KR102594776B1 - Hair treatment composition and method - Google Patents
Hair treatment composition and method Download PDFInfo
- Publication number
- KR102594776B1 KR102594776B1 KR1020180068399A KR20180068399A KR102594776B1 KR 102594776 B1 KR102594776 B1 KR 102594776B1 KR 1020180068399 A KR1020180068399 A KR 1020180068399A KR 20180068399 A KR20180068399 A KR 20180068399A KR 102594776 B1 KR102594776 B1 KR 102594776B1
- Authority
- KR
- South Korea
- Prior art keywords
- hair
- composition
- carbonylation
- mass
- treatment
- Prior art date
Abstract
(과제) 머리카락의 카르보닐화의 억제에 적합한 모발용 조성물, 및 당해 조성물을 사용하는 모발 처리 방법의 제공.
(해결 수단) 모발용 조성물은, 비사보롤 및 글루코실헤스페리딘이 배합된 것이고, 모발 처리 방법은, 비사보롤 및 글루코실헤스페리딘이 배합된 조성물을 사용한다.(Problem) Provision of a hair composition suitable for suppressing carbonylation of hair, and a hair treatment method using the composition.
(Solution) The hair composition contains bisabolol and glucosylhesperidin, and the hair treatment method uses a composition containing bisabolol and glucosylhesperidin.
Description
본 발명은, 열, 자외선 등에 의해 받는 모발에 있어서의 손상의 억제에 적합한 모발용 조성물, 및 이 조성물을 사용하는 모발 처리 방법에 관한 것이다.The present invention relates to a hair composition suitable for suppressing damage to hair caused by heat, ultraviolet rays, etc., and a hair treatment method using this composition.
드라이어, 열 아이론, 헤어 컬러, 퍼머넌트 웨이브 등의 물리적 처리, 열 처리, 또는 화학적 처리에 의해 모발이 손상된다. 모발 손상의 일종으로서, 모발에 있어서의 케라틴이 산화됨으로써 발생하는 카르보닐화가 알려져 있고, 이 카르보닐화의 억제가 요망된다.Hair is damaged by physical treatment, heat treatment, or chemical treatment such as dryers, heat irons, hair curlers, and permanent waves. Carbonylation, which occurs as a result of oxidation of keratin in hair, is known as a type of hair damage, and suppression of this carbonylation is desired.
그런데, 특허문헌 1 에는, 비사보롤과 자외선 흡수제를 함유하는 화장료가 개시되고, 모발에도 적용되는 헤어토닉, 샴푸의 구체적인 배합 성분이 기재되어 있다 (특허청구의 범위, 실시예 8, 실시예 9). 그러나, 카르보닐화의 억제에 관한 기재는 일절 없다.However, Patent Document 1 discloses a cosmetic containing bisabolol and an ultraviolet absorber, and describes specific ingredients for hair tonics and shampoos that are also applied to hair (scope of patent claims, Examples 8 and 9) ). However, there is no description whatsoever regarding inhibition of carbonylation.
본 발명은, 상기 사정을 감안하여, 모발의 카르보닐화의 억제에 적합한 모발용 조성물, 및 당해 조성물을 사용하는 모발 처리 방법의 제공을 목적으로 한다.In view of the above circumstances, the present invention aims to provide a hair composition suitable for suppressing carbonylation of hair, and a hair treatment method using the composition.
본 발명자들이 예의 검토를 실시한 결과, 특정한 성분이 모발에 있어서의 카르보닐화의 억제에 적합한 것을 알아내어, 본 발명을 완성하기에 이르렀다.As a result of intensive studies, the present inventors have found that certain ingredients are suitable for inhibiting carbonylation in hair, and have completed the present invention.
즉, 본 발명에 관련된 모발용 조성물은, 비사보롤 및 글루코실헤스페리딘이 배합된 것을 특징으로 한다.That is, the hair composition according to the present invention is characterized by blending bisabolol and glucosylhesperidin.
본 발명에 관련된 모발용 조성물은, 모발에 도포 후, 씻어내지 않고 사용되는 것이면 된다. 이 사용 양태이면, 모발 세정제 등의 씻어내는 것과 달리, 비사보롤 및 글루코실헤스페리딘이 모발에 머물기 쉬워, 카르보닐화의 억제에 적합하다.The hair composition according to the present invention may be used as long as it is applied to the hair and then used without washing it off. In this mode of use, unlike washing with a hair detergent or the like, bisabolol and glucosylhesperidin tend to remain in the hair, making it suitable for suppressing carbonylation.
본 발명에 관련된 모발용 조성물은, 열 또는 자외선에 의한 모발의 카르보닐화를 억제하기 위해서 사용되면 된다. 열에 의한 모발의 카르보닐화를 억제하는 경우, 그 열의 열원은, 예를 들어, 온풍을 공급하는 헤어 드라이어, 1 쌍의 발열체로 모발을 협지 가능한 헤어 아이론이다.The composition for hair according to the present invention may be used to suppress carbonylation of hair caused by heat or ultraviolet rays. When suppressing carbonylation of hair due to heat, the heat source is, for example, a hair dryer that supplies warm air or a hair iron that can clamp hair with a pair of heating elements.
본 발명에 관련된 모발용 조성물에 있어서, 비사보롤의 배합량이 0.02 질량％ 이상, 글루코실헤스페리딘의 배합량이 0.00005 질량％ 이상이면 된다. 이와 같은 배합량 설정이면, 카르보닐화의 억제에 적합하다.In the hair composition according to the present invention, the amount of bisabolol may be 0.02% by mass or more, and the amount of glucosylhesperidin may be 0.00005% by mass or more. Such a mixing amount setting is suitable for suppressing carbonylation.
본 발명에 관련된 모발용 조성물은, 초기 탄성률의 저하를 억제하기 위해서 사용되면 된다. 카르보닐화에 수반하여 모발의 초기 탄성률은 저하되지만, 카르보닐화의 억제에 적합한 본 발명에 관련된 모발용 조성물을 사용하면, 그 저하를 억제할 수 있다.The composition for hair according to the present invention may be used to suppress a decrease in initial elastic modulus. The initial elastic modulus of hair decreases with carbonylation, but this decrease can be suppressed by using the hair composition according to the present invention suitable for inhibiting carbonylation.
