KR102533738B1 - Optical film for enhancing contrast ratio and viewing angle, polarizing plate comprising the same, and liquid crystal display apparatus comprising the same - Google Patents

Optical film for enhancing contrast ratio and viewing angle, polarizing plate comprising the same, and liquid crystal display apparatus comprising the same Download PDF

Info

Publication number
KR102533738B1
KR102533738B1 KR1020200183480A KR20200183480A KR102533738B1 KR 102533738 B1 KR102533738 B1 KR 102533738B1 KR 1020200183480 A KR1020200183480 A KR 1020200183480A KR 20200183480 A KR20200183480 A KR 20200183480A KR 102533738 B1 KR102533738 B1 KR 102533738B1
Authority
KR
South Korea
Prior art keywords
optical film
contrast ratio
polymer dispersion
viewing angle
less
Prior art date
Application number
KR1020200183480A
Other languages
Korean (ko)
Other versions
KR20220092084A (en
Inventor
배중석
고승진
Original Assignee
도레이첨단소재 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 도레이첨단소재 주식회사 filed Critical 도레이첨단소재 주식회사
Priority to KR1020200183480A priority Critical patent/KR102533738B1/en
Priority to CN202111555111.5A priority patent/CN114675352A/en
Publication of KR20220092084A publication Critical patent/KR20220092084A/en
Application granted granted Critical
Publication of KR102533738B1 publication Critical patent/KR102533738B1/en

Abstract

본 발명은 광학필름에 관한 것으로, 더욱 상세하게는 표시장치의 명암비와 시야각을 개선시키는 광학필름, 이를 포함하는 편광판 및 액정표시장치에 관한 것이다. The present invention relates to an optical film, and more particularly, to an optical film for improving the contrast ratio and viewing angle of a display device, a polarizing plate and a liquid crystal display device including the same.

Description

명암비 및 시야각 개선용 광학필름, 이를 포함하는 편광판 및 액정표시장치{Optical film for enhancing contrast ratio and viewing angle, polarizing plate comprising the same, and liquid crystal display apparatus comprising the same}Optical film for enhancing contrast ratio and viewing angle, polarizing plate comprising the same, and liquid crystal display apparatus comprising the same}

본 발명은 광학필름에 관한 것으로, 더욱 상세하게는 표시장치의 명암비와 시야각을 개선시키는 광학필름, 이를 포함하는 편광판 및 액정표시장치에 관한 것이다.The present invention relates to an optical film, and more particularly, to an optical film for improving the contrast ratio and viewing angle of a display device, a polarizing plate and a liquid crystal display device including the same.

액정표시장치는 백라이트 유닛에서 나온 광이 액정패널을 통해 출사됨으로써 작동된다. 따라서 액정표시장치의 화면 중 정면에서는 명암비(contrast ratio, CR)가 우수하나, 측면 쪽은 정면 대비 명암비가 좋지 않은 것이 일반적이다.The liquid crystal display device operates by radiating light emitted from a backlight unit through a liquid crystal panel. Therefore, among the screens of liquid crystal display devices, the contrast ratio (CR) is excellent at the front, but the contrast ratio is not good at the side.

이를 해결하기 위해서 액정패널 또는 액정 구조를 변형시켜 측면에서의 명암비를 높이기 위한 시도가 있다. 다만, 측면 명암비를 높일수록 정면 명암비는 저하될 수밖에 없다. 따라서 측면 명암비를 높이되 정면 명암비의 감소를 최소화시키는 것이 필요하다. In order to solve this problem, there is an attempt to increase the contrast ratio on the side by deforming the liquid crystal panel or liquid crystal structure. However, as the side contrast ratio increases, the front contrast ratio inevitably decreases. Therefore, it is necessary to increase the side contrast ratio while minimizing the decrease in the front contrast ratio.

한편, 시야각을 증진시키는 방법으로 빛을 확산시키는 방법이 있으며, 이를 위해 비드를 포함하는 광학필름이 채용될 수 있다. 그러나 비드를 포함하는 광학필름은 충분한 시야각을 확보하기 어렵거나 확보하더라도 휘도를 저하시킬 수 있으며, 명암비 개선 효과는 거의 없다. 나아가 이러한 광학필름은 목적하는 물성을 발현하도록 가공이 어려울 수 있다. On the other hand, there is a method of diffusing light as a method of improving the viewing angle, and for this purpose, an optical film including beads may be employed. However, it is difficult to secure a sufficient viewing angle in the optical film including the beads, or even if a sufficient viewing angle is secured, the luminance may be reduced, and the contrast ratio improvement effect is almost absent. Furthermore, such an optical film may be difficult to process to express desired physical properties.

이러한 문제점을 개선하기 위하여 액정표시장치를 구성하는 광학필름에 수지 굴절율차와 미세 광학패턴을 가공하는 방법 등이 다양한 방법으로 연구되고 있다. 그러나 액정표시장치가 점차 대면적화 되는 상황에서 대면적화된 광학필름에 미세 광학 패턴을 형성시키는 것은 쉽지 않은 상황이다. 특히 수십 나노미터에서 수십 마이크론 사이의 미세 패턴을 균일하게 대면적에 구현하는 것은 실질적으로 불가능 하며, 상업적 양산이 가능한 수율을 확보하면서 대면적으로 구현하는 것은 매우 어려운 문제이다. In order to improve these problems, various methods such as a method of processing a resin refractive index difference and a fine optical pattern on an optical film constituting a liquid crystal display device have been studied. However, it is not easy to form a fine optical pattern on a large-area optical film in a situation where liquid crystal display devices are gradually becoming larger. In particular, it is practically impossible to uniformly implement a fine pattern between tens of nanometers and tens of microns on a large area, and it is very difficult to implement it on a large area while securing a yield capable of commercial mass production.

대한민국 공개특허공보 제2002-0050698호Republic of Korea Patent Publication No. 2002-0050698

본 발명은 상술한 문제를 해결하기 위해 안출된 것으로, 명암비 특히 정면 명암비와 측면 명암비를 동시에 향상시켜서 시인성을 향상시킬 수 있는 광학필름, 이를 포함하는 편광판 및 액정표시장치를 제공하는데 목적이 있다.An object of the present invention is to provide an optical film capable of improving visibility by simultaneously improving the contrast ratio, particularly the front contrast ratio and the side contrast ratio, and a polarizing plate and a liquid crystal display device including the same.

또한, 본 발명은 휘도특성을 저하시키지 않고 명암비의 향상과 함께 시야각을 향상시킬 수 있는 광학필름, 이를 포함하는 편광판 및 액정표시장치를 제공하는데 다른 목적이 있다.In addition, another object of the present invention is to provide an optical film capable of improving a viewing angle as well as an improvement in contrast ratio without deteriorating luminance characteristics, a polarizing plate and a liquid crystal display device including the same.

상술한 과제를 해결하기 위해 본 발명은, 매트릭스 및 상호 수직하는 x축, y축 및 z축 중 x축 방향이 길이방향이 되되 y축 및 z축 방향으로는 랜덤하게 상기 매트릭스 내 배열된 다수 개의 폴리머 분산체 구비하는 광학층을 구비하고, 상기 다수 개의 폴리머 분산체는 흑색 안료를 함유하며, y-z 평면인 광학층 절단면에서 상기 폴리머 분산체의 너비가 300㎚ 이하인 명암비 및 시야각 개선용 광학필름을 제공한다.In order to solve the above problems, the present invention, the x-axis direction of the matrix and mutually perpendicular x-axis, y-axis, and z-axis is the longitudinal direction, but the y-axis and z-axis directions are randomly arranged in the matrix A plurality of Provides an optical film for improving the contrast ratio and viewing angle, comprising an optical layer including a polymer dispersion, wherein the plurality of polymer dispersions contain a black pigment, and the width of the polymer dispersion is 300 nm or less in a y-z plane optical layer cut surface. do.

본 발명의 일 실시예에 있어서, 상기 매트릭스와 상기 폴리머 분산체는 서로 직교하는 3개의 축 중 어느 2개의 축 방향에 대한 굴절율의 차이가 0.05 이하이고, 나머지 1개의 축방향에 대한 굴절율의 차이가 0.1 이상일 수 있다.In one embodiment of the present invention, the matrix and the polymer dispersion have a difference in refractive index of 0.05 or less in any two axial directions among three axes orthogonal to each other, and a difference in refractive index in the other axial direction. may be greater than 0.1.

또한, 상기 폴리머 분산체는 매트릭스 및 폴리머 분산체 전체 중량의 35 ~ 65 중량%로 포함될 수 있다.In addition, the polymer dispersion may be included in 35 to 65% by weight of the total weight of the matrix and the polymer dispersion.

또한, 상기 광흡수제는 폴리머 분산체 전체 중량에 대해서 2 ~ 60 중량%로 함유할 수 있다. In addition, the light absorber may be contained in an amount of 2 to 60% by weight based on the total weight of the polymer dispersion.

또한, y-z 평면인 절단면에서 전체 폴리머 분산체 중 z축 방향인 폴리머 분산체의 두께가 250㎚ 이하의 두께를 갖는 폴리머 분산체의 개수가 95% 이상일 수 있다.In addition, the number of polymer dispersions having a thickness of 250 nm or less in the z-axis direction among all the polymer dispersions in the y-z plane section may be 95% or more.

또한, y-z 평면인 절단면에서 전체 폴리머 분산체 중 z축 방향인 폴리머 분산체의 두께가 120nm 이하인 폴리머 분산체의 개수가 60% 이상일 수 있다.In addition, the number of polymer dispersions having a thickness of 120 nm or less in the z-axis direction among all the polymer dispersions in the y-z plane section may be 60% or more.

또한, y-z 평면인 절단면에서 전체 폴리머 분산체 중 z축 방향인 폴리머 분산체의 두께가 50nm 미만인 폴리머 분산체의 개수가 10% 이하일 수 있다. In addition, the number of polymer dispersions having a thickness of less than 50 nm in the z-axis direction among all the polymer dispersions in the y-z plane section may be 10% or less.

또한, y-z 평면인 광학층 절단면에서 상기 폴리머 분산체의 너비는 200㎚ 이하일 수 있다.In addition, the polymer dispersion may have a width of 200 nm or less on a y-z plane, a cutting plane of the optical layer.

또한, 상기 광학필름은 헤이즈가 20% 이하이며, 상기 광학층은 두께가 100㎛ 이하일 수 있다. In addition, the optical film may have a haze of 20% or less, and the optical layer may have a thickness of 100 μm or less.

또한, 상기 광학필름은 상기 광학층의 적어도 일면에 일체로 형성된 스킨층을 더 포함할 수 있다.In addition, the optical film may further include a skin layer integrally formed on at least one surface of the optical layer.

또한, 본 발명은 시인 측인 액정패널 상부에 배치되는 편광판으로서, 흡수편광자 및 상기 흡수편광자의 광 출사면 상에 배치되는 본 발명에 따른 광학필름을 포함하는 편광판을 제공한다.In addition, the present invention provides a polarizing plate disposed on an upper portion of a liquid crystal panel, which is a viewing side, including an absorption polarizer and an optical film according to the present invention disposed on a light exit surface of the absorption polarizer.

또한, 본 발명은 액정 셀, 및 적어도 상기 액정 셀의 광출사면 상에 배치되는 본 발명에 따른 편광판을 포함하는 액정표시장치를 제공한다.In addition, the present invention provides a liquid crystal display device including a liquid crystal cell and a polarizing plate according to the present invention disposed on at least a light exit surface of the liquid crystal cell.

