KR20030006944A - High-performance accessories radiating a lot of negative ions and method for manufacturing the same - Google Patents
High-performance accessories radiating a lot of negative ions and method for manufacturing the same Download PDFInfo
- Publication number
- KR20030006944A KR20030006944A KR1020020021690A KR20020021690A KR20030006944A KR 20030006944 A KR20030006944 A KR 20030006944A KR 1020020021690 A KR1020020021690 A KR 1020020021690A KR 20020021690 A KR20020021690 A KR 20020021690A KR 20030006944 A KR20030006944 A KR 20030006944A
- Authority
- KR
- South Korea
- Prior art keywords
- plating layer
- silver
- mixed
- cyanide
- plating
- Prior art date
Abstract
Description
본 발명은 다량의 음이온을 방출하는 고기능 장신구 및 그 제조방법에 관한 것으로, 보다 구체적으로는 유산동 도금층 위에 희토류금속과 은의 혼합물을 도금한 혼합도금층을 형성하고 그 위에 귀금속을 도금함으로써 음이온을 다량 방출하여 혈액 정화, 세포 활성화, 면역력 증가, 신경안정, 호흡기 및 장기 향상, 피로감 경감 등의 효과를 얻을 수 있도록 한 다량의 음이온을 방출하는 고기능 장신구 및 그 제조방법에 관한 것이다.The present invention relates to a high-performance jewelry that emits a large amount of anions and a method for manufacturing the same, and more specifically, to form a mixed plating layer of a mixture of rare earth metal and silver on the lactic copper plating layer and to release a large amount of anions by plating precious metal thereon. The present invention relates to high-performance jewelry that emits a large amount of anions to obtain effects such as blood purification, cell activation, increased immunity, nerve stability, respiratory and organ improvement, and fatigue reduction, and a method of manufacturing the same.
종래의 목걸이, 팔찌, 귀걸이, 반지, 브로치 등의 장신구나 시계, 거울, 상패 등의 장식품은 표면을 아름답게 하고, 부식되지 않도록 제품의 표면에 도금처리를 하였다.Traditional ornaments such as necklaces, bracelets, earrings, rings, brooches, and ornaments such as watches, mirrors, and plaques are beautifully surfaced and plated on the surface of the product to prevent corrosion.
그러나 종래의 장신구 및 장식품은 표면에서 음이온이 발생되지 않기 때문에 사용자의 면역력 향상, 정신안정, 몸의 기능향상, 노폐물의 배출, 호흡기의 기능향상, 피로감의 경감 등의 효과가 없었다.However, since the conventional ornaments and ornaments do not generate negative ions from the surface, there is no effect of improving the user's immunity, mental stability, body function, discharge of waste, respiratory function, and fatigue.
또한, 음이온을 발생하여도 그 발생량이 극히 적기 때문에 충분한 효과를 얻을 수 없다는 문제점이 있었다.In addition, even if anions are generated, the amount of generation thereof is extremely small, and there is a problem in that sufficient effects cannot be obtained.
아울러, 유산동 도금층 위에 금이나 백금과 같은 귀금속을 추가로 도금하기도 하는데, 이때 귀금속 도금층의 변색이 빠르게 일어나고, 내식성이 좋지 않는 문제점이 있었다.In addition, the plating of the noble metal, such as gold or platinum on the lactic acid copper plating layer additionally, there is a problem that the discoloration of the precious metal plating layer occurs quickly, the corrosion resistance is not good.
따라서, 음이온 방출에 대한 연구가 지속적으로 이루어져 왔고, 그에 대한 결과물이 본 발명자들에 의해 얻어지게 되었다.Thus, research on anion release has been made continuously, and the result thereof has been obtained by the present inventors.
