KR20010103132A - Film for preservation and method for making the same - Google Patents

Film for preservation and method for making the same Download PDF

Info

Publication number
KR20010103132A
KR20010103132A KR1020010066955A KR20010066955A KR20010103132A KR 20010103132 A KR20010103132 A KR 20010103132A KR 1020010066955 A KR1020010066955 A KR 1020010066955A KR 20010066955 A KR20010066955 A KR 20010066955A KR 20010103132 A KR20010103132 A KR 20010103132A
Authority
KR
South Korea
Prior art keywords
transparent
film
members
paint
black
Prior art date
Application number
KR1020010066955A
Other languages
Korean (ko)
Inventor
박창복
이태관
Original Assignee
박창복
이태관
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박창복, 이태관 filed Critical 박창복
Priority to KR1020010066955A priority Critical patent/KR20010103132A/en
Publication of KR20010103132A publication Critical patent/KR20010103132A/en

Abstract

본 발명은, 방향에 따라 빛을 차단하므로서 타인이 알아볼 수 없도록 보안을 유지하고자 하는 부분에 사용되는 보안용필름 및 이를 제작하는 방법에 관한 것으로서, 원통형 또는 다각형의 형상을 가진 투명한 봉인 투명원통부재(180)를 준비하는 단계와, 상기 투명원통부재(180)를 준비한 후 빛을 차단하도록 외측면에 검은색의 페인트인 페인트부재(182)로 칠하는 단계와, 상기 페인트부재(182)를 칠한 후 상기 투명원통부재(180)를 일정한 크기로 절단하여 투명관통부재(184)의 조각을 만드는 단계와, 상기 복수개의 투명관통부재(184)를 차례로 배열한 후 상기 복수개의 투명관통부재(184)의 상하측면에 접착부재(150)를 도포한 후 그 상하면에 상기 투명필름부재(110)를 놓는 단계와, 상기 복수개의 투명필름부재(110)를 올려 놓은 후 일정한 온도로 가열된 통상의 히터형 롤러로 상기 투명필름부재(110)의 외측면을 이동하면서 열융착으로 상기 복수개의 투명필름부재(110) 및 상기 복수개의 투명관통부재(184)가 결착되도록 하는 단계로 구성되어 있는 것을 특징으로 한다.The present invention relates to a security film and a method for manufacturing the same, which is used for a part to maintain security so that others can not recognize by blocking light according to the direction, a transparent sealed transparent cylindrical member having a cylindrical or polygonal shape ( 180) and after preparing the transparent cylindrical member 180, painting with a paint member 182, which is a black paint on the outer surface to block the light, and after painting the paint member 182 Cutting the transparent cylindrical member 180 to a predetermined size to form a piece of the transparent through member 184, and after arranging the plurality of transparent through members 184 in sequence, the plurality of transparent through members 184 Applying the adhesive member 150 on the upper and lower sides and then placing the transparent film member 110 on the upper and lower surfaces, and after placing the plurality of transparent film member 110, the ordinary heated to a constant temperature It characterized in that it comprises the step of allowing the plurality of transparent film member 110 and the plurality of transparent through member 184 to bind by moving the outer surface of the transparent film member 110 with a rotor roller. do.

Description

보안용필름 및 이를 제작하는 방법{FILM FOR PRESERVATION AND METHOD FOR MAKING THE SAME}Security film and how to produce it {FILM FOR PRESERVATION AND METHOD FOR MAKING THE SAME}

본 발명은 보안용필름 및 이를 제작하는 방법에 관한 것으로서, 특히 방향에 따라 빛을 차단하므로서 타인이 알아볼 수 없도록 보안을 유지하고자 하는 부분에 사용되는 보안용필름 및 이를 제작하는 방법에 관한 것이다.The present invention relates to a security film and a method for manufacturing the same, and more particularly, to a security film used in the part to maintain security so that others can not recognize by blocking the light according to the direction and a method for manufacturing the same.

종래의 보안은 외부인이 출입을 하지 못하도록 하므로서 서류 및 관련 내용에 대한 보안을 유지하여 왔으나, 이러한 보안 방법은 현대와 같이 복잡한 시대에 있어서는 적합하지 못하며, 특히 타인과 자연스럽게 관계를 유지하면서도 필요한 부분에 대해서만 집중적으로 보안을 유지할 수 없는 문제점이 있었다.Conventional security has maintained the security of documents and related contents by preventing outsiders from entering and exiting, but such security methods are not suitable in the complicated times as in modern times, especially for those parts that need to be naturally related to others. There was a problem that can not be intensively maintained security.

상기와 같은 문제점을 해결하기 위한 목적은, 타인과 접촉이 빈번하면서도일정한 수준의 보안을 유지하여야 하는 경우 보안을 유지할 수 있는 보안용필름 및 이를 제작하는 방법을 제공하는데 있다.It is an object to solve the above problems, to provide a security film and a method of manufacturing the same that can maintain security when frequent contact with others and to maintain a certain level of security.

