KR200460762Y1 - Stabilization appalatus for manufacturing carbon fiber - Google Patents

Stabilization appalatus for manufacturing carbon fiber Download PDF

Info

Publication number
KR200460762Y1
KR200460762Y1 KR20090012195U KR20090012195U KR200460762Y1 KR 200460762 Y1 KR200460762 Y1 KR 200460762Y1 KR 20090012195 U KR20090012195 U KR 20090012195U KR 20090012195 U KR20090012195 U KR 20090012195U KR 200460762 Y1 KR200460762 Y1 KR 200460762Y1
Authority
KR
South Korea
Prior art keywords
air
carbon fiber
stabilization
stabilization furnace
furnace
Prior art date
Application number
KR20090012195U
Other languages
Korean (ko)
Other versions
KR20110002937U (en
Inventor
오동희
Original Assignee
오동희
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 오동희 filed Critical 오동희
Priority to KR20090012195U priority Critical patent/KR200460762Y1/en
Publication of KR20110002937U publication Critical patent/KR20110002937U/en
Application granted granted Critical
Publication of KR200460762Y1 publication Critical patent/KR200460762Y1/en

Abstract

본 고안은 안정화로에 연결되어 가열된 공기를 공급하는 분기관부를 4개소로 분기 연결되고, 분기된 분기관부 내에는 각각 가열된 공기의 공급량을 제어할 수 있도록 댐퍼가 설치되며, 안정화로의 하단 측에는 공급된 공기의 흐름을 제어할 수 있도록 에어가이드가 구비되어, 산화처리에 필요한 공기를 일정하고 균등하게 공급할 수 있어 탄소섬유 전구체 유기섬유의 형태안정성을 향상시킴으로써 제품의 불량률을 감소시킬 수 있도록 한 탄소섬유 제조용 안정화장치에 관한 것이다.The present invention is branched into four branch pipes connected to the stabilization furnace to supply heated air, and dampers are installed in the branched branch pipes so as to control the supply amount of the heated air, respectively. The air guide is provided on the side to control the flow of the supplied air, and it is possible to uniformly and equally supply the air necessary for the oxidation treatment, thereby reducing the defect rate of the product by improving the shape stability of the carbon fiber precursor organic fiber. It relates to a stabilizer for producing carbon fiber.

본 고안의 바람직한 일 실시예에 따른 탄소섬유 제조용 안정화장치는 안정화로 내에 가열된 공기를 공급해 탄소섬유 전구체 유기섬유의 표면을 산화처리시키는 탄소섬유 제조용 안정화장치에 있어서, 내부에는 탄소섬유 전구체 유기섬유를 이송시키는 컨베이어벨트가 설치되고 하부에는 가열된 공기가 공급되는 유입구가 설치되며 상부에는 산화처리에 사용된 공기가 배출되는 배출구가 설치되는 안정화로와, 상기 배출구와 연결되며 산화처리에 사용된 공기가 이동되는 이동관과, 상기 이동관 상에 설치되며 상기 이동관 내에서 이동되는 공기를 산화반응 가능하도록 처리하는 열풍생성부와, 일단은 상기 이동관에 연결되고 타단은 상기 유입구에 연결되어 재처리된 공기를 탄소섬유 전구체 유기섬유가 위치된 상기 안정화로 내에 공급하는 분기관부와, 상기 분기관부 내에 설치되며 상기 안정화로 내에 공급되는 공기의 양을 제어하는 댐퍼와, 상기 유입구 측에 설치되며 상기 안정화로 내에 공급되는 공기의 흐름을 제어하는 에어가이드부를 포함하는 것을 특징으로 한다.In the stabilizing device for producing carbon fiber according to an embodiment of the present invention is a stabilizing device for producing carbon fiber to oxidize the surface of the carbon fiber precursor organic fiber by supplying heated air in the stabilization furnace, inside the carbon fiber precursor organic fiber Conveyor belt for transporting is installed, the inlet is installed in the lower part is supplied with heated air, the upper part of the stabilization furnace is installed with an outlet for discharging the air used for oxidation treatment, the air connected to the outlet and used for oxidation treatment A moving wind pipe that is moved, installed on the moving pipe, and a hot air generating unit configured to oxidize the air that is moved in the moving pipe; Branch pipes supplied into the stabilization furnace in which fiber precursor organic fibers are located And a damper installed in the branch pipe part to control an amount of air supplied into the stabilization furnace, and an air guide part installed on the inlet side and controlling a flow of air supplied into the stabilization furnace. .

탄소섬유, 산화, 안정화로, 이동관, 열풍생성부, 분기관부, 댐퍼, 에어가이드부 Carbon fiber, oxidation, stabilization furnace, moving pipe, hot air generating part, branch pipe part, damper, air guide part

Description

탄소섬유 제조용 안정화장치{STABILIZATION APPALATUS FOR MANUFACTURING CARBON FIBER} Stabilizer for manufacturing carbon fiber {STABILIZATION APPALATUS FOR MANUFACTURING CARBON FIBER}

