KR102575627B1 - A functional expanding agent with core-shell structure - Google Patents
A functional expanding agent with core-shell structure Download PDFInfo
- Publication number
- KR102575627B1 KR102575627B1 KR1020210068733A KR20210068733A KR102575627B1 KR 102575627 B1 KR102575627 B1 KR 102575627B1 KR 1020210068733 A KR1020210068733 A KR 1020210068733A KR 20210068733 A KR20210068733 A KR 20210068733A KR 102575627 B1 KR102575627 B1 KR 102575627B1
- Authority
- KR
- South Korea
- Prior art keywords
- capsule
- hydrogen peroxide
- urea
- weight
- core
- Prior art date
Abstract
본 발명은 코어-쉘 팽창제의 제조방법 및 이로부터 제조되는 코어-쉘 팽창제에 관한 것으로, 보다 상세하게는 요소 및 과산화수소를 혼합하여 요소-과산화수소 착물을 제조하는 단계; 상기 요소-과산화수소 착물에 유화제를 첨가하여 캡슐 내부층을 형성하는 단계; 상기 캡슐 내부층에 열경화성 수지를 첨가하여 캡슐 외부층을 형성하는 단계; 및 상기 캡슐 외부층을 경화시켜 캡슐을 제조하는 단계를 포함하는 코어-쉘 팽창제의 제조방법 및 이로부터 제조되는 코어-쉘 팽창제에 관한 것이다. The present invention relates to a method for preparing a core-shell expanding agent and a core-shell expanding agent prepared therefrom, and more particularly, to preparing a urea-hydrogen peroxide complex by mixing urea and hydrogen peroxide; forming an inner layer of the capsule by adding an emulsifier to the urea-hydrogen peroxide complex; forming an outer layer of the capsule by adding a thermosetting resin to the inner layer of the capsule; and curing the outer layer of the capsule to produce a capsule.
Description
본 발명은 코어-쉘 팽창제의 제조방법 및 이로부터 제조되는 코어-쉘 팽창제에 관한 것으로, 보다 상세하게는 요소 및 과산화수소를 혼합하여 요소-과산화수소 착물을 제조하는 단계; 상기 요소-과산화수소 착물에 유화제를 첨가하여 캡슐 내부층을 형성하는 단계; 상기 캡슐 내부층에 열경화성 수지를 첨가하여 캡슐 외부층을 형성하는 단계; 및 상기 캡슐 외부층을 경화시켜 캡슐을 제조하는 단계를 포함하는 코어-쉘 팽창제의 제조방법 및 이로부터 제조되는 코어-쉘 팽창제에 관한 것이다. The present invention relates to a method for preparing a core-shell expanding agent and a core-shell expanding agent prepared therefrom, and more particularly, to preparing a urea-hydrogen peroxide complex by mixing urea and hydrogen peroxide; forming an inner layer of the capsule by adding an emulsifier to the urea-hydrogen peroxide complex; forming an outer layer of the capsule by adding a thermosetting resin to the inner layer of the capsule; and curing the outer layer of the capsule to produce a capsule.
팽창제는 플라스틱, 제지, 도료 등의 다양한 분야에 활용되어, 제품의 밀도, 기공도, 단열성, 치수안정성, 기계적 특성, 화학적 특성 등을 조절하는 역할을 수행한다. Expansion agents are used in various fields such as plastics, paper, and paints, and play a role in adjusting the density, porosity, insulation, dimensional stability, mechanical properties, and chemical properties of products.
이와 관련하여 한국공개특허 제10-2020-0010206호는 플루오르화 화합물을 포함하는 팽창제를 개시하고 있다. In this regard, Korean Patent Publication No. 10-2020-0010206 discloses an expanding agent containing a fluorinated compound.
그러나 상기 팽창제는 환경적으로 유해하고, 팽창성, 단열성, 열안정성, 치수안정성 등이 불량하여 플라스틱, 제지, 도료 등의 제품 제조에 효과적으로 사용될 수 없다. However, the expanding agent is environmentally harmful and has poor expansibility, heat insulation, thermal stability, and dimensional stability, so that it cannot be effectively used in the manufacture of products such as plastics, paper, and paints.
따라서 친환경 소재이면서 팽창성, 단열성, 열안정성, 치수안정성 등이 우수하여 플라스틱, 제지, 도료 등의 제품 제조에 효과적으로 사용될 수 있는 팽창제에 대한 기술개발이 필요하다. Therefore, it is necessary to develop a technology for an expanding agent that can be effectively used in the manufacture of products such as plastic, paper, and paint, as it is an eco-friendly material and has excellent expandability, heat insulation, thermal stability, and dimensional stability.
본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로서, 친환경 소재이면서 팽창성, 단열성, 열안정성, 치수안정성 등이 우수하여 플라스틱, 제지, 도료 등의 제품 제조에 안정적으로 사용될 수 있는 팽창제의 제조방법 및 이로부터 제조되는 팽창제를 제공하는 것을 목적으로 한다. The present invention has been devised to solve the above problems, and is an eco-friendly material with excellent expandability, heat insulation, thermal stability, dimensional stability, etc., and a method for producing an expanding agent that can be stably used in the manufacture of products such as plastics, paper, paints, etc. And it is an object to provide an expanding agent prepared therefrom.