그리고 은행의 단말기 등과 같이, 주위의 많은 사람과 함께 업무처리를 하는 경우, 자신에 필요한 관련 데이터에 대해 보안을 유지하기 위해서 사용자가 작업하게 되는 위치에 대해 일정한 각도에 대해서만 관련 데이터를 볼 수 있도록 조작하므로서 편리하게 작업을 할 수 있는 보안용필름 및 이를 제작하는 방법을 제공하는데 있다.And when working with a lot of people around you, such as a terminal in a bank, you can view the related data only at a certain angle with respect to the location where you are working in order to secure the relevant data needed for yourself. Therefore, to provide a security film and a method of producing the same that can be conveniently worked.

그리고 본 발명은 상기와 같은 보안용필름 및 이를 제작하는 방법을 형성하기 위한 다양한 방법을 이용하여 제조하므로서 비용 및 제조원가를 절감할 수 있는 보안용필름 및 이를 제작하는 방법을 제공하는데 있다In another aspect, the present invention provides a security film and a method for producing the same that can be produced by using a variety of methods for forming the security film and a method for manufacturing the same as described above to reduce the cost and manufacturing costs.

상기와 같은 목적을 달성하기 위한 본 발명의 보안용필름 및 이를 제작하는 방법는, 원통형 또는 다각형의 형상을 가진 투명한 봉인 투명원통부재(180)를 준비하는 단계와, 상기 투명원통부재(180)를 준비한 후 빛을 차단하도록 외측면에 검은색의 페인트인 페인트부재(182)로 칠하는 단계와, 상기 페인트부재(182)를 칠한 후 상기 투명원통부재(180)를 일정한 크기로 절단하여 투명관통부재(184)의 조각을 만드는 단계와, 상기 복수개의 투명관통부재(184)를 차례로 배열한 후 상기 복수개의 투명관통부재(184)의 상하측면에 접착부재(150)를 도포한 후 그 상하면에 상기 투명필름부재(110)를 놓는 단계와, 상기 복수개의 투명필름부재(110)를 올려 놓은 후 일정한 온도로 가열된 통상의 히터형 롤러로 상기 투명필름부재(110)의 외측면을 이동하면서 열융착으로 상기 복수개의 투명필름부재(110) 및 상기 복수개의 투명관통부재(184)가 결착되도록 하는 단계로 구성되어 있는 것을 특징으로 한다.Security film and a method of manufacturing the present invention for achieving the above object, the step of preparing a transparent sealing transparent cylindrical member 180 having a cylindrical or polygonal shape, and preparing the transparent cylindrical member 180 After the step of painting with a paint member 182 which is a black paint on the outer surface to block the light, and after painting the paint member 182, the transparent cylindrical member 180 is cut to a certain size to the transparent through member ( 184) and the plurality of transparent through-members 184 are arranged in sequence, and then the adhesive member 150 is applied to the upper and lower sides of the plurality of transparent through-members 184, and then the upper and lower surfaces thereof are transparent. Laying the film member 110, and by placing the plurality of transparent film member 110 to the heat-sealing while moving the outer surface of the transparent film member 110 with a conventional heater roller heated to a constant temperature remind Several transparent film member 110, and is characterized in that it is composed of a step of the plurality of transparent penetrating member 184 so that the engagement.

도 1은 본 발명의 일 실시예에 대한 사시도이며,1 is a perspective view of an embodiment of the present invention,

도 2는 본 발명의 일 실시예를 제조하는 공정중 접착하는 공정이고,2 is a bonding step in the process of manufacturing an embodiment of the present invention,

도 3은 본 발명이 접착된 후 일정한 크기로 수직 또는 일정한 각도를 가지고 절단하는 공정이며,3 is a process of cutting having a vertical or constant angle to a constant size after the present invention is bonded,

도 4는 도 3에서 일정한 절단된 양측면에 접착부재를 접착한 후 투명필름부재를 접착하는 공정이며,Figure 4 is a process of adhering the transparent film member after adhering the adhesive member to both sides cut constant in Figure 3,

도 5는 본 발명의 다른 실시예로서 검은 페인트등을 이용하여 작업한 상태를 도시한 조립도이며,5 is an assembly view showing a state in which the working using black paint as another embodiment of the present invention,

도 6은 본 발명의 또 다른 실시예로서 투명관통부재가 경사지도록 형성되어 있는 사시도이며,6 is a perspective view in which the transparent through member is inclined as another embodiment of the present invention;

도 7은 도 6에 대한 정면도이며,7 is a front view of FIG. 6,

도 8은 본 발명의 또 다른 실시예를 도시한 측면도이며,8 is a side view showing another embodiment of the present invention,

도 9는 본 발명의 또 다른 실시예를 제작하는 과정에 대한 흐름도이며,9 is a flowchart illustrating a process of manufacturing another embodiment of the present invention,

도 10은 본 발명의 투명원통부재 자체에 대한 또 다른 실시예에 대한 사시도이며,10 is a perspective view of another embodiment of the transparent cylindrical member itself of the present invention,

도 11은 본 발명의 투명원통부재에 대한 또 다른 실시예에 대한 사시도이며,11 is a perspective view of another embodiment of a transparent cylindrical member of the present invention,

도 12는 본 발명의 투명관통부재에 대한 또 다른 실시예에 대한 사시도이다.12 is a perspective view of another embodiment of the transparent through member of the present invention.

