KR102472872B1 - Polyester film for display protection - Google Patents

Polyester film for display protection Download PDF

Info

Publication number
KR102472872B1
KR102472872B1 KR1020200136194A KR20200136194A KR102472872B1 KR 102472872 B1 KR102472872 B1 KR 102472872B1 KR 1020200136194 A KR1020200136194 A KR 1020200136194A KR 20200136194 A KR20200136194 A KR 20200136194A KR 102472872 B1 KR102472872 B1 KR 102472872B1
Authority
KR
South Korea
Prior art keywords
polyester film
primer layer
display
film
display protection
Prior art date
Application number
KR1020200136194A
Other languages
Korean (ko)
Other versions
KR20220052425A (en
Inventor
고명준
오동호
강창원
Original Assignee
도레이첨단소재 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 도레이첨단소재 주식회사 filed Critical 도레이첨단소재 주식회사
Priority to KR1020200136194A priority Critical patent/KR102472872B1/en
Priority to CN202011484773.3A priority patent/CN114387876B/en
Publication of KR20220052425A publication Critical patent/KR20220052425A/en
Application granted granted Critical
Publication of KR102472872B1 publication Critical patent/KR102472872B1/en

Abstract

본 발명에 따른 디스플레이 보호용 폴리에스테르 필름은 2축 연신된 기재필름, 기재필름의 일면에 형성된 제1 프라이머층 및 기재필름의 다른 일면에 형성된 제2 프라이머층을 포함하고, 제1 프라이머층 및 제2 프라이머층의 굴절율 차이는 0.1 이상인 구성을 포함하며, 높은 전투과율과 높은 지문 인식율을 가지는 디스플레이 보호용 폴리에스테르 필름을 제공한다.A polyester film for display protection according to the present invention includes a biaxially stretched base film, a first primer layer formed on one side of the base film, and a second primer layer formed on the other side of the base film, and the first primer layer and the second primer layer are formed on the other side of the base film. The primer layer has a refractive index difference of 0.1 or more, and provides a polyester film for protecting a display having a high transmission rate and a high fingerprint recognition rate.

Description

디스플레이 보호용 폴리에스테르 필름{POLYESTER FILM FOR DISPLAY PROTECTION}Polyester film for display protection {POLYESTER FILM FOR DISPLAY PROTECTION}

본 발명은 디스플레이 보호용 폴리에스테르 필름에 관한 것으로, 부착력이 우수하고, 광학적, 기계적 성질이 우수한 디스플레이 보호용 폴리에스테르 필름에 관한 것이다.The present invention relates to a polyester film for display protection, and relates to a polyester film for display protection, which has excellent adhesion and excellent optical and mechanical properties.

최근 액정표시장치, 유기 발광표시장치 및 전자종이에 대한 관심이 급증하면서 이들 표시장치의 최외곽에 보호필름을 구성하여 내구성을 향상시키는 움직임이 활발히 진행되고 있다.Recently, as interest in liquid crystal display devices, organic light emitting display devices, and electronic paper has rapidly increased, a movement to improve durability by constructing a protective film on the outermost periphery of these display devices is actively progressing.

일반적으로 폴리에스테르 필름은 치수 안정성, 두께 균일성 및 광학적 투명성이 우수하여 디스플레이 기기뿐만 아니라 여러 산업용 재료로서 그 이용 범위가 매우 넓다. 특히, 이러한 폴리에스테르 필름에 대해 최근 높은 광학적 특성이 요구되는 디스플레이 보호용 필름으로의 검토도 활발히 진행되고 있다. In general, polyester films have excellent dimensional stability, thickness uniformity, and optical transparency, and thus are widely used as various industrial materials as well as display devices. In particular, with respect to such a polyester film, studies as a film for display protection that requires high optical properties have recently been actively conducted.

이와 같이 폴리에스테르 필름을 광학용 보호필름으로 사용하는 경우, 대부분의 휴대용 디스플레이 디바이스에서 채택하고 있는 광학식 지문인식 기능을 부여하기 위해 높은 전투과율 및 낮은 광손실율이 요구된다. 폴리에스테르 필름에 대한 광손실율의 경우 배향각 혹은 광축으로 대표되는 물성과 연관을 가지는데, 기본적으로 폴리에스테르 필름은 연신 과정에서 결정 및 보잉(Bowing)에 의해 배향각을 가지게 되며, 2축 연신의 경우 광축이 2개가 생김으로써, 편광자로부터 올라오는 편광을 타원이나 원편광 등으로 바꾸게 되고, 사람의 눈에 색감의 변화나 무지개 빛 얼룩이 보이는 경우가 많다.In this way, when the polyester film is used as an optical protective film, a high transmittance rate and a low optical loss rate are required to impart an optical fingerprint recognition function adopted in most portable display devices. In the case of optical loss rate for polyester film, it is related to physical properties represented by orientation angle or optical axis. Basically, polyester film has orientation angle by crystal and bowing during stretching process, and biaxial stretching In this case, since two optical axes are formed, the polarized light coming up from the polarizer is changed into elliptical or circular polarized light, and a change in color or iridescence is often seen by the human eye.

이러한 문제를 해소하기 위해, 폴리에스테르 필름을 이용한 발명이 활발히 진행되어 왔다. 이와 같은 발명의 하나로 일본 공개특허 제2011-532061호는 복굴절성에 의한 광학 이방성을 줄여 무지개 얼룩이 없는 시인성을 확보하고 있다. 그러나 이러한 발명의 경우, 표면가공을 해야 하는 디스플레이 보호필름에 대해서는 지문 인식율 저하 등이 문제로 대두되고 있으며, 이를 위한 주쇄의 배향각을 낮추려는 시도는 없었기 때문에, 실제 유효폭을 얻어내는데 있어서 생산성 저하 등의 문제가 발생하여, 폴리에스테르 필름을 디스플레이 보호용을 사용하는데 있어서 장애가 되고 있었다.In order to solve these problems, inventions using polyester films have been actively pursued. As one of such inventions, Japanese Laid-Open Patent Publication No. 2011-532061 secures visibility without rainbow spots by reducing optical anisotropy due to birefringence. However, in the case of this invention, a decrease in fingerprint recognition rate is emerging as a problem for a display protective film that requires surface processing, and since there has been no attempt to lower the orientation angle of the main chain for this purpose, in obtaining an actual effective width, productivity decrease, etc. problem occurred, and it was becoming an obstacle in using the polyester film for display protection.

또한, 양면 이종코팅으로 전투과율을 높여 폴리에스테르 필름의 광학특성을 개선하는 연구 또한 진행되어 왔으나 일반적인 양면 이종코팅은 배향각 조정 혹은 광손실율 억제 및 올리고머 석출을 개선할 수 없는 문제를 가진다.In addition, research on improving the optical properties of polyester films by increasing the combat efficiency with double-sided heterogeneous coating has also been conducted, but general double-sided heterogeneous coating has problems in that it cannot adjust the orientation angle or suppress light loss and improve oligomer precipitation.

따라서 폴리에스테르 필름 자체의 광학적 특성과 더불어, 프라이머층 및 AG나 하드코팅등 각 층의 계면에서의 응력을 최소화할 수 있는 적절한 구조의 설계와 이물 발생 억제를 위한 설계가 반영된 디스플레이 보호용 폴리에스테르 필름이 요구되고 있는 실정이다.Therefore, in addition to the optical properties of the polyester film itself, a polyester film for display protection that reflects the design of an appropriate structure that can minimize the stress at the interface of each layer such as the primer layer, AG, or hard coating, and the design for suppression of foreign matter. It is currently being demanded.

일본 공개특허 제2011-532061호Japanese Laid-open Patent No. 2011-532061

본 발명은 상기와 같은 문제점을 해결하기 위해 안출한 것으로서, 본 발명의 목적은 필름의 주쇄 결정 각도를 조절하고 주 배향각을 최대한 낮추어 비스듬히 관찰 시에 발생할 수 있는 무지개 얼룩을 최소화할 수 있는 디스플레이 보호용 폴리에스테르 필름을 제공하는 것이다. The present invention has been made to solve the above problems, and an object of the present invention is to adjust the main chain crystal angle of the film and lower the main orientation angle as much as possible to minimize rainbow stains that may occur when observing at an angle. For display protection It is to provide a polyester film.

또한, 본 발명의 목적은 높은 전투과율을 가지며, 광학식 지문인식 기능을 구비한 디스플레이 장치의 보호 필름으로 사용될 때 지문인식율을 떨어 뜨릴 수 있는 광손실을 억제하고, 이물 발생을 최소화할 수 있는 디스플레이 보호용 폴리에스테르 필름을 제공하는 것이다.In addition, an object of the present invention is to protect a display that has a high combat rate and can suppress light loss that can reduce the fingerprint recognition rate when used as a protective film for a display device having an optical fingerprint recognition function and minimize foreign matter generation It is to provide a polyester film.

본 발명의 상기 및 다른 목적과 이점은 바람직한 실시예를 설명한 하기의 설명으로부터 분명해질 것이다.The above and other objects and advantages of the present invention will become apparent from the following description of preferred embodiments.

상기 목적은, 2축 연신된 기재필름, 기재필름의 일면에 형성된 제1 프라이머층 및 기재필름의 다른 일면에 형성된 제2 프라이머층을 포함하고, 제1 프라이머층 및 제2 프라이머층의 굴절율 차이는 0.1 이상인 디스플레이 보호용 폴리에스테르 필름에 의해 달성된다.The above object includes a biaxially stretched base film, a first primer layer formed on one side of the base film, and a second primer layer formed on the other side of the base film, and the difference in refractive index between the first primer layer and the second primer layer is It is achieved by a polyester film for display protection that is 0.1 or more.

