KR102466723B1 - Gold foil printing plates and manufacturing methode of the same - Google Patents

Gold foil printing plates and manufacturing methode of the same Download PDF

Info

Publication number
KR102466723B1
KR102466723B1 KR1020220055488A KR20220055488A KR102466723B1 KR 102466723 B1 KR102466723 B1 KR 102466723B1 KR 1020220055488 A KR1020220055488 A KR 1020220055488A KR 20220055488 A KR20220055488 A KR 20220055488A KR 102466723 B1 KR102466723 B1 KR 102466723B1
Authority
KR
South Korea
Prior art keywords
gold foil
plating layer
copper plate
foil printing
nickel plating
Prior art date
Application number
KR1020220055488A
Other languages
Korean (ko)
Inventor
이수호
Original Assignee
이수호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이수호 filed Critical 이수호
Priority to KR1020220055488A priority Critical patent/KR102466723B1/en
Application granted granted Critical
Publication of KR102466723B1 publication Critical patent/KR102466723B1/en

Abstract

A gold foil printing plate according to the present invention comprises: a copper plate having concavo-convex portions formed on one surface for gold foil printing; a nickel plating layer formed on the surface of the copper plate; and a chrome plating layer formed on the surface of the nickel plating layer. In addition, the gold foil printing plate manufacturing method according to the present invention comprises: a first step of manufacturing a copper plate having concavo-convex portions formed on one surface for gold foil printing; a second step of forming a nickel plating layer on the surface of the copper plate; and a third step of forming a chrome plating layer on the surface of the nickel plating layer. The gold foil printing plate according to the present invention has a high surface roughness, so that the brilliance of the gold foil increases during gold foil printing. Even when heated to high temperatures, the same does not expand significantly. Not only can the service life be extended, but also the quality of the printed gold foil can be improved. In addition, if a gold foil printing plate manufacturing method according to the present invention is used, a gold foil printing plate having high surface roughness and low malleability can be manufactured by adding only a plating process to a conventional gold foil printing plate. Thus, high-quality gold foil printing plates can be produced at low manufacturing costs.

Description

금박인쇄판 및 그 제조방법 {Gold foil printing plates and manufacturing methode of the same}Gold foil printing plates and manufacturing method thereof {Gold foil printing plates and manufacturing methode of the same}

본 발명은 금박인쇄판 및 그 제조방법에 관한 것으로, 더 상세하게는 인쇄된 금박의 광채를 높일 수 있고 고열로 가열되더라도 크게 늘어나지 아니하여 내구성이 우수한 금박인쇄판 및 그 제조방법에 관한 것이다.The present invention relates to a gold foil printing plate and a method for manufacturing the same, and more particularly, to a gold foil printing plate capable of increasing the brilliance of printed gold foil and having excellent durability because it does not greatly stretch even when heated to a high temperature, and a manufacturing method thereof.

책자 표지, 카드, 인사장, 상장, 상장 케이스 등을 인쇄할 때, 시각 효과와 미감을 높이기 위해, 문자나 문양의 전부 또는 일부를 금박으로 인쇄하는 금박인쇄 기법이 널리 이용되고 있다.When printing book covers, cards, greeting cards, certificates, award cases, etc., gold leaf printing techniques in which all or part of letters or patterns are printed with gold foil are widely used in order to enhance visual effects and aesthetics.

일반적으로 금박인쇄장치는 열과 압력을 가하여 금박필름을 인쇄 대상물에 들러붙게 하도록 구성되며, 고온으로 압력을 가하는 금박인쇄판과, 패턴 성형부, 스테이지, 금박필름 공급부, 대상물 고정부 등을 포함할 수 있다. 금박인쇄장치는 스테이지에 대상물 고정부를 이용하여 인쇄 대상물을 고정시킨 후, 금박필름 공급부를 통해 금박필름을 인쇄 대상물로 공급한다. 패턴 성형부는 고온으로 가열된 금박인쇄판 중 금박필름이 부착된 측을 인쇄 대상물에 가압함으로써, 금박필름을 인쇄 대상물에 열압착시키게 된다.In general, a gold foil printing device is configured to attach a gold foil film to an object by applying heat and pressure, and may include a gold foil printing plate that applies pressure at a high temperature, a pattern forming unit, a stage, a gold foil film supply unit, an object fixing unit, and the like. . The gold foil printing apparatus fixes an object to be printed on a stage using an object fixing unit, and then supplies the gold foil film to the printing object through a gold foil film supply unit. The pattern forming unit heat-compresses the gold foil film to the object to be printed by pressing the side of the gold foil printing plate heated to a high temperature to which the gold foil film is attached to the object to be printed.

