KR102668674B1 - Antimicrobial and deodorizing compounds using cellulose-containing substances and manufacturing methods thereof - Google Patents
Antimicrobial and deodorizing compounds using cellulose-containing substances and manufacturing methods thereof Download PDFInfo
- Publication number
- KR102668674B1 KR102668674B1 KR1020210032787A KR20210032787A KR102668674B1 KR 102668674 B1 KR102668674 B1 KR 102668674B1 KR 1020210032787 A KR1020210032787 A KR 1020210032787A KR 20210032787 A KR20210032787 A KR 20210032787A KR 102668674 B1 KR102668674 B1 KR 102668674B1
- Authority
- KR
- South Korea
- Prior art keywords
- cellulose
- antibacterial
- deodorizing
- containing material
- compound
- Prior art date
Abstract
본 발명은 하기 일반식 1로 표시되는 화합물을 포함하는 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물 및 그 제조방법에 관한 것이다.
[일반식 1]
이러한 본 발명에 따르면, 비교적 덜 복잡한 공정으로 마스크, 생리대, 여성청결 패드 등 등의 저렴한 물품에 적용 가능하고, 항균성과 탈취성을 동시에 가지고 있어 청결한 마스크, 생리대, 여성청결 패드 등의 사용이 가능하다. The present invention relates to an antibacterial and deodorizing compound using a cellulose-containing material containing a compound represented by the following general formula 1, and a method for producing the same.
[General Formula 1]
According to this invention, it can be applied to inexpensive products such as masks, sanitary napkins, feminine hygiene pads, etc. with a relatively less complicated process, and has antibacterial and deodorizing properties at the same time, so it can be used as clean masks, sanitary napkins, feminine hygiene pads, etc. .
Description
본 발명은 화합물 및 그 제조방법에 관한 것으로, 보다 구체적으로는 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물 및 그 제조방법에 관한 것이다. The present invention relates to a compound and a method for producing the same, and more specifically, to an antibacterial and deodorizing compound using a cellulose-containing material and a method for producing the same.
최근 들어 코로나 사태로 인해 마스크 등의 사용이 급증하고 있다. 마스크는 대부분 1회용이기 때문에 재사용이 어려운 문제가 있어 또 다른 환경문제의 원인으로 지목되고 있다.Recently, the use of masks has increased rapidly due to the coronavirus outbreak. Since most masks are disposable, they are difficult to reuse, which has been pointed out as another cause of environmental problems.
또한, 일반적으로 사용되는 마스크는 항균성이나 탈취성이 없기 때문에 냄새에는 특별한 대책이 없고 그로 인해 재사용이 더 어려운 실정이다.In addition, since commonly used masks do not have antibacterial or deodorizing properties, there are no special measures against odor, making reuse more difficult.
항균성 셀룰로오스 섬유의 제조방법에 관한 특허로 한국등록특허 제1403527호가 개시되어 있다. 하지만, 반응성 항균 화합물을 제조한 후 안정화 처리하는 과정이 너무 복잡하고, 은이 결합된 셀룰로오스 매트릭스의 항균성 면 섬유 제조방법에 관한 특허로 한국공개특허 제2012-0046714호가 개시되어 있으나 역시 제조 공정이 복잡한 문제가 있다.Korean Patent No. 1403527 is disclosed as a patent regarding the manufacturing method of antibacterial cellulose fiber. However, the process of stabilizing the reactive antibacterial compound after manufacturing it is too complicated, and although Korean Patent Publication No. 2012-0046714 is disclosed as a patent on a method of manufacturing antibacterial cotton fiber of a silver-bound cellulose matrix, the manufacturing process is also complicated. There is.
이에 마스크 등의 저렴한 물품에 적용 가능한 항균성 및 탈취성 있는 화합물의 제조방법이 필요한 실정이다. Accordingly, there is a need for a manufacturing method of a compound with antibacterial and deodorizing properties that can be applied to inexpensive products such as masks.
본 발명의 목적은 마스크 등의 저렴한 물품에 적용 가능하도록 비교적 덜 복잡한 공정으로 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물 및 그 제조방법을 제공하는 것이다. The purpose of the present invention is to provide an antibacterial and deodorizing compound using a cellulose-containing material and a method for producing the same through a relatively less complicated process so that it can be applied to inexpensive products such as masks.
