KR20020060445A - Molding mold and glass mold for manufacturing multi focus eyeglasses lens formed using the same - Google Patents
Molding mold and glass mold for manufacturing multi focus eyeglasses lens formed using the same Download PDFInfo
- Publication number
- KR20020060445A KR20020060445A KR1020010001544A KR20010001544A KR20020060445A KR 20020060445 A KR20020060445 A KR 20020060445A KR 1020010001544 A KR1020010001544 A KR 1020010001544A KR 20010001544 A KR20010001544 A KR 20010001544A KR 20020060445 A KR20020060445 A KR 20020060445A
- Authority
- KR
- South Korea
- Prior art keywords
- axis
- curvature
- point
- radius
- center point
- Prior art date
Abstract
Description
본 발명은 성형몰드 및 그 성형몰드에 의하여 성형된 누진다초점렌즈 제조용 유리몰드에 관한 것이다.The present invention relates to a molding mold and a glass mold for producing a closed-focal lens manufactured by the molding mold.
누진다초점렌즈란, 원용부(far vision viewing portion)라는 불리는 원거리를 보기 위한 영영(이하, 원거리 영역)과, 중간부(intermediate vision viewing portion)이라 불리는 중간거리를 보기 위한 영역(이하, 중거리 영역)과,근용부(near vision viewing portion)이라 불리는 근거리를 보기 위한 영역(이하, 근거리 영역)이 존재한다. 여기서, 중간거리라는 것은 대략적으로 50cm 에서 2m 의 거리를 가리키며, 이보다 먼 거리를 원거리, 이보다 가까운 거리를 부르는 경우가 많다. 그러나, 때로는 원거리는 무한한 원거리만을 의미하기도 하고, 근거리는 30cm 내지 33cm 를 가리키는 경우도 있고, 확실한 정의가 존재하지 않고 있다.A focal lens is an area for viewing a far field called a far vision viewing portion (hereafter referred to as a far field) and an area for viewing an intermediate distance referred to as an intermediate vision viewing portion (hereinafter referred to as a medium distance area). ) And an area (hereinafter, referred to as a near area) for viewing a near field called a near vision viewing portion. Here, the intermediate distance refers to a distance of approximately 50cm to 2m, and the distance farther than this is often called a far distance and a distance closer thereto. However, sometimes the distance means only infinite distance, the short distance may refer to 30 cm to 33 cm, and there is no clear definition.
누진다초점렌즈에는 상기한 영역들 사이의 명료한 경계선이 존재하지 않기 때문에 상기 정의가 확정되어 있지 않아도 실질적으로 안경을 착용함에 있어서 불편함은 없다. 그러나, 렌즈의 설계나 제조, 검사, 또는 안경테에 렌즈를 넣을 때에는 렌즈상에 기준이 되는 점들이 필요하게 된다. 이런 점들 중에서, 현재 가장 일반적인 것으로는, 원거리영역에 형성된 원용도수측정포인트(F ; far vision power measuring position ; 먼거리를 응시할 경우에 렌즈의 굴절력을 측정하기 위한 위치)와, 근거리영역에 형성된 근용도수측정포인트(N ; near vision power measuring position ; 근거리를 응시할 경우에 렌즈의 굴절력을 측정하기 이한 위치)와, 중거리영역에 형성되어 안경착용자가 정면을 응시할 때 시선이 통과되며 도수가 없는 무도수포인트(E) 가 있다.Since the focus lens does not have a clear boundary line between the above-mentioned regions, there is no inconvenience in practically wearing glasses even if the definition is not determined. However, when designing, manufacturing, inspecting, or putting a lens into a spectacle frame, reference points on the lens are required. Among these points, at present, the most common ones include a far vision power measuring position (F) formed in a far field and a nearness range formed in a near field. Near vision power measuring position (N), which is easy to measure the refractive power of the lens when staring at the near field, and is formed in the mid-distance area, where the eye gaze passes when the eye wearer stares at the front, (E)
상기와 같은 누진다초점렌즈는 원거리영역, 중거리영역, 근거리영역 사이의 경계가 보이지 않고, F, N, E 가 존재하여야 하기 때문에 제조하기가 매우 까다롭다. 따라서, 누진다초점렌즈는 대량생산이 어렵고 가격이 매우 고가이다라는 문제점이 있었다.Such a closed focal lens is very difficult to manufacture because the boundary between the far-field, middle-distance and near-field areas is not visible and F, N, and E must be present. Therefore, the focal lens has a problem that mass production is difficult and the price is very expensive.