본 발명에 관련된 모발 처리 방법은, 본 발명에 관련된 모발용 조성물을 사용하는 것을 특징으로 한다.The hair treatment method according to the present invention is characterized by using the hair composition according to the present invention.
본 발명에 관련된 모발용 조성물 및 모발 처리 방법에 의하면, 비사보롤 및 글루코실헤스페리딘에 의해, 모발의 카르보닐화가 억제된다.According to the hair composition and hair treatment method according to the present invention, carbonylation of hair is suppressed by bisabolol and glucosylhesperidin.
본 발명의 실시형태에 기초하여, 본 발명을 이하에 설명한다.Based on embodiments of the present invention, the present invention is described below.
본 실시형태에 관련된 모발용 조성물에는, 비사보롤 및 글루코실헤스페리딘이 배합된다. 또, 실사용상 허용되는 것이면, 공지된 모발용 조성물에 배합되어 있는 성분을 추가로 배합해도 된다.The hair composition according to the present embodiment contains bisabolol and glucosylhesperidin. In addition, components blended in known hair compositions may be additionally mixed as long as they are acceptable in actual use.
비사보롤 및 글루코실헤스페리딘이 배합된 본 실시형태의 모발용 조성물을 사용하면, 그 배합된 양 성분이, 모발의 카르보닐화를 억제한다. 카르보닐화는, 드라이어, 헤어 아이론 등으로부터 받는 열, 태양광 등에 포함되어 있는 자외선이 원인으로 발생하지만, 본 실시형태의 모발용 조성물은, 이 열 또는 자외선에 의한 카르보닐화를 억제한다.When the hair composition of the present embodiment containing bisabolol and glucosylhesperidin is used, both components suppress carbonylation of hair. Carbonylation occurs due to heat received from a dryer, hair iron, etc., or ultraviolet rays contained in sunlight, etc. However, the hair composition of the present embodiment suppresses carbonylation caused by this heat or ultraviolet rays.
본 실시형태의 모발용 조성물에 있어서, 비사보롤의 배합량은 특별히 한정되지 않지만, 0.02 질량％ 이상 3 질량％ 이하가 좋고, 0.03 질량％ 이상 1 질량％ 이하가 바람직하고, 0.04 질량％ 이상 0.5 질량％ 이하가 보다 바람직하다. 0.02 질량％ 이상이면, 카르보닐화의 억제가 보다 우수하고, 3 질량％ 이하이면, 본 실시형태의 모발용 조성물의 저비용화를 도모할 수 있다.In the hair composition of this embodiment, the compounding amount of bisabolol is not particularly limited, but is preferably 0.02% by mass or more and 3% by mass or less, preferably 0.03% by mass or more and 1% by mass or less, and preferably 0.04% by mass or more and 0.5% by mass. The following is more preferable. If it is 0.02% by mass or more, the inhibition of carbonylation is more excellent, and if it is 3% by mass or less, the cost of the hair composition of this embodiment can be reduced.
본 실시형태의 모발용 조성물에 있어서, 글루코실헤스페리딘의 배합량은 특별히 한정되지 않지만, 0.00005 질량％ 이상 3 질량％ 이하가 좋고, 0.00008 질량％ 이상 1 질량％ 이하가 바람직하고, 0.0001 질량％ 이상 0.5 질량％ 이하가 보다 바람직하다. 0.00005 질량％ 이상이면, 카르보닐화의 억제가 보다 우수하고, 3 질량％ 이하이면, 본 실시형태의 모발용 조성물의 저비용화를 도모할 수 있다.In the hair composition of the present embodiment, the amount of glucosylhesperidin is not particularly limited, but is preferably 0.00005% by mass or more and 3% by mass or less, preferably 0.00008% by mass or more and 1% by mass or less, and preferably 0.0001% by mass or more and 0.5% by mass. The following is more preferable. If it is 0.00005 mass% or more, the suppression of carbonylation is more excellent, and if it is 3 mass% or less, the cost of the hair composition of this embodiment can be reduced.
본 실시형태의 모발용 조성물에는, 상기와 같이, 공지된 모발용 조성물에 배합되어 있는 성분을 추가로 배합해도 된다. 그 성분으로는, 모발용 조성물의 용도에 따라 적절히 선정되고, 예를 들어, 카티온 계면 활성제, 양쪽성 계면 활성제, 논이온 계면 활성제, 고급 알코올, 다가 알코올, 유지, 에스테르유, 실리콘, 고분자 화합물이다.In the hair composition of the present embodiment, components blended in known hair compositions may be further mixed as described above. The ingredients are appropriately selected depending on the intended use of the hair composition, and include, for example, cationic surfactants, amphoteric surfactants, nonionic surfactants, higher alcohols, polyhydric alcohols, fats and oils, ester oils, silicones, and polymer compounds. .
본 실시형태의 모발용 조성물은, 모발에 도포 후에 씻어내지 않는 양태에 의해 사용하는 것이 바람직한 것이지만, 이 경우에 비사보롤 및 글루코실헤스페리딘 과 함께 배합되는 성분의 조합예로는, 카티온 계면 활성제, 논이온 계면 활성제, 다가 알코올, 유지, 에스테르유, 실리콘, 합성 고분자 화합물, 천연 고분자 화합물 및 물이다.The hair composition of the present embodiment is preferably used in a manner in which it is not washed off after application to the hair. Examples of combinations of components blended with bisabolol and glucosylhesperidin in this case include a cationic surfactant, These are non-ionic surfactants, polyhydric alcohols, fats and oils, ester oils, silicones, synthetic polymer compounds, natural polymer compounds, and water.
