KR20050044788A - Fabric sheet combined with linen fabric and polyester fabric and method for manufacturing the same - Google Patents
Fabric sheet combined with linen fabric and polyester fabric and method for manufacturing the same Download PDFInfo
- Publication number
- KR20050044788A KR20050044788A KR1020050032975A KR20050032975A KR20050044788A KR 20050044788 A KR20050044788 A KR 20050044788A KR 1020050032975 A KR1020050032975 A KR 1020050032975A KR 20050032975 A KR20050032975 A KR 20050032975A KR 20050044788 A KR20050044788 A KR 20050044788A
- Authority
- KR
- South Korea
- Prior art keywords
- fiber
- sheet
- chemical
- fibers
- natural
- Prior art date
Abstract
본 발명은 천염섬유로서의 마(麻)섬유와 인조섬유(화학섬유)(예컨대 폴리에스테르섬유)를 결합하여 마섬유의 특유의 성질과 화학섬유의 특유한 성질을 갖춘 천연섬유와 화학섬유가 결합된 섬유시트와 그 제조방법에 관한 것이다.The present invention combines hemp fibers and artificial fibers (chemical fibers) (for example, polyester fibers) as natural fiber fibers and combines natural fibers and chemical fibers with unique properties of hemp fibers and chemical fibers. A sheet and a method of manufacturing the same.
바람직한 실시예에 따른 상기 섬유시트는 천연섬유로서의 마섬유의 일면 또는 양면에 솜형태의 화학섬유를 공급하여 니들펀칭방식으로 상호 분리되지 않도록 시트형상으로 결합하고, 그 결합된 시트형상에 대해서는 시트권취롤에 권취하고나서 일정한 길이와 폭으로 재단하여 시트재롤에 재차 권취하고, 그 시트재롤에 권취된 시트재를 함침조내에서 아크릴계 바인더약품에 의해 연질/경질로 가공하며, 상기 바인더약품처리된 시트재를 압착하여 건조시키고나서 프레스로울러에 의해 양면 평탄화처리를 실행하여 제조된다.The fiber sheet according to the preferred embodiment is supplied to the cotton or one side of the hemp fiber as a natural fiber by combining the form of the sheet so as not to be separated from each other by the needle punching method, the combined sheet shape wound sheet After winding on a roll, it is cut to a predetermined length and width, and wound again on a sheet material roll, and the sheet material wound on the sheet material roll is processed into soft / hard by an acrylic binder chemical in an impregnating tank, and the sheet material treated with the binder chemical It is produced by pressing and drying, and then performing a double-sided flattening treatment by a press roller.
필요한 경우, 약품처리과정에서 경화제와 섬유 유연제, 발수제, 정전기방지제, 항균/살균제, 방향제가 선택적으로 혼입되도록 해도 된다.If necessary, the curing agent and the fabric softener, water repellent, antistatic agent, antimicrobial / disinfectant, fragrance may be optionally incorporated.
Description
본 발명은 천연섬유와 화학섬유가 결합된 섬유시트와 그 제조방법에 관한 것으로, 보다 상세하게는 천연섬유로서의 마(麻)섬유에 화학섬유(대표적으로 폴리에스테르(Polyester)섬유)를 결합하여 천연섬유(마섬유)의 성질(통기성/항온도성/항균성)과 화학섬유의 성질(부드러운 접촉감/인장력)이 혼재되는 천연섬유와 화학섬유가 결합된 섬유시트와 그 제조방법에 관한 것이다.The present invention relates to a fiber sheet in which natural fibers and chemical fibers are combined, and a method of manufacturing the same. More specifically, the present invention relates to natural fibers by combining chemical fibers (typically polyester fibers) with hemp fibers as natural fibers. The present invention relates to a fiber sheet in which a natural fiber and a chemical fiber are combined, in which the properties of the fibers (abrasion fibers) (breathability / constant temperature / antibacterial) and the properties of the chemical fibers (smooth contact / tension) are mixed and a method of manufacturing the same.
일반적으로, 섬유는 천연섬유와 인조섬유(또는 화학섬유)로 대별되는 바, 그 중 천연섬유는 천연의 재료에서 얻어진 섬유로서 면(cotton)이라든지 마(flax, linen)가 식물성 천연섬유로서 대표적이고, 인조섬유는 화학합성 또는 재생에 의해 만들어진 섬유로서 폴리아미드(polyamide)라든지 폴리에스테르, 아크릴(acryl), 폴리우레탄(polyurethane)의 합성섬유가 대표적이다. In general, fibers are roughly classified into natural fibers and artificial fibers (or chemical fibers). Among them, natural fibers are fibers obtained from natural materials, and cotton or flax are representative of vegetable natural fibers. Artificial fibers are fibers made by chemical synthesis or regeneration, such as polyamide, synthetic fibers of polyester, acryl, and polyurethane.
