 다른 것과 다른 도체 피치로 일부의 평각 도체를 배치할 수도 있다. 예컨대, 플렉시블 플랫 케이블의 일부의 평각 도체의 단면 형상 및/또는 도체 피치를 다른 것과 다르게 함으로써 허용 전류값이나 도체 저항이 다른 부분을 마련할 수도 있다. 후술하는 바와 같이, 플렉시블 플랫 케이블을 임의의 도중 폭으로 째어 분할 또는 분기시키는 경우, 평각 도체의 단면 형상 및/또는 도체 피치가 서로 다른 부분을 마련하면 분할 또는 분기한 플렉시블 플랫 케이블을 각각의 용도에 따라 적용하는 것도 가능하다. It is preferable that a plurality of flat conductors used in one flexible flat cable have the same cross-sectional shape including their width, thickness, etc., but a plurality of flat conductors having different cross-sectional shapes can be used in combination if necessary. Although it is preferable to also have equal intervals, some flat conductors can also be arrange | positioned by conductor pitch different from one another partially as needed. For example, the cross-sectional shape and / or conductor pitch of the flat conductor of a part of the flexible flat cable may be different from that of the other to provide a portion having a different allowable current value or conductor resistance. As will be described later, when the flexible flat cable is divided or branched by any intermediate width, when the cross-sectional shape and / or conductor pitch of the flat conductor are provided with different portions, the flexible flat cable divided or branched is used for each application. It is also possible to apply accordingly.

본 발명의 플렉시블 플랫 케이블은, 도 1에 도시한 바와 같이, 복수 개의 평각 도체(평판형 도체)(11)를 병렬로 배치하고, 각 평각 도체의 주위 및 각 평각 도체 사이를 절연 피복 재료에 의해 일체적으로 절연 피복 성형하여 절연 피복(12)을 마련한 띠형의 케이블(10)이다. 도 1에서는 평각 도체의 수가 4개인 경우를 나타내었으나, 일반적으로 하나의 플렉시블 플랫 케이블에서의 평각 도체의 수는 전체 폭의 너비, 평각 도체의 형상, 도체 피치의 크기 등에 따라서도 달라지는데, 작은 피치로의 배열에서는 통상 7 내지 100개이고, 큰 피치로의 배열에서는 통상 4 내지 50개인데, 이들에 한정되지 않는다. 평각 도체의 폭의 중심부끼리의 간격을 도체 피치라고 한다. 도체 피치는 원한다면 적당히 설정할 수 있는데, 많은 경우 0.5mm 내지 2.54mm 정도이다. In the flexible flat cable of the present invention, as shown in Fig. 1, a plurality of flat conductors (flat conductors) 11 are arranged in parallel, and an insulation coating material is provided between the periphery of each flat conductor and between the flat conductors. The strip | belt-shaped cable 10 which integrally insulation-coated and provided the insulation coating 12 was carried out. Although the number of flat conductors is shown in FIG. 1, the number of flat conductors in one flexible flat cable generally varies depending on the width of the overall width, the shape of the flat conductor, the size of the conductor pitch, and the like. In the arrangement of, it is usually 7 to 100, and in the arrangement in a large pitch, it is usually 4 to 50, but is not limited to these. The space | interval of the center part of the width | variety of a flat conductor is called conductor pitch. The conductor pitch can be set as desired, in many cases from 0.5 mm to 2.54 mm.

도 1에 도시한 플렉시블 플랫 케이블(10)의 단면 형상은 대략 사각형(가늘고 긴 직사각형)이다. 플렉시블 플랫 케이블은 중심점(PO)에 관하여 대칭인 형상임과 아울러, 인접하는 2개의 평각 도체(11，11)의 중심 위치에서 길이 방향을 따라 절연 피복(12)의 양 표면에 절개홈(13)을 마련하는 것이 바람직하다. 동시에, 두 곳의 마진부(14)의 총 네 귀퉁이에는 코너부 절개홈(15)을 마련하는 것이 바람직하 다.The cross-sectional shape of the flexible flat cable 10 shown in FIG. 1 is approximately square (elongated rectangle). The flexible flat cable has a symmetrical shape with respect to the center point PO, and cuts 13 on both surfaces of the insulating sheath 12 along the longitudinal direction at the center positions of two adjacent flat conductors 11 and 11. It is desirable to provide. At the same time, it is desirable to provide corner cutouts 15 at the four corners of the two margins 14.

절개홈(13)의 형상은 V자 형상, 원호 형상, U자 형상 등이 대표적인 것이다. 이 경우, 폭 또는 폭 및 두께가 같은 평각 도체를 등간격(동일한 도체 피치)으로 배치하는 것이 바람직하다. 마진부의 폭은 각 평각 도체간 간격의 1/2로 하는 것이 바람직하다. 마진부란 플렉시블 플랫 케이블의 길이 방향의 단부와 그에 인접하는 평각 도체의 단부 사이를 의미한다.The shape of the cutting groove 13 is representative of a V shape, an arc shape, a U shape, and the like. In this case, it is preferable to arrange the flat conductors having the same width or width and thickness at equal intervals (same conductor pitch). The width of the margin is preferably set to 1/2 of the spacing between the flat conductors. The margin means a portion between the longitudinal end of the flexible flat cable and the end of the flat conductor adjacent thereto.