이때, 금박인쇄판은 통상적으로 열전도성이 높은 순동으로 제작되는데, 순동으로 제작되는 금박인쇄판은 표면의 조도를 높이는데 한계가 있으므로 금박 인쇄 시 금박의 광채가 떨어지는 단점이 있다. 또한, 순동으로 제작되는 금박인쇄판은 외부로부터 열이 인가되었을 때 쉽게 늘어나는 특성이 있는바, 변형이 유발되고 수명이 짧아진다는 단점도 있다.At this time, the gold leaf printing plate is usually made of pure copper with high thermal conductivity. Since the gold leaf printing plate made of pure copper has a limitation in increasing the surface roughness, there is a disadvantage in that the brilliance of the gold leaf is lowered during gold leaf printing. In addition, since the gold foil printing plate made of pure copper has a property of being easily stretched when heat is applied from the outside, there are disadvantages in that deformation is induced and life is shortened.

KRKR 10-1969210 10-1969210 B1B1

본 발명은 상기와 같은 문제점을 해결하기 위하여 제안된 것으로, 표면 조도를 높여 금박 인쇄 시 금박의 광채를 높일 수 있고, 고온으로 가열되었을 때 크게 늘어나지 아니하도록 전성을 줄일 수 있으며, 사용수명이 증가될 수 있는 금박인쇄판 및 그 제조방법을 제공하는데 목적이 있다.The present invention has been proposed to solve the above problems, and it is possible to increase the brilliance of gold foil when printing gold foil by increasing the surface roughness, reduce the malleability so that it does not greatly increase when heated to a high temperature, and increase the service life. It is an object of the present invention to provide a gold foil printing plate and a manufacturing method thereof.

상기와 같은 목적을 달성하기 위한 본 발명에 의한 금박인쇄판은, 금박 인쇄를 위한 요철부가 일면에 형성되는 동판; 상기 동판의 표면에 형성되는 니켈도금층; 상기 니켈도금층의 표면에 형성되는 크롬도금층;을 포함하여 구성된다.A gold leaf printing plate according to the present invention for achieving the above object includes a copper plate having concavo-convex portions for gold leaf printing formed on one surface; a nickel plating layer formed on the surface of the copper plate; and a chrome plating layer formed on the surface of the nickel plating layer.

상기 동판의 표면에는 미세스크래치가 형성되고, 상기 니켈도금층은 상기 미세스크래치가 형성된 부위를 덮도록 도금되며, 상기 크롬도금층은 상기 니켈도금층의 표면을 덮도록 도금된다.Fine scratches are formed on the surface of the copper plate, the nickel plating layer is plated to cover the portion where the fine scratches are formed, and the chrome plating layer is plated to cover the surface of the nickel plating layer.

상기 동판이 압입되는 규격의 안착홈을 구비하는 지지유닛을 더 포함하고, 상기 니켈도금층과 크롬도금층은 상기 동판이 상기 안착홈에 압입된 이후, 상기 동판과 지지유닛의 외측면을 덮도록 도금된다.A support unit having a seating groove of a standard into which the copper plate is press-fitted, wherein the nickel plating layer and the chrome plating layer are plated to cover outer surfaces of the copper plate and the support unit after the copper plate is press-fitted into the seating groove. .

상기 동판의 외측 가장자리를 둘러싸는 프레임 형상의 지지유닛을 더 포함하고, 상기 니켈도금층과 크롬도금층은 상기 동판과 지지유닛의 외측면을 덮도록 도금된다.A frame-shaped support unit surrounding an outer edge of the copper plate is further included, and the nickel plating layer and the chrome plating layer are plated to cover outer surfaces of the copper plate and the support unit.

