KR20000047319A - Inkjet hanji(korean paper) composition and preparation method thereof - Google Patents
Inkjet hanji(korean paper) composition and preparation method thereof Download PDFInfo
- Publication number
- KR20000047319A KR20000047319A KR1019980064122A KR19980064122A KR20000047319A KR 20000047319 A KR20000047319 A KR 20000047319A KR 1019980064122 A KR1019980064122 A KR 1019980064122A KR 19980064122 A KR19980064122 A KR 19980064122A KR 20000047319 A KR20000047319 A KR 20000047319A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- inkjet
- paper
- hanji
- fiber
- Prior art date
Abstract
Description
본 발명은 잉크젯 한지 조성물과 그 제조 방법에 관한 것으로서, 더욱 상세하게는 닥 및 삼지닥으로 구성되는 인피 섬유에 천연 미표백 목재 섬유 및 표백 목재 섬유를 특정 혼합비로 배합하고, 초지 과정을 특정화하여 제조함으로써 한지로서의 외관적 특성과 잉크젯 프린트 적용시 인쇄의 기능적 특성이 모두 우수하게 되도록 개선시킨 잉크젯 한지 조성물과 그 제조 방법에 관한 것이다.The present invention relates to an inkjet Hanji composition and a method for producing the same, and more particularly, natural unbleached wood fibers and bleached wood fibers are formulated into bast fibers composed of Doc and Samjidak at specific mixing ratios, and the papermaking process is specified. The present invention relates to an inkjet paper composition and a method for producing the same, which are improved so that both the appearance characteristics as Korean paper and the functional properties of printing in the inkjet print application are excellent.
최근 잉크젯 프린터 시장의 급격한 성장과 사무용지의 팬시화, 다양화 요구에 부응하여 '잉크젯 (전)용지’뿐만 아니라, 잉크젯 프린트가 가능한 봉투, 엽서, 명함 및 라벨 등의 각종 무늬지와 색지의 시장이 빠르게 형성되어 가고 있다. 그러나, 상기 무늬지와 색지 등의 수입 고급 지종은 현재 다양한 제품이 출시되어 있는 반면, 한국인의 전통지인 '한지’를 적용 또는 응용한 제품은 전무한 실정이다.In order to meet the recent rapid growth of the inkjet printer market and the demand for the diversification and diversification of office paper, the market for not only 'ink-jet paper' but also various types of paper and color paper such as envelopes, postcards, business cards and labels that can be inkjet printed This is forming rapidly. However, the imported high-quality paper, such as pattern paper and colored paper, while a variety of products are currently being released, there is no product applied or applied to the traditional Korean paper 'hanji'.
종래의 잉크젯 용지는 코팅 방식을 적용하여 잉크젯 적성을 부여함으로써 종이 표면의 섬유 질감을 표현할 수 없었고, 또한 종래의 기계 한지는 수입 닥과 목재 펄프를 주원료로 사용함으로써 잉크젯 적성이 부족함은 물론 고급스런 한지풍의 외양을 갖지 못하였다.Conventional inkjet paper could not express the fiber texture of the paper surface by applying the coating method and impart inkjet aptitude. Also, the traditional Korean paper used the imported paper and wood pulp as the main raw material, which lacks the inkjet aptitude, It has no appearance.
이와 같이, 종래의 잉크젯 용지는 그 외고나상으로 나타나는 미감이나 다양함이 부족하였으므로 이러한 고급스런 잉크젯 용지를 개발할 필요가 있었으며, 이와 더불어 잉크젯 프린트 적용시 프린트 기능상의 특성에서도 뒤지지 않는 새로운 차원의 용지 개발이 요구되고 있는 실정이다.As such, the conventional inkjet paper lacked the aesthetics and variety that appear in the outer image or image. Therefore, it was necessary to develop such a high-quality inkjet paper. It is a required situation.
