KR102579995B1 - Composite waterproof sheet including heat dissipation and heat shielding function and composite waterproofing method using the same - Google Patents

Composite waterproof sheet including heat dissipation and heat shielding function and composite waterproofing method using the same Download PDF

Info

Publication number
KR102579995B1
KR102579995B1 KR1020220158391A KR20220158391A KR102579995B1 KR 102579995 B1 KR102579995 B1 KR 102579995B1 KR 1020220158391 A KR1020220158391 A KR 1020220158391A KR 20220158391 A KR20220158391 A KR 20220158391A KR 102579995 B1 KR102579995 B1 KR 102579995B1
Authority
KR
South Korea
Prior art keywords
waterproof sheet
heat dissipation
layer
composite
composite waterproof
Prior art date
Application number
KR1020220158391A
Other languages
Korean (ko)
Inventor
배규호
Original Assignee
배규호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 배규호 filed Critical 배규호
Priority to KR1020220158391A priority Critical patent/KR102579995B1/en
Application granted granted Critical
Publication of KR102579995B1 publication Critical patent/KR102579995B1/en

Abstract

본 발명은 방열과 차열기능을 포함하는 복합 방수시트를 이용한 방수공법에 관한 것으로서, 보다 상세하게는 누수하자 빈도가 높은 방수시트의 이음부나, 틈새 및 접합부의 균열 부위에 씰링기능 및 자가치유기능을 가지는 아스팔트층을 구비한 방열과 차열기능을 포함하는 복합 방수시트 및 이를 이용한 복합 방수공법에 관한 것이다.The present invention relates to a waterproofing method using a composite waterproof sheet that includes heat dissipation and insulation functions. More specifically, the present invention relates to a waterproofing method using a composite waterproof sheet that has a heat dissipation and insulation function. More specifically, the present invention relates to a sealing function and a self-healing function at the joints, gaps, and cracks of the joints of the waterproof sheet with a high frequency of water leaks. The branch relates to a composite waterproofing sheet with heat dissipation and insulation functions with an asphalt layer and a composite waterproofing method using the same.

Description

방열과 차열기능을 포함하는 복합 방수시트 및 이를 이용한 복합 방수공법 {Composite waterproof sheet including heat dissipation and heat shielding function and composite waterproofing method using the same}Composite waterproof sheet including heat dissipation and heat shielding function and composite waterproofing method using the same {Composite waterproof sheet including heat dissipation and heat shielding function and composite waterproofing method using the same}

본 발명은 방열 및 차열기능을 포함하는 복합 방수시트 및 이를 이용한 복합 방수공법에 관한 것이다.The present invention relates to a composite waterproof sheet including heat dissipation and insulation functions and a composite waterproofing method using the same.

일반적인 건축 구조물은 강수 등으로부터 누수를 방지하며 구조물의 균열이나 내구성의 저하를 막기 위한 방수 작업이 필수적으로 요구된다.In general building structures, waterproofing work is essential to prevent water leakage from precipitation, etc. and to prevent cracks or deterioration of durability of the structure.

기존의 방수공법은 아스팔트 방수, 시멘트 액체방수, 시트방수 및 도막방수 등 여러 가지가 있으며, 이 중 아스팔트 방수는 가장 오래전부터 사용되어온 방수공법으로 아스팔트 펠트, 아스팔트 컴파운드 및 아스팔트 루핑 등의 용융아스팔트를 방수부위에 여러겹 바르는 방법이다. 상기 아스팔트 방수는 방수층의 도막이 비교적 두꺼워 방수효과가 우수하고, 내구성 및 수밀성이 뛰어나 방수효과가 좋으나 고체의 아스팔트를 고온에서 용융시켜 사용해야 하며, 겹층 시공을 하여야 하므로 공정이 복잡하고 특별한 시공기술이 요구되며 인건비가 많이 들어가는 문제점이 있었다. 또한, 상기 공법은 수직면의 시공이 불가능하고 이음부 및 접착부의 들뜸이 일어나기 쉬우며 온도의 변화에 민감하여 저온에서 방수층의 균열이 생기기 쉬운 문제점이 있었다.There are many existing waterproofing methods, such as asphalt waterproofing, cement liquid waterproofing, sheet waterproofing, and film waterproofing. Among these, asphalt waterproofing is the waterproofing method that has been used for the longest time and waterproofs molten asphalt such as asphalt felt, asphalt compound, and asphalt roofing. This is a method of applying several layers to the area. The above-mentioned asphalt waterproofing has excellent waterproofing effect because the coating film of the waterproofing layer is relatively thick, and has excellent durability and watertightness, so it has good waterproofing effect. However, solid asphalt must be melted at high temperature and used, and multi-layer construction must be used, so the process is complicated and special construction technology is required. There was a problem with high labor costs. In addition, the above method had problems in that it was impossible to construct on a vertical surface, that the joints and adhesive parts were easily lifted, and that the waterproofing layer was susceptible to cracks at low temperatures because it was sensitive to changes in temperature.

시트방수는 신축성이 우수한 합성 고무나 합성수지 또는 고무화 아스팔트 등을 주원료로 하여 일정 규격의 방수시트를 제작하고 이러한 시트 형상의 방수재를 방수공사를 하고자 하는 바탕면에 펼쳐 설치함으로써 방수층을 형성하는 방수공법으로서 시공이 비교적 간편하고 공사기간이 단축되는 장점이 있어 오늘날 널리 이용되는 방수공법 중 하나이다.Sheet waterproofing is a waterproofing method that creates a waterproofing layer by manufacturing a waterproofing sheet of a certain standard using highly elastic synthetic rubber, synthetic resin, or rubberized asphalt as the main raw material, and spreading and installing this sheet-shaped waterproofing material on the surface to be waterproofed. It is one of the waterproofing methods widely used today as it is relatively easy to construct and has the advantage of shortening the construction period.

시트방수는 상기 도막방수의 단점 중 방수층 두께 확보와 크랙에 대한 대응성에 대한 문제를 해결하기는 하나, 복잡한 구조물의 모서리나 돌출부의 밀실한 방수층의 확보에 어려움이 있는 단점이 있었다.Although sheet waterproofing solves the problems of securing the thickness of the waterproofing layer and responding to cracks among the disadvantages of the above-mentioned film waterproofing, it has the disadvantage of having difficulty securing a tight waterproofing layer at the corners or protrusions of complex structures.