상기 카티온 계면 활성제로는, 예를 들어, 지방산 아미드아민염, 에스테르 함유 3 급 아민염, 장사슬 알킬트리메틸암모늄염, 디장사슬 알킬디메틸암모늄염을 들 수 있다. 모발용 조성물에 카티온 계면 활성제를 배합하는 경우, 1 종 또는 2 종 이상을 배합하면 된다. 또, 모발용 조성물에 있어서의 카티온 계면 활성제의 배합 농도는, 당해 조성물의 용도에 따라 적절히 설정되는 것이지만, 예를 들어 0.1 질량％ 이상 3 질량％ 이하이다.Examples of the cationic surfactant include fatty acid amidamine salts, ester-containing tertiary amine salts, long-chain alkyltrimethylammonium salts, and di-long chain alkyldimethylammonium salts. When blending a cationic surfactant into a hair composition, one type or two or more types may be blended. In addition, the compounding concentration of the cationic surfactant in the hair composition is appropriately set depending on the use of the composition, but is, for example, 0.1% by mass or more and 3% by mass or less.
상기 논이온 계면 활성제로는, 예를 들어, 폴리옥시에틸렌알킬에테르, 폴리옥시에틸렌폴리옥시프로필렌알킬에테르, 폴리옥시에틸렌 지방산 에스테르, 폴리옥시에틸렌소르비탄 지방산 에스테르, 글리세린 지방산 에스테르, 소르비탄 지방산 에스테르, 폴리글리세린 지방산 에스테르, 자당 지방산 에스테르를 들 수 있다. 모발용 조성물에 논이온 계면 활성제를 배합하는 경우, 1 종 또는 2 종 이상을 배합하면 된다. 또, 모발용 조성물에 있어서의 논이온 계면 활성제의 배합 농도는, 당해 조성물의 용도에 따라 적절히 설정되는 것이지만, 예를 들어 0.1 질량％ 이상 3 질량％ 이하이다.The nonionic surfactant includes, for example, polyoxyethylene alkyl ether, polyoxyethylene polyoxypropylene alkyl ether, polyoxyethylene fatty acid ester, polyoxyethylene sorbitan fatty acid ester, glycerin fatty acid ester, sorbitan fatty acid ester, Examples include polyglycerol fatty acid ester and sucrose fatty acid ester. When blending a non-ionic surfactant in a hair composition, one type or two or more types may be blended. In addition, the blending concentration of the nonionic surfactant in the hair composition is appropriately set depending on the use of the composition, but is, for example, 0.1% by mass or more and 3% by mass or less.
상기 고급 알코올로는, 예를 들어, 세탄올, 스테아릴알코올, 이소스테아릴알코올, 베헤닐알코올, 미리스틸알코올을 들 수 있다. 모발용 조성물에 고급 알코올을 배합하는 경우, 1 종 또는 2 종 이상을 배합하면 된다. 또, 모발용 조성물에 있어서의 고급 알코올의 배합 농도는, 당해 조성물의 용도에 따라 적절히 설정되는 것이지만, 예를 들어 1 질량％ 이상 3 질량％ 이하이다.Examples of the higher alcohol include cetanol, stearyl alcohol, isostearyl alcohol, behenyl alcohol, and myristyl alcohol. When blending a higher alcohol into a hair composition, one type or two or more types may be blended. In addition, the blending concentration of the higher alcohol in the hair composition is appropriately set depending on the use of the composition, but is, for example, 1% by mass or more and 3% by mass or less.
상기 다가 알코올로는, 예를 들어, 에틸렌글리콜, 디에틸렌글리콜, 트리에틸렌글리콜, 프로필렌글리콜, 디프로필렌글리콜, 글리세린, 디글리세린, 부틸렌글리콜을 들 수 있다. 모발용 조성물에 다가 알코올을 배합하는 경우, 1 종 또는 2 종 이상을 배합하면 된다. 또, 모발용 조성물에 있어서의 다가 알코올의 배합 농도는, 당해 조성물의 용도에 따라 적절히 설정되는 것이지만, 예를 들어 0.1 질량％ 이상 8 질량％ 이하이다.Examples of the polyhydric alcohol include ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, glycerin, diglycerol, and butylene glycol. When mixing a polyhydric alcohol into a hair composition, one type or two or more types may be mixed. In addition, the compounding concentration of the polyhydric alcohol in the hair composition is appropriately set depending on the use of the composition, but is, for example, 0.1% by mass or more and 8% by mass or less.
상기 유지로는, 예를 들어 아보카도유, 올리브유, 시어 지유 (脂油), 달맞이꽃유, 동백유, 로즈힙유를 들 수 있다. 모발용 조성물에 유지를 배합하는 경우, 1 종 또는 2 종 이상을 배합하면 된다. 또, 모발용 조성물에 있어서의 유지의 배합 농도는, 당해 조성물의 용도에 따라 적절히 설정되는 것이지만, 예를 들어 0.1 질량％ 이상 2 질량％ 이하이다.Examples of the oils and fats include avocado oil, olive oil, shea oil, evening primrose oil, camellia oil, and rosehip oil. When blending fats and oils into a hair composition, one type or two or more types may be blended. In addition, the blending concentration of oils and fats in the hair composition is appropriately set depending on the use of the composition, but is, for example, 0.1% by mass or more and 2% by mass or less.
상기 에스테르유로는, 예를 들어, 미리스트산이소프로필, 팔미트산이소프로필, 팔미트산세틸, 미리스트산옥틸도데실, 이소스테아르산에틸, 2-에틸헥산산세틸, 이소스테아르산헥실, 테트라 2-에틸헥산산펜타에리트리톨, 락트산미리스틸, 말산디이소스테아릴, 스테아르산콜레스테릴을 들 수 있다. 모발용 조성물에 에스테르유을 배합하는 경우, 1 종 또는 2 종 이상을 배합하면 된다. 또, 모발용 조성물에 있어서의 에스테르유의 배합 농도는, 당해 조성물의 용도에 따라 적절히 설정되는 것이지만, 예를 들어 0.1 질량％ 이상 2 질량％ 이하이다.Examples of the ester oil include isopropyl myrstate, isopropyl palmitate, cetyl palmitate, octyldodecyl myrstate, ethyl isostearate, cetyl 2-ethylhexanoate, hexyl isostearate, Examples include pentaerythritol tetra 2-ethylhexanoate, myristyl lactate, diisostearyl malate, and cholesteryl stearate. When blending ester oil into a hair composition, one type or two or more types may be blended. In addition, the blending concentration of ester oil in the hair composition is appropriately set depending on the use of the composition, but is, for example, 0.1% by mass or more and 2% by mass or less.
