KR20040033097A - Method for manufacture of articial stone plate for interior outside a structure - Google Patents

Method for manufacture of articial stone plate for interior outside a structure Download PDF

Info

Publication number
KR20040033097A
KR20040033097A KR1020020061991A KR20020061991A KR20040033097A KR 20040033097 A KR20040033097 A KR 20040033097A KR 1020020061991 A KR1020020061991 A KR 1020020061991A KR 20020061991 A KR20020061991 A KR 20020061991A KR 20040033097 A KR20040033097 A KR 20040033097A
Authority
KR
South Korea
Prior art keywords
weight
building
artificial stone
stone plate
less
Prior art date
Application number
KR1020020061991A
Other languages
Korean (ko)
Inventor
윤영식
Original Assignee
윤영식
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 윤영식 filed Critical 윤영식
Priority to KR1020020061991A priority Critical patent/KR20040033097A/en
Priority to PCT/KR2003/002062 priority patent/WO2004033385A1/en
Priority to AU2003267843A priority patent/AU2003267843A1/en
Publication of KR20040033097A publication Critical patent/KR20040033097A/en

Abstract

PURPOSE: Provided are artificial stone boards for interior and exterior construction having beautiful colors and functionalities such as catalyst, deodorant and absorbent by using zeolite and natural fine aggregates as main materials. CONSTITUTION: The artificial stone board(10) comprises 40wt.% of natural zeolite, 30wt.% or less of at least one natural fine aggregates(powder type) selected from white cement, pumice and volcanic rock, water adhesive such as acrylate emulsion, silicon, epoxy, latex or PVA, and 10wt.% or less of pigment. The boards are manufactured by the following steps of: mixing zeolite, aggregates, adhesive and water, wherein the desirable mixing ratio is 27-30wt.% of white cement, 8-10wt.% of volcanic rock, 13-15wt.% of pumice, 40-43wt.% of zeolite and 5wt.% of adhesive; spraying pigment on the inside of a mold(30) and feeding mixed materials(12) into the mold, and vibrating for increase of compaction; hot blast drying and hardening at 60-70deg.C for 12-14hrs; demolding.

Description

건축물 내, 외장용 인조석 판재 및 그 제조방법{METHOD FOR MANUFACTURE OF ARTICIAL STONE PLATE FOR INTERIOR OUTSIDE A STRUCTURE}Artificial stone plate for building and exterior and its manufacturing method {METHOD FOR MANUFACTURE OF ARTICIAL STONE PLATE FOR INTERIOR OUTSIDE A STRUCTURE}

본 발명은 예컨대, 건축물의 외벽 보호와 장식을 목적으로 설치되는 건축물내, 외장용 인조석 판재에 관한 것으로, 더욱 상세하게는 인조석 판재의 제조 시에 촉매제 기능, 이온교환, 흡착성, 공기정화 및 원적외선 방사 특성을 갖는 물질을 주원료로 배합·사용하여, 건축물 내, 외장재로 사용 때 실내의 음식냄새, 미세 먼지 및 탁한 공기를 흡착·정화하여 쾌적한 실내환경을 조성하고, 또한 천연석의 미려한 색상연출을 그대로 살리면서 자체 무게의 경량화에 따른 시공의 편리성을 양립하도록 하는 건축물 내, 외장용 인조석 판재 및 그 제조방법에 관한 것이다.The present invention relates to, for example, the interior and exterior artificial stone plate installed for the purpose of protecting and decorating the outer wall of the building, and more particularly, the catalyst function, ion exchange, adsorption, air purification and far-infrared radiation characteristics in the manufacture of the artificial stone plate. It is used as a main raw material to mix and use materials that have a high quality, and to adsorb and purify indoor food smells, fine dust and muddy air when used in building and exterior materials, to create a pleasant indoor environment and to preserve the beautiful color of natural stone. The present invention relates to an artificial stone plate for a building and an exterior, and a method of manufacturing the same, which are compatible with the convenience of construction due to light weight of its own weight.

일반적으로 건축물의 내, 외벽에 외장을 씌우기 위한 방법으로는 통상적으로 인조석 건식 방식과 스프레이 방식이 널리 이용되어 시공되고 있다.In general, as a method for covering the interior and exterior walls of buildings, artificial dry and spray methods are widely used.

특히, 건축물의 내, 외벽을 외장하기 위해 널이 이용되는 상기 인조석 건식 방식에 있어서는 백시멘트, 황사 등의 무기재료의 골재와 물을 혼합한 반죽재료를 일정한 규격의 정사각형 또는 직사각형의 단위 성형몰드에 충진하여 이를 일정한 온도에서 열풍 건조한 후에 탈형하는 것에 의해 건축물의 내, 외장용 인조석 판재가 완성되며, 이와 같이 완성된 인조석 판재를 건축물의 내벽 또는 외벽에 대해 가로 및 세로로 조립·시공하는 것으로, 상기 인조석 판재를 건축물의 내벽 또는 외벽에 시설할 때의 한 예로서, 건축물 내벽 또는 외벽과 인조석 판재의 배면에 각각 시멘트 몰탈을 발라 부착함과 아울러 인조석 판재들과의 사이에 일정간격의 메지를 형성한 후 상기 메지에 접착제 또는 시멘트 몰탈 등을 충진하여 마감처리하고 있는 실정이다.In particular, in the artificial stone dry method in which a board is used to cover the inner and outer walls of a building, a dough material obtained by mixing aggregates of inorganic materials such as back cement and yellow sand and water into a square or rectangular unit molding mold of a certain standard is used. After filling and drying it by hot air drying at a constant temperature, demoulding is completed, and the interior and exterior artificial stone plate of the building is completed, and thus, the artificial stone plate is assembled and constructed horizontally and vertically with respect to the inner wall or the outer wall of the building. As an example of installing a board on an inner wall or an outer wall of a building, cement mortar is applied to the inner wall or outer wall of the building and the back of the artificial stone board, respectively, and a gap is formed between the artificial stone boards. It is a situation that the finishing treatment by filling the message with an adhesive or cement mortar.

