KR20020009127A - method for manufacturing E.V.A midsole having lateral enforcement - Google Patents

method for manufacturing E.V.A midsole having lateral enforcement Download PDF

Info

Publication number
KR20020009127A
KR20020009127A KR1020000042490A KR20000042490A KR20020009127A KR 20020009127 A KR20020009127 A KR 20020009127A KR 1020000042490 A KR1020000042490 A KR 1020000042490A KR 20000042490 A KR20000042490 A KR 20000042490A KR 20020009127 A KR20020009127 A KR 20020009127A
Authority
KR
South Korea
Prior art keywords
midsole
mold
reinforcement
reinforcing
manufacturing
Prior art date
Application number
KR1020000042490A
Other languages
Korean (ko)
Inventor
임성조
Original Assignee
임성조
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 임성조 filed Critical 임성조
Priority to KR1020000042490A priority Critical patent/KR20020009127A/en
Publication of KR20020009127A publication Critical patent/KR20020009127A/en

Abstract

PURPOSE: Provided is a production process of insole in E.V.A midsole with side reinforcing materials included which compresses the midsole and adheres the reinforcing materials in a midsole side simultaneously so that it increases productivity and reduces production cost. CONSTITUTION: The production process of insole in E.V.A midsole with the side reinforcing materials comprises the steps of: (i) preparing midsole and an upper mold with a certain pattern formed inside; (ii) preparing midsole materials as 1.3-1.5 times as wanted form in a semi-processed state, which are made from E.V.A materials; (iii) placing the reinforcing material with hot-melt adhesive coated in a reinforcing formation material which is made from silicone synthetic resin materials with aluminium or copper powder mixed and fixing the reinforcing formation material at the side of the midsole material to contact one side with the adhesive coated to the side of the midsole material; (iv) placing the midsole materials in the mold to compress the midsole and adhere a midsole side in the reinforcing material by compression, heating and cooling; and (v) stripping to complete midsole with the reinforcing material included.

Description

측면 보강재가 구비된 이브이에이 미드솔의 신발중창 제조 방법{method for manufacturing E.V.A midsole having lateral enforcement}Method for manufacturing E.V.A midsole having lateral enforcement

본 발명은 신발중창 제조방법에 관한 것으로, 더욱 상세하게는 중창 측면에 다양한 형태의 보강재가 간단한 방법으로 설치되도록 하여 제품의 상품성 및 생산성이 향상되도록 하는 측면 보강재가 구비된 이브이에이 미드솔의 신발중창 제조 방법에 관한 것이다.The present invention relates to a shoe sole manufacturing method, and more specifically to the sole of the midsole is provided with a side reinforcement to provide a variety of forms of reinforcement to the midsole side in a simple way to improve the productability and productivity of the product It is about a method.

최근에는 생활수준의 향상과 수요자의 다양한 욕구에 의해 다양한 디자인을 가진 수많은 종류의 신발이 제조되고 있으며, 또한 각 기능에 따른 특수신발 역시 다양하게 출시되고 있다. 그러나, 이와 같이 다양한 종류로 출시되는 신발은 그 구조에서 살펴보면 대동소이함을 알 수 있다.Recently, many kinds of shoes with various designs have been manufactured due to improvement of living standards and various needs of consumers, and special shoes for each function are also released in various ways. However, it can be seen that shoes released in various kinds are similar in structure.

도 1에 도시된 바와 같이, 일반적으로 사용되는 신발(1)은, 크게 밑창(2)과, 상기 밑창(2)의 상부에 결합된 갑피(3)로 구성된다. 상기 밑창(2)은, 신발의 바닥창을 이루는 아웃솔(2a)과, 대개 신발의 중창을 이루는 미드솔(2b)로 구성된다. 상기 아웃솔(2a)은 내마모성과 미끄럼 방지를 위한 기능을 충족시킬 수 있도록 고무재질로 이루어지고, 미드솔(2b)은 다양한 재질의 합성수지재가 발포 성형된 구조로 이루어진다.As shown in FIG. 1, a generally used shoe 1 is composed of a sole 2 and an upper 3 coupled to an upper portion of the sole 2. The sole 2 consists of an outsole 2a constituting the sole of the shoe and a midsole 2b constituting the midsole of the shoe. The outsole (2a) is made of a rubber material so as to meet the function for wear resistance and anti-slip, the midsole (2b) is made of a foam-molded structure of a synthetic resin material of various materials.

한편, 미드솔(2b)로 사용되는 합성수지재로는 발포우레탄계, 피브이씨(P.V.C) 또는 티피알(T.P.R)계 그리고 이브이에이계(E.V.A)가 주로 사용된다. 상기 미드솔(2b)의 재료중 발포우레탄계는 액상으로 작업이 이루어지므로 제작작업이 용이하나, 제작 후 쉽게 변색이 되고 무거운 단점이 있을 뿐만 아니라 환경오염을 일으켜 점차 그 생산량이 감축되고 있는 추세이다. 그리고, 상기 합성수지재중 피브이시 또는 티피알계 역시 제작작업은 용이하나 무겁고 환경 호르몬의 발생 등으로 인하여 저가의 신발에만 적용되고 있으며, 그 사용량도 점차 감소하고 있는 추세이다.On the other hand, as the synthetic resin material used as the midsole (2b), foamed urethane-based, PV (C.V.C) or TIP (T.P.R) -based and YB-based (E.V.A) is mainly used. Among the materials of the midsole 2b, the foamed urethane system is easy to manufacture because the work is made in a liquid phase, but it is easily discolored after manufacturing and has a heavy disadvantage as well as environmental pollution, and the production is gradually decreasing. In addition, the fibish or TIPS-based resin of the synthetic resin is also easy to manufacture, but is applied to only low-cost shoes due to the heavy and environmental hormones, the amount of use is also gradually decreasing.