상기 실리콘으로는, 예를 들어, 디메틸실리콘, 환상 디메틸실리콘, 아미노 변성 실리콘을 들 수 있다. 모발용 조성물에 실리콘을 배합하는 경우, 1 종 또는 2 종 이상을 배합하면 된다. 또, 모발용 조성물에 있어서의 실리콘의 배합 농도는, 당해 조성물의 용도에 따라 적절히 설정되는 것이지만, 예를 들어 0.1 질량％ 이상 95 질량％ 이하이다.Examples of the silicone include dimethyl silicone, cyclic dimethyl silicone, and amino-modified silicone. When blending silicone into a hair composition, one type or two or more types may be blended. In addition, the blending concentration of silicone in the hair composition is appropriately set depending on the use of the composition, but is, for example, 0.1% by mass or more and 95% by mass or less.
상기 합성 고분자 화합물로는, 예를 들어, 폴리아크릴산계 고분자 (카르복시비닐 폴리머, 폴리아크릴산아미드, 폴리아크릴산나트륨, (아크릴산/메타크릴산알킬) 코폴리머를 들 수 있다. 반합성 고분자 화합물로는, 예를 들어, 셀룰로오스 유도체 (하이드록시에틸셀룰로오스, 카티온화 셀룰로오스 등), 전분 유도체 (하이드록시프로필전분인산 등), 구아검 유도체 (카티온화 구아검, 하이드록시프로필화 구아검 등) 를 들 수 있다. 또, 상기 천연 고분자로는, 예를 들어, 히알루론산나트륨을 들 수 있다. 모발용 조성물에 고분자 화합물 (합성 고분자 화합물, 반합성 고분자 화합물, 천연 고분자 화합물) 을 배합하는 경우, 1 종 또는 2 종 이상을 배합하면 된다. 또, 모발용 조성물에 있어서의 고분자 화합물의 배합 농도는, 당해 조성물의 용도에 따라 적절히 설정되는 것이지만, 예를 들어 0.1 질량％ 이상 1 질량％ 이하이다.Examples of the synthetic polymer compounds include polyacrylic acid-based polymers (carboxyvinyl polymer, polyacrylic acid amide, sodium polyacrylate, (acrylic acid/alkyl methacrylate) copolymer. Semi-synthetic polymer compounds include, for example, For example, cellulose derivatives (hydroxyethylcellulose, cationized cellulose, etc.), starch derivatives (hydroxypropyl starch phosphate, etc.), and guar gum derivatives (cationized guar gum, hydroxypropylated guar gum, etc.). In addition, the above-mentioned natural polymer includes, for example, sodium hyaluronate.When blending a polymer compound (synthetic polymer compound, semi-synthetic polymer compound, natural polymer compound) in a hair composition, one type or two or more types can be used. In addition, the mixing concentration of the polymer compound in the hair composition is appropriately set depending on the use of the composition, but is, for example, 0.1% by mass or more and 1% by mass or less.
본 실시형태의 모발용 조성물의 사용시의 제형은 특별히 한정되지 않고, 예를 들어, 액상, 크림상, 겔상, 폼상 (거품상), 안개상을 들 수 있다. 또, 본 실시형태의 모발용 조성물이 유상 (油相) 과 수상 (水相) 을 갖는 경우, 외상이 물인 수중유형의 제형, 외상이 유상인 유중수형의 제형 중 어느 것이어도 된다. 수중유형의 제형인 경우, 물의 배합량은, 예를 들어 60 질량％ 이상이다. 유중수형의 제형인 경우, 물의 배합량은, 예를 들어 10 질량％ 이하이다.The dosage form when using the hair composition of this embodiment is not particularly limited, and examples include liquid, cream, gel, foam (foam), and mist. Additionally, when the hair composition of the present embodiment has an oil phase and an aqueous phase, it may be either an oil-in-water formulation in which the outer layer is water, or a water-in-oil formulation in which the outer layer is an oil phase. In the case of an oil-in-water formulation, the mixing amount of water is, for example, 60% by mass or more. In the case of a water-in-oil type formulation, the mixing amount of water is, for example, 10% by mass or less.
본 실시형태의 모발용 조성물의 25 ℃ 에 있어서의 pH 는, 적절히 설정되어야 하는 것인데, 예를 들어 4.0 이상 7.0 이하이다.The pH of the hair composition of the present embodiment at 25°C must be set appropriately, for example, 4.0 or more and 7.0 or less.
본 실시형태의 모발용 조성물은, 모발에 도포하여 모발 처리하는 방법에 있어서 사용된다. 예를 들어, (1) 젖은 모발에 도포 후, 수세하여 씻어내는 사용 방법, 또는, (2) 젖은 모발 또는 건조된 모발에 도포 후, 모발을 씻어내지 않는 사용 방법에 있어서, 본 실시형태의 모발용 조성물이 사용된다. 특히 바람직한 사용 방법은, 모발에 도포 후, 모발을 씻어내지 않는 사용 방법이다. 이 사용 방법이면, 카르보닐화의 억제 성분인 비사보롤 및 글루코실헤스페리딘이 모발에 많이 머문다.The hair composition of this embodiment is used in a method of treating hair by applying it to hair. For example, in (1) a method of use in which the hair is washed after application to wet hair, or (2) a method of use in which the hair is not washed off after application to wet or dried hair, the hair product of the present embodiment The composition is used. A particularly preferred method of use is a method of use that does not wash off the hair after application to the hair. With this method of use, a large amount of bisabolol and glucosylhesperidin, which are carbonylation inhibitors, remain in the hair.