여기서, 디스플레이 보호용 폴리에스테르 필름은 150℃에서 1시간 열처리 후 헤이즈 변화가 1% 이하일 수 있다.Here, the polyester film for display protection may have a haze change of 1% or less after heat treatment at 150° C. for 1 hour.

바람직하게는, 디스플레이 보호용 폴리에스테르 필름은 하기 식 1에 따른 광손실율이 11% 이하일 수 있다.Preferably, the polyester film for display protection may have an optical loss rate of 11% or less according to Formula 1 below.

(식 1)(Equation 1)

광손실율=(편광판 평행니콜 최대 광량-편광판 2매 사이에 필름 삽입후의 최대 광량)/(편광판 평행니콜 최대 광량).Light loss rate = (maximum light amount of polarizing plate parallel nicol - maximum light amount after inserting a film between two polarizing plates) / (maximum light amount of polarizing plate parallel nicol).

바람직하게는, 디스플레이 보호용 폴리에스테르 필름은 배향각과 광축의 차이가 9도 이하일 수 있다.Preferably, the polyester film for display protection may have a difference of 9 degrees or less between an orientation angle and an optical axis.

바람직하게는, 디스플레이 보호용 폴리에스테르 필름은 센터부와 엣지부의 배향각 차이가 20도 이하일 수 있다.Preferably, the polyester film for display protection may have a difference in orientation angle between the center portion and the edge portion of 20 degrees or less.

바람직하게는, 디스플레이 보호용 폴리에스테르 필름은 주쇄의 배향각이 20도 이하일 수 있다.Preferably, the polyester film for display protection may have a main chain orientation angle of 20 degrees or less.

바람직하게는, 제1 프라이머층의 굴절율은 1.58 내지 1.62이고, 제2 프라이머층의 굴절율은 1.45 내지 1.49일 수 있다.Preferably, the refractive index of the first primer layer may be 1.58 to 1.62, and the refractive index of the second primer layer may be 1.45 to 1.49.

바람직하게는, 디스플레이 보호용 폴리에스테르 필름은 MD방향: TD방향 연신비가 1:1.45 내지 1:1.75일 수 있다.Preferably, the polyester film for display protection may have a MD direction: TD direction stretch ratio of 1:1.45 to 1:1.75.

바람직하게는, 디스플레이 보호용 폴리에스테르 필름은 전투과율이 93% 이상일 수 있다.Preferably, the polyester film for protecting the display may have a combat transmittance of 93% or more.

바람직하게는, 제1 프라이머층은 폴리에스테르 공중합체 수지, 폴리우레탄계 수지, 옥사졸린계 경화제, 에폭시계 경화제, 음이온성 계면활성제 및 무기입자를 포함할 수 있다.Preferably, the first primer layer may include a polyester copolymer resin, a polyurethane-based resin, an oxazoline-based curing agent, an epoxy-based curing agent, an anionic surfactant, and inorganic particles.

바람직하게는, 제2 프라이머층은 카르복실기를 관능기로 가지는 폴리아크릴 수지, 멜라민계 경화제, 음이온성 계면활성제 및 무기입자를 포함할 수 있다.Preferably, the second primer layer may include a polyacrylic resin having a carboxyl group as a functional group, a melamine-based curing agent, an anionic surfactant, and inorganic particles.

바람직하게는, 제2 프라이머층은 올리고머 블록 기능을 가지는 것일 수 있다.Preferably, the second primer layer may have an oligomer block function.

바람직하게는, 기재필름은 폴리에틸렌테레프탈레이트, 폴리에틸렌나프탈레이트, 폴리에틸렌이소프탈레이트 및 폴리카보네이트 중에서 선택된 적어도 하나 이상의 물질을 포함할 수 있다.Preferably, the base film may include at least one material selected from polyethylene terephthalate, polyethylene naphthalate, polyethylene isophthalate, and polycarbonate.

바람직하게는, 기재필름의 두께는 25 내지 200㎛일 수 있다.Preferably, the thickness of the base film may be 25 to 200 μm.

또한, 상기 목적은, 폴리에스테르 수지를 용융 압출하여 미연신 시트를 형성하는 제1 단계, 미연신 시트의 일면에 제1 프라이머층을 형성하는 도포액을 도포하고 건조하는 제2 단계, 미연신 시트의 다른 일면에 제2 프라이머층을 형성하는 도포액을 도포하고 건조하는 제3 단계, 제1 프라이머층과 제2 프라이머층이 형성된 미연신 시트를 길이 방향(MD)으로 1축 연신하는 제4 단계, 1축 연신된 시트를 폭 방향(TD)으로 2축 연신하는 제5 단계 및 2축 연신된 시트를 열고정하여 디스플레이 보호용 폴리에스테르 필름을 형성하는 제6 단계를 포함할 수 있다.In addition, the above object is a first step of forming an unstretched sheet by melting and extruding a polyester resin, a second step of applying and drying a coating solution for forming a first primer layer on one surface of the unstretched sheet, and an unstretched sheet. A third step of applying and drying a coating liquid for forming a second primer layer on the other side of the , A fourth step of uniaxially stretching the unstretched sheet on which the first primer layer and the second primer layer are formed in the longitudinal direction (MD). , a fifth step of biaxially stretching the uniaxially stretched sheet in the width direction (TD) and a sixth step of heat-setting the biaxially stretched sheet to form a polyester film for display protection.

바람직하게는, 제1 프라이머층 및 제2 프라이머층의 두께는 10 내지 200nm일 수 있다.Preferably, the thickness of the first primer layer and the second primer layer may be 10 to 200 nm.

바람직하게는, 제6 단계의 열고정 온도는 180 내지 220℃일 수 있다.Preferably, the heat setting temperature of the sixth step may be 180 to 220 °C.

본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 높은 전투과율을 통해 광손실율을 억제할 수 있다. 또한, 디스플레이 장치인 LCD와 OLED 모두 편광판을 사용하고 있기 때문에 높은 지문인식률을 가질 수 있도록 하기 위하여 디스플레이 보호용 폴리에스테르 필름의 광축과 편광판의 광축을 일치시켜 광손실율을 최소화할 수 있으며, 이를 통해 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 광축의 변화가 적어 높은 지문인식율을 가질 수 있다.The polyester film for protecting a display according to an embodiment of the present invention can suppress light loss through a high transmittance. In addition, since both LCD and OLED, which are display devices, use polarizers, the optical axis of the polyester film for display protection and the optical axis of the polarizer can be aligned to minimize the optical loss rate in order to have a high fingerprint recognition rate. Through this, the present invention The polyester film for display protection according to an embodiment of may have a high fingerprint recognition rate with little change in optical axis.

또한, 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 필름 내의 이물을 억제하고 올리고머 발생을 최소화하여 높은 지문인식율을 가질 수 있다.In addition, the polyester film for display protection according to an embodiment of the present invention can have a high fingerprint recognition rate by suppressing foreign matter in the film and minimizing the generation of oligomers.

또한, 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 열 공정상의 이물 발생을 최소화하여 타발 시의 수율을 높일 수 있다.In addition, the polyester film for protecting a display according to an embodiment of the present invention can minimize the generation of foreign substances in a thermal process to increase the yield at the time of punching.

다만, 본 발명의 효과들은 이상에서 언급한 효과로 제한되지 않으며, 언급되지 않은 또 다른 효과들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.However, the effects of the present invention are not limited to the effects mentioned above, and other effects not mentioned will be clearly understood by those skilled in the art from the description below.

도 1은 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름의 단면도이다.1 is a cross-sectional view of a polyester film for protecting a display according to an embodiment of the present invention.

첨부한 도면을 참고로 하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.With reference to the accompanying drawings, embodiments of the present invention will be described in detail so that those skilled in the art can easily carry out the present invention. However, the present invention may be embodied in many different forms and is not limited to the embodiments described herein.

도면에서 여러 층 및 영역을 명확하게 표현하기 위하여 두께를 확대하여 나타내었다. 명세서 전체를 통하여 유사한 부분에 대해서는 동일한 도면 부호를 붙였다. 층, 막, 영역, 판 등의 부분이 다른 부분 "위에" 있다고 할 때, 이는 다른 부분 "바로 위에" 있는 경우뿐 아니라 그 중간에 또 다른 부분이 있는 경우도 포함한다. 반대로 어떤 부분이 다른 부분 "바로 위에" 있다고 할 때에는 중간에 다른 부분이 없는 것을 뜻한다.In the drawings, the thickness is shown enlarged to clearly express the various layers and regions. Like reference numerals have been assigned to like parts throughout the specification. When a part such as a layer, film, region, plate, etc. is said to be “on” another part, this includes not only the case where it is “directly on” the other part, but also the case where there is another part in between. Conversely, when a part is said to be "directly on" another part, it means that there is no other part in between.

달리 정의되지 않는 한, 본 명세서에서 사용되는 모든 기술적 및 과학적 용어는 본 발명이 속하는 기술 분야의 숙련자에 의해 통상적으로 이해되는 바와 동일한 의미를 갖는다. 상충되는 경우, 정의를 포함하는 본 명세서가 우선할 것이다. 또한 본 명세서에서 설명되는 것과 유사하거나 동등한 방법 및 재료가 본 발명의 실시 또는 시험에 사용될 수 있지만, 적합한 방법 및 재료가 본 명세서에 기재된다.Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. In case of conflict, the present specification, including definitions, will control. Also, although methods and materials similar or equivalent to those described herein may be used in the practice or testing of the present invention, suitable methods and materials are described herein.

