KR102637885B1 - Ourdoor transparent patch for blocking ultraviolet and method for manufacturing the same - Google Patents
Ourdoor transparent patch for blocking ultraviolet and method for manufacturing the same Download PDFInfo
- Publication number
- KR102637885B1 KR102637885B1 KR1020230165798A KR20230165798A KR102637885B1 KR 102637885 B1 KR102637885 B1 KR 102637885B1 KR 1020230165798 A KR1020230165798 A KR 1020230165798A KR 20230165798 A KR20230165798 A KR 20230165798A KR 102637885 B1 KR102637885 B1 KR 102637885B1
- Authority
- KR
- South Korea
- Prior art keywords
- skin
- layer
- blocking
- patch
- outdoor use
- Prior art date
Abstract
본 발명은 피부 표면에 대한 점착력을 가지며, 친수성 수지와 피부 개선 기능성 화합물을 포함하는 피부접촉층, 상기 피부접촉층의 상부에 위치하는 자외선 차단 기능성을 갖는 자외선 차단층 및 상기 자외선 차단층의 상부에 위치하는 표면층을 포함하고, 가시광선 투과 특성을 갖는, 자외선 차단 기능성을 갖는 아웃도어용 투명 패치 및 이의 제조방법에 관한 것이다.The present invention provides a skin-contact layer that has adhesive strength to the skin surface and includes a hydrophilic resin and a skin-improving functional compound, a UV-blocking layer with UV-blocking functionality located on top of the skin-contact layer, and a UV-blocking layer on top of the UV-blocking layer. It relates to a transparent patch for outdoor use, including a surface layer located thereon, having visible light transmission properties, and having UV blocking functionality, and a method of manufacturing the same.
Description
본 발명은 자외선 차단 기능성 투명 필름을 포함하는 다층 구조의 아웃도어용 투명 패치로서, 자외선 차단 기능을 유지하는 한편, 피부에 자극없이 부착, 탈착이 가능하고, 투명한 특성을 가져 외관 상 우수한 특성을 갖는 자외선 차단 기능성 아웃도어용 투명 패치 및 이의 제조방법에 관한 것이다.The present invention is a transparent patch for outdoor use with a multi-layered structure containing a transparent film with UV-blocking function. While maintaining the UV-blocking function, it can be attached and detached without irritating the skin, and has transparent properties and excellent appearance characteristics. It relates to a transparent patch for outdoor use that blocks UV rays and a method of manufacturing the same.
야외 활동 시에는 피부에 악영향을 미치는 자외선을 차단하기 위하여 자외선 차단제, 자외선 차단 의류, 모자 등을 착용하는 것이 일반적이다.During outdoor activities, it is common to wear sunscreen, UV-blocking clothing, and a hat to block UV rays that have a negative effect on the skin.
피부에 다양한 증상이나 질병을 유발하는 주요한 원인인 자외선은 태양광을 직접 차단하는 방법이나, 자외선 차단제를 포함하는 화장료 등을 활용하여 자외선을 특이적으로 차단하는 방법에 의하여 차단된다.Ultraviolet rays, which are the main cause of various symptoms and diseases on the skin, are blocked by directly blocking sunlight or by specifically blocking ultraviolet rays using cosmetics containing sunscreen.
자외선은 200nm~400nm의 파장 범위를 갖는 전자기파로서, 자외선 파장 영역을 생체에 미치는 영향에 따라, 자외선 A (UVA, 320nm~400nm), 자외선B (UVB, 320nm~280nm), 자외선C (UVC: 290nm~200nm)로 나눌 수 있다.Ultraviolet rays are electromagnetic waves with a wavelength range of 200 nm to 400 nm. Depending on the effect of the ultraviolet ray wavelength range on the living body, they are divided into ultraviolet A (UVA, 320 nm to 400 nm), ultraviolet B (UVB, 320 nm to 280 nm), and ultraviolet C (UVC: 290 nm). ~200nm).
가장 짧은 파장 범위의 자외선C는 대부분 지구 성층권에서 오존층에 의해 차단되고, 지구 표면까지 도달하는 자외선A와 자외선B가 야외 활동 시 미치는 영향이 크다.Most ultraviolet C, which has the shortest wavelength range, is blocked by the ozone layer in the Earth's stratosphere, and ultraviolet A and ultraviolet B, which reach the Earth's surface, have a significant impact on outdoor activities.
자외선A는 피부 진피까지 투과되어 활성산소(ROS: reactive oxygen species) 생성을 유도하여 DNA 손상을 일으키거나, 홍반, 염증 반응, 피부 노화, 피부암 발생 등을 유발할 수 있고, 자외선 B는 피부의 표피까지 침투되어 홍반과 주근깨, 부종 등을 일으키는 것으로 알려져 있어, 피부 미용과 건강의 측면에서 자외선 차단에 대한 중요성이 부각되고 있다.Ultraviolet A penetrates into the dermis of the skin and induces the production of reactive oxygen species (ROS), which can cause DNA damage, erythema, inflammatory reactions, skin aging, and skin cancer, while ultraviolet B penetrates into the epidermis of the skin. It is known that it penetrates and causes erythema, freckles, and edema, so the importance of UV protection is being highlighted in terms of skin beauty and health.
자외선 차단제는 자외선을 반사, 산란시켜 피부에 도달하는 것을 방지하는 물리적 자외선 차단제와 피부 표면에서 자외선과 반응하여 피부에 직접 도달하기 전에 자외선을 차단하는 화학적 자외선 차단제가 있으며, 용매에 자외선 차단제를 용해, 분산시켜 액상이나 고상의 자외선 차단 화장료로 제조한다.There are two types of sunscreens: physical sunscreens, which reflect and scatter ultraviolet rays and prevent them from reaching the skin, and chemical sunscreens, which react with ultraviolet rays on the skin surface and block them before they directly reach the skin. It is dispersed and manufactured into liquid or solid UV protection cosmetics.
한편, 골프나 테니스, 등산과 같은 야외 활동 시나 여름에는 피부에서 땀이 많이 나므로, 자외선 차단 화장료를 사용하면 땀에 의해 자외선 차단제가 제거되어 자외선 차단 효과가 떨어지거나, 자외선 차단제가 땀과 함께 눈에 들어가 통증을 유발하는 등의 문제가 있었는 바, 최근에는 패치 형태로 피부에 접착력을 갖는 자외선 차단 패치가 개발되어 널리 사용되고 있다.Meanwhile, during outdoor activities such as golf, tennis, mountain climbing, or during summer, the skin sweats a lot, so if you use sunscreen cosmetics, the sunblock will be removed by sweat, reducing the sunscreen effect, or the sunscreen will stick to your eyes along with sweat. There have been problems such as causing pain, and recently, a UV-blocking patch that adheres to the skin in the form of a patch has been developed and is widely used.
대한민국 등록특허 제2242158호는 자외선 차단용 아웃도어 패치에 관한 것으로서, 기재층 및 상기 기재층의 일면에 형성되는 접착층으로 이루어지며, 상기 접착층에는 나이아신아미드, 아데노신, 히알론산나트륨, 프로폴리스 추출물, 하이드롤라이즈드 콜라겐 및 병풀추출물이 함유되어 자외선 차단효과를 가지는 한편, 피부보습 효과, 피부냉각 효과를 가지고, 피부 접착력이 우수할 뿐만 아니라, 피부트러블을 유발하지 않는 효과를 갖는 자외선 차단용 아웃도어 패치를 개시하고 있다.Republic of Korea Patent No. 2242158 relates to an outdoor patch for UV protection, which consists of a base layer and an adhesive layer formed on one side of the base layer. The adhesive layer contains niacinamide, adenosine, sodium hyaluronate, propolis extract, and hydrochloride. An outdoor patch for UV protection that contains rolled collagen and centella asiatica extract to block UV rays, has a skin moisturizing and cooling effect, has excellent skin adhesion, and does not cause skin troubles. is starting.
대한민국 공개특허 제2020-0053432호는, 자외선 차단 패치 및 이의 적용방법에 관한 것으로서, 친수성 수지와 자외선 차단제를 구비한 제1 나노섬유로 형성된 다공성 기재인 자외선 차단층 및 자외선 차단층의 일면에 구비되며 신축성수지와 강도보강수지를 포함하는 혼합수지로 형성된 형상유지층을 구비하여, 자외선 차단제가 피부에 직접 접촉되지 않으며, 물리적 자극에도 박리되거나 피착부위의 움직임을 저해하지 않으면서도 투명도를 가져서 피부에 부착 시 피착부의 가시성이 저하되지 않는 자외선 차단 패치를 개시하고 있다.Republic of Korea Patent Publication No. 2020-0053432 relates to a UV-blocking patch and a method of applying the same, which is provided on one side of the UV-blocking layer and the UV-blocking layer, which is a porous substrate formed of first nanofibers containing a hydrophilic resin and a UV-blocking agent. Equipped with a shape-retaining layer made of a mixed resin containing elastic resin and strength-reinforcing resin, the sunscreen does not come into direct contact with the skin, and has transparency and adheres to the skin without peeling off or impeding the movement of the adhered area due to physical stimulation. We are launching a UV-blocking patch that does not reduce the visibility of the adhesive area.
다만, 상기 기술은 투명하여 피부가 투영되는 한편, 야외 활동 시에 사용하기 적합한 자외선 차단 효과와 부착성 및 우수한 내구성을 가지면서도, 부착된 상태에서 피부 보습이나 피부 미백 등의 피부 개선 기능성을 갖는 유효성분을 피부에 공급하는 자외선 차단용 투명 패치에 대해서는 개시하고 있지 않다.However, the above technology is transparent so that the skin is projected, has a UV blocking effect, adhesion, and excellent durability suitable for use during outdoor activities, and is effective in having skin improvement functions such as skin moisturizing and skin whitening when attached. It does not disclose a transparent patch for UV protection that supplies ingredients to the skin.