상기와 같은 목적을 달성하기 위하여, 본 발명은 요소 및 과산화수소를 혼합하여 요소-과산화수소 착물을 제조하는 단계;In order to achieve the above object, the present invention comprises the steps of preparing a urea-hydrogen peroxide complex by mixing urea and hydrogen peroxide;
상기 요소-과산화수소 착물에 유화제를 첨가하여 캡슐 내부층을 형성하는 단계;forming an inner layer of the capsule by adding an emulsifier to the urea-hydrogen peroxide complex;
상기 캡슐 내부층에 열경화성 수지를 첨가하여 캡슐 외부층을 형성하는 단계; 및forming an outer layer of the capsule by adding a thermosetting resin to the inner layer of the capsule; and
상기 캡슐 외부층을 경화시켜 캡슐을 제조하는 단계를 포함하는 코어-쉘 팽창제의 제조방법을 제공한다.It provides a method for manufacturing a core-shell expanding agent comprising the step of preparing a capsule by curing the outer layer of the capsule.
본 발명의 일실시예에 있어서, 상기 유화제는 폴리스티렌 술폰산(polystyrene sulfonic acid), 스티렌-말레인 무수물 공중합체(styrene-maleic anhydride copolymer), 소르비탄의 지방산 에스테르 및 폴리옥시에틸렌 소르비탄의 지방산 에스테르로부터 하나 이상 선택되는 것을 특징으로 한다. In one embodiment of the present invention, the emulsifier is made from polystyrene sulfonic acid, styrene-maleic anhydride copolymer, fatty acid ester of sorbitan, and fatty acid ester of polyoxyethylene sorbitan. Characterized in that one or more are selected.
본 발명의 일실시예에 있어서, 상기 열경화성 수지는 멜라민 수지, 페놀 수지, 폴리우레탄, 에폭시 수지, 불포화폴리에스테르 수지, 멜라민-포름알데히드 수지 및 페놀-포름알데히드 수지로부터 하나 이상 선택되는 것을 특징으로 한다. In one embodiment of the present invention, the thermosetting resin is characterized in that at least one selected from melamine resin, phenol resin, polyurethane, epoxy resin, unsaturated polyester resin, melamine-formaldehyde resin and phenol-formaldehyde resin .
또한 본 발명은 요소-과산화수소 착물을 포함하는 코어; 및 상기 코어를 둘러싸는 쉘로 이루어지며, 상기 쉘은 코어의 외부에 열경화성 수지가 경화되어 형성되는 것을 특징으로 하는 코어-쉘 팽창제를 제공한다.In another aspect, the present invention relates to a core comprising a urea-hydrogen peroxide complex; and a shell surrounding the core, wherein the shell is formed by curing a thermosetting resin on the outside of the core.
본 발명의 일실시예에 있어서, 상기 열경화성 수지는 멜라민 수지, 페놀 수지, 폴리우레탄, 에폭시 수지, 불포화폴리에스테르 수지, 멜라민-포름알데히드 수지 및 페놀-포름알데히드 수지로부터 하나 이상 선택되는 것을 특징으로 한다.In one embodiment of the present invention, the thermosetting resin is characterized in that at least one selected from melamine resin, phenol resin, polyurethane, epoxy resin, unsaturated polyester resin, melamine-formaldehyde resin and phenol-formaldehyde resin .
본 발명은 친환경 소재이면서 팽창성, 단열성, 열안정성, 치수안정성 등이 우수하여 플라스틱, 제지, 도료 등의 제품 제조에 안정적으로 사용될 수 있는 팽창제의 제조방법 및 이로부터 제조되는 팽창제를 제공할 수 있다. The present invention is an eco-friendly material and excellent in expandability, heat insulation, thermal stability, dimensional stability, etc., so that it can be stably used in the manufacture of products such as plastic, paper, paint, and the like.
도 1은 본 발명의 코어-쉘 팽창제의 광학현미경 이미지를 나타낸다.
도 2는 본 발명의 코어-쉘 팽창제의 SEM 이미지를 나타낸다.
도 3은 본 발명의 코어-쉘 팽창제의 입자크기를 나타낸다. 1 shows an optical microscope image of the core-shell expanding agent of the present invention.
2 shows a SEM image of the core-shell expanding agent of the present invention.
3 shows the particle size of the core-shell expanding agent of the present invention.
이하 실시예를 바탕으로 본 발명을 상세히 설명한다. 본 발명에 사용된 용어, 실시예 등은 본 발명을 보다 구체적으로 설명하고 통상의 기술자의 이해를 돕기 위하여 예시된 것에 불과할 뿐이며, 본 발명의 권리범위 등이 이에 한정되어 해석되어서는 안 된다.The present invention will be described in detail based on the following examples. The terms, examples, etc. used in the present invention are merely exemplified to explain the present invention in more detail and help the understanding of those skilled in the art, and the scope of the present invention should not be construed as being limited thereto.
