KR20010004022A - Method of manufacturing LCD - Google Patents
Method of manufacturing LCD Download PDFInfo
- Publication number
- KR20010004022A KR20010004022A KR1019990024607A KR19990024607A KR20010004022A KR 20010004022 A KR20010004022 A KR 20010004022A KR 1019990024607 A KR1019990024607 A KR 1019990024607A KR 19990024607 A KR19990024607 A KR 19990024607A KR 20010004022 A KR20010004022 A KR 20010004022A
- Authority
- KR
- South Korea
- Prior art keywords
- metal film
- etching
- amorphous silicon
- silicon layer
- gas
- Prior art date
Abstract
Description
본 발명은 액정표시소자의 제조방법에 관한 것으로, 특히, 데이터 라인을 티타늄 금속막과 몰리브덴 금속막의 적층 구조로 형성시키는 액정표시소자의 제조방법에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing a liquid crystal display device, and more particularly, to a method for manufacturing a liquid crystal display device in which a data line is formed in a laminated structure of a titanium metal film and a molybdenum metal film.
텔레비젼 및 그래픽 디스플레이 등의 표시 장치에 이용되는 액정표시소자 (Liquid Crystal Display : 이하, LCD)는 CRT(Cathod-ray tube)를 대신하여 개발되어져 왔다. 특히, 매트릭스 형태로 배열된 각 화소마다 박막 트랜지스터(Thin Film Transistor : 이하, TFT)가 구비된 TFT LCD는 고속 응답 특성을 갖는 잇점과 고화소수에 적합하다는 잇점 때문에 CRT에 필적할만한 화면의 고화질화 및 대형화, 컬러화 등을 실현하고 있다.Liquid crystal displays (hereinafter, LCDs) used in display devices such as televisions and graphic displays have been developed in place of the CRT (Cathod-ray tube). In particular, TFT LCDs equipped with thin film transistors (TFTs) for each pixel arranged in a matrix form have high-speed response characteristics and are suitable for high pixel counts, so that the screen quality comparable to CRTs is increased in size and size. Colorization is realized.
이러한 TFT LCD는 TFT 및 화소전극이 형성된 TFT 어레이 기판과, 컬러필터 및 상대전극이 형성된 컬러필터 기판이 액정층의 개재하에 합착된 구조이다.Such a TFT LCD has a structure in which a TFT array substrate on which a TFT and a pixel electrode are formed, and a color filter substrate on which a color filter and a counter electrode are formed are bonded together through a liquid crystal layer.
한편, TFT 어레이 기판의 제조 공정을 단순화시키는 것은, 즉, 포토 공정의 수를 줄이는 것은 제조비용 측면에서 TFT LCD의 상용화에 크게 영향을 미친다. 따라서, 포토 공정의 수를 감소시키기 위한 여러 가지 구조들이 제안되고 있으며, 한 예로, 최근에는 ITO 금속막으로 이루어진 화소전극을 TFT 어레이 기판의 최상부에 배치시키는 탑 ITO 구조가 제안되고 있다.On the other hand, simplifying the manufacturing process of the TFT array substrate, that is, reducing the number of photo processes greatly affects the commercialization of the TFT LCD in terms of manufacturing cost. Accordingly, various structures for reducing the number of photo processes have been proposed. For example, recently, a top ITO structure in which a pixel electrode made of an ITO metal film is disposed on the top of a TFT array substrate has been proposed.
이러한 탑 ITO 구조는 TFT 어레이 기판은 5단계의 포토 공정에 의해 제작할 수 있기 때문에, 6 또는 7단계의 포토 공정을 요구하는 통상의 TFT 어레이 기판의 제조 공정 보다 그 제조공정의 단순화을 얻을 수 있으며, 이에 따라, 제조비용의 절감 효과를 얻을 수 있다.Since the top ITO structure can produce a TFT array substrate by a five-step photo process, the manufacturing process can be simplified rather than a conventional TFT array substrate manufacturing process requiring a six- or seven-step photo process. Therefore, the manufacturing cost can be reduced.
