KR102420144B1 - Composition of clay comprising sulfur and method for producing the same - Google Patents
Composition of clay comprising sulfur and method for producing the same Download PDFInfo
- Publication number
- KR102420144B1 KR102420144B1 KR1020210100974A KR20210100974A KR102420144B1 KR 102420144 B1 KR102420144 B1 KR 102420144B1 KR 1020210100974 A KR1020210100974 A KR 1020210100974A KR 20210100974 A KR20210100974 A KR 20210100974A KR 102420144 B1 KR102420144 B1 KR 102420144B1
- Authority
- KR
- South Korea
- Prior art keywords
- sulfur
- soil
- powder
- mixed
- composition
- Prior art date
Abstract
본 발명은 갯벌의 개흙이나 각종 점토, 황토, 백토, 흑토 등의 정제한 토양에 유황을 혼합하여 다양한 용도로 사용할 수 있도록 한 유황토 조성물 및 이의 제조방법을 제공코자 하는 것으로서, 상기 본 발명은 토양 50~80중량%와, 유황분말 0.01~30중량%와 가연체 70~99.99중량%가 혼합되어 이루어진 유황법제분말 20~50중량%가 혼합 조성되며, 상기 토양과 유황법제분말이 혼합된 유황혼합토 60~90중량%와, 소금을 투입하여 10~40‰의 염수로 된 혼합촉진제 10~40중량%를 혼합하여 유황토 조성물을 조성하거나, 이에 더하여 유황토 조성물을 10~20%의 함수율을 갖도록 건조한 후 200~500℃에서 2~24시간 동안 소성한 다음, 100~300메시의 입자크기로 분쇄한 분말로 이루어진 것을 특징으로 하며, 이에 의하면 토양과 유황의 자체 성분에 의한 인체에 유익한 효과를 제공하며, 유황토 조성물을 이용하여 훈제분말, 농사용 비료, 입욕제 분말, 라돈저감형 건축용 또는 침구용 패널 및 볼, 염증 등의 환부나 피부에 접착하여 통증완화용 또는 미용용으로 사용할 수 있어서 다양한 용도로 두루 사용할 수 있으며, 이와 같은 다양한 분야에서 인체에 유익한 성분을 공급하여 건강증진효과를 한층 더 배가시킬 수 있는 등 다수의 효과를 기대할 수 있다.The present invention is to provide a sulfur soil composition and a method for manufacturing the same, which can be used for various purposes by mixing sulfur with purified soil such as open soil of tidal flats or various clay, loess, white soil, black soil, etc. 50 to 80% by weight, 0.01 to 30% by weight of sulfur powder, and 70 to 99.99% by weight of combustibles are mixed and composed of 20 to 50% by weight of sulfur-based powder, and sulfur mixed soil in which the soil and sulfur-based powder are mixed 60 to 90% by weight of salt is added and 10 to 40% by weight of a mixing accelerator made of 10 to 40‰ brine is mixed to form a sulfur soil composition, or in addition, the sulfur soil composition to have a moisture content of 10 to 20% It is characterized in that it is made of a powder that is dried and calcined at 200 to 500 ° C for 2 to 24 hours and then pulverized to a particle size of 100 to 300 mesh. It can be used for various purposes because it can be used for pain relief or cosmetic use by using the sulfur soil composition to adhere to the skin or affected areas such as smoked powder, agricultural fertilizer, bath powder, radon-reducing construction or bedding panel and cheek, inflammation, etc. It can be used widely and can be expected to have a number of effects, such as being able to double the health promotion effect by supplying beneficial ingredients to the human body in these various fields.
Description
본 발명은 유황토 조성물 및 이의 제조방법에 대한 것으로서, 이를 보다 상세히 설명하면 갯벌의 개흙이나 다양한 곳의 점토, 황토, 백토, 흑토 등의 토양에 유황을 혼합하여 다양한 용도로 사용할 수 있도록 한 유황토 조성물 및 이의 제조방법에 관한 것이다.The present invention relates to a sulfur soil composition and a method for manufacturing the same, and in more detail, it is a sulfur soil that can be used for various purposes by mixing sulfur with soil such as open soil in tidal flats or clay, loess, white soil, and black soil in various places It relates to a composition and a method for preparing the same.
일반적으로 유황토는 토양인 흙에 유황을 혼합한 것으로서, 흙으로는 미생물이 다량으로 살아있는 갯벌의 개흙이나 산이나 들 및 강가 및 해안가 등의 점토 및 황토, 백토, 흑토 등의 원적외선이 다량으로 방출되는 토양을 사용하고, 유황은 특유의 향과 독성이 있어서 사용용도에 따라서 토양에 비하여 극소량을 사용할 수도 있고, 상대적으로 토양에 비하여 적정 함량으로 혼합하여 사용할 수도 있으며, 이와 같이 미생물이나 미네랄 등이 다량으로 함유되어 있거나 원적외선이나 음이온 등이 다량으로 방출되는 각종 토양에 세계 각국에서 해독작용을 가지고 있어서 유황을 항암치료제, 염증치료제, 류마티스치료제, 각종피부질환 치료제로 다양하게 개발 사용되고 있는 유황을 혼합하여 사용하는 기술이 다양하게 개발되고 있는 실정이다.In general, sulfur soil is a mixture of sulfur and soil, and the soil emits a large amount of far-infrared rays such as loess, white soil, and black soil. Sulfur has a unique flavor and toxicity, so it can be used in a very small amount compared to the soil depending on the intended use, or it can be used by mixing it in an appropriate amount relative to the soil. Sulfur, which has been developed and used in various countries as anticancer drugs, inflammatory drugs, rheumatism drugs, and various skin diseases, is mixed with sulfur because it has a detoxifying effect in various countries around the world on soils containing Various technologies are being developed.
종래 유황토 관련 기술로는 대한민국 공개특허 2003년 제61045호(2003년 7월 18일자 공개)에 게재된 바와 같이 유황을 황토에 희석하여 끊인 다음 목초액을 희석시켜 각종 가축의 사료에 첨가하거나 각종 야채류의 재배에 사용하며, 찌꺼기는 밭의 비료로 사용토록 한 기술이 개발되어 있었으나, 이러한 종래기술에서는 유황의 독성을 없애기 위해 유황 10~30중량%와 황토 30~70중량%를 희석하여 100℃로 5~10시간 동안 끓인다고 하였으나, 유황의 함량이 황토의 함량에 약 30~40% 정도 혼합되면 황토가 회석되더라도 말 그대로 유황의 독성이 희석될 뿐 없앨 수 없으며, 100℃로 끓여도 유황의 독성이나 특유의 냄새를 완전히 없앨 수는 없었던 것으로서, 이러한 황토법제 유황물을 농작물의 물이나 비료로 사용할 시 식물에 치명적일 수도 있으며, 이러한 황토법제 유황물을 섞은 사료를 가축들이나 반려동물 등에 먹이거나 상기 식물이나 가축을 사람이 섭취하였을 시 건강에 해로울 수도 있는 등 다수의 문제점을 가지고 있었던 것이다.As a conventional sulfur soil-related technology, as disclosed in Korean Patent Application Laid-Open No. 61045 (published on July 18, 2003), sulfur is diluted in loess and boiled, and then wood vinegar is diluted and added to feed for various livestock or various vegetables. A technology has been developed in which the residue is used as fertilizer for the field, but in this prior art, 10 to 30 wt% of sulfur and 30 to 70 wt% of loess were diluted to 100 ° C to eliminate the toxicity of sulfur. It was said to boil for 5-10 hours, but if the sulfur content is mixed with the loess content by about 30-40%, even if the loess is dilute, the toxicity of sulfur is literally diluted and cannot be eliminated. As it was not possible to completely remove the unique odor, such sulfur-based sulfur compounds may be fatal to plants when used as water or fertilizer for crops. It had a number of problems, such as being harmful to health when humans ingest livestock.