이 절개홈(13)을 이용하여 플렉시블 플랫 케이블을 임의의 도중 폭으로 째어 분할 또는 분기시킬 수 있다. 마진부(14)의 네 귀퉁이의 코너부 절개홈(15)의 형상은 절연 피복(12)에 마련한 절개홈(13)으로 플렉시블 플랫 케이블을 분할 또는 분기시켰을 때 나타나는 형상이 되도록 하는 것이 바람직하다. 예컨대, 절연 피복(12)에 마련한 절개홈(13)이 V자 형상인 경우, 플렉시블 플랫 케이블을 이 V자 형상의 절개홈(13)에서 째어 분할 또는 분기시키면, 대략 비스듬히 직선형의 코너부 절개홈 형상이 나타나게 된다. 이 경우, 마진부(14)의 네 귀퉁이의 코너부 절개홈(15)의 형상도 미리 동일한 비스듬히 직선형이 되도록 하는 것이 바람직하다. 절연 피복(12)에 마련한 절개홈(13)이 원호 형상인 경우에는, 이 원호 형상의 절개홈(13)에서 째어 분할 또는 분기시키면 대략 반원의 1/2의 단면 형상의 코너부 절개홈 형상이 나타나게 된다. 이 경우에는 마진부(14)의 네 귀퉁이의 코너부 절개홈(15)의 형상도 미리 동일한 반원의 1/2의 단면 형상이 되도록 하는 것이 바람직하다. 절개홈(13)이 다른 형상인 경우에 대해서도 상기와 동일하게 대응한다. Using this cutout 13, the flexible flat cable can be split and branched by any intermediate width. The shape of the corner cutouts 15 at the four corners of the margin 14 is preferably such that the shape appears when the flexible flat cable is divided or branched into the cutouts 13 provided in the insulating coating 12. For example, in the case where the cutout groove 13 provided in the insulating coating 12 has a V-shape, when the flexible flat cable is divided or branched from the V-shaped cutout groove 13, the corner cutaway groove which is approximately obliquely straight is formed. The shape will appear. In this case, it is preferable that the shape of the corner cutouts 15 at the four corners of the margin portion 14 is also the same oblique straight line in advance. In the case where the cutout groove 13 provided in the insulating coating 12 has an arc shape, the corner cutout shape having a cross section of about half of a semicircle is formed when the cutout portion 13 is divided or branched from the arc shaped cutout groove 13. Will appear. In this case, it is preferable that the shape of the corner cutouts 15 at the four corners of the margin 14 is also made to have a cross-sectional shape of 1/2 of the same semicircle in advance. The same applies to the case where the cutout groove 13 has a different shape.

난연성 수지 조성물에 의해 절연 피복된 플렉시블 플랫 케이블은 복수 개의 평각 도체를 소정의 장력과 피치로 압출기의 다이스에 송출하고, 거기에 다이스로부터 난연성 수지 조성물을 용융 압출하여 피복함으로써 제조할 수 있다. 플렉시블 플랫 케이블은 그것을 적용하는 부위에 따라 평각 도체의 수가 다른 경우가 많다. 평각 도체의 수에 맞추어 다이스를 교체하는 것은 비용과 품이 든다. 다수 개의 평각 도체를 갖는 플랫 케이블을 제조하고, 각각의 사양에 대응하여 원하는 수의 평각 도체를 갖는 플렉시블 플랫 케이블로 분할할 수 있다면 상기 문제를 완화시킬 수 있다. 플렉시블 플랫 케이블을 도중에서 분기시킬 필요가 있는 경우에도 마찬가지이다. A flexible flat cable insulated and coated with a flame retardant resin composition can be produced by sending a plurality of flat conductors to a die of an extruder at a predetermined tension and pitch, and melt extruding and coating the flame retardant resin composition therefrom. Flexible flat cables often have different numbers of flat conductors depending on the area where they are applied. Replacing dies with the number of flat conductors is expensive and expensive. The problem can be alleviated if a flat cable having a plurality of flat conductors can be manufactured and divided into flexible flat cables having a desired number of flat conductors corresponding to each specification. The same applies when it is necessary to branch the flexible flat cable in the middle.

그러나, 종래의 플렉시블 플랫 케이블은 그 좌우 양단부에 마련된 마진의 폭이 각 평각 도체간의 간격의 절반의 폭보다 길기 때문에 플렉시블 플랫 케이블을 도중 폭으로 째어 각각 원하는 수의 평각 도체를 갖는 복수 개의 플렉시블 플랫 케이블로 분할하면 분할한 각 플렉시블 플랫 케이블에서의 마진 폭이 서로 달라지게 된다. 따라서, 단부에 커넥터를 부착할 때 평각 도체의 위치가 어긋나므로 위치 조정을 해야 하거나 부착이 불가능해지는 경우가 있었다.However, in the conventional flexible flat cable, since the width of the margin provided at the left and right ends thereof is longer than half the width of the gap between the flat conductors, the flexible flat cable has a plurality of flexible flat cables each having a desired number of flat conductors by cutting the flexible flat cable halfway. By dividing by, the margin widths in the split flexible flat cables will be different. Therefore, when the connector is attached to the end, the position of the flat conductor is shifted so that the position adjustment or the attachment may be impossible.

이에 반해, 상기와 같이 마진(14)의 폭, 절개홈(13)의 형상 및 절개홈(15)의 형상을 조정하면 상기 문제를 해소할 수 있다. 즉, 분할 또는 분기한 플렉시블 플랫 케이블은 항상 일정한 마진을 갖게 된다. 따라서, 평각 도체의 위치가 일정하므로 위치 조정을 하지 않고 커넥터를 용이하게 부착할 수 있다. 분할 또는 분기 후에 복수 종의 원하는 수의 평각 도체를 갖는 플렉시블 플랫 케이블을 한 번의 압출 공정에 의해 동일한 다이스를 이용하여 제조할 수 있다. On the other hand, adjusting the width of the margin 14, the shape of the incision groove 13 and the shape of the incision groove 15 as described above can solve the problem. That is, the split or branched flexible flat cable always has a constant margin. Therefore, since the position of the flat conductor is constant, the connector can be easily attached without adjusting the position. After splitting or branching, a flexible flat cable having a plurality of desired number of flat conductors can be produced using the same die by one extrusion process.