그러나, 상기와 같은 탑 ITO 구조의 TFT 어레이 기판의 제조시에는, 화소전극을 형성하기 위한 ITO 금속막의 식각시에 사용되는 식각 용액(이하, ITO 에천트라 칭함)에 의해 데이터 라인의 손상이 발생되는 문제점이 있다.However, in manufacturing a TFT array substrate having a top ITO structure as described above, data lines are damaged by an etching solution (hereinafter referred to as ITO etchant) used for etching an ITO metal film for forming a pixel electrode. There is a problem.
자세하게, 탑 ITO 구조의 TFT 어레이 기판의 제조 공정중의 하나인 보호막의 형성시에는, 하부층의 표면 단차에 기인하여, 보호막의 스텝 커버리지 특성이 저하되기 때문에, 소오스/드레인 전극을 포함하는 데이터 라인이 보호막에 의해 덮혀지지 않게 되는 현상이 발생하게 되고, 또한, 보호막 내에는 그 증착시에 파티클, 또는, 스트레스에 의한 크랙이 발생하게 된다.In detail, at the time of forming the protective film which is one of the manufacturing processes of the TFT array substrate of the top ITO structure, the step coverage characteristic of the protective film is lowered due to the surface step of the lower layer, so that the data line including the source / drain electrodes is reduced. The phenomenon that the protective film is not covered by the protective film occurs, and in the protective film, particles or cracks due to stress are generated during the deposition.
또한, ITO 에천트로서, 종래에는 염산 및 질산, 또는, 염산 및 초산으로 이루어진 화학 용액을 사용하고 있는데, 이러한 ITO 에천트에 대해 통상 데이터 라인용 금속막으로 사용되고 있는 알루미늄 금속막은 매우 취약한 특성을 보이고 있다.In addition, as an ITO etchant, a chemical solution made of hydrochloric acid and nitric acid, or hydrochloric acid and acetic acid is conventionally used. An aluminum metal film, which is usually used as a metal film for data lines, exhibits very weak characteristics. have.
그런데, 상기와 같이, 데이터 라인이 보호막에 의해 덮혀지지 않거나, 또는, 보호막 내에 파티클 및 크랙이 발생된 상태로 후속의 ITO 공정을 진행하게 되면, ITO 에천트는 파티클 및 크랙을 통해 알루미늄 금속막으로 침투하여 접촉하거나, 또는, 직접적으로 알루미늄 금속막과 접촉하게 되고, 이때, 알루미늄 금속막은 ITO 에천에 대해 매우 취약한 특성을 보이기 때문에, 알루미늄 금속막은 ITO 에천트에 의해 부식되고, 결과적으로, 데이터 라인의 손상이 발생하게 됨은 물론, 심한 경우에는 데이터 라인의 오픈 불량이 발생하게 된다.However, as described above, when the data line is not covered by the protective film or a subsequent ITO process is performed with particles and cracks generated in the protective film, the ITO etchant penetrates into the aluminum metal film through the particles and cracks. Contact with, or in direct contact with, the aluminum metal film, since the aluminum metal film exhibits very fragile properties to the ITO etchant, the aluminum metal film is corroded by the ITO etchant, resulting in damage to the data line. In addition to this, in severe cases, an open failure of the data line may occur.
따라서, 상기와 같은 데이터 라인이 손상되는 것을 방지하기 위하여, 최근에는 ITO 에천트에 대해서 영향을 적게 받는 몰리브덴 금속막을 데이터 라인용 금속막으로 이용하는 방법이 수행되고 있다.Therefore, in order to prevent such a data line from being damaged, a method of using a molybdenum metal film, which is less affected by ITO etchant, as a metal film for data lines has been recently performed.
그러나, 몰리브덴 금속막을 데이터 라인용 금속막으로 이용할 경우에는, 상기 몰리브덴 금속막을 식각함에 있어서, 다음과 같은 문제점이 있다.However, when the molybdenum metal film is used as the data line metal film, there are the following problems in etching the molybdenum metal film.