본 발명에 사용되는 기술 용어 및 과학 용어는 다른 정의가 없다면 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 나타낸다. Technical terms and scientific terms used in the present invention represent meanings commonly understood by those of ordinary skill in the art to which this invention belongs, unless otherwise defined.
본 발명은 요소 및 과산화수소를 혼합하여 요소-과산화수소 착물을 제조하는 단계;The present invention comprises the steps of preparing a urea-hydrogen peroxide complex by mixing urea and hydrogen peroxide;
상기 요소-과산화수소 착물에 유화제를 첨가하여 캡슐 내부층을 형성하는 단계;forming an inner layer of the capsule by adding an emulsifier to the urea-hydrogen peroxide complex;
상기 캡슐 내부층에 열경화성 수지를 첨가하여 캡슐 외부층을 형성하는 단계; 및forming an outer layer of the capsule by adding a thermosetting resin to the inner layer of the capsule; and
상기 캡슐 외부층을 경화시켜 캡슐을 제조하는 단계를 포함하는 코어-쉘 팽창제의 제조방법에 관한 것이다. It relates to a method for manufacturing a core-shell expanding agent comprising the step of preparing a capsule by curing the outer layer of the capsule.
상기 코어-쉘 팽창제는 요소-과산화수소 착물을 포함하는 코어; 및 상기 코어를 둘러싸는 쉘로 이루어지는 나노캡슐 형태를 갖는다. The core-shell expanding agent includes a core containing a urea-hydrogen peroxide complex; And it has a nanocapsule form consisting of a shell surrounding the core.
상기 코어-쉘 팽창제는 요소-과산화수소 착물이 유화된 형태로 캡슐 내부층을 형성하고, 나노캡슐 외부에 열경화성 수지가 경화되어 형성되는 캡슐 외부층을 갖는 코어-쉘 구조를 나타낸다. The core-shell expanding agent has a core-shell structure in which an inner capsule layer is formed in an emulsified form of a urea-hydrogen peroxide complex and an outer capsule layer formed by curing a thermosetting resin outside the nanocapsule.
상기 요소 및 과산화수소를 혼합하여 요소-과산화수소 착물을 제조할 수 있다. 이때 과산화수소 100중량부에 대하여 요소 5~40중량부가 사용될 수 있다. 상기 수치범위를 만족하는 경우 착물의 분산성 및 입자안정성이 극대화될 수 있다. A urea-hydrogen peroxide complex may be prepared by mixing the urea and hydrogen peroxide. At this time, 5 to 40 parts by weight of urea may be used based on 100 parts by weight of hydrogen peroxide. When the above numerical range is satisfied, dispersibility and particle stability of the complex may be maximized.
상기 요소 및 과산화수소를 가열하여 혼합한 후 냉각하여 요소-과산화수소 착물을 수득할 수 있다. The urea and hydrogen peroxide may be mixed by heating and then cooled to obtain a urea-hydrogen peroxide complex.
상기 요소-과산화수소 착물에 유화제를 첨가하고 유화시켜 캡슐 내부층을 형성할 수 있다. An emulsifier may be added and emulsified to the urea-hydrogen peroxide complex to form an inner layer of the capsule.
상기 유화제는 폴리스티렌 술폰산(polystyrene sulfonic acid), 스티렌-말레인 무수물 공중합체(styrene-maleic anhydride copolymer), 소르비탄의 지방산 에스테르 및 폴리옥시에틸렌 소르비탄의 지방산 에스테르로부터 하나 이상 선택될 수 있다. The emulsifier may be one or more selected from polystyrene sulfonic acid, styrene-maleic anhydride copolymer, fatty acid ester of sorbitan, and fatty acid ester of polyoxyethylene sorbitan.
상기 유화제는 수용성 고분자 물질이 사용될 수 있으며, 보다 구체적으로는 음이온성 계면활성제인 수용성 고분자 물질이 사용될 수 있다. The emulsifier may be a water-soluble polymer material, and more specifically, a water-soluble polymer material that is an anionic surfactant.
예를 들어, 상기 수용성 고분자 물질은 폴리스티렌 술폰산, 스티렌-말레인 무수물 공중합체 등을 사용할 수 있으며, 유화제의 중량평균분자량은 100,000~1,000,000g/mol 인 것이 점도 및 유화특성의 측면에서 바람직하다.For example, the water-soluble polymer material may be polystyrene sulfonic acid, styrene-maleic anhydride copolymer, etc., and the weight average molecular weight of the emulsifier is preferably 100,000 to 1,000,000 g/mol in terms of viscosity and emulsification characteristics.