본 발명에서는 상기한 종래 기술의 제반 문제점들을 해결코자 새로운 기술을 창안한 것으로서, 본 발명은 인체에 유익한 각종 미생물과 미네랄 등이 살아 있는 토양에 유황을 혼합 조성하여 분말화시켜서 훈제용 분말, 건축용 또는 침구용 패널 또는 볼의 성형분말, 입욕제 분말, 통증완화 및 미용용 분말 등의 다양한 분야 널리 활용할 수 있도록 한 유황토 조성물 및 이의 제조방법을 제공코자 함에 발명에서 해결하고자 하는 과제를 두고 완성한 것이다.In the present invention, a new technology was created to solve the problems of the prior art, and the present invention is a powder for smoking, building or It was completed with the task to be solved in the present invention to provide a sulfur clay composition and a manufacturing method thereof that can be widely used in various fields such as bedding panel or ball molded powder, bath powder, pain relief and cosmetic powder, etc.
이와 함께 각종 토양에 유황을 미량으로 혼합 후 고온으로 가열하여 유황의 독성 및 냄새를 제거토록 하며, 첨가물을 부가하여 유황을 가열 시 상대적으로 낮은 온도에서 독성 및 악취를 제거할 수 있도록 함을 추가적인 해결과제로 하는 것이다.At the same time, it is possible to remove the toxicity and odor of sulfur by mixing a small amount of sulfur in various soils and heating it at a high temperature. it will be a task
또한 별도로 기술하지는 않았으나, 본 발명의 유황토 조성물 및 이의 제조방법을 상세하게 기술한 하기의 발명을 실시하기 위한 구체적인 내용과 청구범위 및 도면 등을 감안하여 유추할 수 있는 범위 내의 또 다른 목적들도 본 발명의 전체 해결과제에 포함되는 것이다.In addition, although not separately described, other purposes within the scope that can be inferred in consideration of the specific content, claims, drawings, etc. It is to be included in the overall solution of the present invention.
상기한 발명의 과제를 해결하기 위한 구체적인 수단으로 본 발명에서는 유황토 조성물 및 이의 제조방법을 구성하되, 상기 본 발명의 유황토 조성물의 제조방법은 갯벌의 개흙, 점토, 황토, 백토, 흑토 중 어느 하나 또는 둘 이상이 혼합된 토양을 입자크기가 100~200메시로 구비토록 하는 토양준비단계와, 분말로 이루어진 유황 0.01~30중량%에 소나무 등의 목분, 솔잎, 애엽, 곡물겨, 곡식 중 어느 하나 또는 둘이상이 혼합되어 분말로 분쇄한 가연체 70~99.99중량%를 혼합하여 유황법제분말을 조성토록 하는 유황법제분말조성단계와, 토양준비단계에 의해서 구비된 토양 50~80중량%와 유황법제분말조성단계를 거쳐서 조성된 유황법제분말 20~50중량%를 교반기에서 혼합하여 유황혼합토를 구비토록 하는 유황혼합토조성단계와, 유황혼합토조성단계에서 토양과 유황법제분말이 혼합된 유황혼합토 60~90중량%에 소금을 투입하여 10~40‰의 염수로 된 혼합촉진제 10~40중량%를 혼합하여 유황토예비조성물을 구비하는 혼합촉진단계와, 유황토예비조성물을 함수율 10~20%로 건조하여 미소성유황토를 제조하는 건조단계와, 건조단계를 거친 미소성유황토를 200~500℃의 온도로 2~24시간 동안(소성로에 따라 변함) 소성로에서 소성을 거쳐서 소성유황토를 제조하는 소성단계와, 소성단계 후 가열된 소성유황토를 후술하는 분쇄기에 투입 시 분쇄기의 변형이나 파손이 되지 않을 정도로 소정의 온도로 냉각하는 냉각단계와, 냉각단계를 거쳐서 냉각이 이루어진 소성유황토를 분쇄기에 투입하여 100~300메시의 유황토분말로 분쇄토록 하는 분쇄단계가 포함된 것을 특징으로 한다.As a specific means for solving the problems of the present invention, the present invention constitutes a sulfur clay composition and a method for producing the same, but the production method of the sulfur clay composition of the present invention is any one of mudflat, clay, loess, white clay, and black soil. A soil preparation step of preparing one or more mixed soil with a particle size of 100 to 200 mesh, and 0.01 to 30% by weight of sulfur consisting of powder, wood flour such as pine, pine needles, leaf leaves, grain bran, and grain One or two or more are mixed to form a sulfur-based powder by mixing 70 to 99.99% by weight of the combustibles pulverized into powder, and 50 to 80% by weight of the soil prepared by the soil preparation step and sulfur A sulfur mixed soil composition step in which 20-50 wt% of the sulfur-method powder prepared through the legal powder-forming step is mixed with a stirrer to prepare a sulfur-mixed soil, and a sulfur-mixed soil 60- Salt is added to 90% by weight, and 10 to 40% by weight of a mixing accelerator made of 10 to 40% brine is mixed to provide a sulfur soil preliminary composition, and the sulfur soil preliminary composition is dried to a moisture content of 10 to 20%. A drying step to produce uncalcined sulfur soil, and a calcination step to produce calcined sulfur soil by calcining the unburned sulfur soil that has undergone the drying step at a temperature of 200 to 500 ° C for 2 to 24 hours (varies depending on the furnace) And, a cooling step of cooling the calcined sulfur soil to a predetermined temperature so as not to cause deformation or damage to the grinder when the heated calcined sulfur soil is put into the grinder to be described later, and the calcined sulfur soil cooled through the cooling step is put into the grinder Therefore, it is characterized in that it includes a grinding step to grind it into 100-300 mesh sulfur earth powder.
이에 더하여 상기 분쇄단계를 거쳐서 분쇄된 유황토분말을 패널형태나 볼형태로 성형하여 소성단계를 거쳐서 토양에 함유되어 있던 라돈을 저감시켜서 건축용이나 침구용에 사용 시 라돈방출은 최소화 할 수 있도록 제조하는 건축및침구용품성형단계가 더 포함된 것을 특징을 할 수 있다.In addition, the sulfur soil powder pulverized through the pulverization step is molded into a panel shape or a ball shape, and the radon contained in the soil is reduced through the firing step to minimize radon emission when used for construction or bedding. It may be characterized in that the building and bedding product forming step is further included.
이에 더하여 상기 분쇄단계를 거쳐서 분쇄된 유황토분말을 초미립자분쇄기에 투입하여 300~500메시의 입자크기의 초미립자로 미분쇄하는 미분쇄단계와, 미분쇄단계를 거쳐 미분쇄된 유황토미분말에 자체적으로 접착 성분을 가지는 천연의 엿, 꿀, 찹쌀풀 중 어느 하나 또는 둘이상이 혼합된 천연접착제를 섞어서 겔상태가 되도록 제조하여 환부나 피부에 접착토록 해서 염증치료 또는 피부미용에 사용토록 하는 치료및미용용품제조단계가 더 포함된 것을 특징으로 할 수도 있다.In addition, a fine grinding step of putting the sulfur soil powder pulverized through the pulverization step into an ultra-fine particle grinder and fine pulverizing it into ultra-fine particles with a particle size of 300 to 500 mesh, and a fine pulverization step to self-pulverize the fine sulfur earth powder Treatment and beauty in which any one or a mixture of two or more of natural syrup, honey, and glutinous rice paste having an adhesive component is mixed to form a gel, and used for inflammation treatment or skin beauty by adhering to the affected area or skin It may be characterized in that the article manufacturing step is further included.