먼저, 몰리브덴 금속막에 대한 습식 식각은 그 물질 특성상, 균일도의 제어가 어렵기 때문에, 그 적용이 곤란하다. 반면에, 몰리브덴 금속막에 대한 건식 식각은 균일도의 제어가 습식 식각 공정에 비해 용이한 잇점은 있으나, 몰리브덴 금속막의 식각시에, 그 하부에 배치된 오믹층(n+a-Si) 및 반도체층(a-Si)에 데미지를 주게 되고, 아울러, 몰리브덴 금속막과 오믹층을 연속적으로 식각하는 인-시튜(In-Situ) 공정시, 반도체층에 대한 식각 균일도의 제어가 어렵기 때문에, 결과적으로, TFT 특성의 불균일이 발생하게 되는 문제점이 있다.First, the wet etching of the molybdenum metal film is difficult to control because of its material property, which makes it difficult to apply the wet etching. On the other hand, the dry etching of the molybdenum metal film has the advantage that the uniformity is easier to control than the wet etching process. However, when etching the molybdenum metal film, the ohmic layer (n + a-Si) and the semiconductor layer disposed thereunder As a result, damage to (a-Si) and in-situ process of continuously etching the molybdenum metal film and the ohmic layer are difficult to control the etching uniformity of the semiconductor layer. There is a problem that non-uniformity of TFT characteristics occurs.
따라서, 상기와 같은 문제점을 해결하기 위하여 안출된 본 발명은, 몰리브덴 금속막의 식각시에 오믹층 및 반도체층에 데미지가 인가되는 것이 방지되도록, 몰리브덴 금속막의 하부에 티타늄 금속막을 블로킹막으로서 개재시키고, 아울러, 데이터 라인을 형성하기 위한 식각 공정을 3단계로 나누어 수행함으로써, 식각 균일도 및 반도체층의 특성 저하를 방지할 수 있는 LCD의 제조방법을 제공하는데, 그 목적이 있다.Accordingly, the present invention devised to solve the above problems is to interpose a titanium metal film as a blocking film on the lower part of the molybdenum metal film to prevent damage to the ohmic layer and the semiconductor layer during etching of the molybdenum metal film, In addition, by performing the etching process for forming a data line divided into three stages, to provide a method for manufacturing an LCD that can prevent the etching uniformity and the characteristics of the semiconductor layer deteriorated.
도 1a 내지 도 1d는 본 발명의 실시예에 따른 액정표시소자의 제조방법을 설명하기 위한 공정 단면도.1A to 1D are cross-sectional views illustrating a method of manufacturing a liquid crystal display device according to an exemplary embodiment of the present invention.
(도면의 주요 부분에 대한 부호의 설명)(Explanation of symbols for the main parts of the drawing)
1 : 유리기판 2 : 게이트 라인1: glass substrate 2: gate line
3 : 게이트 절연막 4 : 비도핑된 비정질실리콘층3: gate insulating film 4: undoped amorphous silicon layer
4a : 반도체층 5 : 도핑된 비정질실리콘층4a: semiconductor layer 5: doped amorphous silicon layer
5a : 오믹층 6 : 티타늄 금속막5a: ohmic layer 6: titanium metal film
7 : 몰리브덴 금속막 10 : 데이터 라인용 금속막7 molybdenum metal film 10 metal film for data line
10a,10b : 소오스/드레인 전극 11 : 감광막 패턴10a, 10b: source / drain electrodes 11: photosensitive film pattern
상기와 같은 목적을 달성하기 위한 본 발명의 LCD의 제조방법은, 절연성 기판 상에 게이트 라인, 게이트 절연막, 비도핑된 비정질실리콘층 및 도핑된 비정질실리콘층을 순차적으로 형성하는 단계; 상기 도핑된 비정질실리콘층 상에 티타늄 금속막과 몰리브덴 금속막의 적층 구조로 이루어진 데이터 라인용 금속막을 증착하는 단계; 상기 데이터 라인용 금속막인 몰리브덴 금속막 상에 그의 소정 부분을 노출시키는 감광막 패턴을 형성하는 단계; 상기 감광막 패턴을 식각 마스크로해서, 노출된 몰리브덴 금속막 부분은 불소 계열의 식각 가스로 식각하는 단계; 상기 몰리브덴 금속막의 일부분이 식각되어 노출된 티타늄 금속막 부분을 염소 계열의 식각 가스로 식각하는 단계; 및 상기 티타늄 금속막이 식각되어 노출된 도핑된 비정질실리콘층 부분과 그 하부에 배치된 비도핑된 비정질실리콘층의 일부 두께를 불소 계열의 식각 가스로 식각하는 단계를 포함하여 이루어진다.Method of manufacturing an LCD of the present invention for achieving the above object comprises the steps of sequentially forming a gate line, a gate insulating film, an undoped amorphous silicon layer and a doped amorphous silicon layer on an insulating substrate; Depositing a metal film for data line having a stacked structure of a titanium metal film and a molybdenum metal film on the doped amorphous silicon layer; Forming a photoresist pattern on the molybdenum metal film, which is the metal film for data lines, to expose a predetermined portion thereof; Etching the exposed molybdenum metal film portion with a fluorine-based etching gas using the photoresist pattern as an etching mask; Etching a portion of the titanium metal film exposed by etching a part of the molybdenum metal film with a chlorine-based etching gas; And etching a portion of the doped amorphous silicon layer exposed by etching the titanium metal layer and a portion of the undoped amorphous silicon layer disposed below the fluorine-based etching gas.
