KR20000067314A - Waterproof bag-material constitute structure fretwork and manufacturing process thereof - Google Patents

Waterproof bag-material constitute structure fretwork and manufacturing process thereof Download PDF

Info

Publication number
KR20000067314A
KR20000067314A KR1019990015034A KR19990015034A KR20000067314A KR 20000067314 A KR20000067314 A KR 20000067314A KR 1019990015034 A KR1019990015034 A KR 1019990015034A KR 19990015034 A KR19990015034 A KR 19990015034A KR 20000067314 A KR20000067314 A KR 20000067314A
Authority
KR
South Korea
Prior art keywords
lattice
paper
bag
product
sponge
Prior art date
Application number
KR1019990015034A
Other languages
Korean (ko)
Inventor
심명호
Original Assignee
심명호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 심명호 filed Critical 심명호
Priority to KR1019990015034A priority Critical patent/KR20000067314A/en
Publication of KR20000067314A publication Critical patent/KR20000067314A/en

Abstract

PURPOSE: A waterproof skin of bag comprising latticed structure woven in the shape of a mat using polypropylene resin and maintaining the grid structure without deformation is provided. CONSTITUTION: A waterproof skin of bag comprising latticed structure comprises a latticed woven skin which is stitched with a thread and to which a sponge layer(2) and a cloth(3) are deposited on the backside to prevent the deformation of the grid. The waterproof skin is prepared by a method comprising weaving polypropylene resin in the latticed shape to obtain a woven skin; stitching the woven skin in the latticed shape to obtain a first product; uniting the first product with a sponge to obtain a second product; and attaching a nylon cloth to the backside of the second product.

Description

격자 구조로 이루어진 방수 가방지 및 그 제조방법{Waterproof bag-material constitute structure fretwork and manufacturing process thereof}Waterproof bag-material constitute structure fretwork and manufacturing process

본 발명은 골프백이나 가방, 또는 쇼핑백 등과 같은 물품의 외표면에 사용하는 격자 구조로 이루어진 방수 가방지에 관한 것으로, 보다 상세하게는 폴리프로필렌수지를 사용하여 격자상태로 직조한 다음 이들이 서로 흩틀어 지지 않도록 박음질을 하고 그 이면에 아트론 재질의 스펀지를 융착하여 물이 스며들지 않도록 구성된 격자 구조로 이루어진 방수 가방지에 관한 것이다.The present invention relates to a waterproof bag made of a lattice structure for use on the outer surface of an article such as a golf bag, a bag, or a shopping bag, and more particularly, woven in a lattice state using polypropylene resin, and then they are scattered with each other. The present invention relates to a waterproof bag made of a lattice structure configured to be sewn so as to be sewn on the back side thereof, and a sponge made of an atron material to be fused to prevent water from seeping.

일반적으로 골프백이나 가방 등은 내피와 외피로 구성되어 있다.In general, golf bags and bags are composed of the inner and outer shells.

내피는 주로 천이나 쿠션부재로 구성되는 것이 일반적이며 외피는 각종무늬가 표현된 재료를 사용하고 있다.The inner skin is generally composed of cloth or cushion member, and the outer skin is made of a material in which various patterns are expressed.

또한 업계의 통례상 가방지라함은 외피를 말하고 있으며, 현재 사용되고 있는 외피는 인조피혁이나 피혁지를 사용하여 그 표면에 무늬를 형성하는 구조로 이루어져 있다.In addition, in the industry, the bag means the outer shell, and the outer shell currently used is made of artificial leather or leather paper to form a pattern on its surface.

그러나 이와 같은 디자인은 입체감이 없으며 여름철과 같은 계절에는 답답하다는 느낌을 갖게되는 폐단이 있다.However, such a design does not have a three-dimensional feeling, and there is a feeling of being stuffy in seasons such as summer.

이와 같은 폐단을 방지하기 위해서 폴리프로필렌 수지를 사용하여 격자상태로 직조한 돗자리를 가방지로 사용된 바 있는 이와 같은 경우 우천시에는 비가 가방 내로 스며들어오게 되는 폐단과 격자상태로 직조한 수지가 밀리어 그 형태가 변형되는 등의 폐단이 있는 것이다.In order to prevent such closed ends, a mat made of polypropylene resin is used as a bag. In such a case, in the rain, the closed end and the lattice-woven resin are milled with rain. There is a closed end, such as deformed form.

본 발명은 상기의 결함중 폴리프로필렌 수지를 사용하여 격자 구조로 이루어진 방수 가방지가 방수가 될 수 있도록 함과 아울러 격자 무늬가 형태를 유지할 수 있도록 하는 격자 구조로 이루어진 방수 가방지및 그 제조방법을 제공하고자 개발한 것이다.The present invention provides a waterproof bag made of a lattice structure and a method of manufacturing the lattice structure to maintain the shape of the lattice structure to the waterproof bag made of a lattice structure using the polypropylene resin of the above defects. It was developed to.