상술한 과제 해결을 위한 구체적인 수단에 의하면, 본 발명의 유황토 조성물 및 이의 제조방법은 각종 토양에 곡물껍질 또는 목재의 분말이 혼합된 유황을 염수와 함께 소량으로 혼합하여 토양과 유황의 자체 성분에 의한 인체에 유익한 효과를 득하여 건강증진효과를 제공토록 한다.According to the specific means for solving the above-mentioned problems, the sulfur soil composition of the present invention and the method for manufacturing the same are mixed with a small amount of sulfur mixed with grain bark or wood powder in various soils with brine to add the soil and sulfur to their own components. By obtaining beneficial effects on the human body, it provides health-promoting effects.
이와 함께 토양에 유황을 상기와 같이 혼합하여 건조 후 분말화시켜서 닭이나 돈육 등의 훈제 시 훈제기에 투입하여 훈제분말로 사용토록 할 수 있으며, 상기 토양과 유황의 혼합, 건조 후 소성로에서 소성하되, 상기 훈제분말로 사용한 후 분말에 유황을 더 혼합하여 소성하며, 이후 냉각 및 분쇄하여 입욕제 분말, 농사용 비료로 사용하거나, 라돈저감형 건축용 또는 침구용 패널 및 볼의 성형분말로 사용하거나, 염증 등의 환부나 피부에 접착하여 통증완화용 또는 미용용으로 사용할 수 있어서 다양한 용도로 두루 사용할 수 있는 효과와 함께 훈제분말의 경우 훈제 대상물의 향미와 건강증진효능을 향상시키며, 이로 인한 입욕제 및 라돈저감형 패널 또는 볼을 사용하거나 초미립자로 하여 통증완화용이나 미용용으로 사용 시 각종 토양과 유황에 의한 인체에 유익한 성분을 공급하여 건강증진효과를 한층 더 배가시킬 수 있는 효과를 제공토록 한다.At the same time, sulfur is mixed with the soil as described above, dried and powdered, and then put into a smoker when smoking chicken or pork to be used as a smoked powder. After being used as the smoked powder, more sulfur is mixed with the powder and calcined, and then cooled and pulverized to be used as a bath powder powder, agricultural fertilizer, or as a molded powder for radon-reducing building or bedding panels and balls, or inflammation, etc. In the case of smoked powder, it improves the flavor and health-promoting effect of the smoked object with the effect that it can be used for a variety of purposes as it can be used for pain relief or cosmetic use by adhering to the affected area or skin, resulting in a bath agent and radon-reducing panel Alternatively, when using balls or ultra-fine particles for pain relief or cosmetic use, beneficial ingredients are supplied to the human body by various soils and sulfur to provide an effect that can further double the health promotion effect.
이에 더하여 토양에 유황을 혼합할 시 목분(木粉)이나 곡분(穀粉) 등의 가연체(可燃體)와 혼합하여 유황혼합물의 소성 시 보다 높은 온도로 유도하면서 짧은 시간 내에 원활하게 소성이 이루어지도록 하는 효능을 제공하면서, 이에 염수를 혼합하여 토양 및 유황 혼합물의 변질과 세균번식 등을 방지할 수 있는 등 염의 효능을 동시에 제공하게 되는 등 그 기대되는 효과가 다대한 발명인 것이다.In addition, when sulfur is mixed with soil, it is mixed with combustible materials such as wood flour or grain flour to induce a higher temperature than when calcining the sulfur mixture and to ensure smooth firing within a short time. It is a great invention with the expected effects such as simultaneously providing the efficacy of salt, such as being able to prevent deterioration and bacterial propagation of the soil and sulfur mixture by mixing salt water with it.
도 1은 본 발명의 유황토 조성물의 조성을 보인 블록도
도 2는 본 발명의 유황토 조성물의 제조방법으로 훈제용 분말을 제조하는 방법을 보인 공정도
도 3은 본 발명의 유황토 조성물의 제조방법으로 입욕제를 제조하는 방법을 보인 공정도
도 4는 본 발명의 유황토 조성물의 제조방법으로 건축용품이나 침구용품을 제조하는 방법을 보인 공정도
도 5는 본 발명의 유황토 조성물의 제조방법으로 염증치료제나 피부미용팩 등을 제조하는 방법을 보인 공정도1 is a block diagram showing the composition of the sulfur clay composition of the present invention;
Figure 2 is a process chart showing a method for producing a powder for smoking by the method for producing the sulfur clay composition of the present invention
3 is a process chart showing a method of manufacturing a bath agent by the manufacturing method of the sulfur clay composition of the present invention;
Figure 4 is a process diagram showing a method of manufacturing a building article or bedding article by the manufacturing method of the sulfur clay composition of the present invention
5 is a process chart showing a method of manufacturing an inflammatory treatment agent or a skin care pack, etc. by the method of manufacturing the sulfur clay composition of the present invention;
본 발명은 갯벌의 개흙이나 각종 점토, 황토, 백토, 흑토 등의 다양한 광물질의 토양에 유황을 혼합하여 다양한 용도로 사용할 수 있도록 한 유황토 조성물 및 이의 제조방법을 제공코자 하는 것으로서, 이를 하기에서 도면들과 함께 보다 구체적으로 설명토록 하되, 첨부된 도면은 본 발명의 기술적 사상의 내용과 범위를 쉽게 설명하기 위한 예시일 뿐 이에 한정되는 것은 아니며, 사용되는 용어들 역시 실시 예를 구체적으로 설명하기 위한 것일 뿐 해당 용어에 국한되게 해석되어서는 아니 된다.The present invention is to provide a sulfur soil composition and a method for manufacturing the same, which can be used for various purposes by mixing sulfur with various mineral soils such as open soil of tidal flats or various clays, loess, white soil, black soil, and the like. However, the accompanying drawings are only examples for easily explaining the content and scope of the technical idea of the present invention, and are not limited thereto, and the terms used are also used to describe the embodiment in detail. It should not be construed as being limited to the term.
우선 본 발명의 유황토는 광물질인 흙, 즉 토양에 유황을 혼합한 것으로서, 이러한 토양으로는 미생물이 다량으로 살아있는 갯벌의 개흙이나 산이나 들 및 강가 및 해안가 등의 점토 및 황토, 백토, 흑토 등의 다양한 미네랄이 함유되어 있으면서 원적외선이나 음이온 등이 다량으로 방출되는 토양을 사용하고, 유황의 사용 시 유황 특유의 향과 독성을 가지고 있어서 사용용도에 따라서 토양에 비하여 소량 또는 극소량으로 사용토록 한다.First, the sulfur soil of the present invention is a mineral soil, that is, a mixture of sulfur with soil, and such soil includes clay and loess, white soil, black soil, etc. Use soil that contains various minerals and emits a large amount of far-infrared rays or negative ions, and when using sulfur, it has a unique smell and toxicity.
상기 본 발명의 유황토 조성물은 도 1에 도시된 블록도에서와 같이 토양에 유황분말과 가연제가 혼합된 유황법제분말을 혼합하여 유황혼합토를 조성한 후 이에 혼합촉진제를 혼합하여 조성되는 것으로서, 유황혼합토와 혼합촉진제가 혼합된 유황토예비조성물을 건조시켜서 미소성(未燒成)유황토를 조성할 수 있고, 이러한 미소성유황토를 소성 후 냉각과 분쇄하여 소성유황토를 조성할 수도 있는 것이다.As shown in the block diagram shown in FIG. 1 , the sulfur soil composition of the present invention is composed by mixing a sulfur-method powder mixed with a sulfur powder and a flame retardant to the soil to form a sulfur mixed soil, and then mixing a mixing accelerator thereto. Uncalcined sulfur soil can be formed by drying the sulfur soil preliminary composition mixed with the mixture accelerator and calcined sulfur soil, and calcined sulfur soil can be formed by calcining and cooling and pulverizing the unburned sulfur soil.
