KR102441848B1 - Resin compostion for waterproof sheet and waterproof sheet comprising thereof - Google Patents
Resin compostion for waterproof sheet and waterproof sheet comprising thereof Download PDFInfo
- Publication number
- KR102441848B1 KR102441848B1 KR1020210086862A KR20210086862A KR102441848B1 KR 102441848 B1 KR102441848 B1 KR 102441848B1 KR 1020210086862 A KR1020210086862 A KR 1020210086862A KR 20210086862 A KR20210086862 A KR 20210086862A KR 102441848 B1 KR102441848 B1 KR 102441848B1
- Authority
- KR
- South Korea
- Prior art keywords
- waterproof sheet
- resin composition
- sheet
- weight
- parts
- Prior art date
Abstract
Description
본 발명은 방수시트용 수지 조성물 및 상기 수지 조성물을 포함하는 방수시트에 관한 것으로서, 더욱 상세하게는, 수축율이 개선된 방수시트용 수지 조성물 및 상기 수지 조성물을 포함하여 방수 시공 후의 말림 현상(side-up) 발생이 억제된 방수시트에 관한 것이다.The present invention relates to a resin composition for a waterproof sheet and a waterproof sheet comprising the resin composition, and more particularly, to a resin composition for a waterproof sheet with improved shrinkage and a curling phenomenon after waterproofing construction including the resin composition (side- up) It relates to a waterproof sheet with suppressed occurrence.
일반적으로 건축물의 옥상이나 아스팔트 시공 과정에서 방수 시공을 할 때, 바탕면에 프라이머를 형성시킨 후 부직포를 포설하고, 상기 부직포 상에 방수도막을 직접 도포하는 공정을 적용하고 있다. 또한, 최근에는 이러한 방수도막 도포 공정의 효율을 개선하기 위하여 방수시트를 사용하여 방수 시공을 실시하고 있다.In general, when waterproofing construction on the roof or asphalt of a building, a primer is formed on the base surface, then a nonwoven fabric is laid, and a process of directly applying a waterproofing film on the nonwoven fabric is applied. In addition, in recent years, in order to improve the efficiency of such a waterproof coating coating process, waterproofing is carried out using a waterproofing sheet.
방수시트는 두께가 1 내지 3㎜, 폭이 100 내지 130㎝ 정도의 수지 조성물로 제조된 시트로서 시공할 바닥면에 방수시트 롤을 풀어 덮게 된다. 이 경우, 현장 시공 후 방수시트의 말단 부분이 위로 말려 올라가는 현상이 발생하게 되며, 이로 인하여 작업자가 방수시트를 바닥면에 펴주기 위한 작업을 수행해야 하므로 시공 효율이 저하되는 문제점이 있다.The waterproof sheet is a sheet made of a resin composition having a thickness of 1 to 3 mm and a width of 100 to 130 cm. In this case, a phenomenon occurs in which the distal end of the waterproof sheet is rolled up after on-site construction, and therefore, the operator has to perform a work to spread the waterproof sheet on the floor, thereby reducing the construction efficiency.
이러한 말림 현상을 방지하기 위하여 대한민국 등록특허공보 10-2038306호에서는 자착식 방수시트에 알루미늄층을 적층하여 방수시트에 소정의 강성을 부가함으로써 말림 및 울음 등을 억제하고 있다. 또한, 대한민국 등록특허공보 10-1226643호에서는 방수시트를 구성하는 제1합성섬유 부직포 두께와 제2합성섬유 부직포의 두께 비율은 1:0.1 내지 1:1로 하여 방수시트의 말림을 방지하고 있다.In order to prevent such a curling phenomenon, Korean Patent No. 10-2038306 suppresses curling and crying by laminating an aluminum layer on a self-adhesive waterproof sheet and adding a predetermined rigidity to the waterproof sheet. In addition, in Korean Patent No. 10-1226643, the thickness ratio of the first synthetic fiber nonwoven fabric and the second synthetic fiber nonwoven fabric constituting the waterproof sheet is 1:0.1 to 1:1 to prevent the waterproof sheet from curling.
이러한 종래기술들은 방수시트의 말림 현상을 억제하기 위하여 적층구조나 적층방법을 개선하고 있으나, 단층으로 이루어진 방수시트의 경우 이러한 말림 현상을 억제하기 어려운 문제점이 있다.Although these prior arts improve the lamination structure or lamination method in order to suppress the curling phenomenon of the waterproof sheet, there is a problem in that it is difficult to suppress the curling phenomenon in the case of the waterproof sheet made of a single layer.