따라서 최근에는 전체 신발의 무게를 줄여 가벼우면서도 충격을 가하였을 때, 충격을 흡수하면서 복원력이 있으며, 변색방지 및 환경오염을 야기하지 않도록 하기 위해 발포 팽창시켜 사용하는 이브이에이(E.V.A) 재질의 합성수지재를 주로 사용하게 된다. 상기와 같이 발포팽창시켜 사용하는 이브이에이(E.V.A) 발포층 미드솔(2b)은 아웃솔(2a)을 이루는 고무와는 그 재질이 상이하고 또한 제작방법이 달라 대개 따로 따로 제작하여 미드솔(2b)의 저면에 아웃솔(2a)이 부착되도록 하여 밑창(2)을 제작하게 된다.Therefore, in recent years, when the weight of the entire shoe is light and shocked, it is resilient to absorb shock and prevents discoloration and prevents environmental pollution. Mainly used. EVA foam layer midsole (2b) used to expand and expand as described above is different from the rubber forming the outsole (2a), and the material is different, and the production method is different, and is usually produced separately and the bottom surface of the midsole (2b) The sole 2 is attached to the outsole 2a to produce the sole 2.

한편, 나날이 발전해가는 시대의 변화에 따라 신발의 종류도 다양해지고, 다양한 형상 및 무늬를 가진 신발들이 출시되고 있다. 그 일예로 갑피에 다양한 인쇄층을 형성하여 다양한 컬러를 가지는 신발들이 출시되고 있다.On the other hand, with the change of the times, day by day, the types of shoes are also diversified, and shoes with various shapes and patterns are being released. As an example, shoes having various colors have been released by forming various printed layers on uppers.

한편, 상기 갑피와는 별도로 중창인 미드솔의 측면에 역시 다양한 악세사리들을 부착해 신발의 기능성 및 상품성을 높이고 있다. 이러한 미드솔의 측면에 악세사리를 부착하는 과정을 살펴보면, 금형상에 미리 악세사리가 부착될 부위에 악세사리 형상에 대응하는 음각이 조각되고, 이러한 금형에서 중창을 제조한다. 완성된 중창의 측면에는 악세사리가 붙을 조각부가 형성되어 있으므로, 이와는 별도로 제작된 악세사리를 접착제를 이용하여 상기 조각부에 밀착시켜 접착시킴으로서부착시키게 된다.On the other hand, the upper side of the midsole separate from the upper also attached a variety of accessories to increase the functionality and productability of the shoe. Looking at the process of attaching the accessory to the side of the midsole, the intaglio corresponding to the accessory shape is carved on the site where the accessory is attached to the mold in advance, and the midsole is manufactured in such a mold. Since the side portion of the finished midsole is formed with a piece attached to the accessory, the accessory made separately is attached by adhering to the piece by adhering to the piece using an adhesive.

상기와 같은 중창 측면에 악세사리를 부착시키는 방법은 다음과 같은 문제점이 있다.The method of attaching the accessory to the midsole side as described above has the following problems.

금형상에 별도 조각을 형성하여야 하므로 제작비용이 비쌀 뿐만 아니라 그 형상이외에 다른 창의 제조에는 사용될 수 없으므로 악세사리의 형상변경이 발생시 새로운 금형을 제작하여야 하므로 시간 및 노력이 추가되어 생산성이 저하될 뿐만 아니라 별도의 제작비용이 발생하므로 미드솔의 가격이 비싸지는 문제점이 있다.As a separate piece must be formed on the mold, the manufacturing cost is not only expensive but also cannot be used for the manufacture of other windows besides its shape. Therefore, when a change of the shape of the accessory occurs, a new mold must be manufactured. There is a problem that the production cost of the midsole is expensive.

그리고, 미드솔의 완성 후 별도의 접착에 의하여 악세사리를 부착하게 됨으로서 공정의 추가로 제작공정이 복잡해져 미드솔 중창의 제작원가가 비싸다는 문제점이 있다.In addition, after the completion of the midsole is attached to the accessories by a separate adhesion, there is a problem that the manufacturing process is complicated by the addition of the process, the manufacturing cost of the midsole midsole is expensive.

따라서 본 발명은 상기의 문제점들을 해결하기 위한 것으로, 금형내에서 미드솔의 제작과 동시에 측면악세사리를 부착함으로써 제작공정의 단축에 의해 생산성이 향상된 측면 보강제가 구비된 이브이에이 미드솔의 신발중창 제조 방법을 제공하는데 그 목적이 있다.Accordingly, the present invention is to solve the above problems, to provide a shoe sole manufacturing method of Yves midsole equipped with a side reinforcement improved productivity by shortening the manufacturing process by attaching the side accessories at the same time as the production of the midsole in the mold. Its purpose is to.

그리고, 본 발명은, 반복 사용가능한 베이스금형과 조각무늬가 형성되어 분리 결합되는 조각금형을 별도로 구성하여 다양한 형상의 악세사리 부착에 쉽게 적응할 수 있고, 금형제작의 용이성 및 저렴한 비용으로 작업이 이루어지도록 하는 측면 보강제가 구비된 이브이에이 미드솔의 신발중창 제조 방법을 제공하는데 다른 목적이 있다.In addition, the present invention, by repeatedly forming a base mold and a carved pattern is formed to separate the piece mold to be combined separately can be easily adapted to the attachment of accessories of various shapes, the ease of making the mold and low cost Another object of the present invention is to provide a shoe sole manufacturing method of Yves midsole provided with a side reinforcement.

도 1 - 일반적인 신발의 외관을 보인 도.1-shows the appearance of a typical shoe.

