KR102597125B1 - Wet tissue using ozone sterilized water and its manufacturing method - Google Patents
Wet tissue using ozone sterilized water and its manufacturing method Download PDFInfo
- Publication number
- KR102597125B1 KR102597125B1 KR1020230105227A KR20230105227A KR102597125B1 KR 102597125 B1 KR102597125 B1 KR 102597125B1 KR 1020230105227 A KR1020230105227 A KR 1020230105227A KR 20230105227 A KR20230105227 A KR 20230105227A KR 102597125 B1 KR102597125 B1 KR 102597125B1
- Authority
- KR
- South Korea
- Prior art keywords
- ozone
- film
- lldpe
- linear low
- density polyethylene
- Prior art date
Abstract
본 발명은 오존 살균수를 이용한 물티슈 및 그의 제조방법에 관한 것으로서, 본 발명의 방법의 구성은, 오존 발생기를 사용하여 오존을 생성하는 단계와, 오존을 물에 용해시켜서 오존 살균수를 제조하는 단계와, 오존 살균수에 물티슈용 원단을 침지하여 살균하는 단계와, 오존과의 반응이 적은 선형저밀도폴리에틸렌(LLDPE) 필름을 준비하는 단계와, 상기 선형저밀도폴리에틸렌(LLDPE) 필름을 고온 처리하여 오존 저항성을 높이는 단계와, 상기 선형저밀도폴리에틸렌(LLDPE) 필름에 경화 PET 필름을 열압하여 다층구조 오존저항성 필름을 제작하는 단계와, 오존 저항성 노스티커 타입 파우치를 제작하는 단계와, 오존 저항성 노스티커 타입 파우치를 이용하여 패키징하는 단계를 포함하여 이루어진다.The present invention relates to wet tissues using ozone sterilizing water and a method for manufacturing the same. The method of the present invention includes the steps of generating ozone using an ozone generator and dissolving ozone in water to produce ozone sterilizing water. , sterilizing the wet tissue fabric by immersing it in ozone sterilizing water, preparing a linear low-density polyethylene (LLDPE) film that has little reaction with ozone, and treating the linear low-density polyethylene (LLDPE) film at high temperature to achieve ozone resistance. Raising the linear low-density polyethylene (LLDPE) film by hot-pressing the cured PET film to produce a multi-layered ozone-resistant film, producing an ozone-resistant no-sticker type pouch, and producing an ozone-resistant no-sticker type pouch. It includes the step of packaging.
Description
본 발명은 오존 살균수를 이용한 물티슈 및 그의 제조방법에 관한 것으로서, 좀더 세부적으로 말하자면 오존 살균수를 이용하여 물티슈를 제조함으로써 화학 살균제를 쓰지 않고도 모든 균을 죽일 수 있음과 동시에 개봉후 대기에 노출되고 나면 반감기가 짧아서 빨리 분해되어 버리기 때문에 인체에 거의 영향을 주지 않으며, 선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET 필름의 이중층으로 이루어진 파우치 필름을 이용하여 다층구조 오존저항성 필름을 제작함과 동시에, 레이저광의 경사각 조절을 위한 레이저 가공장치를 이용하여 파우치 필름의 상부에 절취선을 가공하여 출구를 형성하는 방법으로 오존 저항성 노스티커 타입 파우치를 제작함으로써 오존을 오랫동안 유지할 수 있으며 파우치 제작단가를 낮출 수 있는, 오존 살균수를 이용한 물티슈 및 그의 제조방법에 관한 것이다.The present invention relates to wet tissues using ozone sterilizing water and a manufacturing method thereof. More specifically, by manufacturing wet tissues using ozone sterilizing water, all germs can be killed without using chemical disinfectants, and at the same time, they are exposed to the atmosphere after opening. Since it has a short half-life and decomposes quickly, it has little effect on the human body. A multi-layered ozone-resistant film is produced using a pouch film made of a double layer of linear low-density polyethylene (LLDPE) film and a cured PET film, and at the same time, the laser light Ozone sterilization is possible by manufacturing ozone-resistant no-sticker type pouches by using a laser processing device to adjust the inclination angle to create an outlet by processing a perforation line on the top of the pouch film, which can maintain ozone for a long time and lower the pouch production cost. It relates to wet tissues using water and their manufacturing method.
일반적으로 물티슈는 합성섬유, 비스코스 섬유, 면 섬유, 셀룰로즈 섬유, 천연 식물성 섬유 등을 얇게 조직화하여 티슈(tissue)로 만들고, 여기에 물을 첨가하고 살균한 것으로서, 장소에 관계없이 사용자의 손과 얼굴 등을 닦을 수 있으며, 근래에 들어서는 영유아의 기저귀 교체시 영유아의 피부를 닦는데도 사용되고 있다.In general, wet tissues are made by thinly organizing synthetic fibers, viscose fibers, cotton fibers, cellulose fibers, natural vegetable fibers, etc. into tissues, adding water to them and sterilizing them, so they can be used on the user's hands and face regardless of location. It can be used to wipe the back, and in recent years, it has also been used to wipe the skin of infants and young children when changing their diapers.
물티슈는 미생물에 취약한 제품이므로, 미생물을 제어하기 위하여 화학 물질인 살균제를 사용하고 있다. 하지만, 이 살균제는 살생 물질로서 미생물에 독성을 가지는 만큼 인체에도 좋지 않은 영향을 줄 수가 있다. Wet tissues are products vulnerable to microorganisms, so chemical disinfectants are used to control microorganisms. However, as this disinfectant is a biocidal substance and is toxic to microorganisms, it can have a negative effect on the human body.
참고로, 대한민국 공개특허공보 공개번호 10-2015-0107687호(공개일자 2015년 09월 23일)의 "살균 물티슈 공급장치 및 방법"에는, 2장의 티슈를 각각 안내하여 상기 티슈를 진행시키는 티슈 진행 단계와, 상기 진행수단에 의해 안내되면서 진행되는 상기 2장의 티슈 사이에 차아염소산이 함유된 살균 용액을 용액 공급부로부터 공급하는 용액 공급 단계를 포함하여 구성된 것을 특징으로 하는 살균 물티슈 공급 방법이 개시된 바 있다.For reference, in Korean Patent Publication No. 10-2015-0107687 (publication date September 23, 2015), “Sterilizing Wet Tissue Supply Apparatus and Method,” a tissue advance method of guiding two tissues each and advancing the tissues. A sterilizing wet tissue supply method has been disclosed, which includes a solution supply step of supplying a sterilizing solution containing hypochlorous acid from a solution supply unit between the two tissues guided by the progress means. .
차아염소산(HOCl)은 수소과산화물로 알려진 살균용액의 주요 성분 중 하나이고, 수소과산화물은 미생물을 제거하는데 강력한 항균 특성을 가지고 있지만, 인체에 높은 농도로 노출될 때 일시적으로 특정 부위에서의 가려움, 홍조 또는 눈물 등의 가벼운 피부 자극이 발생할 수 있는 문제점이 있다.Hypochlorous acid (HOCl) is one of the main ingredients of the sterilizing solution known as hydrogen peroxide. Hydrogen peroxide has strong antibacterial properties in eliminating microorganisms, but when exposed to high concentrations in the human body, it temporarily causes itching and flushing in certain areas. Alternatively, there is a problem that mild skin irritation such as tears may occur.
본 발명의 목적은 상기한 바와 같은 종래의 문제점을 해결하기 위한 것으로서, 오존 살균수를 이용하여 물티슈를 제조함으로써 화학 살균제를 쓰지 않고도 모든 균을 죽일 수 있음과 동시에 개봉후 대기에 노출되고 나면 반감기가 짧아서 빨리 분해되어 버리기 때문에 인체에 거의 영향을 주지 않는, 오존 살균수를 이용한 물티슈 및 그의 제조방법을 제공하는 데 있다. The purpose of the present invention is to solve the conventional problems as described above. By manufacturing wet tissues using ozone sterilizing water, all germs can be killed without using chemical disinfectants, and at the same time, the half-life after opening and exposure to the atmosphere is low. The aim is to provide wet tissues using ozone sterilizing water that have little effect on the human body because they are short and decompose quickly, and a method of manufacturing the same.
