KR200361680Y1 - A building materials using scrapped wood - Google Patents
A building materials using scrapped wood Download PDFInfo
- Publication number
- KR200361680Y1 KR200361680Y1 KR20-2004-0016604U KR20040016604U KR200361680Y1 KR 200361680 Y1 KR200361680 Y1 KR 200361680Y1 KR 20040016604 U KR20040016604 U KR 20040016604U KR 200361680 Y1 KR200361680 Y1 KR 200361680Y1
- Authority
- KR
- South Korea
- Prior art keywords
- wood
- knots
- flaw
- bonded
- adhesive
- Prior art date
Abstract
본 고안은 폐목재를 적용하여 구성되는 건축자재에 관한 것으로, 상세하게는 슬라이스된 목재의 옹이 및 하자 부위가 분리되어 옹이 및 하자 부위 조각면이 형성되고, 상기 옹이 및 하자 부위 조각면과 옹이 및 하자 부위 조각면이 접착제 재질의 봉합사로 봉합되어 일정한 크기의 목재 단판이 형성되고, 상기 목재 단판이 같은 결로 적층으로 접착되고 일정한 온도와 압력으로 압착되어 목재 다층 보드가 형성되고, 상기 목재 다층 보드의 표면에 기판이 접착 형성되어 종래에 폐기되던 목재인 옹이 및 하자 부위를 활용하여 구성되는 고부가가치의 건축자재에 관한 것이다.The present invention relates to a building material configured by applying waste wood, and in particular, the knots and flaws of sliced wood are separated to form knots and flaw pieces, and the knots and flaw pieces and knots and Fragment of the flaw portion is sutured with an adhesive suture to form a wooden end plate of a certain size, the wooden end plate is bonded by the same condensation lamination and pressed at a constant temperature and pressure to form a wooden multilayer board, The present invention relates to a high value-added building material that is formed by using knots and defects, which are wood that has been conventionally disposed of by adhering to a substrate.
Description
본 고안은 목재가 0.5 ∼ 1 ㎜의 두께로 슬라이스되고 그 옹이 및 하자 부위가 분리되어 옹이 및 하자 부위 조각면이 형성되고, 상기 옹이 및 하자 부위 조각면과 옹이 및 하자 부위 조각면이 접착제 재질의 봉합사로 봉합되어 상호간에 연결되어 일정한 크기의 목재 단판이 형성되고, 상기 목재 단판 다수매가 적층으로 접착되고 일정한 온도와 압력으로 압착되어 목재 다층 보드가 형성되고, 상기 목재 다층 보드의 일 표면에 일정한 두께의 기판이 접착제로 접착 형성되어 구성되며 폐목재인 옹이 및 하자 부위를 활용하여 바닥재, 벽재, 천정재 등과 같은 고부가가치의 건축자재를 제조하므로서 목재 활용 비율을 크게 증가시키는 폐목재를 이용한 건축자재에 관한 것이다.According to the present invention, wood is sliced to a thickness of 0.5 to 1 mm and its knots and flaws are separated to form knots and flaw pieces, and the knots and flaw pieces and knots and flaw pieces are made of adhesive material. It is sutured with a suture and connected to each other to form a wooden end plate of a certain size, a plurality of the wooden end plates are bonded in a stack and pressed at a constant temperature and pressure to form a wooden multilayer board, a constant thickness on one surface of the wooden multilayer board Is constructed by adhesive bonding of substrates, and by using knots and defects, which are waste wood, to manufacture high value-added building materials such as flooring, wall, and ceiling materials, the construction materials using waste wood greatly increase the utilization rate of wood. will be.
벌목된 원목에는 옹이 부위 뿐만 아니라 나무진, 변색, 부패, 훼손, 공동 등의 각종 하자 부위가 많이 존재한다.Logged wood has many defects such as knots, discoloration, decay, damage, and cavities.