이하, 본 발명의 플렉시블 플랫 케이블의 보다 바람직한 형상에 대하여 설명한다. Hereinafter, the more preferable shape of the flexible flat cable of this invention is demonstrated.

본 발명의 바람직한 플렉시블 플랫 케이블의 형상은, 도 2에 사시도로 나타낸 바와 같이, 병렬로 배치한 복수 개의 평각 도체를 절연 피복 재료에 의해 일체적으로 절연 피복 성형하여 이루어지는 플렉시블 플랫 케이블(10)로서, 인접하는 2개의 평각 도체(11，11)의 중간 위치에서 길이 방향을 따라 절연 피복의 양 표면에 절개홈(13)이 마련되어 있다. 마진부(14, 14)의 폭은 각 평각 도체간(11, 11)의 간격의 1/2로 한다. 각 평각 도체는 폭 또는 폭 및 두께가 같은 것으로 한다. The shape of the preferred flexible flat cable of the present invention is a flexible flat cable 10 formed by integrally insulating coating molding a plurality of flat conductors arranged in parallel with an insulating coating material, as shown in a perspective view in FIG. Cutting grooves 13 are provided on both surfaces of the insulating coating along the longitudinal direction at intermediate positions of two adjacent flat conductors 11 and 11. The width | variety of the margin parts 14 and 14 shall be 1/2 of the space | interval of each flat conductor 11,11. Each flat conductor is equal in width or width and thickness.

따라서, 평각 도체의 수를 플렉시블 플랫 케이블의 전체 폭을 W; 평각 도체의 배열 피치(도체 피치)를 P; 플렉시블 플랫 케이블의 마진부(14, 14)의 폭을 M; 평각 도체의 폭을 C; 각 평각 도체간 간격을 G;라고 하면, 본 발명의 플렉시블 플랫 케이블은 이하의 관계식을 만족하는 것이 보다 바람직하다. Therefore, the total width of the flexible flat cable W the number of flat conductors; The arrangement pitch (conductor pitch) of the flat conductor is P; The width of the margin portions 14, 14 of the flexible flat cable; Width of the flat conductor C; When the spacing between each flat conductor is G ;, it is more preferable that the flexible flat cable of the present invention satisfies the following relational expression.

(1)W=P×n (1) W = P × n

(2)P=C+2×M(2) P = C + 2 × M

(3)G=2×M (3) G = 2 × M

마진부(14，14)의 코너부 절개홈(15)은, 전술한 바와 같이, 플렉시블 플랫 케이블을 절개홈(13)에서 째어 분할 또는 분기시켰을 때 나타나는 형상과 일치시킨다. The corner cutouts 15 of the margins 14 and 14 coincide with the shapes shown when the flexible flat cable is cut off from the cutout 13 and divided or branched as described above.

도 2에 도시한 플렉시블 플랫 케이블은 임의의 부위의 도중 폭으로 째어 분할 또는 분기시킬 수 있다. 분할 또는 분기한 플렉시블 플랫 케이블은 마진의 폭 및 형상이 동일해져 커넥터에 대한 부착이 용이하다. The flexible flat cable shown in FIG. 2 can be split or branched by the width of an arbitrary portion. The split or branched flexible flat cable has the same width and shape of the margin, making it easy to attach to the connector.

본 발명의 플렉시블 플랫 케이블은 상류측에서 하류측 쪽으로 순서대로 1)평각 도체를 공급하는 공급 릴 그룹; 2)공급받은 평각 도체를 소정의 피치로 나열하는 집선기; 3)절연 피복 재료를 용융 압출하여 절연 피복을 형성하고, 복수 개의 평각 도체를 내부에 포함하는 플렉시블 플랫 케이블을 형성하는 압출기;를 구비한 제조 장치를 이용하여 제조할 수 있다. 본 발명에서는 절연 피복 재료로서 상기한 난연성 수지 조성물을 사용한다. The flexible flat cable of the present invention comprises: 1) a supply reel group for feeding a flat conductor in order from an upstream side to a downstream side; 2) a concentrator for arranging the supplied flat conductor at a predetermined pitch; 3) an extruder which melt-extrudes the insulation coating material to form an insulation coating, and forms a flexible flat cable including a plurality of flat conductors therein; In this invention, the flame-retardant resin composition mentioned above is used as an insulation coating material.

압출기의 하류측에는 권취 드럼을 배치하는데, 그 앞에 압출기를 나온 플렉시블 플랫 케이블을 임의의 도중 폭으로 분할하기 위한 절취기를 배치하고, 둘 이상으로 분할한 플렉시블 플랫 케이블 각각을 권취하기 위한 권취기를 배치한다. 다이스의 중공 형상은 전술한 마진부의 코너부 절개홈(15) 및 절연 피복의 절개홈(13)에 대응하는 단면 형상으로 하는 것이 바람직하다. 다이스의 단면 형상을 조정하기가 어려운 경우 등에는 다이스의 하류측에 마진부의 코너부 절개홈(15) 및 절연 피복의 절개홈(13)을 형성하기 위한 지그를 배치할 수도 있다. On the downstream side of the extruder, a winding drum is arranged, in front of which a cutout for dividing the flexible flat cable exiting the extruder into any intermediate width is arranged, and a winding machine for winding each of the two or more flexible flat cables. The hollow shape of the die is preferably a cross-sectional shape corresponding to the corner cutout 15 of the margin and the cutout 13 of the insulation coating. When it is difficult to adjust the cross-sectional shape of a die, the jig for forming the corner part cut groove 15 of the margin part and the cut-out groove 13 of insulation coating may be arrange | positioned downstream of a die.

