KR20060017602A - 고속 기록을 위한 1회 기록 광 기록매체 - Google Patents
고속 기록을 위한 1회 기록 광 기록매체 Download PDFInfo
- Publication number
- KR20060017602A KR20060017602A KR1020057020975A KR20057020975A KR20060017602A KR 20060017602 A KR20060017602 A KR 20060017602A KR 1020057020975 A KR1020057020975 A KR 1020057020975A KR 20057020975 A KR20057020975 A KR 20057020975A KR 20060017602 A KR20060017602 A KR 20060017602A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- recording
- reflective layer
- thickness
- write
- Prior art date
Abstract
본 발명은 고속 기록을 위한 1회 기록 광 기록매체, 특히 DVD+R 디스크에 관한 것이다. 그러한 기록매체는 일반적으로 적어도 하나의 기판층(3), 기판 층(3)의 상면에 형성된 유기 염료 물질의 기록층(2), 및 기록층(2)의 상면에 형성된 금속 반사층(1)을 구비한다. 기록층과 반사층 간의 경계면에서 덜 가파른 온도 경사를 얻어 기계적 스트레스에 의해 층간박리가 발생하는 것을 방지하기 위해서, 금속 반사층(1)의 두께를 75nm 이하로 감소시키는 것을 제안한다. 기록층(2)과 금속 반사층(1) 사이에 50nm 이하의 두께를 갖는 유전층도 설치한다.
기록매체, 반사층, 기록층
Description
본 발명은 데이터를 고속으로 기록하는데 이용되는, DVD+R 등의 1회 기록 광 기록매체, 특히 단층 DVD+R에 관한 것이다.
현재, 고속 DVD+R 표준의 개발은 높은 우선순위를 갖는다. 현재의 염료(dye)계 고속 DVD+R 매체는 4x까지 혹은 6x까지도 적당한 성능을 나타낸다. 그러나, 전력 마진은 고속에서는 점점 좁아지고 있다. 고속 기록에 필요한 고전력에서는 층간박리(delamination)가 금속 염료(dye-metal) 경계면에서, 즉, 유기 염료 물질로 이루어진 기록층과 기록층을 냉각시키기 위해 설치된 금속 반사층 간의 경계면에서 발생한다. 이들 문제점은 유기 염료 물질로 이루어진 기록층을 구비하는, 1회 기록 광 기록매체, 특히 DVD+R 매체에 대하여 보다 빠른 기록속도를 달성할 가능성에 대한 염려를 증대시킨다. 그러나, 높은 반사성 디스크를 (반사층과 함께) 허용하는 염료 고유의 높은 투과성(transparency)에 의한 현존 플레이어의 기록 디스크의 백워드 호환성(backwards compatibility) 때문에 염료의 사용은 유리한 것으로 간주된다.
금속 반사층의 두께는 통상적으로 대략 100nm정도이다. 금속 반사층 존재의 중요한 효과는 그것의 큰 냉각 전력, 즉 그것의 높은 열 용량성(heat capacity)이다. 따라서, 금속 반사층의 두께 감소에 의해 염료 기록층이 덜 효율적인 냉각을 갖게 될 것이다. 이 염료는 매우 나쁜 열 조건만을 갖기 때문에, 금속 반사층에 의한 효율적인 냉각은 기록층과 금속 반사층 간의 경계면 부근에서 큰 온도 경사를 유발한다. 이러한 급격한 경사에 의한 기계적 스트레스는 상술한 층간박리 문제점을 일으킬 가능성이 있다.
US5,718,961은 제1 유전체막, 제2 유전체막, 기록막 및 반사막이 순차적으로 기판 위에 적층되어 있는 상 변화형 광 디스크에 대해서 개시한다. 이 반사막의 두께는 10~120nm의 넓은 범위에 포함될 수 있다. 제1 및 제2 유전체막의 물질로서 ZnO-BN을 사용하면, 높은 기록 감도 및 열적 안전성을 달성할 수 있으며, 기록 시에 생성된 열을 반사층으로 빠르게 흩어지게 할 수 있다.
본 발명은 층간박리와 같은 기계적 문제점을 해결하기 위해서 기록층과 금속 반사층 간의 경계면에서 온도 경사를 감소시키는 것 이외에도 기록속도를 보다 빠르게 하는 1회 기록 광 기록매체를 제공하는데 그 목적이 있다.
본 발명의 목적을 달성하기 위한 본 발명에 따른 청구항 1에 기재된 1회 기록 광 기록매체는,
기판층,
상기 기판 층의 상면에 형성된 유기 염료 물질의 기록층, 및
상기 기록층의 상면에 형성된 75nm 이하의 두께를 갖는 금속 반사층을 구비 한다.