따라서, 종래에는 목재 가공 공정에서 목재를 일정한 두께로 슬라이스하고 상기 슬라이스된 목재로부터 옹이 및 하자 부위를 제거하고 남은 부분만을 활용하여 베니어, 합판, 기타 목조 건축자재를 제조하며, 상기 목재 가공 과정에서 제거된 옹이 및 하자 부위는 폐기되거나 땔감으로 활용되기 때문에 원목에 대한 목재의 활용 비율이 평균 35 %에 불과하여 대량의 목재가 낭비되며, 이것은 결국 과다한 목재 소비로 연결된다는 문제점이 있다.Therefore, conventionally, in the wood processing process, the wood is sliced to a certain thickness, the knots and flaws are removed from the sliced wood, and only the remaining parts are used to manufacture veneers, plywood, and other wooden building materials, and the wood processing is removed. Since the knots and defects that have been used are discarded or used as firewood, the use ratio of wood to timber is only 35% on average, which causes a large amount of wood to be wasted, which leads to excessive wood consumption.
본 고안의 목적은 목재가 0.5 ∼ 1 ㎜ 두께로 슬라이스되고 그 옹이 및 하자 부위가 분리되어 옹이 및 하자 부위 조각면이 형성되고, 상기 옹이 및 하자 부위 조각면과 옹이 및 하자 부위 조각면이 접착제 재질의 봉합사로 봉합되어 일정한 크기의 목재 단판이 형성되고, 상기 목재 단판이 같은 결로 적층으로 접착되고 일정한 온도와 압력으로 압착되어 목재 다층 보드가 형성되고, 상기 목재 다층 보드의일 표면에 일정한 두께의 기판이 접착되어 구성되며 폐목재인 옹이 및 하자 부위를 활용하여 건축자재를 형성하는 폐목재를 이용한 건축자재를 제공하는데 있다.The object of the present invention is that the wood is sliced to a thickness of 0.5 ~ 1 mm and its knots and flaws are separated to form the knots and flaw pieces, and the knots and flaw pieces and knots and flaws are adhesive material Sutures of suture is formed to form a wooden veneer of a constant size, the wooden veneers are bonded in the same condensation lamination and pressed at a constant temperature and pressure to form a wooden multilayer board, a substrate of constant thickness on one surface of the wooden multilayer board This is to provide a construction material using the waste wood that is bonded to the construction and using the knot and defect parts of the waste wood to form a building material.
도 1은 목재 단판의 구성도1 is a block diagram of a wooden veneer
도 2는 목재 다층 보드의 구성도2 is a block diagram of a wood multilayer board
도 3은 건축자재의 구성도3 is a block diagram of building materials
도 4는 조각면의 결합도4 is a coupling of the engraving surface
* 도면의 주요 부분에 대한 부호의 설명* Explanation of symbols for the main parts of the drawings
1 : 옹이 및 하자 부위 조각면1: engraving of the knots and defects
2 : 목재 단판2: wood veneer
3 : 목재 다층 보드3: wood multilayer board
4 : 기판4: substrate
5 : 봉합사5: suture
본 고안의 폐목재를 이용한 건축자재는 목재가 0.5 ∼ 1 ㎜의 두께로 슬라이스되고 그 옹이 및 하자 부위가 분리되어 옹이 및 하자 부위 조각면(1)이 형성되고, 상기 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)이 접착제 재질의 봉합사(5)로 봉합되어 상호간에 연결되어 일정한 크기의 목재 단판(2)이 형성되고, 상기 목재 단판(2) 다수매가 같은 결로 적층으로 접착되고 일정한 온도와 압력으로 압착되어 목재 다층 보드(3)가 형성되고, 상기 목재 다층 보드(3)의 일 표면에 일정한 두께의 기판(4)이 접착제로 접착 형성되어 구성되는 특징이 있다.Building materials using the waste wood of the present invention is a wood sliced to a thickness of 0.5 ~ 1 mm and its knots and defects are separated to form the knots and defects engraving surface (1), the knots and defects engraving surface ( 1) and the knots and flaw surface (1) is sealed with a suture (5) made of adhesive material and connected to each other to form a wooden end plate (2) of a constant size, the plurality of wood end plates (2) laminated with the same condensation It is adhered to and compressed at a constant temperature and pressure to form a wood multi-layer board (3), the substrate 4 of a constant thickness on one surface of the wood multi-layer board 3 is characterized in that the adhesive formed by the adhesive.
또한, 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)의 변이 접착제로 접합되어 상호간에 연결되어 일정한 크기의 목재 단판(2)이 구성된다.In addition, the sides of the knot and defect portion engraving surface 1 and the knot and defect portion engraving surface 1 are bonded to each other and connected to each other to form a wooden end plate 2 of constant size.