또, (1) 비사보롤을 배합한 조성물을 모발에 도포 후, 글루코실헤스페리딘을 배합한 조성물을 모발에 도포, 또는, (2) 글루코실헤스페리딘을 배합한 조성물을 모발에 도포 후, 비사보롤을 배합한 조성물을 모발에 도포, 에 의해, 본 실시형태의 모발용 조성물을 모발에 있어서 성립시켜, 모발 처리하는 방법을 채용해도 된다.In addition, (1) after applying a composition containing bisabolol to the hair, a composition containing glucosylhesperidin is applied to the hair, or (2) after applying a composition containing glucosylhesperidin to the hair, A method of applying the composition mixed with the roll to the hair to form the hair composition of the present embodiment on the hair and treating the hair may be adopted.
열 또는 자외선에 의해 카르보닐화는, 상기와 같이, 본 실시형태의 모발용 조성물에 의해 억제 가능하다. 온풍을 공급하는 헤어 드라이어에 의해서도 열에 의한 카르보닐화가 발생하고, 당해 카르보닐화의 억제에 대해서도, 본 실시형태의 모발용 조성물이 유효한 것이 확인되었다. 따라서, 헤어 드라이어 등의 모발을 가열하는 장치를 사용하기 전에, 본 실시형태의 모발용 조성물을 도포하면 된다.As described above, carbonylation caused by heat or ultraviolet rays can be suppressed by the hair composition of the present embodiment. It was confirmed that carbonylation due to heat occurs even when a hair dryer supplies warm air, and that the hair composition of the present embodiment is effective in suppressing the carbonylation. Therefore, the hair composition of this embodiment may be applied before using a hair heating device such as a hair dryer.
또, 모발의 초기 탄성률은, 카르보닐화에 수반하여 저하되는 경향이 있다고 생각되므로, 카르보닐화를 억제하는 본 실시형태의 모발용 조성물을 사용하면, 모발의 초기 탄성률의 저하를 억제할 수 있다.In addition, since it is thought that the initial elastic modulus of hair tends to decrease with carbonylation, a decrease in the initial elastic modulus of hair can be suppressed by using the hair composition of this embodiment that suppresses carbonylation.
실시예Example
이하, 실시예에 기초하여 본 발명을 상세히 서술하지만, 이 실시예의 기재에 기초하여 본 발명이 한정적으로 해석되는 것은 아니다.Hereinafter, the present invention will be described in detail based on examples, but the present invention is not to be construed as limited based on the description of these examples.
(모발용 조성물)(Composition for hair)
모발용 조성물 1 로서, 비사보롤을 0.05 질량％, 데카메틸시클로펜타실록산을 99.95 질량％ 배합한 것을 조제하였다. 모발용 조성물 2 로서, 글루코실헤스페리딘을 0.0001 질량％, 물을 99.9999 질량％ 배합한 것을 조제하였다.Composition 1 for hair was prepared by mixing 0.05% by mass of bisabolol and 99.95% by mass of decamethylcyclopentasiloxane. Composition 2 for hair was prepared by mixing 0.0001% by mass of glucosylhesperidin and 99.9999% by mass of water.
(모발 처리 1a, 1b, 2a, 2b 에 있어서의 처리 대상 모속)(Hair bundles to be treated in hair treatment 1a, 1b, 2a, 2b)
10 대 ∼ 20 대의 일본인 여성 5 명으로부터, 헤어 컬러 처리 및 파마 처리를 실시한 적이 없는 모발을 각각 0.2 g 채취하여, 모속으로서 준비하였다. 이 모속을, 아니온 계면 활성제가 배합된 샴푸를 사용하여 세정하고, 건조시켰다. 이 건조 후의 모속을, 하기 모발 처리 1a, 1b, 2a, 2b 에 있어서의 처리 대상 모속으로 하였다.From five Japanese women in their teens to twenties, 0.2 g of hair that had never been subjected to hair color treatment or perm treatment was each collected and prepared as hair bundles. This hair bundle was washed using a shampoo containing an anionic surfactant and dried. The hair bundle after this drying was used as the hair bundle to be treated in the following hair treatments 1a, 1b, 2a, and 2b.
(모발 처리 3a, 3b, 3c, 3d 에 있어서의 처리 대상 모속)(Hair bundle to be treated in hair treatment 3a, 3b, 3c, 3d)
10 대 ∼ 20 대의 일본인 여성으로부터, 헤어 컬러 처리 및 파마 처리를 실시한 적이 없는 모발을 각각 0.2 g 채취하였다 (모발 처리 3a, 3b 에서는, 일본인 여성 3 명으로부터 채취하고, 모발 처리 3c 에서는, 일본인 여성 2 명으로부터 채취하고, 모발 처리 3d 에서는, 일본인 여성 4 명으로부터 채취하였다). 이 모속을, 모발 처리 3a ∼ 3d 에 있어서의 처리 대상으로서 준비하였다. 이 모속을, 아니온 계면 활성제가 배합된 샴푸를 사용하여 세정하고, 건조시켰다. 이 건조 후의 모속을, 하기 모발 처리 3a, 3b, 3c, 3d 에 있어서의 처리 대상 모속으로 하였다.0.2 g of hair that had never been subjected to hair color treatment or perm treatment was each collected from Japanese women in their teens to 20s (in hair treatments 3a and 3b, samples were collected from 3 Japanese women, and in hair treatment 3c, 2 Japanese women were collected). In the 3d hair treatment, samples were collected from 4 Japanese women). This hair bundle was prepared as a treatment target in hair treatments 3a to 3d. This hair bundle was washed using a shampoo containing an anionic surfactant and dried. The hair bundle after this drying was used as the hair bundle to be treated in the following hair treatments 3a, 3b, 3c, and 3d.
(모발 처리 1a, 1b)(Hair Treatment 1a, 1b)
상기 모속에 대해, 다음 (1) 에서 (3) 까지의 처리를 360 회 실시하였다. 하기 (1) 에 있어서, 모발용 조성물 1 을 사용한 처리를 모발 처리 1a 로 하고, 데카메틸시클로펜타실록산을 사용한 처리를 모발 처리 1b 로 하였다.For the hair bundle, the following treatments (1) to (3) were performed 360 times. In (1) below, treatment using hair composition 1 was referred to as hair treatment 1a, and treatment using decamethylcyclopentasiloxane was referred to as hair treatment 1b.