그러한 천연섬유 또는 인조섬유는 의복의 제조에 널리 활용될 뿐만 아니라, 단독적으로 가방이라든지 신발, 벽지, 침대매트리스 등의 제조를 위한 부재(部材)로서 적용되거나 고무재/실리콘재나 지류(紙類) 또는 합성수지재 등과 병합적으로 널리 적용된다.Such natural or artificial fibers are not only widely used in the manufacture of garments, but also applied alone as parts for the manufacture of bags, shoes, wallpaper, bed mattresses, or the like. It is widely applied in combination with synthetic resin materials.
예컨대, 신발의 안창 또는 중창을 형성하기 위해서는 고무재상에 천연섬유로서의 면섬유 또는 인조섬유(화학섬유)를 접착하는 구조가 일반적으로, 고무재상에 천연섬유로서의 면섬유를 접착한 경우 면섬유는 인장력에서 불리한 반면 고무재상에 인조섬유를 접착한 경우에는 인장력의 면에서 다소 유리하기는 하지만 신발내에서의 통기성이라든지 습기조절성 및 항균성이 불량하기 때문에 그 신발부재에 대해 통기성의 보장 및 습기조절/항균 탈취기능의 강화가 요구되는 상황이다. For example, in order to form an insole or midsole of a shoe, a structure that bonds cotton fibers or artificial fibers (chemical fibers) as natural fibers to a rubber material is generally used. When cotton fibers as natural fibers are bonded to a rubber material, cotton fibers are disadvantageous in tensile force. Although it is somewhat advantageous in terms of tensile strength when the artificial fiber is bonded on the rubber material, the breathability and moisture control and antimicrobial properties of the shoe are poor. This situation requires strengthening.
또, 침대매트리스의 경우 탄성체가 내재된 매트리스본체의 외면에는 천연섬유 또는 인조섬유가 특정한 문양을 갖고서 가공된 매트리스커버가 갖추어지게 되는 바, 그러한 매트리스커버에 대해서도 세균의 번식을 극력 억제하는 항균기능이라든지 통기성 및 탈취기능의 강화에 대한 요구가 점차 증가되는 추세이다. In addition, the bed mattress is equipped with a mattress cover processed with natural fibers or artificial fibers having a specific pattern on the outer surface of the mattress body in which the elastic body is embedded. The mattress cover has an antibacterial function that suppresses the growth of bacteria as much as possible. There is a growing demand for enhanced breathability and deodorization.
그 밖에도, 침구류로서의 베개커버라든지 건축자재로서의 바닥재 또는 타일, 벽지, 바닥에 펼쳐지는 카페트, 모자의 챙 등에 대해서도 점차 습도조절기능과 통기성, 탈취기능의 보강에 대해서도 주목되는 상황이다.In addition, there is a situation where attention is gradually paid to the humidity control function, breathability, and deodorization function for pillow covers for beddings, flooring materials for building materials, tiles, wallpaper, carpets spread on the floor, and visors for hats.
따라서, 본 발명은 상기한 종래 기술의 사정을 감안하여 이루어진 것으로, 양호한 통기성과 항균/탈취 작용을 갖는 천연섬유로서의 마(麻)섬유와 부드러운 접촉감과 내구성(인장력)이 양호한 화학섬유(예컨대 폴리에스테르(Polyester)섬유)를 적정한 방식(특히 니들펀칭(niddle punching)방식)으로 결합함으로써 마섬유의 통기성/항온도성/항균성의 특성과 화학섬유의 부드러움과 양호한 인장력이 갖추어진 천연섬유와 화학섬유가 결합된 섬유시트와 그 제조방법을 제공함에 그 목적이 있다.Accordingly, the present invention has been made in view of the above-described circumstances of the prior art, and hemp fiber as a natural fiber having good breathability and antibacterial / deodorizing effect and chemical fiber having good soft contact and durability (tensile strength) (for example, polyester) By combining (Polyester fiber) in an appropriate way (especially needle punching method), natural fiber and chemical fiber combined with breathable / anti-temperature / antibacterial properties of hemp fiber, softness of chemical fiber and good tensile strength The purpose is to provide a fibrous sheet and a method of manufacturing the same.