따라서, 본 발명자들은 우리 전통 한지는 그 외관상의 우아함과 섬유 질감을 가지고 있으며 다양한 느낌을 줄 수 있다는 점에 착안하여 한지와 같은 외관적 특성을 가지면서 잉크젯 프린트 적용시의 기능적 특성도 우수한 새로운 잉크젯 한지를 제조하고자 오랜 연구 끝에 특정의 섬유 조성을 통하여 본 발명을 완성하였다.Therefore, the present inventors have focused on the fact that our traditional Korean paper has the appearance of elegance and textile texture and can give a variety of feelings. After a long research to manufacture the present invention was completed through a specific fiber composition.
이에 본 발명에서는 상기 한지의 주원료인 인피 섬유에 천연 미표백 목재 섬유와 표백 목재 섬유를 특정 혼합비로 배합하고, 초지 과정을 특정화함으로써 한지의 외관적 특성과 잉크젯의 기능적 특성을 모두 겸비한 잉크젯 한지 조성물과 그 제조 방법을 제공하는데 그 목적이 있다.Therefore, in the present invention, by mixing the natural unbleached wood fibers and bleached wood fibers in a specific ratio of the bast fiber, the main raw material of the hanji, by specifying the papermaking process, the inkjet Hanji composition that combines both the appearance characteristics and the functional characteristics of the inkjet and The object is to provide a method for producing the same.
본 발명은 잉크젯 적성을 갖는 용지에 있어서,The present invention provides a paper having inkjet aptitude,
닥 및 삼지닥으로 구성된 인피 섬유 10 ∼ 30 중량%, 천연 미표백 목재 섬유 20 ∼ 40 중량% 및 표백 목재 섬유 30 ∼ 50 중량%로 구성되는 주원료 90 ∼ 95 중량%와 염료 및 지력 증강제를 포함하는 통상의 부원료 5 ∼ 10 중량%로 이루어진 것을 그 특징으로 한다.10 to 30% by weight of bast fiber consisting of Doc and Samjidak, 20 to 40% by weight of natural unbleached wood fiber, and 90 to 95% by weight of main raw material consisting of 30 to 50% by weight of bleached wood fiber, and a dye and a strength enhancer It is characterized by consisting of 5 to 10% by weight of ordinary secondary raw materials.
또한, 본 발명은 상기 잉크젯 용지를 제조하는 방법에 있어서,In addition, the present invention is a method of manufacturing the inkjet paper,
상기의 조성으로 원료를 구성하고;A raw material is constituted by the above composition;
상기 원료로부터 다층 환망 초지기를 사용하여 상층(TOP층)과 하층(BOTTOM층)으로 구성되는 습지를 제조한 후;Manufacturing a wetland consisting of an upper layer (TOP layer) and a lower layer (BOTTOM layer) using a multilayer ring network paper machine from the raw material;
상기 습지의 건조 과정 진입부의 선압을 5 ∼ 20kg/m로 하여 지필의 수분이 10 ∼50%가 되도록 잉크젯 한지를 제조하는 방법을 포함한다.And a method of manufacturing ink jet paper so that the moisture of the paper-based paper becomes 10 to 50% by setting the linear pressure of the wetland drying process entry portion to 5 to 20 kg / m.
이와 같은 본 발명을 더욱 상세하게 설명하면 다음과 같다.The present invention will be described in more detail as follows.
본 발명은 닥 및 삼지닥으로 구성된 인피 섬유, 천연 미표백 목재 섬유 및 표백 목재 섬유를 특정 혼합비로 배합하여 주원료를 제조하고, 통상의 부원료를 첨가한 후 초지 과정을 특정화 함으로써 한지의 외관적 특성과 잉크젯의 기능적 특성을 모두 겸비한 잉크젯 한지에 그 특징이 있다.The present invention is to prepare the main raw material by mixing the bast fiber consisting of Doc and Samjidak, natural unbleached wood fibers and bleached wood fibers in a specific mixing ratio, and after adding the usual secondary raw materials to the appearance characteristics of Hanji It is characterized by inkjet Hanji, which combines all the functional characteristics of the inkjet.
