KR20010088066A - The gel for supersonic probe and its manufacturing method - Google Patents
The gel for supersonic probe and its manufacturing method Download PDFInfo
- Publication number
- KR20010088066A KR20010088066A KR1020000012068A KR20000012068A KR20010088066A KR 20010088066 A KR20010088066 A KR 20010088066A KR 1020000012068 A KR1020000012068 A KR 1020000012068A KR 20000012068 A KR20000012068 A KR 20000012068A KR 20010088066 A KR20010088066 A KR 20010088066A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- viscosity
- added
- less
- Prior art date
Abstract
Description
본 발명은 임신 진단기의 의료용 검사 장비로 많이 사용되고 있는 초음파 프로브를 신체부위에 밀착시켜 진단하는 과정에서 사용되는 초음파 프로브용 윤활제 또는 밀착제에 관한 것으로, 특히 투명도, 점도 및 수분보유력이 뛰어나고 윤활성이 우수하여 초음파 진단기의 프로브를 진단부위에 완전밀착이 가능하며, 기포가 발생되지 않아 초음파의 간섭현상 및 노이즈 현상을 방지하여 선명한 영상을 모니터링 할 수 있도록 한 초음파 프로브용 교화체 및 그 제조방법에 관한 것이다.The present invention relates to an ultrasonic probe lubricant or adhesive agent used in the process of diagnosing the ultrasonic probe, which is widely used as a medical examination equipment of a pregnancy diagnosis device, in close contact with a body part, and in particular, has excellent transparency, viscosity, and moisture retention and excellent lubricity. And a method for manufacturing an ultrasonic probe and a method of manufacturing the same, in which a probe of an ultrasonic diagnostic apparatus can be completely adhered to a diagnosis part, and bubbles are not generated so that interference and noise of ultrasonic waves can be prevented and a clear image can be monitored. .
종래로 부터 초음파 프로브는 임신 진단기의 의료용 검사 장비로 많이 사용되고 있는 것으로 초음파 프로브를 신체부위에 밀착시켜 태아의 건강상태나 임신여부 등을 확인해 왔다.Conventionally, the ultrasonic probe has been widely used as a medical examination equipment of a pregnancy diagnosis device. The ultrasonic probe has been closely attached to a body part and has confirmed the state of health of a fetus or whether a pregnancy is performed.
이때 초음파 프로브를 신체부위에 완전밀착시켜 선명한 영상을 모니터링하기 위하여 윤활제나 밀착제(이하 '교화체'(gel)라 함)등을 신체부위에 먼저 바른 다음 프로브를 이용하여 영상을 모니터링하게 된다.At this time, in order to monitor the clear image by closely attaching the ultrasonic probe to the body part, a lubricant or an adhesive (hereinafter referred to as 'gel') is first applied to the body part, and then the image is monitored by using the probe.
일반적으로 상기 교화체는 충분한 점도 유지와 투명도 및 밀착력이 우수해야초음파의 간섭현상에 의한 노이즈 현상을 방지 할 수 있으며, 따라서 선명한 진단 화면을 볼 수 있게 된다.In general, the corrector should have sufficient viscosity and excellent transparency and adhesion to prevent noise from interference due to ultrasonic interference, and thus a clear diagnostic screen can be seen.
상기 초음파 진단시 프로브를 인체부위에 밀착시키는 과정에서 사용되는 교화체로 물, 글리세린 또는 바세린과 같은 일반 유제 등이 있으며, 상기 교화체를 인체부위에 바른다음 진단을 수행하여 왔다.In the ultrasound diagnosis, there are common oils such as water, glycerin, or petrolatum as a human body used in the process of bringing the probe into close contact with the human body, and the diagnosis has been performed by applying the human body to the human body.
그러나, 물은 유연성이 없으며 쉽게 건조되고 점도가 낮으므로 인체부위와 프로브와의 밀착상태가 불량하여 초음파의 장애요인으로 작용하여 정확한 영상을 모니터에 전달하지 못한다는 결점을 가지고 있다.However, since water is inflexible, easily dried, and has low viscosity, the adhesion state between the human body and the probe is poor, and thus, it is a barrier to ultrasonic waves, which does not transmit accurate images to the monitor.
또한, 글리세린을 교화체로 사용하는 경우 글리세린이 체내에 흡수되어 쉽게 건조됨으로써 지속적인 밀착 효과를 기대할 수 없어 프로브의 이동이 원할하지 못하여 정확한 영상을 모니터링할 수 없다는 문제점이 있다.In addition, when glycerin is used as a substance, glycerin is absorbed into the body and is easily dried, and thus a continuous adhesion effect cannot be expected. Therefore, the movement of the probe is not desired, and thus an accurate image cannot be monitored.
또 바세린의 경우 기포의 발생이 많고 도포된 유제의 건조현상으로 사용 후 끈적거림이 남아 있으며, 특히 기포발생으로 인한 노이즈 현상의 발생으로 정확한 영상을 모니터에 전달하지 못한다는 결점을 가지고 있다.In addition, petrolatum has a drawback in that bubbles are often generated and stickiness remains after use due to the drying phenomenon of the coated emulsion, and in particular, the accurate image cannot be transmitted to the monitor due to the occurrence of noise caused by bubbles.