본 발명의 광학필름은 휘도 저하가 없거나 최소화된 상태로 명암비 특히 정면 명암비와 측면 명암비를 동시에 향상시켜서 시인성을 향상시킬 수 있다. 또한, 이와 동시에 휘도 특성과 함께 시야각을 향상시킬 수 있다. 더불어 본 발명의 일실시예에 의한 광학필름은 이러한 효과를 발현하기 위해서 구비된 폴리머 분산체가 시인되는 것이 방지되며, 휘선보임 현상이나 빛샘 등의 부작용도 함께 방지될 수 있음에 따라서 광원 어셈블리와 같은 액정표시장치의 부품으로 널리 사용될 수 있으며, 이외에 유리창, 각종 편광조명 산업전반에 응용될 수 있다.The optical film of the present invention can improve visibility by simultaneously improving a contrast ratio, particularly a frontal contrast ratio and a side contrast ratio, without or minimizing a decrease in luminance. In addition, at the same time, it is possible to improve the viewing angle along with the luminance characteristics. In addition, the optical film according to an embodiment of the present invention prevents the polymer dispersion provided to express these effects from being recognized, and also prevents side effects such as bright streaks and light leakage, such as liquid crystals such as light source assemblies. It can be widely used as a part of a display device, and can be applied to glass windows and various polarized light industries in general.

도 1은 본 발명의 일 실시예에 따른 광학필름 내 광학층의 SEM 사진이다.
도 2 및 도 3은 본 발명의 일 실시예에 따른 광학필름의 단면도 및 단면확대도이다.
도 4는 본 발명의 일 실시예에 따른 광학필름 내 광학층에 구비된 폴리머 분산체의 길이방향 배열을 예시한 모식도이다.
도 5a 내지 도 5c는 본 발명의 일 실시예에 따른 광학필름 내 광학층에 구비된 폴리머 분산체의 종횡비, 너비 및 두께를 정의하기 위해 예시한 모식도이다.
도 6은 본 발명의 일 실시예에 따른 편광판의 단면도이다.
도 7은 본 발명의 일 실시예에 따른 액정표시장치의 단면도이다.
도 8 내지 도 10은 본 발명의 비교예를 제조하기 위한 제조장치의 모식도와 제조된 광학필름 단면모식도이다.1 is a SEM picture of an optical layer in an optical film according to an embodiment of the present invention.
2 and 3 are cross-sectional and cross-sectional enlarged views of an optical film according to an embodiment of the present invention.
4 is a schematic diagram illustrating a longitudinal arrangement of polymer dispersions provided in an optical layer in an optical film according to an embodiment of the present invention.
5A to 5C are schematic diagrams exemplified for defining an aspect ratio, width, and thickness of a polymer dispersion provided in an optical layer in an optical film according to an embodiment of the present invention.
6 is a cross-sectional view of a polarizing plate according to an embodiment of the present invention.
7 is a cross-sectional view of a liquid crystal display according to an exemplary embodiment of the present invention.
8 to 10 are a schematic diagram of a manufacturing apparatus for manufacturing a comparative example of the present invention and a schematic cross-sectional view of the manufactured optical film.

이하, 첨부한 도면을 참고로 하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 동일 또는 유사한 구성요소에 대해서는 동일한 참조부호를 부가한다. 또한, 도면에 나타난 일 구성의 크기, 형상에 의해 본 발명이 제한되지 않는다. 일예로, 도 2 및 도 3에 도시된 다수 개의 폴리머 분산체 개수와 각각의 크기는 본 발명을 설명하기 위한 예시일 뿐이며, 본 발명에 따른 폴리머 분산체 두께 등에 정확하게 부합하도록 도시된 것이 아님을 밝힌다. 또한, 도 3의 일측면에 도시된 점선은 폴리머 분산체의 길이방향을 대략적으로 설명한 것일 뿐, 도시되지 않은 매트릭스 내부의 폴리머 분산체 길이를 의미하지 않는다.Hereinafter, with reference to the accompanying drawings, embodiments of the present invention will be described in detail so that those skilled in the art can easily carry out the present invention. This invention may be embodied in many different forms and is not limited to the embodiments set forth herein. In order to clearly describe the present invention in the drawings, parts irrelevant to the description are omitted, and the same reference numerals are added to the same or similar components throughout the specification. In addition, the present invention is not limited by the size and shape of one component shown in the drawings. As an example, it is revealed that the number and size of each of the plurality of polymer dispersions shown in FIGS. 2 and 3 are only examples for explaining the present invention, and are not shown to exactly match the thickness of the polymer dispersion according to the present invention. . In addition, the dotted line shown on one side of FIG. 3 only roughly describes the length direction of the polymer dispersion, and does not mean the length of the polymer dispersion inside the matrix, which is not shown.

도 2 내지 도 3을 참조하면, 본 발명의 일 실시예에 의한 광학필름(1000)은 매트릭스(110) 및 상기 매트릭스 내 위치하는 다수 개의 폴리머 분산체(120)를 포함하는 광학층(100)을 구비한다. Referring to FIGS. 2 and 3 , the optical film 1000 according to an embodiment of the present invention includes an optical layer 100 including a matrix 110 and a plurality of polymer dispersions 120 positioned in the matrix. provide

상기 다수 개의 폴리머 분산체(120)는 일 방향으로 긴 로드형 또는 섬유형과 같은 형상을 가질 수 있다. 이에 따라서 다수 개의 폴리머 분산체(120)는 분산체(120) 길이방향 주축과 상기 주축에 수직이 되는 횡단면의 횡축 길이 간 비율인 종횡비가 10 초과, 다른 일예로 100 초과, 1,000 초과, 10,000 초과, 100,000 초과일 수 있다. 상기 횡축길이는 상기 단면의 형상이 원인 경우 원의 직경을 의미하고, 단면이 원이 아닌 경우 둘레를 잇는 두 선분 중 길이가 가장 큰 선분의 길이를 의미한다. 또한, 도 5a에 도시된 것과 같이 광학층(100)의 y-z 평면인 절단면을 기준으로 한 폴리머 분산체(120)의 단면에서 장축길이(a)에 대한 단축길이(b)의 비율(a/b)인 단면 종횡비 역시 1을 초과할 수 있다. 여기서 단축길이(b)란 장축을 수직이등분 하는 축을 단축이라할 때, 상기 단축의 길이를 의미한다.The plurality of polymer dispersions 120 may have a rod-like or fibrous shape elongated in one direction. Accordingly, the plurality of polymer dispersions 120 have an aspect ratio, which is the ratio between the length of the main axis in the longitudinal direction of the dispersion 120 and the length of the transverse axis of the cross section perpendicular to the main axis, greater than 10, in other examples, greater than 100, greater than 1,000, greater than 10,000, may be greater than 100,000. The transverse axis length means the diameter of a circle when the shape of the cross section is circular, and means the length of a line segment having the largest length among two line segments connecting the circumference when the cross section is not a circle. In addition, as shown in FIG. 5A, the ratio (a/b) of the minor axis length (b) to the major axis length (a) in the cross section of the polymer dispersion 120 based on the cut plane, which is the y-z plane of the optical layer 100 ), the cross-sectional aspect ratio may also exceed 1. Here, the minor axis length (b) means the length of the minor axis when the axis perpendicularly bisecting the major axis is referred to as the minor axis.

한편, 다수 개의 폴리머 분산체(120)는 상호 수직하는 세 개의 x축, y축 및 z축 중 x축 방향이 길이방향이 되도록 상기 매트릭스(110) 내 배열된다. 다만, 여기서 x축 방향이 길이방향이 되도록 배열된다는 것은 도 2에 개략적으로 도시한 것과 같이 모든 폴리머 분산체(120)의 길이방향이 x축과 평행하도록 배열됨을 의미하지는 않고, 폴리머 분산체(120)의 길이방향이 되는 주축의 방향이 y축, z축 보다 x축 방향에 가까움을 의미한다. Meanwhile, the plurality of polymer dispersions 120 are arranged in the matrix 110 so that the x-axis direction of three mutually perpendicular x-, y-, and z-axes is a longitudinal direction. However, here, being arranged such that the x-axis direction is the longitudinal direction does not mean that the longitudinal direction of all the polymer dispersions 120 are arranged parallel to the x-axis, as schematically shown in FIG. 2, and the polymer dispersion 120 ) means that the direction of the main axis, which is the longitudinal direction, is closer to the x-axis direction than the y-axis and z-axis.

이에 대하여 도 4를 참조하여 구체적으로 설명하면, 광학층(100)의 x-z 평면에서 제1폴리머 분산체(123)는 길이 방향이 x축 방향과 평행하게 배열되나, 제2폴리머 분산체(121) 및 제3폴리머 분산체(122)는 길이 방향이 z축 방향으로 소정의 각도 기울어져 배열될 수 있다. 또한, 도 4에 도시하지 않았으나 폴리머 분산체는 y축 방향으로도 소정의 각도 기울어져 배열될 수 있음을 밝혀둔다. 단, 여기서 소정의 각도는 일예로 (±)45°미만, (±)35°미만, (±)25°미만, (±)15°미만, (±)10°미만, (±)5°미만, (±)3°미만, (±)1°미만일 수 있다. 4, in the x-z plane of the optical layer 100, the first polymer dispersion 123 is arranged in a longitudinal direction parallel to the x-axis direction, but the second polymer dispersion 121 And the third polymer dispersion 122 may be arranged with a longitudinal direction tilted at a predetermined angle in the z-axis direction. In addition, although not shown in FIG. 4, it should be noted that the polymer dispersion may be arranged inclined at a predetermined angle even in the y-axis direction. However, the predetermined angle here is, for example, less than (±) 45°, (±) 35°, (±) less than 25°, (±) less than 15°, (±) 10°, and (±) 5°). , (±) 3° or less, (±) 1° or less.

또한, 다수 개의 폴리머 분산체(120)는 y축 및 z축 방향을 기준으로는 랜덤하게 배열된다. 즉, 광학층(100)의 y축 및 z축 방향 단면에서 다수 개의 폴리머 분산체(120)는 폴리머 분산체 단면 크기, 모양에 관계없이 위치가 랜덤하게 배열된다. In addition, the plurality of polymer dispersions 120 are randomly arranged along the y-axis and z-axis directions. That is, in the y-axis and z-axis direction sections of the optical layer 100, the positions of the plurality of polymer dispersions 120 are randomly arranged regardless of the size and shape of the cross-section of the polymer dispersion.

또한, 본 발명의 일 실시예에 의하면 상기 매트릭스(110)와 매트릭스 내부에 포함되는 폴리머 분산체(120) 간에는 복굴절 계면이 형성될 수 있고, 이를 통해서 명암비를 향상시키는 효과를 달성하기에 유리하다. 이를 위해 상기 매트릭스(110)와 폴리머 분산체(120)는 복굴절 계면을 형성하여야 하므로 상기 매트릭스(110)가 광학적 등방성인 경우, 폴리머 분산체(120)는 복굴절성을 가질 수 있고, 반대로 상기 매트릭스(110)가 광학적으로 복굴절성을 갖는 경우에는 폴리머 분산체(120)는 광학적 등방성을 가질 수 있다. 구체적으로 상기 폴리머 분산체(120)의 x축 방향의 굴절율이 nX1, y축 방향의 굴절율이 nY1 및 z축 방향의 굴절율이 nZ1이고, 매트릭스(110)의 굴절율이 nX2, nY2 및 nZ2일 때, nX1과 nY1 사이의 면내 복굴절이 발생할 수 있다. 더욱 바람직하게는 매트릭스(110)와 폴리머 분산체(120)의 X, Y, Z축 굴절율 중 적어도 어느 하나가 상이할 수 있으며, 보다 바람직하게는 폴리머 분산체의 길이방향이 X축인 경우 Y축 및 Z축 방향에 대한 굴절율의 차이가 0.05 이하이고, X축향에 대한 굴절율의 차이가 0.1 이상일 수 있다. 만일 모든 축에서 굴절율 차이가 0.05 이하인 경우 명암비 개선 및 시야각 향상의 효과를 달성하기 어려울 수 있다. 또한, X 축 이외에 다른 두 축 중 적어도 하나의 축 역시 굴절율 차이가 0.1 이상 발생할 경우 선형 모아레 문제가 발생할 수 있고, 이러한 문제가 발생한 부분에서 광투과량이 저하될 수 있어서 휘도저하를 유발시킬 수 있는 우려가 있다. In addition, according to an embodiment of the present invention, a birefringent interface may be formed between the matrix 110 and the polymer dispersion 120 included in the matrix, and through this, it is advantageous to achieve an effect of improving the contrast ratio. To this end, since the matrix 110 and the polymer dispersion 120 must form a birefringent interface, when the matrix 110 is optically isotropic, the polymer dispersion 120 may have birefringence, and conversely, the matrix ( 110) has optical birefringence, the polymer dispersion 120 may have optical isotropy. Specifically, when the refractive index of the polymer dispersion 120 in the x-axis direction is nX1, the refractive index in the y-axis direction is nY1, and the refractive index in the z-axis direction is nZ1, and the refractive index of the matrix 110 is nX2, nY2, and nZ2, In-plane birefringence between nX1 and nY1 may occur. More preferably, at least one of the X, Y, and Z-axis refractive indices of the matrix 110 and the polymer dispersion 120 may be different, and more preferably, when the longitudinal direction of the polymer dispersion is the X-axis, the Y-axis and A difference in refractive index in the Z-axis direction may be 0.05 or less, and a difference in refractive index in the X-axis direction may be 0.1 or more. If the difference in refractive index in all axes is 0.05 or less, it may be difficult to achieve effects of improving contrast ratio and viewing angle. In addition, if the difference in refractive index of at least one of the other two axes in addition to the X axis occurs by 0.1 or more, a linear moiré problem may occur, and the light transmittance may decrease in a portion where such a problem occurs, which may cause a decrease in luminance. there is