본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로서, 누진다초점렌즈를 보다 용이하게 대량으로 저렴하게 제조할 수 있는 누진다초점렌즈 제조용 유리몰드 및 그 유리몰드를 성형하기 위한 성형몰드를 제공하는 것을 목적으로 한다.SUMMARY OF THE INVENTION The present invention has been made to solve the above problems, and provides a glass mold for producing a leaking focus lens and a molding mold for molding the glass mold, which can easily and inexpensively manufacture a large amount of leaking focus lens. It aims to do it.
도 1은 본 발명에 따른 성형몰드의 사시도,1 is a perspective view of a molding mold according to the present invention,
도 2 는 도 1의 성형몰드의 정면도,2 is a front view of the molding mold of FIG.
도 3은 도 2의 성형몰드의 X 축을 따른 단면도,3 is a cross-sectional view along the X axis of the molding mold of FIG.
도 4는 도 2의 성형몰드의 A 축을 따른 단면도,4 is a cross-sectional view along the A axis of the molding mold of FIG.
도 5는 도 2의 성형몰드의 Ym 축을 따른 단면도,5 is a cross-sectional view along the Ym axis of the molding mold of FIG.
도 6은 도 1의 성형몰드에 안착되는 성형유리를 도시한 도면,6 is a view showing a molded glass seated on the molding mold of FIG.
도 7은 도 6의 성형몰드에 성형유리가 안착된 상태를 도시한 측면도,7 is a side view showing a state in which the molded glass is seated in the molding mold of FIG.
도 8은 도 6의 성형몰드에 의하여 성형유리가 본 발명의 유리몰드로 성형된 것을 도시한 측면도,8 is a side view showing that the molded glass is molded into the glass mold of the present invention by the molding mold of FIG.
도 9는 도 8의 유리몰드를 발췌하여 도시한 정면도,9 is a front view showing an extract of the glass mold of FIG.
도 10은 도 9의 유리몰드를 이용하여 누진다초점렌즈를 제조하는 방법을 도시한 도면.FIG. 10 illustrates a method of manufacturing a focal lens using the glass mold of FIG. 9; FIG.
<도면의 주요부분에 대한 부호 설명><Description of Signs of Major Parts of Drawings>
10 ... 성형몰드 11 ... 테두리10 ... molding mold 11 ... border
12 ... 원거리영역 13 ... 근거리영역12 ... remote area 13 ... near area
14 ... 중거리영역 20 ... 성형유리14 ... medium range 20 ... molded glass
30 ... 대응유리몰드 40 ... 브라켓30 ... glass mold 40 ... bracket
41 ... 이격부 50 ... 모노말41 ... separation 50 ... mono
200 ... 유리몰드 211 ... 테두리200 ... Glass Mold 211 ... Border
212 ... 원거리영역 213 ... 근거리영역212 ... Far-field 213 ... Near-field
214 ... 중거리영역 R1 ... 제1곡률반경214 ... mid-range R1 ... first radius of curvature
R2 ... 제2곡률반경 G ... 중심포인트R2 ... 2nd radius of curvature G ... center point
F ... 원용도수측정포인트 E ... 무도수포인트F ... Raw water measuring point E ... No counting point
N ... 근용도수측정포인트 D1 ... 제1간격N ... Nearness measure point D1 ... first interval
D2 ... 제2간격 D3 ... 제3간격D2 ... second interval D3 ... third interval
D4 ... 제4간격 d ... 간격D4 ... fourth interval d ... interval
상기와 같은 목적을 달성하기 위하여, 본 발명에 성형몰드는, 전체적으로 오목면을 이루며 기하학적 중심포인트(G)를 가지는 성형몰드에 있어서, 제1곡률반경(R1)이 형성된 원거리영역(12)과, 제2곡률반경(R2)이 형성된 근거리영역(13)과, 상기 원거리영역(12)과 상기 근거리영역(13) 사이에 형성된 중거리영역(14)을 포함하며; 상기 근거리영역(13)은 상기 중심포인트(G)를 지나는 X 축상의 하방에 종 모양으로 형성되어 있으며; 상기 제1곡률반경(R1)은 상기 제2곡률반경(R2)보다 큰 것을 특징으로 한다.In order to achieve the above object, in the present invention, the molding mold, in the molding mold forming a concave surface as a whole and having a geometric center point (G), the far region 12 having the first radius of curvature R1, A near field region (13) having a second radius of curvature (R2) and a medium distance region (14) formed between the far region (12) and the near region (13); The short-range region (13) is formed in a bell shape below the X axis passing through the center point (G); The first radius of curvature R1 is larger than the second radius of curvature R2.