상기한 목적을 달성하기 위해, 본 발명의 바람직한 실시형태에 따르면 천연섬유층과 화학섬유층을 일체로 결합하고 아크릴계바인더에 함침하여 압착건조시킴으로써 형성된 천연섬유와 화학섬유가 결합된 섬유시트가 제공된다.In order to achieve the above object, according to a preferred embodiment of the present invention there is provided a fiber sheet combined with natural fibers and chemical fibers formed by combining the natural fiber layer and the chemical fiber layer integrally, impregnated in an acrylic binder and compressed and dried.
바람직하게, 상기 천연섬유층과 화학섬유층은 니들펀칭방식에 의해 일체화된다.Preferably, the natural fiber layer and the chemical fiber layer is integrated by a needle punching method.
상기 아크릴계 바인더에는 경화제와 섬유 유연제, 발수제, 정전기방지제, 항균/살균제, 방향제가 선택적으로 혼입된다.In the acrylic binder, a curing agent, a fabric softener, a water repellent, an antistatic agent, an antibacterial / disinfectant agent, and an air freshener are selectively mixed.
본 발명의 다른 실시양태에 따르면, 천연섬유층과 화학섬유층 중 어느 하나에 화학섬유성분과 천연섬유성분을 대응적으로 공급하고, 상기 천연섬유층과 화학섬유층 중 어느 하나에 대응하는 화학섬유성분과 천연섬유성분이 상호 분리되지 않도록 결합하여 시트형상으로 형성하며, 상기 시트형상을 시트권취롤에 권취하여 후처리를 실행하는 단계로 이루어진 천연섬유와 화학섬유가 결합된 섬유시트의 제조방법이 제공된다.According to another embodiment of the present invention, a chemical fiber component and a natural fiber component are supplied correspondingly to any one of the natural fiber layer and the chemical fiber layer, and the chemical fiber component and the natural fiber corresponding to any one of the natural fiber layer and the chemical fiber layer. Forming a sheet shape by combining the components so as not to be separated from each other, there is provided a method for producing a fiber sheet combined with natural fibers and chemical fibers consisting of winding the sheet shape on a sheet winding roll to perform a post-treatment.
상기 천연섬유로는 마섬유가 포함되고, 그 마섬유의 일면 또는 양면에 상기 화학섬유층이 니들펀칭방식으로 결합된다.The natural fiber includes hemp fiber, and the chemical fiber layer is bonded to one side or both sides of the hemp fiber by needle punching.
상기 시트형상에 대한 후처리에는 그 시트권취롤에 권취된 시트형상을 일정한 치수와 폭으로 재단하여 시트재로서 시트재롤에 권취하고, 상기 시트재롤에 권취된 시트재를 함침조내에서 바인더약품에 의해 연질/경질로 가공하며, 상기 바인더약품처리된 시트재를 압착하여 건조시키고나서 프레스로울러에 의해 양면 평탄화처리를 실행하는 단계가 포함된다.In the post-treatment of the sheet shape, the sheet shape wound on the sheet winding roll is cut to a certain dimension and width and wound on the sheet material roll as a sheet material, and the sheet material wound on the sheet material roll is subjected to binder chemical in an impregnation tank. Processing to soft / hard, and pressing and drying the binder chemically treated sheet material, and then performing a double-sided planarization treatment by a press roller.
상기 바인더약품은 아크릴계 바인더이고, 경화제와 섬유 유연제, 발수제, 정전기방지제, 항균/살균제, 방향제가 선택적으로 혼입된다.The binder drug is an acrylic binder, and a curing agent, a fabric softener, a water repellent, an antistatic agent, an antibacterial / disinfectant agent, and an aromatic agent are optionally mixed.
이하, 본 발명에 대해 첨부도면을 참조하여 상세하게 설명한다.Hereinafter, with reference to the accompanying drawings, the present invention will be described in detail.
도 1은 본 발명의 바람직한 제 1실시예에 따른 천연섬유와 화학섬유가 결합된 섬유시트의 제조과정을 설명하기 위한 도면이고, 도 2는 도 1에 설명된 본 발명에 따른 천연섬유와 화학섬유가 결합된 섬유시트를 나타낸 도면이다.1 is a view for explaining a manufacturing process of a fiber sheet combined with natural fibers and chemical fibers according to a first embodiment of the present invention, Figure 2 is a natural fiber and chemical fibers according to the present invention described in FIG. Is a view showing a fiber sheet bonded.
