KR102441353B1 - Aircraft arresting coated belt and it's manufactured method - Google Patents
Aircraft arresting coated belt and it's manufactured method Download PDFInfo
- Publication number
- KR102441353B1 KR102441353B1 KR1020220043320A KR20220043320A KR102441353B1 KR 102441353 B1 KR102441353 B1 KR 102441353B1 KR 1020220043320 A KR1020220043320 A KR 1020220043320A KR 20220043320 A KR20220043320 A KR 20220043320A KR 102441353 B1 KR102441353 B1 KR 102441353B1
- Authority
- KR
- South Korea
- Prior art keywords
- belt
- coating
- excess
- coating solution
- aircraft
- Prior art date
Abstract
Description
본 발명은 항공기가 지정된 활주로를 벗어나게 될 때 항공기를 안전하게 정지시키는 항공기 초과 저지벨트가 자외선에 노출된 상태에서 장시간 사용되더라도 강도가 저하되지 않으면서 장시간 사용이 가능케 하는 항공기 초과 저지 코팅 벨트 및 그 제조방법에 관한 것이다.The present invention relates to an over-aircraft jersey coating belt and a method for manufacturing the same that enable long-term use without deterioration of strength even if the over-aircraft jersey belt, which safely stops the aircraft when the aircraft deviates from a designated runway, is used for a long time in a state of exposure to ultraviolet rays is about
항공기 초과저지 벨트는 항공기가 지정된 활주로를 벗어나게 될 때 항공기를 안전하게 정지시키도록 하는 것으로, 활주로에 가로질러 설치된 후크 케이블에 항공기의 바퀴가 걸리도록 하고 상기 후크 케이블에 텐션을 가하여 부하를 가하도록 하되 늘어나지 않고 끊어지지 않으면서도 강한 힘을 견딜 수 있도록 하여 항공기의 제동거리를 단축하여 착륙이 이루어지게 한다.Aircraft overrun belts are designed to safely stop an aircraft when it deviates from a designated runway. The aircraft's wheels are caught on a hook cable installed across the runway, and tension is applied to the hook cable to apply the load, but do not stretch it. It makes the landing possible by shortening the braking distance of the aircraft by allowing it to withstand strong forces without breaking.
기존에는 후크 케이블에 체인을 끌고 가면서 속도를 감속시키기 때문에 항공기의 양쪽으로 균등한 체인부하가 걸리지 않을 경우, 항공기의 방향이 틀어져 안전 착륙에 문제가 발생하기 때문에 현재는 띠 모양의 저지벨트를 후크 케이블의 양쪽에 연결 한 후 저지벨트의 선단이 트레일러에 탑재된 자동 텐션 조절기에 감겨지게 함으로써, 안전한 착륙을 유도하게 되나, 이러한 방식에는 강력한 힘을 받게 되는 저지벨트가 늘어지거나 끊어지지 않아야 함은 물론 텐션 조절기가 탑재된 트레일러가 견고한 고정 상태를 유지하여야 할 필요가 있다.In the past, because the speed was reduced while dragging the chain on the hook cable, if an even chain load was not applied to both sides of the aircraft, the aircraft would be oriented and it would cause a problem in safe landing. Safe landing is induced by having the tip of the jersey belt wound on the automatic tension adjuster mounted on the trailer after connecting to both sides of the It is necessary that the trailer equipped with the adjuster be held firmly in place.
상기 초과저지 벨트는 본 출원인에 의해 특허된 특허등록 10-0725255호에 제시된 벨트를 사용하고 있으나, 초과저지 벨트는 활주로가 설치된 야외에 설치되기 때문에 자외선이나 강렬한 태양열 등에 장시간 노출되는 한편 습기가 벌레 등에 노출될 수밖에 없고, 이로 인하여 초과저지 벨트의 수명이 단축되는 문제가 발생함은 물론 초과저지 벨트가 감긴 텐션 조절기가 탑재된 트레일러가 강력한 힘에 의해 이탈되지 않도록 강하게 잡아주어야만 항공기를 제동시킬 수 있으나, 트레일러를 콘크리트 등으로 고정시킬 수 없기 때문에 트레일러에 가해지는 강력한 힘으로부터 트레일러의 틀어짐이나 이탈 또는 전복 등의 문제가 발생할 수 있다.The excess restraint belt uses the belt presented in Patent Registration No. 10-0725255 patented by the present applicant, but since the excess restraint belt is installed outdoors where the runway is installed, it is exposed to ultraviolet rays or intense solar heat for a long time, while moisture is exposed to insects, etc. It is inevitably exposed, and this causes the problem of shortening the lifespan of the excess restraint belt, as well as braking the aircraft only when the trailer equipped with the tension adjuster on which the excess restraint belt is wound is held firmly so that it does not come off by strong force. Since the trailer cannot be fixed with concrete, etc., problems such as twisting, separation, or overturning may occur from the strong force applied to the trailer.