본 발명에 있어서, 상기 원거리영역(12)에는 상기 중심포인트(G)를 지나는 Y 축상에 그 중심포인트(G)의 상방으로 제1간격(D1) 만큼 떨어진 원용도수측정포인트(F)가 형성되어 있으며, 상기 제1간격(D1)은 9mm ∼ 20mm 의 범위내에 있다.In the present invention, the far-field measuring point F is formed on the Y-axis passing through the center point G, and separated from the center point G by a first distance D1. The first interval D1 is in the range of 9 mm to 20 mm.
또, 상기 중거리영역(14)에는 상기 중심포인트(G)에서 X 축 방향으로 제2간격(D2) 만큼 떨어진 지점의 Ym 축상에 형성된 것으로서, 상기 Ym 축상에 상기 중심포인트(G)의 상방으로 제3간격(D3)만큼 떨어진 무도수포인트(E)가 형성되어 있고; 상기 근거리영역(13)에는 상기 무도수포인트(E)가 형성된 Ym 축상에 상기 중심포인트(G)의 하방으로 제4간격(D4) 만큼 떨어진 근용도수측정포인트(N)가 형성되어 있으며; 상기 제2간격(D2)은 2mm ∼ 4mm 의 범위내에 있고, 상기 제3간격(D3)은 3mm ∼ 5mm 의 범위내에 있으며, 상기 제4간격(D4)은 9mm ∼ 12mm 의 범위내에 있다.In addition, the intermediate distance region 14 is formed on the Ym axis at a point separated by the second interval D2 in the X axis direction from the center point G, and is formed above the center point G on the Ym axis. A non-transmitting point E spaced by three intervals D3 is formed; The near field measurement point (N) is formed on the Ym axis where the non-power point (E) is formed and is located near the center point (G) by a fourth interval (D4); The second interval D2 is in the range of 2 mm to 4 mm, the third interval D3 is in the range of 3 mm to 5 mm, and the fourth interval D4 is in the range of 9 mm to 12 mm.
한편, 상기 오목면의 가장자리에는 X 축을 장축으로 하고, Y 축을 단축으로 하는 타원형상의 테두리(11)가 형성되어 있다.On the other hand, an elliptical edge 11 is formed at the edge of the concave surface with the major axis of the X axis and the minor axis of the Y axis.
여기서, 상기 제1곡률반경(R1) 115mm ∼ 135mm 의 범위내에 있고, 상기 제2곡률반경(R2)은 95mm ∼ 110mm 의 범위내에 있는 것이 바람직하다.Here, it is preferable that the said 1st curvature radius R1 exists in the range of 115 mm-135 mm, and the said 2nd curvature radius R2 exists in the range of 95 mm-110 mm.