바람직하게는 매트릭스(110)가 광학적 등방성이고, 폴리머 분산체(120)가 복굴절성을 가질 수 있고, 이를 통해 광학층(100)을 통과하는 투과광의 왜곡을 감소시키고, 컬러변형을 최소화 또는 방지할 수 있는 이점이 있다. Preferably, the matrix 110 is optically isotropic and the polymer dispersion 120 may have birefringence, thereby reducing distortion of transmitted light passing through the optical layer 100 and minimizing or preventing color distortion. There are advantages that can be

상기 매트릭스(110)는 통상적인 광학필름에 사용되는 재질인 경우 제한 없이 사용될 수 있으며, 바람직하게는 폴리에틸렌나프탈레이트(PEN), 코폴리에틸렌나프탈레이트(co-PEN), 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC), 폴리카보네이트(PC) 얼로이, 폴리스타이렌(PS), 내열폴리스타이렌(PS), 폴리메틸메타아크릴레이트(PMMA), 폴리부틸렌테레프탈레이트(PBT), 폴리프로필렌(PP), 폴리에틸렌(PE), 아크릴로니트릴부타디엔스티렌(ABS), 폴리우레탄(PU),폴리이미드(PI),폴리비닐클로라이드(PVC), 스타이렌아크릴로니트릴혼합(SAN),에틸렌초산비닐(EVA), 폴리아미드(PA), 폴리아세탈(POM), 페놀, 에폭시(EP), 요소(UF), 멜라닌(MF), 불포화포리에스테르(UP), 실리콘(SI) 및 사이크로올레핀 폴리머를 사용할 수 있으며 일예로, 폴리카보네이트(PC) 얼로이 일 수 있다.The matrix 110 may be used without limitation if it is a material used in a conventional optical film, and preferably polyethylene naphthalate (PEN), co-polyethylene naphthalate (co-PEN), polyethylene terephthalate (PET), poly Carbonate (PC), polycarbonate (PC) alloy, polystyrene (PS), heat-resistant polystyrene (PS), polymethyl methacrylate (PMMA), polybutylene terephthalate (PBT), polypropylene (PP), polyethylene ( PE), acrylonitrile butadiene styrene (ABS), polyurethane (PU), polyimide (PI), polyvinyl chloride (PVC), styrene acrylonitrile blend (SAN), ethylene vinyl acetate (EVA), polyamide (PA), polyacetal (POM), phenol, epoxy (EP), urea (UF), melanin (MF), unsaturated polyester (UP), silicone (SI) and cycloolefin polymers may be used, for example, It may be a polycarbonate (PC) alloy.

또한, 상기 폴리머 분산체(120) 역시 통상적인 광학필름에 사용되는 재질인 경우 제한없이 사용될 수 있으며, 바람직하게는 폴리에틸렌나프탈레이트(PEN), 코폴리에틸렌나프탈레이트(co-PEN), 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC), 폴리카보네이트(PC) 얼로이, 폴리스타이렌(PS), 내열폴리스타이렌(PS), 폴리메틸메타아크릴레이트(PMMA), 폴리부틸렌테레프탈레이트(PBT), 폴리프로필렌(PP), 폴리에틸렌(PE), 아크릴로니트릴부타디엔스티렌(ABS), 폴리우레탄(PU),폴리이미드(PI),폴리비닐클로라이드(PVC), 스타이렌아크릴로니트릴혼합(SAN),에틸렌초산비닐(EVA), 폴리아미드(PA), 폴리아세탈(POM), 페놀, 에폭시(EP), 요소(UF), 멜라닌(MF), 불포화포리에스테르(UP), 실리콘(SI) 및 사이크로올레핀폴리머를 단독 또는 혼합하여 사용할 수 있으며,일예로 PEN일 수 있다.In addition, if the polymer dispersion 120 is also a material used in a conventional optical film, it may be used without limitation, and preferably polyethylene naphthalate (PEN), co-polyethylene naphthalate (co-PEN), polyethylene terephthalate ( PET), polycarbonate (PC), polycarbonate (PC) alloy, polystyrene (PS), heat-resistant polystyrene (PS), polymethyl methacrylate (PMMA), polybutylene terephthalate (PBT), polypropylene (PP) ), polyethylene (PE), acrylonitrile butadiene styrene (ABS), polyurethane (PU), polyimide (PI), polyvinyl chloride (PVC), styrene acrylonitrile blend (SAN), ethylene vinyl acetate (EVA) ), polyamide (PA), polyacetal (POM), phenol, epoxy (EP), urea (UF), melanin (MF), unsaturated polyester (UP), silicone (SI) and cycloolefin polymer alone or It can be mixed and used, and for example, PEN may be used.

또한, 광학층(100)에 포함되는 폴리머 분산체(120)는 매트릭스(110)와 폴리머 분산체(120) 전체 중량을 기준으로 35 ~ 65중량%, 보다 바람직하게는 40 ~ 65중량% 포함될 수 있다. 만일 폴리머 분산체가 35 중량% 미만으로 구비되는 경우 광학층(100) 내 폴리머 분산체의 밀도가 감소하며, 폴리머 분산체의 크기를 본 발명에 따른 범위로 제어하기 매우 어려워지는 우려가 있다. 또한, 만일 폴리머 분산체가 65중량%를 초과할 경우 매트릭스 및 폴리머 분산체 간 반전이 일어날 수 있는데, 매트릭스가 광학적 등방성 물질일 경우 반전에 따라서 복굴절성인 폴리머 분산체가 매트릭스로 되고, 이로 인해 투과광의 복굴절성으로 인해 광출사에 왜곡이 증가할 수 있다. 또한, 광학층(100)을 투과하는 광이 컬러필터 등의 색변환층을 통과한 광인 경우 시야각이 큰 측면에서 컬러반전, 컬러변형 문제가 발생할 우려가 있다. In addition, the polymer dispersion 120 included in the optical layer 100 may include 35 to 65% by weight, more preferably 40 to 65% by weight based on the total weight of the matrix 110 and the polymer dispersion 120. there is. If the polymer dispersion is provided in less than 35% by weight, the density of the polymer dispersion in the optical layer 100 decreases, and there is a concern that it becomes very difficult to control the size of the polymer dispersion within the range according to the present invention. In addition, if the polymer dispersion exceeds 65% by weight, inversion between the matrix and the polymer dispersion may occur. If the matrix is an optically isotropic material, the polymer dispersion, which is birefringent according to the inversion, becomes the matrix, resulting in the birefringence of transmitted light. As a result, distortion may increase in light emission. In addition, when light passing through the optical layer 100 is light passing through a color conversion layer such as a color filter, there is a concern that color inversion and color distortion problems may occur in terms of a large viewing angle.

또한, 도 5b에 도시된 것과 같이 폴리머 분산체(120)는 y-z 평면인 광학층(100) 절단면을 기준으로 너비(W1,W2,W3,W4)가 300㎚ 이하, 바람직하게는 200㎚ 이하일 수 있으며, 이를 통해서 광학층(100)을 z축 방향으로 투과하는 투과광의 광손실을 최소화하여 휘도 저하를 방지할 수 있으며, 폴리머 분산체가 육안으로 시인되는 것을 방지할 수 있다. 여기서 폴리머 분산체(120) 너비란 z 축방향에서 폴리머 분산체(120)를 바라보았을 때 2차원 상에 투영된 너비(W1,W2,W3,W4)를 의미하며, y-z 평면인 광학층(100) 절단면에서 폴리머 분산체의 장축길이와는 구별됨을 밝혀둔다. In addition, as shown in FIG. 5B, the polymer dispersion 120 has a width (W 1 , W 2 , W 3 , W 4 ) of 300 nm or less, preferably It may be 200 nm or less, through which light loss of transmitted light transmitted through the optical layer 100 in the z-axis direction can be minimized to prevent a decrease in luminance, and it is possible to prevent the polymer dispersion from being visually recognized. Here, the width of the polymer dispersion 120 means the width (W 1 , W 2 , W 3 , W 4 ) projected on the two-dimensional surface when the polymer dispersion 120 is viewed in the z-axis direction, which is a yz plane It should be noted that the cut plane of the optical layer 100 is distinguished from the major axis length of the polymer dispersion.

또한, 본 발명의 일 실시예에 의하면, 보다 향상된 명암비 및 시야각 개선 효과를 달성하기 위하여 y-z 평면인 광학층(100) 절단면을 기준으로 전체 폴리머 분산체 중 z축 방향인 폴리머 분산체의 두께가 250㎚ 이하인 폴리머 분산체의 개수가 95% 이상일 수 있다. 광학필름(1000) 하부를 통해 투과되는 광은 매트릭스(110)와 다수 개의 폴리머 분산체(120) 간의 계면에서 반사, 투과 등의 광변조가 발생하는데, 반사, 투과되는 서로 다른 광학경로를 갖는 광 간에 보강간섭, 상쇄간섭이 발생하면서 일부 광은 광학필름 상부를 투과해 출사되며, 다른 일부는 상쇄간섭을 통해 소실되고, 나머지는 광학필름의 하부면이나 측면으로 출사될 수 있다. 따라서 광학필름(1000)의 하방에서 입사하는 광이 100% 상방으로 출사하기 어렵고 이로 인해 명암비, 시야각, 휘도가 저하될 수 있는데 두께가 250㎚ 이하인 폴리머 분산체의 개수가 95% 이상을 만족함을 통해 이러한 명암비, 시야각, 휘도 저하를 방지하기 유리하다. 만일 두께가 250㎚이하인 폴리머 분산체의 개수가 95% 미만일 경우, 달리 말하면 두께가 250㎚를 초과하는 폴리머 분산체의 개수가 5% 초과일 경우 휘도, 명암비 및 시야각 개선효과가 미미할 수 있고, 오히려 휘도, 명암비 및/또는 시야각을 저하시킬 수 있는 우려가 있다.In addition, according to an embodiment of the present invention, in order to achieve a more improved contrast ratio and viewing angle improvement effect, the thickness of the polymer dispersion in the z-axis direction of the entire polymer dispersion based on the cut surface of the optical layer 100, which is a y-z plane, is 250 The number of polymer dispersions of nm or less may be 95% or more. Light transmitted through the lower portion of the optical film 1000 undergoes light modulation such as reflection and transmission at the interface between the matrix 110 and the plurality of polymer dispersions 120. As constructive interference and destructive interference occur between the optical films, some of the light passes through the top of the optical film and is emitted, the other part is lost through destructive interference, and the rest may be emitted to the lower surface or side surface of the optical film. Therefore, it is difficult for the light incident from the lower side of the optical film 1000 to be emitted upward by 100%, which may lower the contrast ratio, viewing angle, and luminance. It is advantageous to prevent deterioration of contrast ratio, viewing angle, and luminance. If the number of polymer dispersions having a thickness of 250 nm or less is less than 95%, in other words, if the number of polymer dispersions having a thickness of more than 250 nm is more than 5%, the effect of improving the luminance, contrast ratio and viewing angle may be insignificant, rather There is a concern that luminance, contrast ratio and/or viewing angle may be lowered.