본 발명은 특허등록 10-0725255호의 초과저지 벨트를 사용함에 있어서, 자외선이나 태양열에 장시간 노출됨은 물론 습기나 벌레 등에 취약하여 초과저지 벨트의 수명을 단축시키는 문제를 해결하는 한편 초과저지 벨트가 감긴 텐션 조절기가 탑재된 트레일러가 바닥에 견고히 고정되지 못하여 초과저지 벨트에 가해지는 강한 힘을 견디지 못하는 문제를 해결하기 위한 것으로, 초과저지 벨트의 표면에 물침출, 광분해에 저항성을 갖는 항균제를 코팅 접착제와 안료와 함께 초과저지 벨트의 표면에 코팅시키는 것이다.The present invention solves the problem of shortening the life of the excess restraint belt due to prolonged exposure to ultraviolet rays or solar heat as well as being vulnerable to moisture or insects in using the excess restraint belt of Patent Registration No. 10-0725255, while the tension around the excess restraint belt This is to solve the problem that the trailer equipped with the regulator cannot withstand the strong force applied to the excess restraint belt because it is not firmly fixed to the floor. It is to be coated on the surface of the excess jersey belt with
본 발명은 초과저지 벨트 생지를 믹스통에 잠가준 후 건조로를 통과하면서 표면 코팅이 이루어지게 하는 것으로, 믹스통에는 코팅 접착제와 항균제 및 안료를 포함한 코팅액을 채운 다음 초과저지 벨트 생지가 믹스통에 채워진 코팅액에 잠긴 상태로 이동시키되 1-1.5m/min 의 속도로 이동시키고, 상기 코팅액에 감긴 초과저지 벨트의 양쪽을 압착하여 코팅액을 탈수시킨 후 240oC 이하의 온도를 유지하는 건조로의 내부를 이동시켜 코팅이 이루어지기 전 상태로 건조가 이루어지게 함으로써 이루어지는 것으로, 저지초과 벨트 생지의 표면에 코팅되는 코팅액으로 인하여 광분해가 나타나지 않도록 하는 한편 물침출이나 벌레에 노출되는 것을 방지하는 것이다.The present invention locks the excess jersey belt dough into the mixing bin and then passes through the drying furnace to coat the surface. The mix bin is filled with a coating solution including a coating adhesive, antibacterial agent and pigment, and then the excess jersey belt dough is filled in the mixing bin. Move in a state submerged in the coating solution, move at a speed of 1-1.5 m/min, dehydrate the coating solution by squeezing both sides of the over-resistance belt wound around the coating solution, and then move the inside of a drying furnace that maintains a temperature of 240 o C or less This is done by drying in the state before the coating is made. This is to prevent photodegradation due to the coating solution being coated on the surface of the excess jersey belt dough and to prevent exposure to water leaching or insects.
본 발명은 초과저지 벨트 당 코팅액이 총 코팅이 이루어진 벨트 무게의 3.1%-8.5%에 해당하는 함량으로 포함되게 코팅이 이루어지게 하며, 이러한 본 발명의 벨트는 야외에서 태양광과 기후에 그대로 노출되더라도 물침출과 광분해 및 벌레의 침투에 저항성을 갖도록 함으로써, 장시간 사용하더라도 일정한 벨트의 강연성과 강성을 유지하기 위한 각 코팅액 성분의 함량 비율을 개발하여, 초과저지 벨트가 틀어지거나 끊어지는 등의 문제가 발생하는 않는 것이다.The present invention allows the coating to be made so that the coating solution per excess jersey belt is included in an amount corresponding to 3.1%-8.5% of the total weight of the coated belt, and the belt of the present invention is exposed to sunlight and climate outdoors even if it is exposed as it is. By making it resistant to water leaching, photodegradation, and insect penetration, we developed the content ratio of each coating solution to maintain constant rigidity and rigidity of the belt even after long-term use, resulting in problems such as twisting or breaking of the excess restraint belt will not do
본 발명은 초과저지 벨트의 생지를 코팅액으로 코팅시킴으로써, 야외에서 장시간 노출이 이루어지더라도 광분해나 물침출에 높은 저항성을 갖고, 벌레 등의 침투를 방지하여 초과저지 벨트의 강도가 줄어들지 않아 강한 충격을 견딜 수 있음은 물론 틀어지거나 끊어지는 등의 문제가 발생하지 않는 효과가 있다.The present invention has a high resistance to photodegradation or water leaching even when exposed to the outdoors for a long time by coating the dough of the over-resistance belt with a coating solution, and prevents the penetration of insects, etc. It is durable and has the effect of not causing problems such as twisting or breaking.