따라서, 자외선을 차단하되, 가시광선 투과가 가능하여 패치가 부착되는 피부가 비치는 투명한 특성을 가지면서도 피부에 부착한 상태로 야외 활동을 하여도 패치가 탈락되거나 파손되지 않는 견고한 내구성을 가지며, 피부 개선 기능성을 갖는 자외선 차단용 패치에 대한 개발이 필요한 실정이다.Therefore, it blocks ultraviolet rays, allows visible light to pass through, and has a transparent characteristic that allows the skin to which the patch is attached to see through. It also has solid durability so that the patch does not fall off or break even when engaged in outdoor activities while attached to the skin, improving skin. There is a need for the development of a functional UV-blocking patch.
본 발명은 피부에 자극을 유발할 수 있는 자외선 차단 성분이 피부에 직접 접촉되지 않으면서도 우수한 자외선 차단 효과를 갖는 아웃도어용 투명 패치를 제공하는 것을 목적으로 한다.The purpose of the present invention is to provide a transparent patch for outdoor use that has excellent UV blocking effect without directly contacting the skin with UV blocking ingredients that can cause skin irritation.
본 발명은 패치가 피부와 접촉한 면에 피부 개선 기능성을 갖는 유효 성분을 포함하여 피부 개선 효과를 갖는 아웃도어용 투명 패치를 제공하는 것을 목적으로 한다.The purpose of the present invention is to provide a transparent patch for outdoor use that has a skin-improving effect by containing an active ingredient with skin-improving functionality on the surface of the patch in contact with the skin.
본 발명은 신축성과 유연성이 우수하여 우수함에 따라 움직임 등으로 인한 물리적 자극에도 박리되지 않고, 견고한 내구성을 가져 파손, 파단 우려가 없는 아웃도어용 투명 패치를 제공하는 것을 목적으로 한다.The purpose of the present invention is to provide a transparent patch for outdoor use that has excellent elasticity and flexibility, does not peel off even when exposed to physical stimulation due to movement, etc., and is durable, so there is no risk of damage or breakage.
또한, 본 발명은 자외선의 투과율은 낮고 가시광선 투과율이 높아 피부에 부착 시 피부가 패치를 통해 비치는 효과를 갖는 자외선 차단 기능성 아웃도어 투명 패치를 제공하는 것을 목적으로 한다.In addition, the purpose of the present invention is to provide a functional outdoor transparent patch for blocking ultraviolet rays, which has a low ultraviolet ray transmittance and a high visible light transmittance, so that when attached to the skin, the skin is seen through the patch.
상기와 같은 과제를 해결하기 위한 본 발명에 따른 투명 패치는, 피부 표면에 대한 점착력을 가지며, 친수성 수지와 피부 개선 기능성 화합물을 포함하는 피부접촉층; 상기 피부접촉층의 상부에 위치하는 자외선 차단 기능성을 갖는 자외선 차단층; 및 상기 자외선 차단층의 상부에 위치하는 표면층; 을 포함하고, 가시광선 투과 특성을 갖는다.The transparent patch according to the present invention for solving the above problems includes a skin contact layer that has adhesive strength to the skin surface and includes a hydrophilic resin and a skin-improving functional compound; A UV-blocking layer having UV-blocking functionality located on top of the skin-contact layer; And a surface layer located on top of the ultraviolet ray blocking layer; It contains and has visible light transmission properties.
본 발명에 있어서, 상기 친수성 수지는 폴리비닐알코올 수지를 포함하고, 상기 표면층은 폴리올레핀계 폴리머를 포함할 수 있다.In the present invention, the hydrophilic resin may include a polyvinyl alcohol resin, and the surface layer may include a polyolefin-based polymer.
본 발명에 있어서, 상기 아웃도어용 투명 패치는 필름 형태의 상기 피부접촉층, 상기 자외선 차단층 및 상기 표면층이 구비된 3중층 구조를 포함할 수 있다.In the present invention, the transparent patch for outdoor use may include a triple-layer structure including the skin contact layer, the ultraviolet ray blocking layer, and the surface layer in the form of a film.
본 발명에 있어서, 상기 피부접촉층은 피부 보습, 피부 미백, 피부 주름 개선, 피부 탄력 개선, 피부 홍반 개선, 피부 노화 방지, 멜라닌 형성 억제 및, 피부 진정으로 이루어진 군에서 선택된 하나 이상의 피부 개선 기능성을 갖는 것일 수 있다.In the present invention, the skin contact layer has one or more skin improvement functions selected from the group consisting of skin moisturizing, skin whitening, skin wrinkle improvement, skin elasticity improvement, skin erythema improvement, skin aging prevention, melanin formation inhibition, and skin soothing. It may be something to have.
본 발명에 있어서, 상기 피부 개선 기능성 화합물은 상기 친수성 수지 100 중량부를 기준으로 10 내지 15 중량부로 포함되는 것일 수 있다.In the present invention, the skin improving functional compound may be included in an amount of 10 to 15 parts by weight based on 100 parts by weight of the hydrophilic resin.
본 발명에 있어서, 상기 자외선 차단 성분은 물리적 자외선 차단제 및 화학적 자외선 차단제로 이루어진 군에서 선택된 하나 이상을 포함하는, 아웃도어용 투명 패치.In the present invention, the sunscreen component includes at least one selected from the group consisting of a physical sunscreen and a chemical sunblock, a transparent patch for outdoor use.
본 발명에 있어서, 상기 표면층은 인장강도가 0.5 내지 2 N/mm2일 수 있다.In the present invention, the surface layer may have a tensile strength of 0.5 to 2 N/mm 2 .
본 발명에 있어서, 상기 자외선 차단 성분은 드로메트리졸트리실록산(Drometrizole trisiloxane, DTS), 산화 아연(ZnO), 메틸렌비스-벤조트리아졸릴테트라메틸부틸페놀(Methylene bis-benzotriazolyl tetramethyl-butylphenol, MBBT) 및 비스-에틸헥실옥시페놀메톡시페닐트리아진(Bis-ethylhexyloxy methoxyphenyl triazine, BEMT)로 이루어진 군에서 선택된 하나 이상을 포함할 수 있다.In the present invention, the sunscreen ingredients include drometrizole trisiloxane (DTS), zinc oxide (ZnO), methylene bis-benzotriazolyl tetramethyl-butylphenol (MBBT), and It may include one or more selected from the group consisting of bis-ethylhexyloxy methoxyphenyl triazine (BEMT).
본 발명에 있어서, 상기 피부 개선 기능성 화합물은 수용성 진주분말 및 이의 수용액으로 이루어진 군에서 선택된 하나 이상의 피부 개선 기능성 화합물을 포함할 수 있다.In the present invention, the skin improving functional compound may include one or more skin improving functional compounds selected from the group consisting of water-soluble pearl powder and its aqueous solution.
본 발명에 있어서, 상기 피부 개선 기능성 화합물은 다시마 추출물 및 이의 수용액으로 이루어진 군에서 선택된 하나 이상의 피부 개선 기능성 화합물을 포함할 수 있다.In the present invention, the skin improving functional compound may include one or more skin improving functional compounds selected from the group consisting of kelp extract and an aqueous solution thereof.
본 발명에 있어서, 상기 피부접촉층은 점착 보조제를 더 포함하고, 상기 점착 보조제는 표면에 미세 기공이 형성되어 있는 다공성 PDMS 플레이크 및 상기 미세 기공에 담지된 폴리비닐알코올, 히알루론산 및 비닐아세테이트 공중합체의 혼합물을 포함할 수 있다.In the present invention, the skin contact layer further includes an adhesion aid, and the adhesion aid is a porous PDMS flake with micropores formed on the surface and a copolymer of polyvinyl alcohol, hyaluronic acid, and vinyl acetate supported in the micropores. It may include a mixture of.
본 발명은 또한, 아웃도어용 투명 패치의 제조방법으로서, a) 폴리올레핀계 폴리머 필름을 준비하는 단계; b) 상기 a) 단계의 폴리올레핀계 폴리머 필름의 하부에 자외선 차단 성분과 폴리우레탄 수지하이드로겔을를 포함하는 자외선 차단 필름층을 형성하는 단계; c) 상기 b) 단계에서 형성된 자외선 차단 필름층의 하부에 폴리비닐알코올과 피부 개선 기능성 화합물을 포함하는 피부접촉층을 형성하는 단계; 및 d) 상기 c) 단계에서 제조된 피부접촉층의 하부에 이형필름을 부가하는 단계; 를 포함하는, 아웃도어용 투명 패치의 제조방법을 제공한다.The present invention also provides a method for manufacturing a transparent patch for outdoor use, comprising: a) preparing a polyolefin-based polymer film; b) forming a UV-blocking film layer containing a UV-blocking component and a polyurethane resin hydrogel on the lower part of the polyolefin-based polymer film of step a); c) forming a skin contact layer containing polyvinyl alcohol and a skin-improving functional compound on the lower part of the UV-blocking film layer formed in step b); and d) adding a release film to the lower part of the skin contact layer prepared in step c); It provides a method of manufacturing a transparent patch for outdoor use, including.
상기 제조방법에 있어서, 상기 b) 단계의 자외선 차단 성분은, 혼합 전 적외선을 10 내지 15분간 조사하고, 탄산 가스가 1 내지 1.2 bar로 채워진 챔버 내에 넣고 믹싱하는 단계를 수행한 것을 특징으로 하는 것일 수 있다.In the above manufacturing method, the UV blocking component in step b) is characterized by performing the step of irradiating infrared rays for 10 to 15 minutes before mixing, placing it in a chamber filled with carbon dioxide gas at 1 to 1.2 bar, and mixing. You can.