따라서, 본 발명의 목적은 상기한 문제점을 해결하기 위해 안출된 것으로서, 다량의 음이온을 방출함으로써 혈액정화, 세포 활성화, 면역력 증가, 신경안정, 호흡기 및 장기 향상, 및 피로감 경감등의 신체적인 효능을 얻을 수 있도록 한 다량의 음이온을 방출하는 고기능 장신구 및 그 제조방법을 제공하는 데 있다.Accordingly, an object of the present invention is to solve the above problems, by releasing a large amount of negative ions to improve the physical efficacy of blood purification, cell activation, increased immunity, neurostable, respiratory and organ improvement, and fatigue reduction It is to provide a high-performance jewelry that emits a large amount of negative ions to obtain and a method of manufacturing the same.
본 발명의 다른 목적은 귀금속 도금층의 변색을 방지하고 제품의 내식성을 우수하게 할 수 있도록 한 다량의 음이온을 방출하는 고기능 장신구 및 그 제조방법을 제공하는 데 있다.Another object of the present invention is to provide a high-performance jewelry and a manufacturing method for releasing a large amount of anions to prevent discoloration of the precious metal plating layer and to improve the corrosion resistance of the product.
본 발명의 또 다른 목적은 귀금속 도금층의 두께와 표면을 균일하게 하여 제품의 생산성을 크게 향상시키고, 음이온을 방출하는 제품을 용이하게 제조하며, 그 생산비용을 저렴하게 할 수 있도록 한 다량의 음이온을 방출하는 고기능 장신구 및 그 제조방법을 제공하는 데 있다.Another object of the present invention is to increase the productivity of the product by uniformly the thickness and surface of the noble metal plating layer, to easily produce a product that emits anions, and to produce a large amount of anions to make the production cost low The present invention provides a high-performance releasing ornament and a method of manufacturing the same.
도 1은 본 발명의 일 실시예에 따라 제조된 장신구의 일예를 도시한 사시도.1 is a perspective view showing an example of ornaments manufactured according to an embodiment of the present invention.
도 2는 도 1의 장신구의 A-A선을 따른 단면도.2 is a cross-sectional view taken along the line A-A of the ornament of FIG.
도 3은 본 발명의 다른 실시예에 따른 장신구의 단면도.3 is a sectional view of the ornament according to another embodiment of the present invention.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
10 : 성형체20 : 청화도금층10: molded body 20: cyanized plating layer
30, 30a : 유산동 도금층40, 40a : 혼합도금층30, 30a: copper lactic acid plating layer 40, 40a: mixed plating layer
50 : 귀금속 도금층50: precious metal plating layer
상기와 같은 목적을 달성하기 위하여, 본 발명의 일실시예에 따른 다량의 음이온을 방출하는 고기능 장신구는 금속, 세라믹스 또는 고분자 재료 등으로 제조된 성형체, 상기 성형체의 상부에 청화은, 청화카리, 탄산카리 및 광택제 등의 혼합액을 이용하여 전처리도금으로 형성된 청화도금층, 상기 청화도금층의 상부에 황산, 황산동, 염산 및 광택제 등의 혼합액을 이용하여 형성된 유산동 도금층, 상기 유산동 도금층의 상부에 희토류 금속과 은의 혼합액을 이용하여 형성된 혼합도금층, 및 상기 혼합도금층의 상부에 금, 백금, 은, 또는 로듐 등의 귀금속 액을 이용하여 형성된 귀금속 도금층을 포함한다.In order to achieve the above object, the high-function ornaments releasing a large amount of negative ions according to an embodiment of the present invention is a molded body made of metal, ceramics or polymer material, etc., cyanide silver, cyanide, carbonate And a cyanide plated layer formed by pretreatment plating using a mixed solution such as a brightener, a copper lactate plated layer formed by using a mixed solution of sulfuric acid, copper sulfate, hydrochloric acid, and a brightener on top of the blueprinted layer, and a mixed solution of rare earth metals and silver on top of the lactic acid copper plated layer. Mixed plating layer formed by using, and a precious metal plating layer formed by using a noble metal liquid such as gold, platinum, silver, rhodium on the mixed plating layer.
