KR20010052650A - Unitary absorbent structure containing superabsorbent polymer - Google Patents
Unitary absorbent structure containing superabsorbent polymer Download PDFInfo
- Publication number
- KR20010052650A KR20010052650A KR1020007013883A KR20007013883A KR20010052650A KR 20010052650 A KR20010052650 A KR 20010052650A KR 1020007013883 A KR1020007013883 A KR 1020007013883A KR 20007013883 A KR20007013883 A KR 20007013883A KR 20010052650 A KR20010052650 A KR 20010052650A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- fibers
- storage layer
- web
- liquid
- Prior art date
Abstract
한 면에 연장된 액체포착영역(2)과 다른 면에 연장된 액체분포영역(4)을 가지는 상부섬유성층(12)을 포함하는 단일흡수구조(10)가 개시된다. 하부섬유성 액체저장층(14)은 상부층의 분포영역표면과 유체연락한다. 저장층은 SAP입자(18)를 포함한다. 함유층(8)은 저장층을 둘러싸고 구조의 외부가장자리로 연장된다. 함유층은 상부층의 분포영역표면에 대해 저장층의 SAP입자와, 섬유(6)를 함유한다.A single absorbent structure 10 is disclosed that includes an upper fibrous layer 12 having a liquid trapping region 2 extending on one side and a liquid distribution region 4 extending on the other side. The lower fibrous liquid storage layer 14 is in fluid communication with the surface of the distribution area of the upper layer. The storage layer contains SAP particles 18. The containing layer 8 surrounds the storage layer and extends to the outer edge of the structure. The containing layer contains the SAP particles of the storage layer and the fibers 6 with respect to the surface of the distribution area of the upper layer.
Description
일회용 기저귀, 성인용 실금패드, 생리대 등과 같은 흡수용품은 일반적으로 체액을 받아 보유하기 위한 흡수중심을 가진다. 흡수중심은 일반적으로 그 기능이 유체가 흡수중심으로 통과하도록 하는 것인 액체투과 상면시트와, 그 기능이 유체를 보유하여 그것이 흡수용품을 통과하여 흡수용품 사용자의 옷으로 가는 것을 방지하는 것인 액체불투과 이면시트 사이에 끼워진다.Absorbent articles, such as disposable diapers, adult incontinence pads, sanitary napkins and the like, generally have an absorbent center for receiving and retaining body fluids. Absorption centers are generally liquid permeable topsheets whose function is to allow fluid to pass through the absorption center, and liquids whose function is to retain the fluid and prevent it from passing through the absorbent article to the clothes of the absorbent article user. It is sandwiched between the opaque backsheet.
기저귀와 성인용 실금패드용 흡수중심은 흔히 섬유질제거되고 느슨하고 보풀형성되며 친수성인 셀룰로오스섬유로 구성된 섬유성 속솜 또는 웨브를 포함한다. 중심은 초흡수성 중합체(SAP)입자, 과립, 박편 또는 섬유를 포함할 수도 있다. 이 중심은 일반적으로 저장층이라 불린다.Absorption centers for diapers and adult incontinence pads often include fibrous batts or webs made of cellulose fibers that are de-fiberized, loose, lint-free, and hydrophilic. The center may comprise superabsorbent polymer (SAP) particles, granules, flakes or fibers. This center is generally called the storage layer.
최근에, 더 얇고 더 편안한 흡수용품에 대한 시장수요가 증가하고 있다. 그러한 용품은 기저귀중심의 두께를 감소시키고, SAP입자의 양을 증가시키는 한편 중심에 사용되는 섬유성 물질의 양을 감소시키며, 캘리퍼스를 감소시켜 밀도를 증가시키기 위하여 중심을 캘린더가공하거나 압착함으로써 얻어질 수 있다.Recently, the market demand for thinner and more comfortable absorbent articles is increasing. Such articles can be obtained by reducing the thickness of the diaper center, increasing the amount of SAP particles while reducing the amount of fibrous material used in the center, and calendering or squeezing the center to increase density by reducing calipers Can be.
그러한 고밀도중심은 중심의 고밀도화가 더 작은 유효기공크기를 가져오기 때문에 저밀도중심만큼 빨리 액체를 흡수하지 못한다. 따라서 적절한 액체흡수를 유지하기 위해서는, 흡수용품으로 배출되는 액체의 흡수속도를 증가시키기 위하여 고밀도흡수중심 위에 더 큰 기공크기를 가지는 저밀도층을 제공할 필요가 있다. 저밀도층은 일반적으로 포착층이라 불린다. 다층 흡수중심디자인은 보다 복잡한 제조공정을 포함한다.Such high density centers do not absorb liquids as fast as low density centers because the densification of the center results in a smaller effective pore size. Therefore, in order to maintain proper liquid absorption, it is necessary to provide a low density layer having a larger pore size above the high density absorption center in order to increase the absorption rate of the liquid discharged into the absorbent article. The low density layer is generally called the capture layer. Multilayer absorption center designs involve more complex manufacturing processes.