본 발명의 다른 목적은, 선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET 필름의 이중층으로 이루어진 파우치 필름을 이용하여 다층구조 오존저항성 필름을 제작함과 동시에, 레이저광의 경사각 조절을 위한 레이저 가공장치를 이용하여 파우치 필름의 상부에 절취선을 가공하여 출구를 형성하는 방법으로 오존 저항성 노스티커 타입 파우치를 제작함으로써 오존을 오랫동안 유지할 수 있으며 파우치 제작단가를 낮출 수 있는, 오존 살균수를 이용한 물티슈 및 그의 제조방법을 제공하는 데 있다. Another object of the present invention is to produce a multi-layered ozone-resistant film using a pouch film composed of a double layer of a linear low-density polyethylene (LLDPE) film and a cured PET film, and at the same time, using a laser processing device to adjust the inclination angle of the laser light. We provide a wet tissue using ozone sterilizing water and a manufacturing method thereof that can maintain ozone for a long time and lower the pouch production cost by producing an ozone-resistant no-sticker type pouch by processing a perforation line on the top of the pouch film to form an outlet. It's in doing it.
상기한 목적을 달성하기 위한 수단으로서 본 발명의 방법의 구성은, 오존 발생기를 사용하여 오존을 생성하는 단계와, 오존을 물에 용해시켜서 오존 살균수를 제조하는 단계와, 오존 살균수에 물티슈용 원단을 침지하여 살균하는 단계와, 오존과의 반응이 적은 선형저밀도폴리에틸렌(LLDPE) 필름을 준비하는 단계와, 상기 선형저밀도폴리에틸렌(LLDPE) 필름을 고온 처리하여 오존 저항성을 높이는 단계와, 상기 선형저밀도폴리에틸렌(LLDPE) 필름에 경화 PET 필름을 열압하여 다층구조 오존저항성 필름을 제작하는 단계와, 오존 저항성 노스티커 타입 파우치를 제작하는 단계와, 오존 저항성 노스티커 타입 파우치를 이용하여 패키징하는 단계를 포함하여 이루어지면 바람직하다.As a means to achieve the above object, the method of the present invention includes the steps of generating ozone using an ozone generator, dissolving ozone in water to prepare ozone sterilizing water, and applying wet tissue to the ozone sterilizing water. sterilizing the fabric by immersing it, preparing a linear low-density polyethylene (LLDPE) film that has little reaction with ozone, treating the linear low-density polyethylene (LLDPE) film at high temperature to increase ozone resistance, and Including the steps of producing a multi-layered ozone-resistant film by hot-pressing a cured PET film on a polyethylene (LLDPE) film, producing an ozone-resistant no-sticker type pouch, and packaging using an ozone-resistant no-sticker type pouch. It is desirable if it is accomplished.
본 발명의 방법의 구성은, 상기 선형저밀도폴리에틸렌(LLDPE) 필름을 고온 처리하는 단계는, 선형저밀도폴리에틸렌(LLDPE) 필름의 표면에 플라즈마 가스를 가하여 표면처리를 하는 단계와, 상기 선형저밀도폴리에틸렌(LLDPE) 필름을 진공 환경에서 327~380°C로 2시간 이상 가열하는 단계를 포함하여 이루어지면 바람직하다.The method of the present invention includes the steps of treating the linear low-density polyethylene (LLDPE) film at a high temperature by applying plasma gas to the surface of the linear low-density polyethylene (LLDPE) film, and performing surface treatment on the surface of the linear low-density polyethylene (LLDPE) film. ) It is preferable if it includes the step of heating the film at 327-380°C in a vacuum environment for more than 2 hours.
본 발명의 구성은, 상기 오존 저항성 노스티커 타입 파우치를 제작하는 단계는, 선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET 필름의 이중층으로 이루어진 파우치 필름을 준비하는 단계와. 레이저 가공장치를 이용하여 레이저광의 조사각도가 경사각을 형성하도록 조절하는 단계와, 경사각의 레이저광을 이용하여 파우치 필름의 상부에 절취선을 가공함으로써 출구가 형성되도록 하는 단계를 포함하여 이루어지면 바람직하다.The configuration of the present invention includes preparing a pouch film made of a double layer of a linear low-density polyethylene (LLDPE) film and a cured PET film. It is preferable to include the steps of adjusting the irradiation angle of the laser light to form an inclined angle using a laser processing device, and processing a perforation line on the upper part of the pouch film using the laser light at an inclined angle to form an exit.
본 발명의 방법의 구성은, 상기 레이저 가공장치는 절취선을 가공함에 있어서 레이저광의 조사각도를 경사각으로 조절하여 경화 PET 필름의 깊이까지 절삭한 뒤에 선형저밀도폴리에틸렌(LLDPE) 필름의 깊이 일부까지 절삭하면 바람직하다.The configuration of the method of the present invention is that the laser processing device adjusts the irradiation angle of the laser light to the inclination angle when processing the cut line, cuts to the depth of the cured PET film, and then cuts to a part of the depth of the linear low-density polyethylene (LLDPE) film. do.
본 발명의 방법의 구성은, 상기 선형저밀도폴리에틸렌(LLDPE) 필름에 경화 PET(Polyethylene Terephthalate) 필름을 열압하여 다층구조 오존저항성 필름을 제작하는 단계에서, 선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET(Polyethylene Terephthalate) 필름의 사이에 R-CCP 혹은 G-PET중에서 선택되는 어느 하나를 추가로 합지하면 바람직하다.The configuration of the method of the present invention is to produce a multi-layered ozone-resistant film by hot-pressing a cured PET (Polyethylene Terephthalate) film on the linear low-density polyethylene (LLDPE) film, and the cured PET (Polyethylene Terephthalate) film. It is desirable to additionally laminate either R-CCP or G-PET between the terephthalate (Terephthalate) films.
본 발명의 구성은, 상기 오존 저항성 노스티커 타입 파우치를 제작하는 단계는, 선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET(Polyethylene Terephthalate) 필름의 사이에 R-CCP 혹은 G-PET가 추가로 합지된 필름을 준비하는 단계와. 레이저 가공장치를 이용하여 레이저광의 조사각도가 경사각을 형성하도록 조절하는 단계와, 경사각의 레이저광을 이용하여 파우치 필름의 상부에 절취선을 가공함으로써 출구가 형성되도록 하는 단계를 포함하여 이루어지면 바람직하다.The configuration of the present invention is that the step of manufacturing the ozone-resistant no-sticker type pouch is a film in which R-CCP or G-PET is additionally laminated between a linear low-density polyethylene (LLDPE) film and a cured PET (Polyethylene Terephthalate) film. Steps to prepare and. It is preferable to include the steps of adjusting the irradiation angle of the laser light to form an inclined angle using a laser processing device, and processing a perforation line on the upper part of the pouch film using the laser light at an inclined angle to form an exit.
본 발명의 방법의 구성은, 상기 레이저 가공장치는 절취선을 가공함에 있어서 레이저광의 조사각도를 경사각으로 조절하여 경화 PET(Polyethylene Terephthalate) 필름의 깊이까지 절삭하고, R-CCP 혹은 G-PET도 절삭한 뒤에, 선형저밀도폴리에틸렌(LLDPE) 필름의 깊이 일부까지 절삭하면 바람직하다. The configuration of the method of the present invention is that the laser processing device cuts to the depth of the cured PET (Polyethylene Terephthalate) film by adjusting the irradiation angle of the laser light to the inclination angle when processing the cutting line, and also cuts R-CCP or G-PET. Later, it is desirable to cut to a portion of the depth of the linear low-density polyethylene (LLDPE) film.