본 발명에 의한 금박인쇄판 제조방법은, 금박 인쇄를 위한 요철부가 일면에 형성되는 동판을 제작하는 제1 단계; 상기 동판의 표면에 니켈도금층을 형성하는 제2 단계; 상기 니켈도금층의 표면에 크롬도금층을 형성하는 제3 단계;를 포함한다.A method for manufacturing a gold-foil printing plate according to the present invention includes a first step of manufacturing a copper plate having concave-convex portions formed on one surface for gold-foil printing; a second step of forming a nickel plating layer on the surface of the copper plate; and a third step of forming a chrome plating layer on the surface of the nickel plating layer.

상기 제1 단계는, 상기 요철부의 표면에 미세스크래치를 형성하는 과정을 더 포함한다.The first step may further include forming micro-scratches on the surface of the concavo-convex part.

상기 제2 단계는, 상기 동판의 가장자리를 지지하는 지지유닛을 장착하는 과정과, 상기 동판과 지지유닛의 외측면에 니켈도금층을 형성하는 과정으로 구성된다.The second step includes a process of mounting a support unit supporting an edge of the copper plate and a process of forming a nickel plating layer on the outer surface of the copper plate and the support unit.

본 발명에 의한 금박인쇄판은, 표면 조도가 높아 금박 인쇄 시 금박의 광채가 높아지고, 고온으로 가열되더라도 크게 늘어나지 아니하므로 사용수명이 길어질 뿐만 아니라 인쇄된 금박의 품질을 개선시킬 수 있다는 장점이 있다.The gold foil printing plate according to the present invention has a high surface roughness, so the brilliance of the gold leaf increases during gold leaf printing, and it does not greatly increase even when heated to a high temperature, so it has a long service life and improves the quality of the printed gold leaf.

또한, 본 발명에 의한 금박인쇄판 제조방법을 이용하면 종래의 금박인쇄판에 도금을 하는 과정만을 추가하여 표면 조도가 높고 전성이 낮은 금박인쇄판을 제작할 수 있으므로 낮은 제조비용으로 고품질의 금박인쇄판을 제작할 수 있다는 장점이 있다.In addition, by using the gold foil printing plate manufacturing method according to the present invention, a gold foil printing plate having high surface roughness and low malleability can be manufactured by adding only a process of plating to a conventional gold foil printing plate, so that a high quality gold foil printing plate can be manufactured at a low manufacturing cost. There are advantages.

도 1 내지 도 4는 본 발명에 의한 금박인쇄판의 제조하는 과정을 순차적으로 도시한다.
도 5 및 도 6은 본 발명에 의한 금박인쇄판 제2 실시예의 제조 과정을 순차적으로 도시한다.
도 7 내지 도 9는 본 발명에 의한 금박인쇄판 제3 실시예의 제조 과정을 순차적으로 도시한다.
도 10은 본 발명에 의한 금박인쇄판 제4 실시예의 단면도이다.1 to 4 sequentially show a process of manufacturing a gold foil printing plate according to the present invention.
5 and 6 sequentially show the manufacturing process of the second embodiment of the gold foil printing plate according to the present invention.
7 to 9 sequentially show the manufacturing process of the third embodiment of the gold foil printing plate according to the present invention.
10 is a cross-sectional view of a fourth embodiment of a gold foil printing plate according to the present invention.

이하 첨부된 도면을 참조하여 본 발명에 의한 금박인쇄판 및 그 제조방법의 실시예를 상세히 설명한다.Hereinafter, embodiments of a gold foil printing plate and a manufacturing method thereof according to the present invention will be described in detail with reference to the accompanying drawings.

도 1 내지 도 4는 본 발명에 의한 금박인쇄판의 제조하는 과정을 순차적으로 도시한다.1 to 4 sequentially show a process of manufacturing a gold foil printing plate according to the present invention.