본 발명의 플렉시블 플랫 케이블은 액정 TV의 배선 등 좁은 공간에서의 배선이나 가동부가 있는 전자 기기의 배선 등에 적합하다. 본 발명의 플렉시블 플랫 케이블은 절연 피복에 마련한 절개홈을 이용하여 분할 또는 분기시킬 수 있는 것 이외에, 깔끔하게 절첩하거나 묶는 것도 용이하다. The flexible flat cable of this invention is suitable for wiring in narrow spaces, such as a liquid crystal TV, wiring of an electronic device which has a movable part. The flexible flat cable of the present invention is easy to be folded or bundled neatly, in addition to being able to be divided or branched using a cutting groove provided in an insulating coating.

<실시예> <Example>

이하, 실시예 및 비교예를 들어 본 발명을 보다 구체적으로 설명하는데, 본 발명은 이들 실시예로만 한정되는 것은 아니다. 각 물성 및 특성의 평가 방법은 다음과 같다. Hereinafter, although an Example and a comparative example are given and this invention is demonstrated more concretely, this invention is not limited only to these Examples. The evaluation method of each physical property and a characteristic is as follows.

(1) 난연성 평가 (1) flame retardancy evaluation

UL 규격 1581에 따라 수직 연소 시험 VW-1에 5점의 시료를 제공하고, 5점 모두 합격한 경우에 "합격"으로 판정하였다. 그 판정 기준은 각 시료에 15초 착화를 5회 반복한 경우에, 60초 이내에 소화되고, 하부에 깐 탈지면이 연소 낙하물에 의해 불붙지 않고 시료의 상부에 부착한 크래프트 종이가 타거나 눋지 않는 것을 합격으로 하였다. 5점의 시료 모두 합격한 것에 대해서는 각 시험에서의 최장 연소 시간의 평균값(5점의 평균값)을 기재하였다. When five samples were provided to the vertical combustion test VW-1 according to UL specification 1581, and all five points passed, it determined as "passed". The criterion is that if 15 seconds of ignition are repeated five times for each sample, it is extinguished within 60 seconds, and the cotton wool on the bottom is not burned by the combustion drops and the kraft paper attached on the upper part of the sample is not burned or broken. It was passed. When all five samples passed, the average value (average value of five points) of the longest burning time in each test was described.

(2) 인장 특성 평가 (2) tensile properties evaluation

시료의 절연 피복층에 대하여 인장 시험(인장 속도=50mm/분, 표선간 거리=25mm, 온도=23℃)을 행하고, 인장 강도와 인장 파단 연신도를 각 3점의 시료로 측정하고, 그들의 평균값을 구하였다. UL 규격에 따라 인장 강도가 8.2MPa 이상이면서 인장 파단 연신도 100% 이상인 것을 "합격"으로 판정하였다. Tensile tests (tensile velocity = 50 mm / min, distance between the marking lines = 25 mm, temperature = 23 ° C.) were performed on the insulating coating layer of the sample, and tensile strength and tensile elongation at break were measured with three samples, and their average value was measured. Obtained. According to the UL standard, it was determined as "passed" that the tensile strength was 8.2 MPa or more and the tensile elongation at break was 100% or more.

(3) 내열 노화성 평가 (3) Heat resistance aging evaluation

내열성 평가는 시료의 절연 피복층을 113℃의 기어 오븐 내에 168시간 방치하여 열노화시킨 후, 상기와 동일한 조건으로 인장 시험을 실시함으로써 수행하였다. UL 규격에 따라 연신도 잔률〔=100×(열노화 후의 연신도/열노화 전의 연신도)〕이 75% 이상, 및 인장 강도 잔률〔=100×(열노화 후의 인장 강도/열노화 전의 인장 강도)〕이 75% 이상을 갖는 것을 "합격"으로 판정하였다. Heat resistance evaluation was performed by leaving the insulating coating layer of a sample to stand in a gear oven at 113 degreeC for 168 hours, and heat-aging, and performing a tensile test on the same conditions as the above. According to the UL standard, the elongation residual ratio [= 100 × (extension after thermal aging / expansion before thermal aging)] is 75% or more, and the tensile strength residual ratio == 100 × (tensile strength after thermal aging / tensile strength before thermal aging) ) Was determined to have "passed".

(4) 내가열 변형성 평가 (4) heat resistance deformation evaluation

시료를 100℃의 기어 오븐 내에 세팅하고 60분간 예열 후, 시료 상부로부터 하중 250g, 외경 9.5mm의 원반형 지그로 시료를 60분간 눌러 절연체의 변형 잔률〔=100×(시험 후의 두께/시험 전의 두께)〕이 50% 이상인 것을 "합격"으로 판정하였다. After setting the sample in a gear oven at 100 ° C. and preheating for 60 minutes, the sample was pressed for 60 minutes with a disc jig having a load of 250 g and an outer diameter of 9.5 mm (= 100 × (thickness after the test / thickness before the test)). ] Was determined to be "pass".

(5) 저온 특성 평가 (5) low temperature characteristics evaluation

시료를 -10℃의 저온조에 4시간 방치하고, 그 후 시료의 외경의 2배의 지름의 금속 막대에 -10℃에서 U자 굽힘을 행하고, 절연 피복층의 갈라짐(크랙)의 유무를 육안으로 판정하였다. 갈라짐이 없는 것을 저온 특성이 "합격"인 것으로 판정하였다.The sample was left to stand in a low temperature bath at -10 ° C for 4 hours, and then U-shaped bend was performed at -10 ° C on a metal rod having a diameter twice the outer diameter of the sample to visually determine the presence of cracks (cracks) in the insulating coating layer. It was. The absence of cracking was determined as the low temperature property to be "pass".