본 발명은 상기 문제점을 해결하기 위하여 안출된 것으로서, 방열 및 차열기능을 포함하는 복합 방수시트 및 이를 이용한 복합 방수공법을 제공하기 위한 것이다.The present invention was developed to solve the above problems, and is intended to provide a composite waterproof sheet including heat dissipation and insulation functions and a composite waterproofing method using the same.

본 발명은 누수하자 빈도가 높은 방수시트의 이음부나, 틈새 및 접합부의 균열 부위에 씰링기능 및 자가치유기능을 가지는 아스팔트층을 구비한 방열과 차열기능을 포함하는 복합 방수시트 및 이를 이용한 복합 방수공법을 제공하기 위한 것이다.The present invention relates to a composite waterproof sheet including heat dissipation and insulation functions and an asphalt layer with a sealing function and self-healing function at the joints, gaps, and joint cracks of the waterproof sheet with a high frequency of water leaks, and a composite waterproofing method using the same. It is intended to provide.

본 발명은 PET필름의 상부 및 하부에 부직포를 합지하여 형성되는 제1부직포층; 상기 제1부직포층 상부에 구비되는 제1아스팔트 컴파운드층; 상기 제1아스팔트 컴파운드층 상부에 구비되어 방열성을 가지는 멜라민발포층; 상기 멜라민발포층 상부에 구비되는 제2아스팔트 컴파운드층; 상기 제2아스팔트 컴파운드층 상부에 구비되고 PET필름의 상부 및 하부에 부직포를 합지하여 형성되는 제2부직포층; 상기 제2부직포층 상부에 구비되고 방열성을 가지는 합성고분자층; 상기 합성고분자층 상부에 구비되는 제3부직포층; 을 포함하여 적층구조로 이루어진다.The present invention includes a first non-woven fabric layer formed by laminating non-woven fabric on the top and bottom of a PET film; A first asphalt compound layer provided on the first non-woven fabric layer; A melamine foam layer provided on the first asphalt compound layer and having heat dissipation properties; A second asphalt compound layer provided on top of the melamine foam layer; A second non-woven fabric layer provided on the second asphalt compound layer and formed by laminating non-woven fabric on the top and bottom of the PET film; A synthetic polymer layer provided on the second non-woven fabric layer and having heat dissipation properties; A third non-woven fabric layer provided on top of the synthetic polymer layer; It consists of a layered structure including.

상기 PET필름은 코로나 방전 처리하여 사용하고, 상기 코로나 방전 처리는 상온 및 상압에서 대기가스와 아르곤(Ar)가스를 혼합하는 단계; 코로나 방전장치에 5~12kV의 고주파 고전압 전원을 인가시켜 코로나 방전을 발생시키는 단계; 상기 코로나 방전이 발생되는 영역에 PET 필름을 통과시켜 코로나 방전 처리하는 단계; 상기 코로나 방전 처리하는 단계를 1~3회 반복하는 단계;를 포함하는 것을 특징으로 한다.The PET film is used by corona discharge treatment, and the corona discharge treatment includes mixing atmospheric gas and argon (Ar) gas at room temperature and pressure; Generating corona discharge by applying high-frequency high-voltage power of 5 to 12 kV to the corona discharge device; Corona discharge treatment by passing a PET film through the area where the corona discharge occurs; It is characterized in that it includes; repeating the corona discharge treatment step 1 to 3 times.

상기 제1아스팔트 컴파운드층은 크랙부위에 씰링기능 및 점착성을 가지는 아스팔트 씰링 컴파운드를 포함하되, 상기 아스팔트 씰링 컴파운드는 아스팔트 100중량부를 기준으로, 합성고무 40~60중량부, 합성수지 30~45중량부, 아크릴아마이드 15~18중량부, 규사 10~12중량부, 폴리부텐 30~40중량부를 혼합하여 구성되는 것을 특징으로 한다.The first asphalt compound layer includes an asphalt sealing compound having a sealing function and adhesion to crack areas, wherein the asphalt sealing compound includes 40 to 60 parts by weight of synthetic rubber, 30 to 45 parts by weight of synthetic resin, based on 100 parts by weight of asphalt, It is characterized by mixing 15 to 18 parts by weight of acrylamide, 10 to 12 parts by weight of silica sand, and 30 to 40 parts by weight of polybutene.

상기 제2아스팔트 컴파운드층은 두께가 1.0mm 내지 1.3mm로 형성되고 자가치유기능을 가지는 아스팔트 컴파운드를 포함하되, 상기 아스팔트 컴파운드는 아스팔트 100중량부를 기준으로, 탄산칼슘 20~25중량부, 벤토나이트 2~3중량부, 합성고무 40~60중량부, 합성수지 30~45중량부를 혼합하여 구성되는 것을 특징으로 한다.The second asphalt compound layer has a thickness of 1.0 mm to 1.3 mm and includes an asphalt compound having a self-healing function, wherein the asphalt compound contains 20 to 25 parts by weight of calcium carbonate and 2 to 25 parts by weight of bentonite, based on 100 parts by weight of asphalt. It is characterized by mixing 3 parts by weight, 40 to 60 parts by weight of synthetic rubber, and 30 to 45 parts by weight of synthetic resin.

상기 벤토나이트는 개질 된 벤토나이트를 포함할 수 있고, 상기 개질 된 벤토나이트는 증류수 1~1.5L에 세트리모늄(CTAB) 0.36~0.5g을 용해시킨 후 나노클레이 10~15g을 첨가하여 80~85℃의 온도에서 24~36시간 동안 교반하여 개질 용액을 제조하는 단계; 상기 개질 용액에 벤토나이트를 투입한 후 80~85℃의 온도에서 24~36시간 동안 교반한 다음 여과하는 과정을 3회 반복한 후 세척하는 단계; 상기 세척을 완료하여 개질 된 벤토나이트를 평균 입도가 150~200mesh가 되도록 분쇄하는 단계;를 포함하여 제조되는 것을 특징으로 한다.The bentonite may include modified bentonite, and the modified bentonite is prepared by dissolving 0.36 to 0.5 g of cetrimonium (CTAB) in 1 to 1.5 L of distilled water and then adding 10 to 15 g of nanoclay to a temperature of 80 to 85°C. Preparing a modified solution by stirring at temperature for 24 to 36 hours; Adding bentonite to the modified solution, stirring at a temperature of 80 to 85°C for 24 to 36 hours, then filtering, repeating the process three times, and then washing; It is characterized in that it is manufactured including the step of pulverizing the modified bentonite after completing the washing so that the average particle size is 150 to 200 mesh.