위와 같은 목적을 달성하기 위하여, 본 발명의 실시예에 따른 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물은 하기 일반식 1로 표시되는 화합물을 포함한다.In order to achieve the above object, the antibacterial and deodorizing compound using a cellulose-containing material according to an embodiment of the present invention includes a compound represented by the following general formula 1.
[일반식 1][General Formula 1]
또한, 본 발명의 실시예에 따른 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물은 하기 일반식 2로 표시되는 화합물을 포함한다.In addition, antibacterial and deodorizing compounds using cellulose-containing materials according to embodiments of the present invention include compounds represented by the following general formula 2.
[일반식 2][General Formula 2]
또한, 본 발명의 실시예에 따른 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물 제조방법은 셀룰로오스 (C6H10O5)n 함유 물질을 준비하는 단계; 상기 셀룰로오스 (C6H10O5)n 함유 물질을 환원제 용액에 침지하는 단계; 및 상기 셀룰로오스의 (C6H10O5)n 의 H+ 3개를 제거하여 음이온 셀룰로오스 [(C6H7O5)-]n 를 형성하는 단계를 포함한다.In addition, the method for producing an antibacterial and deodorizing compound using a cellulose-containing material according to an embodiment of the present invention includes the steps of preparing a cellulose (C 6 H 10 O 5 ) n- containing material; Immersing the cellulose (C 6 H 10 O 5 ) n- containing material in a reducing agent solution; And removing H + 3 of (C 6 H 10 O 5 ) n of the cellulose to form anionic cellulose [(C 6 H 7 O 5 ) - ] n .
여기서, 상기 환원제는 SnCl2 일 수 있다. Here, the reducing agent may be SnCl 2 .
아울러, 상기 SnCl2 의 농도는 0.01 ~ 0.1 몰일 수 있다.In addition, the concentration of SnCl 2 may be 0.01 to 0.1 mole.
나아가, 상기 환원제 용액에 침지하는 시간은 9 ~ 11초일 수 있다.Furthermore, the immersion time in the reducing agent solution may be 9 to 11 seconds.
게다가, 미반응한 SnCl2 를 제거하기 위하여 침지 후 즉시 세척한 후에 100℃에서 건조시킬 수 있다. In addition, in order to remove unreacted SnCl 2, it can be washed immediately after immersion and then dried at 100°C.
또한, 상기 음이온 셀룰로오스 [(C6H7O5)-]n 를 AgNO3 용액에 침지하는 단계; 및 은 셀룰로오스 [(C6H7O5Ag3)n] 을 형성하는 단계를 포함할 수 있다. Additionally, immersing the anionic cellulose [(C 6 H 7 O 5 ) - ] n in AgNO 3 solution; and may include forming cellulose [(C 6 H 7 O 5 Ag 3 ) n ].
여기서, 상기 AgNO3 의 농도는 0.005 ~ 0.007 몰일 수 있다.Here, the concentration of AgNO 3 may be 0.005 to 0.007 mol.
나아가, 상기 AgNO3 용액에 침지하는 시간은 2 ~ 4초일 수 있다. Furthermore, the immersion time in the AgNO 3 solution may be 2 to 4 seconds.
아울러, 미반응한 AgNO3 를 제거하기 위하여 침지 후 즉시 세척한 후에 100℃에서 건조시킬 수 있다. In addition, in order to remove unreacted AgNO 3 , it can be washed immediately after immersion and then dried at 100°C.
본 발명의 실시예에 따른 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물 및 그 제조방법에 의하면, According to the antibacterial and deodorizing compound using a cellulose-containing material and its manufacturing method according to an embodiment of the present invention,
첫째, 비교적 덜 복잡한 공정으로 마스크, 생리대, 여성청결 패드 등의 저렴한 물품에 적용 가능하고, 항균성과 탈취성을 동시에 가지고 있어 청결한 마스크 등의 사용이 가능하다.First, it is a relatively less complicated process and can be applied to inexpensive items such as masks, sanitary napkins, and feminine hygiene pads. It has antibacterial and deodorizing properties at the same time, so it can be used for clean masks.