본 발명의 유황토 조성물을 보다 상세히 설명하면 갯벌의 개흙, 점토, 황토, 백토, 흑토 중 어느 하나 또는 둘 이상이 혼합된 것으로 이루어진 토양 50~80중량%와, 유황분말 0.01~30중량%와 소나무 등의 목분, 솔잎, 애엽, 곡물겨, 곡식 중 어느 하나 또는 둘이상이 혼합된 가연체 70~99.99중량%가 혼합되어 이루어진 유황법제분말 20~50중량%이 혼합 조성된다.When the sulfur soil composition of the present invention is described in more detail, 50 to 80% by weight of a soil composed of any one or a mixture of two or more of open soil, clay, loess, white soil, and black soil of the tidal flat, 0.01 to 30% by weight of sulfur powder and pine Wood flour, pine needles, leaf leaves, grain bran, and 20-50 wt% of a sulfur-based powder made by mixing 70 to 99.99 wt% of any one or two or more of the mixed combustible material is mixed composition.
이와 같이 혼합 조성된 유황혼합토 60~90중량%와, 소금을 투입하여 10~40‰(permill)의 염분농도를 갖는 염수로 된 혼합촉진제 10~40중량%가 혼합 조성되는 것이다.As such, 60 to 90% by weight of the sulfur mixed soil mixed in this way and 10 to 40% by weight of a mixing accelerator made of salt having a salt concentration of 10 to 40‰ (permill) are mixed.
상기 유황토 조성물을 10~20%의 함수율을 갖도록 건조한 후 200~500℃에서 2~24시간 동안 소성한 다음, 100~300메시의 입자크기로 분쇄한 분말로 이루어지도록 할 수 있다.The sulfur soil composition may be dried to have a moisture content of 10 to 20%, calcined at 200 to 500° C. for 2 to 24 hours, and then pulverized to a particle size of 100 to 300 mesh.
상기와 같은 유황토 조성물의 제조방법은 하기의 실시 예에서 보는 바와 같이 다양한 제조방법에 따라서 다양한 조성물을 구현할 수 있는 것이다.The manufacturing method of the sulfur soil composition as described above can implement various compositions according to various manufacturing methods, as shown in the examples below.
[[ 실시예1Example 1 ]]
본 발명의 유황토 조성물의 제조방법으로서, 도 2에 도시된 바와 같이 유황토 조성물을 훈제용 분말로 사용하기 위한 제조방법인 것이다.As a manufacturing method of the sulfurous earth composition of the present invention, as shown in FIG. 2 , it is a manufacturing method for using the sulfurous earth composition as a powder for smoking.
1. 토양준비단계1. Soil preparation stage
갯벌의 개흙, 점토, 황토, 백토, 흑토 중 어느 하나 또는 둘 이상이 혼합된 토양을 준비하되, 사용할 토양을 수거한 후 이물질 분리기를 통해서 이물질을 걸러내고, 청정수가 공급되는 저장탱크에서 폭기 방식으로 물과 혼합하여 걸름망을 통과시키면서 걸러낸 다음, 마그네트선별기 또는 비철금속선별기를 사용하여 토양에 포함된 철과 비철금속을 제거한 후 탈수기 등을 사용하여 수분 포함된 함수율이 10~30정도가 되도록 탈수시켜서 입자크기가 100~200메시 정도의 분말이 되도록 구비한다.Prepare any one or a mixture of two or more of open soil, clay, loess, white soil, and black soil of the tidal flat. After collecting the soil to be used, filter out foreign substances through a foreign substance separator, After mixing with water and passing it through a sieve, remove the ferrous and non-ferrous metals contained in the soil using a magnetic separator or non-ferrous metal separator. It is prepared so that it becomes a powder of about 100-200 mesh.
2. 유황법제분말조성단계2. Sulfur-method powder formation step
유황법제분말은 유황과 가연체(可燃體)를 혼합 조성한 것으로서, 이는 분말로 이루어진 유황 0.01~30중량%에 소나무 등의 목분, 솔잎, 애엽, 곡물겨, 곡식 중 어느 하나 또는 둘이상이 혼합되어 분말로 분쇄한 가연체 70~99.99중량%를 혼합한 것이다.Sulfur-method powder is a mixture of sulfur and combustible material, which is composed of 0.01 to 30% by weight of sulfur consisting of powder, wood powder such as pine, pine needles, leaf, grain bran, grain, and any one or two or more of them are mixed. 70 to 99.99% by weight of the combustible body pulverized into powder is mixed.
이때 사용되는 가연체는 유황과 혼합되어 하기의 유황혼합토조성단계에서 토양과 혼합될 시 유황의 혼합이 보다 골고루 이루어지도록 하면서 추후 훈제용 분말이나 소성 시 불에 잘 타게 되어 화력을 높여서 보다 신속하고 높은 온도로 유황과 토양의 소성이 고르게 이루어지도록 하는 기능과 더불어 가연체의 소재인 소나무, 솔잎, 애엽, 곡물겨, 곡식 등의 각 성분이 흡수되도록 하여 유황토 조성물을 제조하기 위한 것이다.The combustible body used at this time is mixed with sulfur so that when it is mixed with the soil in the sulfur mixed soil composition step below, the sulfur is mixed more evenly, and the powder for smoking or later burns easily when calcined. This is to prepare a sulfur soil composition by allowing each component such as pine, pine needles, leaf leaves, grain bran, and grains to be absorbed, which are combustible materials, in addition to the function of ensuring that the sulfur and soil are evenly calcined with temperature.
3. 유황혼합토조성단계3. Sulfur Mixed Soil Formation Step
상기 토양준비단계에 의해서 구비된 토양 50~80중량%와 상기 유황법제분말조성단계를 거쳐서 조성된 유황법제분말 20~50중량%를 교반기에서 혼합하여 유황혼합토를 구비토록 하는 단계로서, 토양과 유황법제분말을 충분히 섞이도록 한다.50 to 80% by weight of the soil prepared by the soil preparation step and 20 to 50% by weight of the sulfur method powder prepared through the sulfur method powder forming step are mixed in a stirrer to prepare a sulfur mixed soil, the soil and sulfur Make sure that the legal powder is sufficiently mixed.
4. 혼합촉진단계4. Mixing promotion step
상기 유황혼합토조성단계에서 토양과 유황법제분말이 혼합된 유황혼합토를 염수로 된 혼합촉진제를 혼합하여 유황토예비조성물을 구비토록 하되, 이러한 유황토예비조성물은 유황혼합토 60~90중량%에 소금을 투입하여 10~40‰의 염분농도를 갖는 염수로 된 혼합촉진제 10~40중량%를 혼합 조성토록 한다.In the sulfur mixed soil composition step, the sulfur mixed soil in which the soil and the sulfur method powder are mixed is mixed with a brine mixing accelerator to prepare a sulfur soil preliminary composition, and this sulfur soil preliminary composition is prepared by adding salt to 60 to 90 wt% of the sulfur mixture soil. By input, 10 to 40% by weight of a mixing accelerator made of brine having a salt concentration of 10 to 40‰ is mixed.