도 2 - 본 발명에 의한 미드솔 제조용 중간금형의 사시도.Figure 2-perspective view of the intermediate mold for producing the midsole according to the present invention.

도 3 - 본 발명의 일 실시예에 의한 보강형성재 및 보강재를 보인도.Figure 3 shows a reinforcement forming member and a reinforcing material according to an embodiment of the present invention.

도 4 - 본 발명의 일 실시예에 의한 보강재가 일체로 부착되는 미드솔의 제작과정을 보인 도.Figure 4 shows a manufacturing process of the midsole to which the reinforcing material is integrally attached according to an embodiment of the present invention.

도 5 - 본 발명에 제작된 미드솔을 보인 도.5 is a view showing a midsole manufactured in the present invention.

도 6 - 본 발명의 다른 실시예에 의한 보강재가 일체로 부착되는 미드솔의 제작과정을 보인 도.6 is a view showing a manufacturing process of the midsole to which the reinforcing material is integrally attached according to another embodiment of the present invention.

* 도면의 주요 부분에 대한 부호의 설명** Explanation of symbols for the main parts of the drawings *

10,10': 금형 12' : 베이스금형10,10 ': Mold 12': Base mold

14' : 조각금형 20 : 보강형성재14 ': sculpture mold 20: reinforcement forming material

20a : 단턱 30 : 보강재20a: step 30: reinforcement

40 : 미드솔재료 a : 접착제40: midsole material a: adhesive

P : 미드솔 재료P: Midsole Material

상기와 같은 목적을 달성하기 위한 본 발명은, 내측면에 소정의 조각무늬가 형성된 미드솔금형과 상부금형을 준비하는 과정과; 발포성형된 이브이에이(E.V.A)재질로 이루어지고, 원하는 형상보다 약 1.3 내지 1.5배 정도 크기의 반가공 상태로 이루어지는 미드솔재료를 준비하는 과정과; 알루미늄 또는 동분말이 혼합된 실리콘합성수지재로 이루어지는 보강형성제의 내측면에 외부면에 핫멜트접착제가 도포된 보강제를 위치시키고, 상기 접착제가 도포된 면이 상기 미드솔재료의 측면에 접하도록 보강형성제를 미드솔재료 측면에 고정시키는 과정과; 상기 보강형성제가 고정된 미드솔재료를 금형상에 위치시키고, 가압,가열 및 냉각에 의해 미드솔의 압축 성형과 보강제의 미드솔측면 접착이 이루어 지도록 프레싱공정을 수행하는 과정; 그리고 탈형시켜 보강제가 부착된 미드솔을 완성시키는 과정으로 이루어져; 미드솔의 압축성형과 동시에 보강제의 측면부착이 이루어지는 측면 보강제가 구비된 이브이에이 미드솔의 신발중창 제조 방법을 제공하는데 그 기술적 요지가 있다.The present invention for achieving the above object, the process of preparing a midsole mold and the upper mold formed a predetermined piece pattern on the inner surface; Preparing a midsole material made of a foamed Y.E. (E.V.A) material and having a semi-processed state about 1.3 to 1.5 times larger than a desired shape; A reinforcement agent having a hot melt adhesive applied to the outer surface thereof is placed on the inner side of the reinforcement agent made of a silicone synthetic resin material in which aluminum or copper powder is mixed, and the reinforcement forming agent so that the side on which the adhesive is applied is in contact with the side surface of the midsole material. Fixing the side of the midsole material; Placing the midsole material on which the reinforcement forming agent is fixed on a mold, and performing pressing by pressing, heating, and cooling to achieve compression molding of the midsole and adhesion of the midsole side of the reinforcing agent; And demolding to complete the midsole to which the reinforcing agent is attached; There is a technical gist of the present invention to provide a sole sole manufacturing method of Yves midsole provided with a side reinforcement in which side reinforcement of the reinforcement is simultaneously formed by compression molding of the midsole.

그리고, 상기 미드솔금형은, 미드솔조각무늬가 형성된 단일금형으로 이루어지거나 또는 알루미늄 재질로 이루어지고, 공간부가 형성된 베이스 금형과; 상기 공간부에 분리 결합되고, 알루미늄 또는 동분말이 혼합된 실리콘함성수지재로 이루어지며 내측면에 미드솔조각무늬가 구비된 조각금형으로 이루어지도록 한다.The midsole mold may include a base mold made of a single mold having a midsole piece pattern or made of aluminum, and having a space part; Separately coupled to the space portion, made of a silicon-containing resin material mixed with aluminum or copper powder and made of a piece mold provided with a midsole piece pattern on the inner surface.

바람직 하기로는 상기 보강형성제는, 조각금형 내측면에 보강제의 형상에 대응하는 음각 조각형성으로 이루어지거나, 내측면에 보강제가 위치되는 홈이 형성되고, 보강제의 모양에 대응하는 형상의 알루미늄 재질로 이루어지는 독립부재로 이루어지도록 한다.Preferably, the reinforcing agent is formed of an intaglio engraving corresponding to the shape of the reinforcing agent on the inner surface of the engraving die, or a groove in which the reinforcing agent is located is formed on the inner side, and is made of an aluminum material of a shape corresponding to the shape of the reinforcing agent. It is made of an independent member made.

따라서 본 발명에 따르면, 보강제의 접착이 미드솔의 압축 성형과 동시에 이루어지므로 제작공정의 단축 및 생산성이 향상되는 잇점이 있다.Therefore, according to the present invention, since the adhesion of the reinforcing agent is made at the same time as the compression molding of the midsole, there is an advantage of shortening the manufacturing process and improving productivity.