본 발명의 다른 실시예에 따른 다량의 음이온을 방출하는 고기능 장신구는 금속, 세라믹스 또는 고분자 재료 등으로 제조된 성형체, 상기 성형체의 상부에 청화은, 청화카리, 탄산카리 및 광택제 등의 혼합액을 이용하여 전처리도금으로 형성된 청화도금층, 상기 청화도금층의 상부에 황산, 황산동, 염산 및 광택제 등의 혼합액을 이용하여 형성된 유산동 도금층, 상기 유산동 도금층의 상부에 희토류 금속과 은의 혼합액을 이용하여 형성된 혼합도금층, 상기 혼합도금층의 상부에 재 도금된 유산동 도금층, 상기 유산동 도금층의 상부에 재 도금된 희토류 금속과 은의 혼합도금층, 및 상기 혼합도금층의 상부에 금, 백금, 은, 또는 로듐 등의 귀금속 액을 이용하여 형성된 귀금속 도금층을 포함한다.According to another embodiment of the present invention, a high-performance trinket that emits a large amount of anions is a preform using a molded body made of metal, ceramics, or a polymeric material, and the like, and a mixed liquid of cyanide silver, cyanide, carbonate, and polish, on top of the molded body. Blue plating layer formed by plating, a copper lactate layer formed by using a mixture of sulfuric acid, copper sulfate, hydrochloric acid, and a brightening agent on the upper portion of the blue water plating layer, a mixed plating layer formed by using a mixed solution of rare earth metal and silver on the upper portion of the lactate copper plating layer, the mixed plating layer A copper plated lactate plated layer re-plated on the upper portion, a mixed plating layer of rare earth metal and silver replated on the upper portion of the lactate copper plated layer, and a precious metal plated layer formed by using a precious metal liquid such as gold, platinum, silver, or rhodium on the mixed plated layer. It includes.
이때, 상기 희토류 금속은 란탄늄, 세륨 및 그들의 혼합물 중 선택된 어느 하나이다.In this case, the rare earth metal is any one selected from lanthanum, cerium, and mixtures thereof.
본 발명에 따른 다량의 음이온을 방출하는 고기능 장신구의 제조방법은 금속, 세라믹스, 고분자 재료를 이용하여 성형체를 제조하는 단계; 상기 성형체로부터 이물질을 제거하기 위하여 황산과 염산의 수용액을 이용하여 상온에서 상기 성형체를 전처리하는 단계; 상기 성형체에 청화은, 청화카리, 탄산카리 및 광택제 등의 혼합액을 이용하여 상온에서 1∼10분 동안 도금하여 0.1∼5.0㎛의 청화도금층을 형성하는 단계; 상기 청화도금층 상부에 50∼100g/l 황산, 100∼300g/l 황산동, 0.5∼2g/l 염산 및 0.5∼1.5g/l 광택제 등의 혼합액을 이용하여 15∼30℃에서 30∼120분 동안 도금하여 1∼30㎛의 유산동 도금층을 형성하는 단계; 상기 유산동도금층 상부에 희토류 금속 분말과 은의 혼합도금액을 이용하여 1.0∼6.0 A/cm2의 전류밀도에서 10∼120분 동안 도금하여 0.5∼20㎛의 희토류 금속과 은의 혼합도금층을 형성하는 단계; 및 상기 혼합도금층의 상부에 귀금속 액을 이용하여 0.1∼10㎛의 귀금속 도금층을 형성하는 단계를 포함한다.According to the present invention, there is provided a method of manufacturing high-performance jewelry that emits large amounts of anions, the method comprising: preparing a molded body using metal, ceramics, and polymer material; Pretreating the molded body at room temperature using an aqueous solution of sulfuric acid and hydrochloric acid to remove foreign substances from the molded body; The cyanide is formed on the molded body by plating for 1 to 10 minutes at room temperature using a mixed solution of cyanide, carbonate and polish, to form a cyanide plating layer of 0.1 to 5.0 μm; Plating on the clarified plating layer for 30 to 120 minutes at 15 to 30 ℃ using a mixture of 50 to 100 g / l sulfuric acid, 100 to 300 g / l copper sulfate, 0.5 to 2 g / l hydrochloric acid and 0.5 to 1.5 g / l varnish To form a lactic acid copper plating layer of 1 to 30㎛; Forming a mixed plating layer of the rare earth metal and the silver of about 0.5 to 20 μm by plating for 10 to 120 minutes at a current density of 1.0 to 6.0 A / cm 2 using a mixed plating solution of the rare earth metal powder and silver on the lactic acid copper plating layer; And forming a precious metal plating layer having a thickness of 0.1 to 10 μm using the noble metal liquid on the mixed plating layer.