상기와 같은 목적을 달성하기 위하여, 상기 성형몰드에 의하여 성형된 본 발명에 따른 누진다초점렌즈 제조용 유리몰드는, 기하학적 중심포인트(G)를 가지는 오목면상에 제1곡률반경(R1)이 형성된 원거리영역(212)과, 제2곡률반경(R2)이 형성된 근거리영역(213)과, 상기 원거리영역(212)과 상기 근거리영역(213) 사이에 형성된 중거리영역(214)이 형성되고; 상기 근거리영역(213)은 상기 중심포인트(G)를 지나는 X 축상의 하방에 종 모양으로 형성되어 있으며; 상기 원거리영역(212)에는, 상기 중심포인트(G)를 지나는 Y 축상에 그 중심포인트(G)의 상방으로 10 mm ∼ 25 mm 만큼 떨어진 원용도수측정포인트(F)가 형성되어 있으며; 상기 중거리영역(214)에는, 상기 중심포인트(G)에서 X 축 방향으로 2 mm ∼ 4 mm 만큼 떨어진 지점의 Ym 축상에 형성된 것으로서, 상기 Ym 축상에 상기 중심포인트(G)의 상방으로 3mm ∼ 5mm 만큼 떨어진 무도수포인트(E)가 형성되어 있고; 상기 근거리영역(213)에는 상기 무도수포인트(E)가 형성된 Ym 축상에 상기 중심포인트(G)의 하방으로 9mm ∼ 12mm 만큼 떨어진 근용도수측정포인트(N)가 형성되어 있는 것을 특징으로 한다.In order to achieve the above object, the glass mold for producing a closed-focus lens according to the present invention, which is molded by the molding mold, has a long radius of curvature R1 formed on a concave surface having a geometric center point (G). A near field region 213 formed with an area 212, a second radius of curvature R2, and a medium distance region 214 formed between the far area 212 and the near area 213; The short range region 213 is formed in a bell shape below the X axis passing through the center point G; The far-field counting point (F) is formed on the Y axis passing through the center point (G) from 10 mm to 25 mm above the center point (G); The intermediate distance region 214 is formed on the Ym axis at a point separated by 2 mm to 4 mm in the X axis direction from the center point G, and is 3 mm to 5 mm above the center point G on the Ym axis. A ballpoint point (E) separated by a number is formed; The near-area 213 is characterized in that the near-measurement measuring point (N) is separated by 9mm to 12mm below the center point (G) on the Ym axis on which the non-conductive point (E) is formed.
본 발명에 있어서. 상기 오목면의 가장자리에는 X 축을 장축으로 하고, Y 축을 단축으로 하는 타원형상의 테두리(211)가 형성되어 있다.In the present invention. At the edge of the concave surface, an elliptical edge 211 having a long axis as the X axis and a short axis as the Y axis is formed.
여기서, 상기 제1곡률반경(R1) 115mm ∼ 135mm 의 범위내에 있고, 상기 제2곡률반경(R2)은 95mm ∼ 110mm 의 범위내에 있는 것이 바람직하다.Here, it is preferable that the said 1st curvature radius R1 exists in the range of 115 mm-135 mm, and the said 2nd curvature radius R2 exists in the range of 95 mm-110 mm.
이하, 첨부된 도면을 참조하며 본 발명에 따른 성형몰드 및 그 성형몰드에 의하여 성형된 누진다초점렌즈 제조용 유리몰드를 상세히 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail a molding mold according to the present invention and a glass mold for producing a dilated focal lens manufactured by the molding mold.
도 1은 본 발명에 따른 성형몰드의 사시도이고, 도 2 는 도 1의 성형몰드의 정면도이며, 도 3은 도 2의 성형몰드의 X 축을 따른 단면도이고, 도 4는 도 2의 성형몰드의 A 축을 따른 단면도이며, 도 5는 도 2의 성형몰드의 Ym 축을 따른 단면도이다.1 is a perspective view of a molding mold according to the present invention, Figure 2 is a front view of the molding mold of Figure 1, Figure 3 is a cross-sectional view along the X axis of the molding mold of Figure 2, Figure 4 is a A of the molding mold of Figure 2 5 is a cross-sectional view along the Ym axis of the molding mold of FIG. 2.