본 발명의 방법의 구성은, 상기 레이저 가공장치는, 레이저 광원으로부터 입사되는 레이저광의 조사각도를 가변시키기 위한 렌즈부와, 상기 렌즈부를 수평이동시키기 위한 수평이동부와, 상기 렌즈부와 수평이동부를 승하강시키기 위한 승하강부와, 상기 렌즈부를 지지하기 위한 지지부를 포함하며; 상기 승하강부는, 지지판과, 상기 지지판의 상부에 설치되는 구동모터와, 상기 구동모터의 회전축에 연결되는 스크류바와, 상기 스크류바의 후면에 설치되는 지지바와, 상기 구동모터와 지지바의 하부를 감싸면서 설치되는 케이싱과, 상기 스크류바와 지지바의 상부에 설치되는 고정판과, 상기 스크류바에 나사결합되어 승하강 운동을 하는 승하강 부재와, 상기 지지바에 설치되어 승하강 부재와 연결됨으로써 승하강 부재와 함께 승하강 운동을 하면서 승하강 부재의 회전을 방지하는 회전방지돌기를 포함하며; 상기 수평이동부는, 상기 승하강부의 승하강 부재에 연결 설치되는 실린더와, 상기 실린더에 일단이 연결되어 있으며 타측에 고정링이 인입되는 연결부재와, 상기 연결부재의 상부에 설치되어 하부가 연결부재의 상부면에 나사결합되며 조임 회전에 따라 하강되며 고정링을 가압 고정하는 고정구를 포함하며; 상기 지지부는, 하부가 지지판에 고정되는 지주와, 상기 지주의 외측으로 상하 이동 가능하게 결합되는 이동부재와, 상기 이동부재에 일측이 고정되고 타측에 고정링의 일측이 안착되는 지지부재와, 상기 지주로부터 이동부재를 지지하는 조절구를 포함하여 이루어지면 바람직하다.The configuration of the method of the present invention is that the laser processing device includes a lens unit for changing the irradiation angle of the laser light incident from the laser light source, a horizontal moving unit for horizontally moving the lens unit, and the lens unit and the horizontal moving unit. It includes a lifting part for raising and lowering, and a support part for supporting the lens part; The raising and lowering unit includes a support plate, a drive motor installed on an upper part of the support plate, a screw bar connected to the rotation axis of the drive motor, a support bar installed on the rear of the screw bar, and a lower part of the drive motor and the support bar. A casing installed while surrounding, a fixing plate installed on the upper part of the screw bar and the support bar, a lifting member that is screwed to the screw bar and moves up and down, and a lifting member that is installed on the support bar and connected to the lifting member. It includes an anti-rotation protrusion that prevents rotation of the raising and lowering member while moving up and down with it; The horizontal movable part includes a cylinder connected to and installed on the elevating member of the elevating lowering part, a connecting member one end of which is connected to the cylinder and a fixing ring inserted into the other side, and a lower part installed on the upper part of the connecting member and connected to the lower part. It is screwed to the upper surface of the member, lowers as the tightening rotation, and includes a fixture that pressurizes and secures the retaining ring; The support part includes a support member whose lower part is fixed to a support plate, a moving member movable upward and downward to the outside of the support member, a support member on one side of which is fixed to the moving member and one side of a fixing ring is seated on the other side, and It is desirable if it includes an adjustment device that supports the moving member from the support.
본 발명의 방법의 구성은, 상기 렌즈부는, 레이저광을 조사각도를 가변시키기 위한 렌즈와, 좌우 한 쌍의 고정링유닛으로 분리되어 상기 렌즈의 테두리를 감싸는 고정링과, 상기 한쌍의 고정링유닛을 회동 가능하게 연결하기 위한 절첩부재와, 상기 한쌍의 고정링유닛을 결속하기 위한 체결수단을 포함하여 이루어지면 바람직하다.The configuration of the method of the present invention is that the lens unit includes a lens for varying the irradiation angle of the laser light, a fixed ring that is separated into a pair of left and right fixed ring units and surrounds the edge of the lens, and the pair of fixed ring units. It is preferable that it includes a folding member for rotatably connecting and a fastening means for fastening the pair of fixing ring units.
본 발명은, 오존 살균수를 이용하여 물티슈를 제조함으로써 화학 살균제를 쓰지 않고도 모든 균을 죽일 수 있음과 동시에 개봉후 대기에 노출되고 나면 반감기가 짧아서 빨리 분해되어 버리기 때문에 인체에 거의 영향을 주지 않으며, 선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET 필름의 이중층으로 이루어진 파우치 필름을 이용하여 다층구조 오존저항성 필름을 제작함과 동시에, 레이저광의 경사각 조절을 위한 레이저 가공장치를 이용하여 파우치 필름의 상부에 절취선을 가공하여 출구를 형성하는 방법으로 오존 저항성 노스티커 타입 파우치를 제작함으로써 오존을 오랫동안 유지할 수 있으며 파우치 제작단가를 낮출 수 있는, 효과를 갖는다.The present invention manufactures wet tissues using ozone sterilizing water, which kills all germs without using chemical disinfectants. At the same time, it has a short half-life and decomposes quickly after opening and exposure to the atmosphere, so it has little effect on the human body. A multi-layered ozone-resistant film was produced using a pouch film made of a double layer of linear low-density polyethylene (LLDPE) film and a cured PET film, and a perforation line was created on the top of the pouch film using a laser processing device to adjust the inclination angle of the laser beam. By manufacturing an ozone-resistant no-sticker type pouch by processing it to form an outlet, ozone can be maintained for a long time and the pouch production cost can be reduced.
도 1은 본 발명의 일 실시예에 따른 오존 살균수를 이용한 물티슈의 제조방법의 공정 순서도이다.
도 2는 본 발명의 일 실시예에 따른 오존 살균수를 이용한 물티슈의 오존 저항성 노스티커 타입 파우치의 구성도이다.
도 3은 본 발명의 일 실시예에 따른 레이저광의 경사각 조절을 위한 레이저 가공장치의 구성도이다.
도 4는 본 발명의 일 실시예에 따른 레이저광의 경사각 조절을 위한 레이저 가공장치의 렌즈부의 분해 사시 구성도이다.Figure 1 is a process flow chart of a method for manufacturing wet tissues using ozone sterilizing water according to an embodiment of the present invention.
Figure 2 is a configuration diagram of an ozone-resistant no-sticker type pouch for wet tissues using ozone sterilizing water according to an embodiment of the present invention.
Figure 3 is a configuration diagram of a laser processing device for adjusting the inclination angle of laser light according to an embodiment of the present invention.
Figure 4 is an exploded perspective view of the lens portion of a laser processing device for adjusting the inclination angle of a laser beam according to an embodiment of the present invention.
이하, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명을 용이하게 실시할 수 있을 정도로 상세히 설명하기 위하여, 본 발명의 바람직한 실시예를 첨부된 도면을 참조로 하여 상세히 설명하기로 한다. 본 발명의 목적, 작용, 효과를 포함하여 기타 다른 목적들, 특징점들, 그리고 동작상의 이점들이 바람직한 실시예의 설명에 의해 보다 명확해질 것이다. Hereinafter, in order to explain the present invention in detail so that a person skilled in the art can easily practice the present invention, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. Other purposes, features, and operational advantages, including the purpose, operation, and effect of the present invention, will become clearer through the description of the preferred embodiment.