상기한 문제점을 해소하기 위해 대한민국 특허 제2146호의 '초음파 프로브용 교화체의 제조방법'에서는 물 1,000중량%에 대하여 카보폴 6 내지 7중량%, 바람직하기로는 6.5 내지 7중량%, 폴리 프로필렌 글리콜 1 내지 15중량%, 트리 에탄올 아민 1.5 내지 40중량%, 그리고 메틸 셀룰로오즈(D-MC)를 0.2 내지 0.3중량% 첨가하고 방부제로서 D-M(다니솔-M) 및 D-B(다니솔-B)를 각각 0.1중량%, 소디움 벤조네이트 0.8 내지 1중량% 첨가한 후 10 내지 20℃의 온도, 특히 바람직하기로는 15 내지20℃의 온도를 유지하면서 10 내지 15일간 교반하는 것에 의한 교화체 제조방법을 개시하고 있다.In order to solve the above problems, in Korean Patent No. 2146 'Method for producing a hybridization body for ultrasonic probe', 6 to 7% by weight, preferably 6.5 to 7% by weight, polypropylene glycol 1 with respect to 1,000% by weight of water To 15% by weight, 1.5 to 40% by weight of triethanolamine, and 0.2 to 0.3% by weight of methyl cellulose (D-MC) and 0.1% of DM (Danisol-M) and DB (Danisol-B) as preservatives, respectively. Disclosed is a method for preparing a crosslinked product by adding 10 wt% and 0.8 wt% sodium benzoate, followed by stirring for 10 to 15 days while maintaining a temperature of 10 to 20 ° C, particularly preferably 15 to 20 ° C. .
그러나 상기 교화체의 제조방법에서 사용되는 카보폴940(CARBOPOL 940,B.F.GOODRICH,USA)은 교화체 제조시 물에 대한 습윤 및 팽윤 시간이 너무 오래 걸려 기포발생의 방지 및 생성된 덩어리를 풀어주기 위해 약 10일 이상씩 저속교반을 시켜주어야 하므로, 제조시간이 길어 생산성이 저하되는 문제점을 가지고 있었다.However, Carbopol 940 (CARBOPOL 940, BFGOODRICH, USA) used in the manufacturing method of the cross-linked body is too long to wet and swell the water during the manufacture of the cross-linked to prevent the occurrence of bubbles and to release the mass Since the slow stirring of about 10 days or more, the production time is long, had a problem that the productivity is lowered.
특히 병원에서 사용되는 초음파 프로브는 별도의 소독과정 없이 여러 환자의 진단 부위에 반복적으로 사용하므로 이로 인한 피부병 및 기타 병원균이 감염될 수 있는 문제점이 있다.In particular, since the ultrasonic probe used in the hospital is repeatedly used in the diagnosis sites of several patients without a separate disinfection process, there is a problem that can be caused by skin diseases and other pathogens.
이에 본 발명은 상기한 종래의 문제점을 해결하기 위한 것으로 투명도, 점도 및 수분보유력이 뛰어나고 윤활성이 우수하여 초음파 진단기의 프로브를 진단부위에 완전밀착이 가능하며, 초음파의 간섭현상 및 노이즈 현상을 방지하여 선명한 영상을 모니터링 할 수 있으며, 특히 제조시간을 단축시켜 생산성을 향상시킬 수 있도록 한 초음파 프로브용 교화체 및 그 제조방법을 제공하는 데 그 목적이 있다.Accordingly, the present invention is to solve the above-mentioned problems, it is excellent in transparency, viscosity, and water retention and excellent lubricity, so that the probe of the ultrasonic diagnostic apparatus can be completely adhered to the diagnosis site, and the interference phenomenon and noise phenomenon of the ultrasonic wave can be prevented. It is an object of the present invention to provide an ultrasonic probe and a method for manufacturing the same, which can monitor a clear image, and in particular, to shorten the manufacturing time and improve productivity.
상기한 목적을 달성하기 위하여 본 발명은 이온교환수 84.5중량부 내지 97.5중량부, 교화제로 카보폴 울트레즈10 0.5중량부 내지 1.5중량부, 유연보조제로 폴리에틸렌글리콜 1.0중량부 내지 5.0중량부, 보습제로 글리세린 1.0중량부 내지 5.0중량부 및 점도 조절제로 트리에탄올아민 4.0중량부이하를 포함하는 것에 의한 초음파 프로브용 교화체를 제공함으로써 달성할 수 있다.In order to achieve the above object, the present invention provides 84.5 parts by weight to 97.5 parts by weight of ion-exchanged water, 0.5 parts by weight to 1.5 parts by weight of Carbopol Ultrez 10 as a binder, 1.0 parts by weight to 5.0 parts by weight of polyethylene glycol as a softening aid, and a moisturizing agent. It can achieve by providing the body for the ultrasonic probe by containing 1.0 weight part-5.0 weight part of low glycerin, and 4.0 weight part or less of triethanolamine with a viscosity modifier.
또한 상기 초음파 프로브용 교화체를 보다 효과적으로 제조하기 위하여 본 발명은 진공탈기 장치가 장착된 고점도용 반응기에 이온교환수 84.5중량부 내지 97.5중량부, 카보폴 울트레즈10 0.5중량부 내지 1.5중량부, 폴리에틸렌글리콜 1.0중량부 내지 5.0중량부 및 글리세린 1.0중량부 내지 5.0중량부를 포함하도록 투입 혼합하여 혼합물을 제조한 다음, 상기 혼합물을 30분간 교반시키고, 15℃ 내지 50℃를 유지하면서 진공펌프로 40mmHg 이하의 진공도로 감압하여 혼합물 내의 기포를 제거한 다음 반응기내의 압력을 대기압 상태로 조절한 다음, 점도 조절제인 트리에탄올아민 4.0중량부 이하를 투입하고 다시 진공펌프로 40mmHg 이하의 진공도로 감압하면서 약 30분간 교반시켜주는 것에 의한 초음파 프로브용 교화체의 제조방법을 제공한다.In addition, the present invention in order to more effectively produce the ultrasonic probe body, the present invention is a high viscosity reactor equipped with a vacuum degassing device 84.5 parts by weight to 97.5 parts by weight of ion exchange water, Carbopol Ultres 10 0.5 parts by weight to 1.5 parts by weight, 1.0 parts by weight to 5.0 parts by weight of polyethylene glycol and 1.0 parts by weight to 5.0 parts by weight of glycerol was prepared by mixing to prepare a mixture, the mixture was stirred for 30 minutes, while maintaining a temperature of 15 ℃ to 50 ℃ 40mmHg or less After decompression with vacuum to remove bubbles in the mixture, the pressure in the reactor was adjusted to atmospheric pressure, and then 4.0 parts by weight or less of triethanolamine as a viscosity regulator was added thereto, and the mixture was stirred with a vacuum pump at a vacuum of 40 mmHg or less for about 30 minutes. It provides a method for producing a body for ultrasonic probe by giving.