도면에서, 10은 천연섬유(마섬유)권취롤에 권취되어 양호한 통기성과 항온도성 및 항균성을 갖는 천연섬유층으로서의 마섬유층을 나타내고, 20은 양호한 접촉감과 내구성을 갖는 화학섬유층(예컨대 폴리에스테르섬유층)을 나타낸다.In the figure, 10 denotes a hemp fiber layer as a natural fiber layer wound around a natural fiber (horse fiber) winding roll and having good breathability, constant temperature and antimicrobial properties, and 20 denotes a chemical fiber layer (for example, a polyester fiber layer) having good contact feeling and durability. Indicates.
본 발명에 따르면, 상기 마섬유층(10)과 상기 화학섬유층(20)은 상호 결합되어 일정한 길이로 시트권취롤(도시 생략)에 권취되고나서 필요한 용도(예컨대 중창재나 안창재 등의 신발부재, 벽지 등의 건축자재, 침대매트리스 등의 침구류, 가방심재 등의 생활용품재 등)에 맞도록 일정한 길이와 폭의 시트재로 재단되어 별도의 시트재롤에 권취된다.According to the present invention, the hemp fiber layer 10 and the chemical fiber layer 20 are bonded to each other and wound on a sheet winding roll (not shown) to a predetermined length (for example, shoe members such as midsole or insole), wallpaper, etc. It is cut into sheet material of a certain length and width so as to be suitable for building materials, beddings such as bed mattresses, and household goods such as bag core materials, and wound on a separate sheet material roll.
여기서, 상기 마섬유층(10)과 화학섬유층(20)의 사이에는 보다 양호한 결합력과 통풍/조습기능 등의 보강을 강화하기 위해 필요한 경우 소정 두께로 중간층으로서 '천연재질의 솜'(도시는 생략)이 개재되어도 바람직하게 된다.In this case, between the hemp fiber layer 10 and the chemical fiber layer 20, 'cotton of natural material' (not shown) as an intermediate layer to a predetermined thickness, if necessary in order to reinforce reinforcement such as better bonding strength and ventilation / humidity function. It is preferable even if this is interposed.
도 3은 본 발명의 제 1실시예에 따른 천연섬유와 인조섬유가 결합된 섬유시트의 제조방법을 설명하기 위한 흐름도이다.3 is a flowchart illustrating a method of manufacturing a fiber sheet combined with natural fibers and artificial fibers according to the first embodiment of the present invention.
먼저, 단계 21에서는 천연섬유층(10)으로서의 마섬유를 직조함과 더불어 화학섬유층(20)을 형성하기 위한 예컨대 폴리에스테르섬유를 준비하고, 단계 22에서 상기 마섬유와 상기 화학섬유를 접착하기 위해 예컨대 니들펀칭머신(Niddle Punching Machine)에 의해 니들펀칭작업(또는 접착제에 의한 접착)을 시행하여 상호 분리되지 않도록 하게 된다.First, in step 21, for example, weaving hemp fibers as the natural fiber layer 10, preparing polyester fibers for forming the chemical fiber layer 20, and in step 22, for example, to bond the hemp fibers and the chemical fibers, The needle punching machine (needle punching machine) is performed by needle punching machine (or adhesive bonding) so as not to be separated from each other.
여기서, 상기 마섬유층(10)과 상기 화학섬유층(20)의 사이에는 중간층으로서 천연재질의 솜을 개재시켜 상호간의 결합력을 강화시킴과 더불어 통기성과 조습기능 등의 향상이 이루어지도록 하게 된다.Here, between the hemp fiber layer 10 and the chemical fiber layer 20 through the cotton of the natural material as an intermediate layer to enhance the mutual bonding force and to improve the breathability and humidity control function.
상기 마섬유층(10) 또는 상기 화학섬유층(20)의 일면에 천연섬유(특히 면)의 솜을 공급하고나서 결합방식으로서 니들펀칭머신에 의해 니들펀칭방식이 적용되는 경우 상기 마섬유층(10) 또는 상기 화학섬유층(20)의 직조 조직내로 천연섬유성분의 솜이 침투하여 조직화되고, 그 상태에서 상기 마섬유층(10)의 솜이 조직화된 일측면에 상기 화학섬유층(20)을 결합하거나 상기 화학섬유층(20)의 솜이 조직화된 일측면에 상기 마섬유층(10)을 결합하게 된다.When the needle punching method is applied by a needle punching machine as a binding method after supplying cotton of natural fibers (particularly cotton) to one surface of the hemp fiber layer 10 or the chemical fiber layer 20 or the hemp fiber layer 10 or The cotton fiber of the natural fiber component penetrates into the woven tissue of the chemical fiber layer 20 and is organized. In that state, the cotton fiber of the hemp fiber layer 10 is bonded to the chemical fiber layer 20 or the chemical fiber layer 20 ) Cotton is combined with the hemp fiber layer 10 on one side of the tissue.
