KR200338568Y1 - a lightweight pannel for building - Google Patents
a lightweight pannel for building Download PDFInfo
- Publication number
- KR200338568Y1 KR200338568Y1 KR20-2003-0032671U KR20030032671U KR200338568Y1 KR 200338568 Y1 KR200338568 Y1 KR 200338568Y1 KR 20030032671 U KR20030032671 U KR 20030032671U KR 200338568 Y1 KR200338568 Y1 KR 200338568Y1
- Authority
- KR
- South Korea
- Prior art keywords
- mixture
- cement
- water
- upper layer
- sand
- Prior art date
Abstract
본 고안은 건축용 경량 마감재에 관한 것으로,The present invention relates to a lightweight finishing material for construction,
건축용 경량 마감재를 구성함에 있어서,In constructing lightweight finishing materials for construction,
모래, 시멘트, 물, 내알카리성 유리섬유의 혼합물을 소정시간 양생시켜 이루어진 하부층과,A lower layer formed by curing a mixture of sand, cement, water, and alkali-resistant glass fibers for a predetermined time;
상기 하부층 상단에 세모래, 시멘트, 물, 고강도 시멘트 혼화제, 인조석, 안료의 혼합물에 소정길이 철강선이 매설한 후 이를 소정시간 양생시켜 이루어진 상부층으로 이루어지는 한편,While the upper layer is made of a predetermined length steel wire embedded in a mixture of fine sand, cement, water, high-strength cement admixture, artificial stone, pigment on top of the lower layer, and curing it for a predetermined time,
상기 상부층에 백시멘트, 축광 및 형광제, 세모래, 물의 혼합물이 양생되어진 발광부재와 백시멘트, 세모래, 물, 안료의 혼합물로 이루어지되 상부층과 차별되는 색으로 착색되어진 무늬부재를 포함하여서 이루어지는 것을 특징으로 하는 본 고안에 의하면,The upper layer includes a light emitting member having a mixture of white cement, a photoluminescent and fluorescent agent, three sand, and water, and a pattern member having a mixture of white cement, three sand, water, and pigment, and colored in a color different from that of the upper layer. According to the present invention characterized in that,
외관이 미려하여 보는 이로 하여금 색다른 심미감을 불러일으키게 되고,The beautiful appearance gives the viewer a different aesthetic,
가벼우면서도 내구성이 우수하여 작업의 편의성이 향상되어질 뿐 아니라 제품 수명을 장기간 유지할 수 있는 효과를 얻을 수 있으며,It is light and durable, which not only improves the convenience of work but also has the effect of long-term product life.
화재 또는 각종 사고 현장에서 인명피해를 줄이는 효과를 얻을 수 있게 되는 것이다.It is possible to obtain the effect of reducing the casualty at fire or various accident sites.
Description
본 고안은 건축용 경량 마감재에 관한 것으로, 더욱 상세하게는 외관이 미려하고, 내구성이 우수할 뿐 아니라 공사기간을 단축시킬 수 있고 공사비를 절감할 수 있으며,The present invention relates to a lightweight finishing material for construction, more specifically, beautiful appearance, excellent durability, can shorten the construction period and reduce construction costs,
특히 화재 및 빛이 없는 사고 현장에서 인명피해를 최소할 수 있도록 한 건축용 경량 마감재에 관한 것이다.In particular, the present invention relates to a lightweight finishing material for construction that can minimize casualties at an accident site without fire and light.
기존 건축용 마감재의 대다수는 습식공법에 의해 제작되므로 환경오염의 원인이 될 뿐 아니라 시멘트 또는 자연석을 사용하고 있어 건축물을 들여다보았을 때 보는 이로 하여금 삭막한 느낌을 갖게 하므로 보다 화려하고 아름다운 시각적 효과를 기대하는 현대인들을 기호를 만족시키지 못하게 되는 문제가 있었다.Most of the existing building finishing materials are manufactured by wet method, so it is not only a cause of environmental pollution, but also using cement or natural stone. There was a problem of not satisfying the taste.
또한, 기존의 마감재는 중량이 무거워서 시공할 때 많은 인력을 필요로 하기 때문에 공사경비 상승의 주 요인이 되고, 공사 일정이 더디게 진행 될 뿐 아니라,In addition, the existing finishing materials are heavy and require a lot of manpower when constructing them, which is a major factor in the increase of construction cost, and not only the construction schedule is slow,
마감처리 외에 별도의 기능을 기대할 수 없는 문제가 있었다.There was a problem that can not expect a separate function in addition to finishing.