예를 들어 일회용 기저귀의 저장층부는 느슨하고 보풀형성된 셀룰로오스로부터, 전환과정 중에, 그 자리에서 형성되는 것이 일반적이다. 그러한 셀룰로오스물질은 흡수패드제조장치로 직접 풀리거나 흡수패드제조장치에서 취급되기에는, 섬유간 결합 또는 얽힘이 부족하여, 불충분한 웨브강도를 나타내기 때문에 사전형성된 롤형태로 이용할 수 없는 것이 일반적이다.For example, the storage layer portion of a disposable diaper is typically formed in place from the loose, fluffed cellulose, during the conversion process. Such cellulosic materials are generally not available in the form of preformed rolls because they are insufficiently loosened or entangled between fibers and exhibit insufficient web strength to be unwound directly into the absorbent pad manufacturing apparatus or handled in the absorbent pad manufacturing apparatus.
초박형 여성용 생리대는 일반적으로 롤제품계 부직포물질로부터 생산된다. 그러한 사전형성된 흡수중심물질의 롤은 기저귀와 실금패드와 같은 보풀계 제품에 필요한 섬유질제거단계없이 흡수용품전환장치로 직접 풀린다. 부직포 웨브는 일반적으로 전환공정에서 취급되기에 충분한 강도를 그것에 부여하는 방식으로 결합되거나 강화된다. 이들 웨브는 SAP입자를 함유할 수도 있다.Ultra-thin women's sanitary napkins are generally produced from roll-based nonwoven materials. Such preformed rolls of absorbent core material are unwound directly into the absorbent article conversion device without the fiber removal step required for fluff based products such as diapers and incontinence pads. Nonwoven webs are generally joined or reinforced in such a way that they give it sufficient strength to be handled in the conversion process. These webs may contain SAP particles.
사전형성된 중심을 제조하는 롤제품접근방식에서 사용되는 웨브강화메카니즘은 웨브에 강도와 크기안정성을 제공한다. 그러한 메카니즘에는 라텍스결합, 열가소성 또는 2성분섬유 또는 열가소성 파우더와의 결합, 유체얽힘, 니들펀칭, 소면 등이 포함된다.The web reinforcement mechanism used in the roll product approach to fabricating preformed cores provides the web with strength and size stability. Such mechanisms include latex bonding, bonding with thermoplastic or bicomponent fibers or thermoplastic powders, fluid entanglement, needle punching, carding and the like.
그러나 웨브는 롤제품 전환을 위하여 충분히 강화될 수 있는 한편, 또한 강화된 웨브는 입자들이 웨브의 간극 내에 포획되기 때문에 SAP입자의 팽창을 억제한다. 입자들은 주위웨브의 증가된 강도와 크기안정성 때문에 팽창할 수 없다. 결과적으로, 상기 구조의 최종흡수용량은 감소된다. 차례로, 고기본중량 및/또는 저밀도흡수중심구조가 아기기저귀 및 성인용 실금패드와 같은 고배출부피제품에 필요한 흡수용량을 제공하기 위하여 필요하다. 또한, 고입자하중에서, 그러한 중심구조들은 불충분한 입자함유를 나타낸다. 즉, 입자들의 일부는 제조, 취급, 수송 및 전환을 하는 동안 구조로부터 빠져나가기 쉽다. 이것은 제조 및 전환장치의 오염을 가져올 수 있다.However, the web can be sufficiently strengthened for roll product conversion, while the reinforced web also suppresses the expansion of the SAP particles because the particles are trapped within the gaps of the web. Particles cannot expand due to the increased strength and size stability of the surrounding web. As a result, the final absorption capacity of the structure is reduced. In turn, a high basis weight and / or low density absorbent center structure is needed to provide the absorbent capacity required for high discharge volume products such as baby diapers and adult incontinence pads. Also, at high particle loads, such central structures exhibit insufficient particle content. That is, some of the particles are likely to escape from the structure during manufacture, handling, transport and conversion. This can lead to contamination of the manufacturing and switching devices.
종래에 생산된 흡수구조에 관해서는, 개시내용이 인용에 의해 본 명세서에 삽입된 미합중국특허 제5,009,650호, 제5,378,528호, 제5,128,082호, 제5,607,414호, 제5,147,343호, 제5,149,335호, 제5,522,810호, 제5,041,104호, 제5,176,668호, 제5,389,181호 및 제4,596,567호를 인용한다.Regarding conventionally produced absorbent structures, U.S. Pat.Nos. 5,009,650, 5,378,528, 5,128,082, 5,607,414, 5,147,343, 5,149,335, 5,522,810, the disclosures of which are incorporated herein by reference. , 5,041,104, 5,176,668, 5,389,181 and 4,596,567.