<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>

100 : 보안용필름 110 : 투명필름부재100: security film 110: transparent film member

130, 132, 184 : 투명관통부재 140, 142 : 흑색필름부재130, 132, 184: transparent through member 140, 142: black film member

150 : 접착부재 160, 182 : 페인트부재150: adhesive member 160, 182: paint member

180 : 투명원통부재 187 : 중간흑색필름부재180: transparent cylindrical member 187: intermediate black film member

200 : 커팅부재200: cutting member

본 발명의 보안용필름 및 이를 제작하는 방법에 대한 실시예와 관련된 기술을 첨부된 도면을 참고로 기술하면 다음과 같다.Referring to the accompanying drawings, a technology related to an embodiment of the security film of the present invention and a method for manufacturing the same are as follows.

도 1은 본 발명의 개략적인 사시도를 도시한 것으로서, 100은 본 발명의 보안용필름 및 이를 제작하는 방법에 대한 필름으로서, 상기 보안용필름(100)의 양측면에 형성되는 통상의 투명한 P.C재질인 복수개의 투명필름부재(110)와, 상기 복수개의 투명필름부재(110)의 내측에 일체로 복수개가 교대로 형성되어 있으며 투명한 재질로 형성되어 있는 투명관통부재(130)와, 상기 복수개의 투명필름부재(110)의 내측에 일체로 복수개가 교대로 형성되어 있으며 검은색을 가지고 있는 흑색필름부재(140)와, 상기 복수개의 투명관통부재(130)와 복수개의 흑색필름부재(140)가 교대로 결착되도록 하고 상기 투명관통부재(130) 및 흑색필름부재(140)가 상기 복수개의 투명필름부재(110)와 일체로 접착되도록 하는 접착부재(150)로 구성되어 있다.Figure 1 shows a schematic perspective view of the present invention, 100 is a film for the security film of the present invention and a method for manufacturing the same, which is a conventional transparent PC material formed on both sides of the security film (100) A plurality of transparent film member 110, the transparent through member 130 is formed integrally with the plurality of transparent film member 110, the inner side of the plurality of transparent film member 110 is formed of a transparent material, and the plurality of transparent film A plurality of black film members 140 are alternately formed inside the member 110 and have a black color, and the plurality of transparent through members 130 and the plurality of black film members 140 alternately. The transparent member 130 and the black film member 140 is configured to be bonded to the adhesive member 150 to be integrally bonded with the plurality of transparent film member 110.

상기 투명필름부재(110)는 상하로 복수개 형성되어 있는 것이며, 투명한 재질로 형성되어 있으며 재질은 통상적으로 사용되는 P.C재질을 사용하나, 그외에 다른 투명한 비닐계열 또는 플라스틱 계열의 재질을 사용할 수도 있는 것이다.The transparent film member 110 is formed in a plurality of up and down, it is formed of a transparent material and the material is used a conventional PC material, but other transparent vinyl-based or plastic-based material may be used. .

그리고 상기 투명관통부재(130)는 투명한 재질로 형성되어 있으며, 상기 흑색필름부재(140)와는 일정한 간격으로 규칙적으로 형성되어 있으나, 필요한 경우에는 불규칙적으로 형성할 수도 있으며, 그리고 필요한 경우에는 일정한 각도를 가지고 형성될 수도 있는 것이다.And the transparent through member 130 is formed of a transparent material, and is formed at regular intervals with the black film member 140, but if necessary may be irregularly formed, and if necessary a constant angle It may be formed with.

즉, 상기 투명관통부재(130)의 형상이 도 1에 도시된 바와 같이 단순히 사각형 또는 직사각형으로 복수개 규칙적으로 형성되는 것이 아니라, 비규칙적으로 형성될 수도 있으며, 이러한 경우에는 도 8에 도시된 바와같이, 상기 투명관통부재(134)가 특정부분에서 특히 얇은 부분이 집중되어 있고, 상기 흑색필름부재(144)의 두께는 일정하다고 할 경우에는 투명한 상기 투명관통부재(134)가 얇게 형성되어 있기 때문에 그만큼 타인이 얇게 형성되어 있는 부분의 글자 또는 그림 등을 보기가 어려우며, 따라서 이러한 형태로 구성하게 되면 보안유지가 더욱 필요한 부분에 대해서 집중적으로 적용될 수 있는 것이다.That is, the shape of the transparent through member 130 is not simply formed as a plurality of regular or rectangular as shown in Figure 1, but may be formed irregularly, in this case, as shown in Figure 8 When the transparent through member 134 is particularly thin in a specific portion, and the thickness of the black film member 144 is constant, since the transparent through member 134 is formed thin, the transparent through member 134 is thin. It is difficult to see the letters or pictures of thinly formed parts, so if configured in such a form, it can be intensively applied to the parts that need more security maintenance.