본 발명의 잉크젯 한지는 닥 및 삼지닥으로 구성된 인피 섬유 10 ∼ 30 중량%, 천연 미표백 목재 섬유 20 ∼ 40 중량% 및 표백 목재 섬유 30 ∼ 50 중량%로 주원료 90 ∼ 95 중량%를 구성하는 것이 바람직하다. 또한, 여기에 통상의 부원료로서 염료, 지력 증강제 등의 부원료를 5 ∼ 10 중량%로 사용하여 한지 조성물을 구성한다.The inkjet Hanji of the present invention preferably comprises 90 to 95% by weight of the main raw material of 10 to 30% by weight of the bast fiber consisting of Doc and Samdak, 20 to 40% by weight of natural unbleached wood fibers and 30 to 50% by weight of bleached wood fibers. Do. In addition, as an ordinary sub raw material, 5-10 weight% of sub raw materials, such as dye and an oil power enhancer, are used for a Hanji composition.
본 발명에서 사용되는 상기 인피 섬유는 닥과 삼지닥의 혼합재로 구성된 것으로서, 상기 삼지닥은 섬유 길이가 0.5㎝ 내외로 상기 닥의 섬유 길이인 1 ㎝에 비해 섬유 길이가 짧고 흡습성이 큰 성질을 가지고 있으며, 바람직하기로는 닥과 더불어서 상기 삼지닥을 인피 섬유에 혼합 사용함으로써 잉크의 흡습성과 표면 평활도를 크게 개선할 수 있다.The bast fiber used in the present invention is composed of a mixture of Doc and Samjidak, the Samjidak has a shorter fiber length and greater hygroscopicity than the fiber length of 1 ㎝ with a fiber length of about 0.5cm In addition, the hygroscopicity and surface smoothness of the ink can be greatly improved by mixing and using the trichassium to the bast fiber together with the Doc.
본 발명에서는 상기 삼지닥이 전체 인피 섬유 중에서 20 ∼ 60 중량%의 함량으로 함유되어 있는 것이 바람직한데, 만일 상기 삼지닥의 함량이 상기 범위를 벗어나면 잉크의 번짐이 심해지고 잉크의 광학밀도(optical-density)가 감소하는 등의 문제가 발생하여 바람직하지 않다.In the present invention, it is preferable that the triad is contained in an amount of 20 to 60% by weight in the whole bast fiber. If the content of the triad is out of the range, the ink bleeding is increased and the optical density of the ink -density) decreases, which is not preferable.
본 발명에서는 상기 인피 섬유를 주원료에 대하여 10 ∼ 30 중량부로 사용하는데, 만일 상기 인피 섬유의 함량이 상기 범위 보다 적으면 한지의 특성이 발현되지 아니하고, 너무 과량이면 생산비가 상승하여 원가가 상승하는 문제가 있어 바람직하지 않다.In the present invention, the bast fiber is used in 10 to 30 parts by weight with respect to the main raw material, if the content of the bast fiber is less than the range does not express the characteristics of the hanji, if too much production cost rises the problem of rising cost It is not desirable to have.
또한, 상기 천연 미표백 목재 섬유는 본 발명에 따른 잉크젯 한지의 자연적인 한지풍을 구현하기 위하여 사용되는 원료로서, 본 발명에서는 상기 목재 섬유의 고해를 칼비터를 사용한 컷팅보다는 날 간격이 촘촘한 고해기를 사용하여 상기 목재 섬유의 피브릴화가 보다 충분히 될 수 있도록 하였다.In addition, the natural unbleached wood fiber is a raw material used to implement a natural Hanji wind of the inkjet Hanji according to the present invention, in the present invention, the pulverization of the finer than the cutting of the wood fiber using a knife beater To make the fibrillation of the wood fibers more sufficient.