그리고 상기 스프레이 방식에 있어서는 건축물을 축조한 후에 건축물 벽면에 외장을 씌우기 위해 시멘트 몰탈을 바르고, 그 위에 단위면적을 갖는 알루미늄 판재, 벽돌, 페인트, 안료 등을 혼합하여 바르는 엷은 벽바름재 방식으로 시공하여 건축물을 내, 외장 처리하는 것이다.In the spray method, after constructing the building, cement mortar is applied to cover the wall of the building, and the construction is performed by using a thin wall coating material by mixing aluminum plate, brick, paint, and pigment having a unit area thereon. It is to process the building inside and outside.

그러나, 상기 인조석 건식 방식에서는 시공이 간편한 반면에 단위 판재의 비중이 무거워 그 자중 또는 경미한 외력에 의해서 인조석 판재가 벽면으로부터 탈형되어 안전사고를 유발하거나 또는 인조석 판재가 갖는 중량 때문에 건축물 자체가 받는 하중이 커져 안정성에 문제가 있으며, 상기 스프레이 방식에 있어서는 표면의 요철형태가 거칠게 이루어져 분진 등의 오염 물질이 점착될 뿐만 아니라 그에 따른 변색이 일어나 환경오염은 물론 외관상 미려하지 못하고, 또 시공비용 및 시공 시간이 많이 소요되는 등 작업손실이 뒤따르는 문제점이 있다.However, in the artificial dry method, the construction is easy, while the specific gravity of the unit plate is heavy so that the artificial stone plate is demolded from the wall by its own weight or slight external force, causing a safety accident or the load of the building itself due to the weight of the artificial stone plate. There is a problem in stability, and in the spray method, the roughness of the surface is rough, so that contaminants such as dust are adhered to it, and the discoloration occurs accordingly, so that the environmental pollution as well as appearance is not beautiful, and construction cost and construction time are increased. There is a problem that a lot of work is followed by a loss of work.

특히, 상기 인조석 건식 방식과 스프레이 방식에 의해 처리된 건축물 내, 외장용 마감재에 있어서는 주로 건축물의 외벽 보호와 장식을 목적으로 시설될 뿐 그 외의 기능, 즉 다시 말해서 실내 공간의 악취와 미세 먼지 및 담배연기와 같은 탁한 공기를 흡착·정화하는 기능으로 활용하지 못하고 있으며, 이것에 의해 밀폐된 실내공간에서 오염이 더욱더 가속화되어 인체 건강에 악영향을 미치게 되는 문제점이 있다.In particular, the interior finishing materials for the exterior of the building treated by the artificial stone dry method and the spray method is mainly provided for the purpose of protecting and decorating the exterior wall of the building, and other functions, that is, the smell of the indoor space and fine dust and tobacco smoke It does not utilize as a function to adsorb and purify the muddy air, such that there is a problem that the pollution is further accelerated in the closed indoor space adversely affects the human health.

따라서, 상기와 같은 문제점들을 치유하면서도 비용 면에서는 보다 저가의 건축물 내, 외장용 인조석 판재를, 그리고 신뢰성 면에서는 자체의 중량이 가벼우면서도 공기중의 분진, 실내의 악취와 미세 먼지 및 탁한 공기를 흡착·정화하여 쾌적한 환경을 조성해 주는 건축물 내, 외장용 인조석 판재를 제공하는 것이 바람직하다.Therefore, while healing the problems mentioned above, it is possible to adsorb and absorb inexpensive interior and exterior artificial stone boards in terms of cost, and in terms of reliability in terms of its own weight and dust in the air, odors and fine dust in the room, and muddy air. It is desirable to provide artificial stone boards for building and exterior use that purify and create a pleasant environment.

따라서, 본 발명의 목적은 실내에 발생되는 음식냄새, 담배연기 및 공기중의 분진 등의 오염물질을 흡착·정화하여 쾌적한 환경을 조성해 주는 건축물 내, 외장용 인조석 판재를 제공하는 것이며, 이 인조석 판재는 촉매, 탈취제, 흡착제 등으로 이용되는 입자가 작고 부드러운 천연 제올라이트(ZEOLITE) 광물을 주원료로 혼합하여 원하는 형상의 성형몰드에 충진한 후에 열풍건조시켜 양생함으로써 달성된다.Accordingly, it is an object of the present invention to provide an interior and exterior artificial stone plate for building a pleasant environment by adsorbing and purifying pollutants such as food odor, tobacco smoke and dust in the air generated indoors. Particles used as catalysts, deodorants, adsorbents, etc. are achieved by mixing small, soft natural zeolite minerals as a main raw material, filling them into molding molds of a desired shape, and then curing them by hot air drying.