이와 같이 10~40‰의 염분농도를 갖는 염수로 된 혼합촉진제를 혼합함으로 해서 혼합되는 토양 및 유황법제분말의 변질과 세균번식 등을 방지할 수 있는 등 염의 효능을 동시에 제공하게 되는 것이다.In this way, by mixing the mixing accelerator made of brine having a salt concentration of 10 to 40‰, the effect of salt can be provided at the same time, such as preventing the deterioration and bacterial propagation of the mixed soil and sulfur powder.
5. 건조단계5. Drying stage
상기 혼합촉진단계를 거쳐서 구비된 유황토예비조성물을 자체 함수율이 10~20%로 건조되도록 건조기 등에서 70~100℃의 열로 예열하고, 이와 같이 건조기에서 70~100℃의 열로 유황토예비조성물을 함수율 10~20%로 건조시켜서 미소성유황토를 제조토록 한다.The sulfur soil preliminary composition provided through the mixing promotion step is preheated with heat of 70 to 100° C. in a dryer, etc. so that its moisture content is dried to 10 to 20%, and in this way, the sulfur soil preliminary composition is heated at 70 to 100° C. in the dryer to increase the moisture content. Dry to 10-20% to produce uncalcined sulfur soil.
6. 훈제분말완성단계6. Smoked powder completion stage
상기 건조단계를 거친 미소성유황토를 100~300메시로 분쇄 후 훈제용 분말로 포장하여 완성하되, 이러한 훈제용 분말의 경우 훈제용기의 내부 하측에 깔아서 훈제용기의 외부에서 가해지는 화염에 가열되어 훈제용기 내부 바닥에 있는 유황토에서 방사하는 원적외선 파장인 공명, 흡수, 진동 등 심달력에 의해 석쇠위에 올려진 고지방질 고기를 태우지 않고 기름을 탈수시키므로 맛과 향, 간이 맞는 고단백질 훈제 육류를 제공하여 국민건강에 기여하는 훈제 음식물을 제공할 수 있다.The unbaked sulfur soil that has undergone the drying step is crushed into 100 to 300 mesh and then packaged into a smoked powder to complete it. In the case of such a smoked powder, it is spread on the lower inside of the smoking container and heated by a flame applied from the outside of the smoking container to smoke. By dehydrating the oil without burning the high-fat meat placed on the grill by the deep calendar such as resonance, absorption, and vibration, which are the wavelengths of far-infrared radiation emitted from the sulfur soil at the bottom of the container, we provide high-protein smoked meat with a good taste, aroma and seasoning. Smoked food that contributes to public health can be provided.
[[ 실시예2Example 2 ]]
본 발명의 유황토 조성물의 제조방법으로서, 도 3에 도시된 바와 같이 유황토 조성물을 입욕용 분말인 입욕제로 사용하기 위한 제조방법인 것이다.As a manufacturing method of the sulfurous earth composition of the present invention, as shown in FIG. 3 , it is a manufacturing method for using the sulfurous earth composition as a bath powder, which is a bath powder.
1. 토양준비단계1. Soil preparation stage
갯벌의 개흙, 점토, 황토, 백토, 흑토 중 어느 하나 또는 둘 이상이 혼합된 토양을 준비하되, 사용할 토양을 수거한 후 이물질 분리기를 통해서 이물질을 걸러내고, 청정수가 공급되는 저장탱크에서 폭기 방식으로 물과 혼합하여 걸름망을 통과시키면서 걸러낸 다음, 마그네트선별기 또는 비철금속선별기를 사용하여 토양에 포함된 철과 비철금속을 제거한 후 탈수기 등을 사용하여 수분 포함된 함수율이 10~30정도가 되도록 탈수시켜서 입자크기가 100~200메시 정도의 분말이 되도록 구비한다.Prepare any one or a mixture of two or more of open soil, clay, loess, white soil, and black soil of the tidal flat. After collecting the soil to be used, filter out foreign substances through a foreign substance separator, After mixing with water and passing it through a sieve, remove the ferrous and non-ferrous metals contained in the soil using a magnetic separator or non-ferrous metal separator. It is prepared so that it becomes a powder of about 100-200 mesh.
2. 유황법제분말조성단계2. Sulfur-method powder formation step
유황법제분말은 유황과 가연체(可燃體)를 혼합 조성한 것으로서, 이는 분말로 이루어진 유황 0.01~30중량%에 소나무 등의 목분, 솔잎, 애엽, 곡물겨, 곡식 중 어느 하나 또는 둘이상이 혼합되어 분말로 분쇄한 가연체 70~99.99중량%를 혼합한 것이다.Sulfur-method powder is a mixture of sulfur and combustible material, which is composed of 0.01 to 30% by weight of sulfur consisting of powder, wood powder such as pine, pine needles, leaf, grain bran, grain, and any one or two or more of them are mixed. 70 to 99.99% by weight of the combustible body pulverized into powder is mixed.
이때 사용되는 가연체는 유황과 혼합되어 하기의 유황혼합토조성단계에서 토양과 혼합될 시 유황의 혼합이 보다 골고루 이루어지도록 하면서 추후 훈제용 분말이나 소성 시 불에 잘 타게 되어 화력을 높여서 보다 신속하고 높은 온도로 유황과 토양의 소성이 이루어지도록 하는 기능과 더불어 가연체의 소재인 소나무, 솔잎, 애엽, 곡물겨, 곡식 등의 각 성분이 흡수되도록 하여 유황토 조성물을 제조하기 위한 것이다.The combustible body used at this time is mixed with sulfur so that when it is mixed with the soil in the sulfur mixed soil composition step below, the sulfur is mixed more evenly, and the powder for smoking or later burns easily when calcined. This is to prepare a sulfur soil composition by allowing each component such as pine, pine needles, aphids, grain bran, and grains to be absorbed, which are combustible materials, in addition to the function of allowing the sulfur and soil to be calcined by temperature.
3. 유황혼합토조성단계3. Sulfur Mixed Soil Formation Step
상기 토양준비단계에 의해서 구비된 토양 50~80중량%와 상기 유황법제분말조성단계를 거쳐서 조성된 유황법제분말 20~50중량%를 교반기에서 혼합하여 유황혼합토를 구비토록 하는 단계로서, 토양과 유황법제분말을 충분히 섞이도록 한다.50 to 80% by weight of the soil prepared by the soil preparation step and 20 to 50% by weight of the sulfur method powder prepared through the sulfur method powder forming step are mixed in a stirrer to prepare a sulfur mixed soil, the soil and sulfur Make sure that the legal powder is sufficiently mixed.
4. 혼합촉진단계4. Mixing promotion step
상기 유황혼합토조성단계에서 토양과 유황법제분말이 혼합된 유황혼합토를 염수로 된 혼합촉진제를 혼합하여 유황토예비조성물을 구비토록 하되, 이러한 유황토예비조성물은 유황혼합토 60~90중량%에 소금을 투입하여 10~40‰의 염분농도를 갖는 염수로 된 혼합촉진제 10~40중량%를 혼합 조성토록 한다.In the sulfur mixed soil composition step, the sulfur mixed soil in which the soil and the sulfur method powder are mixed is mixed with a brine mixing accelerator to prepare a sulfur soil preliminary composition, and this sulfur soil preliminary composition is prepared by adding salt to 60 to 90 wt% of the sulfur mixture soil. By input, 10 to 40% by weight of a mixing accelerator made of brine having a salt concentration of 10 to 40‰ is mixed.