[실시예 1] Example 1

2축 혼합기(45mmφ, L/D=42)를 이용하여 표 1의 실시예 1에 나타낸 배합 처방으로 각 성분을 용융 혼합하고, 스트랜드 모양으로 용융 압출하고, 이어서 용융 스트랜드를 냉각 절단하여 펠렛을 제조하였다. 표 1에 기재한 수지 조성물에는 수지 성분 100중량부에 대하여 활제로서 올레산 아마이드 0.5중량부와, 산화 방지제로서 펜타에리스리톨-테트라키스〔3-(3,5-다이-t-뷰틸-4-하이드록시페닐)프로피오네이트〕 1중량부를 배합하였다. Using a biaxial mixer (45 mmφ, L / D = 42), each component was melt-blended according to the formulation formulation shown in Example 1 of Table 1, melt-extruded into strand shape, and then the melt strand was cooled and cut to prepare pellets. It was. In the resin composition shown in Table 1, 0.5 part by weight of oleic acid amide as a lubricant and 100 parts by weight of resin component, and pentaerythritol-tetrakis [3- (3,5-di-t-butyl-4-hydroxy) as an antioxidant Phenyl) propionate] 1 part by weight of the mixture.

폭 1.2mm, 두께 0.15mm의 평각 도체(평판형 주석 도금 구리선) 8개를 공급 릴 그룹에서 집선기로 보내고, 도체 피치 2.0mm로 병렬로 배치하였다. 이어서 병렬 배치한 8개의 평각 도체를 용융 압출기의 다이스로 보내고, 표 1의 실시예에 나 타낸 수지 조성물의 펠렛을 용융 압출기에서 공급하여 절연 피복하였다. 절연 피복의 두께는 0.2mm이고, 절연 피복의 양면에 마련한 절개홈의 형상은 V자 형상(깊이 0.2mm)이며, 마진부의 코너부 절개홈의 형상은 비스듬한 직선 형상이고, 마진부의 폭은 각 평각 도체간 간격의 1/2이었다.Eight flat conductors (flat tin-plated copper wire) having a width of 1.2 mm and a thickness of 0.15 mm were sent to the concentrator in the supply reel group, and were arranged in parallel with a conductor pitch of 2.0 mm. Subsequently, the eight flat conductors arranged in parallel were sent to the die of the melt extruder, the pellet of the resin composition shown in the Example of Table 1 was supplied from the melt extruder, and was insulated-coated. The thickness of the insulation coating is 0.2 mm, the shape of the cutouts provided on both sides of the insulation coating is V-shaped (0.2 mm in depth), the shape of the corner cutouts of the margin part is an oblique straight line shape, and the width of the margin part is each flat. 1/2 of the spacing between conductors.

이와 같이하여 얻어진 플렉시블 플랫 케이블로부터 8개의 평각 도체를 포함하는 시료를 잘라내어 수직 연소 시험을 행하였더니, 수직 연소 시험 VW-1에 합격하였으며, 5점의 시료의 최장 연소 시간의 평균값은 42초로 난연성이 뛰어났다. 결과를 표 1에 나타내었다. The sample containing eight flat conductors was cut out from the flexible flat cable obtained in this way, and the vertical combustion test was carried out. The vertical combustion test VW-1 was passed, and the average value of the longest burning time of the five samples was 42 seconds. Excellent The results are shown in Table 1.

[실시예 2 내지 8] [Examples 2 to 8]

실시예 1에서 난연성 수지 조성물의 배합 처방을 표 1의 실시예 2 내지 8에 나타낸 것으로 변경한 것 이외에는 실시예 1과 동일한 방법으로 각 플렉시블 플랫 케이블을 제조하였다. 결과를 표 1에 나타내었다.Each flexible flat cable was manufactured by the same method as Example 1 except having changed the formulation prescription of the flame-retardant resin composition in Example 1 to what was shown to Examples 2-8 of Table 1. The results are shown in Table 1.

(각주) (footnote)

(1)아디페이트형 TPU(JIS 경도=A80): 소프트 세그먼트가 아디페이트형이고, JIS 경도가 A80인 열가소성 폴리우레탄 엘라스토머, (1) adipate type TPU (JIS hardness = A80): thermoplastic polyurethane elastomer having a soft segment of adipate type and JIS hardness of A80,

(2)PTMG형 TPU(JIS 경도=A80): 소프트 세그먼트가 폴리테트라메틸렌글리콜형이고, JIS 경도가 A80인 열가소성 폴리우레탄 엘라스토머,(2) PTMG type TPU (JIS hardness = A80): thermoplastic polyurethane elastomer whose soft segment is polytetramethylene glycol type and JIS hardness is A80,

(3)PC형 TPU(JIS 경도=A80): 소프트 세그먼트가 폴리카보네이트형이고, JIS 경도가 A80인 열가소성 폴리우레탄 엘라스토머,(3) PC type TPU (JIS hardness = A80): thermoplastic polyurethane elastomer whose soft segment is polycarbonate type and JIS hardness is A80,

(4)PTMG형 TPU(JIS 경도=A85): 소프트 세그먼트가 폴리테트라메틸렌글리콜형이고, JIS 경도가 A85인 열가소성 폴리우레탄 엘라스토머,(4) PTMG type TPU (JIS hardness = A85): thermoplastic polyurethane elastomer whose soft segment is polytetramethylene glycol type and JIS hardness is A85,