상기 마섬유층(10)과 상기 화학섬유층(20)이 상호 결합되고나면 단계 23에서 그 섬유시트를 소정의 시트권취롤(도시 생략)에 권취한 다음 그 섬유시트의 용도를 고려하여 일정한 길이와 폭으로 재단하여 시트재로서 별개의 시트재롤(도시 생략)에 권취하게 된다.After the hemp fiber layer 10 and the chemical fiber layer 20 are bonded to each other, in step 23, the fiber sheet is wound on a predetermined sheet winding roll (not shown), and then a predetermined length and width are considered in consideration of the use of the fiber sheet. The sheet is rolled up to be wound on a separate sheet roll (not shown) as the sheet member.
상기 시트재롤에 권취된 시트재는 단계 24에서 함침조에 투입되어 바인더약품처리가 실행되는 바, 그 바인더약품의 주원료로서는 해당하는 섬유시트의 용도에 따라 선택되는 아크릴계 바인더, 즉 아크릴산 에스테르를 주성분으로 하는 반응형 및 자기가교형의 아크릴공중합에멀전이나, 스티렌(styrene)과 아크릴산 에스테르공중합체를 주성분으로 하는 에멀전 중 어느 하나가 선택적으로 적용되거나 혼용된 형태가 적용된다.The sheet material wound on the sheet material roll is introduced into the impregnation tank in step 24, and the binder chemical treatment is carried out. As the main raw material of the binder chemical, a reaction based on an acrylic binder, that is, an acrylic ester, selected according to the purpose of the corresponding fiber sheet is used. Either type or self-crosslinked acrylic copolymer emulsions or emulsions based on styrene and acrylic ester copolymers are selectively applied or mixed.
즉, 상기 시트재롤에 권취된 시트재는 그 용도에 따라 연질(soft) 또는 경질(hard)화 가공이 이루어지게 되는 바, 예컨대 신발의 안창과 중창의 경우 연질가공 또는 경질가공이 필요하게 되고, 그러한 용도에 따른 연질/경질가공은 상기 아크릴계 바인더의 양으로 결정하거나 그 아크릴계 바인더의 성질로도 조절이 가능하게 된다.That is, the sheet member wound on the sheet member roll is subjected to soft (hard) or hard (hard) processing depending on its use, for example, insoles and midsoles of shoes need soft or hard processing, such as Soft / hard processing according to the use can be determined by the amount of the acrylic binder or can be controlled by the properties of the acrylic binder.
여기서, 상기 아크릴계 바인더에 대해서는 경화제라든지 섬유유연제, 발수제, 정전기방지제, 항균제/살균제, 방향제 등이 선택적으로 첨가되면 바람직하게 된다.Here, the acrylic binder is preferably a curing agent, a fabric softener, a water repellent, an antistatic agent, an antimicrobial agent / disinfectant, a fragrance, and the like.
상기 함침조내에서 아크릴계 바인더에 함침된 상기 시트재는 단계 25에서 예컨대 압착프레스에 의한 압착이 실행되고, 그 압착된 시트재를 단계 26에서 대략 100∼200℃의 열풍으로 대략 2∼10분간 건조시키게 된다.In the impregnating tank, the sheet material impregnated with the acrylic binder is pressed in step 25, for example, by a pressing press, and the pressed sheet material is dried in step 26 by hot air at approximately 100 to 200 ° C. for about 2 to 10 minutes. .
그 건조된 시트재는 단계 27에서 프레스로울로(도시 생략)에 의해 양면에 대한 평탄화작업이 이루어지고나서 단계 28에서 필요한 문양을 인쇄하고 필요한 형상(즉, 단위 롤 또는 시트)으로 재단하여 상품으로 포장되어 출하된다.The dried sheet material is flattened on both sides by a press roller (not shown) in step 27, and then the necessary pattern is printed in step 28 and cut into a required shape (i.e., unit roll or sheet) and packaged as a product. And shipped.
상기한 과정에 의해 본 발명에 따르면 양호한 통기성과 항균성을 갖는 마섬유와 양호한 접촉감과 내구성을 갖는 화학섬유를 접착하여 상호 보완적인 섬유시트를 얻을 수 있게 된다.According to the present invention by the above process it is possible to obtain a mutually complementary fiber sheet by adhering hemp fibers having good breathability and antibacterial properties and chemical fibers having a good contact feeling and durability.