(1) 0.2 g 의 모속에 대해, 모발용 조성물 1 또는 데카메틸시클로펜타실록산을 약 0.04 g 적하.(1) About 0.04 g of hair composition 1 or decamethylcyclopentasiloxane was added dropwise to 0.2 g of hair bundle.
(2) 모속을, 90 ∼ 105 ℃ 의 항온조 내에 3 분간 방치.(2) The hair bundle is left to stand in a 90-105 degreeC thermostat for 3 minutes.
(3) 모속을 수세.(3) Wash the seedlings.
(모발 처리 2a, 2b)(Hair Treatment 2a, 2b)
상기 모발 처리 1a, 1b 에 있어서의 (1) 을 하기와 같이 한 것 이외에는, 모발 처리 1a, 1b 와 동일하게 하여, 모발 처리 2a, 2b 를 실시하였다. 하기 (1) 에 있어서, 모발 처리 2a 에서는 모발용 조성물 2 를 사용하고, 모발 처리 2b 에서는 물을 사용하였다.Hair treatments 2a and 2b were performed in the same manner as hair treatments 1a and 1b, except that (1) in the hair treatments 1a and 1b was carried out as follows. In (1) below, hair composition 2 was used in hair treatment 2a, and water was used in hair treatment 2b.
(1) 0.2 g 의 모속을, 모발용 조성물 2 또는 물에 침지.(1) 0.2 g of hair bundles were immersed in hair composition 2 or water.
(모발 처리 3a)(Hair Treatment 3a)
상기 모속에 대해, 다음 (1) 에서 (3) 까지의 처리를 360 회 실시하였다.For the hair bundle, the following treatments (1) to (3) were performed 360 times.
(1) 0.2 g 의 모속에 대해, 모발용 조성물 1 을 약 0.04 g 적하하고, 도포.(1) Approximately 0.04 g of hair composition 1 was added dropwise to 0.2 g of hair bundle and applied.
(2) 모속을, 90 ∼ 105 ℃ 의 항온조 내에 3 분간 방치.(2) The hair bundle is left to stand in a 90-105 degreeC thermostat for 3 minutes.
(3) 모속을 수세.(3) Wash the seedlings.
(모발 처리 3b)(Hair Treatment 3b)
상기 모속에 대해, 다음 (1) 에서 (3) 까지의 처리를 360 회 실시하였다.For the hair bundle, the following treatments (1) to (3) were performed 360 times.
(1) 0.2 g 의 모속을, 모발용 조성물 2 에 침지.(1) 0.2 g of hair bundle was immersed in hair composition 2.
(2) 모속을, 90 ∼ 105 ℃ 의 항온조 내에 3 분간 방치.(2) The hair bundle is left to stand in a 90-105 degreeC thermostat for 3 minutes.
(3) 모속을 수세.(3) Wash the seedlings.
(모발 처리 3c)(Hair Treatment 3c)
상기 모속에 대해, 다음 (1) 에서 (4) 까지의 처리를 360 회 실시하였다.For the hair bundle, the following treatments (1) to (4) were performed 360 times.
(1) 0.2 g 의 모속을, 모발용 조성물 2 에 침지.(1) 0.2 g of hair bundle was immersed in hair composition 2.
(2) 모속에 대해, 모발용 조성물 1 을 약 0.04 g 적하하고, 도포.(2) Approximately 0.04 g of Hair Composition 1 was added dropwise to the hair bundle and applied.
(3) 모속을, 90 ∼ 105 ℃ 의 항온조 내에 3 분간 방치.(3) The hair bundle is left to stand in a constant temperature bath of 90 to 105°C for 3 minutes.
(4) 모속을 수세.(4) Wash the seedlings.
(모발 처리 3d)(Hair Treatment 3D)
상기 모발 처리 3a 에 있어서의 (1) 을 생략한 것 이외에는, 모발 처리 3a 와 동일하게 하여, 모발 처리 3d 를 실시하였다.Hair treatment 3d was performed in the same manner as hair treatment 3a, except that (1) in hair treatment 3a was omitted.
(카르보닐화의 억제 평가)(Evaluation of inhibition of carbonylation)
모발의 카르보닐화의 정도 (카르보닐화도) 는, 일본 공개특허공보 2015-210263호에서 개시된 형광 측정을 사용하는 방법에 의해, 평가 가능하다. 이 방법을 사용하여, 「모발 처리 1b 의 모속의 카르보닐화도」에 대한 「모발 처리 1a 후의 모속의 카르보닐화도」, 및 「모발 처리 2b 의 모속의 카르보닐화도」에 대한 「모발 처리 2a 후의 모속의 카르보닐화도」를 산출하여, 카르보닐화의 억제 평가를 실시하였다.The degree of carbonylation (carbonylation degree) of hair can be evaluated by a method using fluorescence measurement disclosed in Japanese Patent Application Laid-Open No. 2015-210263. Using this method, “carbonylation degree of hair bundle after hair treatment 1a” relative to “carbonylation degree of hair bundle of hair treatment 1b” and “carbonylation degree of hair bundle after hair treatment 2a” relative to “carbonylation degree of hair bundle of hair treatment 2b” The carbonylation degree of the hair bundle was calculated to evaluate the inhibition of carbonylation.
또한, 상기 카르보닐화도의 평가는, 상세하게는, 이하의 「모발 용액 조제」, 「표지」, 「회수」, 및 「측정」 의 순서에 따라 실시한 것이다.In addition, the above-mentioned evaluation of the degree of carbonylation was performed in detail in the following order: “Hair solution preparation”, “Labeling”, “Recovery”, and “Measurement”.