또한, 상기 혼합도금층 형성단계와 귀금속 도금층 형성단계 사이에, 유산동 도금층과 희토류금속과 은의 혼합도금층을 순차적으로 형성하는 단계를 더 포함하는 것을 특징으로 한다.The method may further include sequentially forming the mixed copper plating layer, the mixed plating layer of the rare earth metal, and the silver sequentially between the mixed plating layer forming step and the precious metal plating layer forming step.
이하, 도면을 참조하여 본 발명에 따른 다량의 음이온을 방출하는 고기능 장신구 및 그 제조방법에 대해 상세히 설명한다.Hereinafter, with reference to the drawings will be described in detail with respect to the high-function ornaments for releasing a large amount of anions according to the present invention and a method of manufacturing the same.
본 발명에 따른 음이온 방출 장신구의 주된 특징은 유산동 도금층 위에 희토류 금속과 은의 혼합물이 도금된 혼합도금층을 형성하고, 그 혼합도금층 위에 금, 백금, 은 또는 로듐 등의 귀금속 도금층을 형성하여 제조하는 것으로, 그렇게 제조한 제품은 희토류 금속을 음이온 방출재료로 사용하였고 희토류금속과 은의 혼합도금층을 하지층으로 하였기 때문에 다량의 음이온을 방출하게 된다. 본 발명품에서는 제품당 50∼3,000개의 음이온이 방출되고 있다. 또한, 희토류 금속과 은의 혼합물로 된 하지층 위에 금, 백금, 은, 또는 로듐 등의 귀금속을 도금하였기 때문에 귀금속 도금층의 두께와 표면이 아주 균일하다.The main feature of the anion-releasing ornament according to the present invention is to form a mixed plating layer of a mixture of rare earth metal and silver plated on the lactic copper plating layer, and to form a precious metal plating layer such as gold, platinum, silver or rhodium on the mixed plating layer, The manufactured product uses rare earth metal as an anion emitting material and releases a large amount of anions because the mixed plating layer of rare earth metal and silver is used as the base layer. In the present invention, 50 to 3,000 anions are released per product. In addition, since a precious metal such as gold, platinum, silver, or rhodium is plated on a base layer of a mixture of rare earth metal and silver, the thickness and surface of the precious metal plating layer are very uniform.
이때, 사용되는 희토류 금속은 주기율표 제3A족인 스칸듐, 이트륨 및 원자번호 57에서 71인 란탄계열의 15원소를 합친 17원소의 총칭을 말한다.In this case, the rare earth metal used refers to a generic name of 17 elements in which scandium, yttrium of Group 3A of the periodic table and 15 elements of lanthanides having an atomic number of 57 to 71 are combined.