상기 목적을 달성하기 위한 수단으로 폴리프로필렌수지로 이루어지는 통상의 격자 형태의 가방지에 있어서 그 격자무늬의 사이사이를 박음질하여 고정한 다음 이면에 아트론 재질의 스펀지를 열 융착하여 융착된 스펀지에 의해 방수 되도록 한 것이다.As a means for achieving the above object, in a conventional lattice-shaped bag made of polypropylene resin, it is sewn between the lattices to be fixed, and then heat-sealed a sponge of artron on the back thereof to be waterproofed by a fused sponge. will be.

도1은 본 발명의 제조공정을 설명하기 위한 설명도.1 is an explanatory diagram for explaining a manufacturing process of the present invention.

도2는 본 발명 가방지의 사시도.Figure 2 is a perspective view of the bag of the present invention.

도3은 본 발명 가방지의 표면도.Figure 3 is a surface view of the bag of the present invention.

도4는 본 발명의 가방지가 적용된 제품을 보인 사시도 이다.4 is a perspective view showing a product to which the bag of the present invention is applied.

＜도면의 주요부분에 대한 부호의 설명＞<Description of the code | symbol about the principal part of drawing>

1 : 격자형태지 2 : 스펀지층1: lattice-shaped paper 2: sponge layer

3 : 천 4 : 실3: cloth 4: thread

이하 본 발명을 첨부된 도면에 따라 상세히 설명하고자 한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

도1은 본 발명의 제조공정을 설명하기 위한 설명도이고 도2는 본 발명 가방지의 사시도. 도3는 본 발명 가방지의 표면도. 그리고 도4는 본 발명의 가방지가 적용된 제품을 보인 사시도로서,1 is an explanatory view for explaining the manufacturing process of the present invention and Figure 2 is a perspective view of the bag of the present invention. Figure 3 is a surface view of the bag of the present invention. And Figure 4 is a perspective view showing a product to which the bag of the present invention is applied,

본 발명은 격자형태지(1)와 스펀지층(2)그리고 천(3)으로 구성되어 있다.The present invention consists of a lattice paper 1, a sponge layer 2 and a cloth 3.

또한 격자형태지(1)에는 실(4)로 박음질하여 격자형태지가 흩틀어지는 것을 방지하도록 구성된 것이다.In addition, the lattice paper 1 is configured to be sewn into the thread 4 to prevent the lattice paper from being scattered.

이와 같이 구성되는 본 발명에서 스펀지는 열을 가한 후 압착하여 격자형태지와 융착한 것으로 박음질에 의해 격자 형태지가 그 형태를 유지하지만 스펀지에 의해서도 격자형태지가 그 형태를 유지할 수도 있는 것이다.In the present invention constituted as described above, the sponge is fused with the lattice paper by applying heat, and the lattice paper is maintained by the stitching, but the lattice paper may be maintained by the sponge.

이하 본 발명의 제조방법을 실시예에 의해 설명하면,Hereinafter, the production method of the present invention will be described with reference to Examples.

실시예Example

폴리프로필렌으로 이루어지는 수지로 격자형태로 직조하여 직조지를 제조하는 직조단계와;A weaving step of weaving paper into a lattice with a resin made of polypropylene;

직조단계에 의해 생산된 격자형태지에 박음질을 하여 제조되는 1차제품과:Primary products manufactured by stitching lattice-shaped paper produced by the weaving step:

1차제품과 아트론 재질의 스펀지를 합지하는 합지단계에 의해 생산되는 2차제품과;A secondary product produced by a lamination step of laminating a primary product and a sponge made of artron;

상기 2차제품의 이면에 나일론 계통의 천을 합지하는 2차 합지단게에 의해 완제품을 제조하도록 되어 있다.The finished product is to be manufactured by a secondary lamination step of laminating a nylon-based cloth on the back side of the secondary product.

상기 1차 합지단계에서 합지전 직조지는 1.5㎜정도이고 스펀지는 3㎜,였다.또한 이들을 서로 융착하기 위한 압착 로울러의 압착력은 100㎏이며 열원은 700도였다.In the first lamination step, the weaving paper before the lamination was about 1.5 mm and the sponge was 3 mm. The pressing force of the pressing roller for fusion welding was 100 kg and the heat source was 700 degrees.