이하 본 발명의 초음파 프로브용 교화체 및 그 제조방법에 관하여 상세하게 설명하면 먼저 본 발명은 진공탈기 장치가 장착된 고점도용 반응기에 이온교환수, 카보폴 울트레즈10, 폴리에틸렌글리콜 및 글리세린을 투입 혼합하여 혼합물을 제조한 다음 30분간 교반하게 된다.Hereinafter, the present invention will be described in detail with respect to the ultrasonic probe body and the manufacturing method of the present invention is first mixed with ion exchange water, Carbopol Ultres 10, polyethylene glycol and glycerin in a high viscosity reactor equipped with a vacuum degassing apparatus The mixture was prepared and then stirred for 30 minutes.
상기에서 카보폴 울트레즈10은 물에 녹아 수팽창성을 갖게 되어 일정한 점도를 갖는 젤을 형성하기 위해 첨가하는 것으로 그 첨가량이 0.5중량부 미만으로 첨가될 경우 제조된 교화체의 점도가 낮아 건조속도가 빠르고 밀착성이 떨어진다는 문제점이 발생하게 되고, 1.5중량부를 초과하도록 첨가될 경우 점도가 높아 투명성이 저하되고 윤활성이 불량하다는 문제점이 발생하게 되므로, 카보폴 울트레즈10의 첨가량은 0.5중량부 내지 1.5중량부 첨가하는 것이 바람직하다.Carbopol Ultrez 10 is added to form a gel having a certain viscosity by dissolving in water to have a water expandability, when the addition amount is less than 0.5 parts by weight, the viscosity of the prepared body is low drying rate The problem of fast and poor adhesion occurs, and when added to exceed 1.5 parts by weight, the viscosity is high, the transparency is lowered, and the problem of poor lubricity occurs, the addition amount of Carbopol Ultrez 10 is 0.5 parts by weight to 1.5 weight It is preferable to add by addition.
본 발명에서 사용된 카보폴 울트레즈10(CARBOPOLE Ultrez10; B.F.Goodrich,USA)은 종래 교화체 제조에 이용되던 카보폴940과 비교해보면 동일조건하에서 동일한 양을 사용했을 경우 카보폴 울트레즈10이 카보폴940에 비해 약 40% 이상의 더 큰 점도를 나타내며, 특히 교화체 제조시 물에 대한 습윤 및 팽윤 시간이 약 1/5로 단축되어 교화체 제조시간을 단축시킬 수 있다는 장점을 가지고 있다.Carbopol Ultrez 10 used in the present invention (CARBOPOLE Ultrez 10; BFGoodrich, USA) is compared to the Carbopol 940 used in the manufacture of a conventional mating body when the same amount under the same conditions when the Carbopol Ultrez 10 Carbopol Compared to 940, the viscosity is greater than about 40%, and the wet and swelling time with respect to water is particularly shortened to about 1/5 when the crosslinked material is manufactured.
또한 본 발명에서 폴리에틸렌글리콜은 유연보조제로 보습효과와 윤활성을 증진시키기 위해 첨가하게 되는데, 이때 그 첨가량이 1.0중량부 미만으로 첨가하는 경우 보습력이 저하되고, 윤활성이 저하되는 문제점이 발생하게 되고, 폴리에틸렌글리콜의 첨가량이 5.0중량부를 초과하도록 첨가될 경우 점도가 저하되는 문제점이 발생하게 되므로 폴리에틸렌글리콜의 첨가량은 1.0중량부 내지 5.0중량부 첨가하는 것이 바람직하다.In addition, the polyethylene glycol in the present invention is added to improve the moisturizing effect and lubricity as a softening aid, when the addition amount is less than 1.0 parts by weight, the moisturizing power is lowered, there is a problem that the lubricity is lowered, polyethylene When the addition amount of glycol is added to exceed 5.0 parts by weight, a problem occurs that the viscosity is lowered, so the amount of polyethylene glycol is preferably added 1.0 parts by weight to 5.0 parts by weight.
특히, 상기 폴리에틸렌글리콜의 분자량이 600을 초과하게 되면 폴리에틸렌글리콜이 상온에서 고체상태로 존재하게 되며, 따라서 제조된 교화체의 유연성이 떨어질 뿐만 아니라 물에 대한 용해시간이 길어지게 된다는 문제점이 발생하게 되므로 폴리에틸렌글리콜의 분자량은 600이하로 하는 것이 바람직하다.In particular, when the molecular weight of the polyethylene glycol exceeds 600, the polyethylene glycol is present in a solid state at room temperature, and thus the problem of not only decreases the flexibility of the prepared crosslinker but also increases the dissolution time for water. The molecular weight of polyethylene glycol is preferably 600 or less.