(5)PC형 TPU(JIS 경도=A85): 소프트 세그먼트가 폴리카보네이트형이고, JIS 경도가 A85인 열가소성 폴리우레탄 엘라스토머, (5) PC type TPU (JIS hardness = A85): thermoplastic polyurethane elastomer whose soft segment is polycarbonate type and JIS hardness is A85,

(6)아디페이트형 TPU(JIS 경도=A85): 소프트 세그먼트가 아디페이트형이고, JIS 경도가 A85인 열가소성 폴리우레탄 엘라스토머, (6) Adipate type TPU (JIS hardness = A85): thermoplastic polyurethane elastomer whose soft segment is adipate type and JIS hardness is A85,

(7)아디페이트형 TPU(JIS 경도=A97): 소프트 세그먼트가 아디페이트형이고, JIS 경도가 A90인 열가소성 폴리우레탄 엘라스토머,(7) adipate type TPU (JIS hardness = A97): thermoplastic polyurethane elastomer whose soft segment is adipate type and JIS hardness is A90,

(8)PTMG형 TPU(JIS 경도=A98): 소프트 세그먼트가 폴리테트라메틸렌글리콜형이고, JIS 경도가 A98인 열가소성 폴리우레탄 엘라스토머,(8) PTMG type TPU (JIS hardness = A98): thermoplastic polyurethane elastomer having soft segment of polytetramethylene glycol type and JIS hardness of A98,

(9)EVA-1: 아세트산 바이닐 단위의 함유량이 90중량%인 에틸렌-아세트산 바이닐 공중합체〔무니 점도(ML_{1 +4}, 100℃)=28〕,(9) EVA-1: ethylene-vinyl acetate unit content of 90% by weight of a-vinyl acetate copolymer [Mooney viscosity _{(ML 1 +4, 100 ℃)} = 28 ],

(10)EVA-2: 아세트산 바이닐 단위의 함유량이 50중량%인 에틸렌-아세트산 바이닐 공중합체〔무니 점도(ML_{1 +4}, 100℃)=27〕,(10) EVA-2: an ethylene content of vinyl acetate unit of 50% by weight vinyl acetate copolymer [Mooney viscosity _{(ML 1 +4, 100 ℃)} = 27 ],

(11)EVA-3: 아세트산 바이닐 단위의 함유량이 41중량%인 에틸렌-아세트산 바이닐 공중합체(MFR=2g/10분),(11) EVA-3: Ethylene-vinyl acetate copolymer (MFR = 2 g / 10min) whose content of a vinyl acetate unit is 41 weight%,

(12)합성 수산화마그네슘: 평균 입자 직경=0.8μm, BET 비표면적=6m²/g, 아미노실레인 처리품, 합성품,(12) Synthetic magnesium hydroxide: average particle diameter = 0.8 μm, BET specific surface area = 6 m ² / g, aminosilane-treated product, synthetic product,

(13)천연 수산화마그네슘: 평균 입자 직경=3μm, 아미노실레인 처리품, 천연품,(13) Natural magnesium hydroxide: average particle diameter = 3μm, aminosilane-treated products, natural products,

(14)유기화 산화물: 2,5-다이메틸-2,5-다이(t-뷰틸퍼옥시)헥세인,(14) organic oxides: 2,5-dimethyl-2,5-di (t-butylperoxy) hexane,

(15)가교 조제: 트라이에틸렌글리콜다이메타크릴레이트.(15) Crosslinking aid: triethylene glycol dimethacrylate.

<고찰> <Consideration>

표 1에 나타낸 바와 같이, PTMG형 열가소성 폴리우레탄 엘라스토머 40 내지 90중량% 및 에틸렌-아세트산 바이닐 공중합체(아세트산 바이닐 단위의 함유량=50 내지 90중량%) 10 내지 60중량%를 함유하는 수지 성분 100중량부에 대하여 평균 입자 직경 0.8μm이고 아미노실레인 커플링제로 표면 처리한 합성 수산화마그네슘을 40 내지 250중량부의 비율로 함유시킨 난연성 수지 조성물로 피복한 플렉시블 플랫 케이블(실시예 1 내지 4)은 UL 규격의 수직 연소 시험 VW-1에 합격하는 고도의 난연성을 나타내며, 절연 피복층(절연체)의 인장 강도가 10.0MPa 이상이고 인장 파단 연신도가 100% 이상이며, 113℃×168시간 노화 후의 인장 강도의 잔률이 75% 이상이면서 인장 파단 연신도의 잔률이 75% 이상을 나타내며, 가열 변형 시험에서도 잔률이 50% 이상을 나타내어 모든 특성에서 합격하는 것을 알 수 있었다. 또한 이들 절연 전선은 저온 특성 시험에서도 절연 피복에 크랙이 들어가지 않고 합격하는 것을 알 수 있었다. As shown in Table 1, 100 wt% of the resin component containing 40 to 90 wt% of PTMG type thermoplastic polyurethane elastomer and 10 to 60 wt% of ethylene-vinyl acetate copolymer (content of vinyl acetate units = 50 to 90 wt%). The flexible flat cable (Examples 1 to 4) coated with a flame-retardant resin composition containing an average particle diameter of 0.8 µm per part and a surface-treated synthetic magnesium hydroxide in an amount of 40 to 250 parts by weight with an aminosilane coupling agent was UL standard. It exhibits a high flame retardancy that passes the vertical combustion test of VW-1, and the tensile strength of the insulating coating layer (insulator) is 10.0 MPa or more, the tensile elongation at break is 100% or more, and the residual strength of the tensile strength after aging 113 ° C. 168 hours. Is more than 75% and the residual elongation at break is 75% or more, and the residual rate is more than 50% even in the heat deformation test. I could see that. Moreover, it turned out that these insulated wires pass even without a crack in an insulating coating in the low temperature characteristic test.