상기 합성고무는 IIR(Isobutylene Isoprene Rubber), SBR(Styrene Butadiene Rubber), SBS(Styrene Butadiene Styrene), NBR(Nitrile Butadiene Rubber) 중 선택된 어느 하나 이상을 포함하는 것을 특징으로 한다.The synthetic rubber is characterized in that it contains one or more selected from IIR (Isobutylene Isoprene Rubber), SBR (Styrene Butadiene Rubber), SBS (Styrene Butadiene Styrene), and NBR (Nitrile Butadiene Rubber).

상기 합성고분자층은 에틸렌비닐 아세테이트 코폴리머 (EVA), 열가소성 폴리올레핀 (TPO), 고밀도폴리에틸렌(HDPE), 폴리프로필렌(PP), 폴리염화비닐(PVC) 중 선택된 어느 하나 이상으로 이루어지고, 그래파이트를 더 포함하는 것을 특징으로 한다.The synthetic polymer layer is made of one or more selected from ethylene vinyl acetate copolymer (EVA), thermoplastic polyolefin (TPO), high-density polyethylene (HDPE), polypropylene (PP), and polyvinyl chloride (PVC), and graphite is further added. It is characterized by including.

상기 합성 고분자층은 30㎛~50㎛의 두께를 가지는 구리필름 동판층으로 대체하여 사용될 수 있는 것을 특징으로 한다.The synthetic polymer layer is characterized in that it can be used instead of a copper film copper plate layer having a thickness of 30㎛ to 50㎛.

상기 제1부직포층은 노출하여 사용 시 PET필름의 상부 및 하부에 부직포를 합지하여 형성되고, 비노출하여 사용 시 이형필름으로 형성되는 것을 특징으로 한다.The first non-woven fabric layer is formed by laminating non-woven fabric on the top and bottom of the PET film when exposed and used, and is formed as a release film when used not exposed.

상기 복합 방수시트를 이용한 복합 방수공법에 있어서, 방수작업 바탕면의 오염물질 및 수분을 제거하는 전처리단계; 상기 전처리단계가 완료된 상기 바탕면에 프라이머를 도포하는 단계; 상기 프라이머 도포가 완료된 상기 바탕면에 상기 복합 방수시트를 시공하는 복합 방수시트 시공단계; 상기 복합 방수시트가 부착된 바탕면의 코너, 테두리 및 시트간 접합부에 접착테이프를 시공하는 보강단계;를 포함하는 것을 특징으로 한다.In the composite waterproofing method using the composite waterproofing sheet, a pretreatment step of removing contaminants and moisture from the surface of the waterproofing work surface; Applying a primer to the background surface on which the pretreatment step has been completed; A composite waterproof sheet construction step of constructing the composite waterproof sheet on the base surface on which the primer application has been completed; and a reinforcing step of applying adhesive tape to the corners, edges, and joints between sheets of the base surface to which the composite waterproof sheet is attached.

상기 복합 방수시트 시공단계는 자동열풍융착기, 실란트, 메쉬테이프 중 선택된 하나 이상을 사용하여 접착하는 것을 특징으로 한다.The composite waterproof sheet construction step is characterized by bonding using one or more selected from an automatic hot air fusion machine, sealant, and mesh tape.

상기 보강단계 이후 우레탄 방수 도막재를 도포하는 우레탄 코팅단계를 더 포함하여 우레탄 코팅층(800)을 형성하는 것을 특징으로 한다.After the reinforcement step, the urethane coating layer 800 is formed by further including a urethane coating step of applying a urethane waterproof coating material.

상기 우레탄 코팅층(800) 상부에 상도 탑코팅층을 더 포함하여 형성되는 것을 특징으로 한다.It is characterized in that it is formed by further including a top coating layer on top of the urethane coating layer 800.

이상 살펴본 바와 같은 본 발명에 따르면 방열 및 차열기능을 포함하는 복합 방수 시트 및 이를 이용한 복합 방수공법을 제공할 수 있다.According to the present invention as described above, it is possible to provide a composite waterproof sheet including heat dissipation and insulation functions and a composite waterproofing method using the same.

또한, 본 발명에 따르면 누수의 빈도가 높은 방수시트의 이음부, 틈새 및 접합부의 균열부위에 씰링기능 및 자가치유기능을 가지는 아스팔트층을 구비하여 방수시트의 누수 차단이 가능하여 방수시공의 품질이 향상된 방열 및 차열기능을 포함하는 복합 방수 시트 및 이를 이용한 복합 방수공법을 제공할 수 있다.In addition, according to the present invention, an asphalt layer with a sealing function and a self-healing function is provided at the cracks in the joints, gaps, and joints of the waterproof sheet with a high frequency of water leaks, so that it is possible to block water leakage from the waterproof sheet, thereby improving the quality of waterproofing construction. A composite waterproof sheet with improved heat dissipation and insulation functions and a composite waterproofing method using the same can be provided.

또한, 본 발명에 따르면 방열 및 차열기능을 가지는 시트층을 적층한 후 시공 시 우레탄 방수 도막재를 도포 및 상도 탑코팅층을 추가적으로 형성함으로써 방열, 차열 및 방수의 성능이 증진된 방열 및 차열기능을 포함하는 복합 방수 시트 및 이를 이용한 복합 방수공법을 제공할 수 있다.In addition, according to the present invention, after laminating sheet layers with heat dissipation and insulating functions, a urethane waterproof coating material is applied and an additional top coating layer is formed during construction, thereby improving heat dissipation, insulating, and waterproofing performance. A composite waterproof sheet and a composite waterproofing method using the same can be provided.

도 1은 본 발명의 복합 방수시트의 구조를 나타낸 도면.1 is a diagram showing the structure of the composite waterproof sheet of the present invention.

본 발명은 방열과 차열기능을 포함하는 복합 방수시트 및 이를 이용한 복합 방수공법에 관한 것이다.The present invention relates to a composite waterproof sheet including heat dissipation and heat shielding functions and a composite waterproofing method using the same.

이하 첨부된 도면을 참고하여 본 발명의 방열과 차열기능을 포함하는 복합 방수시트에 대하여 상세히 설명한다.Hereinafter, the composite waterproof sheet including heat dissipation and heat shielding functions of the present invention will be described in detail with reference to the attached drawings.