본 발명에 따르면, 데이터 라인을 티타늄 금속막과 몰리브덴 금속막의 적층 구조로 형성하여, 상기 티타늄 금속막이 식각 데미지에 대한 블로킹층으로서의 기능을 하게 함으로써, 상기 몰리브덴 금속막의 식각시에 오믹층 및 반도체층이 손상되는 것을 방지할 수 있으며, 이에 따라, TFT의 특성 저하를 방지할 수 있다.According to the present invention, the data line is formed in a laminated structure of a titanium metal film and a molybdenum metal film, so that the titanium metal film functions as a blocking layer against etching damage. The damage can be prevented, and therefore, the deterioration of the TFT characteristics can be prevented.
이하, 첨부된 도면을 참조하여, 본 발명의 바람직한 실시예를 보다 상세하게 설명하도록 한다.Hereinafter, with reference to the accompanying drawings, it will be described in detail a preferred embodiment of the present invention.
도 1a 내지 도 1d는 본 발명의 실시예에 따른 LCD의 제조방법을 설명하기 위한 공정 단면도이다.1A to 1D are cross-sectional views illustrating a method of manufacturing an LCD according to an exemplary embodiment of the present invention.
먼저, 도 1a에 도시된 바와 같이, 절연성 기판, 예컨데, 유리기판(1) 상에 게이트 라인(2)과 게이트 절연막(3)을 차례로 형성하고, 상기 게이트 절연막(3) 상에 도핑되지 않은 비정질실리콘층(a-Si : 4)과 도핑된 비정질실리콘층(n+a-Si : 5)을 차례로 형성한다. 여기서, 도핑되지 않은 비정질실리콘층(4)은 TFT의 반도체층이 되는 층이며, 도핑된 비정질실리콘층(5)은 상기 반도체층과 후속에서 형성되는 소오스/드레인 전극간의 접촉 특성을 향상시키기 위한 오믹층이 되는 층이다.First, as shown in FIG. 1A, a gate line 2 and a gate insulating film 3 are sequentially formed on an insulating substrate, for example, a glass substrate 1, and then undoped amorphous on the gate insulating film 3. A silicon layer (a-Si: 4) and a doped amorphous silicon layer (n + a-Si: 5) are sequentially formed. Here, the undoped amorphous silicon layer 4 is a layer which becomes the semiconductor layer of the TFT, and the doped amorphous silicon layer 5 is used to improve contact characteristics between the semiconductor layer and the source / drain electrodes formed subsequently. It is a layer which becomes a mix layer.