상기한 PTMG형 열가소성 폴리우레탄 엘라스토머 대신 아디페이트형 열가소성 폴리우레탄 엘라스토머를 사용한 경우(실시예 5 및 6)나 폴리카보네이트형 열가소성 폴리우레탄 엘라스토머를 사용한 경우(실시예 7)에도 UL 규격의 수직 연소 시험 VW-1을 포함하는 모든 특성에서 합격하는 플렉시블 플랫 케이블이 얻어짐을 알 수 있다. Vertical combustion test VW of UL standard even when the adipate type thermoplastic polyurethane elastomer is used instead of PTMG type thermoplastic polyurethane elastomer (Examples 5 and 6) or when the polycarbonate type thermoplastic polyurethane elastomer is used (Example 7). It can be seen that a flexible flat cable that passes in all characteristics including -1 is obtained.

상기한 합성 수산화마그네슘 대신 평균 입자 직경이 3μm이고 아미노실레인 커플링제로 처리한 천연 수산화마그네슘을 사용한 경우(실시예 8)에도 UL 규격의 수직 연소 시험 VW-1을 포함한 모든 특성에서 합격하는 플렉시블 플랫 케이블이 얻어짐을 알 수 있다. Flexible flats that pass in all properties, including the vertical combustion test VW-1 of UL standards, even when using natural magnesium hydroxide treated with an aminosilane coupling agent and having an average particle diameter of 3 μm instead of the synthetic magnesium hydroxide described above (Example 8). It can be seen that a cable is obtained.

[비교예 1 내지 10] [Comparative Examples 1 to 10]

표 2에 나타낸 배합 처방을 갖는 수지 조성물을 사용한 것 이외에는 실시예 1 내지 8과 동일한 방법으로 절연 전선을 제조하였다. 단, 비교예 8에서는 유기화 산화물 0.04중량부와 가교 조제 0.08중량부를 배합하여 열가교한 절연 피복을 갖는 플렉시블 플랫 케이블을 제조하였다. 결과를 표 2에 나타내었다.An insulated wire was manufactured in the same manner as in Examples 1 to 8 except that the resin composition having the formulation formulation shown in Table 2 was used. However, in the comparative example 8, 0.04 weight part of organic oxides and 0.08 weight part of crosslinking adjuvant were mix | blended and the flexible flat cable which has the heat-crosslinked insulation coating was manufactured. The results are shown in Table 2.

(각주)(footnote)

표 1의 각주와 동일하다. Same as footnote of Table 1.

<고찰> <Consideration>

수지 성분으로서 PTMG형 열가소성 폴리우레탄 엘라스토머를 단독으로 사용한 경우(비교예 1)에는 난연성이 불충분하였다. 수지 성분으로서 에틸렌-아세트산 바이닐 공중합체(아세트산 바이닐 단위의 함유량=90중량%)를 단독으로 사용한 경우(비교예 2)에는 내가열 변형성이 불합격이었으며 저온 특성 시험에서도 절연 피복에 크랙이 들어가 불합격이었다. When PTMG type thermoplastic polyurethane elastomer was used alone (Comparative Example 1) as the resin component, the flame retardancy was insufficient. When the ethylene-vinyl acetate copolymer (content of the vinyl acetate unit = 90 wt%) alone was used as the resin component (Comparative Example 2), the heat resistance deformation resistance was failed, and cracks in the insulating coating were also failed in the low temperature characteristic test.

수지 성분 내의 에틸렌-아세트산 바이닐 공중합체(아세트산 바이닐 단위의 함유량=90중량%)의 비율이 70중량%인 수지 조성물을 사용한 경우(비교예 3)에는 난연성이 불충분하였다. The flame retardance was inadequate when the resin composition whose ratio of the ethylene-vinyl acetate copolymer (content of vinyl acetate unit = 90 weight% of vinyl acetate units) in a resin component was 70 weight% (comparative example 3).

에틸렌-아세트산 바이닐 공중합체로서 아세트산 바이닐 단위의 함유량이 41중량%인 EVA-3을 사용한 경우(비교예 4)에는 난연성이 불충분한 것 이외에, 초기의 인장 강도가 비교적 낮고 가열 변형률이 제로이었다. When EVA-3 having 41% by weight of vinyl acetate unit was used as the ethylene-vinyl acetate copolymer (Comparative Example 4), the initial tensile strength was relatively low and the heating strain was zero, in addition to insufficient flame retardancy.

수산화마그네슘의 배합 비율이 지나치게 낮은 경우(비교예 5)에는 크래프트 종이까지 불길이 번졌으며, 수직 연소 시험 VW-1에 불합격이 되었다. 수산화마그네슘의 배합 비율이 지나치게 높은 경우(비교예 6)에는 수직 연소 시험 VW-1에는 합격하지만 인장 특성이 충분하지 않았다. When the blending ratio of magnesium hydroxide was too low (Comparative Example 5), the flame spread to kraft paper and failed in the vertical combustion test VW-1. When the compounding ratio of magnesium hydroxide was too high (comparative example 6), it passed the vertical combustion test VW-1, but the tensile properties were not sufficient.