참고로, 여기에서 개시되는 실시예는 여러가지 실시가능한 예중에서 당업자의 이해를 돕기 위하여 가장 바람직한 실시예를 선정하여 제시한 것일 뿐, 본 발명의 기술적 사상이 반드시 제시된 실시예에만 의해서 한정되거나 제한되는 것은 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위내에서 균등물 내지 대체물들을 포함하는 다양한 변화와 부가 및 변경이 가능하다.For reference, the embodiments disclosed herein are merely presented by selecting the most preferred embodiments from among various possible embodiments to aid the understanding of those skilled in the art, and the technical idea of the present invention is not necessarily limited or restricted only to the presented embodiments. Rather, various changes, additions, and changes, including equivalents and substitutes, are possible without departing from the technical spirit of the present invention.
또한, 본원의 명세서 및 청구범위에 사용된 용어나 단어의 표현은, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 정의된 것으로서, 통상적이거나 사전적인 의미로만 한정해서 해석되어서는 아니되며, 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 일예로서, 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한 복수의 표현을 포함하며, 방향에 관한 표현은 설명상의 편의를 위하여 도면상에 표현된 위치를 기준으로 설정하며, "연결된다"거나 "설치된다"라는 표현은 직접적인 연결 또는 설치뿐만이 아니라 중간에 다른 구성요소를 매개로 하는 연결 또는 설치를 포함한다. In addition, the terms and expressions of words used in the specification and claims of the present application are defined based on the principle that the inventor can appropriately define the concept of the term in order to explain the invention in the best way. , it should not be construed as limited to the usual or dictionary meaning, but should be interpreted as meaning and concept consistent with the technical idea of the present invention. As an example, singular expressions include plural expressions unless the context clearly indicates otherwise, and expressions regarding direction are set based on the position expressed in the drawing for convenience of explanation, and are set as “connected” or “installed.” The expression “becomes possible” includes not only direct connection or installation, but also connection or installation through other intermediate components.
도 1은 본 발명의 일 실시예에 따른 오존 살균수를 이용한 물티슈의 제조방법의 공정 순서도이다.Figure 1 is a process flow chart of a method for manufacturing wet tissues using ozone sterilizing water according to an embodiment of the present invention.
도 1에 도시되어 있는 바와 같이, 본 발명의 일실시예에 따른 오존 살균수를 이용한 물티슈의 제조방법은, 오존 발생기를 사용하여 오존을 생성하는 단계(S10)와, 오존을 물에 용해시켜서 오존 살균수를 제조하는 단계(S20)와, 오존 살균수에 물티슈용 원단을 침지하여 살균하는 단계(S30)와, 오존과의 반응이 적은 선형저밀도폴리에틸렌(Linear Low-Density Polyethylene, LLDPE) 필름을 준비하는 단계(S40)와, 상기 선형저밀도폴리에틸렌(LLDPE) 필름을 고온 처리하여 오존 저항성을 높이는 단계(S50)와, 상기 선형저밀도폴리에틸렌(LLDPE) 필름에 경화 PET(Polyethylene Terephthalate) 필름을 열압하여 다층구조 오존저항성 필름을 제작하는 단계(S60)와, 오존 저항성 노스티커 타입 파우치를 제작하는 단계(S70)와, 오존 저항성 노스티커 타입 파우치를 이용하여 패키징하는 단계(S80)를 포함하여 이루어진다.As shown in Figure 1, the method of manufacturing wet tissues using ozone sterilizing water according to an embodiment of the present invention includes the steps of generating ozone using an ozone generator (S10) and dissolving ozone in water to produce ozone. A step of preparing sterilizing water (S20), a step of sterilizing the wet tissue fabric by immersing it in ozone sterilizing water (S30), and preparing a linear low-density polyethylene (LLDPE) film that has little reaction with ozone. (S40), treating the linear low-density polyethylene (LLDPE) film at a high temperature to increase ozone resistance (S50), and heat-pressing a cured PET (Polyethylene Terephthalate) film on the linear low-density polyethylene (LLDPE) film to form a multilayer structure. It includes a step of producing an ozone-resistant film (S60), a step of producing an ozone-resistant no-sticker type pouch (S70), and a step of packaging using an ozone-resistant no-sticker type pouch (S80).
상기 선형저밀도폴리에틸렌(LLDPE) 필름에 경화 PET(Polyethylene Terephthalate) 필름을 열압하여 다층구조 오존저항성 필름을 제작하는 단계(S60)에서, 선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET(Polyethylene Terephthalate) 필름의 사이에 R-CCP 혹은 G-PET를 추가로 합지할 수도 있다.In the step (S60) of producing a multi-layered ozone-resistant film by hot-pressing a cured PET (Polyethylene Terephthalate) film on the linear low-density polyethylene (LLDPE) film, between the linear low-density polyethylene (LLDPE) film and the cured PET (Polyethylene Terephthalate) film. You can additionally laminate R-CCP or G-PET.
상기 오존은 대기중에서 안정하지 않은 화합물로서, 일정 기간이 지나면 자외선 (UV-B, UV-C) 또는 자유 라디칼과 반응하여 산소 원자(O)와 산소 분자 (O2)로 분해되거나 반감기에 의해 감소하게 된다. 오존의 반감기는 특정 농도의 오존이 반으로 줄어드는데 걸리는 시간을 의미하는 것으로서, 대기 오존의 반감기는 환경 조건에 따라 다를 수 있으며, 주로 대기의 온도, 습도, 햇빛, 자외선 등에 의해 영향을 받는다. 일반적으로 대기의 반감기는 몇 분에서 몇 시간 정도로 짧은데, 이는 오존이 대기 중에서 비교적 빠르게 생성되고 분해되기 때문이다. The ozone is a compound that is not stable in the atmosphere, and after a certain period of time, it reacts with ultraviolet rays (UV-B, UV-C) or free radicals and decomposes into oxygen atoms (O) and oxygen molecules (O 2 ) or is reduced by half-life. I do it. The half-life of ozone refers to the time it takes for a certain concentration of ozone to be reduced by half. The half-life of atmospheric ozone can vary depending on environmental conditions and is mainly affected by atmospheric temperature, humidity, sunlight, and ultraviolet rays. In general, the atmospheric half-life is short, ranging from minutes to hours, because ozone is created and decomposed relatively quickly in the atmosphere.
상기 선형저밀도폴리에틸렌(LLDPE) 필름을 고온 처리하는 단계(S50)는, 선형저밀도폴리에틸렌(LLDPE) 필름의 표면에 플라즈마 가스를 가하여 표면처리를 하는 단계와, 상기 선형저밀도폴리에틸렌(LLDPE) 필름을 진공 환경에서 327~380°C로 2시간 이상 가열하는 단계를 포함하여 이루어진다.The step of treating the linear low-density polyethylene (LLDPE) film at high temperature (S50) includes surface treatment by applying plasma gas to the surface of the linear low-density polyethylene (LLDPE) film, and placing the linear low-density polyethylene (LLDPE) film in a vacuum environment. It includes the step of heating at 327-380°C for more than 2 hours.
상기 오존 저항성 노스티커 타입 파우치를 제작하는 단계(S70)는, 도 2에 도시되어 있는 바와 같이, 선형저밀도폴리에틸렌(LLDPE) 필름(112)과 경화 PET(Polyethylene Terephthalate) 필름(111)의 이중층으로 이루어진 파우치 필름(110)을 준비하는 단계와. 레이저 가공장치를 이용하여 레이저광의 조사각도가 경사각을 형성하도록 조절하는 단계와, 경사각의 레이저광을 이용하여 파우치 필름(110)의 상부에 절취선(114)을 가공함으로써 출구(113)가 형성되도록 하는 단계를 포함하여 이루어진다.As shown in FIG. 2, the step (S70) of manufacturing the ozone-resistant no-sticker type pouch consists of a double layer of a linear low-density polyethylene (LLDPE) film 112 and a cured PET (Polyethylene Terephthalate) film 111. Preparing the pouch film 110 and. A step of adjusting the irradiation angle of the laser light to form an inclination angle using a laser processing device, and forming an outlet 113 by processing a perforation line 114 on the upper part of the pouch film 110 using the laser light at an inclination angle. It includes steps.