둘째, 세척후 마스크, 생리대, 여성청결 패드 등의 재활용이 가능하므로 경제적이고 환경 오염을 줄일 수 있다.Second, since masks, sanitary napkins, feminine hygiene pads, etc. can be recycled after washing, it is economical and reduces environmental pollution.
셋째, 음이온 셀룰로오스 자체만으로도 항균성과 탈취성을 가지고 있고, 은 셀룰로오스는 더 향상된 항균성과 탈취성을 가지고 있다.Third, anionic cellulose itself has antibacterial and deodorizing properties, and silver cellulose has further improved antibacterial and deodorizing properties.
넷째, 셀룰로오스 함유 물질을 환원제에 짧은 시간동안 침지하여 항균성 및 탈취성을 확보하므로 생산 공정이 간편하다. Fourth, the production process is simple because cellulose-containing materials are immersed in a reducing agent for a short period of time to ensure antibacterial and deodorizing properties.
다섯째, 물리적인 세탁시 10회 ~ 100회 정도의 재사용이 가능하다.Fifth, it can be reused about 10 to 100 times when physically washed.
여섯째, 항균성은 99.9%, 탈취성은 37~67%의 효과가 있으며, 체감 탈취 효과는 훨씬 큰 효과가 있다. Sixth, the antibacterial effect is 99.9%, the deodorizing effect is 37-67%, and the perceived deodorizing effect is much greater.
도 1은 본 발명의 실시예에 의해 제조된 셀룰로오스 함유 물질(면, 레이온)을 이용한 항균성 및 탈취성 화합물의 실시예이다.
도 2는 본 발명의 실시예에 의해 제조된 셀룰로오스 함유 물질(셀로판, 종이)을 이용한 항균성 및 탈취성 화합물의 실시예이다.
도 3은 본 발명의 실시예에 따른 항균성 및 탈취성 면섬유로 제직된 면직물에 대한 암모니아 가스의 탈취율 시험을 실시한 시험성적서이다.
도 4는 본 발명의 실시예에 따른 항균성 및 탈취성 면섬유로 제직된 면직물에 대한 항균도 시험을 실시한 시험성적서이다.
도 5 및 도 6은 도 4에 의한 항균성 및 탈취성 면섬유로 제직된 면직물의 박테리아 번식 정도를 보여주는 사진이다.
도 7은 도 3 및 도 4의 시험에 사용된 시료 카드이다.
도 8은 본 발명의 다른 실시예에 따른 항균성 및 탈취성 면섬유로 제직된 면직물에 대한 암모니아 가스의 탈취율 시험을 실시한 시험성적서이다.
도 9는 본 발명의 다른 실시예에 따른 항균성 및 탈취성 면섬유로 제직된 면직물에 대한 항균도 시험을 실시한 시험성적서이다.
도 10 및 도 11은 도 9에 의한 항균성 및 탈취성 면섬유로 제직된 면직물의 박테리아 번식 정도를 보여주는 사진이다.
도 12은 도 8 및 도 9의 시험에 사용된 시료 카드이다. Figure 1 is an example of an antibacterial and deodorizing compound using cellulose-containing materials (cotton, rayon) prepared according to an example of the present invention.
Figure 2 is an example of an antibacterial and deodorizing compound using a cellulose-containing material (cellophane, paper) prepared according to an example of the present invention.
Figure 3 is a test report of a deodorization rate test of ammonia gas on cotton fabric woven with antibacterial and deodorizing cotton fibers according to an embodiment of the present invention.
Figure 4 is a test report of an antibacterial test on cotton fabric woven with antibacterial and deodorizing cotton fibers according to an embodiment of the present invention.
Figures 5 and 6 are photographs showing the degree of bacterial growth in cotton fabrics woven with the antibacterial and deodorizing cotton fibers shown in Figure 4.
Figure 7 is a sample card used in the tests of Figures 3 and 4.
Figure 8 is a test report of a deodorization rate test of ammonia gas on cotton fabric woven with antibacterial and deodorizing cotton fibers according to another embodiment of the present invention.
Figure 9 is a test report of an antibacterial test on a cotton fabric woven with antibacterial and deodorizing cotton fibers according to another embodiment of the present invention.
Figures 10 and 11 are photographs showing the degree of bacterial growth in cotton fabrics woven with antibacterial and deodorizing cotton fibers according to Figure 9.
Figure 12 is a sample card used in the tests of Figures 8 and 9.