또한, 서로 다른 수종의 목재 단판(2) 다수매가 접착제로 접착되어 적층되고 일정한 온도와 압력으로 압착되어 목재 다층 보드(3)가 구성된다.In addition, a plurality of different kinds of wood veneer (2) sheets are bonded and laminated with an adhesive and pressed at a constant temperature and pressure to form a wood multilayer board (3).
도 1은 목재 단판의 구성을 도시한 것이고 도 2는 목재 다층 보드의 구성을 도시한 것이고 도 3은 완성된 건축자재의 구성을 도시한 것이고 도 4는 옹이 및 하자 부위 조각면의 결합 구조의 실시예를 도시한 것이다.Figure 1 shows the configuration of the wood veneer, Figure 2 shows the configuration of the wood multilayer board, Figure 3 shows the configuration of the finished building material and Figure 4 shows the implementation of the combined structure of the knots and defects engraving An example is shown.
원목이 1차 가공된 목재가 0.5 ∼ 1 ㎜의 두께로 슬라이스되고, 상기와 같이 슬라이스된 목재로부터 옹이 및 각종 하자가 존재하는 부위가 분리되어 다양한 크기와 형상의 옹이 및 하자 부위 조각면(1)이 형성된다. 목재가 0.5 ㎜ 미만의 두께로 슬라이스되면 슬라이스된 목재 또는 옹이 및 하자 부위 조각면(1)이 훼손되기 쉽고, 1 ㎜를 초과하는 두께로 슬라이스되면 옹이 및 하자 부위 조각면(1)을 접착제 재질의 봉합사로 봉합하는 작업이 곤란해진다.Primary wood is sliced to a thickness of 0.5 ~ 1 mm, and the knots and defects are separated from the wood sliced as described above, the knots and flaws of various sizes and shapes (1) Is formed. If the wood is sliced to a thickness of less than 0.5 mm, the sliced wood or knot and flap piece 1 is likely to be damaged, and if sliced to a thickness greater than 1 mm, the knot and flaw piece 1 is made of adhesive material. The work of suturing with a suture becomes difficult.
상기와 같이 형성된 다양한 크기와 형상의 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)이 봉합사(5)로 봉합되어 상호간에 연결되고, 이러한 과정을 반복하여 일정한 크기의 목재 단판(2)이 형성된다. 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)이 봉합되어 연결되는 봉합사(5)는 접착제 재질로 구성되며, 옹이 및 하자 부위 조각면(1)이 봉합되어 연결되는 접착제 재질의 봉합사(5)는 같은 결로 적층된 목재 단판(2)이 일정 온도와 압력으로 압착되는 과정에서 용융되어 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1) 사이로 침투하여 경화되므로 상기 접착제 재질의 봉합사(5)의 이음 표시가 노출되지 않으며 적층된 목재 다층 보드(3)의 강도가 배가된다.The knots and defects of the various sizes and shapes formed as described above (1) and the knots and defects of the engraving portion (1) are sutured with a suture (5) and connected to each other, repeating this process the wood of a constant size The end plate 2 is formed. The suture 5, in which the knot and defect portion engraving surface 1 and the knot and defect portion engraving surface 1 are sutured and connected, is made of an adhesive material, and the glue that the knot and defect portion engraving surface 1 is sealed and connected to The suture (5) of the material is melted in the process of pressing the laminated wood veneer (2) at the same temperature and pressure to penetrate between the knot and flaw piece (1) and the knot and flaw piece (1) Since it hardens, the joint mark of the suture 5 of the said adhesive material is not exposed, and the strength of the laminated wood multilayer board 3 is doubled.
또는, 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)의 변이 접착제로 접합되어 상호간에 연결되므로서 일정한 크기의 목재 단판(2)이 구성될 수 있다.Alternatively, the knot and defect portion engraving surface 1 and the sides of the knotting and defect portion engraving surface 1 are bonded to each other by an adhesive, and thus, a wooden end plate 2 having a predetermined size may be formed.
상기와 같이 일정한 크기로 봉합된 목재 단판(2) 다수매가 같은 결로 적층으로 접착되고, 적층된 목재 단판(2)이 일정한 온도와 압력으로 압착되어 목재 다층 보드(3)가 형성된다.As described above, a plurality of wood end plates 2 sealed to a constant size are bonded in the same condensation stack, and the laminated wood end plates 2 are compressed at a constant temperature and pressure to form a wood multilayer board 3.