란탄계열 원소 중 란탄늄을 제외한 세륨 이하의 14원소는 란탄족으로 총칭된다. 또 란탄늄에서 사마륨까지의 6원소를 세륨족 원소, 유로퓸에서 루테튬까지 원소, 이트륨, 및 스칸듐을 합친 11원소를 이트륨족 원소라고 한다. 이러한 원소는 모두 희유원소에 속하며, 프로메튬은 방사성원소(放射性元素)로 안정 동위원소(同位元素)는 존재하지 않는다. 원자번호가 홀수인 것은 짝수인 것에 비해 존재량이 적으며,일반적으로 은백색 또는 회색 금속이다. 또한, 공기 중에서 서서히 산화하며, 산 및 뜨거운 물에는 녹지만 알칼리에는 녹지 않고, 화학적 성질은 아주 비슷하며, 보통 모두 ＋3가의 화합물을 만드는데, 세륨, 테르븀, 프라세오디뮴에서는 ＋4가, 이테르븀, 유로퓸, 사마륨에서는 ＋2가도 있다. 알칼리금속과 알칼리토금속에 이어 양성(陽性)이 현저하고, 수산화물은 염기이다.Of the lanthanide-based elements, 14 elements of cerium or less except for lanthanum are collectively referred to as lanthanides. Moreover, the 11 element which combined six elements from lanthanum to samarium, the element from cerium group, the element from europium to lutetium, yttrium, and scandium is called yttrium group element. All of these elements belong to rare elements, and promethium is a radioactive element, and there is no stable isotope. Odd atomic numbers are less present than even and are usually silver white or gray metal. It also oxidizes slowly in the air, soluble in acids and hot water but insoluble in alkalis, and having very similar chemical properties, usually all of which produce + trivalent compounds, which are +4 in cerium, terbium, praseodymium, and in ytterbium, europium and samarium. There is also +2. Following alkali metals and alkaline earth metals, the positiveness is remarkable, and the hydroxide is a base.
본 발명에서 주로 사용하는 희토류 금속분말의 화학적 성분이 표 1에 기재되어 있다.Table 1 shows the chemical components of the rare earth metal powder mainly used in the present invention.
(표 1)Table 1
본 발명에 따른 음이온 방출 장신구는 도 1 및 도 2에 일예로 도시된 바와 같이, 금속, 세라믹스 또는 고분자 재료 등으로 제조된 성형체(10), 상기 성형체(10)의 상부에 청화은, 청화카리, 탄산카리 및 광택제 등의 혼합액을 이용하여 전처리도금으로 형성된 청화도금층(20), 상기 청화도금층(20)의 상부에 황산,황산동, 염산 및 광택제 등의 혼합액을 이용하여 형성된 유산동 도금층(30), 상기 유산동 도금층(30)의 상부에 희토류 금속과 은의 혼합액을 이용하여 형성된 혼합도금층(40), 및 상기 혼합도금층(40)의 상부에 금, 백금, 은, 또는 로듐 등의 귀금속액을 이용하여 형성된 귀금속 도금층(50)으로 구성된다. 이때, 희토류 금속분말과 은의 혼합도금층(40)으로부터 다량의 음이온이 발생되어 신체에 이로운 약리현상들이 일어나게 되는 것이다.1 and 2, the anion-releasing ornament according to the present invention is a molded body 10 made of metal, ceramics or polymer material, etc., cyanide silver, cyanide, carbonic acid on top of the molded body 10 The cyanide plating layer 20 formed by pretreatment plating using a mixed solution such as a carry and a polishing agent, a lactic acid copper plating layer 30 formed by using a mixed solution of sulfuric acid, copper sulfate, hydrochloric acid, and a brightener on the upper part of the cyanized plating layer 20, the lactic copper Mixed plating layer 40 formed by using a mixture of rare earth metal and silver on the plating layer 30, and precious metal plating layer formed by using a precious metal liquid such as gold, platinum, silver, or rhodium on the mixed plating layer 40 It consists of 50. At this time, a large amount of negative ions are generated from the mixed-plated layer 40 of the rare earth metal powder and silver, which causes pharmacological phenomena beneficial to the body.