그리고 상기 투명관통부재(130,132,134)는 투명한 테이프를 사용하나, 필요한 경우 투명한 P.E.T의 재질을 사용하는 것이 바람직하다.And the transparent through member 130, 132, 134 uses a transparent tape, if necessary, it is preferable to use a transparent P.E.T material.

그리고 본 발명의 다른 실시예는 도 6 및 도 7에 도시된 바와 같이, 상기 투명관통부재(132)가 일정한 각도로 경사지게 형성될 수 있으며, 이러한 경우에는 도 1에서와 달리 사용자가 특정한 각도에서 보기 용이하도록 경사각을 조절할 경우 편리한 경우이며, 도 6에 도시된 각도는 도 3에서 절단시 수직이 아니라 일정한 각도를 가지고 절단하게 되면 절단면과 상기 투명관통부재(132) 및 흑색필름부재(142)와 다양한 각도를 유지하게 되는 것으로서 필요에 따라 다양하게 각도를 조절할 수 있는 것이다.6 and 7, the transparent through member 132 may be formed to be inclined at a predetermined angle. In this case, unlike in FIG. 1, the user may view at a specific angle. It is a convenient case when adjusting the inclination angle to facilitate, the angle shown in Figure 6 is not vertical to cut at the time of cutting in Figure 3 when cutting at a certain angle and the cutting surface and the transparent through member 132 and black film member 142 and various As the angle is maintained, the angle can be adjusted in various ways as needed.

그리고 상기 흑색필름부재(140)는 상기 투명관통부재(130)와 함께 복수개 형성되어 있는 것으로서, 상기 투명관통부재(130)와 흑색필름부재(140)에는접착부재(150)에 의해서 결착되는 것이며, 상기 흑색필름부재(140)는 검은색으로 빛을 차단하도록 통상적으로 검은 필름이 사용되나, 필요한 경우 도 5에 도시된 바와 같이, 통상적으로 시중에 판매되는 검은 페이트 또는 유성물감 등을 이용하여 사용할 수도 있는 것이다.In addition, the black film member 140 is formed in plural together with the transparent through member 130, and is bonded to the transparent through member 130 and the black film member 140 by an adhesive member 150. The black film member 140 is typically used a black film to block the light in black, if necessary, as shown in Figure 5, can also be used using a commercially available black paint or oil paint, etc. It is.

그리고 이러한 경우에는 상기 접착부재(150)가 도 1에 도시된 바와 같이, 상기 흑색필름부재(140)의 양측면에 접착되어 상기 복수개의 투명관통부재(130)와 결착되도록 형성되나, 도 5에서와 같이 검은 페인트 또는 유성 또는 수성 물감으로 형성된 페인트부재(160)를 이용하여 빛을 차단하고자 하는 경우에는 상기 접착부재(150)를 상기 페인트부재(160)의 일측면에만 사용하게 되므로서, 비용절감 및 작업성을 향상시킬 수 있는 것이다.In this case, as shown in FIG. 1, the adhesive member 150 is bonded to both sides of the black film member 140 to be bound to the plurality of transparent through members 130, but as illustrated in FIG. 5. When the light is to be blocked using the paint member 160 formed of black paint or oily or water-based paint, the adhesive member 150 is used only on one side of the paint member 160, thereby reducing costs and It can improve workability.

그리고 도 1의 L1과 L2의 관계는 보안을 유지하고자 하는 범위 또는 제작비용 또는 사용자의 사용상태 등에 관계가 되는 것으로서, 예를 들어 상기 L1이 증가하게 되면 투시할 수 있는 시야의 각도가 좁아지게 되어 보안성이 우수해지나, 절단시 두께가 증가하게 되어 작업성이 좋아지게 되며, L2가 증가하게 되면 반대로 투시할 수 있는 시야가 넓어지게 되어 보안성이 저하되나, 단위폭당 비교하여 보면, 상기 투명관통부재(130) 및 흑색필름부재(140)의 개수가 적게 되어 작업성이 좋아지는 특징이 있다.In addition, the relationship between L1 and L2 of FIG. 1 is related to a range to maintain security or a manufacturing cost or a user's use state. For example, when L1 is increased, the angle of view that can be viewed is narrowed. The security is excellent, but the thickness is increased during cutting, the workability is improved, and when the L2 is increased, the visibility that can be viewed on the contrary is widened, and the security is deteriorated. As the number of the penetrating member 130 and the black film member 140 is reduced, workability is improved.