본 발명에서는 상기 천연 미표백 목재 섬유와 상기 표백 목재 섬유를 주원료 에 대하여 각각 20 ∼ 40 중량% 및 30 ∼ 50 중량%로 사용하는데, 만일 상기 천연 미표백 목재 섬유가 과량이고 표백 목재 섬유의 함량이 소량이면 한지 특성의 부여 효과가 좋아 닥나무 고유의 색상을 표현하는 효과는 좋으나, 흡습성이 저하되어 번짐이 심해지는 등 잉크 인쇄 적성이 떨어지는 문제가 있다.In the present invention, the natural unbleached wood fibers and the bleached wood fibers are used at 20 to 40% by weight and 30 to 50% by weight, respectively, based on the main raw materials. If the amount is small, the effect of imparting the characteristics of Hanji is good, and the effect of expressing the unique color of the mulberry is good.
또한, 본 발명에서는 상기 주원료 이외에 통상적으로 사용되는 염료, 지력 증강제 등의 부원료를 전체 조성중 5 ∼ 10 중량%로 사용하는데, 상기 염료로는 예컨데 제지 산업에서 일반적으로 사용되는 색상 염료가 사용될 수 있고, 지력 증강제는 PAM(poly acryl methacrylate) 계열이 사용될 수 있다.In addition, the present invention is used in addition to the main raw materials, such as dyes, strength enhancers, and other commonly used materials in 5 to 10% by weight of the total composition, the dye may be used, for example, color dyes generally used in the paper industry, The strength enhancer may be a poly acryl methacrylate (PAM) series.
이와 같은 본 발명을 제조 방법에 의거하여 상세히 설명하면 다음과 같다.The present invention will be described in detail based on the manufacturing method as follows.
우선, 상기의 조성으로 원료를 제조한다.First, a raw material is manufactured by said composition.
이 과정에서 상기 천연 미표백 목재 섬유 및 표백 목재 섬유의 여수도를 200 ∼ 400 ㎖CSF으로 조절함으로써 닥섬유와 유사한 외관을 갖도록 하는 효과에 의해 본 발명의 잉크젯 한지가 자연적인 한지풍의 특성을 갖게 되도록 한다.In this process, by adjusting the degree of freedom of the natural unbleached wood fibers and bleached wood fibers to 200-400 ml CSF, the inkjet Hanji of the present invention has the characteristics of natural Korean paper wind by the effect of having a similar appearance to Doc fiber. .
상기 원료로부터 다층 환망 초지기를 사용하여 상층(TOP층)과 하층(BOTTOM층)으로 구성되는 습지를 제조한다.A wetland composed of an upper layer (TOP layer) and a lower layer (BOTTOM layer) is prepared from the raw material using a multilayer ring paper machine.
상기 상층에는 본 발명의 배합비를 적용하여 잉크젯 적성과 한지의 특성을 부여하고, 상기 하층에는 상기 상층과 동일한 색상의 느낌을 갖도록 색상만을 기준으로 하여 배합비를 적용하였다. 이때, 상층 및 하층의 평량은 일반적으로 잉크젯 전용지에서 적용되는 총평량 70 ∼ 90 g/㎡의 범위내에서 임의적으로 조절할 수 있다.The blending ratio of the present invention is applied to the upper layer to impart inkjet aptitude and characteristics of Hanji, and the blending ratio is applied to the lower layer on the basis of color only to have a feeling of the same color as the upper layer. In this case, the basis weight of the upper layer and the lower layer can be arbitrarily adjusted within the range of 70 to 90 g / m 2, which is generally applied in inkjet paper.
상기 습지의 건조 과정 진입부의 선압을 5 ∼ 20kg/m로 하여 지필의 수분이10 ∼ 50%인 잉크젯 한지를 제조하는 것이 표면 밀도와 평활도 등의 종이 면성과 잉크 인쇄 적성을 갖는데 있어서 바람직하다.It is preferable to produce inkjet paper with a water pressure of 10 to 50% with a line pressure of 5 to 20 kg / m in the drying process entry portion of the wetland in order to have paper surface properties such as surface density and smoothness and ink printability.