여기서, 폴리머 분산체의 두께란 y-z 평면의 광학층(100) 절단면에서 폴리머 분산체의 단면을 놓고 볼 때, 광학층(100) 두께방향에 해당하는 z축 방향에 평행한 상기 폴리머 분산체 단면의 둘레를 잇는 선분 중 가장 긴 선분의 길이를 의미한다. 이를 도 5c를 참조하여 설명하면, 제4폴리머 분산체(124)의 두께는 d1이며, 제5폴리머 분산체(125)의 두께는 d2이고, 제6폴리머 분산체(126)의 두께는 d3이며, 제7폴리머 분산체(127)의 두께는 d4이다.Here, the thickness of the polymer dispersion is the cross section of the polymer dispersion parallel to the z-axis direction corresponding to the thickness direction of the optical layer 100 when the cross section of the polymer dispersion is viewed from the cut plane of the optical layer 100 in the yz plane. It is the length of the longest line segment among the line segments connecting the circumference. Referring to FIG. 5C , the thickness of the fourth polymer dispersion 124 is d 1 , the thickness of the fifth polymer dispersion 125 is d 2 , and the thickness of the sixth polymer dispersion 126 is d 3 , and the thickness of the seventh polymer dispersion 127 is d 4 .

또한, 바람직하게는 두께가 120㎚ 이하인 폴리머 분산체의 개수가 60% 이상일 수 있고, 보다 바람직하게는 65% 이상, 더욱 바람직하게는 70% 이상, 더 바람직하게는 80% 이상일 수 있고, 이를 통해 보다 상승된 명암비 및 시야각 개선효과 및 휘도특성 향상을 달성하기에 유리하다. 만일 두께가 120㎚ 이하인 폴리머 분산체의 개수가 60% 미만일 경우 휘도가 현저히 저하될 우려가 있고, 특정 파장 대의 광에 대한 상쇄간섭이 과다하여 광학필름 표면이 붉게 보이는 등 특정 일색을 띠는 등의 문제가 있을 수 있다. 또한, 가시광 파장 영역대에서 반사특성이 저하되어 명암비나 시야각이 저하될 우려가 있다.Also, preferably, the number of polymer dispersions having a thickness of 120 nm or less may be 60% or more, more preferably 65% or more, still more preferably 70% or more, and still more preferably 80% or more. It is advantageous to achieve a higher contrast ratio and viewing angle improvement effect and luminance characteristic improvement. If the number of polymer dispersions having a thickness of 120 nm or less is less than 60%, there is a risk of a significant decrease in luminance, and excessive destructive interference for light in a specific wavelength range, causing the surface of the optical film to appear red, etc. There may be a problem. In addition, there is a concern that the reflection characteristic is lowered in the visible light wavelength range, and the contrast ratio or the viewing angle is lowered.

또한, 보다 바람직하게는 두께가 120㎚ 이하인 폴리머 분산체의 개수가 60% 이상인 경우에도 두께 50㎚ 미만인 폴리머 분산체가 10% 이하인 것이 좋고, 만일 두께 50㎚ 미만인 폴리머 분산체가 10%를 초과할 경우 상대적으로 50㎚ 이상인 두께를 가지는 폴리머 분산체의 개수가 줄어들어 명암비 및 시야각 개선효과가 줄어들 우려가 있다. 또한, 헤이즈 특성이 증가하여 휘도가 감소하는 우려가 있다. 또한, 두께 50㎚ 미만의 폴리머 분산체의 개수가 증가한다는 것은 50㎚ 이상의 두께를 가지는 폴리머 분산체 개수가 줄어드는 것뿐만 아니라 이들 폴리머 분산체 간 거리도 증가할 수 있어서 명암비 및 시야각 개선효과는 더더욱 감소될 우려가 있다. Further, more preferably, even when the number of polymer dispersions having a thickness of 120 nm or less is 60% or more, it is preferable that the polymer dispersion having a thickness of less than 50 nm is 10% or less, and if the polymer dispersion having a thickness of less than 50 nm exceeds 10%, the relative As a result, the number of polymer dispersions having a thickness of 50 nm or more is reduced, and there is a concern that the contrast ratio and viewing angle improvement effect may be reduced. In addition, there is a concern that haze characteristics increase and luminance decreases. In addition, the increase in the number of polymer dispersions having a thickness of less than 50 nm not only reduces the number of polymer dispersions having a thickness of 50 nm or more, but also increases the distance between these polymer dispersions, so the effect of improving the contrast ratio and viewing angle is further reduced. There is a risk of becoming

또한, 두께가 50㎚ 이상 ~ 120㎚ 이하인 폴리머 분산체의 개수는 50% 이상, 보다 바람직하게는 60% 이상, 보다 더 바람직하게는 70% 이상, 80% 이상, 90% 이상일 수 있고, 이를 통해 보다 상승된 명암비 및 시야각 개선효과와 함께, 컬러필터를 통과한 투과광에 대한 컬러변형이 최소화 또는 방지되어 색재현성이 보다 향상될 수 있는 이점이 있다.In addition, the number of polymer dispersions having a thickness of 50 nm or more to 120 nm or less may be 50% or more, more preferably 60% or more, and even more preferably 70% or more, 80% or more, or 90% or more. There is an advantage in that color reproducibility can be further improved by minimizing or preventing color distortion of transmitted light passing through a color filter, along with an effect of improving a contrast ratio and a viewing angle.

또한, 더욱 바람직하게는 두께가 50nm 이상 ~ 90nm 이하인 폴리머 분산체가 차지하는 비율이 클수록 명암비 및 시야각 개선, 색재현성 개선에 좋고, 일예로 45% 이상, 55% 이상, 60% 이상, 70% 이상 포함되는 것이 좋다.In addition, more preferably, the higher the ratio occupied by the polymer dispersion having a thickness of 50 nm or more to 90 nm or less, the better the contrast ratio, the viewing angle, and the color reproducibility. It is good.

또한, 광학층에 구비되는 다수 개의 폴리머 분산체(120) 각각은 광흡수제를함유하여 착색된 것일 수 있으며, 이를 통해 본 발명이 목적하는 명암비 개선 효과를 더욱 향상시킬 수 있다. 상기 광흡수제는 요오드, 헤라파타이트(Herapathit) 등의 색소 또는 2색성 물질, 또는 카본 블랙이 사용될 수 있다. 상기 광흡수제는 폴리머 분산체 전체 중량을 기준으로 2 ~ 60 중량%로 함유될 수 있고, 만일 2중량% 미만으로 함유 시 명암비 개선효과가 미미할 수 있고, 60 중량% 초과하여 구비시 명암비 개선효과 대비 투과되는 광량이 급격이 줄어 들어 휘도 저하의 우려가 있다다. In addition, each of the plurality of polymer dispersions 120 provided in the optical layer may be colored by containing a light absorber, and through this, the effect of improving the contrast ratio desired by the present invention may be further improved. The light absorber may be a pigment or dichroic material such as iodine or Herapathit, or carbon black. The light absorber may be contained in an amount of 2 to 60% by weight based on the total weight of the polymer dispersion, and if it is contained in an amount less than 2% by weight, the effect of improving the contrast ratio may be insignificant. There is a risk of luminance deterioration due to the rapid decrease in the amount of transmitted light.

또한, 폴리머 분산체(120)는 광흡수제 이외에 광흡수 기능을 갖는 공지된 염료를 더 함유할 수 있다. 상기 염료는 유기 염료일 수 있으며, 일예로 포르피린계 염료일 수 있으며, 이를 통해, 특정 파장대에서만 광을 흡수하는 효과를 낼 수 있다. In addition, the polymer dispersion 120 may further contain a known dye having a light absorbing function in addition to the light absorbing agent. The dye may be an organic dye, for example, a porphyrin-based dye, and through this, an effect of absorbing light only in a specific wavelength range may be produced.

한편, 본 발명의 일 실시예에 따른 광학필름(1000)은 도 2 및 도 3에 도시된 것과 같이 광학층(100)의 양면에 배치된 스킨층(211,212)을 더ㄹ 포함할 수 있다. 상기 스킨층(211,212)은 광학층(100)의 기계적 강도를 보완하고, 외부인자로부터 광학층(100)을 보호하는 기능을 담당한다. 이때, 상기 광학층(100)과 스킨층(211,212) 사이에는 별도의 접착층이 더 구비될 수 있으나, 바람직하게는 상기 스킨층(211,212)은 별도의 접착층 없이 광학층(100)과 함께 공압출되어 일체로 형성된 것일 수 있다. 그 결과 접착층으로 인한 광학물성의 저하를 방지할 수 있을 뿐만 아니라 보다 박형화된 광학필름을 구현하기에 유리하다.Meanwhile, the optical film 1000 according to an embodiment of the present invention may further include skin layers 211 and 212 disposed on both sides of the optical layer 100 as shown in FIGS. 2 and 3 . The skin layers 211 and 212 serve to supplement the mechanical strength of the optical layer 100 and protect the optical layer 100 from external factors. At this time, a separate adhesive layer may be further provided between the optical layer 100 and the skin layers 211 and 212, but preferably, the skin layers 211 and 212 are coextruded together with the optical layer 100 without a separate adhesive layer. It may be integrally formed. As a result, it is possible to prevent deterioration of optical properties due to the adhesive layer and to realize a thinner optical film.

나아가, 종래 광학층을 연신한 후 미연신 스킨층과의 후접착 되는 경우와 달리 본 발명의 일실시예에 포함된 스킨층(211,212)은 광학층(100)과 동시에 공압출된 후 연신공정이 수행되므로 적어도 하나의 축방향으로 연신된 것일 수 있다. 이를 통해 미연신된 스킨층에 비하여 표면경도가 향상되어 내스크래치성이 개선되며 내열성이 향상될 수 있다.Furthermore, unlike the case where the conventional optical layer is stretched and then adhered to the unstretched skin layer, the skin layers 211 and 212 included in one embodiment of the present invention are simultaneously co-extruded with the optical layer 100, followed by a stretching process. Since it is performed, it may be stretched in at least one axial direction. Through this, the surface hardness is improved compared to the unstretched skin layer, so that scratch resistance and heat resistance can be improved.

상기 스킨층(211,212)은 광학필름의 지지기능을 수행하기 위하여 통상적으로 사용되는 스킨층의 재질일 수 있고, 바람직하게는 폴리에틸렌나프탈레이트(PEN), 코폴리에틸렌나프탈레이트(co-PEN), 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC), 폴리카보네이트(PC) 얼로이, 폴리스타이렌(PS), 내열폴리스타이렌(PS), 폴리메틸메타아크릴레이트(PMMA), 폴리부틸렌테레프탈레이트(PBT), 폴리프로필렌(PP), 폴리에틸렌(PE), 아크릴로니트릴부타디엔스티렌(ABS), 폴리우레탄(PU),폴리이미드(PI),폴리비닐클로라이드(PVC), 스타이렌아크릴로니트릴혼합(SAN),에틸렌초산비닐(EVA), 폴리아미드(PA), 폴리아세탈(POM), 페놀, 에폭시(EP), 요소(UF), 멜라닌(MF), 불포화포리에스테르(UP), 실리콘(SI) 및 사이크로올레핀폴리머를 단독 또는 혼합하여 사용할 수 있으며 보다 바람직하게는 상술한 매트릭스(110)의 성분과 동일한 재질을 사용할 수 있다.The skin layers 211 and 212 may be a skin layer material commonly used to perform the support function of the optical film, and preferably polyethylene naphthalate (PEN), co-polyethylene naphthalate (co-PEN), polyethylene tere Phthalate (PET), polycarbonate (PC), polycarbonate (PC) alloy, polystyrene (PS), heat-resistant polystyrene (PS), polymethyl methacrylate (PMMA), polybutylene terephthalate (PBT), polypropylene (PP), polyethylene (PE), acrylonitrile butadiene styrene (ABS), polyurethane (PU), polyimide (PI), polyvinyl chloride (PVC), styrene acrylonitrile blend (SAN), ethylene vinyl acetate (EVA), polyamide (PA), polyacetal (POM), phenol, epoxy (EP), urea (UF), melanin (MF), unsaturated polyester (UP), silicone (SI) and cycloolefin polymer. It may be used alone or in combination, and more preferably, the same material as the above-described matrix 110 may be used.