상기 소르비탄의 지방산 에스테르는 소르비탄 모노라우레이트, 소르비탄 모노팔미테이트, 소르비탄 모노스테아레이트, 소르비탄 모노올레이트 등이고, 폴리옥시에틸렌 소르비탄의 지방산 에스테르는 폴리옥시에틸렌 소르비탄 모노라우레이트, 폴리옥시에틸렌 소르비탄 모노팔미테이트, 폴리옥시에틸렌 소르비탄 모노스테아레이트, 폴리옥시에틸렌 소르비탄 모노올레이트 등이 제한 없이 사용될 수 있다. The fatty acid ester of sorbitan is sorbitan monolaurate, sorbitan monopalmitate, sorbitan monostearate, sorbitan monooleate, etc., and the fatty acid ester of polyoxyethylene sorbitan is polyoxyethylene sorbitan monolaurate, Polyoxyethylene sorbitan monopalmitate, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan monooleate and the like can be used without limitation.
구체적인 일예로, 상기 소르비탄의 지방산 에스테르로는 스판 80이 있고, 폴리옥시에틸렌 소르비탄의 지방산 에스테르로는 폴리소르베이트 80을 들 수 있다. As a specific example, the sorbitan fatty acid ester includes Span 80, and the polyoxyethylene sorbitan fatty acid ester includes polysorbate 80.
상기 유화제는 유화제 수용액의 형태로 사용되는 것이 바람직하며, 이때 유화제 수용액에 포함된 유화제의 함량은 1~10중량%인 것이 바람직하다. The emulsifier is preferably used in the form of an aqueous emulsifier solution, wherein the content of the emulsifier contained in the aqueous emulsifier solution is preferably 1 to 10% by weight.
상기 유화제 수용액의 함량은 상기 요소-과산화수소 착물 100중량부에 대해 10~400중량부인 것이 바람직하다. The amount of the aqueous emulsifier solution is preferably 10 to 400 parts by weight based on 100 parts by weight of the urea-hydrogen peroxide complex.
상기 캡슐 내부층에 열경화성 수지를 첨가하고 교반하여 캡슐 외부층을 형성한 후, 상기 캡슐 외부층을 경화시켜 캡슐을 제조할 수 있다. A capsule may be manufactured by adding a thermosetting resin to the inner layer of the capsule and stirring to form an outer layer of the capsule, and then curing the outer layer of the capsule.
상기 나노캡슐 외부층은 열경화성 수지로 형성됨으로써 팽창제의 내구성, 내열성 및 내용매성을 향상시킬 수 있으며, 이로 인해 외부에서 인가되는 온도, 압력, 용매 등에 의해 내부층을 보호할 수 있다. 만약 상기 나노캡슐 외부층이 열가소성 수지로 형성될 경우, 외부에서 인가되는 온도, 압력, 용매 등에 의하여 내부층이 변형되거나 손상되어 팽창특성이 저하될 수 있다. Since the outer layer of the nanocapsule is formed of a thermosetting resin, durability, heat resistance, and solvent resistance of the expanding agent may be improved, and thus the inner layer may be protected by temperature, pressure, solvent, or the like applied from the outside. If the outer layer of the nanocapsule is formed of a thermoplastic resin, the inner layer may be deformed or damaged by externally applied temperature, pressure, solvent, etc., and thus the expansion characteristics may deteriorate.
상기 열경화성 수지는 멜라민 수지, 페놀 수지, 폴리우레탄, 에폭시 수지, 불포화폴리에스테르 수지, 멜라민-포름알데히드 수지 및 페놀-포름알데히드 수지로부터 하나 이상 사용될 수 있다. The thermosetting resin may be one or more selected from melamine resin, phenol resin, polyurethane, epoxy resin, unsaturated polyester resin, melamine-formaldehyde resin and phenol-formaldehyde resin.
상기 열경화성 수지의 함량은 요소-과산화수소 착물 100중량부에 대하여 10~100중량부인 것이 바람직하고, 보다 바람직하게는 30~80중량부인 것이 좋다. 열경화성 수지의 함량이 100중량부를 초과하면 팽창특성이 저하되고, 10중량부 미만이면 나노캡슐의 내열성과 내용매성이 저하된다. The content of the thermosetting resin is preferably 10 to 100 parts by weight, more preferably 30 to 80 parts by weight, based on 100 parts by weight of the urea-hydrogen peroxide complex. If the content of the thermosetting resin exceeds 100 parts by weight, the expansion properties are lowered, and if it is less than 10 parts by weight, the heat resistance and solvent resistance of the nanocapsules are lowered.
상기 열경화성 수지는 멜라민-포름알데히드 수지 및 페놀-포름알데히드 수지를 동시에 사용할 수 있으며, 이때 멜라민-포름알데히드 수지 및 페놀-포름알데히드 수지의 중량비는 60~80:20~40 인 것이 바람직하다. 중량비가 상기 수치범위를 만족하는 경우, 팽창특성 및 내열성이 극대화될 수 있다. The thermosetting resin may use a melamine-formaldehyde resin and a phenol-formaldehyde resin at the same time, and in this case, the weight ratio of the melamine-formaldehyde resin and the phenol-formaldehyde resin is preferably 60 to 80:20 to 40. When the weight ratio satisfies the above numerical range, expansion characteristics and heat resistance may be maximized.