그리고 상기에 기술한 실시예를 제작하는 과정을 기술하면, 먼저 도 2에 도시된 바와 같이, 흑색필름부재(140)의 상단부에 상기 접착부재(150)를 칠하는 단계와, 상기 단계를 수행한 후 그 위에 투명관통부재(130)를 올려놓은 단계와, 상기단계에서 투명관통부재(130)가 올려진 후에는 도시되지 않은 통상의 히터롤러를 이용하여 열융작으로 접착하는 단계와, 상기 열융착으로 접착한 후 상기와 같은 과정을 계속적으로 하여 일정한 두께가 되도록 형성하는 단계와, 상기 단계를 수행한 후 도 3에 도시된 바와 같이, 커팅부재(200)를 이용하여 일정한 두께(ℓ)로 수직 또는 일정한 각도를 가지고 절단하는 단계와, 상기 단계에서 일정한 두께로 절단한 후 도 4에서와 같이 상기 투명관통부재(130)의 양측면에 상기 복수개의 투명필름부재(110)가 접착되어 일체로 형성되도록 상기 접착부재(150)를 칠하는 단계와, 상기 단계에서 상기 접착부재(150)를 칠한 후 상기에서와 같이 히터롤러를 이용하여 열융착하여 상기 복수개의 투명관통부재(130) 및 흑색필름부재(140)와 상기 복수개의 투명필름부재(110)를 일체로 결착하는 단계로 구성되어 있다.And describing the process of manufacturing the above-described embodiment, first, as shown in Figure 2, the step of painting the adhesive member 150 on the upper end of the black film member 140, and performing the step After placing the transparent through member 130 thereon, and after the transparent through member 130 is raised in the step of using a conventional heater roller not shown in the step of heat fusion bonding, and the heat fusion After the step of bonding to continue to form a constant thickness as described above, and after performing the step, as shown in Figure 3, by using a cutting member 200 vertical to a constant thickness (ℓ) Or cutting at a predetermined angle, and after cutting to a predetermined thickness in the step, as shown in Figure 4 the plurality of transparent film member 110 is bonded to both sides of the transparent through member 130 is formed integrally Painting the adhesive member 150 so as to apply the adhesive member 150 in the step, and then thermally fusion using the heater roller as described above to form the plurality of transparent through members 130 and the black film member. 140 and the plurality of transparent film member 110 is integrally bound.

그리고 본 발명의 보안용필름을 제작하는 또 다른 실시예는 도 5에 개략적으로 도시된 바와 같으며, 상기에 기술한 실시예와 차이점은 상기 투명관통부재(130)의 일측면에 검은 페인트 또는 수성 또는 유성 물감 등으로 구성된 상기 페인트부재(160)를 칠한 후 그 외측면에 상기 접착부재(150)로 접착하여 복수개의 상기 투명관통부재(130)가 일체로 형성된 후에는 도 3과 같은 형태로 되고, 이후의 공정은 상기에 기술한 실시예의 공정과 동일하다.And another embodiment of producing the security film of the present invention is as shown schematically in Figure 5, the difference from the above-described embodiment is a black paint or water-based on one side of the transparent through member 130 Or after painting the paint member 160 composed of oil paints, etc. after the adhesive member 150 is formed on the outer surface of the plurality of transparent through member 130 is formed integrally as shown in Figure 3 The subsequent steps are the same as those in the above-described embodiment.

본 발명의 또 다른 실시예는 도 9 내지 도 12에 도시된 바와 같으며, 상기에 기술한 실시예와 차이점은, 상기에 기술한 실시예는 상기 투명관통부재(130)의 형상이 사각형 또는 경사진 사각형 또는 배열이 불규칙한 사각형으로 형성되므로서도 1에 도시된 바와 같이, 타인이 (다) 또는 (바)에 있는 경우 상기 보안용필름(100)의 방향을 변경하여 경사각을 조절하면 타인이 내용을 볼 수 없도록 하는 것이나, 타인이 (나) 및 (마)의 방향에 있는 경우에는 비록 사용자가 상기 보안용필름(100)을 어떠한 형태로 경사지게 설치하더라도 상기 복수개의 흑색필름부재(140)에 의해서 빛이 차단되지 않기 때문에 외부에서 타인이 용이하게 볼수 있는 단점이 있는 것이다.Another embodiment of the present invention is as shown in Figures 9 to 12, the difference from the above-described embodiment, the above-described embodiment is the shape of the transparent through member 130 is rectangular or light As shown in FIG. 1 because the photo rectangle or the array is formed as an irregular rectangle, when the other person is in (C) or (B), the other person adjusts the inclination angle by changing the direction of the security film 100. If the other person is in the direction of (B) and (E), even if the user installs the security film 100 in any form inclined by the plurality of black film member 140 Because it is not blocked, there is a disadvantage that others can easily see from the outside.

그러나 도 8에 기술한 실시예는 상기에 기술한 실시예의 단점을 보완하기 위한 것으로서, 즉 사용자가 필요로 하는 방향에서만 내용을 관찰할 수 있고 상기에 기술한 (나) 및 (마)와 같은 방향에서도 관찰을 할 수없도록 하므로서 보안의 효과를 극대화하기 위한 것이다.However, the embodiment described in FIG. 8 is to compensate for the shortcomings of the above-described embodiment, that is, the content can be observed only in the direction required by the user, and the same direction as (B) and (E) described above. It is to maximize the effect of security by not being able to observe in.