상술한 광학필름(1000)에서 매트릭스(110)의 두께는 100㎛ 이하, 보다 바람직하게는 80㎛ 이하, 보다 더 바람직하게는 60㎛이하, 더 바람직하게는 50㎛ 이하, 더욱 바람직하게는 15 ~ 50㎛일 수 있다. 만일 매트릭스(110)의 두께가 100㎛를 초과할 경우 상술한 이상적인 크기 분포를 가지는 폴리머 분산체가 분산된 경우에도 명암비 및 시야각 개선효과가 미미할 수 있다. In the above-described optical film 1000, the matrix 110 has a thickness of 100 μm or less, more preferably 80 μm or less, even more preferably 60 μm or less, still more preferably 50 μm or less, still more preferably 15 to 15 μm. It may be 50 μm. If the thickness of the matrix 110 exceeds 100 μm, the effect of improving the contrast ratio and viewing angle may be insignificant even when the polymer dispersion having the above-described ideal size distribution is dispersed.

더불어 상기 스킨층의 두께는 5 ~ 20㎛일 수 있으나 이에 제한되지 않는다. In addition, the skin layer may have a thickness of 5 to 20 μm, but is not limited thereto.

또한, 상기 광학필름(1000)은 헤이즈가 20% 이하일 수 있다. 만일 헤이즈가 20%를 초과하면 휘도가 저하되는 등 본 발명의 목적을 달성하기 어려울 수 있다.In addition, the optical film 1000 may have a haze of 20% or less. If the haze exceeds 20%, it may be difficult to achieve the object of the present invention, such as decrease in luminance.

이하 상술한 광학필름(1000)의 제조방법에 대해서 설명한다. 본 발명의 일 실시예에 의한 광학필름(1000)은 매트릭스 성분과, 광흡수제 및 폴리머 분산체 성분을 압출부에 공급하는 단계, 매트릭스 내부에 포함된 폴리머 분산체 성분이 랜덤하게 배열될 수 있도록 흐름제어부에서 퍼짐을 유도하는 단계, 냉각 및 평활화하는 단계, 냉각 및 평활화된 필름을 연신하는 단계, 및 상기 연신된 필름을 열고정하는 단계를 거쳐 제조될 수 있다.Hereinafter, a method of manufacturing the above-described optical film 1000 will be described. The optical film 1000 according to an embodiment of the present invention includes the steps of supplying a matrix component, a light absorber, and a polymer dispersion component to an extrusion unit, and a flow so that the polymer dispersion component included in the matrix can be randomly arranged. It can be manufactured through the steps of inducing spreading in a controller, cooling and smoothing, stretching the cooled and smoothed film, and heat-setting the stretched film.

먼저, (1) 단계로서 매트릭스 성분과, 광흡수제 및 폴리머 분산체 성분을 압출부에 공급하는 단계를 수행할 수 있다. 이들 각각의 성분은 먼저 혼합된 후 단일의 압출부에 공급되거나 각각의 성분이 개별적으로 독립된 압출부들에 공급될 수 있고, 이 경우 압출부는 2개 이상으로 구성될 수 있다. 다만, 바람직하게는 이들 각각의 성분이 압출부에 공급되기 전에 충분한 교반을 통해 혼합된 후 단일의 압출부에 공급될 수 있다. 이때 상기 압출부는 익스트루더일 수 있으며, 이는 고체 상의 공급된 폴리머 성분들을 액상으로 전환시킬 있도록 가열수단 등을 더 포함할 수 있다.First, as step (1), a step of supplying a matrix component, a light absorber, and a polymer dispersion component to an extrusion unit may be performed. Each of these components may be first mixed and then supplied to a single extrusion unit or each component may be individually supplied to independent extrusion units, in which case two or more extrusion units may be configured. However, preferably, each of these components may be mixed through sufficient stirring before being supplied to the extruding unit and then supplied to a single extruding unit. At this time, the extruder may be an extruder, which may further include a heating means to convert the supplied polymer components in a solid phase into a liquid phase.

한편, 매트릭스 성분의 내부에 폴리머 분산체 성분이 배열되기 위해서는 매트릭스 성분과 폴리머 분산체 성분 간 흐름성 차이가 존재함이 바람직하고, 이를 위해 두 성분 간 점도를 차이가 있도록 설계하며, 바람직하게는 매트릭스 성분의 흐름성이 폴리머 분산체 성분보다 좋도록 설계하는 것이 좋다. 매트릭스 성분과 폴리머 분산체 성분은 믹싱존과 메시필터존을 통과하면서 매트릭스 성분 내에 폴리머 분산체 성분이 점성에 차이를 통해 랜덤하게 배열될 수 있다. On the other hand, in order to arrange the polymer dispersion component inside the matrix component, it is preferable that there is a difference in flowability between the matrix component and the polymer dispersion component. It is better to design the component so that the flowability is better than that of the polymer dispersion component. The matrix component and the polymer dispersion component may be randomly arranged through the viscosity difference of the polymer dispersion component in the matrix component while passing through the mixing zone and the mesh filter zone.

상술한 폴리머 분산체(120)의 두께 크기 조절은 1차적으로 (1)단계의 공정 조절을 통해 이루어질 수 있고, 구체적으로 압출부에 각각의 성분이 투입되기 전 충분한 교반을 통해 두 성분이 혼합된 상태로 압출부에 투입하는지 여부나 압출 시 토출량 등을 통해서 폴리머 분산체 두께 크기나 분산성을 조절할 수 있다.The thickness and size of the above-described polymer dispersion 120 can be primarily controlled through the process control in step (1), and specifically, the two components are mixed through sufficient stirring before each component is introduced into the extrusion unit. It is possible to adjust the thickness size or dispersibility of the polymer dispersion through whether or not it is introduced into the extrusion unit in the state or by the discharge amount during extrusion.

다음으로 본 발명의 (2) 단계로서 매트릭스 내부에 위치한 폴리머 분산체 성분이 랜덤하게 배열될 수 있도록 흐름제어부에서 퍼짐을 유도할 수 있다. 상기 흐름제어부는 공지된 흐름제어부를 이용할 수 있고, 일예로 코트-행거 다이를 이용할 수 있다. 상기 (2) 단계의 흐름제어부를 통한 퍼짐의 유도를 통해서 폴리머 분산체 두께나 분산성을 2차적으로 더 조절하는 것이 가능하다. Next, as step (2) of the present invention, the flow control unit can induce spreading so that the polymer dispersion components located inside the matrix can be randomly arranged. The flow control unit may use a known flow control unit, and for example, a coat-hanger die may be used. Through the induction of spreading through the flow control unit in step (2), it is possible to further control the thickness or dispersibility of the polymer dispersion secondarily.

다음으로 본 발명의 (3) 단계로서 냉각 및 평활화하는 단계를 수행할 수 있다. 흐름제어부에서 이송된 필름을 냉각 및 평활화하는 단계로서 통상적인 광학필름의 제조에 이용되는 조건으로 냉각하여 고형화하고 이후 캐스팅 롤공정 등을 통해 평활화 단계를 수행할 수 있다.Next, cooling and smoothing may be performed as step (3) of the present invention. As a step of cooling and smoothing the film transferred from the flow control unit, it is cooled and solidified under the conditions used in the manufacture of conventional optical films, and then the smoothing step may be performed through a casting roll process or the like.

다음으로 본 발명의 (4) 단계로 냉각 및 평활화된 필름을 연신하는 단계를 수행할 수 있다. 상기 연신은 통상의 광학필름에 수행하는 연신공정을 통해 수행될 수 있으며, 이를 통해 매트릭스 성분과 폴리머 분산체 성분 간의 굴절율 차이를 유발시켜 계면에서 광변조 현상을 유발할 수 있다. 상기 연신은 일축연신 또는 이축연신을 수행할 수 있으며, 보다 바람직하게는 일축연신을 수행할 수 있다. 일축연신의 경우 연신방향은 일예로 x축 방향일 수 있다. 또한 연신비는 3 ~ 12배 일 수 있다. Next, a step of stretching the cooled and smoothed film in step (4) of the present invention may be performed. The stretching may be performed through a stretching process performed on a conventional optical film, and through this, a difference in refractive index between the matrix component and the polymer dispersion component may cause light modulation at the interface. The stretching may be performed by uniaxial stretching or biaxial stretching, and more preferably uniaxial stretching. In the case of uniaxial stretching, the stretching direction may be, for example, the x-axis direction. Also, the stretching ratio may be 3 to 12 times.

다음으로 본 발명의 (5) 단계로 상기 연신된 필름을 열고정하는 단계를 수행할 수 있다. 상기 열고정은 통상의 방법을 통해 열고정될 수 있으며, 바람직하게는 180 ~ 200℃ 에서 0.1 ~ 3분 동안 IR 히터를 통해 수행될 수 있다.Next, in step (5) of the present invention, a step of heat-setting the stretched film may be performed. The heat setting may be performed through a conventional method, and preferably may be performed at 180 to 200° C. for 0.1 to 3 minutes using an IR heater.

도 6을 참조하여 설명하면, 상술한 제조방법을 통해 제조되는 본 발명의 일 실시예에 의한 광학필름(1000)은 편광판(4000)을 구현하는데 구비될 수 있고, 특히 액정패널의 하방에 위치하는 백라이트유닛에 대향하도록 액정패널 광입사면 상에 배치되는 하부 편광판과, 상기 액정패널의 광 출사면 상에 배치되는 상부 편광판 중 상부 편광판으로써 적합하다. 본 발명의 일 실시예에 의한 광학필름(1000)을 상부 편광판의 편광자 광 출사면 상에 배치 시 내부광에 의한 명암비 개선효과가 현저하고 시야각이 증대되며 우수한 휘도특성을 달성할 수 있는 이점이 있다. Referring to FIG. 6, the optical film 1000 according to an embodiment of the present invention manufactured through the above-described manufacturing method may be provided to implement a polarizing plate 4000, and is particularly located below the liquid crystal panel. It is suitable as an upper polarizing plate among a lower polarizing plate disposed on the light incident surface of the liquid crystal panel to face the backlight unit and an upper polarizing plate disposed on the light exit surface of the liquid crystal panel. When the optical film 1000 according to an embodiment of the present invention is disposed on the polarizer light exit surface of the upper polarizer, the contrast ratio improvement effect by internal light is remarkable, the viewing angle is increased, and excellent luminance characteristics can be achieved. .

상기 편광판(4000)은 흡수편광자(2000) 및 상기 흡수편광자(2000)의 상부에 배치되는 명암비 및 시야각 개선용 광학필름(1000)을 포함하여 구현된다. The polarizing plate 4000 is implemented by including an absorption polarizer 2000 and an optical film 1000 for improving a contrast ratio and a viewing angle disposed above the absorption polarizer 2000 .