도면을 참조하면, 본 발명에 따른 성형몰드는, 그 상면이 전체적으로 오목면을 이루며 정 중앙에 기하학적 중심포인트(G)가 형성되어 있다. 그리고, 가장자리에는 X 축을 장축으로 하고, Y 축을 단축으로 하는 타원형상의 테두리(11)가 형성되어 있다. 이러한 테두리(11)는 상면과 경계가 형성되고, 상기한 장,단축을 기준으로 하여 기준위치를 정할 수 있다.Referring to the drawings, the molding mold according to the present invention, the upper surface is a concave surface as a whole, the geometric center point (G) is formed at the center. The edge 11 is formed with an elliptical edge 11 having the X axis as the major axis and the Y axis as the minor axis. The edge 11 has a boundary with an upper surface thereof, and a reference position may be determined based on the long and short axes described above.
성형몰드(10)의 테두리(11) 내부에는 제1곡률반경(R1)을 가지는 원거리영역(12)과, 제2곡률반경(R2)을 가지는 근거리영역(13)과, 상기 원거리영역(12)과 상기 근거리영역(13) 사이에 마련된 중거리영역(14)이 형성되어 있다. 이때, 근거리영역(13)은 중심포인트(G)를 지나는 X 축상의 하방에 종 모양으로 형성되어 있으며, 제1곡률반경(R1)은 상기 제2곡률반경(R2)보다 크다.In the edge 11 of the molding mold 10, a far region 12 having a first radius of curvature R1, a near region 13 having a second radius of curvature R2, and the far region 12. And the intermediate distance region 14 provided between the near region 13 is formed. At this time, the near region 13 is formed in a bell shape below the X axis passing through the center point G, and the first radius of curvature R1 is larger than the second radius of curvature R2.
원거리영역(12)에는 중심포인트(G)를 지나는 Y 축상에 그 중심포인트(G)의 상방으로 제1간격(D1) 만큼 떨어진 원용도수측정포인트(F)가 형성되어 있다. 이때, 제1간격(D1)은 9 mm ∼ 20 mm 의 범위내에 있는 것이 바람직한데, 본 실시예에서는 12 mm 로 하였다. 또, 제1곡률반경(R1)은, 115mm ∼ 135mm 의 범위내에 있는 것이 바람직한데, 본 실시예에서는 125.72 mm 로 하였다.In the far region 12, the far-injection counting point F is formed on the Y-axis passing through the center point G and spaced apart by the first interval D1 above the center point G. At this time, the first interval D1 is preferably in the range of 9 mm to 20 mm, but was set to 12 mm in this embodiment. Moreover, although it is preferable that the 1st curvature radius R1 exists in the range of 115 mm-135 mm, in this Example, it was 125.72 mm.
중거리영역(14)에는 중심포인트(G)에서 X 축 방향으로 제2간격(D2) 만큼 떨어진 지점의 Ym 축상에 형성된 것으로서, 상기 Ym 축상에 상기 중심포인트(G)의 상방으로 제3간격(D3)만큼 떨어진 무도수포인트(E)가 형성되어 있다. 이때, 제2간격(D2)은 2mm ∼ 4mm 의 범위내에 있으며, 본 실시예에서는 3 mm 로 하였다. 또한. 제3간격(D3)은 3mm ∼ 5mm 의 범위내에 있으며, 본 실시예에서는 4 mm 로 하였다.The intermediate distance region 14 is formed on the Ym axis at a point separated by the second interval D2 in the X-axis direction from the center point G, and has a third distance D3 above the center point G on the Ym axis. A ballpoint point E spaced apart by) is formed. At this time, the second interval D2 was in the range of 2 mm to 4 mm, and was set to 3 mm in this embodiment. Also. The third interval D3 was in the range of 3 mm to 5 mm, and was set to 4 mm in this example.