본 발명은 상기와 같은 종래기술의 문제점을 해결하기 위하여 안출된 것으로, 방수시트의 수축율을 개선할 수 있는 수지 조성물을 제공하는 것을 그 목적으로 한다.The present invention has been devised to solve the problems of the prior art as described above, and an object of the present invention is to provide a resin composition capable of improving the shrinkage rate of a waterproof sheet.
또한, 상기 수지 조성물 이용함으로써 방수 시공 후의 말림 현상(side-up)을 억제할 수 있도록 한 방수시트를 제공하는 것을 그 목적으로 한다.In addition, an object of the present invention is to provide a waterproof sheet capable of suppressing a curling phenomenon (side-up) after waterproof construction by using the resin composition.
상기와 같은 과제를 해결하기 위한 본 발명의 방수시트용 수지 조성물은 폴리에틸렌(PE), 폴리프로필렌(PP), 에틸렌초산비닐(EVA), 폴리올레핀 엘라스토머(POE), 스티렌-에틸렌-부틸렌-스티렌 공중합체(SEBS), 에틸렌프로필렌 고무(EPR) 및 보강제로 이루어지는 것을 특징으로 한다.The resin composition for a waterproof sheet of the present invention for solving the above problems is polyethylene (PE), polypropylene (PP), ethylene vinyl acetate (EVA), polyolefin elastomer (POE), styrene-ethylene-butylene-styrene air It is characterized in that it consists of a composite (SEBS), ethylene propylene rubber (EPR) and a reinforcing agent.
이때, 상기 폴리에틸렌은 저밀도 폴리에틸렌(LDPE) 및 선형 저밀도 폴리에틸렌(LLDPE) 중 어느 하나 또는 이들의 혼합물일 수 있다.In this case, the polyethylene may be any one of low-density polyethylene (LDPE) and linear low-density polyethylene (LLDPE) or a mixture thereof.
또한, 상기 폴리에틸렌, 폴리프로필렌 및 에틸렌초산비닐 중 어느 하나 또는 그 이상은 재생 수지를 포함할 수 있다.In addition, any one or more of polyethylene, polypropylene, and ethylene vinyl acetate may include a recycled resin.
또한, 본 발명에 따른 방수시트는 기재시트, 상기 기재시트의 일면 또는 양면에 적층되는 점착층, 및 상기 점착층의 상부에 적층되는 이형시트로 이루어지는 것으로서, 상기 기재시트는 상기 수지 조성물로 이루어지는 것을 특징으로 한다.In addition, the waterproof sheet according to the present invention consists of a base sheet, an adhesive layer laminated on one or both sides of the base sheet, and a release sheet laminated on top of the adhesive layer, wherein the base sheet is made of the resin composition characterized.
본 발명에 따른 수지 조성물을 이용하면 방수시트의 수축율을 개선할 수 있으며, 이를 통해 방수시트를 사용하여 방수 시공할 때 시공 후의 말림 현상(side-up)을 억제할 수 있는 효과를 나타낸다.The use of the resin composition according to the present invention can improve the shrinkage rate of the waterproof sheet, thereby exhibiting the effect of suppressing the curling phenomenon (side-up) after construction when waterproofing using the waterproof sheet.
도 1은 본 발명에 따른 방수시트의 적층구조를 나타낸 개념도이다.
도 2는 실시예 1(a), 실시예 2(b), 비교예 1(c), 비교예 2(d)에 따른 방수시트의 말림 현상을 관찰한 사진이다.1 is a conceptual diagram showing a laminated structure of a waterproof sheet according to the present invention.
2 is a photograph observing the curling phenomenon of the waterproof sheet according to Example 1 (a), Example 2 (b), Comparative Example 1 (c), and Comparative Example 2 (d).
이하 본 발명을 보다 상세히 설명한다. 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.Hereinafter, the present invention will be described in more detail. The terms or words used in the present specification and claims are not to be construed as being limited to their ordinary or dictionary meanings, and the inventor may properly define the concept of the term in order to best describe his invention. Based on the principle that there is, it should be interpreted as meaning and concept consistent with the technical idea of the present invention.