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예들을 상세히 설명한다. 이 때, 첨부된 도면에서 동일한 구성 요소는 가능한 동일한 부호로 나타내고 있음에 유의한다. 또한, 본 발명의 요지를 흐리게 할 수 있는 공지 기능 및 구성에 대한 상세한 설명은 생략할 것이다. 마찬가지 이유로 첨부 도면에 있어서 일부 구성요소는 과장되거나 생략되거나 개략적으로 도시되었다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the attached drawings. At this time, note that in the attached drawings, like components are indicated by the same symbols whenever possible. Additionally, detailed descriptions of well-known functions and configurations that may obscure the gist of the present invention will be omitted. For the same reason, some components are exaggerated, omitted, or schematically shown in the accompanying drawings.
도 1은 본 발명의 실시예에 의해 제조된 셀룰로오스 함유 물질(면, 레이온)을 이용한 항균성 및 탈취성 화합물의 실시예, 도 2는 본 발명의 실시예에 의해 제조된 셀룰로오스 함유 물질(셀로판, 종이)을 이용한 항균성 및 탈취성 화합물의 실시예, 도 3은 본 발명의 실시예에 따른 항균성 및 탈취성 면섬유로 제직된 면직물에 대한 암모니아 가스의 탈취율 시험을 실시한 시험성적서, 도 4는 본 발명의 실시예에 따른 항균성 및 탈취성 면섬유로 제직된 면직물에 대한 항균도 시험을 실시한 시험성적서, 도 5 및 도 6은 도 4에 의한 항균성 및 탈취성 면섬유로 제직된 면직물의 박테리아 번식 정도를 보여주는 사진, 도 7은 도 3 및 도 4의 시험에 사용된 시료 카드, 도 8은 본 발명의 다른 실시예에 따른 항균성 및 탈취성 면섬유로 제직된 면직물에 대한 암모니아 가스의 탈취율 시험을 실시한 시험성적서, 도 9는 본 발명의 다른 실시예에 따른 항균성 및 탈취성 면섬유로 제직된 면직물에 대한 항균도 시험을 실시한 시험성적서, 도 10 및 도 11은 도 9에 의한 항균성 및 탈취성 면섬유로 제직된 면직물의 박테리아 번식 정도를 보여주는 사진, 도 12은 도 8 및 도 9의 시험에 사용된 시료 카드이다. Figure 1 shows an example of an antibacterial and deodorizing compound using a cellulose-containing material (cotton, rayon) prepared according to an example of the present invention, and Figure 2 shows an example of a cellulose-containing material (cellophane, paper) prepared according to an example of the present invention. ) Examples of antibacterial and deodorizing compounds using, Figure 3 is a test report of ammonia gas deodorization rate test on cotton fabric woven with antibacterial and deodorizing cotton fibers according to an example of the present invention, Figure 4 is an example of the present invention A test report of an antibacterial test on a cotton fabric woven with antibacterial and deodorizing cotton fibers according to an example, Figures 5 and 6 are photographs showing the degree of bacterial growth of cotton fabrics woven with antibacterial and deodorizing cotton fibers according to Figure 4; 7 is a sample card used in the tests of FIGS. 3 and 4, FIG. 8 is a test report for testing the deodorization rate of ammonia gas on cotton fabric woven with antibacterial and deodorizing cotton fibers according to another embodiment of the present invention, and FIG. 9 is a test report. A test report of an antibacterial test on a cotton fabric woven with antibacterial and deodorizing cotton fiber according to another embodiment of the present invention, Figures 10 and 11 show the degree of bacterial growth of a cotton fabric woven with antibacterial and deodorizing cotton fiber according to Figure 9 A photo showing, Figure 12 is a sample card used in the tests of Figures 8 and 9.
먼저, 본 발명의 실시예에 따른 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물은 하기 일반식 1로 표시되는 화합물을 포함한다.First, the antibacterial and deodorizing compound using a cellulose-containing material according to an embodiment of the present invention includes a compound represented by the following general formula 1.
[일반식 1][General Formula 1]
여기서, 상기 일반식 1로 표시한 화합물은 음이온 셀룰로오스 [(C6H7O5)-]n 라고 표현이 가능하다. Here, the compound represented by General Formula 1 can be expressed as anionic cellulose [(C 6 H 7 O 5 ) - ] n .