상기 흡수편광자(2000)는 서로 직교하는 진동면을 갖는 제1편광 및 제2편광 중, 제1편광(또는 제2편광)은 투과하고 제2편광(또는 제1편광)은 흡수하는 편광자로써, 이러한 광학기능을 갖는 공지된 편광층(2100)을 구비하며, 상기 편광층(2100)은 그 예시로, 폴리비닐알코올 등의 기재필름이 요오드계 성분 또는 이색성 염료로 염착된 것일 수 있다. 또한, 상기 기재에 염착되는 염료 중 하나인 상기 요오드계 성분은 요오드 및/또는 요오드화 칼륨과 같은 요오드계 화합물일 수 있다. 또한 상기 이색성 염료는 분자의 장축방향으로 광범위한 파장에서 큰 흡광도를 가지며, 단축방향으로 흡광도가 극히 작으면서도, 기재가 되는 필름에 친화성이 좋고, 결정영역에도 염색이 가능하며, 기재가 연신될 때 함께 배향되기 쉽고, 색상이 선명하며 시각상의 콘트라스가 크다고 알려진 공지의 이색성 염료의 경우 제한없이 사용될 수 있으므로 본 발명은 이에 대해 특별히 한정하지 않고, 구체적 설명을 생략한다.The absorption polarizer 2000 is a polarizer that transmits first polarized light (or second polarized light) and absorbs second polarized light (or first polarized light) among first and second polarized light having vibration planes orthogonal to each other. A known polarization layer 2100 having an optical function is provided. As an example, the polarization layer 2100 may be a base film such as polyvinyl alcohol dyed with an iodine-based component or a dichroic dye. In addition, the iodine-based component, which is one of the dyes dyed on the substrate, may be an iodine-based compound such as iodine and/or potassium iodide. In addition, the dichroic dye has high absorbance in a wide range of wavelengths in the direction of the long axis of the molecule, and extremely low absorbance in the direction of the short axis, but has good affinity for the film to be the base material, can be dyed even in the crystal region, and can stretch the base material. In the case of known dichroic dyes known to be easily oriented together, vivid in color and high in visual contrast, they can be used without limitation, so the present invention is not particularly limited thereto, and a detailed description thereof will be omitted.

상기 편광층(2100)은 두께가 일예로 10 ~ 200㎛일 수 있으나 이에 제한되는 것은 아니며, 목적에 따라 변경할 수 있다.The polarization layer 2100 may have a thickness of, for example, 10 to 200 μm, but is not limited thereto and may be changed according to the purpose.

또한, 상기 흡수편광자(2000) 편광층(210)을 지지하고 보호하기 위하여 일면 또는 양면에 보호필름(2210,2220)을 구비할 수 있다. 상기 보호필름(2210,2220)은 통상적인 흡수편광필름에 사용되는 보호필름의 경우 제한 없이 사용될 수 있고, 투명성이나 기계적 강도, 열 안정성이나 수분 차폐성 등이 뛰어난 폴리머 등이 바람직하게 채용될 수 있다. 상기 보호필름(2210,2220)은 일예로, 트리아세틸셀룰로오스(TAC)와 같은 아세테이트계 수지, 폴리에스테르계 수지, 폴리에테르술폰계 수지, 폴리카보네이트계 수지, 폴리아미드계 수지, 폴리이미드계 수지, 폴리올레핀계 수지, 아크릴계 수지, 폴리노르보르넨계 수지 등을 사용할 수 있다. 일예로 상기 보호필름은 광학특성을 고려하여 트리아세틸셀룰로오스(TAC) 필름을 사용할 수 있다. 또는 내열성, 내습성 측면에서 폴리에스테르계 필름, 구체적 일예로 폴리에틸렌테레프탈레이트 필름일 수 있다. 상기 폴리에틸렌테레프탈레이트 필름은 면 내 위상차가 8000nm 이상, 또는 10,000 ~ 15,000nm일 수 있다. 또한, 상기 보호필름(2210,2220)은 두께가 50 ~ 150㎛일 수 있으나 이에 제한되는 것은 아니다.In addition, in order to support and protect the polarization layer 210 of the absorption polarizer 2000, protective films 2210 and 2220 may be provided on one or both surfaces. The protective films 2210 and 2220 may be used without limitation in the case of a protective film used in a conventional absorption polarizing film, and a polymer having excellent transparency, mechanical strength, thermal stability, or moisture barrier properties may be preferably used. The protective films 2210 and 2220 are, for example, acetate-based resins such as triacetyl cellulose (TAC), polyester-based resins, polyethersulfone-based resins, polycarbonate-based resins, polyamide-based resins, polyimide-based resins, Polyolefin-based resins, acrylic-based resins, polynorbornene-based resins, and the like can be used. For example, the protective film may use a triacetyl cellulose (TAC) film in consideration of optical characteristics. Alternatively, it may be a polyester-based film in terms of heat resistance and moisture resistance, for example, a polyethylene terephthalate film. The polyethylene terephthalate film may have an in-plane retardation of 8000 nm or more, or 10,000 to 15,000 nm. In addition, the protective films 2210 and 2220 may have a thickness of 50 to 150 μm, but are not limited thereto.

또한, 상술한 흡수편광자(2000)와 광학필름(1000) 간 계면에는 별도의 접착층(미도시)을 개재하여 일체로 접합될 수 있다. 상기 접착층은 광학필름 간의 부착에 사용되며, 광학적 특성을 저하시키지 않는 공지된 접착성분을 사용하여 구현될 수 있고, 일예로, 비닐알콜계 폴리머를 포함하는 접착성분의 단독 또는 붕산, 붕사, 글루타르알데히드, 멜라민, 옥살산 등, 비닐알콜계 폴리머의 수용성 가교제의 적어도 1종과 접착성분이 병용된 접착제로 형성된 것일 수 있다. 또한, 상기 접착제는 다른 첨가제나 산 등의 촉매를 배합할 수 있다. In addition, the interface between the above-described absorption polarizer 2000 and the optical film 1000 may be integrally bonded through a separate adhesive layer (not shown). The adhesive layer is used for attachment between optical films and can be implemented using a known adhesive component that does not degrade optical properties. For example, an adhesive component including a vinyl alcohol-based polymer alone or boric acid, borax, glutar It may be formed of an adhesive in which at least one water-soluble cross-linking agent for a vinyl alcohol-based polymer such as aldehyde, melamine, or oxalic acid is combined with an adhesive component. In addition, the adhesive may contain other additives or catalysts such as acids.

또한, 편광판(4000)은 광학필름(1000) 상에 기능층(1500)을 더 구비할 수 있다. 상기 기능층(1500)은 프라이머층, 하드코팅층, 내지문성층, 반사방지층, 안티글레어층, 저반사층, 초저반사층 등일 수 있다. 또한, 상기 기능층(1500)은 복합기능을 발휘하기 위하여 여러 층이 적층되어 구현될 수도 있다. 상기 기능층(1500)의 두께는 구비되는 기능층의 종류와, 적층수를 고려해 적절히 변경될 수 있으므로 본 발명은 이에 대해 특별히 한정하지 않는다.In addition, the polarizing plate 4000 may further include a functional layer 1500 on the optical film 1000 . The functional layer 1500 may be a primer layer, a hard coating layer, an anti-fingerprint layer, an antireflection layer, an antiglare layer, a low reflection layer, an ultra low reflection layer, and the like. In addition, the functional layer 1500 may be implemented by stacking several layers in order to exhibit multiple functions. Since the thickness of the functional layer 1500 may be appropriately changed in consideration of the type of functional layer and the number of layers, the present invention is not particularly limited thereto.

또한, 도 7에 도시된 것과 같이 본 발명의 일 실시예에 의한 편광판(4000)은 액정패널(5000) 하방에 배치되는 백라이트 유닛(7000)에 대향해서 액정패널(5000) 상방, 즉 액정표시장치(8000)의 시인측에 배치될 수 있으며, 구체적으로 흡수편광자 상부에 배치됨으로써 백라이트 유닛(7000)으로부터 출사된 뒤 하부 편광판인 흡수편광자(2000), 액정패널(5000), 상부 편광판 중 흡수편광자를 통과한 내부광의 명암비를 상승시키며, 특히 측면 명암비를 향상시키면서도 정면 명암비의 감소를 방지하거나 최소화시키는 역할을 수행한다. 더불어 액정표시장치(8000_의 시야각을 향상시킬 수 있다. In addition, as shown in FIG. 7 , the polarizer 4000 according to an embodiment of the present invention opposes the backlight unit 7000 disposed below the liquid crystal panel 5000 and is above the liquid crystal panel 5000, that is, the liquid crystal display device. (8000) may be disposed on the viewing side, and specifically, by being disposed above the absorption polarizer, after being emitted from the backlight unit 7000, the absorption polarizer 2000, which is a lower polarizer, the liquid crystal panel 5000, and the upper polarizer are absorbed. It increases the contrast ratio of the passed internal light, and in particular, prevents or minimizes the reduction of the front contrast ratio while improving the side contrast ratio. In addition, the viewing angle of the liquid crystal display device 8000_ can be improved.

구체적으로 액정표시장치(8000)는 백라이트유닛(7000), 하부편광판으로써 흡수편광자(2000), 액정패널(5000), 색변환층(5300) 및 상부편광판으로써 편광판(4000) 순으로 배치되어 구현될 수 있다. Specifically, the liquid crystal display device 8000 is implemented by arranging a backlight unit 7000, an absorption polarizer 2000 as a lower polarizer, a liquid crystal panel 5000, a color conversion layer 5300, and a polarizer 4000 as an upper polarizer. can

상기 백라이트유닛(7000)은 통상적인 LCD 디스플레이에 채용되는 것일 수 있고, 일예로, 광원, 반사필름, 도광판, 광확산필름, 집광필름, 반사편광필름 등 공지된 구성으로 구성될 수 있다. The backlight unit 7000 may be employed in a conventional LCD display, and may include, for example, a known configuration such as a light source, a reflective film, a light guide plate, a light diffusion film, a condensing film, and a reflective polarizing film.

또한, 상기 액정패널(5000)은 액정층(5100) 및 상기 액정층(5100) 상부와 하부를 지지하는 지지판(5210,5220)을 포함하고, 전극라인 등 공지된 구성을 더 포함할 수 있다. 또한, 액정패널(5000)은 VA(vertical alignment) 모드, IPS 모드, PVA(patterned vertical alignment) 모드 또는 S-PVA(super-patterned vertical alignment) 모드를 채용할 수 있지만, 이에 제한되지 않는다.In addition, the liquid crystal panel 5000 includes a liquid crystal layer 5100 and support plates 5210 and 5220 supporting upper and lower portions of the liquid crystal layer 5100, and may further include a known configuration such as an electrode line. In addition, the liquid crystal panel 5000 may adopt a vertical alignment (VA) mode, an IPS mode, a patterned vertical alignment (PVA) mode, or a super-patterned vertical alignment (S-PVA) mode, but is not limited thereto.

한편 본 발명에서는 광학필름의 용도를 액정표시장치를 중심으로 설명하였지만 이에 한정되는 것은 아니며, 프로젝션 디스플레이, 플라즈마 디스플레이, 전계방출디스플레이, OLED 디스플레이 등 평판디스플레이 기술에 널리 사용될 수 있으며, 이에 국한되지 않고, 유리창, 편광을 요구하는 작업조명 등에 널리 응용될 수 있다. On the other hand, in the present invention, the use of the optical film has been described mainly for liquid crystal display devices, but is not limited thereto, and can be widely used in flat panel display technologies such as projection displays, plasma displays, field emission displays, and OLED displays, but is not limited thereto, It can be widely applied to glass windows and task lighting requiring polarization.

하기의 실시예를 통하여 본 발명을 더욱 구체적으로 설명하기로 하지만, 하기 실시예가 본 발명의 범위를 제한하는 것은 아니며, 이는 본 발명의 이해를 돕기 위한 것으로 해석되어야 할 것이다.Although the present invention will be described in more detail through the following examples, the following examples are not intended to limit the scope of the present invention, which should be interpreted to aid understanding of the present invention.