근거리영역(13)에는 무도수포인트(E)가 형성된 Ym 축상에 중심포인트(G)의 하방으로 제4간격(D4) 만큼 떨어진 근용도수측정포인트(N)가 형성되어 있다. 제4간격(D4)은 9mm ∼ 12mm 의 범위내에 있는 것이 바람직하며, 본 실시예에서는 10.44 mm 로 하였다. 또, 제2곡률반경(R2)은 95mm ∼ 110mm 의 범위내에 있는 것이 바람직한데, 본 실시예에서는 103.03 mm 로 하였다.The near-field area 13 is formed with a near-frequency measurement point N spaced apart from the center point G by the fourth interval D4 on the Ym axis on which the non-power point E is formed. The fourth interval D4 is preferably in the range of 9 mm to 12 mm, and was set to 10.44 mm in this embodiment. The second radius of curvature R2 is preferably in the range of 95 mm to 110 mm, but in the present embodiment, it is set to 103.03 mm.
다음, 상기와 같은 성형몰드에 의하여 성형되는 누진다초점렌즈 제조용 유리몰드의 제조방법을 설명한다.Next, a method of manufacturing a glass mold for producing a closed-focal lens manufactured by the molding mold as described above will be described.
도 6은 도 1의 성형몰드에 안착되는 성형유리를 도시한 도면이고, 도 7은 도 6의 성형몰드에 성형유리가 안착된 상태를 도시한 측면도이며, 도 8은 도 6의 성형몰드에 의하여 성형유리가 본 발명의 유리몰드로 성형된 것을 도시한 측면도이다.6 is a view illustrating a molded glass seated on the molding mold of FIG. 1, FIG. 7 is a side view illustrating a state in which the molding glass is seated on the molding mold of FIG. 6, and FIG. 8 is formed by the molding mold of FIG. 6. It is a side view which shows the shaping | molding glass shape | molded with the glass mold of this invention.
도면을 참조하면, 도 1 내지 도 5에 도시된 성형몰드(10)에, 도 6에 도시된 바와 같이 원거리영역과 동일한 제1곡률반경(R1)을 가지며 그 성형몰드와 동일 직경을 가지는 성형유리(20)를 성형몰드(10) 상에 안착시킨다.Referring to the drawings, in the molding mold 10 shown in Figs. 1 to 5, as shown in Fig. 6, the molding glass having the same first radius of curvature R1 and the same diameter as the molding mold as shown in Figure 6 20 is seated on the molding mold 10.
이 상태에서는 도 7에 도시된 바와 같이, 성형유리(20)의 볼록면과 성형몰드의 오목면(원거리영역(12), 중거리영역(14), 근거리영역(13), 테두리(11))은 완전히 밀착되지 않는 상태로서 부분적으로 이격되어 있다.In this state, as shown in FIG. 7, the convex surface of the molded glass 20 and the concave surface of the molding mold (far-range area 12, intermediate distance area 14, near-area area 13, and edge 11) are formed. Partially spaced apart as not fully adhered.
이후, 성형유리(20)가 안착된 성형몰드(10)를 노에 넣고 2시간 30 분동안 서서히 가열시켜 680℃ ∼ 720℃ 정도로 가열시킨 후, 이후 상기 온도로 5분정도 가열한 후, 노에 전원을 차단하여 8시간 정도에 걸쳐 식힌다. 그러면, 성형유리(20)는 부분 연화되면서 도 8에 도시된 바와 같이, 성형유리(20)의 볼록면이 성형몰드(10) 오목면에 완전히 밀착되면서, 성형유리(20)의 오목면에는 곡률의 변화가 일어나 결국에는 상기한 성형몰드(10)의 원거리영역(12), 중거리영역(14), 근거리영역(13)과 동일한 제1,2곡률반경(R1)(R2), 원용도수측정포인트(F), 무도수포인트(E), 근용도수측정포인트(N) 등이 형성된다. 즉, 상기 성형유리(20)를 성형몰드(10)에 안착시키고 고온상에서 성형유리(20)를 연화시킴으로써 성형유리(20)는 유리몰드(200)로 성형되고, 유리몰드(200)의 오목면에는 성형몰드(10)에 완전히 동일 곡률의 원거리영역(212), 중거리영역(214), 근거리영역(213)과, 원용도수측정포인트(F), 무도수포인트(E), 근용도수측정포인트(N) 등이 형성된다.Thereafter, the molding mold 10 having the molded glass 20 seated therein was slowly heated for 2 hours and 30 minutes, heated to about 680 ° C. to 720 ° C., and then heated to the temperature for about 5 minutes, and then to the furnace. Shut off the power and let it cool for 