상기 열경화성 수지는 50~150℃에서 1~10시간 교반하면서 경화시켜 캡슐 외부층을 형성할 수 있다. The thermosetting resin may be cured while stirring at 50 to 150° C. for 1 to 10 hours to form an outer layer of the capsule.
또한 상기 캡슐 외부층은 아크릴레이트기 함유 실란 커플링제 및 아크릴산 모노머의 공중합체를 추가로 포함할 수 있다. In addition, the outer layer of the capsule may further include a copolymer of an acrylate group-containing silane coupling agent and an acrylic acid monomer.
상기 아크릴레이트기 함유 실란 커플링제로는 3-메타크릴록시프로필메틸디메톡시실란, 3-메타크릴록시프로필트리메톡시실란, 3-메타크릴록시프로필메틸디에톡시실란, 3-메타크릴록시프로필트리에톡시실란, 3-아크릴록시프로필트리메톡시실란, 메타크릴록시메틸트리에톡시실란, 메타크릴록시메틸트리메톡시실란 등이 있다. The acrylate group-containing silane coupling agent includes 3-methacryloxypropylmethyldimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-methacryloxypropylmethyldiethoxysilane, 3-methacryloxypropyltri ethoxysilane, 3-acryloxypropyltrimethoxysilane, methacryloxymethyltriethoxysilane, methacryloxymethyltrimethoxysilane and the like.
상기 아크릴산 모노머는 아크릴산, 메타크릴산, 카르복실 에틸아크릴레이트, 카르복실 에틸메타크릴레이트, 카르복실 펜틸아크릴레이트, 카르복실 펜틸메타크릴레이트, 이타콘산, 말레인산, 푸마르산, 메틸 아크릴산, 에틸 아크릴산, 부틸 아크릴산, 2-에틸 헥실 아크릴산, 데실아크릴산, 메틸 메타크릴산, 에틸 메타크릴산, 부틸 메타크릴산, 2-에틸 헥실 메타크릴산, 데실메타크릴산 등이 있다. The acrylic acid monomer is acrylic acid, methacrylic acid, carboxyl ethyl acrylate, carboxyl ethyl methacrylate, carboxyl pentyl acrylate, carboxyl pentyl methacrylate, itaconic acid, maleic acid, fumaric acid, methyl acrylic acid, ethyl acrylic acid, butyl acrylic acid, 2-ethylhexyl acrylic acid, decyl acrylic acid, methyl methacrylic acid, ethyl methacrylic acid, butyl methacrylic acid, 2-ethylhexyl methacrylic acid, decyl methacrylic acid and the like.
상기 아크릴레이트기 함유 실란 커플링제 및 아크릴산 모노머의 중량비는 10~30:70~90인 것이 바람직하다. The weight ratio of the silane coupling agent containing an acrylate group and the acrylic acid monomer is preferably 10 to 30:70 to 90.
상기 공중합체는 열경화성 수지 100중량부에 대하여 1~10중량부인 것이 바람직하며, 상기 수치범위에서 팽창특성 및 내열성이 극대화될 수 있다. The copolymer is preferably 1 to 10 parts by weight based on 100 parts by weight of the thermosetting resin, and expansion characteristics and heat resistance can be maximized in the above numerical range.
또한 상기 캡슐 외부층은 아크릴레이트기 함유 실란 커플링제 및 2-하이드록시에틸 아크릴레이트(HEA)의 공중합체를 추가적으로 포함할 수 있다. In addition, the outer layer of the capsule may further include a copolymer of a silane coupling agent containing an acrylate group and 2-hydroxyethyl acrylate (HEA).
상기 아크릴레이트기 함유 실란 커플링제 및 2-하이드록시에틸 아크릴레이트의 중량비는 20~40:60~80인 것이 바람직하다. The weight ratio of the silane coupling agent containing an acrylate group and 2-hydroxyethyl acrylate is preferably 20 to 40:60 to 80.
상기 공중합체는 열경화성 수지 100중량부에 대하여 2~10중량부 사용되며, 상기 수치범위에서 팽창특성 및 내열성이 극대화될 수 있다. The copolymer is used in an amount of 2 to 10 parts by weight based on 100 parts by weight of the thermosetting resin, and expansion characteristics and heat resistance can be maximized in the above numerical range.
또한 상기 캡슐 외부층은 아크릴레이트기 함유 실란 커플링제, 아크릴산 모노머 및 2-하이드록시에틸 아크릴레이트(HEA)의 공중합체를 추가적으로 포함할 수 있다. In addition, the outer layer of the capsule may further include a copolymer of a silane coupling agent containing an acrylate group, an acrylic acid monomer, and 2-hydroxyethyl acrylate (HEA).
상기 아크릴레이트기 함유 실란 커플링제, 아크릴산 모노머 및 2-하이드록시에틸 아크릴레이트의 중량비는 2~10:100:20~50인 것이 바람직하며, 상기 수치 범위에서 팽창특성 및 내열성이 극대화될 수 있다. The weight ratio of the acrylate group-containing silane coupling agent, acrylic acid monomer, and 2-hydroxyethyl acrylate is preferably 2 to 10:100:20 to 50, and expansion characteristics and heat resistance can be maximized within the above range.