본 고안은 탄소섬유 제조용 안정화장치에 관한 것으로 더욱 상세하게는 안정화로에 연결되어 가열된 공기를 공급하는 분기관부를 4개소로 분기 연결되고, 분기된 분기관부 내에는 각각 가열된 공기의 공급량을 제어할 수 있도록 댐퍼가 설치되며, 안정화로의 하단 측에는 공급된 공기의 흐름을 제어할 수 있도록 에어가이드가 구비되어, 산화처리에 필요한 공기를 일정하고 균등하게 공급할 수 있어 탄소섬유 전구체 유기섬유의 형태안정성을 향상시킴으로써 제품의 불량률을 감소시킬 수 있도록 한 탄소섬유 제조용 안정화장치에 관한 것이다.The present invention relates to a stabilization device for producing carbon fibers, and more particularly, branched to four branch pipes connected to the stabilization furnace to supply heated air, and controls the amount of supply of heated air in the branched branch pipes, respectively. A damper is installed so that the damper can be provided, and an air guide is provided at the lower side of the stabilization furnace to control the flow of the supplied air, and thus it is possible to uniformly and uniformly supply the air necessary for the oxidation treatment, thereby maintaining the shape stability of the organic fiber of the carbon fiber precursor. The present invention relates to a stabilizer for producing carbon fiber, which can reduce the defective rate of the product by improving the efficiency.

일반적인 탄소섬유의 제조방법은 탄소섬유 전구체인 폴리아크릴로 나이트릴 (polyacrylonitrile), 피치(pitch, 등방성 또는 이방성), 페놀(phenol)-수지 등을 열용융시켜 용융방사(melt spinning) 하거나 용매에 용해시켜 용액방사(solution spinning, dry, wet, dry/wet spinning)하여 탄소섬유 전구체 유기섬유를 얻는다.Common methods for producing carbon fibers are melt spinning or melting in a solvent by thermal melting of polyacrylonitrile, pitch (isotropic or anisotropic), phenol-resin, and the like, which are carbon fiber precursors. Solution spinning (solution spinning, dry, wet, dry / wet spinning) to obtain a carbon fiber precursor organic fiber.

이와 같은 방법으로 얻어진 섬유를 공기분위기하에서 열처리하면서 표면산화반응 시켜 섬유간 융착 내지는 열용융을 방지하여 진공 내지는 불활성 분위기에서 탄소화, 흑연화 또는 활성화하여 탄소섬유(흑연섬유 포함) 또는 활성탄소섬유를 얻는다.The fiber obtained by the above method is subjected to surface oxidation while heat-treating under an air atmosphere to prevent fusion or thermal melting between the fibers, and carbonization, graphitization or activation in a vacuum or inert atmosphere to form carbon fibers (including graphite fibers) or activated carbon fibers. Get

탄소섬유(흑연섬유)나 활성탄소섬유의 물성과 탄화수율은 출발 물질(전구물질)의 화학적 구조, 방사방법, 산화안정화, 탄소화, 활성화 공정 등의 각 조건에 의해서 크게 영향을 받는다. The physical properties and the carbonization yield of carbon fibers (graphite fibers) and activated carbon fibers are greatly influenced by each condition such as chemical structure of the starting material (precursor), spinning method, oxidation stabilization, carbonization, and activation process.

이 중에서 안정화공정은 열가소성 섬유를 열경화성 섬유로 변환시켜 후속하는 고온 탄소화(흑연화), 활성화 공정에서 섬유의 융착 및 열 용융을 방지하기 위해 섬유를 표면으로부터 산화 처리하는 과정으로, 안정화공정을 하지 않고 직접 탄소화 또는 활성화를 하게 되면 개환 및 탈수소 등의 발열반응이 급격히 진행되어 탄소화 되기보다는 연소가 되고 만다.Among these, the stabilization process is a process of converting thermoplastic fibers into thermosetting fibers to oxidize the fibers from the surface in order to prevent the high temperature carbonization (graphitization) and the fusion and thermal melting of the fibers in the activation process. If carbonization or activation is performed directly, exothermic reactions such as ring opening and dehydrogenation proceed rapidly and are burned rather than carbonized.

이러한 안정화공정은 가열된 공기를 안정화로 내에 순환 공급되면서 진행되는데, 종래기술에 따른 안정화장치의 경우 일정하고 균등한 공기의 제어가 제대로 이루어지지 않아 제품에 대한 형태안정성이 보장되지 못해 불량율이 증가되는 문제점이 있었다.This stabilization process is carried out while the heated air is circulated and supplied in the stabilization furnace, and in the case of the stabilization device according to the prior art, since the uniform and uniform air control is not properly performed, the shape stability of the product is not guaranteed and the defective rate is increased. There was a problem.

따라서 본 고안의 목적은 안정화로에 연결되어 가열된 공기를 공급하는 분기관부를 4개소로 분기 연결되고, 분기된 분기관부 내에는 각각 가열된 공기의 공급량을 제어할 수 있도록 댐퍼가 설치되며, 안정화로의 하단 측에는 공급된 공기의 흐름을 제어할 수 있도록 에어가이드가 구비되어, 산화처리에 필요한 공기를 일정하고 균등하게 공급할 수 있어 탄소섬유 전구체 유기섬유의 형태안정성을 향상시킴으로써 제품의 불량률을 감소시킬 수 있도록 한 탄소섬유 제조용 안정화장치를 제공하는 것이다.Therefore, an object of the present invention is branched to four branches connected to the stabilization furnace for supplying heated air, and the damper is installed in the branched branch pipe part to control the supply amount of the heated air, respectively, stabilization The air guide is provided at the bottom side of the furnace to control the flow of the supplied air, and it is possible to supply the air necessary for oxidation treatment uniformly and evenly, thereby reducing the defect rate of the product by improving the shape stability of the carbon fiber precursor organic fiber. It is to provide a stabilizer for the production of carbon fiber.