이하에서는 상기와 같은 구성을 가지는 본 발명에 의한 측면 보강제가 구비된 이브이에이 미드솔의 신발중창 제조 방법의 바람직한 실시예를 도시한 도면을 참조하여 상세하게 설명하기로 한다.Hereinafter will be described in detail with reference to the drawings showing a preferred embodiment of a shoe sole manufacturing method of Yves midsole provided with a side reinforcement according to the present invention having the configuration as described above.

먼저, 도시한 도 2와 도 3의 도면을 참조하여 본 발명에 의한 중창제조에 사용되는 부재를 설명하기로 한다.First, a member used for manufacturing a midsole according to the present invention will be described with reference to FIGS. 2 and 3.

본 발명에 의한 금형중 상부금형 및 하부금형은 종래와 동일하므로 이하 자세한 설명은 생략하기로 한다. 그러나, 중간금형은, 도 2에 도시된 바와 같이, 종래와 같이 동일한 중간금형(10)을 이용하는 경우와, 반복 사용 가능한 베이스금형(12')과 조각무늬가 형성된 조각금형(14')의 두 부분으로 이루어질 수도 있다. 그리고, 상기와 같은 삼단금형이외에 이단금형으로 이루어질 경우에는 미드솔형성을 위한 금형은 하부금형이므로 상기 하부금형의 구조가 상술한 것과 같은 구조를 가진다.Since the upper mold and the lower mold of the mold according to the present invention are the same as in the prior art, a detailed description thereof will be omitted. However, the intermediate mold, as shown in Figure 2, when using the same intermediate mold 10 as in the prior art, the base mold 12 'that can be repeatedly used and the engraving mold (14') formed with a carved pattern 14 ' It may be made of parts. In addition, in the case of forming a two-stage mold in addition to the three-stage mold as described above, since the mold for forming the midsole is a lower mold, the lower mold has a structure as described above.

베이스금형(12')은 원하는 형상의 미드솔보다 큰 크기로 형성되는 조각부가 중앙에 구비되고, 그 재질은 종래와 동일한 알루미늄으로 이루어진다. 그리고, 상기 조각금형(14')은 내면에 별도의 조각무늬가 음각되어 있으며, 이러한 조각무늬는 미드솔의 측면무늬를 형성하는 부위이다. 한편, 상기 내면에는 측면에 부칙되는 보강제의 형상에 대응하는 보강제형성무늬(20')가 음각되도록 할 수도 있다.상기 조각금형(14')은 베이스금형(12')의 내부에 설치되고, 상기 조각금형(14')의 내부에 발포팽창된 미드솔 재료를 넣어 가열압착시켜 중창을 제조하게 된다. 따라서 원하는 중창의 형상에 따라 상기 조각금형(14')만 바뀌게 되고, 베이스금형(12')은 반복사용가능하게 되어 금형제작비가 저렴해진다.Base mold 12 'is provided with a central portion is formed in a larger size than the midsole of the desired shape, the material is made of the same aluminum as the prior art. In addition, the engraving mold 14 ′ is engraved with a separate engraving pattern on the inner surface, which is a portion forming the side pattern of the midsole. The reinforcement forming pattern 20 'corresponding to the shape of the reinforcing agent attached to the side surface may be engraved on the inner surface. The carving mold 14' is installed inside the base mold 12 '. The midsole material is foamed and expanded into the inside of the mold 14 'to be pressed to produce a midsole. Therefore, only the engraving mold 14 'is changed according to the shape of the desired midsole, and the base mold 12' is repeatedly usable, resulting in a low mold production cost.

한편, 상기 조각금형(14')은 그 재질이 종래와 동일한 알루미늄으로 이루어지거나, 또는 실리콘 재질의 합성수지재로 구성될 수도 있다. 이러한 합성수지재에는 열전도성을 위하여 동분말 등이 혼합되어도 좋을 것이다. 이러한 합성수지재로 이루어 질 수 있는 금형재료는 이미 본인의 선출원(국내특허 출원번호 : 98-44772호)에 기재되어 있으므로 이하 자세한 설명은 생략하기로 한다.Meanwhile, the engraving mold 14 'may be made of the same aluminum as the conventional material, or may be made of a synthetic resin material of silicon material. In such a synthetic resin material, copper powder or the like may be mixed for thermal conductivity. Since the mold material which may be made of such a synthetic resin material is already described in its own application (Domestic Patent Application No. 98-44772), the following detailed description will be omitted.

그리고, 본 발명에서는 악세사리등을 중창 측면에 부착시키기 위한 보강형성부재(20)가 준비된다. 이러한 보강형성부재(20)는 도 3에 도시된 바와 같이, 별도의 독립부재로 이루어지거나, 상술한 도2의 경우 처럼 조각금형의 내부면에 보강제형성무늬(20') 형태로 형성되기도 하며, 이러한 각 부재는 형성되는 미드솔의 형성부위에 따라 그 사용이 달라진다. 한편, 상기 보강형성부재(20,20')의 내측면은 부착시키고져 하는 보강제(30)가 설치될 수 있도록 약간 홈이져 형성되고 그 테두리에 단턱(20a)이 형성되도록 하여 삽입되는 보강제(30)의 탈락이 방지될 수 있도록 한다. 독립부재로 이루어 질 경우 그 재질은 프레스에 의한 가압시 변형이 발생되지 않을 정도의 강도와 열전도를 위하여 금형과 동일 재질로 이루어지는 것이 바람직하다.In the present invention, a reinforcement forming member 20 for attaching an accessory or the like to the midsole side is prepared. This reinforcement forming member 20 is made of a separate independent member, as shown in Figure 3, or may be formed in the form of a reinforcement forming pattern (20 ') on the inner surface of the carving mold, as in the case of FIG. Each of these members is used differently depending on where the midsole is formed. On the other hand, the inner surface of the reinforcing member (20, 20 ') is formed to be slightly grooved so that the reinforcement (30) to be attached is installed and the reinforcement (30) is inserted so that the step 20a is formed on the edge thereof. ) Can be prevented from falling off. If the material is made of an independent member, the material is preferably made of the same material as the mold for the strength and heat conduction to the extent that deformation does not occur when pressed by the press.