상기 공중합체는 열경화성 수지 100중량부에 대하여 2~10중량부 사용되며, 함량이 2중량부 미만인 경우 첨가의 효과가 미미하고, 10중량부를 초과하는 경우 팽창특성 및 내열성이 저하된다.The copolymer is used in an amount of 2 to 10 parts by weight based on 100 parts by weight of the thermosetting resin, and when the content is less than 2 parts by weight, the effect of addition is insignificant, and when the content exceeds 10 parts by weight, expansion characteristics and heat resistance are reduced.
또한 본 발명은 요소-과산화수소 착물을 포함하는 코어; 및 상기 코어를 둘러싸는 쉘로 이루어지며, 상기 쉘은 코어의 외부에 열경화성 수지가 경화되어 형성되는 것을 특징으로 하는 코어-쉘 팽창제에 관한 것이다. In another aspect, the present invention relates to a core comprising a urea-hydrogen peroxide complex; and a shell surrounding the core, wherein the shell is formed by curing a thermosetting resin on the outside of the core.
상기 코어를 구성하는 요소-과산화수소 착물은 고온에서 과산화수소가 해리되면서 가스화되어 팽창제로 활용될 수 있으며, 상기 과산화수소는 제품에 항균성, 살균성 등의 특성을 부여할 수 있다. The urea-hydrogen peroxide complex constituting the core can be gasified as hydrogen peroxide is dissociated at a high temperature and used as an expanding agent, and the hydrogen peroxide can impart antibacterial and bactericidal properties to the product.
상기 요소는 고온에서도 분해되지 않아 팽창제를 안정화시킬 수 있으며, 쉘을 구성하는 열경화성 수지는 내열성, 내구성 등이 우수하여 팽창특성을 제어하는 역할을 수행할 수 있다. These elements do not decompose even at high temperatures and can stabilize the expansion agent, and the thermosetting resin constituting the shell has excellent heat resistance and durability and can play a role in controlling expansion characteristics.
상기 코어-쉘 팽창제의 입자크기는 50~500nm인 것이 팽창특성, 내열성 및 내구성 측면에서 바람직하다. The particle size of the core-shell expanding agent is preferably 50 to 500 nm in terms of expansion characteristics, heat resistance and durability.
또한 상기 코어-쉘 팽창제는 아크릴레이트기 함유 실란 커플링제 및 아크릴산 모노머의 공중합체로 표면처리될 수 있다. In addition, the core-shell expanding agent may be surface-treated with a copolymer of an acrylate group-containing silane coupling agent and an acrylic acid monomer.
상기 팽창제의 표면에 코팅되는 공중합체는 조성물의 결합력을 향상시켜 팽창특성을 향상시킬 수 있다. The copolymer coated on the surface of the expanding agent can improve the bonding strength of the composition to improve the expansion characteristics.
상기 아크릴레이트기 함유 실란 커플링제 및 아크릴산 모노머의 중량비는 10~30:70~90인 것이 바람직하다. The weight ratio of the silane coupling agent containing an acrylate group and the acrylic acid monomer is preferably 10 to 30:70 to 90.
상기 공중합체는 팽창제 100중량부에 대하여 1~10중량부인 것이 바람직하며, 공중합체의 함량이 1중량부 미만인 경우 결합력 향상이 미미하고, 10중량부를 초과하는 경우 팽창특성이 저하된다.The copolymer is preferably 1 to 10 parts by weight based on 100 parts by weight of the expanding agent, and when the content of the copolymer is less than 1 part by weight, the bonding strength is insignificant, and when it exceeds 10 parts by weight, the expansion property is reduced.
또한 본 발명은 상기 팽창제의 표면을, 아크릴레이트기 함유 실란 커플링제 및 2-하이드록시에틸 아크릴레이트(HEA)의 공중합체로 추가적으로 처리할 수 있다. In the present invention, the surface of the expanding agent may be additionally treated with a copolymer of a silane coupling agent containing an acrylate group and 2-hydroxyethyl acrylate (HEA).
상기 아크릴레이트기 함유 실란 커플링제 및 2-하이드록시에틸 아크릴레이트의 중량비는 20~40:60~80인 것이 바람직하다. The weight ratio of the silane coupling agent containing an acrylate group and 2-hydroxyethyl acrylate is preferably 20 to 40:60 to 80.
상기 공중합체는 팽창제 100중량부에 대하여 2~10중량부 사용되며, 함량이 2중량부 미만인 경우 첨가의 효과가 미미하고, 10중량부를 초과하는 경우 팽창특성이 저하된다.The copolymer is used in an amount of 2 to 10 parts by weight based on 100 parts by weight of the expanding agent, and when the content is less than 2 parts by weight, the effect of addition is insignificant, and when the content exceeds 10 parts by weight, the expansion properties are deteriorated.