포착영역으로부터 저장영역으로 유체운송을 촉진하고, 고입자하중에서 우수한 입자함유를 나타내며, 얇지만 사용시 고흡수용량을 가지고, 제조 및 전환공정을 단순화시키기 위하여 롤제품형태로 배달될 수 있는 흡수중심물질이 필요하다.Absorbent core materials that promote fluid transfer from the capture zone to the storage zone, exhibit excellent particle content at high particle loads, are thin but have high absorption capacities in use, and can be delivered in rolled form to simplify the manufacturing and conversion process. need.
본 출원은 인용에 의해 본 명세서에 완전히 삽입된, 1998년 6월 8일에 출원된 미합중국 가출원 제60/088,454호에 대하여 35 U.S.C. §119의 우선권을 주장한다.This application is incorporated by reference in U.S.C. 35, US Provisional Application No. 60 / 088,454, filed June 8, 1998, which is fully incorporated herein by reference. Insist on priority of §119.
본 발명은 일회용 기저귀, 성인용 실금패드, 생리대 등의 제조에 유용한 초흡수성 중합체를 함유한 섬유성 흡수구조에 관한 것이다. 보다 상세하게는, 본 발명은 그 구조 내에 느슨한 섬유 및 입자들을 함유하는 봉인된 측면가장자리를 가지는 흡수구조에 관한 것이다.The present invention relates to a fibrous absorbent structure containing a superabsorbent polymer useful for the manufacture of disposable diapers, adult incontinence pads, sanitary napkins and the like. More specifically, the present invention relates to an absorbent structure having a sealed side edge containing loose fibers and particles in the structure.
도 1은 본 발명의 바람직한 단일흡수구조의 단면도이다.1 is a cross-sectional view of a preferred single absorption structure of the present invention.
도 2는 도 1의 구조의 저면도이다.2 is a bottom view of the structure of FIG.
본 발명은 한 면에 연장된 액체포착영역과 다른 면에 연장된 액체분포영역을 가지는 상부 섬유성층을 포함하는 단일흡수구조에 관한 것이다. 하부섬유성 액체저장층은 상부층의 분포영역표면과 유체연락한다. 저장층은 SAP입자를 포함한다. 함유층은 저장층을 둘러싸면서 그 구조의 외부가장자리로 연장되고, 함유층은 상부층의 분포영역표면에 대해 저장층의 섬유와 SAP입자를 보유한다.The present invention relates to a single absorbent structure comprising an upper fibrous layer having a liquid trapping region extending on one side and a liquid distribution region extending on the other side. The lower fibrous liquid storage layer is in fluid communication with the surface of the distribution area of the upper layer. The storage layer contains SAP particles. The containing layer extends to the outer edge of the structure surrounding the storage layer, which contains the fibers and SAP particles of the storage layer relative to the surface of the distribution area of the upper layer.
본 발명은 구조의 두께를 통해 밀도차를 가지는 층상의 단일흡수중심구조를 제공한다. 상기 구조는 밀도차를 통해 유체를 분포시키는 능력을 구조에 부여하는 적어도 2개의 영역을 포함하는 합성물이다. 이들 영역은 손상으로부터 유체를 빨리 포착할 수 있는 상부포착영역, 포착된 유체를 측면으로 분포시키기 위한 분포영역, 및 사용된 물질의 흡수용량을 최대화하기 위하여 Z-방향으로 팽창하는 능력을 가지고 분포영역으로부터 분포된 액체를 흡수하여 저장하기 위한 저장영역을 포함한다. 구조는 구조 내에 결합되지 않거나 가볍게 결합된 섬유 또는 입자의 함유를 개선하기 위하여 그 측면가장자리 주위로 봉해진다. 봉인은 구조의 저장영역 아래에 위치한, 느슨한 섬유 또는 느슨한 입자가 통과할 수 없는 독립함유층을 선택적으로 제공함으로써 이루어진다.The present invention provides a layered single absorption center structure having a density difference through the thickness of the structure. The structure is a composite comprising at least two regions that impart to the structure the ability to distribute the fluid through density differences. These areas are distributed areas with a capturing area that can quickly capture fluid from damage, a distribution area for laterally distributing the captured fluid, and the ability to expand in the Z-direction to maximize the absorption capacity of the materials used. And a storage area for absorbing and storing the liquid distributed therefrom. The structure is sealed around its side edges to improve the inclusion of fibers or particles that are unbonded or lightly bound within the structure. Sealing is accomplished by selectively providing an independent layer, under which the loose fibers or loose particles are located, under the storage area of the structure.