본 발명은 금속 반사층의 두께 감소에 유리한 발견물(finding)에 근거한다. 그 두께의 감소에 의해 냉각의 효율은 저하되지만, 기록층과 반사층 간의 경계면에서의 온도 경사는 더 완만해진다. 이것은 기계적 스트레스를 줄여서 층간박리(delamination)를 방지한다. 따라서, 기록 스택에서 냉각 효율의 저하가 실제로 고속 기록 성능을 향상시킬 수도 있다. 이것은 본 발명에 의해 기록매체가 유기 염료 물질 또는 상 변화 물질로 구성된 기록층을 갖는다는 것을 의미한다.
본 발명의 바람직한 실시예는 종속항들에 한정되어 있다. 75nm이하의 두께를 갖는 금속 반사층에 의해 고속 기록 성능을 향상시킬 수 있지만, 그 두께를 50nm이하, 특히 30nm이하로 더 감소시키면 고속 기록 성능을 더 향상시킬 수 있다.
또 다른 바람직한 실시예에 따르면, 기록층과 금속 반사층 사이에 추가적으로 유전층이 설치된다. 이 유전층은 열 장벽(thermal barrier)으로서 작용하여 반사층의 열 싱크 능력(heat-sink capability)을 감소시킬 수 있다. 이 추가적인 유전층, 예를 들면 SiO2, ZnS, ZnS-SiO2 혼합물(예를 들면 8:2), TiO2 또는 다른 유전체 물질은 감소된 흡수율로 기록 스택의 반사율을 꽤 향상시킨다. 그러나, 이를 보상하기 위해서, 높은 k(k는 복합 굴절율(complex refractive index)의 허수부)값을 갖는 염료, 혹은 통상 100nm의 두께를 갖는 얇은 기록층을 사용한다는 것을 예견할 수 있다.
임의로, 또 다른 유전층이 전체 기록 스택의 안전성을 향상시키기 위해서 기록층과 기판층 사이에 설치될 수 있다. 기록층과 금속 반사층 사이의 적어도 제1 유전층은 50nm 이하의 두께, 특히 25nm 이하의 두께를 갖는다.
금속 반사층의 바람직한 물질은 대체로 은(Ag)으로 이루어져 있다. 그러나, Al, Au 등의 다른 물질들 또는 다른 금속들도 사용될 수 있다.
도 1은 100nm Ag층을 갖는 DVD+R 디스크의 전력 마진을 나타낸다.
도 2는 10nm Ag층을 갖는 DVD+R 디스크의 전력 마진을 나타낸다.
도 3a는 종래의 1회 기록 광 기록매체에 DC-전력 레벨을 인가한 후의 온도 분포를 나타낸다.
도 3b는 본 발명에 따른 1회 기록 광 기록매체에 DC-전력 레벨을 인가한 후의 온도 분포를 나타낸다.
도 4는 본 발명에 따른 기록매체의 다른 실시예의 온도 분포를 나타낸다.
도 5는 본 발명에 따른 기록매체의 또 다른 실시예의 온도 분포를 나타낸다.
도 6은 본 발명에 따른 기록매체의 제1 실시예의 개략적인 레이아웃을 나타낸다.
도 7은 본 발명에 따른 기록매체의 제2 실시예의 개략적인 레이아웃을 나타낸다.
도 1은 DVD+R 디스크에서 두꺼운 반사층, 특히 100nm Ag층의 대표적인 전력 마진을 나타낸다. 그 디스크 상에 기록되는 비트의 리딩 엣지(leading edge)와 트레일링 엣지(trailing edge)는 기록 전력[nw]과 지터[%]로 표시되어 있다. 이 전력 마진은 도 2에 나타낸 얇은 반사층에 대한 전력 마진과 비교되어야 하는데, 도 2에서는 DVD+R에서 Ag로 이루어진 반사층이 10nm의 두께를 갖는다. 도시한 바와 같이 지터는 보다 넓은 범위의 기록 전력에서는 매우 낮으며, 특히 도 1에 나타낸 두꺼운 반사층에 의해 달성된 지터에 비해서는 기록 전력을 높다.
Ag(100nm)으로 이루어진 두꺼운 반사층(1), 염료 기록층(2; 100nm), 및 폴리카보나이트(polycarbonate) 기판층(3; 100nm)을 갖는 종래의 DVD+R 기록 스택에 DC-전력 레벨을 인가한 후의 온도 분포가 도 3a에 도시되어 있다. 두꺼운 반사층의 상면에 UV-경화형 래커(lacquer)에 의해 접착되는 더미 기판은 도 3a에 도시되어 있지 않다. 염료 물질은 매우 나쁜 열 조건을 갖기 때문에, 반사층(1)에 의한 효율적인 냉각은 반사층(1)과 기록층(2) 간의 경계면 부근에 큰 온도 경사를 유발한다. 이 가파른 경사에 의한 기계적 스트레스는 반사층(1)과 기록층(2) 간의 경계면에서 층간 박리(delamination)를 일으킨다.