상기한 과정에 의해 얻어진 본 발명의 제 1실시예에 따른 천연섬유와 화학섬유가 결합된 섬유시트는 신발의 안창이라든지 중창을 포함한 신발부재의 제조에 적절하게 적용가능함은 물론, 모자의 챙이나 벽지, 침구류에서 대표적인 침대매트리스커버나 베개커버, 건축용 바닥재를 포함하는 인테리어부속품, 공간구획을 위한 칸막이용 보드, 신발부재로서의 월형재(月形材), 실내 또는 야외에서 사용가능한 매트 또는 방석, 가방의 제작에 필요한 심재(芯材) 등의 제조에도 적절하게 적용될 수 있다. The fiber sheet in which the natural fiber and the chemical fiber are combined according to the first embodiment of the present invention obtained by the above process is suitably applicable to the manufacture of a shoe member including a shoe insole or a midsole, as well as a visor or a wallpaper of a hat. , Bed mattress cover or pillow cover, interior accessories including building flooring, partition board for space division, wall shape as shoe member, mat or cushion for indoor or outdoor use, bag It can be suitably applied to the manufacture of the core material (에) necessary for the production of.
도 4와 도 5a 및 도 5b는 본 발명의 바람직한 제 2실시예에 따른 천연섬유와 화학섬유가 결합된 섬유시트의 제조과정을 설명하기 위한 도면이고, 도 6은 본 발명의 제 2실시예에 따른 천연섬유와 화학섬유가 결합된 섬유시트를 설명하기 위한 도면이다.4 and 5a and 5b is a view for explaining the manufacturing process of the fiber sheet combined with natural fibers and chemical fibers in accordance with a second preferred embodiment of the present invention, Figure 6 is a second embodiment of the present invention Figure is for explaining a fiber sheet combined natural fibers and chemical fibers according to.
본 발명의 제 2실시예에 따른 천연섬유와 화학섬유가 결합된 섬유시트의 제조방법에 대해 도 7에 도시된 흐름도를 참조하여 상세하게 설명하면, 먼저 천연섬유권취롤(도시 생략)에 권취된 천연섬유로서의 마섬유층(10)상에 화학섬유(대표적으로 폴리에스테르섬유)층(바람직하게는 솜형태이지만, 화학섬유의 원사 또는 조각도 적용 가능)(30)을 공급하게 된다(단계 41).Referring to the flow chart shown in Figure 7 with respect to the manufacturing method of the fiber sheet combined with the natural fiber and the chemical fiber according to the second embodiment of the present invention, first wound on a natural fiber winding roll (not shown) A chemical fiber (typically polyester fiber) layer (preferably cotton, but also yarn or pieces of chemical fiber) 30 is supplied onto the hemp fiber layer 10 as natural fiber (step 41).
그리고나서, 상기 마섬유층(10)상에 공급된 화학섬유층(30)을 니들펀칭머신하면 그 니들펀칭머신의 니들(도 5b에서 "40a∼40n" 참조)이 상기 화학섬유층(30)을 상기 마섬유층(10)의 직조 조직내에 침입(도 5a의 30a)시킴으로써 도 6에 나타낸 상기 마섬유층(10)와 상기 화학섬유층(30)이 결합된 시트형상을 얻을 수 있게 된다(단계 42).Then, when the needle punching machine of the chemical fiber layer 30 supplied on the hemp fiber layer 10, the needle of the needle punching machine (see "40a to 40n" in Figure 5b) to the chemical fiber layer 30 By penetrating into the woven structure of the fibrous layer 10 (30a in FIG. 5A), a sheet shape in which the hemp fiber layer 10 and the chemical fiber layer 30 shown in FIG. 6 are combined can be obtained (step 42).
상기한 과정에 의해 상기 마섬유층(10)의 조직내에 상기 화학섬유층(30)이 일체로 결합된 섬유시트에 대해서는 상기한 제 1실시예에서와 유사하게 소정의 시트권취롤에 권취(단계 43)되고나서 그 섬유시트의 용도에 따라 일정한 길이와 폭을 갖는 시트재로 재단되어 별도의 시트재롤에 권취되고, 그 시트재롤에 권취된 시트재에 대해 후처리로서 함침조내에서 연질/경질화 바인더약품처리(단계 44) 및 압착프레스에 의한 압착(단계 45), 건조기에 의한 열풍건조(단계 46)가 실행된다.The fiber sheet in which the chemical fiber layer 30 is integrally bonded in the tissue of the hemp fiber layer 10 by the above process is wound on a predetermined sheet winding roll similarly to the first embodiment (step 43). After the sheet is cut into sheet material having a certain length and width according to the use of the fiber sheet, it is wound on a separate sheet roll, and the soft / hardened binder chemical in the impregnation tank as a post-treatment for the sheet member wound on the sheet roll. The processing (step 44), the pressing by the pressing press (step 45), and the hot air drying by the dryer (step 46) are performed.