한편, 최근에는 보다 경량의 마감재를 생산하기 위하여 합성수지로 이루어진 마감재가 일부 개발되었으나 이는 생산 단가가 높아 공사비가 많이 소요되고,On the other hand, in order to produce lighter finishes in recent years, some finishes made of synthetic resins have been developed, but the production cost is high, which requires a lot of construction costs.
시공 후 햇빛에 의해 변색되는 경우가 있었으며,There was a case of discoloration by sunlight after the construction,
건축물에 설치된 이후에 기온 차에 의해 변형되어 마감재로서의 역할을 충족시키지 못하게 되는 문제가 있었을 뿐 아니라,Not only was there a problem that after being installed in the building, it was deformed by the temperature difference and could not fulfill its role as a finishing material.
사고에 의해 화재가 발생했을 경우 쉽게 연소되고, 연소 중에 유독가스가 발생되므로 대규모의 인명피해를 일으키게 되는 문제가 있었다.When a fire occurs by accident, it is easily burned, and toxic gas is generated during combustion, which causes a large-scale human injury.
본 고안은 상기와 같은 실정을 감안하여 안출한 것으로 그 외관이 미려하여 보는 이로 하여금 색다른 심미감을 불러일으킬 수 있고,The present invention has been devised in view of the above situation, and its appearance is beautiful and can cause viewers to have a different aesthetics.
내구성과 작업의 편의성이 우수하여 제품 수명 연장과 더불어 공정 단축 및 비용 절감의 효과를 얻을 수 있으며,Its durability and ease of operation make it possible to prolong product life, shorten processes and reduce costs.
화재 및 기타 사고 현장에서 인명피해를 최소할 할 수 있도록 한 건축용 경량 마감재를 제공하는데 그 목적이 있는 것이다.Its purpose is to provide a lightweight construction finish for construction that minimizes casualties at fire and other accident sites.
도 1은 본 고안의 사시도1 is a perspective view of the present invention
도 2는 본 고안의 단면도2 is a cross-sectional view of the present invention
도 3은 본 고안의 성형 단계를 설명하기 위한 단면도Figure 3 is a cross-sectional view for explaining the molding step of the subject innovation
도 4는 본 고안의 다른 형태를 도시한 사시도4 is a perspective view showing another embodiment of the present invention
<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>
100 : 경량 마감재 110 : 하부층100: lightweight finish 110: lower layer
120 : 상부층 121 : 철강선120: upper layer 121: steel wire
130 : 발광부재 140 : 무늬부재130: light emitting member 140: pattern member
150 : 성형틀150: forming mold
본 고안은 상술한 바와 같은 목적을 달성하기 위한 건축용 경량 마감재(100)를 구성함에 있어서,The present invention is to construct a lightweight finishing material for construction 100 to achieve the object as described above,
모래, 시멘트, 물, 내알카리성 유리섬유의 혼합물을 소정시간 양생시켜 이루어진 하부층(110)과,A lower layer 110 formed by curing a mixture of sand, cement, water, and alkali-resistant glass fibers for a predetermined time;
상기 하부층(110) 상단에 세모래, 시멘트, 물, 고강도 시멘트 혼화제, 인조석, 안료의 혼합물에 소정길이 철강선(121)을 매설한 후 이를 소정시간 양생시켜 이루어진 상부층(120)으로 이루어지는 한편,On the top of the lower layer 110 consists of an upper layer 120 formed by burying a predetermined length steel wire 121 in a mixture of fine sand, cement, water, high-strength cement admixture, artificial stone, pigment, and curing it for a predetermined time,
상기 상부층(120)에 백시멘트, 축광제 및 형광제, 세모래, 물의 혼합물이 별도 성형틀에서 성형되고 소정시간 양생되어진 별도의 발광부재(130)와 백시멘트, 세모래, 물, 안료의 혼합물로 이루어지되 상부층과 차별되는 색으로 착색되어진 무늬부재(140)를 포함하여서 이루어지는 것을 특징으로 하며,A mixture of a white cement, a photoluminescent agent and a fluorescent agent, three sand, and water is formed in a separate molding frame and cured for a predetermined time in the upper layer 120, and a mixture of white cement, three sand, water, and pigment. It is made of a characterized in that it comprises a pattern member 140, which is colored in a color different from the upper layer,
이하 그 구체적인 기술내용을 첨부 도면에 의거하여 더욱 상세히 설명하면 다음과 같다.Hereinafter, the specific technical details will be described in detail with reference to the accompanying drawings.