이상에서는 상기와 같은 부재를 이용하여 미드솔 측면에 다양한 형태의 보강제를 설치하는 과정을 통하여 본 발명을 보다 상세하게 설명하기로 한다.In the above, the present invention will be described in more detail through the process of installing various types of reinforcing agents on the side surface of the midsole using such a member.

제 1실시예First embodiment

도 4와 도 5를 참조로 하여 설명하기로 한다.This will be described with reference to FIGS. 4 and 5.

재료 설치Material installation

먼저, 발포팽창된 이브이 판상재료를 절단 가공하거나 또는 인젝션사출에 의해 성형된 프리폼으로 이루어지는 이브이에이 미드솔재료(40)를 준비한다. 상기 미드솔재료(40)는 프레스의 가압,가열에 의한 압축성형을 고려하여 약 1.3배정도의 크기로 반가공된 상태이다. 그리고 상기 미드솔재료(40) 측면에 부착하고져 하는 보강제(30)를 준비한다.First, Eve Y midsole material 40 which consists of preform shape | molded by foam expanded Eve cutting the plate-shaped material or injection injection is prepared. The midsole material 40 is semi-processed to about 1.3 times the size in consideration of compression molding by press and heating of the press. And the reinforcing agent 30 to be attached to the side surface of the midsole material 40 is prepared.

상기 보강제(30)는, 여러 가지로 이루어질 수 있으며, 예들들어 운동화의 경우 상품성을 높이기 위한 인쇄된 컬러무늬를 가지는 악세사리, 등산화의 경우 중창의 측면 강도를 보강하기 위한 고무재질의 강도보강제 등으로 구성할 수도 있으며, 이 이외에도 야간인식표지 등 다양하게 구성될 수 있을 것이다.The reinforcement 30 may be made of a variety of, for example, sneakers with a printed color pattern for improving the productability, in the case of hiking boots composed of a rubber material reinforcement for reinforcing the side strength of the midsole In addition, it may be configured in various ways, such as night recognition signs.

상기 보강제(30)를 보강형성재(20)의 내측면에 고정한다. 이때, 외부에서 인식되는 외면이 보강형성재(20)의 내측면에 밀착되도록 하고, 다른 면에는 핫멜트 접착제를 도포시킨다. 상기 보강재(30)가 보강형성재(20)의 홈부에 설치될 경우에는 홈부 주위의 단턱(20a)에 의해 고정되므로 외부로의 이탈이 방지될 수 있게 된다. 상기의 상태에서 상기 보강재(30)가 설치된 보강형성재(20)를 미드솔재료(40)의 측면에 밀착시킨 상태에서 중간금형(10)에 설치한다.The reinforcement 30 is fixed to the inner side of the reinforcement forming material (20). At this time, the outer surface recognized from the outside to be in close contact with the inner surface of the reinforcing forming material 20, the other surface is applied with a hot melt adhesive. When the reinforcing member 30 is installed in the groove portion of the reinforcing forming member 20, the reinforcing member 30 is fixed by the stepped portion 20a around the groove portion, thereby preventing departure from the outside. The reinforcement forming member 20 provided with the reinforcing member 30 in the above state is installed in the intermediate mold 10 in a state in which the reinforcing forming member 20 is in close contact with the side surface of the midsole material 40.

그리고, 보강재(30)로서, 이브이에이 필름시트 또는 티피알시트 같은 경우에는 열에 의해 미드솔재료에 접착이 이루어지므로 핫멜트 접착제가 필요없이 부착할 수 있게 된다.In addition, as the reinforcing material 30, in the case of an YV film sheet or a TIRP sheet, since the adhesion is made to the midsole material by heat, the hot melt adhesive can be attached without the need.

중창제조Midsole manufacturing

상기와 같이 미드솔재료(40)에 보강재(30)가 구비된 보강형성재(20)가 설치된 상태에서 미드솔 형성을 위한 중간금형(10)의 미드솔형성부내에 위치시킨 상태에서 상부금형을 덮고서 프레싱공정을 수행한다. 좀 더 상세히 설명하면, 고열과 냉각수의 전달이 이루어지는 프레스의 상판과 하판 사이에 상기 금형을 위치시킨 후, 금형의 상하면을 통해 압력과 열전달이 이루어진다. 이때 가해지는 압력은 약 50kgf/㎤ 내지 70kgf/㎤ 정도가 되도록 하고, 온도는 약 140 내지 160℃정도 되도록 한다. 상기 가해지는 압력과 온도에 의해 미드솔재료(40)의 변형이 이루어져 미드솔이 형성되게 된다.Pressing while covering the upper mold in a state in which the midsole forming portion of the intermediate mold 10 for forming the midsole in the state in which the reinforcing forming material 20 provided with the reinforcing material 30 is installed in the midsole material 40 as described above. Perform the process. In more detail, after placing the mold between the upper plate and the lower plate of the press where high heat and cooling water is transferred, pressure and heat transfer are performed through the upper and lower surfaces of the mold. In this case, the pressure applied is about 50 kgf / cm 3 to about 70 kgf / cm 3, and the temperature is about 140 to 160 ° C. The midsole material 40 is deformed by the applied pressure and temperature to form a midsole.