5. 건조단계5. Drying stage
상기 혼합촉진단계를 거쳐서 구비된 유황토예비조성물을 자체 함수율이 10~20%로 건조되도록 건조기 등에서 70~100℃의 열로 예열하고, 이와 같이 건조기에서 70~100℃의 열로 유황토예비조성물을 함수율 10~20%로 건조시켜서 미소성유황토를 제조토록 한다.The sulfur soil preliminary composition provided through the mixing promotion step is preheated with heat of 70 to 100° C. in a dryer, etc. so that its moisture content is dried to 10 to 20%, and in this way, the sulfur soil preliminary composition is heated at 70 to 100° C. in the dryer to increase the moisture content. Dry to 10-20% to produce uncalcined sulfur soil.
6. 훈제분말완성단계6. Smoked powder completion stage
상기 건조단계를 거친 미소성유황토를 100~300메시로 분쇄 후 훈제용 분말로 포장하여 완성토록 한다.The unbaked sulfur soil that has passed through the drying step is crushed into 100-300 mesh, and then packaged with powder for smoking to complete.
여기까지는 상기 실시예1과 같으나, 이와 같이 훈제용 분말로 사용한 후 회수하여 소성, 냉각, 분쇄단계를 거치거나, 상기 훈제용 분말로 사용하지 않고서 건조단계 다음에 바로 소성, 냉각, 분쇄단계를 거쳐서 소성유황토로 사용할 수 있는 것이다.Up to this point, it is the same as in Example 1, but after being used as a smoked powder in this way, it is recovered and then calcined, cooled, and pulverized. It can be used as calcined sulfur soil.
7. 훈제분말회수단계7. Smoked powder recovery step
상기 훈제분말완성단계를 거쳐서 제조된 훈제용 분말을 훈제대상물을 훈제할 시 사용 후 회수토록 한다.When smoking a smoked object, the smoked powder manufactured through the smoked powder completion step is recovered after use.
8. 유황재투입단계8. Reintroduction of sulfur
상기 훈제분말회수단계에 의해서 회수된 훈제분말에는 유황의 냄새를 싫어하는 식객을 위하여 유황비율을 최소화하였으므로 이때 회수된 훈제회수분말 100중량부에 유황분말 0.01~30중량부를 재투입해서 유황의 효능을 증가하는 공정을 거치도록 한다.In the smoked powder recovered by the smoked powder recovery step, the sulfur ratio was minimized for those who do not like the smell of sulfur. to go through the process.
9. 소성단계9. Firing Step
소성단계는 상기에서도 명시하였던 바와 같이 건조단계에서 훈제분말완성단계와 훈제분말회수단계와 유황재투입단계를 거쳐서 진입할 수도 있고, 건조단계에서 훈제분말로 사용하지 않고 바로 진입할 수도 있는 것이다.As stated above, the firing step may be entered through the smoked powder completion step, the smoked powder recovery step, and the sulfur re-injection step in the drying step, as described above, or may be entered directly without using the smoked powder in the drying step.
먼저 유황재투입단계를 거친 훈제회수분말을 200~500℃의 온도로 2~24시간 동안 소성로에서 소성을 거쳐서 소성유황토를 제조토록 하거나, 훈제분말로 사용하지 않고 건조단계를 거친 미소성유황토를 200~500℃의 온도로 2~24시간 동안 소성로에서 소성을 거쳐서 소성유황토를 제조토록 한다.First, the smoked recovery powder, which has undergone the sulfur re-injection step, is calcined in a kiln at a temperature of 200 to 500 ° C for 2 to 24 hours to produce calcined sulfur clay, or uncalcined sulfur clay that has gone through the drying step without using it as a smoked powder. The calcined sulfur soil is produced through calcination in a calcination furnace at a temperature of 200~500℃ for 2~24 hours.
이러한 소성단계에 의하면 유황 특유의 냄새나 독성을 200~500℃의 온도에서 소멸시켜주는 기능을 하면서 광물질인 토양에서 배출되는 라돈을 최소화시키는 기능을 하게 되는 것으로서, 소성 시 미송성유황토에 혼합되어 있는 유황법제분말 내의 가연체에 의해서 200~500℃의 온도에서보다 높은 온도에서 연소되는 효과를 내어 보다 단시간에 함께 혼합되어 있던 유황을 가열하여 유황의 독성과 냄새를 원천적으로 제거할 수 있으며, 이러한 가연체의 기능에 의해서 토양이 높은 온도에서 가열되면서 라돈의 방출을 현저하게 저감되어 현재 문제가 많이 되고 있는 라돈의 방출을 최소화시킬 수 있는 것이다.According to this calcination step, it has a function of extinguishing the peculiar smell or toxicity of sulfur at a temperature of 200~500℃ while minimizing radon emitted from the soil, which is a mineral. The combustible material in the sulfur powder produces the effect of burning at a higher temperature than that of 200~500℃, heating the sulfur mixed together in a shorter time, so that the toxicity and smell of sulfur can be fundamentally removed. As the soil is heated at a high temperature by the function of the sieve, the emission of radon is significantly reduced, and the emission of radon, which is currently a problem, can be minimized.
이러한 라돈 검출을 직접 테스트하여 아래 표와 같이 종래의 황토로만 된 황토분말과, 본 발명에서 소성 전의 미소성유황토조성물과, 본 발명에서 소성단계를 거친 소성유황토조성물을 동일한 라돈측정기로 측정한 결과를 대비한 것과 같이 라돈 방출 수치가 소성을 거치면서 극감함을 알 수 있는 것이다.As shown in the table below, the radon detection was directly tested and the result of measuring the conventional loess-only loess powder, the uncalcined sulfuric earth composition before calcination in the present invention, and the calcined sulfuric earth composition that went through the calcination step in the present invention with the same radon meter as shown in the table below. It can be seen that the level of radon emission is drastically reduced through firing.
10. 냉각단계10. Cooling stage
소성단계 후 가열된 소성유황토를 후술하는 분쇄기에 투입 시 분쇄기의 변형이나 파손이 되지 않을 정도로 소정의 온도로 냉각토록 하되, 각종 열교환기나 냉각기를 이용하는 인공 냉각과 상온에 두거나 자연바람에 의한 자연 냉각 중 어떤 방식으로도 가능하다.After the calcination step, when the heated calcined sulfur soil is put into the pulverizer to be described later, it is cooled to a predetermined temperature so as not to cause deformation or damage to the pulverizer. can be done in any way.
11. 분쇄단계11. Crushing step
상기의 냉각단계를 거쳐서 냉각이 이루어진 소성유황토를 분쇄기에 투입하여 100~300메시의 유황토분말로 분쇄토록 한다.The calcined sulfur soil, which has been cooled through the cooling step, is put into the grinder and pulverized into 100-300 mesh sulfur soil powder.
상기 분쇄된 소성유황토는 도 3에서 보는 바와 같이 입욕용 분말인 입욕제로 바로 사용할 수 있는 것이다.The pulverized calcined sulfur soil can be directly used as a bath powder, which is a bath powder, as shown in FIG. 3 .
[[ 실시예3Example 3 ]]
본 발명의 실시예3은 도 4에 도시된 바와 같이 도 3의 상기 실시예2의 토양준비단계 내지 건조단계를 거친 미소성유황토를 훈제분말완성단계, 훈제분말회수단계, 유황재투입단계를 거쳐서 회수된 훈제회수분말 또는 건조단계에서 바로 공급된 미소성유황토를 소성단계와 냉각단계 및 분쇄단계를 거쳐서 완성된 유황토분말을 이용하여 건축용 패널이나 침구용 패널이나 침구용 볼 등의 건축용품 및 침구용품을 제조하기 위해 건축및침구용품성형단계를 거치도록 한 것이다.In Example 3 of the present invention, as shown in FIG. 4, the uncalcined sulfur soil that has gone through the soil preparation step to the drying step of Example 2 of FIG. 3 is smoked powder completion step, smoked powder recovery step, and sulfur re-input step Recovered smoked recovery powder or uncalcined sulfur soil supplied directly from the drying step is used for calcining, cooling, and pulverization steps, and then using the completed sulfur clay powder for building panels, bedding panels, bedding balls, and other building products and bedding It is to go through the building and bedding product molding steps to manufacture the product.