여기서, 상기 단계 44에서의 바인더약품처리과정에서는 그 약품처리를 위한 예컨대 아크릴계 바인더에 경화제라든지 섬유유연제, 발수제, 정전기방지제, 항균제/살균제, 방향제 등이 선택적으로 첨가되는 일도 상정된다.Here, in the binder chemical treatment process in step 44, it is also assumed that a curing agent, a fabric softener, a water repellent, an antistatic agent, an antimicrobial agent / disinfectant, a fragrance, or the like is selectively added to, for example, the acrylic binder for the chemical treatment.
또, 그 건조된 섬유시트는 단계 47에서 프레스로울러에 의해 양면에 대한 평탄화작업이 이루어지고나서 단계 48에서 필요한 문양의 인쇄 및 필요한 형상(예컨대 단위 롤 또는 시트)으로의 재단이 이루어지고나서 상품으로 포장되어 출하된다.In addition, the dried fiber sheet is flattened on both sides by a press roller in step 47, and then, in step 48, printing of the required pattern and cutting into the required shape (for example, a unit roll or sheet) are performed. Packed and shipped.
상기한 과정에 의해 제조된 제 2실시예에 따른 섬유시트는 상기한 제 1실시예에 따른 섬유시트와 동일하게 양호한 통기성과 항균성을 갖는 마섬유의 특성과 양호한 접촉감과 내구성을 갖는 화학섬유의 특성을 갖는 섬유시트를 얻을 수 있게 되고, 그 섬유시트는 신발안창(도 8 참조)을 포함하는 신발부재라든지 모자의 챙이나 벽지, 침구류에서 대표적인 침대매트리스커버나 베개커버, 건축용 바닥재나 인테리어부속품, 공간구획을 위한 칸막이용 보드, 신발부재로서의 월형재, 실내 또는 야외에서 사용가능한 매트 또는 방석, 가방의 제작에 필요한 심재 등의 제조에 적용가능하게 된다. The fiber sheet according to the second embodiment prepared by the above process is the same as the fiber sheet according to the first embodiment described above, the characteristics of hemp fibers having good breathability and antibacterial properties, and the properties of chemical fibers having good contact feeling and durability. It is possible to obtain a fiber sheet having a fiber sheet, such as a shoe member including a shoe insole (see FIG. 8), a visor or wallpaper of a hat, a bed mattress cover or a pillow cover in beddings, building flooring or interior accessories, It is possible to apply to the production of a partition board for space partition, a wall shape member as a shoe member, a mat or a cushion that can be used indoors or outdoors, and a core material necessary for manufacturing a bag.
한편, 본 발명은 상기한 실시예로 한정되지는 않고 발명의 기술적 요지 및 요점을 이탈하지 않는 범위내에서 다양한 변경 및 변형실시가 가능함은 물론으로, 상기 제 1 및 제 2실시예에서 마섬유에 화학섬유층이 결합된 시트형상이 시트권취롤에 권취되고나면 그 용도에 따라 일정한 길와 폭을 갖는 시트재로 재단이 먼저 실행되고나서 약품처리가 후속되는 순서로 설명되어 있지만, 시트권취롤에 권취된 시트형상에 대해 약품처리와 압착/건조/평탄화처리가 실행되고나서 그 섬유시트의 용도에 따라 시트재로서 재단이 이루어지도록 해도 된다.On the other hand, the present invention is not limited to the above embodiments, and various changes and modifications can be made within the scope not departing from the technical gist and gist of the invention, as well as to the hemp fiber in the first and second embodiments After the sheet shape combined with the chemical fiber layer is wound on the sheet winding roll, the cutting is first performed with the sheet material having a certain length and width depending on the purpose, and then the chemical treatment is followed in the order followed by the chemical treatment. After the chemical treatment and the compression / drying / flattening treatment are performed on the sheet shape, the sheet may be cut as a sheet material according to the use of the fiber sheet.