도 1은 본 발명의 방열과 차열기능을 포함하는 복합 방수시트의 구조를 나타낸 도면이다.Figure 1 is a diagram showing the structure of a composite waterproof sheet including heat dissipation and heat shielding functions of the present invention.

도 1에 도시된 바와 같이, 본 발명의 복합 방수시트는 제1부직포층(100), 제1아스팔트층(200), 멜라민발포층(300), 제2아스팔트층(400), 제2부직포층(500), 합성고분자층(600) 및 제3부직포층(700)을 포함하여 적층구조로 구성된다.As shown in Figure 1, the composite waterproof sheet of the present invention includes a first non-woven layer 100, a first asphalt layer 200, a melamine foam layer 300, a second asphalt layer 400, and a second non-woven layer. It is composed of a laminated structure including (500), a synthetic polymer layer (600), and a third nonwoven layer (700).

또한 도 1에 도시된 바와 같이, 본 발명의 복합 방수시트를 이용한 복합 방수공법에 의한 상기 복합 방수시트 부착시공 시 우레탄 방수 도막재를 도포하여 우레탄 코팅층(800)을 더 포함할 수 있다.In addition, as shown in Figure 1, when attaching the composite waterproof sheet by a composite waterproofing method using the composite waterproof sheet of the present invention, a urethane waterproof coating material may be applied to further include a urethane coating layer 800.

상기 제1부직포층(100), 상기 제2부직포층(500) 및 상기 제3부직포층(700)은 열을 차단하는 역할을 위하여 PET필름의 상부 및 하부에 부직포를 합지하여 형성되는 것이 바람직하다. The first non-woven fabric layer 100, the second non-woven fabric layer 500, and the third non-woven fabric layer 700 are preferably formed by laminating non-woven fabric on the top and bottom of the PET film to block heat. .

여기에서, 상기 부직포는 상기 복합 방수시트의 기본 모양의 지지하기 위하여 구성되고 완충효과를 더 포함할 수 있다.Here, the non-woven fabric is configured to support the basic shape of the composite waterproof sheet and may further include a cushioning effect.

여기에서, 상기 PET필름의 두께는 30㎛ 내지 40㎛로 이루어지는 것이 바람직하다.Here, the thickness of the PET film is preferably 30㎛ to 40㎛.

상기 PET필름은 상기 부직포와의 접착효율을 높이기 위하여 코로나 방전 처리하여 사용하는 것이 바람직하다.It is preferable to use the PET film after corona discharge treatment to increase adhesion efficiency with the nonwoven fabric.

상기 코로나 방전 처리는 상온 및 상압에서 대기가스와 아르곤(Ar)가스를 혼합하는 단계; 코로나 방전장치에 5~12kV의 고주파 고전압 전원을 인가시켜 코로나 방전을 발생시키는 단계; 상기 코로나 방전이 발생되는 영역에 PET 필름을 통과시켜 코로나 방전 처리하는 단계; 상기 코로나 방전 처리하는 단계를 1~3회 반복하는 단계;를 포함하는 것이 바람직하다.The corona discharge treatment includes mixing atmospheric gas and argon (Ar) gas at room temperature and pressure; Generating corona discharge by applying high-frequency high-voltage power of 5 to 12 kV to the corona discharge device; Corona discharge treatment by passing a PET film through the area where the corona discharge occurs; It is preferable to include the step of repeating the corona discharge treatment step 1 to 3 times.

상기 제1부직포층(100)은 상기 방수시트를 노출하여 사용 시 PET필름의 상부 및 하부에 부직포를 합지하여 형성되고, 비노출 사용 시 이형필름으로 형성되는 것이 바람직하다.The first non-woven fabric layer 100 is preferably formed by laminating non-woven fabric on the top and bottom of the PET film when the waterproof sheet is used exposed, and is preferably formed as a release film when used not exposed.

상기 제1아스팔트층(200)은 상기 제1부직포층(100)의 상부에 구비되어 크랙부위에 씰링기능을 가지며 점착성을 포함하는 아스팔트 씰링 컴파운드로 이루어지는 것이 바람직하다.The first asphalt layer 200 is preferably provided on the top of the first non-woven fabric layer 100, has a sealing function in crack areas, and is made of an asphalt sealing compound containing adhesiveness.

상기 아스팔트 씰링 컴파운드는 접착력과 복원력이 우수하여 균열부 충진에 적합하며, 아스팔트 100중량부를 기준으로, 합성고무 40~60중량부, 합성수지 30~45중량부, 아크릴아마이드 15~18중량부, 규사 10~12중량부, 폴리부텐 30~40중량부를 혼합하여 구성되는 것이 바람직하다.The asphalt sealing compound has excellent adhesion and resilience and is suitable for filling cracks. Based on 100 parts by weight of asphalt, it contains 40 to 60 parts by weight of synthetic rubber, 30 to 45 parts by weight of synthetic resin, 15 to 18 parts by weight of acrylamide, and 10 parts by weight of silica sand. It is preferable to mix ~12 parts by weight and 30 to 40 parts by weight of polybutene.

또한, 상기 아스팔트 씰링 컴파운드는 내충격성 및 신축성이 강하여 시공 후 균열이 일어나지 않고 노화에도 강하며, 강력한 피막을 형성하므로 방수성능의 신용도가 매우 높은 것으로 알려져 있다.In addition, the asphalt sealing compound has strong impact resistance and elasticity, does not crack after construction, is resistant to aging, and forms a strong film, so it is known to have very high reliability in waterproofing performance.

상기 폴리부텐은 점착성능을 높이기 위하여 사용되는 첨가제이며, 저온유연성이 좋으며 내한성을 유지시킬 수 있어 저온에서의 부러짐을 방지하고, 바탕체와의 접착성을 가지며 화학적으로 안정되어 있어 자외선 변화가 적다.The polybutene is an additive used to increase adhesion performance. It has good low-temperature flexibility and can maintain cold resistance to prevent breaking at low temperatures. It has adhesion to the substrate and is chemically stable, so it is less susceptible to changes in ultraviolet rays.

상기 멜라민발포층(300)은 상기 제1아스팔트층(200)와 상기 제2아스팔트층(400)의 사이에 구비되어 단열성 및 방열성을 부여하는 중심재 역할을 하는 것이 바람직하다.The melamine foam layer 300 is preferably provided between the first asphalt layer 200 and the second asphalt layer 400 to serve as a central material that provides heat insulation and heat dissipation.