<실시예1> <Example 1>

굴절율이 1.65인 폴리에텔렌나프탈레이트(PEN) 99.5중량%와 광흡수제로 카본블랙 3 중량% 혼합된 분산체 성분과 매트릭스 성분으로서 테레프탈레이트와 에틸글리콜과 사이크로헥산디메탄올 1:2 몰비로 중합반응한 폴리시클로헥실렌 디메틸렌테레프탈레이트(poly cyclohexylene dimethylene terephthalate, PCTG)를 38중량%, 폴리카보네이트 60 중량% 및 인산염이 포함된 열안정제 2.0 중량%를 포함한 굴절률이 1.58인 폴리카보네이트 얼로이를 1차 분산시켜 각각 제1 압출부에 투입하였다. 스킨층 성분으로서 매트릭스 성분과 동일한 성분을 포함한 원료를 제2 압출부에 투입하되 제2압출부는 유로기를 사용하여 스킨층이 동일한 두께로 매트릭스 상부 및 하부 표층 상에 구성되도록 하여 제조 하였다.99.5% by weight of polyethylene naphthalate (PEN) with a refractive index of 1.65 and 3% by weight of carbon black as a light absorber Polymerization reaction with 1:2 molar ratio of terephthalate, ethyl glycol and cyclohexanedimethanol as a matrix component and a dispersion component mixed A polycarbonate alloy with a refractive index of 1.58 containing 38% by weight of polycyclohexylene dimethylene terephthalate (PCTG), 60% by weight of polycarbonate, and 2.0% by weight of a heat stabilizer containing phosphate is primarily dispersed. and each was put into the first extrusion unit. Raw materials containing the same ingredients as the matrix component as the skin layer component were introduced into the second extrusion unit, but the second extrusion unit was prepared by using a flow path so that the skin layer had the same thickness on the upper and lower surface layers of the matrix.

매트릭스 성분과 분산체 성분의 압출 온도는 245℃로 하고 Cap.Rheometer 확인하여 양 성분의 I.V.차가 0.013 나도록 폴리머 흐름을 보정하고, Filteration Mixer가 적용된 유로 통과하여 매트릭스 성분 내부에 분산체가 랜덤 분산되도록 유도하였고, 이후 매트릭스 성분의 양면에 스킨층 성분을 합지하였다. 이후 폴리머를 유속 및 압력구배를 보정하는 코트행거 다이에서 퍼짐을 유도하였다. 구체적으로 다이 입구의 폭은 200mm이고 두께는 10mm이며 다이출구의 폭은 1,260 mm이고, 두께는 0.75mm이며, 유속은 1.0m/min이었다. 그 뒤 냉각 및 캐스팅 롤에서 평활화 공정을 수행하고 MD 방향으로 6배 연신하였다. 이어서 180℃에서 2분 동안 히터챔버를 통해 열고정을 수행하여 매트릭스 두께가 60㎛이고, 두께가 30.25㎛인 스킨층을 상기 매트릭스 주표면 양면에 구비한 총 두께는 125㎛이고, 도 2와 같은 단면구조를 갖는 분산체가 매트릭스 내부에 랜덤하게 분산된 광학층을 갖는 하기 표 1과 같은 광학필름을 제조하였다. 제조된 광학필름에서 분산체 성분의 굴절율은 (nx: 1.88, ny:1.58, nz:1.58)이고 매트릭스 성분의 굴절율은 1.58었다.The extrusion temperature of the matrix component and the dispersion component was set to 245 ° C, and the cap. rheometer was checked to correct the polymer flow so that the IV difference between the two components was 0.013, and the dispersion was randomly dispersed inside the matrix component by passing through the flow path to which the Filteration Mixer was applied. , Then, the skin layer components were laminated on both sides of the matrix component. The polymer was then induced to spread in a coat hanger die compensating for the flow rate and pressure gradient. Specifically, the width of the die entrance was 200 mm and the thickness was 10 mm, the width of the die exit was 1,260 mm, the thickness was 0.75 mm, and the flow rate was 1.0 m/min. After that, a smoothing process was performed on a cooling and casting roll, and it was stretched 6 times in the MD direction. Subsequently, heat setting was performed through a heater chamber at 180° C. for 2 minutes, so that a matrix thickness of 60 μm and skin layers having a thickness of 30.25 μm were provided on both sides of the main surface of the matrix, and the total thickness was 125 μm, as shown in FIG. An optical film as shown in Table 1 below having an optical layer in which a dispersion having a cross-sectional structure was randomly dispersed inside a matrix was prepared. In the prepared optical film, the refractive index of the dispersion component was (n x : 1.88, n y : 1.58, n z : 1.58) and the refractive index of the matrix component was 1.58.

<실시예2 ~ 3><Examples 2 to 3>

실시예1과 동일하게 실시하여 제조하되, 제법 상 압출온도 및 점도를 조정하여 하기 표 1과 같이 폴리머 분산체의 두께가 변경된 광학필름을 제조하였다.It was prepared in the same manner as in Example 1, but the extrusion temperature and viscosity were adjusted to prepare an optical film having a changed thickness of the polymer dispersion as shown in Table 1 below.

<실시예 4 ~ 6><Examples 4 to 6>

실시예2와 동일하게 실시하여 제조하되, 제조되는 광학층의 두께를 변경하여 하기 표 1과 같은 광학필름을 제조하였다.It was prepared in the same manner as in Example 2, but the thickness of the optical layer was changed to prepare an optical film as shown in Table 1 below.

<실시예 7 ~ 8><Examples 7 to 8>

실시예3과 동일하게 실시하여 제조하되, 카본블랙 함량을 조정하여 하기 표 1과 같은 광학필름을 제조하였다.It was prepared in the same manner as in Example 3, but the carbon black content was adjusted to prepare an optical film as shown in Table 1 below.

<비교예1><Comparative Example 1>

폴리머 분산체가 랜덤하게 배열되지 않은 광학필름을 제조했다. 구체적으로 폴리머 분산체 성분(이하 제1성분)으로서 굴절율이 1.65인 PEN과, 매트릭스 성분(이하 제2성분)으로서 테레프탈레이트와 에틸글리콜과 사이크로헥산디메탄올 1:2 몰비로 중합반응한 폴리시클로헥실렌 디메틸렌테레프탈레이트(poly cyclohexylene dimethylene terephthalate, PCTG)를 38중량%, 폴리카보네이트 60 중량% 및 인산염이 포함된 열안정제 2 중량% 포함한 굴절률이 1.58인 폴리카보네이트 얼로이 및 스킨층 성분으로서 매트릭스 성분과 동일한 성분을 각각 도 8의 제1 압출부(220), 제2 압출부(221) 및 제3 압출부(222)에 투입하였다. 제1 성분과 제2 성분의 압출 온도는 295℃로 하고 Cap.Rheometer 확인하여 I.V. 조정을 통해 폴리머 흐름을 보정하고, 스킨층은 280℃온도 수준에서 압출공정을 수행하였다. 상기 제1 성분을 제1 가압수단(230, 가와사키사 기어펌프)로 이송하고 제2 성분 역시 제2 가압수단(231, 가와사키사 기어펌프)으로 이송하였다. 제1 가압수단의 토출량은 각각 순서대로 8.9 kg/h 이고, 제2 가압수단의 토출량은 8.9 kg/h 이다. 이후 도 9와 같은 해도형 압출구금을 이용하여 해도형 복합류를 제조하였다. 구체적으로 해도형 압출구금 중 제4 구금분배판(T4)의 도성분 레이어의 개수는 400개이고, 도성분 공급로의 구금홀의 직경은 0.17mm이며 도성분 공급로의 개수는 각각 25000개 였다. 제6 구금분배판의 토출구의 직경은 15 mm×15 mm 이었다. 3층 구조의 피드블록에서 상기 제3 압출부로부터 스킨층 성분이 유로를 통해 흘러들어 상기 해도형 복합류(매트릭스 폴리머)의 상하면에 스킨층을 형성하였다. 해도형 복합류의 종횡비가 1/30295가 되도록 상기 스킨층이 형성된 기재층 폴리머를 유속 및 압력구배를 보정하는 코트행거다이에서 퍼짐을 유도하였다. 구체적으로 다이 입구의 폭은 200mm이고 두께는 20mm이며 다이출구의 폭은 960 mm이고, 두께는 2.4 mm이며, 유속은 1m/min이었다. 그 뒤 냉각 및 캐스팅 롤에서 평활화 공정을 수행하고 MD 방향으로 6배 연신하였다. 그 결과 제1 성분은 길이방향 단면의 장축길이는 변화가 없었으나 단축길이가 줄어들었다. 그 뒤 180℃에서 2분 동안 IR 히터를 통해 열고정을 수행하여 도 10과 같은 판산형 폴리머 분산체가 분산된 광학층이 포함된 광학필름을 제조하였다. 제조된 광학필름 내 폴리머 분산체 성분의 굴절율은 (nx: 1.88, ny:1.58, nz:1.58)이고 매트릭스 성분의 굴절율은 1.58였으며, 중합체의 종횡비는 대략 1/180000이고, 층수는 400 레이어이며, 두께는 84nm, 장축길이 15.5mm이었다. 이때 제조된 광학층의 두께는 100㎛이며, 양면에 스킨층 포함하여 광학필름 총 두께가 125㎛이었다. An optical film in which the polymer dispersion is not randomly arranged was prepared. Specifically, PEN having a refractive index of 1.65 as a polymer dispersion component (hereinafter, the first component), and terephthalate, ethyl glycol, and cyclohexanedimethanol as a matrix component (hereinafter, the second component) Polycyclopolymerized at a molar ratio of 1: 2 A polycarbonate alloy with a refractive index of 1.58 containing 38% by weight of hexylene dimethylene terephthalate (PCTG), 60% by weight of polycarbonate, and 2% by weight of a heat stabilizer containing phosphate and a matrix component as a skin layer component The same ingredients were introduced into the first extruding unit 220, the second extruding unit 221, and the third extruding unit 222 of FIG. 8, respectively. The extrusion temperature of the first component and the second component was set to 295 ° C, and the cap. rheometer was checked to correct the polymer flow through IV adjustment, and the skin layer was extruded at a temperature level of 280 ° C. The first component was transferred to the first pressurizing means (230, Kawasaki gear pump), and the second component was also transferred to the second pressurizing means (231, Kawasaki gear pump). The discharge amount of the first pressurizing means is 8.9 kg/h in each order, and the discharge amount of the second pressurizing means is 8.9 kg/h. Thereafter, sea-island type composites were manufactured using the sea-island type extrusion nozzle as shown in FIG. 9 . Specifically, the number of island component layers of the fourth cap distribution plate (T4) in the sea-island type extrusion cap was 400, the diameter of the cap hole of the island component supply path was 0.17 mm, and the number of island component supply channels was 25,000 respectively. The diameter of the outlet of the sixth confinement distribution plate was 15 mm × 15 mm. In the feed block having a three-layer structure, skin layer components flowed from the third extrusion part through a flow path to form skin layers on the upper and lower surfaces of the island-in-the-sea composites (matrix polymer). The base layer polymer on which the skin layer was formed was induced to spread in a coat hanger die for correcting the flow rate and pressure gradient so that the aspect ratio of the sea-island composites was 1/30295. Specifically, the width of the die entrance was 200 mm and the thickness was 20 mm, the width of the die exit was 960 mm, the thickness was 2.4 mm, and the flow rate was 1 m/min. After that, a smoothing process was performed on a cooling and casting roll, and it was stretched 6 times in the MD direction. As a result, the first component had no change in the length of the major axis of the cross section in the longitudinal direction, but the length of the minor axis decreased. Thereafter, heat setting was performed at 180° C. for 2 minutes using an IR heater to prepare an optical film including an optical layer in which the pansan-type polymer dispersion as shown in FIG. 10 was dispersed. The refractive index of the polymer dispersion component in the prepared optical film was (n x : 1.88, n y : 1.58, n z : 1.58) and the refractive index of the matrix component was 1.58, the aspect ratio of the polymer was approximately 1/180000, and the number of layers was 400. layer, the thickness was 84 nm, and the major axis length was 15.5 mm. At this time, the thickness of the optical layer prepared was 100 μm, and the total thickness of the optical film including the skin layer on both sides was 125 μm.