또한 본 발명은 촉감을 향상시키기 위하여 글리세린을 첨가하게 되는 데, 그 첨가량이 1.0중량부 미만으로 첨가될 경우 그 충분한 효과를 얻을 수 없는 문제점이 발생하게 되고, 5.0중량부를 초과하도록 첨가될 경우 끈적거리는 느낌이 드는 문제점이 발생하게 되므로 글리세린의 첨가량은 1.0중량부 내지 5.0중량부 첨가하는 것이 바람직하다.In addition, the present invention is to add a glycerine to improve the touch, if the addition amount is added less than 1.0 parts by weight, the problem occurs that the sufficient effect can not be obtained, if added to exceed 5.0 parts by weight sticky Since there is a problem of feeling, it is preferable to add 1.0 parts by weight to 5.0 parts by weight of glycerin.
이때 교화체에 살균력을 부여하기 위하여 상기 혼합물에 살균제를 첨가할 수 있는데, 상기와 같이 살균제를 첨가하게 되면 별도의 소독과정 없이 여러 환자의 진단 부위에 반복적으로 사용하는 경우에도 이로 인한 피부병 및 기타 병원균이 감염되는 것을 방지할 수 있게 되는 것이다.In this case, a disinfectant may be added to the mixture in order to give bactericidal power to the mixture, and when the disinfectant is added as described above, even if it is repeatedly used at the diagnosis site of several patients without a separate disinfection process, it may cause dermatosis and other pathogens. This can prevent the infection.
상기 살균제로 사용가능한 것으로는 트리클로산(Triclosan) 등이 있으며 그 첨가량이 0.0005중량부 미만으로 첨가될 경우 그 충분한 효과를 낼 수 없으며, 0.001중량부를 초과하도록 첨가할 경우 물에 대한 용해도가 떨어져 제품의 투명도가 저하되는 문제점이 발생하게 되므로 그 첨가량은 0.0005중량부 내지 0.001중량부 첨가하는 것이 바람직하다.The bactericide can be used as Triclosan, etc., and if the added amount is less than 0.0005 parts by weight, the effect cannot be sufficient. Since the problem of lowering will occur, the addition amount is preferably added in 0.0005 parts by weight to 0.001 parts by weight.
상기와 같은 비율로 이온교환수, 폴리아크릴산 공중합체, 폴리에틸렌글리콜 및 글리세린을 진공탈기 장치가 장착된 고점도용 반응기에 투입하고 30분간 교반하게 되는데, 교반속도는 통상적인 교반속도인 30rpm 내지 60rpm의 속도로 교반하게 되며, 상기 교반하는 동안 기포가 발생하게 된다.Ion-exchanged water, polyacrylic acid copolymer, polyethylene glycol and glycerin are introduced into a high viscosity reactor equipped with a vacuum degassing apparatus and stirred for 30 minutes at the same ratio, and the stirring speed is a speed of 30 rpm to 60 rpm, which is a typical stirring speed. It is stirred as, and bubbles are generated during the stirring.
이때 발생하는 기포는 초음파 프로브를 이용하여 진단하는 과정에서 노이즈를 발생시키는 원인으로 작용하기 때문에 제거할 필요가 있는데, 상기 기포를 제거하기 위하여 반응기의 온도를 15℃ 내지 50℃를 유지하면서 진공펌프로 40mmHg 이하의 진공도로 감압하게 된다.The bubbles generated at this time need to be removed because they act as a cause of noise in the process of diagnosis using an ultrasonic probe. In order to remove the bubbles, a vacuum pump is maintained while maintaining the temperature of the reactor at 15 ° C to 50 ° C. The pressure is reduced to a vacuum of 40 mmHg or less.
이때 상기 기포제거시 온도는 15℃ 미만일 경우 울트레즈10의 용해속도가 느려지게 되어 결과적으로 장시간에 걸쳐 교반을 해주어야 하므로 기포제거에 상당한 시간이 소요되는 문제점이 발생하게 되고, 50℃를 초과할 경우 수분의 증발로 인한 젤의 점도가 급증하여 제조된 교화체의 윤활성 및 투명도가 저하되는 문제점이 발생하게 되므로 반응기의 온도는 15℃ 내지 50℃로 유지하면서 교반하는 것이 바람직하다.At this time, when the temperature of the bubble removal is less than 15 ℃, the dissolution rate of the Ultrez 10 is slowed down as a result of the need for agitation over a long time, a problem that takes a considerable time to remove the bubble occurs, if the temperature exceeds 50 ℃ Since the viscosity of the gel due to the evaporation of water is rapidly increased, the problem is that the lubricity and transparency of the prepared crosslinking substance is lowered, it is preferable to maintain the temperature of the reactor while stirring at 15 ℃ to 50 ℃.
또한 감압시 진공도가 40mmHg를 초과할 경우 기포제거가 용이하지 않아 제조된 교화체의 기포발생에 의한 노이즈 현상으로 정확한 영상을 모니터링할 수 없다는 문제점이 발생하므로 감압시 진공도는 40mmHg 이하로 하는 것이 바람직하다.In addition, when the vacuum degree exceeds 40mmHg during decompression, it is not easy to remove bubbles, and thus a problem arises in that the accurate image cannot be monitored due to the noise phenomenon caused by the bubble generation of the prepared crosslinker. Therefore, the vacuum degree during the decompression is preferably 40mmHg or less. .
상기와 같은 온도 및 진공도로 감압을 하게 되면 짧은 시간내에 기포제거가 가능하며, 이때 상기와 같이 감압을 하지 않을 경우에는 기포발생을 방지하기 위하여 약 7일 이상을 서서히 교반해야 하는 문제점이 있다.If the pressure is reduced to the temperature and vacuum as described above, it is possible to remove the bubble within a short time, in this case, if the pressure is not reduced as described above, there is a problem that you need to stir more than about 7 days to prevent the occurrence of bubbles.