반사층(1)의 두께를 감소시키면, 냉각의 효율은 저하되지만, 온도 경사는 도 3b에 도시한 바와 같이 더 완만해 진다. 도 3b는 본 발명에 따른 기록매체의 제1 실시예에 DC-전력 레벨을 인가한 후의 온도 분포는 나타낸다. 여기서, 반사층은 대략 10nm정도의 두께를 가지며 Ag로 형성되어 있다.
본 발명에 따른 기록매체의 제2 실시예의 온도(thermal) 분포가 도 4에 도시되어 있다. 여기서, 도 3a에 도시한 기록매체와 비교하여, 20nm의 두께를 가진, SiO2로 이루어진 유전층(5)이 추가적으로 40nm의 두께를 갖는 반사층(1)과 기록층(2) 사이에 형성되어 있다. 40nm의 두꺼운 반사층의 상면에 UV-경화형 래커 (lacquer)에 의해 접착되는 더미 기판은 도 4에 도시되어 있지 않다. 또한, 기록층(2)은 더 효율적인 흡수율(absorption)을 유발하는 80nm의 감소된 두께를 가지므로 어느 정도 높은 최대 온도에 도달한다는 것은 명확하다. 추가 유전층(5)은 반사층(1)과 기록층(2) 간의 온도 경사를 더 줄여서 기계적 스트레스를 감소시키며 층간박리를 방지한다.
본 발명에 따른 기록 매체의 제3 실시예의 온도(thermal) 분포는 도 5에 도시되어 있다. 여기서, Ag로 이루어진 반사층은 약간 높은 반사율을 제공하는 30nm의 두께를 가지만, 열 용량(thermal capacity)은 3.3으로 감소된다. 그럼에도 불구하고 이 실시예에서는 온도 경사가 덜 가파르다. 두꺼운 반사층의 상면에 UV-경화형 래커(lacquer)에 의해 접착되는 더미 기판은 도 5에는 도시되어 있지 않다.
도 6 및 도 7은 본 발명에 따른 기록 매체의 2종류의 실시예를 개략적으로 나타낸다. 도 6은 도 5에 도시된 온도 특성에 대한 실시예를 나타낸다. 도 5에 도시된 3개의 층 이외에도, 제2 폴리카보나이트 기판층(4; 대략 0.6nm)이 도시되어 있는데, 이 제2 폴리카보나이트 기판층(4)은 반사층(1)의 상면에 UV-경화형 래커에 의해 접착되어 있다. 도 7은 도 4에 도시된 온도 특성에 대한 실시예를 나타낸다. 도 4에 도시된 4개의 층 이외에도, 제2 폴리카보나이트 기판층(4; 대략 0.6nm)이 도시되어 있다.
이들 도면에 나타낸 실시예는 구체적인 예로 이해될 것이다. 또 다른 다수의 실시예들 및 다른 층들의 두께의 변화뿐만 아니라 또 다른 층의 연속 및 설치도 가능하다. 본 발명은 1회 기록 광 기록매체, 특히 DVD+R 매체에 대하여 보다 넓은 전 력 마진을 얻을 수 있는 이점을 제공한다. 더 나아가서, 기록 속도를 더 향상시킬 수 있다. 또, 얇은 반사층에 의해 스퍼터(sputter)하는 시간이 적게 걸려, 즉 제작 시간이 빨라져, 제조비용을 줄일 수 있다.
Claims (6)
- 기판층(3)과,상기 기판 층의 상면에 형성된 유기 염료 물질의 기록층(2)과,상기 기록층(2)의 상면에 형성된 75nm이하의 두께를 갖는 금속 반사층(1)을 구비하는 것을 특징으로 하는 1회 기록 광 기록매체.
- 제 1 항에 있어서,상기 기록층(2)과 상기 금속 반사층(1) 사이에 유전층(5)을 더 구비하는 것을 특징으로 하는 1회 기록 광 기록매체.
- 제 2 항에 있어서,상기 유전층(5)은 50nm 이하의 두께, 특히 25nm 이하의 두께를 갖는 것을 특징으로 하는 1회 기록 광 기록매체.
- 제 1 항에 있어서,상기 기록층(2)과 상기 기판층(3) 사이에 유전층을 더 구비하는 것을 특징으 로 하는 1회 기록 광 기록매체.
- 제 1 항에 있어서,상기 금속 반사층(1)은 Ag, Al, Au로 이루어져 있는 그룹의 물질, 특히 Ag로 형성되는 것을 특징으로 하는 1회 기록 광 기록매체.
- 제 1 항에 있어서,상기 금속 반사층(1)은 50nm 이하, 특히 30nm 이하의 두께를 갖는 것을 특징으로 하는 1회 기록 광 기록매체.