본 발명에 의한 금박인쇄판은 책자 표지, 카드, 인사장, 상장, 상장 케이스 등을 인쇄할 때 시각 효과와 미감을 높이기 위해 문자나 문양의 전부 또는 일부를 금박으로 인쇄하는 인쇄판의 하나로서, 인쇄대상 종이에 금박필름을 고온 고압으로 가압하는 용도로 사용된다.The gold foil printing plate according to the present invention is one of the printing plates in which all or part of characters or patterns are printed with gold foil to enhance visual effects and aesthetics when printing book covers, cards, greeting cards, certificates, certificate cases, etc. It is used for pressurizing gold foil film on paper at high temperature and high pressure.

이때, 상기 언급한 바와 같이 금박을 인쇄하는 용도로 활용되는 인쇄판은, 순동(純銅)과 같이 열을 잘 전달하도록 전도성이 높으면서도 금박필름을 고압으로 가압할 수 있도록 기준치 이상의 강도를 갖는 금속으로 제작된다. 이와 같이 금박인쇄판이 순동으로 제작되는 경우 금박인쇄판의 표면을 매끄럽게 가공하는데 한계가 있으므로 즉, 금박인쇄판의 표면 조도를 높이는데 한계가 있으므로, 순동으로 제작된 금박인쇄판으로 금박필름을 가압하였을 때 금박필름의 표면이 매끄럽지 못하여 인쇄된 금박의 광채가 떨어지게 되는 문제가 발생한다.At this time, as mentioned above, the printing plate used for printing the gold leaf is made of a metal having high conductivity such as pure copper to transmit heat well and having strength above the standard value so that the gold foil film can be pressurized with high pressure. do. In this way, when the gold foil printing plate is made of pure copper, there is a limit to smooth processing of the surface of the gold foil printing plate, that is, there is a limit to increasing the surface roughness of the gold foil printing plate. There is a problem that the brilliance of the printed gold foil falls because the surface is not smooth.

물론, 상기 금박인쇄판을 매끄럽게 제작하면 즉, 알루미늄 등과 같이 표면조도를 높게 가공할 수 있는 재료로 금박인쇄판을 제작하면 인쇄된 금박의 채광을 높일 수는 있으나, 제조 비용이 높아질 뿐만 아니라 금박인쇄판의 전체적인 경도가 떨어져 수명이 짧아진다는 문제가 발생하게 된다.Of course, if the gold leaf printing plate is made smoothly, that is, if the gold leaf printing plate is made of a material that can be processed to have a high surface roughness, such as aluminum, the mining of the printed gold leaf can be increased, but the manufacturing cost is increased and the overall quality of the gold foil printing plate is increased. A decrease in hardness causes a problem in that life is shortened.

본 발명에 의한 금박인쇄판은 이와 같은 문제점을 해결할 수 있도록 즉, 표면을 매끄럽게 가공할 수 있으면서 전체적인 제품의 경도를 높여 수명을 연장시킬 수 있도록, 금박필름을 가압하는 요철부(110)가 일면에 형성되는 동판(100)과, 상기 동판(100)의 표면에 형성되는 니켈도금층(200)과, 상기 니켈도금층(200)의 표면에 형성되는 크롬도금층(300)을 포함하여 구성된다.The gold foil printing plate according to the present invention has a concave-convex portion 110 for pressurizing the gold foil film formed on one surface to solve the above problems, that is, to increase the hardness of the overall product and extend the life while smoothing the surface. It is configured to include a copper plate 100, a nickel plating layer 200 formed on the surface of the copper plate 100, and a chrome plating layer 300 formed on the surface of the nickel plating layer 200.

본 발명에 의한 금박인쇄판을 제작할 때에는 먼저 도 1에 도시된 바와 같이 금박필름을 가압할 요철부(110)를 구비하는 동판(100)을 먼저 제작한다. 이때 상기 동판(100)은 도 2에 도시된 바와 같이 전체가 순동으로 제작되는데, 이와 같이 순동으로 제작되는 인쇄판은 종래에도 다양한 용도로 상용화되어 있으므로 상기 동판(100)을 제작하는 과정에 대한 상세한 설명은 생략한다.When manufacturing a gold foil printing plate according to the present invention, first, as shown in FIG. At this time, the copper plate 100 is entirely made of pure copper as shown in FIG. 2. Since the printing plate made of pure copper has been commercialized for various purposes in the past, detailed description of the process of manufacturing the copper plate 100 is omitted.