이러한 음이온 셀룰로오스 [(C6H7O5)-]n 제조방법은 아래와 같이 단계 S110 내지 단계 S130을 포함한다.This anionic cellulose [(C 6 H 7 O 5 ) - ] n production method includes steps S110 to S130 as follows.
먼저, 단계 S110은 셀룰로오스 (C6H10O5)n 함유 물질을 준비하는 단계이다.First, step S110 is a step of preparing a cellulose (C 6 H 10 O 5 ) n- containing material.
셀룰로오스(C6H10O5)n 함유 물질로는 면, 셀로판지, 종이, 레이온 등 같은 물질을 예로 들 수 있다. Examples of materials containing cellulose (C 6 H 10 O 5 ) n include materials such as cotton, cellophane, paper, and rayon.
단계 S120은 셀룰로오스 (C6H10O5)n 함유 물질을 환원제 용액에 침지하는 단계이다. 여기서, 상기 환원제는 SnCl2 일 수 있다. Step S120 is a step of immersing a cellulose (C 6 H 10 O 5 ) n- containing material in a reducing agent solution. Here, the reducing agent may be SnCl 2 .
이때, SnCl2 의 농도는 0.01 ~ 0.1 몰일 수 있고, 환원제 용액에 침지하는 시간은 9 ~ 11초일 수 있다.At this time, the concentration of SnCl 2 may be 0.01 to 0.1 mol, and the immersion time in the reducing agent solution may be 9 to 11 seconds.
미반응한 SnCl2 를 제거하기 위하여 침지 후 즉시 세척한 후에 100℃에서 건조시킬 수 있다. To remove unreacted SnCl 2 , it can be washed immediately after immersion and then dried at 100°C.
단계 S130은 상기 셀룰로오스의 (C6H10O5)n 의 H+ 3개를 제거하여 음이온 셀룰로오스 [(C6H7O5)-]n 를 형성하는 단계이다. Step S130 is a step of removing the H + 3 of (C 6 H 10 O 5 ) n of the cellulose to form anionic cellulose [(C 6 H 7 O 5 ) - ] n .
즉, 셀룰로오스(C6H10O5)n 함유 물질에 환원제를 가하여 셀룰로오스 한 분자에 포함되어 있는 2개의 OH와 1개의 CH2OH 중에 포함되어 있는 3개의 OH에서 3개의 H+를 환원 제거함으로써 3개의 산소가 이온화된 음이온 셀룰로오스 (셀룰로오스 O-3)를 제조하는 것이며, 화학식은 아래와 같다. In other words, a reducing agent is added to a cellulose (C 6 H 10 O 5 ) n- containing material to reduce and remove 3 H + from 2 OH contained in one cellulose molecule and 3 OH contained in 1 CH 2 OH. Anionic cellulose (cellulose O -3 ) in which three oxygens are ionized is produced, and the chemical formula is as follows.
[화학식 1][Formula 1]
(C6H10O5)n + SnCl2 → [(C6H7O5)-]n + SnCl4 (C 6 H 10 O 5 ) n + SnCl 2 → [(C 6 H 7 O 5 ) - ] n + SnCl 4
도 1의 왼쪽에는 면과 레이온에 음이온 셀룰로오스 [(C6H7O5)-]n 를 형성한 것이 도시되어 있고, 도 2의 왼쪽에는 셀로판과 종이에 음이온 셀룰로오스 [(C6H7O5)-]n 를 형성한 것이 도시되어 있다.
실시예 1
첫번째 단계에서는 셀룰로오스 (C6H10O5)n 함유 물질을 준비한다. 셀룰로오스(C6H10O5)n 함유 물질로는 면, 셀로판지, 종이, 레이온 등이다.
두번째 단계에서는 셀룰로오스 (C6H10O5)n 함유 물질을 환원제인 SnCl2 용액에 침지한다. 이때, SnCl2 의 농도는 0.05몰이고, 환원제 용액에 침지하는 시간은 10초 정도이다. 이때 미반응한 SnCl2 를 제거하기 위하여 침지 후 즉시 세척한 후에 100℃에서 건조시킨다.