계속해서, 도핑된 비정질실리콘층(5) 상에 티타늄 금속막(6)과 몰리브덴 금속막(7)이 차례로 증착된 적층 구조의 데이터 라인용 금속막(10)을 형성하고, 이어서, 상기 데이터 라인용 금속막(10)인 몰리브덴 금속막(7) 상에 그의 소정 부분을 노출시키는 감광막 패턴(11)을 형성한다. 여기서, 몰리브덴 금속막(7)은 실질적인 데이터 라인의 기능을 하는 막으로서, 2,000∼3,000Å 두께로 증착한다. 그리고, 티타늄 금속막(6)은 상기 몰리브덴 금속막(7)의 식각시에, 식각 데미지가 하부층으로 전달되는 것을 막기 위한 블로킹층으로서의 기능을 하는 막으로서, 300∼500Å의 두께로 증착한다.Subsequently, on the doped amorphous silicon layer 5, a metal film 10 for a data line having a laminated structure in which a titanium metal film 6 and a molybdenum metal film 7 were sequentially deposited was formed, and then the data line. The photosensitive film pattern 11 which exposes the predetermined part is formed on the molybdenum metal film 7 which is the metal film 10 for metals. Here, the molybdenum metal film 7 is a film which functions as a substantial data line, and is deposited at a thickness of 2,000 to 3,000 Å. The titanium metal film 6 is a film which functions as a blocking layer for preventing the etching damage from being transferred to the lower layer during the etching of the molybdenum metal film 7 and is deposited at a thickness of 300 to 500 kPa.
다음으로, 도 1b에 도시된 바와 같이, 감광막 패턴을 식각 마스크로해서, 노출된 몰리브덴 금속막(7) 부분을 불소 계열의 가스, 예를들어, SF6가스와 CF4가스의 혼합 가스로 식각·제거한다. 이때, 전술한 바와 같이, 티타늄 금속막(6)은 몰리브덴 금속막(7)의 식각시에, 도핑된 비정질실리콘층(5) 및 비도핑된 비정질실리콘층(4)에 인가되는 식각 데미지를 막아주기 때문에, 상기 도핑된 비정질실리콘층(5)과 비도핑된 비정질실리콘층(4)의 손상은 일어나지 않는다.Next, as shown in FIG. 1B, using the photoresist pattern as an etching mask, the exposed molybdenum metal film 7 is etched with a fluorine-based gas, for example, a mixed gas of SF 6 gas and CF 4 gas. Remove At this time, as described above, the titanium metal film 6 prevents the etch damage applied to the doped amorphous silicon layer 5 and the undoped amorphous silicon layer 4 during the etching of the molybdenum metal film 7. As a result, damage of the doped amorphous silicon layer 5 and the undoped amorphous silicon layer 4 does not occur.
이어서, 도 1c에 도시된 바와 같이, 몰리브덴 금속막(7)이 식각되어 노출된 티타늄 금속막(6) 부분을 염소 계열의 가스, 예를들어, HCl, BCl3또는 Cl2가스 중에서 선택되는 하나의 가스를 사용하여 식각·제거한다. 이 결과, 소오스/드레인 전극(10a, 10b)이 형성되며, 아울러, 도핑된 비정질실리콘층(5)의 일부분은 노출된다.Subsequently, as shown in FIG. 1C, the part of the titanium metal film 6 exposed by etching the molybdenum metal film 7 is selected from a chlorine-based gas such as HCl, BCl 3, or Cl 2 gas. Etch and remove with gas. As a result, source / drain electrodes 10a and 10b are formed, and part of the doped amorphous silicon layer 5 is exposed.
그리고나서, 도 1d에 도시된 바와 같이, 노출되어진 도핑된 비정질실리콘층(5) 부분은 불소 계열의 가스, 예를들어, SF6가스 또는 CF4가스 중에서 선택되는 하나의 가스로 식각·제거된다. 이때, 식각 공정은 과도 식각으로 수행되며, 이에 따라, 비도핑된 비정질실리콘층의 일부 두께도 함께 식각·제거되고, 이 결과로, 오믹층(5a) 및 BCE 구조의 반도체층(4a)이 얻어지며, 전체적으로는 TFT가 완성된다.Then, as shown in FIG. 1D, the exposed doped amorphous silicon layer 5 portion is etched and removed with a gas selected from a fluorine-based gas such as SF 6 gas or CF 4 gas. . At this time, the etching process is performed by excessive etching, and thus, a part of the thickness of the undoped amorphous silicon layer is also etched and removed. As a result, the ohmic layer 5a and the BCE structure semiconductor layer 4a are obtained. Overall, the TFT is completed.