전술한 본 고안의 목적은 안정화로 내에 가열된 공기를 공급해 탄소섬유 전구체 유기섬유의 표면을 산화처리시키는 탄소섬유 제조용 안정화장치에 있어서, 내부에는 탄소섬유 전구체 유기섬유를 이송시키는 컨베이어벨트가 설치되고 하부에는 가열된 공기가 공급되는 유입구가 설치되며 상부에는 산화처리에 사용된 공기가 배출되는 배출구가 설치되는 안정화로와, 상기 배출구와 연결되며 산화처리에 사용된 공기가 이동되는 이동관과, 상기 이동관 상에 설치되며 상기 이동관 내에서 이동되는 공기를 산화반응 가능하도록 처리하는 열풍생성부와, 일단은 상기 이동관에 연결되고 타단은 상기 유입구에 연결되어 재처리된 공기를 탄소섬유 전구체 유기섬유가 위치된 상기 안정화로 내에 공급하는 분기관부와, 상기 분기관부 내에 설치되며 상기 안정화로 내에 공급되는 공기의 양을 제어하는 댐퍼와, 상기 유입구 측에 설치되며 상기 안정화로 내에 공급되는 공기의 흐름을 제어하는 에어가이드부를 포함하는 것을 특징으로 하는 탄소섬유 제조용 안정화장치를 제공함에 의해 달성된다.An object of the present invention described above is a stabilization apparatus for producing carbon fibers for supplying heated air in a stabilization furnace to oxidize the surface of the carbon fiber precursor organic fibers, wherein a conveyor belt for transporting the carbon fiber precursor organic fibers is installed inside It is provided with an inlet through which heated air is supplied, and a stabilization furnace in which an outlet for discharging air used for oxidation treatment is installed, a moving tube connected to the outlet for moving the air used for oxidation treatment, and in the moving tube. Is installed in the hot air generating unit for processing the oxidation of the air moved in the moving tube, one end is connected to the moving tube and the other end is connected to the inlet to the reprocessed air carbon fiber precursor organic fiber is located Branch pipe portion to be supplied in the stabilization furnace, and installed in the branch pipe portion It is achieved by providing a stabilizer for producing carbon fiber, characterized in that it comprises a damper for controlling the amount of air supplied into the furnace, and an air guide portion installed on the inlet side and controlling the flow of air supplied into the stabilization furnace. do.

본 고안의 바람직한 특징에 따르면 전술한 유입구는 상기 안정화로 일측 하부의 전,후방 2개소와, 타측 하부의 전,후방 2개소에 각각 구비되며, 상기 배출구는 상기 안정화로 상부 중앙측에 구비되는 것으로 한다.According to a preferred feature of the present invention, the inlet described above is provided at two front and rear portions at one side of the lower side of the stabilization furnace, and at two front and rear positions of the other lower portion, and the discharge port is provided at the upper center side of the stabilization furnace. do.

본 고안의 더 바람직한 특징에 따르면 전술한 열풍생성부는, 상기 배출구 측에 위치되며 산화처리에 사용된 공기를 가열하는 히터와, 상기 히터 후방에 위치되며 가열된 공기를 필터링하는 필터와, 상기 필터의 후방에 위치되며 필터링된 공기를 상기 안정화로 측으로 강제순환시키는 송풍기를 포함하는 것으로 한다.According to a more preferable feature of the present invention, the above-described hot air generating unit, a heater located on the outlet side and heating the air used for the oxidation treatment, a filter located behind the heater and filters the heated air, And a blower positioned rearward and forcibly circulating the filtered air to the stabilization path.

본 고안의 더욱 바람직한 특징에 따르면 전술한 분기관부는 그 일단이 상기 이동관의 단부와 연결된 다음 4개소로 분기되며 분기된 분기관부는 상기 안정화로 일측 및 타측 하부의 전, 후방으로 각각 연장 형성된 다음 상기 유입구와 각각 연결되는 것으로 한다.According to a more preferable feature of the present invention, the branch pipe portion described above is branched into four places, one end of which is connected to the end of the moving tube, and the branched branch pipe portion is formed in the stabilization direction before and after the lower side of the other side, respectively. It is supposed to be connected to the inlet, respectively.

본 고안의 더욱 더 바람직한 특징에 따르면 전술한 에어가이드부는, 상기 분기관부와 인접된 측에 설치되어 유입되는 열풍의 좌우방향을 제어하는 제 1 가이드와, 상기 제 1 가이드의 후방에 위치되며 유입되는 열풍의 상하방향을 제어하는 제 2 가이드와, 상기 제 2 가이드의 후방에 위치되며 유입되는 열풍을 균등하게 구획하는 제 3 가이드를 포함하는 것으로 한다.According to an even more preferable feature of the present invention, the above-described air guide portion is installed on the side adjacent to the branch pipe portion, the first guide for controlling the left and right direction of the hot air flows in, and located behind the first guide And a second guide for controlling the vertical direction of the hot air, and a third guide positioned at the rear of the second guide and equally partitioning the incoming hot air.