본 고안에 의한 마감재(100)는 도 1 및 도 2에 도시되어진 바와 같이 크게 하부층(110), 상부층(120), 발광부재(130), 무늬부재(140)로 구성되는데,Finishing material 100 according to the present invention is composed of a lower layer 110, an upper layer 120, a light emitting member 130, a pattern member 140, as shown in Figure 1 and 2,
상기 하부층(110)은 모래, 시멘트, 물, 내알카리성 유리섬유의 혼합물로 이루어진 것이고,The lower layer 110 is made of a mixture of sand, cement, water, alkali-resistant glass fibers,
상기 상부층(120)은 세모래, 시멘트, 물, 고강도 시멘트 혼화제, 인조석, 안료의 혼합물로 이루어진 것이며,The upper layer 120 is made of a mixture of fine sand, cement, water, high strength cement admixture, artificial stone, pigment,
상기 발광부재(130)는 백시멘트, 축광제 및 형광제, 세모래, 물의 혼합물로 이루어진 것이고,The light emitting member 130 is made of a mixture of white cement, photoluminescent agent and fluorescent agent, three sand, water,
상기 무늬부재(140)는 백시멘트, 세모래, 물, 안료의 혼합물로 이루어진 것이다.The pattern member 140 is made of a mixture of white cement, fine sand, water, pigment.
한편, 상기와 같이 하부층(110), 상부층(120), 발광부재(130), 마감부재(140)로 이루어진 마감재(100)를 제조하기 위해서는On the other hand, in order to manufacture a finish 100 consisting of the lower layer 110, the upper layer 120, the light emitting member 130, the finishing member 140 as described above
먼저 도 3a에 도시되어진 바와 같이 일정형태의 성형틀(150) 바닥 특정 위치에 발광부재(130)와 무늬부재(140)를 위치시킨 후,First, as shown in FIG. 3a, the light emitting member 130 and the pattern member 140 are positioned at a specific position of the bottom of the molding die 150 of a predetermined shape.
도 3b에 도시되어진 바와 같이 제2 혼합단계(42)에 의해 얻어진 혼합물을 소정량 충전하여 마감재(100)의 상부층(120)을 형성하며,As shown in FIG. 3B, the mixture obtained by the second mixing step 42 is filled in a predetermined amount to form the upper layer 120 of the finishing material 100.
도 3c에 도시되어진 바와 같이 제2 혼합단계(42)에 의한 혼합물의 퇴적층 상면의 제1 혼합단계(41)에 의해 얻어진 혼합물을 소정 두께로 충전하여 마감재(100)의 하부층(110)을 형성하게 되는 것이다.As shown in FIG. 3C, the mixture obtained by the first mixing step 41 of the upper surface of the deposition layer of the mixture by the second mixing step 42 is filled to a predetermined thickness to form the lower layer 110 of the finishing material 100. Will be.
이때, 상부층(120)을 형성하기 위한 혼합물을 성형틀(150)에 담을 때 상기 혼합물 내부에 소정길이의 철강선(121)을 매설하게 되는데 이를 통해 제품의 압축강도 및 휨 강도를 보강할 수 있게 되며,At this time, when the mixture for forming the upper layer 120 is contained in the mold 150, the steel wire 121 of a predetermined length is embedded in the mixture, thereby reinforcing the compressive strength and the bending strength of the product. ,
상부층(120)에서 발광부재(130), 무늬부재(140) 주변은 성형이 매끄럽지 않을 수 있으므로 제품 연마 단계(90)에서는 이점을 고려하여 연마작업을 진행하는것이 바람직하다.Since the molding may not be smooth around the light emitting member 130 and the pattern member 140 in the upper layer 120, it is preferable to proceed with the polishing operation in consideration of the advantage in the product polishing step 90.