그리고, 본 발명은 초과저지 벨트의 생지에 포함될 일정한 벨트의 강연성과 강성을 유지하기 위한 각 코팅액 성분의 함량 비율을 개발하여 코팅액에 의해 코팅이 이루어지면 부드러운 상태의 초과저지 벨트가 적당한 딱딱한 느낌의 단단함을 갖기 때문에 강한 충격을 견딜 수 있는 저항력을 갖는다. And, the present invention develops the content ratio of each coating solution component to maintain a certain rigidity and rigidity of the belt to be included in the dough of the over-resistance belt. It has the resistance to withstand strong impact.
도 1은 본 발명의 실시예 구성도
도 2는 본 발명의 초과저지 벨트 사시도
도 3은 본 발명의 초과저지 벨트 평면도
도 4는 본 발명 끈세폭띠형 초과저지 벨트의 조직도
도 5는 본 발명의 끈세폭띠형 초과저지 벨트가 감긴 릴 사시도1 is a block diagram of an embodiment of the present invention;
Figure 2 is a perspective view of the excess restraint belt of the present invention;
3 is a plan view of the over-resistance belt of the present invention
Figure 4 is an organization chart of the present invention string narrow belt type excess jersey belt
5 is a perspective view of a reel around which the string narrow belt-type excess restraint belt of the present invention is wound;
본 발명은 부드러운 특허등록 10-0725255호로 제시되고 도 4의 조직도를 갖는 끈세폭띠형 초과저지 벨트의 표면에 코팅액을 코팅하여 물침출과 광분해에 저항성을 갖도록 하는 한편 벌레 등의 침투가 발생하지 않도록 함으로써, 장시간 사용이 이루어지더라도 강도가 변하지 않아 끊어지거나 틀어지게 되는 현상을 방지하는 것이다.The present invention is presented by soft patent registration No. 10-0725255 and coating the coating solution on the surface of the string-type over-resistance belt having the organization chart of FIG. 4 to have resistance to water leaching and photolysis while preventing the penetration of insects , it is to prevent the phenomenon that the strength does not change even if it is used for a long time and it is broken or distorted.
본 발명은 초과저지 벨트의 생지를 공급하는 과정과, 초과저지 벨트를 믹스통에 채워진 코팅액에 잠긴 채로 서서히 이동시키는 과정과, 믹스통에서 코팅액에 잠긴 초과저지 벨트의 표면을 압착하여 코팅액을 탈수시키는 과정과, 탈수가 이루어진 초과저지 벨트를 고온의 건조로에서 서서히 이동시켜 건조가 이루어지는 과정을 포함함으로써 이루어지는 것으로, 초과저지 벨트의 코팅액은 총 코팅이 이루어진 벨트 무게의 3.1%-8.5%에 해당하는 함량으로 코팅이 이루어지게 된다.The present invention relates to a process of supplying the dough for the excess restraint belt, a process of slowly moving the excess restraint belt immersed in the coating liquid filled in the mixing tub, and dehydrating the coating liquid by squeezing the surface of the excess restraint belt submerged in the coating liquid in the mixing tub This is accomplished by including the process and the process of moving the dehydrated excess restraint belt in a high-temperature drying furnace slowly to dry it, and the coating solution of the excess restraint belt is 3.1%-8.5% of the total weight of the coated belt. coating is made.
본 발명의 코팅액은 물, 코팅 접착제, 카본 블랙이 포함되는 안료, 항균제 등을 혼합하여 액체 형태로 이루어지며, 이러한 코팅액에 초과저지 벨트의 생지가 잠긴 채로 이동하면서 표면 코팅이 이루어진 후 고온의 건조로를 통과하면서 코팅액의 건조가 이루어지는 것이다.The coating solution of the present invention is made in a liquid form by mixing water, coating adhesive, pigment containing carbon black, antibacterial agent, etc., and after surface coating is made while the dough of the over-resistance belt is immersed in this coating solution, a high-temperature drying furnace is used. As it passes, the coating solution is dried.