본 고안의 바람직한 일 실시예에 따른 탄소섬유 제조용 안정화장치에 따르면 안정화로에 연결되어 가열된 공기를 공급하는 분기관부를 4개소로 분기 연결되고, 분기된 분기관부 내에는 각각 가열된 공기의 공급량을 제어할 수 있도록 댐퍼가 설치되며, 안정화로의 하단 측에는 공급된 공기의 흐름을 제어할 수 있도록 에어가이드가 구비되어, 산화처리에 필요한 공기를 일정하고 균등하게 공급할 수 있어 탄소섬유 전구체 유기섬유의 형태안정성을 향상시킴으로써 제품의 불량률을 감소시킬 수 있는 탁월한 효과가 있다.According to the stabilization device for producing carbon fiber according to an embodiment of the present invention is connected to the branch pipe portion connected to the stabilization furnace to supply the heated air to four places, the branched branch pipe portion to supply the amount of air A damper is installed to control, and an air guide is provided at the lower side of the stabilization furnace to control the flow of the supplied air, and thus it is possible to uniformly and uniformly supply the air required for the oxidation treatment, thereby forming a carbon fiber precursor organic fiber. By improving stability, there is an excellent effect to reduce the defective rate of the product.

도 1에는 본 고안의 일 실시예에 따른 탄소섬유 제조용 안정화장치의 단면도가 도시되고, 도 2에는 본 고안의 일 실시예에 따른 탄소섬유 제조용 안정화장치의 평면도가 도시되며, 도 3에는 본 고안의 일 실시예에 따른 탄소섬유 제조용 안정화장치의 부분확대 단면도가 도시된다.Figure 1 is a cross-sectional view of a stabilizing device for producing carbon fiber according to an embodiment of the present invention, Figure 2 is a plan view of a stabilizing device for producing carbon fiber according to an embodiment of the present invention, Figure 3 A partially enlarged cross-sectional view of a stabilizing device for manufacturing carbon fiber according to one embodiment is shown.

본 고안의 바람직한 일 실시예에 따른 탄소섬유 제조용 안정화장치(1)는 안정화로(10) 내에 가열된 공기를 공급해 탄소섬유 전구체 유기섬유의 표면을 산화처리시키는 탄소섬유 제조용 안정화장치(1)에 있어서, 내부에는 탄소섬유 전구체 유 기섬유를 이송시키는 컨베이어벨트(16)가 설치되고 하부에는 가열된 공기가 공급되는 유입구(12)가 설치되며 상부에는 산화처리에 사용된 공기가 배출되는 배출구(14)가 설치되는 안정화로(10)와, 배출구(14)와 연결되며 산화처리에 사용된 공기가 이동되는 이동관(20)과, 이동관(20) 상에 설치되며 이동관(20) 내에서 이동되는 공기를 산화반응 가능하도록 처리하는 열풍생성부(30)와, 일단은 이동관(20)에 연결되고 타단은 유입구(12)에 연결되어 재처리된 공기를 탄소섬유 전구체 유기섬유가 위치된 안정화로(10) 내에 공급하는 분기관부(40)와, 분기관부(40) 내에 설치되며 상기 안정화로(10) 내에 공급되는 공기의 양을 제어하는 댐퍼(50)와, 유입구(12) 측에 설치되며 안정화로(10) 내에 공급되는 공기의 흐름을 제어하는 에어가이드부(60)를 포함한다.In the stabilization device (1) for producing carbon fiber according to a preferred embodiment of the present invention in the stabilization device (1) for producing carbon fiber by supplying heated air in the stabilization furnace (10) to oxidize the surface of the carbon fiber precursor organic fiber The inside of the conveyor belt 16 for transporting the carbon fiber precursor organic fibers is installed, the inlet 12 is provided with a heated air is provided in the lower portion, the outlet 14 for exhausting the air used for oxidation treatment in the upper portion It is connected to the stabilization furnace 10 is installed, the discharge port 14, the moving pipe 20 is used to move the air used in the oxidation treatment, and the moving pipe 20 is installed on the moving pipe 20 The hot air generating unit 30 to process the oxidation reaction, and one end is connected to the moving tube 20 and the other end is connected to the inlet 12, the stabilization furnace 10 where the carbon fiber precursor organic fiber is located Supply within It is installed in the branch pipe portion 40, the branch pipe portion 40 and the damper 50 for controlling the amount of air supplied in the stabilization path 10, and is installed on the inlet 12 side stabilization furnace 10 It includes an air guide unit 60 for controlling the flow of air supplied therein.

여기서 안정화로(10)는 그 내부에 탄소섬유 전구체 유기섬유가 위치되며 공급되는 공기를 통해 이를 산화처리하는 역할을 하는 것으로, 내부에는 탄소섬유 전구체 유기섬유를 이송시키는 컨베이어벨트(16)가 작동가능하게 설치되고 하부에는 가열된 공기가 공급되는 유입구(12)가 설치되며 상부에는 산화처리에 사용된 공기가 배출되는 배출구(14)가 설치된다.Here, the stabilization furnace 10 is located in the carbon fiber precursor organic fiber is located therein and serves to oxidize it through the air supplied, the conveyor belt 16 for transporting the carbon fiber precursor organic fiber inside is operable. The inlet 12 is installed in the lower portion and the heated air is supplied at the lower portion thereof, and the outlet 14 at which the air used for the oxidation treatment is discharged is installed at the upper portion thereof.

전술한 컨베이어벨트(16)는 종래기술에 따른 컨베이어벨트(16)와 동일한 것이며 바람직하게는 컨베이어벨트(16)의 직하부에 스키드레일(18)이 구비되도록 하여 컨베이어벨트(16)가 하부로 쳐지는 것을 방지한다.The conveyor belt 16 described above is the same as the conveyor belt 16 according to the related art. Preferably, the conveyor belt 16 is bent downward so that the skid rail 18 is provided directly under the conveyor belt 16. To prevent it.