음이온을 발생시키기 위해 첨가되는 상기 희토류 금속분말은 란탄늄, 세륨 및 그들의 혼합물 중 선택된 어느 하나를 사용하고 1∼4㎛의 입경을 가지는 것이 바람직하다.The rare earth metal powder added to generate an anion preferably uses any one selected from lanthanum, cerium, and mixtures thereof, and has a particle size of 1 to 4 µm.
또 다른 실시예로서, 귀금속 도금층의 광택이 중요할 경우에는, 희토류 금속과 은의 혼합도금층(40)을 도금한 후 다시 유산동 도금층(30a)을 형성하고, 그 위에 희토류 금속과 은의 혼합도금층(40a)을 다시 한번 형성한 후에, 귀금속 도금층(50)을 형성할 수도 있다.As another embodiment, when the gloss of the noble metal plating layer is important, after plating the mixed plating layer 40 of the rare earth metal and silver, the copper plating layer 30a is formed again, and the mixed plating layer of the rare earth metal and silver 40a thereon. After forming once again, the precious metal plating layer 50 may be formed.
또한, 본 발명에 따른 다량의 음이온을 방출하는 고기능 장신구의 제조방법은 크게 장신구 및 장식품의 성형체 제조단계, 전처리단계, 청화도금층 형성단계, 유산동 도금층 형성단계, 희토류금속과 은의 혼합도금층 형성단계, 및 귀금속 도금층 형성단계로 구분될 수 있으며, 그 상세한 설명은 다음과 같다.In addition, the manufacturing method of the high-function ornaments releasing a large amount of negative ions according to the present invention is largely in the production of molded articles of ornaments and ornaments, pre-treatment step, clarified plating layer forming step, lactic copper plating layer forming step, rare earth metal and silver mixed plating layer forming step, and Precious metal plating layer may be divided into steps, the detailed description of which is as follows.
(1) 장신구 및 장식품의 성형체 제조단계(1) Manufacturing steps of molded articles of ornaments and ornaments
금속, 세라믹스, 고분자 재료를 이용하여 목걸이, 팔지, 귀걸이, 반지, 브로치 등의 장신구나 시계, 거울, 상패 등의 장식품 성형체를 제조한다.Metal, ceramics, and polymer materials are used to manufacture ornaments such as necklaces, bracelets, earrings, rings, and brooches, or ornaments such as watches, mirrors, and plaques.
(2) 전처리 단계(2) pretreatment step
황산과 염산의 수용액을 이용하여 상온에서 장신구나 장식품의 성형체를 전처리하여 이물질을 제거한다.Using an aqueous solution of sulfuric acid and hydrochloric acid to remove foreign substances by pre-treating the molded body of ornaments or ornaments at room temperature.
(3) 청화 도금층 형성단계(3) blue-green plating layer forming step
청화은, 청화카리, 탄산카리 및 광택제 등의 혼합액을 이용하여 상온에서 1∼10분 동안 도금하여 0.1∼5.0㎛의 청화도금층을 형성한다.Cyanide is plated for 1 to 10 minutes at room temperature using a mixed solution of cyanide, carbonate and polish to form a cyanide plating layer of 0.1 to 5.0 탆.
(4) 유산동 도금층 형성단계(4) lactic acid copper plating layer forming step
50∼100g/l 황산, 100∼300g/l 황산동, 0.5∼2g/l 염산 및 0.5∼1.5g/l 광택제 등의 혼합액을 이용하여 15∼30℃에서 30∼120분 동안 도금하여 1∼30㎛의 유산동 도금층을 만든다.1 to 30 μm by plating for 30 to 120 minutes at 15 to 30 ° C. using a mixture of 50 to 100 g / l sulfuric acid, 100 to 300 g / l copper sulfate, 0.5 to 2 g / l hydrochloric acid, and 0.5 to 1.5 g / l polish Make a plate of lactic acid copper.