또, 상기한 제 1 및 제 2실시예에서는 마섬유의 일측면에 화학섬유층이 결합된 구조가 설명되었지만, 본 발명은 그러한 예로 한정되지는 않고 마섬유의 일측면에 화학섬유층이 결합되고나서 그 마섬유의 타측면에 대해서도 동일한 과정에 의해 화학섬유층이 결합되도록 해도 된다.In addition, in the above-described first and second embodiments, the structure in which the chemical fiber layer is bonded to one side of the hemp fiber has been described, but the present invention is not limited thereto, and the chemical fiber layer is bonded to one side of the hemp fiber. The chemical fiber layer may be bonded to the other side of the hemp fiber by the same process.
또, 상기한 설명에서는 천연섬유로서의 마섬유에 화학섬유층이 결합되는 방식이 설명되었지만, 본 발명은 그러한 예로도 한정되지는 않고 화학섬유에 천연섬유층(특히 마섬유층)을 공급하여 그 화학섬유의 조직내에 천연섬유층이 일체로 결합되도록 해도 된다.In addition, in the above description, the manner in which the chemical fiber layer is bonded to the hemp fiber as the natural fiber has been described. The natural fiber layer may be integrally combined in the film.
상기한 바와 같이, 본 발명에 따른 천연섬유층과 화학섬유층이 결합된 섬유시트와 그 제조방법에 의하면 양호한 통기성과 항균/탈취 작용을 갖는 천연섬유로서의 마섬유와 부드러운 접촉감과 내구성이 양호한 화학섬유(폴리에스테르섬유)를 결합함으로써 마섬유의 특유한 통기성과 탈취/항균성과 화학섬유의 특유한 부드러운 접촉감과 내구성을 갖는 섬유시트를 얻을 수 있게 된다.As described above, according to the present invention, a fiber sheet in which a natural fiber layer and a chemical fiber layer are combined, and a method of manufacturing the same, a hemp fiber as a natural fiber having good breathability and antibacterial / deodorizing effect, and a soft contact feeling and good chemical fiber (poly Ester fiber), it is possible to obtain a fiber sheet having the unique breathability and deodorization / antibacterial properties of the hemp fiber and the soft contact and durability of the chemical fiber.
도 1은 본 발명의 바람직한 제 1실시예에 따른 천연섬유와 화학섬유가 결합된 섬유시트의 제조과정을 설명하기 위한 도면,1 is a view for explaining a manufacturing process of a fiber sheet combined with natural fibers and chemical fibers according to a first embodiment of the present invention,
도 2는 도 1에 설명된 본 발명에 따른 천연섬유와 화학섬유가 결합된 섬유시트를 나타낸 도면,2 is a view showing a fiber sheet combined with natural fibers and chemical fibers according to the present invention described in FIG.
도 3은 본 발명의 제 1실시예에 따른 천연섬유와 인조섬유가 결합된 섬유시트의 제조방법을 설명하기 위한 흐름도,3 is a flowchart illustrating a method of manufacturing a fiber sheet in which natural fibers and artificial fibers are combined according to a first embodiment of the present invention;
도 4와 도 5a 및 도 5b는 본 발명의 바람직한 제 2실시예에 따른 천연섬유와 화학섬유가 결합된 섬유시트의 제조과정을 설명하기 위한 도면,4 and 5a and 5b is a view for explaining the manufacturing process of the fiber sheet combined with natural fibers and chemical fibers according to a second embodiment of the present invention,
도 6은 본 발명의 제 2실시예에 따른 천연섬유와 화학섬유가 결합된 섬유시트를 나타낸 도면,6 is a view showing a fiber sheet combined with natural fibers and chemical fibers according to a second embodiment of the present invention,
도 7은 본 발명의 제 2실시예에 따른 천연섬유와 화학섬유가 결합된 섬유시트의 제조방법을 설명하기 위한 흐름도,7 is a flowchart illustrating a method of manufacturing a fiber sheet in which natural fibers and chemical fibers are combined according to a second embodiment of the present invention;
도 8은 본 발명에 따른 천연섬유와 화학섬유가 결합된 섬유시트가 신발부재의 제조에 적용된 예를 설명하기 위한 도면이다. 8 is a view for explaining an example in which the natural and chemical fiber fiber sheet combined according to the present invention is applied to the production of a shoe member.
*도면의 주요부분에 대한 부호의 설명** Description of the symbols for the main parts of the drawings *
10: 천연섬유층(마섬유층), 20,30: 화학섬유층(폴리에스테르섬유),10: natural fiber layer (hemp fiber layer), 20, 30: chemical fiber layer (polyester fiber),
40a∼40n: 니들펀칭머신의 니들. 40a-40n: Needle of a needle punching machine.
Claims (7)