흡수구조는 개선된 입자함유용량을 가진 결합되지 않은 에어펠트구조의 흡수용량을 가지고, 롤제품형태로 배달될 수 있으며, 기저귀, 성인용 실금패드 및 브리프, 및 여성용 생리대와 같은 일회용 흡수용품용 흡수중심으로서 특히 유용하다.The absorbent structure has an absorbent capacity of unbonded air felt structure with improved particle content and can be delivered in the form of a roll, absorbent center for disposable absorbent articles such as diapers, adult incontinence pads and briefs, and women's sanitary napkins. It is particularly useful as
도면을 참조하면, 본 발명의 흡수구조는 포착(2), 분포(4) 및 저장(14)영역을 가지는, 다층섬유성구조(10)를 포함한다. 구조의 포착 및 분포영역은 사전형성되거나 저장층과 동시에 형성될 수 있는 포착-분포층(12)(ADL)을 가지고 있다. 결합된 구조는 에어레이드, 웨트레이드, 열결합, 소면 등의 기술에 의해 형성될 수 있다. 구조의 저장영역은 셀룰로로스섬유의 에어펠트층(6)을 가지고 있다. 저장영역은 또한 SAP입자, 과립 또는 섬유(18)를 포함한다. 본 명세서에서 사용된 바와 같이, 에어펠트층은 서로 결합되지 않은 에어레이드섬유의 층이다. 에어펠트층은 낮은 웨브강도를 가지기 때문에, SAP입자와 혼합된 셀룰로오스섬유를 ADL(12)의 분포영역면(4)으로 직접 에어레잉함으로써 형성된다. 그 결과 발생하는 ADL-에어펠트구조의 구조적 완전성은 에어펠트층을 ADL에 봉인함으로써 유지된다. 전환하는 동안 흡수중심의 측면가장자리를 형성할 그러한 위치에서 봉인이 이루어진다. 바람직하게는, 함유층(8)은 구조의 에어펠트층의 노출된 표면 위에 제공된다. 동시에 함유층은 저장영역과 SAP가 Z방향으로 압박없이 또는 실질적으로 압박없이 팽창하도록 충분한 부피를 제공하기 위하여 구조에 봉해진다.Referring to the drawings, the absorbent structure of the present invention includes a multi-layered fibrous structure 10 having a capture 2, distribution 4, and storage 14 area. The capture and distribution regions of the structure have a capture-distribution layer 12 (ADL) that can be preformed or formed simultaneously with the storage layer. The bonded structure can be formed by techniques such as airlaid, wetlaid, thermal bonding, carding and the like. The storage area of the structure has an air felt layer 6 of cellulose fiber. The storage area also includes SAP particles, granules or fibers 18. As used herein, an air felt layer is a layer of airlaid fibers that are not bonded to each other. Since the air felt layer has a low web strength, it is formed by directly airlaying cellulose fibers mixed with SAP particles to the distribution area surface 4 of the ADL 12. The structural integrity of the resulting ADL-air felt structure is maintained by sealing the air felt layer in the ADL. Sealing takes place at such locations that will form the lateral edges of the absorption center during the transition. Preferably, the containing layer 8 is provided on the exposed surface of the air felt layer of the structure. At the same time, the containing layer is sealed in the structure to provide sufficient volume for the storage area and the SAP to expand in the Z direction without pressure or substantially without pressure.
포착-분포층Capture-Distribution Layer
바람직하게는, 본 발명의 ADL은 적어도 2개의 이산층을 가지는 부직포구조이다. 흡수제품의 사용자에게 가장 가까운 ADL층(상부 또는 포착층)은 전적으로 변형된 셀룰로오스 또는 합성섬유와 결합제수지로 구성된 섬유함량을 가진다. 흡수구조의 액체저장(바닥)층(분포층)에 가장 가까운 ADL층(분포층)은 우선 에어레이드-보풀 셀룰로오스, 화학적으로 변형된 셀룰로오스 섬유, 교차결합된 셀룰로오스섬유, 목화잔털섬유 또는 그들의 혼합물로 구성된 섬유함량을 가진다. 각 층의 기본중량은 30 내지 120 gsm인 총 ADL기본중량에 대해 15-60 gsm의 범위인 것이 바람직하다. 선택적으로 중간층이 포함될 수 있다. 그러한 중간층은 100% 보풀 셀룰로오스 및/또는 화학적으로 변형된 셀룰로오스섬유인 섬유조성을 가지거나 합성섬유와 셀룰로오스섬유의 혼합인 섬유조성을 가질 수 있다.Preferably, the ADL of the present invention is a nonwoven structure having at least two discrete layers. The ADL layer (top or capture layer) closest to the user of the absorbent product has a fiber content consisting entirely of modified cellulose or synthetic fibers and binder resin. The ADL layer (distribution layer) closest to the liquid storage (bottom) layer of the absorbent structure is first composed of airlaid- fluff cellulose, chemically modified cellulose fibers, cross-linked cellulose fibers, cotton fuzz fibers or mixtures thereof. It has a configured fiber content. The basis weight of each layer is preferably in the range of 15-60 gsm relative to the total ADL basis weight of 30 to 120 gsm. Optionally an interlayer can be included. Such intermediate layer may have a fiber composition which is 100% fluff cellulose and / or chemically modified cellulose fibers or a fiber composition which is a mixture of synthetic and cellulose fibers.