본 발명의 코팅 접착제는 결합력을 높이는 한편 표면의 흡착력을 높이게 되고, 항균제는 물침출과 광분해에 저항성을 갖게 되고, 안료는 검은색을 나타내도록 한다.The coating adhesive of the present invention increases the bonding strength while increasing the surface adsorption force, the antibacterial agent has resistance to water leaching and photolysis, and the pigment shows black color.
본 발명을 실시예 도면에 의거 상세히 설명한다.The present invention will be described in detail with reference to the drawings.
본 발명의 초과저지 벨트(10)는 특허등록 10-0725255호에 제시되고 도 4의 조직도로 직조되는 생지를 이용하게 되는 것으로, 기존에는 초과저지 벨트(10)를 그대로 사용하여 광분해성에 취약함은 물론 물의 침투가 용이하여 쉽게 변형이 오는 한편 강도가 저하됨은 물론 벌레 등의 침투가 이루어지는 문제가 있기 때문에 본 발명에서는 초과저지 벨트(10)의 표면에 광분해와 물침출에 저항을 갖는 코팅액을 견고히 부착시킴으로써 장시간 사용에도 성능 변화가 발생하지 않아 일정한 강연성을 유지하며, 끊김이나 틀어짐을 방지하는 것이다.The
본 발명은 초과저지 벨트(10)를 코팅액(21)이 담긴 믹스통(20)에 투입하여 서서히 이동하며 표면에 코팅액의 충분한 코팅이 이루어지게 하는 것으로, 롤 형태로 공급되는 초과저지 벨트(10)는 가이드 롤러(1)(2)를 타고 믹스통(20)에 투입된 후 가이드 롤러(3)(4)에 의해 코팅액(21)에 잠긴 채로 이동이 이루어지고, 믹스통(20)에 잠긴 초과저지 벨트(10)는 압착롤러(5)(6)를 거치면서 코팅액(21)의 탈수가 이루어진 후 건조로(30)로 이동되게 한다.The present invention is to put the
믹스통(20)에는 물 150리터, 코팅 접착제(PVB(Polyvinyl Butyral) 15리터, 항균제 0.9리터, 카본 블랙이 포함되는 안료 10리터를 혼합하여 이루어진 코팅액(21)이 채워지고, 초과저지 벨트(10)는 믹스통(20)의 코팅액(21)에 잠긴 채로 1-1.5m/min의 속도로 이동시키면서 코팅액(21)이 초과저지 벨트(10)의 조직 사이로 충분한 침투가 이루어지게 한다.The
본 발명의 코팅액(21)을 구성하는 코팅 접착제(Polyvinyl Butyral)은 접착수지 내 빠른 결합력과, 표면에 대한 높은 접착력과, 유연성을 가진 범위 강인성과, 표면적 투명성을 갖추는 한편 내산성과 내알칼리성의 성질을 갖게 되고, 흑색 안료(microtint black)는 계면 활성제, 모노프로필레 글리콘, 방부제 및 물의 혼합물에 분산된 유기 및 무기 안료를 사용하여 제작되며, 항균제는 mystox의 상호를 갖는 기성품을 사용하는 것으로, 섬유직물과 원사를 보호하기 위하여 환경영향을 최소화 하면서 저용량 활성성분을 기반으로 하는 것으로, 물침출과 광분해에 높은 수준의 저항성을 갖게 된다.The coating adhesive (Polyvinyl Butyral) constituting the
본 발명의 믹스통(20)에는 물 150리터, 코팅 접착제(PVB(Polyvinyl Butyral) 15리터, 항균제 0.9리터, 흑색 안료 10리터를 혼합한 코팅액(21)이 채워진 상태에서 초과저지 벨트(10)가 상기 코팅액(21)에 잠긴 채로 1-1.5m/min의 속도로 이동하게 되며, 초과저지 벨트(10)는 가이드롤러(3)(4)를 거치면서 코팅액(21)에 잠긴 채로 이동한다.In the
믹스통(20)의 코팅액(21)에 잠긴 초과저지 벨트(10)는 압착롤러(5)(6) 사이를 통과하면서 코팅액(21)의 탈수가 이루어진 다음 고온의 건조로(30)로 이동하게 되며, 건조로(30)에서는 초기의 초과저지 벨트(10)와 같은 수분 함량이 이루어진 상태로 건조시킨다.The
본 발명의 건조로(30)는 초과저지 벨트(10)가 롤러를 타고 이동하면서 고열에 노출되어 코팅액(21)의 건조가 이루어지는 것으로, 건조로(30)의 내벽에 설치되는 히터 등의 발열수단에 의해 240oC 의 온도를 유지한 채로 건조가 이루어지게 하고, 건조로(30)의 상측에는 건조에 의해 증발된 수분이 배출되는 배출구멍을 형성하며, 건조로(30)에서는 초기에 코팅액(21)의 코팅이 이루어지기 전의 수분 함량으로 건조가 이루어져 초과저지 벨트(40)를 완성하게 한다.In the