기포제거가 끝나면 감압을 풀어 반응기내의 압력을 대기압으로 조절하고 점도 조절제인 트리에탄올아민 4.0중량부 이하를 투입하고 다시 진공펌프로 40mmHg 이하의 진공도로 감압하면서 약 30분간 교반시켜주게 된다.After the bubble is removed, the pressure is released to adjust the pressure in the reactor to atmospheric pressure, and 4.0 parts by weight or less of triethanolamine, which is a viscosity modifier, is added thereto and then stirred for about 30 minutes while reducing the vacuum degree to 40 mmHg or less with a vacuum pump.
이때 트리에탄올아민은 교화체의 점도를 조절 및 신체에 적합한 pH를 조절하기 위하여 첨가하는 것으로 4.0중량부를 초과할 경우 급격한 pH의 상승으로 인하여 점도가 급격하게 낮아지는 문제점이 발생하게 되므로 트리에탄올아민의 첨가량은 4.0중량부 미만으로 하는 것이 바람직하다.In this case, the triethanolamine is added to control the viscosity of the crosslinked substance and to adjust the pH suitable for the body. When the content exceeds 4.0 parts by weight, the problem of the viscosity rapidly decreases due to the rapid rise of the pH. It is preferable to set it as less than 4.0 weight part.
상기와 같이 점도조절제인 트리에탄올아민을 투입하고 다시 진공펌프로 감압하면서 교반하면 본 발명에 의한 초음파 프로브용 교화체를 제조할 수 있게 되는 것이다.By adding triethanolamine, which is a viscosity modifier as described above, and stirring the product under reduced pressure with a vacuum pump again, it is possible to manufacture the ultrasonic probe for the ultrasonic probe according to the present invention.
상기와 같이 온도 및 감압조건을 적절하게 유지하게 되면 교화체 제조시간을 1시간 내지 2시간 정도로 단축할 수 있어 종래 10일 이상 걸리던 교화체 제조방법에 비해 생산성이 극대화될 수 있다는 장점이 있다.Maintaining the temperature and pressure-reducing conditions as described above can shorten the manufacturing time of the cross-linked body to about 1 hour to 2 hours, there is an advantage that the productivity can be maximized compared to the method of manufacturing a cross-linked body that took 10 days or more.
이하 본 발명은 하기한 실시예를 통해 보다 상세하게 설명하기로 하나, 본 발명은 하기한 설명에 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to the following examples, but the present invention is not limited to the following description.
<실시예 1><Example 1>
진공탈기 장치가 장착된 고점도용 반응기에 이온교환수 95중량부와 카보폴 울트레즈10 0.8중량부, 폴리에틸렌글리콜 2.0중량부 및 글리세린 3.0중량부를 투입하여 30분간 교반시키고, 25℃를 유지하면서 진공펌프로 30mmHg의 진공도로 감압하여 반응기내의 기포를 제거한 다음 혼합물 내의 압력을 대기압 상태로 조절하고, 점도 조절제인 트리에탄올아민 1.2중량부를 투입하고 다시 진공펌프로 30mmHg로 감압하면서 30분간 교반하여 초음파 프로브용 교화체를 제조한 다음, 하기한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.95 parts by weight of ion-exchanged water, 0.8 parts by weight of Carbopol Ultrez 10, 2.0 parts by weight of polyethylene glycol and 3.0 parts by weight of glycerin were added to a high viscosity reactor equipped with a vacuum degassing apparatus, stirred for 30 minutes, and maintained at 25 ° C. in a vacuum pump. The pressure in the reactor to remove bubbles in the reactor by adjusting the pressure to 30 mmHg, and then adjusting the pressure in the mixture to atmospheric pressure, adding 1.2 parts by weight of triethanolamine, which is a viscosity modifier, and stirring it for 30 minutes while reducing the pressure to 30 mmHg with a vacuum pump again. After the preparation, the flexibility, transparency, viscosity and bubble generation were measured by the following method, and the results are shown in Table 1.
- 유연성 -- flexibility -
인체의 측정부위에 제조된 교화체를 일정량 도포한 다음 프로브를 움직이면서 부드럽게 움직이는 경우에는 양호로 판단하고, 그렇지 않은 경우는 불량으로 나타내었다.After applying a certain amount of the human body prepared on the measurement part of the human body and moving the probe gently moving is judged to be good, otherwise it was represented as bad.
- 투명도 --Transparency-
밑면이 평편한 유리병의 바닥에 흰색바탕지를 놓은 다음, 상기 유리병에 제조된 교화체의 양을 점점 증가시키면서 넣고, 이때 유리병 바닥의 흰색이 더 이상 보이지 않을 때까지의 길이를 측정하였다. 이때 길이가 길수록 투명도가 높은 것으로 판단하며, 길이가 짧을 수록 투명도가 낮은 것으로 판단하였다.The white base paper was placed on the bottom of the glass bottle with a flat bottom surface, and the amount of the mixed substance prepared in the glass bottle was gradually increased, and the length of the glass bottle until the white color was no longer visible was measured. The longer the length, the higher the transparency was determined, the shorter the length was determined to be lower transparency.
- 점도 -- Viscosity -
제조된 교화체를 브룩필드(Brook field) 점도계로 스핀들 7번 및 20rpm의 속도로 상온에서 3회 측정하여 그 평균값을 점도로 나타내었다.The prepared crosslinked product was measured three times at room temperature with a Brookfield viscometer at a speed of spindle 7 and 20 rpm, and the average value was expressed as a viscosity.
- 기포발생 --Bubble occurrence-
제조된 교화체를 밀페된 투명 유리병에 넣고 육안으로 기포가 발생했는지의 여부를 관찰하고 하기한 방법으로 표기하였다.The prepared crosslinked product was placed in a sealed transparent glass bottle, and whether or not bubbles were produced with the naked eye was observed and described by the following method.