구체적으로, 목재 단판(2)의 표면에 접착제가 일정한 두께로 도포되어 다른 목재 단판(2)이 접착되고, 이러한 과정을 반복하여 다수매의 목재 단판(2)이 같은결로 차례로 적층되며, 적층된 목재 단판(2)이 롤러 사이로 통과되어 일정한 압력과 온도 조건으로 압착되어 목재 다층 보드(3)가 형성된다. 목재 단판(2)의 표면에 도포된 접착제는 같은 결로 적층된 목재 단판(2)을 일정 온도와 압력으로 압착하는 과정에서 용융되어 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)의 변 사이로 침투하여 경화된다.Specifically, an adhesive is applied to the surface of the wood veneer (2) with a certain thickness to bond the other wood veneer (2), and repeating this process, a plurality of wood veneer (2) is sequentially stacked in the same texture, laminated The wood veneer 2 is passed between the rollers and pressed under constant pressure and temperature conditions to form a wood multilayer board 3. The adhesive applied to the surface of the wood veneer (2) is melted in the process of pressing the laminated wood veneer (2) at the same temperature and pressure at a constant temperature and pressure, so that the knot and flaw engraving surface (1) and the knot and flaw engraving surface ( It penetrates between the sides of 1) and hardens.
목재 다층 보드(3)로 적층되는 목재 단판(2)의 수효가 3 매 미만이면 목재 다층 보드(3)의 강도와 내구성의 부족으로 인하여 건축자재로서의 적용이 불가하며, 적층되는 목재 단판(2)의 수효가 11 매를 초과하면 필요 이상의 적층 공정이 발생하여 목재 다층 보드(3)의 제조원가가 상승하여 경제성이 저하된다.If the number of wood veneers 2 laminated by the wood multilayer board 3 is less than three sheets, it cannot be applied as a building material due to the lack of strength and durability of the wood multilayer board 3, and the laminated wood veneer 2 When the number of sheets exceeds 11 sheets, more than necessary lamination processes will occur, resulting in an increase in the manufacturing cost of the wood multilayer board 3, resulting in lower economic efficiency.
선택적으로, 서로 다른 수종의 목재 단판(2) 다수매가 접착제로 접착되어 적층되고 적층된 목재 단판(2)이 일정한 온도와 압력으로 압착되어 목재 다층 보드(3)가 구성될 수 있다. 예를 들면, 참나무의 목재 단판(2)과 박달나무의 목재 단판(2)과 단풍나무의 목재 단판(2)이 교대로 접착되어 적층되고 일정한 온도와 압력으로 압착되어 서로 다른 수종으로 이루어지는 목재 다층 보드(3)가 구성된다.Optionally, a plurality of different kinds of wood veneers 2 may be adhesively laminated and laminated, and the laminated wood veneers 2 may be pressed at a constant temperature and pressure to constitute a wood multilayer board 3. For example, a wood veneer (2) of oak, a wood veneer (2) of birch and a wood veneer (2) of maple are alternately glued together and laminated, compressed to a certain temperature and pressure, and made of different wood varieties. The board 3 is constructed.
상기와 같이 적층 형성된 목재 다층 보드(3)의 일 표면에 일정한 두께의 기판(4)이 접착제로 접착되어 건축자재가 구성하며, 선택적으로 상기 목재 다층 보드(3)의 반대 표면에 장식지 또는 장식 쉬트 또는 무늬목판 등이 접착제로 접착되어 미려한 외관의 건축자재가 구성된다. 상기와 같이 구성된 건축자재는 바닥재, 벽재, 천정재 등과 같이 주로 건축물의 내장재 용도로 사용 가능하다. 이러한 건축자재의 사용 목적과 설치 장소 등에 따라서 목재 다층 보드(3)의 표면에 접착되는 일정한 두께의 기판(4)은 목재, 철, 동, 합금, 합성수지 재질로 다양하게 선택되며, 상기와 같은 재질로 구성된 기판(4)이 목재 다층 보드(3)를 지지한다.As described above, a substrate 4 having a predetermined thickness is bonded to one surface of the laminated multilayer wood board 3 with an adhesive to construct a building material, and optionally, a decorative paper or a decorative sheet on an opposite surface of the wood multilayer board 3. Alternatively, a wooden board or the like is bonded with an adhesive to form a beautiful building material. The building materials configured as described above can be used mainly for interior materials of buildings, such as flooring, walling, and ceiling materials. According to the purpose of use of the building materials and the installation location, the substrate 4 having a predetermined thickness bonded to the surface of the wood multilayer board 3 is variously selected from wood, iron, copper, alloy, synthetic resin, and the like. The board | substrate 4 which consists of these supports the wooden multilayer board 3.