도 1은 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름의 단면도이다.1 is a cross-sectional view of a polyester film for protecting a display according to an embodiment of the present invention.

도 1을 참조하면, 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 기재필름(2), 기재필름(2)의 일면에 형성된 제1 프라이머층(1) 및 기재필름(2)의 다른 일면(타면)에 형성된 제2 프라이머층(3)을 포함한다. 이때, 제1 프라이머층(1) 및 제2 프라이머층(3)의 위치는 변경되어도 무방하다.Referring to FIG. 1 , a polyester film for protecting a display according to an embodiment of the present invention includes a base film 2, a first primer layer 1 formed on one surface of the base film 2, and another layer of the base film 2. and a second primer layer 3 formed on one surface (the other surface). At this time, the positions of the first primer layer 1 and the second primer layer 3 may be changed.

일 실시예에서, 기재필름(2)은 폴리에틸렌테레프탈레이트, 폴리에틸렌나프탈레이트, 폴리에틸렌이소프탈레이트 및 폴리카보네이트 중에서 선택된 적어도 하나의 폴리에스테르를 포함하는 것이 바람직하고, 2축 연신된 필름일 수 있다.In one embodiment, the base film 2 preferably includes at least one polyester selected from polyethylene terephthalate, polyethylene naphthalate, polyethylene isophthalate, and polycarbonate, and may be a biaxially stretched film.

일 실시예에서, 기재필름(2)의 두께는 25 내지 250㎛인 것이 바람직하다. 기재필름(2)의 두께가 25㎛ 미만인 경우 표면 가공 및 편광판 합지 과정에서 주름이 혼입되기 쉬워 수율이 떨어질 수 있으며, 기재필름(1)의 두께가 250㎛를 초과하는 경우 위상차 제어가 어렵고 디스플레이 전체 두께가 두꺼워지는 문제가 있다.In one embodiment, the thickness of the base film 2 is preferably 25 to 250 μm. When the thickness of the base film 2 is less than 25 μm, wrinkles are easily incorporated in the process of surface processing and laminating the polarizer, and the yield may decrease. When the thickness of the base film 1 exceeds 250 μm, it is difficult to control the retardation and the entire display There is a problem with increasing the thickness.

또한, 기재필름(2)은 필요 목적에 따라 자외선을 흡수할 수 있는 자외선 흡수제나 자외선 흡수제의 갈변을 억제하기 위한 산화방지제와 같은 첨가물질을 더 포함할 수 있다.In addition, the base film 2 may further include an additive material such as an ultraviolet absorber capable of absorbing ultraviolet rays or an antioxidant for suppressing browning of the ultraviolet absorber according to a necessary purpose.

일 실시예에서, 기재필름(2)의 일면에 형성된 제1 프라이머층(1)과 다른 일면에 형성된 제2 프라이머층(3)의 굴절율 차이는 0.1 이상인 것이 바람직하다. 제1 프라이머층(1)과 제2 프라이머층(3)의 굴절율 차이가 0.1 미만인 경우 전투과율이 낮아져 필름의 광손실이 많아진다.In one embodiment, it is preferable that the difference in refractive index between the first primer layer 1 formed on one surface of the base film 2 and the second primer layer 3 formed on the other surface is 0.1 or more. When the difference in refractive index between the first primer layer 1 and the second primer layer 3 is less than 0.1, the transmittance is lowered and the light loss of the film increases.

일 실시예에서, 제1 프라이머층(1)은 하드코팅을 구성하는 경우가 많기 때문에 표면에 하드코팅을 형성할 때 간섭에 의한 무지개 얼룩을 제어하기 위해 이의 굴절율은 1.58 내지 1.62인 것이 바람직하고, 1.59 내지 1.60인 것이 더욱 바람직하다.In one embodiment, since the first primer layer 1 often constitutes a hard coating, the refractive index thereof is preferably 1.58 to 1.62 to control rainbow stains caused by interference when forming a hard coating on the surface, It is more preferably 1.59 to 1.60.

일 실시예에서, 제1 프라이머층(1)은 바인더 수지로 폴리에스테르 공중합체 수지 및 폴리우레탄계 수지 중에서 선택된 적어도 1종 이상의 주재를 포함한다. 바람직하게는 2종의 주재를 포함할 수 있다.In one embodiment, the first primer layer 1 includes at least one main material selected from a polyester copolymer resin and a polyurethane-based resin as a binder resin. Preferably, two types of main materials may be included.

또한, 제1 프라이머층(1)은 경화제 수지로 옥사졸린계, 카보디이미드계 및 멜라민계 중에서 선택된 적어도 1종 이상의 물질을 포함한다. 특히, 옥사졸린계 경화제는 내습성을 통해 필름에 투습되는 수분을 억제하며, 멜라민계 경화제는 주재와도 반응을 하지만 멜라민 사이의 자체적인 경화반응을 통하여 도막 강도를 향상시킴으로써 양면 코팅 시 발생할 수 잇는 블로킹 현상을 방지하는 역할을 수행한다. 바람직하게는 옥사졸린계 경화제와 멜라민계 경화제로 이루어진 경화제 혼합물을 포함할 수 있다.In addition, the first primer layer 1 includes at least one material selected from oxazoline-based, carbodiimide-based, and melamine-based materials as a curing agent resin. In particular, the oxazoline-based curing agent suppresses moisture permeable to the film through its moisture resistance, and the melamine-based curing agent reacts with the main material, but improves the strength of the coating film through its own curing reaction between melamine, which can occur during double-sided coating. It plays a role in preventing the blocking phenomenon. Preferably, a curing agent mixture composed of an oxazoline-based curing agent and a melamine-based curing agent may be included.

또한, 제1 프라이머층(1)은 첨가제로서 음이온성 계면활성제를 포함하는 것이 바람직하다. Also, the first primer layer 1 preferably contains an anionic surfactant as an additive.

또한, 제1 프라이머층(1)은 코팅성 및 기능성 향상을 위하여 코팅액에 추가적인 첨가제를 더 포함할 수 있다. 이와 같이 제1 프라이머층(1)에 사용되는 첨가제로는 유기입자, 무기입자, 소포제 등을 사용할 수 있다. In addition, the first primer layer 1 may further include additional additives in the coating solution to improve coating properties and functionality. As such, additives used in the first primer layer 1 may include organic particles, inorganic particles, and antifoaming agents.

본 발명에서 제1 프라이머층(1)은 무기 입자를 통해 주행성을 확보할 수 있으며, 무기 입자의 평균입경은 10 내지 300nm인 것이 바람직하다. 무기 입자의 평균입경이 300nm를 초과하게 되면 헤이즈가 높아지는 문제가 발생하고, 10nm 미만인 경우 주행성을 확보할 수 없다. In the present invention, the first primer layer 1 can secure runability through inorganic particles, and the inorganic particles preferably have an average particle diameter of 10 to 300 nm. When the average particle diameter of the inorganic particles exceeds 300 nm, a problem in that the haze increases, and when the average particle diameter is less than 10 nm, it is not possible to secure runability.

또한, 무기입자는 실리카 입자 및 실리카-유기물 합성체 중 선택되는 적어도 하나 이상인 것이 바람직하고, 제1 프라이머층(1)의 굴절율을 고려하여 무기 입자의 굴절율은 1.5 이상인 것이 바람직하다.In addition, the inorganic particles are preferably at least one selected from silica particles and silica-organic composites, and considering the refractive index of the first primer layer 1, the inorganic particles preferably have a refractive index of 1.5 or more.

일 실시예에서, 제1 프라이머층(1)은 폴리에스테르 공중합체 수지와 폴리우레탄계 수지의 혼합물로 이루어진 바인더 수지, 옥사졸린계 경화제와 멜라민계 경화제의 혼합물로 이루어진 경화제, 음이온성 계면활성제 및 무기입자를 포함하는 도포액을 기재필름(2) 상에 도포하여 형성하는 것이 바람직하다. In one embodiment, the first primer layer 1 is a binder resin made of a mixture of polyester copolymer resin and polyurethane-based resin, a curing agent made of a mixture of oxazoline-based curing agent and melamine-based curing agent, anionic surfactant and inorganic particles It is preferable to form by applying a coating solution containing the on the base film (2).

제1 프라이머층(1)을 구성하는 상기 조성은 물과 함께 수분산액 형태의 도포액으로 제조되어 기재필름(2)의 일면에 도포된다. 일 실시예에서, 제1 프라이머층(1)의 도포 두께는 10 내지 200nm인 것이 바람직하다. 도포 두께가 10nm 미만인 경우 표면 가공 후 반사 레인보우가 관찰될 수 있고 부착력이 저하되는 문제가 있으며, 200nm를 초과하는 경우 반사 레인보우 및 블로킹이 발생한다.The composition constituting the first primer layer 1 is prepared as a coating liquid in the form of an aqueous dispersion with water and applied to one surface of the base film 2 . In one embodiment, the coating thickness of the first primer layer 1 is preferably 10 to 200 nm. When the coating thickness is less than 10 nm, a reflective rainbow may be observed after surface processing and adhesion is deteriorated, and when the coating thickness exceeds 200 nm, a reflective rainbow and blocking occur.

일 실시예에서, 제1 프라이머층(1)과 기재필름(2) 사이의 부착력 및 내습부착력은 95 내지 100%인 것이 바람직하다.In one embodiment, the adhesion and moisture resistance between the first primer layer 1 and the base film 2 are preferably 95 to 100%.