기포가 발생하지 않음 : ○No bubbles occur: ○
기포발생 : ×Bubble Occurrence: ×
<실시예 2><Example 2>
카보폴 울트레즈10의 첨가량을 0.4중량부 첨가하는 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Except for adding 0.4 parts by weight of the addition amount of Carbopol Ultrez 10 was prepared in the same manner as in Example 1 to prepare a human body for the ultrasonic probe, and then in the same manner as in Example 1 flexibility, transparency, viscosity and bubbles The occurrence was measured and the results are shown in Table 1.
<실시예 3><Example 3>
카보폴 울트레즈10의 첨가량을 1.6중량부 첨가하는 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Except for adding 1.6 parts by weight of Carbopol Ultrez 10, the same procedure as in Example 1 was carried out to prepare a cross-body for ultrasonic probe, and then the flexibility, transparency, viscosity and bubbles in the same manner as in Example 1. The occurrence was measured and the results are shown in Table 1.
<실시예 4><Example 4>
폴리에틸렌글리콜의 첨가량을 0.5중량부 첨가하는 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Except for adding 0.5 parts by weight of polyethylene glycol was prepared in the same manner as in Example 1 to prepare a cross-linking body for the ultrasonic probe, and then the flexibility, transparency, viscosity and bubble generation in the same manner as in Example 1 The measurement results are shown in Table 1.
<실시예 5>Example 5
폴리에틸렌글리콜의 첨가량을 6.0중량부 첨가하는 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Except for adding 6.0 parts by weight of polyethylene glycol was prepared in the same manner as in Example 1 to prepare a cross-linking body for the ultrasonic probe, and then in the same manner as in Example 1 whether flexibility, transparency, viscosity and bubble generation The measurement results are shown in Table 1.
<실시예 6><Example 6>
글리세린의 첨가량을 0.5중량부 첨가하는 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Except for adding 0.5 parts by weight of glycerin was added in the same manner as in Example 1 to prepare a cross-linking body for the ultrasonic probe, and then measuring the flexibility, transparency, viscosity and bubble generation in the same manner as in Example 1 The results are shown in Table 1.
<실시예 7><Example 7>
글리세린의 첨가량을 6.0중량부 첨가하는 것을 제외하고는 실시예1과 동일한방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Except for adding 6.0 parts by weight of glycerin was added in the same manner as in Example 1 to prepare a cross-linking body for the ultrasonic probe, and then measuring the flexibility, transparency, viscosity and bubble generation in the same manner as in Example 1 The results are shown in Table 1.
<실시예 8><Example 8>
트리에탄올아민의 첨가량을 5.0중량부 첨가하는 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Except for adding 5.0 parts by weight of triethanolamine, the same procedure as in Example 1 was carried out to prepare an ultrasonic probe crosslinker, and then the flexibility, transparency, viscosity and bubble generation were performed in the same manner as in Example 1. The measurement results are shown in Table 1.
<실시예 9>Example 9
기포제거시 온도를 10℃로 조절한 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Except for adjusting the temperature to 10 ℃ when removing the bubble was prepared in the same manner as in Example 1 to prepare a hybrid body for the ultrasonic probe, and then in the same manner as in Example 1 flexibility, transparency, viscosity and bubble generation The measurement results are shown in Table 1.
<실시예 10><Example 10>
기포제거시 온도를 60℃로 조절한 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Except for adjusting the temperature to 60 ℃ to remove the bubble was carried out in the same manner as in Example 1 to prepare a human body for the ultrasonic probe, then in the same manner as in Example 1 flexibility, transparency, viscosity and whether bubbles are generated The measurement results are shown in Table 1.
<실시예 11><Example 11>
기포를 제거하는 과정에서 감압을 하지 않고 대기압상태에서 실시한 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.In the process of removing bubbles, except that it was carried out at atmospheric pressure without decompression, the same procedure as in Example 1 was carried out to prepare an agglomerate for an ultrasonic probe, and then the flexibility, transparency, viscosity and Bubble generation was measured and the results are shown in Table 1.
<실시예 12><Example 12>
진공탈기 장치가 장착된 고점도용 반응기에 이온교환수 95중량부와 카보폴 울트레즈10 0.8중량부, 폴리에틸렌글리콜 2.0중량부, 글리세린 3.0중량부 및 살균제 0.001중량부를 투입하여 30분간 교반시키고, 25℃를 유지하면서 진공펌프로 30mmHg의 진공도로 감압하여 반응기내의 기포를 제거한 다음 반응기내의 압력을 대기압 상태로 조절하고, 점도 조절제인 트리에탄올아민 1.2중량부를 투입하고 다시 진공펌프로 40mmHg로 감압하면서 30분간 교반하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.95 parts by weight of ion-exchanged water, 0.8 parts by weight of Carbopol Ultrez 10, 2.0 parts by weight of polyethylene glycol, 3.0 parts by weight of glycerin and 0.001 parts by weight of a disinfectant were added to a high viscosity reactor equipped with a vacuum degassing apparatus, stirred for 30 minutes, and 25 ° C. While maintaining the vacuum pressure of 30mmHg with a vacuum pump to remove the bubbles in the reactor to adjust the pressure in the reactor to atmospheric pressure, 1.2 parts by weight of triethanolamine as a viscosity regulator was added again and the pressure was reduced to 40mmHg with a vacuum pump and stirred for 30 minutes After preparing a hybridization body for an ultrasonic probe, the flexibility, transparency, viscosity, and bubble generation were measured in the same manner as in Example 1, and the results are shown in Table 1.