즉, 상기 투명필름부재(110)의 내측에 배설되어 있는 복수개의 조각으로 형성되어 있는 투명관통부재(184)와, 상기 복수개의 투명관통부재(184)의 외측면에 검은색으로 빛을 차단하는 페이트로 칠해져 있는 페인트부재(182)와, 상기 복수개의 페인트부재(182)의 상하면에 상기 복수개의 투명필름부재(110)와 접착시키기 위해 접착제인 접착부재(150)로 형성되어 있다.That is, to block light in black on the outer surface of the transparent through member 184 formed of a plurality of pieces disposed inside the transparent film member 110 and the plurality of transparent through member 184. The paint member 182 is painted with a paint and an adhesive member 150 which is an adhesive for bonding the plurality of transparent film members 110 to the upper and lower surfaces of the plurality of paint members 182.

본 발명의 다른 실시예를 제작하는 단계를 기술하면, 먼저, 원통형 또는 다각형의 형상을 가진 투명한 봉인 투명원통부재(180)를 준비하는 단계와, 상기 투명원통부재(180)를 준비한 후 빛을 차단하도록 외측면에 검은색의 페인트인 페인트부재(182)로 칠하는 단계와, 상기 페인트부재(182)를 칠한 후 상기 투명원통부재(180)를 일정한 크기로 절단하여 투명관통부재(184)의 조각을 만드는단계와, 상기 복수개의 투명관통부재(184)를 차례로 배열한 후 상기 복수개의 투명관통부재(184)의 상하측면에 접착부재(150)를 도포한 후 그 상하면에 상기 투명필름부재(110)를 놓는 단계와, 상기 복수개의 투명필름부재(110)를 올려 놓은 후 일정한 온도로 가열된 통상의 원통형 히터형 롤러로 상기 투명필름부재(110)의 외측면을 이동하면서 상기 접착부재(150)를 열융착시키므로서 상기 복수개의 투명필름부재(110) 및 상기 복수개의 투명관통부재(184)가 결착되도록 하는 단계로 구성되어 있다.Referring to the steps of manufacturing another embodiment of the present invention, first, preparing a transparent sealing transparent cylindrical member 180 having a cylindrical or polygonal shape, and after preparing the transparent cylindrical member 180 to block the light Painting the outer surface with a paint member 182 which is black paint, and after painting the paint member 182, cutting the transparent cylindrical member 180 to a predetermined size to cut the transparent through member 184. And arranging the plurality of transparent through members 184 in sequence, and then applying an adhesive member 150 to upper and lower sides of the plurality of transparent through members 184, and then placing the transparent film member 110 on upper and lower surfaces thereof. And placing the plurality of transparent film members 110, and then moving the outer surface of the transparent film member 110 to a general cylindrical heater-type roller heated to a constant temperature, wherein the adhesive member 150 is moved. Heat-sealed The plurality of transparent film member 110 and the plurality of transparent through member 184 is configured to bind.

그리고 도 10 내지 도 12는 본 발명의 또 다른 실시예를 나타낸 것으로서, 상기에 도시한 실시예는 도 9에 도시된 실시예와 달리, 상기 투명관통부재(184)가 반드시 원형이 아니라, 삼각형, 사각형 또는 다각형 또는 타원형 등으로 형성될 수 있으며, 그리고 도 11에서는 상기 투명관통부재(184)의 내측에 복수개의 흑색페인트인 중간흑색필름부재(187)를 형성하고 있다는 점이며, 도 12는 도 7에 도시된 바와 같이, 도 8의 투명원통부재(180)에 페인트부재(182)를 칠한 후 절단시 수직으로 절단하지 않고 일정한 각도를 가지고 절단할 경우 형성되는 것으로서, 예를 들어 원형 또는 사각형의 모양만을 도시하였으나, 본 발명은 상기에 기술한 내용에 한정되는 것이 아니라 그외의 다각형의 형상에도 적용되는 것이다.10 to 12 show another embodiment of the present invention, which is different from the embodiment shown in FIG. 9, wherein the transparent through member 184 is not necessarily circular, triangular, Square or polygonal or elliptical, etc., and in FIG. 11 is a middle black film member 187, which is a plurality of black paint is formed on the inner side of the transparent through member 184, Figure 12 is FIG. As illustrated in FIG. 8, the paint member 182 is coated on the transparent cylindrical member 180 of FIG. 8, and is formed when the cutting member is cut at a predetermined angle without being cut vertically, for example, in the shape of a circular or square shape. Although shown only, the present invention is not limited to the above description but also applies to other polygonal shapes.

상기와 같이 구성된 본 보안용필름 및 이를 제작하는 방법은, 타인과 접촉이 빈번하면서도 일정한 수준의 보안을 유지하여야 하는 경우 필요하며, 특히 은행의 단말기 등과 같이, 주위의 많은 사람과 함께 업무처리를 하는 경우, 자신에 필요한관련 데이터에 대해 보안을 유지하기 위해서 사용자가 작업하게 되는 위치에 대해 일정한 각도에 대해서만 관련 데이터를 볼 수 있도록 조작하므로서 편리하게 작업을 할 수 있는 발명이다.The security film configured as described above and a method of manufacturing the same are necessary when frequent contact with others and maintaining a certain level of security, in particular, such as a terminal of the bank, such as a terminal to handle business with a lot of people In this case, in order to maintain security of related data required for the user, the invention can be conveniently operated by manipulating the related data to be viewed only at a certain angle with respect to the position at which the user works.