상기 과정을 좀 더 상세히 설명하기로 한다. 상기 가해지는 압력과 온도에 의해 금형(10) 내부에 위치한 미드솔재료(40)는 변형이 발생한다. 즉, 가해지는 압력과 온도에 의해 미드솔재료(40)는 팽창 후 압축되면서 미드솔형성부의 각 섬세한 조각면에 밀착되어 미드솔 외측표면을 형성하게 되며, 이때 최초의 미드솔재료(40)는 경도가 약 35 내지 40을 유지하나, 압축이 이루어진 미드솔은 약 50 내지 55 정도의 경도를 유지하게 된다.The process will be described in more detail. Deformation occurs in the midsole material 40 located inside the mold 10 due to the pressure and temperature applied thereto. That is, the midsole material 40 is compressed and then compressed by the applied pressure and temperature to form an outer surface of the midsole by being in close contact with each of the delicate pieces of the midsole forming portion, wherein the first midsole material 40 has a hardness of about 35 To maintain the 40 to 40, but the compressed midsole is to maintain a hardness of about 50 to 55 degrees.

한편, 상기 미드솔재료(40)의 측면에는 금형과 동일 재질로 이루어진 보강형성재(30)가 위치된 상태이다. 이때 상기 보강형성재(20)는 충분한 강도를 가지므로 프레스에 의한 압력에도 형태 변화없이 그대로 존재할 수 있을 정도의 강도를유지하므로 보강형성재(20)는 미드솔재료(40)의 변형에 상관없이 그 형상을 그대로 유지할 수 있게 된다. 따라서 보강형성재(20) 내측면에 위치된 보강재(30) 역시 상기 보강형성재(20)에 의해 보호되므로 프레스에 의해 가해지는 열과 압력에도 변형없이 그대로 존재할 수 있게 된다. 그리고, 이때 프레스에 의해 가해지는 열에 의해 보강재(30)의 일측면에 도포된 핫멜트 접착제는 미드솔재료(40)의 측면에 보강재(30)가 단단히 접착될 수 있게 한다.Meanwhile, the reinforcement forming member 30 made of the same material as the mold is positioned on the side surface of the midsole material 40. At this time, since the reinforcement forming member 20 has sufficient strength, the reinforcement forming member 20 maintains the strength enough to exist as it is without changing the form even under pressure by the press. The shape can be maintained as it is. Therefore, since the reinforcement member 30 positioned on the inner surface of the reinforcement forming member 20 is also protected by the reinforcement forming member 20, the reinforcement forming member 20 may be present without deformation even in the heat and pressure applied by the press. In this case, the hot melt adhesive applied to one side of the reinforcement 30 by the heat applied by the press enables the reinforcement 30 to be firmly adhered to the side surface of the midsole material 40.

보강형성재(20) 제거에 따른 미드솔(P) 제작Manufacture of midsole (P) by removing reinforcement forming material (20)

열과 가압 그리고 급냉에 의해 미드솔(P)이 제작된 후, 프레스 압력을 해지하고 상부금형을 제거한 후, 꺼내게 된다. 상기의 상태에서 보강형성재(20)를 제거한다. 이때 상기 보강형성재(20) 내측면의 단턱(20a)에 의해 보호되는 보강재(30)는 핫멜트접착제(a)에 의해 미드솔의 측면에 단단히 결합된 상태이므로 보강형성재(20) 제거시 미드솔(P)의 측면부위에는 보강재(30)가 부착되어, 도 5와 같은 형상을 유지하게 된다. 따라서 상기와 같은 방법에서는 별도의 공정이 필요치 않고 미드솔(P)의 제작과 동시에 접착이 가능하므로 작업공정의 단축이 가능하게 된다.After the midsole P is manufactured by heat, pressurization, and quenching, the press pressure is released, the upper mold is removed, and then taken out. The reinforcement forming material 20 is removed in the above state. At this time, since the reinforcement material 30 protected by the step 20a of the inner surface of the reinforcement forming material 20 is firmly coupled to the side surface of the midsole by the hot melt adhesive (a), when the reinforcement forming material 20 is removed, the midsole ( The reinforcing material 30 is attached to the side portion of P), thereby maintaining the shape as shown in FIG. Therefore, the method as described above does not require a separate process and can be bonded at the same time as the production of the midsole (P) it is possible to shorten the work process.

그리고, 상기 방법에서 사용되는 금형(10)은 종래와 동일하므로 별도 금형이 필요치 않으며, 단순히 부착시키고져 하는 보강재(30)의 형상에 따른 보강형성재(20)만 준비함으로서, 다양한 위치에 다양한 형태의 보강재(30)를 설치할 수 있게 된다.In addition, since the mold 10 used in the above method is the same as the conventional method, a separate mold is not required, and by simply preparing the reinforcement forming material 20 according to the shape of the reinforcing material 30 to be attached, various forms at various positions. The reinforcement 30 can be installed.

제 2 실시예Second embodiment

본 실시예에서는 금형 및 보강형성재(30)의 설치 및 회수가 제1실시예와 다르다. 즉, 본 실시예에서는 베이스금형(12')과 조각금형(14')의 두가지로 이루어지는 금형을 사용한다(10'). 그리고, 보강형성재(20)는 별도로 구비되거나 또는 조각금형(14')상에 형성되는 보강형성무늬를 이용하도록 한다. 도시된 도 6을 참고로 하여 설명하기로 한다.In this embodiment, the installation and the recovery of the mold and the reinforcement forming material 30 are different from those in the first embodiment. That is, in this embodiment, a mold consisting of two types, a base mold 12 'and an engraving mold 14', is used (10 '). Then, the reinforcing forming material 20 is provided separately or to use a reinforcing forming pattern formed on the carving mold (14 '). This will be described with reference to FIG. 6.