실시예를 참조하여 본 고안을 상세하게 설명하면,Referring to the present invention in detail with reference to the embodiment,
원목을 1차 가공한 목재를 양 방향으로 왕복시키면서 깍아내어 0.5 ㎜의 두께로 슬라이스하고, 상기 슬라이스된 목재로부터 옹이 및 각종 하자가 존재하는 부위를 식별하고, 식별된 옹이 및 하자 부위를 절단기로 분리하여 다양한 크기와 형상의 옹이 및 하자 부위 조각면(1)을 형성한다.The wood is first chopped and chopped wood in both directions, sliced to a thickness of 0.5 mm, and the areas where knots and various defects exist from the sliced wood are identified, and the identified knots and defects are separated by a cutter. To form knots and defects engraving surfaces 1 of various sizes and shapes.
상기 다양한 크기와 형상의 옹이 및 하자 부위 조각면(1)을 적절하게 배열하고, 봉합기를 사용하여 접착제 재질의 봉합사(5)로 봉합하여 상기 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1) 사이를 연결하고, 이러한 봉합 과정을 반복하여 0.5 ㎜ 두께인 사각형의 목재 단판(2)을 형성한다.The knots and defect portion engraving surfaces 1 of various sizes and shapes are appropriately arranged, and sutured with the sutures 5 of an adhesive material using a suture, and the knots and defect portions of the knots and defect portions engraving surface 1 The connection between the pieces 1 is repeated and this suture process is repeated to form a square wood veneer 2 of 0.5 mm thickness.
상기 목재 단판(2)의 표면에 목재 가공용 친환경적 멜라민 접착제를 0.1 ㎜의 두께로 도포하고 도포된 접착제층에 다른 목재 단판(2)을 대면하여 접착하고, 이러한 과정을 반복하여 9 매의 목재 단판(2)을 같은 결로 차례로 적층하며, 적층된 목재 단판(2)을 2 개의 롤러 사이로 통과시켜서 압착하여 9 층의 목재 다층 보드(3)를 형성한다. 선택적으로, 상기 목재 다층 보드(3)를 절단기로 절단하여 일정한 크기와 형태로 분할한다.Applying the eco-friendly melamine adhesive for wood processing to the surface of the wood veneer (2) to a thickness of 0.1 mm and bonding the other wood veneer (2) face to face to the applied adhesive layer, and repeat this process to nine wood veneers ( 2) are laminated in sequence with the same condensation, and the laminated wood veneer 2 is passed through two rollers to be pressed to form a nine-layer wood multilayer board 3. Optionally, the wood multilayer board 3 is cut with a cutter and divided into a predetermined size and shape.
상기 목재 다층 보드(3)의 일 표면에 접착제를 도포하고 동 재질의 기판(4)을 접착하여 바닥재인 건축자재를 완성한다.An adhesive is applied to one surface of the wood multilayer board 3 and the substrate 4 of the same material is bonded to complete a building material as a flooring material.
상기 완성된 바닥재를 건축물의 실내 바닥에 차례로 배설하여 시공하며, 이때 상기 건축 자재의 기판(4)을 바닥에 대면하도록 접착하여 지하의 수맥파가 차단되는 마루 바닥을 완공한다.The completed flooring materials are sequentially disposed on the indoor floor of the building, and at this time, the substrate 4 of the building material is bonded to face the floor, thereby completing the flooring floor in which the submerged water waves are blocked.