마지막 세번째 단계에서는 셀룰로오스의 (C6H10O5)n 의 H+ 3개를 제거하여 음이온 셀룰로오스 [(C6H7O5)-]n 를 형성한다.The left side of Figure 1 shows the formation of anionic cellulose [(C 6 H 7 O 5 ) - ] n on cotton and rayon, and the left side of Figure 2 shows the formation of anionic cellulose [(C 6 H 7 O 5 ) on cellophane and paper. ) - ] n is shown.
Example 1
In the first step, cellulose (C 6 H 10 O 5 ) n- containing material is prepared. Materials containing cellulose (C 6 H 10 O 5 ) n include cotton, cellophane, paper, and rayon.
In the second step, the cellulose (C 6 H 10 O 5 ) n- containing material is immersed in a reducing agent, SnCl 2 solution. At this time, the concentration of SnCl 2 is 0.05 mol, and the immersion time in the reducing agent solution is about 10 seconds. At this time, in order to remove unreacted SnCl 2 , it is washed immediately after immersion and then dried at 100°C.
In the third and final step, the H + 3 of (C 6 H 10 O 5 ) n of cellulose is removed to form anionic cellulose [(C 6 H 7 O 5 ) - ] n .
이렇게 형성된 음이온 셀룰로오스 [(C6H7O5)-]n 는 항균성이 우수하고 탈취성이 있는 물질이며 다양한 용도로 사용할 수 있다.The anionic cellulose [(C 6 H 7 O 5 ) - ] n formed in this way is a material with excellent antibacterial and deodorizing properties and can be used for various purposes.
항균성 음이온 셀룰로오스 [(C6H7O5 -)]n의 수명은 물리적인 세탁시 10회 정도이어서 세탁후 재사용이 가능하다.The lifespan of antibacterial anionic cellulose [(C 6 H 7 O 5 - )] n is approximately 10 times when physically washed, so it can be reused after washing.
그리고, 도 3 내지 도 7에 도시된 것처럼 시험결과 면에 음이온 셀룰로오스 [(C6H7O5)-]n 를 형성한 물질의 항균성의 능력은 99.9%이고, 탈취성의 능력은 67.8%임을 확인할 수 있다. 하지만 실제 임상 실험 결과 체감 탈취성 능력은 매우 뛰어나서 냄새를 거의 맡을 수 없는 수준으로 확인된다. And, as shown in Figures 3 to 7, the test results confirm that the antibacterial ability of the material forming anionic cellulose [(C 6 H 7 O 5 ) - ] n on cotton is 99.9%, and the deodorizing ability is 67.8%. You can. However, as a result of actual clinical trials, it has been confirmed that the perceived deodorizing ability is so excellent that you can barely smell it.
다음으로, 본 발명의 다른 실시예에 따른 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물은 하기 일반식 2로 표시되는 화합물을 포함한다.Next, the antibacterial and deodorizing compound using a cellulose-containing material according to another embodiment of the present invention includes a compound represented by the following general formula 2.
[일반식 2][General Formula 2]
여기서, 상기 일반식 2로 표시한 화합물은 은 셀룰로오스 [(C6H7O5Ag3)n]라고 표현이 가능하다. Here, the compound represented by General Formula 2 can be expressed as silver cellulose [(C 6 H 7 O 5 Ag 3 ) n ].
이러한 은 셀룰로오스 [(C6H7O5Ag3)n] 제조방법은 단계 S210 및 S220을 포함한다.This method of producing silver cellulose [(C 6 H 7 O 5 Ag 3 ) n ] includes steps S210 and S220.
먼저 단계 S210은 앞서 설명한 음이온 셀룰로오스 [(C6H7O5)-]n 를 AgNO3 용액에 침지하는 단계이고, 단계 S220은 은 셀룰로오스 [(C6H7O5Ag3)n] 을 형성하는 단계를 포함할 수 있다. First, step S210 is a step of immersing the previously described anionic cellulose [(C 6 H 7 O 5 ) - ] n in an AgNO 3 solution, and step S220 is a step of forming cellulose [(C 6 H 7 O 5 Ag 3 ) n ]. It may include steps.
여기서, AgNO3 의 농도는 0.005 ~ 0.007 몰일 수 있고, AgNO3 용액에 침지하는 시간은 2 ~ 4초일 수 있다. Here, the concentration of AgNO 3 may be 0.005 to 0.007 mole, and the immersion time in the AgNO 3 solution may be 2 to 4 seconds.