본 발명에 따른 아웃도어용 투명 패치는 자외선 차단 성분이 피부에 직접 접촉되지 않아 피부 우수한 자외선 차단 효과를 갖는다.The transparent patch for outdoor use according to the present invention has an excellent UV-blocking effect on the skin because the UV-blocking ingredient does not come into direct contact with the skin.
본 발명은 패치가 피부와 접촉한 면에 피부 개선 기능성을 갖는 유효 성분을 포함하여 피부 개선 효과를 갖는다.The present invention has a skin-improving effect by including an active ingredient with skin-improving functionality on the surface where the patch is in contact with the skin.
본 발명은 신축성과 유연성이 우수하여 우수함에 따라 움직임 등으로 인한 물리적 자극에도 박리되지 않고, 견고한 내구성을 가져 쉽게 파손, 파단되지 않는 효과를 갖는다.The present invention has excellent elasticity and flexibility, so it does not peel off even when exposed to physical stimulation due to movement, etc., and has strong durability so that it is not easily broken or broken.
또한, 본 발명은 자외선의 투과율은 낮고 가시광선 투과율이 높아 피부에 부착 시 피부가 패치를 통해 비치는 효과를 갖는다.In addition, the present invention has a low ultraviolet ray transmittance and a high visible light transmittance, so that when attached to the skin, the skin is reflected through the patch.
본 발명은 또한, 서로 다른 물질로 구성된 3개의 층이 움직임 등으로 인한 물리적 자극에도 층간 분리가 발생되지 않고 하나의 패치로서 유지될 수 있는 견고한 내구성을 갖는다.In addition, the present invention has strong durability in that three layers made of different materials can be maintained as a single patch without separation between layers even when subjected to physical stimulation due to movement, etc.
도 1은 본 발명의 일 실시예에 따른 투명 패치의 수직 단면도이다.
도 2는 본 발명의 일 실시예에 따른 투명 패치의 사진이다.1 is a vertical cross-sectional view of a transparent patch according to an embodiment of the present invention.
Figure 2 is a photograph of a transparent patch according to an embodiment of the present invention.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 각 구성을 보다 상세히 설명하나, 이는 하나의 예시에 불과할 뿐, 본 발명의 권리범위가 다음 내용에 의해 제한되지 아니한다.Hereinafter, each configuration of the present invention will be described in more detail so that those skilled in the art can easily implement it. However, this is only an example, and the scope of rights of the present invention is determined by the following contents. Not limited.
본 발명에 사용된 "바람직한" 또는 "바람직하게는"은 특정 조건에서 특정 장점을 갖는 본 발명의 실시예를 나타낸다. 그러나, 다른 실시예 또한 동일 조건 또는 다른 조건에서 바람직할 수 있다. 또한, 하나 이상의 바람직한 실시예는 다른 실시예가 유용하지 않다는 것을 의미하는 것은 아니며, 본 발명의 범위 내에 있는 다른 실시예를 배제하는 것도 아니다.As used herein, “preferred” or “preferably” refers to an embodiment of the invention that has certain advantages under certain conditions. However, other embodiments may also be preferred under the same or different conditions. Additionally, the identification of one or more preferred embodiments does not mean that other embodiments are not useful, nor does it exclude other embodiments that are within the scope of the invention.
본 명세서에 사용된 "포함한다"는 용어는 본 발명에 유용한 재료, 조성물, 장치, 및 방법들을 나열할 때 사용되며 그 나열된 예에 제한되는 것은 아니다.As used herein, the term “comprising” is used to list materials, compositions, devices, and methods useful in the present invention and is not limited to the listed examples.
특히, 본 발명에서 "포함한다"는 용어는 구성요소를 그대로 포함하는 상태, 구성요소를 전구물질로 하여 가공된 상태, 가공된 후에 구성요소를 만족하는 상태 등과 같이 다양한 상태를 지칭하는 것이며, 그 나열된 예에 제한되는 것은 아니다.In particular, in the present invention, the term "comprising" refers to various states, such as a state in which the component is included as is, a state in which the component is processed as a precursor, a state in which the component is satisfied after processing, etc. It is not limited to the examples listed.
본 발명은 골프, 테니스, 등산 등의 야외 활동 시, 자외선 차단을 위해 피부에 부착하여 사용하는 자외선 차단 기능성 아웃도어용 투명 패치에 관한 것으로서, i) 피부와 자외선 차단 성분이 직접 접촉하지 않도록 하면서도 높은 자외선 차단 효과를 갖는 자외선 차단층, ii) 지지층으로 기능하며 우수한 유연성과 신축성으로 인한 견고한 내구성을 부여하는 표면층, iii) 피부에 대한 부착성이 우수하면서도 피부로부터 박리 시 피부 자극을 유발하지 않는 피부접착층을 포함하며, 각 층이 투명한 특성을 가져, 적층한 상태에서도 높은 가시광선 투과율을 가져 피부가 비치는 효과를 가지며, 서로 다른 성분을 포함하는 각 층을 합지한 상태에서도 층간 분리가 일어나지 않는 효과를 갖는 것을 특징으로 한다.The present invention relates to a transparent patch for outdoor use with UV-blocking functionality that is attached to the skin to block UV rays during outdoor activities such as golf, tennis, and mountaineering. i) It provides high UV protection while preventing direct contact between the skin and UV-blocking ingredients UV-blocking layer with UV-blocking effect, ii) a surface layer that functions as a support layer and provides solid durability due to excellent flexibility and elasticity, iii) a skin-adhesive layer that has excellent adhesion to the skin but does not cause skin irritation when peeled from the skin Each layer has transparent properties and has a high visible light transmittance even in the laminated state, which has the effect of showing the skin, and has the effect of preventing separation between layers even when each layer containing different ingredients is laminated. It is characterized by
구체적으로, 본 발명에 따른 아웃도어용 투명 패치는, 피부 표면에 대한 점착력을 가지며, 친수성 수지와 피부 개선 기능성 화합물을 포함하는 피부접촉층, 상기 점착층의 상부에 위치하는 자외선 차단 기능성을 갖는 자외선 차단층 및 상기 자외선 차단층의 상부에 위치하는 표면층을 포함하고, 가시광선 투과 특성을 갖는다.Specifically, the transparent patch for outdoor use according to the present invention has an adhesive force to the skin surface, a skin contact layer containing a hydrophilic resin and a skin-improving functional compound, and an ultraviolet ray blocking function located on the upper part of the adhesive layer. It includes a blocking layer and a surface layer located on top of the ultraviolet ray blocking layer, and has visible light transmission properties.
본 발명에 따른 아웃도어용 투명 패치는, 필름 형태의 피부접촉층, 자외선 차단층 및 표면층이 구비된 3중층 구조의 포함하여, 자외선 차단 기능성을 가지면서도, 피부 접촉 면에서 피부 개선 기능성을 가지며, 패치의 부착면과 주변부의 움직임에도 피부에서 쉽게 탈락되지 않고, 피부가 투명하게 비치는 것을 특징으로 한다.The transparent patch for outdoor use according to the present invention has a triple-layer structure including a film-type skin contact layer, an ultraviolet ray blocking layer, and a surface layer, and has ultraviolet ray blocking functionality while also having skin improvement functionality in terms of skin contact, It is characterized by not being easily removed from the skin even when the attachment surface and surrounding area of the patch moves, and the skin is transparent.
이하에서는, 본 발명의 구성을 보다 상세히 설명한다.Below, the configuration of the present invention will be described in more detail.
1. 피부접촉층1. Skin contact layer
본 발명에 따른 아웃도어용 투명 패치에서 피부에 집적 접촉되는 층으로서, 피부 표면에 대한 점착력을 갖는 한편, 피부와 접촉한 상태에서 피부 개선 기능성을 갖는 것을 특징으로 한다.It is a layer that directly contacts the skin in the transparent patch for outdoor use according to the present invention, and is characterized by having adhesive power to the skin surface and having skin improvement functionality while in contact with the skin.
구체적으로, 상기 피부접촉층은 친수성 수지와 피부 개선 기능성 화합물을 포함하도록 하면서도, 피부 표면에 대한 점착성을 향상시킨 것을 특징으로 한다.Specifically, the skin contact layer is characterized by improved adhesion to the skin surface while containing a hydrophilic resin and a skin-improving functional compound.
사람 피부 표면은 피지가 존재하고, 표피가 친유성을 갖기 때문에, 친수성이 너무 높지 않도록 구성하여, 피부 표면에 대한 점착성을 우수하게 유지할 수 있도록 구성된다.Since the surface of human skin contains sebum and the epidermis has lipophilic properties, it is configured so that the hydrophilicity is not too high and excellent adhesion to the skin surface can be maintained.
상기 친수성 수지는 피부 개선 기능성 화합물 중 친수성 성분을 피부접촉층 내에 균일하게 함유하고, 상분리 등의 불안정한 상태가 유발되지 않도록 하기 위해 사용된다.The hydrophilic resin is used to uniformly contain hydrophilic components among skin-improving functional compounds within the skin contact layer and to prevent unstable conditions such as phase separation.
상기 친수성 수지는 피부에 유해한 소재가 아니며, 본 발명의 목적을 벗어나지 않는 범위 내에서 어떠한 것이든 사용할 수 있으나, 가장 바람직하게는, 폴리비닐알코올 수지를 사용할 수 있다.The hydrophilic resin is not a material harmful to the skin, and any material can be used without departing from the purpose of the present invention, but most preferably, polyvinyl alcohol resin can be used.