상기와 같이 실시예를 참조하여 본 고안의 폐목재를 이용한 건축자재의 제조 방법을 상세하게 설명하였으나, 본 고안의 구성 및 기술사상은 상기한 실시예에 의해 한정되지 않으며, 옹이 및 하자 부위 조각면(1)의 두께, 목재 단판(2)으로 봉합되는 옹이 및 하자 부위 조각면(1)의 배치, 적층되는 목재 단판(2)의 수효, 압착 과정에서 적용되는 온도 및 압력 등과 같은 본 고안의 구체적인 실시 과정은 당업자에 의해 실용신안청구범위에 기재된 내용이나 기술사상을 벗어나지 않는 범위 내에서 다양하게 수정하거나 변경시킬 수 있다.Although the manufacturing method of the building material using the waste wood of the present invention was described in detail with reference to the embodiment as described above, the construction and technical spirit of the present invention are not limited to the above-described embodiment, and the knots and flaw surface engraving Specific thickness of the present invention, such as the thickness of (1), the knots and defects enclosed with the wood veneer (2), the surface of the engraving surface (1), the number of laminated wood veneer (2), the temperature and pressure applied in the pressing process, etc. The implementation process may be variously modified or changed by those skilled in the art without departing from the contents or technical spirit described in the utility model claims.
본 고안에서는 일정한 두께로 슬라이스된 목재로부터 옹이가 존재하는 부위를 분리하여 형성되는 옹이 및 하자 부위 조각면(1)을 적용하여 고부가가치의 건축자재를 구성하므로 종래에 폐기되거나 땔감으로 사용되던 목재의 옹이 및 하자 부위를 활용할 수 있기 때문에 원목에 대한 목재의 활용 비율이 종래의 평균 35 %에서 70 %로 크게 증가된다.In the present invention, a high value-added building material is applied by applying the knots and flaw pieces (1) formed by separating the knots existing from the wood sliced to a certain thickness so that the knots of the wood that have been discarded or used in the prior art The availability of knots and defects greatly increases the utilization of wood to timber from 70% to 35% on average.
또한, 목재 단판(2)이 적층되어 목재 다층 보드(3)가 구성되므로 설치된 건축자재의 표면, 즉 목재 다층 보드(3)의 최상층이 훼손되는 경우에는 상기 훼손된 최상층의 목재 단판(2)을 그라인더로 용이하게 깍아내고 그 하부층의 목재 단판(2)을 노출시키므로서 상기 건축자재를 연속적으로 활용하기 때문에 건축자재의 수명을 건축물의 수명과 동일하게 연장시킬 수 있으며, 특히 목재 다층 보드(3)가 서로 다른 수종의 목재 단판(2)으로 접착 구성되는 경우에는 최상층의 목재 단판(2)을깍아내면 다른 수종의 목재 단판(2)이 노출되어 새로운 무늬와 분위기의 건축자재를 연출할 수 있다.In addition, when the wood veneer (2) is laminated to constitute a wood multi-layer board (3), when the surface of the installed building material, that is, the top layer of the wood multi-layer board (3) is damaged, the damaged top layer of wood veneer (2) is grindered. It is possible to extend the life of the building material to the same as the life of the building because the building material is continuously utilized by easily cutting off the wood and exposing the wooden veneer 2 of the lower layer. When the adhesive consists of different kinds of wood veneer (2), by cutting off the wood veneer (2) of the uppermost layer, the other wood veneer (2) can be exposed to produce a new pattern and building materials.
본 고안에 의한 폐목재를 이용한 건축자재는 슬라이스된 목재의 옹이 및 하자 부위가 분리되어 옹이 및 하자 부위 조각면가 형성되고, 상기 옹이 및 하자 부위 조각면과 옹이 및 하자 부위 조각면이 접착제 재질의 봉합사로 봉합되어 목재 단판이 형성되고, 상기 목재 단판이 적층되고 압착되어 목재 다층 보드가 형성되고, 상기 목재 다층 보드의 표면에 기판이 접착되어 구성되어 종래에는 폐기되던 목재의 옹이 및 하자 부위를 활용하여 바닥재, 벽재, 천정재 등과 같은 고부가가치의 건축자재를 제조하므로서 원목에 대한 목재 활용 비율을 배가하고 원목 소비를 억제하는 효과가 있다.Building materials using waste wood according to the present invention is the knot and flaw portion of the sliced wood is separated to form the knot and flaw portion fragments, the knot and flaw portion fragments and the knots and flaw portion fragments of the adhesive material suture It is sealed to form a wood veneer, the wood veneer is laminated and compressed to form a wood multi-layer board, the substrate is bonded to the surface of the wood multi-layer board by using the knots and defects of the conventionally discarded wood By manufacturing high value-added building materials such as flooring, walling and ceiling materials, it has the effect of doubling the ratio of wood to wood and suppressing the consumption of wood.
Claims (3)