본 발명의 다른 목적은 자체 무게의 경량화에 의해 다루기가 쉬워 안정성 및 시공의 편리성이 있음은 물론 건축물의 외벽에 대해 탈형이 방지되는 건축물 내, 외장용 인조석 판재를 제공함에 있다.Another object of the present invention is to provide an artificial stone plate for the interior and exterior of the building that is easy to handle by light weight of its own weight, there is stability and convenience of construction, as well as demoulding is prevented against the outer wall of the building.

본 발명의 또다른 목적은 천연석의 미려한 외관과 질감 등의 특성을 그대로 살리면서 일반 건축물 내, 외장재가 이루지 못하는 경제적인 면이나 기능적인 면을 획기적으로 커버할 수 있는 건축물 내, 외장용 인조석 판재의 제조방법을 제공하는 것이며, 이 인조석 판재의 제조방법은 접착보강재와 입자가 작고 부드러운 천연 제올라이트를 주원료로 하고, 이에 선택적으로, 백시멘트, 입자가 작고 가벼운 소량의 화산석, 프라이트(경석) 및 안료를 물과 혼합 반죽하여 자연형태의 성형몰드에 충진한 다음 열풍건조실에서 양생시켜 성형함으로써 달성된다.Still another object of the present invention is to manufacture artificial stone plate for building and exterior which can cover economical and functional aspects that cannot be achieved in general buildings and exterior materials while maintaining the beautiful appearance and texture of natural stone as it is. The method of manufacturing the artificial stone plate is made of an adhesive reinforcing material and a natural zeolite having a small particle size and a soft material, and optionally, water containing a small amount of white cement, small particles and light volcanic stone, fryer and pigment. It is achieved by mixing and kneading with a mold to form a natural molding mold, and then curing by molding in a hot air drying chamber.

본 발명의 또다른 목적들은 다음의 상세한 설명과 첨부된 도면으로부터 보다 명확해질 것이다.Other objects of the present invention will become more apparent from the following detailed description and the accompanying drawings.

도 1 내지 도 3은 본 발명에 따른 건축물 내, 외장용 인조석 판재의 설명에 제공되는 실시 예를 나타내는 구성도로서,1 to 3 is a block diagram showing an embodiment provided for the description of the artificial stone plate for building, exterior in accordance with the present invention,

도 1은 상기 건축물 내외장용 인조석 판재를 제조하기 위해 반죽재료가 성형몰드에 충진된 상태를 나타내어 보인 단면도이고,1 is a cross-sectional view showing a state in which the dough material is filled in a molding mold to manufacture the building interior and exterior artificial stone plate,

도 2는 도 1의 건축물 내, 외장용 인조석 판재의 반죽재료가 충진된 상태에서 밀도를 높이기 위해 성형몰드를 진동시키는 과정을 보인 단면도이고,2 is a cross-sectional view showing a process of vibrating the molding mold in order to increase the density in the state of filling the dough material of the exterior artificial stone plate in the building of Figure 1,

도 3은 도 2의 성형몰드의 반죽재료를 경화·탈형시켜 제조·완성된 건축물 내, 외장용 인조석 판재의 사시도이다.FIG. 3 is a perspective view of an exterior artificial stone plate material in a building manufactured and completed by curing and demolding the dough material of the molding mold of FIG. 2. FIG.

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

10 : 인조석 판재 12 : 반죽재료10: artificial stone plate 12: dough material

30 : 성형몰드30: molding mold

상기와 같은 목적들을 달성하기 위한 본 발명에 의한 건축물 내, 외장용 인조석 판재의 제조방법에 의하면, 입도분포가 작고 가벼운 분말형태의 화산석, 프라이트, 백시멘트로 이루어진 군에서 선택되는 하나 이상의 잔입도 골재 30중량%이하와 입도분포가 작고 부드러운 천연 제올라이트 40중량%를 물과 혼합하여 반죽하는 재료 혼합공정; 단위면적을 갖는 성형몰드에 상기 반죽재료를 충진한 후 진동시켜 충진밀도를 높이는 성형공정; 상기 성형공정에서 성형된 반죽재료를 열풍건조시켜 경화시키는 소성공정; 및 상기 경화된 반죽재료를 상기 성형몰드로부터 탈형시키는 마무리공정을 포함한다.According to the manufacturing method of the artificial stone plate for the interior of the building according to the present invention for achieving the above objects, the particle size distribution is small and light one or more fine aggregate aggregate selected from the group consisting of powder, volcanic stone, frit, back cement 30 A material mixing step of kneading by mixing 40% by weight or less and 40% by weight of soft natural zeolite with a small particle size distribution and water; A molding process of filling the mold material with a unit area with the dough material and vibrating to increase the filling density; A baking step of curing the dough material formed in the forming step by hot air drying; And a finishing process of demolding the cured dough material from the molding mold.

바람직하기로, 상기 재료 혼합공정에서 상기 반죽재료가 5중량%의 접착보강재를 더 포함한 것을 특징으로 한다.Preferably, the dough material in the material mixing step is characterized in that it further comprises an adhesive reinforcement of 5% by weight.

선택적으로, 상기 접착보강재는 에멜존 아크릴 레이트, 실리콘 수지, 수용성 에폭시, 라텍스, PVA 수지 중 어느 하나인 것을 특징으로 한다.Optionally, the adhesive reinforcing material is characterized in that any one of the melzone acrylate, silicone resin, water-soluble epoxy, latex, PVA resin.