상기 선형저밀도폴리에틸렌(LLDPE) 필름(112)과 경화 PET(Polyethylene Terephthalate) 필름(111)의 이중층으로 이루어진 파우치 필름(110)을 준비하는 단계에서는, 선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET(Polyethylene Terephthalate) 필름의 사이에 R-CCP 혹은 G-PET가 추가로 합지된 필름을 사용할 수도 있다.In the step of preparing the pouch film 110 made of a double layer of the linear low-density polyethylene (LLDPE) film 112 and the cured PET (Polyethylene Terephthalate) film 111, the linear low-density polyethylene (LLDPE) film and the cured PET (Polyethylene Terephthalate) film 111 are prepared. ) You can also use a film with R-CCP or G-PET additionally laminated between the films.
상기 레이저 가공장치는 절취선(114)을 가공함에 있어서 레이저광의 조사각도를 경사각으로 조절하여 경화 PET(Polyethylene Terephthalate) 필름(111)의 깊이까지 절삭한 뒤에 선형저밀도폴리에틸렌(LLDPE) 필름(112)의 깊이 일부까지 절삭함으로써 사용자가 출구(113)를 쉽게 박리할 수 있도록 하고, 사용자가 출구(113)의 일부만을 박리한 경우에는 입구(113)의 나머지 부분이 파우치 필름(110)에 연결된 상태를 유지할 수 있도록 한다.When processing the cutting line 114, the laser processing device adjusts the irradiation angle of the laser light to the inclination angle to cut to the depth of the cured PET (Polyethylene Terephthalate) film 111 and then to the depth of the linear low-density polyethylene (LLDPE) film 112. By cutting to a portion, the user can easily peel off the outlet 113, and if the user peels off only part of the outlet 113, the remaining part of the inlet 113 can remain connected to the pouch film 110. Let it happen.
선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET(Polyethylene Terephthalate) 필름의 사이에 R-CCP 혹은 G-PET가 추가로 합지된 필름을 사용하는 경우에는 경화 PET(Polyethylene Terephthalate) 필름(111)의 깊이까지 절삭하고, R-CCP 혹은 G-PET도 절삭한 뒤에 선형저밀도폴리에틸렌(LLDPE) 필름(112)의 깊이 일부까지 절삭하게 된다. When using a film in which R-CCP or G-PET is additionally laminated between a linear low-density polyethylene (LLDPE) film and a cured PET (Polyethylene Terephthalate) film, cut to the depth of the cured PET (Polyethylene Terephthalate) film (111). And, after cutting R-CCP or G-PET, the linear low density polyethylene (LLDPE) film 112 is cut to a portion of its depth.
도 3은 본 발명의 일 실시예에 따른 레이저광의 경사각 조절을 위한 레이저 가공장치의 구성도이다.Figure 3 is a configuration diagram of a laser processing device for adjusting the inclination angle of laser light according to an embodiment of the present invention.
도 3에 도시되어 있는 바와 같이 본 발명의 일 실시예에 따른 레이저광의 경사각 조절을 위한 레이저 가공장치는, 레이저 광원(도시되지 않음)으로부터 입사되는 레이저광의 조사각도를 가변시키기 위한 렌즈부(240)와, 상기 렌즈부(240)를 수평이동시키기 위한 수평이동부(290)와, 상기 렌즈부(240)와 수평이동부(290)를 승하강시키기 위한 승하강부(270)와, 상기 렌즈부(240)를 지지하기 위한 지지부(280)를 포함하여 이루어진다.As shown in FIG. 3, the laser processing device for adjusting the inclination angle of laser light according to an embodiment of the present invention includes a lens unit 240 for varying the irradiation angle of laser light incident from a laser light source (not shown). and a horizontal moving unit 290 for horizontally moving the lens unit 240, an elevating and lowering unit 270 for raising and lowering the lens unit 240 and the horizontal moving unit 290, and the lens unit ( It includes a support portion 280 for supporting 240).
상기 승하강부(270)는, 지지판(271)과, 상기 지지판(271)의 상부에 설치되는 구동모터(272)와, 상기 구동모터(272)의 회전축에 연결되는 스크류바(276)와, 상기 스크류바(276)의 후면에 설치되는 지지바(275)와, 상기 구동모터(272)와 지지바(273)의 하부를 감싸면서 설치되는 케이싱(273)과, 상기 스크류바(276)과 지지바(275)의 상부에 설치되는 고정판(274)과, 상기 스크류바(276)에 나사결합되어 승하강 운동을 하는 승하강 부재(277)와, 상기 지지바(278)에 설치되어 승하강 부재(277)와 연결됨으로써 승하강 부재(277)와 함께 승하강 운동을 하면서 승하강 부재(277)의 회전을 방지하는 회전방지돌기(278)을 포함하여 이루어진다.The raising and lowering unit 270 includes a support plate 271, a drive motor 272 installed on the top of the support plate 271, a screw bar 276 connected to the rotation axis of the drive motor 272, and the A support bar 275 installed on the rear of the screw bar 276, a casing 273 installed surrounding the lower part of the drive motor 272 and the support bar 273, and a support bar 276 and the screw bar 276. A fixing plate 274 installed on the upper part of the bar 275, a lifting member 277 that is screwed to the screw bar 276 and moves up and down, and a lifting member 277 installed on the support bar 278. It includes a rotation prevention protrusion 278 that is connected to (277) and prevents rotation of the raising and lowering member 277 while moving up and down with the lifting member 277.
상기 지지판(271)은 일정 면적을 가지면서 실내 바닥면 등에 설치될 수 있다.The support plate 271 has a certain area and can be installed on an indoor floor, etc.
상기 구동모터(272)는 외부로부터 인가되는 전원에 의해 구동되면서 스크류바(276)를 회전시켜 승강부재(277)가 승하강되도록 한다.The drive motor 272 is driven by power applied from the outside and rotates the screw bar 276 to raise and lower the lifting member 277.
상기 케이싱(273)은 하부가 개방되는 통 형태를 이루면서 하부가 지지판(271)의 상면에 고정될 수 있다.The casing 273 has a cylindrical shape with the lower part open, and the lower part may be fixed to the upper surface of the support plate 271.
상기 스크류바(276)는 외주면에 나사산이 형성되며 케이싱(273)에 설치되는 베어링 등에 의해 회전 가능하게 고정된다.The screw bar 276 has threads formed on its outer peripheral surface and is rotatably fixed by a bearing installed in the casing 273.
상기 승하강부재(277)는 링 형태를 이루면서 내주면에 나사산이 형성되어 스크류바(276)와 나사결합되면서 스크류바(276)의 회전에 따라 상하 이동된다.The raising and lowering member 277 has a ring shape and has screw threads formed on its inner peripheral surface, is screwed to the screw bar 276, and moves up and down as the screw bar 276 rotates.
상기 회전방지돌기(278)는 일단부가 승강부재(277)에 고정되고 타단부로 지지바(275)가 통과되면서 구동모터(272)의 회전에 따른 승강부재(277)의 회전을 방지하면서 승하강부재(277)의 상하 이동을 가이드할 수 있다.The rotation prevention protrusion 278 has one end fixed to the lifting member 277 and the other end through which the support bar 275 passes, preventing rotation of the lifting member 277 due to the rotation of the driving motor 272 and moving up and down. The vertical movement of the member 277 can be guided.