다음으로, 제2 프라이머층(3)은 표면에 점착제 또는 접착제의 가공이 이루어 지기 때문에, 점착제 또는 접착제 가공을 할 수 있는 프라이머층을 구성하는 것이 바람직하며, 열처리 후 이물 발생을 억제하기 위해 올리고머 블록 기능을 가지는 것이 바람직하다. 제2프라이머층(3)은 주재에 경화제와 반응할 수 있는 관능기를 늘리고, 관능기와 반응성이 우수한 경화제를 사용함으로써, 프라이머층의 경화 후 네트워크 구조를 올리고머 크기보다 작게 함으로써 열처리 후 발생하는 올리고머가 프라이머층 위로 석출되는 것을 방지할 수 있다. 이와 같이 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 열 공정상의 이물 발생을 최소화하여 타발 시의 수율을 높일 수 있다.Next, since the surface of the second primer layer 3 is processed with an adhesive or adhesive, it is preferable to configure a primer layer capable of processing an adhesive or adhesive, and to suppress the occurrence of foreign substances after heat treatment, an oligomer block It is desirable to have a function. In the second primer layer 3, functional groups capable of reacting with the curing agent are increased in the main material, and a curing agent having excellent reactivity with the functional group is used to make the network structure after curing of the primer layer smaller than the size of the oligomer, so that the oligomer generated after heat treatment is the primer. Precipitation on the layer can be prevented. As such, the polyester film for protecting a display according to an embodiment of the present invention can minimize the generation of foreign substances in a thermal process and increase the yield at the time of punching.

일 실시예에서, 제2 프라이머층의 굴절율은, 제1 프라이머층 및 제2 프라이머층의 굴절율 차이가 0.1 이상이 되도록, 1.45 내지 1.49인 것이 바람직하다.In one embodiment, the refractive index of the second primer layer is preferably 1.45 to 1.49 such that a difference in refractive index between the first primer layer and the second primer layer is 0.1 or more.

일 실시예에서, 제2 프라이머층(3)은 바인더 수지로 카르복실기를 관능기로 가지는 폴리아크릴 수지 및/또는 폴리알킬렌옥사이드 수지를 적용하고 특정가교시스템을 설계하는 것이 바람직하다. 바람직하게는 카르복실기를 관능기로 가지는 폴리아크릴 수지를 포함할 수 있다.In one embodiment, it is preferable to design a specific crosslinking system by applying a polyacrylic resin and/or a polyalkylene oxide resin having a carboxyl group as a functional group to the second primer layer 3 as a binder resin. Preferably, a polyacrylic resin having a carboxyl group as a functional group may be included.

또한, 제2 프라이머층(3)은 경화제로 옥사졸린계, 카보디이미드계 및 멜라민계 중에서 선택된 적어도 1종 이상의 물질을 포함한다. 특히, 옥사졸린계 경화제는 필름에 투습되는 수분을 억제하고, 멜라민계 경화제는 주재와도 반응을 하지만 멜라민 사이의 자체적인 경화반응을 통하여 도막 강도를 향상시킴으로써 양면 코팅 시 발생할 수 잇는 블로킹 현상을 방지하는 역할을 수행한다. 바람직하게는 멜라민계 경화제를 포함할 수 있다.In addition, the second primer layer 3 includes at least one material selected from oxazoline-based, carbodiimide-based, and melamine-based curing agents. In particular, the oxazoline-based curing agent suppresses moisture permeable to the film, and the melamine-based curing agent reacts with the main material, but it enhances the strength of the coating film through its own curing reaction between melamine, preventing the blocking phenomenon that can occur during double-sided coating play a role Preferably, a melamine-based curing agent may be included.

또한, 제2 프라이머층(3)은 첨가제로서 음이온성 계면활성제를 포함하는 것이 바람직하다. Also, the second primer layer 3 preferably contains an anionic surfactant as an additive.

또한, 제2 프라이머층(3)은 코팅성 및 기능성 향상을 위하여 코팅액에 추가적인 첨가제를 더 포함할 수 있다. 이와 같이 제2 프라이머층(3)에 사용되는 첨가제로는 유기입자, 무기입자, 소포제 등을 사용할 수 있다. In addition, the second primer layer 3 may further include additional additives in the coating solution to improve coating properties and functionality. As such, additives used in the second primer layer 3 may include organic particles, inorganic particles, and antifoaming agents.

본 발명에서 제2 프라이머층(3)은 무기 입자를 통해 주행성을 확보할 수 있으며, 무기 입자의 평균입경은 10 내지 300nm인 것이 바람직하다. 무기 입자의 평균입경이 300nm를 초과하게 되면 헤이즈가 높아지는 문제가 발생하고, 10nm 미만인 경우 주행성을 확보할 수 없다. 그리고 무기입자는 실리카 입자 및 실리카-유기물 합성체 중 선택되는 적어도 하나 이상인 것이 바람직하다. 이때 무기 입자는 상술한 제1 프라이머층(1)의 무기 입자와 동일한 무기 입자를 사용할 수 있다.In the present invention, the second primer layer 3 can secure runability through inorganic particles, and the inorganic particles preferably have an average particle diameter of 10 to 300 nm. When the average particle diameter of the inorganic particles exceeds 300 nm, a problem in that the haze increases, and when the average particle diameter is less than 10 nm, it is not possible to secure runability. The inorganic particles are preferably at least one selected from silica particles and silica-organic composites. At this time, the same inorganic particles as those of the first primer layer 1 described above may be used as the inorganic particles.

제2 프라이머층(3)을 구성하는 상기 조성은 물과 함께 수분산액 형태의 도포액으로 제조되어 기재필름(2)의 다른 일면(제1 프라이머층이 도포되지 않은 면)에 도포된다. 일 실시예에서, 도포 두께는 10nm~200nm인 것이 바람직하다. 이때, 도포 두께가 10nm미만일 경우, 주행성 확보가 어렵고 점착제와의 부착력에 문제가 발생할 가능성이 높으며, 200nm초과의 경우, 필름 자체의 색이 황색으로 보일 가능성이 높기 때문에 바람직하지 않다.The composition constituting the second primer layer 3 is prepared as a coating liquid in the form of an aqueous dispersion with water and applied to the other surface of the base film 2 (the surface on which the first primer layer is not coated). In one embodiment, the coating thickness is preferably 10 nm to 200 nm. At this time, when the coating thickness is less than 10 nm, it is difficult to secure runability and there is a high possibility of problems with adhesion with the adhesive, and in the case of more than 200 nm, the color of the film itself is likely to look yellow, which is not preferable.

일 실시예에서, 제2 프라이머층(3)과 기재필름(2) 사이의 부착력 및 내습부착력은 95 내지 100%인 것이 바람직하다. In one embodiment, it is preferable that the adhesion between the second primer layer 3 and the base film 2 and the moisture resistance are 95 to 100%.

본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 길이방향(MD) 및/또는 폭방향(TD)으로 2축 연신된 필름인 것이 바람직하다. 특히, 기재필름(2)을 구성하는 폴리에틸렌 테레프탈레이트는 미연신 상태에서는 결정성을 가지지 않기 때문에 기계적인 강도가 약하고, 낮은 후도 제어에 어려움이 따르기 때문에 이축연신 필름인 것이 더욱 바람직하다.The polyester film for display protection according to an embodiment of the present invention is preferably a biaxially stretched film in the machine direction (MD) and/or the width direction (TD). In particular, since polyethylene terephthalate constituting the base film 2 does not have crystallinity in an unstretched state, mechanical strength is weak and it is difficult to control low thickness, so it is more preferable that it is a biaxially stretched film.

디스플레이 보호용 폴리에스테르 필름에서 주쇄 방향의 배향각은 연신 공정을 거쳐 열고정 처리를 할 때, 연신 방향으로 폴리에스테르계 재료의 결정성에 의해 방향이 설정된다. In the polyester film for display protection, the orientation angle in the main chain direction is set by the crystallinity of the polyester-based material in the stretching direction when heat setting is performed through the stretching process.

주쇄의 배향각은 필름의 폭방향 대비 주쇄의 결정이 이루고 있는 각도를 의미한다. 필름은 2축 연신 공정을 거쳐 열고정 처리를 하는 과정에서 연신 방향에 대한 폴리에스테르계 재료(폴리에스테르 수지)의 결정성에 의해 주쇄 방향의 배향각 방향이 설정된다. 먼저, 폴리에스테르로 형성된 미연신 필름에 대해 길이방향(MD) 연신이 끝나고, 폭방향(TD)으로 연신을 하게 되는데, 이때 통상 폭방향의 연신 끝부분에서 주쇄의 배향각이 0도가 된다. 그리고 열고정 처리를 하면서, 연신 후 잔존 응력에 의해 보잉(bowing) 현상이 발생하게 되는데, 이러한 보잉 현상에 의해 필름 진행 방향의 반대 방향으로 활 모양의 구배를 갖게 된다. The orientation angle of the main chain refers to an angle formed by crystals of the main chain with respect to the width direction of the film. In the process of heat setting the film through a biaxial stretching process, the orientation angle direction of the main chain direction is set by the crystallinity of the polyester-based material (polyester resin) with respect to the stretching direction. First, an unstretched film formed of polyester is stretched in the longitudinal direction (MD) and then stretched in the width direction (TD). At this time, the orientation angle of the main chain is usually 0 degrees at the end of the stretch in the width direction. In addition, while performing the heat setting treatment, a bowing phenomenon occurs due to residual stress after stretching, and due to this bowing phenomenon, a bow-shaped gradient is obtained in a direction opposite to the direction in which the film travels.