선택적으로, 상기 재료 혼합공정에서 상기 반죽재료가 채색을 위한 10중량% 이하의 안료를 더 포함한 것을 특징으로 한다.Optionally, the dough material in the material mixing process is characterized in that it further comprises up to 10% by weight of pigment for coloring.

본 발명에 의한 건축물 내, 외장용 인조석 판재에 의하면, 입도분포가 작고 가벼운 분말형태의 화산석, 프라이트, 백시멘트로 이루어진 군에서 선택되는 적어도 하나 이상의 잔입도 골재; 상기 선택된 하나 이상의 잔입자 골재와 입도분포가 작고 부드러운 천연 제올라이트를 물과 혼합하여 된 반죽재료; 및 상기 반죽재료를 단위면적을 가지는 성형몰드에 충진·경화시켜 이루어짐을 특징으로 한다.According to the interior of the building, exterior artificial stone plate according to the present invention, the particle size distribution has a small particle size distribution of at least one selected from the group consisting of volcanic stone, frit, back cement; A dough material obtained by mixing the selected one or more residual particle aggregates and small particle size distribution and soft natural zeolite with water; And filling and curing the dough material in a molding mold having a unit area.

바람직하기로, 상기 반죽재료가 에멜존 아크릴레이트, 실리콘 수지, 수용성 에폭시, 라텍스, PVA 수지로 이루어진 군에서 선택되는 하나 이상의 접착보강재를 더 포함한 것을 특징으로 한다.Preferably, the dough material is characterized in that it further comprises at least one adhesive reinforcing material selected from the group consisting of ethylene zone acrylate, silicone resin, water-soluble epoxy, latex, PVA resin.

바람직하기로, 상기 선택된 하나 이상의 잔입도 골재가 백시멘트와 프라이트라 하고, 상기 접착보강재가 에멜존 아크릴레이트라 할 때, 상기 백시멘트 30중량% 이하, 프라이트 15중량%와 상기 에멜존 아크릴 레이트 5중량% 및 천연 제올라이트 50중량% 이하가 물과 혼합·반죽된 것을 특징으로 한다.Preferably, when the selected at least one residual aggregate aggregates with the back cement, and the adhesive reinforcing material is an emelzone acrylate, the back cement is 30% by weight or less, frit 15% by weight and the emelone acrylate 5 It is characterized by mixing and kneading with water and 50% by weight or less of natural zeolite.

바람직하기로, 상기 선택된 하나 이상의 잔입도 골재가 백시멘트와 화산석 이라 하고, 상기 접착보강재가 에멜존 아크릴레이트라 할 때, 상기 백시멘트 30중량% 이하, 화산적 10중량%와 상기 에멜존 아크릴 레이트 5중량% 및 천연 제올라이트 50중량% 이하가 물과 혼합·반죽된 것을 특징으로 한다.Preferably, when the selected at least one residual aggregate is called back cement and volcanic stone, and the adhesive reinforcing material is called emel acrylate, the weight of the back cement is 30% by weight or less, 10% by weight of volcanic acid and the mellzone acrylate. 5 wt% and 50 wt% or less of natural zeolite are mixed and kneaded with water.

본 발명에 의한 건축물 내, 외장용 인조석 판재에 의하면 입도분포가 작고 가벼운 분말형태의 화산석 10중량% 이하, 백시멘트 30중량% 이하, 프라이트(경석) 15중량% 이하를 입도분포가 작고 부드러운 천연 제올라이트 40중량%, 에멜존아크릴레이트 5중량% 이하를 물과 혼합하여 반죽한 후 상기 반죽된 재료를 단위면적을 갖는 성형몰드에 충진하고 경화시켜 이루어진 것을 특징으로 한다.According to the artificial stone plate for building and exterior according to the present invention, the particle size distribution has a small particle size distribution of 10% by weight or less of light-weight volcanic stone, 30% by weight or less of cement, and 15% by weight or less of frit (pumice). 5% by weight or less of the emelzone acrylate is mixed with water and kneaded, and then the kneaded material is filled into a molding mold having a unit area and cured.

이와 같이, 촉매, 탈취제, 흡착제 등으로 이용되는 입도분포가 작고 부드러우며 가벼운 천연 제올라이트를 주원료로 하고, 이에 화산석, 프라이트, 백시멘트 중에서 하나 이상의 잔입도 골재를 접착보강재 및 물과 함께 혼합하여 원하는 성형몰드에 충진·경화시킨 후에 탈형하여 성형하게 됨을 알 수 있다.In this way, the particle size distribution used as a catalyst, deodorant, adsorbent, etc. is made of small, soft and light natural zeolite as the main raw material, and at least one residual aggregate of volcanic stone, frit, and back cement is mixed with an adhesive reinforcing material and water to form a desired molding. It can be seen that after the mold is filled and cured, the mold is demolded and molded.