바람직한 실시형태에서, ADL의 포착층면은 10-20중량%의 라텍스와 결합된 절단길이 6㎜이고 크기가 6.7 wt/길이의 섬유 dtex인 폴리에스테르(PET)섬유 80-90중량%이다. 바닥 또는 분포층은 10-20%의 수성 결합제와 결합된 80-90% 섬유질제거 보풀 셀룰로오스섬유이다. ADL의 총 기본중량은 60-80 gsm이고 상부합성섬유층은 ADL의 총 기본중량의 25-50%이다. 섬유화된 보풀 셀룰로오스섬유는 폴리보풀(Foley fluff)과 같은 목재셀룰로오스, 목화잔털펄프, 교차결합된 셀룰로오스섬유와 같은 화학적으로 변형된 셀룰로오스, 또는 벅아이(Buckeye) HPF{테네시주 멤피스의 벅아이 테크놀로지즈 인코포레이티드(Buckeye Technologies, Inc.)로부터 각각 이용할 수 있음}와 같은 고정제 셀룰로오스섬유로부터 선택될 수 있다.In a preferred embodiment, the trapping layer surface of the ADL is 80-90% by weight of polyester (PET) fiber having a cut length of 6 mm combined with 10-20 wt. The bottom or distribution layer is 80-90% defiber lint cellulose fibers combined with 10-20% aqueous binder. The total basis weight of ADL is 60-80 gsm and the top synthetic fiber layer is 25-50% of the total basis weight of ADL. Fibrillated fluff cellulose fibers are wood cellulose, such as Foley fluff, cotton wool pulp, chemically modified cellulose, such as cross-linked cellulose fibers, or Buckeye HPF (Buckeye HPF, Memphis, Tennessee). Fixative cellulose fibers, such as each available from Buckeye Technologies, Inc.).
다른 바람직한 실시형태에서, ADL의 상부층과 바닥층은 상기와 같은 조성을 가지고, 또한 PET와 셀룰로오스섬유의 혼합물인 중간층을 포함할 수 있다. 이 실시형태에서, 상부층은 총 ADL중량의 적어도 10%이고, 바닥층은 총 ADL 기본중량의 50% 정도이다.In another preferred embodiment, the top and bottom layers of ADL have the composition as above and may also include an intermediate layer that is a mixture of PET and cellulose fibers. In this embodiment, the top layer is at least 10% of the total ADL weight and the bottom layer is on the order of 50% of the total ADL basis weight.
저장층Storage layer
상기에서 설명된 바와 같이, 저장층은 섬유화된 보풀 셀룰로오스섬유로 만들어지는 것이 바람직하다. 가장 바람직한 것은 폴리보풀과 같은 목재셀룰로오스이다. 또한 목화잔털펄프, 교차결합된 셀룰로오스섬유와 같은 화학적으로 변형된 셀룰로오스와 벅아이 HPF(테네시주 멤피스의 벅아이 테크놀로지즈 인코포레이티드로부터 각각 이용할 수 있음)와 같은 고정제 셀룰로오스섬유도 바람직하다. 보풀섬유는 PET와 같은 폴리에스테르, 나일론, 폴리에틸렌 또는 폴리프로필렌과 같은 합성섬유와 혼합될 수 있다. 또한, 2성분 열가소성 섬유도 셀룰로오스 또는 합성섬유와 혼합될 수 있다. 바람직한 열가소성섬유는 호치스트-셀라니즈(Hoechst-Celanese)사의 셀본드 타입 255 비코섬유(Celbond Type 255 Bico fiber)와 혼합될 수 있다. 비코섬유는 폴리에스테르중심과 활성화된 공-폴리올레핀 덮개를 가진다.As described above, the storage layer is preferably made of fibrillated fluff cellulose fibers. Most preferred is wood cellulose such as poly fluff. Also preferred are chemically modified celluloses such as cotton wool pulp, crosslinked cellulose fibers and fixative cellulose fibers such as Buckeye HPF (available from Buckeye Technologies Inc. of Memphis, Tennessee, respectively). Fluff fibers can be mixed with polyester, such as PET, nylon, polyethylene, or synthetic fibers, such as polypropylene. In addition, bicomponent thermoplastic fibers can also be mixed with cellulose or synthetic fibers. Preferred thermoplastic fibers can be mixed with Cellbond Type 255 Bico fibers from Hoechst-Celanese. Bicofibers have a polyester center and an activated co-polyolefin sheath.