Claims (9)

보안용필름(100)의 양측면에 형성되는 투명한 P.C재질인 복수개의 투명필름부재(110)와, 상기 복수개의 투명필름부재(110)의 내측에 일체로 규칙적 또는 비규칙적으로 교대로 형성되어 있으며 투명한 재질인 투명테이프로 형성되어 있는 투명관통부재(130)와, 상기 복수개의 투명필름부재(110)의 내측에 일체로 복수개가 교대로 형성되어 있으며 검은색을 가지고 있는 흑색필름부재(140)와, 상기 복수개의 투명관통부재(130)와 복수개의 흑색필름부재(140)가 교대로 결착되도록 하고 상기 투명관통부재(130) 및 흑색필름부재(140)가 상기 복수개의 투명필름부재(110)와 일체로 접착되도록 하는 통사의 피이접착제인 접착부재(150)로 구성되어 있는 것을 특징으로 하는 보안용필름.A plurality of transparent film members 110, which are transparent PC materials formed on both sides of the security film 100, and are formed integrally or regularly alternately integrally inside the plurality of transparent film members 110 and are transparent A transparent through member 130 formed of a transparent tape made of a material, a plurality of integrally formed integrally inside the plurality of transparent film members 110, and a black film member 140 having black color; The plurality of transparent through members 130 and the plurality of black film members 140 alternately bind, and the transparent through member 130 and the black film member 140 are integrated with the plurality of transparent film members 110. Security film, characterized in that consisting of the adhesive member 150 is an easy-to-fit adhesive to be bonded to. 제 1항에 있어서, 상기 투명관통부재(130)는 수직이 아니라 일정한 각도를 가지고 형성되는 것을 특징으로 하는 보안용필름.According to claim 1, The transparent member 130 is a security film, characterized in that it is formed at a predetermined angle rather than vertical. 제 1항에 있어서, 상기 투명관통구재는 P.E.T로 형성되는 것을 특징으로 하는 보안용필름.The security film of claim 1, wherein the transparent through-hole material is formed of P.E.T. 제 1항에 있어서, 상기 흑색필름부재(140)는 검은 페이트 또는 유성물감 등을 사용한 것을 특징으로 하는 보안용필름.According to claim 1, wherein the black film member 140 is a security film, characterized in that the use of black paint or oil paint. 흑색필름부재(140)의 상단부에 상기 접착부재(150)를 칠하는 단계와, 상기 단계를 수행한 후 그 위에 투명관통부재(130)를 올려놓은 단계와, 상기 단계에서 투명관통부재(130)가 올려진 후에는 도시되지 않은 통상의 히터롤러를 이용하여 열융작으로 접착하는 단계와, 상기 열융착으로 접착한 후 상기와 같은 과정을 계속적으로 하여 일정한 두께가 되도록 형성하는 단계와, 상기 단계를 수행한 후 커팅부재(200)를 이용하여 일정한 두께로 수직으로 절단하는 단계와, 상기 단계에서 일정한 두께로 절단한 후 상기 투명관통부재(130)의 양측면에 상기 복수개의 투명필름부재(110)가 접착되어 일체로 형성되도록 상기 접착부재(150)를 칠하는 단계와, 상기 단계에서 상기 접착부재(150)를 칠한 후 상기에서와 같이 히터롤러를 이용하여 열융착하여 상기 복수개의 투명관통부재(130) 및 흑색필름부재(140)와 상기 복수개의 투명필름부재(110)를 일체로 결착하는 단계로 구성되어 있는 것을 특징으로 하는 보안용필름을 제작하는 방법.Painting the adhesive member 150 on the upper end of the black film member 140, placing the transparent through member 130 thereon after performing the above step, and in the step, the transparent through member 130 After the step of mounting by using a common heater roller not shown in the step of thermal fusion, and the step of gluing by the heat fusion continuously forming the same process to form a constant thickness, and the step, After performing the step of vertically cutting to a predetermined thickness using a cutting member 200, and after cutting to a predetermined thickness in the step, the plurality of transparent film member 110 on both sides of the transparent through member 130 Painting the adhesive member 150 to be bonded and integrally formed, and then painting the adhesive member 150 in the step, and thermally fusion using a heater roller as described above to form the plurality of transparent materials. Method for producing a security film, characterized in that consisting of the step of integrally binding the penetrating member 130 and the black film member 140 and the plurality of transparent film member (110). 제 5항에 있어서, 상기 투명관통부재(130)의 일측면에 검은 페인트 또는 수성 또는 유성 물감 등을 칠한 후 그 외측면에 상기 접착부재(150)를 형성하므로서 복수개의 상기 투명관통부재(130)가 일체로 형성되도록 하는 것을 특징으로 하는 보안용필름을 제작하는 방법.The method of claim 5, wherein the one side of the transparent through member 130 is coated with black paint or an aqueous or oil paint, and the like to form the adhesive member 150 on the outer surface of the plurality of transparent through member 130 Method for producing a security film, characterized in that to be formed integrally. 