(5) 희토류 금속과 은의 혼합도금층 형성단계(5) forming a mixed plating layer of rare earth metal and silver
음이온을 발생시키기 위해 첨가하는 희토류 금속 분말은 란탄늄, 세륨 또는 그들의 혼합물을 사용하는 것이 좋고, 1-4㎛의 입경을 가지고 있다. 또한, 상기 희토류 금속 분말이 첨가된 은 도금액을 제조한 후, 1.0∼6.0 A/cm2의 전류밀도에서 10∼120분 동안 도금하여 0.5∼20㎛의 희토류 금속과 은의 혼합도금층을 얻는다.The rare earth metal powder added to generate an anion preferably uses lanthanum, cerium, or a mixture thereof, and has a particle size of 1-4 µm. In addition, after preparing a silver plating solution to which the rare earth metal powder is added, plating is performed for 10 to 120 minutes at a current density of 1.0 to 6.0 A / cm 2 to obtain a mixed plating layer of rare earth metal and silver of 0.5 to 20 µm.
또 다른 실시예로서, 희토류 금속과 은의 혼합도금층 위에 있는 금, 백금, 은, 또는 로듐 등의 귀금속 도금층의 광택이 중요할 때 희토류 금속과 은의 혼합도금층을 형성한 후 다시 유산동 도금층을 형성하고, 희토류 금속과 은의 혼합도금층을 다시 한번 형성할 수도 있다.In another embodiment, when the gloss of the precious metal plating layer such as gold, platinum, silver, or rhodium on the mixed plating layer of the rare earth metal and silver is important, the mixed plating layer of the rare earth metal and silver is formed, and then a copper oxide plating layer is formed again. The mixed plating layer of metal and silver may be formed once again.
(6) 귀금속 도금층 형성단계(6) Precious metal plating layer forming step
금, 백금, 은 또는 로듐 등의 귀금속 액을 이용하여 희토류 금속과 은의 도금 층 위에 0.1∼10㎛의 귀금속 도금층을 형성한다.A noble metal plating layer of 0.1 to 10 탆 is formed on the rare earth metal and silver plating layer using a noble metal liquid such as gold, platinum, silver or rhodium.
<실시예><Example>
구리를 이용하여 목걸이 체인을 제조하고, 황산과 염산의 수용액을 이용하여 상온에서 상기 목걸이 체인을 전처리하여 이물질을 제거한다. 이물질이 제거된 목걸이 체인에 청화은, 청화카리, 탄산카리 및 광택제의 혼합액을 이용하여 상온에서 5분 동안 청화도금하고, 80g/l 황산, 200g/l 황산동, 0.8g/l 염산 및 1.0g/l 광택제 등의 혼합액을 이용하여 25℃에서 60분 동안 유산동 도금을 한다. 그 후에, 란탄늄과 세륨의 희토류 금속분말을 포함하는 은 도금액을 이용하여 1.5 A/cm2의 전류밀도에서 30분 동안 도금하여 5.0㎛의 희토류 금속과 은의 혼합도금층을 얻는다. 마지막으로, 상기 혼합도금층 위에 금 도금액을 이용하여 1㎛의 금 도금층을 형성하여, 완성된 목걸이를 얻는 것이다.A necklace chain is prepared using copper, and the necklace chain is pretreated at room temperature using an aqueous solution of sulfuric acid and hydrochloric acid to remove foreign substances. In the necklace chain from which foreign substances were removed, cyanide was plated at room temperature for 5 minutes using a mixture of silver, blue, carbonate and brightener, and 80 g / l sulfuric acid, 200 g / l copper sulfate, 0.8 g / l hydrochloric acid and 1.0 g / l Copper lactate is plated at 25 ° C. for 60 minutes using a mixed solution such as a brightener. Thereafter, using a silver plating solution containing a rare earth metal powder of lanthanum and cerium, plating is performed for 30 minutes at a current density of 1.5 A / cm 2 to obtain a mixed plating layer of rare earth metal and silver of 5.0 µm. Finally, by using a gold plating solution on the mixed plating layer to form a gold plating layer of 1㎛, to obtain a finished necklace.