흡수중심의 에어레이드제조Absorption-oriented Airlaid Manufacturing
바람직하게는, ADL은 에어레이드 웨브로 제조된다. 에어레이드 웨브는 개별화된 섬유를 제공하기 위하여, 일반적으로 해머밀에 의하여, 셀룰로오스펄프시트 또는 시트들을 분해하거나 섬유질제거함으로써 제조되는 것이 일반적이다. 개별화된 섬유는 그 다음에 에어레이드웨브형성장치 상으로 형성헤드로 공기운송된다. 덴마크의 M＆J 화이버테크(M＆J Fibertech)와 덴마크의 댄-웨브(Dan-Web)를 포함한, 여러 제조자들이 에어레이드웨브형성장치를 만든다. 형성헤드는 섬유들이 진공에 의해 소공압축드럼 또는 소공형성 컨베이어(또는 형성와이어)로 끌어당겨질 때까지 섬유분리를 유지하는 역할을 하는 일반적으로 레이스트랙구조 내에, 회전 또는 교반드럼을 포함한다. M＆J장치에서는, 형성헤드는 스크린 위에 회전교반기를 포함한다. 합성 열가소성섬유와 같은 다른 섬유들도 섬유개시기, 투여장치 및 공기컨베이어를 포함하는 섬유투여시스템을 통해 형성헤드에 도입될 수 있다. 보풀펄프분포층과 합성섬유포착층과 같은 2개의 규정층이 바람직한 경우, 각 형태의 섬유마다 하나씩 두 개의 독립형성헤드가 제공된다.Preferably, the ADL is made of airlaid web. Airlaid webs are generally produced by hammer milling, by breaking down or de-fiberizing cellulose pulp sheets or sheets, to provide individualized fibers. The individualized fibers are then air conveyed onto the forming heads on the airlaid web forming apparatus. Several manufacturers, including Denmark's M & J Fibertech and Denmark's Dan-Web, make airlaid web forming devices. The forming head includes a rotating or stirring drum, generally in a racetrack structure, which serves to maintain fiber separation until the fibers are pulled into the pore compression drum or pore forming conveyor (or forming wire) by vacuum. In the M & J apparatus, the forming head includes a rotary stirrer on the screen. Other fibers, such as synthetic thermoplastics, can also be introduced into the forming head through a fiber dosing system including a fiber initiator, a dosing device and an air conveyor. If two prescribed layers, such as a fluff pulp distribution layer and a synthetic fiber trapping layer, are desired, two independent heads are provided, one for each type of fiber.
저장층은 에어펠트형태로 제조되는 것이 바람직하다. 상기에서 설명된 바와 같이, 에어펠트는 에어레이드장치를 사용하여 만들어지지만 별도의 결합제는 사용되지 않는다. 본 발명에 대해 잘 생각함에 따라, 에어레이드웨브형성장치의 형성헤드는 흡수중심의 저장영역을 위해 원하는 섬유는 ADL층으로 분포시킨다. 바람직하게는, 이 섬유는 셀룰로오스보풀이다. SAP과립은 형성헤드에 의해 분포되도록 보풀과 혼합되거나 투여헤드에 의해 에어펠트웨브에 별도로 도포된다. SAP뿐 아니라, 다른 기능성 미립자들도 에어펠트 내에 포함될 수 있다. 그러한 미립자에는 제올라이트, 방향제 등과 같은 냄새제어제가 포함된다.The storage layer is preferably manufactured in the form of an air felt. As described above, the air felt is made using an airlaid device but no separate binder is used. As is well understood in the present invention, the forming head of the airlaid web forming apparatus distributes the desired fibers to the ADL layer for the storage area of the absorption center. Preferably, this fiber is cellulose fluff. The SAP granules are mixed with the fluff to be distributed by the forming head or applied separately to the air felt web by the dosing head. In addition to SAP, other functional particulates may also be included in the air felt. Such particulates include odor control agents such as zeolites, fragrances and the like.