본 발명에서는 섬유 배합비 이외에 초지 과정에서 습지의 건조 과정 진입부의 선압을 상기 범위로 조절함으로써 잉크젯 적성과 면성을 유지할 수 있는데, 만일 상기 건조 과정 진입부의 선압이 5kg/m 미만이면 밀도가 너무 낮아져서 잉크가 종이 표면에 머무르기 보다 흡수되므로 광학 밀도가 적정 수준 이하로 낮아지며, 상기 건조 과정 진입부의 선압이 20kg/m를 초과하면 평활도는 향상되어 면성이 좋아지나, 밀도가 높아지고 투기도가 낮아져 잉크가 종이 속으로 흡수되는 속도가 느려지고 표면에서 머무르는 시간이 많아지므로 잉크 번짐이 심해지는 문제가 있어 바람직하지 않다,In the present invention, it is possible to maintain the inkjet aptitude and surface area by adjusting the linear pressure of the entry process of the wetland drying process in the above range in addition to the fiber blending ratio, if the linear pressure of the entry process of the drying process is less than 5kg / m is too low density ink Absorption rather than staying on the surface of the paper, the optical density is lower than the appropriate level, when the linear pressure of the entry portion exceeds 20kg / m smoothness is improved to improve the surface area, but the density is higher and the air permeability is lowered, the ink into the paper Since the speed of absorption is slowed down and the time to stay on the surface increases, there is a problem that the ink bleeding is severe, which is not preferable.
본 발명에서는 상기 지필이 10 ∼ 50%의 수분을 함유하는 것이 바람직한데,만일 수분의 함량이 상기 범위를 벗어나면 건조 과정에서 주름이 발생하는 문제가 있어 바람직하지 않다. 또한, 본 발명에서는 상기 과정중 다양한 무늬의 펠트를 사용하여 잉크젯 한지의 표면에 다양한 무늬를 넣을 수도 있다.In the present invention, it is preferable that the paper-based paper contains 10 to 50% of water. If the water content is out of the above range, wrinkles occur during the drying process, which is not preferable. In addition, in the present invention, various patterns may be put on the surface of the inkjet Hanji using various patterns of felt during the process.
상기한 바와 같이, 본 발명에 따른 조성과 방법으로 제조된 잉크젯 한지는 한지의 외관적 특성과 잉크젯의 기능적 특성을 모두 겸비한 것으로서 잉크젯용 이외에도 인쇄용, 사진 인화지용 등 다양한 용도로 활용할 수 있다.As described above, the inkjet Hanji prepared by the composition and method according to the present invention combines both the appearance characteristics of the Korean paper and the functional properties of the inkjet, and can be used for various purposes such as printing, photo paper, and the like.
이와 같은 본 발명을 실시예에 의거하여 상세히 설명하면 다음과 같은 바, 본 발명이 실시예에 한정되는 것은 아니다.If the present invention will be described in detail based on the embodiment as follows, the present invention is not limited to the embodiment.
실시예Example
닥과 삼지닥은 칼비터로 고해하여 투입하고, 미표백 목재 섬유와 표백 목재 섬유는 날이 촘촘한 고해기를 사용하여 여수도 350 ㎖CSF로 고해한 후 투입하였다. 상층의 평량을 20g/㎡으로 하층의 평량을 65g/㎡으로 조절하고 환망 다층 초지기를 사용하여 85g/㎡의 단면을 갖는 잉크젯 한지를 제조하였으며, 이때 습지의 건조 과정 진입부의 선압을 15kg/m로 하여 최종 밀도를 0.6g/㎤로 하였다.The Doc and Samjidak were added by confession with Kalbiter, and the unbleached wood fiber and bleached wood fiber were added after beating at 350 ml CSF in Yeosu Island using a fine blasting machine. The basis weight of the upper layer was adjusted to 20 g / m 2, and the basis weight of the lower layer was adjusted to 65 g / m 2, and an inkjet paper was prepared having a cross section of 85 g / m 2 using a circular network multi-layer paper machine. The final density was 0.6 g / cm 3.