본 발명의 방수시트용 수지 조성물은 폴리에틸렌(PE), 폴리프로필렌(PP), 에틸렌초산비닐(EVA), 폴리올레핀 엘라스토머(POE), 스티렌-에틸렌-부틸렌-스티렌 고무(SEBS), 에틸렌프로필렌 고무(EPR) 및 보강제로 이루어지는 것을 특징으로 한다. 상기 수지 조성물에서 각 성분의 조합은 방수시트로 성형 가공했을 때의 수축율을 고려한 것으로서, 상기 성분들이 적절하게 조합됨으로써 방수시트의 물성을 향상시킬 수 있게 된다.The resin composition for a waterproof sheet of the present invention is polyethylene (PE), polypropylene (PP), ethylene vinyl acetate (EVA), polyolefin elastomer (POE), styrene-ethylene-butylene-styrene rubber (SEBS), ethylene propylene rubber ( EPR) and a reinforcing agent. The combination of each component in the resin composition takes into account the shrinkage rate when molded into a waterproof sheet, and by appropriately combining the components, the physical properties of the waterproof sheet can be improved.
상기 수지 조성물은 폴리에틸렌, 폴리프로필렌 및 에틸렌초산비닐로 이루어진 수지 성분과 폴리올레핀 엘라스토머, 스티렌-에틸렌-부틸렌-스티렌 공중합체, 에틸렌프로필렌 고무로 이루어진 엘라스토머 성분 및 보강제로 이루어지는데, 상기 수지 성분은 방수시트로 제조했을 때의 말림 현상(side-up)을 고려하여 선택된 것이다.The resin composition consists of a resin component composed of polyethylene, polypropylene and ethylene vinyl acetate, an elastomer component composed of a polyolefin elastomer, a styrene-ethylene-butylene-styrene copolymer, an ethylene propylene rubber, and a reinforcing agent, wherein the resin component is a waterproof sheet It was selected in consideration of the curling phenomenon (side-up) when manufactured.
방수시트의 말림 현상은 시편을 제조한 후 말단이 시트의 수평면에 대해 들리는 정도를 마이크로미터 캘리퍼스로 측정한 비율로 구할 수 있는데, 일반적으로 수지 또는 수지 조성물을 190 내지 230℃의 온도에서 사출 성형하여 10×30㎝의 면적, 3㎜의 두께로 시편을 제조하고 24시간 경과한 후 실온에서 측정하게 된다. 이러한 측정 방법에 의해 말림 현상을 측정하면 폴리에틸렌 및 폴리프로필렌의 경우 16/1000 내지 18/1000㎜ 정도로 측정되며, 에틸렌초산비닐은 10/1000㎜ 정도로 측정된다. 또한, 수지 조성물을 성형하여 시편을 제조하면 12/1000 내지 13/1000㎜ 정도의 말림 현상이 나타나는 것으로 측정된다. 이에 대하여 본 발명의 수지 조성물을 적용하여 시편을 제조한 경우 3/1000 내지 5/1000㎜의 말림 현상이 측정되어 종래의 방수시트에 비해 말림 현상이 현저히 줄어드는 것을 확인할 수 있다.The curling phenomenon of the waterproof sheet can be obtained at a rate measured with a micrometer caliper to determine the degree to which the end is lifted with respect to the horizontal plane of the sheet after the specimen is prepared. A specimen with an area of 10 × 30 cm and a thickness of 3 mm is prepared and measured at room temperature after 24 hours have elapsed. When the curling phenomenon is measured by this measuring method, in the case of polyethylene and polypropylene, it is measured to be about 16/1000 to 18/1000 mm, and for ethylene vinyl acetate, it is measured to be about 10/1000 mm. In addition, when the specimen is prepared by molding the resin composition, it is measured that a curling phenomenon of about 12/1000 to 13/1000 mm appears. On the other hand, when the specimen is prepared by applying the resin composition of the present invention, the curling phenomenon of 3/1000 to 5/1000 mm is measured, and it can be confirmed that the curling phenomenon is significantly reduced compared to the conventional waterproof sheet.