에어레이드 웨브는 형성와이어로부터 웨브의 밀도를 증가시키고, 그것의 강도을 증가시키며 웨브두께를 제어하기 위하여 캘린더가공 또는 다른 고밀도화단계로 운반된다. 웨브의 섬유는 그 다음에 라텍스분무 또는 거품추가시스템을 적용하여 결합된 후, 건조 또는 경화된다. 선택적으로, 또는 추가적으로, 웨브 내에 존재하는 어떤 열가소성 섬유는 웨브의 섬유들을 결합시키기 위해 열을 가함으로써 부드러워지거나 부분적으로 용융될 수 있다. 결합된 웨브는 그 다음에 강도를 증가시키거나 웨브를 디자인 또는 패턴으로 가공하기 위하여 2번째로 캘린더가공될 수 있다. 열가소성 섬유가 있다면, 패턴형성된 결합을 웨브에 가하기 위하여 열캘린더가공이 사용될 수 있다. 특정 또는 원하는 수분함량을 유지하고, 먼지제거작업을 최소화하며 정전기의 축적을 감소시키기 위하여 필요하다면 웨브에 물을 추가할 수 있다. 장래 사용을 위하여 최종 웨브를 감는다.Airlaid webs are conveyed from the forming wire to calendering or other densification to increase the density of the web, increase its strength and control the web thickness. The fibers of the web are then joined by applying a latex spray or foam addition system and then dried or cured. Alternatively, or in addition, any thermoplastic fibers present in the web may be softened or partially melted by applying heat to join the fibers of the web. The bonded web can then be calendered a second time to increase strength or to process the web into a design or pattern. If there are thermoplastic fibers, thermal calendaring can be used to apply the patterned bonds to the web. Water can be added to the web as needed to maintain a specific or desired moisture content, minimize dust removal and reduce static buildup. Wind the final web for future use.
선택적으로, ADL과 에어펠트층을 조립하기 위하여, 에어레이드 라인 위에 에어펠트층을 형성할 수 있다. 미리 제조된 에어레이드 ADL은 에어펠트층형성 및 투여헤드의 상부로 풀린다. 그 다음에 함유층이 에어펠트층으로 풀린다. 다음으로, 함유층이 에어펠트층, SAP 및 다른 미립자들을 함유하도록 봉해진다.Optionally, an air felt layer can be formed over the airlaid line to assemble the ADL and the air felt layer. The pre-made airlaid ADL is unwound to the top of the air felt layering and dosing head. The containing layer is then loosened with an air felt layer. Next, the containing layer is sealed to contain an air felt layer, SAP and other fine particles.
함유층Containing layer
함유층은 SAP와 선택적으로 다른 입자를 함유하는 가볍게 결합되거나 결합되지 않은 에어펠트저장층을 그 자리에 보유하는데 사용된다. 함유층은 저장층의 섬유와 SAP입자가 액체흡수에 따라 Z방향으로 팽창하는 것을 억제하지 않으면서 보유해야 한다. 함유층은 흡수층의 역할을 하지 않고 사실 액체불투과바닥층의 역할도 할 수 있다. 함유층에 적합한 물질에는 열가소성 막, 소면된 부직포 또는 직물조직 등이 포함된다. 적합한 열가소성 물질의 예에는 폴리에틸렌과 폴리프로필렌이 포함된다.The containing layer is used to hold in place a lightly bonded or unbonded air felt storage layer containing SAP and optionally other particles. The containing layer should be retained without inhibiting the fibers of the storage layer and the SAP particles from expanding in the Z direction upon liquid absorption. The containing layer does not act as an absorbing layer but may in fact also serve as a liquid impermeable bottom layer. Suitable materials for the containing layer include thermoplastic membranes, carded nonwovens or woven fabrics. Examples of suitable thermoplastics include polyethylene and polypropylene.
함유층은 여러 가지 방법으로 흡수구조에 봉인될 수 있다. 함유층은 원하는 위치에서 구조에 선택적으로 열봉인될 수 있은 열가소성물질로 만들어질 수 있다. 선택적으로 함유층은 함유층이 도포되기 전에 원하는 봉인위치에서 구조에 압력민감성 또는 열용융된 접착제를 도포함으로써 구조에 봉인될 수 있다. 라텍스 또는 다른 결합제도 접착제로 사용될 수 있다. 초음파 용접도 함유층을 구조에 봉하는데 사용될 수 있다. 열가소성 섬유가 저장층 내에 있다면, 봉인형성이 바람직한 곳에 국부적인 열을 가함으로써 함유층을 저장층에 봉인하는데 사용될 수 있다. 함유층은 유체흡수에 따라 저장층의 팽창을 억제하지 않을 정도까지 봉인하는 동안 아래에 놓인 저장층을 압축하거나 억제하지 않아야 한다.The containing layer can be sealed to the absorbent structure in a number of ways. The containing layer can be made of a thermoplastic material that can optionally be sealed to the structure at the desired location. Optionally, the containing layer may be sealed to the structure by applying a pressure sensitive or hot melt adhesive to the structure at the desired sealing position before the containing layer is applied. Latex or other binders may also be used as the adhesive. Ultrasonic welding can also be used to seal the containing layer to the structure. If the thermoplastic fibers are in the storage layer, they can be used to seal the containing layer to the storage layer by applying local heat where sealing is desired. The containing layer should not compress or inhibit the underlying storage layer while sealing to such an extent that it will not inhibit expansion of the storage layer upon fluid absorption.