이러한 주쇄 결정의 배향은 광축의 변화를 야기시키기 때문에, 배향각을 낮게 조정하지 않을 경우 보호필름 구성 후 광손실이 발생하여 지문 인식율을 떨어 뜨린다. 이러한 현상을 최소화하기 위해, 엣지부(필름의 모서리 부분)도 폭 중심의 물성과 최대한 유사하게 설정될 수 있도록, 보잉 현상을 억제할 필요가 있다. 보잉 현상을 억제하기 위해서는 MD방향의 연신 대비 TD방향의 연신을 크게 해야할 필요가 있으며, 이에 따라 MD연신:TD연신이 1:1.45 이상인 것이 바람직하며, 공정 안정성 및 후도 제어를 위해 1:1.75이하로 조절하는 것이 바람직하다.Since the orientation of the main chain crystal causes a change in the optical axis, if the orientation angle is not adjusted low, light loss occurs after the protective film is formed, thereby lowering the fingerprint recognition rate. In order to minimize this phenomenon, it is necessary to suppress the bowing phenomenon so that the edge portion (corner portion of the film) can be set to be as similar as possible to the physical properties of the center of width. In order to suppress the bowing phenomenon, it is necessary to increase the stretching in the TD direction compared to the stretching in the MD direction. Accordingly, it is preferable that the MD stretching:TD stretching ratio is 1:1.45 or more, and 1:1.75 or less for process stability and thickness control. It is preferable to adjust to .

일 실시예에서, 디스플레이 보호용 폴리에스테르 필름의 주쇄의 배향각은 20도 이하가 바람직하며, 17도 이하가 더욱 바람직하고, 12도 이하가 더욱 더 바람직하다. 디스플레이 보호용 폴리에스테르 필름의 주쇄의 배향각이 20도를 초과하면 광축과 배향각의 편차가 커지기 때문에 광손실율이 커진다.In one embodiment, the orientation angle of the main chain of the polyester film for display protection is preferably 20 degrees or less, more preferably 17 degrees or less, and even more preferably 12 degrees or less. When the orientation angle of the main chain of the polyester film for display protection exceeds 20 degrees, the optical loss rate increases because the deviation between the optical axis and the orientation angle increases.

또한, 광손실율은 편광판 평행니콜에서 필름이 삽입되었을 때, 각도에 따른 빛의 손실을 나타내는 수치로서 식 1로 나타낼 수 있다.In addition, the light loss rate can be represented by Equation 1 as a numerical value representing the loss of light according to the angle when the film is inserted in the parallel Nicols polarizer.

(식 1)(Equation 1)

광손실율=(편광판 평행니콜 최대 광량-편광판 2매 사이에 필름 삽입후의 최대 광량)/(편광판 평행니콜 최대 광량)Light loss rate = (Maximum amount of light in parallel Nicols of polarizing plate - Maximum amount of light after inserting a film between 2 polarizing plates) / (Maximum amount of light in parallel Nicols of polarizing plate)

이때, 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름의 식 1에 따른 광손실율은 11% 이하인 것이 바람직하다. 광손실율이 11%를 초과하는 경우 높은 광손실로 인해 지문인식율이 저하되는 문제가 발생하게 된다.At this time, the optical loss rate according to Equation 1 of the polyester film for display protection according to an embodiment of the present invention is preferably 11% or less. When the light loss rate exceeds 11%, a problem in that the fingerprint recognition rate is lowered due to the high light loss occurs.

본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름에서 식 1에 따른 광손실율은 통상 배향각 0도 근방의 센터부에서 최소치를 가지며, 배향각이 올라갈수록 증가하는 경향이 있다. 따라서, 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름에서는 광손실율 최소화를 위해 상기의 배향각 조정을 통해, 엣지부도 최대한 센터부와 유사한 물성을 가질 수 있도록 한다. 이를 위해 디스플레이 보호용 폴리에스테르 필름은 센터부와 엣지부의 배향각 차이가 20도 이하인 것이 바람직하다. 센터부와 엣지부의 배향각 차이가 20도 초과인 경우 광손실율이 증가하게 된다.In the polyester film for display protection according to an embodiment of the present invention, the light loss rate according to Equation 1 usually has a minimum value in the center portion near 0 degrees of orientation angle, and tends to increase as the orientation angle increases. Therefore, in the polyester film for protecting a display according to an embodiment of the present invention, the edge portion can have physical properties similar to those of the center portion as much as possible through the adjustment of the orientation angle in order to minimize the light loss rate. To this end, the polyester film for display protection preferably has a difference in orientation angle between the center portion and the edge portion of 20 degrees or less. When the difference in orientation angle between the center portion and the edge portion exceeds 20 degrees, the light loss rate increases.

일 실시예에서, 디스플레이 보호용 폴리에스테르 필름은 배향각과 광축의 차이가 9도 이하인 것이 바람직하다. 배향각과 광축의 차이가 9도 초과인 경우 디스플레이 디바이스 안의 편광판과의 광축 차이가 커지게 되어, 편광판 광축에 맞추어 타발을 진행할 수 없으며, 타발을 할 경우에도 지문인식율이 크게 저하되고, 화면 색의 왜곡을 발생시켜 보호필름으로서의 기능을 할 수 없는 문제가 생긴다.In one embodiment, the polyester film for display protection preferably has a difference of 9 degrees or less between an orientation angle and an optical axis. If the difference between the orientation angle and the optical axis exceeds 9 degrees, the optical axis difference between the polarizer and the polarizer in the display device increases, making it impossible to perform punching in line with the optical axis of the polarizer. occurs, resulting in a problem in that it cannot function as a protective film.

또한, 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 전광선 투과율이 93% 이상인 것이 바람직하고, 95% 이상인 것이 더욱 바람직하다. 전광선 투과율이 93% 미만인 경우 지문인식율이 떨어지고 디스플레이 소재의 휘도가 저하되는 문제가 발생한다.In addition, the polyester film for display protection according to an embodiment of the present invention preferably has a total light transmittance of 93% or more, more preferably 95% or more. When the total light transmittance is less than 93%, a problem in that the fingerprint recognition rate is lowered and the luminance of the display material is lowered occurs.

또한, 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 150℃ 온도에서 1시간 열처리 후 헤이즈(Haze) 변화가 1% 이하인 것이 바람직하다. 헤이즈가 1%를 초과하는 경우 투명성이 낮아져 명암비가 낮아지는 문제가 발생한다.In addition, the polyester film for display protection according to an embodiment of the present invention preferably has a haze change of 1% or less after heat treatment at 150 ° C for 1 hour. When the haze exceeds 1%, the transparency is lowered and the contrast ratio is lowered.

상기와 같은 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름의 제조방법은 폴리에스테르 수지를 용융 압출하여 미연신 시트를 형성하는 제1 단계, 미연신 시트의 일면에 제1 프라이머층을 형성하는 도포액을 도포하고 건조하는 제2 단계, 미연신 시트의 다른 일면에 제2 프라이머층을 형성하는 도포액을 도포하고 건조하는 제3 단계, 제1 프라이머층과 제2 프라이머층이 형성된 미연신 시트를 길이 방향(MD)으로 1축 연신하는 제4 단계, 1축 연신된 시트를 폭 방향(TD)으로 2축 연신하는 제5 단계 및 2축 연신된 시트를 열고정하여 디스플레이 보호용 폴리에스테르 필름을 형성하는 제6 단계를 포함한다.Method for manufacturing a polyester film for display protection according to an embodiment of the present invention as described above is a first step of forming an unstretched sheet by melting and extruding a polyester resin, forming a first primer layer on one side of the unstretched sheet A second step of applying and drying a coating solution, a third step of applying and drying a coating solution for forming a second primer layer on the other side of the unstretched sheet, and an unstretched sheet having a first primer layer and a second primer layer formed thereon. A fourth step of uniaxially stretching in the longitudinal direction (MD), a fifth step of biaxially stretching the uniaxially stretched sheet in the width direction (TD), and heat-setting the biaxially stretched sheet to form a polyester film for display protection. It includes the sixth step of doing.

일 실시예에서, 열고정 처리 온도는 180 내지 220℃인 것이 바람직하며, 180 내지 200℃인 것이 더욱 바람직하다. 이때 열고정 처리 온도가 180℃ 미만인 경우 기재필름(2)과 제1 프라이머층(1) 및 제2 프라이머층(3)의 열고정이 제대로 이루어지지 않으며, 220℃를 초과하는 경우 보잉 현상이 발생하여 배향각과 광축의 차이가 커질 수 있다. 이와 같이, 통상의 열고정 처리 온도보다 낮은 온도에서 열처리하여, 연신부와 열고정부의 응력 차이를 최소화할 수 있다.In one embodiment, the heat setting treatment temperature is preferably 180 to 220 ° C, more preferably 180 to 200 ° C. At this time, when the heat setting treatment temperature is less than 180 ° C, the heat setting of the base film 2, the first primer layer 1, and the second primer layer 3 is not properly performed, and when it exceeds 220 ° C, a bowing phenomenon occurs. A difference between an orientation angle and an optical axis may increase. In this way, by performing the heat treatment at a temperature lower than the normal heat setting treatment temperature, it is possible to minimize a stress difference between the stretching part and the heat setting part.

본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름의 제조방법에서 상술한 디스플레이 보호용 폴리에스테르 필름과 중복된 설명은 생략한다.In the manufacturing method of the polyester film for display protection according to an embodiment of the present invention, descriptions overlapping with the polyester film for display protection described above will be omitted.

이하, 실시예와 비교예를 통하여 본 발명의 구성 및 그에 따른 효과를 보다 상세히 설명하고자 한다. 그러나, 본 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것이며, 본 발명의 범위가 이들 실시예에 한정되는 것은 아니다.Hereinafter, the configuration of the present invention and its effects will be described in more detail through Examples and Comparative Examples. However, these examples are for explaining the present invention in more detail, and the scope of the present invention is not limited to these examples.