미반응한 AgNO3 를 제거하기 위하여 침지 후 즉시 세척한 후에 100℃에서 건조시킬 수 있다.To remove unreacted AgNO 3 , it can be washed immediately after immersion and then dried at 100°C.
즉, 환원된 음이온 셀룰로오스에 Ag+ 이온을 무전해 도금하여 항균성과 탈취성이 있는 은 셀룰로오스(셀룰로오스 OAg3)를 제조하는 것이며, 화학식은 아래와 같다. In other words, silver cellulose (cellulose OAg 3 ) with antibacterial and deodorizing properties is manufactured by electroless plating Ag + ions on reduced anionic cellulose, and the chemical formula is as follows.
[화학식 2][Formula 2]
[(C6H7O5)-]n + 3nAgNO3 → [(C6H7O5Ag3)n] + SnCl4 [(C 6 H 7 O 5 ) - ] n + 3nAgNO 3 → [(C 6 H 7 O 5 Ag 3 ) n ] + SnCl 4
도 1의 오른쪽에는 면과 레이온에 은 셀룰로오스 [(C6H7O5Ag3)n] 를 형성한 것이 도시되어 있고, 도 2의 오른쪽에는 셀로판과 종이에 은 셀룰로오스 [(C6H7O5Ag3)n] 를 형성한 것이 도시되어 있다.
실시예 2
첫번째 단계에서는 먼저 앞서 설명한 음이온 셀룰로오스 [(C6H7O5)-]n 를 AgNO3 용액에 침지한다. 여기서, AgNO3 의 농도는 0.006 몰이고, AgNO3 용액에 침지하는 시간은 3초이다. 이렇게 해서 은 셀룰로오스 [(C6H7O5Ag3)n] 을 형성한다.
미반응한 AgNO3 를 제거하기 위하여 침지 후 즉시 세척한 후에 100℃에서 건조시킨다. On the right side of Figure 1, silver cellulose [(C 6 H 7 O 5 Ag 3 ) n ] is shown formed on cotton and rayon, and on the right side of Figure 2, silver cellulose [(C 6 H 7 O) is formed on cellophane and paper. The formation of 5 Ag 3 ) n ] is shown.
Example 2
In the first step, the previously described anionic cellulose [(C 6 H 7 O 5 ) - ] n is immersed in AgNO 3 solution. Here, the concentration of AgNO 3 is 0.006 mole, and the immersion time in the AgNO 3 solution is 3 seconds. In this way, cellulose [(C 6 H 7 O 5 Ag 3 ) n ] is formed.
To remove unreacted AgNO 3 , it is washed immediately after immersion and then dried at 100°C.
이렇게 형성된 은 셀룰로오스 [(C6H7O5Ag3)n] 역시 항균성이 우수하고 탈취성이 있는 물질이며 다양한 용도로 사용할 수 있다.Silver cellulose [(C 6 H 7 O 5 Ag 3 ) n ] formed in this way is also a material with excellent antibacterial and deodorizing properties and can be used for various purposes.
항균성의 은 셀룰로오스 [(C6H7O5Ag3)n]의 물리적 수명은 100회 정도의 물세탁이 가능해서 세탁후 재사용이 가능하다.The physical lifespan of antibacterial silver cellulose [(C 6 H 7 O 5 Ag 3 ) n ] can be washed with water about 100 times, so it can be reused after washing.
그리고, 도 8 내지 도 12에 도시된 것처럼 시험결과 면에 음이온 셀룰로오스 [(C6H7O5)-]n 를 형성한 물질의 항균성의 능력은 99.9%이고, 탈취성의 능력은 37.9%임을 확인할 수 있다. 여기서도 실제 임상 실험 결과 체감 탈취성 능력은 매우 뛰어나서 냄새를 거의 맡을 수 없는 수준으로 확인된다. And, as shown in Figures 8 to 12, the test results confirm that the antibacterial ability of the material forming anionic cellulose [(C 6 H 7 O 5 ) - ] n on cotton is 99.9%, and the deodorizing ability is 37.9%. You can. Here, too, the actual clinical test results show that the perceived deodorizing ability is so excellent that you can barely smell it.