그 결과, 천연 제올라이트를 주원료 하여 성형된 인조석 판재를 건축물 내, 외장재로 사용 시에 천연 제올라이트에 의해 음식냄새, 담배연기, 화장실 등에서 발생되는 암모니아 및 분진 등의 오염물질이 흡착·정화되어 쾌적한 실내환경이 조성될 뿐만 아니라 원적외적 방사에 의해 건강도모에 효과가 있고, 또한 천연석의 미려한 외관과 질감 등의 특성에 의해 건축물의 미려한 내, 외장용으로 우수하게 사용될 수 있음은 물론 자체 무게의 경량화에 의해 안정성 및 시공의 편리성이 있는 이점이 있다.As a result, when using artificial stone plate formed by using natural zeolite as a main raw material in building and exterior material, natural zeolite absorbs and purifies pollutants such as food smell, tobacco smoke, toilet, etc. Not only is this composition effective for promoting health by far-infrared radiation, and it is also used for the beautiful interior and exterior of buildings by the beautiful appearance and texture of natural stone, and it is stable by light weight of its own. And there is an advantage in the convenience of construction.

그리고, 본 발명의 실시 예로는 다수개가 존재할 수 있으며, 이하에서는 가장 바람직한 실시 예에 대하여 상세히 설명하고자 한다.And, there may be a plurality of embodiments of the present invention, the following will be described in detail for the most preferred embodiment.

이 바람직한 실시 예를 통해 본 발명의 목적, 기타의 목적, 특징 및 이점은 예시할 목적으로 도시한 첨부 도면과 관련해서 본 발명에 의한 실시 예를 가지고 이하의 설명으로부터 보다 명백해질 것이다.Through this preferred embodiment, the objects, other objects, features and advantages of the present invention will become more apparent from the following description with an embodiment according to the present invention in connection with the accompanying drawings shown for illustrative purposes.

이하, 첨부한 도면을 참조하여 본 발명에 따른 건축물 내, 외장용 인조석 판재의 바람직한 실시 예를 상세히 설명하기로 한다.Hereinafter, with reference to the accompanying drawings will be described in detail a preferred embodiment of the building interior, exterior artificial stone plate according to the present invention.

도 1은 본 발명에 따른 건축물 내외장용 인조석 판재를 제조하기 위해 반죽재료가 성형몰드에 충진된 상태를 나타내어 보인 단면도이고, 도 2는 도 1의 건축물 내, 외장용 인조석 판재의 반죽재료가 충진된 상태에서 밀도를 높이기 위해 성형몰드를 진동시키는 과정을 보인 단면도이며, 도 3은 도 2의 성형몰드의 반죽재료를 경화·탈형시켜 제조·완성된 건축물 내, 외장용 인조석 판재의 단면도이다.1 is a cross-sectional view illustrating a state in which a dough material is filled in a molding mold to manufacture an interior and exterior artificial stone board according to the present invention, and FIG. 2 is a state in which the dough material of the exterior artificial stone board is filled in the building of FIG. 1. In Figure 3 is a cross-sectional view showing a process of vibrating the molding mold to increase the density, Figure 3 is a cross-sectional view of the artificial stone plate for the interior of the building manufactured and completed by curing and demolding the dough material of the molding mold of FIG.

본 실시 예에 따른 건축물 내, 외장용 인조석 판재는 입도분포가 작고 가벼운 화산석, 프라이트, 백시멘트로 이루어진 군에서 선택되는 적어도 하나 이상의 잔입도 골재와 접착강화를 위한 접착보강재 및 입도분포가 작고 부드러운 천연 제올라이트를 재료혼합공정에서 물과 고르게 혼합하여 반죽하고 상기 반죽재료를 성형공정에서 바닥면이 자연석 형태, 즉 혹두기 형태를 이루는 단위면적의 성형몰드에 충진하고 진동시켜 충진밀도를 높인 후 소정공정에서 열풍으로 건조시켜 경화시키고 마무리공정에서 상기 경화된 경질의 인조석 판재를 탈형시킴으로써 제품이 완성되는 것이다.In the building according to the present embodiment, the exterior artificial stone plate has a small particle size distribution and at least one selected from the group consisting of light volcanic stone, frit, and back cement, and a reinforcement material for strengthening adhesion and a soft natural zeolite having a small particle size distribution. Is kneaded with water evenly in the material mixing process, and the kneading material is filled and vibrated in a molding mold having a unit area of natural stone shape, that is, a lump shape, in a molding process and vibrated to increase the filling density, followed by hot air in a predetermined process. The product is completed by curing by drying with a mold and demolding the hardened artificial stone plate in the finishing process.

이하 본 발명을 실시 예에 의하여 상세히 설명한다.Hereinafter, the present invention will be described in detail by examples.

〈재료혼합공정〉〈Material Mixing Process〉

기본적으로, 입도분포가 작고 부드러운 천연 제올라이트와 백시멘트 및 상기 백시멘트와 천연 제올라이트의 결합을 용이하게 하기 위한 에멜존 아크릴 레이트계(실리콘 수지, 수용성 에폭시, 라텍스, EVA 수지, PVA 수지 등)의 접착보강재, 그리고 제품을 가볍게 하기 위해 입도분포가 작고 가벼운 잔입도 골재, 즉 화산석과 프라이트(경석)를 혼합기에 투여하여 고르게 혼합한 후에, 그 혼합된 재료에 물을 투입하고 교반하여 반죽상태의 재료를 준비한다.Basically, adhesion of soft natural zeolite with small particle size distribution and back cement and emelone acrylate type (silicone resin, water soluble epoxy, latex, EVA resin, PVA resin, etc.) for facilitating bonding of the back cement with natural zeolite. In order to lighten the reinforcement material and the product, the particle size distribution is small and light residue aggregate, that is, volcanic stone and frit is administered to the mixer and mixed evenly. Then, water is added to the mixed material and stirred to prepare the dough material. Prepare.