상기 제2아스팔트층(400)은 상기 멜라민발포층(300)의 상부에 구비되어 두께가 1.0mm 내지 1.3mm로 형성되고, 자가치유기능을 가지는 아스팔트 컴파운드를 포함하는 것이 바람직하다.The second asphalt layer 400 is provided on top of the melamine foam layer 300, has a thickness of 1.0 mm to 1.3 mm, and preferably includes an asphalt compound having a self-healing function.

상기 아스팔트 컴파운드는 아스팔트 100중량부를 기준으로, 탄산칼슘 20~25중량부, 벤토나이트 2~3중량부, 합성고무 40~60중량부, 합성수지 30~45중량부를 혼합하여 구성되는 것이 바람직하다.The asphalt compound is preferably composed of mixing 20 to 25 parts by weight of calcium carbonate, 2 to 3 parts by weight of bentonite, 40 to 60 parts by weight of synthetic rubber, and 30 to 45 parts by weight of synthetic resin, based on 100 parts by weight of asphalt.

상기 합성고무는 IIR(Isobutylene Isoprene Rubber), SBR(Styrene Butadiene Rubber), SBS(Styrene Butadiene Styrene), NBR(Nitrile Butadiene Rubber) 중 선택된 어느 하나 이상을 포함하는 것이 바람직하다.The synthetic rubber preferably includes one or more selected from IIR (Isobutylene Isoprene Rubber), SBR (Styrene Butadiene Rubber), SBS (Styrene Butadiene Styrene), and NBR (Nitrile Butadiene Rubber).

상기 IIR(Isobutylene Isoprene Rubber)는 부틸고무로, 이소부틸렌 (Isobutylen)과 소량의 이소프렌(Isoprene)을 약 -100℃에서 공중합체시켜 얻을 수 있고, 긴 사슬모양의 구조를 지닌 불활성 재료로서 극소량의 이중결합만 존재하는 포화도가 극도로 높은 고무이다. The IIR (Isobutylene Isoprene Rubber) is butyl rubber, which can be obtained by copolymerizing isobutylene and a small amount of isoprene at about -100°C. It is an inert material with a long chain-like structure and contains a very small amount of isoprene. It is an extremely highly saturated rubber with only double bonds present.

상기 IIR(Isobutylene Isoprene Rubber)는 주로 자착식 부틸형 방수층을 구성하는 재료로서, 접착제나 열풍기를 사용하지 않고 부틸고무 고유의 점착성과 부착성에 의해 방수층 형성이 가능한 고내구성 재료로 사용된다.The IIR (Isobutylene Isoprene Rubber) is mainly a material that constitutes a self-adhesive butyl-type waterproofing layer, and is used as a highly durable material capable of forming a waterproofing layer due to the inherent adhesiveness and adhesion of butyl rubber without using adhesives or heaters.

상기 벤토나이트는 주성분이 몬모릴로나이트인 점토광물로서, 상기 아스팔트 컴파운드를 구성하기 위한 배합공정에 첨가되는 물과 만나면 다량의 물을 흡수하여 팽창하는 능력이 있어 자가치유기능 가지는 아스팔트층을 형성할 수 있다.The bentonite is a clay mineral whose main component is montmorillonite, and has the ability to absorb a large amount of water and expand when it comes into contact with water added in the mixing process to form the asphalt compound, forming an asphalt layer with a self-healing function.

상기 벤토나이트는 개질 된 벤토나이트를 사용하는 것이 바람직하다.It is preferable to use modified bentonite as the bentonite.

상기 개질 된 벤토나이트는 증류수 1~1.5L에 세트리모늄(CTAB) 0.36~0.5g을 용해시킨 후 나노클레이 10~15g을 첨가하여 80~85℃의 온도에서 24~36시간 동안 교반하여 개질 용액을 제조하는 단계; 상기 개질 용액에 벤토나이트를 투입한 후 80~85℃의 온도에서 24~36시간 동안 교반한 다음 여과하는 과정을 3회 반복한 후 세척하는 단계; 상기 세척을 완료하여 개질 된 벤토나이트를 평균입도가 150~200mesh가 되도록 분쇄하는 단계;를 포함하여 제조하는 것이 바람직하다.The modified bentonite was prepared by dissolving 0.36 to 0.5 g of cetrimonium (CTAB) in 1 to 1.5 L of distilled water, adding 10 to 15 g of nanoclay, and stirring for 24 to 36 hours at a temperature of 80 to 85°C to form a modified solution. manufacturing step; Adding bentonite to the modified solution, stirring at a temperature of 80 to 85°C for 24 to 36 hours, then filtering, repeating the process three times, and then washing; It is preferable to manufacture it including the step of pulverizing the modified bentonite after completing the washing so that the average particle size is 150 to 200 mesh.

상기 합성고분자층(600)은 제2부직포층 상부에 구비되고 방열성을 가지는 에틸렌비닐 아세테이트 코폴리머(EVA), 열가소성 폴리올레핀(TPO), 고밀도폴리에틸렌(HDPE), 폴리프로필렌(PP), 폴리염화비닐(PVC) 중 선택된 어느 하나 이상으로 이루어지는 것이 바람직하다. The synthetic polymer layer 600 is provided on the second non-woven fabric layer and is made of ethylene vinyl acetate copolymer (EVA), thermoplastic polyolefin (TPO), high-density polyethylene (HDPE), polypropylene (PP), and polyvinyl chloride ( It is preferable that it is made of at least one selected from PVC).

여기에서, 상기 합성고분자층은 방열성능을 더욱 향상시키기 위하여 그래파이트를 더 포함하는 것이 바람직하다. Here, the synthetic polymer layer preferably further includes graphite to further improve heat dissipation performance.

여기에서, 상기 그래파이트는 상기 합성고분자층을 기준으로 0.5~1.0wt% 포함하는 것이 바람직하며, 0.5wt% 미만으로 포함할 경우에는 방열효과가 감소되고, 1.0wt% 초과하여 포함할 경우에는 딱딱하게 굳어 시트 층이 손상될 수 있다. Here, the graphite is preferably contained in an amount of 0.5 to 1.0 wt% based on the synthetic polymer layer. If it is contained in an amount of less than 0.5 wt%, the heat dissipation effect is reduced, and if it is contained in an amount exceeding 1.0 wt%, it becomes hard. It may harden and damage the sheet layer.