한편, 본 명세서와 도면에 개시된 본 발명의 실시예들은 본 발명의 기술 내용을 쉽게 설명하고 본 발명의 이해를 돕기 위해 특정 예를 제시한 것일 뿐이며, 본 발명의 범위를 한정하고자 하는 것은 아니다. 여기에 개시된 실시예들 이외에도 본 발명의 기술적 사상에 바탕을 둔 다른 변형예들이 실시 가능하다는 것은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 자명한 것이다. Meanwhile, the embodiments of the present invention disclosed in the specification and drawings are merely provided as specific examples to easily explain the technical content of the present invention and to facilitate understanding of the present invention, and are not intended to limit the scope of the present invention. It is obvious to those skilled in the art that in addition to the embodiments disclosed herein, other modifications based on the technical idea of the present invention can be implemented.
Claims (11)
상기 셀룰로오스 (C6H10O5)n 함유 물질을 환원제 용액에 침지하는 단계; 및
상기 셀룰로오스의 (C6H10O5)n 의 H+ 3개를 제거하여 음이온 셀룰로오스 [(C6H7O5)-]n 를 형성하는 단계를 포함하는 것으로,
상기 환원제는 SnCl2 이고,
상기 SnCl2 의 농도는 0.01 ~ 0.1 몰이고,
상기 환원제 용액에 침지하는 시간은 9 ~ 11초인 것을 특징으로 하는 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물의 제조방법.Preparing a cellulose (C 6 H 10 O 5 ) n- containing material;
Immersing the cellulose (C 6 H 10 O 5 ) n- containing material in a reducing agent solution; and
It includes the step of removing H + 3 of (C 6 H 10 O 5 ) n of the cellulose to form anionic cellulose [(C 6 H 7 O 5 ) - ] n ,
The reducing agent is SnCl 2 ,
The concentration of SnCl 2 is 0.01 to 0.1 mol,
A method for producing an antibacterial and deodorizing compound using a cellulose-containing material, characterized in that the immersion time in the reducing agent solution is 9 to 11 seconds.
미반응한 SnCl2 를 제거하기 위하여 침지 후 즉시 세척한 후에 100℃에서 건조시키는 것을 특징으로 하는 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물의 제조방법.In claim 1,
A method for producing an antibacterial and deodorizing compound using a cellulose-containing material, characterized in that it is washed immediately after immersion and then dried at 100°C to remove unreacted SnCl 2 .
하기 일반식 1로 표시되는 화합물을 포함하는 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물.
[일반식 1]
Manufactured by the manufacturing method of claim 1,
An antibacterial and deodorizing compound using a cellulose-containing material containing a compound represented by the following general formula 1.
[General Formula 1]
상기 음이온 셀룰로오스 [(C6H7O5)-]n 를 AgNO3 용액에 침지하는 단계; 및
은 셀룰로오스 [(C6H7O5Ag3)n] 을 형성하는 단계를 포함하고,
상기 AgNO3 의 농도는 0.005 ~ 0.007 몰이고,
상기 AgNO3 용액에 침지하는 시간은 2 ~ 4초인 것을 특징으로 하는 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물의 제조방법.In claim 1,
Immersing the anionic cellulose [(C 6 H 7 O 5 ) - ] n in AgNO 3 solution; and
includes the step of forming cellulose [(C 6 H 7 O 5 Ag 3 ) n ],
The concentration of AgNO 3 is 0.005 to 0.007 mol,
A method for producing an antibacterial and deodorizing compound using a cellulose-containing material, characterized in that the immersion time in the AgNO 3 solution is 2 to 4 seconds.
미반응한 AgNO3 를 제거하기 위하여 침지 후 즉시 세척한 후에 100℃에서 건조시키는 것을 특징으로 하는 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물의 제조방법.In claim 4,
A method for producing an antibacterial and deodorizing compound using a cellulose-containing material, characterized in that it is washed immediately after immersion and then dried at 100°C to remove unreacted AgNO 3 .
하기 일반식 2로 표시되는 화합물을 포함하는 셀룰로오스 함유 물질을 이용한 항균성 및 탈취성 화합물.
[일반식 2]
Manufactured by the manufacturing method of claim 4,
An antibacterial and deodorizing compound using a cellulose-containing material containing a compound represented by the following general formula 2.
[General Formula 2]