강한 극성의 수산화기를 가진 폴리비닐알코올 수지를 사용하여, 피부 개선 기능성 화합물과 균일하게 혼합이 가능하도록 구성되며, 투명한 특성을 가져, 가시광선이 투과되어 피부가 투명 패치를 통해 비칠 수 있다.It is made of polyvinyl alcohol resin with a strong polar hydroxyl group so that it can be mixed evenly with skin-improving functional compounds, and has transparent properties, allowing visible light to pass through and shine through the transparent patch.
상기 피부접촉층은 피부 개선 기능성 화합물을 더 포함하여, 피부 개선 기능성을 갖는 것을 특징으로 한다. 상기 피부 개선 기능성 화합물은 상기 폴리비닐알코올 수지 100 중량부를 기준으로 10 내지 15 중량부로 포함될 수 있다.The skin contact layer further includes a skin-improving functional compound and has skin-improving functionality. The skin improving functional compound may be included in an amount of 10 to 15 parts by weight based on 100 parts by weight of the polyvinyl alcohol resin.
보다 바람직하게는, 11 내지 13 중량부로 포함될 수 있으며, 가장 바람직하게는, 12.5 중량부로 포함될 수 있다.More preferably, it may be included in 11 to 13 parts by weight, and most preferably, it may be included in 12.5 parts by weight.
상기 함량보다 과량으로 포함되는 경우에는, 제형이 불안정하고, 피부 개선 기능성 화합물이 보관 중에 용출되는 문제가 있을 수 있고, 상기 함량보다 소량으로 첨가되는 경우에는, 피부 개선 기능이 미미한 문제가 있을 수 있다.If it is included in excess of the above content, the formulation may be unstable and there may be a problem with the skin-improving functional compound dissolving during storage, and if it is added in a smaller amount than the above content, there may be a problem of insignificant skin improvement function. .
상기 함량 수치는 피부 개선 기능성 화합물의 종류와 무관하게 최소 첨가량과 최대 첨가량을 한정한 것으로서, 각 함량 수치는 각 화합물의 종류에 따라 다소 상이하게 변경 가능하다.The above content values limit the minimum and maximum addition amounts regardless of the type of skin improvement functional compound, and each content value can be changed somewhat differently depending on the type of each compound.
구체적으로, 상기 피부접촉층은 피부 보습, 피부 미백, 피부 주름 개선, 피부 탄력 개선, 피부 홍반 개선, 피부 노화 방지 및 멜라닌 형성 억제로 이루어진 군에서 선택된 하나 이상의 피부 개선 기능성을 갖는 것일 수 있다. 상기 피부 개선 기능성의 의미는 피부의 문제 상태를 보다 나은 상태로 개선할 수 있는 기능성을 갖는 것을 의미한다. Specifically, the skin contact layer may have one or more skin improvement functions selected from the group consisting of skin moisturizing, skin whitening, skin wrinkle improvement, skin elasticity improvement, skin erythema improvement, skin aging prevention, and melanin formation inhibition. The meaning of skin improvement functionality means having functionality that can improve the problematic condition of the skin to a better state.
보다 상세하게는, 피부 보습 및 피부 미백으로 이루어진 군에서 선택된 하나 이상의 피부 개선 기능성을 갖는 것일 수 있다.More specifically, it may have one or more skin improvement functions selected from the group consisting of skin moisturizing and skin whitening.
상기 피부 개선 기능성 화합물은, 필요에 따라 화장료 조성물, 마스크팩 등과 같은 화장료 분야에서 사용되는 것이면 적절히 선택하여 사용할 수 있다.The skin-improving functional compound can be appropriately selected and used as long as it is used in the cosmetic field such as cosmetic compositions and mask packs, as needed.
상세하게는, 수용성 진주분말 및 이의 수용액, 다시마 추출물 및 이의 수용액으로 이루어진 군에서 선택된 하나 이상의 피부 개선 기능성 화합물을 포함할 수 있다.In detail, it may include one or more skin improving functional compounds selected from the group consisting of water-soluble pearl powder and its aqueous solution, kelp extract, and its aqueous solution.
상기 수용성 진주분말 및 이의 수용액은, 진부분말로부터 탄산칼슘과 유기물질을 녹여내고, 그 용액을 동결건조하여 기능성 유기성분의 소실이 최소화되도록 하여 제조된 것이다. 이온화되고, 유기물질 손실이 최소화됨에 따라, 티로시나제의 활성을 저해하여 멜라닌 생성을 억제하여 미백효과가 우수하고, NO 생성을 억제하여 염증발생을 억제하므로 피부진정(항염)효과가 우수하며, 콜라겐생산을 촉진시키므로 피부노화 억제효과가 우수하다. 따라서, 이를 피부촉진층에 포함함으로써, 피부 미백, 피부 진정(항염증), 피부 노화 방지(억제) 등의 피부 개선 기능성을 가질 수 있다.The water-soluble pearl powder and its aqueous solution are prepared by dissolving calcium carbonate and organic substances from the pearl powder and freeze-drying the solution to minimize loss of functional organic components. As it is ionized and the loss of organic substances is minimized, it inhibits the activity of tyrosinase and suppresses melanin production, resulting in excellent whitening effect. It suppresses NO production and inflammation, so it has an excellent skin soothing (anti-inflammatory) effect and collagen production. It has an excellent anti-aging effect as it promotes skin aging. Therefore, by including it in the skin promotion layer, it can have skin improvement functions such as skin whitening, skin soothing (anti-inflammatory), and skin aging prevention (inhibition).
상기 수용성 진주분말 및 이의 수용액에 관해서는, 대한민국 등록특허 제1771055호의 내용을 참고할 수 있다.Regarding the water-soluble pearl powder and its aqueous solution, the contents of Republic of Korea Patent No. 1771055 may be referred to.
다시마는 갈조 해조류로서 알긴산, 푸코이단 등의 유용성 성분을 포함하고 있으며, 다시마 추출물은 항산화 작용, 항균 작용, 항염증 작용, 항노화 작용, 항멜라닌 형성 작용 등을 하는 것으로 알려져 있어, 이를 피부촉진층에 첨가하여 피부에 적용하는 경우, 피부 노화 방지, 멜라닌 형성 억제, 피부 진정 등의 피부 개선 기능성을 가질 수 있다.Kelp is a brown seaweed that contains oil-soluble ingredients such as alginic acid and fucoidan. Kelp extract is known to have antioxidant, antibacterial, anti-inflammatory, anti-aging, and anti-melanin forming effects, and is used in the skin stimulating layer. When added and applied to the skin, it can have skin improvement functions such as preventing skin aging, inhibiting melanin formation, and soothing the skin.
상기 피부접촉층의 두께는 100 내지 500 ㎛일 수 있다.The thickness of the skin contact layer may be 100 to 500 ㎛.
상기 두께보다 얇은 경우에는, 피부에 대한 점착력이 저하되는 문제가 있고, 상기 두께보다 두꺼운 경우에는, 피부 개선 기능성 효과나 점착력 개선이나 향상 효과 없이 제조 단가가 증가하게 되는 문제가 있다.If it is thinner than the above thickness, there is a problem that the adhesion to the skin is reduced, and if it is thicker than the above thickness, there is a problem that the manufacturing cost increases without any skin improvement functional effect or adhesion improvement or enhancement effect.
한편, 상기 피부접촉층은 피부와의 점착력을 향상시키기 위해 점착 보조제를 더 포함할 수 있다.Meanwhile, the skin contact layer may further include an adhesion aid to improve adhesion to the skin.
상기 점착 보조제는 표면에 미세 기공이 형성되어 있는 다공성 PDMS(Polydimethylsiloxane) 플레이크(Flake) 및 상기 미세 기공에 담지된 폴리비닐알코올, 히알루론산 및 비닐아세테이트 공중합체의 혼합물을 포함하도록 구성되며, 미세 기공이 형성되어 있는 플레이크 형상의 다공성의 PDMS 입자를 제조하고 이를 미리 준비된 폴리비닐알코올, 히알루론산 및 비닐아세테이트 공중합체가 분산된 수용액에 침지시켜 점착 보조제로 제조한다.The adhesion aid is composed of porous PDMS (polydimethylsiloxane) flakes with micropores formed on the surface and a mixture of polyvinyl alcohol, hyaluronic acid, and vinyl acetate copolymer supported in the micropores, and the micropores are The formed flake-shaped porous PDMS particles are prepared and prepared as an adhesion aid by immersing them in a previously prepared aqueous solution in which polyvinyl alcohol, hyaluronic acid, and vinyl acetate copolymer are dispersed.
상기 점착 보조제는 피부에 투명 패치를 부착하면 체온에 의하여 1~3시간 경과 시부터 미세 기공에서 방출되어 점착력을 유지, 개선하는 효과를 갖는다.When a transparent patch is attached to the skin, the adhesion aid is released from the micropores after 1 to 3 hours due to body temperature and has the effect of maintaining and improving adhesion.
상기 점착 보조제를 더 포함하는 경우에는, 상기 친수성 수지 100 중량부를 기준으로 3 내지 5 중량부로 포함될 수 있다. When the adhesion aid is further included, it may be included in an amount of 3 to 5 parts by weight based on 100 parts by weight of the hydrophilic resin.
상기 함량보다 과량으로 첨가되는 경우에는, 상대적으로 피부 개선 기능성 화합물의 함량이 적어져, 피부 개선 효과가 미미한 문제가 있고, 상기 함량보다 소량으로 첨가되는 경우에는, 첨가하여도 점착력의 개선 효과가 미미하여 무용하게 되는 문제가 있다.If it is added in excess of the above content, the content of the skin-improving functional compound will be relatively small, causing a problem that the skin improvement effect will be minimal. If it is added in a smaller amount than the above content, the effect of improving adhesion will be minimal even if added. There is a problem with it becoming useless.