여기에서, 상기 합성고분자층은 30㎛~50㎛의 두께를 가지는 구리필름 동판층으로 대체하여 사용될 수 있다.Here, the synthetic polymer layer can be replaced with a copper film copper plate layer having a thickness of 30㎛ to 50㎛.

상기 제2부직포층(500), 상기 합성고분자층(600) 및 상기 제3부직포층(700) 세가지 층의 적층구조 두께는 0.3mm 내지 0.7mm로 형성되는 것이 바람직하다.The thickness of the three layers of the second non-woven fabric layer 500, the synthetic polymer layer 600, and the third non-woven fabric layer 700 is preferably 0.3 mm to 0.7 mm.

여기에서, 세 층의 두께가 0.3mm 미만인 경우 너무 얇아 강성이 부족하여 시트의 울음현상이 나타날 수 있고, 0.7mm를 초과하는 경우 너무 두꺼워 소성이 부족하여 시트의 유연성이 저하될 수 있다.Here, if the thickness of the three layers is less than 0.3mm, it is too thin and lacks rigidity, which may cause the sheet to cry. If it exceeds 0.7mm, it is too thick and plasticity may be insufficient, which may reduce the flexibility of the sheet.

본 발명의 또 다른 목적은 상기 방열과 차열기능을 포함하는 복합 방수시트를 이용한 복합 방수공법을 제공하는 것이다.Another object of the present invention is to provide a composite waterproofing method using a composite waterproof sheet that includes the heat dissipation and insulation functions.

본 발명의 방열과 차열기능을 포함하는 복합 방수시트를 이용한 복합 방수공법은 방수작업 바탕면의 오염물질 및 수분을 제거하는 전처리단계; 상기 전처리단계가 완료된 상기 바탕면에 프라이머를 도포하는 단계; 상기 프라이머 도포가 완료된 상기 바탕면에 상기 복합 방수시트를 시공하는 복합 방수시트 시공단계; 상기 복합 방수시트가 부착된 바탕면의 코너, 테두리 및 시트간 접합부에 접착테이프를 시공하는 보강단계;를 포함한다.The composite waterproofing method using a composite waterproof sheet containing heat dissipation and insulation functions of the present invention includes a pretreatment step of removing contaminants and moisture from the surface of the waterproofing work surface; Applying a primer to the background surface on which the pretreatment step has been completed; A composite waterproof sheet construction step of constructing the composite waterproof sheet on the base surface on which the primer application has been completed; It includes a reinforcing step of applying adhesive tape to the corners, edges, and joints between sheets of the base surface to which the composite waterproof sheet is attached.

상기 전처리단계는 상기 바탕면이 완전히 건조되었는지 확인한 후 구멍, 요철부분을 없애고 브러쉬나 압축공기를 이용하여 먼지, 녹, 모래 등과 같은 이물질을 깨끗이 제거하는 과정을 포함할 수 있다.The pretreatment step may include confirming that the background surface is completely dry, removing holes and uneven parts, and thoroughly removing foreign substances such as dust, rust, sand, etc. using a brush or compressed air.

상기 프라이머는 롤러나, 스프레이를 이용하여 도포할 수 있고, 도포된 프라이머는 점성이 없어질 때까지 건조시킨 후 오염이 없는지 확인하여 1~2회 재도포하는 과정을 포함할 수 있다.The primer can be applied using a roller or spray, and the applied primer may be dried until its viscosity disappears, then checked to see if there is any contamination, and then reapplied 1-2 times.

상기 복합 방수시트 시공단계는 자동열풍융착기, 실란트, 메쉬테이프 중 선택된 하나 이상을 사용하여 접착하는 것이 바람직하다.In the construction step of the composite waterproof sheet, it is preferable to adhere using one or more selected from an automatic hot air fusion machine, sealant, and mesh tape.

상기 보강단계 이후 우레탄 방수 도막재를 도포하는 우레탄 코팅단계를 더 포함하여 우레탄 코팅층(800)을 형성할 수 있고, 상기 우레탄 코팅층(800)의 두께는 1.0mm 내지 1.3mm으로 형성되는 것이 바람직하다.After the reinforcement step, a urethane coating step of applying a urethane waterproof coating material may be further included to form the urethane coating layer 800, and the thickness of the urethane coating layer 800 is preferably 1.0 mm to 1.3 mm.

상기 우레탄 방수 도막재는 일반 우레탄 방수 도막재 및 차열 우레탄 방수 도막재 중 선택된 어느 하나 이상을 사용할 수 있다.The urethane waterproofing coating material may be one or more selected from general urethane waterproofing coating materials and heat-insulating urethane waterproofing coating materials.

상기 우레탄 코팅층(800) 상부에 상도 탑코팅층을 더 포함하여 형성될 수 있다.It may be formed by further including a top coating layer on top of the urethane coating layer 800.

상기 상도 탑코팅층은 일반 상도 탑코팅 및 차열 상도 탑코팅 중 선택된 어느 하나 이상을 사용하여 상도 탑코팅층을 형성할 수 있다.The top coat top coating layer may be formed using one or more selected from a general top coat and a heat-insulating top coat.

이상에서 살펴본 바와 같이 본 발명의 방열과 차열기능을 포함하는 복합 방수시트 및 이를 이용한 복합 방수공법은 누수의 빈도가 높은 방수시트의 이음부, 틈새 및 접합부의 균열부위에 씰링기능 및 자가치유기능을 가지는 아스팔트층을 구비하여 복합 방수시트의 누수 차단이 가능하여 방수시공의 품질이 향상되며, 방열 및 차열기능을 가지는 시트층을 적층한 후 시공 시 우레탄 방수 도막재를 도포 및 상도 탑코팅층을 추가적으로 형성함으로써 방열, 차열 및 방수의 성능이 증진된 방열 및 차열기능을 포함하는 복합 방수시트 및 이를 이용한 복합 방수공법을 제공할 수 있다.As discussed above, the composite waterproof sheet containing heat dissipation and insulation functions of the present invention and the composite waterproofing method using the same have a sealing function and self-healing function in cracks at joints, gaps, and joints of the waterproof sheet with a high frequency of water leaks. The branch is equipped with an asphalt layer to prevent water leakage from the composite waterproof sheet, improving the quality of waterproofing construction. After laminating sheet layers with heat dissipation and insulation functions, a urethane waterproof coating material is applied and an additional top coating layer is formed during construction. By doing so, it is possible to provide a composite waterproof sheet including heat dissipation and insulation functions with improved heat dissipation, insulation, and waterproofing performance, and a composite waterproofing method using the same.