이러한 건축및침구용품성형단계는 상기 분쇄단계를 거쳐서 분쇄된 유황토분말을 패널형태나 볼형태로 성형하여 소성단계를 거쳐서 토양에 함유되어 있던 라돈을 저감시켜서 건축용이나 침구용에 사용 시 라돈방출은 최소화시킨 건축용품 및 침구용품을 제조하기 위한 것으로서, 이러한 건축및침구용품성형단계에서 건축 및 침구용품의 분진 비산을 방지하기 위해서 성형 후 함수율이 10~30%정도 내 유지하도록 습도조절기를 사용할 수도 있다.In this building and bedding product forming step, the sulfur soil powder pulverized through the pulverization step is molded into a panel shape or a ball shape, and the radon contained in the soil is reduced through the firing step to reduce radon emission when used for construction or bedding. As for the manufacture of minimized construction and bedding products, in order to prevent dust scattering of construction and bedding products in this construction and bedding product molding step, a humidity controller may be used to maintain the moisture content within 10 to 30% after molding. .
상기 건축용품이나 침구용품으로는 실내외의 벽에 부착 고정시키는 건축용 패널이나, 침대의 매트리스 상면 또는 내측에 안치 또는 고정되는 침대 매트리스용 패널이나, 침대 매트리스 내측의 상하 포지에 의해서 생성된 포켓에 내입되는 볼 형태의 침대 매트리스용 볼이나, 베개나 방석 또는 쿠션 등에 패널 형태나 볼 형태로 내입되도록 하여 사용할 수는 등 다양한 분야에 라돈의 검출을 최소화시켜서 두루 사용할 수 있는 것이다.The building products or bedding products include a building panel that is attached and fixed to an indoor and outdoor wall, a panel for a bed mattress that is placed or fixed on the upper surface or inside of the mattress of the bed, or a pocket created by the upper and lower forges inside the bed mattress. It can be used universally by minimizing the detection of radon in various fields, such as a ball-shaped bed for mattress balls, a pillow, a cushion, or a cushion, etc.
[[ 실시예4Example 4 ]]
본 발명의 실시예4는 도 5에 도시된 바와 같이 도 3 및 도 4의 상기 실시예2 및 실시예3의 토양준비단계 내지 건조단계를 거친 미소성유황토를 훈제분말완성단계, 훈제분말회수단계, 유황재투입단계를 거쳐서 회수된 훈제회수분말 또는 건조단계에서 바로 공급된 미소성유황토를 소성단계와 냉각단계 및 분쇄단계를 거쳐서 완성된 유황토분말을 초미립자로 더 잘게 분쇄하여 염증치료 또는 피부미용 등의 치료용품 및 미용용품을 제조하기 위해서 미분쇄단계, 치료및미용용품제조단계, 발향단계를 거치도록 한 것이다.In Example 4 of the present invention, as shown in FIG. 5, smoked powder completion step, smoked powder recovery step of the uncalcined sulfur soil that has passed through the soil preparation step to the drying step of Examples 2 and 3 of FIGS. 3 and 4 Inflammation treatment or skin care by finely pulverizing the smoked recovery powder recovered through the sulfur re-injection step or the uncalcined sulfur soil supplied directly from the drying step into ultra-fine particles through the firing step, cooling step, and pulverization step In order to manufacture therapeutic and cosmetic products, such as, a fine grinding step, a treatment and cosmetic product manufacturing step, and a scent diffusion step.
이러한 미분쇄단계는 상기 분쇄단계를 거쳐서 분쇄된 유황토분말을 초미립자분쇄기에 투입하여 300~500메시의 입자크기의 초미립자로 미분쇄토록 한 것이고, 이러한 치료및미용용품제조단계는 상기 미분쇄단계를 거쳐 미분쇄된 유황토미분말에 자체적으로 접착 성분을 가지는 천연의 엿, 꿀, 찹쌀풀 중 어느 하나 또는 둘이상이 혼합된 천연접착제를 섞어서 겔상태가 되도록 제조하여 환부나 피부에 접착토록 해서 염증치료 또는 피부미용에 사용토록 한 것이며, 필요에 따라서 발향단계를 더할 수 있는 것으로서, 이러한 발향단계는 상기 치료및미용용품제조단계에서 천영접착제의 혼합 시 천연접착제 100중량부에 5~30중량부의 함량으로 다양한 향료를 투입하여 다양한 향을 방출토록 할 수 있는 것이다.In this fine pulverization step, the sulfur earth powder pulverized through the pulverization step is put into an ultra-fine particle grinder to be pulverized into ultra-fine particles having a particle size of 300 to 500 mesh. Inflammation treatment by mixing finely pulverized sulfur tomi powder with any one of natural syrup, honey, and glutinous rice paste having its own adhesive component, or a natural adhesive mixed with two or more, to form a gel, and adhere to the affected area or skin Alternatively, it is intended to be used for skin care, and a fragrance diffusion step can be added as needed. This fragrance diffusion step is performed in the treatment and beauty product manufacturing stage, when mixing the natural adhesive with a content of 5 to 30 parts by weight in 100 parts by weight of the natural adhesive. It is possible to emit various fragrances by adding various fragrances.
상기 본 발명의 유황토 조성물 및 이의 제조방법에 의하면 각종 토양에 곡물껍질 또는 목재의 분말이 혼합된 유황을 염수와 함께 소량으로 혼합하여 토양과 유황의 자체 성분에 의한 인체에 유익한 효과를 득하여 건장증진효과를 제공하는바, 닭이나 돈육 등의 훈제 시 훈제기에 투입하여 훈제분말로 사용토록 할 수 있으며, 농업용 비료, 입욕제 등의 분말로 사용할 수 있으며, 라돈저감형 건축용 또는 침구용 패널 및 볼의 성형분말로 사용할 수 있으며, 염증 등의 환부나 피부에 접착하여 통증완화용 또는 미용용으로 사용할 수 있어서 다양한 용도로 두루 사용할 수 있으므로 다양한 분야에 두루 적용할 수 있는 효과를 가진다.According to the sulfur soil composition of the present invention and its manufacturing method, a small amount of sulfur mixed with grain bark or wood powder in various soils is mixed with brine in a small amount to obtain beneficial effects on the human body due to its own components of soil and sulfur, thereby improving health As it provides an effect, it can be used as a smoked powder by putting it into a smoker when smoking chicken or pork, and can be used as a powder for agricultural fertilizers and bathing agents, and forming radon-reducing architectural or bedding panels and balls It can be used as a powder, and it can be used for various purposes because it can be used for pain relief or cosmetic by adhering to the affected area such as inflammation or skin, so it has an effect that can be applied to various fields.
이에 더하여 토양에 유황을 혼합할 시 목분이나 곡분 등의 가연체와 혼합하여 유황혼합물의 소성 시 보다 높은 온도로 유도하면서 짧은 시간 내에 원활하게 소성이 이루어지도록 하는 효능과 함께 염수를 혼합하여 토양 및 유황 혼합물의 변질과 세균번식 등을 방지할 수 있는 등 염의 효능을 동시에 제공하게 되는 것이다.In addition, when sulfur is mixed with soil, it is mixed with combustible materials such as wood flour or grain flour to induce a higher temperature than when calcining the sulfur mixture, while mixing the brine with the effect of smoothly calcining within a short time. It is to provide the efficacy of the salt at the same time, such as preventing deterioration of the mixture and bacterial propagation.