[실시예][Example]

[제조예][Production Example]

(도포액 1)(Coating liquid 1)

바인더 수지로 물 70중량%와 폴리우레탄 수지(H-15, 제일공업社) 30중량%의 주재1과 물 70% 중량%와 폴리에스테르계 공중합체 수지(TR620K, 타카마츠 유지社) 30% 중량%의 주재2를 각각 12.5중량%로 하여 혼합하였다. 이렇게 구성한 주재 수지 수분산액 20.0중량%와 내습성을 향상시키기 위한 경화제로 옥사졸린계 경화제(WS500, 니폰 카바이드社) 40중량%와 물 60 중량%로 구성된 경화제 1과 멜라민계 경화제(PM80, DIC社) 70 중량%와 물 30 중량%로 구성된 경화제 2를 각각 1.87중량%로 하여 혼합하였다. 이렇게 제조된 도포액에 물 90중량% 및 음이온계 계면활성제(RY-2, Goo Chemical社) 10중량%로 구성된 계면활성제 수분산액 1.0 중량%와 실리카 입자 70중량% 및 물 30중량%로 구성된 수분산 입자 도포액 0.5 중량%와 잔량의 물을 이용하여 도포액 1을 제조하였다.As a binder resin, 70% by weight of water and 30% by weight of polyurethane resin (H-15, Jeil Industry Co., Ltd.) 30% by weight of main material 1, 70% by weight of water and 30% by weight of polyester copolymer resin (TR620K, Takamatsu Yuji Co., Ltd.) % of the main material 2 was mixed at 12.5% by weight, respectively. Curing agent 1 composed of 20.0% by weight of the aqueous dispersion of the main resin and 40% by weight of an oxazoline-based curing agent (WS500, Nippon Carbide Co.) and 60% by weight of water as a curing agent for improving moisture resistance and melamine-based curing agent (PM80, manufactured by DIC Co., Ltd.) ) 70% by weight and 30% by weight of water curing agent 2 was mixed at 1.87% by weight, respectively. In the coating liquid prepared as described above, 1.0% by weight of a surfactant aqueous dispersion composed of 90% by weight of water and 10% by weight of an anionic surfactant (RY-2, Goo Chemical Co.), 70% by weight of silica particles, and 30% by weight of water. A coating liquid 1 was prepared using 0.5% by weight of the dispersion particle coating liquid and the remaining amount of water.

(도포액 2)(Coating liquid 2)

바인더 수지로 물 70중량% 및 카르복실기를 관능기로 가지는 폴리아크릴 수지(RX-7013ED, 니폰 카바이드社) 30중량%의 주재 수지 수분산액 20중량%와 멜라민계 경화제(PM80, DIC社) 30중량% 및 물 70중량%의 경화제 수분산액 10중량%를 혼합하여 만들어진 혼합액에 물 90중량% 및 음이온성 계면활성제(RY-2, Goo Chemical社) 10중량%로 구성된 계면활성제 수분산액 1.0중량%와 실리카 입자 70중량% 및 물 30중량%로 구성된 수분산 입자 도포액 0.5중량%와 잔량의 물을 이용하여 도포액 2를 제조하였다.As a binder resin, 70% by weight of water and 30% by weight of a polyacrylic resin having a carboxyl group as a functional group (RX-7013ED, Nippon Carbide Co.) 20% by weight of an aqueous dispersion of the main resin and 30% by weight of a melamine-based curing agent (PM80, DIC Co.) 1.0% by weight of a surfactant aqueous dispersion consisting of 90% by weight of water and 10% by weight of an anionic surfactant (RY-2, Goo Chemical Co.) and silica particles in a mixture prepared by mixing 10% by weight of a curing agent aqueous dispersion of 70% by weight of water A coating solution 2 was prepared using 0.5% by weight of a water-dispersed particle coating solution composed of 70% by weight and 30% by weight of water and the remaining amount of water.

(도포액 3)(Coating liquid 3)

바인더 수지로 폴리우레탄 수지(H-15, 제일공업社) 대신 폴리우레탄 수지(AP-40F, DIC社)을 사용한 것을 제외하고는 도포액 1과 동일하게 하여 도포액 3을 제조하였다.Coating solution 3 was prepared in the same manner as in coating solution 1, except that polyurethane resin (AP-40F, DIC Co.) was used instead of polyurethane resin (H-15, Jeil Industrial Co.) as a binder resin.

[실시예 1~4][Examples 1 to 4]

폴리에틸렌테레프탈레이트 원료 칩을 용융 압출한 후 캐스팅 롤에서 미연신 형태의 시트를 제조한 다음 미연신 시트의 일면 및 다른 일면에 metal bar #4를 이용하여 도포액을 각각 도포하고 80℃에서 건조시켜 각각 두께가 100nm인 제1 프라이머층 및 제2 프라이머층을 형성하였다. 다음으로 길이 방향(MD) 및 폭 방향(TD)으로 각각 연신한 후 190℃에서 열고정하여 2축 연신된 디스플레이 보호용 폴리에스테르 필름을 제조하였다.After melting and extruding the polyethylene terephthalate raw material chips, an unstretched sheet is prepared from a casting roll, then the coating liquid is applied to one side and the other side of the unstretched sheet using a metal bar #4, and dried at 80 ° C, respectively. A first primer layer and a second primer layer having a thickness of 100 nm were formed. Next, it was stretched in the machine direction (MD) and the width direction (TD), respectively, and then heat-set at 190° C. to prepare a biaxially stretched polyester film for display protection.

이때 도포액의 조성, 연신 조건 및 필름 전체의 두께는 표 1에 나타내었고 제1 프라이머층과 제2 프라이머층의 굴절율은 각각 표 3에 나타내었다.At this time, the composition of the coating solution, stretching conditions, and the thickness of the entire film are shown in Table 1, and the refractive indices of the first primer layer and the second primer layer are shown in Table 3, respectively.

[비교예 1~5][Comparative Examples 1 to 5]

하기 표 1과 같이 도포액의 조성 및 연신 조건을 변경한 것을 제외하고는 실시예 1과 동일하게 디스플레이 보호용 폴리에스테르 필름을 제조하였다.A polyester film for display protection was prepared in the same manner as in Example 1, except for changing the composition and stretching conditions of the coating liquid as shown in Table 1 below.

구분division MD
연신비MD
stretch ratio TD
연신비TD
stretch ratio MD : TD
연신비율MD: TD
elongation ratio 필름 두께
(㎛)film thickness
(μm) 제1 프라이머층1st primer layer 제2 프라이머층2nd primer layer 실시예1Example 1 3.03.0 4.354.35 1:1.451:1.45 125125 도포액 1coating liquid 1 도포액 2coating liquid 2 실시예 2Example 2 3.03.0 4.654.65 1:1.551:1.55 125125 도포액 1coating liquid 1 도포액 2coating liquid 2 실시예3Example 3 3.03.0 4.954.95 1:1.651:1.65 125125 도포액 1coating liquid 1 도포액 2coating liquid 2 실시예4Example 4 3.03.0 5.255.25 1:1.751:1.75 125125 도포액 1coating liquid 1 도포액 2coating liquid 2 비교예1Comparative Example 1 3.03.0 3.53.5 1:1.171:1.17 125125 도포액 1coating liquid 1 도포액 2coating liquid 2 비교예2Comparative Example 2 3.03.0 3.53.5 1:1.171:1.17 125125 도포액 1coating liquid 1 도포액 3coating liquid 3 비교예3Comparative Example 3 3.03.0 4.954.95 1:1.651:1.65 125125 도포액 1coating liquid 1 도포액 1coating liquid 1 비교예4Comparative Example 4 3.03.0 4.954.95 1:1.651:1.65 125125 도포액 2coating liquid 2 도포액 2coating liquid 2 비교예 5Comparative Example 5 3.03.0 3.03.0 1:11:1 125125 도포액 1coating liquid 1 도포액 2coating liquid 2

상기 실시예 1 내지 4 및 비교예 1 내지 5에 따른 폴리에스테르 필름을 사용하여 다음과 같은 실험예를 통해 물성을 측정하고 그 결과를 다음 표 2 및 3에 나타내었다.Physical properties were measured through the following experimental examples using the polyester films according to Examples 1 to 4 and Comparative Examples 1 to 5, and the results are shown in Tables 2 and 3 below.

[실험예][Experimental Example]

(1) 전투과율 측정(1) Measurement of combat negligence

헤이즈 미터기(NDH-4000, 니폰 덴쇼쿠社)로 필름의 전투과율을 측정하였다.The combat transmittance of the film was measured with a haze meter (NDH-4000, Nippon Denshoku Co., Ltd.).

(2) 두께 측정(2) Thickness measurement

마이크로미터(VL-50aS, 미쯔도요社)를 이용하여 필름의 두께를 측정하였다. The thickness of the film was measured using a micrometer (VL-50aS, Mitutoyo Co., Ltd.).

(3) 광손실율 측정(3) Optical loss rate measurement

필름을 가로 5㎝ 및 세로 5㎝로 재단한 후, 편광필름 2장을 100% 투과 상태(평행니콜)로 만들어 최대 광량을 확인하고, 2장의 편광필름 사이에 재단된 필름을 위치시킨 후, 필름의 각도를 변경하면서 최대 광량의 변화를 측정하고, 식 1을 통해 광손실율을 산출하였다.After cutting the film into 5 cm wide and 5 cm long, make two polarizing films in a 100% transmission state (parallel Nicols) to check the maximum amount of light, place the cut film between the two polarizing films, and The change in the maximum amount of light was measured while changing the angle of , and the light loss rate was calculated through Equation 1.