2. 자외선 차단층2. UV protection layer
자외선 차단층은 상기 피부접촉층의 상부에 위치하는 별개의 층으로서, 자외선 차단 성분을 포함하여 투명 패치가 자외선 차단 기능성을 갖도록 구성하는 한편, 피부와 직접 접촉하지 않도록 구성되며, 표면층의 하부에 위치시켜 외부에 노출되지 않도록 구성하여, 자외선 차단 성분의 소실이나 자외선 차단층이 파손되지 않도록 구성된다.The ultraviolet ray blocking layer is a separate layer located on top of the skin contact layer, and includes a ultraviolet ray blocking ingredient so that the transparent patch has ultraviolet ray blocking functionality, while being constructed so as not to come into direct contact with the skin, and is located at the lower part of the surface layer. It is designed so that it is not exposed to the outside, so that the UV-blocking ingredients are not lost or the UV-blocking layer is damaged.
상기 자외선 차단층은, 자외선 차단 성분과 폴리우레탄 수지를 포함한다.The ultraviolet ray blocking layer includes a ultraviolet ray blocking component and a polyurethane resin.
상기 자외선 차단 성분은 폴리우레탄 수지로 합성하기 전의 디이소시아네이트와 폴리올이 혼합된 프리폴리머와 함께 혼합한 후에 폴리우레탄 수지로 합성되어 자외선 차단층을 형성함으로써, 상기 피부접촉층과는 별개의 층으로 구성될 수 있다.The UV blocking component is mixed with a prepolymer that is a mixture of diisocyanate and polyol before being synthesized with a polyurethane resin, and then synthesized with a polyurethane resin to form a UV blocking layer, so that it is composed of a separate layer from the skin contact layer. You can.
상기 자외선 차단 성분은 자외선 차단 기능성을 가지며, 본 발명의 목적을 벗어나지 않는 범위에서 특별히 제한되지 않고 사용될 수 있다. 물리적 자외선 차단제 및 화학적 자외선 차단제로 이루어진 군에서 선택된 하나 이상을 포함될 수 있으며, 필요에 따라 혼합하여 사용하는 것 또한, 가능하다.The ultraviolet ray blocking component has ultraviolet ray blocking functionality and can be used without particular limitation as long as it does not deviate from the purpose of the present invention. It may contain one or more selected from the group consisting of physical sunscreens and chemical sunscreens, and it is also possible to mix and use them as needed.
물리적 자외선 차단제로는 예를 들어, 징크옥사이드(Zinc Oxide. 산화아연)와 티타늄디옥사이드(Titanium Dioxide.이산화티타늄) 등의 무기화학물질이 있으며, 필요에 따라 무기화학물질에 추가 가공처리를 한 복합체 형태의 자외선 차단제로 구성될 수 있다.Physical sunscreens include, for example, inorganic chemicals such as zinc oxide and titanium dioxide, and are in the form of complexes that are additionally processed with inorganic chemicals as needed. It can be composed of sunscreen.
화학적 자외선 차단제는, 화장료로 사용될 수 있는 것은 어떠한 것이든 사용이 가능하다. 예를 들면, 드로메트리졸트리실록산(Drometrizole trisiloxane, DTS), 산화 아연(ZnO), 메틸렌비스-벤조트리아졸릴테트라메틸부틸페놀(Methylene bis-benzotriazolyl tetramethyl-butylphenol, MBBT) 및 비스-에틸헥실옥시페놀메톡시페닐트리아진(Bis-ethylhexyloxy methoxyphenyl triazine, BEMT)으로 이루어진 군에서 선택된 어느 하나일 수 있다.Any chemical sunscreen that can be used as a cosmetic can be used. For example, Drometrizole trisiloxane (DTS), Zinc Oxide (ZnO), Methylene bis-benzotriazolyl tetramethyl-butylphenol (MBBT), and Bis-ethylhexyloxyphenol. It may be any one selected from the group consisting of methoxyphenyltriazine (Bis-ethylhexyloxy methoxyphenyl triazine, BEMT).
보다 바람직하게는, 비스-에틸헥실옥시페놀메톡시페닐트리아진(Bis-ethylhexyloxy methoxyphenyl triazine, BEMT)을 포함할 수 있다. 이를 포함하는 경우에는, UVA 영역과 UVB 영역을 모두 차단할 수 있는 효과를 가져, 보다 넓은 파장 범위의 자외선 차단 기능성을 갖도록 구성할 수 있다.More preferably, it may include bis-ethylhexyloxy methoxyphenyl triazine (BEMT). If it is included, it has the effect of blocking both UVA and UVB areas, and can be configured to have UV blocking functionality over a wider wavelength range.
상기 자외선 차단 성분은 상기 친수성 수지 100 중량부를 기준으로 10 내지 20 중량부로 포함될 수 있다.The UV blocking component may be included in an amount of 10 to 20 parts by weight based on 100 parts by weight of the hydrophilic resin.
상기 함량보다 과량으로 포함되는 경우에는, 자외선 차단층의 상부에 위치하는 표면층 및 하부에 위치하는 피부접촉층과의 친화력이 저하되어, 패치로 제조한 후에 층간 분리가 발생될 수 있는 문제가 있고, 상기 함량보다 소량으로 포함되는 경우에는, 자외선 차단 효과가 미미한 문제가 있다.If it is included in excess of the above content, the affinity between the surface layer located on top of the ultraviolet ray blocking layer and the skin contact layer located below decreases, and there is a problem that separation between layers may occur after manufacturing into a patch. If it is included in a smaller amount than the above amount, there is a problem that the ultraviolet ray blocking effect is minimal.
상기 폴리우레탄 수지는 디이소시아네이트와 폴리올을 혼합한 프리폴리머 상태에서 경화제를 이용하여 폴리우레탄 수지로 형성되는데, 시중에서 화장료, 마스크팩 등에 이용될 수 있는 폴리우레탄 수지이면 특별히 제한되지 않고 사용이 가능하며, 투명 패치의 모든 영역에서 균일한 자외선 차단 효과를 갖도록 하기 위하여, 프리폴리머 상태에서 자외선 차단 성분과 균일하게 혼합한 후에, 필름 형태로 제조하여 자외선 차단층으로 제조한다.The polyurethane resin is formed from a prepolymer mixture of diisocyanate and polyol using a curing agent. Any polyurethane resin that can be used in cosmetics, mask packs, etc. on the market can be used without particular restrictions. In order to have a uniform UV-blocking effect in all areas of the transparent patch, the prepolymer is uniformly mixed with UV-blocking ingredients and then manufactured into a film form to form a UV-blocking layer.
예를 들면, 메틸렌디페닐디이소시아네이트(Methylene Diphenyl Diisocyanate, MDI) 및 에틸렌글리콜을 이용하여 폴리우레탄 수지를 제조할 수 있다.For example, polyurethane resin can be manufactured using methylene diphenyl diisocyanate (MDI) and ethylene glycol.
한편, 본 발명에 따른 자외선 차단층은 자외선에 대한 선택적인 차단이 가능하며, 짧은 파장의 가시광선, 즉, 자외선 파장에 인접한 영역의 가시광선에 대해서는 일부 차단 효과를 가질 수 있으나, 가시광선에 대해서는 투과성을 갖는 것을 특징으로 한다.Meanwhile, the ultraviolet ray blocking layer according to the present invention is capable of selectively blocking ultraviolet rays, and may have a partial blocking effect for short-wavelength visible rays, that is, visible rays in the area adjacent to the ultraviolet ray wavelength, but may have a partial blocking effect for visible rays. It is characterized by having permeability.
상세하게는, 가시광선에 대해 투과성을 가져 투명 패치가 부착되는 피부가 투명 패치의 상부에 비치는 효과를 갖는다. 보다 상세하게는, 가시광선에 대한 투과율이 75% 이상일 수 있다.In detail, it has transparency to visible light, so that the skin to which the transparent patch is attached has the effect of being reflected on the upper part of the transparent patch. More specifically, the transmittance of visible light may be 75% or more.
3. 표면층3. Surface layer
표면층은 아웃도어용 투명 패치의 외면을 의미하는 것으로서, 외부에 노출된 면에 위치하는 층이다. The surface layer refers to the outer surface of the outdoor transparent patch and is a layer located on the surface exposed to the outside.
표면층은 외부의 물리, 화학적 자극에 의하여 손상이 방지되는 강성이 있는 층으로서, 상대적으로 강성이 낮은 자외선 차단층과 피부접착층의 손상을 방지하는 역할을 한다.The surface layer is a rigid layer that prevents damage from external physical and chemical stimuli, and serves to prevent damage to the ultraviolet ray blocking layer and skin adhesive layer, which have relatively low rigidity.
한편, 상기 표면층은 쉽게 손상되지 않도록 견고한 재질로 구성되는 한편, 사용자가 인체에 부착한 상태에서 움직이더라도 불편함을 느끼지 않도록 신축성과 유연성을 갖는 것을 특징으로 한다.Meanwhile, the surface layer is made of a sturdy material so that it is not easily damaged, and is characterized by elasticity and flexibility so that the user does not feel uncomfortable even when moving while attached to the human body.
보다 상세하게는, 상기 표면층은 인강강도가 0.5 내지 2 N/mm2일 수 있다. 더욱 바람직하게는, 1.0 내지 2.0 N/mm2일 수 있다.More specifically, the surface layer may have a tensile strength of 0.5 to 2 N/mm 2 . More preferably, it may be 1.0 to 2.0 N/mm 2 .