상기 수평이동부(290)는, 상기 승하강부(270)의 승하강 부재(277)에 연결 설치되는 실린더(293)와, 상기 실린더(293)에 일단이 연결되어 있으며 타측에 고정링(241)이 인입되는 연결부재(291)와, 상기 연결부재(291)의 상부에 설치되어 하부가 연결부재(291)의 상부면에 나사결합되며 조임 회전에 따라 하강되며 고정링(241)을 가압 고정하는 고정구(292)를 포함하여 이루어진다.The horizontal moving part 290 includes a cylinder 293 connected to the elevating member 277 of the elevating and lowering part 270, one end of which is connected to the cylinder 293, and a fixing ring 241 on the other side. This incoming connecting member 291 is installed on the upper part of the connecting member 291, and the lower part is screwed to the upper surface of the connecting member 291, and is lowered according to the tightening rotation and pressurizes and secures the retaining ring 241. It includes a fixture (292).
상기 연결부재(291)는 일측이 개방되는 'ㄷ'자 형태를 이루면서 내측으로 고정링(241)의 타측이 인입된다.The connecting member 291 forms a 'L' shape with one side open, and the other side of the fixing ring 241 is drawn inward.
상기 고정구(292)는 연결부재(291)의 상부에 나사결합되면서 조임 회전에 따라 하강되며 고정링(241)을 가압 고정한다.The fixture 292 is screwed to the upper part of the connecting member 291, lowers as it tightens and rotates, and presses and secures the retaining ring 241.
상기 실린더(293)는 구동에 따라 연결부재(291)와 함께 렌즈부(240)가 직선 이동될 수 있도록 하여 렌즈부(240)의 적정 위치가 조절될 수 있도록 한다.The cylinder 293 allows the lens unit 240 to move in a straight line together with the connecting member 291 when driven, so that the appropriate position of the lens unit 240 can be adjusted.
상기 지지부(280)는, 하부가 지지판(271)에 고정되는 지주(281)와, 상기 지주(281)의 외측으로 상하 이동 가능하게 결합되는 이동부재(282)와, 상기 이동부재(282)에 일측이 고정되고 타측에 고정링(241)의 일측이 안착되는 지지부재(283)와, 상기 지주(281)로부터 이동부재(282)를 지지하는 조절구(284)를 포함하여 이루어진다.The support portion 280 includes a strut 281 whose lower part is fixed to the support plate 271, a moving member 282 coupled to the outside of the strut 281 so as to be movable up and down, and the moving member 282. It includes a support member 283 on which one side is fixed and one side of the fixing ring 241 is seated on the other side, and an adjuster 284 that supports the moving member 282 from the support 281.
상기 지주(281)는 외주면에 나사산이 형성되며, 상기 조절구(274)는 내주면에 나사산이 형성되어 지주(281)와 나사결합된다.The strut 281 has threads formed on its outer circumferential surface, and the adjustment tool 274 has threads formed on its inner circumferential surface and is screwed to the strut 281.
상기 이동부재(282)는 원통 형태를 이루면서 지주(281)의 외측으로 상하 이동 가능하게 결합된다.The moving member 282 has a cylindrical shape and is coupled to the outside of the support 281 to be able to move up and down.
상기 이동부재(282)는 렌즈부(240)보다 하부에 위치된 상태에서 구동모터(272)의 구동에 따라 렌즈부(240)의 높이 위치가 조절되면 위로 승강되며, 이에 따라 지지부재(283)에 고정링(242)의 일측이 안착되도록 할 수 있다.The moving member 282 is positioned lower than the lens unit 240 and is lifted upward when the height position of the lens unit 240 is adjusted according to the driving of the driving motor 272, and thus the support member 283 One side of the fixing ring 242 can be seated.
상기 조절구(284)는, 지지부재(283)에 고정링(2412의 일측이 안착되면, 회전에 따라 승강되면서 이동부재(282)와 접하게 되면서 이동부재(282)를 고정시키게 된다.When one side of the fixing ring 2412 is seated on the support member 283, the adjuster 284 moves up and down as it rotates and comes into contact with the moving member 282, thereby fixing the moving member 282.
도 4는 본 발명의 일 실시예에 따른 레이저광의 경사각 조절을 위한 레이저 가공장치의 렌즈부의 분해 사시 구성도이다.Figure 4 is an exploded perspective view of the lens portion of a laser processing device for adjusting the inclination angle of a laser beam according to an embodiment of the present invention.
도 4에 도시되어 있는 바와 같이 본 발명의 일 실시예에 따른 레이저광의 경사각 조절을 위한 레이저 가공장치의 렌즈부(240)는, 레이저광을 조사각도를 가변시키기 위한 렌즈(241)와, 좌우 한 쌍의 고정링유닛으로 분리되어 상기 렌즈(241)의 테두리를 감싸는 고정링(242)과, 상기 한쌍의 고정링유닛을 회동 가능하게 연결하기 위한 절첩부재(243)과, 상기 한쌍의 고정링유닛을 결속하기 위한 체결수단(244)을 포함하여 이루어진다.As shown in FIG. 4, the lens unit 240 of the laser processing device for adjusting the inclination angle of the laser light according to an embodiment of the present invention includes a lens 241 for varying the irradiation angle of the laser light, and one left and right A fixing ring 242 that is separated into a pair of fixing ring units and surrounds the edge of the lens 241, a folding member 243 for rotatably connecting the pair of fixing ring units, and a pair of fixing ring units. It includes a fastening means 244 for binding.
상기 고정링(242)은 내주면에 'ㄷ'자 형태에 인입홈(242a)이 형성되면서 내측으로 렌즈(241)의 가장자리가 인입되며 고정되도록 할 수 있다.The fixing ring 242 has a 'ㄷ' shaped recess groove 242a formed on its inner circumferential surface so that the edge of the lens 241 can be retracted and fixed to the inside.
상기 고정링(242)은 좌우 한 쌍의 고정링유닛으로 분리되어 일단부가 절첩부재(243)에 의해 회동 가능하게 연결되고 타단부가 체결수단(244)에 의해 결속된다.The fixing ring 242 is divided into a pair of left and right fixing ring units, one end of which is rotatably connected by a folding member 243, and the other end of which is fastened by a fastening means 244.
상기 절첩부재(243)는 경첩 등으로 이루어질 수 있다.The folding member 243 may be made of a hinge or the like.
상기 체결수단(244)은, 한 쌍의 고정링유닛의 타단부로부터 외측으로 돌출되는 한 쌍의 체결돌기(244a)와, 한 쌍의 체결돌기(244a)의 외측으로 나사결합되는 체결부재(244b)를 포함하여 이루어진다.The fastening means 244 includes a pair of fastening protrusions 244a protruding outward from the other end of the pair of fixing ring units, and a fastening member 244b screwed to the outside of the pair of fastening protrusions 244a. ), including.
상기 한 쌍의 체결돌기(244a)는 대향되는 일면이 평면을 이루고 배향되는 타면이 반원을 이루면서 상호 접함에 따라 원기둥 형태를 형성한다.The pair of fastening protrusions 244a form a cylindrical shape as one opposing surface is flat and the other oriented surface contacts each other to form a semicircle.
상기 체결부재(244b)는 한 쌍의 체결돌기(244a)의 외주면으로 나사결합되면서 한 쌍의 고정링유닛을 결속하는 한편, 인입홈(241a)으로 결합된 렌즈(241)를 고정할 수 있다.The fastening member 244b is screwed to the outer peripheral surface of the pair of fastening protrusions 244a to fasten a pair of fixing ring units, and can fix the lens 241 coupled to the recess groove 241a.
상기한 구성에 의한, 본 발명의 일실시예에 따른 오존 살균수를 이용한 물티슈 및 그의 제조방법의 작용은 다음과 같다.The operation of the wet tissue using ozone sterilizing water and its manufacturing method according to an embodiment of the present invention according to the above configuration is as follows.