(식 1)(Equation 1)

광손실율=(편광판 평행니콜 최대 광량-편광판 2매 사이에 필름 삽입 후의 최대 광량)/(편광판 평행니콜 최대 광량)Light loss rate = (Maximum amount of light in parallel Nicols of polarizing plate - Maximum amount of light after inserting a film between 2 polarizing plates) / (Maximum amount of light in parallel Nicols of polarizing plate)

(4) 배향각 측정(4) Orientation angle measurement

필름을 2축 연신한 후 필름 샘플을 배향각 측정장비(SST-4000, 노무라 쇼지社)로 필름 폭방향에 대한 주쇄의 결정 방향을 센터부와 엣지부에서 각각 측정하였다. 이때 센터부는 배향각이 0도이기 때문에 하기 표 2의 배향각은 엣지부의 배향각을 나타낸다.After biaxially stretching the film, the crystal orientation of the main chain with respect to the film width direction was measured at the center portion and the edge portion of the film sample using an orientation angle measuring device (SST-4000, Nomura Shoji Co., Ltd.), respectively. At this time, since the orientation angle of the center portion is 0 degrees, the orientation angle of Table 2 below represents the orientation angle of the edge portion.

(5) 광축 측정(5) Optical axis measurement

편광판 크로스 니콜 상태에서 필름을 편광판 2매 사이에 넣은 후, 블랙모드가 구현되는 각도를 확인하여, 각도기로 측정하였다.After inserting the film between two polarizers in the cross-Nicol polarizer state, the angle at which the black mode is implemented was checked and measured with a protractor.

(6) 무지개 얼룩 검사(6) Rainbow blot test

제조된 필름 뒷면에 절연테이프(Niito社)를 붙여 형광등 반사 하에서 육안으로 검사한 다음 하기와 같이 평가하였다.Insulation tape (Niito Co.) was attached to the back of the prepared film, visually inspected under fluorescent light reflection, and then evaluated as follows.

○: 무지개 얼룩 미관측○: no observation of rainbow stains

X; 무지개 얼룩 관측X; Observation of rainbow blobs

(7) 헤이즈 변화 측정(7) Haze change measurement

제조된 필름에 대해 헤이즈 미터기(NDH-4000, 니폰 덴쇼쿠社)를 이용하여 열처리 전 헤이즈를 측정하고, 150℃ 오븐에서 1시간 열처리한 후의 헤이즈를 각각 측정하였다.The haze of the prepared film was measured before heat treatment using a haze meter (NDH-4000, Nippon Denshoku Co., Ltd.), and the haze after heat treatment in an oven at 150 ° C. for 1 hour was measured.

(8) 부착력 측정(8) Measurement of adhesion

#20 와이어바를 사용하여 제1 프라이머층 표면에 아크릴계 UV 경화수지를 도포한 다음, 절단기로 제조된 필름에 절단선을 만들어서, 10 × 10의 매트릭스에 1㎜ × 1㎜ 정사각형들을 배치한다. 그리고 절단선이 형성된 필름에 셀로판 테이프(No. 405, NICHIBAN社, 넓이: 24㎜)를 붙이고, 벨벳을 이용하여 테이프를 문질러서 필름에 강력하게 부착시킨 후, 수직으로 테이프를 떼어낸다. 이때, 아크릴계 UV 경화수지로 형성된 코팅층에 남아있는 프라이머층의 면적을 하기 식 2에 대입하여 부착력을 산출하였다.An acrylic UV curable resin is applied to the surface of the first primer layer using a #20 wire bar, and then 1 mm x 1 mm squares are arranged in a matrix of 10 x 10 by making cut lines on the film made with a cutter. Then, cellophane tape (No. 405, NICHIBAN Co., width: 24 mm) is attached to the film on which the cut lines are formed, and the tape is strongly adhered to the film by rubbing the tape using velvet, and then the tape is removed vertically. At this time, the adhesion was calculated by substituting the area of the primer layer remaining in the coating layer formed of the acrylic UV curable resin into Equation 2 below.

(식 2)(Equation 2)

Figure 112020111081266-pat00001
Figure 112020111081266-pat00001

또한, 동일하게 준비된 필름을 60℃ 온도 및 90% 습도 환경에서 100시간을 방치한 후 동일한 방법으로 내습 부착력을 측정하였다.In addition, after leaving the film prepared in the same way for 100 hours in a 60° C. temperature and 90% humidity environment, moisture resistance adhesion was measured in the same manner.

(9) 프라이머층 굴절율 측정(9) Measurement of the refractive index of the primer layer

유리판 상에 도포액 1 내지 3의 도포액을 각각 도포하여 열경화시킨 후, 도포액이 코팅되지 않은 유리판의 뒷면에 검은색 절연 테이프를 붙인 후, 엘립소미터(Elli-SE, ㈜엘립소테크놀러지社)를 이용하여 굴절율을 측정하였다.After applying the coating liquids 1 to 3 on a glass plate and curing them with heat, a black insulating tape is attached to the back of the glass plate that is not coated with the coating liquid, and then an ellipsometer (Elli-SE, Ellipso Technology Co., Ltd.) Company) was used to measure the refractive index.

구분division 전투과율
(%)battle rate
(%) 배향각
(°)orientation angle
(°) 광축
(°)optical axis
(°) 무지개
얼룩rainbow
stain 헤이즈변화
(%)Haze change
(%) 광손실율light loss rate 실시예 1Example 1 94.294.2 2020 2727 ○○ 0.80.8 1111 실시예 2Example 2 93.893.8 1717 2222 ○○ 0.90.9 10.310.3 실시예 3Example 3 93.593.5 1414 1818 ○○ 0.80.8 9.29.2 실시예 4Example 4 9393 1111 1313 ○○ 1.01.0 6.86.8 비교예1Comparative Example 1 9393 4747 5252 ○○ 0.90.9 1515 비교예2Comparative Example 2 9191 4747 5252 ○○ 3.23.2 1818 비교예3Comparative Example 3 8989 1414 1818 ○○ 3.13.1 2020 비교예4Comparative Example 4 9292 1414 1818 XX 0.60.6 1616 비교예 5Comparative Example 5 9393 5050 6262 ○○ 0.80.8 2222

구분division 제1 프라이머층 굴절율Refractive index of the first primer layer 제2 프라이머층 굴절율Refractive index of the second primer layer 프라이머층간
굴절율 차between primer layers
refractive index difference 부착력
(%)adhesion
(%) 내습부착력
(%)Moisture resistance adhesion
(%) 실시예 1Example 1 1.591.59 1.471.47 0.120.12 100100 100100 실시예 2Example 2 1.591.59 1.471.47 0.120.12 100100 100100 실시예 3Example 3 1.591.59 1.471.47 0.120.12 100100 100100 실시예 4Example 4 1.591.59 1.471.47 0.120.12 100100 100100 비교예1Comparative Example 1 1.591.59 1.471.47 0.120.12 100100 100100 비교예2Comparative Example 2 1.591.59 1.551.55 0.040.04 100100 100100 비교예3Comparative Example 3 1.591.59 1.591.59 00 100100 100100 비교예4Comparative Example 4 1.471.47 1.471.47 00 100100 100100 비교예 5Comparative Example 5 1.591.59 1.471.47 0.120.12 100100 100100

상기 표 2 및 표 3에 기재된 바와 같이, 본원발명에 따른 실시예 1 내지 4는 모두 부착력이 우수하고, 광학적 및 기계적 성질이 우수한 것으로 전투과율, 광손실율, 배향각, 광축, 간섭에 의한 무지개 얼룩, 헤이즈 변화량이 모두 보호필름에 필요한 모든 물성을 충족하는 것을 알 수 있다.As described in Tables 2 and 3, Examples 1 to 4 according to the present invention all have excellent adhesion and excellent optical and mechanical properties, and have excellent transmission rate, light loss rate, orientation angle, optical axis, and rainbow stains due to interference. , it can be seen that the amount of change in haze satisfies all physical properties required for the protective film.

반면에, 비교예 1은 기재필름 양면에 위치한 제1 프라이머층 및 제2 프라이머층의 굴절율 차이가 0.1 이상이나 MD방향 및 TD방향의 낮은 연신비율로 인해 주쇄의 배향각이 20을 초과하고 과도한 광손실이 발생하는 것을 알 수 있다.On the other hand, in Comparative Example 1, the difference in refractive index between the first primer layer and the second primer layer located on both sides of the base film is 0.1 or more, but the orientation angle of the main chain exceeds 20 due to the low stretching ratio in the MD direction and the TD direction, and excessive light It can be seen that losses occur.

또한, 기재필름 양면에 위치한 제1 프라이머층 및 제2 프라이머층의 굴절율 차이가 0.1 미만이고, MD방향 및 TD방향의 낮은 연신비율을 가진 비교예 2는 주쇄의 배향각이 20을 초과하고 헤이즈 변화가 크며, 과도한 광손실이 발생하는 것을 알 수 있다.In addition, in Comparative Example 2, in which the difference in refractive index between the first primer layer and the second primer layer located on both sides of the base film was less than 0.1 and had a low elongation ratio in the MD and TD directions, the orientation angle of the main chain exceeded 20 and the haze changed. is large, and it can be seen that excessive light loss occurs.