동판(100)의 제작이 완료되면, 도 3에 도시된 바와 같이 상기 동판(100)의 표면에 니켈도금층(200)을 형성한 후, 크롬도금층(300)을 니켈도금층 상에 형성한다. 이때 상기 크롬도금층(300)은 동판(100)보다 경도가 높으면서 표면조도가 높도록 제작되는바, 최종적으로 제작이 완료된 금박인쇄판은 도 4에 도시된 바와 같이 표면이 매우 매끄러운 상태가 되어 금박필름을 인쇄하였을 때 금박의 채광이 현저히 높아지는 효과를 얻을 수 있게 된다. 또한 크롬도금층(300)은 일반 금속에 비해 경도가 매우 높으므로 본 발명에 의한 금박인쇄판을 수 회에 걸쳐 반복 사용하더라도 변형의 우려가 매우 낮아 상기 금박인쇄판의 수명이 현저히 길어지는 효과도 얻을 수 있게 된다.When the manufacturing of the copper plate 100 is completed, as shown in FIG. 3 , after forming the nickel plating layer 200 on the surface of the copper plate 100, the chrome plating layer 300 is formed on the nickel plating layer. At this time, the chrome plating layer 300 is manufactured to have a higher hardness and higher surface roughness than the copper plate 100, and the gold foil printing plate finally manufactured has a very smooth surface as shown in FIG. 4, thereby forming a gold foil film. When printed, it is possible to obtain the effect of remarkably increasing the mining of gold foil. In addition, since the chrome plating layer 300 has a very high hardness compared to general metal, even if the gold foil printing plate according to the present invention is repeatedly used several times, the risk of deformation is very low, so that the life of the gold foil printing plate can be significantly extended. do.

한편, 상기 크롬도금층(300)은 동판(100)에 비해 경도가 높다는 특성이 있으므로, 최종적으로 제작된 금박인쇄판은 전체적으로 전성이 낮아지는 특성을 갖게 된다. 이와 같이 금박인쇄판의 전성이 낮아지면 금박을 인쇄하는 과정에서 고온으로 가열되었을 때 팽창률이 낮아지므로 금박 인쇄물의 정밀도를 높일 수 있을 뿐만 아니라, 열팽창 및 열수축에 의한 제품 수명이 급격하게 단축되는 문제를 해결할 수 있게 된다.On the other hand, since the chrome plating layer 300 has a higher hardness than the copper plate 100, the finally manufactured gold foil printing plate has a lower malleability as a whole. In this way, if the malleability of the gold foil printing plate is lowered, the expansion rate is lowered when heated to a high temperature in the process of printing the gold foil, so that the precision of the gold leaf printed material can be improved, and the problem of rapidly shortening the product life due to thermal expansion and contraction can be solved. be able to

도 5 및 도 6은 본 발명에 의한 금박인쇄판 제2 실시예의 제조 과정을 순차적으로 도시한다.5 and 6 sequentially show the manufacturing process of the second embodiment of the gold foil printing plate according to the present invention.

본 발명에 의한 금박인쇄판은 동판(100)으로부터 니켈도금층(200)이 박리될 우려는 낮출 수 있도록 즉, 동판(100)과 도금층(300) 간의 결합력을 높일 수 있도록, 도 5에 도시된 바와 같이 상기 동판(100)의 표면에 미세스크래치를 형성한 후, 미세스크래치가 형성된 면에 니켈도금층(200)을 형성한 후 크롬도금층(300)이 형성되도록 구성될 수 있다.As shown in FIG. 5, the gold foil printing plate according to the present invention can reduce the possibility of peeling of the nickel-plated layer 200 from the copper plate 100, that is, to increase the bonding strength between the copper plate 100 and the plating layer 300. After forming fine scratches on the surface of the copper plate 100, the nickel plating layer 200 may be formed on the surface where the fine scratches are formed, and then the chrome plating layer 300 may be formed.