먼저, 오존 발생기를 사용하여 오존을 생성한다(S10). 오존 발생기는 공기 또는 산소를 이용하여 오존을 생성하는 장치로서, 일반적으로 강력한 전기 방전을 이용하여 산소 분자를 산소 원자와 결합시켜 오존을 생성한다.First, ozone is generated using an ozone generator (S10). An ozone generator is a device that generates ozone using air or oxygen. It generally creates ozone by combining oxygen molecules with oxygen atoms using a strong electric discharge.
다음에, 오존을 물에 용해시켜서 오존 살균수를 제조한다(S20).Next, ozone is dissolved in water to prepare ozone sterilizing water (S20).
이어서, 오존 살균수에 물티슈용 원단을 침지하여 살균을 한다(S30).Next, the wet tissue fabric is sterilized by immersing it in ozone sterilizing water (S30).
다음에, 오존과의 반응이 적은 선형저밀도폴리에틸렌(LLDPE) 필름을 준비한다(S40). Next, prepare a linear low-density polyethylene (LLDPE) film that has little reaction with ozone (S40).
이어서, 상기 선형저밀도폴리에틸렌(LLDPE) 필름을 고온 처리하여 폴리머의 구조를 강화시켜 오존과의 반응을 최소화시킴으로써 오존 저항성을 더욱 높여준다(S50). Next, the linear low-density polyethylene (LLDPE) film is treated at high temperature to strengthen the polymer structure and minimize reaction with ozone to further increase ozone resistance (S50).
다음에, 선형저밀도폴리에틸렌(LLDPE) 필름에 경화 PET(Polyethylene Terephthalate) 필름을 열압하여 다층구조 오존저항성 필름을 제작한다(S60). Next, a multilayer ozone-resistant film is produced by hot-pressing a cured PET (Polyethylene Terephthalate) film on a linear low-density polyethylene (LLDPE) film (S60).
이어서, 선형저밀도폴리에틸렌(LLDPE) 필름(112)과 경화 PET(Polyethylene Terephthalate) 필름(111)의 이중층으로 이루어진 파우치 필름(110)을 준비한 후, 레이저 가공장치를 이용하여 레이저광의 조사각도가 경사각을 형성하도록 조절하면서 경사각의 레이저광을 이용하여 파우치 필름(110)의 상부에 절취선(114)을 가공함으로써 출구(113)가 형성되도록 하여 오존 저항성 노스티커 타입 파우치를 제작한다(S70).Next, after preparing the pouch film 110 made of a double layer of a linear low-density polyethylene (LLDPE) film 112 and a cured PET (Polyethylene Terephthalate) film 111, the irradiation angle of the laser light forms an inclination angle using a laser processing device. An ozone-resistant no-sticker type pouch is manufactured by processing a perforation line 114 on the upper part of the pouch film 110 using laser light at an inclined angle to form an outlet 113 (S70).
다음에, 오존 살균수로 살균된 물티슈용 원단을 상기 오존 저항성 노스티커 타입 파우치를 이용하여 패키징을 한다(S80). 상기 오존 저항성 노스티커 타입 파우치는 오존의 투과를 방지할 뿐만 아니라 산소의 투과를 낮추어 줌으로써 파우치내의 오존의 농도를 장기간 유지할 수 있도록 한다.Next, the wet tissue fabric sterilized with ozone sterilizing water is packaged using the ozone-resistant no-sticker type pouch (S80). The ozone-resistant no-sticker type pouch not only prevents the penetration of ozone, but also reduces the penetration of oxygen, thereby maintaining the concentration of ozone in the pouch for a long period of time.
사용자가 오존 저항성 노스티커 타입 파우치의 상부에 형성되어 있는 절취선(114)을 이용하여 출구(113)를 개방하게 되면, 오존이 대기와 접촉하게 되면서 반감기가 짧아서 빨리 분해되어 버리기 때문에 인체에 거의 영향을 주지 않게 된다.When the user opens the outlet 113 using the perforated line 114 formed on the top of the ozone-resistant no-sticker type pouch, ozone comes into contact with the atmosphere and is quickly decomposed due to its short half-life, so it has little effect on the human body. It will not be given.
240 : 렌즈부 270 : 승하강부
280 : 지지부 290 : 수평이동부240: Lens unit 270: Elevation and lowering unit
280: support part 290: horizontal moving part
Claims (10)
오존을 물에 용해시켜서 오존 살균수를 제조하는 단계와,
오존 살균수에 물티슈용 원단을 침지하여 살균하는 단계와,
오존과의 반응이 적은 선형저밀도폴리에틸렌(LLDPE) 필름을 준비하는 단계와,
상기 선형저밀도폴리에틸렌(LLDPE) 필름을 고온 처리하여 오존 저항성을 높이는 단계와,
상기 선형저밀도폴리에틸렌(LLDPE) 필름에 경화 PET(Polyethylene Terephthalate) 필름을 열압하여 다층구조 오존저항성 필름을 제작하는 단계와,
오존 저항성 노스티커 타입 파우치를 제작하는 단계와,
오존 저항성 노스티커 타입 파우치를 이용하여 패키징하는 단계를 포함하여 이루어지는 것을 특징으로 하는 오존 살균수를 이용한 물티슈의 제조방법. generating ozone using an ozone generator;
Dissolving ozone in water to produce ozone sterilization water;
A step of sterilizing the wet tissue fabric by immersing it in ozone sterilizing water,
Preparing a linear low-density polyethylene (LLDPE) film that has little reaction with ozone;
Increasing ozone resistance by treating the linear low-density polyethylene (LLDPE) film at high temperature;
Producing a multilayer ozone-resistant film by hot-pressing a cured PET (Polyethylene Terephthalate) film on the linear low-density polyethylene (LLDPE) film;
Steps of producing an ozone-resistant no-sticker type pouch,
A method of manufacturing wet tissues using ozone sterilizing water, comprising the step of packaging using an ozone-resistant no-sticker type pouch.
상기 선형저밀도폴리에틸렌(LLDPE) 필름을 고온 처리하는 단계는,
선형저밀도폴리에틸렌(LLDPE) 필름의 표면에 플라즈마 가스를 가하여 표면처리를 하는 단계와,
상기 선형저밀도폴리에틸렌(LLDPE) 필름을 진공 환경에서 327~380°C로 2시간 이상 가열하는 단계를 포함하여 이루어지는 것을 특징으로 하는 오존 살균수를 이용한 물티슈의 제조방법. According to clause 1,
The step of high temperature treating the linear low density polyethylene (LLDPE) film,
A step of surface treatment by applying plasma gas to the surface of a linear low-density polyethylene (LLDPE) film;
A method of manufacturing wet tissues using ozone sterilization water, comprising the step of heating the linear low-density polyethylene (LLDPE) film at 327 to 380 ° C for more than 2 hours in a vacuum environment.
상기 오존 저항성 노스티커 타입 파우치를 제작하는 단계는,
선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET 필름의 이중층으로 이루어진 파우치 필름을 준비하는 단계와,
레이저 가공장치를 이용하여 레이저광의 조사각도가 경사각을 형성하도록 조절하는 단계와,
경사각의 레이저광을 이용하여 파우치 필름의 상부에 절취선을 가공함으로써 출구가 형성되도록 하는 단계를 포함하여 이루어지는 것을 특징으로 하는 오존 살균수를 이용한 물티슈의 제조방법. According to clause 2,
The step of producing the ozone-resistant no-sticker type pouch is,
Preparing a pouch film composed of a double layer of a linear low-density polyethylene (LLDPE) film and a cured PET film;
adjusting the irradiation angle of the laser light to form an inclination angle using a laser processing device;
A method of manufacturing wet tissues using ozone sterilizing water, comprising the step of forming a perforation line on the upper part of the pouch film using a laser light at an inclined angle to form an outlet.