8 hours. Then, the molded glass 20 is partially softened, and as shown in FIG. 8, the convex surface of the molded glass 20 is completely adhered to the concave surface of the molding mold 10, and the curvature is formed on the concave surface of the molded glass 20. Changes in the first and second radius of curvature R1 (R2) and raw water frequency measurement, which are the same as those of the far zone 12, the intermediate distance 14, and the near distance 13 of the molding mold 10. A point F, a power point E, and a near-frequency measure point N are formed. That is, the molded glass 20 is molded into the glass mold 200 by seating the molded glass 20 on the molding mold 10 and softening the molding glass 20 at a high temperature, and the concave surface of the glass mold 200. In the molding mold 10, the far-field 212, the intermediate-distance 214, the near-field 213 and the raw water measuring point F, the non-water counting point E, and the near-water count having the same curvature are included. The point N etc. are formed.
즉, 상기와 유리몰드(200)를 좀더 상세히 설명하면 다음과 같다.That is, the glass mold 200 will be described in more detail as follows.
도 9는 도 8의 유리몰드를 발췌하여 도시한 정면도이다.9 is a front view showing an extract of the glass mold of FIG.
도면을 참조하면, 유리몰드(200)는, 기하학적 중심포인트(G)를 가지는 오목면상에 제1곡률반경(R1)이 형성된 원거리영역(212)과, 제2곡률반경(R2)이 형성된 근거리영역(213)과, 상기 원거리영역(212)과 상기 근거리영역(213) 사이에 형성된 중거리영역(214)을 가진다. 이때, 근거리영역(213)은 중심포인트(G)를 지나는 X 축상의 하방에 종 모양으로 형성되어 있다. 또, 유리몰드(200)의 오목면의 가장자리에는 X 축을 장축으로 하고, Y 축을 단축으로 하는 타원형상의 테두리(211)가 형성되어 있다.Referring to the drawings, the glass mold 200 includes a far region 212 having a first radius of curvature R1 formed on a concave surface having a geometric center point G, and a near region having a second radius of curvature R2 formed therein. 213 and a middle distance region 214 formed between the far region 212 and the near region 213. At this time, the near-area 213 is formed in a bell shape below the X-axis passing through the center point (G). Moreover, the edge of the concave surface of the glass mold 200 is provided with the oval-shaped edge 211 which makes an X axis a long axis and a Y axis a short axis.
원거리영역(212)에는, 중심포인트(G)를 지나는 Y 축상에 그 중심포인트(G)의 상방으로 10 mm ∼ 25 mm 만큼 떨어진 원용도수측정포인트(F)가 형성되어 있다. 제1곡률반경(R1) 115mm ∼ 135mm 의 범위내에 있고, 본 실시예에서는 125.72 mm 로 되어 있다.In the far region 212, a far-in use measuring point F is formed by 10 mm to 25 mm above the center point G on the Y axis passing through the center point G. The first radius of curvature R1 is in the range of 115 mm to 135 mm, and is 125.72 mm in this embodiment.
중거리영역(214)에는, 상기 중심포인트(G)에서 X 축 방향으로 10 mm ∼ 25 mm 만큼 떨어진 지점의 Ym 축상에 형성된 것으로서, Ym 축상에 상기 중심포인트(G)의 상방으로 3mm ∼ 5mm 만큼 떨어진 무도수포인트(E)가 형성되어 있다.The intermediate distance region 214 is formed on the Ym axis at a point 10 mm to 25 mm apart from the center point G in the X axis direction, and is 3 mm to 5 mm above the center point G on the Ym axis. The pointless point E is formed.