이와 같이 동판(100)의 표면에 미세스크래치를 형성하면, 니켈도금층(200)과 동판(100) 간의 결합력이 현저히 향상되는바, 고온 고압의 환경에서 본 발명에 의한 금박인쇄판을 장시간 사용하더라도 니켈도금층(200) 및 크롬도금층(300)이 벗겨지는 현상을 감소시킬 수 있다는 장점이 있다.When fine scratches are formed on the surface of the copper plate 100 in this way, the bonding strength between the nickel-plated layer 200 and the copper plate 100 is remarkably improved, even if the gold foil printing plate according to the present invention is used for a long time in a high-temperature and high-pressure environment. (200) and the chrome plating layer (300) has the advantage of being able to reduce the peeling phenomenon.

이때, 도 5 및 도 6에서는 미세스크래치를 명확하게 나타내기 위해 상기 동판(100)에 형성되는 미세스크래치 크기를 매우 크게 도시하고 있으나, 상기 동판(100) 표면에 형성되는 미세스크래치는 육안으로 확인하기 어려울 정도의 크기로 작게 형성되어야 할 것이다.5 and 6 show the size of the micro-scratches formed on the copper plate 100 as very large in order to clearly show the micro-scratches, but the micro-scratches formed on the surface of the copper plate 100 are difficult to visually check. It will have to be formed in a small enough size to be difficult.

도 7 내지 도 9는 본 발명에 의한 금박인쇄판 제3 실시예의 제조 과정을 순차적으로 도시한다.7 to 9 sequentially show the manufacturing process of the third embodiment of the gold foil printing plate according to the present invention.

본 발명에 의한 금박인쇄판은 상기 동판(100)의 전성 및 열팽창이 물리적으로 억제될 수 있도록 상기 동판(100)을 가압하는 별도의 지지유닛(400)을 추가로 구비할 수 있다.The gold foil printing plate according to the present invention may further include a separate support unit 400 that presses the copper plate 100 so that malleability and thermal expansion of the copper plate 100 can be physically suppressed.

상기 지지유닛(400)은 도 7에 도시된 바와 같이 상기 동판(100)이 압입되는 규격의 안착홈(410)을 구비하도록 제작되고, 상기 동판(100)은 상기 안착홈(410)에 끼워맞춤 방식으로 압입되도록 상기 지지유닛(400)과 일체로 결합된다.As shown in FIG. 7 , the support unit 400 is manufactured to have a seating groove 410 of a standard into which the copper plate 100 is press-fitted, and the copper plate 100 is fitted into the seating groove 410. It is integrally coupled with the support unit 400 so as to be press-fitted in a manner.

이때 상기 지지유닛(400)은 강철 등과 같이 동판(100)에 비해 전성과 열팽창률이 낮은 재료로 제작되므로, 도 8에 도시된 바와 같이 상기 동판(100)이 지지유닛(400)의 안착홈(410)에 압입되면, 상기 동판(100)은 가열되더라도 폭방향으로 늘어나지 못하게 되므로 인쇄하고자 하는 금박의 규격이 일정하게 유지되는 효과 즉, 금박의 인쇄 정밀도가 향상되는 효과를 얻을 수 있게 된다.At this time, since the support unit 400 is made of a material having a lower malleability and coefficient of thermal expansion than the copper plate 100, such as steel, the copper plate 100 is a seating groove of the support unit 400 as shown in FIG. 410), since the copper plate 100 does not stretch in the width direction even when heated, the effect of maintaining the standard of the gold leaf to be printed constant, that is, the effect of improving the printing accuracy of the gold leaf can be obtained.

이때, 동판(100)과 지지유닛(400)의 접촉면 사이로 이물질이 유입되지 아니하도록, 상기 니켈도금층(200) 및 크롬도금층(300)은 상기 동판(100)이 상기 안착홈(410)에 압입된 이후 상기 동판(100)과 지지유닛(400)의 외측면을 덮도록 도금됨이 바람직하다.At this time, the nickel plating layer 200 and the chrome plating layer 300 are press-fitted into the seating groove 410 so that foreign matter does not flow between the contact surface of the copper plate 100 and the support unit 400. Afterwards, it is preferable to plate the outer surfaces of the copper plate 100 and the support unit 400 .

도 10은 본 발명에 의한 금박인쇄판 제4 실시예의 단면도이다.10 is a cross-sectional view of a fourth embodiment of a gold foil printing plate according to the present invention.