모발 용액 조제hair solution preparation
DL-디티오트레이톨이 50 mM, 우레아가 8 M, 트리스(하이드록시메틸)아미노메탄염산염이 50 mM 인 pH 7.5 의 수용액을 조제하였다. 이 수용액 50 ㎖ 에, 세단한 모속 0.2 g 을 침지하고 나서, 50 ℃, 2 일간의 조건으로 수용액을 진탕시켰다. 그 후, 수용액의 상청액을 취출하여, 시판되는 총 단백질 정량 키트를 사용하여, 모발로부터 추출된 케라틴이 40 ㎍/ℓ 인 모발 용액 (Ⅰ) 을 조제하였다.An aqueous solution of pH 7.5 containing 50 mM DL-dithiothreitol, 8 M urea, and 50 mM tris(hydroxymethyl)aminomethane hydrochloride was prepared. After 0.2 g of shredded hair bundles were immersed in 50 ml of this aqueous solution, the aqueous solution was shaken under conditions of 50°C for 2 days. Thereafter, the supernatant of the aqueous solution was taken out, and hair solution (I) containing 40 μg/L of keratin extracted from hair was prepared using a commercially available total protein determination kit.
표지sign
20 μM 의 플루오레세인-5-티오세미카바자이드를, 용액 (Ⅰ) 에 대해 등용량 첨가하였다. 이 후, 용액 (Ⅰ) 을 어두운 곳 내에서 실온에서 1 시간 진탕시켰다.20 μM of fluorescein-5-thiosemicarbazide was added in an equal amount to solution (I). After this, solution (I) was shaken at room temperature in the dark for 1 hour.
회수collect
상기 표지 순서를 거친 용액 (Ⅰ) 에 9 배 용량의 아세톤을 첨가한 후에, 격렬하게 교반하고 나서 어두운 곳 내에서 1 시간 방치하였다. 다음으로, 원심을 실시하여 불용화된 케라틴을 침전시키고 나서, 액상부를 제거하였다. 그리고, 케라틴을 함유하는 고체부에 아세톤을 첨가하고, 상기와 동일하게, 교반, 원심, 액상부의 제거를 실시하고 나서, 케라틴을 회수하였다.After adding 9 times the volume of acetone to solution (I) that had gone through the above labeling procedure, it was stirred vigorously and left to stand in a dark place for 1 hour. Next, centrifugation was performed to precipitate the insoluble keratin, and then the liquid portion was removed. Then, acetone was added to the solid portion containing keratin, and in the same manner as above, stirring, centrifugation, and removal of the liquid portion were performed, and then keratin was recovered.
측정measurement
상기 회수한 케라틴에, 300 ㎕ 의 50 mM 트리스(하이드록시메틸)아미노메탄염산염 (pH 7.5) 을 첨가하여 용액 (Ⅱ) 를 조제하였다. 이 용액 (Ⅱ) 의 형광 측정을, 코로나 전기사 제조 「마이크로 플레이트 리더 SH-9000」을 사용하여 실시하고, 형광 강도의 값을 얻었다. 이 때의 측정 조건은, 여기 파장 : 485 ∼ 495 ㎚, 측정 형광 파장 : 538 ㎚, 광전자 증배관 전압 : High 설정, 반치폭 (FWHM) : 12 ㎚, 측정 감도 : X1 로 하였다.To the recovered keratin, 300 μl of 50 mM tris(hydroxymethyl)aminomethane hydrochloride (pH 7.5) was added to prepare solution (II). Fluorescence measurement of this solution (II) was performed using “Microplate Reader SH-9000” manufactured by Corona Electric Co., Ltd., and the value of fluorescence intensity was obtained. The measurement conditions at this time were excitation wavelength: 485 to 495 nm, measurement fluorescence wavelength: 538 nm, photomultiplier voltage: set to High, full width at half maximum (FWHM): 12 nm, and measurement sensitivity: X1.
상기 형광 측정에서 얻어진 값 (형광 강도) 의 평균값을, 카르보닐화의 억제 평가를 위해서 사용하는 값으로 하였다. 그 평균값은, 5 명으로부터 채취한 모속의 평균값으로, 각 모속의 형광 강도는, 모발 용액 조정에 의해 얻어진 용액 (Ⅰ) 로부터 3 회 채취하여, 측정한 형광 강도의 평균으로 하였다.The average value of the values (fluorescence intensity) obtained in the above fluorescence measurement was taken as the value used for evaluating inhibition of carbonylation. The average value is the average value of the hair bundles collected from 5 people, and the fluorescence intensity of each hair bundle was taken as the average of the fluorescence intensities measured three times from solution (I) obtained by adjusting the hair solution.
하기 표 1 에, 카르보닐화의 억제 평가의 결과를 나타낸다. 표 1 에 있어서, 「카르보닐화의 억제」의 수치가 1 미만이면 카르보닐화가 억제된 것을 의미하고, 비사보롤 또는 글루코실헤스페리딘에 의해, 카르보닐화를 억제할 수 있던 것을 확인할 수 있다.Table 1 below shows the results of the carbonylation inhibition evaluation. In Table 1, if the value of “inhibition of carbonylation” is less than 1, it means that carbonylation is suppressed, and it can be confirmed that carbonylation can be suppressed by bisabolol or glucosylhesperidin.
(초기 탄성률의 평가 1)(Evaluation of initial elastic modulus 1)
초기 탄성률의 측정은, 다음과 같이 실시하였다. 모발 1 개에 대해, 20 ㎜ 의 길이로 커트하고, 양단에 테이프를 첩부 (貼付) 하였다. 그 모발의 모경을 측정한 후, 이 모발 시료를 증류수에 밤새도록 침지하였다. 그 후, 초기 탄성률을 TENSILON YTM-Ⅱ-20 (ORIENTEC 사 제조) 을 사용하여, 2 ㎜/min 의 속도로 연신했을 때의 응력을 측정하고, 얻어진 데이터를 해석 프로그램 (X 축을 연신율, Y 축을 응력으로 했을 때의 초기의 기울기, 이른바 훅의 기울기를 산출) 을 사용하여 구하였다.The initial elastic modulus was measured as follows. One hair was cut to a length of 20 mm, and tape was attached to both ends. After measuring the hair diameter, the hair sample was immersed in distilled water overnight. After that, the initial elastic modulus was measured using TENSILON YTM-Ⅱ-20 (manufactured by ORIENTEC) and the stress when stretched at a speed of 2 mm/min, and the obtained data was analyzed using an analysis program (X-axis is elongation, Y-axis is stress). The initial slope, the so-called Hooke slope, was calculated using .