또한 본 발명은 상기 팽창제의 표면을, 아크릴레이트기 함유 실란 커플링제, 아크릴산 모노머 및 2-하이드록시에틸 아크릴레이트(HEA)의 공중합체로 추가적으로 처리할 수 있다. In the present invention, the surface of the expanding agent may be additionally treated with a copolymer of an acrylate group-containing silane coupling agent, an acrylic acid monomer, and 2-hydroxyethyl acrylate (HEA).
상기 아크릴레이트기 함유 실란 커플링제, 아크릴산 모노머 및 2-하이드록시에틸 아크릴레이트의 중량비는 2~10:100:20~50인 것이 바람직하다. The weight ratio of the acrylate group-containing silane coupling agent, acrylic acid monomer and 2-hydroxyethyl acrylate is preferably 2 to 10:100:20 to 50.
상기 공중합체는 팽창제 100중량부에 대하여 2~10중량부 사용되며, 함량이 2중량부 미만인 경우 첨가의 효과가 미미하고, 10중량부를 초과하는 경우 팽창특성이 저하된다.The copolymer is used in an amount of 2 to 10 parts by weight based on 100 parts by weight of the expanding agent, and when the content is less than 2 parts by weight, the effect of addition is insignificant, and when the content exceeds 10 parts by weight, the expansion properties are deteriorated.
이하 실시예를 통해 본 발명을 상세히 설명한다. 하기 실시예는 본 발명의 실시를 위하여 예시된 것일 뿐, 본 발명의 내용이 하기 실시예에 의하여 한정되는 것은 아니다. The present invention will be described in detail through the following examples. The following examples are only exemplified for the practice of the present invention, and the content of the present invention is not limited by the following examples.
(실시예 1) 유화제 수용액의 제조(Example 1) Preparation of aqueous emulsifier solution
물에 스티렌-말레인 무수물 공중합체를 첨가하여 5중량%의 유화제 수용액을 제조하였다. A 5% by weight aqueous emulsifier solution was prepared by adding a styrene-maleic anhydride copolymer to water.
90℃에서 10시간 교반한 후 40℃에서 필터로 여과하여 유화제 수용액을 수득하였다. After stirring at 90 °C for 10 hours, the mixture was filtered through a filter at 40 °C to obtain an aqueous emulsifier solution.
(실시예 2) (Example 2)
과산화수소 100중량부 및 요소 20중량부를 70℃에서 1시간 혼합한 후 냉각하여 요소-과산화수소 착물을 수득하였다. 100 parts by weight of hydrogen peroxide and 20 parts by weight of urea were mixed at 70° C. for 1 hour and then cooled to obtain a urea-hydrogen peroxide complex.
상기 요소-과산화수소 착물 100중량부에 실시예 1에서 제조한 유화제 수용액 100중량부를 투입하여 70℃에서 8,000rpm으로 5분간 유화시켜 캡슐 내부층을 형성하였다.100 parts by weight of the emulsifier aqueous solution prepared in Example 1 was added to 100 parts by weight of the urea-hydrogen peroxide complex, and emulsified at 70 ° C. at 8,000 rpm for 5 minutes to form an inner layer of the capsule.
상기 캡슐 내부층에 멜라민-포름알데히드 수지 50중량부를 투입하여 80℃에서 2시간 동안 반응시켜 코어-쉘 팽창제를 제조하였다. A core-shell expanding agent was prepared by adding 50 parts by weight of a melamine-formaldehyde resin to the inner layer of the capsule and reacting at 80° C. for 2 hours.
도 1 내지 3은 제조된 코어-쉘 팽창제의 광학현미경 이미지, SEM 이미지 및 입자크기를 나타낸다. 1 to 3 show optical microscope images, SEM images, and particle sizes of the prepared core-shell expanding agent.
(실시예 3) (Example 3)
멜라민-포름알데히드 수지 5중량부를 사용한 것을 제외하고는 실시예 2와 동일한 방법으로 팽창제를 제조하였다.An expanding agent was prepared in the same manner as in Example 2, except that 5 parts by weight of the melamine-formaldehyde resin was used.
(실시예 4) (Example 4)
멜라민-포름알데히드 수지 120중량부를 사용한 것을 제외하고는 실시예 2와 동일한 방법으로 팽창제를 제조하였다.An expanding agent was prepared in the same manner as in Example 2, except that 120 parts by weight of the melamine-formaldehyde resin was used.
(실시예 5) (Example 5)
3-메타크릴록시프로필트리메톡시실란 20중량부 및 아크릴산 80중량부를 반응시켜 공중합체를 제조하였다. A copolymer was prepared by reacting 20 parts by weight of 3-methacryloxypropyltrimethoxysilane and 80 parts by weight of acrylic acid.
캡슐 외부층에 상기 공중합체 2중량부를 추가로 사용한 것을 제외하고는 실시예 2와 동일한 방법으로 팽창제를 제조하였다.An expanding agent was prepared in the same manner as in Example 2, except that 2 parts by weight of the copolymer was additionally used in the outer layer of the capsule.