본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구의 범위에 의하여 나타내어지며, 특허청구의 범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.Those skilled in the art to which the present invention pertains will understand that the present invention can be implemented in other specific forms without changing its technical idea or essential features. Therefore, the embodiments described above should be understood in all respects as illustrative and not restrictive. The scope of the present invention is indicated by the scope of the claims described below rather than the detailed description above, and all changes or modified forms derived from the meaning and scope of the claims and their equivalent concepts are included in the scope of the present invention. must be interpreted.

1: 복합 방수시트
100 : 제1부직포층, 200 : 제1아스팔트 컴파운드층
300 : 멜라민발포층, 400 : 제2아스팔트 컴파운드층
500 : 제2부직포층, 600 : 합성고분자층
700 : 제3부직포층, 800 : 우레탄코팅층1: Composite waterproof sheet
100: first non-woven layer, 200: first asphalt compound layer
300: Melamine foam layer, 400: Second asphalt compound layer
500: second nonwoven layer, 600: synthetic polymer layer
700: third nonwoven layer, 800: urethane coating layer

Claims (13)

방열과 차열기능을 포함하는 복합 방수시트(1)에 있어서,
PET필름의 상부 및 하부에 부직포를 합지하여 형성되는 제1부직포층(100);
상기 제1부직포층 상부에 구비되는 제1아스팔트 컴파운드층(200);
상기 제1아스팔트 컴파운드층 상부에 구비되어 방열성을 가지는 멜라민발포층(300);
상기 멜라민발포층 상부에 구비되는 제2아스팔트 컴파운드층(400);
상기 제2아스팔트 컴파운드층 상부에 구비되고 PET필름의 상부 및 하부에 부직포를 합지하여 형성되는 제2부직포층(500);
상기 제2부직포층 상부에 구비되고 방열성을 가지는 합성고분자층(600);
상기 합성고분자층 상부에 구비되는 제3부직포층(700);을 포함하여 적층구조로 이루어지고,
상기 제1아스팔트 컴파운드층은,
크랙부위에 씰링기능 및 점착성을 가지는 아스팔트 씰링 컴파운드를 포함하되,
상기 아스팔트 씰링 컴파운드는 아스팔트 100중량부를 기준으로, 합성고무 40~60중량부, 합성수지 30~45중량부, 아크릴아마이드 15~18중량부, 규사 10~12중량부, 폴리부텐 30~40중량부를 혼합하여 구성되는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트.In the composite waterproof sheet (1) including heat dissipation and insulation functions,
A first non-woven fabric layer 100 formed by laminating non-woven fabric on the top and bottom of the PET film;
A first asphalt compound layer 200 provided on the first non-woven fabric layer;
A melamine foam layer 300 provided on the first asphalt compound layer and having heat dissipation properties;
A second asphalt compound layer 400 provided on top of the melamine foam layer;
A second non-woven fabric layer 500 provided on the second asphalt compound layer and formed by laminating non-woven fabric on the top and bottom of the PET film;
A synthetic polymer layer (600) provided on the second non-woven fabric layer and having heat dissipation properties;
It has a laminated structure, including a third non-woven fabric layer 700 provided on top of the synthetic polymer layer,
The first asphalt compound layer,
Contains an asphalt sealing compound that has a sealing function and adhesion to the crack area,
The asphalt sealing compound is a mixture of 40 to 60 parts by weight of synthetic rubber, 30 to 45 parts by weight of synthetic resin, 15 to 18 parts by weight of acrylamide, 10 to 12 parts by weight of silica sand, and 30 to 40 parts by weight of polybutene, based on 100 parts by weight of asphalt. A composite waterproof sheet containing heat dissipation and heat shielding functions, characterized in that it is composed of: 제1항에 있어서,
상기 PET필름은 코로나 방전 처리하여 사용하고,
상기 코로나 방전 처리는,
상온 및 상압에서 대기가스와 아르곤(Ar)가스를 혼합하는 단계;
코로나 방전장치에 5~12kV의 고주파 고전압 전원을 인가시켜 코로나 방전을 발생시키는 단계;
상기 코로나 방전이 발생되는 영역에 PET 필름을 통과시켜 코로나 방전 처리하는 단계;
상기 코로나 방전 처리하는 단계를 1~3회 반복하는 단계;를 포함하는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트.According to paragraph 1,
The PET film is used after corona discharge treatment,
The corona discharge treatment is,
Mixing atmospheric gas and argon (Ar) gas at room temperature and pressure;
Generating corona discharge by applying high-frequency high-voltage power of 5 to 12 kV to the corona discharge device;
Corona discharge treatment by passing a PET film through the area where the corona discharge occurs;
A composite waterproof sheet including heat dissipation and heat shielding functions, comprising: repeating the corona discharge treatment step 1 to 3 times. 삭제delete 제1항에 있어서,
상기 제2아스팔트 컴파운드층은 두께가 1.0mm 내지 1.3mm로 형성되고 자가치유기능을 가지는 아스팔트 컴파운드를 포함하되,
상기 아스팔트 컴파운드는,
아스팔트 100중량부를 기준으로, 탄산칼슘 20~25중량부, 벤토나이트 2~3중량부, 합성고무 40~60중량부, 합성수지 30~45중량부를 혼합하여 구성되는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트.According to paragraph 1,
The second asphalt compound layer has a thickness of 1.0 mm to 1.3 mm and includes an asphalt compound having a self-healing function,
The asphalt compound is,
Based on 100 parts by weight of asphalt, it is composed of mixing 20 to 25 parts by weight of calcium carbonate, 2 to 3 parts by weight of bentonite, 40 to 60 parts by weight of synthetic rubber, and 30 to 45 parts by weight of synthetic resin, and includes heat dissipation and insulation functions. Composite waterproof sheet. 제1항 또는 제4항 중 어느 한 항에 있어서,
상기 합성고무는,
IIR(Isobutylene Isoprene Rubber), SBR(Styrene Butadiene Rubber), SBS(Styrene Butadiene Styrene), NBR(Nitrile Butadiene Rubber) 중 선택된 어느 하나 이상을 포함하는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트.According to any one of paragraphs 1 and 4,
The synthetic rubber is,
A composite waterproof sheet with heat dissipation and insulation functions, characterized in that it contains at least one selected from IIR (Isobutylene Isoprene Rubber), SBR (Styrene Butadiene Rubber), SBS (Styrene Butadiene Styrene), and NBR (Nitrile Butadiene Rubber). 제4항에 있어서,