[조성][Furtherance]
1. 상층1. Upper floor
닥 5 중량%Doc 5 wt%
삼지닥 10 중량%Sanjidak 10 wt%
미표백 목재 섬유 30 중량%30% by weight of unbleached wood fibers
표백 목재 섬유 50 중량%50% by weight of bleached wood fibers
분산제/지력중강제 5 중량%Dispersant / Intellectual Strength 5% by weight
2. 하층2. Lower Tier
미표백 목재 섬유 40 중량%40% by weight of unbleached wood fibers
표백 목재 섬유 50 중량%50% by weight of bleached wood fibers
분산제/지력중강제 10 중량%Dispersant / Intellectual Strength 10% by weight
비교예 1Comparative Example 1
닥은 칼비터로 고해하여 투입하고, 미표백 목재 섬유와 표백 목재섬유는 날이 촘촘한 고해기를 사용하여 여수도 500 ㎖CSF로 고해한 후 투입하였다. 상층의 평량을 20g/㎡으로 하층의 평량을 65g/㎡으로 조절하고 다층 환망 초지기를 사용하여 85g/㎡의 단면을 갖는 잉크젯 한지를 제조하였으며, 이때 습지의 건조 과정 진입부의 선압을 15kg/m로 하여 최종 밀도를 0.6g/㎤로 하였다.Doc was added by confession with a calbiter, and unbleached wood fibers and bleached wood fibers were added after beating at 500 ml CSF in Yeosu Island using a fine blasting machine. The basis weight of the upper layer was adjusted to 20 g / m 2, and the basis weight of the lower layer was adjusted to 65 g / m 2, and an inkjet paper was prepared having a cross section of 85 g / m 2 using a multi-layer circular paper machine. The final density was 0.6 g / cm 3.
[조성][Furtherance]
1. 상층1. Upper floor
닥 10 중량%Doc 10 wt%
미표백 목재 섬유 30 중량%30% by weight of unbleached wood fibers
표백 목재 섬유 55 중량%Bleached Wood Fiber 55% by weight
분산제/지력중강제 5 중량%Dispersant / Intellectual Strength 5% by weight
2. 하층2. Lower Tier
미표백 목재 섬유 40 중량%40% by weight of unbleached wood fibers
표백 목재 섬유 50 중량%50% by weight of bleached wood fibers
분산제/지력중강제 10 중량%Dispersant / Intellectual Strength 10% by weight
비교예 2Comparative Example 2
닥은 칼비터로 고해하여 투입하고, 미표백 목재 섬유와 표백 목재섬유는 날이 촘촘한 고해기를 사용하여 여수도 350 ㎖CSF로 고해한 후 투입하였다. 상층의 평량을 20g/㎡으로 하층의 평량을 65g/㎡으로 조절하고 다층 환망 초지기를 사용하여 85g/㎡의 단면을 갖는 잉크젯 한지를 제조하였으며, 이때 습지의 건조 과정 진입부의 선압을 1kg/m로 하여 최종 밀도를 0.45g/㎤로 하였다.Doc was added by confession with a calbiter, and unbleached wood fibers and bleached wood fibers were added after beating at 350 ml CSF in Yeosu Island using a fine blasting machine. The basis weight of the upper layer was adjusted to 20 g / m 2, and the basis weight of the lower layer was adjusted to 65 g / m 2, and an inkjet paper was prepared having a cross section of 85 g / m 2 using a multi-layered paper machine. The final density was 0.45 g / cm 3.
[조성][Furtherance]
1. 상층1. Upper floor
닥 10 중량%Doc 10 wt%
미표백 목재 섬유 30 중량%30% by weight of unbleached wood fibers
표백 목재 섬유 55 중량%Bleached Wood Fiber 55% by weight
분산제/지력중강제 5 중량%Dispersant / Intellectual Strength 5% by weight
2. 하층2. Lower Tier
미표백 목재 섬유 40 중량%40% by weight of unbleached wood fibers
표백 목재 섬유 50 중량%50% by weight of bleached wood fibers
분산제/지력중강제 10 중량%Dispersant / Intellectual Strength 10% by weight
실험예Experimental Example
상기 실시예 및 비교예 1 ∼ 2의 물성을 하기의 방법으로 측정하였고, 그 결과를 표 1에 나타내었다.The physical properties of the Examples and Comparative Examples 1 and 2 were measured by the following method, and the results are shown in Table 1.