금형준비Mold preparation

베이스금형(12')은, 상술한 바와 같이, 반복 사용가능한 기본틀로서 사용된다. 조각금형(14')은 별도로 준비한다. 상기 조각금형(14')의 내측면에는 원하는 형상의 미드솔조각무늬가 조각되어 있으며, 이러한 조각금형(14')은 알루미늄 또는 동분말이 혼합된 실리콘수지로 이루어지도록 구성한다. 따라서 상기 베이스금형(12')은 미드솔의 종류에 상관없이 기본틀로서 반복사용되고, 미드솔의 종류에 따른 조각금형(14')만 교체하여 상기 베이스금형(12')에 결합시켜 사용하게 된다.The base mold 12 'is used as a basic frame which can be repeatedly used as mentioned above. Engraving mold 14 'is separately prepared. The inner surface of the engraving mold 14 'is carved a midsole piece pattern of the desired shape, such a mold 14' is configured to be made of a silicon resin mixed with aluminum or copper powder. Therefore, the base mold 12 'is used repeatedly as a base frame regardless of the type of the midsole, and replaces only the engraving mold 14' according to the type of the midsole, and is used by being coupled to the base mold 12 '.

미드솔재료(30) 투입Input midsole material (30)

제1 실시예와 동일한 형태의 미드솔재료(30)를 준비한다. 그리고, 상기 미드솔재료(30)의 측면에 부착될 보강재(30)의 지지역활을 위한 보강형성재(20)는 두가지로 이루어질 수 있다.A midsole material 30 of the same type as in the first embodiment is prepared. In addition, the reinforcement forming material 20 for supporting the local area of the reinforcing material 30 to be attached to the side of the midsole material 30 may be made of two kinds.

첫째로 상기 조각금형(14')의 내측면에 별도의 보강재(30)의 형상에 대응하는 음각이 조각되어 보강형성재(20) 역할을 수행하는 경우이다. 이때, 상기 보강재(30)는 조각금형(14') 내측면에 형성된 보강형성재(20)의 내측면에 밀착시켜 위치시킨다. 이때, 상기 보강재(30)의 남은 면에는 핫멜트접착제(a)를 도포된 상태이다. 상기의 상태에서 조각금형(14')을 베이스금형(12')의 공간부에 위치시킨 후, 미드솔재료(40)를 조각금형(14')의 내부로 위치시킨다.First, the intaglio corresponding to the shape of a separate reinforcing material 30 is carved on the inner surface of the engraving mold 14 'to serve as the reinforcing forming material 20. At this time, the reinforcing material 30 is placed in close contact with the inner surface of the reinforcing forming material 20 formed on the inner surface of the carving mold (14 '). At this time, the hot melt adhesive (a) is applied to the remaining surface of the reinforcing material 30. In the above state, the engraving mold 14 'is positioned in the space portion of the base mold 12', and then the midsole material 40 is placed inside the engraving mold 14 '.

둘째로 상술한 제1실시예와 동일한 보강형성재(20)를 준비하고, 보강재(30)가 구비된 보강형성재(20)를 미드솔재료(40) 측면에 위치시킨다. 이때에는 상기 조각금형(14')이 베이스금형(12')의 공간부에 위치된 상태에서 상기 보강형성재(20)가 구비된 미드솔재료(40)를 조각금형(14')의 내측에 위치시킨다.Secondly, the same reinforcement forming member 20 as in the first embodiment is prepared, and the reinforcing forming member 20 provided with the reinforcing member 30 is positioned on the midsole material 40 side. In this case, the midsole material 40 provided with the reinforcing forming material 20 is positioned inside the engraving mold 14 'while the engraving mold 14' is located in the space portion of the base mold 12 '. Let's do it.

보강형성재(20) 제거에 따른 미드솔 제작Manufacture of midsole by removing reinforcement forming material (20)

열과 가압 그리고 급냉에 의해 미드솔이 제작된 후, 프레스 압력을 해지하고 상부금형을 제거한 후, 압축 성형된 미드솔(P)을 꺼내게 된다.After the midsole is manufactured by heat, pressurization and quenching, the press pressure is released and the upper mold is removed, and then the compression molded midsole P is taken out.

이때, 조각금형(14') 내에 보강형성재(20)가 형성된 경우에는 보강재(30)가 미드솔(P) 측면에 부착된 상태이므로 별도의 조치 없이 바로 측면에 보강재(30)가 부착된 미드솔(P)의 제작이 완료된다. 그러나, 별도의 보강형성재(20)가 구비된 경우에는 제1실시예와 동일하게 보강형성재(20)를 제거하여 완성된 미드솔(P)을 제작하게 된다.At this time, when the reinforcement forming material 20 is formed in the engraving mold 14 ', since the reinforcing material 30 is attached to the side of the midsole P, the midsole to which the reinforcing material 30 is directly attached to the side without additional measures ( Production of P) is completed. However, when the additional reinforcement forming material 20 is provided, the finished midsole P is manufactured by removing the reinforcing forming material 20 as in the first embodiment.

상기 실시예의 경우, 베이스금형(12')은 기본틀로서 반복사용하고, 조각금형(14')만 별도 제작함으로서 금형제작비용이 저렴해지는 잇점이 있다.In the case of the above embodiment, the base mold 12 'is repeatedly used as a base frame, and only the engraving mold 14' is manufactured separately, thereby making the mold manufacturing cost low.

이상에서 설명한 바와 같이, 본 발명에 따르면, 미드솔의 측면테두리에 다양한 형태의 보강재를 부착함에 있어, 별도의 추가공정 없이 미드솔의 압축성형과 동시에 이루어지므로 제작공정의 단축 및 작업 능률 향상으로 인하여 생산성의 증대 및 미드솔 생산원가가 저렴해지는 효과가 있다.As described above, according to the present invention, in attaching various types of reinforcement to the side border of the midsole, it is made simultaneously with the compression molding of the midsole without any additional process, so that the production process is shortened and the work efficiency is improved. Increasing and reducing the cost of producing midsole.