상기 수지 성분을 구성하는 폴리에틸렌으로는 저밀도 폴리에틸렌(LDPE) 및 선형 저밀도 폴리에틸렌(LLDPE) 중 어느 하나를 사용할 수 있고, 저밀도 폴리에틸렌과 선형 저밀도 폴리에틸렌을 혼합하여 사용할 수도 있다. 저밀도 폴리에틸렌과 선형 저밀도 폴리에틸렌을 혼합하는 경우에는 0.5:1 내지 1:1의 중량비로 혼합하는 것이 바람직하며, 방수시트의 말림 현상과 내구성을 고려하여 상기 범위 내에서 혼합량을 적절히 조절할 수 있다.As the polyethylene constituting the resin component, any one of low-density polyethylene (LDPE) and linear low-density polyethylene (LLDPE) may be used, and a mixture of low-density polyethylene and linear low-density polyethylene may be used. When mixing low-density polyethylene and linear low-density polyethylene, it is preferable to mix them in a weight ratio of 0.5:1 to 1:1, and the mixing amount can be appropriately adjusted within the above range in consideration of the curling phenomenon and durability of the waterproof sheet.
폴리프로필렌, 저밀도 폴리에틸렌, 선형 저밀도폴리에틸렌, 고밀도폴리에틸렌, 에틸렌초산비닐, 폴레에틸렌 테레프탈레이트(PET) 등의 수지 성분은 대한민국 등록특허공보 10-1614749호 등에서 방수시트를 구성하는 수지 성분으로 공지된 것인데, 본 발명에서는 다양한 수지 성분들 중 폴리에틸렌, 폴리프로필렌 및 에틸렌초산비닐을 선택하여 조합함으로써 제조된 방수시트의 말림 현상이 개선되도록 하고 있다.Resin components such as polypropylene, low-density polyethylene, linear low-density polyethylene, high-density polyethylene, ethylene vinyl acetate, and polyethylene terephthalate (PET) are known as resin components constituting the waterproof sheet in Korean Patent Publication No. 10-1614749, etc. In the present invention, the curling phenomenon of the waterproof sheet manufactured by selecting and combining polyethylene, polypropylene and ethylene vinyl acetate among various resin components is improved.
구체적으로 상기 수지 성분은 폴리에틸렌 15 내지 20 중량부, 폴리프로필렌 15 내지 20 중량부 및 에틸렌초산비닐 20 내지 25 중량부로 이루어지는 것이 바람직하다. 상기 범위 내에서 상기 수지 성분들을 혼합함으로써 제조된 방수시트의 내구성을 확보하면서도 말림 현상이 개선되는 것으로 나타났다.Specifically, the resin component is preferably composed of 15 to 20 parts by weight of polyethylene, 15 to 20 parts by weight of polypropylene, and 20 to 25 parts by weight of ethylene vinyl acetate. It was found that the curling phenomenon was improved while ensuring the durability of the manufactured waterproof sheet by mixing the resin components within the above range.
또한, 상기 수지 성분을 구성하는 폴리에틸렌, 폴리프로필렌, 에틸렌초산비닐은 신재를 사용할 수 있으나, 재생 수지를 사용할 수도 있다. 재생 수지를 사용할 경우 전체 수지 성분을 재생 수지로 사용할 수도 있으며, 신재와 재생 수지를 혼합하여 사용할 수도 있다. 혼합 비율은 특별히 제한되지 않으며 방수시트의 물성을 저해하지 않는 범위 내에서 혼합될 수 있다.In addition, polyethylene, polypropylene, and ethylene vinyl acetate constituting the resin component may use a new material, but a recycled resin may also be used. In the case of using a recycled resin, the entire resin component may be used as the recycled resin, or a mixture of a new material and a recycled resin may be used. The mixing ratio is not particularly limited and may be mixed within a range that does not impair the physical properties of the waterproof sheet.
또한, 상기 수지 조성물은 폴리올레핀 엘라스토머, 스티렌-에틸렌-부틸렌-스티렌 공중합체 및 에틸렌프로필렌 고무로 이루어진 엘라스토머 성분을 함유한다. 상기 엘라스토머 성분을 함유함으로써 방수시트의 내구성 및 장기 신뢰성을 확보할 수 있고 방수 및 방근 특성을 얻을 수 있다.In addition, the resin composition contains an elastomer component consisting of a polyolefin elastomer, a styrene-ethylene-butylene-styrene copolymer, and an ethylenepropylene rubber. By containing the elastomer component, durability and long-term reliability of the waterproof sheet can be secured, and waterproof and rust-proof properties can be obtained.