또한, 기재필름 양면에 위치한 제1 프라이머층 및 제2 프라이머층이 동일한 도포액으로 형성된 비교예 3 및 비교예 4는 프라이머층간 굴절율이 동일하여 낮은 전투과율을 가지며 무지개 얼룩이 발생하거나 높은 헤이즈 변화가 발생하는 것을 알 수 있다.In addition, Comparative Example 3 and Comparative Example 4 in which the first primer layer and the second primer layer located on both sides of the base film were formed with the same coating solution had the same refractive index between the primer layers, so they had a low transmittance, and rainbow stains or high haze changes occurred. can know that

또한, 비교예 5는 배향각과 광축의 차이가 9도를 초과한 결과 광손실율이 11%를 초과하여 과도한 광손실이 발생하는 것을 알 수 있다.Further, in Comparative Example 5, as a result of the difference between the orientation angle and the optical axis exceeding 9 degrees, the light loss rate exceeded 11%, indicating that excessive light loss occurred.

이와 같이 본 발명의 일 실시예에 따른 디스플레이 보호용 폴리에스테르 필름은 표면에 하드코팅 가공 후 간섭무라 현상을 최소화하여 후가공시의 생산성을 좋게 할 수 있으며, 올리고머 블록 기능을 통해 이물 발생을 억제하고, 낮은 배향각에 따른 광손실율을 제어함으로써 지문이식율을 높일 수 있다. 또한, 광학적 특성이 우수하기 때문에 보호필름 이외의 광학용 필름으로도 널리 사용 가능하다.As described above, the polyester film for display protection according to an embodiment of the present invention can improve productivity during post-processing by minimizing the interference mura phenomenon after hard coating on the surface, suppressing foreign matter generation through the oligomer block function, and By controlling the light loss rate according to the orientation angle, the fingerprint implantation rate can be increased. In addition, since it has excellent optical properties, it can be widely used as an optical film other than a protective film.

이상에서 본 발명의 바람직한 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.Although the preferred embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and improvements of those skilled in the art using the basic concept of the present invention defined in the following claims are also made according to the present invention. falls within the scope of the rights of

1: 제1 프라이머층 2: 기재필름
3: 제2 프라이머층1: first primer layer 2: base film
3: second primer layer

Claims (17)

2축 연신된 기재필름;
상기 기재필름의 일면에 형성된 제1 프라이머층; 및
상기 기재필름의 다른 일면에 형성된 제2 프라이머층;
을 포함하고,
상기 제1 프라이머층 및 상기 제2 프라이머층의 굴절율 차이는 0.1 이상이며,
배향각과 광축의 차이가 9도 이하이고, 주쇄의 배향각이 20도 이하인, 디스플레이 보호용 폴리에스테르 필름.Biaxially stretched base film;
a first primer layer formed on one surface of the base film; and
a second primer layer formed on the other side of the base film;
including,
The difference in refractive index between the first primer layer and the second primer layer is 0.1 or more,
The difference between the orientation angle and the optical axis is 9 degrees or less, and the orientation angle of the main chain is 20 degrees or less, a polyester film for display protection. 제1항에 있어서,
상기 디스플레이 보호용 폴리에스테르 필름은 150℃에서 1시간 열처리 후 헤이즈 변화가 1% 이하인, 디스플레이 보호용 폴리에스테르 필름.According to claim 1,
The polyester film for display protection has a change in haze of 1% or less after heat treatment at 150 ° C. for 1 hour or less, a polyester film for display protection. 제1항에 있어서,
상기 디스플레이 보호용 폴리에스테르 필름은 하기 식 1에 따른 광손실율이 11% 이하인, 디스플레이 보호용 폴리에스테르 필름.
(식 1)
광손실율=(편광판 평행니콜 최대 광량-편광판 2매 사이에 필름 삽입 후의 최대 광량)/(편광판 평행니콜 최대 광량).According to claim 1,
The polyester film for protecting the display has an optical loss rate of 11% or less according to Formula 1 below, a polyester film for protecting a display.
(Equation 1)
Light loss rate = (maximum light amount of polarizing plate parallel nicol - maximum light amount after inserting the film between 2 polarizers) / (maximum light amount of polarizing plate parallel nicol). 삭제delete 제1항에 있어서,
상기 디스플레이 보호용 폴리에스테르 필름은 센터부와 엣지부의 배향각 차이가 20도 이하인, 디스플레이 보호용 폴리에스테르 필름.According to claim 1,
The polyester film for protecting the display is a polyester film for protecting a display having a center portion and an orientation angle difference of 20 degrees or less at an edge portion. 삭제delete 제1항에 있어서,
상기 제1 프라이머층의 굴절율은 1.58 내지 1.62이고, 제2 프라이머층의 굴절율은 1.45 내지 1.49인, 디스플레이 보호용 폴리에스테르 필름.According to claim 1,
The refractive index of the first primer layer is 1.58 to 1.62, and the refractive index of the second primer layer is 1.45 to 1.49, a polyester film for display protection. 제1항에 있어서,
상기 디스플레이 보호용 폴리에스테르 필름은 MD방향:TD방향 연신비가 1:1.45 내지 1:1.75인, 디스플레이 보호용 폴리에스테르 필름. According to claim 1,
The polyester film for protecting the display is MD direction: TD direction stretch ratio of 1: 1.45 to 1: 1.75, a polyester film for display protection. 제1항에 있어서,
상기 디스플레이 보호용 폴리에스테르 필름은 전투과율이 93% 이상인, 디스플레이 보호용 폴리에스테르 필름.According to claim 1,
The polyester film for protecting the display has a combat rate of 93% or more, a polyester film for protecting the display. 제1항에 있어서,
상기 제1 프라이머층은 폴리에스테르 공중합체 수지, 폴리우레탄계 수지, 옥사졸린계 경화제, 멜라민계 경화제, 음이온성 계면활성제 및 무기입자를 포함하는, 디스플레이 보호용 폴리에스테르 필름.According to claim 1,
The first primer layer is a polyester film for display protection comprising a polyester copolymer resin, a polyurethane-based resin, an oxazoline-based curing agent, a melamine-based curing agent, an anionic surfactant and inorganic particles. 제1항에 있어서,
상기 제2 프라이머층은 카르복실기를 가지는 폴리아크릴 수지, 멜라민계 경화제, 음이온성 계면활성제 및 무기입자를 포함하는, 디스플레이 보호용 폴리에스테르 필름.According to claim 1,
The second primer layer is a polyester film for display protection comprising a polyacrylic resin having a carboxyl group, a melamine-based curing agent, an anionic surfactant and inorganic particles. 제1항에 있어서,
상기 제2 프라이머층은 올리고머 블록 기능을 가지는, 디스플레이 보호용 폴리에스테르 필름.According to claim 1,
The second primer layer has an oligomer block function, a polyester film for display protection. 제1항에 있어서,
상기 기재필름은 폴리에틸렌테레프탈레이트, 폴리에틸렌나프탈레이트, 폴리에틸렌이소프탈레이트 및 폴리카보네이트 중에서 선택된 적어도 하나인, 디스플레이 보호용 폴리에스테르 필름.According to claim 1,
The base film is at least one selected from polyethylene terephthalate, polyethylene naphthalate, polyethylene isophthalate and polycarbonate, a polyester film for display protection. 제1항에 있어서,
상기 기재필름의 두께는 25 내지 250㎛인, 디스플레이 보호용 폴리에스테르 필름.According to claim 1,
The thickness of the base film is 25 to 250㎛, a polyester film for display protection. 폴리에스테르 수지를 용융 압출하여 미연신 시트를 형성하는 제1 단계;
상기 미연신 시트의 일면에 제1 프라이머층을 형성하는 도포액을 도포하고 건조하는 제2 단계;
상기 미연신 시트의 다른 일면에 제2 프라이머층을 형성하는 도포액을 도포하고 건조하는 제3 단계;
상기 제1 프라이머층과 상기 제2 프라이머층이 형성된 미연신 시트를 길이 방향(MD)으로 1축 연신하는 제4 단계;
상기 1축 연신된 시트를 폭 방향(TD)으로 2축 연신하는 제5 단계; 및
상기 2축 연신된 시트를 열고정하여 디스플레이 보호용 폴리에스테르 필름을 형성하는 제6 단계;
를 포함하며,
상기 제6단계에서 형성된 디스플레이 보호용 폴리에스테르 필름은 배향각과 광축의 차이가 9도 이하이고, 주쇄의 배향각이 20도 이하인, 디스플레이 보호용 폴리에스테르 필름의 제조방법.A first step of melt-extruding a polyester resin to form an unstretched sheet;
A second step of applying a coating liquid for forming a first primer layer on one surface of the unstretched sheet and drying it;
A third step of applying a coating liquid for forming a second primer layer on the other surface of the unstretched sheet and drying it;
A fourth step of uniaxially stretching the unstretched sheet on which the first primer layer and the second primer layer are formed in a longitudinal direction (MD);
A fifth step of biaxially stretching the uniaxially stretched sheet in a width direction (TD); and
A sixth step of forming a polyester film for display protection by heat-setting the biaxially stretched sheet;
Including,
The polyester film for display protection formed in the sixth step has a difference between the orientation angle and the optical axis of 9 degrees or less, and the orientation angle of the main chain is 20 degrees or less, a method for producing a polyester film for display protection. 제15항에 있어서,
상기 제1 프라이머층 및 상기 제2 프라이머층의 두께는 10 내지 200nm인, 디스플레이 보호용 폴리에스테르 필름의 제조방법.According to claim 15,
The thickness of the first primer layer and the second primer layer is 10 to 200nm, a method of manufacturing a polyester film for protecting a display. 제15항에 있어서,
상기 제6 단계의 열고정 온도는 180 내지 220℃인, 디스플레이 보호용 폴리에스테르 필름의 제조방법. According to claim 15,
The heat setting temperature of the sixth step is 180 to 220 ° C., a method for manufacturing a polyester film for protecting a display.
KR1020200136194A 2020-10-20 2020-10-20 Polyester film for display protection KR102472872B1 (en)