열가소성 폴리우레탄 엘라스토머로서 JIS 경도가 98A인 PTMG형 열가소성 폴리우레탄 엘라스토머를 사용한 경우(비교예 7)에는 수직 연소 시험 VW-1에는 합격하지만 절연 피복층(절연체)의 인장 파단 연신도가 70%로 열악하였다. 따라서 기타 특성에 대해서는 측정을 생략하였다. When a PTMG-type thermoplastic polyurethane elastomer having JIS hardness of 98A was used as the thermoplastic polyurethane elastomer (Comparative Example 7), the vertical burn test VW-1 was passed, but the tensile fracture elongation of the insulating coating layer (insulator) was poor at 70%. . Therefore, the measurement was omitted for the other characteristics.

에틸렌-아세트산 바이닐 공중합체로서 아세트산 바이닐 단위의 함유량이 41중량%인 EVA-3을 사용하고, 유기화 산화물과 가교 조제를 배합하여 열가교한 경우(비교예 8)에는 수직 연소 시험 VW-1에 불합격이었다. When ethylene-vinyl acetate copolymer contains EVA-3 having 41% by weight of vinyl acetate units, and is thermally crosslinked by combining an organic oxide and a crosslinking aid (Comparative Example 8), the vertical combustion test VW-1 fails. It was.

수지 성분 내의 아디페이트형 열가소성 폴리우레탄 엘라스토머(JIS 경도=A85)의 중량 비율을 30중량%로 하고, 수산화마그네슘의 배합 비율을 120중량으로 한 경우(비교예 9)에는 절연 피복층(절연체)의 인장 파단 연신도가 100%를 밑돌아 기계 물성이 떨어졌다. 따라서, 다른 제반 특성의 측정을 생략하였다. When the weight ratio of the adipate-type thermoplastic polyurethane elastomer (JIS hardness = A85) in the resin component is 30% by weight, and the compounding ratio of magnesium hydroxide is 120% (Comparative Example 9), the tension of the insulating coating layer (insulator) Elongation at break was below 100%, resulting in poor mechanical properties. Therefore, the measurement of other various characteristics was omitted.

에틸렌-아세트산 바이닐 공중합체로서 아세트산 바이닐 단위의 함유량이 41중량%인 EVA-3을 사용하고, 수지 성분 내의 폴리카보네이트형 열가소성 폴리우레탄 엘라스토머의 중량 비율을 70중량%로 높인 경우(비교예 10)에는 수직 연소 시험 VW-1에 불합격이었다. 따라서 다른 제반 특성의 측정을 생략하였다. When EVA-3 having 41% by weight of vinyl acetate unit is used as the ethylene-vinyl acetate copolymer and the weight ratio of the polycarbonate-type thermoplastic polyurethane elastomer in the resin component is increased to 70% by weight (Comparative Example 10) It failed the vertical combustion test VW-1. Therefore, the measurement of other various characteristics was omitted.

본 발명의 플렉시블 플랫 케이블은 전자 기기 등의 기내 배선에 적합하게 이용할 수 있다. The flexible flat cable of this invention can be used suitably for in-flight wiring, such as an electronic device.

도 1은 본 발명의 플렉시블 플랫 케이블의 일례의 개략 단면도이다. 1 is a schematic cross-sectional view of an example of a flexible flat cable of the present invention.

도 2는 본 발명의 플렉시블 플랫 케이블의 바람직한 구조의 일례를 보인 설명도이다. 2 is an explanatory view showing an example of a preferred structure of the flexible flat cable of the present invention.

<부호의 설명><Description of the code>

10: 플렉시블 플랫 케이블,10: flexible flat cable,

11: 평각 도체,11: flat conductor,

12: 절연 피복,12: insulation cloth,

13: 절개홈, 13: incision groove,

14: 마진부, 14: margin,

15: 마진부의 코너부 절개홈, 15: corner incision groove of the margin part,

PO: 중심점, PO: center point,

M: 마진부의 폭, M: width of the margin,

P: 도체 피치, P: conductor pitch,

C: 평각 도체의 폭, C: width of the flat conductor,

G: 각 평각 도체간 간격, G: spacing between each flat conductor,

W: 플렉시블 플랫 케이블의 전체 폭 W: overall width of flexible flat cable

Claims (2)

병렬로 배치한 복수 개의 평각 도체를 절연 피복 재료에 의해 일괄적으로 절연 피복 성형하여 이루어지는 플렉시블 플랫 케이블에 있어서, In the flexible flat cable formed by collectively insulating coating molding a plurality of flat conductors arranged in parallel with an insulating coating material, 이 절연 피복 재료가, JIS K 7311에 따라 측정한 JIS 경도가 A97 이하인 열가소성 폴리우레탄 엘라스토머(A)와 아세트산 바이닐 단위의 함유량이 50 내지 90중량%인 에틸렌-아세트산 바이닐 공중합체(B)를 중량비(A:B)로 40:60 내지 90:10의 비율로 함유하는 수지 성분 100중량부에 대하여 금속 수산화물(C)을 40 내지 250중량부의 비율로 함유시킨 난연성 수지 조성물인 것을 특징으로 하는 플렉시블 플랫 케이블. This insulating coating material is a thermoplastic polyurethane elastomer (A) having a JIS hardness of A97 or less measured according to JIS K 7311 and an ethylene-vinyl acetate copolymer (B) having a content of 50 to 90% by weight of vinyl acetate units (by weight ratio) A flexible flat cable comprising a metal hydroxide (C) in a proportion of 40 to 250 parts by weight with respect to 100 parts by weight of a resin component contained in a ratio of 40:60 to 90:10 in A: B). . 제 1 항에 있어서, The method of claim 1, 인접하는 평각 도체의 중간 위치에서 길이 방향을 따라 절연 피복의 양 표면에 절개홈이 마련되어 있는 플렉시블 플랫 케이블. Flexible flat cable provided with cutouts on both surfaces of an insulating sheath along the longitudinal direction at intermediate positions of adjacent flat conductors.