상기 벤토나이트는 개질 된 벤토나이트를 포함할 수 있고,
상기 개질 된 벤토나이트는,
증류수 1~1.5L에 세트리모늄(CTAB) 0.36~0.5g을 용해시킨 후 나노클레이 10~15g을 첨가하여 80~85℃의 온도에서 24~36시간 동안 교반하여 개질 용액을 제조하는 단계;
상기 개질 용액에 벤토나이트를 투입한 후 80~85℃의 온도에서 24~36시간 동안 교반한 다음 여과하는 과정을 3회 반복한 후 세척하는 단계;
상기 세척을 완료하여 개질 된 벤토나이트를 평균 입도가 150~200mesh가 되도록 분쇄하는 단계;를 포함하여 제조되는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트.According to paragraph 4,
The bentonite may include modified bentonite,
The modified bentonite is,
Preparing a modified solution by dissolving 0.36-0.5 g of cetrimonium (CTAB) in 1-1.5 L of distilled water, adding 10-15 g of nanoclay, and stirring for 24-36 hours at a temperature of 80-85°C;
Adding bentonite to the modified solution, stirring at a temperature of 80 to 85°C for 24 to 36 hours, then filtering, repeating the process three times, and then washing;
A composite waterproof sheet containing heat dissipation and heat shielding functions, characterized in that it is manufactured including the step of pulverizing the modified bentonite after completing the washing so that the average particle size is 150 to 200 mesh. 제1항에 있어서,
상기 합성고분자층은,
에틸렌비닐 아세테이트 코폴리머 (EVA), 열가소성 폴리올레핀 (TPO), 고밀도폴리에틸렌(HDPE), 폴리프로필렌(PP), 폴리염화비닐(PVC) 중 선택된 어느 하나 이상으로 이루어지고,
그래파이트를 더 포함하는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트.According to paragraph 1,
The synthetic polymer layer is,
Consists of one or more selected from ethylene vinyl acetate copolymer (EVA), thermoplastic polyolefin (TPO), high-density polyethylene (HDPE), polypropylene (PP), and polyvinyl chloride (PVC),
A composite waterproof sheet with heat dissipation and heat shielding functions, characterized by further containing graphite. 제1항에 있어서,
상기 합성 고분자층은,
30㎛~50㎛의 두께를 가지는 구리필름 동판층으로 대체하여 사용될 수 있는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트.According to paragraph 1,
The synthetic polymer layer is,
A composite waterproof sheet containing heat dissipation and insulation functions, characterized in that it can be used in place of a copper film layer having a thickness of 30㎛ to 50㎛. 제1항에 있어서,
상기 제1부직포층은,
노출하여 사용 시 PET필름의 상부 및 하부에 부직포를 합지하여 형성되고,
비노출하여 사용 시 이형필름으로 형성되는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트.According to paragraph 1,
The first nonwoven layer is,
When exposed and used, it is formed by laminating non-woven fabric on the top and bottom of the PET film,
A composite waterproof sheet containing heat dissipation and heat shielding functions, which is formed into a release film when used in a non-exposed manner. 복합 방수시트를 이용한 복합 방수공법에 있어서,
방수작업 바탕면의 오염물질 및 수분을 제거하는 전처리단계;
상기 전처리단계가 완료된 바탕면에 프라이머를 도포하는 단계;
상기 프라이머 도포가 완료된 바탕면에 복합 방수시트를 시공하는 복합 방수시트 시공단계;
상기 복합 방수시트가 시공된 바탕면의 코너, 테두리 및 시트간 접합부에 접착테이프를 시공하는 보강단계;를 포함하되,
상기 복합 방수시트는 제1항, 제2항, 제4항 및 제6항 내지 제9항 중 어느 한 항의 방열과 차열기능을 포함하는 복합 방수시트인 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트를 이용한 복합 방수공법.In the composite waterproofing method using a composite waterproof sheet,
Pretreatment step to remove contaminants and moisture from the waterproofing work surface;
Applying a primer to the background surface on which the pretreatment step has been completed;
A composite waterproof sheet construction step of constructing a composite waterproof sheet on the base surface on which the primer application has been completed;
Including a reinforcing step of applying adhesive tape to the corners, edges, and joints between sheets of the base surface on which the composite waterproof sheet is constructed,
The composite waterproof sheet includes heat dissipation and heat insulating functions, characterized in that it is a composite waterproof sheet including the heat dissipation and insulating functions of any one of claims 1, 2, 4, and 6 to 9. Composite waterproofing method using composite waterproofing sheets. 제10항에 있어서,
상기 복합 방수시트 시공단계는,
자동열풍융착기, 실란트, 메쉬테이프 중 선택된 하나 이상을 사용하여 접착하는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트를 이용한 복합 방수공법.According to clause 10,
The composite waterproof sheet construction step is,
A composite waterproofing method using a composite waterproofing sheet with heat dissipation and heat shielding functions, characterized in that it is bonded using one or more selected from an automatic hot air welder, sealant, or mesh tape. 제10항에 있어서,
상기 보강단계 이후 우레탄 방수 도막재를 도포하는 우레탄 코팅단계를 더 포함하여 우레탄 코팅층(800)을 형성하는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트를 이용한 복합 방수공법.According to clause 10,
A composite waterproofing method using a composite waterproof sheet containing heat dissipation and insulation functions, characterized in that it further includes a urethane coating step of applying a urethane waterproofing coating material after the reinforcement step to form a urethane coating layer (800). 제12항에 있어서,
상기 우레탄 코팅층(800) 상부에 상도 탑코팅층을 더 포함하여 형성되는 것을 특징으로 하는 방열과 차열기능을 포함하는 복합 방수시트를 이용한 복합 방수공법.
According to clause 12,
A composite waterproofing method using a composite waterproof sheet containing heat dissipation and heat shielding functions, characterized in that a top coating layer is further formed on top of the urethane coating layer 800.
KR1020220158391A 2022-11-23 2022-11-23 Composite waterproof sheet including heat dissipation and heat shielding function and composite waterproofing method using the same KR102579995B1 (en)