상기 수치보다 인장강도가 큰 경우에는, 투명 패치를 사용차가 부착한 상태에서 움직임에 불편함을 느낄 수 있고, 상기 수치보다 인장강도가 작은 경우에는, 자외선 차단층, 피부접촉층을 지지하는 기능이 떨어질 수 있고, 외부의 자극에 의하여 파손, 손상되기 쉬운 문제가 있다.If the tensile strength is greater than the above value, the user may feel uncomfortable moving while the transparent patch is attached, and if the tensile strength is lower than the above value, the function of supporting the ultraviolet ray blocking layer and the skin contact layer may be impaired. There is a problem that it can fall and is easily broken or damaged by external stimuli.
상기 표면층은 폴리올레핀계 폴리머를 포함하도록 구성될 수 있으며, 가장 바람직하게는, 폴리에틸렌, 폴리프로필렌으로 이루어진 군에서 선택된 하나 이상을 포함할 수 있다.The surface layer may be composed of a polyolefin-based polymer, and most preferably, may include one or more selected from the group consisting of polyethylene and polypropylene.
상기 표면층의 두께는 100 내지 500 ㎛인 필름 형태를 가지며, 상기 두께보다 두꺼운 경우에는, 사용자가 부착한 상태에서 움직임이 부자연스럽고 사용감이 저하되는 문제가 있고, 상기 두께보다 얇은 경우에는, 움직임이 많은 경우에 쉽게 피부에서 탈락되거나, 패치 자체의 파손이 발생될 수 있는 문제가 있다.The thickness of the surface layer is in the form of a film of 100 to 500 ㎛. If it is thicker than the thickness, there is a problem that movement is unnatural and the feeling of use is reduced when the user attaches it, and if it is thinner than the thickness, there is a problem that there is a lot of movement In some cases, there is a problem that it can easily fall off from the skin or the patch itself can be damaged.
상기 표면층 또한, 본 발명에 따른 아웃도어용 투명 패치에 사용하기 적합하도록, 투명성을 갖는 것이 바람직하다. 3중층으로 합지하여 제조된 투명 패치의 투명성이 저하되지 않도록 투명한 특성을 갖는 것이 바람직하다.The surface layer also preferably has transparency so as to be suitable for use in the outdoor transparent patch according to the present invention. It is desirable that the transparent patch manufactured by lamination of three layers has transparent characteristics so that the transparency is not reduced.
4. 제조방법4. Manufacturing method
본 발명에 따른 아웃도어용 투명 패치의 제조방법은, a) 폴리올레핀계 폴리머 필름을 준비하는 단계, b) 상기 a) 단계의 폴리올레핀계 폴리머 필름의 하부에 자외선 차단 성분과 폴리우레탄 수지를 포함하는 자외선 차단 필름층을 형성하는 단계, c) 상기 b) 단계에서 형성된 자외선 차단 필름층의 하부에 폴리비닐알코올과 피부 개선 기능성 화합물을 포함하는 피부접촉층을 형성하는 단계 d) 상기 c) 단계에서 제조된 피부접촉층의 하부에 이형필름을 부가하는 단계를 포함한다.The method of manufacturing a transparent patch for outdoor use according to the present invention includes the steps of a) preparing a polyolefin-based polymer film, and b) adding a UV-blocking component and a polyurethane resin to the lower part of the polyolefin-based polymer film in step a). forming a blocking film layer, c) forming a skin contact layer containing polyvinyl alcohol and a skin-improving functional compound on the lower part of the UV blocking film layer formed in step b), d) forming a skin contact layer prepared in step c). It includes adding a release film to the lower part of the skin contact layer.
상기 a) 단계는 표면층을 구성하는 필름을 준비하는 단계로서, 이의 일면에 자외선 차단층을 형성하기 전에, 해당 면에 불필요한 오염물 등을 제거하여, 두 층 간의 접착력이 보다 향상되도록 하는 단계이다. 필요에 따라, 탈지, 세척 등의 과정을 거칠 수 있다.Step a) is a step of preparing the film constituting the surface layer, and before forming a UV blocking layer on one side, unnecessary contaminants, etc. are removed from that side to further improve the adhesion between the two layers. If necessary, processes such as degreasing and washing may be performed.
상기 b) 단계는 상기 a) 단계의 폴리올레핀계 폴리머 필름의 일면에 자외선 차단 성분과 폴리우레탄 수지를 포함하는 자외선 차단 필름층을 형성하는 단계로서, 자외선 차단 성분과 디이소시아네이트와 폴리올을 혼합하여 프리폴리머를 제조한 후, 이를 상기 폴리올레핀계 폴리머 필름의 일면(하부)에 도포하여 필름 형태의 층으로 형성한다.Step b) is a step of forming a UV-blocking film layer containing a UV-blocking component and a polyurethane resin on one side of the polyolefin-based polymer film of step a), wherein a prepolymer is prepared by mixing the UV-blocking component, diisocyanate, and polyol. After manufacturing, it is applied to one side (lower part) of the polyolefin-based polymer film to form a film-shaped layer.
이 때, 상기 b) 단계에서 프리폴리머를 제조하기 전에, 상기 자외선 차단 성분은 미리 전처리 과정을 수행하여, 자외선 차단 성분과 폴리우레탄 수지의 혼화성을 향상시킬 수 있는데, 혼합 전 적외선을 10 내지 15분간 조사하고, 탄산 가스가 1 내지 1.2 bar로 채워진 챔버 내에 넣고 믹싱하는 단계를 수행함으로써, 폴리우레탄 수지와의 혼화성이 향상되고, 이로 인하여, 표면층과 피부점착층 간의 접착력이 우수하여 3중층 구조에서도 층간 박리가 일어나지 않는다.At this time, before preparing the prepolymer in step b), the UV blocking component may be subjected to a pretreatment process in advance to improve the miscibility of the UV blocking component and the polyurethane resin. Before mixing, infrared rays may be applied for 10 to 15 minutes. By performing the step of irradiating and mixing in a chamber filled with carbon dioxide gas at 1 to 1.2 bar, miscibility with polyurethane resin is improved, and as a result, the adhesion between the surface layer and the skin adhesive layer is excellent, even in a three-layer structure. Delamination between layers does not occur.
상기 c) 단계는 상기 b) 단계에서 형성된 자외선 차단 필름층의 하부에 폴리비닐알코올과 피부 개선 기능성 화합물을 포함하는 피부접촉층을 형성하는 단계로서, 상기 자외선 차단층이 표면층과 접한 면의 반대면(자외선 차단층의 하부)에 피부접촉층을 형성하는 단계이다. 피부 개선 기능성 화합물과 폴리비닐알코올을 혼합하여, 상기 자외선 차단층을 필름 형태로 형성한다.Step c) is a step of forming a skin contact layer containing polyvinyl alcohol and a skin-improving functional compound on the lower part of the UV blocking film layer formed in step b), wherein the UV blocking layer is on the opposite side of the surface contacting the surface layer. This is the step of forming a skin contact layer (under the UV blocking layer). The skin-improving functional compound and polyvinyl alcohol are mixed to form the ultraviolet ray blocking layer in the form of a film.
마지막으로, d) 단계는 c) 단계에서 제조된 피부접촉층의 하부에 이형필름을 부가하는 단계로서, 아웃도어용 투명 패치의 하부, 즉, 피부접촉층의 점착력 저하를 방지하기 위하여 이형필름을 부가하는 단계이다.Finally, step d) is a step of adding a release film to the lower part of the skin contact layer prepared in step c). The release film is applied to the lower part of the outdoor transparent patch, that is, to prevent deterioration of the adhesion of the skin contact layer. This is the addition step.
이형필름은 마스크팩에 사용하기 적합한 것이면 특별히 제한되지 않고 사용이 가능하다.The release film can be used without particular restrictions as long as it is suitable for use in a mask pack.
이하에서는, 실시예에 기초하여 본 발명을 설명한다.Below, the present invention will be explained based on examples.
<실시예 1><Example 1>
비스-에틸헥실옥시페놀메톡시페닐트리아진(Bis-ethylhexyloxy methoxyphenyl triazine, BEMT, Tinosorb S)과 메틸렌디페닐디이소시아네이트와 에틸렌글리콜을 혼합하여 프리폴리머로 제조한 다음 준비된 폴리프로필렌 필름(표면층, 두께: 300㎛)의 일면에 도포하여 자외선 차단층 450㎛의 두께로 형성하였다.A prepolymer was prepared by mixing Bis-ethylhexyloxy methoxyphenyl triazine (BEMT, Tinosorb S), methylenediphenyl diisocyanate, and ethylene glycol, and then the prepared polypropylene film (surface layer, thickness: 300 ㎛) was applied to one side to form a UV blocking layer with a thickness of 450 ㎛.
이 때, 비스-에틸헥실옥시페놀메톡시페닐트리아진은 폴리우레탄 수지 100 중량부를 기준으로 15 중량부로 첨가된다.At this time, bis-ethylhexyloxyphenolmethoxyphenyltriazine is added in an amount of 15 parts by weight based on 100 parts by weight of the polyurethane resin.
자외선 차단층이 상기 필름과 접하는 면의 반대면에는 폴리비닐알코올 수지 100중량부와 수용성 진주분말(대한민국 특허등록 제1771055호에 따라 제조됨) 5 중량부를 혼합하여 300㎛ 두께의 피부접촉층을 제조하고, 그 하부에 이형필름을 부가하여, 3중층의 자외선 차단 기능성 아웃도어용 투명 패치를 제조하였다.On the opposite side of the surface where the UV blocking layer is in contact with the film, a 300㎛ thick skin contact layer was prepared by mixing 100 parts by weight of polyvinyl alcohol resin and 5 parts by weight of water-soluble pearl powder (manufactured in accordance with Korean Patent Registration No. 1771055). Then, a release film was added to the bottom to produce a triple-layer UV-blocking functional outdoor transparent patch.