또한 전술한 유입구(12)는 안정화로(10) 일측 하부의 전,후방 2개소와, 타측 하부의 전,후방 2개소에 각각 구비되는데, 이 유입구(12)는 추후에 설명될 분기관 부(40)와 연결되어 가열된 공기가 유입되도록 하는 역할을 하는 것이다.In addition, the inlet 12 described above is provided at two front and rear portions at one lower side of the stabilization furnace 10 and at two front and rear portions of the other lower portion, and the inlet 12 is a branch pipe part (to be described later) ( It is connected to 40 and serves to let the heated air flow in.

이러한 유입구(12)는 가열된 공기가 컨베이어벨트(16) 상에 위치된 탄소섬유 전구체 유기섬유를 산화시킬 수 있도록 전술한 스키드레일(18) 하부까지 연통 형성되어 관로를 형성되는 것으로 한다.The inlet 12 is configured to communicate with the above-described skid rail 18 to form a conduit so that heated air can oxidize the carbon fiber precursor organic fiber located on the conveyor belt 16.

또한 전술한 배출구(14)는 안정화로(10)의 상부 중앙측에 구비되는데, 이 배출구(14)는 산화처리에 사용된 공기가 배출되도록 하는 역할을 하는 것으로 추후에 설명될 이동관(20)과 연결되게 된다.In addition, the above-described outlet 14 is provided at the upper center side of the stabilization furnace 10, the outlet 14 serves to discharge the air used in the oxidation treatment and the moving tube 20 to be described later Will be connected.

이와 같은 본 고안의 일 실시예에 따른 안정화로(10)의 나머지 구성부재와 그 작동관계 및 제어방법은 종래기술에 따른 안정화로(10)와 동일한 것으로 하여 더 이상의 상세한 설명은 명세서의 간략화를 위해 생략하기로 한다.As such, the remaining components of the stabilization furnace 10 according to an embodiment of the present invention and its operating relationship and control method are the same as those of the stabilization furnace 10 according to the prior art, and thus, more detailed description will be made for the purpose of simplicity of the specification. It will be omitted.

한편, 전술한 배출구(14)에는 이동관(20)이 연결되는데 이 이동관(20)은 산화처리에 사용된 공기를 재처리하기 위해 이동시키는 역할을 하는 것이다.On the other hand, the above-described discharge port 14 is connected to the moving tube 20, the moving tube 20 is to move to reprocess the air used in the oxidation treatment.

이러한 이동관(20)의 일단은 배출구(14)와 연결되고 그 타단은 추후에 설명될 분기관부(40)와 연결되어 안정화로(10)에서 배출되는 공기를 분기관부(40)까지 이동시키게 된다. 또한 이동관(20) 상에는 추후에 설명될 열풍생성부(30)가 설치되어 이동관(20)을 통해 이동되는 공기를 재처리 하게 된다.One end of the moving tube 20 is connected to the outlet 14 and the other end thereof is connected to the branch pipe part 40 to be described later to move the air discharged from the stabilization path 10 to the branch pipe part 40. In addition, the hot air generating unit 30, which will be described later, is installed on the moving tube 20 to reprocess the air moving through the moving tube 20.

한편, 전술한 이동관(20) 상에는 열풍생성부(30)가 설치되는데 이 열풍생성부(30)는 이동관(20) 내에서 이동되는 공기를 산화처리 가능하도록 가열, 필터링 및 순환시키는 역할을 하는 것이다.On the other hand, the hot air generating unit 30 is installed on the above-described moving tube 20, the hot air generating unit 30 serves to heat, filter and circulate the air to be oxidized in the moving tube 20. .

이러한 열풍생성부(30)는, 배출구(14) 측에 위치되며 산화처리에 사용된 공기를 재가열하는 히터(32)와, 히터(32)의 후방에 위치되며 전방에서 가열된 공기를 필터링하는 필터(34)와, 필터(34)의 후방에 위치되며 전방에서 필터링된 공기를 분기관부(40)를 통해 안정화로(10) 측으로 강제순환시키는 송풍기(36)를 포함한다.The hot air generating unit 30 is located on the outlet 14 side, the heater 32 for reheating the air used for the oxidation treatment, and the filter located in the rear of the heater 32 to filter the heated air from the front 34 and a blower 36 positioned behind the filter 34 and forcibly circulating the air filtered from the front to the stabilization path 10 through the branch pipe 40.

이러한 히터(32), 필터(34) 및 송풍기(36)는 전술한 안정화로(10)와 마찬가지로 종래기술에 따른 안정화로(10)에 장착되는 히터(32), 필터(34) 및 송풍기(36)와 동일한 것으로 하여 더 이상의 상세한 설명은 명세사의 간략화를 위해 생략하기로 한다.The heater 32, the filter 34, and the blower 36 are the heater 32, the filter 34, and the blower 36 mounted in the stabilization furnace 10 according to the related art, similar to the stabilization furnace 10 described above. In this case, further description will be omitted for the sake of simplicity of specification.