이때, 상기 각 재료의 중량비로써는, 잔입도 골재의 백시멘트 27 내지 30중량%와 화산석 8내지 10중량%, 프라이트 13 내지 15중량%, 그리고 마사토 형태의 천연 제올라이트 40 내지 43중량% 및 접착보강재 5중량%로 하는 것이 바람직하다.In this case, as the weight ratio of each material, 27 to 30% by weight of the back cement aggregate and 8 to 10% by weight volcanic stone, 13 to 15% by weight frying, and 40 to 43% by weight of natural zeolite in the form of masato and adhesive reinforcement 5 It is preferable to set it as weight%.

여기서, 상기 잔입도 골재 중에서 백시멘트와 프라이트만을 적용했을 경우에그 중량비로써, 백시멘트 28 내지 30중량%, 프라이트 13 내지 15중량%, 그리고 상기 접착보강재 5중량% 및 천연 제올라이트 45중량% 이하로 하는 것도 가능하며, 또한 상기 잔입도 골재 중에서 백시멘트와 화산석만을 적용했을 경우에는, 그 중량비로써, 백시멘트 28 내지 30중량%, 화산적 8 내지 10중량%, 접착보강재 5중량% 및 천연 제올라이트 50중량%로 하는 것도 가능하다.Here, when only the back cement and the frit are applied in the residual aggregate, the weight ratio is 28 to 30% by weight, 13 to 15% by weight, and 5% by weight of the adhesive reinforcing material and 45% by weight of the natural zeolite. In addition, when only the back cement and the volcanic stone are applied among the above-mentioned aggregates, the weight ratio is 28 to 30% by weight, 8 to 10% by weight, 5% by weight of the adhesive reinforcing material, and 50% by weight of the natural zeolite. It is also possible to set it as weight%.

〈성형공정〉<Molding process>

바닥면이 자연석 형태, 즉 혹두기 형태로 형성된 성형몰드(30)를 준비한다.A molding mold 30 having a bottom surface formed in a natural stone form, that is, a hump form, is prepared.

이후 채색을 위해서 안료용액 10중량% 이하를 준비된 성형몰드(30)의 성형면에 고르게 뿌려 도포한다. 안료가 도포된 상태에서 상기 재료혼합공정에서 준비된 반죽상태의 재료(12)를 단위면적을 갖는 성형몰드(30)에 충진하면서 도 2에 나타내는 바와 같이, 성형몰드(30)를 전후좌우로 진동시키면 반죽재료(12)의 충진밀도가 향상됨과 아울러 상기 안료가 반죽재료의 표면에 희석되어지고 성형몰드(30)의 바닥면과 같은 성형이 이루어진다.Thereafter, for coloring, 10 wt% or less of the pigment solution is evenly sprayed onto the molding surface of the prepared molding mold 30 and applied. As shown in Figure 2, while filling the molding mold 30 having a unit area with the dough 12 prepared in the material mixing step in the state that the pigment is applied, and vibrating the molding mold 30 in front, rear, left and right In addition to improving the packing density of the dough material 12, the pigment is diluted on the surface of the dough material and the molding such as the bottom surface of the molding mold 30 is performed.

〈소성공정〉<Firing process>

상기 성형공정에서 반죽재료(12)가 고르게 충진되어진 성형몰드(30)를 열풍건조실에서 60 내지 70℃의 온도로 12 내지 14시간 건조시켜 수분이 제거되면 경화되어 도 3과 같은 경질의 인조석 판재(10)가 되는 것이다.In the molding process, the molding mold 30 in which the dough material 12 is evenly filled is dried in a hot air drying room at a temperature of 60 to 70 ° C. for 12 to 14 hours, and then cured when moisture is removed. 10).

〈마무리공정〉<Finishing process>

상기 소성공정에서 건조 완료된 후에 성형몰드(30)로부터 인조석 판재(10)를 탈형함으로써 도 3과 같이 미려한 색상을 갖는 제품이 완성되는 것이다.After the drying is completed in the firing process, by deforming the artificial stone plate 10 from the molding mold 30, a product having a beautiful color as shown in FIG. 3 is completed.

상기의 과정을 거쳐 완성된 인조석 판재를 건축물에 시공하고자 할 때에는 시멘트 몰탈을 시공할 벽면에 바르고, 또한 인조석 판재(10)를 벽면에 압착하여 부착시킨다.When the artificial stone plate completed through the above process is to be installed in the building, cement mortar is applied to the wall to be constructed, and the artificial stone plate 10 is pressed onto the wall and adhered thereto.

상기와 같이 부착된 인조석 판재(10)는 자체 무게가 경량이 때문에 벽면으로부터 탈형이 되지 않고, 또한 건축물 자체가 받는 하중이 작아 안정성을 보장할 수 있다.Since the artificial stone plate 10 attached as described above is light in weight, it is not demolded from the wall surface, and the load that the building itself receives is small, thereby ensuring stability.