도 9에 도시된 바와 같이 동판(100)이 지지유닛(400)의 안착홈(410)에 압입되로록 구성되면, 상기 동판(100)의 팽창은 방지될 수 있지만 상기 동판(100) 중 요철부(110)가 형성된 면의 반대측면이 지지유닛(400)이 의해 가려지므로 상기동판(100)으로 열을 전도하는 방법에 어려움이 있을 수 있다.As shown in FIG. 9 , when the copper plate 100 is configured to be press-fitted into the seating groove 410 of the support unit 400, the expansion of the copper plate 100 can be prevented, but the unevenness of the copper plate 100 Since the side opposite to the side where the portion 110 is formed is covered by the support unit 400, it may be difficult to conduct heat to the copper plate 100.

따라서 본 발명에 의한 금박인쇄판은 동판(100)의 전성 및 열팽창율을 낮출 수 있으면서 상기 동판(100)으로의 열전달을 용이하게 할 수 있도록, 도 10에 도시된 바와 같이 상기 지지유닛(400)이 상기 동판(100)의 외측 가장자리만을 둘러싸는 프레임 형상으로 제작될 수 있다.Therefore, in the gold foil printing plate according to the present invention, as shown in FIG. 10, the support unit 400 can facilitate heat transfer to the copper plate 100 while reducing the malleability and thermal expansion of the copper plate 100. It may be manufactured in a frame shape surrounding only the outer edge of the copper plate 100 .

이와 같이 상기 지지유닛(400)이 가운데가 개방된 프레임 형상으로 형성되면, 상기 동판(100)이 지지유닛(400)에 장착되었을 때 요철부(110)가 형성된 면의 반대면이 지지유닛(400)에 의해 가려지지 아니하므로, 작업자는 상기 동판(100)으로 열을 직접적으로 전달할 수 있어 상기 동판(100)의 가열시간을 단축시킬 수 있다는 장점이 있다.In this way, when the support unit 400 is formed in a frame shape with an open center, when the copper plate 100 is mounted on the support unit 400, the surface opposite to the surface on which the concavo-convex part 110 is formed is the support unit 400. ), the operator can directly transfer heat to the copper plate 100, thereby shortening the heating time of the copper plate 100.

물론, 본 실시예에 도시된 바와 같이 상기 지지윤닛이 프레임 형상으로 제작되는 경우에 있어서도 상기 동판(100)과 지지유닛(400) 사이에 틈새가 발생하지 아니하도록, 상기 니켈도금층(200) 및 크롬도금층(300)은 상기 동판(100)과 지지유닛(400)의 외측면 전체를 덮도록 도금됨이 바람직하다.Of course, as shown in the present embodiment, even when the support unit is manufactured in a frame shape, the nickel plating layer 200 and the chrome plated layer 200 do not create a gap between the copper plate 100 and the support unit 400. The plating layer 300 is preferably plated to cover the entire outer surfaces of the copper plate 100 and the support unit 400 .

이상, 본 발명을 바람직한 실시예를 사용하여 상세히 설명하였으나, 본 발명의 범위는 특정 실시예에 한정되는 것은 아니며, 첨부된 특허청구범위에 의하여 해석되어야 할 것이다. 또한, 이 기술분야에서 통상의 지식을 습득한 자라면, 본 발명의 범위에서 벗어나지 않으면서도 많은 수정과 변형이 가능함을 이해하여야 할 것이다.In the above, the present invention has been described in detail using preferred embodiments, but the scope of the present invention is not limited to specific embodiments, and should be interpreted according to the appended claims. In addition, those skilled in the art should understand that many modifications and variations are possible without departing from the scope of the present invention.