본 발명에서는 수지 조성물의 물성을 고려하여 폴리올레핀 엘라스토머 15 내지 20 중량부, 스티렌-에틸렌-부틸렌-스티렌 공중합체 1 내지 5 중량부 및 에틸렌프로필렌 고무 5 내지 10 중량부로 이루어지도록 하는데, 상기 범위 내에서 상기 엘라스토머 성분을 형성함으로써 제조되는 방수시트의 내구성, 장기 신뢰성과 함께 양호한 방수 및 방근 특성을 얻을 수 있는 것으로 나타났다.In the present invention, 15 to 20 parts by weight of a polyolefin elastomer, 1 to 5 parts by weight of a styrene-ethylene-butylene-styrene copolymer, and 5 to 10 parts by weight of an ethylene propylene rubber in consideration of the physical properties of the resin composition. It was found that by forming the elastomer component, good waterproof and rustproof properties can be obtained along with durability and long-term reliability of the waterproof sheet manufactured.
또한, 상기 보강제는 수지 조성물의 흡착 성능을 높여 방수 특성을 향상시키기 위한 것으로 일반적으로 탈크가 사용되나, 본 발명에서는 비중과 가격을 고려하여 탄산칼슘(CaCO3)을 사용한다. 상기 보강제는 20 내지 25 중량부의 범위에서 사용될 수 있으며, 보강제의 함량이 지나치게 많거나 적은 경우 수지 조성물의 물성이 저하되기 때문에 상기 범위 내에서 사용되는 것이 적합하다.In addition, the reinforcing agent is for improving the water-repellent properties by increasing the adsorption performance of the resin composition, and talc is generally used, but in the present invention, calcium carbonate (CaCO 3 ) is used in consideration of specific gravity and price. The reinforcing agent may be used in the range of 20 to 25 parts by weight, and if the content of the reinforcing agent is too large or too small, the physical properties of the resin composition are deteriorated, so it is suitable to be used within the above range.
본 발명에 따른 방수시트는 상기와 같은 수지 조성물을 이용하여 제조되는 것으로서, 도 1에서와 같이 기재시트, 상기 기재시트에 적층되는 점착층 및 상기 점착층 상부에 적층되는 이형시트로 이루어질 수 있다. 이때, 도 1(a)에서와 같이 기재시트의 일면에 점착층을 형성하고 상기 점착층의 상부에 이형시트를 적층할 수도 있고, 도 1(b)에서와 같이 기재시트의 양면에 점착층을 적층하고 상기 점착층 각각의 상부에 이형시트를 적층하여 방수시트를 구성할 수도 있다.The waterproof sheet according to the present invention is manufactured using the resin composition as described above, and as shown in FIG. 1 , may include a base sheet, an adhesive layer laminated on the substrate sheet, and a release sheet laminated on the adhesive layer. At this time, an adhesive layer may be formed on one side of the base sheet as in FIG. A waterproof sheet may be formed by laminating and laminating a release sheet on each of the adhesive layers.
또한, 상기 기재시트는 상기 수지 조성물을 성형하여 형성한 것으로서, 방수시트를 시공할 때 상기 이형시트를 제거하고 상기 이형시트가 제거된 면을 바닥면에 깔아 시공하게 된다.In addition, the base sheet is formed by molding the resin composition, and when the waterproof sheet is constructed, the release sheet is removed and the surface from which the release sheet is removed is laid on the floor surface.
본 발명에 따른 수지 조성물과 이를 사용하여 제조된 방수시트의 물성을 평가하기 위하여 표 1과 같은 수지 조성물을 제조하였다.In order to evaluate the physical properties of the resin composition according to the present invention and a waterproof sheet prepared using the same, a resin composition as shown in Table 1 was prepared.
상기 수지 조성물을 이용하여 190 내지 230℃에서 압출 성형하여 기재시트를 제조하였고, 일면에 점착층을 형성한 후 이형지를 부착하여 방수시트 샘플을 제조하였다. 제조된 기재시트를 24시간 동안 실온에서 방치한 후 시트 말단의 말림 현상을 마이크로미터 캘리퍼스를 사용하여 측정하였다. A base sheet was prepared by extrusion molding at 190 to 230° C. using the resin composition, an adhesive layer was formed on one side, and then a release paper was attached to prepare a waterproof sheet sample. After the prepared base sheet was left at room temperature for 24 hours, curling at the end of the sheet was measured using a micrometer caliper.