[실험 방법][Experimental method]
1. 밀도(g/㎠).1. Density (g / cm 2).
평량(g/㎡)/두께(㎛), 평량, 두께의 측정 방법은 각각 KS M-7013, KS M-7021을 따랐다.The measurement method of basis weight (g / m <2>) / thickness (micrometer), basis weight, and thickness followed KS M-7013 and KS M-7021, respectively.
2. 투기도(㎖/min).2. Air permeability (ml / min).
공기가 종이를 통과하는 정도를 나타내는 것으로, 종이에 걸린 표면과 이면의 압력차에 의하여 통과하는 공기량을 측정한다.The amount of air passing through the paper is measured by measuring the pressure difference between the surface and the back surface of the paper.
3. 평활도(sec).3. Smoothness (sec).
종이 표면의 윤곽 상태를 나타내는 것으로, 일정 시간동안 일정량의 공기가 일정 면적의 측면으로 빠져 나가는데 소요되는 시간을 측정한다. 수치가 클수록 평활도 가 높다.By showing the contour of the paper surface, the time taken for a certain amount of air to escape to the side of a certain area for a certain time is measured. The larger the value, the higher the smoothness.
4. 색상(L, a, b).4. Color (L, a, b).
종이의 색상을 나타내는 것으로, L은 흰색(100)∼검은색(0), a는 빨간색(+100) ∼ 녹색(-100), b는 노란색(+100) ∼ 파란색(-100)을 의미한다.It represents the color of paper, where L means white (100) to black (0), a means red (+100) to green (-100), and b means yellow (+100) to blue (-100). .
5. 광학 밀도(optical-density).5. Optical-density.
색의 밀도(선명도)를 나타내는 것으로, 수치가 클수록 선명하다.It shows the density (sharpness) of the color, and the larger the value, the clearer it is.
6. 번짐.6. Smeared.
잉크 번짐을 의미하며, 육안으로 판정하였다.It means ink bleeding and was visually judged.
상기 표 1에서 알 수 있듯이, 본 발명의 조성과 제법으로 제조한 실시예의 잉크젯 한지가 본 발명의 경우와 다른 조성으로 제조한 비교예 1 ∼ 2의 것보다 각 색상별로 비교할 때 광학 밀도(Optical-Density)가 높고 번짐이 양호하여 잉크젯 적성이 가장 우수하다.As can be seen from Table 1, the inkjet Hanji of the embodiment prepared by the composition of the present invention and the manufacturing method is compared with the case of the present invention and compared with each color than those of Comparative Examples 1-2 prepared with a different composition (Optical- It has high density and good bleeding so it has the best inkjet aptitude.
본 발명의 잉크젯 한지는 잉크젯 적성 뿐만 아니라, 미적 특성을 강조하여 고급스런 한지풍의 외양을 가지므로 종래 기능성 위주의 잉크젯 용지, 잉크젯 고급 지종의 수입 무늬지 및 색지 등과는 차별화되는 제품이다. 또한, 소수의 예술인들과 서예가들에 한정되어 있던 한지의 사용 범위를 크게 확대하여 판화와 같은 예술 작품은 물론 범용적으로 잉크젯용으로 뿐만 아니라, 최근 시장이 확장되고 있는 개인용 컴퓨터를 이용한 전자 출판, 즉 소형 소량의 인쇄물과 고급 선전 인쇄물용 등 다양한 목적으로 활용될 수 있는 효과가 있다.The inkjet Hanji of the present invention is not only inkjet aptitude, but also emphasizes aesthetic characteristics, and thus has the appearance of a high-quality Korean paper, and thus is differentiated from conventional functional inkjet paper, imported pattern paper and color paper of inkjet high-quality paper. In addition, the use of Hanji, which was limited to a small number of artists and calligraphers, has been greatly expanded, and not only for works of art such as prints, but also for inkjets in general, as well as electronic publishing using personal computers, which are expanding in recent years. In other words, there is an effect that can be used for a variety of purposes, such as small prints and high-quality propaganda printed material.
Claims (4)