상기 레이저 가공장치는 절취선을 가공함에 있어서 레이저광의 조사각도를 경사각으로 조절하여 경화 PET 필름의 깊이까지 절삭한 뒤에 선형저밀도폴리에틸렌(LLDPE) 필름의 깊이 일부까지 절삭하는 것을 특징으로 하는 오존 살균수를 이용한 물티슈의 제조방법. According to clause 3,
The laser processing device uses ozone sterilizing water to cut to the depth of the cured PET film by adjusting the irradiation angle of the laser light to the inclination angle when processing the cutting line, and then cuts to a part of the depth of the linear low-density polyethylene (LLDPE) film. Method of manufacturing wet tissues.
상기 선형저밀도폴리에틸렌(LLDPE) 필름에 경화 PET(Polyethylene Terephthalate) 필름을 열압하여 다층구조 오존저항성 필름을 제작하는 단계에서, 선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET(Polyethylene Terephthalate) 필름의 사이에 R-CCP 혹은 G-PET중에서 선택되는 어느 하나를 추가로 합지하는 것을 특징으로 하는 오존 살균수를 이용한 물티슈의 제조방법. According to clause 2,
In the step of producing a multi-layered ozone-resistant film by hot-pressing a cured PET (Polyethylene Terephthalate) film on the linear low-density polyethylene (LLDPE) film, R- A method of manufacturing wet tissues using ozone sterilizing water, characterized by additionally laminating either CCP or G-PET.
상기 오존 저항성 노스티커 타입 파우치를 제작하는 단계는,
선형저밀도폴리에틸렌(LLDPE) 필름과 경화 PET(Polyethylene Terephthalate) 필름의 사이에 R-CCP 혹은 G-PET가 추가로 합지된 필름을 준비하는 단계와,
레이저 가공장치를 이용하여 레이저광의 조사각도가 경사각을 형성하도록 조절하는 단계와,
경사각의 레이저광을 이용하여 파우치 필름의 상부에 절취선을 가공함으로써 출구가 형성되도록 하는 단계를 포함하여 이루어지는 것을 특징으로 하는 오존 살균수를 이용한 물티슈의 제조방법. According to clause 5,
The step of producing the ozone-resistant no-sticker type pouch is,
Preparing a film in which R-CCP or G-PET is additionally laminated between a linear low-density polyethylene (LLDPE) film and a cured PET (Polyethylene Terephthalate) film;
adjusting the irradiation angle of the laser light to form an inclination angle using a laser processing device;
A method of manufacturing wet tissues using ozone sterilizing water, comprising the step of forming a perforation line on the upper part of the pouch film using a laser light at an inclined angle to form an outlet.
상기 레이저 가공장치는 절취선을 가공함에 있어서 레이저광의 조사각도를 경사각으로 조절하여 경화 PET(Polyethylene Terephthalate) 필름의 깊이까지 절삭하고, R-CCP 혹은 G-PET도 절삭한 뒤에, 선형저밀도폴리에틸렌(LLDPE) 필름의 깊이 일부까지 절삭하는 것을 특징으로 하는 오존 살균수를 이용한 물티슈의 제조방법. According to clause 6,
When processing a cut line, the laser processing device adjusts the irradiation angle of the laser light to the inclination angle to cut to the depth of the cured PET (Polyethylene Terephthalate) film, and after cutting R-CCP or G-PET, linear low-density polyethylene (LLDPE). A method of manufacturing wet tissues using ozone sterilized water, characterized by cutting to a portion of the depth of the film.
상기 레이저 가공장치는,
레이저 광원으로부터 입사되는 레이저광의 조사각도를 가변시키기 위한 렌즈부와,
상기 렌즈부를 수평이동시키기 위한 수평이동부와,
상기 렌즈부와 수평이동부를 승하강시키기 위한 승하강부와,
상기 렌즈부를 지지하기 위한 지지부를 포함하며;
상기 승하강부는, 지지판과, 상기 지지판의 상부에 설치되는 구동모터와, 상기 구동모터의 회전축에 연결되는 스크류바와, 상기 스크류바의 후면에 설치되는 지지바와, 상기 구동모터와 지지바의 하부를 감싸면서 설치되는 케이싱과, 상기 스크류바와 지지바의 상부에 설치되는 고정판과, 상기 스크류바에 나사결합되어 승하강 운동을 하는 승하강 부재와, 상기 지지바에 설치되어 승하강 부재와 연결됨으로써 승하강 부재와 함께 승하강 운동을 하면서 승하강 부재의 회전을 방지하는 회전방지돌기를 포함하며;
상기 수평이동부는, 상기 승하강부의 승하강 부재에 연결 설치되는 실린더와, 상기 실린더에 일단이 연결되어 있으며 타측에 고정링이 인입되는 연결부재와, 상기 연결부재의 상부에 설치되어 하부가 연결부재의 상부면에 나사결합되며 조임 회전에 따라 하강되며 고정링을 가압 고정하는 고정구를 포함하며;
상기 지지부는, 하부가 지지판에 고정되는 지주와, 상기 지주의 외측으로 상하 이동 가능하게 결합되는 이동부재와, 상기 이동부재에 일측이 고정되고 타측에 고정링의 일측이 안착되는 지지부재와, 상기 지주로부터 이동부재를 지지하는 조절구를 포함하여 이루어지는 것을 특징으로 하는 오존 살균수를 이용한 물티슈의 제조방법. According to claim 4 or 7,
The laser processing device,
A lens unit for varying the irradiation angle of the laser light incident from the laser light source,
a horizontal moving unit for horizontally moving the lens unit;
A lifting and lowering unit for raising and lowering the lens unit and the horizontal moving unit,
It includes a support part for supporting the lens part;
The raising and lowering unit includes a support plate, a drive motor installed on an upper part of the support plate, a screw bar connected to the rotation axis of the drive motor, a support bar installed on the rear of the screw bar, and a lower part of the drive motor and the support bar. A casing installed while surrounding, a fixing plate installed on the upper part of the screw bar and the support bar, a lifting member that is screwed to the screw bar and moves up and down, and a lifting member that is installed on the support bar and connected to the lifting member. It includes an anti-rotation protrusion that prevents rotation of the raising and lowering member while moving up and down with it;
The horizontal movable part includes a cylinder connected to the elevating member of the elevating lowering part, a connecting member whose one end is connected to the cylinder and a fixing ring is inserted into the other side, and which is installed on the upper part of the connecting member and the lower part is connected. It is screwed to the upper surface of the member, lowers as the tightening rotation, and includes a fixture that pressurizes and secures the retaining ring;
The support part includes a support member whose lower part is fixed to a support plate, a moving member movable upward and downward to the outside of the support member, a support member on one side of which is fixed to the moving member and one side of a fixing ring is seated on the other side, and A method of manufacturing wet tissues using ozone sterilizing water, comprising an adjustment device for supporting a moving member from a support.
상기 렌즈부는,
레이저광을 조사각도를 가변시키기 위한 렌즈와,
좌우 한 쌍의 고정링유닛으로 분리되어 상기 렌즈의 테두리를 감싸는 고정링과,
상기 한쌍의 고정링유닛을 회동 가능하게 연결하기 위한 절첩부재와,
상기 한쌍의 고정링유닛을 결속하기 위한 체결수단을 포함하여 이루어지는 것을 특징으로 하는 오존 살균수를 이용한 물티슈의 제조방법. According to clause 8,
The lens unit,
A lens for changing the irradiation angle of the laser light,
A fixing ring that is separated into a pair of left and right fixing ring units and surrounds the edge of the lens,
A folding member for rotatably connecting the pair of fixing ring units;
A method of manufacturing wet tissues using ozone sterilizing water, comprising a fastening means for binding the pair of fixing ring units.
A wet tissue using ozone sterilizing water, characterized in that it is manufactured by the method of any one of claims 1 to 7.