압착로울러를 통과한 직조지와 스펀지는 접합되었으며 통과한 후의 직조지는 1.5㎜정도로 변함이 없고, 이에 비하여 스펀지는 1㎜정도로 수축되었다.The weaving paper and the sponge passed through the pressing roller were bonded and the weaving paper after passing did not change to about 1.5 mm, whereas the sponge was shrunk to about 1 mm.

상기 2차 합지단계에서도 1차 합지 단계와 동일한 상태로 합지 하였다.The second lamination step was also laminated in the same state as the first lamination step.

상기와 같이 제조 될 때 본 발명에서 합지하는 온도를 700도로 그리고 압착력은 100㎏으로, 여기서의 압착력은 양로울러 사이를 통과할 때의 압착력을 말한다 또한 온도와 압착력은 여기에 한정되는 것은 아니며 압착력의 증감에 따라 온도 또한 700도에서 ± 50도정도 까지는 변화를 가져올 수 있으며 스펀지의 두께에 따라서도 다소 증감될 수 있는 것으로 본 발명에서의 특징은 격자형태지에 박음질을 하고 그 이면에 스펀지를 접합 구성하여 방수될 수 있도록 함에 그 특징을 두고 있다할 것이다.When manufactured as described above, the lamination temperature in the present invention is 700 degrees and the compressive force is 100 kg, where the compressive force refers to the compressive force when passing between the rollers, and the temperature and the compressive force are not limited thereto. Depending on the increase and decrease, the temperature can also be changed from 700 degrees to ± 50 degrees, and can be slightly increased or decreased depending on the thickness of the sponge. Its features are to make it waterproof.

또한 본 발명에서 스펀폰지에 열을 가하여 격자지에 융착 시켰으나 스펀지에 한정되는것은 아니며, 격자지에 방수층을 형성한 것은 본 발명에 속한다고 보아야 할 것이다.In addition, in the present invention, the sponge is fused to the lattice paper by applying heat to the lattice paper, but the present invention is not limited to the sponge, and a waterproof layer formed on the lattice paper belongs to the present invention.

상기와 같이 제조되는 본 발명 가방지는 형태가 격자형태지로 구성되어 있기 때문에 제품에 적용하였을 경우 돗자리를 제품에 부착한 것과 동일한 효과를 갖을가질 있는 것이며, 비가 오더라도 가방 내에는 빗물이 유입되지 않는 효과가 있는 것이다.The bag according to the present invention manufactured as described above has the same effect as when the mat is attached to the product when it is applied to the product because the form is composed of lattice-shaped paper, and rain does not flow into the bag even when it rains. There is.

또한 격자형태지를 폴리프로필렌으로 구성 하였기 때문에 물로 세척이 가능하게 되는 효과가 있는 것이다.In addition, since the lattice-shaped paper is made of polypropylene, it is possible to wash with water.

Claims (3)

격자형태지(1)로 구성되는 가방지에 있어서, 격자형태지(1)을 실(4)로 박음질하고 그 이면에 스펀지층(2)과 천(3)을 융착하여 격자형태지가 흩틀어지는 것을 방지하도록 구성된 것을 특징으로 하는 격자 구조로 이루어진 방수 가방지.In the bag made of the lattice paper 1, the lattice paper 1 is sewn into the thread 4 and the sponge layer 2 and the cloth 3 are fused on the back side thereof to prevent the lattice paper from being scattered. Waterproof bag made of a lattice structure, characterized in that configured to. 폴리프로필렌으로 이루어지는 수지로 격자형태로 직조하여 직조지를 제조하는 직조단계와;A weaving step of weaving paper into a lattice with a resin made of polypropylene; 직조단계에 의해 생산된 격자형태지에 박음질을 하여 제조되는 1차제품과:Primary products manufactured by stitching lattice-shaped paper produced by the weaving step: 1차제품과 아트론 재질의 스펀지를 합지하는 합지단계에 의해 생산되는 2차제품과;A secondary product produced by a lamination step of laminating a primary product and a sponge made of artron; 상기 2차제품의 이면에 나일론 계통의 천을 합지하는 2차 합지단계에 의해 제조됨을 특징으로 하는 격자 구조로 이루어진 방수 가방지 제조방법.Method for producing a waterproof bag made of a lattice structure characterized in that it is manufactured by a secondary lamination step of laminating a cloth of nylon system on the back of the secondary product. 제2항에 있어서, 상기 1, 2차 합지단계의 온도는 700도 압착력은 100㎏임을 특징으로 하는 격자 구조로 이루어진 방수 가방지 제조방법.The method of claim 2, wherein the temperature of the first and second lamination step is 700 degrees, the compressive force is 100kg waterproof bag manufacturing method characterized in that the grid structure.
KR1019990015034A 1999-04-27 1999-04-27 Waterproof bag-material constitute structure fretwork and manufacturing process thereof KR20000067314A (en)