그리고, 근거리영역(213)에는 무도수포인트(E)가 형성된 Ym 축상에 중심포인트(G)의 하방으로 9mm ∼ 12mm 만큼 떨어진 근용도수측정포인트(N)가 형성되어 있다. 제2곡률반경(R2)은 95mm ∼ 110mm 의 범위내에 있고, 본 실시예에서는, 103.03 mm 로 되어 있다.In the near-area 213, a near-frequency measurement point N is formed by 9 mm to 12 mm below the center point G on the Ym axis where the non-power point E is formed. The second radius of curvature R2 is in the range of 95 mm to 110 mm, and is 103.03 mm in this embodiment.
다음, 유리몰드(200)를 이용하여 누진다초점렌즈를 제조하는 방법을 설명한다.Next, a method of manufacturing the focal lens using the glass mold 200 will be described.
도 10은 도 9의 유리몰드를 이용하여 누진다초점렌즈를 제조하는 방법을 도시한 도면이다. 도면을 참조하면, 상기와 같은 방법으로 제조된 유리몰드(200)와 소정의 일정 곡률을 가진 대응유리몰드(30)를 브라켓(40)에 끼어넣는다. 이때, 브라켓(40)에는 이격부(41)가 마련되어 있어 유리몰드(200)와 대응유리몰드(30) 사이에 소정 두께의 이격부(d)가 형성된다.FIG. 10 is a view illustrating a method of manufacturing a focal lens using the glass mold of FIG. 9. Referring to the drawings, the glass mold 200 manufactured by the above method and the corresponding glass mold 30 having a predetermined predetermined curvature are inserted into the bracket 40. At this time, the bracket 40 is provided with a spaced portion 41, and the spaced portion d having a predetermined thickness is formed between the glass mold 200 and the corresponding glass mold 30.
다음, 이격부(d) 사이로 누진다초점렌즈의 재료가 되는 모노말(50)(MONOMER)을 주입한 후, 소정시간동안 냉각시켜 굳힌다. 모노말은 안경을 제조하는 업계에서는 일반적으로 사용하는 것이라서 더 이상의 상세한 설명은 생략한다.Next, the monolith 50 (MONOMER), which is the material of the focus lens, is injected between the spaced portions d, and then cooled and hardened for a predetermined time. Monomal is generally used in the industry of eyeglass manufacturing, and thus detailed description thereof is omitted.
이후, 모노말(50)이 완전히 굳으며 브라켓(40) 및 대응유리몰드(30), 유리몰드(200)를 제거한다. 그러면, 상술한 제1,2곡률반경, 원거리영역, 중거리영역, 근거리영역, 원용도수측정포인트, 무도수포인트 및 근용도수측정포인트가 형성된 누진다초점렌즈가 완성된다.After that, the mono 50 is completely hardened, and the bracket 40, the corresponding glass mold 30, and the glass mold 200 are removed. Then, the lapse-focal lens in which the above-described first and second curvature radii, far-range, mid-distance, near-area, far-away frequency measuring point, non-numbering point and near-frequency counting point are formed is completed.
본 발명은 상기와 같은 실시예를 참고로 설명되었으나, 이는 일 실시예에 불과하고, 본 발명에 속하는 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양한 타 실시예를 구현할 수 있음은 물론이다.Although the present invention has been described with reference to the above embodiments, this is only one embodiment, and those of ordinary skill in the art can implement a variety of other embodiments from this.
본 발명에 따른 성형몰드 및 그 성형몰드에 의하여 성형되는 누진다초점렌즈 제조용 유리몰드에 따르면, 유리몰드를 보다 용이하고 저렴하게 성형할 수 있고, 그 유리몰드를 이용하여 누진다초점렌즈를 대량으로 저렴하게 제조할 수 있다는 효과가 있다.According to the molding mold according to the present invention and the glass mold for producing a lumped focal lens manufactured by the molding mold, the glass mold can be molded more easily and inexpensively, and the lumped focal lens is massed using the glass mold. There is an effect that can be manufactured at low cost.
Claims (8)