한편, 재처리된 공기가 이동되는 이동관(20)의 단부에는 분기관부(40)가 연결되는데, 이 분기관부(40)는 산화처리 가능하도록 재처리된 공기를 탄소섬유 전구체 유기섬유가 위치된 안정화로(10)의 하부측으로 분기하여 공급하는 역할을 하는 것이다.On the other hand, the branch pipe portion 40 is connected to the end of the moving tube 20 to which the reprocessed air is moved, the branch pipe portion 40 is the stabilization of the reprocessed air carbon fiber precursor organic fiber is located to be oxidized It serves to branch and supply to the lower side of the furnace (10).

이러한 분기관부(40)는 그 일단이 이동관(20)의 단부와 연결된 다음 제 1 분기관(42), 제 2 분기관(44), 제 3 분기관(46) 및 제 4 분기관(48)와 같이 4개소로 분기되며 분기된 분기관부(40)는 안정화로(10) 일측 및 타측 하부의 전, 후방으로 각각 연장 형성된 다음 전술한 유입구(12)와 각각 연결된다.The branch pipe portion 40 has one end connected to the end of the moving pipe 20, and then the first branch pipe 42, the second branch pipe 44, the third branch pipe 46, and the fourth branch pipe 48. Branching branch portion 40 is branched into four places as described above is formed to extend to the front and rear of one side and the other lower portion of the stabilization path 10 and then connected to the inlet 12 described above, respectively.

즉, 이동관(20)이 바로 안정화로(10)와 직결되는 것이 아니라 4개소로 분기된 분기관부(40)를 거쳐 안정화로(10)의 하부 4개소에 각각 연결되어 재처리된 공기를 공급해 줌으로써 균등한 공기의 공급이가능해 일측 방향으로 치우지지 않는 산화처리가 가능하게 된다.That is, the moving pipe 20 is not directly connected to the stabilization path 10, but is connected to each of the four lower portions of the stabilization path 10 through four branch pipe parts 40 branched to supply reprocessed air. It is possible to supply the air evenly, so that the oxidation treatment can be carried out in one direction.

이러한 분기관부(40)는 본 고안의 일 실시예에서와 같이 4개소로 분기될 수도 있으나 안정화로(10)의 크기와 산화되는 탄소섬유 전구체 유기섬유의 양에 따라서 6개소, 8개소 등으로 다양하게 분기되어 사용될 수 있음은 물론이다.The branch pipe portion 40 may be branched into four places as in one embodiment of the present invention, but varies in six places, eight places, etc., depending on the size of the stabilization furnace 10 and the amount of carbon fiber precursor organic fiber to be oxidized. Of course, it can be used to branch.

또한 전술한 분기관부(40)에는 댐퍼(50)가 구비되는데, 이 댐퍼(50)는 안정화로(10) 내부에 공급되는 공기의 양을 제어하는 역할을 하는 것으로 4개소로 분기된 분기관부(40)마다 각각 설치되는 것으로 한다.In addition, the above-described branch pipe part 40 is provided with a damper 50. The damper 50 serves to control the amount of air supplied into the stabilization path 10. The branch pipe part branched into four places ( It shall be installed in every 40).

이러한 댐퍼(50)는 전술한 안정화로(10) 및 열풍생성부(30)와 마찬가지로 굴뚝?노(爐)?덕트(duct) 등에 설치되어 공기 또는 가스의 양을 가감하는데 사용되는 종래기술에 따른 댐퍼(50)와 동일한 것으로 하여 더 이상의 상세한 설명은 명세사의 간략화를 위해 생략하기로 한다.The damper 50 is installed in a chimney, a furnace, a duct, and the like, as in the stabilization furnace 10 and the hot air generating unit 30, according to the related art. The same detailed description as that of the damper 50 will be omitted for the sake of simplicity.

전술한 유입구(12)의 내측에는 에어가이드부(60)가 설치되는데 이 에어가이드부(60)는 안정화로(10) 내에 공급된 공기의 흐름을 제어하여 컨베이어벨트(16) 상에 위치된 탄소섬유 전구체 유기섬유를 향해 균등하고 안정적으로 공급되도록 하는 역할을 하는 것이다.An air guide part 60 is installed inside the inlet 12 described above, and the air guide part 60 controls the flow of air supplied into the stabilization path 10 so that the carbon placed on the conveyor belt 16 is provided. The fiber precursor serves to supply uniformly and stably toward the organic fiber.

이러한 에어가이드부(60)는, 분기관부(40)와 인접된 측에 설치되어 유입되는 열풍의 좌우방향을 제어하는 제 1 가이드(62)와, 제 1 가이드(62)의 후방에 위치되며 유입되는 열풍의 상하방향을 제어하는 제 2 가이드(64)와, 제 2 가이드(64)의 후방에 위치되며 유입되는 열풍을 균등하게 구획하는 제 3 가이드(66)를 포함한다.The air guide part 60 is installed at a side adjacent to the branch pipe part 40 and is positioned at the rear of the first guide 62 and the first guide 62 to control the left and right directions of the hot air flowing therein. It includes a second guide 64 for controlling the vertical direction of the hot air to be, and a third guide 66 which is located behind the second guide 64 and evenly divides the incoming hot air.

즉, 분기관부(40)를 지나 유입구(12)측으로 유입된 공기는 제 1 가이드(62) 의 회동각에 따라 좌, 우 방향으로의 공급량이 결정되며, 제 2 가이드(64)의 회동각에 따라 상, 하방향으로의 공급량이 결정된 다음, 안정화로(10) 하측 내부를 구획하는 제 3 가이드(66)를 통해 공급량의 변화없이 일정하게 안정화로(10) 내부까지 이동된다.That is, the air flowing through the branch pipe portion 40 toward the inlet 12 is determined in the left and right directions according to the rotation angle of the first guide 62, and is applied to the rotation angle of the second guide 64. Accordingly, the supply amount in the up and down directions is determined, and then uniformly moved to the inside of the stabilization furnace 10 without changing the supply amount through the third guide 66 partitioning the lower inside of the stabilization furnace 10.