<비교예 1>Comparative Example 1
카보폴울트레즈10을 첨가하지 않은 대신 종래 교화체 제조에 사용되는 카보폴940 0.8중량부를 첨가하고, 대기압상태에서 10일간 교반하는 것을 제외하고는 실시예1과 동일한 방법으로 실시하여 초음파 프로브용 교화체를 제조한 다음, 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.In the same manner as in Example 1 except that 0.8 parts by weight of Carbopol 940, which is conventionally used for the preparation of the crosslinked product, was added instead of Carbopol Ultrez 10, and stirred at atmospheric pressure, and the refining for the ultrasonic probe was performed. After the sieve was prepared, flexibility, transparency, viscosity, and bubble generation were measured in the same manner as in Example 1, and the results are shown in Table 1.
<비교예 2>Comparative Example 2
글리세린 단독으로 실시예1과 동일한 방법으로 유연성, 투명도, 점도 및 기포발생여부를 측정하여 그 결과를 표1에 나타내었다.Glycerin alone was measured in the same manner as in Example 1 flexibility, clarity, viscosity and whether bubbles were generated and the results are shown in Table 1.
상기 표1에서 보는 바와 같이 본 발명의 바람직한 범위내에서 실시한 실시예1의 경우 유연성, 투명도 및 점도가 우수하고, 기포가 발생하지 않은 것을 확인할 수 있다.As shown in Table 1, in Example 1 carried out within the preferred range of the present invention, it is confirmed that the flexibility, transparency and viscosity are excellent and bubbles are not generated.
그러나 카보폴 울트레즈10의 첨가량이 본 발명의 범위인 0.5중량부 미만인 0.4중량부 첨가한 실시예2의 경우 본 발명의 범위내인 0.8중량부 첨가한 실시예1에 비해 투명도는 우수하나 유연성이 불량하며, 1.5중량부를 초과한 1.6중량부 첨가한 실시예3의 경우 실시예1에 비해 유연성 및 투명도가 불량하며, 특히 실시예2의 경우 점도가 15,000으로 상당히 낮을 것을 알 수 있으며 실시예3의 경우 점도가 100,000으로 상당히 높은 것을 확인할 수 있다.However, in Example 2, in which the amount of Carbopol Ultrez 10 was added in an amount of 0.4 parts by weight, which is less than 0.5 parts by weight of the present invention, the transparency was superior to Example 1, in which 0.8 parts by weight of the present invention was added. Poor, in the case of Example 3 added 1.6 parts by weight exceeding 1.5 parts by weight, the flexibility and transparency is poor compared to Example 1, in particular in the case of Example 2 it can be seen that the viscosity is significantly low as 15,000 of Example 3 It can be seen that the viscosity is very high as 100,000.
상기와 같이 점도가 낮은 경우에는 제조된 교화체의 건조속도가 빠르게 진행되며 밀착성이 저하되는 문제가 발생하게 되며 점도가 높은 경우에는 투명성이 저하되는 문제가 있으므로, 따라서 카보폴 울트레즈10의 첨가량은 본 발명의 범위내인 0.5중량부 내지 1.5중량부 첨가하는 것이 바람직하다는 것을 알 수 있다.When the viscosity is low as described above, the drying speed of the prepared crosslinking material proceeds rapidly and the problem of deterioration of adhesiveness occurs, and when the viscosity is high, there is a problem of deterioration of transparency. Therefore, the addition amount of Carbopol Ultrez 10 It can be seen that it is preferable to add 0.5 parts by weight to 1.5 parts by weight within the scope of the present invention.
또한 폴리에틸렌글리콜의 첨가량이 본 발명의 범위인 1.0중량부 미만인 0.5중량부 첨가한 실시예4 및 5.0중량부를 초과한 6.0중량부 첨가한 실시예5의 경우 폴리에틸렌글리콜의 첨가량을 본 발명의 범위내인 2.0중량부 첨가한 실시예1에 비해 유연성 및 투명도가 불량하며, 특히 실시예 5의 경우 점도가 저하되는 것을 상기 표1을 통해 확인할 수 있으므로, 폴리에틸렌글리콜의 첨가량은 1.0중량부 내지 6.0중량부 첨가하는 것이 바람직하다는 것을 알 수 있다.In addition, in the case of Example 4 which added 0.5 weight part of which the addition amount of polyethyleneglycol is less than 1.0 weight part of the range of this invention, and the 6.0 weight part which added 6.0 weight part exceeding 5.0 weight part, the addition amount of polyethyleneglycol is within the range of this invention Flexibility and transparency is poor compared to Example 1 added 2.0 parts by weight, especially in Example 5 can be confirmed that the viscosity is reduced through Table 1, the amount of polyethylene glycol is added 1.0 parts by weight to 6.0 parts by weight It can be seen that it is preferable to.
마찬가지로, 글리세린의 첨가량이 본 발명의 범위인 1.0중량부 미만인 0.5중량부 첨가한 실시예6 및 5.0중량부를 초과한 6.0중량부 첨가한 실시예7의 경우 본 발명의 범위내인 3.0중량부 첨가한 실시예1에 비해 유연성 및 투명도가 불량하며, 특히 실시예 7의 경우 점도가 저하되는 것을 상기 표1을 통해 확인할 수 있으므로, 글리세린의 첨가량은 1.0중량부 내지 6.0중량부 첨가하는 것이 바람직하다는 것을 확인 할 수 있다.Similarly, in the case of Example 6 which added 0.5 weight part which is less than 1.0 weight part which is the range of this invention, and the 6.0 weight part which exceeded 5.0 weight part, the addition amount of glycerin added 3.0 weight part within the range of this invention Flexibility and transparency is poor compared to Example 1, in particular, in the case of Example 7, it can be confirmed through the Table 1 that the viscosity is reduced, it is confirmed that the addition amount of glycerin 1.0 parts by weight to 6.0 parts by weight is preferably added can do.