제 1항에 있어서, 상기 투명필름부재(110)의 내측에 배설되어 있는 복수개의조각으로 형성되어 있는 투명관통부재(184)와, 상기 복수개의 투명관통부재(184)의 외측면에 검은색으로 빛을 차단하는 페이트로 칠해져 있는 페인트부재(182)와, 상기 복수개의 페인트부재(182)의 상하면에 상기 복수개의 투명필름부재(110)와 접착시키기 위해 접착제인 접착부재(150)로 형성되어 있는 것을 특징으로 하는 보안용필름.The method of claim 1, wherein the transparent through member 184 formed in a plurality of pieces disposed inside the transparent film member 110 and the outer surface of the plurality of transparent through member 184 in black It is formed of a paint member 182, which is painted with a paint blocking the light, and an adhesive member 150 which is an adhesive to adhere to the plurality of transparent film member 110 on the upper and lower surfaces of the plurality of paint members 182 Security film, characterized in that. 보안용필름(100)의 양측면에 형성되는 투명한 P.C재질인 복수개의 투명필름부재(110)와, 상기 복수개의 투명필름부재(110)의 내측에 일체로 규칙적 또는 비규칙적으로 교대로 형성되어 있으며 투명한 재질인 투명테이프로 형성되어 있는 투명관통부재(130)와, 상기 복수개의 투명필름부재(110)의 내측에 일체로 복수개가 교대로 칠하여져 있는 검은색의 흑색페인트부재(160)와, 상기 복수개의 투명관통부재(130)와 복수개의 흑색페인트부재(160)가 교대로 결착되도록 하고 상기 투명관통부재(130) 및 흑색페인트부재(140)가 상기 복수개의 투명필름부재(110)와 일체로 접착되도록 하는 통상의 피이접착제인 접착부재(150)로 구성되어 있는 것을 특징으로 하는 보안용필름.A plurality of transparent film members 110, which are transparent PC materials formed on both sides of the security film 100, and are formed integrally or regularly alternately integrally inside the plurality of transparent film members 110 and are transparent A transparent penetrating member 130 formed of a transparent tape made of a material, a black paint member 160 having a plurality of colors integrally painted integrally inside the plurality of transparent film members 110, and the plurality of Two transparent through members 130 and a plurality of black paint members 160 are alternately bonded, and the transparent through members 130 and the black paint member 140 are integrally bonded to the plurality of transparent film members 110. Security film, characterized in that consisting of the adhesive member 150 which is a normal to-be-adhesive to make. 원통형 또는 다각형의 형상을 가진 투명한 봉인 투명원통부재(180)를 준비하는 단계와, 상기 투명원통부재(180)를 준비한 후 빛을 차단하도록 외측면에 검은색의 페인트인 페인트부재(182)로 칠하는 단계와, 상기 페인트부재(182)를 칠한 후 상기 투명원통부재(180)를 일정한 크기로 절단하여 투명관통부재(184)의 조각을 만드는 단계와, 상기 복수개의 투명관통부재(184)를 차례로 배열한 후 상기 복수개의 투명관통부재(184)의 상하측면에 접착부재(150)를 도포한 후 그 상하면에 상기 투명필름부재(110)를 놓는 단계와, 상기 복수개의 투명필름부재(110)를 올려 놓은 후 일정한 온도로 가열된 통상의 히터형 롤러로 상기 투명필름부재(110)의 외측면을 이동하면서 열융착으로 상기 복수개의 투명필름부재(110) 및 상기 복수개의 투명관통부재(184)가 결착되도록 하는 단계로 구성되어 있는 것을 특징으로 하는 보안용필름을 제작하는 방법.Preparing a transparent cylindrical member 180 having a transparent seal having a cylindrical or polygonal shape, and preparing the transparent cylindrical member 180 and painting with a paint member 182 which is black paint on the outer surface to block light. And cutting the transparent cylindrical member 180 to a predetermined size after painting the paint member 182 to make a piece of the transparent through member 184, and then sequentially rotating the plurality of transparent through members 184. After arranging, applying the adhesive member 150 to the upper and lower sides of the plurality of transparent through member 184, and then placing the transparent film member 110 on the upper and lower surfaces, and the plurality of transparent film member 110 The plurality of transparent film members 110 and the plurality of transparent through members 184 are thermally fused by moving the outer surface of the transparent film member 110 with a conventional heater-type roller heated to a constant temperature after being placed thereon. Stage of binding Method for producing a security film, characterized in that consisting of the system.
KR1020010066955A 2001-10-30 2001-10-30 Film for preservation and method for making the same KR20010103132A (en)