전술한 제 1 가이드(62) 및 제 2 가이드(64)는 전 공정을 마무리 해 제조가 완료된 탄소섬유 제품의 불량률을 면밀하게 분석한 다음 그 완성도에 따라 회동각을 조절해 줌으로써 완벽한 산화가 진행될 수 있도록 제어해 준다.The above-described first guide 62 and second guide 64 finishes the entire process to closely analyze the defective rate of the finished carbon fiber product, and then adjust the angle of rotation according to the degree of completeness to allow perfect oxidation. To control it.

이하에는 본 고안의 바람직한 일 실시예에 따른 탄소섬유 제조용 안정화장치(1)의 전체적인 작동관계에 대해 설명하면 다음과 같다.Hereinafter will be described the overall operating relationship of the stabilizer for producing carbon fiber 1 according to an embodiment of the present invention.

전 단계에서의 처리가 마무리된 탄소섬유 전구체 유기섬유가 컨베이어벨트(16)를 통해 안정화로(10) 내에 도달되면 히터(32) 및 송풍기(36)의 작동이 시작되면서 내부 공기의 강제 순환이 시작된다.When the carbon fiber precursor organic fiber finished in the previous step is reached in the stabilization furnace 10 through the conveyor belt 16, the operation of the heater 32 and the blower 36 is started and the forced circulation of the internal air starts. do.

먼저 히터(32)를 통해 목표온도까지 공기가 가열되면 가열된 공기가 필터(34)를 통과하면서 필터링 되면 송풍기(36)에 의해 이동관(20) 및 분기관부(40)를 이동하며서 강제 순환되게 된다.First, when the air is heated to the target temperature through the heater 32, the heated air is filtered while passing through the filter 34, and is forcedly circulated by moving the moving pipe 20 and the branch pipe part 40 by the blower 36. .

분기관부(40) 내부에는 댐퍼(50)가 구비되어 있어 이에 의해 공급되는 공기의 양이 제어되고, 댐퍼(50)를 지나 유입구(12)에 다다른 공기는 제 1 가이드(62) 및 제 2 가이드(64)에 의해 그 공급방향이 결졍되고 제 3 가이드(66)에 의해 변화없이 일정하게 안정화로(10) 내부로 공급된다.A damper 50 is provided in the branch pipe part 40 so that the amount of air supplied thereto is controlled, and the air reaching the inlet 12 through the damper 50 passes through the first guide 62 and the second. The supply direction is determined by the guide 64 and is constantly supplied into the stabilization furnace 10 without change by the third guide 66.

안정화로(10) 내부에 공급된 가열된 공기는 탄소섬유 전구체 유기섬유를 산화시켜 형태안정성을 부여함으로써 불량률을 현저하게 저하시킬 수 있게 되며, 산화처리에 사용된 공기는 다시 배출구(14)를 통해 배출되어 동일한 공정을 반복하게 된다.The heated air supplied inside the stabilization furnace 10 can oxidize the carbon fiber precursor organic fiber to impart morphological stability, thereby significantly reducing the defect rate, and the air used for the oxidation treatment is again discharged through the outlet 14. It is discharged and the same process is repeated.

본 고안은 실용신안등록청구범위에서 청구하는 청구의 요지를 벗어나지 않고도 당해 기술분야에서 통상의 지식을 가진 자에 의하여 다양하게 변경 실시될 수 있으므로, 본 고안의 기술보호범위는 상술한 특정의 바람직한 실시예에 한정되지 않는다.The present invention can be variously modified by those skilled in the art without departing from the scope of the claims claimed in the utility model registration claims, the technical protection scope of the present invention is the specific preferred embodiment described above It is not limited to the example.

도 1은 본 고안의 일 실시예에 따른 탄소섬유 제조용 안정화장치의 단면도.1 is a cross-sectional view of the stabilizing device for producing carbon fiber according to an embodiment of the present invention.

도 2는 본 고안의 일 실시예에 따른 탄소섬유 제조용 안정화장치의 평면도.Figure 2 is a plan view of a stabilizing device for producing carbon fiber according to an embodiment of the present invention.

도 3은 본 고안의 일 실시예에 따른 탄소섬유 제조용 안정화장치의 부분확대 단면도.Figure 3 is a partially enlarged cross-sectional view of the stabilizing device for producing carbon fiber according to an embodiment of the present invention.