<실시예 2><Example 2>
PDMS와 실리카 입자를 혼합한 조성물을 이용하여 표면에 미세 기공이 형성되어 있는 다공성 PDMS 플레이크를 제조하였다. 별도로 폴리비닐알코올, 히알루론산 및 비닐아세테이트 공중합체를 2: 3: 1의 중량비율로 정제수를 용매로 용해시키고 균일하게 혼합되도록 섞는다.Porous PDMS flakes with micropores formed on the surface were manufactured using a mixture of PDMS and silica particles. Separately, polyvinyl alcohol, hyaluronic acid, and vinyl acetate copolymer were dissolved in purified water as a solvent in a weight ratio of 2:3:1 and mixed until uniformly mixed.
상기 실시예 1에서, 피부접촉층에 폴리비닐알코올 수지 100 중량부를 기준으로, 점착 보조제 4 중량부를 첨가하여 제조한 것을 제외하고는 실시예 1과 동일한 방법으로 제조하였다.In Example 1, the skin contact layer was manufactured in the same manner as Example 1, except that 4 parts by weight of an adhesion auxiliary agent was added to the skin contact layer based on 100 parts by weight of polyvinyl alcohol resin.
<실시예 3><Example 3>
상기 실시예 1에서, 비스-에틸헥실옥시페놀메톡시페닐트리아진을 프리폴리머로 제조하기 전에, 적외선을 15분간 조사하고, 탄산 가스가 1 bar로 채워진 챔버 내에 넣어 믹싱하는 단계를 수행한 후에, 이를 이용하여 폴리우레탄 프리폴리머를 제조한 것을 제외하고는 실시예 1과 동일한 방법으로 제조하였다. In Example 1, before preparing bis-ethylhexyloxyphenolmethoxyphenyltriazine as a prepolymer, a step of irradiating infrared rays for 15 minutes and mixing in a chamber filled with carbon dioxide gas at 1 bar was performed. It was prepared in the same manner as Example 1, except that a polyurethane prepolymer was prepared.
<비교예 1><Comparative Example 1>
상기 실시예 1에서, 상기 피부접촉층에 포함되는 폴리비닐알코올 수지 대신, 카르복시메틸셀룰로오스를 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.It was prepared in the same manner as Example 1, except that carboxymethyl cellulose was used instead of the polyvinyl alcohol resin included in the skin contact layer.
<비교예 2><Comparative Example 2>
상기 실시예 1에서, 상기 피부접촉층에 포함되는 폴리비닐알코올 수지 대신, 히알루론산을 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.It was prepared in the same manner as Example 1, except that hyaluronic acid was used instead of the polyvinyl alcohol resin included in the skin contact layer.
<비교예 3><Comparative Example 3>
상기 실시예 1에서, 상기 피부접촉층에 포함되는 폴리비닐알코올 수지 대신, 폴리비닐피롤리돈을 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.It was prepared in the same manner as Example 1, except that polyvinylpyrrolidone was used instead of the polyvinyl alcohol resin included in the skin contact layer.
<비교예 4><Comparative Example 4>
상기 실시예 1에서, 상기 피부접촉층에 포함되는 폴리비닐알코올 수지 대신, 메틸렌디페닐디이소시아네이트와 에틸렌글리콜로 합성된 폴리우레탄을 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.It was prepared in the same manner as Example 1, except that polyurethane synthesized from methylenediphenyldiisocyanate and ethylene glycol was used instead of the polyvinyl alcohol resin included in the skin contact layer.
<비교예 5> <Comparative Example 5>
상기 실시예 1에서, 상기 피부접촉층에 포함되는 수용성 진주분말을 5 중량부로 포함하는 대신, 1 중량부를 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.It was prepared in the same manner as Example 1, except that 1 part by weight of the water-soluble pearl powder included in the skin contact layer was used instead of 5 parts by weight.
<비교예 6> <Comparative Example 6>
상기 실시예 1에서, 상기 피부접촉층에 포함되는 수용성 진주분말을 5 중량부로 포함하는 대신, 10 중량부를 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.It was prepared in the same manner as Example 1, except that 10 parts by weight of the water-soluble pearl powder included in the skin contact layer was used instead of 5 parts by weight.
<비교예 7> <Comparative Example 7>
상기 실시예 1에서, 상기 자외선 차단층에 포함되는 비스-에틸헥실옥시페놀메톡시페닐트리아진을 15 중량부로 포함하는 대신, 20 중량부를 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.In Example 1, it was prepared in the same manner as Example 1, except that 20 parts by weight of bis-ethylhexyloxyphenolmethoxyphenyltriazine included in the ultraviolet ray blocking layer was used instead of 15 parts by weight. .
<비교예 8><Comparative Example 8>
상기 실시예 1에서, 상기 자외선 차단층에 포함되는 폴리우레탄 수지 대신, 폴리비닐알코올을 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.It was prepared in the same manner as Example 1, except that polyvinyl alcohol was used instead of the polyurethane resin included in the ultraviolet ray blocking layer.
<비교예 9><Comparative Example 9>
상기 실시예 1에서, 상기 자외선 차단층에 포함되는 폴리우레탄 수지 대신, 폴리프로필렌을 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.It was manufactured in the same manner as Example 1, except that polypropylene was used instead of the polyurethane resin included in the ultraviolet ray blocking layer.
<비교예 10><Comparative Example 10>
상기 실시예 1에서, 상기 표면층을 폴리우레탄 필름을 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 제조하였다.In Example 1, the surface layer was manufactured in the same manner as Example 1, except that a polyurethane film was used.
<실험방법><Experiment method>
1. 자외선 차단율(KS K 0850:2019)1. UV protection rate (KS K 0850:2019)
실시예와 비교예에 따른 패치 시편을 자외선 차단지수 측정기기(SPF-290AS, solar light)를 이용하여 자외선 차단지수(SPF) 수치를 측정하였다. 측정은 패치 내 서로 다른 위치에서 10회 진행하고, 측정값의 평균을 하기 표 1에 기재하였다.The sun protection factor (SPF) values of the patch specimens according to the examples and comparative examples were measured using a sun protection factor measuring device (SPF-290AS, solar light). Measurements were conducted 10 times at different locations within the patch, and the average of the measured values is listed in Table 1 below.
2. 투명성 평가2. Transparency evaluation
실시예와 비교예에 따른 패치 시편에 대해 자외선-가시광선-근적외선 분광광도계(UV-VIS-NIR Spectrophotometer)를 이용하여 가시광선에 대한 광투과율을 측정하였다. 측정은 패치 내 기포가 없는, 서로 다른 위치에서 10회 진행하고, 측정값의 평균을 표 1에 기재하였다.The light transmittance for visible light was measured for the patch specimens according to the examples and comparative examples using an ultraviolet-visible-near-infrared spectrophotometer (UV-VIS-NIR Spectrophotometer). Measurements were conducted 10 times at different locations without air bubbles in the patch, and the average of the measured values is listed in Table 1.
3. 부착력 평가3. Adhesion evaluation
피부에 특이 질환이 없는 20-40대 성인 남녀 50명을 대상으로, 실시예와 비교예에 따른 패치 시편에 대한 부착력 평가를 진행하였다.The adhesion of patch specimens according to Examples and Comparative Examples was evaluated on 50 adult men and women in their 20s and 40s without any specific skin diseases.
패치 시편을 오른쪽 허벅지 전면부에 부착하고 90분동안 러닝머신을 뛰도록 하고, 과정 중에 패치가 피부로부터 탈락되는 경우에는 X, 탈락되지 않았으나 일부 떼진 부분이 있거나 부착력이 미미한 경우는 △, 패치가 피부에 완전히 부착되어 있는 경우에는 O로 평가하였다(부착력 평가1).Attach the patch specimen to the front of the right thigh and run on the treadmill for 90 minutes. If the patch falls off from the skin during the process, mark If it was completely attached, it was evaluated as O (adhesion evaluation 1).
이어서, O로 평가된 패치 시편에 대해서는, 박리 시에 피부 자극 여부를 평가하도록 하였다. 피부 자극이 있는 경우는 X, 피부 자극 없이 부드럽게 박리되는 경우에는 O로 평가하였다(부착력 평가2).Next, the patch specimen evaluated as O was evaluated for skin irritation upon peeling. If there was skin irritation, it was rated as
4. 내구성 평가4. Durability evaluation
실시예와 비교예에 따른 패치 시편을 인공피부모델에 부착하고, 10회 내지 50회까지 부착과 박리를 반복하여 진행하고, 시편의 파단, 파손 시의 횟수를 기록하였다(내구성 평가1).The patch specimens according to the examples and comparative examples were attached to the artificial skin model, attachment and peeling were repeated 10 to 50 times, and the number of times the specimen was broken or damaged was recorded (durability evaluation 1).
시편이 파단, 파손되지 않은 경우에는, 추가 20회 부착과 박리를 반복하여 진행한 후, 3중층의 층간 박리 여부를 확인하여, 박리된 경우 X, 변화없는 경우 O로 평가하였다(내구성 평가2).If the specimen was not fractured or damaged, attachment and peeling were repeated an additional 20 times, and then the triple layer was checked for interlayer separation. If peeled, it was evaluated as .