본 발명에서 초과저지 벨트(10)의 무게 당 3.1%-8.5%에 해당하는 함량의 코팅액(21)의 코팅이 이루어지는 형태로 코팅과정을 진행하고, 초과저지 벨트(10)의 이동속도가 높거나 느린 경우에는 효과적인 코팅이 이루어지지 않거나 과도한 코팅액(21)의 코팅이 이루어져, 물침출이나 광분해의 저항성을 낮추게 된다.In the present invention, the coating process is performed in a form in which the
본 발명의 코팅액(21)을 구성하는 재료의 함량을 초과하거나 과도하게 부족할 경우, 목적하는 물침출과 광분해에 저항성을 갖는 초과저지 벨트(40)를 제공하지 못하게 되고, 수명도 연장시킬 수 없게 된다.When the content of the material constituting the
본 발명은 물침출과 광분해에 저항성을 갖는 항균제를 효과적으로 초과저지 벨트(10)에 코팅시키기 위하여 코팅 접착제를 사용하고 있으며, 코팅액(21)의 효과적인 코팅과 벌레 등의 침투를 방지하기 위하여 흑색의 안료를 포함하고 있는 것으로, 코팅액(21)으로 코팅이 이루어진 초과저지 벨트(40)는 흑색을 띄고, 광분해에 저항성을 갖기 때문에 자외선이나 태양열에 의해 분해가 이루어지지 않으며, 또한, 카본 블랙을 포함하는 안료를 사용하여 항균제의 코팅이 이루어지기 때문에 벌레나 해충에 의한 침투가 발생하지 않고, 코팅액의 코팅은 비교적 단단한 초과저지 벨트(40)를 완성하기 때문에 강력한 충격이나 틀어짐에 견디는 힘이 증가되어 장기간 사용이 가능하고, 초과저지 벨트(40)가 일정한 강연성을 유지하며, 끊어짐이나 틀어짐이 발생하지 않는다.The present invention uses a coating adhesive to effectively coat the antibacterial agent with resistance to water leaching and photolysis on the
10 : 초과저지 벨트 20 : 믹스통
21 : 코팅액 30 : 건조로
40 : 초과저지 벨트10: excess restraint belt 20: mix barrel
21: coating solution 30: drying furnace
40: excess jersey belt
Claims (3)
상기 초과저지 벨트(10)를 믹스통(20)에 채워진 코팅액(21)에 잠긴 상태에서 1-1.5m/min의 속도로 이동시키는 과정을 수행하되 상기 믹스통(20)에는 물 150리터, 코팅 접착제(Polyvinyl Butyral) 15리터, 항균제(mystox) 0.9리터, 흑색 안료(microtint black) 10리터를 혼합한 코팅액(21)이 채워지고,
믹스통(20)에서 코팅액(21)이 코팅된 초과저지 벨트(10)는 압착롤러(5)(6) 사이를 통과하면서 탈수시키는 과정을 수행하고,
탈수가 이루어진 초과저지 벨트(10)는 240oC 의 온도를 유지하는 건조로(30)를 통과하면서 초과저지 벨트(40)를 완성하는 과정을 수행하여 이루어지는 것을 특징으로 하는 항공기 초과 저지 벨트의 코팅방법.To perform the process of supplying by unraveling the excess restraint belt (10) dried in a roll form,
A process of moving the excess prevention belt 10 at a speed of 1-1.5 m/min in a state of being immersed in the coating solution 21 filled in the mixing tub 20 is performed, but the mixing tub 20 contains 150 liters of water, coating 15 liters of adhesive (Polyvinyl Butyral), 0.9 liters of antibacterial agent (mystox), and 10 liters of microtint black are mixed with coating solution 21,
In the mixing tank 20, the excess resistance belt 10 coated with the coating solution 21 performs a process of dehydration while passing between the pressing rollers 5 and 6,
The dehydration of the excess restraint belt 10 is made by performing the process of completing the excess restraint belt 40 while passing through the drying furnace 30 maintaining a temperature of 240 o C. Coating of the aircraft excess restraint belt Way.