*도면의 주요부분에 대한 부호의 설명** Description of the symbols for the main parts of the drawings *

1 : 탄소섬유 제조용 안정화장치 10 : 안정화로1: Stabilizer for manufacturing carbon fiber 10: Stabilization furnace

12 : 유입구 14 : 배출구12: inlet 14: outlet

16 : 컨베이어벨트 18 : 스키드레일16: conveyor belt 18: ski rail

20 : 이동관 30 : 열풍생성부20: moving tube 30: hot air generating unit

32 : 히터 34 : 필터32: heater 34: filter

36 : 송풍기 40 : 분기관부36: blower 40: branch pipe

42 : 제 1 분기관 44 : 제 2 분기관42: first branch pipe 44: second branch pipe

46 : 제 3 분기관 48 : 제 4 분기관46: third branch pipe 48: fourth branch pipe

50 : 댐퍼 60 : 에어가이드부50: damper 60: air guide portion

62 : 제 1 가이드 64 : 제 2 가이드62: first guide 64: second guide

66 : 제 3 가이드66: The Third Guide

Claims (5)

안정화로 내에 가열된 공기를 공급해 탄소섬유 전구체 유기섬유의 표면을 산화처리시키는 탄소섬유 제조용 안정화장치에 있어서,In the stabilization apparatus for producing carbon fibers to supply air heated in the stabilization furnace to oxidize the surface of the carbon fiber precursor organic fibers, 내부에는 탄소섬유 전구체 유기섬유를 이송시키는 컨베이어벨트가 설치되고 하부에는 가열된 공기가 공급되는 유입구가 설치되며 상부에는 산화처리에 사용된 공기가 배출되는 배출구가 설치되는 안정화로;A stabilization furnace in which a conveyor belt for transferring the carbon fiber precursor organic fibers is installed, and an inlet for supplying heated air is installed in the lower part, and an outlet for discharging air used for oxidation treatment is installed in the upper part; 상기 배출구와 연결되며 산화처리에 사용된 공기가 이동되는 이동관;A moving tube connected to the outlet and moving air used for oxidation treatment; 상기 이동관 상에 설치되며 상기 이동관 내에서 이동되는 공기를 산화반응 가능하도록 처리하는 열풍생성부;A hot air generating unit installed on the moving tube and configured to process the air moved in the moving tube to be oxidized; 일단은 상기 이동관에 연결되고 타단은 상기 유입구에 연결되어 재처리된 공기를 탄소섬유 전구체 유기섬유가 위치된 상기 안정화로 내에 공급하는 분기관부; A branch pipe part connected to the mobile pipe at one end thereof and connected to the inlet port to supply reprocessed air into the stabilization furnace in which the carbon fiber precursor organic fiber is located; 상기 분기관부 내에 설치되며 상기 안정화로 내에 공급되는 공기의 양을 제어하는 댐퍼; 및A damper installed in the branch pipe part to control an amount of air supplied into the stabilization furnace; And 상기 유입구 측에 설치되며 상기 안정화로 내에 공급되는 공기의 흐름을 제어하는 에어가이드부;를 포함하고,And an air guide unit installed at the inlet side and controlling the flow of air supplied into the stabilization furnace. 상기 에어가이드부는, 상기 분기관부와 인접된 측에 설치되어 유입되는 열풍의 좌우방향을 제어하는 제 1 가이드와, 상기 제 1 가이드의 후방에 위치되며 유입되는 열풍의 상하방향을 제어하는 제 2 가이드와, 상기 제 2 가이드의 후방에 위치되며 유입되는 열풍을 균등하게 구획하는 제 3 가이드를 포함하는 것을 특징으로 하는 탄소섬유 제조용 안정화장치.The air guide part may include a first guide installed at a side adjacent to the branch pipe part to control a left and right direction of the introduced hot wind, and a second guide positioned at the rear of the first guide to control a vertical direction of the introduced hot air. And a third guide positioned at the rear of the second guide and equally partitioning the incoming hot air. 청구항 1에 있어서,The method according to claim 1, 상기 유입구는 상기 안정화로 일측 하부의 전,후방 2개소와, 타측 하부의 전,후방 2개소에 각각 구비되며, 상기 배출구는 상기 안정화로 상부 중앙측에 구비되는 것을 특징으로 하는 탄소섬유 제조용 안정화장치.The inlet is provided in the front and rear two places of the lower side of the stabilization furnace, and the front and rear two places of the lower side of the other, respectively, the discharge port is stabilized device for producing carbon fiber, characterized in that provided in the upper center side of the stabilization furnace . 청구항 1 또는 청구항 2에 있어서,The method according to claim 1 or 2, 상기 열풍생성부는, 상기 배출구 측에 위치되며 산화처리에 사용된 공기를 가열하는 히터와, 상기 히터 후방에 위치되며 가열된 공기를 필터링하는 필터와, 상기 필터의 후방에 위치되며 필터링된 공기를 상기 안정화로 측으로 강제순환시키는 송풍기를 포함하는 것을 특징으로 하는 탄소섬유 제조용 안정화장치.The hot air generating unit, a heater for heating the air used for the oxidation treatment, located on the outlet side, a filter for filtering the heated air located behind the heater, and the filtered air located behind the filter Stabilizing apparatus for producing carbon fiber, comprising a blower for forced circulation to the stabilization furnace side. 청구항 3에 있어서,The method of claim 3, 상기 분기관부는 그 일단이 상기 이동관의 단부와 연결된 다음 4개소로 분기되며 분기된 분기관부는 상기 안정화로 일측 및 타측 하부의 전, 후방으로 각각 연장 형성된 다음 상기 유입구와 각각 연결되는 것을 특징으로 하는 탄소섬유 제조용 안정화장치.The branch pipe portion is one end is connected to the end of the moving pipe and then branched into four places, the branched branch pipe portion is formed to extend to the front and rear of one side and the other lower portion of the stabilization path, respectively, characterized in that connected to the inlet Stabilizer for manufacturing carbon fiber. 삭제delete
KR20090012195U 2009-09-16 2009-09-16 Stabilization appalatus for manufacturing carbon fiber KR200460762Y1 (en)