이후, 도시하지는 않았으나, 상기 결과물의 상부에 보호막을 도포하고, 이어서, 상기 보호막에 TFT의 소오스 전극을 노출시키는 콘택홀을 형성한 후, 마지막으로, ITO 공정을 수행하여 상기 보호막 상에 소오스 전극과 콘택하는 화소전극을 형성한다.Subsequently, although not shown, a protective film is coated on the resultant, and then a contact hole for exposing the source electrode of the TFT is formed in the protective film, and finally, an ITO process is performed to perform a source electrode on the protective film. A pixel electrode to contact is formed.
한편, 전술한 본 발명의 실시예에서, 몰리브덴 금속막에 대한 식각 공정과, 티타늄 금속막에 대한 식각 공정 및 상기 도핑된 비정질실리콘층과 비도핑된 비정질실리콘층에 대한 식각 공정은 인-시튜(In-Situ) 방식으로 수행할 수 있다.Meanwhile, in the above-described embodiment of the present invention, the etching process for the molybdenum metal film, the etching process for the titanium metal film, and the etching process for the doped amorphous silicon layer and the undoped amorphous silicon layer are in-situ ( In-Situ) can be performed.
즉, 종래에는 반도체층의 식각 균일성 확보 측면에서, 몰리브덴 금속막과 도핑된 비정질실리콘층 및 비도핑된 비정질실리콘층에 대한 식각 공정을 인-시튜 방식으로 수행할 수 없다. 그러나, 본 발명의 경우에는 티타늄 금속막이 몰리브덴 금속막의 식각시에 상기 도핑된 비정질실리콘층과 비도핑된 비정질실리콘층에 데미지가 인가되는 것을 방지하기 때문에 반도체층의 식각 균일성을 확보할 수 있고, 아울러, 식각 공정을 3단계에 걸쳐 수행하기 때문에, 상기한 식각 공정들을 인-시튜 방식으로 수행할 수 있게 된다.That is, conventionally, in terms of ensuring the etching uniformity of the semiconductor layer, the etching process for the molybdenum metal film, the doped amorphous silicon layer, and the undoped amorphous silicon layer cannot be performed in-situ. However, in the present invention, since the titanium metal film prevents damage from being applied to the doped amorphous silicon layer and the undoped amorphous silicon layer during the etching of the molybdenum metal film, the etching uniformity of the semiconductor layer can be ensured. In addition, since the etching process is performed in three steps, the above etching processes can be performed in-situ.
이상에서와 같이, 본 발명은 티타늄 금속막과 몰리브덴 금속막을 데이터 라인용 금속막으로 이용하기 때문에, ITO 에천트에 의해 데이터 라인의 손상을 방지할 수 있다.As described above, in the present invention, since the titanium metal film and the molybdenum metal film are used as the data line metal film, damage to the data line can be prevented by the ITO etchant.
또한, 티타늄 금속막이 몰리브덴 금속막의 식각시에 식각 데미지에 대한 블로킹층으로 작용하기 때문에, 반도체층의 식각 균일성을 확보할 수 있고, 이에 따라, TFT 특성을 향상시킬 수 있다.In addition, since the titanium metal film acts as a blocking layer for etching damage during the etching of the molybdenum metal film, the etching uniformity of the semiconductor layer can be ensured, thereby improving the TFT characteristics.
게다가, 데이터 라인용 금속막의 식각 공정과 오믹층 및 반도체층에 대한 식각 공정을 인-시튜 방식으로 수행할 수 있기 때문에, 공정 시간의 단축 효과를 얻을 수 있다.In addition, since the etching process of the metal film for data line and the etching process for the ohmic layer and the semiconductor layer can be performed in-situ, the process time can be shortened.
한편, 여기에서는 본 발명의 특정 실시예에 대하여 설명하고 도시하였지만, 당업자에 의하여 이에 대한 수정과 변형을 할 수 있다. 따라서, 이하, 특허청구의 범위는 본 발명의 진정한 사상과 범위에 속하는 한 모든 수정과 변형을 포함하는 것으로 이해할 수 있다.Meanwhile, although specific embodiments of the present invention have been described and illustrated, modifications and variations can be made by those skilled in the art. Accordingly, the following claims are to be understood as including all modifications and variations as long as they fall within the true spirit and scope of the present invention.
Claims (6)