본 발명에 의해 생각된 흡수중심은 기저귀, 성인용 실금패드 및 여성용 위생패드에 사용하기 위하여, 직사각형, 모래시계, T자형, 또는 다른 포개진 형태로 절단되는 것이 일반적이다. 직사각형 중심의 각 가장자리에서 봉인을 형성하기 위해서는, 세로봉인(롤의 기계방향임)이 흡수중심의 원하는 폭만큼 이격된 웨브를 따라 열봉인을 형성하기 위한 예를 들면 리브로 둘러싸이고 가열된 캘린더에 의해, 웨브에 적용되는 것이 바람직하다. 그 다음에 웨브는 원하는 흡수중심폭의 독립웨브를 형성하기 위하여 열 봉인에서 기계방향으로 분할될 수 있고, 각 폭이 좁은 웨브는 양 가장자리를 따라 열봉인을 가진다. 폭이 좁은 웨브에는 교차방향으로 이격된 열봉인이 가해진다. 이러한 방식으로, 분할나이프는 열봉인을 2개로 분할할 수 있고 노출되고 봉인되지 않은 가장자리를 남기거나 물질을 낭비하는 것을 피할 수 있다.The absorption center contemplated by the present invention is generally cut into rectangular, hourglass, T-shaped, or other nested forms for use in diapers, adult incontinence pads, and feminine sanitary pads. To form a seal at each edge of the rectangular center, a longitudinal seal (in the machine direction of the roll) is for example formed by a ribbed and heated calender to form a heat seal along the web spaced apart by the desired width of the absorption center. It is preferable to apply to a web. The web can then be divided in the machine direction from the heat seal to form an independent web of desired absorption center width, with each narrow web having heat seals along both edges. Narrow webs are subjected to heat seals spaced apart in the cross direction. In this way, the splitting knife can split the heat seal into two and avoid leaving exposed and unsealed edges or wasting material.
분할된 열봉인은 분할 후 2개의 유효봉인을 제공하기에 충분한 폭이어야만 한다. 이러한 봉인의 간격은 최종 흡수중심의 원하는 길이에 의해 결정된다. 마지막으로, 폭이 좁은 웨브는 최종제품으로 전환할 준비가 된 개별적인 흡수중심을 형성하기 위하여 교차방향열봉인에서 절단될 수 있다. 그러나 바람직하게는, 폭이 좁은 웨브는 (교차방향 열봉인이 팽창되더라도) 절단되지 않고 전환위치로 수송하기 위하여 감겨진다.The divided heat seals shall be of sufficient width to provide two effective seals after dividing. The spacing of these seals is determined by the desired length of the final absorption center. Finally, narrow webs can be cut in crosswise heat seals to form individual absorption centers ready to be converted into final products. Preferably, however, the narrow web is wound to transport to the switching position without cutting (even if the crosswise seal is expanded).
흡수중심의 웨트레이드제조Absorbent Wet Laid Manufacturing
에어레이드웨브 제조방법이 본 발명의 흡수중심의 제조에 바람직하지만, ??레이드방법도 선택적으로 사용될 수 있다. 구조를 제조하기 위하여, 델타형성자를 사용한 다중헤드박스페이퍼장치가 사용된다. 제1헤드박스는 포착영역섬유를 분포시킨다. 제2헤드박스는 분포영역섬유를 분포시킨다. 그 결과로 생긴 웨브는 에어레잉에 의해 저장영역섬유와 SAP를 도포하기 전에 건조기부분을 통과한다. 그 다음에 함유층이 구조에 도포되고 상기에서 설명된 바와 같이 봉인이 이루어진다.Although the airlaid web manufacturing method is preferred for producing the absorption center of the present invention, the ?? laiding method may also be optionally used. In order to manufacture the structure, a multihead box paper apparatus using a delta former is used. The first headbox distributes the capture area fibers. The second headbox distributes the distribution area fibers. The resulting web passes through the dryer section before applying the storage area fibers and SAP by airlaying. The containing layer is then applied to the structure and sealed as described above.
Claims (9)