상기 초기 탄성률의 측정 대상은, 1 명으로부터 채취한 모발이고, 모발 처리 1a, 1b, 2a 또는 2b 로 처리한 모발과, 미처리된 모발이다. 또, 초기 탄성률의 평가 1 에 있어서는, 10 개의 초기 탄성률의 평균값을 산출하여, 평가하였다.The object for measuring the initial elastic modulus is hair collected from one person, hair treated with hair treatment 1a, 1b, 2a or 2b, and untreated hair. In addition, in evaluation 1 of the initial elastic modulus, the average value of 10 initial elastic moduli was calculated and evaluated.
하기 표 2 에, 초기 탄성률의 측정 결과를 나타낸다. 모발 처리 1a 및 1b 와 미처리와 대비한 경우, 비사보롤을 배합한 모발용 조성물을 사용한 모발 처리 1a 는, 그 배합이 없는 모발 처리 1b 보다 초기 탄성률의 저하가 억제되어 있었던 것을 확인할 수 있다. 이것은, 비사보롤에 의한 카르보닐화의 억제와 상관이 있다.Table 2 below shows the measurement results of the initial elastic modulus. When comparing hair treatments 1a and 1b with untreated hair, it can be confirmed that the decrease in initial elastic modulus was suppressed in hair treatment 1a using a hair composition containing bisabolol than in hair treatment 1b without the composition. This is correlated with the inhibition of carbonylation by bisabolol.
하기 표 3 에, 초기 탄성률의 측정 결과를 나타낸다. 모발 처리 2a 및 2b 와 미처리와 대비한 경우, 글루코실헤스페리딘을 배합한 모발용 조성물을 사용한 모발 처리 2a 는, 그 배합이 없는 모발 처리 2b 보다 초기 탄성률의 저하가 억제되어 있었던 것을 확인할 수 있다. 이것은, 글루코실헤스페리딘에 의한 카르보닐화의 억제와 상관이 있다.Table 3 below shows the measurement results of the initial elastic modulus. When comparing hair treatments 2a and 2b with untreated hair, it can be confirmed that the decrease in initial elastic modulus was suppressed in hair treatment 2a using a hair composition containing glucosylhesperidin compared to hair treatment 2b without the composition. This is correlated with the inhibition of carbonylation by glucosylhesperidin.
(초기 탄성률의 평가 2)(Evaluation of initial elastic modulus 2)
모발 처리 3a ∼ 3d 의 처리를 실시한 처리 모발 및 미처리된 모발의 초기 탄성률을, 상기 「초기 탄성률의 평가 1」과 동일하게 하여 측정하고, 평균값을 산출하였다. 그리고, 초기 탄성률의 유지율을 「초기 탄성률의 유지율 (％) ＝ (처리 모발의 초기 탄성률)/(미처리 모발의 초기 탄성률) × 100」에 기초하여 산출하였다.The initial elastic modulus of the treated hair and untreated hair subjected to the hair treatments 3a to 3d was measured in the same manner as in “Evaluation of Initial Elastic Modulus 1” above, and the average value was calculated. And, the maintenance rate of the initial elastic modulus was calculated based on “retention rate of the initial elastic modulus (%) = (initial elastic modulus of treated hair)/(initial elastic modulus of untreated hair) × 100.”
하기 표 4 에, 초기 탄성률의 유지율을 나타낸다. 모발 처리 3a 및 3b 와, 모발 처리 3d 를 대비한 경우, 비사보롤 또는 글루코실헤스페리딘을 배합한 모발용 조성물을 사용한 모발 처리 3a, 3b 는, 그 사용이 없는 모발 처리 3d 보다 초기 탄성률의 유지율이 높았던 것을 확인할 수 있다. 이것은, 비사보롤 또는 글루코실헤스페리딘에 의한 카르보닐화의 억제와 상관이 있다고 생각된다.Table 4 below shows the maintenance rate of the initial elastic modulus. When comparing hair treatments 3a and 3b with hair treatment 3d, hair treatments 3a and 3b using a hair composition containing bisabolol or glucosylhesperidin had a higher maintenance rate of initial elastic modulus than hair treatment 3d without use. You can check that. This is thought to be related to the inhibition of carbonylation by bisabolol or glucosylhesperidin.
또, 모발 처리 3a 및 3b 와, 모발 처리 3c 를 대비한 경우, 모발용 조성물 1, 2 를 병용한 모발 처리 3c 는, 일방의 조성물만을 사용한 모발 처리 3a 및 3b 보다 초기 탄성률의 유지율이 높았던 것을 확인할 수 있다. 이것은, 비사보롤 및 글루코실헤스페리딘의 병용이, 카르보닐화의 억제에 특히 의미가 있게 된다고 생각된다.In addition, when hair treatments 3a and 3b were compared with hair treatment 3c, it was confirmed that hair treatment 3c using the hair compositions 1 and 2 in combination had a higher initial elastic modulus retention rate than hair treatments 3a and 3b using only one composition. there is. This is thought to make the combined use of bisabolol and glucosylhesperidin particularly meaningful in suppressing carbonylation.
Claims (7)
모발에 도포 후, 씻어내지 않고 사용되는 모발용 조성물.According to claim 1,
A composition for hair that is applied to the hair and then used without washing it off.
열 또는 자외선에 의한 모발의 카르보닐화를 억제하기 위해서 사용되는 모발용 조성물.According to claim 1,
A composition for hair used to inhibit carbonylation of hair caused by heat or ultraviolet rays.
상기 열의 열원이, 헤어 드라이어 또는 헤어 아이론인 모발용 조성물.According to claim 3,
A composition for hair wherein the heat source is a hair dryer or hair iron.
비사보롤의 배합량이 0.02 질량％ 이상, 글루코실헤스페리딘의 배합량이 0.00005 질량％ 이상인 모발용 조성물.According to claim 1,
A hair composition containing 0.02% by mass or more of bisabolol and 0.00005% by mass or more of glucosylhesperidin.
초기 탄성률의 저하를 억제하기 위해서 사용되는 모발용 조성물.According to claim 1,
A composition for hair used to suppress a decrease in initial elastic modulus.