도 2는 24시간 경과후의 방수시트의 상태를 촬영한 사진이다. 실시예 1(a), 실시예 2(b), 비교예 1(c), 비교예 2(d)에 따른 방수시트를 살펴보면, 비교예 1 및 2에서 심한 말림 현상이 나타나는 것을 알 수 있다. 이에 대하여 실시예 1 및 2에서는 말림 현상이 거의 나타나지 않는 것을 확인할 수 있다.2 is a photograph of the state of the waterproof sheet after 24 hours have elapsed. Looking at the waterproof sheets according to Example 1 (a), Example 2 (b), Comparative Example 1 (c), and Comparative Example 2 (d), it can be seen that severe curling occurs in Comparative Examples 1 and 2. On the other hand, in Examples 1 and 2, it can be seen that the curling phenomenon hardly appears.
또한, 상기 방수시트에 대해 마이크로미터 캘리퍼스를 사용하여 측정한 결과, 실시예 1 및 실시예 2는 3/1000, 4/1000㎜의 말림 현상이 측정되었으나, 비교예 1, 2의 경우 10/1000, 12/1000㎜의 말림 현상이 측정되어 종래의 방수시트에서 발생하는 말림 현상과 유사한 정도의 말림이 발생하는 것으로 나타났다.In addition, as a result of measuring the waterproof sheet using a micrometer caliper, the curling phenomenon of 3/1000 and 4/1000 mm was measured in Examples 1 and 2, but 10/1000 in Comparative Examples 1 and 2 , the curling phenomenon of 12/1000mm was measured, and it was found that the curling phenomenon similar to that occurring in the conventional waterproof sheet occurred.
이러한 시험결과로부터 본 발명에 따른 수지 조성물을 적용한 방수시트는 시공 시 말림 현상을 크게 억제할 수 있어 공정 효율을 향상시킬 수 있는 것으로 평가되었다.From these test results, it was evaluated that the waterproof sheet to which the resin composition according to the present invention is applied can greatly suppress the curling phenomenon during construction, thereby improving process efficiency.
상술한 바와 같이 바람직한 실시예를 들어 본 발명을 설명하였으나, 상기 실시예에 한정되지 아니하며 본 발명의 정신을 벗어나지 않는 범위 내에서 통상의 기술자에 의해 다양한 변형과 변경이 가능하며, 그러한 변형예 및 변경예는 본 발명과 첨부된 특허청구범위의 범위 내에 속하는 것으로 보아야 한다.Although the present invention has been described with reference to a preferred embodiment as described above, it is not limited to the above embodiment and various modifications and changes are possible by those skilled in the art within the scope of not departing from the spirit of the present invention, and such modifications and changes Examples are to be considered as falling within the scope of the present invention and the appended claims.
Claims (4)
15 to 20 parts by weight of polyethylene (PE), 15 to 20 parts by weight of polypropylene (PP), 20 to 25 parts by weight of ethylene vinyl acetate (EVA), 15 to 20 parts by weight of polyolefin elastomer (POE), styrene-ethylene-butylene -Styrene copolymer (SEBS) 1 to 5 parts by weight, ethylene propylene rubber (EPR) 5 to 10 parts by weight, and a reinforcing agent calcium carbonate (CaCO 3 ) A resin composition for a waterproof sheet, characterized in that it consists of 20 to 25 parts by weight.
상기 폴리에틸렌은 저밀도 폴리에틸렌(LDPE) 및 선형 저밀도 폴리에틸렌(LLDPE) 중 어느 하나 또는 이들의 혼합물인 것을 특징으로 하는 방수시트용 수지 조성물.
The method according to claim 1,
The polyethylene is a resin composition for a waterproof sheet, characterized in that any one or a mixture of low-density polyethylene (LDPE) and linear low-density polyethylene (LLDPE).
상기 폴리에틸렌, 폴리프로필렌 및 에틸렌초산비닐 중 어느 하나 또는 그 이상은 재생 수지를 포함하는 것을 특징으로 하는 수시트용 수지 조성물.
The method according to claim 1,
Any one or more of polyethylene, polypropylene, and ethylene vinyl acetate is a resin composition for sous sheet, characterized in that it contains a recycled resin.
상기 기재시트는 청구항 1에 따른 수지 조성물로 이루어지는 것을 특징으로 하는 방수시트.A waterproof sheet comprising a base sheet, an adhesive layer laminated on one or both sides of the base sheet, and a release sheet laminated on top of the adhesive layer,
The base sheet is a waterproof sheet, characterized in that made of the resin composition according to claim 1.