상기의 실시예에 의해 제조된 장신구로부터 방출되는 음이온을 이온시험기(일본의 에코 홀리스틱(ECO HOLISTIC)사 생산)를 통해 평가한 결과, 제품당 50∼3,000개의 음이온이 방출되었으며, 이러한 음이온 방출로 인하여 혈액 정화, 세포 활성화, 면역력 증가, 신경 안정, 호흡기 및 장기 향상, 피로감 경감 등의 약리효과를 얻을 수 있었다.As a result of evaluating the anion released from the jewelry manufactured by the above example through an ion tester (produced by ECO HOLISTIC Co., Ltd. of Japan), 50 to 3,000 anions were released per product. Pharmacological effects such as blood purification, cell activation, immunity increase, nerve stabilization, respiratory and organ improvement, and fatigue reduction were obtained.
이상과 같이 본 발명의 실시예를 설명하였으나 본 고안의 구체적인 구성은 상기 실시예에 한정하지 않고 본 발명의 요지를 이탈하지 않는 범위의 설계변경이든 본 발명에 포함된다.Although the embodiments of the present invention have been described as described above, the specific configuration of the present invention is not limited to the above embodiments, and any modifications of the design without departing from the gist of the present invention are included in the present invention.
상기 희토류 금속분말과 은의 혼합액에 원적외선을 방출하는 맥반석, 옥, 제올라이트, 또는 숯 등의 분말이 소량 첨가될 수도 있다.A small amount of powder, such as elvan, jade, zeolite, or charcoal, which emits far infrared rays, may be added to the mixed solution of the rare earth metal powder and silver.
또한, 성형체도 목걸이나 팔찌등의 장신구에 한정하지 않고 실생활 주변에서 다양하게 사용되는 장식품에 폭 넓게 응용될 수도 있다.In addition, the molded body is not limited to jewelry such as necklaces and bracelets, but may be widely applied to ornaments that are used variously around the real life.
상기에 언급된 바와 같이, 본 발명에 따른 다량의 음이온을 방출하는 고기능 장신구 및 그 제조방법에 의하면, 다량의 음이온을 방출함으로써 혈액정화, 세포 활성화, 면역력 증가, 신경안정, 호흡기 및 장기 향상, 및 피로감 경감등의 신체적인 효능을 얻을 수 있고, 음이온을 방출하는 제품을 용이하게 제조하고, 그 생산비용을 저렴하게 할 수 있다.As mentioned above, according to the high-functional jewelry releasing a large amount of anions according to the present invention and a method for producing the same, by purifying a large amount of anions, blood purification, cell activation, increased immunity, neurostable, respiratory and organ improvement, and Physical effects such as fatigue reduction can be obtained, and a product which releases negative ions can be easily manufactured, and the production cost thereof can be reduced.
또한, 귀금속 도금층의 변색을 방지하고, 제품의 내식성을 우수하게 하고, 귀금속 도금층의 두께와 표면을 균일하게 하여 제품의 생산성을 크게 향상시키고, 음이온을 방출하는 제품의 제조를 용이하게 하며, 그 생산비용을 저렴하게 할 수 있는 장점이 있다.In addition, it prevents discoloration of the noble metal plating layer, improves the corrosion resistance of the product, makes the thickness and the surface of the noble metal plating layer uniform, greatly improves the productivity of the product, and facilitates the manufacture of the product that emits negative ions. The advantage is that the cost can be lowered.
한편, 상기에서는 본 발명의 바람직한 실시예들을 참조하여 설명하였지만,해당 기술분야에서 통상의 지식을 가진 자라면 하기의 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.On the other hand, while the above has been described with reference to the preferred embodiments of the present invention, those of ordinary skill in the art various modifications of the present invention without departing from the spirit and scope of the present invention described in the claims below. It will be understood that modifications and changes can be made.
Claims (6)