한편, 비교 예로서, 종래의 기술, 즉 다시 말해서 인조석 건식 방식과 스프레이 방식에 의해 처리된 건축물 내, 외장용 마감재가 주로 건축물의 외벽 보호와 장식을 목적으로 시설되는 것과는 달리, 본 발명은 촉매, 탈취제, 흡착제 등으로 이용되는 천연 제올라이트를 주원료로 하고, 이에 화산석, 프라이트, 백시멘트 중에서 하나 이상의 잔입도 골재를 접착보강재 및 물과 함께 혼합하여 원하는 형태의 인조석 판재를 성형하게 됨을 알 수 있다.On the other hand, as a comparative example, unlike the conventional technology, that is, in the building treated with artificial stone dry method and spray method, the exterior finishing material is mainly installed for the purpose of protecting and decorating the exterior wall of the building, the present invention is a catalyst, deodorant Natural zeolite used as an adsorbent is used as a main raw material, and one or more residual aggregates of volcanic stone, frit and back cement are mixed with an adhesive reinforcing material and water to form an artificial stone plate of a desired shape.

이 결과에서 본 발명에 의하면, 천연 제올라이트를 주원료 하여 성형된 인조석 판재를 건축물 내, 외장재로 사용 시에 천연 제올라이트의 기능성에 의해 음식냄새, 담배연기, 암모니아 및 분진 등의 오염물질이 흡착·정화되어 쾌적한 실내환경이 조성되는 이점이 있는 것이다.As a result, according to the present invention, when the artificial stone plate formed by using the natural zeolite as a main raw material is used as a building material or exterior material, contaminants such as food smell, tobacco smoke, ammonia and dust are absorbed and purified by the functionality of the natural zeolite. There is an advantage that a pleasant indoor environment is created.

그리고, 상기에서 본 발명의 특정한 실시 예가 설명 및 도시되었지만 본 발명이 당업자에 의해 다양하게 변형되어 실시될 가능성이 있는 것은 자명한 일이다.In addition, although specific embodiments of the present invention have been described and illustrated above, it is obvious that the present invention may be variously modified and implemented by those skilled in the art.

이와 같은 변형된 실시 예들은 본 발명의 기술적 사상이나 전망으로부터 개별적으로 이해되어져서는 안되며, 이와 같은 변형된 실시 예들은 본 발명의 첨부된 특허청구범위 안에 속한다 해야 할 것이다.Such modified embodiments should not be individually understood from the technical spirit or the prospect of the present invention, and such modified embodiments should fall within the appended claims of the present invention.

상술한 설명으로부터 분명한 본 발명의 건축물 내, 외장용 인조석 판재에 의하면, 촉매, 탈취제, 흡착제 등으로 이용되는 천연 제올라이트를 주원료 하여 성형함으로써, 실내의 음식냄새, 담배연기, 화장실 등에서 발생되는 암모니아 및 분진 등의 오염물질이 흡착·정화되어 쾌적한 실내환경이 조성되고, 또한 천연 제올라이트로부터 원적외적이 방사됨으로써, 건강도모에 효과가 있을 뿐만 아니라 천연석의 미려한 외관과 질감에 의해 건축물의 미려한 내, 외장용으로 우수하게 사용될 수 있으며, 또 자체 무게의 경량화에 의해서 안정성과 시공의 편리성이 보장되는 효과가 있다.According to the artificial stone sheet for building and exterior of the present invention, which is apparent from the above description, a natural zeolite used as a catalyst, a deodorant, an adsorbent, and the like is formed by molding the main raw material, so that ammonia and dust generated in the indoor food smell, tobacco smoke, toilet, etc. Of contaminants are adsorbed and purified, creating a pleasant indoor environment and radiating far-infrared rays from natural zeolites, which not only contribute to health promotion, but are also excellent for the beautiful interior and exterior of buildings due to the beautiful appearance and texture of natural stones. It can be used, and also by the weight reduction of its own weight has the effect of ensuring stability and convenience of construction.

Claims (10)