5. 피부 개선 기능성 평가5. Skin improvement functional evaluation
피부에 특이 질환이 없는 20-40대 성인 남녀 50명을 대상으로, 실시예와 비교예에 따른 패치 시편을 6시간 부착한 후, 피부 개선 효과에 대한 평가를 진행하였다.For 50 adult men and women in their 20s and 40s without any specific skin diseases, patch specimens according to Examples and Comparative Examples were attached for 6 hours, and then the skin improvement effect was evaluated.
피부 보습 개선 여부에 대한 평가를 진행하도록 하였다.An evaluation was conducted to determine whether skin moisturization was improved.
평가는 0점(아무 차이 없음)~5점(패치 제거 후에도 보습감 유지됨)으로 평가하였다.The evaluation was from 0 (no difference) to 5 (moisturizing effect maintained even after patch removal).
6. 사용감 평가6. Evaluation of feeling of use
피부에 특이 질환이 없는 20-40대 성인 남녀 50명을 대상으로, 실시예 및 비교예에 따른 패치를 피부에 부착하여 패치의 사용감 평가를 진행하였다. 움직임에 따라 패치가 유연하게 늘어나거나 변형 가능하여 착용감에 따라 5점만점으로 평가하여 평균을 나타냈다(불편하거나, 이물감이 심함: 1점 ~ 착용감이 느껴지지 않음: 5점).For 50 adult men and women in their 20s and 40s without any specific skin diseases, patches according to Examples and Comparative Examples were attached to the skin and the feeling of use of the patches was evaluated. The patch can flexibly stretch or deform depending on movement, so the fit was evaluated on a 5-point scale, with an average score (uncomfortable or foreign body sensation: 1 point to no feeling of fit: 5 points).
차단율(%)UV-rays
Blocking rate (%)
투과율(%)visible light
Transmittance (%)
상기 표 1을 참고하면, 실시예에 따른 패치는 자외선 차단율이 높으면서도 가시광선 투과율이 높아 투명성을 갖는 것을 확인할 수 있다.Referring to Table 1 above, it can be seen that the patch according to the example has a high ultraviolet ray blocking rate and a high visible light transmittance, making it transparent.
더욱이, 실시예의 경우, 부착력, 내구성이 우수하며, 피부접촉층에 포함된 피부 개선 기능성 유효 성분으로 인한 피부 개선 효과가 우수하면서도, 사용감 또한 우수함을 확인할 수 있다.Moreover, in the case of the examples, it can be confirmed that the adhesion and durability are excellent, the skin improvement effect due to the skin improvement functional ingredient contained in the skin contact layer is excellent, and the feeling of use is also excellent.
한편, 실시예 2는 실시예 1 및 3과 대비하여 점착 보조제를 더 포함하는 피부 접촉층이 피부에 대해 부착력이 더 우수함을 확인할 수 있고, 실시예 3의 경우에는, 층간 박리가 억제됨을 확인할 수 있는 바, 다층 구조의 필름의 내구성이 특히 우수함을 확인할 수 있다.On the other hand, in Example 2, compared to Examples 1 and 3, it can be confirmed that the skin contact layer further containing an adhesion auxiliary agent has better adhesion to the skin, and in the case of Example 3, it can be confirmed that peeling between layers is suppressed. As a result, it can be seen that the durability of the multi-layered film is particularly excellent.
10: 표면층
20: 자외선 차단층
30: 피부접촉층10: surface layer
20: UV blocking layer
30: Skin contact layer
Claims (11)
상기 피부접촉층의 상부에 위치하는 자외선 차단 기능성을 갖는 자외선 차단층; 및
상기 자외선 차단층의 상부에 위치하는 표면층;
을 포함하고,
상기 피부접촉층은 점착 보조제를 더 포함하고,
상기 점착 보조제는 표면에 미세 기공이 형성되어 있는 다공성 PDMS 플레이크 및 상기 미세 기공에 담지된 폴리비닐알코올, 히알루론산 및 비닐아세테이트 공중합체의 혼합물을 포함하며,
가시광선 투과 특성을 갖는, 아웃도어용 투명 패치.
A skin contact layer that has adhesion to the skin surface and includes a hydrophilic resin and a skin-improving functional compound;
A UV-blocking layer having UV-blocking functionality located on top of the skin-contact layer; and
A surface layer located on top of the ultraviolet ray blocking layer;
Including,
The skin contact layer further includes an adhesion aid,
The adhesion aid includes porous PDMS flakes with micropores formed on the surface and a mixture of polyvinyl alcohol, hyaluronic acid, and vinyl acetate copolymer supported in the micropores,
Transparent patch for outdoor use with visible light transmission properties.
상기 친수성 수지는 폴리비닐알코올 수지를 포함하고,
상기 표면층은 폴리올레핀계 폴리머를 포함하는, 아웃도어용 투명 패치.
According to paragraph 1,
The hydrophilic resin includes polyvinyl alcohol resin,
A transparent patch for outdoor use, wherein the surface layer includes a polyolefin-based polymer.
상기 피부접촉층은 피부 보습, 피부 미백, 피부 주름 개선, 피부 탄력 개선, 피부 홍반 개선, 피부 노화 방지, 멜라닌 형성 억제 및 피부 진정으로 이루어진 군에서 선택된 하나 이상의 피부 개선 기능성을 갖는, 아웃도어용 투명 패치.
According to paragraph 1,
The skin contact layer is an outdoor transparent layer having one or more skin improvement functions selected from the group consisting of skin moisturizing, skin whitening, skin wrinkle improvement, skin elasticity improvement, skin erythema improvement, skin aging prevention, melanin formation inhibition, and skin soothing. patch.
상기 피부 개선 기능성 화합물은 상기 친수성 수지 100 중량부를 기준으로 10 내지 15 중량부로 포함되는, 아웃도어용 투명 패치.
According to paragraph 1,
A transparent patch for outdoor use, wherein the skin improving functional compound is contained in an amount of 10 to 15 parts by weight based on 100 parts by weight of the hydrophilic resin.
상기 표면층은 인장강도가 0.5 내지 2 N/mm2인 아웃도어용 투명 패치.
According to paragraph 1,
The surface layer is a transparent patch for outdoor use with a tensile strength of 0.5 to 2 N/mm 2 .
상기 자외선 차단 성분은 드로메트리졸트리실록산(Drometrizole trisiloxane, DTS), 산화 아연(ZnO), 메틸렌비스-벤조트리아졸릴테트라메틸부틸페놀(Methylene bis-benzotriazolyl tetramethyl-butylphenol, MBBT) 및 비스-에틸헥실옥시페놀메톡시페닐트리아진(Bis-ethylhexyloxy methoxyphenyl triazine, BEMT)로 이루어진 군에서 선택된 하나 이상을 포함하는, 아웃도어용 투명 패치.
According to paragraph 1,
The sunscreen ingredients include drometrizole trisiloxane (DTS), zinc oxide (ZnO), methylene bis-benzotriazolyl tetramethyl-butylphenol (MBBT), and bis-ethylhexyloxy. A transparent patch for outdoor use, comprising at least one selected from the group consisting of phenolmethoxyphenyltriazine (Bis-ethylhexyloxy methoxyphenyl triazine, BEMT).
상기 피부 개선 기능성 화합물은 수용성 진주분말 및 이의 수용액으로 이루어진 군에서 선택된 하나 이상의 피부 개선 기능성 화합물을 포함하는, 아웃도어용 투명 패치.
According to paragraph 1,
The skin improving functional compound is a transparent patch for outdoor use, comprising at least one skin improving functional compound selected from the group consisting of water-soluble pearl powder and an aqueous solution thereof.
상기 피부 개선 기능성 화합물은 다시마 추출물 및 이의 수용액으로 이루어진 군에서 선택된 하나 이상의 피부 개선 기능성 화합물을 포함하는, 아웃도어용 투명 패치.
According to paragraph 1,
The skin improving functional compound is a transparent patch for outdoor use, comprising at least one skin improving functional compound selected from the group consisting of kelp extract and an aqueous solution thereof.
a) 폴리올레핀계 폴리머 필름을 준비하는 단계;
b) 상기 a) 단계의 폴리올레핀계 폴리머 필름의 하부에 자외선 차단 성분과 하이드로겔을 포함하는 자외선 차단 필름층을 형성하는 단계;
c) 상기 b) 단계에서 형성된 자외선 차단 필름층의 하부에 폴리비닐알코올과 피부 개선 기능성 화합물을 포함하는 피부접촉층을 형성하는 단계; 및
d) 상기 c) 단계에서 제조된 피부접촉층의 하부에 이형필름을 부가하는 단계; 를 포함하는, 아웃도어용 투명 패치의 제조방법.
A method of manufacturing a transparent patch for outdoor use according to claim 1,
a) preparing a polyolefin-based polymer film;
b) forming a UV-blocking film layer containing a UV-blocking component and a hydrogel on the lower part of the polyolefin-based polymer film of step a);
c) forming a skin contact layer containing polyvinyl alcohol and a skin-improving functional compound on the lower part of the UV-blocking film layer formed in step b); and
d) adding a release film to the lower part of the skin contact layer prepared in step c); Method for manufacturing a transparent patch for outdoor use, including.
상기 b) 단계의 자외선 차단 성분은, 혼합 전 적외선을 10 내지 15분간 조사하고, 탄산 가스가 1 내지 1.2 bar로 채워진 챔버 내에 넣고 믹싱하는 단계를 수행한 것을 특징으로 하는,
아웃도어용 투명 패치의 제조방법.According to clause 10,
The UV blocking component in step b) is characterized in that the step of irradiating infrared rays for 10 to 15 minutes before mixing, placing it in a chamber filled with carbon dioxide gas at 1 to 1.2 bar, and mixing.
Method of manufacturing a transparent patch for outdoor use.