100 : 동판 110 : 요철부
200 : 니켈도금층 300 : 크롬도금층
400 : 지지유닛 410 : 안착홈100: copper plate 110: uneven portion
200: nickel plating layer 300: chrome plating layer
400: support unit 410: seating groove

Claims (7)

금박 인쇄를 위한 요철부(110)가 일면에 형성되는 동판(100);
상기 동판(100)의 표면에 형성되는 니켈도금층(200);
상기 니켈도금층(200)의 표면에 형성되는 크롬도금층(300);
을 포함하여 구성되며,
상기 동판(100)의 표면에는 미세스크래치가 형성되고,
상기 니켈도금층(200)은 상기 미세스크래치가 형성된 부위를 덮도록 도금되며,
상기 크롬도금층(300)은 상기 니켈도금층(200)의 표면을 덮도록 도금되는 것을 특징으로 하는 금박인쇄판.
A copper plate 100 having concave-convex portions 110 for gold leaf printing formed on one surface;
a nickel plating layer 200 formed on the surface of the copper plate 100;
a chrome plating layer 300 formed on the surface of the nickel plating layer 200;
It consists of,
Fine scratches are formed on the surface of the copper plate 100,
The nickel plating layer 200 is plated to cover the portion where the micro scratches are formed,
The chromium plating layer 300 is plated to cover the surface of the nickel plating layer 200, characterized in that the gold foil printing plate.
 삭제delete 제1항에 있어서,
상기 동판(100)이 압입되는 규격의 안착홈(410)을 구비하는 지지유닛(400)을 더 포함하고,
상기 니켈도금층(200)과 크롬도금층(300)은 상기 동판(100)이 상기 안착홈(410)에 압입된 이후, 상기 동판(100)과 지지유닛(400)의 외측면을 덮도록 도금되는 것을 특징으로 하는 금박인쇄판.
According to claim 1,
Further comprising a support unit 400 having a seating groove 410 of a standard into which the copper plate 100 is press-fitted,
The nickel plating layer 200 and the chrome plating layer 300 are plated to cover the outer surfaces of the copper plate 100 and the support unit 400 after the copper plate 100 is press-fitted into the seating groove 410. Characterized by a gold foil printing plate.
 제1항에 있어서,
상기 동판(100)의 외측 가장자리를 둘러싸는 프레임 형상의 지지유닛(400)을 더 포함하고,
상기 니켈도금층(200)과 크롬도금층(300)은 상기 동판(100)과 지지유닛(400)의 외측면을 덮도록 도금되는 것을 특징으로 하는 금박인쇄판.
According to claim 1,
Further comprising a frame-shaped support unit 400 surrounding an outer edge of the copper plate 100,
The nickel plating layer 200 and the chrome plating layer 300 are plated so as to cover the outer surfaces of the copper plate 100 and the support unit 400.
 금박 인쇄를 위한 요철부(110)가 일면에 형성되는 동판(100)을 제작하는 제1 단계;
상기 동판(100)의 표면에 니켈도금층(200)을 형성하는 제2 단계;
상기 니켈도금층(200)의 표면에 크롬도금층(300)을 형성하는 제3 단계;
를 포함하며,
상기 제1 단계는,
상기 요철부(110)의 표면에 미세스크래치를 형성하는 과정을 더 포함하는 것을 특징으로 하는 금박인쇄판 제조방법.
A first step of manufacturing a copper plate 100 having concave-convex portions 110 for gold foil printing formed on one surface;
A second step of forming a nickel plating layer 200 on the surface of the copper plate 100;
A third step of forming a chrome plating layer 300 on the surface of the nickel plating layer 200;
Including,
The first step is
The manufacturing method of the gold foil printing plate, characterized in that it further comprises a process of forming fine scratches on the surface of the uneven portion (110).
 삭제delete 제5항에 있어서,
상기 제2 단계는,
상기 동판(100)의 가장자리를 지지하는 지지유닛(400)을 장착하는 과정과, 상기 동판(100)과 지지유닛(400)의 외측면에 니켈도금층(200)을 형성하는 과정으로 구성되는 것을 특징으로 하는 금박인쇄판 제조방법.According to claim 5,
The second step,
It is characterized by the process of mounting the support unit 400 supporting the edge of the copper plate 100 and the process of forming the nickel plating layer 200 on the outer surfaces of the copper plate 100 and the support unit 400. A method for manufacturing a gold foil printing plate.
KR1020220055488A 2022-05-04 2022-05-04 Gold foil printing plates and manufacturing methode of the same KR102466723B1 (en)