(비교예 1)(Comparative Example 1)
멜라민-포름알데히드 수지 대신에, 폴리비닐아코올을 사용한 것을 제외하고는 실시예 2와 동일한 방법으로 팽창제를 제조하였다.An expanding agent was prepared in the same manner as in Example 2, except that polyvinyl alcohol was used instead of the melamine-formaldehyde resin.
(분산성)(dispersity)
상기 실시예 및 비교예에서 제조된 팽창제를 물에 분산시켜 용기에 넣고 25℃에서 12시간동안 정치시킨 후 입자의 크기변화를 통해 분산성을 확인하였다. 초기 입자의 크기 대비 12시간 정치 후의 입자의 크기를 비교하여 입자 크기의 변화율을 계산하였다. The expanding agent prepared in Examples and Comparative Examples was dispersed in water, placed in a container, and allowed to stand at 25° C. for 12 hours, and then dispersibility was confirmed through a change in particle size. The particle size change rate was calculated by comparing the particle size after 12 hours of standing with the initial particle size.
(팽창특성)(expansion characteristics)
탠덤 발포 압출기에 폴리프로필렌 수지 100중량부, 탈크 1중량부 및 팽창제 3중량부를 혼합한 후 가공하여 폴리프로필렌 발포시트를 제조하였으며, 제조된 발포시트의 독립 기포율을 측정하였다. 100 parts by weight of polypropylene resin, 1 part by weight of talc, and 3 parts by weight of an expanding agent were mixed in a tandem foam extruder, and then processed to prepare a polypropylene foam sheet, and the closed cell ratio of the prepared foam sheet was measured.
(내열성)(heat resistance)
상기 팽창제를 60℃에서 10시간 방치한 후의 색상의 변화를 육안으로 관찰하여 탁월, 우수, 보통, 불량으로 표기하였다.After leaving the expanding agent at 60 ° C. for 10 hours, the change in color was observed with the naked eye and marked as excellent, excellent, normal, or poor.
(%)Change rate of particle size
(%)
(%)closed cell rate
(%)
상기 표 1에서 볼 수 있는 바와 같이, 실시예 2 내지 5는 팽창제의 분산성, 팽창특성 및 내열성이 우수함을 알 수 있다. 특히 실시예 2 및 5는 상기 특성이 가장 우수하다. As can be seen from Table 1 above, it can be seen that Examples 2 to 5 have excellent dispersibility, expansion characteristics and heat resistance of the expansion agent. In particular, Examples 2 and 5 have the most excellent properties.
반면 비교예 1은 상기 특성이 실시예에 비하여 열등함을 확인할 수 있다. On the other hand, Comparative Example 1 can confirm that the properties are inferior to those of Examples.
Claims (5)
상기 요소-과산화수소 착물에 유화제를 첨가하여 캡슐 내부층을 형성하는 단계;
상기 캡슐 내부층에 열경화성 수지를 첨가하여 캡슐 외부층을 형성하는 단계; 및
상기 캡슐 외부층을 경화시켜 캡슐을 제조하는 단계를 포함하는 코어-쉘 팽창제의 제조방법에 있어서,
상기 열경화성 수지는 멜라민 수지, 페놀 수지, 폴리우레탄, 불포화폴리에스테르 수지, 멜라민-포름알데히드 수지 및 페놀-포름알데히드 수지로부터 하나 이상 선택되고,
상기 열경화성 수지는 50~150℃에서 1~10시간 교반하면서 경화시켜 캡슐 외부층을 형성하며,
상기 열경화성 수지의 함량은 요소-과산화수소 착물 100중량부에 대하여 10~100중량부인 것을 특징으로 하는 코어-쉘 팽창제의 제조방법.
preparing a urea-hydrogen peroxide complex by mixing urea and hydrogen peroxide;
forming an inner layer of the capsule by adding an emulsifier to the urea-hydrogen peroxide complex;
forming an outer layer of the capsule by adding a thermosetting resin to the inner layer of the capsule; and
In the method for manufacturing a core-shell expanding agent comprising the step of preparing a capsule by curing the outer layer of the capsule,
The thermosetting resin is at least one selected from melamine resins, phenol resins, polyurethanes, unsaturated polyester resins, melamine-formaldehyde resins and phenol-formaldehyde resins,
The thermosetting resin is cured while stirring at 50 to 150 ° C. for 1 to 10 hours to form an outer layer of the capsule,
The content of the thermosetting resin is 10 to 100 parts by weight based on 100 parts by weight of the urea-hydrogen peroxide complex.
상기 유화제는 폴리스티렌 술폰산(polystyrene sulfonic acid), 스티렌-말레인 무수물 공중합체(styrene-maleic anhydride copolymer), 소르비탄의 지방산 에스테르 및 폴리옥시에틸렌 소르비탄의 지방산 에스테르로부터 하나 이상 선택되는 것을 특징으로 하는 코어-쉘 팽창제의 제조방법.
According to claim 1,
The emulsifier is a core, characterized in that at least one selected from polystyrene sulfonic acid, styrene-maleic anhydride copolymer, fatty acid ester of sorbitan, and fatty acid ester of polyoxyethylene sorbitan. - Manufacturing method of shell expansion agent.