상술한 바와 같이 이루어진 본 고안은 고강도 시멘트 혼화제, 철강선(121) 등을 포함하고 있어 고도의 압축강도 및 휨 강도를 유지할 수 있게 되고,The present invention made as described above includes a high strength cement admixture, steel wire 121 and the like, it is possible to maintain a high compressive strength and bending strength,
내알카리성 유리섬유를 포함하고 있어 경량이면서도 충격, 균열에 관한 저항성 및 인성이 극대화되어질 뿐 아니라,It contains alkali-resistant glass fiber, which maximizes resistance to light and impact and cracks,
축광제 및 형광제를 포함하고 있는 발광부재(130)가 화재, 정전과 같은 사고시 사고현장에 있는 사람들에게 길을 안내할 수 있게 되므로 인명피해를 최소화할 수 있도록 하며,The light emitting member 130 including the photoluminescent agent and the fluorescent agent can guide the way to the people at the accident site in case of an accident such as fire or power failure, thereby minimizing human injury.
제품 상부층(120) 전체에 안료가 착색되어 있고 이와 차별되는 색상으로 이루어진 무늬부재(140)가 구비되어 있어 자체에 보다 화려하고 아름다운 시각적 효과를 전달할 수 있게 되므로 보는 이로 하여금 색다른 심미감을 불러일으킬 수 있게 된다.Pigment is colored in the entire upper layer 120, and the pattern member 140 is made of a color that is different from the other is provided so that it can deliver a more colorful and beautiful visual effect to the viewer to induce a different aesthetic do.
한편, 본 고안에서는 마감재(100) 형태를 평판형으로 도시하였으나 이는 응용 가능한 범위 안에서 자유롭게 변형되어질 수 있으므로 도 4에 도시되어진 바와 같이 마감재(100) 형태를 "ㄱ"자 형태로 하여 계단용 패널 등으로 사용할 수 있고, 이때 발광부재(130)의 형태 또한 자유롭게 변형 가능하며, 계단용 패널의 경우 그 상면에 논슬립 홈(100a)을 형성하는 것이 바람직하다.Meanwhile, in the present invention, the shape of the finishing material 100 is shown as a flat plate, but since it may be freely deformed within the applicable range, the finishing material 100 is shown in FIG. In this case, the shape of the light emitting member 130 is also freely deformable, in the case of the staircase panel, it is preferable to form a non-slip groove (100a) on the upper surface.
상술한 바와 같이 본 고안은 건축용 경량 마감재를 구성함에 있어서,As described above, the subject innovation in constructing a lightweight finishing material for construction,
모래, 시멘트, 물, 내알카리성 유리섬유의 혼합물을 소정시간 양생시켜 이루어진 하부층과,A lower layer formed by curing a mixture of sand, cement, water, and alkali-resistant glass fibers for a predetermined time;
상기 하부층 상단에 세모래, 시멘트, 물, 고강도 시멘트 혼화제, 인조석, 안료의 혼합물에 소정길이 철강선이 매설한 후 이를 소정시간 양생시켜 이루어진 상부층으로 이루어지는 한편,While the upper layer is made of a predetermined length steel wire embedded in a mixture of fine sand, cement, water, high-strength cement admixture, artificial stone, pigment on top of the lower layer, and curing it for a predetermined time,
상기 상부층에 백시멘트, 축광제 및 형광제, 세모래, 물의 혼합물이 양생되어진 발광부재와 백시멘트, 세모래, 물, 안료의 혼합물로 이루어진 무늬부재를 포함하여서 이루어진 것으로,The upper layer includes a light emitting member having a mixture of white cement, a photoluminescent agent and a fluorescent agent, three sand, and water, and a pattern member composed of a mixture of white cement, three sand, water, and pigment,
제품 외관이 미려하여 보는 이로 하여금 색다른 심미감을 불러일으킬 수 있게되고,The beautiful appearance of the product makes it possible for viewers to evoke a different aesthetic.
내구성과 작업의 편의성이 우수하여 제품 수명이 장기간 유지될 뿐 아니라 공기 단축 및 공사비용 절감의 효과를 얻을 수 있게되며,Its durability and ease of operation make it possible to maintain product life for a long time, and to reduce air and reduce construction costs.
화재 및 기타 사고 현장에서 인명피해를 최소화하는 효과를 얻을 수 있게 되는 것이다.Minimizing human injury at fire and other accident sites can be achieved.
Claims (3)