그리고, 별도의 보강형성재를 이용함으로서 다양한 위치에 다양한 형태의 보강제 부착이 쉬어지며, 각 형상변경에 따른 금형전체의 변형이 필요없으므로 다품종 소량생산이 가능한 다른 효과도 있다.In addition, by using a separate reinforcing forming material, it is easy to attach various types of reinforcing agents at various positions, and there is another effect that enables the production of small quantities of various types since there is no need for deformation of the entire mold according to each shape change.

또한, 형상변형에 따른 금형제작이 불필요하므로 금형제작비용이 저렴해지고 생산기일의 단축에 의해 미드솔이 저렴해지는 또 다른 효과도 있다.In addition, since mold manufacturing is not necessary due to shape deformation, there is another effect that the mold manufacturing cost is lowered and the midsole is made cheaper by shortening the production date.

Claims (5)

내측면에 소정의 조각무늬가 형성된 미드솔금형과 상부금형을 준비하는 과정과;Preparing a midsole mold and an upper mold having predetermined engravings on the inner surface thereof; 발포성형된 이브이에이(E.V.A)재질로 이루어지고, 원하는 형상보다 약 1.3 내지 1.5배 정도 크기의 반가공 상태로 이루어지는 미드솔재료를 준비하는 과정과;Preparing a midsole material made of a foamed Y.E. (E.V.A) material and having a semi-processed state about 1.3 to 1.5 times larger than a desired shape; 알루미늄 또는 동분말이 혼합된 실리콘합성수지재로 이루어지는 보강형성재의 내측면에 외부면에 핫멜트접착제가 도포된 보강재를 위치시키고, 상기 접착제가 도포된 면이 상기 미드솔재료의 측면에 접하도록 보강형성재를 미드솔재료 측면에 고정시키는 과정과;Place the reinforcing material coated with a hot melt adhesive on the outer surface of the reinforcing forming material made of a silicone synthetic resin material mixed with aluminum or copper powder, and reinforcing the forming material so that the surface coated with the adhesive is in contact with the side surface of the midsole material. Fixing the side of the midsole material; 상기 보강형성재가 고정된 미드솔재료를 금형상에 위치시키고, 가압,가열 및 냉각에 의해 미드솔의 압축 성형과 보강재의 미드솔측면 접착이 이루어 지도록 프레싱공정을 수행하는 과정; 그리고Placing the midsole material on which the reinforcement forming member is fixed on the mold, and performing pressing by pressing, heating, and cooling to achieve compression molding of the midsole and adhesion of the midsole side of the reinforcing material; And 탈형시켜 보강재가 부착된 미드솔을 완성시키는 과정으로 이루어져;Demolding to complete the midsole with reinforcement; 미드솔의 압축성형과 동시에 보강재의 측면부착이 이루어지는 것을 특징으로 하는 측면 보강재가 구비된 이브이에이 미드솔의 신발중창 제조 방법.A method of manufacturing a shoe sole of Yves midsole provided with a side reinforcement, characterized in that the side of the reinforcement is attached at the same time as the compression molding of the midsole. 제 1 항에 있어서,The method of claim 1, 상기 미드솔금형은, 미드솔조각무늬가 형성된 단일금형으로 이루어짐을 특징으로 측면 보강재가 구비된 이브이에이 미드솔의 신발중창 제조 방법.The midsole mold is a shoe sole manufacturing method of Yves midsole provided with a side reinforcement, characterized in that consisting of a single mold formed with a midsole piece pattern. 제 1 항에 있어서,The method of claim 1, 상기 미드솔금형은,The midsole mold, 알루미늄 재질로 이루어지고, 공간부가 형성된 베이스 금형과;A base mold made of aluminum and having a space portion; 상기 공간부에 분리 결합되고, 알루미늄 또는 동분말이 혼합된 실리콘함성수지재로 이루어지며 내측면에 미드솔조각무늬가 구비된 조각금형으로 이루어짐을 특징으로 하는 측면 보강재가 구비된 이브이에이 미드솔의 신발중창 제조 방법.Shoe sole of Yves midsole provided with a side reinforcement, which is separated and bonded to the space portion, made of a silicon-containing resin material mixed with aluminum or copper powder, and made of a piece mold having a midsole piece pattern on an inner surface thereof. Manufacturing method. 제 3 항에 있어서,The method of claim 3, wherein 상기 보강형성재는,The reinforcement forming material, 조각금형 내측면에 보강재의 형상에 대응하는 음각 조각형성으로 이루어짐을 특징으로 하는 측면 보강재가 구비된 이브이에이 미드솔의 신발중창 제조 방법.A method of manufacturing a shoe sole of Yves midsole provided with a side reinforcement, characterized in that the inner surface of the engraving mold is formed in the engraved piece corresponding to the shape of the reinforcement. 제 1 항 또는 제 3 항중 어느 하나의 항에 있어서,The method according to any one of claims 1 to 3, 상기 보강형성재는,The reinforcement forming material, 내측면에 보강재가 위치되는 홈이 형성되고, 보강재의 모양에 대응하는 형상의 알루미늄 재질로 이루어지는 독립부재로 이루어짐을 특징으로 하는 측면 보강재가 구비된 이브이에이 미드솔의 신발중창 제조 방법.A groove in which a reinforcement is positioned on an inner surface thereof, and the sole of the YEI midsole provided with the side reinforcement, characterized in that the independent member is made of an aluminum material having a shape corresponding to the shape of the reinforcement.
KR1020000042490A 2000-07-24 2000-07-24 method for manufacturing E.V.A midsole having lateral enforcement KR20020009127A (en)