<비교예2><Comparative Example 2>

실시예1과 동일하게 실시하여 수행하되, 폴리머 분산체에 카본블랙을 포함시키지 않은 광학필름을 제조하였다.An optical film was prepared in the same manner as in Example 1, except that carbon black was not included in the polymer dispersion.

<실험예1><Experimental Example 1>

실시예 및 비교예에서 제조된 광학필름에 대해서 하기의 물성을 측정하여 그 결과를 하기 표 1과 표 2에 나타내었다.The following physical properties were measured for the optical films prepared in Examples and Comparative Examples, and the results are shown in Tables 1 and 2 below.

1. 헤이즈1. Haze

헤이즈 및 투과도 측정기(니폰 덴쇼쿠 고교 코포레이티드(Nippon Denshoku Kogyo Co.) 제품) 분석설비를 이용하여 헤이즈를 측정하였다.Haze and permeability meter (manufactured by Nippon Denshoku Kogyo Co.) were used to measure haze using an analysis facility.

2. 폴리머 분산체의 두께2. Thickness of polymer dispersion

실시예 및 비교예의 광학필름의 신장방향을 x축으로 하고, 두께방향을 z축으로 할 때, y-z 평면이 절단된 면이 되도록 수직하게 절단한 후 절단된 면에 대해서 SEM 사진을 촬영하였다. 촬영된 SEM 사진에서 5㎛×5㎛ 영역 내 위치하는 폴리머 분산체의 두께를 측정하였다.When the stretching direction of the optical films of Examples and Comparative Examples was the x-axis and the thickness direction was the z-axis, the y-z plane was cut vertically to become the cut surface, and then SEM pictures were taken of the cut surface. The thickness of the polymer dispersion located in the area of 5 μm × 5 μm was measured in the SEM picture taken.

<실험예2><Experimental Example 2>

실시예 및 비교예에서 제조된 광학필름에 대해서 상면에 저굴절 코팅 가공을 진행하였다. 준비된 광학필름을 흡수편광자 상면에 합지하고, 흡수편광자 하부면에는 TAC(트리아세테이트 셀룰로오스)가 구비된 편광판을 제조하였고, 제조된 편광판을 시중에 판매되는 LCD의 액정패널 상부 편광판과 교체한 후 이를 대상으로 정면 및 측면 방향 휘도와 명암비를 측정하여 하기 표 1에 나타내었다.A low refractive index coating process was performed on the upper surface of the optical films prepared in Examples and Comparative Examples. The prepared optical film was laminated on the upper surface of the absorption polarizer, and a polarizing plate equipped with TAC (triacetate cellulose) was prepared on the lower surface of the absorption polarizer. The front and side direction luminance and contrast ratio were measured and shown in Table 1 below.

이때, 휘도는 실시예 및 비교예에 따른 광학필름이 구비된 편광판으로 상부 편광판 교체 전 없이 해당 LCD에서 측정된 휘도를 100%로 기준하여 실시예 및 비교예에 따른 편광판으로 교체한 후 측정된 휘도를 상대적인 백분율로 표시하였다. At this time, the luminance is the luminance measured after replacing the polarizing plate according to the examples and comparative examples with the polarizing plate equipped with the optical film according to the examples and comparative examples based on the luminance measured in the LCD without replacing the upper polarizing plate as 100%. was expressed as a relative percentage.

실시예1Example 1 실시예2Example 2 실시예3Example 3 실시예4Example 4 실시예5Example 5 실시예6Example 6 실시예7Example 7 실시예8Example 8 비교예1Comparative Example 1 비교예2Comparative Example 2 두께
(㎛)thickness
(μm) 전체두께overall thickness 125125 125125 125125 125125 125125 125125 125125 125125 125125 125125 광학층optical layer 6060 4343 3535 8080 100100 120120 3535 3535 100100 6060 스킨층skin layer 6565 8282 9090 4545 2525 55 9090 9090 2525 6565 폴리머분산체polymer dispersion 분산타입Distributed type 랜덤random 랜덤random 랜덤random 랜덤random 랜덤random 랜덤random 랜덤random 랜덤random 비랜덤non-random 랜덤random 광흡수제 함유여부Containing light absorber ○○ ○○ ○○ ○○ ○○ ○○ ○○ ○○ ×× ×× 광흡수제 함량(wt%)Light absorber content (wt%) 33 33 33 33 33 33 0.30.3 6565 -- -- 평균너비(㎚)Average width (nm) 195195 180180 167167 180180 180180 180180 167167 167167 1550015500 195195 두께 별 폴리머분산체 비율(%)Polymer dispersion ratio by thickness (%) 250nm이하250 nm or less 9595 100100 100100 100100 100100 100100 100100 100100 100100 9595 120nm이하120 nm or less 5050 6363 7070 6363 6363 6363 7070 7070 100
(84㎚)100
(84nm) 5050 50nm미만less than 50 nm 44 1313 88 1313 1313 1313 88 88 00 44 50nm 이상 ~ 90nm 이하50nm or more ~ 90nm or less 4040 4545 5252 4545 4545 4545 5252 5252 00 4040 물성Properties 상대휘도
(%)relative luminance
(%) WhiteWhite 8383 8787 9090 8888 8686 7777 9494 6262 8282 8989 BlackBlack 113113 105105 102102 105105 107107 118118 132132 8282 125125 116116 CR특성
(%)CR characteristics
(%) 정면face 8585 8989 9494 9393 9191 8989 8585 7373 7979 8181 측면
(60°)side
(60°) 135135 139139 142142 140140 138138 130130 121121 127127 118118 122122 헤이즈(%)Haze (%) 2727 2525 2121 2121 2323 3030 1717 5656 2828 2525

표 1을 통해 확인할 수 있듯이,As can be seen from Table 1,

비교예1 및 비교예2에 따른 광학필름에 대비해 실시예들의 경우 정면 및 측면 명암비 개선 효과가 매우 개선된 것을 알 수 있다. 다만, 실시예 중에서도 광흡수제가 과소하게 함유된 실시예7은 명암비 개선 효과가 미미했고, 실시예8의 경우 광흡수제가 과도하게 함유되어 휘도가 매우 저하된 것을 알 수 있다.Compared to the optical films according to Comparative Example 1 and Comparative Example 2, in the case of Examples, it can be seen that front and side contrast ratio improvement effects are greatly improved. However, it can be seen that among the Examples, Example 7, in which the light absorber was excessively contained, had little effect of improving the contrast ratio, and in Example 8, the light absorber was excessively contained, resulting in a very low luminance.

Claims (12)

매트릭스 및
상기 매트릭스 내 상호 수직하는 x축, y축 및 z축에서 x축 방향이 각각의 길이방향이 되되 y축 및 z축 방향으로는 랜덤하게 상기 매트릭스 내 배열된 다수 개의 폴리머 분산체 구비하는 광학층;을 구비하고,
상기 다수 개의 폴리머 분산체는 광흡수제를 함유하며, 상기 광학층은 두께가 100㎛ 이하이고, 상기 광학층의 y-z 절단면에서 상기 폴리머 분산체의 너비는 300㎚ 이하이며, 상기 절단면에서 전체 폴리머 분산체 중 z축 방향인 폴리머 분산체의 두께가 250㎚ 이하인 폴리머 분산체의 개수가 95% 이상이면서 폴리머 분산체의 두께가 120nm 이하인 폴리머 분산체의 개수가 60% 이상인 명암비 및 시야각 개선용 광학필름. matrix and
an optical layer including a plurality of polymer dispersions randomly arranged in the matrix in the matrix in which the x-axis directions are longitudinal directions, but the y-axis and z-axis directions are mutually perpendicular to each other in the matrix; to provide,
The plurality of polymer dispersions contain a light absorber, the optical layer has a thickness of 100 μm or less, the width of the polymer dispersion on the yz cut surface of the optical layer is 300 nm or less, and the entire polymer dispersion on the cut surface An optical film for improving contrast ratio and viewing angle, wherein the number of polymer dispersions having a thickness of 250 nm or less in the z-axis direction is 95% or more and the number of polymer dispersions having a thickness of 120 nm or less is 60% or more. 제1항에 있어서,
상기 매트릭스와 상기 폴리머 분산체는 y축 및 z축 방향에 대한 굴절율의 차이가 0.05 이하이고, x축 방향에 대한 굴절율의 차이가 0.1 이상인 명암비 및 시야각 개선용 광학필름.According to claim 1,
The optical film for improving contrast ratio and viewing angle, wherein the matrix and the polymer dispersion have a difference in refractive index of 0.05 or less in the y-axis and z-axis directions, and a difference in refractive index in the x-axis direction of 0.1 or more. 제1항에 있어서,
상기 폴리머 분산체는 매트릭스 및 폴리머 분산체 전체 중량의 35 ~ 65 중량%로 포함되는 명암비 및 시야각 개선용 광학필름.According to claim 1,
The polymer dispersion is an optical film for improving the contrast ratio and viewing angle contained in 35 to 65% by weight of the total weight of the matrix and the polymer dispersion. 제1항에 있어서,
상기 광흡수제는 폴리머 분산체 전체 중량에 대해서 2 ~ 60 중량%로 함유되는 명암비 및 시야각 개선용 광학필름.According to claim 1,
The optical film for improving the contrast ratio and viewing angle, wherein the light absorber is contained in an amount of 2 to 60% by weight based on the total weight of the polymer dispersion. 삭제delete 삭제delete 제1항에 있어서,
y-z 평면인 광학층 절단면에서 전체 폴리머 분산체 중 z축 방향인 폴리머 분산체의 두께가 50nm 미만인 폴리머 분산체의 개수가 10% 이하인 것을 특징으로 하는 명암비 및 시야각 개선용 광학필름.According to claim 1,
An optical film for improving contrast ratio and viewing angle, characterized in that the number of polymer dispersions having a thickness of less than 50 nm in the z-axis direction among all polymer dispersions in the yz-plane optical layer cut surface is 10% or less. 제1항에 있어서,
y-z 평면인 광학층 절단면에서 폴리머 분산체의 너비는 200㎚ 이하인 명암비 및 시야각 개선용 광학필름.According to claim 1,
An optical film for improving contrast ratio and viewing angle, wherein the width of the polymer dispersion is 200 nm or less on the yz-plane optical layer cut surface. 제1항에 있어서,
상기 광학필름은 헤이즈가 20% 이하인 것을 특징으로 하는 명암비 및 시야각 개선용 광학필름.According to claim 1,
The optical film is an optical film for improving the contrast ratio and viewing angle, characterized in that the haze is 20% or less. 제1항에 있어서,
상기 광학필름은 상기 광학층의 적어도 일면에 일체로 형성된 스킨층을 더 포함하는 명암비 및 시야각 개선용 광학필름.According to claim 1,
The optical film for improving contrast ratio and viewing angle further comprises a skin layer integrally formed on at least one surface of the optical layer. 시인 측인 액정패널 상부에 배치되는 편광판으로서, 상기 편광판은
흡수편광자; 및
상기 흡수편광자의 광 출사면 상에 배치되는 제1항 내지 제4항 및 제7항 내지 제10항 중 어느 한 항에 따른 광학필름;을 포함하는 편광판.A polarizing plate disposed above the liquid crystal panel on the viewing side, the polarizing plate comprising:
absorption polarizer; and
A polarizing plate comprising an optical film according to any one of claims 1 to 4 and 7 to 10 disposed on the light exit surface of the absorption polarizer. 액정 셀; 및
적어도 상기 액정 셀의 광 출사면 상 배치되는 제11항에 따른 편광판;을 포함하는 액정표시장치.liquid crystal cell; and
A liquid crystal display device comprising: a polarizing plate according to claim 11 disposed on at least the light exit surface of the liquid crystal cell.
KR1020200183480A 2020-12-24 2020-12-24 Optical film for enhancing contrast ratio and viewing angle, polarizing plate comprising the same, and liquid crystal display apparatus comprising the same KR102533738B1 (en)