(1) 입도분포가 작고 가벼운 분말형태의 화산석, 프라이트, 백시멘트로 이루어진 군에서 선택되는 하나 이상의 잔입도 골재 30중량% 이하와 입도분포가 작고 부드러운 천연 제올라이트 40중량%를 물과 혼합하여 반죽하는 재료 혼합공정;(1) Kneading by mixing water with less than 30% by weight of aggregates and 40% by weight of soft and natural zeolite with a small particle size distribution, selected from the group consisting of small and light powders of volcanic stone, frit and back cement Material mixing process; (2) 단위면적을 갖는 성형몰드에 상기 반죽재료를 충진하고 진동시켜 충진밀도를 높이는 성형공정;(2) a molding process of filling and vibrating the dough material in a molding mold having a unit area to increase the filling density; (3) 상기 성형공정에서 성형된 반죽재료를 열풍으로 건조시켜 경화시키는 소성공정; 및(3) a firing step of drying and curing the dough material formed in the forming step with hot air; And (4) 상기 경화된 반죽재료를 상기 성형몰드로부터 탈형시키는 마무리공정을 포함한 것을 특징으로 하는 건축물 내, 외장용 인조석 판재의 제조방법.(4) A method of manufacturing artificial stone plate for building, characterized in that it comprises a finishing step of demolding the cured dough material from the molding mold. 청구항 1에 있어서,The method according to claim 1, 상기 재료혼합공정에서 상기 반죽재료가 5중량%의 접착보강재를 더 포함한 것을 특징으로 하는 건축물 내, 외장용 인조석 판재의 제조방법.In the building material mixing process, the dough material further comprises 5% by weight of the adhesive reinforcement in the building, the exterior of the artificial stone plate manufacturing method. 청구항 2에 있어서,The method according to claim 2, 상기 접착보강재는 에멜존 아크릴레이트, 실리콘 수지, 수용성 에폭시, 라텍스, PVA 수지 중 어느 하나인 것을 특징으로 하는 건축물 내, 외장용 인조석 판재의 제조방법.The adhesive reinforcing material is an emerald acrylate, a silicone resin, a water-soluble epoxy, latex, PVA resin, characterized in that any one of the building artificial stone plate manufacturing method. 청구항 1에 있어서,The method according to claim 1, 상기 재료혼합공정에서 상기 반죽재료가 10중량% 이하의 안료를 더 포함한 것을 특징으로 하는 건축물 내, 외장용 인조석 판재의 제조방법.In the material mixing process, the kneading material further comprises a pigment of 10% by weight or less, the method of manufacturing artificial stone plate for building interior. (1) 입도분포가 작고 가벼운 화산석, 프라이트, 백시멘트로 이루어진 군에서 선택되는 적어도 하나 이상의 잔입도 골재;(1) at least one fine-grained aggregate selected from the group consisting of small and light volcanic stones, frits and back cement; (2) 상기 선택된 하나 이상의 잔입자 골재와 입도분포가 작고 부드러운 천연 제올라이트를 물과 혼합하여 된 반죽재료; 및(2) a dough material obtained by mixing the selected one or more residual particle aggregates and small particle size distribution and soft natural zeolite with water; And (3) 상기 반죽재료가 단위면적을 가지는 성형몰드에 충진·경화된 후에 탈형되어 이루워진 것을 특징으로 하는 건축물 내, 외장용 인조석 판재.(3) The artificial stone plate for building and exterior of the building, characterized in that the dough material is demolded after being filled and cured in a molding mold having a unit area. 청구항 5에 있어서,The method according to claim 5, 상기 반죽재료가 에멜존 아크릴레이트, 실리콘 수지, 수용성 에폭시, 라텍스, PVA 수지로 이루어진 군에서 선택되는 하나 이상의 접착보강재를 더 포함한 것을 특징으로 하는 건축물 내, 외장용 인조석 판재.The dough material is an emerald acrylate, silicone resin, water-soluble epoxy, latex, artificial stone plate for building interior, characterized in that it further comprises at least one adhesive reinforcement selected from the group consisting of resin. 청구항 5 또는 청구항 6에 있어서,The method according to claim 5 or 6, 상기 선택된 하나 이상의 잔입도 골재가 백시멘트와 프라이트라 하고, 상기 접착보강재가 에멜존 아크릴레이트라 할 때, 상기 백시멘트 30중량% 이하, 프라이트 15중량%와 상기 에멜존 아크릴 레이트 5중량% 및 천연 제올라이트 50중량% 이하가 물과 혼합·반죽되어 이루어진 것을 특징으로 하는 건축물 내, 외장용 인조석 판재.When the selected at least one residual aggregate aggregates with the back cement, and the adhesive reinforcing material is called emelzone acrylate, the back cement is 30% by weight or less, frit 15% by weight and 5% by weight of the emmel acrylate and natural 50% by weight or less of zeolite is mixed and kneaded with water. 청구항 5 또는 청구항 6에 있어서,The method according to claim 5 or 6, 상기 선택된 하나 이상의 잔입도 골재가 백시멘트와 화산석 이라 하고, 상기 접착보강재가 에멜존 아크릴레이트라 할 때, 상기 백시멘트 30중량% 이하, 화산적 10중량%와 상기 에멜존 아크릴 레이트 5중량% 및 천연 제올라이트 50중량% 이하가 물과 혼합·반죽되어 이루어진 것을 특징으로 하는 건축물 내, 외장용 인조석 판재.When the selected at least one residual aggregate aggregate is called back cement and volcanic stone, and the adhesive reinforcing material is called emel acrylate, the weight of the back cement is 30 wt% or less, volcanic 10 wt%, and 5 wt% of the mellzone acrylate and 50% by weight or less of natural zeolite is mixed and kneaded with water. 청구항 5에 있어서,The method according to claim 5, 상기 반죽재료에 안료용액이 더 포함된 것을 특징으로 하는 건축물 내, 외장용 인조석 판재.In-building, exterior artificial stone plate, characterized in that the dough material further comprises a pigment solution. 입도분포가 작고 가벼운 분말형태의 화산석 10중량% 이하, 백시멘트 30중량% 이하, 프라이트 15중량% 이하를 입도분포가 작고 부드러운 천연 제올라이트 40중량%, 에멜존아크릴레이트 5중량% 이하를 물과 혼합하여 반죽한 후 상기 반죽된 재료를 단위면적을 갖는 성형몰드에 충진하고 경화시켜 이루어진 것을 특징으로 하는 건축물 내, 외장용 인조석 판재.10% by weight or less of powdered volcanic stone with a small particle size distribution, 30% by weight or less with cement, and 15% by weight or less, and 40% by weight of natural zeolite with a small particle size distribution and 5% by weight of emelone acrylate are mixed with water. After kneading by filling the kneaded material in a molding mold having a unit area and hardened in the building, it is an artificial stone plate for building.
KR1020020061991A 2002-10-11 2002-10-11 Method for manufacture of articial stone plate for interior outside a structure KR20040033097A (en)