특히 점도조절제로 첨가하는 트리에탄올아민의 첨가량이 본 발명의 범위인 4.0중량부를 초과하여 5.0중량부를 첨가한 실시예8의 경우 본 발명의 범위인 1.2중량부 첨가한 실시예1에 비해 점도가 10,000으로 매우 낮은 것을 알 수 있는데, 이것은 트리에탄올아민의 첨가량이 증가할 수록 pH가 증가하게 되고, 상기 pH가 증가함에 따라 점도가 급격히 감소하는 카보폴 울트레즈10의 경향성에 의한 것이다.In particular, in the case of Example 8 in which the amount of triethanolamine added as a viscosity modifier was added in an amount of 5.0 parts by weight exceeding 4.0 parts by weight of the range of the present invention, the viscosity was 10,000 compared to Example 1 in which 1.2 parts by weight of the range of the present invention was added. It can be seen that very low, this is due to the tendency of Carbopol Ultrez 10 that the pH increases with the addition amount of triethanolamine, and the viscosity decreases sharply as the pH is increased.
따라서 트리에탄올 아민의 첨가량은 4.0중량부 미만으로 첨가하는 것이 바람직하다는 것을 확인할 수 있다.Therefore, the addition amount of triethanol amine can confirm that it is preferable to add less than 4.0 weight part.
또한 기포제거시 온도를 15℃ 미만인 10℃로 하여 실시한 실시예9 및 50℃를 초과한 60℃로 실시한 실시예10의 경우 25℃로 실시한 실시예1에 비해 유연성 및투명도가 떨어지고, 특히 실시예9의 경우 기포제거가 용이하지 않아 제조된 교화체에서 다량의 기포가 발생하는 것을 확인할 수 있다.In addition, in the case of Example 9 carried out at a temperature of less than 15 ℃ to 10 ℃ when removing bubbles and Example 10 carried out at 60 ℃ over 50 ℃, flexibility and transparency is inferior compared to Example 1 carried out at 25 ℃, especially Example In case of 9, it is not easy to remove bubbles, and it can be seen that a large amount of bubbles are generated in the prepared crosslinked material.
마찬가지로 기포제거시 감압을 하지 않고 대기압상태에서 실시한 실시예11의 경우 30mmHg로 감압하여 실시한 실시예1에 비해 유연성 및 투명도가 떨어지고, 특히 제조된 교화체에서 다량의 기포가 발생하는 것을 상기 표1을 통해 확인할 수 있다.Similarly, in the case of Example 11 carried out at atmospheric pressure without decompression when removing bubbles, the flexibility and transparency are inferior to Example 1 carried out by reducing the pressure to 30 mmHg, and in particular, a large amount of bubbles are produced in the prepared crosslinker. You can check
실시예12는 실시예1에 살균제를 더 첨가하여 실시한 것으로 실시예1과 유사한 결과를 얻은 것을 상기 표1을 통해 확인할 수 있다.Example 12 was performed by further adding a fungicide to Example 1, and it can be confirmed through Table 1 that results similar to those of Example 1 were obtained.
또한 카보폴울트레즈10 대신 카보폴940을 사용하여 교화체를 제조한 비교예1의 경우 실시예1과 비교하여 볼때 유연성 및 투명도는 양호한 것을 확인할 수 있으나 점도가 낮은 것을 확인할 수 있다.In addition, in Comparative Example 1 prepared by using the carbopol 940 instead of the Carbopol Ultrez 10 compared to Example 1 it can be confirmed that the flexibility and transparency is good, but the viscosity is low.
특히 교화체 제조에 10시간 이상을 교반하여 기포를 제거해야 하는데 비해 실시예1의 경우 1시간 내지 2시간 정도 교반하는 것에 의해 교화체를 제조할 수 있으므로, 실시예1의 경우 종래 교화체 제조방법에 비해 제조시간을 단축시킬 수 있었다.Particularly, in the case of Example 1, since the agglomerates can be prepared by stirring for about 1 hour to 2 hours, the agglomerates can be prepared by stirring at least 10 hours to prepare the agglomerates. Compared with the above, manufacturing time could be shortened.
마찬가지로 글리세린 단독으로 측정한 비교예2의 경우 투명도는 우수하나 유연성 및 점도가 매우 불량하여 교화체로는 부적합하다는 것을 확인할 수 있다.Similarly, in the case of Comparative Example 2 measured by glycerin alone, the transparency was excellent, but the flexibility and the viscosity were very poor, and thus it was confirmed that it was not suitable as a substance.
상기에서 설명한 바와 같이 본 발명은 투명도, 점도 및 수분보유력이 뛰어나 윤활성이 우수하여 초음파 진단기의 프로브를 진단부위에 완전밀착이 가능하며, 기포가 발생되지 않음으로 초음파의 간섭현상 및 노이즈 현상을 방지하여 선명한 영상을 모니터링 할 수 있으며, 특히 제조시간을 단축시켜 생산성을 향상시킬 수 있도록 한 초음파 프로브용 교화체 및 그 제조방법을 제공하는 유용한 발명인 것이다.As described above, the present invention is excellent in transparency, viscosity, and water retention, and thus has excellent lubricity, so that the probe of the ultrasonic diagnostic apparatus can be completely adhered to the diagnosis site, and bubbles are not generated to prevent interference and noise from ultrasonic waves. It is a useful invention that can monitor a clear image, and in particular, to provide an ultrasonic probe for rehabilitation and a method of manufacturing the same to shorten the manufacturing time to improve productivity.
Claims (5)