본 발명에서 사용되는 유황은 질병치유의 오랜 역사를 가지고 있으며, 광물질 유황은 만병을 물리친다는 천하의 명약으로 알려진 금단의 주원료로 쓰여 왔을 만큼 그 약성이 매우 강하다고 알려져 있는 것이다.Sulfur used in the present invention has a long history of healing diseases, and mineral sulfur is known to have very strong weakness as it has been used as a forbidden main ingredient known as the world's best medicine to defeat all diseases.
이러한 유황토가 인체에 미치는 영향으로는 각종 암 발생 종양인자를 괴멸시켜는 면역세포 TNF를 증강시켜 각종 암 발생 억제기능과, 피부병을 생기게 하는 충을 괴멸시키므로 각종 피부질환 억제기능과, 몸 안에 냉기를 몰아내므로 힘줄과 뼈를 튼튼하게 하며 양기를 도와주는 기능 등을 한다고 알려져 있다.The effects of sulfur soil on the human body include the function of suppressing the occurrence of various cancers by enhancing the immune cell TNF that destroys various cancer-causing tumor factors, and suppressing various skin diseases by destroying the insects that cause skin diseases, It is known to have the function of strengthening tendons and bones and helping yang by driving away the
이상과 같이 본 발명의 상세한 설명에는 본 발명의 가장 바람직한 실시 예에 관하여 설명하였으나, 본 발명의 기술범위에 벗어나지 않는 범위 내에서는 다양한 변형실시도 가능하다 할 것이며, 따라서 본 발명의 보호범위는 상기 실시 예에 한정하여 정해지는 것이 아니라, 후술하는 특허청구범위의 기술들과 이들 기술로부터 균등한 기술수단들에까지 보호범위가 인정되어야 할 것이다.As described above, in the detailed description of the present invention, the most preferred embodiment of the present invention has been described, but various modifications are possible within the scope that does not depart from the technical scope of the present invention. It is not limited to the example, but the scope of protection should be recognized from the techniques of the claims to be described later and equivalent technical means from these techniques.
Claims (3)
분말로 이루어진 유황 0.01~30중량%에 소나무 등의 목분, 솔잎, 애엽, 곡물겨, 곡식 중 어느 하나 또는 둘이상이 혼합되어 분말로 분쇄한 가연체 70~99.99중량%를 혼합하여 유황법제분말을 조성토록 하는 유황법제분말조성단계;
토양준비단계에 의해서 구비된 토양 50~80중량%와 유황법제분말조성단계를 거쳐서 조성된 유황법제분말 20~50중량%를 교반기에서 혼합하여 유황혼합토를 구비토록 하는 유황혼합토조성단계;
유황혼합토조성단계에서 토양과 유황법제분말이 혼합된 유황혼합토 60~90중량%에 소금을 투입하여 10~40‰의 염수로 된 혼합촉진제 10~40중량%를 혼합하여 유황토예비조성물을 구비하는 혼합촉진단계;
유황토예비조성물을 함수율 10~20%로 건조하여 미소성유황토를 제조하는 건조단계;
건조단계를 거친 미소성유황토를 200~500℃의 온도로 2~24시간 동안 소성로에서 소성을 거쳐서 소성유황토를 제조하는 소성단계;
소성단계 후 가열된 소성유황토를 후술하는 분쇄기에 투입 시 분쇄기의 변형이나 파손이 되지 않을 정도로 소정의 온도로 냉각하는 냉각단계;
냉각단계를 거쳐서 냉각이 이루어진 소성유황토를 분쇄기에 투입하여 100~300메시의 유황토분말로 분쇄토록 하는 분쇄단계;
가 포함된 것을 특징으로 하는 유황토 조성물의 제조방법.
A soil preparation step of preparing one or a mixture of two or more of open soil, clay, loess, white soil, and black soil of the tidal flat with a particle size of 100 to 200 mesh;
Sulfur-method powder is prepared by mixing 0.01 to 30% by weight of sulfur consisting of powder and 70 to 99.99% by weight of a combustible body pulverized by mixing one or more of wood flour such as pine, pine needles, leaf leaves, grain bran, and grains. Sulfur-method powder formation step to make the composition;
A sulfur mixed soil composition step of mixing 50 to 80% by weight of the soil prepared by the soil preparation step and 20 to 50% by weight of the sulfur prepared powder prepared through the sulfur method powder forming step in a stirrer to prepare a sulfur mixed soil;
In the sulfur mixed soil composition step, salt is added to 60 to 90% by weight of sulfur mixed soil in which the soil and sulfur powder are mixed, and 10 to 40% by weight of a mixing accelerator made of 10 to 40‰ brine is mixed to provide a sulfur soil preliminary composition. mixing promotion step;
A drying step of drying the sulfur soil preliminary composition to a moisture content of 10 to 20% to produce uncalcined sulfur soil;
A calcination step of producing calcined sulfur soil by calcining the uncalcined sulfur soil that has undergone the drying step in a calcination furnace at a temperature of 200 to 500° C. for 2 to 24 hours;
A cooling step of cooling the heated calcined sulfur soil to a predetermined temperature so as not to deform or damage the pulverizer when the calcined sulfur soil is put into a pulverizer to be described later after the calcination step;
a crushing step of putting the calcined sulfur soil cooled through the cooling step into a crusher and pulverizing it into a sulfur soil powder of 100 to 300 mesh;
A method for producing a sulfur soil composition comprising a.
분쇄단계를 거쳐서 분쇄된 유황토분말을 패널형태나 볼형태로 성형하여 소성단계를 거쳐서 토양에 함유되어 있던 라돈을 저감시켜서 건축용이나 침구용에 사용 시 라돈방출은 최소화 할 수 있도록 제조하는 건축및침구용품성형단계;
가 더 포함된 것을 특징으로 하는 유황토 조성물의 제조방법.
The method of claim 1 ;
Construction and bedding manufactured to minimize radon emission when used for construction or bedding by reducing the radon contained in the soil through the firing step by molding the sulfur soil powder pulverized through the crushing step into a panel or ball shape. article forming step;
Method for producing a sulfur soil composition, characterized in that it further comprises.
분쇄단계를 거쳐서 분쇄된 유황토분말을 초미립자분쇄기에 투입하여 300~500메시의 입자크기의 초미립자로 미분쇄하는 미분쇄단계;
미분쇄단계를 거쳐 미분쇄된 유황토미분말에 자체적으로 접착 성분을 가지는 천연의 엿, 꿀, 찹쌀풀 중 어느 하나 또는 둘이상이 혼합된 천연접착제를 섞어서 겔상태가 되도록 제조하여 환부나 피부에 접착토록 해서 염증치료 또는 피부미용에 사용토록 하는 치료및미용용품제조단계;
가 더 포함된 것을 특징으로 하는 유황토 조성물의 제조방법.The method of claim 1 ;
A fine pulverization step of putting the sulfur earth powder pulverized through the pulverization step into an ultra-fine particle grinder and pulverizing it into ultra-fine particles having a particle size of 300 to 500 mesh;
It is manufactured in a gel state by mixing the finely pulverized sulfur tomi powder with any one or more of natural syrup, honey, and glutinous rice paste having its own adhesive component to form a gel, and adheres to the affected area or skin. A treatment and cosmetic product manufacturing step to be used for inflammation treatment or skin beauty;
Method for producing a sulfur soil composition, characterized in that it further comprises.